  The present invention relates to an aquatic organism adhesion preventing adhesive tape. In detail, the present invention is that underwater organisms adhere to underwater structures (such as ships, buoys, harbor facilities, offshore oilfield facilities, waterways for power plant cooling water, waterways for factory cooling water, water floating passages, etc.). The present invention relates to an aquatic organism adhesion prevention adhesive tape for preventing breeding.

  Underwater structures such as ships, where they come into contact with seawater, marine organisms such as barnacles, oysters, blue mussels, hydra, cell plastics, squirts, bryozoans, aosa, aonori, and attached diatoms grow and adhere, increasing fluid resistance. It causes unfavorable conditions such as deterioration of equipment and machine performance such as deterioration of thermal conductivity and diffusion of attached marine organisms overseas. In addition, the work for removing the attached marine organisms requires a large amount of labor and enormous time, and suffers an economic loss.

  In order to prevent such damage, antifouling paint has been conventionally applied to underwater structures. Antifouling paints have long contained toxic antifouling agents such as organotin compounds and now cuprous oxide. The adhesion growth of marine organisms can be almost suppressed by the toxicity of antifouling paints, but toxic antifouling agents such as organotin compounds and cuprous oxide have a considerable adverse effect on the human body and the environment. It becomes. Further, when the antifouling paint is dried after being applied, about 30% by weight of the organic solvent (VOC) is volatilized, which adversely affects the work environment and the surrounding environment. In spray coating, in addition to discharging VOC into the atmosphere, it is said that 10 wt% to 20 wt% of the paint is scattered around by the wind. On the other hand, when repainting antifouling paints that have been used for many years, old antifouling paints are peeled off with sandblasting or a metal polishing machine, but at that time, toxic antifouling agents such as organotin compounds and cuprous oxide are removed. A large amount of the coated film pieces are scattered around and adversely affect workers and the environment, and the peeled antifouling paint is treated as industrial waste, which is a big problem.

  As described above, although antifouling paints so far have an adhesion inhibiting effect on marine organisms, they have a great adverse effect on the human body and the environment, and the current situation is that many problems have not been solved. .

Then, the adhesive tape which bonded copper thin and the adhesive through the primer is proposed (refer patent documents 1 and 2). However, such an adhesive tape has a problem that there is a possibility of an adverse effect on the environment because adhesion of marine organisms is suppressed by a thin copper component. In addition, such an adhesive tape is designed to have a peel adhesive strength to the FRP plate of 2.6 kg / 25 mm or 7.5 kg / 25 mm (after primer pretreatment), and the adhesive tape after use is replaced. In this case, it is difficult to think that the adhesive tape is easily peeled off by human power, and after all, an action such as scraping is required, which requires a lot of labor. Moreover, copper is a heavy substance with a specific gravity of 8.94 g / cm ^3, and its use in a moving structure such as a ship deteriorates fuel efficiency and is not economically preferable.

  In addition, an antifouling tape composed of two layers of silicone rubber and an adhesive has been proposed (see Patent Document 3). However, the silicone rubber layer responsible for the antifouling effect does not contain an antifouling agent such as oil, and is a silicone rubber itself. When the antifouling agent is not included, the adhesion of marine organisms can be suppressed by its water repellency in the short term, but the antifouling effect cannot be sustained in the long term. In addition, since such an antifouling tape is composed of two layers of silicone rubber and an adhesive, there is a great concern about strength. In general, silicone rubber has a very low strength at break, and therefore, when such an antifouling tape is peeled off after use, it is difficult to peel off as a tape state, which is not practical.

  In addition, a sheet-like tape has been proposed in which a silicone elastomer is provided on a base material via a primer and an adhesive layer is provided on the opposite side of the base material (see Patent Document 4). However, since there is no description regarding the adhesive composition that can be used in water and no description regarding adhesive strength, Patent Document 4 is not realistic in considering application to an aquatic organism adhesion prevention adhesive tape. In addition, when applying antifouling tape to underwater structures, it is necessary to design for flexibility and extensibility so that it can be applied to curved surfaces and acute angles, and when antifouling tape is peeled off after use Although strength design is required so that the base material does not break in the middle, Patent Document 4 does not have such description at all, and is not realistic in considering application to an aquatic organism adhesion prevention adhesive tape.

Japanese Examined Patent Publication No. 63-62487 Japanese Patent Publication No. 1-54397 Japanese Patent No. 3000101 JP 2002-69246 A

  The problem of the present invention is that it can exhibit good adhesiveness even in water, has good mechanical properties, is easy to peel off, can maintain an antifouling effect over a long period of time, has little burden on the human body and the environment, An object of the present invention is to provide an aquatic organism adhesion-preventing pressure-sensitive adhesive tape that is light in weight, can maintain stable quality, and can effectively prevent adhesion of aquatic organisms.

The aquatic organism adhesion preventing adhesive tape of the present invention is
An adhesive tape comprising an antifouling layer, a base material layer and an adhesive layer in this order,
The antifouling layer contains a silicone resin.

  In a preferred embodiment, the antifouling layer contains an antifouling agent.

  In preferable embodiment, the content rate of the said antifouling agent with respect to the said silicone resin is 2 weight% or more.

  In a preferred embodiment, the antifouling agent is at least one selected from silicone oil, liquid paraffin, and surfactant.

The aquatic organism adhesion preventing adhesive tape of the present invention is
An adhesive tape comprising an antifouling layer, a base material layer and an adhesive layer in this order,
The adhesion between the antifouling layer and aquatic organisms is 0.10 N / mm ² or less.

  In a preferred embodiment, the base material layer has an elongation of 100% or more and a stress at break of 10 MPa or more.

  In a preferred embodiment, the adhesive layer has a 180-degree peel adhesive strength of 30 N / 20 mm or less at 23 ° C. and a tensile speed of 300 mm / min.

  In a preferred embodiment, when the pressure-sensitive adhesive layer is contacted with seawater, the compression elastic modulus of the portion of the pressure-sensitive adhesive layer in contact with seawater is 1.1 times the compression elastic modulus of the pressure-sensitive adhesive layer before seawater contact. That's it.

  According to the present invention, good adhesiveness can be expressed even in water, it has good mechanical properties, is easy to peel off, can maintain an antifouling effect over a long period of time, has little impact on the human body and the environment, It is possible to provide an aquatic organism adhesion-preventing pressure-sensitive adhesive tape that is light in weight, can maintain stable quality, and can effectively prevent aquatic organism adhesion.

It is a schematic sectional drawing of an example of the aquatic organism adhesion prevention adhesive tape of this invention. It is a photograph figure which shows the state of the outdoor antifouling test result of the adhesive tape (2) obtained in Example 2. It is a photograph figure which shows the state of the outdoor antifouling test result of the adhesive tape (13) obtained in Example 13. It is a photograph figure which shows the state of the outdoor antifouling test result of the adhesive tape (14) obtained in Example 14. It is a photograph figure which shows the state of the outdoor antifouling test result of the adhesive tape (C1) obtained by the comparative example 1. It is a photograph figure which shows the state of the field antifouling test result of the adhesive tape (C2) obtained by the comparative example 2. It is the schematic of the method of measuring the adhesive force of a pollution protection layer and aquatic organisms.

  The aquatic organism adhesion prevention adhesive tape of this invention contains an antifouling layer, a base material layer, and an adhesion layer in this order.

  The aquatic organism adhesion-preventing pressure-sensitive adhesive tape of the present invention has any appropriate other layer as long as the antifouling layer, the base material layer, and the pressure-sensitive adhesive layer are included in this order, as long as the effects of the present invention are not impaired. May be. The thickness of the aquatic organism adhesion prevention adhesive tape of this invention is set to arbitrary appropriate thickness in the range which does not impair the effect of this invention by the thickness of each layer contained in it. The thickness of the aquatic organism adhesion preventing adhesive tape of the present invention is preferably 50 μm to 5000 μm.

  In FIG. 1, the schematic sectional drawing of an example of the aquatic organism adhesion prevention adhesive tape of this invention is shown. The aquatic organism adhesion prevention adhesive tape 100 of this invention contains the antifouling layer 2, the base material layer 3, and the adhesion layer 4 in this order. As shown in FIG. 1, a release film 1 may be provided on the surface of the antifouling layer 2 or the surface of the adhesive layer 4.

In aquatic adhesion preventing pressure-sensitive adhesive tape of the present invention, adhesion between the antifouling layer and the aquatic organisms is preferably not more than 0.10 N / mm ^2, more preferably less 0.08 N / mm ^2, more preferably Is 0.05 N / mm ² or less, particularly preferably 0.04 N / mm ² or less. The lower limit of the adhesion between the antifouling layer and the aquatic organism is preferably as small as possible. However, in consideration of materials and the like, in practice, it is preferably 0.005 N / mm ² or more, more preferably 0. 0.001 N / mm ² or more. When the adhesion between the antifouling layer and the aquatic organisms is within the above range, the aquatic organism adhesion preventing adhesive tape of the present invention can very effectively prevent the aquatic organisms from adhering. In addition, the measuring method of the adhesive force of an antifouling layer and aquatic organisms is mentioned later.

  The antifouling layer preferably contains a silicone resin. Arbitrary appropriate content rates can be employ | adopted for the content rate of the silicone resin in an antifouling layer by the content rate of other components, such as an antifouling agent. The content ratio of the silicone resin in the antifouling layer is preferably 30% by weight to 98% by weight, more preferably 40% by weight to 97% by weight, still more preferably 45% by weight to 96% by weight, Especially preferably, it is 50 to 95 weight%. When the content ratio of the silicone resin in the antifouling layer is within the above range, the antifouling effect of the antifouling layer can be sufficiently exhibited, and the mechanical characteristics of the antifouling layer can be sufficiently expressed. When the content ratio of the silicone resin in the antifouling layer is less than 30% by weight, the mechanical properties of the antifouling layer may be deteriorated. When the content ratio of the silicone resin in the antifouling layer exceeds 98% by weight, the antifouling effect of the antifouling layer may not be sufficiently exhibited.

  Any appropriate silicone resin can be adopted as the silicone resin as long as the effects of the present invention are not impaired. Only one type of silicone resin may be used, or two or more types may be used. Such a silicone resin may be a silicone resin that is liquid at normal temperature, or may be a silicone resin that is solid at normal temperature. Such a silicone resin may be a condensation type silicone resin or an addition type silicone resin. Such a silicone resin may be a one-component silicone resin that is dried alone, or a two-component silicone resin that contains a curing agent. In the present invention, among these, a one-component room temperature curable (RTV) resin and a two-component room temperature curable (RTV) resin are preferable. Examples of the one-component RTV resin include KE-3475, KE-45S, KE-445, KE-44, KE-441, KE-3497, and KE-4896 manufactured by Shin-Etsu Chemical Co., Ltd. . Examples of the two-component RTV resin include KE-106, KE-66, KE-1031, and KE-1800 manufactured by Shin-Etsu Chemical Co., Ltd.

  In order to improve the easy removal of aquatic organisms in the aquatic organism adhesion-preventing pressure-sensitive adhesive tape of the present invention, the silicone resin can be easily peeled off due to elastic deformation of the resin surface due to water pressure at the time of water washing removal. A silicone resin having such physical properties is preferred. Such a silicone resin has a 100% modulus (tensile stress) of the silicone resin of preferably 0.1 MPa to 10 MPa, more preferably 0.1 MPa to 6 MPa. Such silicone resin is preferably soluble in an organic solvent.

  The antifouling layer preferably contains an antifouling agent. Only one type of antifouling agent may be used, or two or more types may be used. When the antifouling layer contains an antifouling agent, the antifouling agent migrates to the surface of the silicone resin as a matrix and covers the surface with an antifouling substance, thereby suppressing the adhesion of aquatic organisms to the silicone resin surface. Furthermore, since it is non-hydrolyzable, it can exhibit the effect of maintaining a high antifouling effect for a long period of time.

  In the antifouling layer, the content ratio of the antifouling agent to the silicone resin is preferably 2% by weight or more, more preferably 2% by weight to 200% by weight, and further preferably 3% by weight to 150% by weight. Particularly preferred is 4 to 120% by weight, and most preferred is 5 to 100% by weight. When the content ratio of the antifouling agent to the silicone resin is within the above range, the antifouling effect of the antifouling layer can be sufficiently exhibited, and the appearance characteristics and mechanical characteristics of the antifouling layer can be sufficiently expressed. When the content ratio of the antifouling agent to the silicone resin is less than 2% by weight, the antifouling effect of the antifouling layer may not be sufficiently exhibited. When the content of the antifouling agent relative to the silicone resin exceeds 200% by weight, the appearance of the final molded product or the film may be deteriorated, and the antifouling layer strength is lowered and the antifouling property cannot be maintained. There is a fear.

  As the antifouling agent, any appropriate antifouling agent can be adopted as long as the effects of the present invention are not impaired. Examples of such an antifouling agent include silicone oil, liquid paraffin, surfactant, wax, petrolatum, animal fats, fatty acids and the like. In the present invention, the antifouling agent is preferably at least one selected from silicone oil, liquid paraffin, and surfactant.

  The silicone oil is preferably one that does not have reactivity with the silicone resin or self-condensation. As such a silicone oil, any appropriate silicone oil can be adopted as long as the effects of the present invention are not impaired. Such a silicone oil is preferably incompatible with the organopolysiloxane contained in the silicone resin to some extent, and is represented by, for example, the general formula (I) in that the antifouling effect can be maintained over a long period of time. Silicone oil is preferred.

In general formula (I), R ¹ is the same or different and represents an alkyl group having 1 to 10 carbon atoms, an aryl group, an aralkyl group, a fluoroalkyl group, a polyether group, or a hydroxyl group, and R ² is the same or Differently, it represents an alkyl group having 1 to 10 carbon atoms, an aryl group, an aralkyl group, a polyether group or a fluoroalkyl group, and n represents an integer of 0 to 150.

R ¹ in the general formula (I) is preferably a methyl group, a phenyl group, or a hydroxyl group. R ² in the general formula (I) is preferably a methyl group, a phenyl group, or a 4-trifluorobutyl group.

  The number average molecular weight of the silicone oil represented by the general formula (I) is preferably 180 to 20000, and more preferably 1000 to 10,000.

  The viscosity of the silicone oil represented by the general formula (I) is preferably 10 centistokes to 10000 centistokes, more preferably 100 centistokes to 5000 centistokes.

As the silicone oil represented by the general formula (I), specifically, for example, terminal hydroxyl group-containing dimethyl silicone oil R ¹ at both ends or one end is a hydroxyl group, all of R ¹ and R ² is a methyl group And dimethyl silicone oils in which some of the methyl groups of these dimethyl silicone oils are substituted with phenyl groups.

  Examples of commercially available silicone oils represented by the general formula (I) include KF96L, KF96, KF69, KF99, KF50, KF54, KF410, KF412, KF414, FL, Toray Dow Corning manufactured by Shin-Etsu Chemical Co., Ltd. Examples include BY16-846, SF8416, SH200, SH203, SH230, SF8419, FS1265, SH510, SH550, SH710, FZ-2110, and FZ-2203 manufactured by Corporation.

  Examples of the surfactant include an anionic surfactant, a cationic surfactant, and a nonionic surfactant.

  As antifouling agents, diatomaceous adhesion inhibitors, agricultural chemicals, pharmaceuticals (such as medetomidine), enzyme activity inhibitors (such as alkylphenols and alkylresorcinols), and biological repellents may be used. By using these antifouling agents, the adhesion preventing effect of aquatic organisms such as diatoms and barnacles is further improved.

  The antifouling layer may contain any appropriate other additive as long as the effects of the present invention are not impaired.

  Arbitrary appropriate thickness can be employ | adopted for the thickness of a pollution protection layer by the use of the aquatic organism adhesion prevention adhesive tape of this invention, use environment, etc. The thickness of the antifouling layer is preferably 5 μm to 500 μm. When the thickness of the antifouling layer is within the above range, the antifouling effect is effective for a sufficiently long time, and the handling property is excellent. When the thickness of the antifouling layer is less than 5 μm, the period during which the antifouling effect is effective is shortened and may not be practical. If the antifouling layer is thicker than 500 μm, the aquatic organism adhesion-preventing pressure-sensitive adhesive tape of the present invention becomes thick and heavy, resulting in poor handling, large irregularities at the joints of the tape, and dirt. There is a fear.

  As a base material layer, arbitrary appropriate base material layers can be employ | adopted in the range which does not impair the effect of this invention. Such a material for the base material layer is preferably excellent in water resistance, strength, flexibility and tearability. Examples of the material for the base material layer include polyurethane resin, polyurethane acrylic resin, rubber resin, vinyl chloride resin, polyester resin, silicone resin, elastomers, fluororesin, polyamide resin, polyolefin resin (polyethylene, polypropylene, etc.) ) And the like. The material of such a base material layer may be only one type or two or more types.

  The elongation of the base material layer is preferably 100% or more, more preferably 120% or more, and further preferably 150% or more. When the elongation of the base material layer is 100% or more, the aquatic organism adhesion-preventing pressure-sensitive adhesive tape of the present invention can follow the shape of various adherends well and can be affixed to a flat surface well. It can be satisfactorily applied to curved surface portions, 90-degree angle portions, acute angle portions, and the like. When the elongation of the base material layer is less than 100%, the shape of various adherends cannot be sufficiently followed, and wrinkles and unbonded portions of the adhesive may be generated, which may cause poor appearance and poor adhesion. There is. The upper limit of the elongation of the base material layer is preferably 2000% or less from the viewpoint of the strength of the base material layer.

  The base material layer has a breaking stress of preferably 10 MPa or more, more preferably 12 MPa or more, and further preferably 15 MPa or more. When the stress at break of the base material layer is within the above range, the base material layer can be prevented from being cut when the used aquatic organism adhesion preventing adhesive tape of the present invention is peeled off from the adherend. When the stress at break of the base material layer is less than 10 MPa, the base material layer is frequently cut when the used aquatic organism adhesion-preventing pressure-sensitive adhesive tape of the present invention is peeled off from the adherend, and the working efficiency is extremely poor. There is a risk. The upper limit of the breaking point stress of the base material layer is preferably 200 MPa or less from the viewpoint of the handleability of the base material layer.

  The elastic modulus of the base material layer is preferably 4000 MPa or less, more preferably 1000 MPa or less, still more preferably 100 MPa or less, and particularly preferably 50 MPa or less. When the elastic modulus of the base material layer is 4000 MPa or less, the aquatic organism adhesion-preventing pressure-sensitive adhesive tape of the present invention can satisfactorily follow various shapes of adherends, and workability is improved. The lower limit of the elastic modulus of the base material layer is preferably 0.1 MPa or more from the viewpoint of handleability of the base material layer.

  The base material layer may contain any appropriate additive as long as the effects of the present invention are not impaired. Examples of such additives include olefin resins, silicone polymers, liquid acrylic copolymers, tackifiers, anti-aging agents, hindered amine light stabilizers, ultraviolet absorbers, antioxidants, and antistatic agents. , Polyethyleneimine, fatty acid amide, fatty acid ester, phosphate ester, lubricant, surfactant, filler and pigment (for example, calcium oxide, magnesium oxide, silica, zinc oxide, titanium oxide, carbon black, etc.).

  The base material layer preferably contains an ultraviolet absorber. The weather resistance of the aquatic organism adhesion prevention adhesive tape of this invention improves because a base material layer contains a ultraviolet absorber. When the base material layer does not contain an ultraviolet absorber, the base material is likely to be deteriorated by sunlight during outdoor use, and it may be difficult to maintain the initial base material strength. When the base material deteriorates, the base material layer is frequently cut when the used aquatic organism adhesion preventing adhesive tape of the present invention is peeled off from the adherend, and the work efficiency may be significantly deteriorated. There is.

  Arbitrary appropriate thickness can be employ | adopted for the thickness of a base material layer according to the use, use environment, etc. of the aquatic organism adhesion prevention adhesive tape of this invention. The thickness of a base material layer becomes like this. Preferably they are 1 micrometer-1000 micrometers, More preferably, they are 10 micrometers-800 micrometers, More preferably, they are 20 micrometers-500 micrometers. By keeping the thickness of the base material layer within the above range, the aquatic organism adhesion-preventing pressure-sensitive adhesive tape of the present invention can be easily attached to a portion other than a flat surface such as a curved surface or an acute angle surface with good workability. Appearance defects such as wrinkles and floats are unlikely to occur on the surface. When the thickness of the base material layer is too thin, the handling property is deteriorated, the role as a base material cannot be played, and there is a possibility that it is not practical. When the thickness of the base material layer is too thick, it is impossible to sufficiently follow the shape of the adherend, the unevenness of the joint portion of the tape becomes large, and there is a possibility that it is easily stained.

  In order to improve adhesion to the antifouling layer, a primer may be applied to the base material layer in advance, or a silane coupling agent may be added in advance. When the antifouling layer contains a silicone resin, adhesion to the base material layer may be low due to the low surface energy that is a characteristic of the silicone resin. If the adhesion between the antifouling layer and the base material layer is low, the antifouling layer that exhibits the antifouling effect peels off from the base material layer due to impact or physical damage during use, and the original antifouling effect continues. It may not be possible. Therefore, a primer is applied to the surface of the base material layer in advance to improve the adhesion to the antifouling layer, or silanol groups and alkoxysilane groups that react with the silicone resin are introduced into the base material layer with a silane coupling agent. The adhesion can be improved by performing a condensation reaction with a reactive group on the base material layer during application of the condensation type silicone resin.

  Only one type of silane coupling agent may be used, or two or more types may be used. Specific examples of commercially available silane coupling agents include KBM5103, KBM1003, KBM903, KBM403, and KBM802 manufactured by Shin-Etsu Chemical Co., Ltd.

  When a silane coupling agent is contained in the base material layer, the content ratio of the silane coupling agent in the base material layer is preferably 0.01% by weight to 10% by weight. By keeping the content ratio of the silane coupling agent in the base material layer within the above range, it is possible to suppress the base material layer from becoming too hard, and there is sufficient adhesion between the base material layer and the antifouling layer. It can be expressed. When the content rate of the silane coupling agent in a base material layer exceeds 10 weight%, there exists a possibility that a silane coupling agent may become a crosslinking point and a base material layer may become hard. When the content rate of the silane coupling agent in a base material layer is less than 0.01 weight%, there exists a possibility that sufficient adhesiveness cannot be expressed between a base material layer and an antifouling layer.

  Any appropriate pressure-sensitive adhesive layer can be adopted as the pressure-sensitive adhesive layer as long as the effects of the present invention are not impaired. Examples of the material for such an adhesive layer include acrylic resin adhesives, epoxy resin adhesives, amino resin adhesives, vinyl resin (vinyl acetate polymers, etc.) adhesives, and curable acrylic resin adhesives. Agents, silicone resin adhesives, and the like. The material of the adhesive layer may be only one type or two or more types.

  The pressure-sensitive adhesive layer has a 180-degree peel adhesive strength at 23 ° C. and a tensile speed of 300 mm / min, preferably 30 N / 20 mm or less, more preferably 20 N / 20 mm or less, and further preferably 15 N / 20 mm or less. When the 180 degree peel adhesive force at 23 ° C. and a tensile speed of 300 mm / min is within the above range, the aquatic organism adhesion preventing adhesive tape of the present invention can be easily peeled off from the adherend. If the adhesive layer has a 180 degree peel adhesive force of 30 N / 20 mm at 23 ° C. and a tensile speed of 300 mm / min, it becomes difficult to peel off the used aquatic organism adhesion preventing adhesive tape of the present invention from the adherend. There is a risk that the efficiency is remarkably deteriorated. The lower limit of the 180-degree peel adhesive strength at 23 ° C. and a tensile speed of 300 mm / min is preferably 5 N / 20 mm or more from the viewpoint of maintaining sufficient adhesive strength.

  When the pressure-sensitive adhesive layer is contacted with seawater, the compression elastic modulus of the portion of the pressure-sensitive adhesive layer in contact with seawater is preferably 1.1 times the compression elastic modulus of the pressure-sensitive adhesive layer before seawater contact. More preferably, it is 1.2 times or more, and more preferably 1.5 times or more. When the pressure-sensitive adhesive layer is in contact with seawater and the compression elastic modulus of the portion of the pressure-sensitive adhesive layer in contact with seawater is 1.1 times the compression elastic modulus of the pressure-sensitive adhesive layer before seawater contact, Can exhibit good adhesiveness. When the pressure-sensitive adhesive layer is contacted with seawater, the upper limit of the compression elastic modulus of the portion of the pressure-sensitive adhesive layer that is in contact with seawater with respect to the compression elastic modulus in the pressure-sensitive adhesive layer before seawater contact is from the viewpoint of handling properties. Preferably it is 100 times or less.

  Arbitrary appropriate thickness can be employ | adopted for the thickness of the adhesion layer by the use, use environment, etc. of the aquatic organism adhesion prevention adhesive tape of this invention. The thickness of the adhesive layer is preferably 10 μm or more. When the thickness of the pressure-sensitive adhesive layer is less than 10 μm, it is impossible to sufficiently follow the shape of the adherend, the adhesion area is reduced, and there is a possibility that sufficient pressure-sensitive adhesive force cannot be expressed. The upper limit of the thickness of the pressure-sensitive adhesive layer is preferably 100 μm or less from the viewpoint of handleability.

  The aquatic organism adhesion prevention adhesive tape of this invention can be manufactured by arbitrary appropriate methods. Examples of such a method include, for example, a method of forming an antifouling layer by applying an antifouling layer forming material on the base material layer after pasting a separately prepared base material layer and an adhesive layer, and one of the base material layers. A method of forming an adhesive layer by applying an adhesive layer forming material on the surface and forming an antifouling layer by applying an antifouling layer forming material to the other surface of the base material layer, the base layer forming material and the adhesive layer For example, a method of forming the antifouling layer by applying the antifouling layer forming material on the base material layer after co-extrusion of the forming material to form a base material layer / adhesive layer laminate.

  Examples of the method for applying the antifouling layer forming material on the base material layer include spraying, brushing, roller, curtain flow, roll, dip, and coater. The antifouling layer-forming material is applied onto the base material layer by these methods, and the antifouling layer is formed, for example, by drying at a temperature from room temperature to 250 ° C. (preferably from room temperature to 180 ° C.). can do. In particular, in the aquatic organism adhesion-preventing pressure-sensitive adhesive tape of the present invention, it is one of preferred embodiments that a precision coater such as a comma coater is used to apply the antifouling layer forming material onto the base material layer.

  EXAMPLES Hereinafter, although an Example demonstrates this invention concretely, this invention is not limited to these Examples at all.

<Evaluation of elongation and stress at break>
In accordance with JIS 7161, JIS 7162, and JIS 7127, using a tensile tester (AUTOGRAPH AGS-X, manufactured by Shimadzu Corporation) and analysis software (TRAPEZIUM X, manufactured by Shimadzu Corporation), the elongation and breaking points of the base material layer Stress was measured.

<Measurement of 180 degree peel adhesion>
The pressure-sensitive adhesive in the pressure-sensitive adhesive layer was transferred to a polyester film (trade name “S-10”, manufactured by Toray Industries, Inc., thickness 38 μm) using a hand roller to obtain a pressure-sensitive adhesive sheet with a substrate. This was cut into a test piece size of 80 mm × 20 mm. As the adherend, a plastic FRP plate reinforced by putting a glass cloth in an epoxy resin of 30 mm × 100 mm × thickness 2 mm was used. The test piece was attached to the adherend by reciprocating once with a 2 kg roller, and allowed to stand at 23 ° C. for 30 minutes, and then the initial 180-degree peel adhesive strength was measured. The tensile speed was 300 mm / min.

<Measurement of compression modulus>
The pressure-sensitive adhesive tape was immersed in commercially available simulated seawater for 7 days at room temperature with the pressure-sensitive adhesive layer in contact with seawater, and the compression modulus of the portion of the pressure-sensitive adhesive layer in contact with seawater before and after immersion was compared. The evaluation conditions were as follows. The compression elastic modulus was obtained from the load-displacement curve obtained by measurement with the attached analysis software.
Evaluation apparatus: Nanoindenter, Hysitron Inc. Made by Tribo Scope
Working indenter: Berkovich, triangular pyramid Measuring method: Single indentation measurement Measuring temperature: 25 ° C
Pushing depth setting: about 1.1μm

<Outdoor antifouling test>
All of the pressure-sensitive adhesive tapes to be evaluated were cut out to a size of 10 cm × 10 cm, and attached to a vinyl chloride plate having almost the same size. All these plates (samples) were further fixed to a vinyl chloride plate having a length of 23 cm and a width of 90 cm. Install this unit at a breakwater in the yacht harbor in the Seto Inland Sea (around Himeji) 2m below the sea level (at the highest tide) or 0.5m below (at the lowest tide). Was placed on the opposite side of the breakwater wall. It was left as it was for 3 months, and then visually evaluated. The evaluation criteria are as follows.
○: There is almost no attached organism, or even if it is attached, it is easily peeled off with a finger.
(Triangle | delta): The state to which the adhesion organism has adhered to about 10% of the surface.
X: A state in which attached organisms are attached to about 20% of the surface.
XX: A state in which attached organisms are attached to about 30% or more of the surface.

<Measurement of adhesive force>
A measuring adapter (mountain adapter on extension bar) was attached to the digital force gauge (manufactured by SHIMPO, FGN-50B) to prepare the measuring machine.
An adhesive tape or film with a barnacle attached was selected, and the diameter of the barnacle was measured with calipers.
After resetting the measurement value of the measuring instrument, as shown in Fig. 7, gently place the measuring adapter on the lower part of the outer shell of the barnacle attached to the surface of the adhesive tape or film, parallel to the surface of the adhesive tape or film. The measuring machine was slid so that the barnacle was peeled off. The maximum load value (N) displayed on the measuring machine at this time was recorded.
The barnacle adhesion area (mm ² ) is calculated from the diameter of the barnacle previously measured by the circle area formula, the recorded maximum load value is divided by the adhesion area, and the load per unit area (N / mm ² ) was obtained by calculation, and this was defined as adhesion.

[Production Example 1]
<Creation of base material layer>
In a reaction vessel equipped with a condenser, a thermometer, and a stirrer, 71 parts by weight of isobornyl acrylate (trade name “IBXA”, manufactured by Osaka Organic Chemical Industry Co., Ltd.) as a (meth) acrylic monomer, n -19 parts by weight of butyl acrylate (BA, manufactured by Toa Gosei Co., Ltd.), 10 parts by weight of acrylic acid (AA), poly (oxytetramethylene) glycol (PTMG650, Mitsubishi Chemical Corporation) having a number average molecular weight of 650 as a polyol 68.4 parts by weight) and 0.01 part by weight of dibutyltin dilaurate (DBTL) as a catalyst, and 25 g of hydrogenated xylylene diisocyanate (HXDI, manufactured by Mitsui Chemicals Polyurethane Co., Ltd.) with stirring. 5 parts by weight were dropped and reacted at 65 ° C. for 5 hours to obtain a urethane polymer-acrylic monomer mixture. Thereafter, 6.1 parts by weight of hydroxyethyl acrylate (trade name “Acrix HEA”, manufactured by Toa Gosei Co., Ltd.) was further added and reacted at 65 ° C. for 1 hour, whereby acryloyl group-terminated urethane polymer-acrylic system A monomer mixture was obtained. Thereafter, 1 part by weight of 3-acryloxypropyltrimethoxysilane (KBM-5103, manufactured by Shin-Etsu Chemical Co., Ltd.) and diphenyl (2,4,6, -trimethoxybenzoyl) phosphine oxide (product) as a photopolymerization initiator 0.25 parts by weight of the name “Lucirin TPO” (manufactured by BASF), 1.25 parts by weight of UV absorber (trade name “TINUVIN123”, manufactured by BASF), and antioxidant (trade name “TINUVIN400”, manufactured by BASF) A syrup was obtained by adding 0.6 parts by weight.
A syrup was coated on the surface of a separator (trade name “MRF38”, manufactured by Mitsubishi Plastics, Inc., thickness 38 μm) with an applicator to form a base material syrup layer having a thickness of 150 μm. A cover separator (trade name “MRF38”, manufactured by Mitsubishi Plastics Co., Ltd., thickness 38 μm) is bonded to the base material syrup layer with a hand roller, and further irradiated with ultraviolet rays (ultraviolet illumination: 3). 4 mW / cm ² , cumulative irradiation amount: 2000 mJ / cm ² ), and a substrate layer having a thickness of 150 μm was obtained.
As a result of evaluating the elongation and stress at break of the prepared base material layer, the elongation was 420% and the stress at break was 27 MPa.

[Production Example 2]
<Creation of adhesive layer>
In a reaction vessel equipped with a cooling tube, a nitrogen introduction tube, a thermometer, and a stirrer, 90 parts by weight of 2-ethylhexyl acrylate (2EHA, manufactured by Toagosei Co., Ltd.) as a (meth) acrylic monomer, acrylic acid (AA) 10 parts by weight and 0.05 parts by weight of 2,2-dimethoxy-1,2-diphenylethane-1-one (trade name “Irgacure 651”, manufactured by BASF) as a photopolymerization initiator are dispersed and stirred. The acrylic monomer mixture was obtained by converting a part of the monomer into a polymer by adjusting the viscosity so that it can be applied by UV irradiation from above in a nitrogen stream. 0.08 parts by weight of 1,6-hexanediol diacrylate (HDDA) as a crosslinking agent was added to this acrylic monomer mixture, and the surface of the separator (trade name “MRF50”, manufactured by Mitsubishi Plastics, Inc., thickness 50 μm) By applying the cover separator (trade name “MRF38”, manufactured by Mitsubishi Plastics Co., Ltd., thickness: 38 μm) with a hand roller, and further irradiating with an ultraviolet lamp (BL type) (ultraviolet rays) Illuminance: 3.4 mW / cm ² , cumulative irradiation amount: 2000 mJ / cm ² ), and an adhesive layer having a thickness of 50 μm was obtained.
It was 13.3N / 20mm as a result of measuring the 180 degree | times peel adhesive force in 23 mmC of the created adhesion layer in the tension speed of 300 mm / min.

[Example 1]
<Preparation of antifouling layer forming material>
In the formulation shown in Table 1, silicone oil (KF50-100cs, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent to silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) After that, an antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (1) for coating on the base material layer.
<Creation of adhesive tape>
The adhesive layer created in Production Example 2 was attached to the base material layer created in Production Example 1 by transfer. Thereafter, the antifouling layer-forming material (1) was applied to the surface of the base material layer opposite to the adhesive layer with an applicator and dried in an oven at 150 ° C. for 10 minutes to prepare an adhesive tape (1).
The structure of the adhesive tape (1) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

[Example 2]
In the formulation shown in Table 1, silicone oil (KF50-100cs, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent to silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) After that, an antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (2) for coating on a substrate.
Using the antifouling layer forming material (2), the same procedure as in Example 1 was performed to prepare an adhesive tape (2).
The structure of the adhesive tape (2) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.
Moreover, the photograph figure which shows the state of the field antifouling test result of an adhesive tape (2) was shown in FIG.

Example 3
In the formulation shown in Table 1, liquid paraffin (hydrocarbon liquid paraffin, manufactured by Wako Pure Chemical Industries, Ltd.) as an antifouling agent for silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) Then, the mixture was stirred using a homomixer to uniformly dissolve or disperse the antifouling agent in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (3) for coating on a substrate.
Using the antifouling layer forming material (3), the same procedure as in Example 1 was carried out to produce an adhesive tape (3).
The configuration of the adhesive tape (3) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 4
In the formulation shown in Table 1, a surfactant (DKS-NL-DASH400, nonionic ether type surfactant) as an antifouling agent for silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) After the addition of Daiichi Kogyo Seiyaku Co., Ltd., the mixture was stirred using a homomixer to uniformly dissolve or disperse the antifouling agent in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (4) for coating on a substrate.
Using the antifouling layer forming material (4), an adhesive tape (4) was prepared in the same manner as in Example 1.
The configuration of the adhesive tape (4) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 5
In the formulation shown in Table 1, silicone oil (KF96-10cs, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent to silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) After that, an antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (5) for coating on a substrate.
Using the antifouling layer forming material (5), an adhesive tape (5) was prepared in the same manner as in Example 1.
The configuration of the adhesive tape (5) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 6
In the formulation shown in Table 1, silicone oil (KF96-100cs, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent for silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) After that, an antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (6) for application to a substrate.
Using the antifouling layer forming material (6), the same procedure as in Example 1 was carried out to produce an adhesive tape (6).
The configuration of the adhesive tape (6) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 7
In the formulation shown in Table 1, silicone oil (KF96-5000cs, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent to silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) After that, an antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (7) for coating on a substrate.
Using the antifouling layer forming material (7), an adhesive tape (7) was prepared in the same manner as in Example 1.
The configuration of the adhesive tape (7) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 8
In the formulation shown in Table 1, silicone oil (KF54, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent for silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) The product was stirred using a homomixer, and the antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (8) for application to a substrate.
Using the antifouling layer forming material (8), the same procedure as in Example 1 was performed to prepare an adhesive tape (8).
The structure of the adhesive tape (8) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 9
In the formulation shown in Table 1, silicone oil (KF6015, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent for silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) The product was stirred using a homomixer, and the antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (9) for coating on a substrate.
Using the antifouling layer forming material (9), an adhesive tape (9) was prepared in the same manner as in Example 1.
The configuration of the adhesive tape (9) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 10
In the formulation shown in Table 1, silicone oil (KF414, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent for silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) The product was stirred using a homomixer, and the antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (10) for coating on a substrate.
Using the antifouling layer forming material (10), an adhesive tape (10) was prepared in the same manner as in Example 1.
The structure of the adhesive tape (10) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 11
In the formulation shown in Table 1, silicone oil (KF50-100cs, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent to silicone resin (KE1842, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) After that, an antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (11) for coating on a substrate.
Using the antifouling layer forming material (11), an adhesive tape (11) was prepared in the same manner as in Example 1.
The structure of the adhesive tape (11) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 12
In the formulation shown in Table 1, silicone oil (KF50-100cs, non-reactive silicone oil, manufactured by Shin-Etsu Chemical Co., Ltd.) as an antifouling agent to silicone resin (LR7665, heat addition type resin, manufactured by Asahi Kasei Wacker Silicone Co., Ltd.) Then, the mixture was stirred using a homomixer to uniformly dissolve or disperse the antifouling agent in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (12) for coating on a substrate.
Using the antifouling layer forming material (12), an adhesive tape (12) was prepared in the same manner as in Example 1.
The configuration of the adhesive tape (12) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

Example 13
In the formulation shown in Table 1, silicone oil (KF50-100cs, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent to silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) After that, an antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (13) for coating on a substrate.
Using the antifouling layer forming material (13), an adhesive tape (13) was prepared in the same manner as in Example 1.
The structure of the adhesive tape (13) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.
Moreover, the photograph figure which shows the state of the field antifouling test result of an adhesive tape (13) was shown in FIG.

Example 14
In the formulation shown in Table 1, only a silicone resin (KE445, room temperature curable (RTV) resin, manufactured by Shin-Etsu Chemical Co., Ltd.) is stirred using a homomixer, defoamed, and applied to the substrate. An antifouling layer-forming material (14) for work was obtained.
Using the antifouling layer forming material (14), an adhesive tape (14) was prepared in the same manner as in Example 1.
The configuration of the adhesive tape (14) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.
Moreover, the photograph figure which shows the state of the field antifouling test result of an adhesive tape (14) was shown in FIG.

[Comparative Example 1]
In the formulation shown in Table 1, silicone oil (KF50-100cs, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) was used as an antifouling agent in the syrup (uncured resin before irradiation with an ultraviolet lamp) obtained in Production Example 1. )) And stirring with a homomixer, the antifouling agent is uniformly dissolved or dispersed in the resin, and then the resin is cured with an ultraviolet lamp in the same manner as in Production Example 1 to obtain a substrate having a thickness of 150 μm. A layer was obtained. In addition, about the comparative example 1, the antifouling layer of Table 1 is read as a base material layer.
The pressure-sensitive adhesive layer obtained in Production Example 2 was attached to the obtained base material layer by transfer to produce a pressure-sensitive adhesive tape (C1).
The structure of the adhesive tape (C1) was a base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.
Moreover, the photograph figure which shows the state of the field antifouling test result of an adhesive tape (C1) was shown in FIG.

[Comparative Example 2]
In the formulation shown in Table 1, SEBS (styrene-ethylene / butylene-styrene block polymer, G1652, manufactured by Kraton Co., Ltd.) dissolved in a toluene solvent is used as an antifouling agent, and silicone oil (KF50-100cs, non-reactive silicone oil, Shin-Etsu) Chemical Industry Co., Ltd.) was added and stirred using a homomixer, and the antifouling agent was uniformly dissolved or dispersed in the resin. Then, this mixture was coated on the cover separator with an applicator and dried at 150 ° C. for 10 minutes to obtain a substrate layer having a thickness of 150 μm. For Comparative Example 2, the antifouling layer described in Table 1 is read as the base material layer.
The pressure-sensitive adhesive layer obtained in Production Example 2 was attached to the obtained base material layer by transfer to produce a pressure-sensitive adhesive tape (C2).
The configuration of the pressure-sensitive adhesive tape (C2) was base material layer (thickness = 150 μm) / pressure-sensitive adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.
Moreover, the photograph figure which shows the state of the field antifouling test result of an adhesive tape (C2) was shown in FIG.

[Comparative Example 3]
Liquid paraffin (hydrocarbon liquid paraffin, manufactured by Wako Pure Chemical Industries, Ltd.) as an antifouling agent for the syrup (uncured resin before irradiation with an ultraviolet lamp) obtained in Production Example 1 with the formulation shown in Table 1 After stirring with a homomixer, the antifouling agent is uniformly dissolved or dispersed in the resin, and then the resin is cured with an ultraviolet lamp in the same manner as in Production Example 1 to obtain a substrate layer having a thickness of 150 μm. It was. For Comparative Example 3, the antifouling layer described in Table 1 is read as the base material layer.
The pressure-sensitive adhesive layer obtained in Production Example 2 was attached to the obtained base material layer by transfer to produce a pressure-sensitive adhesive tape (C3).
The configuration of the pressure-sensitive adhesive tape (C3) was base material layer (thickness = 150 μm) / pressure-sensitive adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

[Comparative Example 4]
In the formulation shown in Table 1, liquid paraffin (hydrocarbon liquid paraffin, manufactured by Wako Pure Chemical Industries, Ltd.) is added as an antifouling agent to SEBS (styrene-ethylene / butylene-styrene block polymer, G1652, manufactured by Clayton). Then, the mixture was stirred using a homomixer, and the antifouling agent was uniformly dissolved or dispersed in the resin. After stirring, defoaming was performed to obtain an antifouling layer-forming material (C4) for coating on a substrate.
Using the antifouling layer forming material (C4), the same procedure as in Example 1 was carried out to produce an adhesive tape (C4).
The configuration of the adhesive tape (C4) was antifouling layer (thickness = 150 μm) / base material layer (thickness = 150 μm) / adhesive layer (thickness = 50 μm).
The evaluation results are shown in Table 2.

[Comparative Example 5]
In the formulation shown in Table 1, silicone oil (KF50-100cs, non-reactive silicone oil, Shin-Etsu Chemical Co., Ltd.) as an antifouling agent for vinyl chloride (Mitsubishi Kasei Vinyl Co., Ltd., trade name “Vinica 37H”) ) Was added for 10 minutes using a super mixer, and the antifouling agent was uniformly dispersed in the resin. After stirring, the mixture was sufficiently kneaded on two mill rolls heated to 180 ° C. to prepare a film (C5) having a thickness of 150 μm. The outdoor antifouling test was carried out by fixing the film (C5) with a nail on a vinyl chloride plate cut out to 10 cm × 10 cm.
The evaluation results are shown in Table 2.

[Comparative Example 6]
In the formulation shown in Table 1, polymethyl methacrylate (manufactured by Wako Pure Chemical Industries, Ltd.) as an antifouling agent, silicone oil (KF50-100cs, non-reactive silicone oil, manufactured by Shin-Etsu Chemical Co., Ltd.), as solvent After adding ethyl acetate, the mixture was mixed for 10 minutes using a homomixer to disperse the antifouling agent uniformly in the resin. After stirring, it was coated on a PET separator with an applicator and dried at 70 ° C. to prepare a film (C6) having a thickness of 150 μm. The outdoor antifouling test was carried out by fixing a film (C6) with a nail on a vinyl chloride plate cut out to 10 cm × 10 cm.
The evaluation results are shown in Table 2.

  Since the aquatic organism adhesion preventing adhesive tape of the present invention can prevent aquatic organisms from adhering and breeding, underwater structures (ships, buoys, port facilities, offshore oilfield facilities, waterways for power plant cooling water, factory cooling) It can be suitably used for water channels and floating passages.

DESCRIPTION OF SYMBOLS 1 Release film 2 Antifouling layer 3 Base material layer 4 Adhesive layer 100 Aquatic organism adhesion prevention adhesive tape

Claims (1)

An adhesive tape comprising an antifouling layer, a base material layer and an adhesive layer in this order,
The material of the base material layer is at least one selected from polyurethane resin and polyurethane acrylic resin,
The elastic modulus of the base material layer is 1000 MPa or less,
The outermost layer on the antifouling layer side is the antifouling layer or a release film provided on the antifouling layer surface,
The antifouling layer comprises a silicone resin;
The silicone resin is at least one selected from a condensation type silicone resin and an addition type silicone resin,
The antifouling layer contains a silicone oil represented by the general formula (I),
The content ratio of the silicone oil to the silicone resin is 2% by weight or more,
The adhesive layer has a 180-degree peel adhesive strength of 30 N / 20 mm or less at 23 ° C. and a tensile speed of 300 mm / min.
Aquatic organism adhesion prevention adhesive tape.
Here, in general formula (I), R ¹ is the same or different and represents an alkyl group having 1 to 10 carbon atoms, an aryl group, an aralkyl group, a polyether group, or a hydroxyl group, and R ² is the same or different. Represents an alkyl group having 1 to 10 carbon atoms, an aryl group, an aralkyl group, and a polyether group, and n represents an integer of 0 to 150.
However, the case where there is a silicone primer layer between the antifouling layer and the base material layer is excluded.
However, the case where the silicone resin is a silicone resin having a hydroxyalkyl group or an alkoxy group having a number average molecular weight of 250 to 30000 and a viscosity of 20 to 50000 centistokes represented by the following general formula is excluded.
(In the formula, R represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, an aryl group or an aralkyl group, and R ¹ has 1 to 40 carbon atoms which may intervene an ether group, an ester group or -NH-. R ² represents a hydrogen atom or a lower alkyl group having 1 to 6 carbon atoms, and x and y are 0.01 ≦ x <3.99 and 0.01 ≦ y <3. 99 and 0.02 ≦ x + y <4.)