JP5810798B2 - Hydraulic transfer film and method for producing decorative molded product using the same - Google Patents

Description

  The present invention relates to a hydraulic transfer film suitable for forming a transfer layer on the surface of a molded body having a three-dimensional surface or a curved surface due to unevenness, and a method for producing a decorative molded product using the same.

For automobile interior parts, home appliances, office automation equipment, and the like, molded products having decorations such as wood grain or metallic tone (metallic luster) on the surface are used. Many of these molded products have a complicated three-dimensional shape, and conventionally, a method for simply applying a decoration having a high design property to a molded product having a complicated shape has been studied.
As such a decoration method, a water pressure transfer method using water pressure is known. In the hydraulic transfer method, a transfer film in which a desired decorative layer is printed on a water-soluble or water-swellable water-soluble film is prepared, and an activator composition composed of an organic solvent is applied to the decorative layer of the transfer film. Swell and stick the decorative layer (this is called activation). Before or after that, the transfer film is floated on the water surface with the decorative layer (printing layer) surface for transfer as the upper surface, and then the article to be transferred is pressed onto the transfer film by water pressure. After the transfer film is brought into intimate contact with the transfer surface of the transfer object to be decorated, the water-soluble film is removed and the decoration layer is transferred (see, for example, Patent Document 1).

  The water pressure transfer method is a curved surface decoration method that is excellent in terms of “depth” such as a clear paint feeling, adaptability to three-dimensional surfaces, and high-quality pattern expression. Attempts have been made to add superiority and impart a superior sense of quality. For example, in Patent Document 2, in order to form a printed pattern layer exhibiting a pearly feeling, glass fibers are added in advance to a synthetic resin molding that is a transfer target, and printing is performed on the surface of the synthetic resin molding by a hydraulic transfer method. It has been proposed to transfer the pattern layer. However, in this method, the material of the synthetic resin molded body is limited, and the production of the synthetic resin molded body is complicated.

In order to solve the above problems, Patent Document 3 attempts to improve the hydraulic transfer sheet, and comprises a nitrified cotton / alkyd transparent resin layer on a water-soluble film, and a deposited metal layer on the transparent resin layer, There has been proposed a hydraulic transfer sheet in which the transparent resin layer is embossed between a vapor-deposited metal layer and the transparent resin layer.
However, the vapor-deposited metal layer has an excellent property that a metallic design with high glitter can be obtained, but when the transparent resin layer of the hydraulic transfer sheet is swollen, it does not extend in the same manner as the transparent resin layer. However, there was a problem that non-uniform cracks (cracks) were generated, and on the contrary, the beauty was impaired. In addition, by providing a vapor-deposited metal layer, a high metallic design can be obtained, but it is difficult to adjust the metallic tone to express a calm metallic tone, that is, a design with an appropriate glossiness. There was also a problem that it was not possible to sufficiently meet the diversifying consumer preferences.

JP 54-33115 A JP-A-4-107182 JP 2001-328398 A

  Under such circumstances, the present invention provides a hydraulic transfer film having a metal thin film layer, imparting an appropriate gloss to the transfer target, and having good blocking properties, and decorative molding using the film The issue is to provide products with high productivity.

As a result of intensive studies to solve the above problems, the present inventors have obtained the following knowledge.
A water-soluble film, a transfer adjustment layer on the water-soluble film, and a metal thin film layer on the transfer adjustment layer, and the transfer adjustment layer is a resin constituting the layer, preferably a polyvinylpyrrolidone resin. On the other hand, the above-mentioned problem can be solved by a hydraulic transfer film containing fine particles at a specific ratio, and the hydraulic transfer film hardly generates blocking, that is, the blocking property is good. It has been found that a decorative molded product having a calm metal tone, that is, an appropriate glossiness can be obtained with a high productivity by passing through a specific process. The present invention has been completed based on such findings.

That is, the present invention
[1] A hydraulic transfer film having a water-soluble film, a transfer adjusting layer on the water-soluble film, and a metal thin film layer on the transfer adjusting layer, wherein the transfer adjusting layer contains fine particles and the transfer adjusting layer. And a decoration using the hydraulic transfer film according to [2] above, wherein the content is greater than 0% and less than 2.0% by mass with respect to the resin constituting A method of manufacturing a molded article,
Step (a): an activator composition application step for applying the activator composition to the metal thin film layer before or after floating on the water surface so that the water-soluble film side of the hydraulic transfer film faces downward and toward the water surface side,
Step (b): a step of pressing the transferred material against the hydraulic transfer film that has undergone the above step (a), and causing the metal thin film layer to adhere to the transferred surface of the transferred material by water pressure, and step (c): the transferred material A film removal process for removing the water-soluble film and the transfer adjustment layer which are in close contact with the transfer surface of the transfer body;
A method for producing a decorative molded product, characterized in that
Is to provide.

  According to the present invention, a hydraulic transfer film having a metal thin film layer, imparting an appropriate gloss feeling to a transfer target, and having a good blocking property, and a decorative molded product using the film with high productivity. Can be provided.

It is a schematic sectional drawing which shows an example of a structure of the hydraulic transfer film of this invention.

Hereinafter, the present invention will be described with reference to the drawings. FIG. 1 is a schematic cross-sectional view showing an example of the configuration of the hydraulic transfer film of the present invention.
The hydraulic transfer film 1 of the present invention is a hydraulic transfer film having a water-soluble film 2, a transfer adjustment layer 3 on the water-soluble film 2, and a metal thin film layer 4 on the transfer adjustment layer 3. It is characterized by containing fine particles in a proportion of more than 0% and less than 2.0% by mass with respect to the resin constituting the layer.

[Water-soluble film]
The water-soluble film according to the present invention may be any water-soluble or water-swellable film, and can be appropriately selected from water-soluble films generally used as a conventional hydraulic transfer film.
Examples of the resin constituting the water-soluble film include polyvinyl alcohol resin, dextrin, gelatin, glue, casein, shellac, gum arabic, starch, protein, polyacrylamide, sodium polyacrylate, polyvinyl methyl ether, and methyl vinyl ether. Examples thereof include various water-soluble polymers such as a copolymer with maleic anhydride, a copolymer of vinyl acetate and itaconic acid, polyvinyl pyrrolidone, acetyl cellulose, acetyl butyl cellulose, carboxymethyl cellulose, methyl cellulose, hydroxyethyl cellulose, and sodium alginate.
These resins may be used alone or in combination of two or more. In addition, rubber components, such as mannan, xanthan gum, and guar gum, may be added to the water-soluble film.

Among the above water-soluble films, polyvinyl alcohol (PVA) resin films are particularly preferable from the viewpoints of production stability, solubility in water and economy. In addition, the polyvinyl alcohol-type resin film may contain additives, such as starch and rubber | gum, besides PVA.
When a polyvinyl alcohol-based resin film forms a printing layer for transfer on a water-soluble film by changing the polymerization degree of polyvinyl alcohol, the degree of saponification, and the blending amount of additives such as starch and rubber. Adjust the required mechanical strength, moisture resistance during handling, speed of softening by water absorption after floating on the water surface, time required for spreading or spreading in water, ease of deformation in the transfer process, etc. Can do.

A suitable water-soluble film comprising a polyvinyl alcohol-based resin film is the one described in JP-A-54-92406, for example, 80% by mass of PVA resin, 15% by mass of polymer water-soluble resin. %, 5% by mass starch, and about 3% by mass equilibrium water content is preferred.
The polyvinyl alcohol-based resin film is water-soluble, but preferably remains as a film while being swollen and softened in the water before being dissolved in water. This is because, by performing the hydraulic transfer while the film is still alive, it is possible to prevent an excessive flow and deformation of the printing layer for transfer during the hydraulic transfer.

  As thickness of the water-soluble film 2, 10-100 micrometers is preferable. When it is 10 μm or more, the uniformity of the film is good and the production stability is high. On the other hand, when it is 100 μm or less, the solubility in water is moderate and the printability is excellent. From the above viewpoint, the thickness of the water-soluble film is more preferably in the range of 20 to 60 μm.

  The water-soluble film can be used by being laminated with a water-permeable base material such as paper, non-woven fabric, cloth, etc., but such a water-permeable base material and water-soluble or water are used. When laminating a water-soluble film having swellability, the substrate having water permeability is separated from the water-soluble or water-swellable film before the hydraulic transfer film floats on the water surface, It is preferable that the water-permeable substrate is separated from the water-soluble or water-swellable water-soluble film by the action of water after floating.

[Transfer adjustment layer]
The transfer adjustment layer 3 according to the present invention swells at an appropriate speed and in an appropriate range at the time of hydraulic transfer, and does not cause nonuniform cracks in the metal thin film layer 4. It is an indispensable layer provided for generating cracks). As the resin constituting the transfer adjustment layer 3, any resin that can exhibit the function of the transfer adjustment layer as described above can be used without particular limitation, and among them, a polyvinylpyrrolidone resin is preferable. . The resin constituting the transfer adjustment layer 3 may be composed of a polyvinyl pyrrolidone resin alone, or may be a resin mixture containing a polyvinyl pyrrolidone resin. In the resin mixture, the effect of using the polyvinyl pyrrolidone resin, That is, it is preferable that an amount capable of exhibiting the function of the transfer adjustment layer is included, and it is preferable that the transfer adjustment layer is included as a main component.
The polyvinyl pyrrolidone resin is a polymer compound in which N-vinyl-2-pyrrolidone is polymerized, dissolves in water, and has good water swellability. By using this polyvinyl pyrrolidone resin, the transfer adjustment layer 3 swells at an appropriate speed and in an appropriate range at the time of hydraulic transfer, so that the metal thin film layer 4 is less likely to crack non-uniformly and has a uniform fineness. Cracks are generated, transferability is improved, and addition of fine particles, which will be described later, provides an appropriate gloss feeling in addition to transferability.
In addition, since the polyvinyl pyrrolidone resin does not swell too quickly, the hydraulic transfer film is floated on the surface of the water, and then transferred to the transfer target after securing an appropriate time in the activator application step (a) described later. can do.

(Fine particles)
In the hydraulic transfer film of the present invention, in order to impart an appropriate gloss feeling to the decorative molded product formed using the hydraulic transfer film and to suppress blocking properties, the transfer adjustment layer is composed of it. It is necessary to contain fine particles in a proportion of more than 0% and less than 2.0% by mass with respect to the resin to be used.
When the content of the fine particles is 0%, that is, when the fine particles are not contained, the blocking suppressing effect is not exerted, the productivity of the decorative molded product is lowered, and the metallic product is too high in quality. Cannot be obtained. On the other hand, in the case of 2.0% by mass or more, the gloss feeling is lowered and the matte feeling becomes strong, and the design property is lowered. From such a viewpoint, the preferable content of the fine particles is 0.15 to 1.5% by mass.

The average particle diameter of the fine particles is preferably about 1 to 10 μm, and more preferably 1 to 5 μm, from the viewpoint of an appropriate gloss feeling imparting effect and blocking suppression effect. When the average particle size is within the above range, a moderate gloss feeling imparting effect and a blocking suppression effect are sufficiently exhibited. Here, the average particle diameter of the fine particles contained in the transfer adjustment layer is a value measured by observation with a SEM (scanning electron microscope).
The content of fine particles and the average particle size may be appropriately selected according to the desired gloss feeling.

The material of the fine particles is not particularly limited as long as it has an appropriate gloss feeling imparting effect and blocking suppression effect, and various inorganic fine particles and organic fine particles can be used.
Examples of the inorganic fine particles include silica fine particles (particles obtained by a wet method and a dry method), titania fine particles, zirconia fine particles, and the like. Examples of the organic fine particles include silicone fine particles, melamine resin fine particles, and acrylic resin fine particles (for example, polycrystal fine particles). Methyl methacrylate fine particles), polycarbonate fine particles, benzoguanamine resin fine particles and the like.
These inorganic fine particles and organic fine particles may be used singly or in combination of two or more, but silica fine particles are preferred from the viewpoints of effects and economy.

  The thickness of the transfer adjustment layer 3 containing these fine particles is preferably about 0.5 to 20 μm, more preferably 1 to 10 μm. If the thickness of the transfer adjustment layer is in this range, fine cracks (cracks) are more uniformly generated in the metal thin film layer 4, and a more suitable time for the activator application step (a) is ensured. It can be transferred to a transfer target. From these viewpoints, 1 to 6 μm is particularly preferable.

  Further, the transfer adjustment layer 3 can be provided with a concavo-convex pattern on the metal thin film layer side by a method such as embossing as necessary in order to further improve the design of the decorative molded product.

[Metal thin film layer]
The metal thin film layer 4 is an indispensable layer in the hydraulic transfer film of the present invention, and is a layer that imparts a glossy design to the transfer object in combination with the transfer adjustment layer 3 described above. In the present invention, the metal thin film layer 4 alone is too metallic, but when combined with the transfer adjustment layer 3 described above, a moderate gloss feeling that is a calm metallic tone can be obtained.
The metal thin film layer 4 is preferably formed by a vapor-deposited metal thin film formed by vapor deposition of a metal material, a thin film obtained by coating a paste composition containing metal powder, or the like. In order to obtain a more appropriate gloss feeling, it is preferable to employ a vapor deposited metal thin film.
As the metal forming the metal thin film layer 4, for example, a metal such as aluminum, chromium, nickel, cobalt, copper, gold, silver, tin, zinc, brass, stainless steel, an alloy, a metal oxide, or the like can be used. . Examples of the metal oxide include aluminum oxide and silicon dioxide. Of these, aluminum is preferable from the viewpoint of uniformly generating cracks.
The thickness of the metal thin film layer 4 is usually preferably 10 to 80 nm, and more preferably 20 to 60 nm. When the thickness of the metal thin film layer 4 is within the above range, a fine crack having a crack width of 1 to 120 μm can be uniformly generated.

[Picture printing layer]
In the hydraulic transfer film of the present invention, a pattern printing layer (not shown) can be provided between the transfer adjustment layer 3 and the metal thin film layer 4 as desired for the purpose of improving the design of the transfer target.
It is preferable to use the same resin as the transfer adjustment layer 3 as the binder resin of the pattern printing layer. As the colorant, those conventionally used are used.

[Method for producing hydraulic transfer film]
The method for producing the hydraulic transfer film 1 of the present invention includes, for example, a step (A) of laminating a transfer adjustment layer 3 preferably containing a polyvinylpyrrolidone resin on a water-soluble film 2 and a metal thin film on the surface of the transfer adjustment layer 3. A method including the step (B) of forming the layer 4 is preferable.

In step (A), the transfer adjustment layer 3 is laminated on the water-soluble film 2 by laminating a known coating method or printing method, co-extrusion method with a water-soluble film, or resin film on the water-soluble film 2. Is done. Known coating methods include gravure coating, reverse coating and the like, and known printing methods include gravure printing and the like.
Moreover, before providing the metal thin film layer 4, in order to raise the designability of a decorative molded product more, an uneven | corrugated pattern can be given to the transcription | transfer adjustment layer 3 as needed. The uneven pattern may be applied by a conventionally performed method such as embossing.

In the step (B), the metal thin film layer 4 is preferably formed by a known metal vapor deposition method such as vacuum vapor deposition, sputtering, or ion plating.
Moreover, you may provide the process (C) which provides a pattern printing layer between a process (A) and a process (B) if desired. However, when the step (C) is provided, after the step (C), the surface of the pattern printing layer is smoothed by, for example, subjecting the surface of the pattern printing layer to hot pressing or passing through a smoothing roll. It is desirable.

[Method of manufacturing decorative molded product]
Next, the manufacturing method of the decorative molded product of this invention is demonstrated.
The manufacturing method of the decorative molded product of the present invention is characterized in that it has the following steps (a), (b), and (c) in order, and further includes a step (d) as necessary.

(Process (a))
Step (a) is an activator composition in which the activator composition is applied to the metal thin film layer 4 before or after floating on the water surface so that the water-soluble film 2 side of the hydraulic transfer film 1 of the present invention faces the water surface side. It is a coating process. In this step, by applying an activator to the metal thin film layer 4, the surface of the metal thin film layer 4 is roughened, and the metal thin film layer 4 easily adheres to the transfer target. It floats on the water surface so that the water-soluble film 2 side of the hydraulic transfer film 1 faces the water surface side. In order to float the hydraulic transfer film 1 on the surface of the water, it is possible to float the printed matter one by one. Alternatively, the water is flowed in one direction, and a continuous belt-like hydraulic transfer film is continuously supplied on the surface of the water. And may be suspended.

(Activator composition)
The activator composition is not particularly limited as long as it is a composition that can roughen the metal thin film layer 4 for transfer in the hydraulic transfer film 1 and has a function of dissolving the surface of the transfer target described later, It is preferable that the metal thin film layer 4 does not evaporate until the metal thin film layer 4 is transferred to the transfer surface of the transfer target. As such an activator composition, the composition containing ester, acetylene glycol, ethers, and resin is mentioned preferably, for example.
Preferred examples of esters include ethyl acetate, propyl acetate, butyl acetate, isobutyl acetate, sec-butyl acetate, tert-butyl acetate, dibutyl oxalate, dibutyl phthalate, dimethyl phthalate, dioctyl phthalate, and diisooctyl phthalate. It is done.
Preferred examples of acetylene glycols include methoxybutyl acetate, ethoxybutyl acetate, ethyl carbitol acetate, propyl carbitol acetate, and butyl carbitol acetate.
Preferred examples of ethers include methyl cellosolve, butyl cellosolve, and isoamyl cellosolve.
In addition, as resins, thermoplastic resins such as acrylate monomers alone or copolymers, polyamide resins, polyester resins, phenol resins, melamine resins, urea resins, epoxy resins, alkyd phthalate resins, diallyl phthalates Preferred examples include thermosetting resins such as resins, alkyd resins, and polyurethane resins, and among these, thermosetting resins are preferred.
The content of each preferable composition of the activator composition used in the present invention is 5 to 40% by mass for esters, 40 to 80% by mass for acetylene glycols, 5 to 30% by mass for ethers, and 1 for resin. About 20% by mass.

The activator composition may be applied by spray coating or the like, and the application amount is usually 1 to 50 g / m ² , preferably 3 to 30 g / m ² , more preferably 10 to ²⁰ g / m ^{2. 2} .

(Process (b))
The step (b) is a step of pressing the transferred body onto the hydraulic transfer film 1 that has undergone the step (a) and bringing the metal thin film layer 4 into close contact with the transferred surface of the transferred body by water pressure.
The water for applying the floating water pressure to the hydraulic transfer film 1 should be adjusted to an appropriate water temperature according to the type of the water-soluble film 2 of the hydraulic transfer film 1, and preferably about 25 to 50 ° C. Preferably it is 25-35 degreeC.
The transfer time between the hydraulic transfer film 1 of the present invention and the transfer target is preferably about 20 to 120 seconds, more preferably about 30 to 60 seconds. In order to widen the crack width, the application amount may be increased, the water temperature may be increased, and the transfer time may be increased. Here, the transfer time is the time from when the transfer film 1 of the present invention is suspended in water until the transfer to the transfer target is completed.

(Transfer material)
Examples of the transfer object used in the present invention include polystyrene resin, acrylonitrile-butadiene-styrene copolymer (ABS resin), polycarbonate resin, melamine resin, phenol resin, urea resin, fiber resin, polyethylene, and polypropylene. In addition to a resin or a resin obtained by mixing these, a structure made of a material such as a metal such as iron, aluminum, or copper, ceramics such as ceramics, glass, or wood, or wood can be used.
In addition, the shape of the transfer surface may be a two-dimensional shape that is a planar shape, or may be a three-dimensional shape such as an uneven shape or a curved shape. Of these, resin structures are usually used frequently. In the resin structure, a mold release agent adheres at the time of molding, and dust and fat may also adhere. In order to transfer the printing layer of the hydraulic transfer film with good adhesion, the resin structure is previously coated with a degreasing liquid. It is preferable to clean the transfer surface.

  In the step (b), the activator composition applied on the metal thin film layer 4 is in contact with the transferred body, and the surface of the transferred body is dissolved, so that the transfer film 1 of the present invention and the transferred body are adhered. The property is good.

(Film removal step (c))
The film removal step (c) is a step of removing the water-soluble film 2 and the transfer adjustment layer 3 that are in close contact with the transfer surface of the transfer target.
The removal of the water-soluble film 2 and the transfer adjusting layer 3 can be performed by, for example, shower cleaning using water. By this step (c), the water-soluble film 2 and the transfer adjustment layer 3 attached to the transfer surface are removed. The shower cleaning conditions vary depending on the material for forming the water-soluble film 2 and the transfer adjustment layer 3, but usually a water temperature of about 15 to 60 ° C. and a cleaning time of about 10 seconds to 5 minutes are preferable. Then, after the step (c), if the transferred body is sufficiently dried and moisture is evaporated, the decorative molding to which a desired design is given by the metal thin film layer 4 transferred to the transferred surface of the transferred body Goods are obtained.

(Process (d))
Step (d) is a step of forming a protective film as desired on the transferred metal thin film layer 4.
In the step (d), the metal thin film layer 4 transferred to the transfer surface of the transfer object in the step (c) is coated as necessary for improving the surface strength, protecting the surface, adjusting the surface gloss, etc. Can be applied to form a protective film. The protective film is formed of a resin composition containing, for example, a thermoplastic resin, a thermosetting resin, an ultraviolet curable resin, specifically, a urethane resin, an epoxy resin, an acrylic resin, a fluororesin, a silicon resin, or the like. Is preferred.

  The protective film can be formed by coating and curing these resin compositions. As a coating method, known methods such as spray coating, electrostatic coating, brush coating, and dip coating can be used. Moreover, what is necessary is just to select suitably as the method of hardening with the resin composition to be used, and when using a thermoplastic resin, it should just cure for several days. On the other hand, heat treatment may be performed when a thermosetting resin is used, and irradiation with appropriate ultraviolet light may be performed when an ultraviolet curable resin is used.

The decorative molded product thus obtained has a fine crack (crack) of 1 to 120 μm as a crack (crack) width on the surface thereof, that is, the metal thin film layer, and therefore has good transferability.
In order to uniformly generate a fine crack (crack) of 1 to 120 μm as a crack (crack) width at the time of transfer and adjust the crack (crack) width, the selection of the resin for forming the transfer adjustment layer 3 and its This can be done by selecting the thickness and the thickness of the metal thin film layer 4. For example, in order to increase the crack width, the thickness of the metal thin film layer 4 may be increased, and the thickness of the transfer adjustment layer 3 may be increased.

  The crack width is also adjusted by various conditions of the hydraulic transfer method, for example, the coating amount of the activator composition, the temperature of the water in which the hydraulic transfer film 1 is suspended, the transfer time between the film 1 and the transfer target. Can do. For example, if the application amount of the activator composition is increased, the crack width tends to increase, and if the temperature of water is increased, the crack width tends to increase, and if the transfer time is increased, the crack width tends to increase. .

  Since the decorative molded product of the present invention is obtained using the hydraulic transfer film of the present invention, it has an appropriate gloss feeling, and since it uses a hydraulic transfer film having good blocking properties, it is manufactured with high productivity. can do. Furthermore, a preferable embodiment of the transfer adjustment layer of the hydraulic transfer film, that is, by adopting a polyvinylpyrrolidone resin as a resin constituting the transfer adjustment layer, non-uniform cracks (cracks) hardly occur in the metal thin film layer during the hydraulic transfer, Since the transferability is good, the decorative molded product of the present invention has a more excellent design.

EXAMPLES Next, although an Example demonstrates this invention further in detail, this invention is not limited at all by these examples.
In addition, the performance evaluation shown below was performed about the decorative molded product using the hydraulic transfer film obtained in each case.

(1) 60 ° specular gloss (evaluation of gloss feeling)
For decorative molded products, measure the 60 ° specular gloss (60 ° gloss value) in accordance with JIS K 5400 using a gloss meter (manufactured by BYK Gardner, model name “Micro Gloss”), and determine the following: The gloss feeling was evaluated by the standard.
○: 60 ° gloss value is 150 or more and less than 180 Δ: 60 ° gloss value is 100 or more and less than 150, or 180 or more and less than 200 ×: 60 ° gloss value is 200 or more or less than 100

(2) Cracked state of the metal thin film layer The surface state of the decorative molded product was observed with a microscope at a magnification of 100 times and evaluated according to the following criteria.
<Evaluation criteria>
(Double-circle): It was a very uniform fine crack.
A: Almost uniform and fine cracks.
(Triangle | delta): Although it was a fine crack, the magnitude | size was nonuniform.
X: Large cracks occurred.

(3) Transferability The surface state of the decorative molded product obtained after the film removal step (c) was visually observed and evaluated according to the following criteria.
○: The uneven pattern is uniformly transferred, and there is no distortion of the pattern.
Δ: Pattern distortion occurred in part of the transferred concavo-convex pattern.
X: Most of the transferred concavo-convex pattern had pattern distortion. Alternatively, the metal thin film layer did not extend and could not be transferred.

(4) Blocking property of decorative molded product Two films obtained by providing a transfer adjustment layer on a water-soluble film were stacked and allowed to stand for 2 days (40 ° C., 4 kg / cm ² load), and then evaluated according to the following criteria: did.
A: The film was easily peeled off. ○: Although the film was peeled off, a slight tack feeling was felt. X: A remarkable tack feeling was felt.

(5) Printability of resin composition for forming transfer adjustment layer The drying rate of the transfer adjustment layer after applying the resin composition when providing the transfer adjustment layer was evaluated visually according to the following criteria.
○: Dried immediately and did not feel tack even when touched △: Although it took some time to dry, almost no tack was felt even when touched after drying ×: It took a considerable time to dry, Tack feeling remained

Example 1
As a water-soluble film, a PVA film (thickness 30 μm) is used, and on one side thereof, a polyvinyl pyrrolidone resin and 1.5% by mass of silica fine particles having an average particle diameter of 1 μm (as content relative to the resin) are contained as fine particles. Was applied at a coating amount of 3 g / m ² , a transfer adjustment layer having a thickness of 2 μm was provided, and an uneven pattern was formed by embossing on the side of the transfer adjustment layer on which the metal thin film layer was provided. Next, a 35 nm-thick metal thin film layer made of aluminum metal was formed on the transfer adjustment layer by a vacuum vapor deposition method to produce a hydraulic transfer film.
Next, 3 g / m ^{2 of} an activator composition having the following composition is applied to the surface of the metal thin film layer of the hydraulic transfer film, and the activator composition is made uniform with a smoothing roll to activate the transfer adjusting layer and the metal thin film layer. After the agent coating step (a), the transferred body is pressed against the hydraulic transfer film, the metal thin film layer is brought into close contact with the transferred surface of the transferred body by water pressure, and the film removal step (c) Then, a decorative molded product was produced and performance evaluation was performed.
The results are shown in Table 1.
<Composition of activator composition>
Phthalic acid alkyd resin: 6 parts by weight Microsilica (pigment): 2 parts by weight Dibutyl phthalate: 17 parts by weight Solvent (butyl carbitol acetate): 60 parts by weight Solvent (butyl cellosolve) 15 parts by weight

Examples 2-6 and Comparative Examples 1-2
In Example 1, each hydraulic transfer film was prepared in the same manner as in Example 1 except that the content or average particle diameter of silica fine particles used as the fine particles was as shown in Table 1, and each decorative molding was further performed. The product was produced and its performance was evaluated. The results are shown in Table 1.

［注］転写調整層の金属薄膜層側にエンボス加工により凹凸模様が施されている。

[Note] An uneven pattern is formed on the metal thin film layer side of the transfer adjustment layer by embossing.

As can be seen from Table 1, the decorative molded product of the present invention has a calm metallic tone, that is, an appropriate glossiness. Therefore, the hydraulic transfer film of the present invention is a material to be transferred. It was confirmed that the decorative molded product was imparted with an appropriate gloss feeling. Moreover, since the hydraulic transfer film of this invention has favorable blocking property, the resin molded product was obtained with high productivity. Furthermore, the hydraulic transfer film of the present invention was excellent in transferability because the metal thin film layer was less likely to be unevenly cracked during hydraulic transfer.
On the other hand, in Comparative Example 1 containing no fine particles at all, the metallic tone is too high to obtain an appropriate gloss feeling, and it cannot be said that the design property is excellent, and the printability when forming the transfer adjustment layer is extremely high. It was bad. Further, in Comparative Example 2 in which the content of fine particles was large, an appropriate gloss feeling was not obtained and the design was poor.

  The hydraulic transfer film of the present invention has a metal thin film layer and can impart an appropriate gloss tone to the transfer target. Moreover, since the hydraulic transfer film of this invention has favorable blocking property, a decorative molded product can be manufactured with high productivity by using this hydraulic transfer film. The obtained decorative molded product can be suitably used for a molded product having a three-dimensional shape, for example, an automobile interior product, a home appliance, or an OA device.

1 Hydraulic transfer film 2 Water-soluble film 3 Transfer adjustment layer 4 Metal thin film layer

Claims (6)

  A hydraulic transfer film having a water-soluble film, a transfer adjustment layer on the water-soluble film, and a metal thin film layer on the transfer adjustment layer, wherein the transfer adjustment layer constitutes the transfer adjustment layer A hydraulic transfer film characterized by comprising a content of more than 0% and less than 2.0% by mass relative to the resin.   The hydraulic transfer film according to claim 1, wherein the resin constituting the transfer adjustment layer is a polyvinylpyrrolidone resin. Particles, water pressure transfer film according to claim 1 or 2 is silica fine particles. Hydraulic transfer film according to any one of claims 1 to 3, the metal thin film layer side of the transfer control layer has an uneven pattern. Metal, hydraulic transfer film according to any one of claims 1 to 4 which is aluminum to form the metal thin film layer. It is a manufacturing method of the decorative molded product using the hydraulic transfer film in any one of Claims 1-5 ,
Step (a): an activator composition application step for applying the activator composition to the metal thin film layer before or after floating on the water surface so that the water-soluble film side of the hydraulic transfer film faces downward and toward the water surface side,
Step (b): a step of pressing the transferred material against the hydraulic transfer film that has undergone the above step (a), and causing the metal thin film layer to adhere to the transferred surface of the transferred material by water pressure, and step (c): the transferred material A film removal process for removing the water-soluble film and the transfer adjustment layer which are in close contact with the transfer surface of the transfer body;
The manufacturing method of the decorative molded product characterized by having sequentially.