JP5484740B2 - Soundproof synthetic resin pipe and method for producing the same - Google Patents
Soundproof synthetic resin pipe and method for producing the same Download PDFInfo
- Publication number
- JP5484740B2 JP5484740B2 JP2009010965A JP2009010965A JP5484740B2 JP 5484740 B2 JP5484740 B2 JP 5484740B2 JP 2009010965 A JP2009010965 A JP 2009010965A JP 2009010965 A JP2009010965 A JP 2009010965A JP 5484740 B2 JP5484740 B2 JP 5484740B2
- Authority
- JP
- Japan
- Prior art keywords
- synthetic resin
- sound
- layer
- soundproof
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、優れた吸音性と遮音性を有する防音性合成樹脂管であって、制振作用に優れ、安価に製造できるものであり、不織布または連続気泡フォームからなる吸音層表面に不燃性無機化合物微粉とポリマー混和剤とからなる柔軟性のある遮音層が形成されてなる、低層住宅やビル等の配管で排水時に発生する流水音を遮断するのに好適な防音性合成樹脂管に関する。 The present invention is a sound-insulating synthetic resin tube having excellent sound absorption and sound insulation, which has excellent vibration damping action and can be manufactured at low cost, and has a non-combustible inorganic surface on the surface of the sound absorption layer made of nonwoven fabric or open-cell foam. The present invention relates to a soundproof synthetic resin pipe suitable for blocking running sound generated at the time of drainage in pipes of low-rise houses and buildings, in which a flexible sound insulation layer composed of compound fine powder and a polymer admixture is formed.
防音材は、通常音波を熱に変換して音量を低下させる吸音層と、吸音層を透過してきた音を発生した方向に反射する遮音層とから構成される。したがって、防音効果は吸音層の吸音効果と遮音層の反射効果の組み合わされたものとして定義されている。
従来、住宅用排水管には、合成樹脂管表面に水硬性材料（例えば、繊維強化モルタル等）で被覆した被覆二層合成樹脂管が主として使用されてきた。これ自体は、安価で、耐火性があり、施工も容易で、かつ、水の流れが良好であるという優れたものであるため、広く使用されてきたが、この種の二層管は、吸音材層を有していないため、遮音性能が低い。
The soundproofing material is usually composed of a sound absorbing layer that converts sound waves into heat to lower the volume, and a sound insulating layer that reflects in the direction in which the sound transmitted through the sound absorbing layer is generated. Therefore, the sound insulation effect is defined as a combination of the sound absorption effect of the sound absorption layer and the reflection effect of the sound insulation layer.
Conventionally, a coated two-layer synthetic resin pipe in which a surface of a synthetic resin pipe is covered with a hydraulic material (for example, fiber reinforced mortar) has been mainly used for a residential drain pipe. This itself has been widely used because it is inexpensive, fireproof, easy to construct, and has a good flow of water. Since it does not have a material layer, the sound insulation performance is low.
この対策として、住宅やビル等の排水により発生する音を遮断するために、配管の外周にグラスウール、ロックウール等の吸音材や、これらの吸音材からなる吸音シートを巻き付けて針金等で固定することが行われている。
また、配管等においては、筒状に成形した遮音シートの内周面に、軟質吸音材を積層し、長手方向に亘って割り溝を設けた配管用遮音材が提案されている（特許文献１）。
しかしながら、現場でグラスウール等の吸音材や吸音シートを配管に巻き付けて針金等で固定する方法は、施工に手間がかかり、吸音効果はともかく、防音効果は十分なものとは言えない。また、筒状に曲成して割り溝を設けた吸音材を形成するには、特別な工程を必要とし、コストアップの要因となる。
As a countermeasure, in order to cut off the sound generated by the drainage of houses and buildings, a sound absorbing material such as glass wool or rock wool or a sound absorbing sheet made of these sound absorbing materials is wrapped around the outer periphery of the pipe and fixed with a wire or the like. Things have been done.
Moreover, in piping etc., the sound insulation material for piping which laminated | stacked the soft sound-absorbing material on the inner peripheral surface of the sound insulation sheet shape | molded in the cylinder shape, and provided the dividing groove over the longitudinal direction is proposed (patent document 1). ).
However, the method of winding a sound absorbing material such as glass wool or a sound absorbing sheet around a pipe and fixing it with a wire or the like on the site is troublesome in construction, and it cannot be said that the soundproofing effect is sufficient, regardless of the sound absorbing effect. In addition, a special process is required to form a sound absorbing material that is bent into a cylindrical shape and has a split groove, which increases costs.
吸音材として、かさ密度０．０２〜０．２、厚み２０〜５０ｍｍの不織布の片側面から炭酸カルシウム、酸化鉄、フライアッシュ又は硫酸バリウム等の無機粉末を含有するスラリーを含浸させて形成した含浸層を有し、該含浸層のかさ密度を０．１〜１．８、厚み２〜５ｍｍとした遮音用含浸不織布（特許文献２）の提案があるが、これは、遮音材が組み込まれていないため、吸音性はあるが、この層を通過した音はそのまま外部に放散するため、防音性としては問題がある。 Impregnation formed by impregnating a slurry containing inorganic powder such as calcium carbonate, iron oxide, fly ash or barium sulfate from one side of a nonwoven fabric having a bulk density of 0.02 to 0.2 and a thickness of 20 to 50 mm as a sound absorbing material There is a proposal of an impregnated nonwoven fabric for sound insulation (Patent Document 2) in which a bulk density of the impregnated layer is 0.1 to 1.8 and a thickness is 2 to 5 mm. Since there is no sound absorption, sound passing through this layer is diffused to the outside as it is, so there is a problem as soundproofing.
また、配管部材と、前記配管部材の外周を囲着する配管防音部材からなる配管防音構造であって、前記配管防音部材が、吸音材、遮音材、防振材及び制振材からなる防音材からなり、前記配管防音部材が少なくとも前記吸音材を含む２層以上の防音材層を備えており、前記吸音材が８５重量％以上の無機質人造繊維の不織布からなり、その表面及び裏面の一方又は双方に遮蔽層が設けられた配管防音構造（特許文献３）が提案されている。
これは、吸音材層、遮音材層を設けた防音材構造を示しているが、それぞれの層は粘着材層、接着剤層等を用いて接合されているものであり、遮音材層が排水時の振動や結露水等で剥離する危険がある上、高価なゴムやプラスチックシートを用いるため、コストダウンさせることが困難である。
Also, a pipe soundproof structure comprising a pipe member and a pipe soundproof member surrounding the outer periphery of the pipe member, wherein the pipe soundproof member is composed of a sound absorbing material, a sound insulating material, a vibration insulating material, and a vibration insulating material. And the pipe soundproofing member includes at least two soundproofing material layers including the sound absorbing material, and the sound absorbing material is made of 85% by weight or more of inorganic man-made non-woven fabric, and one or both of its front and back surfaces A pipe soundproof structure (Patent Document 3) in which a shielding layer is provided is proposed.
This shows a soundproof material structure provided with a sound absorbing material layer and a sound insulating material layer, but each layer is bonded using an adhesive material layer, an adhesive layer, etc., and the sound insulating material layer is drained. There is a risk of peeling due to vibrations or condensed water, and expensive rubber or plastic sheets are used, making it difficult to reduce costs.
さらに、遮音層と吸音層の二層からなる配管用防音材の配管で、遮音層（アスファルトに熱可塑性ポリマー、無機充填剤を添加後均一に混合して得られたもの）と吸音層は接着固定され、配管に施工する際、配管の直線部分は、吸音層の配管側にシワを配管と平行に発生させ、配管と配管用防音材とが部分的に接触して空気層が形成されるようにする配管の遮音方法（特許文献４）の提案がある。
この場合、吸音層と遮音層を設けているため、防音効果は高いと思われるが、遮音層が高価である上、吸音層の配管側に、配管に対して高精度に平行にシワを作製することは、工程的に面倒、煩雑であり、問題がある。
Furthermore, it is a pipe made of a sound insulation material for pipes consisting of two layers: a sound insulation layer and a sound absorption layer. The sound insulation layer (obtained by mixing thermoplastic polymer and inorganic filler in asphalt and then mixing uniformly) and the sound absorption layer are bonded. When fixed to the pipe, the straight part of the pipe generates wrinkles on the pipe side of the sound absorbing layer in parallel with the pipe, and the pipe and the soundproofing material for the pipe partially contact to form an air layer There is a proposal of a sound insulation method for a pipe (Patent Document 4).
In this case, the sound-absorbing layer and the sound-insulating layer are provided, so the sound-insulating effect seems to be high, but the sound-insulating layer is expensive, and wrinkles are made on the piping side of the sound-absorbing layer with high accuracy parallel to the piping. Doing this is troublesome, complicated and problematic.
本発明は、合成樹脂管表面に、不燃性無機化合物微粉とポリマー混和剤とからなる遮音層と、不織布または連続気泡フォームからなる吸音層との２層からなる防音層を有する防音性合成樹脂管であって、防音性、制振性が高く、安価に製造、施工が可能であり、流水の衝撃等による振動、騒音を効果的に防止し、低層住宅用の防音性排水管として優れた効果を有する防音性合成樹脂管およびその製造方法の提供を目的とする。 The present invention relates to a soundproof synthetic resin pipe having a soundproof layer comprising two layers of a sound insulation layer comprising a nonflammable inorganic compound fine powder and a polymer admixture and a sound absorption layer comprising a nonwoven fabric or open cell foam on the surface of the synthetic resin pipe. It is highly soundproof and vibration-damping, can be manufactured and installed at low cost, effectively prevents vibration and noise caused by the impact of running water, etc., and has excellent effects as a soundproof drainage pipe for low-rise housing An object of the present invention is to provide a sound-insulating synthetic resin tube having the above and a method for producing the same.
本発明は、
［１］合成樹脂管の外表面に不織布からなる吸音層が形成され、前記吸音層の表面に不燃性無機化合物微粉およびポリマー混和剤とからなるスラリー硬化物による気密性の遮音層が形成されていることを特徴とする防音性合成樹脂管、
The present invention
[1] the sound absorbing layer made of non-woven fabric on the outer surface of the synthetic resin pipe is formed, the sound absorbing layer airtight sound insulation layer by the slurry cured product comprising a non-combustible inorganic compound fine and polymeric admixture to the surface of formed A soundproof synthetic resin tube,
［２］前記遮音層が、前記不織布に前記スラリーを含浸させ、硬化させたスラリー含浸層を含むものであることを特徴とする上記［１］記載の防音性合成樹脂管、
［３］前記スラリー硬化物は、破断時の伸び率が１０％以上であることを特徴とする上記［１］または［２］に記載の防音性合成樹脂管、
［４］前記合成樹脂管が、硬質ポリ塩化ビニルまたはポリエチレンテレフタレートからなることを特徴とする上記［１］〜［３］のいずれかに記載の防音性合成樹脂管、
［５］前記ポリマー混和剤が、水性ポリマーディスパージョンまたは再乳化型粉末樹脂であることを特徴とする上記［１］〜［４］のいずれかに記載の防音性合成樹脂管、
［６］前記不燃性無機化合物微粉が、炭酸カルシウム、水酸化カルシウム、水酸化アルミニウム、水酸化マグネシウム、硫酸バリウム、硫酸カルシウム、タルク、高炉スラグ、砂、硅砂、ポゾラン、マイカ、珪藻土、酸化チタン、酸化鉄、フェライトおよびフライアッシュのうちの少なくとも１種であることを特徴とする上記［１］〜［５］のいずれかに記載の防音性合成樹脂管、
［７］前記不織布が、有機系繊維または無機系繊維の圧縮体またはニードルパンチされたフェルトであることを特徴とする上記［１］〜［６］のいずれかに記載の防音性合成樹脂管、
[2] The soundproofing synthetic resin pipe according to the above [1], wherein the sound insulating layer includes a slurry impregnated layer obtained by impregnating the nonwoven fabric with the slurry and curing the nonwoven fabric.
[3] The soundproof synthetic resin pipe according to [1] or [2], wherein the cured slurry has an elongation at break of 10% or more,
[ 4 ] The soundproof synthetic resin pipe according to any one of [1] to [3], wherein the synthetic resin pipe is made of hard polyvinyl chloride or polyethylene terephthalate.
[ 5 ] The soundproof synthetic resin pipe according to any one of [1] to [4], wherein the polymer admixture is an aqueous polymer dispersion or a re-emulsifying powder resin.
[ 6 ] The incombustible inorganic compound fine powder is calcium carbonate, calcium hydroxide, aluminum hydroxide, magnesium hydroxide, barium sulfate, calcium sulfate, talc, blast furnace slag, sand, cinnabar, pozzolana, mica, diatomaceous earth, titanium oxide, The soundproof synthetic resin pipe according to any one of the above [1] to [ 5 ], which is at least one of iron oxide, ferrite, and fly ash,
[ 7 ] The soundproof synthetic resin pipe according to any one of [1] to [ 6 ], wherein the nonwoven fabric is a compressed body of organic fiber or inorganic fiber or a needle punched felt.
［８］低層住宅用排水管用であることを特徴とする上記［１］〜［７］のいずれかに記載の防音性合成樹脂管、 [ 8 ] The soundproofing synthetic resin pipe according to any one of the above [1] to [7], which is used for a low-rise residential drainage pipe,
［９］上記防音性合成樹脂管を製造する方法であって、合成樹脂製パイプの外表面に不織布からなる吸音層を形成した後、前記吸音層の表面に不燃性無機化合物微粉およびポリマー混和剤からなるスラリーを塗布、吹き付けまたは浸漬することにより遮音層を形成することを特徴とする防音性合成樹脂管の製造方法、
［１０］上記防音性合成樹脂管を製造する方法であって、筒状に成形された不織布からなる吸音層の外表面に不燃性無機化合物微粉とポリマー混和剤とからなる遮音層が形成された配管用防音材に、合成樹脂管を挿入することを特徴とする防音性合成樹脂管の製造方法、
を開発することにより上記の課題を解決した。
[9] above in a method of producing a sound insulation synthetic resin tube, synthesis after the outer surface of the resin pipe forming a sound absorbing layer made of non-woven fabric, the non-combustible on the surface of the backing layer inorganic compound fines and polymer admixtures A method for producing a soundproof synthetic resin tube, characterized in that a sound insulation layer is formed by applying, spraying or dipping a slurry comprising:
[10] A method for manufacturing the acoustic insulation synthetic resin tube, sound insulation layer on the outer surface of the sound absorbing layer made of molded into a cylindrical shape nonwoven fabric made of a non-combustible inorganic compound fine and polymer admixture is formed A method for producing a soundproofing synthetic resin pipe, characterized by inserting a synthetic resin pipe into a soundproofing material for piping,
By solving this problem, the above problems were solved.
本発明の防音性合成樹脂管は、不織布からなる吸音層と不燃性無機化合物微粉とポリマー混和剤からなるスラリーの硬化物（以下、「スラリー硬化物」と略称する。）からなる遮音層とからなり、従来の耐火性二層管に比し、軽量であって防音性に優れており、安価に製造可能である。
内側の吸音層は、不織布からなるため、振動をよく吸収し、合成樹脂管自体の振動およびその内部の液の流れに基づく振動の伝達を効率よく制御できる。
また、表面層の遮音層は、不燃性無機化合物微粉からなるにもかかわらず、ポリマー混和剤の粘弾性により、ある程度の弾力性、可撓性を有するため、施工も容易であるという特徴がある。
The soundproofing synthetic resin tube of the present invention comprises a sound absorbing layer made of nonwoven fabric, and a sound insulating layer made of a cured product of a slurry made of nonflammable inorganic compound fine powder and a polymer admixture (hereinafter abbreviated as “slurry cured product”). Therefore, it is lighter and more soundproof than a conventional fireproof double-layer tube, and can be manufactured at low cost.
Since the inner sound absorbing layer is made of non-woven fabric , it absorbs vibrations well and can efficiently control the vibration of the synthetic resin tube itself and the vibration transmission based on the liquid flow inside.
In addition, the sound insulation layer of the surface layer has a certain elasticity and flexibility due to the viscoelasticity of the polymer admixture, despite the fact that it is made of non-combustible inorganic compound fine powder. .
具体的には、本発明は、以下の点にメリットがある。
（１）合成樹脂管表面は、不燃性のスラリー硬化物で被覆されているため、吸音層に無機系繊維を使用したときは不燃性を有しているとともに、施工時に吸音層の不織布繊維の飛散を防止することができる。
（２）合成樹脂管の表面は、不織布製吸音層と弾性のあるスラリー硬化物による遮音層を有しているため、排水管等としての振動に対する防音性は抜群に高い。
（３）弾性のあるスラリー硬化物を使用しているため、スラリーの硬化後であっても、柔軟性があり、成形加工が容易である。
Specifically, the present invention is advantageous in the following points.
(1) Since the surface of the synthetic resin tube is coated with a non-flammable slurry cured product, it has non-flammability when inorganic fibers are used for the sound absorbing layer, and the non-woven fiber of the sound absorbing layer at the time of construction. Scattering can be prevented.
(2) Since the surface of the synthetic resin pipe has a non-woven sound absorbing layer and a sound insulation layer made of a cured slurry with elasticity, the sound insulation against vibration as a drain pipe or the like is remarkably high.
(3) Since an elastic slurry cured product is used, even after the slurry is cured, it is flexible and easy to mold.
スラリー硬化物は、それ自体がある程度の難燃性能を有しているため、筒状とした防音材に合成樹脂管をその内部に挿入することにより、戸建て住宅等の低層住宅用の難燃性がある排水等配管用防音パイプを容易に製造することができる。 Since the cured slurry itself has a certain level of flame retardancy, it can be used for low-rise buildings such as detached houses by inserting a synthetic resin tube into the cylindrical soundproof material. It is possible to easily manufacture a soundproof pipe for piping such as drainage.
以下、図面を参照して、本発明を説明する。
図１に、合成樹脂管１の表面に、吸音層２である不織布、および、その外側に遮音層３である不燃性無機化合物微粉とポリマー混和剤とからなるスラリー硬化物層とが形成された本発明の防音性合成樹脂管を示す。なお、吸音層２と遮音層３の間に、スラリー含浸層が形成されていてもよい。
Hereinafter, the present invention will be described with reference to the drawings.
1, the surface of the
本発明において使用する合成樹脂管は、耐熱性のない通常の建築物の排水管等に一般的に使用されているポリ塩化ビニル管、ポリエチレンテレフタレート管等である。
本発明における吸音材層は、不織布または連続気泡フォームが使用可能ではあるが、特に、不織布が好ましい。不織布としては、原材料の繊維は有機系繊維または無機系繊維のいずれであってもよい。
The synthetic resin pipe used in the present invention is a polyvinyl chloride pipe, a polyethylene terephthalate pipe or the like generally used for a drainage pipe of a normal building having no heat resistance.
As the sound absorbing material layer in the present invention, a nonwoven fabric or open-cell foam can be used, but a nonwoven fabric is particularly preferable. As the nonwoven fabric, the raw material fibers may be either organic fibers or inorganic fibers.
本発明における遮音層は、不燃性無機化合物微粉とポリマー混和剤のスラリー硬化物とからなるものである。
不燃性無機化合物微粉としては、安価で入手しやすく、取り扱いが安全で、耐熱性のあるものであれば、ほとんどのものを使用することができる。例えば、炭酸カルシウム、水酸化カルシウム、水酸化アルミニウム、水酸化マグネシウム、硫酸バリウム、硫酸カルシウム、タルク、高炉スラグ、砂、硅砂、ポゾラン、マイカ、珪藻土、酸化チタン、酸化鉄、フェライトおよびフライアッシュを挙げることができる。
The sound insulation layer in the present invention comprises a nonflammable inorganic compound fine powder and a cured slurry of a polymer admixture.
As the incombustible inorganic compound fine powder, almost any fine powder can be used as long as it is inexpensive, easily available, safe to handle, and heat resistant. Examples include calcium carbonate, calcium hydroxide, aluminum hydroxide, magnesium hydroxide, barium sulfate, calcium sulfate, talc, blast furnace slag, sand, dredged sand, pozzolana, mica, diatomaceous earth, titanium oxide, iron oxide, ferrite and fly ash. be able to.
本発明において、遮音層に使用する不燃性無機化合物微粉としては、特に、炭酸カルシウム、水酸化カルシウム、水酸化アルミニウム、タルク、高炉スラグ、砂、硅砂の使用が有効である。中でも、難燃性付与のためには、難燃材として用いられている炭酸カルシウム、水酸化カルシウム、水酸化アルミニウムを用いることが好ましい。
これらの不燃性無機化合物微粉は、水硬性材料、特に、セメント系材料とは異なり、水和反応が進むことにより硬化が進むことはなく、硬化することにより脆くなって靱性が低下し、耐久性が低下するということがない。また、この結果、不燃性無機化合物とポリマー混和剤のスラリーの硬化物層は、外からの振動を吸収し、外部への伝導を効果的に遮断できる性能がある。
In the present invention, the use of calcium carbonate, calcium hydroxide, aluminum hydroxide, talc, blast furnace slag, sand and cinnabar is particularly effective as the incombustible inorganic compound fine powder used for the sound insulation layer. Among these, for imparting flame retardancy, it is preferable to use calcium carbonate, calcium hydroxide, or aluminum hydroxide used as a flame retardant.
Unlike non-hydraulic materials, especially cement-based materials, these non-combustible inorganic compound fine powders do not proceed with hardening due to the progress of the hydration reaction, but become brittle and reduce toughness when cured. There is no decline. As a result, the cured product layer of the slurry of the non-combustible inorganic compound and the polymer admixture has the capability of absorbing external vibration and effectively blocking conduction to the outside.
本発明におけるポリマー混和剤としては、その配合により、遮音層に粘弾性を付与するものであり、例えば、ゴム系ラテックス、樹脂エマルジョン（再乳化型粉末樹脂であってもよい。）等の水性ディスパージョン、好ましくは、ゴム系ラテックス、例えば、天然ゴム（ＮＲ系）ラテックス、合成ゴム系ラテックス（スチレン−ブタジエンゴム；ＳＢＲ系、クロロプレンゴム；ＣＲ系、メタクリル酸メチル−ブタジエンゴム；ＭＢＲ系、アクリロニトリル−ブタジエンＮＢＲ系、イソプレンゴム；ＩＲ系など）等を配合することが必要である。
前記樹脂エマルジョンとしては、再乳化型粉末樹脂（ＪＩＳ Ａ ６２０３）を水中に分散したもの、または、各種熱可塑性樹脂もしくはゴム等との混合エマルジョンも使用することができる。
The polymer admixture in the present invention imparts viscoelasticity to the sound insulation layer by its blending. For example, aqueous dispersers such as rubber latex and resin emulsion (may be re-emulsified powder resin). John, preferably rubber latex such as natural rubber (NR) latex, synthetic rubber latex (styrene-butadiene rubber; SBR, chloroprene rubber; CR, methyl methacrylate-butadiene rubber; MBR, acrylonitrile- It is necessary to blend butadiene NBR, isoprene rubber; IR, etc.).
As the resin emulsion, a re-emulsified powder resin (JIS A 6203) dispersed in water, or a mixed emulsion with various thermoplastic resins or rubbers can be used.
ポリマー混和剤の機能としては、安価で、密度が適度にあり、破断時の伸び率が１０％以上ある、遮音性に優れた遮音層を形成することができることが求められる。
また、これらのポリマー混和剤は、目的に応じて選択することが必要であり、ワーカビリティー、コンシスタンシー等を考慮し、例えば、耐光性、難燃性を目的とするときはＣＲ系を、伸びの性能を目的とするときはＮＲ系、ＭＢＲ系等を選択することになる。樹脂系の場合に伸びを確保するためには、配合比を多くする必要がある。
The function of the polymer admixture is required to be able to form a sound insulation layer that is inexpensive, has an appropriate density, has an elongation at break of 10% or more, and is excellent in sound insulation.
These polymer admixtures need to be selected according to the purpose. Considering workability, consistency, etc., for example, when aiming at light resistance and flame retardancy, the CR system is elongated. In order to achieve the above performance, the NR system, the MBR system, or the like is selected. In order to ensure elongation in the case of a resin system, it is necessary to increase the compounding ratio.
前記遮音層は、配管のサイズにより最低限の必要な破断時の伸び率が異なり、小径管ほど曲率が小さくなるため、大きな破断時の伸び率が必要となる（ポリマー混和剤配合比率が高くなる。）。通常、建築で使用される一般的な配管サイズ（呼び径２０〜１５０ｍｍφ）では１０％以上が必要である。
不燃性無機化合物微粉（Ｃ）とポリマー混和剤（Ｐ）の配合比（Ｐ／Ｃ）は、使用する材料、目的とするスラリー硬化物の破断時の伸び率等により変わるが、セレタックＧ（登録商標）でＰ／Ｃ＝３０〜２００％であれば、１０％以上の破断時の伸び率を確保することができる。破断時の伸び率を大きくしたいときは、Ｐ／Ｃを大きくすればよい。
The minimum required elongation at break differs depending on the size of the pipe, and the sound insulation layer requires a larger elongation at break because the smaller the diameter of the pipe, the greater the elongation at break (the polymer blending ratio increases). .) Normally, 10% or more is necessary for a general piping size (nominal diameter of 20 to 150 mmφ) used in construction.
The compounding ratio (P / C) of the nonflammable inorganic compound fine powder (C) and the polymer admixture (P) varies depending on the material used, the elongation at break of the target slurry cured product, etc., but Celetac G (registered) (Trademark), if P / C = 30 to 200%, an elongation at break of 10% or more can be secured. To increase the elongation at break, P / C should be increased.
また、使用する硬化前の不燃性無機化合物微粉とポリマー混和剤のスラリーの粘度は、不織布の面重量（密度）、不織布層の厚さ、含浸層の厚さ等を考慮して決定する必要がある。該スラリーは、粘度を調整することにより、それ自体保型性を付与することができるため、不織布層に含浸させない時においても、吸音層表面に安定しており、引張強度および曲げ強度があり、気密性、耐熱性のある遮音層を形成する。 In addition, the viscosity of the slurry of the non-combustible inorganic compound fine powder and polymer admixture before curing used must be determined in consideration of the surface weight (density) of the nonwoven fabric, the thickness of the nonwoven fabric layer, the thickness of the impregnation layer, and the like. is there. By adjusting the viscosity, the slurry can impart shape retention itself, so even when the nonwoven fabric layer is not impregnated, it is stable on the surface of the sound absorbing layer and has tensile strength and bending strength. An airtight and heat resistant sound insulation layer is formed.
吸音層として使用する不織布のための有機系繊維としては、ポリエチレンテレフタレート系（以下、「ＰＥＴ系ポリエステル」という）、ポリアミド（６−ナイロン、６，６ナイロン等）、アクリル系繊維、木綿、羊毛等、各種のものが使用することができる。無機系繊維としては、ガラス繊維、ロックウール、セラミック繊維等が挙げられる。
制振、吸音効果の点で、不織布またはフェルトを使用することが好ましい。特に好ましいものの例としては、ポリエステル等の合成繊維からなる不織布が挙げられ、耐火性の点からは、ガラス繊維、ロックウール、セラミック繊維等の不織布が好ましい。
Examples of organic fibers for the nonwoven fabric used as the sound absorbing layer include polyethylene terephthalate (hereinafter referred to as “PET polyester”), polyamide (6-nylon, 6,6 nylon, etc.), acrylic fibers, cotton, wool, etc. Various types can be used. Examples of the inorganic fiber include glass fiber, rock wool, and ceramic fiber.
It is preferable to use a nonwoven fabric or felt in terms of vibration damping and sound absorption effects. Particularly preferable examples include nonwoven fabrics made of synthetic fibers such as polyester. From the viewpoint of fire resistance, nonwoven fabrics such as glass fibers, rock wool and ceramic fibers are preferred.
なお、本発明においては、フェルトとは、圧縮した繊維層、ニードルパンチしたフェルト等を含むものである。
使用するフェルト層の厚さは、目的、吸音性、材質や使用箇所により変更が必要であるが、通常２〜３０ｍｍ、好ましくは３〜１５ｍｍである。
In the present invention, the felt includes a compressed fiber layer, a needle punched felt, and the like.
Although the thickness of the felt layer to be used needs to be changed depending on the purpose, sound absorption, material and location of use, it is usually 2 to 30 mm, preferably 3 to 15 mm.
連続気泡フォームとしては、発泡ウレタンフォーム等の連続気泡フォームも使用可能であり、フェルト層とほぼ同一程度の厚さで使用することができる。連続気泡フォームは、不織布に比して、スラリー硬化物含浸層に対する補強効果が小さく、不織布に比してメリットは小さい。以下においては、不織布を代表として説明する。 As the open-cell foam, open-cell foam such as foamed urethane foam can be used, and it can be used with a thickness approximately the same as the felt layer. The open-cell foam has a smaller reinforcing effect on the slurry-cured product-impregnated layer than the non-woven fabric, and has less merit than the non-woven fabric. Below, a nonwoven fabric is demonstrated as a representative.
本発明における配管用防音材は、内面は不織布の吸音層であり、その外表面を不燃性無機化合物微粉とポリマー混和剤とからなるスラリー硬化物による遮音層で被覆されているものである。したがって、この防音材は、処理したい発生源の壁面等に貼り付けることにより防音することできる。この場合、その外表面を、さらに、樹脂フィルム、織布、表面コート材、遮音シート、その他の表面材で被覆することは自由である。
前記遮音層は、不燃性無機化合物微粉とポリマー混和剤とからなるスラリーの硬化に際し、ある程度の収縮が避けられないが、内面に不織布層があるため、それらの歪みは吸収され、内部に対する形状保持性、成形性に悪影響を与えない。また、該遮音層は、遮音性に優れていることはもちろんであるが、排水管等の被覆に使用したとき、振動がかかっても、前記吸音層の助けもあって、ひび割れの危険がないものである。
In the soundproofing material for piping in the present invention, the inner surface is a non-woven sound-absorbing layer, and the outer surface is coated with a sound insulating layer made of a slurry cured product composed of a non-combustible inorganic compound fine powder and a polymer admixture. Therefore, this soundproofing material can be soundproofed by sticking it to the wall surface of the source to be treated. In this case, the outer surface can be further covered with a resin film, a woven fabric, a surface coating material, a sound insulating sheet, and other surface materials.
The sound insulation layer is inevitably shrunk to some extent when curing a slurry composed of a non-combustible inorganic compound fine powder and a polymer admixture. Does not adversely affect properties and moldability. In addition, the sound insulation layer is excellent in sound insulation, but when used for covering a drain pipe or the like, there is no risk of cracking even if vibration is applied with the help of the sound absorption layer. Is.
前記スラリー硬化物による遮音層の厚さは、適宜選ぶ必要があるが、通常０．５〜５ｍｍ、スラリー含浸層を厚くしすぎると、防音材の柔軟性が低下するため、好ましくは１〜３ｍｍ程度で、遮音性を発揮することができる。 The thickness of the sound insulation layer by the slurry cured product needs to be appropriately selected, but usually 0.5 to 5 mm, and if the slurry impregnated layer is too thick, the flexibility of the soundproofing material is lowered. Sound insulation can be exhibited at a certain degree.
特に、前記防音材は、遮音層が不燃性無機化合物微粉とポリマー混和剤とからなるスラリー硬化物であるため、ある程度の加工は可能ではある。Ｙ字管、Ｔ字管、継手等においては、予め不織布等の吸音層を、これらの防音性を必要とするものに巻き付け、接着テープまたは紐等を用いて固定した後、その表面に、不燃性無機化合物微粉とポリマー混和剤とからなるスラリーを、浸漬法、吹き付け法またはコーターを使用した塗布法等により均一なスラリー層として形成することが好ましい。このようにすれば、遮音層が、成形困難な形状であっても、不定形のスラリーで形成することにより、遮音層のスラリー硬化物層を一体的に均一に形成することが可能である。 In particular, the soundproofing material can be processed to some extent because the soundproofing layer is a slurry cured product composed of a nonflammable inorganic compound fine powder and a polymer admixture. For Y-shaped tubes, T-shaped tubes, joints, etc., a sound absorbing layer such as a nonwoven fabric is wrapped around these materials that require soundproofing beforehand, fixed with adhesive tape or string, and then nonflammable on the surface. It is preferable to form a slurry composed of a fine inorganic compound powder and a polymer admixture as a uniform slurry layer by a dipping method, a spraying method or a coating method using a coater. In this way, even if the sound insulation layer has a shape that is difficult to form, the slurry cured product layer of the sound insulation layer can be formed uniformly and uniformly by forming it with an irregular slurry.
以上から明らかなように、本発明の防音性合成樹脂管は、吸音層と遮音層の間に接着剤は使用しない。吸音層の不織布層の一表面側のみに、硬化物となって遮音層となるスラリーを塗布または含浸させ、硬化させることにより、表面側に重量のある遮音層を形成する。音源からの音波は、その一部が吸音層で熱として変換されて吸音され、この吸音層を透過してきた音波を遮音層で反射させ、音源の反対側または排水管等の外部に音波の漏れることを防止するものである。このため、遮音層は重量が必要であるが、防音性合成樹脂管としては軽量であることが求められており、遮音層の厚みで、これを調整することになる。 As is clear from the above, the soundproofing synthetic resin tube of the present invention does not use an adhesive between the sound absorbing layer and the sound insulating layer. A heavy weight sound insulation layer is formed on the surface side by applying or impregnating a slurry which becomes a cured product and becomes a sound insulation layer only on the one surface side of the nonwoven fabric layer of the sound absorbing layer. The sound wave from the sound source is partly converted as heat in the sound absorbing layer and absorbed, and the sound wave that has passed through the sound absorbing layer is reflected by the sound insulating layer, and the sound wave leaks to the opposite side of the sound source or the outside such as a drain pipe. This is to prevent this. For this reason, although the sound insulation layer needs weight, it is calculated | required that it is lightweight as a soundproof synthetic resin pipe | tube, and this is adjusted with the thickness of a sound insulation layer.
本発明の防音性合成樹脂管における防音材は、柔軟性に富み、成形性に優れているため、防音性を必要とする合成樹脂管の防音被覆材として好適である。
すなわち、（ａ）予め吸音層を筒状に成形し、その外表面側からスラリーを含浸させて筒状の防音材とした後、合成樹脂管に嵌入してもよく、また、（ｂ）筒状の吸音層を合成樹脂管に嵌入した後、その外表面側からスラリーを含浸させて、防音性を有する合成樹脂管を作製してもよい。本発明の方法は、遮音層につなぎ目ができず、好ましい方法である。この防音性合成樹脂管は、通常、アパート、戸建て住宅等の建築物のトイレ、風呂場、台所等の排水に用いられている排水管等に利用することができる。これらの排水管は、排水騒音を大幅に低減することが可能である。
Since the soundproofing material in the soundproofing synthetic resin pipe of the present invention is rich in flexibility and excellent in moldability, it is suitable as a soundproof coating material for a synthetic resin pipe that requires soundproofing.
That is, (a) a sound-absorbing layer may be formed into a cylindrical shape in advance and impregnated with slurry from the outer surface side to form a cylindrical soundproofing material, and then fitted into a synthetic resin tube. After inserting the sound absorbing layer into the synthetic resin tube, the synthetic resin tube having soundproofing properties may be produced by impregnating the slurry from the outer surface side. The method of the present invention is a preferable method because there is no joint in the sound insulation layer. This soundproofing synthetic resin pipe can be used for drainage pipes and the like which are usually used for drainage of toilets, bathrooms, kitchens and the like of buildings such as apartments and detached houses. These drain pipes can greatly reduce drainage noise.
以下、本発明を実施例に基づきさらに具体的に説明するが、本発明は下記実施例により制限されるものではない。
［実施例１］
長さ１．４ｍ、呼び径１００ｍｍφの硬質塩化ビニルパイプ（ＰＶＣ管；重量４．７８ｋｇ、外径約１１４ｍｍφ）に、ＰＥＴフェルト（２０デニール、厚さ５ｍｍ、面重量４００ｇ／ｍ2）を巻き付け、その表面に不燃性無機化合物微粉（主成分：炭酸カルシウム粉体）とポリマー混和剤（商品名：セレタック混和剤Ｇ（登録商標）；アクリル−ＥＶＡ系ポリマーエマルジョン、固形分濃度５６％）のスラリーとを不燃性無機化合物微粉：ポリマー混和剤＝１：１で混合したものを塗布し、厚さ１ｍｍ（面重量２ｋｇ／ｍ2）のスラリー硬化物による遮音層を形成し、防音性合成樹脂管とした。
該防音性合成樹脂管を用い、半無響室（Ｗ：２ｍ×Ｌ：３ｍ×Ｈ：２ｍ）内の試験装置（リオン社製：ＮＡ−２９）にセットして、一定流量：４リットル／秒の水を定常的に流し、管壁面から５０ｃｍ、床面から１１０ｃｍの高さにセットしたマイクを用いて、発生する騒音を測定した。等価騒音レベル（Ｌｅｑ）として１０秒間測定し、その値を騒音値とした。また、そのときのオクターブ周波数分析の結果を表１に示す。測定値は、ともにＡ特性で計測したものである。
EXAMPLES Hereinafter, although this invention is demonstrated more concretely based on an Example, this invention is not restrict | limited by the following Example.
[Example 1]
A PET felt (20 denier, thickness 5 mm, surface weight 400 g / m 2 ) is wound around a rigid polyvinyl chloride pipe (PVC pipe; weight 4.78 kg, outer diameter about 114 mmφ) having a length of 1.4 m and a nominal diameter of 100 mmφ, A slurry of non-combustible inorganic compound fine powder (main component: calcium carbonate powder) and a polymer admixture (trade name: Celetac admixture G (registered trademark); acrylic-EVA polymer emulsion, solid content concentration 56%) on its surface A non-combustible inorganic compound fine powder: polymer admixture mixed with 1: 1 is applied to form a sound insulation layer with a cured slurry of 1 mm thickness (
Using this soundproof synthetic resin tube, it was set in a test apparatus (Lion: NA-29) in a semi-anechoic chamber (W: 2 m × L: 3 m × H: 2 m), and a constant flow rate: 4 liters / The generated noise was measured using a microphone set at a height of 50 cm from the wall of the tube and 110 cm from the floor. The equivalent noise level (Leq) was measured for 10 seconds, and the value was taken as the noise value. Table 1 shows the results of octave frequency analysis at that time. Both measured values were measured with the A characteristic.
［比較例１］
実施例１と同様に、長さ１．４ｍの呼び径１００ｍｍφの硬質塩化ビニルパイプ（ＰＶＣ管：重量４．７８ｋｇ、外径約１１４ｍｍφ）に、ＰＥＴフェルト（２０デニール、厚さ５ｍｍ、面重量４００ｇ／ｍ2）を巻きつけた防音性合成樹脂管を用いて、半無響室にセットして、一定流量：４リットル／秒の水を定常的に流し、管壁面から５０ｃｍ、床面から１１０ｃｍの高さにセットしたマイクを用いて、発生する騒音を測定した。
[Comparative Example 1]
In the same manner as in Example 1, a rigid vinyl chloride pipe (PVC pipe: weight 4.78 kg, outer diameter approximately 114 mmφ) having a nominal diameter of 100 mmφ having a length of 1.4 m and PET felt (20 denier, thickness 5 mm, surface weight 400 g). / M 2 ) is set in a semi-anechoic chamber using a soundproof synthetic resin tube wrapped around, and a constant flow rate: 4 liters / second of water is steadily flown, 50 cm from the tube wall surface, 110 cm from the floor surface The generated noise was measured using a microphone set at a height of.
［比較例２］
比較例１において、前記ＰＥＴフェルトの外側にゴム系遮音シート（厚さ１ｍｍ、面重量２ｋｇ／ｍ2）を巻いたＰＶＣ管を用いて、発生する騒音測定を行った。
[Comparative Example 2]
In Comparative Example 1, the generated noise was measured using a PVC pipe in which a rubber sound insulation sheet (
１ 合成樹脂管
２ 吸音層
３ 遮音層
1
Claims (10)
合成樹脂製パイプの外表面に不織布からなる吸音層を形成した後、前記吸音層の表面に不燃性無機化合物微粉およびポリマー混和剤からなるスラリーを塗布、吹き付けまたは浸漬することにより遮音層を形成することを特徴とする防音性合成樹脂管の製造方法。 A method for producing a soundproofing synthetic resin pipe according to any one of claims 1 to 8,
After forming the sound absorbing layer made of non-woven fabric on the outer surface of the synthetic resin pipe, forming the sound insulation layer by a slurry comprising nonflammable inorganic compounds fines and polymer admixture on the surface of the backing layer coating, to spraying or dipping A method for producing a soundproofing synthetic resin tube.
筒状に成形された不織布からなる吸音層の外表面に不燃性無機化合物微粉とポリマー混和剤とからなる遮音層が形成された配管用防音材に、合成樹脂管を挿入することを特徴とする防音性合成樹脂管の製造方法。 A method for producing a soundproofing synthetic resin pipe according to any one of claims 1 to 8,
Incombustible inorganic compound fine powder and piping deadening sound insulating layer comprising a polymer admixture is formed on the outer surface of the sound absorbing layer made of cylindrical shape shaped nonwoven, characterized by inserting the synthetic resin tube A method for producing a soundproof synthetic resin pipe.