JP6085932B2 - Polyethylene-coated steel material and epoxy resin primer layer forming material - Google Patents

Description

  The present invention relates to a polyethylene-coated steel material and an epoxy resin primer layer forming material used for producing the polyethylene-coated steel material.

  Polyethylene-coated steel material with a polyethylene resin layer coated on steel as an anti-corrosion layer is excellent in anti-corrosion properties, so it can be used for various pipes for gas, water, cable protection, pipelines, and civil engineering steel pipes. Widely used for piles.

  Polyethylene-coated steel materials have been increasingly applied to applications that are buried in the seabed or underground. In that case, anticorrosion is often used together. Although steel is protected by the effect of cathodic protection, on the other hand, once the coating is damaged, there arises a problem that the polyethylene layer peels off from the interface with the steel material. This stripping is known as cathodic stripping.

  It is known that chromate treatment is effective as a method of suppressing this cathode peeling. For example, Patent Document 1 discloses a resin-coated heavy anti-corrosion steel material in which an epoxy primer layer, a maleic anhydride-modified polyolefin layer, and a polyolefin layer are sequentially laminated on a chromate-treated steel material having a chromate layer on the surface of the steel material.

  Patent Document 2 discloses that the surface of a steel material is chromated and a specific epoxy primer is applied thereon.

  The chromate treatment has been widely used as a base treatment for organic coating materials. However, in recent years it has been refrained from use due to environmental concerns. Therefore, at present, there is a demand for a technique for obtaining an organic coated steel material having excellent corrosion resistance by performing non-chromate treatment, for example, without performing chromate treatment.

  For example, Patent Document 3 describes a technique for obtaining an organic coated steel sheet having excellent corrosion resistance by performing a non-chromate treatment. However, since the non-chromate treatment is performed on the surface of the plated steel sheet and not directly on the surface of the steel material, the non-chromate treatment is not a treatment for suppressing cathode peeling.

  Patent Document 4 discloses an example in which a cathode film is suppressed by suppressing oxygen permeation by forming a clay film layer on a steel material. However, since the clay film layer is brittle and easily peeled off, there is a problem in durability. Furthermore, since a clay mineral aqueous dispersion must be used for the formation of the clay film layer, the technique described in Patent Document 4 uses a steel material surface on which the clay film layer is to be formed to form the clay film layer. It is necessary to make it horizontal, apply an aqueous dispersion thereto, leave it for a long time to deposit clay minerals, and further dry it for a long time, which is very difficult to apply industrially.

JP-A-2005-35061 JP 2000-190422 A JP 2011-111638 A JP 2008-229998 A

  In view of such circumstances, an object of the present invention is to improve the cathode peel resistance of a polyethylene-coated steel material.

  Means for solving the above problems are as follows.

  The inventors have prepared an epoxy resin primer layer (this material) formed on a steel material surface using a primer layer forming material (primer solution before curing) containing a specific amount of an epoxy resin, a curing agent, a clay mineral, and a silane coupling agent. In the specification, it has been found that a “primer layer” may be effective in preventing the cathode peeling.

  As described above, the clay film layer mainly composed of clay minerals is excellent in gas barrier properties, but has a problem in durability because it is brittle and easily peeled off. However, in the present invention, although the primer layer forming material contains a clay mineral, the problem that the primer layer is brittle and easily peels off does not occur unlike the clay film layer. This is because the clay mineral and the silane coupling agent are bonded to each other, so that the clay minerals are indirectly bonded to each other via the silane coupling agent, and the silane coupling agent is bonded to the clay mineral and the curing agent has a function. It is presumed that the primer layer does not become brittle because the clay mineral and the epoxy resin are indirectly bonded by reacting and bonding with the group. Moreover, it is estimated that a silane coupling agent contributes to the adhesive improvement of a primer layer by reacting with the hydroxyl group which exists on the steel material surface, and producing | generating an adhesive bond between a primer layer and steel materials.

  The present invention is based on the above findings and has the following characteristics.

  On the steel material, at least an epoxy resin primer layer, an adhesive polyethylene resin layer, and a polyethylene resin layer are provided in this order from the steel material side, and the epoxy resin primer layer has a total of 100 parts by mass of the epoxy resin and the curing agent. On the other hand, it is a layer formed by curing a primer layer forming material containing 10 to 100 parts by mass of a clay mineral and 5 to 40 parts by mass of a silane coupling agent having an epoxy group with respect to 100 parts by mass of the clay mineral. Polyethylene-coated steel material characterized by

  In the polyethylene-coated steel material of the present invention, the clay mineral is preferably a purified product of montmorillonite and / or a purified product of smectite.

  An epoxy resin primer layer forming material for forming an epoxy resin primer layer on a steel material, containing 10 to 100 parts by mass of a clay mineral with respect to a total of 100 parts by mass of an epoxy resin and a curing agent, and having an epoxy group An epoxy resin primer layer forming material comprising 5 to 40 parts by mass of a silane coupling agent having 100 parts by mass of the clay mineral.

  The polyethylene coating layer formed by sequentially forming an epoxy resin primer layer containing a clay mineral and a silane coupling agent, an adhesive polyethylene resin layer and a polyethylene resin layer on a steel material is compared with the clay film layer shown in Patent Document 4. It is difficult to peel off easily because it is strong, and cathode peeling due to adhesion deterioration of the epoxy resin primer layer when the anticorrosion is used together can be suppressed to the same extent as the chromate treatment. As described above, the polyethylene-coated steel material of the present invention has excellent cathode peeling resistance without using chromate, which is refrained from use due to environmental concerns. It is suitable for.

  The present invention will be described in detail below, but the present invention is not limited to the following embodiments.

The polyethylene-coated steel material of the present invention has at least an epoxy resin primer layer (primer layer), an adhesive polyethylene resin layer, and a polyethylene resin layer in this order on the steel material. Hereinafter, the steel material, the primer layer, the adhesive polyethylene resin layer, and the polyethylene resin layer will be described.
<Steel>
In the present invention, the type of steel material is not particularly limited, and any of ordinary steel or alloy steel to which elements such as Ni, Cu, Cr, Mo, Mg, Al, Ti, W, and Sb are added can be used. Further, the shape of the steel material is not particularly limited, and any of a shape steel, a steel plate, a steel bar, a steel pipe pile, a steel sheet pile, a steel pipe and the like can be used as the steel material.

  Steel materials used outdoors, especially in the ground and seawater, are usually anti-corrosive, so that the coating is damaged, and once the exposed steel is formed, the problem of cathode peeling tends to occur. However, with the polyethylene-coated steel material of the present invention, the problem of cathode peeling can be suppressed to the same extent as when a chromate treatment agent is used. Examples of “steel materials used outdoors, especially in the ground and seawater” include steel pipes used for various pipes such as gas, water, cable protection, and pipelines, and steel pipes used for civil engineering. Examples include piles.

In the present invention, it is preferable to use a steel material that has been subjected to sand blasting, steel grid blasting, alkaline degreasing, pickling, etc. in order to remove scales and contaminants on the surface of the steel.
<Epoxy resin primer layer>
The primer layer contains 10 to 100 parts by mass of clay mineral with respect to 100 parts by mass in total of the epoxy resin and the curing agent, and 5 to 40 parts by mass of the silane coupling agent having an epoxy group with respect to 100 parts by mass of the clay mineral. This is a layer formed by curing the primer layer forming material contained in part.

  Here, the sum of the epoxy resin and the curing agent refers to an epoxy resin and a curing agent that mainly form a cured film when cured.

  Hereinafter, the epoxy resin, the curing agent, the clay mineral, the silane coupling agent, and other components will be described in order.

  What is necessary is just to have 2 or more of epoxy groups in 1 molecule with an epoxy resin, and the kind is not specifically limited. Examples of epoxy resins include glycidyl ether type epoxy resins obtained by reaction of polyphenol compounds such as bisphenol A and bisphenol F with epihalohydrin, hydrogenated bisphenol A type epoxy resins, glycidyl ester type epoxy resins, and other glycidyl ether type epoxy resins. , Alicyclic epoxy resins, modified epoxy resins obtained by modifying these epoxy resins with alkylphenols and / or fatty acids, phenol novolac resins or novolac epoxy resins obtained by reacting alkylphenol novolac resins with epichlorohydrin, and the like. be able to. These can be used alone or in combination of two or more. In the present invention, it is preferable to use a so-called bisphenol type epoxy resin which is a glycidyl ether of bisphenols.

  The kind of the curing agent is not particularly limited, and for example, an amine curing agent such as polyamine or a modified product thereof can be preferably used. Examples of amine-based curing agents include aliphatic polyamines, alicyclic polyamines, aromatic polyamines, Michael addition products, epoxy resin adducts, Mannich addition products of these polyamines, and ketimines, polyamides, polyamides. Examples thereof include a reaction product of an amine, a fatty acid and a polyamine, a reaction product of a dimer acid and a polyamine, and an aliphatic polyamine or a modified product thereof is preferable. These can be used alone or in combination of two or more.

  The blending amount of the epoxy resin and the curing agent may be such that each of them reacts and cures almost without excess, specifically, the ratio of the number of moles of epoxy groups to the number of moles of active hydrogen in the curing agent. May be blended so as to be 1.0: 0.8 to 1.0: 1.2. The compounding quantity of a hardening | curing agent is 10-100 mass parts normally with respect to 100 mass parts of epoxy resins.

  The clay mineral enhances the gas barrier property of the primer layer and improves the cathode peel resistance of the polyethylene-coated steel sheet.

  Although the kind of clay mineral is not particularly limited, for example, bentonite, montmorillonite, beidellite, saponite, smectite, illite, glowconite, chlorite, zeolite, kaolinite and the like can be used. These can be used alone or in combination of two or more.

  In particular, a purified product obtained by artificially purifying clay minerals is preferable because it does not contain impurities. Moreover, in this invention, you may use what is marketed as a purified product. In the present invention, it is particularly preferable to use artificially purified montmorillonite or artificially purified smectite.

  In the present invention, a clay mineral having a hydroxyl group on the surface can be preferably used from the viewpoint of further improving the cathode peelability. The hydroxyl group on the surface of the clay mineral is likely to be bonded to the silane coupling agent, and the primer layer becomes a stronger film. Therefore, it is considered that the cathode peelability is remarkably improved.

  The compounding quantity of a clay mineral is 10-100 mass parts with respect to a total of 100 mass parts of an epoxy resin and a hardening | curing agent. If the amount is less than 10 parts by mass, sufficient gas barrier properties cannot be obtained, and the effect of improving the cathode peel resistance becomes insufficient. When the amount exceeds 100 parts by mass, the primer layer becomes brittle and the resistance to cathodic peeling becomes insufficient.

  In the present invention, a silane coupling agent having an epoxy group as an organic functional group is used as the silane coupling agent. This is because the silane coupling agent having an epoxy group is excellent in reactivity with the curing agent. Examples of the silane coupling agent having an epoxy group include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldiethoxysilane, and 3-glycidoxypropyltriethoxysilane. These epoxy group-containing silane coupling agents are also preferable in that they all have a plurality of silanol groups by hydrolysis. In the case of a silane coupling agent having a plurality of silanol groups, clay minerals are indirectly bonded via a silane coupling agent, or a silane coupling agent and a steel material are bonded, via a silane coupling agent. As a result of the indirect bonding between the epoxy resins and the dense formation of the cross-linked structure, a fixing effect for firmly fixing the primer layer on the steel surface can be expected.

  The compounding quantity of a silane coupling agent is 5-40 mass parts with respect to 100 mass parts of clay minerals. When the blending amount is less than 5 parts by mass, the above-mentioned various bonding effects do not appear, and when it exceeds 40 parts by mass, a large number of silane coupling agents undergo a self-condensation reaction. Or, the number of bonds between epoxy resins and clay minerals is reduced, and the bonds are weakened. In addition, there are adverse effects such as loss of the stability of the primer solution before curing. In addition, in this invention, you may use it combining 2 or more types of silane coupling agents other than using one type of silane coupling agent.

  The primer layer forming material may contain other components other than the essential components as long as the effects of the present invention are not impaired.

  Examples of other components include pigments such as silica and titanium oxide, rust preventive pigments such as aluminum phosphate, aluminum polyphosphate, ammonium zirconium carbonate, ammonium zircon fluoride, and ammonium metavanadate, and reactive diluents. The blending amount of these components is preferably less than 50% by mass in the primer layer forming material.

  Then, the formation method of a primer layer is demonstrated. First, an epoxy resin, a clay mineral, and other components to be blended as necessary are mixed at a predetermined blending ratio. After mixing, a silane coupling agent is added and further mixed. The mixing time in mixing after addition of the silane coupling agent is not particularly limited, but is usually 30 minutes to 1 hour 30 minutes.

  Subsequently, a primer layer forming material is obtained by adding to the mixture such that the curing agent has a predetermined blending ratio.

  Next, this primer layer forming material is adhered to the steel surface. The method of attaching is not particularly limited, and examples thereof include spray coating, roll coating, brush coating, and ironing. The adhesion amount of the primer layer forming material is not particularly limited, but is generally set to such an adhesion amount that the primer layer has a thickness of 10 to 70 μm.

Next, the primer layer forming material attached by heating is cured to form a primer layer on the steel material. The heating temperature is not particularly limited, but is generally 100 to 250 ° C. Also, the heating method is not particularly limited, and any method such as high-frequency induction heating, far-infrared heating, or gas heating can be employed.
<Adhesive polyethylene resin layer>
An adhesive polyethylene resin layer is formed between the primer layer and the polyethylene resin layer. By having the adhesive polyethylene resin layer, the polyethylene resin layer and the primer layer are in close contact with each other, and the problem of peeling between the polyethylene resin layer and the primer layer hardly occurs.

  The adhesive polyethylene resin layer is made of polyethylene resin such as high density polyethylene, medium density polyethylene, low density polyethylene, and linear low density polyethylene with unsaturated carboxylic acid such as maleic acid, acrylic acid or methacrylic acid or its acid anhydride. A modified product or a product obtained by appropriately diluting the modified product with a polyolefin resin is a conventionally known modified polyethylene resin.

In the present invention, the thickness of the adhesive polyethylene resin layer is not particularly limited, but is usually 0.1 to 1 mm, and more generally 0.3 to 0.8 mm.
<Polyethylene resin layer>
The polyethylene resin layer is a layer containing a polyethylene resin as an essential component. The kind of polyethylene resin is not particularly limited, and any of high density polyethylene, medium density polyethylene, low density polyethylene, and linear low density polyethylene can be used. These can be used alone or in combination of two or more.

  The compounding quantity of the polyethylene resin in a polyethylene resin layer is not specifically limited. For example, it is preferable that it is 90-100 mass%.

  The polyethylene resin layer may contain other resins, stabilizers, antioxidants, pigments, crystal nucleating agents, reinforcing agents and the like as long as the effects of the present invention are not impaired.

  The method for forming the adhesive polyethylene resin layer and the polyethylene resin layer on the primer layer is not particularly limited, and a conventionally known method can be applied. For example, an extrusion coating method can be adopted.

  When forming by the extrusion coating method, the adhesive polyethylene resin in a molten state is extruded from an extruder and attached onto a steel material to form an adhesive polyethylene resin layer, and then a polyethylene resin layer is similarly formed thereon. Alternatively, two layers of adhesive polyethylene resin and polyethylene resin may be coextruded at the same time and pasted onto a steel material, so that the adhesive polyethylene resin layer and the polyethylene resin layer are simultaneously pasted and then cooled to form a resin layer. It may be formed.

In the present invention, the thickness of the polyethylene resin layer is not particularly limited, but is usually 1 to 5 mm, and more generally 1.5 to 3.5 mm.
<Other layers>
The polyethylene-coated steel material of the present invention only needs to be obtained by laminating at least a primer layer, an adhesive polyethylene resin layer, and a polyethylene resin layer in this order on the steel material. There may be a layer. Further, the other layer may be a single layer or a multilayer.

  Examples of the layer formed between the steel material and the primer layer include a chemical conversion treatment layer. A chemical conversion treatment layer is a layer formed by performing chemical conversion treatment to the steel material surface. By having the chemical conversion treatment layer, the corrosion resistance of the polyethylene-coated steel material is further improved. In addition, the chemical conversion treatment uses a non-chromate chemical conversion treatment agent that is a chemical conversion treatment agent that does not contain chromium (the chemical conversion treatment agent may be contained if it is chromium having an inevitable impurity level).

Hereinafter, the present invention will be described in detail with reference to examples. The present invention is not limited to the following examples.
<Example 1>
1. Preparation of test material Test material No 1-9, 14-22, 27-30
As a steel material, a 6 mm × 100 mm × 100 mm hot-rolled steel plate treated with a steel grid blast was used.

  The primer applied to the steel material surface was prepared by the following procedure.

  Commercially available liquid epoxy resin ("Basic liquid type 828" manufactured by Mitsubishi Chemical Corporation), purified montmorillonite as clay mineral ("Kunipia F" manufactured by Kunimine Kogyo Co., Ltd., having a hydroxyl group on the surface) or purification of smectite A predetermined amount of a product (“Smecton SA” manufactured by Kunimine Kogyo Co., Ltd., having a hydroxyl group on the surface) was added, stirred well, and uniformly dispersed.

  A predetermined amount of a commercially available epoxy silane coupling agent (“KBM-403” manufactured by Shin-Etsu Chemical Co., Ltd.) was mixed and stirred for 60 minutes.

  Subsequently, 20 parts by mass of a curing agent (“modified aliphatic amine grade T” manufactured by Mitsubishi Chemical Corporation) was mixed with 100 parts by mass of the epoxy resin to obtain a primer layer forming material. The primer layer forming material is spray-coated on the surface of the steel material so that the film thickness becomes 40 μm, the steel material is heated by induction heating, and the applied primer layer forming material is cured at a maximum heating temperature of 150 ° C., A primer layer was formed on the steel surface.

Then, on the steel plate on which the primer layer is formed, a sheet (0.5 mm thick) of a commercially available adhesive polyethylene resin (“Admer NE065” manufactured by Mitsui Chemicals, Inc.), polyethylene resin (Prime Polymer Co., Ltd.) ) “HI-ZEX5100E” sheet (thickness 2.5 mm) was melt-pressed (210 ° C., 5 minutes) with a hot press to prepare a polyethylene-coated steel material.
Test materials No10-13, 23-26, 31-33, 34-55
About test material No10-13, 23-26, 31-33, test material No1-9, 14-22 except having made the addition amount shown in Table 1 into the addition amount of a clay mineral and the addition amount of a silane coupling agent. , 27 to 30 were used to produce a polyethylene-coated steel material.

For test materials 34 to 55, test materials No 1 to 9, 14 to 22, and 27 to 27 except that talc and silica as fillers were added instead of artificially refined clay minerals (montmorillonite, smectite). A polyethylene-coated steel material was produced in the same manner as in No. 30.
Test material No56
As a reference example, a test agent produced using a chromate treatment solution was prepared. Using a chromate treatment solution (“Cosmer 100” manufactured by Kansai Paint Co., Ltd.) diluted to 1/5 with pure water, spray-applied to the steel surface so that the Cr equivalent adhesion amount is 300 mg / m ^2. The chromate layer was formed by heating and drying so that the ultimate temperature was 100 ° C.

  A primer layer forming material formed by mixing a commercially available liquid epoxy resin (“Basic Liquid Type 828” manufactured by Mitsubishi Chemical Corporation) with a curing agent (“Modified Aliphatic Amine Grade T” manufactured by Mitsubishi Chemical Corporation), Spray coating is applied to the surface of the steel material so that the film thickness is 40 μm, the steel material is heated by induction heating, and the applied primer layer forming material is cured at a maximum heating temperature of 150 ° C. Formed.

  Then, on the steel plate on which the primer layer is formed, a sheet (0.5 mm thick) of a commercially available adhesive polyethylene resin (“Admer NE065” manufactured by Mitsui Chemicals, Inc.), polyethylene resin (Prime Polymer Co., Ltd.) ) “HI-ZEX5100E” sheet (thickness 2.5 mm) was melt-pressed (210 ° C., 5 minutes) with a hot press to prepare a polyethylene-coated steel material.

The amount of Cr equivalent adhesion was prepared by preparing a dummy plate having a chromate layer formed by the same method as described above, peeling the chromate film of a predetermined area with 10% NaOH, and then measuring the Cr amount in the stripping solution by absorptiometry, Based on this, the Cr conversion adhesion amount per 1 m ² was calculated.

The cathode peel resistance of the polyethylene-coated steel material (test material) obtained as described above was evaluated. The measurement method and evaluation method are shown below.
2. Evaluation of Cathodic Peeling Resistance A circular artificial defect having a diameter of 6 mmφ was created at the center of the test material, and the steel material was exposed. An acrylic cylinder having a diameter of 70 mmφ centered on the artificial defect was placed vertically on the coating layer, fixed to the coating layer with a sealant, and the interior was filled with a 3 mass% NaCl aqueous solution to form a cell. Platinum was used for the counter electrode, and the electric potential of the steel material in the defective portion was held using a potentiostat at -1.5 V vs SCE. The test material was allowed to stand in a constant temperature bath at 60 ° C., and the potential was maintained for 28 days. Next, after collecting the test material, the cell was removed, and the periphery of the artificial defect was forcibly separated using a chisel and a cutter. Since the coating layer was peeled off from the steel material and the surface of the steel material was exposed at the periphery of the artificial defect, in order to investigate the peeling distance from the artificial defect portion, four directions (12 o'clock, 3 o'clock, 6 o'clock, 9 o'clock) The distance of the peeled portion from the edge of the artificial defect was measured in the time direction), and the average value was taken as the cathode peel distance. The smaller the cathode peeling distance, the better, and 20 mm or less was accepted. The results are shown in Tables 1 and 2.

As shown in Table 1 and Table 2, in the example of the present invention, the cathode peeling distance is reduced as compared with the comparative example. And it turns out that the outstanding performance more than a fixed level is ensured although it is equivalent to chromate treatment or inferior to chromate treatment.
<Example 2>
1. Preparation of test material The same test materials as those of the test materials No 1 to 9, 14 to 22, and 27 to 30 were prepared as test materials of the present invention.

As a comparative example, a coated steel material similar to that shown in Invention Example 1 of Patent Document 4 was produced. Steel grit blasting was performed as a base treatment on a hot rolled steel sheet having dimensions of 6 mm × 100 mm × 100 mm. Next, a polyurethane resin two-component curing type primer (“Permguard 331” manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) was applied to the surface of the hot-rolled steel sheet by 30 to 40 μm. The primer was cured for 24 hours at room temperature after painting. Next, a clay mineral dispersion was prepared. As the clay mineral, purified montmorillonite (“Kunipia F” manufactured by Kunimine Industry Co., Ltd.) was used. The purified montmorillonite was added to distilled water and stirred well to uniformly disperse the montmorillonite, thereby preparing a dispersion having a montmorillonite concentration of 1.0% by mass. 60 cm ³ of this dispersion was poured onto the steel plate coated with the primer from a stainless steel enclosure so that the dispersion did not flow out, poured from above, placed in an electric furnace together with the steel plate, and allowed to stand horizontally. This was slowly deposited at room temperature for 24 hours, and then water was forcibly evaporated at 50 ° C. for 24 hours to form a clay film layer having a thickness of 30 μm. Thereafter, the primer was coated on the clay film layer and cured for 24 hours. After that, 3.0 to 3.5 mm of polyurethane resin was applied as an anticorrosion resin layer. Here, the polyurethane resin is a commercially available product “Permaguard 137 (main agent: A black (Z), hardener: B, main agent: hardener ratio = 2.7: 1.0)”. Was used and cured at room temperature (20 ° C. or higher) for 7 days.
2. Evaluation of peel resistance The peel resistance of the coating was evaluated by the peel strength test of the coating described in JIS G3469 (2010) for the test material of the present invention and the comparative example prepared by the method of cited document 4. . A test piece having a length of 80 mm and a width of 10 mm was cut out from the center of the test material with a cutting machine. Next, one end of the coating was peeled up and pinched with a chuck of a tensile tester, and the load when the coating was peeled off at 20 ° C. at a speed of 50 mm / min was measured. All the test materials of the examples of the present invention had a load of 15 kg / 10 mm or more. However, when the test material of the comparative example cuts and processes a test piece of length 80 mm × width 10 mm from the center of the test material with a cutting machine, both when the cutting oil is used and when not used, The clay film layer was destroyed, and the upper coating (polyurethane resin layer having a thickness of 3 mm or more) of the clay film layer was peeled off, so that a test piece could not be prepared and a subsequent test could not be performed.

  From this, it can be seen that the coated steel material by the method of the cited document 4 has remarkably low peeling resistance of the coating layer compared to that according to the present invention. Moreover, the test material of this invention has the corrosion resistance superior to the test material manufactured by the method based on the cited reference 4 as a result of having coat | covered the primer layer firmly.

Claims (3)

On the steel material, at least an epoxy resin primer layer, an adhesive polyethylene resin layer, and a polyethylene resin layer in this order from the steel material side,
The epoxy resin primer layer is 50 to 100 parts by mass of clay mineral and 5 to 100 parts by mass of the silane coupling agent having an epoxy group with respect to 100 parts by mass of the epoxy resin and the curing agent. A polyethylene-coated steel material, which is a layer formed by curing a primer layer forming material containing ~ 40 parts by mass.   The polyethylene-coated steel material according to claim 1, wherein the clay mineral is a purified product of montmorillonite and / or a purified product of smectite. An epoxy resin primer layer forming material for forming an epoxy resin primer layer on a steel material,
For a total of 100 parts by mass of epoxy resin and curing agent,
Containing 50 to 100 parts by mass of clay mineral,
An epoxy resin primer layer forming material comprising 5 to 40 parts by mass of a silane coupling agent having an epoxy group with respect to 100 parts by mass of the clay mineral.