JP5847686B2 - Method of adding mold flux into continuous casting mold - Google Patents

Description

  The present invention relates to a method of adding mold flux into a mold during continuous casting.

  In continuous casting, casting is generally performed in a state where a flux is added into a mold and a flux layer (a molten layer and an unmelted layer) is formed on the molten steel in the mold. The flux layer can prevent reoxidation of the molten steel bath surface and heat dissipation from the molten steel bath surface, and can capture inclusions floating in the molten steel. Further, since the melted flux flows between the slab and the mold, the slab can be pulled out satisfactorily, and the slab can be prevented from being rapidly cooled at the initial stage of casting. However, if flux is mixed into the slab and remains in the slab, it remains in the product as a surface defect. Therefore, conventionally, methods for adding flux and improving the physical properties of the flux have been proposed.

  For example, Patent Document 1 discloses a method of changing the flux input locus a plurality of times so that the flux is dispersed over the entire surface of the mold as a method of improving the flux addition method. Moreover, in patent document 2, the thickness of the flux on molten steel is made uniform by vibrating a supply nozzle when adding a flux.

  In Patent Document 3, as a method for improving the physical properties of the flux, powder (flux) obtained by pulverizing a once melted mold powder and mixing the obtained pulverized material with an ultrafine carbon material is used.

  Furthermore, in patent document 4, the thickness of the molten mold flux layer in a casting_mold | template and the thickness of an unmelted mold flux layer are adjusted so that the defect incidence rate of a slab or a product may become below a predetermined value.

Japanese Patent Laid-Open No. 11-239856 JP-A-63-123555 JP-A-10-113754 JP 2010-99697 A

  When the flux is added by the methods disclosed in Patent Documents 1 to 4, defects caused by the flux can be almost solved. However, it cannot be solved completely, and defects may occur on the surface of the slab. For this reason, the methods disclosed in Patent Documents 1 to 4 cause defects in the product, leading to quality degradation.

  Therefore, an object of the present invention is to provide a flux addition method that can improve the quality of a product.

  In order to solve the above problems, the present inventor has eagerly studied the cause of defects in the conventional methods (Patent Documents 1 to 4 and the like), and is caused by the fact that the flux is not added in an appropriate manner. I understood.

  Specifically, when the flux is added by an appropriate method in a state where the flux layer (molten layer and unmelted layer) is formed on the molten steel, the flux rises in temperature in the mold, and partly Sinter by decarburizing and then melt. Here, the decarburization and sintering occur in the unmelted layer, and then melted to drop the flux to form a molten layer. As described above, when the flux is added by an appropriate method, the “decarburization, sintering, melting, and dropping process” is performed.

  However, if a large amount of flux is suddenly added into the mold, such as when the flux is added in an inappropriate manner, the bath surface of the molten layer is disturbed at the time of addition, or the power of the added unmelted flux causes The unmelted flux (a part of the unmelted layer) may sink into the melted layer and prevent proper melting of the flux. Here, the proper melting of the flux is hindered by the fact that the unmelted flux in the mold is immersed in the molten layer without going through the above-mentioned “decarburization, sintering, melting and dripping process”. Refers to the state in which only melts and sinters (oversintering). As a result, a sintered product (lumps) whose inside is in an unmelted state is generated.

  Such a sintered product becomes a huge slag bear whose inside is in an unmelted state by adhering to a molten flux (slag rim) during solidification. The slag bear causes vertical cracking as a result of hindering the molten flux from flowing between the slab and the mold. Moreover, when a large molten metal surface fluctuation | variation generate | occur | produces or when the surface flow velocity of molten steel is large, a slag bear will be taken in into a slab and a surface defect will be produced (norrole). And depending on the degree of Norokami, it causes a breakout due to the slab development failure of the Norokami part.

  As described above, in the conventional methods (Patent Documents 1 to 4 and the like), as a result of oversintering due to the flux being added in an inappropriate manner, defects due to the flux have occurred. Therefore, the present inventor has devised an appropriate flux addition method according to various physical properties of the mold flux in order to prevent oversintering of the flux during addition.

  Here, in order to add the flux appropriately, it was found that the three requirements of the addition height, the fall area, and the supply speed in the fall area have a great influence. In the present invention, an appropriate addition method in consideration of the above three requirements was found, and knowledge that oversintering can be prevented by adding a flux by this method was obtained.

Specifically, when the addition from the feeder while moving the feeder of mold flux into the mold to continuously cast steel, 0.7 the casting speed when casting slab [m / min.] To 2.4 [m / min.] or less, when casting a bloom, the casting speed is 0.5 [m / min.] or more and 0.9 [m / min.] or less, and the bulk specific gravity of the mold flux before addition is 1 0.2 [g / cm ³ ] or less, a viscosity of 0.05 to 0.24 Pa · s, a molten mold flux thickness on the molten steel bath surface in the mold of 10 [mm] or more and 20 [mm] or less , The thickness of the unmelted layer (unmelted mold flux layer) on the flux is set to 20 [mm] or more and 60 [mm] or less . And the fall distance (additional height) to the drop start position and unmelted layer (upper surface) which makes mold flux fall freely shall be 250 [mm] or less. In addition, the flux falling area at each time when the mold flux is added is 0.0025 [m ² ] or more and 0.0201 [m ² ] or less, and the mold flux supply speed in the dropping area is 1760 [kg / (m ² · min.)] Add mold flux into the mold in the following manner.
In addition, when continuously casting steel by adding mold flux into the mold with the addition height and addition position fixed, the casting speed is 0.7 [m / min.] Or more when casting the slab. 4 [m / min.] Or less, and when casting a bloom, the casting speed is 0.5 [m / min.] Or more and 0.9 [m / min.] Or less, and the bulk specific gravity of the mold flux before addition is set to 1.2 g / cm ³ or less, a viscosity of 0.05 to 0.24 Pa · s, a molten mold flux thickness on the molten steel bath surface in the mold of 10 mm or more and 20 mm or less, and an unmelted layer thickness on the molten mold flux 20 mm or more and 60 mm or less, the fall distance from the drop start position where the mold flux is freely dropped to the unmelted layer is 250 mm or less, and the flux falling area when the mold flux is added is .0025m and ^more 0.0201M ² below, the addition of mold flux supply rate of the mold flux in the fall region to ^{1760kg / (m 2 · min.} ) Or less and while the mold. Here, the “falling area area” is the area of the area where the flux has fallen in the unmelted layer (upper surface), and the “supply speed” is the supply speed in the flux falling area of the unmelted layer (upper surface). .

  As described above, in the present invention, a mold flux having a bulk specific gravity of a predetermined value or less is used, and a mold flux layer (a molten layer and an unmelted layer) having a predetermined thickness is formed in the mold, The mold flux is added by an appropriate method in consideration of the three requirements of the drop area area and the supply speed in the drop area. Thereby, since the influence of the disturbance of the molten layer bath surface at the time of addition and the power of the added flux can be suppressed, it is possible to prevent the unmelted mold flux (part of the unmelted layer) from entering the molten layer and oversintering. . Therefore, the occurrence of defects due to the mold flux can be prevented, so that the quality of the product can be improved.

In addition, in patent documents 1-4, it is not clarified about the cause which this inventor clarified, therefore, the appropriate addition method which can prevent this, ie, the addition height of a mold flux, a fall area area, and a fall It not found added method considering all three requirements for feed rate in the region. Therefore, in patent documents 1-4, as a result of oversintering at the time of flux addition, the defect resulting from a flux arose.

  According to the present invention, by adding a mold flux of a predetermined bulk specific gravity in an appropriate manner considering the three requirements of mold flux addition height, drop area area, and supply speed in the drop area, Oversintering of unmelted flux can be prevented. Thereby, since generation | occurrence | production of the defect resulting from a flux can be prevented, the quality of a product can be improved.

It is a schematic sectional drawing which shows the casting mold upper periphery of a continuous casting machine. It is a schematic perspective view which shows the inside of a casting_mold | template. It is a top view which shows the operation example of a feeder, and is a figure along the III-III line of FIG. It is a figure which shows the relationship between the supply speed Q of mold flux, and time t. It is a figure which shows the experimental conditions of an Example, and is a top view of the casting_mold | template which shows the measurement position of molten layer thickness and unmelted layer thickness. It is a figure which shows the experimental conditions of an Example, and is a figure which shows the example of the measuring method of molten layer thickness and unmelted layer thickness.

  Hereinafter, preferred embodiments of the present invention will be described with reference to the drawings.

  Here, the addition method of the mold flux which is one embodiment of the present invention (when added using a feeder) will be described below with reference to FIGS.

[Continuous casting machine]
As shown in FIGS. 1 and 2, the continuous casting machine 100 includes an immersion nozzle 1 attached to the bottom of the tundish and a mold 2 in which a lower portion of the immersion nozzle 1 is disposed. Molten steel 21 is supplied into the mold 2 from the immersion nozzle 1. On the molten steel 21, an unmelted layer 22 and a molten layer 23 of mold flack are formed in order from the top. In this embodiment, a feeder 3 for adding mold flux is disposed above the mold 2.

  The immersion nozzle 1 is a two-hole nozzle, and a pair of opposed discharge holes 11 and 12 are formed in the lower part. And the lower part of the immersion nozzle 1 is arrange | positioned in the casting_mold | template 2 so that the discharge holes 11 and 12 may oppose the short side wall of the casting_mold | template 2 (refer FIG.2, 3).

  Further, an in-mold electromagnetic stirring device is disposed outside the mold 2. By operating this, the molten steel 21 in the mold 2 can be flowed. The in-mold electromagnetic stirrer is operated or stopped depending on the steel type and casting conditions.

  The feeder 3 disposed above the mold 2 is connected to a hopper or the like in which mold flux is stored. The mold flux in the hopper is pushed out to the feeder 3 by a mechanical method such as pressure feeding or a screw, and added into the mold 2.

  Here, in FIG. 3, the form of the flux supply by the feeder 3 in this embodiment is shown. In this figure, the form in the case where mold flack is continuously sprinkled clockwise along the inner wall of the mold from above the upper left corner of the mold 2 is shown (see the arrow shown in FIG. 3). In addition, about the track | orbit of the feeder 3, you may change at any time in view of the dispersion | distribution state of a flux, you may program so that the track | orbit previously set may be followed, and the party can select arbitrarily. Further, the moving speed and speed change of the feeder 3 can be arbitrarily selected by the party. Furthermore, the cutting speed (blowing speed) of the mold flux from the feeder can be arbitrarily selected including continuous cutting and complete cutting.

  The addition of the mold flux is started almost simultaneously with the start of casting, and thereafter the mold flux is continuously added. The added mold flux spreads over the entire surface of the mold 2 to become an unmelted layer 22, and then melts to become a molten layer 23.

When the casting speed is increased after the start of casting and a steady state is reached, as shown in FIGS. 1 and 2, the thickness T _u of the unmelted layer 22 in the mold 2 becomes 20 [mm] or more, and the molten layer 23 In a state where the thickness Tm of the steel _sheet becomes 10 [mm] or more, the addition height H of the mold flux, the drop area A, and the supply speed Q in the drop area are added within the following ranges. Here, the “steady state” is a state in which the casting speed has reached a predetermined target speed, or a state in which the casting speed has reached a constant speed even if the casting speed has not reached the predetermined target speed.

Note that the thickness T _u of the unmelted layer 22 and the thickness T _m of the molten layer 23 are T _u ≧ 20 [mm] and T _m ≧ 10 [mm] for the following reasons.
(Unmelted layer thickness)
The unmelted layer 22 having a thickness of 20 [mm] or more serves as a buffer material when a mold flux is added. Therefore, the mold flux can be prevented from entering the molten layer 23 at the time of addition. On the other hand, if the thickness T _u unmelted layer 22 is less than 20 [mm], disturbed or large bath surface of the molten layer 23 during the addition, by the power of the added mold flux unmelted flux (unmelted layer 22 Some) are likely to sink into the molten layer 23. Thereby, as a result of producing a sintered product in which the inside is in an unmelted state, defects are generated on the surface of the slab. Therefore, the thickness T _u unmelted layer 22 and 20 [mm] or more. The thickness _{Tu of the} unmelted layer 22 indicates a vertical distance from the upper end of the unmelted layer 22 to the upper end of the molten layer 23 as shown in FIG.

(Molten layer thickness)
When the thickness T _m of the molten layer 23 is as thin as less than 10 [mm], the molten layer 23 becomes high temperature due to the heat of the molten steel 21. When an unmelted mold flux is entrained in such a molten layer 23, a sintered product in which the inside is in an unmelted state is generated, thereby causing surface defects in the slab. Therefore, the thickness T _m of a molten layer 23 and 10 [mm] or more. As shown in FIG. 1, the thickness T _m of the molten layer 23 indicates a vertical distance from the upper end of the molten layer 23 (the lower end of the unmelted layer 22) to the molten steel 21 bath surface.

(Additional height H)
The “added height H” of the mold flux is a drop distance of the mold flux from the drop start position where the mold flux is freely dropped to the unmelted layer 22. When the mold flux is added using the feeder 3 as in this embodiment, the “added height H” is vertical from the tip of the feeder 3 to the upper surface of the unmelted layer 22 as shown in FIGS. Indicates the direction distance.

  When the addition height H of the mold flux exceeds 250 [mm], the flux is added from a high position, so that the bath surface of the molten layer 23 is greatly disturbed at the time of addition or unmelted due to the power of the added mold flux. The layer flux (a part of the unmelted layer 22) tends to sink into the molten layer 23. As a result, a sintered product in which the inside is in an unmelted state is generated, so that a defect occurs on the surface of the slab. Therefore, the addition height H is set to 250 [mm] or less. If the addition height H is too low, the distance between the addition position and the unmelted layer 22 becomes very short, so that the mold flux does not easily spread over the entire surface of the mold 2. Therefore, the addition height H is preferably 40 [mm] or more, but the lower limit value of the addition height H is not limited to this.

(Fall area A)
The “falling area area A” of the mold flux is the falling area of the mold flux on the unmelted layer 22 bath surface (upper surface) as shown in FIG. 2 (“falling area area A” in FIGS. 2 and 3). reference). When the drop area A is as small as less than 0.0025 [m ² ], the mold flux is difficult to spread entirely in the mold 2, so the mold flux discharge rate from the feeder 3 needs to be increased. However, if the discharge speed is too high, the bath surface of the molten layer 23 is greatly disturbed at the time of addition, or the unmelted flux (a part of the unmelted layer 22) sinks into the molten layer 23 due to the power of the added mold flux. It's easy to do. As a result, a sintered product whose inside is in an unmelted state is generated. Therefore, the fall area is set to 0.0025 [m ² ] or more. Here, when the fall area is different at each position in the mold 2, the minimum fall area of the fall areas is set to 0.0025 [m ² ] or more.

When adding the mold flux using the feeder 3 as in this embodiment, 1) when the discharge rate of the mold flux discharged from the feeder 3 is constant, and 2) when the addition height H is constant, as shown in FIGS. 3 and 4, drop region area a (maximum drop region area _{a x, a y, a 1} , a 2, a 3 ···) are all the same area. In the present embodiment, the smallest drop region area A in the casting section (steady _{state) (A x, A y,} A 1, A 2, A 3 ···) is a 0.0025 [m ^2] or more ing.

In FIG. 3, only A, A _x , and A _y are schematically illustrated as mold powder fall area areas, and FIG. 4 illustrates mold powder fall area areas as A ₁ , A ₂ , A ₃ ... A ₁₀ is schematically illustrated. However, in the present embodiment, the mold flux is continuously added during the movement of the feeder 3 (continuous movement type spraying). , fall region area a shown in _{a x, a y, a 1} , a 2, a 3 ···, not limited to a _10. Here, the drop area areas A ₁ , A ₂ , A ₃ ... Indicate the following areas (see FIG. 4).
Fall area A ₁ : Drop area of mold flux added to t = t ₁ [s] Fall area A ₂ : Drop area of mold flux added to t = t ₂ [s] Fall area A ₃ : Drop area of mold flux added to t = t ₃ [s] Fall area A ₄ , A ₅ ...: Mold flux added to t = t ₄ , t _5. Falling area

(Supply speed Q)
When the supply rate Q exceeds 1760 [kg / (m ² · min.)], The supply rate Q is too fast, so that the bath surface of the molten layer 23 is greatly disturbed at the time of addition, or the power of the added mold flux is not sufficient. The molten flux (a part of the unmelted layer 22) tends to sink into the molten layer 23. As a result, a sintered product whose inside is in an unmelted state is generated. Therefore, the supply rate Q is set to 1760 [kg / (m ² · min.)] Or less. The added mold flux becomes an unmelted layer 22 in the mold 2 and then melts to become a molten layer 23. For this reason, if the supply rate Q of the mold flux is low, the unmelted layer 22 cannot be maintained at a sufficient thickness. When the thickness of the unmelted layer 22 is reduced, the unmelted layer 22 does not function as a buffer material at the time of addition. Therefore, the supply rate Q is preferably 1.0 [kg / (m ² · min.)] Or more. The lower limit value of the supply speed Q is not limited to this.

  Here, an example of the supply speed Q of the present embodiment will be described with reference to FIG.

FIG. 4 shows a relationship (an example) between the supply speed Q and time. In this example, 1) the discharge speed of the mold flux discharged from the feeder 3 is constant, 2) the addition height H is constant, 3) the moving speed of the feeder 3 is constant, and 4) the fall area A is This is a constant example. FIG. 4A shows the supply speed Q of the drop area area A ₄ and the drop area area A ₉ . FIG. 4B shows the supply speed Q of the drop area areas A ₁ , A ₂ , A ₃ ... A ₁₀ .

<Falling area A ₄ >
As shown in FIG. 4 (a), a drop region area A _{4 is, t = t a [s]} ~t b [s] by the addition of between, mold flux is supplied (t _a <t ₄ <t _b ). The supply speed Q gradually increases from t = t _a [s] to t ₄ [s], reaches a maximum at t = t ₄ [s], then decreases gradually, and Q = 0 at t = t _b [s]. It becomes. Here, the fall area area at t = t ₄ [s] is A ₄ , and the supply speed Q at t = t ₄ [s] is 1760 [kg / (m ² · min.)] (FIG. 4). (See (b) Q _max = 1760 [kg / (m ² · min.)]). Incidentally, t = 0 [s] ~t a [s] _{between, t b [s] ~t d} [s] between, (feed rate = 0) for the mold flux is not added to the fall region area A _4, The supply rate during this period is not used to calculate the supply rate Q.

<Falling area A ₉ >
Mold flux is supplied to the drop area A ₉ by addition between t = t _c [s] and t _d [s] (t _c <t ₉ <t _d ). The supply speed Q gradually increases from t = t _c [s] to t ₉ [s], reaches a maximum at t = t ₉ [s], then decreases gradually, and Q = 0 at t = t _d [s]. It becomes. Here, the fall area area at t = t ₉ [s] is A ₉ , and the supply speed Q at t = t ₉ [s] is 1760 [kg / (m ² · min.)] (FIG. 4). (See (b) Q _max = 1760 [kg / (m ² · min.)]). Incidentally, t = 0 between [s] ~t _c [s], since the falling region area A ₄ mold flux is not added (feed rate = 0), during which the feed rate to calculate the supply rate Q Not used for.

Thus, under the conditions of this example (conditions in which the discharge speed is constant, the addition height H is constant, the movement speed of the feeder 3 is constant, and the drop area A is constant), as shown in FIGS. As the feeder 3 moves, the position of the fall area A (A _x , A _y , A ₁ , A ₂ , A ₃ ...) Moves, but the supply amount supplied to each fall area A is When the drop area area is A (A ₁ , A ₂ , A ₃ ...) (T = t ₁ , t ₂ , t ₃ ...), The supply speeds Q are all the same ( FIG. 4B shows “Q _max ”). In this example, Q _max = 1760 [kg / (m ² · min.)], And Q ≦ 1760 [kg / (m ² · min.)]) In all drop regions.

Thus, when casting reaches a steady state, the thickness T _u of the unmelted layer 22 in the mold 2 is 20 [mm] or more, and the thickness T _m of the molten layer 23 is 10 [mm] or more, the mold flux Addition height H is set within 250 [mm], drop area A is set to 0.0025 [m ² ] or more, and supply speed Q in the drop area is set to 1760 [kg / (m ² · min.)] Or less. Added. When the mold flux is added at such an addition height H, drop area A and supply speed Q, the thickness T _u of the unmelted layer 22 in the mold 2 becomes 20 [mm] or more, and the thickness T of the molten layer 23 _m is 10 [mm] or more.

In the present embodiment, a mold flux (unmelted before addition) having a bulk specific gravity of 1.2 [g / cm ³ ] or less is used. In the mold flux having a bulk specific gravity exceeding 1.2 [g / cm ³ ], since the drop energy per unit volume of addition is large, the bath surface of the molten layer 23 is greatly disturbed at the time of addition, or the power of the added mold flux Unmelted flux (a part of the unmelted layer 22) tends to sink into the melted layer 23. As a result, a sintered product having an unmelted inside is generated. Inside the sintered product, CO ₂ is generated by oxidation of C in the unmelted flux, so that the sintered product becomes large. Then, the enlarged sintered product adheres to the molten flux (slag rim), causing vertical cracks in the slab, slacking, and breakout during casting, resulting in surface defects in the product. Therefore, the bulk specific gravity of the mold flux (unmelted before addition) is set to 1.2 [g / cm ³ ] or less.

In addition, the bulk specific gravity of mold flux can be adjusted with the raw material to be used, the compounding rate of a raw material, and the granulation form. For example, when adjusting the raw material used and the mixing ratio of the raw materials, it can be adjusted by changing the silicon dioxide (SiO ₂ ) raw material, changing the calcium carbonate (CaCO ₃ ) raw material, using expansive graphite, or the like. Moreover, when adjusting with a granulation form, it can adjust by changing the particle shape, changing a binder kind , adjusting the water concentration in the slurry at the time of granulation, etc.

As described above, in this embodiment, a mold flux having a bulk specific gravity of 1.2 [g / cm ³ ] or less is used, and a mold flux layer (an unmelted layer 22 and a molten layer) having a predetermined thickness is used in the mold 2. 23), the mold flux is added by an appropriate method in consideration of the three requirements of the addition height H, the fall area A, and the supply speed Q. Thereby, since the influence of the disturbance of the molten layer 23 bath surface at the time of addition and the power of the added flux can be suppressed, the unmelted mold flux (a part of the unmelted layer 22) sinks into the molten layer 23. Can prevent over-sintering of the flux. Therefore, it is possible to prevent the occurrence of defects due to mold flux (slab vertical cracks, blades and breakouts) caused by oversintering, so that the quality of the product can be improved.

  Moreover, since generation | occurrence | production of a slab vertical crack and a blade can be suppressed, since the grinding process by the scarfing after a casting and a grinder can be abbreviate | omitted, a working cost can be reduced and a yield improvement can be aimed at. Moreover, since HCR operation becomes possible, delivery time can be shortened and the basic unit of the heating furnace can be reduced. In addition, if a breakout caused by slab vertical cracks or blades occurs, the operation will be stopped, causing a long pause due to restoration and equipment restoration costs, but it is possible to prevent the occurrence of breakout. , Loss of production machinery and equipment recovery costs can be prevented.

Here, an example of the casting conditions and the configuration of the continuous casting machine are shown below. The casting conditions and the configuration of the continuous casting machine are not limited to the conditions and configurations shown below, and can be changed. Moreover, although the feeder 3 is arrange | positioned above the casting_mold | template 2 in this embodiment, you may add a mold flux by another method, without using the feeder 3. FIG. Therefore, the feeder 3 may not be disposed above the mold 2.
-Steel component Carbon content [C]: 0.0015 [mass%] or more and 1.00 [mass%] or less-Specific water amount 0.15 [l / kg-steel] or more and 2.0 [l / kg-steel]・ Casting speed (steady state)
<Slab> 0.7 [m / min.] Or more and 2.4 [m / min.] Or less
<Bloom> 0.5 [m / min.] Or more and 0.9 [m / min.] Or less ・ Opening at the upper end of the mold (inner dimensions)
<Slab>
(Short side) 240 [mm] x (Long side) 800 [mm] to 1800 [mm]
(Short side) 280 [mm] x (Long side) 2100 [mm]
<Bloom>
(Short side) 380 [mm] x (Long side) 600 [mm]
・ Immersion nozzle
Inner diameter r: 60 [mm] or more 90 [mm] (see FIG. 1)
(However, the inner diameter r is the inner diameter of the portion where the discharge holes 11 and 12 are not formed.)
Inclination angle θ of discharge holes 11 and 12: 10 ° ≦ θ ≦ 45 ° (see FIG. 1)
(10 ° to 45 ° with respect to the horizontal direction, tilted downward)

  If the casting speed is too slow, 1) the molten steel 21 bath surface in the mold 2 is solidified, and 2) the melting of the mold flux is hindered by the above 1), and the melt flows between the slab and the mold. The shortage of mold flux causes problems such as seizure and slab vertical cracks. On the other hand, if the casting speed is too high, the bath surface of the molten steel 21 in the mold 2 is disturbed (disturbance not depending on the method of adding mold flux), and the thickness of the molten layer 23 is locally reduced. As a result, 1) Oversintering is likely to occur when mold flux is added, and 2) Insufficient flow of molten mold flux between the slab and mold tends to cause seizure and slab vertical cracking. Such problems arise. Therefore, the casting speed is preferably set to the normal speed as described above.

In the above-described embodiment, as shown in FIGS. 3 and 4, the fall area areas A _x , A _y , A ₁ , A ₂ , A ₃ ... Are all the same area. May be different. For example, during the movement of the feeder 3, each fall region area A can be made different by 1) changing the discharge speed discharged from the feeder 3, 2) changing the addition height H, and the like.

Furthermore, in the above-described embodiment, as illustrated in FIG. 4, the case where the maximum supply speed Q _{max in} all falling regions is 1760 [kg / (m ² · min.)] Is exemplified. Q _max may be less than 1760 [kg / (m ² · min.)], And the maximum supply speed Q _max of each drop region may be different. For example, 1) change the moving speed of the feeder 3, 2) change the falling area A, 3) make the falling area A constant and change the discharge speed from the feeder 3, etc. The speed Q _max can be a different speed.

  Moreover, in embodiment mentioned above, although the mold flux was continuously added using the feeder 3 (continuous movement type dispersion | distribution), you may add a mold flux without using the feeder 3. FIG. Below, the other addition method is demonstrated.

[Manual addition (spraying by batch method)]
Using a tool such as a scoop or a kite, a certain amount of mold flux is spread and dispersed in the mold 2. In this case, the “added height H” indicates a vertical distance from the position of the scoop or the soot at the time of addition to the unmelted layer 22 (bath surface). The “falling area A” indicates the area of the area in which the mold flux is dispersed on the unmelted layer 22 bath surface by a single addition. Further, the supply speed Q can be obtained by the following equation.
Supply rate Q = (addition amount per kg [kg]) ÷ (falling area area A [m ² ] at the time of addition) ÷ (from dropping start (addition start) to dropping end in one addition in the dropping area) Time [min.])

[Other addition methods]
Mold flux is stored at the upper end of the mold 2 or above the mold 2 and is extruded and added by a pusher or the like, or a predetermined amount is cut out using a shutter or the like. In this case, the “added height H” indicates the vertical distance from the mold flux storage position to the unmelted layer 22 (bath surface). For example, when the mold flux is stored at the upper end of the mold 2, the “added height H” indicates the vertical distance from the upper end of the mold 2 to the unmelted layer 22 (bath surface).

  Next, examples and comparative examples of the present invention will be described.

  The presence or absence of defects when the bulk specific gravity of the mold flux and the addition conditions of the mold flux were changed was examined.

  Tables 1 to 3 show execution conditions (casting conditions), experimental conditions (bulk specific gravity and addition conditions of mold flux), and experimental results (whether or not defects are generated). Table 4 shows steel components a to d in Tables 1 to 3, Table 5 shows slab sizes 1 to 4, and Table 6 shows representative components of mold flux brands α to ε.

  The implementation conditions, experimental conditions, and experimental results shown in Tables 1 to 3 will be described below.

[Conditions]
<During casting level level change>
When the relative position of the immersion nozzle and the meniscus is intentionally changed at regular intervals, Tables 1 to 3 show “execution”, and the case where the immersion nozzle and the meniscus are not changed are shown as “unimplemented”. In the “performed” experiment, the relative position of the immersion nozzle and the meniscus was changed by moving the immersion nozzle up and down or moving the meniscus position (molten steel bath surface) up and down. At this time, the change speed of the molten steel bath surface was set to 0.013 [mm / s] or more and 0.25 [mm / s]. Moreover, the bathing surface level was changed by 15 [mm] or more before and after the change.
<Electromagnetic stirring in mold>
The “magnetic field frequency” and “magnetic field strength” when the in-mold electromagnetic stirring device is operated are shown. In this example, “magnetic field frequency” and “magnetic field strength” are measured a plurality of times when the mold is empty, and an average value thereof is obtained, which are shown in Tables 1 to 3. The measurement (measurement point) of “magnetic field frequency” and “magnetic field strength” is as follows: 1) The horizontal position is 15 [mm] from the long side wall part and 15 [mm] from the short side wall part of the inner wall surface of the mold. 2) The vertical position was set at the same height as the iron core center of the electromagnetic coil installed outside the mold. Further, a Gauss meter (Tesla meter, magnetic flux density meter) was used for the measurement. Here, the “magnetic field frequency” is preferably 1 to 4 [Hz], and generally 2 to 3 [Hz] is adopted. Therefore, in this example, the frequency is uniformly 3 [Hz].

[Experimental conditions]
<Bulk specific gravity of mold flux>
The bulk specific gravity of the unmelted mold flux before addition was measured according to JIS-K5101.
<Melted layer thickness H _m , unmelted layer thickness H _u >
(1) As shown in FIG. 5, a representative point is a position that is 1/4 w away from the short side wall part and 1/2 t away from the long side wall part in the mold having an inner dimension of short side t × long side w. (For example, point P shown in FIG. 5), the “melted layer thickness” and “unmelted layer thickness” at this point were measured. In addition, in the implementation conditions of Tables 1 to 3, it is understood that the thickness (melted layer thickness and unmelted layer thickness) other than the measurement site can be controlled to a thickness equivalent to the measurement site based on the thickness of the measurement site (representative point). ing. Therefore, the thickness of the representative point was evaluated as the thickness in the entire mold.
(2) Further, in this example, after the casting speed becomes a steady speed, the thickness is measured at the initial stage of casting, the middle stage of casting, and the last stage of casting, and the average values thereof are “melted layer thickness H _m ” and “unmelted layer thickness”. H _u ”.
(3) Further, the thickness was measured by 1) immersing Al wire and iron wire or SUS wire, or 2) using an infrared sensor, a microwave meter, and a vortex meniscus level sensor.
Specifically, in 1), the tape 50 is wound around an Al wire and an iron wire or a SUS wire, and the portion below the wound position is immersed in the molten steel for a predetermined time as shown in FIG. 6 (a). (FIG. 6A illustrates an Al wire and a SUS wire). Here, the molten steel, the molten layer, and the unmolten layer in the mold have a higher temperature in this order, and the Al wire melts at the temperature of the molten steel and the molten layer, but does not melt at the temperature of the unmolten layer. On the other hand, iron wire or SUS wire melts at the temperature of the molten steel, but does not melt at the temperature of the molten layer and the unmelted layer. Alternatively, when a thick iron wire or SUS wire is immersed, the molten steel is solidified and adheres to these wires. Therefore, as shown in FIG. 6A, in the Al wire after immersion, the length l _u of the unmelted portion below the tape 50 is defined as “unmelted layer thickness”. Further, in the iron wire or SUS wire after immersion, the length l _{u + m} of the unmelted portion below the tape 50 was defined as “total of unmelted layer thickness and molten layer thickness”. Then, “melted layer thickness” was determined from “l _{u + m} −l _u ” (= total of unmelted layer thickness and molten layer thickness−unmelted layer thickness).
In 2), as shown in FIG. 6 (b), the distance L ₁ to the upper end of the unmelted layer by an infrared sensor, a microwave meter, and a vortex meniscus level sensor fixed at the same height position, The distance L ₂ to the upper end of the molten layer and the distance L ₃ to the upper end of the molten steel were measured, the unmelted layer thickness was determined from “L ₂ -L ₁ ”, and the molten layer thickness was determined from “L ₃ -L ₂ ”.
<Method of adding mold flux>
The case where the mold flux is added by the continuous moving spraying method (refer to the present embodiment) is “continuous”, and the case where the mold flux is manually added using a tool such as a scoop or a basket is called “batch”.
<Falling area A>
In the case of continuous movement type spraying ("continuous" in Tables 1 to 3), when adding while stopping the movement of the feeder, the maximum drop area area at the time of addition during the stop was defined as "fall area A". On the other hand, when added while moving the feeder, the fall area area at each time at the time of addition was defined as “fall area A”.
In addition, when manually added (“batch” in Tables 1 to 3), the area of the region dispersed in the mold by one addition was defined as “falling area A”.
Here, in this example, moving images were taken of the state of mold flux dropping, and the fall area A was calculated from image analysis. For some conditions (batch, etc.), the same conditions as in the mold were reproduced outside the mold, and the measured value in that area was defined as the fall area A.
<Supply speed Q>
The supply rate Q was calculated from the following formula.
Q = (Supply amount to drop area A [kg / min.]) ÷ (Drop area A [m ² ])
Here, “amount of supply to the fall area A” is “a drop speed at the time of continuous addition of mold flux” shown in Tables 1 to 3, and when the mold flux is discharged from the feeder as in the case of continuous moving spraying. Was obtained using the discharge rate of the mold flux from the feeder. In addition, when added manually ("Batch" in Tables 1 to 3), "Supply amount to fall area A" is obtained from "Input mass per kg [kg] ÷ Drop time [min.]" It was.

[Experimental result]
<Vertical cracking of slabs, Norokami>
After the slab was cooled to room temperature, the slab surface (wide surface and narrow surface) was ground by 1.5 [mm / surface] by scarfing or a grinder. Then, the surface of the cast slab after grinding is visually confirmed, and when there is no crack, “None” (evaluation: ◯) is shown in Tables 1 to 3, and when there is a crack, “Yes” (evaluation: X). Further, by visual confirmation, the case where no wolf is present is indicated as “none” (evaluation: ◯), and the case where a crack is present is indicated as “present” (evaluation: x).
Here, since the thickness range of 1.5 [mm] from the slab surface is the amount of scale loss generated in the heating-rolling process after casting, if there are no cracks deeper than this, product defects Does not occur. Therefore, in this example, the evaluation was made based on the thickness of 1.5 [mm] from the surface of the slab.
<Breakout>
When breakout occurs, Tables 1 to 3 indicate “Yes” (evaluation: ×), and when breakout does not occur, “No” (evaluation: ◯). The breakout that occurred in this example (comparative example) was caused by large vertical cracks and blades, and unsolidified molten steel flowed out of the defect site under the mold. In the evaluation, it was determined whether the breakout was caused by investigating whether the slab had vertical cracks or blades before the breakout occurred.

  Next, the results of Examples and Comparative Examples will be described.

  From Tables 1 and 2, in Examples 1 to 42, no vertical cracks and no scratches were observed in the slab. Also, no breakout occurred during casting. In Examples 11 and 33, the scab was present on the surface of the slab, but the scab was removed by carrying out the scarf.

On the other hand, in Comparative Examples 1 to 4, a mold flux having a bulk specific gravity exceeding 1.2 [g / cm ³ ] was used (1.3 [g / cm ³ ], 1.4 [g / cm ³ ]). Therefore, it is considered that vertical cracks occurred in the slab because the unmelted mold flux (a part of the unmelted layer) dipped into the melted layer and a sintered product was generated at the time of addition.

In Comparative Example 5-7, since the molten layer thickness H _m was less than 10 [mm] (5 [mm ], 9 [mm]), the molten layer becomes very hot. It is considered that an unmelted mold flux was entrained in such a molten layer, so that a sintered product was generated, and vertical cracks and slag were generated in the slab.

In Comparative Examples 8 to 10, since unmelted layer thickness H _u was thinner and less than 20 [mm] (15 [mm ], 19 [mm]), unmelted layer is sufficiently functions as a buffer material upon addition There wasn't. Therefore, it is considered that vertical cracks and breakout due to this occurred due to the unmelted mold flux entering into the molten layer and forming a sintered product at the time of addition.

  Moreover, in Comparative Examples 11-14, the addition height H of the mold flux exceeded 250 [mm], and the mold flux was added from a high position (255 [mm], 300 [mm]). For this reason, it is considered that vertical cracks and sags occurred due to the unmelted mold flux dipping into the molten layer during the addition and forming a sintered product.

Furthermore, in Comparative Examples 15 and 17, the fall area A was as small as less than 0.0025 [m ² ] (0.0020 [m ² ]). In Comparative Examples 16 and 18, the supply rate Q exceeded 1760 [kg / (m ² · min.)], And the supply rate Q was fast (1764 [kg / (m ² · min.)], 2000 [ kg / (m ² · min.)]). For this reason, it is considered that the unmelted mold flux dipped into the molten layer 23 at the time of addition, and that a sintered product was generated, thereby causing vertical cracks and stagnation.

Further, in Comparative Example 19, all the conditions of the bulk specific gravity of the mold flux, the molten layer thickness H _m , the unmelted layer thickness H _u , the addition height H, the drop region area A, and the supply speed Q are out of the scope of the present invention. This is an example. When added under such conditions, the unmelted mold flux sunk into the molten layer 23 to produce a sintered product, which caused vertical cracks, stagnation and breakout.

  From the above results, it was found that in the examples in which the mold flux was added by the addition method of the present invention, defects (defects in the product) caused by the mold flux such as vertical cracks, scents and breakouts could be prevented. On the other hand, when it added by the method which does not satisfy | fill one requirement of the addition method of this invention (comparative example), the defect resulting from a mold flux was not able to be prevented. That is, it has been found that oversintering of the flux cannot be prevented even if only one of the requirements of the addition method of the present invention is considered. Thus, when adding mold powder, even if only one of the requirements of the present invention is set to an appropriate range (even if the range of the present invention is satisfied), the cause of the defect remains, but the occurrence of the defect cannot be prevented. It has been found that defects can be prevented if all requirements are properly considered (within the scope of the present invention).

  As mentioned above, although embodiment of this invention was described based on drawing, it should be thought that a specific structure is not limited to these embodiment. The scope of the present invention is indicated not by the above description but by the scope of claims, and includes all modifications within the meaning and scope equivalent to the scope of claims.

  For example, the casting conditions and the configuration of the continuous casting machine described above are examples, and the conditions and the configuration can be changed. Moreover, the addition method of the present invention can be applied to the casting of steels of various steel types and shapes (slabs, blooms, billets, etc.). For steel types for thin plate products, steel types for thick plates, and steel types for filaments, etc. It can be suitably applied.

  In addition, when the mold flux is continuously added (continuous movement type spraying), the operation (trajectory) of the feeder, the position and number of feeders, etc. are not limited to the present embodiment or the examples shown in FIGS. Is possible.

  Since this invention can improve the quality of a product by preventing generation | occurrence | production of the defect resulting from a mold flux, it can utilize for continuous casting of steel.

DESCRIPTION OF SYMBOLS 1 Immersion nozzle 2 Mold 3 Feeder 11, 12 Discharge hole 21 Molten steel 22 Unmelted layer 23 Molten layer (molten mold flux)
50 tape 100 continuous casting machine

Claims (2)

The mold flux from the feeder while moving the feeder Upon the addition into the mold to continuously cast steel,
When casting the slab, the casting speed is 0.7 [m / min.] Or more and 2.4 [m / min.] Or less,
When casting bloom, the casting speed is 0.5 [m / min.] Or more and 0.9 [m / min.] Or less,
The bulk specific gravity of the mold flux before addition is 1.2 g / cm ³ or less, the viscosity is 0.05 to 0.24 Pa · s,
The molten mold flux thickness on the molten steel bath surface in the mold is 10 mm or more and 20 mm or less ,
The unmelted layer thickness on the molten mold flux is 20 mm or more and 60 mm or less ,
The fall distance from the drop start position where the mold flux is freely dropped to the unmelted layer is 250 mm or less,
Mold is cast into the mold while the flux falling area is 0.0025 m ² or more and 0.0201 m ² or less at each time when the mold flux is added, and the mold flux supply speed in the dropping area is 1760 kg / (m ² · min.) Or less. A method of adding mold flux to a continuous casting mold, comprising adding flux. In continuous casting of steel by adding mold flux into the mold with the addition height and addition position fixed,
When casting the slab, the casting speed is 0.7 [m / min.] Or more and 2.4 [m / min.] Or less,
When casting bloom, the casting speed is 0.5 [m / min.] Or more and 0.9 [m / min.] Or less,
The bulk specific gravity of the mold flux before addition is 1.2 g / cm ^Three The viscosity is set to 0.05 to 0.24 Pa · s,
The molten mold flux thickness on the molten steel bath surface in the mold is 10 mm or more and 20 mm or less,
The unmelted layer thickness on the molten mold flux is 20 mm or more and 60 mm or less,
The fall distance from the drop start position where the mold flux is freely dropped to the unmelted layer is 250 mm or less,
0.0025m of flux fall area when mold flux is added ² 0.0201m ² The mold flux supply rate in the falling region is 1760 kg / (m ² Min.) A method for adding mold flux to a continuous casting mold, wherein the mold flux is added into the mold while maintaining the following.