  The present invention relates to a resist composition, a resist pattern forming method, and a polymer compound.

In lithography technology, for example, a resist film made of a resist material is formed on a substrate, and the resist film is selectively exposed to light such as light or an electron beam through a mask on which a predetermined pattern is formed. And a development process is performed to form a resist pattern having a predetermined shape on the resist film.
A resist material in which the exposed portion changes to a property that dissolves in the developer is referred to as a positive type, and a resist material that changes to a property in which the exposed portion does not dissolve in the developer is referred to as a negative type.
In recent years, in the manufacture of semiconductor elements and liquid crystal display elements, pattern miniaturization has been rapidly progressing due to advances in lithography technology.
As a technique for miniaturization, the exposure light source is generally shortened in wavelength (increased energy). Specifically, conventionally, ultraviolet rays typified by g-line and i-line have been used, but at present, mass production of semiconductor elements using a KrF excimer laser or an ArF excimer laser has started. Further, studies have been made on electron beams having shorter wavelengths (higher energy) than these excimer lasers, EUV (extreme ultraviolet rays), X-rays, and the like.

Resist materials are required to have lithography characteristics such as sensitivity to these exposure light sources and resolution capable of reproducing a pattern with fine dimensions.
Conventionally, as a resist material satisfying such requirements, there is a chemically amplified resist composition containing a base material component whose solubility in a developing solution is changed by the action of an acid and an acid generator component that generates an acid upon exposure. It is used. For example, when the developer is an alkali developer (alkaline development process), the positive chemically amplified resist composition includes a resin component (base resin) whose solubility in an alkali developer is increased by the action of an acid, an acid Those containing a generator component are generally used. When a resist film formed using such a resist composition is selectively exposed at the time of resist pattern formation, an acid is generated from the acid generator component in the exposed portion, and the polarity of the base resin increases due to the action of the acid. Thus, the exposed portion becomes soluble in the alkaline developer. Therefore, by performing alkali development, a positive pattern in which an unexposed portion remains as a pattern is formed. On the other hand, when a solvent development process using a developer containing an organic solvent (organic developer) is applied, the solubility in the organic developer is relatively lowered when the polarity of the base resin is increased. The unexposed portion is dissolved and removed by the organic developer, and a negative resist pattern is formed in which the exposed portion remains as a pattern. Such a solvent development process for forming a negative resist pattern is sometimes referred to as a negative development process (for example, Patent Document 1).

  The base resin used in the chemically amplified resist composition generally has a plurality of structural units for improving lithography properties and the like. For example, in the case of a resin component whose solubility in an alkaline developer is increased by the action of an acid, a structural unit containing an acid-decomposable group that is decomposed by the action of an acid generated from an acid generator or the like to increase polarity is used However, other structural units including a lactone-containing cyclic group, structural units including a polar group such as a hydroxyl group, and the like are used (for example, see Patent Document 2).

JP 2009-025723 A JP 2003-241385 A

In the future, with further progress in lithography technology and further miniaturization of resist patterns, resist materials are desired to further improve various lithography properties such as line roughness and sensitivity.
However, when a conventional structural unit as described in Patent Document 2 is used, there is still room for improvement in lithography characteristics and pattern shapes.
This invention is made | formed in view of the said situation, Comprising: It aims at providing the resist composition excellent in the lithography characteristic, the resist pattern formation method, and a high molecular compound.

［式中、Ｒ ^１ ’は、水素原子又は炭素数１〜５のアルキル基である。］ A first aspect of the present invention is a resist composition that generates an acid upon exposure and changes its solubility in a developer due to the action of the acid, and is a base material component whose solubility in the developer changes due to the action of an acid (A), and the base material component (A) is analyzed by a high performance liquid chromatography (HPLC) method using a reverse phase column, and the retention time is longer than β- (methacryloyl) oxy-γ-butyrolactone. short is a structural unit derived from a monomer (a0), it has the structural unit (a2) containing a structural unit (a1) and the lactone-containing cyclic group containing an acid-decomposable group that exhibits increased polarity by the action of an acid, and, look-containing polymer compound softening point of 130 ° C. or more (A1), the monomer is a resist composition characterized by containing a compound represented by the following general formula (1 ').
The softening point of the polymer compound (A1) is measured by the following procedures (1) to (4).
Procedure (1) As a sample, a solution of 15% by mass of the polymer compound (A1) is prepared.
Procedure (2) A 500 nm-thick resin film is formed using the sample solution.
Procedure (3) Using a local thermal analyzer, the AFM probe is brought into contact with the surface of the resin film and allowed to stand to heat the AFM probe that is a thermal cantilever.
Procedure (4) When the temperature rise rate is 10 ° C. per second and the heating is continued, the temperature at which the probe moves from “sled” (thermal expansion of the film) to “deflection” (softening of the film) is the softening point. It is defined as

[Wherein, R ¹ ′ represents a hydrogen atom or an alkyl group having 1 to 5 carbon atoms. ]

  According to a second aspect of the present invention, a resist pattern is formed on a support using the resist composition of the first aspect, the resist film is exposed, and the resist film is developed to form a resist pattern. It is a resist pattern formation method including the process of forming.

  ADVANTAGE OF THE INVENTION According to this invention, the resist composition excellent in the lithography characteristic, the resist pattern formation method, and a high molecular compound can be provided.

It is a figure which shows the specific example of the softening point in this invention.

In the present specification and claims, “aliphatic” is a relative concept with respect to aromatics, and is defined to mean groups, compounds, etc. that do not have aromaticity.
Unless otherwise specified, the “alkyl group” includes linear, branched and cyclic monovalent saturated hydrocarbon groups.
The “alkylene group” includes linear, branched, and cyclic divalent saturated hydrocarbon groups unless otherwise specified. The same applies to the alkyl group in the alkoxy group.
The “halogenated alkyl group” is a group in which part or all of the hydrogen atoms of the alkyl group are substituted with a halogen atom, and examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
“Fluorinated alkyl group” or “fluorinated alkylene group” refers to a group in which part or all of the hydrogen atoms of an alkyl group or alkylene group are substituted with fluorine atoms.
“Structural unit” means a monomer unit (monomer unit) constituting a polymer compound (resin, polymer, copolymer).
“A structural unit derived from an acrylate ester” means a structural unit formed by cleavage of an ethylenic double bond of an acrylate ester.
“Acrylic acid ester” is a compound in which the hydrogen atom at the carboxy group terminal of acrylic acid (CH ₂ ═CH—COOH) is substituted with an organic group.
In the acrylate ester, the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent. The substituent (R ^α ) for substituting the hydrogen atom bonded to the α-position carbon atom is an atom or group other than a hydrogen atom, such as an alkyl group having 1 to 5 carbon atoms or a halogenated group having 1 to 5 carbon atoms. Examples thereof include an alkyl group and a hydroxyalkyl group. The α-position carbon atom of the acrylate ester is a carbon atom to which a carbonyl group is bonded unless otherwise specified.
Hereinafter, an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position is substituted with a substituent may be referred to as an α-substituted acrylate ester. Further, the acrylate ester and the α-substituted acrylate ester may be collectively referred to as “(α-substituted) acrylate ester”.
“A structural unit derived from hydroxystyrene or a hydroxystyrene derivative” means a structural unit formed by cleavage of an ethylenic double bond of hydroxystyrene or a hydroxystyrene derivative.
“Hydroxystyrene derivative” is a concept including those in which the hydrogen atom at the α-position of hydroxystyrene is substituted with another substituent such as an alkyl group or an alkyl halide group, and derivatives thereof. The derivatives include those in which the hydrogen atom at the α-position may be substituted with a substituent, the hydrogen atom of the hydroxyl group of hydroxystyrene substituted with an organic group, and the hydrogen atom at the α-position substituted with a substituent. Examples include those in which a substituent other than a hydroxyl group is bonded to a good benzene ring of hydroxystyrene. The α-position (α-position carbon atom) means a carbon atom to which a benzene ring is bonded unless otherwise specified.
Examples of the substituent for substituting the hydrogen atom at the α-position of hydroxystyrene include the same substituents as those mentioned as the substituent at the α-position in the α-substituted acrylic ester.
The “structural unit derived from vinyl benzoic acid or a vinyl benzoic acid derivative” means a structural unit configured by cleavage of an ethylenic double bond of vinyl benzoic acid or a vinyl benzoic acid derivative.
The “vinyl benzoic acid derivative” is a concept including a compound in which the hydrogen atom at the α-position of vinyl benzoic acid is substituted with another substituent such as an alkyl group or an alkyl halide group, and derivatives thereof. These derivatives include those obtained by substituting the hydrogen atom of the carboxy group of vinyl benzoic acid with an organic group, which may be substituted with a hydrogen atom at the α-position, and the hydrogen atom at the α-position with a substituent. Examples thereof include those in which a substituent other than a hydroxyl group and a carboxy group is bonded to the benzene ring of vinyl benzoic acid. The α-position (α-position carbon atom) means a carbon atom to which a benzene ring is bonded unless otherwise specified.
“Styrene” is a concept including styrene and those in which the α-position hydrogen atom of styrene is substituted with another substituent such as an alkyl group or a halogenated alkyl group.
“Structural unit derived from styrene” and “structural unit derived from styrene derivative” mean a structural unit formed by cleavage of an ethylenic double bond of styrene or a styrene derivative.
The alkyl group as a substituent at the α-position is preferably a linear or branched alkyl group, specifically, an alkyl group having 1 to 5 carbon atoms (methyl group, ethyl group, propyl group, isopropyl group). , N-butyl group, isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group) and the like.
Specific examples of the halogenated alkyl group as the substituent at the α-position include groups in which part or all of the hydrogen atoms of the above-mentioned “alkyl group as the substituent at the α-position” are substituted with a halogen atom. It is done. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
Specific examples of the hydroxyalkyl group as a substituent at the α-position include a group in which part or all of the hydrogen atoms of the “alkyl group as the substituent at the α-position” are substituted with a hydroxyl group. 1-5 are preferable and, as for the number of the hydroxyl groups in this hydroxyalkyl group, 1 is the most preferable.
When it is described as “may have a substituent”, when a hydrogen atom (—H) is substituted with a monovalent group, and when a methylene group (—CH ₂ —) is substituted with a divalent group Including both.
“Exposure” is a concept including general irradiation of radiation.

≪Resist composition≫
The resist composition of the present invention is a resist composition that generates an acid upon exposure and changes its solubility in a developer by the action of an acid, and is a base material component that changes its solubility in a developer by the action of an acid ( A), and the base material component (A) is shorter in retention time than β- (methacryloyl) oxy-γ-butyrolactone by high performance liquid chromatography (HPLC) analysis using a reverse phase column. A polymer compound (A1) having a structural unit (a0) derived from a monomer and a structural unit (a1) containing an acid-decomposable group whose polarity is increased by the action of an acid, and having a softening point of 130 ° C. or higher It is characterized by including.

The resist composition of the present invention is a resist composition that generates an acid upon exposure and changes its solubility in a developer by the action of an acid, and is a base material component that changes its solubility in a developer by the action of an acid ( A) (hereinafter also referred to as “component (A)”).
When a resist film is formed using such a resist composition and the resist film is selectively exposed, an acid is generated in the exposed portion, and the action of the acid causes the solubility of the component (A) in the developer. On the other hand, since the solubility of the component (A) in the developer does not change in the unexposed area, a difference in solubility in the developer occurs between the exposed and unexposed areas. Therefore, when the resist film is developed, when the resist composition is positive, the exposed portion is dissolved and removed to form a positive resist pattern, and when the resist composition is negative, the unexposed portion is dissolved. This is removed to form a negative resist pattern.
In this specification, a resist composition in which an exposed portion is dissolved and removed to form a positive resist pattern is referred to as a positive resist composition, and a resist composition that forms a negative resist pattern in which an unexposed portion is dissolved and removed. Is referred to as a negative resist composition.
The resist composition of the present invention may be a positive resist composition or a negative resist composition.
In addition, the resist composition of the present invention may be used for an alkali development process using an alkali developer for development processing at the time of forming a resist pattern, and a developer (organic developer) containing an organic solvent is used for the development processing. It may be for the solvent development process used.

The resist composition of the present invention has an acid generating ability to generate an acid upon exposure, and the component (A) may generate an acid upon exposure, and is an additive added separately from the component (A). The component may generate an acid upon exposure.
Specifically, the resist composition of the present invention comprises:
(1) It may contain an acid generator component (B) that generates an acid upon exposure (hereinafter referred to as “component (B)”);
(2) The component (A) may be a component that generates an acid upon exposure;
(3) The component (A) is a component that generates an acid upon exposure, and may further contain a component (B).
That is, in the case of the above (2) and (3), the component (A) is a “base material component that generates an acid upon exposure and changes its solubility in a developer due to the action of the acid”. When the component (A) is a base material component that generates an acid upon exposure and changes its solubility in a developer due to the action of the acid, the component (A1) described later generates an acid upon exposure, and A polymer compound whose solubility in a developing solution is changed by the action of an acid is preferable. As such a polymer compound, a resin having a structural unit that generates an acid upon exposure can be used. A well-known thing can be used as a structural unit which generate | occur | produces an acid by exposure.
The resist composition of the present invention is particularly preferably the case (1) above.

<(A) component>
In the present invention, the “base component” is an organic compound having a film forming ability, and preferably an organic compound having a molecular weight of 500 or more is used. When the molecular weight of the organic compound is 500 or more, the film forming ability is improved, and in addition, a nano-level resist pattern is easily formed.
Organic compounds used as the base material component are roughly classified into non-polymers and polymers.
As the non-polymer, those having a molecular weight of 500 or more and less than 4000 are usually used. Hereinafter, the “low molecular compound” refers to a non-polymer having a molecular weight of 500 or more and less than 4000.
As the polymer, those having a molecular weight of 1000 or more are usually used. Hereinafter, the term “resin” refers to a polymer having a molecular weight of 1000 or more.
As the molecular weight of the polymer, a polystyrene-reduced mass average molecular weight by GPC (gel permeation chromatography) is used.
As the component (A), a resin may be used, a low molecular compound may be used, or these may be used in combination.
Component (A) may have increased solubility in a developer due to the action of an acid, or may decrease solubility in a developer due to the action of an acid.
In the present invention, the component (A) may generate an acid upon exposure.

[Polymer Compound (A1)]
In the present invention, the component (A) is derived from a monomer having a retention time shorter than that of β- (methacryloyl) oxy-γ-butyrolactone, as determined by high performance liquid chromatography (HPLC) using a reversed phase column. It has a structural unit (a0) and a polymer compound (A1) having a structural unit (a1) containing an acid-decomposable group whose polarity is increased by the action of an acid and having a softening point of 130 ° C. or higher.

(Structural unit (a0))
The structural unit (a0) is a structural unit derived from a monomer having a retention time shorter than β- (methacryloyl) oxy-γ-butyrolactone in a high performance liquid chromatography (HPLC) analysis using a reverse phase column. is there.

  In the present invention, the structural unit (a0) is a target of two or more monomers by high performance liquid chromatography (HPLC) using a reverse phase column. Comparison can be made by retention time when analyzed under the same conditions. In the present invention, it is a structural unit derived from a monomer having a retention time shorter than that of β- (methacryloyl) oxy-γ-butyrolactone in the measurement by the HPLC method.

The apparatus and conditions used for the HPLC method are general apparatuses and conditions used for the analysis of the compound, and are not particularly limited as long as the target monomer can be analyzed. Specifically, it can be measured under the following conditions.
Eluent (developing solvent): acetonitrile / buffer solution (using a gradient analysis method, 10/90 (volume ratio) until 0.5 minutes from the start, and then changing the volume ratio linearly with time, and then starting 20 90/10 (volume ratio) per minute.)
Buffer solution: 0.1 mass% trifluoroacetic acid aqueous solution.
Apparatus: Dionex U3000 (manufactured by Dionex).
Column: Superiorex ODS (manufactured by Shiseido); column length 25 cm.
Detector: UV detector (manufactured by Dionex).
Flow rate: 2 mL / min.
Column temperature: 30 ° C.
Sample concentration: acetonitrile solution having a solid content of 0.1% by mass.
Injection volume: 5 μL.
The sample concentration indicates the solid content concentration of the compound in which the monomer has various target structures.

  The monomer is a structural unit derived from a monomer having a retention time measured under specific conditions of the HPLC method shorter than that of β- (methacryloyl) oxy-γ-butyrolactone, and the retention time under the conditions is What is 8 minutes or less is preferable. The shorter the holding time, the higher the polarity and the better the effect of the present invention. The lower limit is not particularly limited, but is more preferably 2 minutes or longer.

  The structural unit (a0) of the present invention is a structural unit derived from a monomer having a retention time shorter than β- (methacryloyl) oxy-γ-butyrolactone, and is a compound represented by the following general formula (1) or It is preferable to contain the compound represented by Formula (2).

［前記Ｒ^１は炭素数１〜５のアルキル基である。］

[R ¹ is an alkyl group having 1 to 5 carbon atoms. ]

  The proportion of the structural unit (a0) in the component (A1) is preferably 1 to 70 mol%, more preferably 3 to 65 mol%, and more preferably 5 to 60 mol% with respect to all the structural units constituting the component (A1). Is more preferable. By setting the lower limit value or more, lithography properties such as sensitivity, resolution, and LWR are also improved. Moreover, the balance with another structural unit can be taken by making it below an upper limit.

  In addition to the structural unit (a0), the component (A1) has a structural unit (a1) containing an acid-decomposable group whose polarity is increased by the action of an acid. Note that the structural unit (a1) does not correspond to the structural unit (a0).

(Structural unit (a1))
The structural unit (a1) is a structural unit containing an acid-decomposable group whose polarity is increased by the action of an acid.
The “acid-decomposable group” is an acid-decomposable group that can cleave at least part of bonds in the structure of the acid-decomposable group by the action of an acid.
Examples of the acid-decomposable group whose polarity increases by the action of an acid include a group that decomposes by the action of an acid to generate a polar group.
Examples of the polar group include a carboxy group, a hydroxyl group, an amino group, a sulfo group (—SO ₃ H), and the like. Among these, a polar group containing —OH in the structure (hereinafter sometimes referred to as “OH-containing polar group”) is preferable, a carboxy group or a hydroxyl group is preferable, and a carboxy group is particularly preferable.
More specifically, examples of the acid-decomposable group include groups in which the polar group is protected with an acid-dissociable group (for example, a group in which a hydrogen atom of an OH-containing polar group is protected with an acid-dissociable group).
Here, “acid-dissociable group” means
(I) an acid-dissociable group capable of cleaving a bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group by the action of an acid, or
(Ii) a group capable of cleaving a bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group by further decarboxylation reaction after partial bond cleavage by the action of an acid ,
Both.
The acid-dissociable group constituting the acid-decomposable group must be a group having a lower polarity than the polar group generated by dissociation of the acid-dissociable group. Is dissociated, a polar group having a polarity higher than that of the acid dissociable group is generated to increase the polarity. As a result, the polarity of the entire component (A1) increases. As the polarity increases, the solubility in the developer changes relatively. When the developer is an alkaline developer, the solubility increases. When the developer is an organic developer, the solubility increases. Decrease.

  The acid-dissociable group is not particularly limited, and those that have been proposed as acid-dissociable groups for base resins for chemically amplified resists can be used.

  Examples of the acid dissociable group that protects a carboxy group or a hydroxyl group among the polar groups include, for example, an acid dissociable group represented by the following general formula (a1-r-1) (hereinafter referred to as “acetal acid dissociable group”). May be included).

［式中、Ｒａ’^１、Ｒａ’^２は水素原子またはアルキル基であり、Ｒａ’^３は炭化水素基であって、Ｒａ’^３は、Ｒａ’^１、Ｒａ’^２のいずれかと結合して環を形成してもよい。］

[Wherein, Ra ′ ¹ and Ra ′ ² are a hydrogen atom or an alkyl group, Ra ′ ³ is a hydrocarbon group, and Ra ′ ³ is bonded to either Ra ′ ¹ or Ra ′ ² to form a ring. May be formed. ]

In formula (a1-r-1), at least one of Ra ′ ¹ and Ra ′ ² is preferably a hydrogen atom, and more preferably both are hydrogen atoms.
In the case where Ra ′ ¹ or Ra ′ ² is an alkyl group, the alkyl group is the alkyl group mentioned as the substituent that may be bonded to the α-position carbon atom in the description of the α-substituted acrylate ester. The same thing is mentioned, A C1-C5 alkyl group is preferable. Specifically, linear or branched alkyl groups such as methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, tert-butyl, pentyl, isopentyl, and neopentyl And a methyl group or an ethyl group is preferable, and a methyl group is particularly preferable.

In formula (a1-r-1), examples of the hydrocarbon group for Ra ′ ³ include linear, branched, or cyclic alkyl groups. The linear alkyl group preferably has 1 to 5 carbon atoms, more preferably 1 to 4, and still more preferably 1 or 2. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group, and an n-pentyl group. Among these, a methyl group, an ethyl group, or an n-butyl group is preferable, and a methyl group or an ethyl group is more preferable.
The branched alkyl group preferably has 3 to 10 carbon atoms, and more preferably 3 to 5 carbon atoms. Specific examples include isopropyl group, isobutyl group, tert-butyl group, isopentyl group, neopentyl group and the like, and isopropyl group is most preferable.
The cyclic alkyl group preferably has 3 to 20 carbon atoms, and more preferably 4 to 12 carbon atoms. Specific examples thereof include monocycloalkanes such as cyclopentane and cyclohexane, and groups obtained by removing one or more hydrogen atoms from polycycloalkanes such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. A part of carbon atoms constituting the ring of the cyclic alkyl group may be substituted with an etheric oxygen atom (—O—).

When Ra ′ ³ is bonded to either Ra ′ ¹ or Ra ′ ² to form a ring, the cyclic group is preferably a 4- to 7-membered ring, and more preferably a 4- to 6-membered ring. Specific examples of the cyclic group include a tetrahydropyranyl group and a tetrahydrofuranyl group.

  Among the polar groups, examples of the acid dissociable group that protects the carboxy group include an acid dissociable group represented by the following general formula (a1-r-2) (the following formula (a1-r-2) Among the acid dissociable groups represented by), those composed of an alkyl group may hereinafter be referred to as “tertiary alkyl ester type acid dissociable groups” for convenience).

［式中、Ｒａ’^４〜Ｒａ’^６はそれぞれ炭化水素基であって、Ｒａ’^５、Ｒａ’^６は互いに結合して環を形成してもよい。］

[Wherein, Ra ′ ^{4 to} Ra ′ ⁶ are each a hydrocarbon group, and Ra ′ ⁵ and Ra ′ ⁶ may be bonded to each other to form a ring. ]

As the hydrocarbon group for Ra ′ ^{4 to} Ra ′ ^6, the same groups as those described above for Ra ′ ³ can be mentioned.
Ra ′ ⁴ is preferably an alkyl group having 1 to 5 carbon atoms. In the case where Ra ′ ⁵ and Ra ′ ⁶ are bonded to each other to form a ring, a group represented by the following general formula (a1-r2-1) is exemplified. On the other hand, when Ra ′ ^{4 to} Ra ′ ⁶ are not bonded to each other and are independent hydrocarbon groups, groups represented by the following general formula (a1-r2-2) are exemplified.

［式中、Ｒａ’^１０は炭素数１〜１０のアルキル基、Ｒａ’^１１はＲａ’^１０が結合した炭素原子と共に脂肪族環式基を形成する基、Ｒａ’^１２〜Ｒａ’^１４は、それぞれ独立に炭化水素基を示す。］

[Wherein, Ra ′ ¹⁰ is an alkyl group having 1 to ¹⁰ carbon atoms, Ra ′ ¹¹ is a group that forms an aliphatic cyclic group together with a carbon atom to which Ra ′ ¹⁰ is bonded, and Ra ′ ^{12 to} Ra ′ ¹⁴ are Independently represents a hydrocarbon group. ]

In formula (a1-r2-1), the alkyl group of the alkyl group having 1 to ¹⁰ carbon atoms of Ra ′ ¹⁰ is a linear or branched alkyl group of Ra ′ ³ in formula (a1-r-1) The groups mentioned as are preferred. Wherein (a1-r2-1), Ra 'aliphatic cyclic ^{group 11} is configured, Ra in formula (a1-r-1)' group listed as a cyclic alkyl group of ³ is preferred.

In formula (a1-r2-2), Ra ′ ¹² and Ra ′ ¹⁴ are preferably each independently an alkyl group having 1 to 10 carbon atoms, and the alkyl group is represented by Ra in formula (a1-r-1). 'The group mentioned as a linear or branched alkyl group of ³ is more preferable, It is more preferable that it is a C1-C5 linear alkyl group, It is especially preferable that it is a methyl group or an ethyl group .
In formula (a1-r2-2), Ra ′ ¹³ is a linear, branched or cyclic alkyl group exemplified as the hydrocarbon group for Ra ′ ³ in formula (a1-r-1). Is preferred. Among these, a group exemplified as the cyclic alkyl group for Ra ′ ³ is more preferable.

Specific examples of the formula (a1-r2-1) are given below. “*” Indicates a bond.

  Specific examples of the formula (a1-r2-2) are given below.

  Examples of the acid dissociable group for protecting the hydroxyl group among the polar groups include, for example, an acid dissociable group represented by the following general formula (a1-r-3) (hereinafter referred to as “tertiary alkyloxycarbonyl acid for convenience”). Sometimes referred to as a “dissociable group”).

［式中、Ｒａ’^７〜Ｒａ’^９はそれぞれアルキル基である。］

[Wherein, Ra ′ ^{7 to} Ra ′ ⁹ each represents an alkyl group. ]

In the formula (a1-r-3), the Ra ′ ^{7 to} Ra ′ ⁹ groups are preferably alkyl groups having 1 to 5 carbon atoms, and more preferably 1 to 3 groups.
Moreover, it is preferable that the total carbon number of each alkyl group is 3-7, it is more preferable that it is 3-5, and it is most preferable that it is 3-4.

  The structural unit (a1) is a structural unit derived from an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position may be substituted with a substituent, and an acid whose polarity is increased by the action of an acid. A structural unit containing a decomposable group; a structural unit in which at least a part of hydrogen atoms in the hydroxyl group of a structural unit derived from hydroxystyrene or a hydroxystyrene derivative is protected by a substituent containing the acid-decomposable group; vinylbenzoic acid or Examples include a structural unit in which at least a part of hydrogen atoms in —C (═O) —OH of a structural unit derived from a vinylbenzoic acid derivative is protected by a substituent containing the acid-decomposable group.

Among the above, the structural unit (a1) is preferably a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent.
Preferable specific examples of the structural unit (a1) include the following general formulas (a1-1) and (a1-2).

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基である。Ｖａ^１はエーテル結合、ウレタン結合、又はアミド結合を有していてもよい２価の炭化水素基であり、ｎ_ａ１はそれぞれ独立に０〜２であり、Ｒａ^１は上記式（ａ１−ｒ−１）〜（ａ１−ｒ−２）で表される酸解離性基である。Ｗａ^１はｎ_ａ２＋１価の炭化水素基であり、ｎ_ａ２は１〜３であり、Ｒａ^２は上記式（ａ１−ｒ−１）または（ａ１−ｒ−３）で表される酸解離性基である。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms. Va ¹ is a divalent hydrocarbon group which may have an ether bond, a urethane bond, or an amide bond, n _a1 is independently 0 to 2, and Ra ¹ is the above formula (a1-r— 1) It is an acid dissociable group represented by (a1-r-2). Wa ¹ is a n _a2 +1 valent hydrocarbon group, n _a2 is 1 to 3, and Ra ² is an acid dissociation property represented by the above formula (a1-r-1) or (a1-r-3) It is a group. ]

In the formula (a1-1), the alkyl group having 1 to 5 carbon atoms is preferably linear or branched, and specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, or an n-butyl group. , Isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group and the like. The halogenated alkyl group having 1 to 5 carbon atoms is a group in which part or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms are substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a fluorinated alkyl group having 1 to 5 carbon atoms, and is most preferably a hydrogen atom or a methyl group in terms of industrial availability.
The divalent hydrocarbon group for Va ¹ may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group. An aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity. The aliphatic hydrocarbon group as a divalent hydrocarbon group in Va ¹ may be saturated or unsaturated, and is usually preferably saturated.
More specifically, examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group or an aliphatic hydrocarbon group containing a ring in the structure.
Examples of Va ¹ include those in which the divalent hydrocarbon group is bonded through an ether bond, a urethane bond, or an amide bond.

The linear or branched aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6, more preferably 1 to 4, and most preferably 1 to 3.
As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specifically, a methylene group [—CH ₂ —], an ethylene group [— (CH ₂ ) ₂ —], a trimethylene group [ — (CH ₂ ) ₃ —], tetramethylene group [— (CH ₂ ) ₄ —], pentamethylene group [— (CH ₂ ) ₅ —] and the like can be mentioned.
As the branched aliphatic hydrocarbon group, a branched alkylene group is preferred, and specifically, —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as - _{CH (CH 3) CH 2 -} , - CH (CH 3) CH (CH 3) -, - C (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - C (CH 2 CH _{3) 2} -CH ₂ - alkyl groups such _{as; -CH (CH 3) CH 2} CH 2 -, - CH 2 CH (CH 3) CH 2 - alkyl trimethylene groups such as; -CH _(CH 3) _{CH 2 CH 2 CH 2 -,} - CH 2 CH (CH 3) CH 2 CH 2 - And the like alkyl alkylene group such as an alkyl tetramethylene group of. The alkyl group in the alkyl alkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

Examples of the aliphatic hydrocarbon group containing a ring in the structure include an alicyclic hydrocarbon group (a group obtained by removing two hydrogen atoms from an aliphatic hydrocarbon ring), and an alicyclic hydrocarbon group that is linear or branched. Examples thereof include a group bonded to the end of a chain aliphatic hydrocarbon group and a group in which an alicyclic hydrocarbon group is interposed in the middle of a linear or branched aliphatic hydrocarbon group. Examples of the linear or branched aliphatic hydrocarbon group include those described above.
The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The alicyclic hydrocarbon group may be polycyclic or monocyclic. The monocyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a polycycloalkane, and the polycycloalkane is preferably one having 7 to 12 carbon atoms, specifically adamantane. , Norbornane, isobornane, tricyclodecane, tetracyclododecane and the like.

The aromatic hydrocarbon group is a hydrocarbon group having an aromatic ring.
The aromatic hydrocarbon group as the divalent hydrocarbon group in Va ¹ preferably has 3 to 30 carbon atoms, more preferably 5 to 30 carbon atoms, still more preferably 5 to 20 carbon atoms, and 6 to 6 carbon atoms. 15 is particularly preferable, and 6 to 10 is most preferable. However, the carbon number does not include the carbon number in the substituent.
Specific examples of the aromatic ring possessed by the aromatic hydrocarbon group include aromatic hydrocarbon rings such as benzene, biphenyl, fluorene, naphthalene, anthracene, and phenanthrene; some of the carbon atoms constituting the aromatic hydrocarbon ring are heterogeneous. Aromatic heterocycles substituted with atoms; and the like. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom.
Specifically, the aromatic hydrocarbon group is a group obtained by removing two hydrogen atoms from the aromatic hydrocarbon ring (arylene group); a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring (aryl group) A group in which one of the hydrogen atoms is substituted with an alkylene group (for example, arylalkyl groups such as benzyl, phenethyl, 1-naphthylmethyl, 2-naphthylmethyl, 1-naphthylethyl, 2-naphthylethyl, etc.) And a group obtained by removing two hydrogen atoms from an aromatic compound (eg, biphenyl, fluorene, etc.) containing two or more aromatic rings. The alkylene group (alkyl chain in the arylalkyl group) preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

In the formula (a1-2), the n _a2 +1 valent hydrocarbon group in Wa ¹ may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group. The aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity, may be saturated or unsaturated, and is usually preferably saturated. Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group including a ring in the structure, or a linear or branched aliphatic hydrocarbon group. It includes a group formed by combining an aliphatic hydrocarbon group in the structure containing a ring, and specific examples thereof include the same groups as Va ¹ of the aforementioned formula (a1-1).
The n _a2 +1 valence is preferably 2 to 4, and more preferably 2 or 3.

  As the formula (a1-2), a structural unit represented by general formula (a1-2-01) shown below is particularly desirable.

In formula (a1-2-01), Ra ² is an acid dissociable group represented by the above formula (a1-r-1) or (a1-r-3). n _a2 is an integer of 1 to 3, preferably 1 or 2, and more preferably 1. c is an integer of 0 to 3, preferably 0 or 1, and more preferably 1. R is the same as described above.

Specific examples of the formula (a1-1) are shown below. In the following formula, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

  Specific examples of the formula (a1-2) are shown below.

  The proportion of the structural unit (a1) in the component (A1) may be 100 mol%, preferably 20 to 80 mol%, preferably 20 to 75 mol%, based on all structural units constituting the component (A1). Is more preferable, and 25-70 mol% is further more preferable. By setting the lower limit value or more, lithography properties such as sensitivity, resolution, and LWR are also improved. Moreover, the balance with another structural unit can be taken by making it below an upper limit.

(Other structural units)
In addition to the structural unit (a0) and the structural unit (a1), the component (A1) may further include another structural unit that does not correspond to the structural unit (a0) and the structural unit (a1). The other structural unit is not particularly limited as long as it is a structural unit not classified into the structural units described above. Resin resins for ArF excimer laser, KrF excimer laser (preferably for ArF excimer laser), etc. A number of hitherto known compounds can be used, and examples include the structural units (a2) to (a4) shown below.

(Structural unit (a2))
The structural unit (a2) is a structural unit including a lactone-containing cyclic group, an —SO ₂ -containing cyclic group, or a carbonate-containing cyclic group.
The lactone-containing cyclic group, -SO ₂ -containing cyclic group or carbonate-containing cyclic group of the structural unit (a2) is transferred to the resist film substrate when the component (A1-1) is used for forming a resist film. It is effective in improving the adhesion of the material.
In addition, when the structural unit (a1) includes a lactone-containing cyclic group, an —SO ₂ -containing cyclic group, or a carbonate-containing cyclic group in the structure, the structural unit is also included in the structural unit (a2). Although applicable, such a structural unit corresponds to the structural unit (a1) and does not correspond to the structural unit (a2).

The “lactone-containing cyclic group” refers to a cyclic group containing a ring (lactone ring) containing —O—C (═O) — in the ring skeleton. The lactone ring is counted as the first ring. When only the lactone ring is present, it is called a monocyclic group, and when it has another ring structure, it is called a polycyclic group regardless of the structure. The lactone-containing cyclic group may be a monocyclic group or a polycyclic group.
The lactone-containing cyclic group in the structural unit (a2) is not particularly limited, and any lactone-containing cyclic group can be used. Specific examples include groups represented by general formulas (a2-r-1) to (a2-r-7) shown below.

［式中、Ｒａ’^２１はそれぞれ独立に水素原子、アルキル基、アルコキシ基、ハロゲン原子、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基またはシアノ基であり；Ｒ”は水素原子またはアルキル基であり；Ａ”は酸素原子（−Ｏ−）もしくは硫黄原子（−Ｓ−）を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子であり、ｎ’は０〜２の整数であり、ｍ’は０または１である。］

[Wherein, Ra ′ ²¹ each independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group or a cyano group. Yes; R ″ is a hydrogen atom or an alkyl group; A ″ is an alkylene group having 1 to 5 carbon atoms, oxygen atom or sulfur which may contain an oxygen atom (—O—) or a sulfur atom (—S—). An atom, n ′ is an integer of 0 to 2, and m ′ is 0 or 1. ]

In the general formulas (a2-r-2), (a2-r-3), and (a2-r-5), A ″ is the same as A ″ in the general formula (a0-r-1). .
In the general formulas (a2-r-1) to (a2-r-7), Ra ′ ²¹ is the same as Ra ′ ⁰¹ in the general formula (a0-r-1).
R ″ in —COOR ″ and —OC (═O) R ″ in Ra ′ ²¹ is the same as R ″ in —COOR ″ and —OC (═O) R ″ in Ra ′ ⁰¹ .
Specific examples of groups represented by general formulas (a2-r-1) to (a2-r-7) are given below.

The “—SO ₂ -containing cyclic group” refers to a cyclic group containing a ring containing —SO ₂ — in the ring skeleton, specifically, the sulfur atom (S) in —SO ₂ — is It is a cyclic group that forms part of the ring skeleton of the cyclic group. The ring containing —SO ₂ — in the ring skeleton is counted as the first ring, and when it is only the ring, it is a monocyclic group, and when it has another ring structure, it is a polycyclic group regardless of the structure. Called. The —SO ₂ — containing cyclic group may be a monocyclic group or a polycyclic group.
-SO ₂ - containing cyclic group, in particular, -O-SO ₂ - within the ring skeleton cyclic group containing, i.e. -O-SO ₂ - -O-S- medium is a part of the ring skeleton A cyclic group containing a sultone ring to be formed is preferable.
More specifically, examples of the —SO ₂ -containing cyclic group include groups represented by general formulas (a5-r-1) to (a5-r-4) shown below.

［式中、Ｒａ’^５１はそれぞれ独立に水素原子、アルキル基、アルコキシ基、ハロゲン原子、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基またはシアノ基であり；Ｒ”は水素原子またはアルキル基であり；Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子であり、ｎ’は０〜２の整数である。］

[Wherein, Ra ′ ⁵¹ independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group or a cyano group. Yes; R ″ is a hydrogen atom or an alkyl group; A ″ is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom or a sulfur atom, and n ′ is 0 to 2 Is an integer. ]

In the general formulas (a5-r-1) to (a5-r-4), A ″ is the same as A ″ in the general formula (a0-r-1).
The alkyl group, alkoxy group, halogen atom, halogenated alkyl group, —COOR ″, —OC (═O) R ″, and hydroxyalkyl group in Ra ′ ⁵¹ are each represented by the general formula (a0-r-1). It includes the same ones as exemplified in the description about the ra ^'01.
Specific examples of groups represented by general formulas (a5-r-1) to (a5-r-4) are given below. “Ac” in the formula represents an acetyl group.

The “carbonate-containing cyclic group” refers to a cyclic group containing a ring (carbonate ring) containing —O—C (═O) —O— in the ring skeleton. When the carbonate ring is counted as the first ring, the carbonate ring alone is called a monocyclic group, and when it has another ring structure, it is called a polycyclic group regardless of the structure. The carbonate-containing cyclic group may be a monocyclic group or a polycyclic group.
Any carbonate ring-containing cyclic group can be used without any particular limitation. Specific examples include groups represented by the following general formulas (ax3-r-1) to (ax3-r-3).

［式中、Ｒａ’^ｘ３１はそれぞれ独立に水素原子、アルキル基、アルコキシ基、ハロゲン原子、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基またはシアノ基であり；Ｒ”は水素原子またはアルキル基であり；Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子でありｑ’は０または１である。］

[ ^Wherein , Ra ′ ^x31 each independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group or a cyano group. Yes; R ″ is a hydrogen atom or an alkyl group; A ″ is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom or a sulfur atom, and q ′ is 0 or 1. is there. ]

In the general formulas (ax3-r-1) to (ax3-r-3), A ″ is the same as A ″ in the general formula (a0-r-1).
As the alkyl group, alkoxy group, halogen atom, halogenated alkyl group, —COOR ″, —OC (═O) R ″, and hydroxyalkyl group in Ra ′ ³¹ , respectively, in the general formula (a0-r-1), It includes the same ones as exemplified in the description about the ra ^'01.
Specific examples of groups represented by general formulas (ax3-r-1) to (ax3-r-3) are given below.

  The structural unit (a2) is preferably a structural unit represented by the following general formula (a2-1).

［式中、Ｒは水素原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基である。Ｙａ^２１は単結合または２価の連結基である。Ｌａ^２１は−Ｏ−、−ＣＯＯ−、−ＣＯＮ（Ｒ’）−又は−ＯＣＯ−、−ＣＯＮＨＣＯ−又は−ＣＯＮＨＣＳ−であり、Ｒ’は水素原子またはメチル基を示す。ただしＬａ^２１が−Ｏ−の場合、Ｙａ^２１は−ＣＯ−にはならない。Ｒａ^２１はラクトン含有環式基、カーボネート含有環式基、又は−ＳＯ_２−含有環式基である。］

[In formula, R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group. Ya ²¹ is a single bond or a divalent linking group. La ²¹ represents —O—, —COO—, —CON (R ′) — or —OCO—, —CONHCO— or —CONHCS—, and R ′ represents a hydrogen atom or a methyl group. However, when La ²¹ is —O—, Ya ²¹ is not —CO—. Ra ²¹ is a lactone-containing cyclic group, a carbonate-containing cyclic group, or an —SO ₂ -containing cyclic group. ]

In formula (a2-1), R is the same as described above.
The divalent linking group of Ya ²¹ is not particularly limited, and preferred examples thereof include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom.
The divalent hydrocarbon group which may have a substituent in Ya ^{21 and} the divalent linking group containing a hetero atom are the same as the divalent linking group of Ya ⁰¹ in the formula (a0-1). This is the same as the divalent hydrocarbon group which may have a substituent and the divalent linking group containing a hetero atom, which are exemplified in the description.

In the formula (a2-1), Ra ²¹ is a lactone-containing cyclic group, an —SO ₂ -containing cyclic group, or a carbonate-containing cyclic group.
The lactone-containing cyclic group, -SO ₂ -containing cyclic group, and carbonate-containing cyclic group in Ra ²¹ are each represented by the general formulas (a2-r-1) to (a2-r-7) described above. Groups represented by general formulas (a5-r-1) to (a5-r-4), groups represented by general formulas (ax3-r-1) to (ax3-r-3), respectively. Are preferable.
Among these, a lactone-containing cyclic group or an —SO ₂ -containing cyclic group is preferable, and each is represented by the general formula (a2-r-1), (a2-r-2), or (a5-r-1). Group is preferred, and the chemical formulas (r-lc-1-1) to (r-lc-1-7), (r-lc-2-1) to (r-lc-2-13), (r-sl -1-1) and any group represented by (r-sl-1-18), respectively, is more preferable.

The structural unit (a2) contained in the component (A1-1) may be one type or two or more types.
When the component (A1-1) has the structural unit (a2), the proportion of the structural unit (a2) is 1 to 80 mol% with respect to the total of all the structural units constituting the component (A1-1). It is preferably 10 to 70 mol%, more preferably 10 to 65 mol%, and particularly preferably 10 to 60 mol%. By setting it to the lower limit value or more, the effect of containing the structural unit (a2) can be sufficiently obtained, and by setting it to the upper limit value or less, balance with other structural units can be achieved. The lithography characteristics and pattern shape of the film are improved.

Structural unit (a3):
The structural unit (a3) is a structural unit containing a polar group-containing aliphatic hydrocarbon group (except for those corresponding to the structural units (a1) and (a2) described above).
It is considered that when the component (A1) has the structural unit (a3), the hydrophilicity of the component (A-1) is increased and the resolution is improved.

Examples of the polar group include a hydroxyl group, a cyano group, a carboxy group, and a hydroxyalkyl group in which a part of hydrogen atoms of an alkyl group is substituted with a fluorine atom. A hydroxyl group is particularly preferable.
Examples of the aliphatic hydrocarbon group include a linear or branched hydrocarbon group having 1 to 10 carbon atoms (preferably an alkylene group) and a cyclic aliphatic hydrocarbon group (cyclic group). The cyclic group may be a monocyclic group or a polycyclic group. For example, a resin for a resist composition for an ArF excimer laser can be appropriately selected from those proposed. The cyclic group is preferably a polycyclic group, and more preferably 7 to 30 carbon atoms.
Among them, a structural unit derived from an acrylate ester containing an aliphatic polycyclic group containing a hydroxyalkyl group in which a part of hydrogen atoms of a hydroxyl group, a cyano group, a carboxy group, or an alkyl group is substituted with a fluorine atom Is more preferable. Examples of the polycyclic group include groups in which two or more hydrogen atoms have been removed from bicycloalkane, tricycloalkane, tetracycloalkane and the like. Specific examples include groups in which two or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among these polycyclic groups, there are groups in which two or more hydrogen atoms have been removed from adamantane, groups in which two or more hydrogen atoms have been removed from norbornane, and groups in which two or more hydrogen atoms have been removed from tetracyclododecane. Industrially preferable.

The structural unit (a3) is not particularly limited as long as it contains a polar group-containing aliphatic hydrocarbon group, and any structural unit can be used.
The structural unit (a3) is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent, and includes a polar group-containing aliphatic hydrocarbon group A structural unit is preferred.
The structural unit (a3) is derived from a hydroxyethyl ester of acrylic acid when the hydrocarbon group in the polar group-containing aliphatic hydrocarbon group is a linear or branched hydrocarbon group having 1 to 10 carbon atoms. When the hydrocarbon group is a polycyclic group, the structural unit represented by the following formula (a3-1), the structural unit represented by the formula (a3-2), the formula ( The structural unit represented by a3-3) is preferred.

［式中、Ｒは前記と同じであり、ｊは１〜３の整数であり、ｋは１〜３の整数であり、ｔ’は１〜３の整数であり、ｌは１〜５の整数であり、ｓは１〜３の整数である。］

[Wherein, R is the same as above, j is an integer of 1 to 3, k is an integer of 1 to 3, t ′ is an integer of 1 to 3, and l is an integer of 1 to 5] And s is an integer of 1 to 3. ]

In formula (a3-1), j is preferably 1 or 2, and more preferably 1. When j is 2, it is preferable that the hydroxyl group is bonded to the 3rd and 5th positions of the adamantyl group. When j is 1, it is preferable that the hydroxyl group is bonded to the 3-position of the adamantyl group.
j is preferably 1, and a hydroxyl group bonded to the 3-position of the adamantyl group is particularly preferred.

  In formula (a3-2), k is preferably 1. The cyano group is preferably bonded to the 5th or 6th position of the norbornyl group.

  In formula (a3-3), t ′ is preferably 1. l is preferably 1. s is preferably 1. In these, a 2-norbornyl group or a 3-norbornyl group is preferably bonded to the terminal of the carboxy group of acrylic acid. The fluorinated alkyl alcohol is preferably bonded to the 5th or 6th position of the norbornyl group.

The structural unit (a3) contained in the component (A1) may be one type or two or more types.
When the component (A1) has the structural unit (a3), it is preferably 5 to 50 mol%, more preferably 5 to 40 mol%, based on the total of all structural units constituting the component (A1). 5-25 mol% is more preferable. By setting the proportion of the structural unit (a3) to the lower limit value or more, the effect of including the structural unit (a3) can be sufficiently obtained, and by setting the proportion of the structural unit (a3) to the upper limit value or less, balance with other structural units can be obtained. It becomes easy.

Structural unit (a4):
The structural unit (a4) is a structural unit containing an acid non-dissociable aliphatic cyclic group.
When the component (A1) has the structural unit (a4), the dry etching resistance of the formed resist pattern is improved. Moreover, the hydrophobicity of (A-1) component increases. The improvement in hydrophobicity is thought to contribute to the improvement of resolution, resist pattern shape, etc., particularly in the case of organic solvent development.
The “acid non-dissociable cyclic group” in the structural unit (a4) is generated when an acid is generated in the resist composition by exposure (for example, when an acid is generated from the component (A1) or the component (B) described later). In addition, the cyclic group remains in the structural unit as it is without dissociating even when the acid acts.
As the structural unit (a4), for example, a structural unit derived from an acrylate ester containing a non-acid-dissociable aliphatic cyclic group is preferable. Examples of the cyclic group include those similar to those exemplified for the structural unit (a1), such as for ArF excimer laser, for KrF excimer laser (preferably for ArF excimer laser), etc. A number of hitherto known materials can be used as the resin component of the resist composition.
In particular, at least one selected from a tricyclodecyl group, an adamantyl group, a tetracyclododecyl group, an isobornyl group, and a norbornyl group is preferable in terms of industrial availability. These polycyclic groups may have a linear or branched alkyl group having 1 to 5 carbon atoms as a substituent.
Specific examples of the structural unit (a4) include structural units represented by general formulas (a4-1) to (a4-7) shown below.

［式中、Ｒ^αは前記と同じである。］

[Wherein, R ^α is the same as defined above. ]

The structural unit (a4) contained in the component (A1) may be one type or two or more types.
When the component (A1) has the structural unit (a4), the proportion of the structural unit (a4) is preferably 1 to 30 mol% with respect to the total of all the structural units constituting the component (A1). 3-20 mol% is more preferable. By setting the proportion of the structural unit (a4) to the lower limit value or more, the effect of containing the structural unit (a4) can be sufficiently obtained, and by setting the proportion of the structural unit (a4) to the upper limit value or less, balance with other structural units can be obtained. It becomes easy.

The component (A1) is a copolymer having the structural unit (a0) and the structural unit (a1). In addition to the structural unit (a0) and the structural unit (a1), any one of (a2) and (a3) It is preferable that it is a copolymer which has these.
As the component (A1-),
A polymer compound comprising a repeating structure of the structural unit (a0) and the structural unit (a1);
A polymer compound comprising a repeating structure of the structural unit (a0), the structural unit (a1), and the structural unit (a2);
A polymer compound comprising a repeating structure of the structural unit (a0), the structural unit (a1), and the structural unit (a3);
Etc. are preferable.

The polymer compound (A1) of the present invention has a softening point of 130 ° C. or higher. Here, the softening point is measured by the following procedure.
Procedure (1): A 15% by mass solution of the polymer compound (A1) is prepared as a sample.
Procedure (2): A 500 nm resin film is formed using the sample solution.
Procedure (3): Using a local thermal analyzer (ANASYS INSTRUMENTS, VESTA), the AFM probe is brought into contact with the resin film surface and allowed to stand to heat the AFM probe as a thermal cantilever. The temperature at this time was taken as the horizontal axis, and the amount of probe deflection for drawing a curve was taken as the vertical axis (see FIG. 1).
Procedure (4): The softening point is read at a rate of temperature increase of 10 ° C. per second, and the probe moves from “warp” (thermal expansion of the film) to “deflection” (film softening) when heating continues. The temperature at the point of change to is defined as the softening point.

The mass average molecular weight (Mw) of the component (A1) (polystyrene conversion standard by gel permeation chromatography) is not particularly limited, preferably 1000 to 50000, more preferably 1500 to 30000, most preferably 2500 to 20000. preferable. If it is below the upper limit of this range, it has sufficient solubility in a resist solvent to be used as a resist, and if it is above the lower limit of this range, dry etching resistance and resist pattern cross-sectional shape are good.
Further, the dispersity (Mw / Mn) of the component (A1) is not particularly limited, and is preferably 1.0 to 5.0, more preferably 1.0 to 3.0, and 1.2 to 2 .5 is most preferred. In addition, Mn shows a number average molecular weight.

As the component (A1), one type may be used alone, or two or more types may be used in combination.
The proportion of the component (A1) in the substrate component (A) is preferably 25% by mass or more, more preferably 50% by mass, even more preferably 75% by mass with respect to the total mass of the substrate component (A). It may be mass%. When the proportion is 25% by mass or more, lithography properties such as MEF, circularity, and roughness are further improved.

[(A2) component]
The resist composition of the present invention may contain, as the component (A), a base material component (hereinafter referred to as the component (A2)) that does not correspond to the component (A1) and whose polarity is increased by the action of an acid. .
The component (A2) is not particularly limited, and is conventionally known as a substrate component for a chemically amplified resist composition (for example, for ArF excimer laser, for KrF excimer laser (preferably ArF excimer laser). Base resin) and the like may be arbitrarily selected and used. For example, the base resin for ArF excimer laser includes a resin having the structural unit (a1) as an essential structural unit and optionally further including the structural units (a2) to (a4).
(A2) A component may be used individually by 1 type and may be used in combination of 2 or more type.

In the resist composition of the present invention, as the component (A), one type may be used alone, or two or more types may be used in combination.
In the resist composition of the present invention, the content of the component (A) may be adjusted according to the resist film thickness to be formed.

<Acid generator component; (B) component>
The resist composition of the present invention preferably contains an acid generator component (B) that generates an acid upon exposure (hereinafter referred to as component (B)). The component (B) is not particularly limited, and those that have been proposed as acid generators for chemically amplified resists can be used.
Examples of such acid generators include onium salt acid generators such as iodonium salts and sulfonium salts, oxime sulfonate acid generators, bisalkyl or bisarylsulfonyldiazomethanes, and diazomethanes such as poly (bissulfonyl) diazomethanes. Examples include an acid generator, a nitrobenzyl sulfonate acid generator, an imino sulfonate acid generator, and a disulfone acid generator. Of these, it is preferable to use an onium salt acid generator.

  Examples of the onium salt-based acid generator include a compound represented by the following general formula (b-1) (hereinafter also referred to as “(b-1) component”) and a general formula (b-2). A compound (hereinafter also referred to as “(b-2) component”) or a compound represented by the general formula (b-3) (hereinafter also referred to as “(b-3) component”) can be used.

［式中、Ｒ^１０１、Ｒ^１０４〜Ｒ^１０８はそれぞれ独立に置換基を有していてもよい環式基、置換基を有していてもよい鎖状のアルキル基、または置換基を有していてもよい鎖状のアルケニル基である。Ｒ^１０４、Ｒ^１０５は、相互に結合して環を形成していてもよい。Ｒ^１０６〜Ｒ^１０７のいずれか２つは、相互に結合して環を形成していてもよい。Ｒ^１０２はフッ素原子または炭素数１〜５のフッ素化アルキル基である。Ｙ^１０１は単結合または酸素原子を含む２価の連結基である。Ｖ^１０１〜Ｖ^１０３はそれぞれ独立に単結合、アルキレン基、またはフッ素化アルキレン基である。Ｌ^１０１〜Ｌ^１０２はそれぞれ独立に単結合または酸素原子である。Ｌ^１０３〜Ｌ^１０５はそれぞれ独立に単結合、−ＣＯ−又は−ＳＯ_２−である。Ｍ’^ｍ＋はｍ価の有機カチオンである（前記式（ｂ１−１）の化合物におけるカチオンを除く）。］

[Wherein, R ¹⁰¹ and R ^{104 to} R ¹⁰⁸ each independently has a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. A chain alkenyl group which may be present. R ¹⁰⁴ and R ¹⁰⁵ may be bonded to each other to form a ring. Any two of R ^{106 to} R ¹⁰⁷ may be bonded to each other to form a ring. R ¹⁰² is a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms. Y ¹⁰¹ is a single bond or a divalent linking group containing an oxygen atom. V ^{101 to} V ¹⁰³ are each independently a single bond, an alkylene group, or a fluorinated alkylene group. L ^{101 to} L ¹⁰² are each independently a single bond or an oxygen atom. L ^{103 to} L ¹⁰⁵ are each independently a single bond, —CO— or —SO ₂ —. M ′ ^{m +} is an m-valent organic cation (excluding the cation in the compound of the formula (b1-1)). ]

{Anion part}
-Anion moiety of component (b-1) In formula (b-1), R ¹⁰¹ represents a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, Alternatively, a chain alkenyl group which may have a substituent.

(Cyclic group which may have a substituent)
The cyclic group is preferably a cyclic hydrocarbon group, and the cyclic hydrocarbon group may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group.
The aromatic hydrocarbon group for R ¹⁰¹ is the aromatic hydrocarbon ring mentioned for the divalent aromatic hydrocarbon group for Va ¹ in the formula (a1-1), or an aromatic compound containing two or more aromatic rings. Examples include an aryl group in which one hydrogen atom is removed, and a phenyl group and a naphthyl group are preferable.
The cyclic aliphatic hydrocarbon group for R ¹⁰¹ is a group obtained by removing one hydrogen atom from the monocycloalkane or polycycloalkane mentioned as the divalent aliphatic hydrocarbon group for Va ¹ in the formula (a1-1). And an adamantyl group and a norbornyl group are preferable.
In addition, the cyclic hydrocarbon group in R ¹⁰¹ may contain a hetero atom such as a heterocycle, and is specifically represented by the general formulas (a2-r-1) to (a2-r-7). include-containing cyclic group, a heterocyclic group mentioned for other less - lactone-containing cyclic group, -SO ₂ respectively represented by the general formula (a5-r-1) ~ (a5-r-4) to be It is done.

Examples of the substituent in the cyclic hydrocarbon group of R ¹⁰¹ include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, and a nitro group.
The alkyl group as a substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
The alkoxy group as a substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group. Most preferred is an ethoxy group.
Examples of the halogen atom as a substituent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
As the halogenated alkyl group as a substituent, a part or all of hydrogen atoms such as an alkyl group having 1 to 5 carbon atoms, for example, a methyl group, an ethyl group, a propyl group, an n-butyl group, a tert-butyl group, and the like And a group substituted with a halogen atom.

(A chain alkyl group which may have a substituent)
The chain alkyl group for R ¹⁰¹ may be either linear or branched.
The linear alkyl group preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms, and most preferably 1 to 10 carbon atoms. Specifically, for example, methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decanyl group, undecyl group, dodecyl group, tridecyl group, isotridecyl group, tetradecyl group Group, pentadecyl group, hexadecyl group, isohexadecyl group, heptadecyl group, octadecyl group, nonadecyl group, icosyl group, heicosyl group, docosyl group and the like.
The branched alkyl group preferably has 3 to 20 carbon atoms, more preferably 3 to 15 carbon atoms, and most preferably 3 to 10 carbon atoms. Specifically, for example, 1-methylethyl group, 1-methylpropyl group, 2-methylpropyl group, 1-methylbutyl group, 2-methylbutyl group, 3-methylbutyl group, 1-ethylbutyl group, 2-ethylbutyl group, Examples include 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group and the like.

(Chain-like alkenyl group which may have a substituent)
The chain alkenyl group for R ¹⁰¹ may be either linear or branched, preferably has 2 to 10 carbon atoms, more preferably 2 to 5, still more preferably 2 to 4, more preferably 3 Is particularly preferred. Examples of the linear alkenyl group include a vinyl group, a propenyl group (allyl group), and a butynyl group. Examples of the branched alkenyl group include a 1-methylpropenyl group and a 2-methylpropenyl group.
Among the above, the chain alkenyl group is particularly preferably a propenyl group.

Examples of the substituent in the chain alkyl group or alkenyl group of R ¹⁰¹ include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, a nitro group, an amino group, and the cyclic group in R ¹⁰¹ described above. Can be mentioned.

Among these, R ¹⁰¹ is preferably a cyclic group which may have a substituent, and more preferably a cyclic hydrocarbon group which may have a substituent. More specifically, a phenyl group, a naphthyl group, a group obtained by removing one or more hydrogen atoms from a polycycloalkane, and lactones represented by the above formulas (a2-r-1) to (a2-r-7), respectively. The containing cyclic group, the —SO ₂ -containing cyclic group represented by the general formulas (a5-r-1) to (a5-r-4), respectively, and the like are preferable.

In formula (b-1), Y ¹⁰¹ represents a single bond or a divalent linking group containing an oxygen atom.
When Y ¹⁰¹ is a divalent linking group containing an oxygen atom, Y ¹⁰¹ may contain an atom other than an oxygen atom. Examples of atoms other than oxygen atoms include carbon atoms, hydrogen atoms, sulfur atoms, and nitrogen atoms.
Examples of the divalent linking group containing an oxygen atom include an oxygen atom (ether bond: —O—), an ester bond (—C (═O) —O—), and an oxycarbonyl group (—O—C (═O). )-), Amide bond (—C (═O) —NH—), carbonyl group (—C (═O) —), carbonate bond (—O—C (═O) —O—), etc. A combination of a non-hydrocarbon oxygen atom-containing linking group and an alkylene group; and the like. A sulfonyl group (—SO ₂ —) may be further linked to the combination. Examples of the combination include linking groups represented by the following formulas (y-al-1) to (y-al-7), respectively.

［式中、Ｖ’^１０１は単結合または炭素数１〜５のアルキレン基であり、Ｖ’^１０２は炭素数１〜３０の２価の飽和炭化水素基である。］

[Wherein, V ′ ¹⁰¹ is a single bond or an alkylene group having 1 to 5 carbon atoms, and V ′ ¹⁰² is a divalent saturated hydrocarbon group having 1 to 30 carbon atoms. ]

The divalent saturated hydrocarbon group for V ′ ¹⁰² is preferably an alkylene group having 1 to 30 carbon atoms.

The alkylene group for V ′ ¹⁰¹ and V ′ ¹⁰² may be a linear alkylene group or a branched alkylene group, and a linear alkylene group is preferred.
Specific examples of the alkylene group in V ′ ¹⁰¹ and V ′ ¹⁰² include a methylene group [—CH ₂ —]; —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as ethylene Groups [—CH ₂ CH ₂ —]; —CH (CH ₃ ) CH ₂ —, —CH (CH ₃ ) CH (CH ₃ ) —, —C (CH ₃ ) ₂ CH ₂ —, —CH (CH ₂ CH - ₃₎ CH ₂ alkyl groups such as, trimethylene group (n- propylene _{group) [- CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH 2 CH 2 -, - CH 2 CH (CH 3) CH ₂ - and the like alkyl trimethylene group; tetramethylene _{[-CH 2 CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH 2 CH 2 CH 2 -, - CH 2 CH (CH 3) CH 2 CH 2 - alkyl tetramethylene group and the like; pentamethylene group _{[-CH 2 CH 2 CH 2 CH} 2 CH 2 -] , and the like.
Moreover, some methylene groups in the alkylene group in V ′ ¹⁰¹ or V ′ ¹⁰² may be substituted with a C 5-10 divalent aliphatic cyclic group. The aliphatic cyclic group is preferably a divalent group obtained by further removing one hydrogen atom from the cyclic aliphatic hydrocarbon group of Ra ′ ^{3 in} the formula (a1-r-1). 1,5-adamantylene group or 2,6-adamantylene group is more preferable.

Y ¹⁰¹ is preferably a divalent linking group containing an ester bond or an ether bond, and linking groups represented by the above formulas (y-al-1) to (y-al-5) are preferred.

In formula (b-1), V ¹⁰¹ represents a single bond, an alkylene group, or a fluorinated alkylene group. The alkylene group and fluorinated alkylene group for V ¹⁰¹ preferably have 1 to 4 carbon atoms. ^Examples of the fluorinated alkylene group for V ¹⁰¹ include groups in which some or all of the hydrogen atoms of the alkylene group for V ¹⁰¹ have been substituted with fluorine atoms. Among ^{them, V 101} is preferably a single bond, or a fluorinated alkylene group having 1 to 4 carbon atoms.

In formula (b-1), R ¹⁰² represents a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms. R ¹⁰² is preferably a fluorine atom or a C 1-5 perfluoroalkyl group, and more preferably a fluorine atom.

(B-1) Specific examples of the anion moiety of the component, for example, if the Y ¹⁰¹ is a single bond, fluorinated alkyl sulfonate anions such as trifluoromethane sulfonate anion or perfluorobutane sulfonate anion can be exemplified; Y ¹⁰¹ is In the case of a divalent linking group containing an oxygen atom, anions represented by any one of the following formulas (an-1) to (an-3) can be mentioned.

［式中、Ｒ”^１０１は、置換基を有していてもよい脂肪族環式基、前記式（ｒ−ｈｒ−１）〜（ｒ−ｈｒ−６）でそれぞれ表される基、又は置換基を有していてもよい鎖状のアルキル基であり；Ｒ”^１０２は、置換基を有していてもよい脂肪族環式基、前記式（ａ２−ｒ−１）〜（ａ２−ｒ−７）でそれぞれ表されるラクトン含有環式基、又は前記一般式（ａ５−ｒ−１）〜（ａ５−ｒ−４）でそれぞれ表される−ＳＯ_２−含有環式基であり；Ｒ”^１０３は、置換基を有していてもよい芳香族環式基、置換基を有していてもよい脂肪族環式基、又は置換基を有していてもよい鎖状のアルケニル基であり；Ｖ”^１０１は、フッ素化アルキレン基であり；Ｌ”^１０１は、−Ｃ（＝Ｏ）−又は−ＳＯ_２−であり；ｖ”はそれぞれ独立に０〜３の整数であり、ｑ”はそれぞれ独立に１〜２０の整数であり、ｎ”は０または１である。］

[Wherein R ″ ¹⁰¹ represents an aliphatic cyclic group which may have a substituent, a group represented by each of the above formulas (r-hr-1) to (r-hr-6), or a substituent. A chain-like alkyl group which may have a group; R ″ ¹⁰² represents an aliphatic cyclic group which may have a substituent, the above formulas (a2-r-1) to (a2-r); lactone-containing cyclic group represented respectively by -7), or the formula (a5-r-1) ~ (a5-r-4) with -SO ₂ respectively represented - be-containing cyclic group; R ¹⁰³ is an aromatic cyclic group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a chain alkenyl group which may have a substituent. ^{There; V "101} is an fluorinated alkylene ^{group; L" 101} is, -C (= O) - or -SO ₂ - a and; v "0 to 3 are each independently Is an integer, q "are each independently an integer of 1 to 20, n" is 0 or 1. ]

The aliphatic cyclic group which may have a substituent of R ″ ¹⁰¹ , R ″ ¹⁰² and R ″ ¹⁰³ is preferably the group exemplified as the cyclic aliphatic hydrocarbon group in R ¹⁰¹ . Examples of the substituent include the same substituents that may be substituted for the cyclic aliphatic hydrocarbon group in R ¹⁰¹ .

The aromatic cyclic group which may have a substituent in R ″ ¹⁰³ is preferably the group exemplified as the aromatic hydrocarbon group in the cyclic hydrocarbon group in R ¹⁰¹ . , R ¹⁰¹ and the same substituents that may be substituted for the aromatic hydrocarbon group.

The chain alkyl group which may have a substituent in R ″ ¹⁰¹ is preferably the group exemplified as the chain alkyl group in R ^101. The chain in R ″ ¹⁰³ has a substituent. The good chain alkenyl group is preferably the group exemplified as the chain alkenyl group in R ¹⁰¹ . V ″ ¹⁰¹ is preferably a fluorinated alkylene group having 1 to 3 carbon atoms, and particularly preferably —CF ₂ —, —CF ₂ CF ₂ —, —CHFCF ₂ —, —CF (CF ₃ ) CF ₂ —. , —CH (CF ₃ ) CF ₂ —.

-Anion part of component (b-2) In formula (b-2), R ¹⁰⁴ and R ¹⁰⁵ may each independently have a cyclic group which may have a substituent or a substituent. Examples thereof include a good chain alkyl group or a chain alkenyl group which may have a substituent, and examples thereof include the same as those described above for R ¹⁰¹ in formula (b-1). However, R ¹⁰⁴ and R ¹⁰⁵ may be bonded to each other to form a ring.
R ¹⁰⁴ and R ¹⁰⁵ are preferably a chain alkyl group which may have a substituent, and are a linear or branched alkyl group, or a linear or branched fluorinated alkyl group. It is more preferable.
The chain alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 7 carbon atoms, and still more preferably 1 to 3 carbon atoms. The carbon number of the chain alkyl group of R ¹⁰⁴ and R ¹⁰⁵ is preferably as small as possible for reasons such as good solubility in a resist solvent within the above carbon number range. In addition, in the chain alkyl group of R ¹⁰⁴ and R ^105, the greater the number of hydrogen atoms substituted with fluorine atoms, the stronger the acid strength, and against high-energy light and electron beams of 200 nm or less Since transparency improves, it is preferable. The proportion of fluorine atoms in the chain alkyl group, that is, the fluorination rate is preferably 70 to 100%, more preferably 90 to 100%, and most preferably all hydrogen atoms are substituted with fluorine atoms. Perfluoroalkyl group.
In formula (b-2), V ¹⁰² and V ¹⁰³ are each independently a single bond, an alkylene group, or a fluorinated alkylene group, and each of them is the same as V ¹⁰¹ in formula (b-1). Can be mentioned.
In formula (b-2), L ^{101 to} L ¹⁰² each independently represents a single bond or an oxygen atom.

-Anion part of (b-3) component In formula (b-3), R < ¹⁰⁶ > -R < ¹⁰⁸ > may have the cyclic group which may have a substituent, and a substituent each independently. Examples thereof include a good chain alkyl group or a chain alkenyl group which may have a substituent, and examples thereof include the same as those described above for R ¹⁰¹ in formula (b-1).
L ^{103 to} L ¹⁰⁵ are each independently a single bond, —CO— or —SO ₂ —.

{Cation part}
In the formulas (b-1), (b-2) and (b-3), M ′ ^{m +} is an m-valent organic cation other than the cation in the compound of the formula (b1-1), and in particular, a sulfonium cation Or it is preferable that it is an iodonium cation, and the cation respectively represented by the following general formula (ca-1)-(ca-4) is especially preferable.

［式中、Ｒ^２０１〜Ｒ^２０７、およびＲ^２１１〜Ｒ^２１２は、それぞれ独立に置換基を有していてもよいアリール基、アルキル基またはアルケニル基を表し、Ｒ^２０１〜Ｒ^２０３、Ｒ^２０６〜Ｒ^２０７、Ｒ^２１１〜Ｒ^２１２は、相互に結合して式中のイオウ原子と共に環を形成してもよい。Ｒ^２０８〜Ｒ^２０９はそれぞれ独立に水素原子または炭素数１〜５のアルキル基を表し、Ｒ^２１０は置換基を有していてもよいアリール基、アルキル基、アルケニル基、又は−ＳＯ_２−含有環式基であり、Ｌ^２０１は−Ｃ（＝Ｏ）−または−Ｃ（＝Ｏ）−Ｏ−を表し、Ｙ^２０１は、それぞれ独立に、アリーレン基、アルキレン基またはアルケニレン基を表し、ｘは１または２であり、Ｗ^２０１は（ｘ＋１）価の連結基を表す。］

[Wherein, R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² each independently represents an aryl group, an alkyl group or an alkenyl group which may have a substituent, and R ^{201 to} R ²⁰³ , R ²⁰⁶ to R ²⁰⁷ and R ^{211 to} R ²¹² may be bonded to each other to form a ring together with the sulfur atom in the formula. R ^{208 to} R ²⁰⁹ each independently represent a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, and R ²¹⁰ is an aryl group, alkyl group, alkenyl group, or —SO ₂ — containing an optionally substituted substituent. A cyclic group, L ²⁰¹ represents —C (═O) — or —C (═O) —O—, Y ²⁰¹ each independently represents an arylene group, an alkylene group or an alkenylene group, and x represents 1 or 2 and W ²⁰¹ represents a (x + 1) -valent linking group. ]

Examples of the aryl group in R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² include an unsubstituted aryl group having 6 to 20 carbon atoms, and a phenyl group and a naphthyl group are preferable.
The alkyl group in R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² is a chain or cyclic alkyl group and preferably has 1 to 30 carbon atoms.
The alkenyl group in R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² preferably has 2 to 10 carbon atoms.
Examples of the substituent that R ^{201 to} R ²⁰⁷ and R ^{210 to} R ²¹² may have include an alkyl group, a halogen atom, a halogenated alkyl group, a carbonyl group, a cyano group, an amino group, an aryl group, and an arylthio group. And groups represented by the following formulas (ca-r-1) to (ca-r-7).
The aryl group in the arylthio group as a substituent is the same as that described for R ¹⁰¹ , and specifically includes a phenylthio group or a biphenylthio group.

［式中、Ｒ’^２０１はそれぞれ独立に、水素原子、置換基を有していてもよい環式基、鎖状のアルキル基、または鎖状のアルケニル基である。］

[Wherein, R ′ ²⁰¹ each independently represents a hydrogen atom, an optionally substituted cyclic group, a chain alkyl group, or a chain alkenyl group. ]

The cyclic group which may have a substituent of R ′ ^201, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent are as described above. In addition to the same groups as those described above for R ^{101 in} formula (b-1), a cyclic group which may have a substituent or a chain alkyl group which may have a substituent may have the above formula ( Examples thereof include the same acid dissociable groups represented by a1-r-2).

^{R 201 ~R 203, R 206 ~R} 207, R 211 ~R 212 , when bonded to each other to form a ring with the sulfur atom, a sulfur atom, an oxygen atom, or a hetero atom such as nitrogen atom, carbonyl _{group, -SO -, - SO 2 -} , - SO 3 -, - COO -, - CONH- , or -N _(R N) - (. the _{R N} is an alkyl group having 1 to 5 carbon atoms), etc. You may couple | bond through the functional group of. As the ring to be formed, one ring containing a sulfur atom in the ring skeleton in the formula is preferably a 3- to 10-membered ring, particularly a 5- to 7-membered ring, including the sulfur atom. preferable. Specific examples of the ring formed include, for example, thiophene ring, thiazole ring, benzothiophene ring, thianthrene ring, benzothiophene ring, dibenzothiophene ring, 9H-thioxanthene ring, thioxanthone ring, thianthrene ring, phenoxathiin ring, tetrahydro A thiophenium ring, a tetrahydrothiopyranium ring, etc. are mentioned.

R ^{208 to} R ²⁰⁹ each independently represent a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, preferably a hydrogen atom or an alkyl group having 1 to 3 carbon atoms, and when formed into an alkyl group, they are bonded to each other to form a ring. May be formed.

R ²¹⁰ may have an aryl group which may have a substituent, an alkyl group which may have a substituent, an alkenyl group which may have a substituent, or a substituent. -SO ₂ - containing cyclic group.
The aryl group in R ^210, include unsubstituted aryl group having 6 to 20 carbon atoms, a phenyl group, a naphthyl group.
The alkyl group for R ²¹⁰ is preferably a chain or cyclic alkyl group having 1 to 30 carbon atoms.
The alkenyl group for R ²¹⁰ preferably has 2 to 10 carbon atoms.
The —SO ₂ — containing cyclic group which may have a substituent in R ²¹⁰ is the same as the “—SO ₂ — containing cyclic group” of Ra ^{21 in} the general formula (a2-1). The group represented by the general formula (a5-r-1) is preferable.

Y ²⁰¹ each independently represents an arylene group, an alkylene group or an alkenylene group.
Examples of the arylene group for Y ²⁰¹ include a group in which one hydrogen atom has been removed from the aryl group exemplified as the aromatic hydrocarbon group for R ¹⁰¹ in the above formula (b-1).
Examples of the alkylene group and alkenylene group for Y ²⁰¹ include the same aliphatic hydrocarbon groups as the divalent hydrocarbon group for Va ¹ in the general formula (a1-1).

In the formula (ca-4), x is 1 or 2.
W ²⁰¹ is a (x + 1) valent, that is, a divalent or trivalent linking group.
The divalent linking group in W ²⁰¹ is preferably a divalent hydrocarbon group which may have a substituent, and examples thereof include the same hydrocarbon groups as Ya ²¹ in the general formula (a2-1). The divalent linking group in W ²⁰¹ may be linear, branched or cyclic, and is preferably cyclic. Of these, a group in which two carbonyl groups are combined at both ends of the arylene group is preferable. Examples of the arylene group include a phenylene group and a naphthylene group, and a phenylene group is particularly preferable.
^Examples of the trivalent linking group in W ²⁰¹ include a group obtained by removing one hydrogen atom from the divalent linking group in W ²⁰¹ , a group in which the divalent linking group is further bonded to the divalent linking group, and the like. Can be mentioned. The trivalent linking group in W ²⁰¹ is preferably a group in which two carbonyl groups are bonded to an arylene group.

  Specific examples of suitable cations represented by the formula (ca-1) include cations represented by the following formulas (ca-1-1) to (ca-1-63), respectively.

［式中、ｇ１、ｇ２、ｇ３は繰返し数を示し、ｇ１は１〜５の整数であり、ｇ２は０〜２０の整数であり、ｇ３は０〜２０の整数である。］

[Wherein, g1, g2, and g3 represent the number of repetitions, g1 is an integer of 1 to 5, g2 is an integer of 0 to 20, and g3 is an integer of 0 to 20. ]

［式中、Ｒ”^２０１は水素原子又は置換基であって、置換基としては前記Ｒ^２０１〜Ｒ^２０７、およびＲ^２１０〜Ｒ^２１２が有していてもよい置換基として挙げたものと同様である。］

[Wherein R ″ ²⁰¹ is a hydrogen atom or a substituent, and the substituent is the same as the substituents that R ^{201 to} R ²⁰⁷ and R ^{210 to} R ²¹² may have. is there.]

  Specific examples of suitable cations represented by the formula (ca-3) include cations represented by the following formulas (ca-3-1) to (ca-3-6).

  Specific examples of suitable cations represented by the formula (ca-4) include cations represented by the following formulas (ca-4-1) to (ca-4-2).

As the component (B), one type of acid generator described above may be used alone, or two or more types may be used in combination.
When the resist composition of this invention contains (B) component, 0.5-60 mass parts is preferable with respect to 100 mass parts of (A) component, and, as for content of (B) component, 1-50 mass parts Is more preferable, and 1-40 mass parts is further more preferable. By forming the content of the component (B) within the above range, pattern formation is sufficiently performed. Moreover, when each component of a resist composition is melt | dissolved in the organic solvent, since a uniform solution is obtained and storage stability becomes favorable, it is preferable.

<Basic compound component; (D) component>
In addition to the component (A) or the components (A) and (B), the resist composition of the present invention further includes an acid diffusion controller component (hereinafter also referred to as “component (D)”). You may contain.
The component (D) acts as a quencher (acid diffusion controller) that traps acid generated by exposure from the component (B) and the like.
The component (D) in the present invention may be a photodegradable base (D1) (hereinafter referred to as “(D1) component”) that is decomposed by exposure and loses acid diffusion controllability. A non-corresponding nitrogen-containing organic compound (D2) (hereinafter referred to as “component (D2)”) may be used.

[(D1) component]
By forming the resist composition containing the component (D1), the contrast between the exposed portion and the non-exposed portion can be improved when forming a resist pattern.
The component (D1) is not particularly limited as long as it is decomposed by exposure and loses acid diffusion controllability, and is a compound represented by the following general formula (d1-1) (hereinafter referred to as “(d1-1) component”). ), A compound represented by the following general formula (d1-2) (hereinafter referred to as “(d1-2) component”) and a compound represented by the following general formula (d1-3) (hereinafter referred to as “(d1- One or more compounds selected from the group consisting of “3) component”) are preferred.
The components (d1-1) to (d1-3) are decomposed in the exposed part and lose acid diffusion controllability (basicity), and therefore do not act as a quencher, and act as a quencher in an unexposed part.

［式中、Ｒｄ^１〜Ｒｄ^４は置換基を有していてもよい環式基、置換基を有していてもよい鎖状のアルキル基、または置換基を有していてもよい鎖状のアルケニル基である。ただし、式（ｄ１−２）中のＲｄ^２における、Ｓ原子に隣接する炭素原子にはフッ素原子は結合していないものとする。Ｙｄ^１は単結合、または２価の連結基である。Ｍ^ｍ＋はそれぞれ独立にｍ価の有機カチオンである。］

[Wherein Rd ^{1 to} Rd ⁴ are a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain which may have a substituent. Of the alkenyl group. However, a fluorine atom is not bonded to a carbon atom adjacent to the S atom in Rd ² in the formula (d1-2). Yd ¹ is a single bond or a divalent linking group. M ^{m +} is each independently an m-valent organic cation. ]

{(D1-1) component}
During Anion formula (d1-1), Rd ¹ is have an optionally substituted cyclic group which may have a substituent chain alkyl group or a substituted group, Or a similar chain alkenyl group to the same as R ¹⁰¹ .
Among these, Rd ¹ may have an aromatic hydrocarbon group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a substituent. A chain hydrocarbon group is preferred. The substituent that these groups may have is preferably a hydroxyl group, a fluorine atom or a fluorinated alkyl group.
The aromatic hydrocarbon group is more preferably a phenyl group or a naphthyl group.
The aliphatic cyclic group is more preferably a group in which one or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane or tetracyclododecane.
As the chain hydrocarbon group, a chain alkyl group is preferable. The chain alkyl group preferably has 1 to 10 carbon atoms, and specifically includes a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, and a nonyl group. A linear alkyl group such as a group or decyl group; 1-methylethyl group, 1-methylpropyl group, 2-methylpropyl group, 1-methylbutyl group, 2-methylbutyl group, 3-methylbutyl group, 1-ethylbutyl group And branched chain alkyl groups such as 2-ethylbutyl group, 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group, and the like.

When the chain alkyl group is a fluorinated alkyl group having a fluorine atom or a fluorinated alkyl group as a substituent, the fluorinated alkyl group preferably has 1 to 11 carbon atoms, more preferably 1 to 8 carbon atoms. The fluorinated alkyl group, which is more preferably ˜4, may contain an atom other than a fluorine atom. Examples of atoms other than fluorine atoms include oxygen atoms, carbon atoms, hydrogen atoms, sulfur atoms, and nitrogen atoms.
Rd ¹ is preferably a fluorinated alkyl group in which some or all of the hydrogen atoms constituting the linear alkyl group are substituted by fluorine atoms, and the hydrogen atom constituting the linear alkyl group It is preferable that all are fluorinated alkyl groups (linear perfluoroalkyl groups) substituted with fluorine atoms.

  Preferred specific examples of the anion moiety of the component (d1-1) are shown below.

-Cation part In formula (d1-1), Mm ⁺ is an m-valent organic cation.
The organic cation of M ^{m +} is not particularly limited, and examples thereof include those similar to the cations represented by the general formulas (ca-1) to (ca-4), respectively, and the formula (ca-1- Cations represented by 1) to (ca-1-63) are preferable.
As the component (d1-1), one type may be used alone, or two or more types may be used in combination.

{(D1-2) component}
· During anion formula (d1-2), Rd ² is has an optionally substituted cyclic group which may have a substituent chain alkyl group or a substituted group, A chain alkenyl group which may be the same as R ¹⁰¹ .
However, a fluorine atom is not bonded to a carbon atom adjacent to the S atom in Rd ² (not fluorine-substituted). Thereby, the anion of (d1-2) component turns into a moderate weak acid anion, and the quenching ability of (D) component improves.
Rd ² is preferably an aliphatic cyclic group which may have a substituent, and a group in which one or more hydrogen atoms have been removed from adamantane, norbornane, isobornane, tricyclodecane, tetracyclododecane or the like. (It may have a substituent); it is more preferably a group obtained by removing one or more hydrogen atoms from camphor or the like.
The hydrocarbon group of Rd ² may have a substituent, and examples of the substituent include a hydrocarbon group (aromatic hydrocarbon group, aliphatic hydrocarbon group) in Rd ¹ of the formula (d1-1). The same thing as the substituent which this may have is mentioned.

  Preferred specific examples of the anion moiety of the component (d1-2) are shown below.

-Cation part In formula (d1-2), Mm ⁺ is an m-valent organic cation, and is the same as Mm ⁺ in formula (d1-1).
As the component (d1-2), one type may be used alone, or two or more types may be used in combination.

{(D1-3) component}
During Anion formula (d1-3), Rd ³ is have an optionally substituted cyclic group which may have a substituent chain alkyl group or a substituted group, A chain alkenyl group that may be the same as R ^101, and is preferably a cyclic group containing a fluorine atom, a chain alkyl group, or a chain alkenyl group. Among them, a fluorinated alkyl group is preferable, and the same as the fluorinated alkyl group for Rd ¹ is more preferable.

In formula (d1-3), Rd ⁴ may have a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. Examples of the chain alkenyl group include those similar to R ¹⁰¹ .
Among these, an alkyl group, an alkoxy group, an alkenyl group, or a cyclic group which may have a substituent is preferable.
The alkyl group in Rd ⁴ is preferably a linear or branched alkyl group having 1 to 5 carbon atoms, specifically, methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group. Tert-butyl group, pentyl group, isopentyl group, neopentyl group and the like. A part of the hydrogen atoms of the alkyl group of Rd ⁴ may be substituted with a hydroxyl group, a cyano group, or the like.
The alkoxy group in Rd ⁴ is preferably an alkoxy group having 1 to 5 carbon atoms. Specific examples of the alkoxy group having 1 to 5 carbon atoms include methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n- Examples include butoxy group and tert-butoxy group. Of these, a methoxy group and an ethoxy group are preferable.

Examples of the alkenyl group in Rd ⁴ include those similar to R ¹⁰¹ described above, and a vinyl group, a propenyl group (allyl group), a 1-methylpropenyl group, and a 2-methylpropenyl group are preferable. These groups may further have, as a substituent, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms.

Examples of the cyclic group for Rd ⁴ include the same groups as those described above for R ^101, and one or more hydrogen atoms are removed from a cycloalkane such as cyclopentane, cyclohexane, adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. An alicyclic group or an aromatic group such as a phenyl group or a naphthyl group is preferred. When Rd ⁴ is an alicyclic group, the resist composition is well dissolved in an organic solvent, whereby the lithography properties are improved. In addition, when Rd ⁴ is an aromatic group, in lithography using EUV or the like as an exposure light source, the resist composition is excellent in light absorption efficiency, and sensitivity and lithography characteristics are good.

In formula (d1-3), Yd ¹ represents a single bond or a divalent linking group.
The divalent linking group in Yd ¹ is not particularly limited, but may be a divalent hydrocarbon group (aliphatic hydrocarbon group or aromatic hydrocarbon group) which may have a substituent, or a hetero atom containing 2 Valent linking groups and the like. These may be the same as those exemplified in the description of the divalent linking group of Ya ²¹ in the formula (a2-1).
Yd ¹ is preferably a carbonyl group, an ester bond, an amide bond, an alkylene group, or a combination thereof. The alkylene group is preferably a linear or branched alkylene group, and more preferably a methylene group or an ethylene group.

  Preferred specific examples of the anion moiety of the component (d1-3) are shown below.

-Cation part In formula (d1-3), Mm ⁺ is an m-valent organic cation, and is the same as Mm ⁺ in formula (d1-1).
As the component (d1-3), one type may be used alone, or two or more types may be used in combination.

As the component (D1), only one of the above components (d1-1) to (d1-3) may be used, or two or more may be used in combination.
The content of the component (D1) is preferably 0.5 to 10 parts by mass, more preferably 0.5 to 8 parts by mass, with respect to 100 parts by mass of the component (A). More preferably, it is part by mass.
When the content of the component (D1) is not less than the preferable lower limit value, particularly good lithography characteristics and a resist pattern shape can be obtained. On the other hand, when it is not more than the upper limit value, the sensitivity can be maintained well and the throughput is also excellent.

  The manufacturing method of said (d1-1) component and (d1-2) component is not specifically limited, It can manufacture by a well-known method.

  The content of the component (D1) is preferably 0.5 to 10.0 parts by mass and more preferably 0.5 to 8.0 parts by mass with respect to 100 parts by mass of the component (A). 1.0 to 8.0 parts by mass is even more preferable. When it is at least the lower limit of the above range, particularly good lithography properties and resist pattern shape can be obtained. When the amount is not more than the upper limit of the above range, the sensitivity can be maintained satisfactorily and the throughput is excellent.

((D2) component)
(D) component may contain the nitrogen-containing organic compound component (henceforth (D2) component) which does not correspond to the said (D1) component.
The component (D2) is not particularly limited as long as it functions as an acid diffusion control agent and does not correspond to the component (D1), and any known component may be used. Of these, aliphatic amines, particularly secondary aliphatic amines and tertiary aliphatic amines are preferred.
An aliphatic amine is an amine having one or more aliphatic groups, and the aliphatic groups preferably have 1 to 12 carbon atoms.
Examples of the aliphatic amine include an amine (alkyl amine or alkyl alcohol amine) or a cyclic amine in which at least one hydrogen atom of ammonia NH ₃ is substituted with an alkyl group or hydroxyalkyl group having 12 or less carbon atoms.
Specific examples of alkylamines and alkyl alcohol amines include monoalkylamines such as n-hexylamine, n-heptylamine, n-octylamine, n-nonylamine, n-decylamine; diethylamine, di-n-propylamine, di- -Dialkylamines such as n-heptylamine, di-n-octylamine, dicyclohexylamine; trimethylamine, triethylamine, tri-n-propylamine, tri-n-butylamine, tri-n-pentylamine, tri-n-hexylamine , Trialkylamines such as tri-n-heptylamine, tri-n-octylamine, tri-n-nonylamine, tri-n-decylamine, tri-n-dodecylamine; diethanolamine, triethanolamine, diisopropanolamine, Li isopropanolamine, di -n- octanol amines, alkyl alcohol amines tri -n- octanol amine. Among these, a trialkylamine having 5 to 10 carbon atoms is more preferable, and tri-n-pentylamine or tri-n-octylamine is particularly preferable.

Examples of the cyclic amine include heterocyclic compounds containing a nitrogen atom as a hetero atom. The heterocyclic compound may be monocyclic (aliphatic monocyclic amine) or polycyclic (aliphatic polycyclic amine).
Specific examples of the aliphatic monocyclic amine include piperidine and piperazine.
As the aliphatic polycyclic amine, those having 6 to 10 carbon atoms are preferable. Specifically, 1,5-diazabicyclo [4.3.0] -5-nonene, 1,8-diazabicyclo [5. 4.0] -7-undecene, hexamethylenetetramine, 1,4-diazabicyclo [2.2.2] octane, and the like.

  Other aliphatic amines include tris (2-methoxymethoxyethyl) amine, tris {2- (2-methoxyethoxy) ethyl} amine, tris {2- (2-methoxyethoxymethoxy) ethyl} amine, tris {2 -(1-methoxyethoxy) ethyl} amine, tris {2- (1-ethoxyethoxy) ethyl} amine, tris {2- (1-ethoxypropoxy) ethyl} amine, tris [2- {2- (2-hydroxy Ethoxy) ethoxy} ethyl] amine, triethanolamine triacetate and the like, and triethanolamine triacetate is preferable.

As the component (D2), an aromatic amine may be used.
Aromatic amines include aniline, pyridine, 4-dimethylaminopyridine, pyrrole, indole, pyrazole, imidazole or derivatives thereof, diphenylamine, triphenylamine, tribenzylamine, 2,6-diisopropylaniline, N-tert-butoxy. And carbonylpyrrolidine.

(D2) A component may be used independently and may be used in combination of 2 or more type.
(D2) A component is normally used in 0.01-5.0 mass parts with respect to 100 mass parts of (A) component. By setting the content in the above range, the resist pattern shape, the stability over time, and the like are improved.

(D) A component may be used individually by 1 type and may be used in combination of 2 or more type.
When the resist composition of this invention contains (D) component, it is preferable that (D) component is 0.1-15 mass parts with respect to 100 mass parts of (A) component, 0.3- More preferably, it is 12 mass parts, and it is still more preferable that it is 0.5-12 mass parts. When it is at least the lower limit of the above range, lithography properties such as LWR are further improved when a resist composition is used. Further, a better resist pattern shape can be obtained. When the amount is not more than the upper limit of the above range, the sensitivity can be maintained satisfactorily and the throughput is excellent.

<Optional component>
[(E) component]
The resist composition of the present invention comprises, as optional components, an organic carboxylic acid, a phosphorus oxo acid, and derivatives thereof for the purpose of preventing sensitivity deterioration and improving the resist pattern shape, retention stability over time, and the like. At least one compound (E) selected from the group (hereinafter referred to as component (E)) can be contained.
As the organic carboxylic acid, for example, acetic acid, malonic acid, citric acid, malic acid, succinic acid, benzoic acid, salicylic acid and the like are suitable.
Examples of phosphorus oxo acids include phosphoric acid, phosphonic acid, and phosphinic acid. Among these, phosphonic acid is particularly preferable.
Examples of the oxo acid derivative of phosphorus include esters in which the hydrogen atom of the oxo acid is substituted with a hydrocarbon group, and the hydrocarbon group includes an alkyl group having 1 to 5 carbon atoms and 6 to 6 carbon atoms. 15 aryl groups and the like.
Examples of phosphoric acid derivatives include phosphoric acid esters such as di-n-butyl phosphate and diphenyl phosphate.
Examples of phosphonic acid derivatives include phosphonic acid esters such as phosphonic acid dimethyl ester, phosphonic acid-di-n-butyl ester, phenylphosphonic acid, phosphonic acid diphenyl ester, and phosphonic acid dibenzyl ester.
Examples of phosphinic acid derivatives include phosphinic acid esters and phenylphosphinic acid.
(E) A component may be used individually by 1 type and may use 2 or more types together.
(E) A component is normally used in 0.01-5.0 mass parts with respect to 100 mass parts of (A) component.

[(F) component]
The resist composition of the present invention may contain a fluorine additive (hereinafter referred to as “component (F)”) in order to impart water repellency to the resist film.
Examples of the component (F) include JP 2010-002870 A, JP 2010-032994 A, JP 2010-277043 A, JP 2011-13569 A, and JP 2011-128226 A. The described fluorine-containing polymer compound can be used.
More specifically, examples of the component (F) include a polymer having a structural unit (f1) represented by the following formula (f1-1). Examples of such a polymer include a polymer consisting of only the structural unit (f1) (homopolymer); a copolymer of the structural unit represented by the following formula (f1) and the structural unit (a1); ), A copolymer of the structural unit derived from acrylic acid or methacrylic acid, and the structural unit (a1).

［式中、Ｒは前記同様であり、Ｒｆ^１０２およびＲｆ^１０３はそれぞれ独立して水素原子、ハロゲン原子、炭素数１〜５のアルキル基、又は炭素数１〜５のハロゲン化アルキル基を表し、Ｒｆ^１０２およびＲｆ^１０３は同じであっても異なっていてもよい。ｎｆ^１は１〜５の整数であり、Ｒｆ^１０１はフッ素原子を含む有機基である。］

[Wherein, R is the same as defined above, and Rf ¹⁰² and Rf ¹⁰³ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, Rf ¹⁰² and Rf ¹⁰³ may be the same or different. nf ¹ is an integer of ¹ to 5, and Rf ¹⁰¹ is an organic group containing a fluorine atom. ]

In formula (f1-1), R is the same as described above. R is preferably a hydrogen atom or a methyl group.
In formula (f1-1), examples of the halogen atom for Rf ¹⁰² and Rf ¹⁰³ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. Examples of the alkyl group having 1 to 5 carbon atoms of Rf ¹⁰² and Rf ¹⁰³ include the same as the alkyl group having 1 to 5 carbon atoms of R, and a methyl group or an ethyl group is preferable. Specific examples of the halogenated alkyl group having 1 to 5 carbon atoms of Rf ¹⁰² and Rf ¹⁰³ include a group in which part or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms are substituted with a halogen atom. Can be mentioned. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. The inter alia ^{Rf 102} and ^{Rf 103,} hydrogen atom, a fluorine atom, or an alkyl group having 1-5 carbon atoms preferably, hydrogen atom, a fluorine atom, methyl group or ethyl group is preferred.
In formula (f1-1), nf ¹ is an integer of ¹ to 5, preferably an integer of 1 to 3, and more preferably 1 or 2.

In formula (f1-1), Rf ¹⁰¹ is an organic group containing a fluorine atom, and is preferably a hydrocarbon group containing a fluorine atom.
The hydrocarbon group containing a fluorine atom may be linear, branched or cyclic, and preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms. The carbon number of 1 to 10 is particularly preferable.
The hydrocarbon group containing a fluorine atom preferably has 25% or more of the hydrogen atoms in the hydrocarbon group fluorinated, more preferably 50% or more fluorinated, and 60% or more. Fluorination is particularly preferable because the hydrophobicity of the resist film during immersion exposure is increased.
Among ^these, as ^{Rf 101,} particularly preferably a fluorinated hydrocarbon group having 1 to 5 carbon atoms, a methyl _{group, -CH 2 -CF 3, -CH 2} -CF 2 -CF 3, -CH (CF 3) 2 _{, -CH} 2 _-CH 2 _-CF 3, and most preferably _{-CH 2 -CH 2 -CF 2 -CF 2} -CF 2 -CF 3.

(F) As for the mass mean molecular weight (Mw) (polystyrene conversion reference | standard by a gel permeation chromatography), 1000-50000 are preferable, 5000-40000 are more preferable, and 10000-30000 are the most preferable. If it is below the upper limit of this range, it has sufficient solubility in a resist solvent to be used as a resist, and if it is above the lower limit of this range, dry etching resistance and resist pattern cross-sectional shape are good.
The dispersity (Mw / Mn) of the component (F) is preferably 1.0 to 5.0, more preferably 1.0 to 3.0, and most preferably 1.2 to 2.5.

(F) A component may be used individually by 1 type and may use 2 or more types together.
(F) A component is used in the ratio of 0.5-10 mass parts with respect to 100 mass parts of (A) component.

  The resist composition of the present invention further contains, if desired, miscible additives such as additional resins for improving the performance of the resist film, dissolution inhibitors, plasticizers, stabilizers, colorants, antihalation agents, A dye or the like can be appropriately added and contained.

[(S) component]
The resist composition of the present invention can be produced by dissolving the material in an organic solvent (hereinafter sometimes referred to as (S) component).
As the component (S), any component can be used as long as it can dissolve each component to be used to form a uniform solution. Conventionally, any one of known solvents for chemically amplified resists can be used. Two or more types can be appropriately selected and used.
For example, lactones such as γ-butyrolactone; ketones such as acetone, methyl ethyl ketone (MEK), cyclohexanone, methyl-n-pentyl ketone, methyl isopentyl ketone, 2-heptanone; ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol Polyhydric alcohols such as: ethylene glycol monoacetate, diethylene glycol monoacetate, propylene glycol monoacetate, dipropylene glycol monoacetate, etc., compounds having an ester bond, monohydric ethers of the polyhydric alcohols or compounds having an ester bond , Monoalkyl ethers such as monoethyl ether, monopropyl ether, monobutyl ether or monophenyl ether Derivatives of polyhydric alcohols such as compounds having an ether bond [in these, propylene glycol monomethyl ether acetate (PGMEA) and propylene glycol monomethyl ether (PGME) are preferred]; cyclic ethers such as dioxane, and lactic acid Esters such as methyl, ethyl lactate (EL), methyl acetate, ethyl acetate, butyl acetate, methyl pyruvate, ethyl pyruvate, methyl methoxypropionate, ethyl ethoxypropionate; anisole, ethyl benzyl ether, cresyl methyl ether, Diphenyl ether, dibenzyl ether, phenetol, butyl phenyl ether, ethylbenzene, diethylbenzene, pentylbenzene, isopropylbenzene, toluene, xylene, cymene, mesitylene, etc. An aromatic organic solvent, dimethyl sulfoxide (DMSO), etc. can be mentioned.
These organic solvents may be used independently and may be used as 2 or more types of mixed solvents.
Of these, PGMEA, PGME, γ-butyrolactone, and EL are preferable.
Moreover, the mixed solvent which mixed PGMEA and the polar solvent is also preferable. The blending ratio (mass ratio) may be appropriately determined in consideration of the compatibility between PGMEA and the polar solvent, preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. It is preferable to be within the range.
More specifically, when EL or cyclohexanone is blended as the polar solvent, the mass ratio of PGMEA: EL or cyclohexanone is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. . Moreover, when mix | blending PGME as a polar solvent, the mass ratio of PGMEA: PGME becomes like this. Preferably it is 1: 9-9: 1, More preferably, it is 2: 8-8: 2, More preferably, it is 3: 7-7: 3.
In addition, as the component (S), a mixed solvent of at least one selected from PGMEA and EL and γ-butyrolactone is also preferable. In this case, the mixing ratio of the former and the latter is preferably 70:30 to 95: 5.
(S) The usage-amount of a component is not specifically limited, It is a density | concentration which can be apply | coated to a board | substrate etc., and is suitably set according to a coating film thickness. Generally, it is used so that the solid content concentration of the resist composition is in the range of 1 to 20% by mass, preferably 2 to 15% by mass.

≪Resist pattern formation method≫
More specifically, the resist pattern forming method of the second aspect of the present invention can be performed, for example, as follows.
First, the resist composition is applied onto a support using a spinner or the like, and a baking (post-apply bake (PAB)) treatment is performed, for example, at a temperature of 80 to 150 ° C. for 40 to 120 seconds, preferably 60 to 90 seconds. To form a resist film. Next, the resist film is exposed through a mask (mask pattern) on which a predetermined pattern is formed using an exposure apparatus such as an ArF exposure apparatus, an electron beam drawing apparatus, or an EUV exposure apparatus, or a mask pattern. After performing selective exposure by drawing or the like by direct irradiation with an electron beam without passing through, baking (post-exposure baking (PEB)) treatment is performed, for example, at a temperature of 80 to 150 ° C. for 40 to 120 seconds, preferably 60 Apply for ~ 90 seconds. The resist film is developed with an organic developer, and then preferably rinsed with a rinse containing an organic solvent and dried.
After the development process or the rinsing process, a process of removing the developer or the rinsing liquid adhering to the pattern with a supercritical fluid may be performed.
In some cases, a baking (post-baking) treatment may be performed after the development treatment, the rinsing treatment or the supercritical fluid treatment in order to remove the remaining organic solvent.

The support is not particularly limited, and a conventionally known one can be used, and examples thereof include a substrate for electronic components and a substrate on which a predetermined wiring pattern is formed. More specifically, a silicon substrate, a metal substrate such as copper, chromium, iron, and aluminum, a glass substrate, and the like can be given. As a material for the wiring pattern, for example, copper, aluminum, nickel, gold or the like can be used.
Further, the support may be a substrate in which an inorganic and / or organic film is provided on the above-described substrate. An inorganic antireflection film (inorganic BARC) is an example of the inorganic film. Examples of the organic film include organic films such as an organic antireflection film (organic BARC) and a lower organic film in a multilayer resist method.
Here, the multilayer resist method is a method in which at least one organic film (lower organic film) and at least one resist film (upper resist film) are provided on a substrate, and the resist pattern formed on the upper resist film is used as a mask. This is a method of patterning a lower organic film, and it is said that a pattern with a high aspect ratio can be formed. That is, according to the multilayer resist method, the required thickness can be secured by the lower organic film, so that the resist film can be thinned and a fine pattern with a high aspect ratio can be formed.
In the multilayer resist method, basically, a method of forming a two-layer structure of an upper resist film and a lower organic film (two-layer resist method), and one or more intermediate layers between the upper resist film and the lower organic film And a method of forming a multilayer structure of three or more layers (metal thin film etc.) (three-layer resist method).

The wavelength used for the exposure is not particularly limited, and ArF excimer laser, KrF excimer laser, F ₂ excimer laser, EUV (extreme ultraviolet), VUV (vacuum ultraviolet), EB (electron beam), X-ray, soft X-ray, etc. Can be done using radiation. The resist composition is highly useful for KrF excimer laser, ArF excimer laser, EB or EUV, and is particularly useful for ArF excimer laser, EB or EUV.

The exposure method of the resist film may be normal exposure (dry exposure) performed in an inert gas such as air or nitrogen, or may be immersion exposure (Liquid Immersion Lithography).
In immersion exposure, the space between the resist film and the lens at the lowest position of the exposure apparatus is previously filled with a solvent (immersion medium) having a refractive index larger than that of air, and exposure (immersion exposure) is performed in that state. It is an exposure method.
As the immersion medium, a solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film to be exposed is preferable. The refractive index of such a solvent is not particularly limited as long as it is within the above range.
Examples of the solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film include water, a fluorine-based inert liquid, a silicon-based solvent, and a hydrocarbon-based solvent.
Specific examples of the fluorine-based inert liquid include a fluorine-based compound such as C ₃ HCl ₂ F ₅ , C ₄ F ₉ OCH ₃ , C ₄ F ₉ OC ₂ H ₅ , and C ₅ H ₃ F ₇ as a main component. Examples thereof include liquids, and those having a boiling point of 70 to 180 ° C are preferable, and those having a boiling point of 80 to 160 ° C are more preferable. It is preferable that the fluorine-based inert liquid has a boiling point in the above range since the medium used for immersion can be removed by a simple method after the exposure is completed.
As the fluorine-based inert liquid, a perfluoroalkyl compound in which all hydrogen atoms of the alkyl group are substituted with fluorine atoms is particularly preferable. Specific examples of the perfluoroalkyl compound include a perfluoroalkyl ether compound and a perfluoroalkylamine compound.
More specifically, examples of the perfluoroalkyl ether compound include perfluoro (2-butyl-tetrahydrofuran) (boiling point: 102 ° C.). Examples of the perfluoroalkylamine compound include perfluorotributylamine ( Boiling point of 174 ° C.).
As the immersion medium, water is preferably used from the viewpoints of cost, safety, environmental problems, versatility, and the like.

  The organic solvent contained in the organic solvent used for development is not particularly limited as long as it can dissolve the base component (A) (base component (A) before exposure), and is appropriately selected from known organic solvents. it can. Specific examples include polar solvents such as ketone solvents, ester solvents, and nitrile solvents. As the ester solvent, butyl acetate is preferred. As the ketone solvent, methyl amyl ketone (2-heptanone) is preferable.

  The ketone solvent is an organic solvent containing C—C (═O) —C in the structure. The ester solvent is an organic solvent containing C—C (═O) —O—C in the structure. The alcohol solvent is an organic solvent containing an alcoholic hydroxyl group in the structure, and “alcoholic hydroxyl group” means a hydroxyl group bonded to a carbon atom of an aliphatic hydrocarbon group. The amide solvent is an organic solvent containing an amide group in the structure. The ether solvent is an organic solvent containing C—O—C in the structure. Among organic solvents, there are organic solvents that contain a plurality of types of functional groups that characterize each of the above solvents in the structure. Shall. For example, diethylene glycol monomethyl ether corresponds to both alcohol solvents and ether solvents in the above classification. The hydrocarbon solvent is a hydrocarbon solvent made of hydrocarbon and having no substituent (a group or atom other than a hydrogen atom and a hydrocarbon group).

  Specific examples of each solvent include ketone solvents such as 1-octanone, 2-octanone, 1-nonanone, 2-nonanone, acetone, 4-heptanone, 1-hexanone, 2-hexanone, diisobutylketone, cyclohexanone, Methylcyclohexanone, phenylacetone, methylethylketone, methylisobutylketone, acetylacetone, acetonylacetone, ionone, diacetylalcohol, acetylcarbinol, acetophenone, methylnaphthylketone, isophorone, propylene carbonate, γ-butyrolactone, methylamylketone (2- Heptanone) and the like.

Examples of ester solvents include methyl acetate, butyl acetate, ethyl acetate, isopropyl acetate, amyl acetate, isoamyl acetate, ethyl methoxyacetate, ethyl ethoxyacetate, propylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, ethylene glycol mono Propyl ether acetate, ethylene glycol monobutyl ether acetate, ethylene glycol monophenyl ether acetate, diethylene glycol monomethyl ether acetate, diethylene glycol monopropyl ether acetate, diethylene glycol monoethyl ether acetate, diethylene glycol monophenyl ether acetate, diethylene glycol monobutyl ether acetate, diethylene Recall monoethyl ether acetate, 2-methoxybutyl acetate, 3-methoxybutyl acetate, 4-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, 3-ethyl-3-methoxybutyl acetate, propylene glycol monomethyl ether acetate, Propylene glycol monoethyl ether acetate, propylene glycol monopropyl ether acetate, 2-ethoxybutyl acetate, 4-ethoxybutyl acetate, 4-propoxybutyl acetate, 2-methoxypentyl acetate, 3-methoxypentyl acetate, 4-methoxypentyl acetate, 2-methyl-3-methoxypentyl acetate, 3-methyl-3-methoxypentyl acetate, 3-methyl-4-methoxy Nethyl acetate, 4-methyl-4-methoxypentyl acetate, propylene glycol diacetate, methyl formate, ethyl formate, butyl formate, propyl formate, ethyl lactate, butyl lactate, propyl lactate, ethyl carbonate, propyl carbonate, butyl carbonate, pyrubin Methyl acid, ethyl pyruvate, propyl pyruvate, butyl pyruvate, methyl acetoacetate, ethyl acetoacetate, methyl propionate, ethyl propionate, propyl propionate, isopropyl propionate, methyl 2-hydroxypropionate, 2-hydroxypropionate Examples include ethyl acid, methyl-3-methoxypropionate, ethyl-3-methoxypropionate, ethyl-3-ethoxypropionate, and propyl-3-methoxypropionate.
Examples of the nitrile solvent include acetonitrile, propionitryl, valeronitrile, butyronitryl and the like.

  A known additive can be blended in the organic developer as required. Examples of the additive include a surfactant. Examples of the surfactant include those described above, and nonionic surfactants are preferable, and fluorine-based surfactants or silicon-based surfactants are more preferable.

  Development processing using an organic developer can be carried out by a known development method, for example, a method in which a support is immersed in the developer for a certain period of time (dip method), or a surface tension of the developer on the surface of the support. A method that swells and rests for a certain period of time (paddle method), a method of spraying developer on the surface of the support (spray method), and a developer coating nozzle that scans at a constant speed on a support that rotates at a constant speed. For example, there is a method of continuously applying the developer (dynamic dispensing method).

After the developing treatment, before the drying, a rinsing treatment can be performed using a rinsing liquid containing an organic solvent. By rinsing, a good pattern can be formed.
As the organic solvent used in the rinsing liquid, for example, organic solvents that are difficult to dissolve the resist pattern among the organic solvents mentioned as the organic solvent used in the organic developer can be used. Usually, at least one solvent selected from hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents, amide solvents and ether solvents is used. Among these, at least one selected from hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents and amide solvents is preferable, and at least one selected from alcohol solvents and ester solvents is preferable. More preferred are alcohol solvents.
The alcohol solvent used for the rinse liquid is preferably a monohydric alcohol having 6 to 8 carbon atoms, and the monohydric alcohol may be linear, branched or cyclic. Specific examples include 1-hexanol, 1-heptanol, 1-octanol, 2-hexanol, 2-heptanol, 2-octanol, 3-hexanol, 3-heptanol, 3-octanol, 4-octanol, and benzyl alcohol. It is done. Among these, 1-hexanol, 2-heptanol, and 2-hexanol are preferable, and 1-hexanol or 2-hexanol is more preferable.
Any one of these organic solvents may be used alone, or two or more thereof may be mixed and used. Moreover, you may mix and use the organic solvent and water other than the above. However, in consideration of development characteristics, the blending amount of water in the rinsing liquid is preferably 30% by mass or less, more preferably 10% by mass or less, further preferably 5% by mass or less, more preferably 3% by mass or less based on the total amount of the rinsing liquid. Is particularly preferred.
A well-known additive can be mix | blended with a rinse liquid as needed. Examples of the additive include a surfactant. Examples of the surfactant include those described above, and nonionic surfactants are preferable, and fluorine-based surfactants or silicon-based surfactants are more preferable.
When the surfactant is blended, the blending amount is usually 0.001 to 5% by mass, preferably 0.005 to 2% by mass, and 0.01 to 0.5% by mass with respect to the total amount of the rinse liquid. % Is more preferable.
The rinsing treatment (washing treatment) using the rinsing liquid can be carried out by a known rinsing method. For example, the rinsing liquid is continuously applied onto a support rotating at a constant speed (rotary coating method). A method of immersing the support in a rinsing solution for a certain time (dip method), a method of spraying a rinsing solution on the surface of the support (spray method), and the like.

  The third aspect of the present invention is a structure derived from a monomer having a retention time shorter than that of β- (methacryloyl) oxy-γ-butyrolactone in a high performance liquid chromatography (HPLC) method using a reverse phase column. The polymer compound has a unit (a0) and a structural unit (a1) containing an acid-decomposable group whose polarity is increased by the action of an acid, and has a softening point of 130 ° C. or higher. The description of the polymer compound of the present invention is the same as the description of the component (A1) in the resist composition of the present invention.

In the polymer compound of the present invention, the proportion of the structural unit (a0-1) is preferably 5 to 80 mol% with respect to all the structural units constituting the polymer compound.
In addition, the polymer compound of the present invention preferably has a structural unit (a1) containing an acid-decomposable group whose maximum is increased by the action of an acid.
The details of the polymer compound of the present invention are the same as those described for the component (A1) in the resist composition of the present invention described above.
The polymer compound of the present invention is suitable as a resin for the base of the resist composition.

The resist composition of the present invention is excellent in various lithography properties such as LWR and sensitivity. The reason is guessed as follows.
The resist composition of the present invention is a structural unit derived from a monomer having a retention time shorter than that of β- (methacryloyl) oxy-γ-butyrolactone in high-performance liquid chromatography (HPLC) analysis using a reversed-phase column. (A0) and a polymer compound having a structural unit (a1) containing an acid-decomposable group whose polarity is increased by the action of an acid and having a softening point of 130 ° C. or higher. This increases the polarity of the resist composition and makes it easier to control the diffusion length of the acid acting in the resist film, so that the lithography properties such as resolution, LER, and LWR are considered to be improved. In the case of an alkali development process, it is considered that the solubility of the polymer compound in the developer is increased and the sensitivity of the resist composition is increased.

  EXAMPLES Hereinafter, although an Example demonstrates this invention more concretely, this invention is not limited to a following example.

[Synthesis Method of Monomer 6]
In a 50 ml three-necked flask, 3.0 g of N-hydroxysuccinimide (N-hydroxysuccinimide) and 10 g of tetrahydrofuran (THF) were added and stirred at room temperature to dissolve, and 3.43 g of triethylamine (TEA) was added thereto. Dripping. After the dropwise addition, the suspension that had become cloudy due to salt formation with triethylamine was cooled to an internal temperature of about 0 ° C., and 2.7 g of methacryloyl chloride dissolved in 10 g of THF was added dropwise over 20 minutes. After completion of the dropwise addition, the reaction solution was returned to room temperature and stirring was continued for 4 hours. After completion of the reaction, the precipitate produced by the reaction was removed by suction filtration, the filtrate was collected, and THF was removed by concentration under reduced pressure. Thereafter, the remaining solid was dissolved in 50 g of ethyl acetate, 20 g of water was added, and washing was performed three times using a separatory funnel. Thereafter, the ethyl acetate solution was concentrated under reduced pressure, the obtained solid was stirred and washed with 50 g of heptane, suction filtered, and the solid on the filter paper was vacuum-dried for one day to obtain 4.3 g of the target monomer 6 (yield). Rate 90%).

[Synthesis example of polymer compound]
As the polymer compounds 1 to 26, the following monomers (1) to (14) for deriving structural units constituting each polymer compound were used, and the polymer compound 13 and the polymer compound 14 were synthesized by the following method.
As for the polymer compounds 1 to 12, 15 to 26, the polymer compound having the monomer 6 is the polymer compound 13, the polymer compound having the monomer 7 or the polymer compounds 19 to 26 for the comparative examples. A polymer compound was synthesized in the same manner as the polymer compound 14.
About the obtained high molecular compound, the copolymer composition ratio (ratio (molar ratio) of each structural unit in structural formula) calculated | required by the carbon 13 nuclear magnetic resonance spectrum (600MHz- ^13C -NMR, internal standard: tetramethylsilane). )), The standard polystyrene equivalent weight average molecular weight (Mw) and molecular weight dispersity (Mw / Mn) determined by GPC measurement, and the softening points measured by AFM are shown in Tables 1 to 4, respectively.

[Synthesis of Polymer Compound 13]
In a separable flask connected with a thermometer, a reflux tube, and a nitrogen introduction tube, 12.00 g (70.52 mmol) of monomer 10, 12.40 g (70.73 mmol) of monomer 5, 2.94 g (16.03 mmol) Monomer 6 was dissolved in 82.01 g of γ-butyrolactone (GBL). To this solution, 14.43 mmol of dimethyl azobisisobutyrate (V-601) as a polymerization initiator was added and dissolved to prepare a dropping solution. 19.06 g of γ-butyrolactone (GBL) was heated to 80 ° C., and the dropping solution was added dropwise over 4 hours under a nitrogen atmosphere. After completion of the dropwise addition, the reaction solution was heated and stirred for 1 hour, and then the reaction solution was cooled to room temperature. The obtained reaction polymerization solution was dropped into a methanol: water = 1: 1 mixed solution to precipitate a polymer, and the precipitated white powder was separated by filtration, washed with methanol and dried. 19.32 g of certain polymer compound 13 was obtained.
The mass average molecular weight (Mw) in terms of standard polystyrene determined by GPC measurement for this polymer compound 13 was 7,800, and the molecular weight dispersity (Mw / Mn) was 2.17.
The copolymer composition ratio (ratio of each structural unit in the structural formula (molar ratio)) determined by carbon 13 nuclear magnetic resonance spectrum (600 MHz — ¹³ C-NMR) is 1 / m / n = 45/45 / 10.

[Synthesis of Polymer Compound 14]
In a separable flask connected with a thermometer, a reflux tube, and a nitrogen introduction tube, 4.00 g (28.34 mmol) of monomer 4, 9.79 g (35.43 mmol) of monomer 5, 1.67 g (7.09 mmol) of Monomer 6 was dissolved in 19.85 g of propylene glycol-1-monomethyl ether-2-acetate (PM): cyclohexanone (CH) = 1: 1 mixture. To this solution, 10 mmol of dimethyl azobisisobutyrate (V-601) as a polymerization initiator was added and dissolved to prepare a dropping solution.
16.37 g of a PM: CH = 1: 1 mixed solution was heated to 80 ° C., and the dropping solution was added dropwise over 4 hours under a nitrogen atmosphere. After completion of the dropwise addition, the reaction solution was heated and stirred for 1 hour, and then the reaction solution was cooled to room temperature.
The obtained reaction polymerization solution was dropped into a large amount of a mixture of heptane (Hep): ethyl acetate (AcOEt) = 4: 1 to precipitate a polymer, and the precipitated white powder was separated by filtration. Hep: AcOEt = 6: 4 Washed with a mixed solution and dried to obtain 8.84 g of the target polymer compound 14.
The mass average molecular weight (Mw) in terms of standard polystyrene determined by GPC measurement for this polymer compound 14 was 7,800, and the molecular weight dispersity (Mw / Mn) was 1.59.
The copolymer composition ratio (ratio of each structural unit in the structural formula (molar ratio)) determined by carbon 13 nuclear magnetic resonance spectrum (600 MHz — ¹³ C-NMR) is 1 / m / n = 45/45 / 10.

<Measurement method of retention time>
The retention time when two or more monomers of interest were analyzed under the same conditions was measured by a high performance liquid chromatography (HPLC) method using a reverse phase column.
The apparatus and conditions used for the HPLC method in the following Example are shown.
Eluent (developing solvent): acetonitrile / buffer solution (using a gradient analysis method, 10/90 (volume ratio) until 0.5 minutes from the start, and then changing the volume ratio linearly with time, and then starting 20 90/10 (volume ratio) per minute.)
Buffer solution: 0.1 mass% trifluoroacetic acid aqueous solution.
Apparatus: Dionex U3000 (manufactured by Dionex).
Column: Superiorex ODS (manufactured by Shiseido); column length 25 cm.
Detector: UV detector (manufactured by Dionex).
Flow rate: 2 mL / min.
Column temperature: 30 ° C.
Sample concentration: acetonitrile solution having a solid content of 0.1% by mass.
Injection volume: 5 μL.
The sample concentration indicates the solid content concentration of the compound in which the monomer has various target structures.
The value of retention time (minutes) is written below each monomer below.

<Measurement method of softening point>
The polymer compounds shown in Tables 1 to 4 below were dissolved in PGMEA, and the resin solution was adjusted so that the resin concentration was 15% by mass. Next, a resin film having a thickness of 500 nm was formed using each resin solution.
A local thermal analyzer (manufactured by ANASYS INSTRUMENTS, VESTA) is used to bring the AFM probe (material: silicon) into contact with the surface of the resin film and leave it to heat the AFM probe that is a thermal cantilever. The temperature at this time is taken as the horizontal axis, and the amount of deflection of the probe for drawing a curve is taken as the vertical axis.
When the probe is brought into contact with each resin film and heated (temperature increase rate: 10 ° C. per second), the probe is deflected from the initial state due to the thermal expansion of the film, and then the resin film is softened when further heated. Changes from “sledge” to “deflection”. The temperature at the change point was defined as the softening point, and the value was read. The numerical values are shown in Tables 1 to 4 below.

Using the obtained polymer compound, resist compositions (Examples 1 to 9 and Comparative Examples 1 to 8) in which the respective components were blended at the blending ratios shown in Table 5 below were prepared. However, Examples 1-3 and Examples 5-9 are reference examples.

In Table 5, each symbol has the following meaning, and the numerical value in [] is a blending amount (part by mass).
-(A) -1-2: The said high molecular compounds 1-2, respectively.
(A) -4: the polymer compound 4.
-(A) -13-26: The polymer compounds 13-26, respectively.
-(B) -1: The following compound (B) -1.
-(D) -1: Tri-n-pentylamine.
-(F) -1: The following compound (F) -1. (L / m = 77/23, Mw = 13800, Mw / Mn = 1.5).
(S) -1: PGMEA.
(S) -2: PGME.
-(S) -3: cyclohexanone.

<Formation of resist pattern; Examples 1 to 9, Comparative Examples 1 to 8>
An organic antireflective film composition “ARC95” (trade name, manufactured by Brewer Science) is applied onto a 12-inch silicon wafer using a spinner, and baked on a hot plate at 110 ° C. for 60 seconds to be dried. Thereby, an organic antireflection film having a thickness of 90 nm was formed.
Each of the resist compositions shown in Table 4 (Examples 1 to 9, Comparative Examples 1 to 8) was applied onto the antireflection film using a spinner, and prebaked (PAB) on the hot plate under the conditions shown in Table 5. By performing the treatment and drying, a resist film having a thickness of 90 nm was formed.
Next, an immersion ArF exposure apparatus NSR-S609B [manufactured by Nikon; NA (numerical aperture) = 1.07, Dipole (in / out = 0.78 / 0.97) with Polano, An immersion medium: water] was selectively irradiated with an ArF excimer laser (193 nm) through a photomask (6% halftone).
Next, alkali development is performed for 10 seconds with a 2.38 mass% TMAH aqueous solution (trade name: NMD-3, manufactured by Tokyo Ohka Kogyo Co., Ltd.) at 23 ° C., and then water rinse for 30 seconds using pure water. Then, it was shaken and dried.
As a result, in each example, a 1: 1 line and space (LS) pattern having a line width of 50 nm and a pitch of 100 nm was formed.

[Exposure Amount Eop (mJ / cm ² ; Sensitivity)]
The optimum exposure dose Eop (mJ / cm ² ; sensitivity) for forming the LS pattern was determined. The results are shown in Table 6.

[LWR (line width roughness) evaluation]
In the above LS pattern, the space width was measured at 400 locations in the longitudinal direction of the space with a length measurement SEM (scanning electron microscope, acceleration voltage 300 V, trade name: S-9380, manufactured by Hitachi High-Technologies Corporation). A triple value (3 s) of the standard deviation (s) was obtained, and a value averaged over 3 s at 400 locations was calculated as a scale indicating LWR. The results are shown in Table 6.
A smaller value of 3s means that the roughness of the line width is smaller, and an LS pattern having a more uniform width is obtained.

  From the above results, it was confirmed that the resist compositions of Examples 1 to 9 had better lithography properties such as LWR and sensitivity than the resist compositions of Comparative Examples 1 to 8.

Claims (2)

A resist composition that generates an acid upon exposure and changes its solubility in a developer by the action of an acid, and includes a base material component (A) whose solubility in a developer changes by the action of an acid,
The base material component (A) is derived from a monomer having a retention time shorter than that of β- (methacryloyl) oxy-γ-butyrolactone in analysis by a high performance liquid chromatography (HPLC) method using a reversed phase column. a unit (a0), has the structural unit (a2) containing a structural unit (a1) and the lactone-containing cyclic group containing an acid-decomposable group that exhibits increased polarity by the action of an acid, and a softening point of 130 ° C. or higher a polymer compound (A1) only contains,
The said monomer contains the compound represented by the following general formula (1 '), The resist composition characterized by the above-mentioned.
The softening point of the polymer compound (A1) is measured by the following procedures (1) to (4).
Procedure (1) As a sample, a solution of 15% by mass of the polymer compound (A1) is prepared.
Procedure (2) A 500 nm-thick resin film is formed using the sample solution.
Procedure (3) Using a local thermal analyzer, the AFM probe is brought into contact with the surface of the resin film and allowed to stand to heat the AFM probe that is a thermal cantilever.
Procedure (4) When the temperature rise rate is 10 ° C. per second and the heating is continued, the temperature at which the probe moves from “sled” (thermal expansion of the film) to “deflection” (softening of the film) is the softening point. It is defined as

[Wherein, R ¹ ′ represents a hydrogen atom or an alkyl group having 1 to 5 carbon atoms. ] A resist pattern comprising a step of forming a resist film using the resist composition according to claim 1 on a support, a step of exposing the resist film, and a step of developing the resist film to form a resist pattern. Forming method.