JP5846540B2 - 窒化鉄粉末の製造方法 - Google Patents
窒化鉄粉末の製造方法 Download PDFInfo
- Publication number
- JP5846540B2 JP5846540B2 JP2011150472A JP2011150472A JP5846540B2 JP 5846540 B2 JP5846540 B2 JP 5846540B2 JP 2011150472 A JP2011150472 A JP 2011150472A JP 2011150472 A JP2011150472 A JP 2011150472A JP 5846540 B2 JP5846540 B2 JP 5846540B2
- Authority
- JP
- Japan
- Prior art keywords
- iron
- powder
- acid
- iron nitride
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
乾燥工程:上記ゲルを乾燥して乾燥体を作製する工程。
分離工程:上記乾燥体中の有機成分を除去して前駆体を作製する工程。
還元・窒化工程:上記前駆体に還元処理及び窒化処理を順次施して窒化鉄粒子を生成する工程。
[窒化鉄粉末の製造方法]
(準備工程)
<鉄粉>
原料として、純鉄(Fe含有量:99.99質量%以上)からなる鉄粉を用意する。鉄粉は、種々の形態のものが利用でき、例えば、還元鉄粉、鉄繊維、鋳鉄粉、海綿状鉄粉などが挙げられる。列挙したいずれの鉄粉も比較的安価で市販されており、容易に入手可能である上に、コストの低減も図れる。複数の異なる形態の鉄粉を組み合せて用いてもよい。
本発明では、上記鉄粉を用いて、鉄錯体を含有するゲルを生成するにあたり、カルボン酸を利用する。カルボン酸は、弱酸であることから、カルボン酸溶液に鉄粉を混合すると、原料鉄粒子と穏やかに反応でき、かつキレート作用を有することから、原料鉄粒子の表面から内部に至って反応を進行でき、最終的に鉄錯体を生成できる。従って、強酸を用いる場合と異なり、カルボン酸を用いる本発明製造方法は、鉄粉と酸とを完全に反応させることができる。また、鉄錯体から酸化鉄粒子を生成することで、ナノオーダーといった微細な粒子を生成し易く、このような微粒子を出発材料とすることで、結果として、ナノオーダーといった微細な窒化鉄粒子を得易い。
ゲルは、溶媒の水などを含んだ湿潤状態である。そこで、乾燥工程では、主としてゲルから水を除去する。乾燥は、所定の温度に保持した熱処理炉にゲルを載置して排気しながら行うと、水のみを効率よく除去できる。乾燥条件は、温度:100℃〜150℃、保持時間:3時間〜12時間が挙げられる。乾燥工程の雰囲気は、大気雰囲気、真空雰囲気、窒素雰囲気が挙げられる。
乾燥工程を経て、鉄錯体を含有する乾燥体は、カルボン酸の有機成分を含んだ状態である。そこで、分離工程では、主として有機成分(錯体)を除去して、鉄錯体を酸化鉄(ヘマタイト:Fe2O3)にする。有機成分の除去は、所定の温度に保持した熱処理炉に乾燥体を載置して排気しながら行うと、有機成分のみを効率よく除去できる。分離条件は、温度:300℃〜500℃、保持時間:1時間〜5時間が挙げられる。分離工程の雰囲気は、大気雰囲気、アルゴン雰囲気、窒素雰囲気が挙げられる。
分離工程で生成された酸化鉄粒子:前駆体に熱処理を施して、当該酸化鉄粒子から窒化鉄粒子を生成する。まず、還元を行って、鉄粒子(実質的にα-Feから構成される粒子)を生成し、次に窒化を行って、窒化鉄粒子(実質的にα"Fe16N2から構成される粒子)を生成する。上述のように酸化鉄粒子がナノオーダーで、アスペクト比が大きな粒子であると、最終的にナノオーダーで、アスペクト比が大きな窒化鉄粒子を得易く、磁気特性に優れる窒化鉄粉末が得られる。
本発明窒化鉄粉末を構成する各窒化鉄粒子は、実質的にα"Fe16N2からなる(99.5体積%以上)とする。窒化鉄粒子は、細長い針状の形状であり、短軸の長さに対する長軸の長さの比:アスペクト比が大きい。具体的には、短軸を1とするとき、長軸が10以上である形態(短軸:長軸=1:10以上)が挙げられる。アスペクト比が大きいほど、形状磁気異方性に優れる。ここで、窒化鉄粒子のアスペクト比は、鉄粒子のアスペクト比に起因し、鉄粒子のアスペクト比が大き過ぎると、窒化鉄の生成が阻害される。そのため、窒化鉄粒子の短軸を1とするとき、長軸が20以下である形態(短軸:長軸=1:20以下)が好ましい。アスペクト比は、カルボン酸の種類・モル比、鉄粉の粒径、印加する磁場の大きさなどを調整することで変化させられる。磁場が大きいほど、アスペクト比が大きくなる傾向にある。
この試験では、ゲルの作製にあたり、溶液の温度を変化させた。
この試験では、ゲルの作製にあたり、鉄粉の大きさを変化させた。
この試験では、ゲルの作製にあたり、鉄粉とカルボン酸とのモル比を変化させた。
この試験では、ゲルの作製にあたり、鉄粉とカルボン酸溶液との混合溶液のpHを変化させた。
この試験では、ゲルの作製にあたり、他の試験例とは別のカルボン酸を用いた。また、比較として、ゲルの作製にあたり、硝酸鉄を用いた試料を作製した。
Claims (7)
- 磁場を印加した状態で鉄粉をカルボン酸溶液中で溶解してゲルを作製する準備工程と、
前記ゲルを乾燥して乾燥体を作製する乾燥工程と、
前記乾燥体中の有機成分を除去して前駆体を作製する分離工程と、
前記前駆体に還元処理及び窒化処理を順次施して窒化鉄粒子を生成する還元・窒化工程とを具える窒化鉄粉末の製造方法。 - 前記鉄粉の平均粒径が1μm以上100μm以下である請求項1に記載の窒化鉄粉末の製造方法。
- 前記カルボン酸は、クエン酸、リンゴ酸、酒石酸、マロン酸、フタル酸、コハク酸、マレイン酸、及びグルコン酸からなる群から選択された1種以上である請求項1又は請求項2に記載の窒化鉄粉末の製造方法。
- 前記鉄粉は、還元鉄粉、鉄繊維、及び鋳鉄粉からなる群から選択された1種以上である請求項1〜請求項3のいずれか1項に記載の窒化鉄粉末の製造方法。
- 前記鉄粉のモル数と前記カルボン酸のモル数との比率を鉄:カルボン酸=1:3〜1:10とする請求項1〜請求項4のいずれか1項に記載の窒化鉄粉末の製造方法。
- 前記準備工程では、前記鉄粉と前記カルボン酸溶液との混合溶液の温度を50℃以上100℃以下、前記混合溶液のpHを1以上5以下として、前記ゲルを作製する請求項1〜請求項5のいずれか1項に記載の窒化鉄粉末の製造方法。
- 前記準備工程では、3T以上の磁場を印加する請求項1〜請求項6のいずれか1項に記載の窒化鉄粉末の製造方法。