JP5337680B2 - Liquid fiber product treatment composition - Google Patents
Liquid fiber product treatment composition Download PDFInfo
- Publication number
- JP5337680B2 JP5337680B2 JP2009275677A JP2009275677A JP5337680B2 JP 5337680 B2 JP5337680 B2 JP 5337680B2 JP 2009275677 A JP2009275677 A JP 2009275677A JP 2009275677 A JP2009275677 A JP 2009275677A JP 5337680 B2 JP5337680 B2 JP 5337680B2
- Authority
- JP
- Japan
- Prior art keywords
- component
- fragrance
- mass
- agent composition
- fiber product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、液状繊維製品処理剤組成物に関する。 The present invention relates to a liquid fiber product treating agent composition.
香気の放出を長続きさせる技術を一般にロングラスティング技術という。この技術は、様々な技術分野で利用されており、例えば香料を含む柔軟剤、仕上げ剤、その他各種の繊維製品処理剤を繊維製品に適用して香料を繊維製品に付着させている。
従来、ロングラスティング技術として、マイクロカプセルの活用（例えば、特許文献１）、香料前駆体の使用（例えば、特許文献２）、特定の香料成分の組合せ（例えば、特許文献３）などが公開されている。また、香料成分と粘土鉱物とを含む複数の成分を組み合わせる技術が提案されている。たとえば特許文献４では、繊維製品に高い残香性を付与できる液体仕上げ剤組成物として、香料組成物と、有機変性粘土鉱物と、アルキレンオキシド付加型非イオン界面活性剤と、水性液体とを配合したものが提案されている。
The technology that continues the release of fragrance is generally called the long lasting technology. This technology is used in various technical fields. For example, a softener containing a fragrance, a finishing agent, and various other fiber product treatment agents are applied to the fiber product to attach the fragrance to the fiber product.
Conventionally, utilization of microcapsules (for example, Patent Document 1), use of a fragrance precursor (for example, Patent Document 2), a combination of specific fragrance components (for example, Patent Document 3), etc. have been disclosed as long lasting techniques. ing. Moreover, the technique which combines the some component containing a fragrance | flavor component and a clay mineral is proposed. For example, in Patent Document 4, a fragrance composition, an organically modified clay mineral, an alkylene oxide-added nonionic surfactant, and an aqueous liquid are blended as a liquid finish composition that can impart high residual fragrance properties to a textile product. Things have been proposed.
しかしながら、従来の技術では、残香の付与性能の向上と、繊維製品処理剤に求められる液外観の透明性とを両立することが難しい。たとえば繊維製品に望ましい残香を充分に付与することができなかったり、ある程度良好な残香を付与できたとしても、液外観の透明性が低く、繊維製品に直接噴霧する等の用途に適さない等の問題がある。
たとえばマイクロカプセルを活用する技術は、繊維製品等、香料を適用した対象物を擦ることでカプセルを破壊し、香りを発散させる技術であり、カプセルが破壊されなければ香りは発散しない。従って、マイクロカプセルを破壊し得る程度の力が対象物に加わらないような状況下では、ロングラスティング効果を期待できない。また、そのような力を対象物に加えることができる状況下でのロングラスティング効果は高いが、擦ることによって対象物が傷むこともある。さらに、この場合に使用するマイクロカプセルは水不溶性であるため、組成物の外観を透明にすることは困難である。香料前駆体を使用した場合、前駆体から放出される香料成分の香りが持続するが、残香の香調が限定される。特定の香料の組合せの場合、ラストノートとよばれる成分の香りは持続するが、残香の香調が限定される。特許文献４に記載の方法の場合、仕上げ剤として洗濯の際に用いる分にはあまり問題にはならないが、繊維製品に直接噴霧するには液外観の透明性が充分とはいえない。
本発明は、上記事情に鑑みてなされたものであって、繊維製品に望ましい残香を付与でき、透明性にも優れた液状繊維製品処理剤組成物および繊維製品処理剤製品を提供することを目的とする。
However, with the conventional technology, it is difficult to achieve both improvement in the performance of imparting residual scent and transparency of the liquid appearance required for a textile product treating agent. For example, even if the desired residual fragrance cannot be sufficiently imparted to the textile product, or even if a somewhat favorable residual fragrance can be imparted, the liquid appearance is not transparent and is not suitable for applications such as spraying directly on the textile product. There's a problem.
For example, a technique using a microcapsule is a technique that breaks a capsule by rubbing an object to which a fragrance is applied, such as a textile product, and emits a scent. If the capsule is not broken, the scent does not diverge. Accordingly, the long lasting effect cannot be expected under a situation where a force that can break the microcapsules is not applied to the object. In addition, the long lasting effect in a situation where such a force can be applied to the object is high, but the object may be damaged by rubbing. Furthermore, since the microcapsules used in this case are insoluble in water, it is difficult to make the appearance of the composition transparent. When a fragrance | flavor precursor is used, the fragrance of the fragrance | flavor component discharge | released from a precursor continues, but the fragrance | flavor tone of a residual fragrance is limited. In the case of a combination of specific fragrances, the scent of the component called “last note” persists, but the scent of the remaining scent is limited. In the case of the method described in Patent Document 4, there is not much problem with the amount used as a finishing agent in washing, but it cannot be said that the transparency of the liquid appearance is sufficient for spraying directly on textiles.
The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a liquid fiber product treating agent composition and a fiber product treating agent product that can impart a desired residual scent to a fiber product and that are excellent in transparency. And
上記課題を解決する本発明は、以下の態様を有する。
［１］（Ａ）合成スメクタイトを０．０１〜５質量％、（Ｂ）常圧における沸点が２６０℃未満であって、ＣｌｏｇＰ値が１．０以上６．０以下である香料成分（ｂ１）を含有する香料組成物を０．０１〜５質量％、（Ｃ）水溶性溶剤を０．１〜５０質量％未満、（Ｄ）ＨＬＢが１０〜１４で、ポリオキシエチレン硬化ヒマシ油、ポリオキシエチレンアルキルエーテルおよびポリオキシエチレンアルケニルエーテルから選ばれる少なくとも１種の非イオン性界面活性剤を０．０１〜５質量％含有し、波長６６０ｎｍにおける吸光度が１．５未満である液状繊維製品処理剤組成物。
［２］前記（Ａ）成分の含有量が０．５〜５質量％である、［１］に記載の液状繊維製品処理剤組成物。
［３］前記（Ｄ）成分が、オキシエチレン基の平均付加モル数が３０〜４０モルのポリオキシエチレン硬化ヒマシ油である、［１］または［２］に記載の液状繊維製品処理剤組成物。
［４］前記（Ｃ）成分の含有量が２０〜４０質量％である、［１］〜［３］のいずれか一項に記載の液状繊維製品処理剤組成物。
［５］前記（Ａ）成分および前記（Ｂ）成分の含有量の質量比が、（Ａ）成分：（Ｂ）成分＝１：３〜３：１の範囲内である、［１］〜［４］のいずれか一項に記載の液状繊維製品処理剤組成物。
［６］前記（Ｂ）成分が、前記香料成分（ｂ１）として、シトロネロール、リモネン、ゲラニオール、メントール、シトロネラール、シトラール及びピネンからなる群から選ばれる少なくとも１種の特定香料成分を含有し、前記（Ｂ）成分中の前記特定香料成分の含有量が１０質量％以上である、［１］〜［５］のいずれか一項に記載の液状繊維製品処理剤組成物。
［７］さらに、（Ｅ）下記一般式（１）または（２）で表される化合物から選ばれる少なくとも１種のシリコーン化合物を含有する、［１］〜［６］のいずれか一項に記載の液状繊維製品処理剤組成物。
The present invention for solving the above problems has the following aspects.
[1] (A) 0.01-5% by mass of synthetic smectite, (B) Perfume component (b1) having a boiling point at atmospheric pressure of less than 260 ° C. and a ClogP value of 1.0 or more and 6.0 or less A fragrance composition containing 0.01 to 5% by mass, (C) 0.1 to less than 50% by mass of a water-soluble solvent, (D) HLB is 10 to 14, polyoxyethylene hydrogenated castor oil, polyoxy Liquid fiber product treating agent composition containing 0.01 to 5% by mass of at least one nonionic surfactant selected from ethylene alkyl ether and polyoxyethylene alkenyl ether and having an absorbance at a wavelength of 660 nm of less than 1.5 object.
[2] The liquid fiber product treating agent composition according to [1], wherein the content of the component (A) is 0.5 to 5% by mass.
[3] The liquid fiber product treating agent composition according to [1] or [2], wherein the component (D) is a polyoxyethylene hydrogenated castor oil having an average addition mole number of oxyethylene groups of 30 to 40 moles. .
[4] The liquid fiber product treating agent composition according to any one of [1] to [3], wherein the content of the component (C) is 20 to 40% by mass.
[5] The mass ratio of the content of the component (A) and the component (B) is within the range of (A) component: (B) component = 1: 3 to 3: 1. 4] The liquid fiber product treating agent composition according to any one of [4].
[ 6 ] The component (B) contains at least one specific fragrance component selected from the group consisting of citronellol, limonene, geraniol, menthol, citronellal, citral and pinene as the fragrance component (b1), B) The liquid fiber product treating agent composition according to any one of [1] to [5] , wherein the content of the specific flavor component in the component is 10% by mass or more.
[ 7 ] The method according to any one of [1] to [6], further comprising (E) at least one silicone compound selected from compounds represented by the following general formula (1) or (2): A liquid fiber product treating agent composition.
［８］［１］〜［７］のいずれか一項に記載の液状繊維製品処理剤組成物を、トリガー式スプレー容器に収容した繊維製品処理剤製品。 [ 8 ] A fiber product treating agent product containing the liquid fiber product treating agent composition according to any one of [1] to [ 7 ] in a trigger spray container.
本発明によれば、繊維製品に望ましい残香を付与でき、透明性にも優れた液状繊維製品処理剤組成物および繊維製品処理剤製品を提供できる。 According to the present invention, it is possible to provide a liquid fiber product treating agent composition and a fiber product treating agent product that can impart a desired residual scent to the fiber product and are excellent in transparency.
≪液状繊維製品処理剤組成物≫
本発明の液状繊維製品処理剤組成物（以下、単に処理剤組成物ということがある。）は、以下に示す（Ａ）〜（Ｄ）成分を含有する。
本発明の処理剤組成物は、さらに、後述する（Ｅ）成分を含有することが好ましい。
≪Liquid fiber product treatment composition≫
The liquid fiber product treating agent composition of the present invention (hereinafter sometimes simply referred to as a treating agent composition) contains the following components (A) to (D).
It is preferable that the processing agent composition of this invention contains the (E) component mentioned later further.
＜（Ａ）成分＞
（Ａ）成分は合成スメクタイトである。
スメクタイトは、層状構造を有する無機化合物であり、たとえばモンモリロナイト、バイデライト、ノントロナイト、サポナイト、ヘクトライト、ソーコナイト、スチーブンサイト等が挙げられる。
スメクタイトには天然産出品と合成品とが存在する。天然には、主に、粘土の主成分として産出され、たとえばベントナイトはモンモリロナイトを主成分として含んでいる。
本発明においては、処理剤組成物の外観を透明または半透明にする観点から、合成品を用いることが必要である。特に、２５℃のイオン交換水を用いて当該合成スメクタイトの１質量％水溶液を調製した場合に、該水溶液の外観が透明または半透明となるものを用いることが好ましい。
ここで、本発明の処理剤組成物または前記１質量％水溶液の外観が「透明または半透明」であるとは、吸光度計（例えば、ＨＩＴＡＣＨＩ Ｓｐｅｃｔｒｏｐｈｏｔｏｍｅｔｅｒ Ｕ−３０１０、１ｃｍ×１ｃｍの石英セル、対照はイオン交換水）を使用し、当該処理剤組成物または１質量％水溶液の波長６６０ｎｍにおける吸光度を測定した際に、その測定値が１．５未満であることを意味する。
前記１質量％水溶液の前記吸光度の測定値は、１．０未満であることが好ましく、０．８未満であることがより好ましい。
また、本発明の処理剤組成物の前記吸光度の測定値は、１．０未満であることがより好ましい。
（Ａ）成分としては、合成ヘクトライトおよび合成サポナイトから選ばれる少なくとも１種が好ましく、合成ヘクトライトが特に好ましい。
市場で入手可能な（Ａ）成分として、例えば、スメクトンＳＡ（クニミネ工業（株）製）、イオナイトＨ（水澤化学工業（株）製）、ＳＷＮ、ＳＷＦ（以上、コープケミカル（株）製）、ラポナイトＲＤ、ラポナイトＸＬＧ、ラポナイトＳ４８２（以上、ロックウッドアディティヴス（株）製）などが挙げられる。これらの中でも、処理剤組成物の外観の透明性、及び残香性の観点から、ラポナイトＲＤ、ラポナイトＸＬＧ（以上、ロックウッドアディティヴス（株）製）が特に好ましい。
（Ａ）成分は、１種を単独で用いてもよく、２種類以上を組み合わせて用いてもよい。
本発明の処理剤組成物中、（Ａ）成分の含有量は、処理剤組成物の全量を基準として、０．０１〜５質量％であり、残香の香り強度を適度なものにし、フレッシュな香りを長続きさせる観点から、０．５〜２質量％が好ましい。一方、５質量％を超えて配合すると処理剤組成物の外観を透明にすることが困難となるおそれがある
<(A) component>
The component (A) is synthetic smectite.
Smectite is an inorganic compound having a layered structure, and examples thereof include montmorillonite, beidellite, nontronite, saponite, hectorite, soconite, and stevensite.
Smectite has both natural products and synthetic products. Naturally, it is mainly produced as a main component of clay. For example, bentonite contains montmorillonite as a main component.
In the present invention, it is necessary to use a synthetic product from the viewpoint of making the appearance of the treatment composition transparent or translucent. In particular, when a 1% by mass aqueous solution of the synthetic smectite is prepared using ion-exchanged water at 25 ° C., it is preferable to use a solution in which the appearance of the aqueous solution is transparent or translucent.
Here, the appearance of the treatment composition of the present invention or the 1% by mass aqueous solution is “transparent or translucent” means that the absorbance meter (for example, HITACHI Spectrophotometer U-3010, 1 cm × 1 cm quartz cell, control is This means that when the absorbance at a wavelength of 660 nm of the treating agent composition or 1% by mass aqueous solution is measured using ion-exchanged water, the measured value is less than 1.5.
The measured value of the absorbance of the 1% by mass aqueous solution is preferably less than 1.0, and more preferably less than 0.8.
Moreover, it is more preferable that the measured value of the absorbance of the treatment agent composition of the present invention is less than 1.0.
As the component (A), at least one selected from synthetic hectorite and synthetic saponite is preferable, and synthetic hectorite is particularly preferable.
As the component (A) available on the market, for example, Smecton SA (manufactured by Kunimine Industry Co., Ltd.), Ionite H (manufactured by Mizusawa Chemical Industry Co., Ltd.), SWN, SWF (manufactured by Coop Chemical Co., Ltd.), Laponite RD, Laponite XLG, Laponite S482 (above, manufactured by Rockwood Additives Co., Ltd.) and the like can be mentioned. Among these, Laponite RD and Laponite XLG (manufactured by Rockwood Additives Co., Ltd.) are particularly preferable from the viewpoints of the transparency of the appearance of the treating agent composition and the remaining fragrance.
As the component (A), one type may be used alone, or two or more types may be used in combination.
In the treatment agent composition of the present invention, the content of the component (A) is 0.01 to 5% by mass based on the total amount of the treatment agent composition, and the fragrance strength of the remaining scent is made moderate and fresh. From the viewpoint of long-lasting fragrance, 0.5 to 2% by mass is preferable. On the other hand, when it exceeds 5 mass%, it may be difficult to make the appearance of the treatment composition transparent.
＜（Ｂ）成分＞
（Ｂ）成分は、常圧（１気圧、１０１３．２５ｈＰａ）における沸点が２６０℃未満であって、ＣｌｏｇＰ値が１．０以上６．０以下である香料成分（ｂ１）を含有する香料組成物である。香料成分（ｂ１）を含有することにより、本発明の処理剤組成物で繊維製品を処理した際、フレッシュな香りを感じさせることが可能となる。加えて消費者の嗜好性も高い。
香料成分（ｂ１）の沸点は、２４０℃未満が好ましく、２００℃未満がより好ましい。また、該沸点は、香りが衣類等の繊維製品に残りやすい点から、１４０℃以上が好ましく、１５０℃以上がより好ましい。
香料成分（ｂ１）のＣｌｏｇＰ値は、２．０以上５．０以下であることが好ましく、２．５以上５．０以下であることがより好ましい。
<(B) component>
(B) The fragrance | flavor composition containing the fragrance | flavor component (b1) whose boiling point in a normal pressure (1 atmosphere, 101.25 hPa) is less than 260 degreeC, and whose ClogP value is 1.0 or more and 6.0 or less. It is. By containing the fragrance component (b1), it is possible to feel a fresh scent when the fiber product is treated with the treatment agent composition of the present invention. In addition, consumer preference is high.
The boiling point of the fragrance component (b1) is preferably less than 240 ° C, and more preferably less than 200 ° C. In addition, the boiling point is preferably 140 ° C. or higher, more preferably 150 ° C. or higher, from the viewpoint that the fragrance is likely to remain in textiles such as clothing.
The ClogP value of the fragrance component (b1) is preferably 2.0 or more and 5.0 or less, and more preferably 2.5 or more and 5.0 or less.
本発明において、香料成分の沸点は、例えば「Ｐｅｒｆｕｍｅ ａｎｄ Ｆｌａｖｏｒ Ｃｈｅｍｉｃａｌｓ 」Ｖｏｌ．Ｉａｎｄ ＩＩ，Ｓｔｅｆｆｅｎ Ａｒｃｔａｎｄｅｒ，Ａｌｌｕｒｅｄ Ｐｕｂ．Ｃｏ．（１９９４）及び「合成香料 化学と商品知識」、印藤元一著、化学工業日報社（１９９６）及び「Ｐｅｒｆｕｍｅ ａｎｄ Ｆｌａｖｏｒ Ｍａｔｅｒｉａｌｓ ｏｆ Ｎａｔｕｒａｌ Ｏｒｉｇｉｎ」，Ｓｔｅｆｆｅｎ Ａｒｃｔａｎｄｅｒ，Ａｌｌｕｒｅｄ Ｐｕｂ．Ｃｏ．（１９９４）及び「香りの百科」、日本香料協会編、朝倉書店（１９８９）及び「香料と調香の基礎知識」、産業図書（１９９５）に記載されており、本明細書ではそれらの文献から引用する。
ＣｌｏｇＰ値とは、化学物質について、１−オクタノール中及び水中の平衡濃度の比を表す１−オクタノール／水分配係数Ｐを、底１０に対する対数ｌｏｇＰの形態で表した値である。前記ＣｌｏｇＰ値は、ｆ値法（疎水性フラグメント定数法）により、化合物の化学構造をその構成要素に分解し、各フラグメントの有する疎水性フラグメント定数・ｆ値を積算して求めることができる（例えば、Ｃｌｏｇ ３ Ｒｅｆｅｒｅｎｃｅ Ｍａｎｕａｌ ＤａｙｌｉｇｈｔＳｏｆｔｗａｒｅ ４．３４，Ａｌｂｅｒｔ Ｌｅｏ，Ｄａｖｉｄ Ｗｅｉｎｉｎｇｅｒ， Ｖｅｒｓｉｏｎ １，Ｍａｒｃｈ １９９４ 参照）。
一般に、香料成分はＣｌｏｇＰ値が大きいほど疎水的であることから、ＣｌｏｇＰ値が小さい香料成分を多く含んで構成された香料組成物は、ＣｌｏｇＰ値が大きい香料成分を多く含んで構成された香料組成物よりも親水的な香料であるといえる。
前記ＣｌｏｇＰ値が前記範囲内であると、香料成分の親水性と疎水性とのバランスが良好で、より香気バランスに優れ嗜好性が高い香料組成物となる点で有利である。
In the present invention, the boiling point of the fragrance component is, for example, “Perfume and Flavor Chemicals” Vol. Iand II, Steffen Arctander, Allured Pub. Co. (1994) and “Synthetic fragrance chemistry and commercial knowledge”, Motoichi Into, Chemical Industry Daily (1996) and “Perfume and Flavor Materials of Natural Origin”, Stephen Arctander, Allred Pub. Co. (1994) and "Encyclopedia of Scent", edited by Japan Fragrance Association, Asakura Shoten (1989) and "Basic knowledge of perfume and fragrance", Sangyo Tosho (1995). Quote.
The ClogP value is a value representing a 1-octanol / water partition coefficient P representing a ratio of equilibrium concentrations in 1-octanol and in water in the form of logarithmic logP with respect to the base 10 for a chemical substance. The ClogP value can be obtained by f-method (hydrophobic fragment constant method) by decomposing the chemical structure of a compound into its components and integrating the hydrophobic fragment constants / f values possessed by each fragment (for example, , Clog 3 Reference Manual DaylightSoftware 4.34, Albert Leo, David Weininger, Version 1, March 1994).
Generally, since a fragrance | flavor component is so hydrophobic that a ClogP value is large, the fragrance | flavor composition comprised including many fragrance components with a small ClogP value is a fragrance | flavor composition comprised including many fragrance components with a large ClogP value. It can be said that the fragrance is more hydrophilic than the product.
When the ClogP value is within the above range, it is advantageous in that the fragrance composition has a good balance between the hydrophilicity and hydrophobicity of the fragrance component and has a better fragrance balance and higher palatability.
香料成分（ｂ１）としては、特に制限はなく、目的に応じて、公知の香料成分のなかから、所望の沸点およびＣｌｏｇＰ値を有するものを適宜選択して用いることができる。
公知の香料成分としては、例えば、繊維製品用仕上げ剤や柔軟剤に一般的に使用される香料成分や、人体に対する生理活性機能を持つ香料成分、蚊などの虫に対する忌避効果のある香料成分などが挙げられる。このような香料成分の具体例としては、例えば、アルデヒド類、フェノール類、アルコール類、エーテル類、エステル類、ハイドロカーボン類、ケトン類、ラクトン類、ムスク類、テルペン骨格を有する香料、天然香料、動物性香料などが挙げられる。
前記アルデヒド類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、ウンデシレンアルデヒド、ラウリルアルデヒド、アルデヒドＣ−１２ＭＮＡ、ミラックアルデヒド、α−アミルシンナミックアルデヒド、シクラメンアルデヒド、エチルバニリン、ヘリオトロピン、アニスアルデヒド、α−ヘキシルシンナミックアルデヒド、オクタナール、リグストラール、リリアール、リラール、トリプラール、バニリン、ヘリオナールなどが挙げられる。
前記フェノール類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、オイゲノール、イソオイゲノールなどが挙げられる。
前記アルコール類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、バクダノール、ジハイドロミルセノール、ジハイドロリナロール、リナロール、ネロール、サンダロール、サンタレックス、ターピネオール、テトラハイドロリナロール、フェニルエチルアルコールなどが挙げられる。
前記エーテル類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、セドランバー、グリサルバ、メチルオイゲノール、メチルイソオイゲノールなどが挙げられる。
前記エステル類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、シス−３−ヘキセニルアセテート、シス−３−ヘキセニルプロピオネート、シス−３−ヘキセニルサリシレート、ｐ−クレジルアセテート、ｐ−ｔ−ブチルシクロヘキシルアセテート、アミルアセテート、メチルジヒドロジャスモネート、アミルサリシレート、ベンジルサリシレート、ベンジルベンゾエート、ベンジルアセテート、セドリルアセテート、シトロネリルアセテート、デカハイドロ−β−ナフチルアセテート、ジメチルベンジルカルビニルアセテート、エリカプロピオネート、エチルアセトアセテート、エリカアセテート、ゲラニルアセテート、ゲラニルフォーメート、ヘディオン、リナリルアセテート、β−フェニルエチルアセテート、ヘキシルサリシレート、スチラリルアセテート、ターピニルアセテート、ベチベリルアセテート、ｏ−ｔ−ブチルシクロヘキシルアセテート、マンザネート、アリルヘプタノエートなどが挙げられる。
前記ハイドロカーボン類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、ミルセンなどが挙げられる。
前記ケトン類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、α−イオノン、β−イオノン、メチル−β−ナフチルケトン、α−ダマスコン、β−ダマスコン、δ−ダマスコン、シス−ジャスモン、メチルイオノン、アリルイオノン、カシュメラン、ジハイドロジャスモン、イソイースーパー、ベルトフィックス、イソロンジフォラノン、コアボン、ローズフェノン、ラズベリーケトン、ダイナスコンなどが挙げられる。
前記ラクトン類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、γ−デカラクトン、γ−ウンデカラクトン、γ−ノナラクトン、γ−ドデカラクトン、クマリン、アンブロキサンなどが挙げられる。
前記ムスク類としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、シクロペンタデカノライド、エチレンブラシレート、ガラキソライド、ムスクケトン、トナリッド、ニトロムスク類などが挙げられる。
前記テルペン骨格を有する香料としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、ゲラニオール（ゼラニオール）、ネロール、リナロール、シトラール、シトロネロール、メントール、ミント、シトロネラール、ミルセン、ピネン、リモネン、テレピネロール、カルボン、ヨノン、カンファー（樟脳）、ボルネオールなどが挙げられる。
前記天然香料としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、オレンジ油、レモン油、ライム油、プチグレン油、ユズ油、ネロリ油、ベルガモット油、ラベンダー油、ラバンジン油、アビエス油、アニス油、ベイ油、ボアドローズ油、イランイラン油、シトロネラ油、ゼラニウム油、ペパーミント油、ハッカ油、スペアミント油、ユーカリ油、レモングラス油、パチュリ油、ジャスミン油、ローズ油、シダー油、ベチバー油、ガルバナム油、オークモス油、パイン油、樟脳油、白檀油、芳樟油、テレピン油、クローブ油、クローブリーフ油、カシア油、ナツメッグ油、カナンガ油、タイム油などの精油が挙げられる。
前記動物性香料としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、じゃ香、霊猫香、海狸香、竜涎香などが挙げられる。
There is no restriction | limiting in particular as a fragrance | flavor component (b1), According to the objective, what has a desired boiling point and ClogP value can be suitably selected and used from well-known fragrance | flavor components.
Known fragrance ingredients include, for example, fragrance ingredients commonly used in textile finishing agents and softeners, fragrance ingredients with physiologically active functions for the human body, fragrance ingredients with repellent effects against insects such as mosquitoes, etc. Is mentioned. Specific examples of such a fragrance component include, for example, aldehydes, phenols, alcohols, ethers, esters, hydrocarbons, ketones, lactones, musks, fragrances having a terpene skeleton, natural fragrances, Examples include animal flavors.
There is no restriction | limiting in particular as said aldehydes, According to the objective, it can select suitably, For example, undecylenaldehyde, lauryl aldehyde, aldehyde C-12MNA, miracaldehyde, (alpha) -amyl cinnamamic aldehyde, cyclamen aldehyde, ethyl Examples include vanillin, heliotropin, anisaldehyde, α-hexylcinnamic aldehyde, octanal, ligustral, lyial, rilal, tripral, vanillin, helional and the like.
There is no restriction | limiting in particular as said phenols, According to the objective, it can select suitably, For example, eugenol, isoeugenol, etc. are mentioned.
The alcohol is not particularly limited and may be appropriately selected depending on the intended purpose.For example, bacdanol, dihydromyrcenol, dihydrolinalool, linalool, nerol, sandalol, santarex, terpineol, tetrahydro Examples include linalool and phenylethyl alcohol.
There is no restriction | limiting in particular as said ether, According to the objective, it can select suitably, For example, cedula bar, glycalva, methyl eugenol, methyl isoeugenol etc. are mentioned.
The esters are not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include cis-3-hexenyl acetate, cis-3-hexenyl propionate, cis-3-hexenyl salicylate, p-cresate. Dil acetate, pt-butyl cyclohexyl acetate, amyl acetate, methyl dihydrojasmonate, amyl salicylate, benzyl salicylate, benzyl benzoate, benzyl acetate, cedryl acetate, citronellyl acetate, decahydro-β-naphthyl acetate, dimethylbenzyl Carvinyl acetate, Ericapropionate, ethyl acetoacetate, Erica acetate, geranyl acetate, geranyl formate, hedion, linalyl acetate, β-phenylethyl acetate Hexyl salicylate, styryl acetate, terpinyl acetate, tiviberyl acetate, ot-butylcyclohexyl acetate, manzanate, allyl heptanoate, and the like.
There is no restriction | limiting in particular as said hydrocarbons, According to the objective, it can select suitably, For example, myrcene etc. are mentioned.
The ketones are not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include α-ionone, β-ionone, methyl-β-naphthyl ketone, α-damascon, β-damascon, and δ-damascon. Cis-jasmon, methylionone, allylionone, cashmerelan, dihydrojasmon, iso-Esuper, belt fix, isolone diforanone, coabon, rosephenone, raspberry ketone, dynascon and the like.
The lactone is not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include γ-decalactone, γ-undecalactone, γ-nonalactone, γ-dodecalactone, coumarin, and ambroxan. It is done.
There is no restriction | limiting in particular as said musk, According to the objective, it can select suitably, For example, a cyclopentadecanolide, ethylene brush rate, galaxolide, a musk ketone, a tonalid, nitromusk etc. are mentioned.
The fragrance having the terpene skeleton is not particularly limited and may be appropriately selected depending on the intended purpose.For example, geraniol (zelaniol), nerol, linalool, citral, citronellol, menthol, mint, citronellal, myrcene, pinene, Examples include limonene, terpineol, carvone, yonon, camphor, and borneol.
The natural perfume is not particularly limited and may be appropriately selected depending on the intended purpose. For example, orange oil, lemon oil, lime oil, petitgren oil, yuzu oil, neroli oil, bergamot oil, lavender oil, lavandin oil , Abies oil, anise oil, bay oil, bored rose oil, ylang ylang oil, citronella oil, geranium oil, peppermint oil, peppermint oil, spearmint oil, eucalyptus oil, lemongrass oil, patchouli oil, jasmine oil, rose oil, cedar oil , Essential oils such as vetiver oil, galvanum oil, oak moss oil, pine oil, camphor oil, sandalwood oil, mellow oil, turpentine oil, clove oil, clove leaf oil, cassia oil, nutmeg oil, cananga oil, thyme oil, etc. .
There is no restriction | limiting in particular as said animal fragrance | flavor, According to the objective, it can select suitably, For example, a scent, a ghost cat scent, a sea scent incense, a dragon scent etc. are mentioned.
（Ｂ）成分中に含まれる香料成分（ｂ１）は１種であっても２種以上であってもよい。
本発明においては、残香が特にフレッシュな香りになることから、（Ｂ）成分が、香料成分（ｂ１）として、シトロネロール、リモネン、ゲラニオール、メントール、シトロネラール、シトラール及びピネンからなる群から選ばれる少なくとも１種の特定香料成分を含有することが好ましい。この場合、（Ｂ）成分中の前記特定香料成分の含有量は、（Ｂ）成分の全量を基準として、１０質量％以上であることが好ましく、２０質量％以上がより好ましく、３０質量％以上がさらに好ましく、４０質量％以上が特に好ましい。
（Ｂ）成分中、香料成分（ｂ１）の含有量は、（Ｂ）成分の全量を基準として、３０質量％以上が好ましく、５０質量％以上がより好ましく、８０質量％以上がさらに好ましい。香料成分（ｂ１）の割合が多いほど、残香がさらにフレッシュな香りになる。
（Ｂ）成分は、本発明の効果を損なわない範囲で、香料成分（ｂ１）以外の香料成分（以下、香料成分（ｂ２）という。）を含有してもよい。香料成分（ｂ２）としては、特に限定されず、たとえば上述した公知の香料成分のなかから、香料成分（ｂ１）に該当しないものを適宜選択して用いることができる。
(B) The fragrance | flavor component (b1) contained in a component may be 1 type, or 2 or more types may be sufficient as it.
In the present invention, since the residual scent becomes a particularly fresh scent, the component (B) is at least one selected from the group consisting of citronellol, limonene, geraniol, menthol, citronellal, citral and pinene as the fragrance component (b1). It is preferable to contain a specific perfume component. In this case, the content of the specific fragrance component in the component (B) is preferably 10% by mass or more, more preferably 20% by mass or more, and more preferably 30% by mass or more based on the total amount of the component (B). Is more preferable, and 40% by mass or more is particularly preferable.
In the component (B), the content of the fragrance component (b1) is preferably 30% by mass or more, more preferably 50% by mass or more, and further preferably 80% by mass or more based on the total amount of the component (B). The greater the proportion of the fragrance component (b1), the more fresh the scent becomes.
The component (B) may contain a fragrance component other than the fragrance component (b1) (hereinafter referred to as the fragrance component (b2)) as long as the effects of the present invention are not impaired. The fragrance component (b2) is not particularly limited. For example, from the above-described known fragrance components, those not corresponding to the fragrance component (b1) can be appropriately selected and used.
（Ｂ）成分は、香料成分以外に、溶剤（香料用溶剤）を含有してもよい。
香料用溶剤としては、香料成分とともに通常用いる溶剤が利用でき、たとえばアセチン（トリアセチン）、ＭＭＢアセテート（３−メトキシ−３−メチルブチルアセテート）、スクロースジアセテートヘキサイソブチレート、エチレングリコールジブチレート、ヘキシレングリコール、ジブチルセバケート、デルチールエキストラ（イソプロピルミリステート）、メチルカルビトール（ジエチレングリコールモノメチルエーテル）、カルビトール（ジエチレングリコールモノエチルエーテル）、ＴＥＧ（トリエチレングリコール）、安息香酸ベンジル、プロピレングリコール、フタル酸ジエチル、トリプロピレングリコール、アボリン（ジメチルフタレート）、デルチルプライム（イソプロピルパルミテート）、ジプロピレングリコール、ファルネセン、ジオクチルアジペート、トリブチリン（グリセリルトリブタノエート）、ヒドロライト−５（１，２−ペンタンジオール）、プロピレングリコールジアセテート、セチルアセテート（ヘキサデシルアセテート）、エチルアビエテート、アバリン（メチルアビエテート）、シトロフレックスＡ−２（アセチルトリエチルシトレート）、シトロフレックスＡ−４（トリブチルアセチルシトレート）、シトロフレックスＮｏ．２（トリエチルシトレート）、シトロフレックスＮｏ．４（トリブチルシトレート）、ドゥラフィックス（メチルジヒドロアビエテート）、ＭＩＴＤ（イソトリデシルミリステート）、ポリリモネン（リモネンポリマー）、１，３−ブチレングリコール等が挙げられる。
（Ｂ）成分中、前記香料用溶剤の含有量は、（Ｂ）成分の全量を基準として、０〜３０質量％が好ましく、０．１〜３０質量％がより好ましく、１〜２０質量％がさらに好ましい。
（Ｂ）成分は、本発明の効果を妨げない限り、必要に応じて、酸化防止剤、防腐剤等の添加剤を通常の使用量の範囲内で配合することも可能である。
The component (B) may contain a solvent (perfume solvent) in addition to the perfume component.
As the fragrance solvent, commonly used solvents can be used together with the fragrance component. For example, acetin (triacetin), MMB acetate (3-methoxy-3-methylbutyl acetate), sucrose diacetate hexaisobutyrate, ethylene glycol dibutyrate, Xylene glycol, dibutyl sebacate, deltile extra (isopropyl myristate), methyl carbitol (diethylene glycol monomethyl ether), carbitol (diethylene glycol monoethyl ether), TEG (triethylene glycol), benzyl benzoate, propylene glycol, phthalic acid Diethyl, tripropylene glycol, aborin (dimethyl phthalate), deltyl prime (isopropyl palmitate), dipropylene glycol, vinyl Runesene, dioctyl adipate, tributyrin (glyceryl tributanoate), hydrolite-5 (1,2-pentanediol), propylene glycol diacetate, cetyl acetate (hexadecyl acetate), ethyl abiate, avaline (methyl abietate), Citroflex A-2 (acetyl triethyl citrate), Citroflex A-4 (tributyl acetyl citrate), Citroflex No. 2 (triethyl citrate), Citroflex No. 4 (tributyl citrate), Durafix (methyl dihydroabietate), MITD (isotridecyl myristate), polylimonene (limonene polymer), 1,3-butylene glycol and the like.
In the component (B), the content of the fragrance solvent is preferably 0 to 30% by mass, more preferably 0.1 to 30% by mass, and 1 to 20% by mass based on the total amount of the component (B). Further preferred.
As long as the component (B) does not interfere with the effects of the present invention, additives such as antioxidants and preservatives can be blended as necessary within the range of ordinary amounts used.
本発明の処理剤組成物中、（Ｂ）成分の含有量は、処理剤組成物の全量を基準として、０．０１〜５質量％であり、残香の香り強度を適度なものにし、フレッシュな香りを長続きさせる観点から、０．５〜２質量％が好ましい。
また、本発明の処理剤組成物中、（Ａ）成分および（Ｂ）成分の含有量の比率は、質量比で、（Ａ）成分：（Ｂ）成分＝１：３〜３：１の範囲であることが好ましく、１：２〜２：１の範囲であることがより好ましく、１：２〜１：１の範囲であることがさらに好ましい。該比率が上記範囲内であると、本発明の処理剤組成物を噴霧等により適用した繊維製品の香り強度を適度なものにし、トップノートを含むフレッシュな香りを長続きさせることができる。
In the treatment agent composition of the present invention, the content of the component (B) is 0.01 to 5% by mass based on the total amount of the treatment agent composition, and the fragrance strength of the remaining scent is moderate, and the freshness is fresh. From the viewpoint of long-lasting fragrance, 0.5 to 2% by mass is preferable.
In the treatment agent composition of the present invention, the content ratio of the component (A) and the component (B) is a mass ratio, and the range of (A) component: (B) component = 1: 3 to 3: 1. It is preferable that it is in the range of 1: 2 to 2: 1, more preferably in the range of 1: 2 to 1: 1. When the ratio is within the above range, the scent strength of the fiber product to which the treatment composition of the present invention is applied by spraying or the like can be made moderate, and the fresh scent including the top note can last for a long time.
＜（Ｃ）成分＞
（Ｃ）成分は水溶性溶剤である。（Ｃ）成分は、本発明の処理剤組成物の外観を透明または半透明なものとするために必要である。
ここで「水溶性溶剤」とは、水に任意の割合で溶解する溶剤のことを意味する。
（Ｃ）成分としては、エタノール、イソプロパノールなどの、炭素数２〜３の１価アルコール；エチレングリコール、プロピレングリコール、ジプロピレングリコールなどの、炭素数２〜６のグリコール；グリセリンなどの炭素数３〜８の３〜６価の多価アルコール；ジエチレングリコールモノブチルエーテルなどの、炭素数３〜８の多価アルコール誘導体；などが挙げられる。香気や価格の点からエタノール、グリセリン、ジエチレングリコールモノブチルエーテルが好ましい。
（Ｃ）成分としては、これらのいずれか１種を単独で用いてもよく、２種以上を併用してもよい。
本発明の処理剤組成物中、（Ｃ）成分の含有量は、処理剤組成物の全量を基準として、０．１〜５０質量％未満であり、５〜４５質量％が好ましく、２０〜４０質量％がより好ましい。この範囲内とすることで、処理剤組成物の外観を透明から半透明な状態にすることができる。
<(C) component>
Component (C) is a water-soluble solvent. The component (C) is necessary for making the appearance of the treatment agent composition of the present invention transparent or translucent.
Here, the “water-soluble solvent” means a solvent that dissolves in water at an arbitrary ratio.
(C) As a component, C2-C3 monohydric alcohols, such as ethanol and isopropanol; C2-C6 glycols, such as ethylene glycol, propylene glycol, and dipropylene glycol; C3-C3, such as glycerol 8-3 to 6-valent polyhydric alcohols; polyhydric alcohol derivatives having 3 to 8 carbon atoms such as diethylene glycol monobutyl ether; Ethanol, glycerin, and diethylene glycol monobutyl ether are preferable from the viewpoint of aroma and price.
As the component (C), any one of these may be used alone, or two or more may be used in combination.
In the treatment agent composition of the present invention, the content of the component (C) is less than 0.1 to 50% by mass, preferably 5 to 45% by mass, based on the total amount of the treatment agent composition, and 20 to 40%. The mass% is more preferable. By setting it within this range, the appearance of the treatment agent composition can be changed from transparent to translucent.
＜（Ｄ）成分＞
（Ｄ）成分は、ＨＬＢが１０〜１４で、ポリオキシエチレン硬化ヒマシ油、ポリオキシエチレンアルキルエーテルおよびポリオキシエチレンアルケニルエーテルから選ばれる少なくとも１種の非イオン性界面活性剤である。（Ｄ）成分を配合することにより、処理剤組成物の外観を透明または半透明にすることができる。
「ＨＬＢ」とは、界面活性剤の分子がもつ親水性と親油性の相対的な強さのことであり、その親水親油バランスを数量的に表したものをいう。ＨＬＢが１０〜１４の範囲を外れると、液外観を充分に透明または半透明とすることが難しい。（Ｄ）成分のＨＬＢは、１１〜１３が好ましい。
ポリオキシエチレン硬化ヒマシ油、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルケニルエーテルは、それぞれ、硬化ヒマシ油、アルキルアルコール、アルケニルアルコールにエチレンオキシドが付加したものである。
ポリオキシエチレン硬化ヒマシ油におけるオキシエチレン基の平均付加モル数は２０〜６０モルが好ましく、２０〜５０モルがより好ましく、３０〜４０モルが特に好ましい。
ポリオキシエチレンアルキルエーテルにおけるアルキル基、ポリオキシエチレンアルケニルエーテルにおけるアルケニル基の炭素数は、それぞれ、１０〜２２が好ましく、１２〜１８がより好ましい。
ポリオキシエチレンアルキルエーテルおよびポリオキシエチレンアルケニルエーテルにおけるオキシエチレン基の平均付加モル数は、それぞれ、３〜２０モルが好ましく、３〜１０モルがより好ましい。
（Ｄ）成分としては、オキシエチレン基の平均付加モル数が３０〜４０モルであるポリオキシエチレン硬化ヒマシ油が最も好ましい。
（Ｄ）成分としては、これらのいずれか１種を単独で用いてもよく、２種以上を併用してもよい。
本発明の処理剤組成物中、（Ｄ）成分の含有量は、処理剤組成物の全量を基準として、０．０１〜５質量％未満であり、０．１〜２質量％が好ましく、０．５〜１質量％がより好ましい。この範囲内とすることで、処理剤組成物の外観を透明から半透明な状態にすることができ、処理剤組成物を繊維製品に噴霧したあとシミなどができにくい。
<(D) component>
The component (D) is an HLB of 10 to 14, and is at least one nonionic surfactant selected from polyoxyethylene hydrogenated castor oil, polyoxyethylene alkyl ether and polyoxyethylene alkenyl ether. (D) By mix | blending component, the external appearance of a processing agent composition can be made transparent or translucent.
“HLB” refers to the relative strength between hydrophilicity and lipophilicity of a surfactant molecule, and represents the hydrophilic / lipophilic balance quantitatively. If the HLB is outside the range of 10 to 14, it is difficult to make the liquid appearance sufficiently transparent or translucent. (D) As for HLB of a component, 11-13 are preferable.
Polyoxyethylene hydrogenated castor oil, polyoxyethylene alkyl ether, and polyoxyethylene alkenyl ether are obtained by adding ethylene oxide to hydrogenated castor oil, alkyl alcohol, and alkenyl alcohol, respectively.
20-60 mol is preferable, as for the average addition mole number of the oxyethylene group in polyoxyethylene hydrogenated castor oil, 20-50 mol is more preferable, and 30-40 mol is especially preferable.
As for carbon number of the alkyl group in polyoxyethylene alkyl ether and the alkenyl group in polyoxyethylene alkenyl ether, 10-22 are respectively preferable, and 12-18 are more preferable.
The average number of moles of oxyethylene groups added in the polyoxyethylene alkyl ether and polyoxyethylene alkenyl ether is preferably 3 to 20 moles and more preferably 3 to 10 moles.
(D) As a component, the polyoxyethylene hydrogenated castor oil whose average addition mole number of an oxyethylene group is 30-40 mol is the most preferable.
As the component (D), any one of these may be used alone, or two or more may be used in combination.
In the treating agent composition of the present invention, the content of the component (D) is 0.01 to less than 5% by mass, preferably 0.1 to 2% by mass, based on the total amount of the treating agent composition. More preferable is 5 to 1% by mass. By setting it within this range, the appearance of the treatment agent composition can be changed from a transparent state to a semitransparent state, and it is difficult to cause a stain or the like after the treatment agent composition is sprayed on the fiber product.
＜（Ｅ）成分＞
（Ｅ）成分は、下記一般式（１）または（２）で表される化合物から選ばれる少なくとも１種のシリコーン化合物である。（Ｅ）成分は、処理剤組成物の繊維製品への浸透力を向上させ、残香の強度を高める効果を与える。
<(E) component>
The component (E) is at least one silicone compound selected from the compounds represented by the following general formula (1) or (2). The component (E) gives the effect of improving the penetrating power of the treatment composition into the fiber product and increasing the strength of the remaining scent.
式（１）中、Ｒとしては、炭素数１〜３のアルキル基が好ましく、メチル基またはエチル基がより好ましい。
Ｒ２としては、水素原子または炭素数１〜３のアルキル基が好ましく、水素原子またはメチル基がより好ましい。
ｘとしては、２または３が好ましく、３がより好ましい。
ｙとしては、７〜１５の整数が好ましく、７〜１２の整数がより好ましい。
Ｒ３としては、炭素数１〜３のアルキル基が好ましく、メチル基またはエチル基がより好ましい。
Ｒ５としては、水素原子または炭素数１〜３のアルキル基が好ましく、水素原子またはメチル基がより好ましい。
ｐとしては、２または３が好ましく、３がより好ましい。
ｑとしては、７〜１５の整数が好ましく、７〜１２の整数がより好ましい。
ｍとしては、２〜５の整数が好ましく、２〜４の整数がより好ましい。
In formula (1), as R, a C1-C3 alkyl group is preferable and a methyl group or an ethyl group is more preferable.
R 2 is preferably a hydrogen atom or an alkyl group having 1 to 3 carbon atoms, more preferably a hydrogen atom or a methyl group.
As x, 2 or 3 is preferable, and 3 is more preferable.
As y, an integer of 7 to 15 is preferable, and an integer of 7 to 12 is more preferable.
R 3 is preferably an alkyl group having 1 to 3 carbon atoms, and more preferably a methyl group or an ethyl group.
R 5 is preferably a hydrogen atom or an alkyl group having 1 to 3 carbon atoms, more preferably a hydrogen atom or a methyl group.
As p, 2 or 3 is preferable, and 3 is more preferable.
As q, the integer of 7-15 is preferable and the integer of 7-12 is more preferable.
As m, the integer of 2-5 is preferable and the integer of 2-4 is more preferable.
（Ｅ）成分としては、上記の中でも、一般式（１）で表される化合物が、繊維製品に処理剤組成物を繊維の奥まで浸透させて残香強度を高めることができる点からより好ましい。
（Ｅ）成分は、例えばオルガノハイドロジェンポリシロキサンとポリオキシアルキレンアリルエーテルとを付加させる等の公知の方法で製造することができる。また、市場で入手可能な物として、ＳＩＬＷＥＴ Ｌ−７７（モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製）等が挙げられる。
（Ｅ）成分としては、これらのいずれか１種を単独で用いてもよく、２種以上を併用してもよい。
本発明の処理剤組成物中、（Ｅ）成分の含有量は、処理剤組成物の全量を基準として、０．０１質量％以上が好ましく、０．０５質量％以上がより好ましく、０．１質量％以上がさらに好ましい。０．０１質量％以上にすることにより、（Ｅ）成分を配合することによる効果が充分に発揮される。また、本発明の処理剤組成物中、（Ｅ）成分の含有量は、処理剤組成物の全量を基準として、５質量％以下が好ましく、２質量％以下がより好ましく、１質量％以下がさらに好ましい。（Ｅ）成分の配合量を５質量％以下とすることにより、処理剤組成物を散布した繊維製品にしみが発生することを防ぐことができる。
Among these, as the component (E), the compound represented by the general formula (1) is more preferable from the viewpoint that the treating agent composition can penetrate into the fiber product to the back of the fiber to increase the residual scent strength.
The component (E) can be produced by a known method such as addition of organohydrogenpolysiloxane and polyoxyalkylene allyl ether. Moreover, SILWET L-77 (made by Momentive Performance Materials Japan GK) etc. is mentioned as a thing which can be obtained in a market.
As the component (E), any one of these may be used alone, or two or more may be used in combination.
In the treating agent composition of the present invention, the content of the component (E) is preferably 0.01% by mass or more, more preferably 0.05% by mass or more, based on the total amount of the treating agent composition, 0.1% The mass% or more is more preferable. By making it 0.01% by mass or more, the effect of blending the component (E) is sufficiently exhibited. Further, in the treatment agent composition of the present invention, the content of the component (E) is preferably 5% by mass or less, more preferably 2% by mass or less, and more preferably 1% by mass or less, based on the total amount of the treatment agent composition. Further preferred. (E) By making the compounding quantity of a component into 5 mass% or less, it can prevent that the blotch generate | occur | produces in the textiles which spread the processing agent composition.
本発明の処理剤組成物は、本発明の効果を損なわない範囲で、上記（Ａ）〜（Ｅ）成分以外の他の成分を含有してもよい。該他の成分としては、たとえばｐＨ調整剤、酸化防止剤、キレート剤、防腐剤、抗菌剤、平均粒子径が５００ｎｍ以下のシリカ微粒子等が挙げられる。なお、「平均粒子径」は、一般的な粒度分布測定装置（例えば、濃厚系粒径アナライザー ＦＰＡＲ-１０００ 大塚電子（株）社製）を用いて測定できる。
本発明の処理剤組成物は、通常、（Ａ）〜（Ｅ）成分、および上記任意の他の成分を除く残部は水である。本発明の処理剤組成物中、水の含有量は、処理剤組成物の全量を基準として、８０質量％以下が好ましく、６０質量％以下がより好ましい。
本発明の処理剤組成物の調製方法は特に限定されず、常法に従って調製できる。たとえば上記各成分を、必要に応じて水とともに混合することにより調製できる。より透明性を高めるために、（Ａ）成分の水溶液と、（Ｂ）〜（Ｅ）成分の水溶液を別々に調製し、最後に両者を混合する方法が好ましい。
The treatment agent composition of the present invention may contain components other than the components (A) to (E) as long as the effects of the present invention are not impaired. Examples of the other components include pH adjusters, antioxidants, chelating agents, preservatives, antibacterial agents, and silica fine particles having an average particle size of 500 nm or less. The “average particle size” can be measured using a general particle size distribution measuring device (for example, a concentrated particle size analyzer FPAR-1000 manufactured by Otsuka Electronics Co., Ltd.).
In the treatment agent composition of the present invention, the balance except for the components (A) to (E) and any other components described above is usually water. In the treatment agent composition of the present invention, the water content is preferably 80% by mass or less, and more preferably 60% by mass or less, based on the total amount of the treatment agent composition.
The preparation method of the processing agent composition of this invention is not specifically limited, It can prepare according to a conventional method. For example, it can prepare by mixing each said component with water as needed. In order to further increase the transparency, a method in which the aqueous solution of the component (A) and the aqueous solutions of the components (B) to (E) are separately prepared and finally both are mixed is preferable.
本発明の処理剤組成物は、香気の安定性を高める観点から、２５℃におけるｐＨが５〜１１であることが好ましく、７〜１０であることがより好ましい。該ｐＨは、塩酸や水酸化ナトリウムなどのｐＨ調整剤により調節できる。
本発明の処理剤組成物は、ハンドリング性の点から、２５℃における粘度が１０ｍＰａ・ｓ以下であることが好ましい。特にスプレー容器に収容して使用する場合には、該粘度が５ｍＰａ・ｓ以下であることが好ましい。該粘度は、（Ｃ）成分や水の配合量、（Ａ）成分の種類・配合量等により調節できる。
From the viewpoint of enhancing the stability of the fragrance, the treating agent composition of the present invention preferably has a pH at 25 ° C. of 5 to 11, more preferably 7 to 10. The pH can be adjusted with a pH adjusting agent such as hydrochloric acid or sodium hydroxide.
The treating agent composition of the present invention preferably has a viscosity at 25 ° C. of 10 mPa · s or less from the viewpoint of handling properties. In particular, when used in a spray container, the viscosity is preferably 5 mPa · s or less. The viscosity can be adjusted by the amount of component (C) and water, the type and amount of component (A), and the like.
以上説明した本発明の処理剤組成物によれば、繊維製品に望ましい残香を付与できる。たとえば多様な香料成分を配合可能であることから付与する香調が限定されない。また、付与した香りの強度やフレッシュさにも優れており、該香りの持続性にも優れる。
また、本発明の処理剤組成物は、透明性にも優れており、透明または半透明の外観を有する。そのため、特にトリガー式スプレー容器に収容して繊維製品に噴霧する際、透明容器にも収納することができ商品展開の幅が広がるとともに、内容物が沈殿する、或いはスプレーノズルに詰まる等の問題を生じにくい。そのため、本発明の処理剤組成物は、トリガー式スプレー容器用の内容液として好適である。
さらに、本発明の処理剤組成物は、当該処理剤組成物中に含まれる（Ａ）成分の分散安定性等も良好であり、透明または半透明の外観を長期にわたって安定に維持できる。
上記効果が得られる理由は、定かではないが、（Ａ）成分が合成品であるため、粒子径が小さく且つ粒度分布の幅が狭い、夾雑物が少ない等により（Ｃ）成分、または（Ｃ）成分と水との混合物中に均一に分散するとともに、（Ａ）成分の層間に（Ｂ）成分中の香料成分が効率よく保持されること等が考えられる。さらに、（Ｄ）成分を加えることにより、（Ｂ）成分を担持した（Ａ）成分が凝集することが防止され、透明度を高めることができると考えられる。
According to the treatment agent composition of the present invention described above, a desired residual aroma can be imparted to a textile product. For example, the fragrance to be imparted is not limited because various fragrance ingredients can be blended. Moreover, it is excellent in the intensity | strength and freshness of the provided fragrance, and is excellent also in the sustainability of this fragrance.
Moreover, the processing agent composition of this invention is excellent also in transparency, and has a transparent or translucent external appearance. For this reason, in particular, when it is housed in a trigger type spray container and sprayed onto a textile product, it can also be housed in a transparent container, which expands the range of product development and causes problems such as sedimentation of contents or clogging of the spray nozzle. Hard to occur. Therefore, the treatment agent composition of the present invention is suitable as a content liquid for a trigger spray container.
Furthermore, the treatment agent composition of the present invention has good dispersion stability of the component (A) contained in the treatment agent composition, and can maintain a transparent or translucent appearance stably over a long period of time.
The reason why the above effect is obtained is not clear, but since the component (A) is a synthetic product, the component (C), or (C It is conceivable that the fragrance component in the component (B) is efficiently retained between the layers of the component (A), while being uniformly dispersed in the mixture of the component) and water. Furthermore, by adding the component (D), it is considered that the component (A) carrying the component (B) is prevented from agglomerating and the transparency can be increased.
本発明の処理剤組成物による繊維製品の処理は、たとえば該処理剤組成物を、トリガー式スプレー容器に収容し、繊維製品に直接噴霧することにより実施できる。噴霧後、必要に応じて乾燥処理を行ってもよい。
繊維製品としては、特に制限されるものではなく、たとえば衣類、カーテン、ソファー、カーペット、タオル、ハンカチ、シーツ、マクラカバー等が挙げられる。
繊維製品に対する処理剤組成物の塗布量は、繊維製品１００ｇあたり、０．５〜１０ｇが好ましく、１〜５ｇがより好ましい。
The treatment of the fiber product with the treatment agent composition of the present invention can be carried out, for example, by storing the treatment agent composition in a trigger spray container and spraying the fiber product directly. After spraying, you may perform a drying process as needed.
The fiber product is not particularly limited, and examples thereof include clothing, curtains, sofas, carpets, towels, handkerchiefs, sheets, and macula covers.
The amount of the treatment composition applied to the fiber product is preferably 0.5 to 10 g, more preferably 1 to 5 g, per 100 g of the fiber product.
≪繊維製品処理剤製品≫
本発明の繊維製品処理剤製品は、前記本発明の処理剤組成物を、トリガー式スプレー容器（以下、トリガー容器という。）に収容したものである。
トリガー容器としては、特に限定されず、一般に、衣類等の繊維製品に対して香りや消臭効果などの付与等を行うために用いられている繊維製品処理剤製品に用いられているトリガー容器と同様のものを使用できる。
本発明に使用するトリガー容器としては、噴霧性状、スプレーパターンが良好であること、アフタードローが発生しないとの観点から、蓄圧式のトリガー容器が好ましい。
また、１回の噴霧量は、処理剤組成物を散布した繊維製品にしみが発生することを防ぐ観点、また、手に過度の疲労感を与えずに好ましい香りを付与するとの観点から、０．２〜０．６ｇであることが好ましい。
≪Fiber product treatment product≫
The textile product treating agent product of the present invention is one in which the treating agent composition of the present invention is accommodated in a trigger spray container (hereinafter referred to as a trigger container).
The trigger container is not particularly limited, and is generally a trigger container used for a textile product treating agent product used for imparting a fragrance or a deodorizing effect to a textile product such as clothing. Similar ones can be used.
As the trigger container used in the present invention, an accumulator type trigger container is preferable from the viewpoints of good spray properties and spray pattern and no occurrence of afterdraw.
In addition, the amount of spraying once is 0 from the viewpoint of preventing a stain from being generated on the textile product sprayed with the treatment agent composition, and from the viewpoint of imparting a preferable scent without giving excessive fatigue to the hand. It is preferable that it is 2-0.6g.
本発明について、実施例を示してさらに具体的に説明する。ただし本発明はこれらに限定されるものではない。
以下の各実施例および比較例にて使用した原料および評価方法を以下に示す。
The present invention will be described more specifically with reference to examples. However, the present invention is not limited to these.
The raw materials and evaluation methods used in the following examples and comparative examples are shown below.
＜使用原料＞
［（Ａ）成分］
Ａ−１：合成ヘクトライト（ロックウッド（株）製「Ｌａｐｏｎａｉｔｅ ＸＧＤ」）。
Ａ−２：合成ヘクトライト（ロックウッド（株）製「Ｌａｐｎａｉｔｅ ＲＤ」）。
Ａ―３：天然ベントナイト（クニミネ工業（株）製「クニピアＦ」）。
Ａ―４：有機変性ベントナイト（（株）ホージュン製「エスベンＮ−４００」）。
<Raw materials>
[(A) component]
A-1: Synthetic hectorite ("Laponite XGD" manufactured by Rockwood Corporation).
A-2: Synthetic hectorite ("Lapnaite RD" manufactured by Rockwood Co., Ltd.).
A-3: Natural bentonite ("Kunipia F" manufactured by Kunimine Industry Co., Ltd.).
A-4: Organic modified bentonite (“Esben N-400” manufactured by Hojun Co., Ltd.).
［（Ｂ）成分］
Ｂ−１：表４に示す組成の香料組成物（ｂ−１）［特定香料成分含有量２１％］。
Ｂ−２：表５に示す組成の香料組成物（ｂ−２）［特定香料成分含有量４１．５％］。
Ｂ−３：表６に示す組成の香料組成物（ｂ−３）［特定香料成分含有量７９．５％］。
Ｂ−４：表７に示す組成の香料組成物（ｂ−４）［特定香料成分含有量５％］。
[Component (B)]
B-1: Fragrance composition (b-1) having a composition shown in Table 4 [specific fragrance component content 21%].
B-2: Fragrance composition (b-2) having a composition shown in Table 5 [specific fragrance component content: 41.5%].
B-3: Fragrance composition (b-3) having a composition shown in Table 6 [specific fragrance component content: 79.5%].
B-4: Fragrance composition (b-4) having a composition shown in Table 7 [specific fragrance component content 5%].
［（Ｃ）成分］
Ｃ−１：エタノール（日本合成アルコール（株）社製）。
Ｃ−２：ジエチレングリコールモノブチルエーテル（日本乳化剤社製）。
[Component (C)]
C-1: Ethanol (made by Nippon Synthetic Alcohol Co., Ltd.).
C-2: Diethylene glycol monobutyl ether (manufactured by Nippon Emulsifier Co., Ltd.).
［（Ｄ）成分］
Ｄ−１：ポリオキシエチレン硬化ヒマシ油（日本エマルジョン（株）「ＥＭＡＬＥＸ ＨＣ３０」、オキシエチレン基の平均付加モル数３０、ＨＬＢ＝１１）。
Ｄ−２：ポリオキシエチレンアルキルエーテル（日光ケミカルズ（株）製「ＮＩＫＫＯＬ ＢＬ−４．２」、ラウリルアルコール（１−ドデカノール）のエチレンオキシド付加物、オキシエチレン基の平均付加モル数４、ＨＬＢ＝１１．５）。
Ｄ−３：ポリオキシエチレン硬化ヒマシ油（日光ケミカルズ（株）製「ＮＩＫＫＯＬ ＨＣＯ−１００」、オキシエチレン基の平均付加モル数１００、ＨＬＢ＝１６．５）。
[(D) component]
D-1: Polyoxyethylene hydrogenated castor oil (Nippon Emulsion Co., Ltd. “EMALEX HC30”, average addition mole number of oxyethylene group 30, HLB = 11).
D-2: Polyoxyethylene alkyl ether ("NIKKOL BL-4.2" manufactured by Nikko Chemicals Co., Ltd.), ethylene oxide adduct of lauryl alcohol (1-dodecanol), average addition mole number of oxyethylene group: 4, HLB = 11 .5).
D-3: Polyoxyethylene hydrogenated castor oil (“NIKKOL HCO-100” manufactured by Nikko Chemicals Co., Ltd., average added mole number of oxyethylene group: 100, HLB = 16.5).
［（Ｅ）成分］
Ｅ−１：前記一般式（１）中、Ｒが全てメチル基であり、Ｒ１が−Ｃ３Ｈ６Ｏ（Ｃ２Ｈ４Ｏ）１１−Ｈである化合物。
Ｅ−２：前記一般式（２）中、Ｒ３が全てメチル基であり、Ｒ４が−Ｃ３Ｈ６Ｏ（Ｃ２Ｈ４Ｏ）１１−ＣＨ３であり、ｍが３である化合物。
[(E) component]
E-1: A compound in which, in the general formula (1), R is all methyl groups and R 1 is —C 3 H 6 O (C 2 H 4 O) 11 —H.
E-2: Compound in which R 3 is all a methyl group, R 4 is —C 3 H 6 O (C 2 H 4 O) 11 —CH 3 , and m is 3 in the general formula (2). .
＜評価方法＞
［外観（透明度）の評価］
処理剤組成物の吸光度を下記測定条件にて測定した。
吸光度計：ＨＩＴＡＣＨＩ Ｓｐｅｃｔｒｏｐｈｏｔｏｍｅｔｅｒ Ｕ−３０１０）。
測定波長：６６０ｎｍ。
セル：１ｃｍ×１ｃｍの石英セル。
対照としてイオン交換水を用い、サンプル側のセルにイオン交換水を入れて０補正を行った。
<Evaluation method>
[Evaluation of appearance (transparency)]
The absorbance of the treatment agent composition was measured under the following measurement conditions.
Absorbance meter: HITACHI Spectrophotometer U-3010).
Measurement wavelength: 660 nm.
Cell: A quartz cell of 1 cm × 1 cm.
Ion exchanged water was used as a control, and ion exchanged water was added to the cell on the sample side to perform zero correction.
上記吸光度の測定結果から、下記判定基準で各処理剤組成物の外観（透明度）を評価した。該評価結果のうち、○または◎を合格とした。
（外観の判定基準）
×：吸光度が２．０以上。
△：吸光度が１．５以上２．０未満。
○：吸光度が１．０以上〜１．５未満。
◎：吸光度が１．０未満。
From the absorbance measurement results, the appearance (transparency) of each treatment composition was evaluated according to the following criteria. Among the evaluation results, “◯” or “◎” was regarded as acceptable.
(Appearance criteria)
X: Absorbance is 2.0 or more.
Δ: Absorbance is 1.5 or more and less than 2.0.
○: Absorbance is 1.0 or more and less than 1.5.
A: Absorbance is less than 1.0.
［残香強度の評価］
トリガー容器として、市販の衣類手入れ剤（商品名「スタイルガード しわもニオイもスッキリスプレー」、ライオン（株）製）の容器の中身を取り出し、よく洗浄し、しっかりと水分を乾かしたものを用意した。
評価布として、市販の肌シャツ（綿１００％）を、洗濯することなくそのまま用いた。
処理剤組成物をトリガー容器に充填し、評価布に対し、２％ｏ．ｗ．ｆ（＝処理剤組成物の重量（ｇ）／評価布の重量（ｇ）×１００）の量を均一になるよう噴霧した。その後、評価布を室温で一晩乾燥させた。
噴霧してから一日後の評価布に残っている香りの強度を、比較例１の処理剤組成物を用いて処理した評価布に残っている香りの強度を基準として、２０〜３０代の女性１０人に、下記の判定基準に従って評価してもらい、１０人の平均値を算出した。
（残香強度の判定基準）
３点：比較例１に比べ、非常に香りが残っている。
２点：比較例１に比べ、かなり香りが残っている。
１点：比較例１に比べ、やや香りが残っている。
０点：比較例１と同程度、またはそれ以下しか香りが残っていない。
[Evaluation of residual scent intensity]
As a trigger container, the contents of a commercially available clothing care product (trade name “Style Guard wrinkles and odors are refreshing spray”, manufactured by Lion Co., Ltd.) were taken out, washed thoroughly, and dried thoroughly. .
As an evaluation cloth, a commercially available skin shirt (100% cotton) was used as it was without washing.
A treatment agent composition is filled in a trigger container, and 2% o. w. The amount of f (= treatment agent composition weight (g) / evaluation fabric weight (g) × 100) was sprayed to be uniform. Thereafter, the evaluation fabric was dried overnight at room temperature.
Women in their 20s and 30s based on the intensity of the scent remaining in the evaluation cloth treated with the treatment composition of Comparative Example 1 for the intensity of the scent remaining in the evaluation cloth one day after spraying Ten people were evaluated according to the following criteria, and the average value of the ten people was calculated.
(Criteria for residual scent intensity)
3 points: Compared to Comparative Example 1, the scent remains very much.
2 points: Compared to Comparative Example 1, a considerable scent remains.
1 point: Compared to Comparative Example 1, a little scent remains.
0 point: The scent remains only as low as or lower than that of Comparative Example 1.
［残香フレッシュ感の評価］
前記［残香強度の評価］と同様に処理した評価布について、噴霧してから一日後の評価布に残っている香りのフレッシュ感を、比較例１の処理剤組成物を用いて処理した評価布に残っている香りのフレッシュ感を基準として、２０〜３０代の女性１０人に、下記の判定基準に従って評価してもらい、１０人の平均値を算出した。
（残香フレッシュ感の判定基準）
３点：比較例１に比べ、非常にフレッシュな香りである。
２点：比較例１に比べ、かなりフレッシュな香りである。
１点：比較例１に比べ、ややフレッシュな香りである。
０点：比較例１と同程度、またはそれ以下のフレッシュさである。
[Evaluation of fresh feeling of remaining scent]
Evaluation cloth treated with the treatment composition of Comparative Example 1 for the evaluation cloth treated in the same manner as in the above [Evaluation of residual scent strength], with the fresh feeling of the fragrance remaining on the evaluation cloth one day after spraying. On the basis of the fresh scent of the scent remaining, 10 women in their 20s and 30s were evaluated according to the following criteria, and the average value of 10 people was calculated.
(Judgment criteria for fresh scent)
3 points: Compared to Comparative Example 1, the scent is very fresh.
2 points: Compared to Comparative Example 1, the scent is considerably fresher.
1 point: Slightly fresh scent compared to Comparative Example 1.
0 point: Freshness comparable to or less than that of Comparative Example 1.
＜実施例１〜１３、比較例１〜６＞
表１〜３に示す配合量で各成分を混合して処理剤組成物を調製した。
表１〜３中、各成分の配合量の単位は「質量％」であり、イオン交換水の「バランス」は、処理剤組成物の全量が１００質量％となる量である。
得られた各処理剤組成物について、上記手順で外観、残香強度および残香フレッシュ感を評価した。その結果を表１〜３に併記する。
これらの結果に示すとおり、実施例１〜１３は、外観の透明性が高かった。また、残香強度および残香フレッシュ感のいずれも２．２以上であり、対照である比較例１に比べて残香性が優れていた。残香強度は、特定香料成分の含有量が２１％以上になっているＢ−１〜Ｂ−３を用いた例で特に高く、なかでもＢ−２またはＢ−３を配合した実施例２〜３、５〜８、１２〜１３では、残香フレッシュ感も優れていた。また、（Ｅ）成分の配合の有無以外は同じ組成の実施例９〜１０と実施例４、実施例１１と実施例１、実施例１２と実施例２、実施例１３と実施例３をそれぞれ対比すると、（Ｅ）成分を配合した実施例９〜１０、１１〜１３の方が、残香強度が高かった。
一方、（Ａ）成分を配合していない比較例１〜２は、外観は良好であるものの残香性が悪く、非合成品のベントナイトであるＡ−３またはＡ−４を用いた比較例３〜４は、対照である比較例１に比べて良好な残香性を有していたが、外観が悪かった。（Ｃ）成分を６０質量％配合した比較例５は、外観が悪く、残香フレッシュ感も、実施例１〜１３に比べて低めだった。ＨＬＢが１６．５のＤ−３を配合した比較例６は、外観が不良だった。
<Examples 1-13, Comparative Examples 1-6>
Each component was mixed by the compounding quantity shown to Tables 1-3, and the processing agent composition was prepared.
In Tables 1 to 3, the unit of the amount of each component is “mass%”, and the “balance” of ion-exchanged water is such that the total amount of the treatment agent composition is 100 mass%.
About each obtained processing agent composition, the external appearance, the residual scent intensity | strength, and the residual scent fresh feeling were evaluated in the said procedure. The results are also shown in Tables 1-3.
As shown in these results, Examples 1 to 13 had high appearance transparency. Moreover, both the residual scent intensity and the residual scent fresh feeling were 2.2 or more, and the residual fragrance was superior to Comparative Example 1 as a control. The residual scent strength is particularly high in the examples using B-1 to B-3 in which the content of the specific fragrance component is 21% or more, and in particular, Examples 2-3 in which B-2 or B-3 is blended , 5-8, 12-13, the residual scent freshness was also excellent. Moreover, Example 9-10 and Example 4, Example 11 and Example 1, Example 12 and Example 2, Example 13 and Example 3 of the same composition except the presence or absence of the mixing | blending of (E) component, respectively. In contrast, the residual scent intensity was higher in Examples 9 to 10, 11 to 13 in which the component (E) was blended.
On the other hand, Comparative Examples 1-2 in which the component (A) was not blended had a good appearance but poor residual fragrance, and Comparative Examples 3 to 3 using A-3 or A-4, which is a non-synthetic bentonite. No. 4 had better residual fragrance as compared with Comparative Example 1 as a control, but the appearance was poor. The comparative example 5 which mix | blended (C) component 60 mass% had a bad external appearance, and the residual scent fresh feeling was also low compared with Examples 1-13. The comparative example 6 which mix | blended D-3 whose HLB is 16.5 had a bad external appearance.
Claims (8)