JP5341733B2 - Cushion material surface layer and heat press cushion material - Google Patents

Cushion material surface layer and heat press cushion material Download PDF

Info

Publication number
JP5341733B2
JP5341733B2 JP2009275580A JP2009275580A JP5341733B2 JP 5341733 B2 JP5341733 B2 JP 5341733B2 JP 2009275580 A JP2009275580 A JP 2009275580A JP 2009275580 A JP2009275580 A JP 2009275580A JP 5341733 B2 JP5341733 B2 JP 5341733B2
Authority
JP
Japan
Prior art keywords
layer
resin
woven fabric
rubber
cushion material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2009275580A
Other languages
Japanese (ja)
Other versions
JP2011116034A (en
Inventor
晃 吉田
孝充 尾関
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yamauchi Corp
Original Assignee
Yamauchi Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yamauchi Corp filed Critical Yamauchi Corp
Priority to JP2009275580A priority Critical patent/JP5341733B2/en
Publication of JP2011116034A publication Critical patent/JP2011116034A/en
Application granted granted Critical
Publication of JP5341733B2 publication Critical patent/JP5341733B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide a surface layer material for cushioning medium, which shows excellent unevenness follow-up properties and the reduction of the incidence of crazes, creases and cracks. <P>SOLUTION: This surface layer material 11a for cushioning medium includes a resin layer 12 arranged on the face side of the surface layer material 11a and covering the one face of the surface layer material 11a, a rubber layer 13 arranged on the back side of the surface layer material 11a and covering the back side of the surface layer material 11a, and a fabric layer 14 arranged between the resin layer 12 and the rubber layer 13 and using a bulky yarn as at least either one of the warp or the weft. The fabric layer 14 is arranged on the resin layer 12 side, and includes a fabric/resin composite layer 17 formed by impregnating part of the fabric with a resin constituting the resin layer 12 and a fabric/rubber composite layer 18 arranged on the rubber layer 13 side and formed by impregnating part of the fabric with a rubber constituting the rubber layer 13. In addition, voids 20 are formed inside the fabric layer 14. <P>COPYRIGHT: (C)2011,JPO&amp;INPIT

Description

この発明は、熱プレスに用いられるクッション材用表層材および熱プレス用クッション材に関するものであり、特に、銅張積層板、フレキシブルプリント基板、多層板等のプリント基板や、ICカード、液晶表示板、セラミックス積層板などの精密機器部品(以下、この発明において、「積層板」という)を製造する工程で、対象製品をプレス成形や熱圧着する際に使用される熱プレス用クッション材およびクッション材用表層材に関するものである。   TECHNICAL FIELD The present invention relates to a cushioning surface layer material and a hot pressing cushion material used for hot pressing, and more particularly to printed boards such as copper-clad laminates, flexible printed boards and multilayer boards, IC cards, and liquid crystal display boards. Cushioning material and cushioning material for hot press used for press molding and thermocompression bonding of the target product in the process of manufacturing precision equipment parts (hereinafter referred to as “laminated board” in the present invention) such as ceramic laminated board It relates to a surface layer material.

積層板の製造工程においては、まず、材料となる積層板素材を重ね合わせて被圧縮体を作る。そして、これを熱盤の間に投入した後、熱プレス、すなわち、プレスによる加熱加圧を行い、積層板素材に含まれる熱可塑性樹脂または熱硬化性樹脂を、流動状態を経て硬化させ、一体化させる。   In the manufacturing process of a laminated board, first, the to-be-compressed body is made by superimposing the laminated board materials used as materials. And after putting this between hot plates, heat press, that is, heat pressurization by press, to cure the thermoplastic resin or thermosetting resin contained in the laminated board material through a fluidized state, Make it.

この加熱加圧を行う工程において、熱盤や投入部材である被圧縮体に厚みムラ、熱による歪み、温度ムラ等があると、後に製品となる被圧縮体に均一な温度、圧力が加えられない。その結果、製品に板厚不良、クラック、反り等の欠陥が発生する。そこで、製品の板厚不良等を解消するため、プレス成形の際に熱プレス用クッション材(以下、単に「クッション材」ということもある。)が用いられる。   In this heating and pressurizing step, if there is unevenness in thickness, heat distortion, temperature unevenness, etc. in the heated plate or the material to be compressed, uniform temperature and pressure are applied to the material to be compressed later. Absent. As a result, defects such as defective plate thickness, cracks, and warp occur in the product. Therefore, in order to eliminate the defective plate thickness of the product, a hot press cushioning material (hereinafter sometimes simply referred to as “cushioning material”) is used during press molding.

ここで、クッション材については、上記した製品の板厚不良等を解消するための良好なクッション性に加え、耐熱性や、接触する熱盤に対しての良好な剥離性等が求められる。そして、昨今のクッション材においては、剥離性等の向上の観点から、クッション性を有するクッション材本体に加え、その表面にクッション材用表層材(以下、単に「表層材」ということもある。)が用いられることがある。   Here, the cushioning material is required to have good heat resistance and good peelability with respect to a contacting hot plate, in addition to good cushioning properties for eliminating the above-described defective product thickness. And in recent cushion materials, from the viewpoint of improving peelability and the like, in addition to the cushion material main body having cushioning properties, a surface material for cushion material (hereinafter sometimes simply referred to as “surface material”) is provided on the surface thereof. May be used.

このような表層材を有し、熱プレスに用いられる熱プレス用クッション材に関する技術が、特開2004−344962号公報(特許文献1)および特許第3221978号(特許文献2)に開示されている。   A technique relating to a cushion material for a hot press that has such a surface layer material and is used in a hot press is disclosed in Japanese Patent Application Laid-Open No. 2004-344966 (Patent Document 1) and Patent No. 3221978 (Patent Document 2). .

特許文献1に開示の熱プレス用シートは、クッション材用表層材であって、シート状の基材と、基材上に形成された離型性塗膜とを備えることとしている。そして、塗膜は、樹脂組成物100質量%中に、有機粉末5〜55質量%および無機粉末5〜55質量%が合計で30〜60質量%混入された樹脂組成物からなることとしている。こうすることにより、表層材において、表面の離型性塗膜にひけや凹みが発生するのを防止することとしている。   The sheet for hot press disclosed in Patent Document 1 is a surface material for cushion material, and includes a sheet-like base material and a releasable coating film formed on the base material. The coating film is made of a resin composition in which 5 to 55% by mass of organic powder and 5 to 55% by mass of inorganic powder are mixed in 30 to 60% by mass in 100% by mass of the resin composition. By doing so, in the surface layer material, sinks and dents are prevented from occurring in the surface releasable coating film.

特許文献2においては、耐熱性を向上させる観点から、耐熱性材料からなるシート状の基材の両面に未加硫のフッ素ゴムを塗布し、さらにその上から片面に耐熱性塗料を塗布してなる熱プレス成形用クッション材の耐熱性感熱接着シート、すなわち、クッション材用の表層材を開示している。   In Patent Document 2, from the viewpoint of improving heat resistance, unvulcanized fluororubber is applied to both sides of a sheet-like base material made of a heat-resistant material, and then a heat-resistant paint is applied to one side from above. A heat-resistant heat-sensitive adhesive sheet for a heat press molding cushion material, that is, a surface material for a cushion material is disclosed.

また、アラミドクロスを用いた部材を表層材に備えた熱プレス用クッション材もある。すなわち、クッション性を有するシート状の部材の表層に、アラミドクロスが配置された構成である。   There is also a hot press cushion material in which a member using an aramid cloth is provided as a surface layer material. In other words, the aramid cloth is arranged on the surface layer of the sheet-like member having cushioning properties.

特開2004−344962号公報Japanese Patent Application Laid-Open No. 2004-344962 特許第3221978号Japanese Patent No. 3221978

特許文献1および特許文献2に示すクッション材用表層材においては、表層材自体の表面が、比較的硬かった。そうすると、プレス時において、クッション材と被圧縮体または熱盤との間に、コンタミネーション、いわゆる異物を噛み込んだ際に、表層材を有するクッション材が異物の影響による微小な凹凸を吸収することができなかった。すなわち、クッション材の表面における凹凸追従性が不十分であった。そうすると、クッション材と被圧縮体または熱盤との間に異物が噛み込んだ際に、熱プレスによって製造される製品に凹凸が反映されることとなり、製品の不具合を発生させるおそれがあった。このような観点から、クッション材については、異物による微小な凹凸による影響を吸収する高い凹凸追従性が要求される。特に、昨今のクッション材に対しては、薄肉化の要求を兼ね備えながら、高い凹凸追従性を有するクッション材が求められる。   In the surface material for cushion material shown in Patent Document 1 and Patent Document 2, the surface of the surface material itself was relatively hard. Then, at the time of pressing, when a contamination, that is, a so-called foreign matter is bitten between the cushion material and the object to be compressed or the hot platen, the cushion material having the surface layer material absorbs minute unevenness due to the influence of the foreign matter. I could not. That is, the unevenness followability on the surface of the cushion material was insufficient. Then, when a foreign object is caught between the cushion material and the object to be compressed or the hot platen, unevenness is reflected on the product manufactured by hot pressing, which may cause a defect of the product. From such a point of view, the cushion material is required to have high unevenness followability that absorbs the influence of minute unevenness caused by foreign matter. In particular, a cushion material having high unevenness followability is demanded for a recent cushion material while having a demand for thinning.

また、特許文献1および特許文献2に示す表層材を有するクッション材においては、クッション材の柔軟性が比較的低かった。そうすると、例えば、クッション材の取り扱い時において、クッション材にひびやシワ、クラックが生じるおそれもあった。具体的には、一般的な積層板の製造に用いられる熱プレスで使用されるクッション材は、数m×数mのサイズである。このようなクッション材について、端部を局所的に持ち上げた場合、その自重によってクッション材が垂れ下がって、クッション材の一部にひびが入ったり、シワやクラックが生じるおそれがあった。このような観点から、高い柔軟性を有し、持ち運びや取り扱いが容易なクッション材が求められている。   Moreover, in the cushion material which has the surface material shown in patent document 1 and patent document 2, the softness | flexibility of the cushion material was comparatively low. Then, for example, when the cushion material is handled, the cushion material may be cracked, wrinkled, or cracked. Specifically, a cushion material used in a hot press used for manufacturing a general laminated board has a size of several m × several m. In such a cushion material, when the end portion is locally lifted, the cushion material hangs down due to its own weight, and there is a possibility that a part of the cushion material is cracked or wrinkled or cracked. From such a point of view, there is a demand for a cushion material that has high flexibility and is easy to carry and handle.

また、上記したアラミドクロスを表層材としたクッション材の場合には、繰り返しの使用により、その表面に毛羽が発生していた。この毛羽は、コンタミネーションの基となるため、毛羽の発生自体の低減が要求される。特に、昨今は、ポリイミド樹脂等の材料が積層板の材料として用いられており、比較的高温での熱プレス、具体的には、例えば、200℃以上での熱プレスが行なわれる。このような高温での熱プレスにおいては、アラミドクロスの繊維の劣化が特に顕著であり、毛羽の発生が多発することになる。さらに、アラミドクロスを表層材として用いた場合、使用後の劣化によりその表面が硬くなり、上記した凹凸追従性が悪化してしまうことになる。   Moreover, in the case of the cushion material which used the above-mentioned aramid cloth as the surface layer material, fluff was generated on the surface by repeated use. Since this fluff is a basis for contamination, it is required to reduce the occurrence of fluff itself. In particular, recently, materials such as polyimide resin are used as the material of the laminated plate, and hot pressing at a relatively high temperature, specifically, for example, hot pressing at 200 ° C. or higher is performed. In such a hot press at a high temperature, the degradation of the fibers of the aramid cloth is particularly remarkable, and fluff frequently occurs. Furthermore, when an aramid cloth is used as a surface layer material, the surface becomes hard due to deterioration after use, and the above-described uneven followability is deteriorated.

この発明の目的は、凹凸追従性が優れており、ひびやシワ、クラックの発生を低減させたクッション材用表層材を提供することである。   An object of the present invention is to provide a surface layer material for a cushion material that has excellent unevenness followability and reduces the occurrence of cracks, wrinkles, and cracks.

この発明の他の目的は、凹凸追従性が優れており、ひびやシワ、クラックの発生を低減させた熱プレス用クッション材を提供することである。   Another object of the present invention is to provide a hot press cushioning material that has excellent unevenness followability and reduces the occurrence of cracks, wrinkles and cracks.

本願発明者は、クッション材の内部層であるクッション材本体にクッション性を具備させるのみならず、クッション材の表層に配置されるクッション材用表層材自体についても、クッション性を具備させればよいことに着目した。もちろん、クッション材用表層材に対しては、上記した観点から、毛羽の発生の低減や剥離性、内部層であるクッション材本体への接着性も良好にする必要がある。   The inventor of this application not only provides the cushioning material body which is the inner layer of the cushioning material with cushioning properties, but also provides cushioning properties for the surface material for the cushioning material itself disposed on the surface layer of the cushioning material. Focused on that. Of course, for the surface layer material for the cushion material, it is necessary to reduce the generation of fluff, release properties, and adhesion to the cushion material body as the inner layer from the above viewpoint.

この発明に係るクッション材用表層材は、熱プレス用クッション材の表層に配置されるシート状のクッション材用表層材であって、表層材の一方面側に配置され、表層材の一方面を覆う樹脂層と、表層材の他方面側に配置され、表層材の他方面を覆うゴム層と、シート状の織布から構成されており、樹脂層およびゴム層の間に配置され、経糸および緯糸のうちの少なくともいずれか一方に嵩高糸を用いた織布層とを備える。そして、織布層は、樹脂層側に設けられ、織布の一部に樹脂層を構成する樹脂を含浸させて形成される織布−樹脂複合層と、ゴム層側に設けられ、織布の一部にゴム層を構成するゴムを含浸させて形成される織布−ゴム複合層とを含む。そして、織布層の内部には、空隙が設けられている。 The surface material for a cushion material according to the present invention is a surface material for a cushion material that is disposed on the surface layer of a cushion material for hot press, and is disposed on one surface side of the surface material, and one surface of the surface material is A resin layer covering, a rubber layer disposed on the other side of the surface layer material, covering the other surface of the surface layer material, and a sheet-like woven fabric , disposed between the resin layer and the rubber layer, A woven fabric layer using bulky yarn is provided on at least one of the wefts. The woven fabric layer is provided on the resin layer side. The woven fabric-resin composite layer is formed by impregnating a part of the woven fabric with the resin constituting the resin layer. The woven fabric layer is provided on the rubber layer side. And a woven fabric-rubber composite layer formed by impregnating a part of the rubber with rubber constituting the rubber layer. And the space | gap is provided in the inside of a woven fabric layer.

本願発明に係る表層材は、織布層として、経糸および緯糸のうちの少なくともいずれか一方に嵩高糸(Texturized yarn)を用いている。このような嵩高糸は、ガラス糸を構成する短繊維同士が平行状態ではなく、絡み合い、乱れた状態で引きそろえられた占有面積の大きな糸である。言い換えれば、嵩高糸は毛糸のようなふくらみを持つので、嵩高糸を用いた織布は、通常の織布とは異なり、内部に多くの空隙を含んでいる。   The surface layer material according to the present invention uses, as a woven fabric layer, a bulky yarn (textured yarn) for at least one of warp and weft. Such a bulky yarn is a yarn having a large occupation area in which the short fibers constituting the glass yarn are not in a parallel state but are entangled and disordered. In other words, since the bulky yarn has a bulge like a woolen yarn, the woven fabric using the bulky yarn includes many voids inside unlike a normal woven fabric.

そして、織布−樹脂複合層では、織布に含浸された樹脂が嵩高糸の持つ空隙および織り目の空隙に適度に入り込み、しかも空隙を完全には塞がずにある程度の空隙性を維持させるものである。織布−ゴム複合層でも同様に、織布に含浸されたゴムが嵩高糸の持つ空隙および織り目の空隙に適度に入り込み、しかも空隙を完全には塞がずにある程度の空隙性を維持させている。このような空隙は、周囲のほとんどが樹脂やゴムに覆われているため、押しつぶされるような圧力が加えられたとしても、除圧時に、元の形状に戻ろうとする復元力が強いものである。   In the woven fabric-resin composite layer, the resin impregnated in the woven fabric appropriately enters the voids of the bulky yarn and the voids of the weave, and maintains a certain degree of porosity without completely closing the voids. It is. Similarly, in the woven fabric-rubber composite layer, the rubber impregnated in the woven fabric appropriately enters the voids of the bulky yarn and the voids of the weave, and maintains a certain degree of porosity without completely closing the voids. Yes. Since these voids are almost entirely covered with resin or rubber, even if pressure is applied to them, they have a strong restoring force to return to the original shape when the pressure is removed. .

すなわち、このようなクッション材用表層材は、一方面側に配置される樹脂層と他方面側に配置されるゴム層との間に設けられる織布層の内部に空隙を有するため、凹凸追従性を優れたものとすることができると共に、柔軟性を高くすることができる。そうすると、クッション材と被圧縮体または熱盤との間に微小な異物が噛み込んだ場合でも、異物による凹凸の影響を吸収することができる。したがって、製品に対する凹凸の影響を少なくすることができる。また、柔軟性が高いため、ひびやシワ、クラックの発生を低減することができる。また、このようなクッション材用表層材は、一方面側が樹脂層から構成されているため、毛羽の発生を低減することができると共に、熱盤等に対する剥離性を向上させることができる。また、他方面側がゴム層から構成されているため、クッション材本体に対する表層材の接着性を高めることができる。   That is, such a surface layer material for cushioning material has a void in the woven fabric layer provided between the resin layer disposed on one side and the rubber layer disposed on the other side, and therefore has an uneven surface. It is possible to improve the flexibility and increase the flexibility. Then, even when a minute foreign matter is caught between the cushion material and the object to be compressed or the hot platen, the influence of the unevenness due to the foreign matter can be absorbed. Therefore, the influence of unevenness on the product can be reduced. In addition, since the flexibility is high, generation of cracks, wrinkles, and cracks can be reduced. Moreover, since the surface layer material for cushion materials is composed of a resin layer on one side, it is possible to reduce the occurrence of fluff and improve the peelability to a hot platen or the like. Moreover, since the other surface side is comprised from the rubber layer, the adhesiveness of the surface layer material with respect to a cushion material main body can be improved.

織布層については、織布を構成する経糸および緯糸のうちのいずれか一方に嵩高糸を用いることとしたが、もちろん両方に嵩高糸を用いてもよい。経糸および緯糸のうちのいずれか一方が嵩高糸である場合、他方は、通常の単糸または合撚糸で構成することができる。なお、嵩高糸の種類としては、バルキーヤーン(bulked yarn)、ステープルヤーン(staple yarn)、スライバヤーン(sliver yarn)等を挙げることができる。バルキーヤーンは、エアージェットなどで嵩高に加工した糸である。ステープルヤーンは、綿状のガラス短繊維を紡績して糸状にしたものである。スライバヤーンは、撚りのない嵩高の短繊維(スライバ:sliver)に撚りをかけて作る糸である。   For the woven fabric layer, bulky yarn is used for either one of the warp and weft constituting the woven fabric, but of course bulky yarn may be used for both. When either one of the warp and the weft is a bulky yarn, the other can be composed of a normal single yarn or a twisted yarn. Examples of the bulky yarn include bulky yarn, staple yarn, and sliver yarn. The bulky yarn is a yarn processed to be bulky with an air jet or the like. The staple yarn is obtained by spinning cotton-like short glass fibers into a yarn shape. The sliver yarn is a yarn made by twisting bulky short fibers (sliver) without twist.

また、基材としての織布に対する織布層の空隙残存率は、70%以上である。織布層について、このような空隙残存率とすることにより、より確実に凹凸追従性および高い柔軟性を確保することができる。   Further, the void remaining ratio of the woven fabric layer with respect to the woven fabric as the base material is 70% or more. By setting such a void remaining rate for the woven fabric layer, it is possible to more surely ensure unevenness followability and high flexibility.

ここで、空隙残存率について説明する。まず、基材としての織布、すなわち、樹脂およびゴムを含浸していない状態での織布の空隙率を算出する。空隙率は、まず、織布の厚みに面積を乗じたものを織布全体の体積とし、目付け量および嵩高糸の比重から嵩高糸の体積を算出し、織布全体の体積から嵩高糸の体積を差し引いたものを空隙の体積とした。そして、織布全体の体積に対する空隙の体積の比率を、空隙率として算出した。空隙残存率については、まず、樹脂およびゴムを含浸した織布における空隙率を、さらにゴムおよび樹脂の比重を用いて算出する。そして、樹脂およびゴムを含浸していない織布の空隙率に対しての樹脂およびゴムを含浸した織布における空隙率の比率を、空隙残存率とした。すなわち、空隙残存率は、樹脂およびゴムを含浸していない状態における織布の空隙に対して、樹脂およびゴムを含浸した織布における空隙がどれくらい残存しているかを示すものである。   Here, the void remaining rate will be described. First, the porosity of the woven fabric as the base material, that is, the woven fabric in a state not impregnated with resin and rubber is calculated. For the porosity, first, the volume of the woven fabric multiplied by the area is taken as the volume of the entire woven fabric, the volume of the bulky yarn is calculated from the weight per unit area and the specific gravity of the bulky yarn, and the volume of the bulky yarn is calculated from the volume of the entire woven fabric. The volume obtained by subtracting was used as the void volume. And the ratio of the volume of the space | gap with respect to the volume of the whole woven fabric was computed as a porosity. As for the void ratio, first, the void ratio in the woven fabric impregnated with resin and rubber is calculated using the specific gravity of rubber and resin. The ratio of the porosity of the woven fabric impregnated with resin and rubber to the porosity of the woven fabric not impregnated with resin and rubber was defined as the void residual ratio. That is, the void remaining rate indicates how much voids remain in the woven fabric impregnated with the resin and rubber relative to the voids in the woven fabric in a state where the resin and rubber are not impregnated.

樹脂としては、上記した熱プレスによる熱への耐性を有する耐熱性樹脂であることが好ましい。具体的には、一例として、耐熱性樹脂の融点およびガラス転移点のうちの少なくともいずれか一方は、200℃以上である樹脂を用いるのが良い。熱プレスについては、昨今、高温での処理が要求される。例えば、製造される製品の耐熱性を高めるために、製品を構成する樹脂についても、耐熱性を有する樹脂が使用される。そこで、クッション材用表層材についても、200℃の温度に耐え得るような樹脂が要求される。すなわち、融点およびガラス転移点のうちの少なくともいずれか一方が200℃以上であれば、製品が耐熱性樹脂から構成されており、高温、例えば、200℃程度の温度で熱プレスが行なわれても、クッション材用表層材として使用に耐え得る。もちろん、融点およびガラス転移点の双方が、200℃以上であってもよい。   The resin is preferably a heat-resistant resin having resistance to heat by the hot press described above. Specifically, as an example, at least one of the melting point and the glass transition point of the heat resistant resin may be a resin having a temperature of 200 ° C. or higher. As for the hot press, recently, processing at a high temperature is required. For example, in order to increase the heat resistance of a product to be manufactured, a resin having heat resistance is also used as a resin constituting the product. Therefore, a resin capable of withstanding a temperature of 200 ° C. is also required for the surface material for the cushion material. That is, if at least one of the melting point and the glass transition point is 200 ° C. or higher, the product is made of a heat-resistant resin, and even if hot pressing is performed at a high temperature, for example, about 200 ° C. It can withstand use as a surface material for cushion materials. Of course, both the melting point and the glass transition point may be 200 ° C. or higher.

樹脂としては、例えば、フッ素樹脂、フェノール樹脂、メラミン樹脂、エポキシ樹脂、不飽和ポリエステル樹脂、シリコーン樹脂、ポリイミド樹脂、熱硬化性アクリル樹脂、フラン樹脂、ユリア油脂、ジアリルフタレート樹脂、ポリウレタン樹脂からなる群から選択される1種の樹脂または2種以上の樹脂の混合物であることが好ましい。特に耐熱性等が良好なフッ素樹脂が最も好ましい。   Examples of the resin include a group consisting of fluorine resin, phenol resin, melamine resin, epoxy resin, unsaturated polyester resin, silicone resin, polyimide resin, thermosetting acrylic resin, furan resin, urea oil, diallyl phthalate resin, and polyurethane resin. It is preferable that it is 1 type of resin selected from these, or a mixture of 2 or more types of resin. In particular, a fluororesin having good heat resistance and the like is most preferable.

また、樹脂には、導電性を有する無機粉末が含有されていることが好ましい。こうすることにより、比較的帯電し易い樹脂の帯電を抑制することができる。無機粉末としては、カーボン粉末、アルミニウム粉末、酸化チタン粉末、酸化亜鉛粉末、酸化鉄粉末からなる群から選択される1種の粉末または2種以上の粉末の混合物であることが好ましい。なお、無機粉末の平均粒子径については、0.1μm〜10.0μm程度が良い。   Moreover, it is preferable that resin contains the inorganic powder which has electroconductivity. By doing so, charging of the resin that is relatively easily charged can be suppressed. The inorganic powder is preferably a single powder selected from the group consisting of carbon powder, aluminum powder, titanium oxide powder, zinc oxide powder, and iron oxide powder, or a mixture of two or more powders. In addition, about the average particle diameter of inorganic powder, about 0.1 micrometer-10.0 micrometers are good.

好ましくは、織布は、バルキーヤーンを用いたガラス繊維である。ガラス繊維のバルキーヤーンを用いた織布としては、例えば、ユニチカ株式会社製のA305、A330、A400、A415、A450、A500、T330、T540、T790、T860、T900や、日東紡績株式会社製のKS4010、KS4155、KS4325等が市販されている。また、織布として、アラミド繊維を用いることもできる。   Preferably, the woven fabric is a glass fiber using a bulky yarn. Examples of the woven fabric using glass fiber bulky yarn include A305, A330, A400, A415, A450, A500, T330, T540, T790, T860, and T900 manufactured by Unitika Ltd., and KS4010 manufactured by Nitto Boseki Co., Ltd. , KS4155, KS4325, etc. are commercially available. Moreover, an aramid fiber can also be used as a woven fabric.

織布については、1重織りまたは多重織りされたものであってもよい。織布の織り方としては、平織り、綾織、その他の織りがあるが、特定の織り方に限定されない。糸の番手、織密度、織り方等を適宜選択して、織布の目付け精度や空隙率を調整することができる。   The woven fabric may be single woven or multiple woven. The weaving method of the woven fabric includes plain weave, twill weave, and other weaves, but is not limited to a specific weaving method. The fabric weight, the weaving density, the weaving method, and the like can be appropriately selected to adjust the fabric weight and the porosity of the woven fabric.

ゴムは、フッ素ゴム、EPM、EPDM、水素化ニトリルゴム、シリコーンゴム、アクリルゴムおよびブチルゴムからなる群から選択される1種のゴムまたは2種以上のゴムの混合物であることが好ましい。これらのゴムはいずれも、耐熱性に優れているため、熱プレス用として良好である。特に、フッ素ゴムについては、耐熱性、および強度等の物性が優れているとの観点から、最も好ましい。   The rubber is preferably one rubber selected from the group consisting of fluorine rubber, EPM, EPDM, hydrogenated nitrile rubber, silicone rubber, acrylic rubber and butyl rubber, or a mixture of two or more rubbers. Since these rubbers are all excellent in heat resistance, they are good for hot pressing. In particular, fluorine rubber is most preferable from the viewpoint of excellent physical properties such as heat resistance and strength.

この発明の他の局面においては、熱プレス用クッション材は、熱プレスに用いられる熱プレス用クッション材であって、熱プレス用クッション材は、その表層に配置されるシート状のクッション材用表層材を含む。クッション材用表層材は、表層材の一方面側に配置され、表層材の一方面を覆う樹脂層と、表層材の他方面側に配置され、表層材の他方面を覆うゴム層と、シート状の織布から構成されており、樹脂層およびゴム層の間に配置され、経糸および緯糸のうちの少なくともいずれか一方に嵩高糸を用いた織布層とを備える。そして、織布層は、樹脂層側に設けられ、織布の一部に樹脂層を構成する樹脂を含浸させて形成される織布−樹脂複合層と、ゴム層側に設けられ、織布の一部にゴム層を構成するゴムを含浸させて形成される織布−ゴム複合層とを含む。そして、織布層の内部には、空隙が設けられている。 In another aspect of the present invention, the hot-press cushion material is a hot-press cushion material used for hot press, and the hot-press cushion material is a sheet-shaped cushion material surface layer disposed on the surface layer thereof. Including wood. The surface material for cushion material is disposed on one side of the surface material, a resin layer covering one surface of the surface material, a rubber layer disposed on the other surface of the surface material, and covering the other surface of the surface material, and a sheet And a woven fabric layer disposed between the resin layer and the rubber layer and using a bulky yarn for at least one of warp and weft. The woven fabric layer is provided on the resin layer side. The woven fabric-resin composite layer is formed by impregnating a part of the woven fabric with the resin constituting the resin layer. The woven fabric layer is provided on the rubber layer side. And a woven fabric-rubber composite layer formed by impregnating a part of the rubber with rubber constituting the rubber layer. And the space | gap is provided in the inside of a woven fabric layer.

このような熱プレス用クッション材は、凹凸追従性が優れており、ひびやシワ、クラックの発生を低減することができる。したがって、良好な製品を効率的に製造することができると共に、取扱いが良好で、耐久性を向上することができる。   Such a cushion material for hot press has excellent unevenness followability, and can reduce the occurrence of cracks, wrinkles and cracks. Therefore, a good product can be produced efficiently, handling is good, and durability can be improved.

この発明に係るクッション材用表層材によれば、一方面側に配置される樹脂層と他方面側に配置されるゴム層との間に設けられる織布層の内部に空隙を有するため、凹凸追従性を優れたものとすることができると共に、柔軟性を高くすることができる。そうすると、クッション材と被圧縮体または熱盤との間に微小な異物が噛み込んだ場合でも、異物による凹凸の影響を吸収することができる。したがって、製品に対する凹凸の影響を少なくすることができる。また、柔軟性が高いため、ひびやシワ、クラックの発生を低減することができる。   According to the surface layer material for a cushion material according to the present invention, since there is a void inside the woven fabric layer provided between the resin layer disposed on one side and the rubber layer disposed on the other side, The followability can be improved, and the flexibility can be increased. Then, even when a minute foreign matter is caught between the cushion material and the object to be compressed or the hot platen, the influence of the unevenness due to the foreign matter can be absorbed. Therefore, the influence of unevenness on the product can be reduced. In addition, since the flexibility is high, generation of cracks, wrinkles, and cracks can be reduced.

また、この発明に係る熱プレス用クッション材は、良好な製品を効率的に製造することができると共に、取扱いが良好で、耐久性を向上することができる。   Moreover, the cushion material for hot presses according to the present invention can efficiently produce a good product, can be handled well, and can improve durability.

この発明の一実施形態に係るクッション材用表層材を厚み方向に切断した場合の模式図である。It is a schematic diagram at the time of cut | disconnecting the surface material for cushion materials which concerns on one Embodiment of this invention to the thickness direction. この発明の一実施形態に係るクッション材用表層材の断面写真であり、約60倍に拡大した場合を示す。It is a section photograph of the surface material for cushion materials concerning one embodiment of this invention, and shows the case where it expands about 60 times. この発明の一実施形態に係るクッション材用表層材の断面写真であり、約32倍に拡大した場合を示す。It is a section photograph of the surface material for cushion materials concerning one embodiment of this invention, and shows the case where it expands about 32 times. この発明の一実施形態に係るクッション材用表層材を含む熱プレス用クッション材を厚み方向に切断して分解した場合の概略断面図である。It is a schematic sectional drawing at the time of cut | disconnecting and cutting | disconnecting the cushion material for hot presses containing the surface material for cushion materials which concerns on one Embodiment of this invention to the thickness direction. 通気度を試験するフラジール形試験機の概略図である。It is the schematic of the Frazier type testing machine which tests air permeability. この発明の他の実施形態に係るクッション材用表層材を含む熱プレス用クッション材を厚み方向に切断して分解した場合の概略断面図である。It is a schematic sectional drawing at the time of cut | disconnecting and cutting | disconnecting the cushion material for hot presses containing the surface material for cushion materials which concerns on other embodiment of this invention to the thickness direction. この発明のさらに他の実施形態に係るクッション材用表層材を含む熱プレス用クッション材を厚み方向に切断して分解した場合の概略断面図である。It is a schematic sectional drawing at the time of cut | disconnecting and cutting | disconnecting the cushion material for hot presses containing the surface material for cushion materials which concerns on other embodiment of this invention to the thickness direction. この発明のさらに他の実施形態に係るクッション材用表層材を含む熱プレス用クッション材を厚み方向に切断して分解した場合の概略断面図である。It is a schematic sectional drawing at the time of cut | disconnecting and cutting | disconnecting the cushion material for hot presses containing the surface material for cushion materials which concerns on other embodiment of this invention to the thickness direction.

以下、この発明の実施の形態を、図面を参照して説明する。図1は、この発明の一実施形態に係るクッション材用表層材を厚み方向に切断した場合の模式図である。図2は、この発明の一実施形態に係るクッション材用表層材の断面写真であり、約60倍に拡大した場合を示す。図3は、この発明の一実施形態に係るクッション材用表層材の断面写真であり、約32倍に拡大した場合を示す。なお、図1は、図2および図3を参考にして、この発明の一実施形態に係るクッション材用表層材を模式的に表したものである。   Embodiments of the present invention will be described below with reference to the drawings. Drawing 1 is a mimetic diagram when the surface material for cushion materials concerning one embodiment of this invention is cut in the thickness direction. FIG. 2 is a cross-sectional photograph of a surface material for a cushion material according to an embodiment of the present invention, and shows a case where the surface material is enlarged about 60 times. FIG. 3 is a cross-sectional photograph of a surface material for a cushion material according to an embodiment of the present invention, and shows a case where the surface material is enlarged about 32 times. FIG. 1 schematically shows a surface material for a cushion material according to an embodiment of the present invention with reference to FIGS. 2 and 3.

図1〜図3を参照して、この発明の一実施形態に係るクッション材用表層材11aは、後述する熱プレス用クッション材本体の表層、具体的には、熱プレス用クッション材本体の表面側および裏面側に配置されるものである。クッション材用表層材11aは、シート状である。表層材11aは、一方面側に配置され、表層材11aの一方面を覆う樹脂層12と、表層材11aの他方面側に配置され、表層材11aの他方面を覆うゴム層13とを備える。そして、樹脂層12とゴム層13との間には、織布層14が備えられている。すなわち、表層材11aの厚み方向において、樹脂層12とゴム層13との間に挟み込まれるようにして、織布層14が配置されている。樹脂層12の表面15aおよびゴム層13の表面15bは、比較的平滑な面である。織布層14、具体的には、織布層14を構成する嵩高糸16は、表面15a、15bからほとんど露出していない構成である。   With reference to FIGS. 1-3, the surface layer material 11a for cushion materials which concerns on one Embodiment of this invention is the surface of the cushion material main body for hot press mentioned later, specifically, the surface of the cushion material main body for hot press It is arranged on the side and the back side. The cushion material surface layer material 11a has a sheet shape. The surface layer material 11a includes a resin layer 12 disposed on one side and covering one surface of the surface layer material 11a, and a rubber layer 13 disposed on the other surface side of the surface layer material 11a and covering the other surface of the surface layer material 11a. . A woven fabric layer 14 is provided between the resin layer 12 and the rubber layer 13. That is, the woven fabric layer 14 is disposed so as to be sandwiched between the resin layer 12 and the rubber layer 13 in the thickness direction of the surface layer material 11a. The surface 15a of the resin layer 12 and the surface 15b of the rubber layer 13 are relatively smooth surfaces. The woven fabric layer 14, specifically, the bulky yarn 16 constituting the woven fabric layer 14 is a configuration that is hardly exposed from the surfaces 15 a and 15 b.

織布層14は、経糸および緯糸のうちの少なくともいずれか一方に嵩高糸16を用いた織布が適用される。嵩高糸16としては、例えば、バルキーヤーンを用いたガラス繊維またはアラミド繊維が用いられる。   The woven fabric layer 14 is applied with a woven fabric using bulky yarn 16 for at least one of warp and weft. As the bulky yarn 16, for example, glass fiber or aramid fiber using a bulky yarn is used.

なお、樹脂層12内には、図示はしないが、導電性を有する無機粉末が含有されている。これにより、比較的帯電し易い樹脂の帯電を抑制することができる。   In addition, although not shown in figure, the resin layer 12 contains the inorganic powder which has electroconductivity. Thereby, it is possible to suppress charging of the resin that is relatively easily charged.

ここで、織布層14については、樹脂層12側に設けられ、織布の一部に樹脂層12を構成する樹脂を含浸させて形成される織布−樹脂複合層17と、ゴム層13側に設けられ、織布の一部にゴム層13を構成するゴムを含浸させて形成される織布−ゴム複合層18とを含む構成である。織布−樹脂複合層17と織布−ゴム複合層18とは、対向する面19a、19bがほとんどの領域で接触している構成である。   Here, the woven fabric layer 14 is provided on the resin layer 12 side, and a woven fabric-resin composite layer 17 formed by impregnating a resin constituting the resin layer 12 into a part of the woven fabric, and the rubber layer 13. And a woven fabric-rubber composite layer 18 formed by impregnating a part of the woven fabric with rubber constituting the rubber layer 13. The woven fabric-resin composite layer 17 and the woven fabric-rubber composite layer 18 are configured such that the opposed surfaces 19a and 19b are in contact with each other in most regions.

すなわち、表層材11aは、図1中において、紙面上側から、樹脂層12、織布−樹脂複合層17、織布−ゴム複合層18、ゴム層13の順に配置される構成である。樹脂層12と織布−樹脂複合層17とは、ほとんどの領域で連続して連なる構成であり、ゴム層13と織布−ゴム複合層18とも、ほとんどの領域で連続して連なる構成である。一方、織布−樹脂複合層17と織布−ゴム複合層18とは、ほとんどの領域で必ずしも連なっておらず、所々で織布−樹脂複合層17と織布−ゴム複合層18との間に、織布および織布間に位置する空隙のみから構成される部分も存在する。なお、図1においては、織布−樹脂複合層17および織布−ゴム複合層18の厚みがほぼ同程度であり、樹脂層12およびゴム層13の厚みが比較的薄く図示されているが、用途等に応じて、各層の厚みは任意に変更される。   That is, the surface layer material 11a has a configuration in which the resin layer 12, the woven fabric-resin composite layer 17, the woven fabric-rubber composite layer 18, and the rubber layer 13 are arranged in this order from the upper side in FIG. The resin layer 12 and the woven fabric-resin composite layer 17 are continuously connected in most regions, and the rubber layer 13 and the woven fabric-rubber composite layer 18 are continuously connected in most regions. . On the other hand, the woven fabric-resin composite layer 17 and the woven fabric-rubber composite layer 18 are not necessarily continuous in most regions, and are located between the woven fabric-resin composite layer 17 and the woven fabric-rubber composite layer 18 in some places. In addition, there is a portion composed only of a woven fabric and a gap located between the woven fabrics. In FIG. 1, the woven fabric-resin composite layer 17 and the woven fabric-rubber composite layer 18 have substantially the same thickness, and the resin layer 12 and the rubber layer 13 are relatively thin. Depending on the application and the like, the thickness of each layer is arbitrarily changed.

ここで、織布層14の内部には、空隙20が設けられている。ここでは、図1に示すように、織布−樹脂複合層17の内部、および織布−ゴム複合層18の内部にそれぞれ、空隙20が設けられている。このような空隙20のほとんどは、基材としての織布層14を構成する嵩高糸16自身が元々有する空隙が残存したものである。この空隙については、そのほとんどの部分が樹脂やゴムに覆われたものである。したがって、押しつぶされるような圧力が加えられたとしても、除圧時に、元の形状に戻ろうとする復元力が強いものである。   Here, a void 20 is provided inside the woven fabric layer 14. Here, as shown in FIG. 1, voids 20 are provided inside the woven fabric-resin composite layer 17 and inside the woven fabric-rubber composite layer 18, respectively. Most of such voids 20 are the ones in which the bulky yarns 16 constituting the woven fabric layer 14 as the base material originally have residual voids. Most of the voids are covered with resin or rubber. Therefore, even if a pressure that is crushed is applied, the restoring force to return to the original shape is strong when the pressure is released.

次に、このような表層材11aの製造方法について、簡単に説明する。まず、上記した構成のシート状の織布を準備する。そして、シート状の織布の一方側の面に樹脂を含浸させる。この場合、織布に含浸させやすいように樹脂を溶剤に溶かしたり、ワニス状にしたものを用いるとよい。さらに、予め樹脂に含有させる導電性を有する無機粉末を加えておいてもよい。含浸に際しては、織布の一方側の面に樹脂層が形成され、他方側の面まで樹脂が染み渡らないようにして含浸させる。すなわち、一方面側は、樹脂層が露出し、他方面側は、織布を構成する嵩高糸が露出するように含浸させる。このようにして、まず、樹脂層および織布−樹脂複合層を形成する。その後、焼成を行い、溶剤を揮発させ、樹脂層および織布−樹脂複合層を固める。   Next, a method for manufacturing such a surface layer material 11a will be briefly described. First, a sheet-like woven fabric having the above-described configuration is prepared. Then, one surface of the sheet-like woven fabric is impregnated with resin. In this case, a resin dissolved in a solvent or varnished may be used so that the woven fabric can be easily impregnated. Furthermore, you may add the inorganic powder which has the electroconductivity previously contained in resin. In the impregnation, a resin layer is formed on one surface of the woven fabric, and impregnation is performed so that the resin does not penetrate to the other surface. That is, the impregnation is performed so that the resin layer is exposed on one side and the bulky yarn constituting the woven fabric is exposed on the other side. In this way, first, a resin layer and a woven fabric-resin composite layer are formed. Then, baking is performed, the solvent is volatilized, and the resin layer and the woven fabric-resin composite layer are hardened.

次に、他方面側からゴムを含浸させる。この場合、織布の他方面にゴム層が形成され、織布の厚み方向に亘って含浸させるようにする。具体的には、例えば、粘度の低い未加硫のフッ素ゴムを、他方面側から塗布するようにして含浸させる。その後、所定の時間乾燥させる。   Next, rubber is impregnated from the other side. In this case, a rubber layer is formed on the other side of the woven fabric and impregnated over the thickness direction of the woven fabric. Specifically, for example, an unvulcanized fluororubber having a low viscosity is impregnated so as to be applied from the other side. Then, it is dried for a predetermined time.

このようにして、この発明に係る表層材を製造する。この場合、含浸度合い、具体的には、例えば、ワニス状にした樹脂の粘度や含浸時間、含浸温度、未加硫フッ素ゴムの塗布状態、また、織布における嵩高糸の織り状態等を考慮して、織布層の内部に残存させる空隙の度合い、すなわち、残存空隙率を調整する。   Thus, the surface layer material according to the present invention is manufactured. In this case, the degree of impregnation, specifically, for example, the viscosity of the varnished resin, the impregnation time, the impregnation temperature, the application state of the unvulcanized fluoro rubber, the weaving state of the bulky yarn in the woven fabric, etc. are considered. Thus, the degree of voids remaining in the woven fabric layer, that is, the residual void ratio is adjusted.

このような表層材は、上記したように、表層材自体、具体的には、表層材の内部に配置される織布層の内部に空隙が設けられているため、表層材自体が凹凸追従性を有し、かつ、柔軟性が高いものとなる。また、一方面側が樹脂層から構成されているため、剥離性等が良好である。また、他方面側がゴム層から構成されているため、接着性が良好である。   As described above, since the surface layer material has a void in the surface layer material itself, specifically, the woven fabric layer arranged inside the surface layer material, the surface layer material itself has an uneven followability. And has high flexibility. Moreover, since one surface side is comprised from the resin layer, peelability etc. are favorable. Moreover, since the other surface side is comprised from the rubber layer, adhesiveness is favorable.

次に、上記した図1等に示すクッション材用表層材を含む熱プレス用クッション材の構成について説明する。図4は、この発明の一実施形態に係るクッション材用表層材を含む熱プレス用クッション材を厚み方向に切断して分解した場合の概略断面図である。   Next, the structure of the cushion material for hot press including the surface material for cushion material shown in FIG. FIG. 4 is a schematic cross-sectional view of a hot press cushion material including a cushion material surface layer material according to an embodiment of the present invention, which is cut and disassembled in the thickness direction.

図4を参照して、熱プレス用クッション材21は、上記した構成の2枚の表層材11a、11bと、4枚のクッション材本体22a、22b、22c、22dとを備える構成である。   With reference to FIG. 4, the cushion material 21 for hot press is a structure provided with the two surface layer materials 11a and 11b of the structure mentioned above, and the four cushion material main bodies 22a, 22b, 22c, and 22d.

熱プレス用クッション材21は、表面となる一方面側および裏面となる他方面側に2枚のクッション材用表層材11a、11bが配置される構成である。表面側に配置される第一の表層材11aについては、樹脂層が外方面、すなわち、図4中の紙面上側となるように設けられる。一方、裏面側に配置される第二の表層材11bについては、樹脂層が外方面、すなわち、図4中の紙面下側となるように設けられる。第一の表層材11aは、ゴム層の表面とクッション材本体22aの表面とを接着するようにして取り付けられる。また、第二の表層材11bは、ゴム層の表面とクッション材本体22dの表面とを接着するようにして取り付けられる。具体的には、未加硫のフッ素ゴム層とクッション材本体とを接触させ、圧力と熱を加えて未加硫フッ素ゴムを加硫すると同時に全体を接着一体化させるようにする。各クッション材本体22a〜22dは、それぞれの厚み方向の間に接着材23a、23b、23cを介在するようにして接着される。このようにして、熱プレス用クッション材21が構成されている。   The cushioning material 21 for hot pressing has a configuration in which two cushion material surface layers 11a and 11b are disposed on the one surface serving as the front surface and the other surface serving as the back surface. About the 1st surface layer material 11a arrange | positioned at the surface side, a resin layer is provided so that it may become an outer surface, ie, the paper surface upper side in FIG. On the other hand, about the 2nd surface layer material 11b arrange | positioned at a back surface side, a resin layer is provided so that it may become an outer surface, ie, the paper surface lower side in FIG. The first surface layer material 11a is attached so as to adhere the surface of the rubber layer and the surface of the cushion material body 22a. The second surface layer material 11b is attached so as to adhere the surface of the rubber layer and the surface of the cushion material body 22d. Specifically, the unvulcanized fluororubber layer and the cushion material body are brought into contact with each other, and pressure and heat are applied to vulcanize the unvulcanized fluororubber, and at the same time, the whole is bonded and integrated. Each cushion material main body 22a-22d is adhere | attached so that adhesive material 23a, 23b, 23c may be interposed between each thickness direction. Thus, the hot press cushion material 21 is configured.

このような熱プレス用クッション材21は、第一および第二の表層材11a、11b、具体的には、第一および第二の表層材11a、11b中の樹脂層により、熱盤や被圧縮体に対する剥離性が良好である。したがって、熱プレス時において、熱盤および被圧縮体の間に挟まれた場合でも、熱盤および被圧縮体への引っ付きを低減することができる。また、このような熱プレス用クッション材21は、第一および第二の表層材11a、11b、具体的には、第一および第二の表層材11a、11b中のゴム層により、クッション材本体22a、22bとの接着性が良好である。   Such a cushioning material 21 for hot press is composed of the first and second surface layer materials 11a and 11b, specifically, the hot platen and the object to be compressed by the resin layer in the first and second surface layer materials 11a and 11b. Good peelability to the body. Therefore, even when sandwiched between the hot platen and the compressed body during hot pressing, it is possible to reduce the sticking to the hot platen and the compressed object. Moreover, the cushion material 21 for such a hot press is composed of the first and second surface layer materials 11a and 11b, specifically, the cushion material body by the rubber layers in the first and second surface layer materials 11a and 11b. Adhesiveness with 22a and 22b is good.

また、このような熱プレス用クッション材21は、第一および第二の表層材11a、11bにより、凹凸追従性が良好であり、かつ、柔軟性が良好であるため、良好な製品を効率的に製造することができると共に、取扱いが良好で、耐久性の向上を図ることができる。   In addition, such a hot press cushion material 21 has good unevenness followability and good flexibility due to the first and second surface layer materials 11a and 11b, so that a good product can be efficiently used. In addition to being able to be manufactured, the handling is good and the durability can be improved.

織布として、バルキーヤーンを用いたガラス織布「A515」(ユニチカ株式会社製)を用いた。ガラス繊維の比重は、2.54(g/m)であり、目付け量は、515(g/m)である。そして、準備したガラス織布に対し、ガラス織布の片面側にワニス状にしたフッ素樹脂を塗布し、焼成を行った。フッ素樹脂の比重は、1.71(g/m)である。ここで、フッ素樹脂中には、導電性無機酸化物「23K」(ハクスイテック(株)製)を所定量含有させた。焼成後、その裏面に未加硫のフッ素ゴムを塗布し、乾燥させた。フッ素ゴムの比重は、1.96(g/m)である。このようにして、上記した構成の表層材を得た。 As the woven fabric, a glass woven fabric “A515” (manufactured by Unitika Ltd.) using a bulky yarn was used. The specific gravity of the glass fiber is 2.54 (g / m 3 ), and the basis weight is 515 (g / m 2 ). And the fluororesin made into the varnish form was apply | coated to the one side of the glass woven fabric with respect to the prepared glass woven fabric, and it baked. The specific gravity of the fluororesin is 1.71 (g / m 3 ). Here, a predetermined amount of conductive inorganic oxide “23K” (manufactured by Hakusuitec Co., Ltd.) was contained in the fluororesin. After firing, unvulcanized fluororubber was applied to the back surface and dried. The specific gravity of the fluororubber is 1.96 (g / m 3 ). In this way, a surface layer material having the above-described configuration was obtained.

クッション材本体としては、以下のように製造した。まず、バルキーヤーンを用いたガラス織布「T860」(ユニチカ株式会社製)を準備し、未加硫フッ素ゴム溶液に含浸させた。そして、これを十分に乾燥させて溶剤を除去した。その後、230℃で5時間、ベーキング処理し、クッション材本体を得た。なお、クッション材本体の構成および製造方法の詳細については、特開2008−132656号公報を参照するとよい。   The cushion material body was manufactured as follows. First, a glass woven fabric “T860” (manufactured by Unitika Ltd.) using a bulky yarn was prepared and impregnated with an unvulcanized fluororubber solution. And this was fully dried and the solvent was removed. Thereafter, baking was performed at 230 ° C. for 5 hours to obtain a cushion material body. For details of the configuration of the cushion material body and the manufacturing method, refer to Japanese Patent Application Laid-Open No. 2008-132656.

このようにして得られたクッション材本体を、2枚の表層材で挟み込み、この発明に係る熱プレス用クッション材を製造した。得られた熱プレス用クッション材の特性を、実施例1として評価した。   The cushion material body thus obtained was sandwiched between two surface layer materials to produce a hot press cushion material according to the present invention. The characteristic of the obtained cushion material for hot presses was evaluated as Example 1.

なお、比較例1として、特許文献1に記載の表層材を用いた。具体的な比較例1の構成として、表層材としての熱プレス用シートは、目付け量200(g/m)のガラスクロス「H201」(ユニチカ株式会社製)の片面に塗布量30(g/m)の離型性塗膜を形成し、その裏面にフッ素ゴムを塗布してなるものである。離型性塗膜の比重としては、1.09(g/m)である。フッ素ゴムの比重は、2.22(g/m)である。 In addition, as Comparative Example 1, the surface layer material described in Patent Document 1 was used. As a specific configuration of Comparative Example 1, a sheet for hot pressing as a surface layer material is applied on one side of a glass cloth “H201” (manufactured by Unitika Ltd.) having a basis weight of 200 (g / m 2 ). m 2 ) is formed, and a fluororubber is applied to the back surface thereof. The specific gravity of the releasable coating film is 1.09 (g / m 3 ). The specific gravity of the fluororubber is 2.22 (g / m 3 ).

比較例2として、アラミドクロスのみからなる表層材を用いた。アラミドクロスの比重は、1.37(g/m)であり、目付け量200(g/m)である。 As Comparative Example 2, a surface layer material made only of aramid cloth was used. The specific gravity of the aramid cloth is 1.37 (g / m 3 ), and the basis weight is 200 (g / m 2 ).

比較例3として、未処理のバルキークロス、すなわち、樹脂層やゴム層が形成されていない実施例1のガラス織布「A515」を表層材として用いた。   As Comparative Example 3, an untreated bulky cloth, that is, the glass woven fabric “A515” of Example 1 in which no resin layer or rubber layer was formed, was used as a surface layer material.

比較例4として、特許文献2に記載の表層材を用いた。具体的な比較例4の構成として、表層材としての接着シートは、目付け量200(g/m)のガラスクロス「H201」(ユニチカ株式会社製)からなる基材の両面に未加硫のフッ素ゴムを塗布し、さらにその上からポリイミド樹脂系の耐熱塗料を塗布してなる構成である。樹脂の比重は、2.19(g/m)である。また、フッ素ゴムは、比較例1と同じものを使用している。 As Comparative Example 4, the surface layer material described in Patent Document 2 was used. As a specific configuration of Comparative Example 4, the adhesive sheet as the surface layer material is unvulcanized on both surfaces of a base material made of glass cloth “H201” (manufactured by Unitika Ltd.) having a basis weight of 200 (g / m 2 ). In this configuration, a fluororubber is applied and a polyimide resin heat-resistant paint is further applied thereon. The specific gravity of the resin is 2.19 (g / m 3 ). Further, the same fluororubber as in Comparative Example 1 is used.

なお、比較例1〜比較例4のクッション材本体は、実施例1におけるクッション材本体と同じである。すなわち、実施例1、比較例1〜比較例4におけるクッション材は、表層材のみが異なる構成である。   The cushion material body of Comparative Examples 1 to 4 is the same as the cushion material body in Example 1. That is, the cushion material in Example 1 and Comparative Examples 1 to 4 has a configuration in which only the surface layer material is different.

表1および表2中のプレスの条件については、温度230℃で加圧力4MPaの荷重を加えたものである。プレスのサイクルとしては、加熱60分、冷却15分とした。なお、プレス10回後とは、プレスを10回行った後の状態で測定したものである。また、表1中、「−」は、測定していないことを示し、通気度の「0」は、全く通気していない状態、すなわち、気密性が最も良好であることを示す。表2中、○印は、「良好」な状態を示し、△印は、「やや問題有り」という状態を示し、×印は、「問題有り」という状態を示す。また、表1中の樹脂付着量とは、樹脂を織布に含浸させた際に樹脂が織布に付着した量であり、樹脂層および織布−樹脂複合層にある樹脂の量である。ゴム付着量とは、ゴムを織布に含浸させた際にゴムが織布に付着した量であり、ゴム層および織布−ゴム複合層にあるゴムの量である。   The press conditions in Tables 1 and 2 are those obtained by applying a load of 4 MPa at a temperature of 230 ° C. The press cycle was 60 minutes for heating and 15 minutes for cooling. In addition, after 10 times of press is measured in a state after 10 times of pressing. In Table 1, “-” indicates that no measurement is performed, and “0” of the air permeability indicates a state where no air is ventilated, that is, the airtightness is the best. In Table 2, ◯ indicates a “good” state, Δ indicates a “somewhat problematic” state, and x indicates a “problematic” state. Moreover, the resin adhesion amount in Table 1 is the amount of the resin adhered to the woven fabric when the woven fabric is impregnated with the resin, and is the amount of the resin in the resin layer and the woven fabric-resin composite layer. The rubber adhesion amount is the amount of rubber adhered to the woven fabric when the woven fabric is impregnated with rubber, and is the amount of rubber in the rubber layer and the woven fabric-rubber composite layer.

ここで、通気度を算出する通気性試験の試験方法については、JIS R3420(2006年)に準拠した方法であり、以下、簡単に説明する。通気性試験については、図5に示すフラジール形試験機31を用いる。フラジール形試験機31は、垂直形油気圧計32と、傾斜形油気圧計33と、2つの貯油槽34a、34bと、試験片Sを押さえるクランプ35と、円筒の仕切壁36と、空気孔37と、空気そらせ板38と、空気放出口39と、吸込ファン40とを備える。   Here, the test method of the air permeability test for calculating the air permeability is a method based on JIS R3420 (2006), and will be briefly described below. For the breathability test, a Frazier type testing machine 31 shown in FIG. 5 is used. The Frazier type tester 31 includes a vertical oil pressure gauge 32, an inclined oil pressure gauge 33, two oil storage tanks 34a and 34b, a clamp 35 for holding the test piece S, a cylindrical partition wall 36, an air hole 37, an air baffle plate 38, an air discharge port 39, and a suction fan 40.

操作方法については、以下の通りである。円筒の一端に試験片Sを置き、クランプ35で押さえて、取り付ける。加減抵抗器によって傾斜形油気圧計33が124.5Paの圧力を示すように空気を吸い込み、吸込ファン40を調整する。そのときの垂直形油気圧計32の示す圧力と、使用した空気孔37の種類とから、試験機に附属の表によって、試験片Sを通過する空気量cm×cm−2×s−1(cm/cmsec(秒))を求める。 The operation method is as follows. The test piece S is placed on one end of the cylinder and is attached by pressing with the clamp 35. Air is sucked in and the suction fan 40 is adjusted so that the inclination type oil pressure gauge 33 shows a pressure of 124.5 Pa by the adjusting resistor. From the pressure indicated by the vertical oil pressure gauge 32 at that time and the type of air hole 37 used, the amount of air passing through the test piece S according to the table attached to the tester cm 3 × cm −2 × s −1. (Cm 3 / cm 2 sec (seconds)) is obtained.

通気度、いわゆる、気密性に関しては、熱プレス用クッション材の取扱い時における吸引搬送のし易さ等の観点から、その値が低い方が良い。   Regarding the air permeability, so-called airtightness, it is better that the value is lower from the viewpoint of easiness of suction conveyance at the time of handling the cushion material for hot press.

表1を参照して、実施例1の空隙残存率は、初期において85.2%、プレス10回後において70.5%であり、プレス10回後においても、70%以上である。これに対し、比較例1の空隙残存率は、初期において68.4%、プレス10回後において46.9%、比較例4の空隙残存率は、初期において68.3%、プレス10回後において51.3%であり、いずれの場合も70%を切っている。通気度については、実施例1は、初期において0.2(cm/cmsec)、プレス10回後において0であり、気密性が非常に高いものである。比較例1および比較例4についても、気密性は良好であるが、比較例2および比較例3については、初期においてそれぞれ14.9(cm/cmsec)、19.5(cm/cmsec)、プレス10回後においてもそれぞれ、1.0(cm/cmsec)、2.0(cm/cmsec)であり、気密性について問題のあるレベルである。 Referring to Table 1, the void remaining rate of Example 1 is 85.2% in the initial stage, 70.5% after 10 presses, and 70% or more after 10 presses. On the other hand, the void remaining ratio of Comparative Example 1 was 68.4% at the initial stage, 46.9% after 10 presses, and the void remaining ratio of Comparative Example 4 was 68.3% at the initial stage, after 10 presses. In this case, it is less than 70%. The air permeability of Example 1 is 0.2 (cm 3 / cm 2 sec) in the initial stage and 0 after 10 presses, and the airtightness is very high. In Comparative Examples 1 and 4, the airtightness is also good, but in Comparative Examples 2 and 3, 14.9 (cm 3 / cm 2 sec) and 19.5 (cm 3 / cm 2 sec) and after 10 presses, 1.0 (cm 3 / cm 2 sec) and 2.0 (cm 3 / cm 2 sec), respectively, which are problematic levels of airtightness.

表2を参照して、実施例1に係る熱プレス用クッション材は、初期およびプレス10回後においても、凹凸追従性、曲げシワ、毛羽発生、剥離性の点において、全て良好であった。これに対し、比較例1および比較例4は、初期およびプレス10回後のいずれにおいても、凹凸追従性および曲げシワについて、問題があった。剥離性についても、不十分であった。比較例2は、初期における剥離性に問題があり、毛羽発生について不十分であった。プレス10回後においては、曲げシワ以外の項目で、問題があった。比較例3は、初期において、毛羽発生について問題があった。プレス10回後においては、凹凸追従性および毛羽発生について問題があった。   Referring to Table 2, the cushion material for hot press according to Example 1 was all good in terms of unevenness followability, bending wrinkle, fluff generation, and peelability even at the initial stage and after 10 presses. On the other hand, Comparative Example 1 and Comparative Example 4 had problems with respect to unevenness followability and bending wrinkles both in the initial stage and after 10 presses. The peelability was also insufficient. In Comparative Example 2, there was a problem in the peelability at the initial stage, and the generation of fluff was insufficient. There were problems in items other than bending wrinkles after 10 presses. In Comparative Example 3, there was a problem with the occurrence of fluff in the initial stage. After 10 presses, there was a problem with uneven tracking and fluff generation.

以上より、実施例1については、凹凸追従性、曲げシワ、毛羽発生、剥離性の点において、全て良好であり、さらに、気密性が良好である。一方、比較例1〜比較例4においては、上記した項目の少なくとも一つに問題のあるレベルである。   As mentioned above, about Example 1, all are favorable in terms of uneven | corrugated followable | trackability, a bending wrinkle, fluff generation | occurrence | production, and peelability, and also airtightness is favorable. On the other hand, in Comparative Examples 1 to 4, there is a problem level in at least one of the above items.

なお、上記の実施の形態において、熱プレス用クッション材は、2枚の表層材と、4枚のクッション材本体とを備えることとしたが、このような形態に限らず、例えば、以下のような構成のものであってもよい。   In the above embodiment, the hot press cushion material includes two surface layer materials and four cushion material bodies. However, the present invention is not limited to such a form, and for example, as follows. It may be of a simple configuration.

図6は、この発明の他の実施形態に係るクッション材用表層材を含む熱プレス用クッション材を厚み方向に切断して分解した場合の概略断面図である。図6を参照して、熱プレス用クッション材41は、2枚の表層材42a、42bと、1枚のクッション材本体43とを備える。2枚の表層材42a、42bについては、クッション材本体43の表裏に取り付けられるようにして配置される。この場合も上記した図4に示すクッション材と同様に、表層材42a、42bのそれぞれのゴム層が、クッション材本体43の両面に接着するようにして取り付けられる。このような構成であってもよい。   FIG. 6 is a schematic cross-sectional view of a hot-press cushion material including a cushion material surface layer material according to another embodiment of the present invention cut and disassembled in the thickness direction. Referring to FIG. 6, the hot press cushion material 41 includes two surface layer materials 42 a and 42 b and one cushion material main body 43. The two surface layer materials 42 a and 42 b are arranged so as to be attached to the front and back of the cushion material main body 43. Also in this case, similarly to the cushion material shown in FIG. 4 described above, the respective rubber layers of the surface layer materials 42 a and 42 b are attached so as to adhere to both surfaces of the cushion material body 43. Such a configuration may be used.

また、図7に示すように、クッション材46は、2枚の表層材47a、47bと、複数枚のクッション材本体48とを備える構成であってもよい。すなわち、複数枚のクッション材本体48をそれぞれ、接着材49で接着し、クッション材46の最外面となる表面側および裏面側に、2枚の表層材47a、47bを配置させる。このような構成であってもよい。   Further, as shown in FIG. 7, the cushion material 46 may be configured to include two surface layer materials 47 a and 47 b and a plurality of cushion material bodies 48. That is, the plurality of cushion material bodies 48 are respectively bonded with the adhesive material 49, and the two surface layer materials 47 a and 47 b are arranged on the front surface side and the back surface side which are the outermost surfaces of the cushion material 46. Such a configuration may be used.

さらに、図8に示すように、クッション材51は、2枚の表層材52a、52bと、2枚のクッション材本体53a、53bに加え、シート状のフッ素ゴム54を配置させるようにしてもよい。この場合、フッ素ゴム54とクッション材本体53a、53bとの間を接着材55a、55bにより接着するようにする。このような構成であってもよい。   Further, as shown in FIG. 8, the cushion material 51 may include a sheet-like fluoro rubber 54 in addition to the two surface layer materials 52 a and 52 b and the two cushion material bodies 53 a and 53 b. . In this case, the fluororubber 54 and the cushion material bodies 53a and 53b are bonded by the adhesive materials 55a and 55b. Such a configuration may be used.

なお、上記の実施の形態においては、樹脂として耐熱性樹脂を用いることとしたが、これに限らず、プレス時に高温の熱が加えられない場合には、耐熱性を有しない樹脂を用いることもできる。また、この場合、ゴムについても、耐熱性を有しないゴムを適用することとしてもよい。   In the above embodiment, the heat-resistant resin is used as the resin. However, the present invention is not limited to this, and if high-temperature heat is not applied during pressing, a resin having no heat resistance may be used. it can. In this case, a rubber that does not have heat resistance may be applied to the rubber.

以上、図面を参照してこの発明の実施の形態を説明したが、この発明は、図示した実施の形態のものに限定されない。図示した実施の形態に対して、この発明と同一の範囲内において、あるいは均等の範囲内において、種々の修正や変形を加えることが可能である。   Although the embodiments of the present invention have been described with reference to the drawings, the present invention is not limited to the illustrated embodiments. Various modifications and variations can be made to the illustrated embodiment within the same range or equivalent range as the present invention.

この発明に係るクッション材用表層材および熱プレス用クッション材は、積層板の良好な生産性等が要求される場合に、有効に利用される。   The cushion material surface layer material and the hot press cushion material according to the present invention are effectively used when good productivity and the like of the laminated board are required.

11a,11b,42a,42b,47a,47b,52a,52b 表層材、12 樹脂層、13 ゴム層、14 織布層、15a,15b 表面、17 織布−樹脂複合層、18 織布−ゴム複合層、19a,19b 面、20 空隙、21,41,46,51 クッション材、22a,22b,22c,22d,43,48,53a,53b クッション材本体、23a,23b,23c,49,55a,55b 接着材、31 フラジール形試験機、32 垂直形油気圧計、33 傾斜形油気圧計、34a,34b 貯油槽、35 クランプ、36 仕切壁、37 空気孔、38 空気そらせ板、39 空気放出口、40 吸込ファン、54 フッ素ゴム。   11a, 11b, 42a, 42b, 47a, 47b, 52a, 52b Surface material, 12 resin layer, 13 rubber layer, 14 woven fabric layer, 15a, 15b surface, 17 woven fabric-resin composite layer, 18 woven fabric-rubber composite Layer, 19a, 19b surface, 20 air gap, 21, 41, 46, 51 cushion material, 22a, 22b, 22c, 22d, 43, 48, 53a, 53b cushion material body, 23a, 23b, 23c, 49, 55a, 55b Adhesive, 31 Frazier type testing machine, 32 Vertical oil pressure gauge, 33 Inclined oil pressure gauge, 34a, 34b Oil storage tank, 35 Clamp, 36 Partition wall, 37 Air hole, 38 Air baffle plate, 39 Air outlet, 40 Suction fan, 54 Fluoro rubber.

Claims (11)

熱プレス用クッション材の表層に配置されるシート状のクッション材用表層材であって、
前記表層材の一方面側に配置され、前記表層材の一方面を覆う樹脂層と、
前記表層材の他方面側に配置され、前記表層材の他方面を覆うゴム層と、
シート状の織布から構成されており、前記樹脂層および前記ゴム層の間に配置され、経糸および緯糸のうちの少なくともいずれか一方に嵩高糸を用いた織布層とを備え、
前記織布層は、前記樹脂層側に設けられ、前記織布の一部に前記樹脂層を構成する樹脂を含浸させて形成される織布−樹脂複合層と、
前記ゴム層側に設けられ、前記織布の一部に前記ゴム層を構成するゴムを含浸させて形成される織布−ゴム複合層とを含み、
前記織布層の内部には、空隙が設けられている、クッション材用表層材。
A surface layer material for a cushion material in the form of a sheet placed on the surface layer of a heat press cushion material,
A resin layer disposed on one side of the surface material and covering one surface of the surface material;
A rubber layer disposed on the other surface side of the surface layer material and covering the other surface of the surface layer material;
It is composed of a sheet-like woven fabric, and is disposed between the resin layer and the rubber layer, and includes a woven fabric layer using a bulky yarn for at least one of warp and weft,
The woven fabric layer is provided on the resin layer side, and a woven fabric-resin composite layer formed by impregnating a part of the woven fabric with a resin constituting the resin layer;
A woven fabric-rubber composite layer provided on the rubber layer side and formed by impregnating a part of the woven fabric with rubber constituting the rubber layer;
A surface layer material for a cushion material, wherein a gap is provided inside the woven fabric layer.
基材としての織布に対する前記織布層の空隙残存率は、70%以上である、請求項1に記載のクッション材用表層材。 The surface layer material for cushion materials according to claim 1, wherein a void remaining ratio of the woven fabric layer with respect to the woven fabric as a base material is 70% or more. 前記樹脂は、耐熱性樹脂である、請求項1または2に記載のクッション材用表層材。 The cushion material surface layer material according to claim 1, wherein the resin is a heat-resistant resin. 前記耐熱性樹脂の融点およびガラス転移点のうちの少なくともいずれか一方は、200℃以上である、請求項3に記載のクッション材用表層材。 The surface material for a cushion material according to claim 3, wherein at least one of the melting point and the glass transition point of the heat resistant resin is 200 ° C or higher. 前記樹脂は、フッ素樹脂、フェノール樹脂、メラミン樹脂、エポキシ樹脂、不飽和ポリエステル樹脂、シリコーン樹脂、ポリイミド樹脂、熱硬化性アクリル樹脂、フラン樹脂、ユリア油脂、ジアリルフタレート樹脂、ポリウレタン樹脂からなる群から選択される1種の樹脂または2種以上の樹脂の混合物である、請求項1〜4のいずれかに記載のクッション材用表層材。 The resin is selected from the group consisting of fluorine resin, phenol resin, melamine resin, epoxy resin, unsaturated polyester resin, silicone resin, polyimide resin, thermosetting acrylic resin, furan resin, urea oil, diallyl phthalate resin, and polyurethane resin. The surface layer material for cushion materials according to any one of claims 1 to 4, which is one kind of resin or a mixture of two or more kinds of resins. 前記樹脂には、導電性を有する無機粉末が含有されている、請求項1〜5のいずれかに記載のクッション材用表層材。 The cushion material surface layer material according to any one of claims 1 to 5, wherein the resin contains conductive inorganic powder. 前記無機粉末は、カーボン粉末、アルミニウム粉末、酸化チタン粉末、酸化亜鉛粉末、酸化鉄粉末からなる群から選択される1種の粉末または2種以上の粉末の混合物である、請求項6に記載のクッション材用表層材。 The inorganic powder is one kind of powder selected from the group consisting of carbon powder, aluminum powder, titanium oxide powder, zinc oxide powder, and iron oxide powder, or a mixture of two or more kinds of powders. Surface material for cushioning material. 前記織布は、バルキーヤーンを用いたガラス繊維またはアラミド繊維である、請求項1〜7のいずれかに記載のクッション材用表層材。 The said woven fabric is the surface material for cushion materials in any one of Claims 1-7 which are the glass fiber or aramid fiber which used the bulky yarn. 前記織布は、1重織りまたは多重織りされたものである、請求項1〜8のいずれかに記載のクッション材用表層材。 The surface material for a cushion material according to any one of claims 1 to 8, wherein the woven fabric is a single woven fabric or a multi-woven fabric. 前記ゴムは、フッ素ゴム、EPM、EPDM、水素化ニトリルゴム、シリコーンゴム、アクリルゴムおよびブチルゴムからなる群から選択される1種のゴムまたは2種以上のゴムの混合物である、請求項1〜9のいずれかに記載のクッション材用表層材。 The rubber is one rubber selected from the group consisting of fluorine rubber, EPM, EPDM, hydrogenated nitrile rubber, silicone rubber, acrylic rubber and butyl rubber, or a mixture of two or more rubbers. The surface material for cushion materials according to any one of the above. 熱プレスに用いられる熱プレス用クッション材であって、
前記熱プレス用クッション材は、その表層に配置されるシート状のクッション材用表層材を含み、
前記クッション材用表層材は、前記表層材の一方面側に配置され、前記表層材の一方面を覆う樹脂層と、前記表層材の他方面側に配置され、前記表層材の他方面を覆うゴム層と、シート状の織布から構成されており、前記樹脂層および前記ゴム層の間に配置され、経糸および緯糸のうちの少なくともいずれか一方に嵩高糸を用いた織布層とを備え、
前記織布層は、前記樹脂層側に設けられ、前記織布の一部に前記樹脂層を構成する樹脂を含浸させて形成される織布−樹脂複合層と、
前記ゴム層側に設けられ、前記織布の一部に前記ゴム層を構成するゴムを含浸させて形成される織布−ゴム複合層とを含み、
前記織布層の内部には、空隙が設けられている、熱プレス用クッション材。
It is a cushion material for hot press used for hot press,
The cushion material for hot press includes a sheet-shaped cushion material surface layer material disposed on the surface layer,
The cushion material surface layer material is disposed on one surface side of the surface layer material, the resin layer covering one surface of the surface layer material, and the other surface side of the surface layer material, covering the other surface of the surface layer material. It is composed of a rubber layer and a sheet-like woven fabric, and is provided between the resin layer and the rubber layer, and includes a woven fabric layer using bulky yarn for at least one of warp and weft. ,
The woven fabric layer is provided on the resin layer side, and a woven fabric-resin composite layer formed by impregnating a part of the woven fabric with a resin constituting the resin layer;
A woven fabric-rubber composite layer provided on the rubber layer side and formed by impregnating a part of the woven fabric with rubber constituting the rubber layer;
A cushioning material for hot pressing, wherein a gap is provided inside the woven fabric layer.
JP2009275580A 2009-12-03 2009-12-03 Cushion material surface layer and heat press cushion material Active JP5341733B2 (en)