JP5362967B2 - 伝動ベルト - Google Patents
伝動ベルト Download PDFInfo
- Publication number
- JP5362967B2 JP5362967B2 JP2007187430A JP2007187430A JP5362967B2 JP 5362967 B2 JP5362967 B2 JP 5362967B2 JP 2007187430 A JP2007187430 A JP 2007187430A JP 2007187430 A JP2007187430 A JP 2007187430A JP 5362967 B2 JP5362967 B2 JP 5362967B2
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- adhesive
- reinforcing fiber
- rubber composition
- fiber material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
しかし、これらのゴム成分を用いた伝動ベルトは、ベルト走行時の摩擦等により高温となった場合に軟化しやすく、高温における走行性能を満足するものではない。つまり、耐熱性の面で問題を有している。
これに対し、エチレン−α-オレフィン共重合ゴムは耐熱性の面で優れているため、伝動ベルトのゴム成分として用いられてきている。
ところが、エチレン−α-オレフィン共重合ゴムをゴム成分として用いた伝動ベルトにおいては、伝動ベルトを補強するために伝動ベルトに備えられている補強用繊維材(例えば、心線、帆布など)とゴムとの接着力が上記ゴム成分を用いた場合と比較して小さいため、走行中に心線とゴムとの界面で剥離を生じたり、帆布がゴムから剥がれたりするといった現象が起きやすい。
そこで、ゴム成分としてエチレン−α-オレフィン共重合ゴムを用い、補強用繊維材である心線の表面をレゾルシン−ホルマリン−ラテックス(RFL)接着剤で処理し、ゴムと心線との接着力を高めた伝動ベルトが提案されている(特許文献1)。
前記接着剤には、商品名「ケムロック」に代表される加硫接着剤に比べて一般的に安価であり、伝動ベルトの製造コストを低減させ得る点においてRFL接着剤を用いることが好ましい。しかも加硫接着剤には塩素化合物を含有するものが多く、例えば廃棄時に焼却処分されたりするとダイオキシンなどの塩素系有害物質を発生させるおそれがある。一方RFL接着剤は塩素化合物を含まない組成を容易に選定し得る。従って、RFL接着剤を用いることで塩素系有害物質を環境中への排出させるおそれを低減することができ、環境に優しい伝動ベルトを提供し得る。
エポキシとしては、例えば、エチレングリコール、グリセリン、ペンタエリスリトール等の多価アルコールやポリエチレングリコール等のポリアルキレングリコールと、エピクロルヒドリンのようなハロゲン含有エポキシ化合物との反応生成物が挙げられる。また、レゾルシン、ビス(4−ヒドロキシフェニル)ジメチルメタン、フェノール−ホルムアルデヒド樹脂、レゾルシン−ホルムアルデヒド樹脂等の多価フェノール類とハロゲン含有エポキシ化合物との反応生成物なども挙げられる。
イソシアネートとしては、例えば、4,4’−ジフェニルメタンジイソシアネート、トリレン2,4−ジイソシアネート、ポリメチレンポリフェニルジイソシアネート、ヘキサメチレンジイソシアネート、ポリアリールポリイソシアネート等が挙げられる。また、上記イソシアネートにフェノール類、第3級アルコール類、第2級アルコール類等のブロック化剤を反応させてポリイソシアネートのイソシアネート基をブロック化したブロック化ポリイソシアネートも挙げられる。
前記エチレン−α-オレフィン共重合体ゴムの組成中における前記ジエンの割合は5〜12重量%が好ましい。前記ジエンの割合が5重量%以上であることにより、補強用繊維材とこれに隣接するゴム組成物との接着力がより大きくなる。なお、前記ジエンの割合が12重量%を超えるエチレン−α-オレフィン共重合体ゴムの市販品については、現段階では入手するのが困難である。
これらの加硫促進剤を含有していることにより、エチレン−α-オレフィン共重合ゴムを含有するゴム組成物と補強用繊維材との接着力不足に起因する伝動ベルトの破壊がさらに抑制され、伝動ベルトがより長時間走行できる。
これらの添加剤、配合剤は、ゴム用組成物用の一般的なものを用いることができる。それらの配合量も特に制限されず、任意に選択できる。
前記心線の太さに対する接着ゴム層20の厚さ割合の範囲としては、通常、(接着ゴム層の厚さ/心線の太さ)=0.5〜2が挙げられる。
また、前記背面層30は、前記帆布1のみで形成されているものに限られない。
また、例えば、心線2ではなく帆布1が前記接着ゴム層20に埋設されたVリブドベルトの実施形態も挙げられる。
なお、補強用繊維材とエチレン−α-オレフィン共重合体ゴムを含有するゴム組成物との接着力をより向上させ得る点において、前記補強用繊維材前処理工程は実施することが好ましい。接着剤の担持方法については、接着剤処理液を用いる方法に限定されるものではないが、容易に接着剤を担持させることができる点において接着剤処理液を用いることが好ましい。
エチレン-α-オレフィン共重合体ゴム1(EPDM):
JSR社製、商品名「EP25」組成中ENB量5.1重量%
エチレン-α-オレフィン共重合体ゴム2(EPDM):
JSR社製、商品名「EP22」組成中ENB量4.5重量%
エチレン-α-オレフィン共重合体ゴム3(EPDM):
JSR社製、商品名「EP33」組成中ENB量8.1重量%
カーボンブラック:東海カーボン社製、商品名「シースト3」
パラフィン系プロセスオイル:サンオイル社製、商品名「サンパー2280」
ステアリン酸:日本油脂社製、商品名「ビーズステアリン酸椿」
酸化亜鉛:堺化学社製、商品名「亜鉛華1号」
硫黄:鶴見化学工業社製、商品名「オイルサルファー」
ジクミルパーオキサイド:日本油脂社製、商品名「パークミルD」
チウラム系加硫促進剤1:
大内新興化学社製、テトラキス(2-エチルヘキシル)チウラムジスルフィド
商品名「ノクセラーTOT−N」(有効成分67重量%)
スルフェンアミド系加硫促進剤1:
大内新興化学社製、N-シクロヘキシル-2-ベンゾチアゾリルスルフェンアミド
商品名「ノクセラーCZ」
チウラム系加硫促進剤2:大内新興化学社製、テトラブチルチウラムジスルフィド
商品名「ノクセラーTBT」
スルフェンアミド系加硫促進剤2:大内新興化学社製、
N,N'-ジシクロヘキシル-2-ベンゾチアゾリルスルフェンアミド
商品名「ノクセラーDZ」
チウラム系加硫促進剤3:大内新興化学社製、テトラエチルチウラムジスルフィド
商品名「ノクセラーTET」
ジチオカルバミン酸塩系加硫促進剤:大内新興化学社製、
ジエチルジチオカルバミン酸亜鉛 商品名「ノクセラーEZ」
チアゾール系加硫促進剤:大内新興化学社製、ジ-2-ベンゾチアゾリルジスルフィド
商品名「ノクセラーDM」
フェニレンジマレイミド:大内新興化学社製、N,N'-1,3-フェニレンジマレイミド
商品名「バルノックPM」
ポリジニトロソベンゼン:大内新興化学社製、ポリ-1,4-ジニトロソベンゼン
商品名「バルノックDNB」(有効成分25重量%)
なお、表1において配合量の数値は純分換算ではなく、配合量そのものの重量部を表す。
(1)接着剤処理液の作製
4,4’−ジフェニルメタンジイソシアネートをトルエンに溶解させ、固形分20重量%のイソシアネート溶液を調製した。
また、以下のようにしてRFL接着剤組成物を調製した。レゾルシン7.31重量部とホルマリン(37重量%濃度)10.77重量部とを混合、攪拌し、これに水酸化ナトリウム水溶液(固形分0.33重量部)を加えて攪拌し、その後、水160.91重量部を加え、5時間熟成して、レゾルシン・ホルマリン樹脂(レゾルシン−ホルマリン初期縮合物、以下RFともいう)R/F比0.5の水溶液を調製した。このRF水溶液にビニルピリジンラテックス(日本ゼオン株式会社 2518FS 固形分40重量%)をRF/L比が0.25になるように、ラテックス固形分量あわせて45.2重量部 加え、さらに水を加え、固形分が20重量%となるように調製した。攪拌し、12時間熟成して、RFL接着剤組成物を調製した。
さらに、表1の配合例1に示す接着ゴム層と同じ配合物をトルエンに溶解してなる固形分濃度20重量%の接着ゴム溶液を調製した。
心線として直径1mmのポリエステル繊維(帝人社製、ポリエステルコード、1000デニール、/2×3 上撚り9.5T/10cm(Z)、下撚り2.19T/10cm)を用いた。
次に、上述のごとく調製したイソシアネート溶液に前述のポリエステル心線を浸漬した後、240℃で40秒間加熱乾燥した。
次いで、イソシアネート溶液で処理したポリエステル心線を、前記RFL接着剤組成物に浸漬し、200℃で80秒間加熱乾燥した。
このように処理したポリエステル心線を前記接着ゴム溶液に浸漬した後、60℃で40秒間加熱乾燥して、前処理ポリエステル心線を得た。
表1に示す配合例1の接着ゴム層用の配合に従い、バンバリーミキサーを用いて組成物を混練し、この組成物をカレンダーロールにてシート状に圧延し、厚さ5mmの接着ゴム未加硫シートを作製した(2枚)。
上記の前処理ポリエステル心線7本を前記接着ゴム未加硫シートの間に挟み、これを面圧3920kPa、温度160℃で35分間、加圧加熱し、プレス加硫した。このようにして、接着力を評価するためのサンプルを作製した。
接着力を評価するためのサンプルの心線のうち、両端を除き、1本おきに選択した3本のポリエステル心線を、上下のチャックで挟み、チャック間40mm、剥離速度50mm/分、剥離距離80mmの剥離条件下で同時に剥離させ、接着力を測定した。また、接着力を測定した時の破壊時の態様を観察した。結果を表2に示す。
接着ゴム溶液及び接着ゴム層の組成を、それぞれ表1の配合例2〜12の組成とした点以外は、試験例1と同様にして接着力を評価するためのサンプル(心線埋設サンプル)を作製し、接着力を測定し、破壊時の態様を観察した。結果を表2に示す。
(1)接着剤処理液の作製
試験例1と同様にして、RFL接着組成物と接着ゴム溶液とを調製した。
帆布としてポリエステル綿帆布[(広角に加工した時点での特性)糸の材質:ポリエステルと綿との混紡帆布;ポリエステルと綿との質量比 50:50;糸構成 経糸:20S/2(20番手を2本よりあわせたものの意味)、緯糸:20 S/2(20番手を2本よりあわせたものの意味);撚り数:経糸S撚り 59回/10cm、緯糸:59回/10cm;織り方:平織り物を、経糸と緯糸との交差角度が、120°になるように加工(90°でも可);糸密度 経糸:85本/5cm、緯糸:85本/5cm]を用いた。このポリエステル綿帆布を試験例1と同じRFL接着組成物に浸漬し、150℃で3分間加熱乾燥させた。このように処理したポリエステル綿帆布を試験例1と同様に表1の配合例1に示す接着ゴム層と同じ配合物をトルエンに溶解してなる接着ゴム溶液に浸漬した後、60℃で10秒間加熱乾燥して、ポリエステル綿帆布に処理を施した前処理ポリエステル綿帆布を得た。
表1に示す配合例1の接着ゴム層用の配合に従い、バンバリーミキサーを用いて組成物を混練し、この組成物をカレンダーロールにてシート状に圧延し、厚さ5mmの接着ゴム未加硫シートを作製した。
上記のように処理した前処理ポリエステル綿帆布を前記接着ゴム未加硫シートの上に重ね、試験例1と同様なプレス条件でプレス加硫して、接着力を評価するためのサンプルを作製した。
得られたサンプルについて、JIS K 6256(1999)に準じて接着力を測定した。具体的には、サンプルを幅2.540cmに切断し、剥離試験機に入れ、ゴムシート部分とポリエステル綿帆布とを180°になるようにしながら、50mm/分の引張速度で剥離させることにより接着力を測定した。また、接着力を測定した時の破壊時の態様を観察した。結果を表3に示す。
接着ゴム溶液及び接着ゴム層の組成を、それぞれ表1の配合例2〜12の組成とした点以外は、試験例13と同様にして接着力を評価するためのサンプル(帆布サンプル)を作製し、接着力を測定し、破壊時の態様を観察した。結果を表3に示す。
まず、表1の配合例1に従い、試験例1と同様にして未加硫ゴムシートを作製する未加硫ゴムシート作製工程を実施し、厚さ0.5mmの接着ゴム層用未加硫ゴムシート2枚を作製した。また、表4の組成に従い、未加硫ゴムシート作製工程を実施し、厚さ0.5mmの圧縮ゴム層用未加硫ゴムシートを作製した。
次に、試験例1で用いたものと同じ心線に対して、試験例1と同様に前処理を行う補強用繊維材前処理工程を実施し、前処理ポリエステル心線を作製した。また、試験例13で用いたものと同じ帆布に対して、試験例13と同様に前処理を行う補強用繊維材前処理工程を実施し、ゴムコート帆布を作製した。
続いて、予備成形体作製工程を実施した。具体的には、表面が平滑な円筒状の成形ドラムの周面にゴムコート帆布、及び、接着ゴム層用未加硫ゴムシートを巻き付けた後、この上に前処理ポリエステル心線を螺旋状にスピニングし、更に、その上にもう1つの接着ゴム層用未加硫ゴムシートを巻き付けた後、圧縮ゴム層用未加硫ゴムシートを4回巻き付けて予備積層体を作製した。
次に、加硫工程を実施した。具体的には、作製した予備積層体を内圧588kPa、外圧883kPa、温度165℃、時間35分間で加硫缶中にて加熱加圧し、蒸気加硫して、環状物となった一次成形体を作製した。
次いで、リブ形成工程を実施した。具体的には、一次成形体を駆動ロールと従動ロールとからなる第1の駆動システムに取り付けて、所定の張力の下で走行させながら、これに研削ホイールにて表面に3つのリブを形成した。
この後、切断工程を実施した。具体的には、リブが形成された一次成形体を更に別の駆動ロールと従動ロールとならなる第2の駆動システムに取り付けて、走行させながら、所定の幅に裁断した。
以上のようにして、リブ数3、周長さ1000mmのVリブドベルトを製造した。
接着ゴム溶液及び接着ゴム層の組成において、参考例2、実施例3〜5、参考例6、実施例7、8はそれぞれ表1の配合例2〜8の組成とし、比較例1〜4はそれぞれ表1の配合例9〜12の組成とした点以外は、参考例1と同様にしてVリブドベルトを製造した。
得られたVリブドベルトを図3に示すように駆動プーリ11(直径120mm)と従動プーリ12(直径120mm)とこれらのプーリの間に配置したアイドラープーリ13(直径70mm)とテンションプーリ14(直径55mm)とからなるベルト駆動システムに取り付けた。ただし、アイドラープーリにはベルト背面を係合させた。温度130℃の雰囲気温度の下で、従動プーリの負荷を16馬力とし、テンションプーリの初張力を834Nとし、駆動プーリを回転数4900rpmで駆動して、ベルトを走行させ、ベルトから心線が露出するか、帆布が剥離するか、又はゴム層に割れを生じるまでの走行時間を評価した。結果を表5に示す。
2・・・心線
4・・・リブ
5・・・溝
6・・・短繊維
7・・・上ゴム層
8・・・Vリブドベルト
9・・・Vベルト
10・・・圧縮ゴム層
20・・・接着ゴム層
30・・・背面層
11・・・駆動プーリ
12・・・従動プーリ
13・・・アイドラープーリ
14・・・テンションプーリ
Claims (1)
- エチレン−α-オレフィン共重合体ゴムを含有するゴム組成物と補強用繊維材とが加硫一体化されてなる伝動ベルトであって、
フェニレンジマレイミド及びポリジニトロソベンゼンのうちの少なくとも1種と、硫黄系加硫剤とが前記ゴム組成物に含まれ、該ゴム組成物が、N−シクロヘキシル−2−ベンゾチアゾリルスルフェンアミドか、N,N’−ジシクロヘキシル−2−ベンゾチアゾリルスルフェンアミドかの何れかのスルフェンアミド系加硫促進剤及びテトラキス(2−エチルヘキシル)チウラムジスルフィドか、テトラブチルチウラムジスルフィドかの何れかのチウラム系加硫促進剤をさらに含有しており、前記補強用繊維材にはレゾルシン−ホルマリン−ラテックス(RFL)接着剤による処理が施されてなり、該補強用繊維材が心線又は帆布であり、該心線又は帆布の少なくとも一方と接する接着ゴム層の形成に前記ゴム組成物が用いられていることを特徴とする伝動ベルト。