JP5298635B2 - Electrophotographic photoreceptor, image forming method, image forming apparatus, and process cartridge - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an electrophotographic photoreceptor having a surface layer containing at least a binder resin and a filler and an intermediate layer comprising an amorphous oxide semiconductor, having excellent wear durability, capable of suppressing charges injected from a support into a photosensitive layer without causing an increase in a potential in an exposed portion, as well as having extremely little decrease in electrophotographic characteristics such as decrease in chargeability even when used for a long period of time, and capable of continuously giving high-quality images with little defects; and to provide an image forming method, an image forming apparatus and a process cartridge using the electrophotographic photoreceptor. <P>SOLUTION: The electrophotographic photoreceptor has a support, and at least an intermediate layer, a photosensitive layer and a surface layer formed in this order on the support, wherein: the surface layer contains at least a binder resin and a filler; and the intermediate layer contains an amorphous oxide semiconductor. <P>COPYRIGHT: (C)2010,JPO&amp;INPIT

Description

  The present invention uses an electrophotographic photoreceptor capable of suppressing a decrease in chargeability, background contamination, and poor charging without causing an increase in potential of an exposed portion even after long-term use, and the electrophotographic photoreceptor. The present invention relates to an electrophotographic image forming apparatus, an image forming method, and a process cartridge, such as a copying machine, a printer, a facsimile, or a complex machine thereof.

In recent years, from the viewpoints of saving office space, expanding business opportunities, etc., electrophotographic image forming apparatuses are desired to be faster, smaller, more colored, and higher in image quality and easier to maintain. ing. These are regarded as problems to be solved by developing an electrophotographic photosensitive member because they are related to improvement in characteristics and durability of the electrophotographic photosensitive member. From the viewpoint of improving ease of maintenance, there is a reduction in the replacement frequency of the electrophotographic photosensitive member. This is to reduce the main image defects derived from the electrophotographic photosensitive member as much as possible over a long period of time, which is nothing but the extension of the life of the electrophotographic photosensitive member. In addition, in recent years, there have been many reports on development relating to extending the life of electrophotographic photosensitive members because they are related to the improvement of the image quality of output images over a long period of time.
In order to achieve a long life of the electrophotographic photosensitive member, it is an important issue to improve durability against various hazards that the electrophotographic photosensitive member receives from the image forming process. The hazards mentioned here can be broadly divided into two types: mechanical hazards and electrical hazards.

  An example of a mechanical hazard is one derived from blade cleaning, which is one of means for removing toner remaining on the electrophotographic photosensitive member after transfer of the image forming process (so-called toner cleaning process). Blade cleaning is a means for forcibly removing toner from the electrophotographic photosensitive member by contacting an elastic member (so-called cleaning blade) on the photosensitive member, and has a large toner removing ability in a small space. This is very effective for miniaturization of an electrophotographic apparatus. However, on the other hand, since the elastic member is brought into direct contact with the electrophotographic photosensitive member and rubbed, the mechanical stress on the electrophotographic photosensitive member is very large, and the layer disposed on the outermost surface of the photosensitive member is worn away. The demerit that it is easy is pointed out. For this reason, in an electrophotographic apparatus to which this cleaning method is applied, wear of the electrophotographic photosensitive member is often a problem for extending the life, and a technique for laminating a high-hardness protective layer is proposed for this problem. (See Patent Documents 1 to 5).

Next, the electrostatic hazard will be described. In a normal image forming process, an electric charge is applied to the surface of the electrophotographic photosensitive member, and after charging to a predetermined potential, the electric charge applied to the surface via the photosensitive member is removed by exposure to the electrophotographic photosensitive member. At this time, electrostatic stress is applied to the electrophotographic photosensitive member as charges pass through each layer (for example, a surface layer, a charge generation layer, a charge transport layer, and an intermediate layer) of the electrophotographic photosensitive member. Currently, the most widely used electrophotographic photoreceptors are composed of organic materials, and in the current electrophotographic processes in which repeated charging and discharging are repeated, the organics constituting the electrophotographic photoreceptor are included. The material gradually changes in quality due to the electrostatic hazard, and the electrophotographic characteristics are deteriorated as exemplified by generation of charge traps in the layer and change in chargeability. In particular, it is known that a decrease in chargeability has a great influence on the image quality of an output image, and causes serious problems such as a decrease in image density, background contamination, and image homogeneity during continuous output.
Various reduction factors are cited for the reduction in chargeability of the photoreceptor. For example, it has been pointed out that the discharge product generated in the charging process in the image forming process affects the photoconductor (see Patent Documents 6 to 8), and thereby the bulk conductivity of the charge transport layer and the surface layer is reduced. This improves the chargeability of the electrophotographic photosensitive member. On the other hand, a technique for suppressing a decrease in chargeability by adding an antioxidant to the charge transport layer or the surface layer has been disclosed (see Patent Document 8). In addition, a charging technique that generates less discharge products as a charging process has been disclosed (see Patent Documents 6 and 7). By applying this charging method to a charging process in an image forming process, it is possible to suppress a decrease in charging property of the electrophotographic photosensitive member caused by a discharge product.

  Moreover, the deterioration of the intermediate layer can be considered as another cause of the decrease in chargeability. The intermediate layer widely used at present is in the form of inorganic fine particles dispersed in a binder made of an organic resin, and has a function of preventing charge injection from the support to the photosensitive layer, and the charge generated in the photosensitive layer. It is preferable to have a function of transporting to a support. For example, if the function of preventing charge injection from the support to the photosensitive layer is insufficient, when the electrophotographic photosensitive member is charged, a charge having a polarity opposite to the charged polarity of the photosensitive member is injected from the support into the photosensitive layer. Since the charge on the body surface can be easily erased, a phenomenon that it is difficult to obtain a desired charge occurs. In addition, when the function of transporting the charge generated in the photosensitive layer to the support is insufficient, the potential of the exposed portion is increased due to a decrease in charge generation efficiency, and chargeability failure due to charge trapping in the intermediate layer is likely to occur. Various techniques for coexistence and maintenance of these two functions have been developed, but these functions are likely to have a reciprocal relationship, and it is very difficult to achieve both functions. For example, a technique for achieving an improvement in the function of preventing charge injection by applying a high insulating layer as a constituent layer of the intermediate layer is disclosed (see Patent Documents 9 and 10). When this technology is used for electrophotographic photoreceptors, it is reported that image defects such as scumming due to a decrease in chargeability of the photoreceptor are extremely small, and extremely good output images are maintained even after repeated use. Has been. However, the function of charge transport from the charge generation material to the support, which is another function that the intermediate layer should bear, becomes insufficient, and it tends to cause an increase in the potential of the exposed area and poor charging. As a result, a phenomenon such as an increase in the potential of the exposed portion and defective charging is likely to manifest.

For example, in an image forming process in which the surface of an electrophotographic photosensitive member is negatively charged, a technique has been proposed in which an electron transport material is blended in the intermediate layer of the electrophotographic photosensitive member (see Patent Document 11). According to this proposal, the reverse polarity charge (in this case, positive charge) on the surface of the photoreceptor is difficult to be injected from the support to the photosensitive layer, and the negative charge generated in the charge generation layer can be transported to the support. Thus, an intermediate layer satisfying the two functions of the intermediate layer is obtained. When such an intermediate layer is applied to an electrophotographic photosensitive member, very good electrophotographic characteristics are initially exhibited.
However, in the above proposal, there are few electron transport materials exhibiting excellent electron transfer characteristics, the organic material constituting the intermediate layer is likely to be deteriorated by repeated electrostatic hazards, and further, the electron transport material is made of oxygen in the atmosphere. Due to the fact that it is easy to form charge traps by being affected, it is a problem that electrophotographic characteristics are deteriorated by repeated electrostatic hazards.

  Therefore, it has excellent wear durability, can suppress charge injection from the support to the photosensitive layer without causing an increase in potential of the exposed area, and deteriorates electrophotographic characteristics such as a decrease in chargeability even after long-term use. Electrophotographic photosensitive member capable of continuously obtaining a high-quality image with extremely few defects and few defects, and an image forming method, an image forming apparatus, and a process cartridge using the electrophotographic photosensitive member have not been obtained. The present situation is that the prompt provision is desired.

JP-A-5-181299 JP 2002-6526 A JP 2002-82465 A JP 2000-284514 A JP 2001-194413 A Japanese Patent Laid-Open No. 9-26685 JP 2002-229241 A JP 2006-99028 A Japanese Patent Laid-Open No. 3-45762 Japanese Patent Laid-Open No. 7-281463 JP 2006-259141 A

  An object of the present invention is to solve various problems in the prior art and achieve the following objects. That is, the present invention has a surface layer containing at least a binder resin, a filler, and an intermediate layer made of an amorphous oxide semiconductor, has excellent wear durability, and does not cause an increase in exposed area potential. In addition to being able to suppress charge injection from the support to the photosensitive layer, it is possible to continuously obtain high-quality images with few defects with extremely little deterioration in electrophotographic characteristics such as deterioration in chargeability even after long-term use. It is an object of the present invention to provide an electrophotographic photosensitive member that can be used, and an image forming method, an image forming apparatus, and a process cartridge using the electrophotographic photosensitive member.

In order to solve the above-mentioned problems, the present inventors have conducted intensive research to achieve the above object, and as a result, the support has at least an intermediate layer, a photosensitive layer, and a surface layer in this order, and the surface layer has at least a binder resin. In addition, by using an amorphous oxide semiconductor for the intermediate layer, it is possible to suppress the injection of unnecessary charges from the support to the photosensitive layer, and the intermediate layer can be used even when used. The occurrence of charge trapping in the inside and unnecessary injection of unnecessary charges from the support hardly occur, the chargeability of the electrophotographic photosensitive member does not deteriorate for a long time, and the defect of the output image can be extremely reduced. It has been found that an electrophotographic photosensitive member that can be produced can be produced. Furthermore, it has been found that the above-described effect is remarkably exhibited by using an amorphous oxide containing at least indium, zinc and gallium as the amorphous oxide semiconductor.
By using the electrophotographic photoreceptor of the present invention, injection of unnecessary charges from the intermediate layer to the charge generation layer and the charge transport layer can be suppressed, and the charge generated from the charge generation material can be effectively supported. Since the intermediate layer formed by the method of the present invention is extremely robust against charge hazard, the above characteristics can be maintained over a long period of time. As a result, even when the electrophotographic photosensitive member is repeatedly used, output image defects such as image density reduction and scumming do not occur, and long-life electrophotography is durable against mechanical hazards derived from the image forming process. A photoreceptor can be provided.

The present invention is based on the above findings by the present inventors, and means for solving the above problems are as follows. That is,
<1> A support, and at least an intermediate layer, a photosensitive layer, and a surface layer are provided in this order on the support.
The surface layer contains at least a binder resin and a filler,
The electrophotographic photosensitive member is characterized in that the intermediate layer contains an amorphous oxide semiconductor.
In the electrophotographic photoreceptor of the above <1>, unnecessary charges (in particular, positive charges in the present invention) are injected into the charge generation layer or the charge transport layer from the support through the intermediate layer. It can be suppressed by utilizing the unique electrical characteristics, and has a surface layer with excellent mechanical durability, excellent electrostatic stability, and various types of electrons even over long-term use. It is possible to provide an excellent electrophotographic photosensitive member with little variation in photographic characteristics and less occurrence of defects related to output image quality.
<2> The electrophotographic photosensitive member according to <1>, wherein the amorphous oxide semiconductor contains at least indium, zinc, and gallium.
<3> The electrophotographic photosensitive member according to any one of <1> to <2>, wherein the intermediate layer has a thickness of 0.1 μm to 0.9 μm.
The electrophotographic photoreceptors of the above <2> and <3> are an inorganic material group capable of relatively easily forming an n-type semiconductor composed of a homogeneous amorphous oxide, and film forming conditions, etc. By adjusting the thickness, it is possible to form an intermediate layer with excellent electrostatic stability that can change the electrical characteristics of the amorphous oxide semiconductor and the thickness of the intermediate layer. Therefore, it is possible to provide an excellent electrophotographic photosensitive member with less wear, less variation in electrophotographic characteristics, and less occurrence of defects related to output image quality.
<4> The electrophotographic photosensitive member according to any one of <1> to <3>, wherein the support has a surface roughness (Rz) of 0.6 μm or more.
In the electrophotographic photoreceptor of <4>, it is possible to provide an excellent electrophotographic photoreceptor that does not cause moiré even when the electrophotographic photoreceptor is exposed to writing light with high coherency.
<5> The electrophotographic photosensitive member according to any one of <1> to <4>, wherein the filler is a metal oxide.
<6> The electrophotographic photosensitive member according to <5>, wherein the metal oxide is at least one selected from aluminum oxide, titanium oxide, and silica.
<7> The electrophotographic photosensitive member according to any one of <5> to <6>, wherein the metal oxide is α-alumina.
In the electrophotographic photoreceptors according to <5>, <6>, and <7>, a surface layer excellent in wear durability is obtained without impairing characteristics (chargeability / light attenuation) required for the electrophotographic photoreceptor. It is possible to provide an excellent electrophotographic photosensitive member that can be obtained and has little wear on the photosensitive member, little variation in electrophotographic characteristics, and few occurrences of defects related to output image quality even after long-term use.
<8> The electrophotographic photosensitive member according to any one of <1> to <7>, wherein the binder resin is at least one of a polycarbonate resin and a polyarylate resin.
In the electrophotographic photoreceptor of the above <8>, a surface layer excellent in wear durability can be obtained without impairing characteristics (chargeability / light attenuation) required for the electrophotographic photoreceptor, and used for a long time. Therefore, it is possible to provide an excellent electrophotographic photosensitive member with less wear of the photosensitive member, less variation in electrophotographic characteristics, and less occurrence of defects related to output image quality.
<9> The electrophotographic photosensitive member according to any one of <1> to <8>, wherein the binder resin is a polymer charge transport material.
<10> The electrophotographic photosensitive member according to <9>, wherein the polymer charge transport material is at least one polymer selected from polycarbonate, polyurethane, polyester, and polyether.
<11> The electrophotographic photosensitive member according to any one of <9> to <10>, wherein the polymer charge transport material has a triarylamine structure.
In the electrophotographic photoreceptors according to <9>, <10> and <11>, a surface layer excellent in wear durability is obtained without impairing characteristics (chargeability / light attenuation) required for the electrophotographic photoreceptor. It is possible to provide an excellent electrophotographic photosensitive member that can be obtained and has little wear on the photosensitive member, little variation in electrophotographic characteristics, and few occurrences of defects related to output image quality even after long-term use.
<12> The electrophotographic photosensitive member according to any one of <1> to <11>, wherein the surface layer further contains a charge transport material.
In the electrophotographic photosensitive member according to the above <12>, a surface layer excellent in wear durability can be obtained without impairing characteristics (chargeability / light attenuation) required for the electrophotographic photosensitive member. Therefore, it is possible to provide an excellent electrophotographic photosensitive member with less wear of the photosensitive member, less variation in electrophotographic characteristics, and less occurrence of defects related to output image quality.
<13> The electrophotographic photosensitive member according to any one of <1> to <12>, wherein the photosensitive layer is a laminated type including a charge generation layer and a charge transport layer.
In the electrophotographic photoreceptor of <13>, a surface layer can be formed without having a clear interface with the charge transport layer, and the charge injection at the charge transport layer / surface layer interface is not physically inhibited. , A charge transport layer having an excellent charge transport function can be obtained, and even with long-term use, the photoreceptor is less worn, has excellent electrophotographic characteristics, and has little fluctuations in the characteristics. An excellent electrophotographic photosensitive member with few defects can be provided.
<14> A charging step for charging the surface of the electrophotographic photosensitive member, an exposure step for exposing the charged electrophotographic photosensitive member surface to form an electrostatic latent image, and developing the electrostatic latent image using toner. In an image forming method comprising at least a development step for forming a visible image and a transfer step for transferring the visible image to a recording medium,
The electrophotographic photosensitive member is the electrophotographic photosensitive member according to any one of <1> to <13>.
In the <14> image forming method, it is possible to provide an excellent image forming method in which the chargeability does not deteriorate over a long period of time and the occurrence of defects related to the output image quality is small.
<15> An electrophotographic photosensitive member, a charging unit that charges the surface of the electrophotographic photosensitive member, an exposure unit that exposes the surface of the charged electrophotographic photosensitive member to form an electrostatic latent image, and the electrostatic latent image In an image forming apparatus having at least developing means for developing a visible image by developing a toner and transfer means for transferring the visible image to a recording medium,
An electrophotographic photosensitive member according to any one of <1> to <13>, wherein the electrophotographic photosensitive member is an image forming apparatus.
In the <15> image forming apparatus, it is possible to provide an excellent image forming apparatus in which the chargeability does not deteriorate over a long period of time and the occurrence of defects related to the output image quality is small.
<16> Development for forming a visible image by developing the electrophotographic photosensitive member according to any one of <1> to <13> and an electrostatic latent image formed on the electrophotographic photosensitive member with toner. And a process cartridge that is detachable from the main body of the image forming apparatus.
In the process cartridge <16>, it is possible to provide an excellent process cartridge in which the chargeability does not deteriorate over a long period of time and the occurrence of defects related to the output image quality is small.

  In the present invention, in order to achieve a long life of the electrophotographic photosensitive member, it is important to impart durability to various hazards received from each process in image formation as described above. In particular, two hazards, a mechanical hazard that is applied in a cleaning process for removing toner remaining on the surface of the electrophotographic photosensitive member, and an electrostatic hazard that is received from a charging process or a transfer process give a large stress to the photosensitive member. It is considered to cause a change in the characteristics of the photoreceptor and to be an impeding factor for extending the life of the photoreceptor. Of these, the present invention relates to an improvement in durability against electrostatic hazards, and more specifically, relates to a durability improvement technique related to charging properties such as background contamination and image density unevenness.

The charging process in the electrophotographic image forming process is to charge the surface of the photosensitive member to a constant potential. The uniformity is related to image density unevenness, background stains, etc., and the charging ability is related to high speed. It is considered an important technology for speeding up. In the electrophotographic photosensitive member, the characteristics required for uniformly charging the surface include no unnecessary charge injection from the support and few charge traps in the electrophotographic photosensitive member. If the electrophotographic photosensitive member does not have these characteristics, charge injection with a polarity opposite to the charging polarity occurs from the support when the electrophotographic photosensitive member is charged in the charging process, canceling the charge applied to the surface. The accumulated charge in the electrophotographic photosensitive member cancels the charge applied to the surface, thereby causing a phenomenon that desired chargeability cannot be obtained.
In addition, as a recent development trend of electrophotographic photosensitive members, the service life has been extended to be environmentally friendly and easy to maintain, and there is no unnecessary charge injection or charge trapping from the support shown here. Is required to be maintained over a long period of time. In other words, even though the characteristics related to the chargeability shown here have very excellent characteristics at the beginning, the organic material used by use deteriorates, and an injection site of unnecessary charges is generated. In addition, the electrical durability of the material to be used is required to cause a decrease in chargeability due to generation of a new charge trap in the layer.
Accordingly, the electrophotographic photosensitive member of the present invention has a surface layer containing at least a binder resin and a filler, has durability against passing charges, and electrochemically injects unnecessary charges into the photosensitive layer. By applying an amorphous oxide semiconductor that is difficult to resist, especially an amorphous oxide semiconductor containing indium, gallium, and zinc, to the intermediate layer, high quality with few defects, which is less likely to cause deterioration in chargeability even after long-term use. Images can be obtained continuously and are applied to the image forming method, the image forming apparatus, and the process cartridge of the present invention.

  According to the present invention, the conventional problems can be solved and the object can be achieved, and a surface layer containing at least a binder resin, a filler, and an intermediate layer made of an amorphous oxide semiconductor are provided. It has excellent wear durability and can suppress charge injection from the support to the photosensitive layer without causing an increase in the exposed area potential. There can be provided an electrophotographic photosensitive member capable of continuously obtaining a high-quality image with extremely little deterioration and few defects, and an image forming method, an image forming apparatus, and a process cartridge using the electrophotographic photosensitive member. .

(Electrophotographic photoreceptor)
The electrophotographic photoreceptor of the present invention comprises a support and at least an intermediate layer, a photosensitive layer and a surface layer in this order on the support, and further comprises other layers as necessary.

<Intermediate layer>
The intermediate layer has a function of suppressing injection of unnecessary charges (charges having a polarity opposite to the charge polarity of the photosensitive member) from the support to the photosensitive layer, and the charge polarity of the photosensitive member among the charges formed in the photosensitive layer. And the function of transporting charges having the same polarity as the above. For example, when it is necessary to negatively charge the photoreceptor as an image forming process, the intermediate layer has a hole injection blocking function (hole blocking property) from the support to the photosensitive layer and an electron from the photosensitive layer to the support. It is necessary to combine the transport function (electron transportability). In order to obtain a long-life electrophotographic photosensitive member, it is important that the characteristics do not change due to repeated electrostatic hazards.
Since the intermediate layer has a hole blocking property, the characteristics to be possessed as the intermediate layer include that the ionization potential of the intermediate layer or the work function in the electron full band is higher than the Fermi rank of the support, and that the intermediate layer itself is positive. It is mentioned that the hole transportability is extremely small. Preferred examples of the material having these characteristics include n-type semiconductor materials. In addition, from the viewpoint of work function, it can be mentioned that the band gap is relatively large. Furthermore, in order to transport electrons generated in the photosensitive layer to the support (electron transportability), the characteristics that the intermediate layer should have are that the electron affinity of the photosensitive layer is smaller than the electron affinity of the intermediate layer, and the intermediate layer has electron transport properties. It is mentioned to have.
Examples of the intermediate layer satisfying these characteristics include an electron transport layer formed by dispersing an organic material having an electron transport structure in a binder, an inorganic semiconductor exhibiting n-type, and the like. As the material in which the characteristics of the material are less likely to change due to electrostatic hazard, the n-type inorganic semiconductor material as shown in the latter is preferable. Further, in consideration of in-plane variation in electrical characteristics in a device having a relatively large area as typified by an electrophotographic photoreceptor, an amorphous material is preferable.
The amorphous oxide means a solid state oxide having an irregular atomic arrangement. This oxide is roughly classified into a glass oxide semiconductor obtained by quenching an oxide in a high-temperature fluid state and an amorphous oxide semiconductor formed at a relatively low temperature by a technique such as sputtering. it can. In consideration of the heat resistance of the support, it is preferable to select an amorphous oxide semiconductor as mentioned in the latter.

  The amorphous oxide semiconductor that can be applied to the intermediate layer is not particularly limited and may be appropriately selected depending on the intended purpose. For example, at least two elements of indium oxide, indium, zinc, and tin Amorphous oxide semiconductor containing at least two elements of indium, zinc and gallium; amorphous oxide semiconductor containing at least two elements of indium, tin and zinc; indium, tungsten And an amorphous oxide semiconductor containing at least two elements of zinc; an amorphous oxide semiconductor containing at least two elements of yttrium, manganese and titanium (however, it can be formed by low-temperature film formation). Among these, an amorphous oxide semiconductor composed of three elements of indium, zinc and gallium is particularly preferable from the viewpoint of electrostatic stability and electrical conductivity.

-Method for forming amorphous oxide semiconductor-
The method for depositing the amorphous oxide semiconductor on the support is not particularly limited, and can be appropriately selected from generally used methods for depositing inorganic materials.
The general film forming methods are roughly classified into a vapor phase growth method, a liquid phase growth method, and a solid phase growth method.
The vapor deposition method is further classified into a physical vapor deposition method (PVD) and a chemical vapor deposition method (CVD).
Examples of the physical vapor deposition method include vacuum deposition, electron beam deposition, laser ablation method, laser ablation MBE, MOMBE, reactive deposition, ion plating, cluster ion beam method, glow discharge sputtering, ion beam sputtering, Examples include reactive sputtering.
Examples of the liquid phase growth method include thermal CVD, MOCVD, RF plasma CVD, ECR plasma CVD, photo CVD, and laser CVD. Examples of the liquid phase method include an LPE method, an electroplating method, an electroless plating method, and a coating method. Examples of the solid phase method include SPE, recrystallization method, graphoepitaxy, LB method, and sol-gel method.
Of these film forming methods, physical vapor deposition is widely applied to form a homogeneous film in a relatively large area such as an electrophotographic photosensitive member. The laser ablation method is suitable when fine composition control of the crystalline oxide semiconductor is necessary, and various sputtering methods are suitable when mass productivity is necessary.

Next, the film forming conditions of the amorphous oxide semiconductor, particularly the film forming conditions related to the sputtering method will be described in detail.
-Cleaning the substrate-
In order to obtain an amorphous oxide semiconductor exhibiting uniform electrical characteristics, it is very important to clean the substrate on which the amorphous oxide semiconductor is formed, in the present invention, the support. The surface of a clean support is ideally free of contaminants other than at least the support (eg aluminum), but it is very difficult to achieve that condition. Therefore, it is preferable to obtain a desired support surface by applying a generally proposed cleaning method in accordance with the amount of surface contaminants required and the performance of the apparatus used in the experiment.
The cleaning method is not particularly limited and may be appropriately selected depending on the purpose. For example, the wet cleaning method, sputter etching method, high temperature thermal etching method, low temperature thermal etching method, electron beam irradiation etching method, synchrotron Examples thereof include a radiation light irradiation etching method and a laser light irradiation etching method.

-Target-
In forming the amorphous oxide semiconductor on the support by sputtering, a polycrystalline sintered body containing a constituent element of the formed amorphous oxide semiconductor is generally used. The element used for the polycrystalline sintered body may be appropriately selected depending on the constituent element of the amorphous oxide semiconductor to be formed.
Further, in order to obtain an amorphous oxide semiconductor composed of at least indium, zinc, and gallium, it is necessary to use a polycrystalline sintered body containing at least indium, zinc, and gallium. Such a polycrystalline sintered body can be produced by a generally known target production method. As an example of the production method, each powder of indium oxide, zinc oxide and gallium oxide can be blended at a desired blending ratio, and it can be obtained by wet mixing using ethanol until homogeneous and then sintering. It is.
Further, for the purpose of controlling the conductivity of the amorphous oxide semiconductor, a target may be doped with a desired impurity in advance. There is no restriction | limiting in particular as a metal to dope, According to the objective, it can select suitably, For example, Li, Na, Mn, Ni, Pd, Cu, Cd, C, N, P, Ti, Zr, V, Ru, Ge, Sn, F, etc. are mentioned.

−Film forming pressure−
In the sputtering method, plasma is generated by applying an electric field on a target during film formation. For this reason, when the sputtering method is used, it is necessary to form a reduced pressure atmosphere using a vacuum chamber or the like. If the pressure during film formation is insufficient, plasma cannot be formed or the plasma is unstable, so care must be taken because the formed film becomes non-uniform. The reduced pressure atmosphere may be appropriately selected from the film forming method, apparatus, conditions, desired film quality, and the like.

-Inflow gas type-
In sputtering, an amorphous oxide semiconductor is formed on a substrate (support) placed on a counter electrode by forming a plasma while flowing a mixed gas of an inert gas and an oxygen gas into a reduced-pressure atmosphere. can do. The inert gas used here is not particularly limited as long as it is generally used, and examples thereof include helium, argon, and other gases typified by nitrogen gas as typified by Group 18 elements. Moreover, in order to add the said impurity, in addition to inert gas and oxygen, you may use together 1 or more types of gas.

-Oxygen partial pressure-
A general oxide semiconductor has a feature that the conductivity can be controlled by the amount of oxygen (amount of oxygen vacancies) in the oxide semiconductor without doping impurities, and the amorphous oxide described in the present invention Semiconductors have similar properties. This property indicates that the conductivity control of the amorphous oxide semiconductor can be controlled only by the oxygen flow rate (oxygen partial pressure) during film formation, which is important from the viewpoint of controlling the electron transport properties in the intermediate layer. It becomes film conditions.
The proportion of oxygen gas circulated at the time of film formation varies depending on the apparatus and other conditions described later, but generally 0.05 vol% or more and 20 vol% or less is preferable with respect to the total gas flow circulated, and 0.1 vol% or more and 15 vol%. The following is more preferable. When the proportion of the oxygen gas exceeds 20 vol%, the electron conductivity may be extremely low due to the carrier concentration of the formed amorphous oxide semiconductor being too low.

-Target / substrate distance-
It is known that the amount of oxygen (amount of oxygen vacancies) in the amorphous oxide semiconductor changes by changing the target / substrate distance. In general, when the target / substrate distance is increased, the amount of oxygen vacancies decreases and the formed amorphous oxide semiconductor becomes a high-resistance material. On the other hand, when the distance between the target and the substrate is reduced, the homogeneous film is affected by the influence on the film quality due to the substrate temperature rising due to the plasma on the target surface, and the influence of the plasma itself on the amorphous oxide semiconductor. Care should be taken because it may be difficult to manufacture. Since the target / substrate distance differs depending on the film forming method, apparatus, and other film forming conditions, it is preferable to select a target / substrate distance that provides desired electrical characteristics.

-Substrate temperature-
In the sputtering method, the temperature of the substrate tends to rise due to the discharge of the target surface. The substrate temperature is controlled by methods such as cooling the substrate and increasing the distance between the target and the substrate because it is known that the increase in the substrate temperature affects the electrical properties, denseness, and structure of the film. It is preferable.

-Film quality of amorphous oxide semiconductor-
In the present invention, in order to show good electrophotographic characteristics, attention should be paid to the film quality of the amorphous oxide semiconductor.
In the present invention, it is important that the intermediate layer is a homogeneous amorphous film. The method for confirming that the film formed on the support by the above-described method is amorphous is generally determined by crystal structure analysis by X-ray diffraction. In addition, a structural analysis method such as an electron diffraction method or a neutron diffraction method, or a method using a microstructure observation means such as a transmission electron microscope (TEM) may be used to determine the cross section of the formed film.
In addition, as a feature of an amorphous oxide semiconductor that affects electrophotographic characteristics, the composition and distribution of the film are important. As a composition analysis method of an amorphous oxide semiconductor, a method generally used as an elemental analysis method can be applied. For example, fluorescent X-ray analysis, X-ray photoelectron spectroscopy, Auger electron spectroscopy, energy dispersive X Examples of constituent element analysis methods for substances such as line spectroscopy.

  The electrical characteristics of the amorphous oxide semiconductor used as the intermediate layer greatly influence the electrical characteristics of the electrophotographic photosensitive member. Therefore, in order to obtain the desired electrical characteristics of the electrophotographic photosensitive member, an amorphous material applied to the intermediate layer is used. It is necessary to appropriately select the electrical characteristics of the oxide semiconductor. The following are typical examples of the electrical characteristics of an amorphous oxide semiconductor.

-Carrier concentration-
The amorphous oxide semiconductor can control the amount of oxygen vacancies (so-called carrier concentration) in the film according to the amount of oxygen flow during film formation without doping with an impurity metal or the like. In addition, the carrier concentration can be adjusted by appropriately doping impurities. As a method for quantifying the carrier concentration, a method using the Hall effect is generally used.

-Surface resistance-
There is no restriction | limiting in particular as a measuring method of the surface resistance of the said amorphous oxide semiconductor, The surface resistivity measuring method generally used can be used. Specifically, for a low resistance body having a surface resistivity of 10 ⁶ Ω / cm ² or less, a constant current application method described in JIS K 7194 is exemplified. Further, for a high resistance body having a surface resistivity of 10 ⁶ Ω / cm ² or more, a constant voltage application / leakage current measurement method described in JIS K 6911 is exemplified. Further, in addition to this method, measurement may be performed by a generally known method such as a four-probe method, a four-terminal method, or a two-terminal method.

-Band gap-
In the present invention, the band gap of the amorphous oxide semiconductor is also considered to be related to the characteristics of the electrophotographic photosensitive member, particularly the hole blocking property from the support, so that the band gap ( To be precise, the work function in the full band of the amorphous oxide semiconductor may be selected as appropriate.
The band gap measurement method is measured by an electrochemical measurement method, a photochemical measurement method, or the like. For example, a band gap energy measurement method using a Tauc plot, which is one of the photochemical measurement methods, can be exemplified. In this method, in general, an absorption coefficient α and light energy hν (where h is a Planck constant and ν is a wave number) in a region of relatively large absorption near the optical absorption edge on the long wavelength side of a semiconductor. And the following equation is considered to hold between the band cap energy E0.
αhν = B (hν−E0) ² (B is a constant)
Therefore, the absorption spectrum is measured, hν is plotted against (αhν) ^1/2 (so-called Tauc plot), and the value of hν at α = 0 obtained by extrapolating the straight line section is the band gap energy.
The band gap is not particularly limited, and may be measured by using the above-described method, and various measurement methods can be used when characteristic values that are synonymous electrochemically and photochemically can be obtained.

-Intermediate layer thickness-
It is considered that the thickness of the amorphous oxide semiconductor used for the intermediate layer also affects the electrical characteristics of the electrophotographic photoreceptor. Currently, the light source widely used in the exposure process is laser light with high coherence, so that moire is likely to occur due to interference between incident laser light and reflected light from the support, and the support and intermediate layer. In order to compensate for physical contact, the surface of the support often has arbitrary irregularities. In such a case, when the thickness of the intermediate layer is small, the film thickness deviation becomes large due to the surface irregularities of the support, which may cause partial charging failure. Further, when an amorphous oxide semiconductor is used for the intermediate layer as in the present invention, if the thickness is too large, the variation in composition in the depth direction of the film will increase, resulting in variations in electrical characteristics depending on the location. Since the time required for the film becomes long, the cost for film formation becomes very large, which is not realistic.
The thickness of the intermediate layer is preferably 0.05 μm or more and 1.5 μm or less, and more preferably 0.1 μm or more and 0.9 μm or less. When the thickness of the intermediate layer is less than 0.05 μm, it is difficult to uniformly coat the surface of the support, and the effects of the present invention may not be sufficiently exhibited. When the thickness exceeds 1.5 μm, film formation is performed. There is a possibility that the cost is excessively high and the electrical characteristics of the intermediate layer are different between the vicinity of the support and the vicinity of the photosensitive layer.

―Layer structure of electrophotographic photosensitive member―
The electrophotographic photoreceptor of the present invention has a support and at least an intermediate layer, a photosensitive layer, and a surface layer in this order on the support.
The photosensitive layer may have a single layer structure or a multilayer structure as long as it has a charge generation function and a charge transport function. An example of this embodiment will be described with reference to FIGS.
The schematic cross-sectional view of the electrophotographic photosensitive member shown in FIG. 1 is an example in the case where the photosensitive layer is a single layer, and a photosensitive material mainly composed of a charge generating material and a charge transporting material on a support 31 and an intermediate layer 32. A layer 36 and a surface layer 35 are provided. Here, the surface layer 35 is a crosslinkable surface layer described below.
The schematic cross-sectional views of the electrophotographic photosensitive member shown in FIGS. 2 and 3 are examples in the case where the photosensitive layer is laminated. On the support 31 and the intermediate layer 32, the charge generating layer 33 having a charge generating function, and the charge The charge transport layer 34 having a transport function is separated and stacked. In the case of taking this embodiment, as shown in the figure, the order of stacking the charge generation layer and the charge transport layer is not particularly limited, and can be properly used according to the application. The surface layer 35 is provided on the outermost surface of the photoreceptor. Are stacked.

<Surface layer>
The surface layer contains at least a binder resin and a filler, and further contains other components as necessary.

  In the surface layer, the filler is preferably dispersed in the binder resin. Since the surface layer is used by being laminated on a charge transport layer, which will be described later, it is necessary to have at least a function to be performed by the charge transport layer, that is, a charge transport function and chargeability. In order to impart a charge transport function to the surface layer, it can be achieved by dispersing a charge transport material in the layer in the same manner as the charge transport layer described later. In addition, the chargeability has a large relationship with the capacitance of the surface layer. As is well known, the charge amount of the dielectric is determined from the relationship of Q = CV (where Q is the charge amount, C is the capacitance of the film, and V is the charge potential). In order to obtain a large charging potential, it is important that the capacitance is small. In general charging theory of a resin film, it is often regarded as a dielectric having a resistance component (that is, a parallel circuit of a capacitor and a resistor) instead of an ideal dielectric. Therefore, it is also important to obtain a charging potential of the surface layer that there is little charge leakage in the surface layer. For these reasons, in order to obtain sufficient chargeability as the surface layer, it is important that the capacitance is small and the resistance is large. From the viewpoint of the charge transport function, it is preferable that there is no physical interface at the interface between the charge transport layer and the surface layer. In order to obtain a surface layer having both of these electrical characteristics and the wear durability described in the present invention, fillers, binder resins and additives as shown below can be appropriately selected and used.

  In order to obtain a long-life electrophotographic photosensitive member, it is important to have high durability against hazards from various electrophotographic processes. As described above, the hazards mentioned here include mechanical hazards applied from cleaning members and transfer members, and electrostatic hazards applied from charging members and transfer members. As described above, it is known that the electrostatic durability is excellent by applying the amorphous semiconductor described in the present invention, and an electrophotographic photoreceptor having wear durability can be used. In that case, the lifetime is expected to improve dramatically.

-Filler-
In the present invention, it is preferable to provide a surface layer in which at least one of an organic filler and an inorganic filler is dispersed in a binder resin for the purpose of imparting abrasion durability to the electrophotographic photosensitive member.
There is no restriction | limiting in particular as said organic type filler, According to the objective, it can select suitably, For example, fluororesin powder like polytetrafluoroethylene, silicone resin powder, carbon powder etc. are mentioned. .
The inorganic filler is not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include metal powders such as copper, tin, aluminum and indium, aluminum oxide, silicon oxide, silica, tin oxide and oxide. Examples thereof include metal oxides such as zinc, titanium oxide, indium oxide, antimony oxide, bismuth oxide, tin oxide doped with antimony, indium oxide doped with tin, and inorganic materials such as potassium titanate.
Among the fillers, from the viewpoint of the hardness of the filler, inorganic fillers are preferable, metal oxides are more preferable, aluminum oxide, titanium oxide, and silica are even more preferable, and α-alumina having a hexagonal close-packed structure is most preferable. .
The volume average particle diameter of the filler is preferably in the range of 0.1 μm to 2 μm, and more preferably in the range of 0.3 μm to 1.5 μm. When the volume average particle size of the filler is less than 0.1 μm, the wear resistance is not sufficiently exhibited, and when it is larger than 2 μm, the surface property of the coating film is deteriorated or the coating suitability is deteriorated. May be difficult to form.
The average particle diameter of the filler in the present invention is a volume average particle diameter unless otherwise specified, and is measured by an ultracentrifugal automatic particle size distribution analyzer (CAPA-700, manufactured by HORIBA, Ltd.), and 50% of the cumulative distribution. Is calculated as a particle diameter corresponding to (Median type).
It has also been found important that the standard deviation of each particle measured simultaneously is 1 μm or less. When the standard deviation value is larger than 1 μm, the particle size distribution becomes wide, and as described above, the surface property of the electrophotographic photosensitive member may be deteriorated or film formation may be difficult, and excellent wear durability. The surface layer having the property may not be formed.
The filler concentration in the surface layer varies depending on the type of filler used and the image forming process conditions using the photoconductor, but the ratio of filler to the total solid content on the outermost layer side of the surface layer is 5% by mass or more. Is preferable, 10 mass% or more and 50 mass% or less are more preferable, and 15 mass% or more and 30 mass% or less are especially preferable.
When the filler concentration in the surface layer is less than 5% by mass with respect to the total solid content on the outermost layer side of the surface layer, the wear durability becomes insufficient, and the desired wear durability / electrostatic durability. May not be an electrophotographic photoreceptor having both. On the other hand, when the filler concentration in the surface layer is within the particularly preferable range, it is advantageous in that excellent wear durability can be obtained.

In the filler-dispersed surface layer as described in the present invention, attention must be paid because the electrical characteristics of the filler used may affect the output image. The electrical characteristics mentioned here refer to the charged state and electrical resistance of the filler surface.
Normally, particles dispersed in a liquid are charged positively or negatively, and ions having opposite charges gather to try to keep it electrically neutral, and an electric double layer is formed there. The dispersed state of the particles is stabilized. The potential (zeta potential) gradually decreases with increasing distance from the particle, and the potential in a region that is sufficiently away from the particle and electrically neutral is zero. Therefore, the stability increases as the repulsive force of the particles increases due to the increase in the absolute value of the zeta potential, and the particles tend to aggregate and become unstable as they approach zero. On the other hand, the zeta potential varies greatly depending on the pH value of the system, and at a certain pH value, the potential becomes zero and has an isoelectric point. Therefore, the dispersion system is stabilized by increasing the absolute value of the zeta potential as far as possible from the isoelectric point of the system.
In the configuration of the present invention, the filler having a pH at the isoelectric point of at least 5 is preferably from the viewpoint of the resolution of the output image, and the more basic the filler, the higher the effect. It was confirmed that there is. The filler having a high basic pH at the isoelectric point has a higher zeta potential when the system is acidic, so that dispersibility and stability thereof are improved.
Here, the pH of the filler in the present invention indicates the pH value at the isoelectric point from the zeta potential, and the zeta potential was measured with a laser zeta potentiometer manufactured by Otsuka Electronics Co., Ltd.

Furthermore, in order to obtain a high-quality output image over a long period of time, the filler used for the surface layer is preferably a filler with high electrical insulation (specific resistance is 10 ¹⁰ Ω · cm or more), and the filler has a pH of Those having a dielectric constant of 5 or more can be used particularly effectively.
As the filler, either a filler having a pH of 5 or more and a filler having a dielectric constant of 5 or more may be used alone, or a filler having a pH of 5 or less and a filler having a pH of 5 or more may be used. A mixture of the above may be used, or a filler having a dielectric constant of 5 or less and a filler having a dielectric constant of 5 or more may be mixed and used.
Among the fillers, α-alumina, which has a hexagonal close-packed structure with high insulation properties, high thermal stability and high wear resistance, is particularly useful in terms of high image quality and improved wear resistance. is there.
The specific resistance of the filler used in the present invention is defined as follows. Since the specific resistance value of a powder such as a filler varies depending on the filling rate, it is necessary to measure under certain conditions. In the present invention, the specific resistance of the filler is measured using an apparatus having the same configuration as the measuring apparatus shown in Japanese Patent Laid-Open No. 5-94049 (see FIG. 1) and Japanese Patent Laid-Open No. 5-113688 (see FIG. 1). The value was measured and used. In the measuring device, the electrode area is 4.0 cm ² . Prior to the measurement, a load of 4 kg is applied to the electrode on one side for 1 minute, and the sample amount is adjusted so that the distance between the electrodes is 4 mm. At the time of measurement, the measurement is performed with the upper electrode weight (1 kg) loaded, and the applied voltage is measured at 100V. The area of 10 ⁶ Ω · cm or higher was measured with a HIGH RESISTER METER (Yokogawa Hewlett Packard), and the area below it was measured with a digital multimeter (Fluk). The specific resistance value thus obtained is defined as the specific resistance value in the present invention.

In the present invention, it is possible to perform surface treatment with at least one surface treatment agent for the purpose of improving the dispersibility of the filler. Decreasing the dispersibility of the filler not only increases the residual potential, but also decreases the transparency of the coating, causes defects in the coating, and decreases the wear resistance. It can develop into a big problem.
The surface treatment agent is not particularly limited, and any conventionally used surface treatment agent can be used, but a surface treatment agent capable of maintaining the insulating properties of the filler is preferable, a titanate coupling agent, an aluminum series Coupling agent, zircoaluminate-based coupling agent, higher fatty acid, etc., or those obtained by mixing these with silane coupling agent, Al ₂ O ₃ , TiO ₂ , ZrO ₂ , silicone, aluminum stearate, etc. Alternatively, those subjected to a mixing treatment thereof are more preferable from the viewpoint of dispersibility of the filler and image blur. The treatment with the silane coupling agent affects the output image, but there are cases where the influence can be suppressed by performing a mixing treatment of the surface treatment agent and the silane coupling agent.
The surface treatment amount varies depending on the average primary particle size of the filler used, but is preferably 3% by mass to 30% by mass and more preferably 5% by mass to 20% by mass with respect to the filler mass. When the surface treatment amount is less than 3% by mass, the filler dispersion effect may not be obtained. When the surface treatment amount is more than 30% by mass, the residual potential may be significantly increased.
These filler materials may be used alone or in combination of two or more.
In addition, the surface treatment amount of a filler is defined by the mass ratio of the surface treating agent used with respect to filler mass as mentioned above.

-Binder resin-
The binder resin is not particularly limited and may be appropriately selected depending on the intended purpose. For example, polystyrene, styrene-acrylonitrile copolymer, styrene-butadiene copolymer, styrene-maleic anhydride copolymer, polyester , Polyvinyl chloride, vinyl chloride-vinyl acetate copolymer, polyvinyl acetate, polyvinylidene chloride, polyarylate resin, phenoxy resin, polycarbonate resin, cellulose acetate resin, ethyl cellulose resin, polyvinyl butyral, polyvinyl formal, polyvinyl toluene, poly- Examples thereof include thermoplastic or thermosetting resins such as N-vinyl carbazole, acrylic resin, silicone resin, epoxy resin, melamine resin, urethane resin, phenol resin, and alkyd resin.
The binder resin also includes a polymer charge transport material having a charge transport function. The polymer charge transport material is not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include polymer materials such as polyester, polyurethane, polyether, polysiloxane, and acrylic resin, and polymer materials having a polysilane skeleton.

-Other ingredients-
The other components are not particularly limited as long as the effects of the present invention are not impaired, and can be appropriately selected according to the purpose. Examples thereof include a charge transport material.

-Charge transport material-
The charge transport material is not particularly limited and may be appropriately selected depending on the intended purpose. For example, a hole transport material having a hole transport structure such as triarylamine, hydrazone, pyrazoline, carbazole, a condensed poly Examples thereof include electron transport materials having an electron transport structure such as a ring quinone, diphenoquinone, an electron-withdrawing aromatic ring having a cyano group or a nitro group.
The hole transport material is not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include poly-N-vinylcarbazole and derivatives thereof, poly-γ-carbazolylethyl glutamate and derivatives thereof, and pyrene. -Formaldehyde condensates and derivatives thereof, polyvinylpyrene, polyvinylphenanthrene, polysilane, oxazole derivatives, oxadiazole derivatives, imidazole derivatives, monoarylamine derivatives, diarylamine derivatives, triarylamine derivatives, stilbene derivatives, α-phenylstilbene derivatives, Benzidine derivatives, diarylmethane derivatives, triarylmethane derivatives, 9-styrylanthracene derivatives, pyrazoline derivatives, divinylbenzene derivatives, hydrazone derivatives, indene derivatives, butadiene derivatives , Pyrene derivatives, bisstilbene derivatives, enamine derivatives, and other known materials. The said hole transport material may be used independently and may be used as a 2 or more types of mixture.
The electron transport material is not particularly limited and may be appropriately selected depending on the intended purpose. For example, chloroanil, bromilyl, tetracyanoethylene, tetracyanoquinodimethane, 2,4,7-trinitro-9-fluorenone 2,4,5,7-tetranitro-9-fluorenone, 2,4,5,7-tetranitroxanthone, 2,4,8-trinitrothioxanthone, 2,6,8-trinitro-4H-indeno [1 , 2-b] thiophen-4-one, 1,3,7-trinitrodibenzothiophene-5,5-dioxide, and diphenoquinone derivatives. The said electron transport substance may be used independently and may be used as a 2 or more types of mixture.
The charge transport materials may be used alone or in combination of two or more. As content in the surface layer of the said charge transport substance, 20 mass%-80 mass% are preferable with respect to the total mass of a surface layer, and 30 mass%-70 mass% are more preferable.
If the content of the charge transport material in the surface layer is less than 20% by mass with respect to the total mass of the surface layer, the charge transport property of the surface layer may be reduced and desired light attenuation characteristics may not be obtained. If it is more than 80% by mass, the desired wear durability may not be obtained. On the other hand, when the content of the charge transport material in the surface layer is within the particularly preferable range, it is advantageous in that an electrophotographic photoreceptor having both desired light attenuation characteristics and wear durability can be obtained.

Also, a polymer charge transport material having both the function of the binder resin and the function of the charge transport material can be used. The surface layer composed of the polymer charge transport material is excellent in wear resistance.
The polymer charge transport material is not particularly limited and may be a known material, but is preferably at least one polymer selected from polycarbonate, polyurethane, polyester and polyether. In particular, a polycarbonate containing a triarylamine structure in at least one of the main chain and the side chain is preferable in terms of wear durability. Among these, polymer charge transport materials represented by the following formulas (1) to (10) are preferably used.
In the formula (1), R ₁ , R ₂ and R ₃ are each independently a substituted or unsubstituted alkyl group or halogen atom, R ₄ is a hydrogen atom or a substituted or unsubstituted alkyl group, R ₅ and R ₆ are A substituted or unsubstituted aryl group, o, p, q are each independently an integer of 0-4, k, j represents a composition, 0.1 ≦ k ≦ 1, 0 ≦ j ≦ 0.9, n is Represents the number of repeating units and is an integer of 5 to 5,000. X represents an aliphatic divalent group, a cycloaliphatic divalent group, or a divalent group represented by the following general formula (I) or (II).

In general formula (I), R ₁₀₁ and R ₁₀₂ each independently represents a substituted or unsubstituted alkyl group, aryl group or halogen atom. l and m are integers of 0 to 4, Y is a single bond, a linear, branched or cyclic alkylene group having 1 to 12 carbon atoms, -O-, -S-, -SO-, -SO2-, —CO—, —CO—O—Z—O—CO— (wherein Z represents an aliphatic divalent group). Here, R ₁₀₁ and R ₁₀₂ may be the same or different.

In general formula (II), a represents an integer of 1 to 20, b represents an integer of 1 to 2,000, and R ₁₀₃ and R ₁₀₄ represent a substituted or unsubstituted alkyl group or aryl group. Here, R ₁₀₃ and R ₁₀₄ may be the same or different.

In formula (2), R ₇ and R ₈ represent a substituted or unsubstituted aryl group, and Ar ₁ , Ar ₂ , and Ar ₃ represent the same or different arylene groups. X, k, j, and n are the same as in the case of the formula (1).

In formula (3), R ₉ and R ₁₀ represent a substituted or unsubstituted aryl group, and Ar ₄ , Ar ₅ and Ar ₆ represent the same or different arylene groups. X, k, j, and n are the same as in the case of the formula (1).

In formula (4), R ₁₁ and R ₁₂ represent a substituted or unsubstituted aryl group, and Ar ₇ , Ar ₈ and Ar ₉ represent the same or different arylene groups. X, k, j, and n are the same as in the case of the formula (1).

In Formula (5), R ₁₃ and R ₁₄ are substituted or unsubstituted aryl groups, Ar ₁₀ , Ar ₁₁ and Ar ₁₂ are the same or different arylene groups, X ₁ and X ₂ are substituted or unsubstituted ethylene groups, or A substituted or unsubstituted vinylene group is represented. X, k, j, and n are the same as in the case of the formula (1).

In the formula (6), R ₁₅ , R ₁₆ , R ₁₇ and R ₁₈ are substituted or unsubstituted aryl groups, Ar ₁₃ , Ar ₁₄ , Ar ₁₅ and Ar ₁₆ are the same or different arylene groups, Y ₁ , Y ₂ , Y ₃ represents a single bond, a substituted or unsubstituted alkylene group, a substituted or unsubstituted cycloalkylene group, a substituted or unsubstituted alkylene ether group, an oxygen atom, a sulfur atom, or a vinylene group, which may be the same or different. Good. X, k, j, and n are the same as in the case of the formula (1).

In formula (7), R ₁₉ and R ₂₀ represent a hydrogen atom or a substituted or unsubstituted aryl group, and R ₁₉ and R ₂₀ may form a ring. Ar ₁₇ , Ar ₁₈ and Ar ₁₉ represent the same or different arylene groups. X, k, j, and n are the same as in the case of the formula (1).

In formula (8), R ₂₁ represents a substituted or unsubstituted aryl group, and Ar ₂₀ , Ar ₂₁ , Ar ₂₂ , Ar ₂₃ represent the same or different arylene groups. X, k, j, and n are the same as in the case of the formula (1).

In formula (9), R ₂₂ , R ₂₃ , R ₂₄ and R ₂₅ represent a substituted or unsubstituted aryl group, and Ar ₂₄ , Ar ₂₅ , Ar ₂₆ , Ar ₂₇ and Ar ₂₈ represent the same or different arylene groups. X, k, j, and n are the same as in the case of the formula (1).

In formula (10), R ₂₆ and R ₂₇ represent a substituted or unsubstituted aryl group, and Ar ₂₉ , Ar ₃₀ , and Ar ₃₁ represent the same or different arylene groups. X, k, j, and n are the same as in the case of the formula (1).

  The surface layer is a surface layer containing at least a binder resin and a filler. In addition to this, the surface layer coating liquid may contain various plasticizers (for the purpose of stress relaxation and adhesion improvement) and leveling as necessary. An additive such as an agent and a low molecular charge transport material can be contained. As these additives, known additives can be used, and as plasticizers, those used in general resins such as dibutyl phthalate and dioctyl phthalate can be used, and the amount used is the total solid content of the coating liquid. To 20 parts by mass or less, preferably 10 parts by mass or less. As leveling agents, silicone oils such as dimethyl silicone oil and methylphenyl silicone oil, polymers or oligomers having a perfluoroalkyl group in the side chain can be used, and the amount used is based on the total solid content of the coating liquid. On the other hand, 3 parts by mass or less is appropriate.

  The surface layer is formed by applying and drying a coating solution containing at least the above-described binder resin and filler on a photosensitive layer described later. The coating liquid may contain the aforementioned charge transport material for the purpose of imparting a charge transport function to the surface layer.

  Since most of the constituent components of the surface layer are solid at normal temperature and normal pressure, a solvent having a high affinity with the constituent components is used in preparing the coating liquid. The solvent used here is not particularly limited as long as it is usually used. For example, alcohols such as methanol, ethanol, propanol and butanol, ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone and cyclohexanone, esters such as ethyl acetate and butyl acetate, ethers such as tetrahydrofuran, dioxane and propyl ether, dichloromethane And halogen series such as dichloroethane, trichloroethane and chlorobenzene, aromatic series such as benzene, toluene and xylene, and cellosolv series such as methyl cellosolve, ethyl cellosolve and cellosolve acetate. These solvents may be used alone or in combination of two or more.

  The filler can be dispersed in the coating liquid by a ball mill, a sand mill, a KD mill, a three roll mill, a pressure homogenizer, ultrasonic dispersion, or the like. If the filler is not sufficiently dispersed, an inorganic filler having a large particle diameter is found on the surface of the formed surface layer. As a result, the cleaning member or the like is damaged, resulting in poor cleaning. For this reason, when dispersing an inorganic filler by said method, it is preferable that the average particle diameter of an inorganic filler shall be less than 1 micrometer. In addition, when the inorganic filler is pulverized more than necessary, re-aggregation of the inorganic filler occurs in the inorganic filler dispersion step, and as a result, extremely large average particle diameters are often generated. For this reason, the average particle size of the inorganic filler used is preferably 0.1 μm or more. By setting the average particle size of the mixed filler to about 0.3 μm to 0.6 μm, high durability of the electrophotographic photosensitive member can be enjoyed.

  The coating method used for forming the surface layer is not particularly limited as long as it is a commonly used coating method. A coating method may be appropriately selected depending on the viscosity of the coating liquid, the desired thickness of the surface layer, and the like. Examples include dip coating, spray coating, bead coating, ring coating, and the like.

  The thickness of the surface layer is preferably 1 μm to 15 μm, more preferably 3 μm to 10 μm from the viewpoint of protecting the photosensitive layer. When the thickness of the surface layer is small, not only the photosensitive layer cannot be protected from mechanical wear due to a contact member to the photosensitive member, proximity discharge by a charger, etc., but also it becomes difficult to level during film formation. The film surface may be distorted. On the other hand, when the thickness of the surface layer is large, the entire photoreceptor layer becomes thick, and the reproducibility of the image due to the diffusion of electric charges is not preferable.

  The film formed by the above means needs to be heated by some means from the viewpoint of electrophotographic characteristics and film viscosity to remove the solvent as described above from the film. As the thermal energy, air, nitrogen or other gas, steam, various heat media, infrared rays, or electromagnetic waves can be used, and heating is performed from the coating surface side or the support side. The heating temperature is preferably 100 ° C. or higher and 170 ° C. or lower. When the temperature is lower than 100 ° C., it is confirmed that the organic solvent in the film cannot be sufficiently removed, and the electrophotographic characteristics are deteriorated and the wear durability is reduced. On the other hand, when the treatment is performed at a temperature higher than 170 ° C., a surface-like defect or crack may occur on the surface, or peeling may occur at the interface with the adjacent layer. Further, when the volatile component in the photosensitive layer is sprayed to the outside, it is not preferable because desired electrical characteristics may not be obtained.

In order to prevent delamination due to poor adhesion between the surface layer and the photosensitive layer, an adhesive layer may be provided between the two layers as necessary.
As the adhesive layer, a radical polymerizable compound or a non-crosslinked polymer compound may be used.
There is no restriction | limiting in particular as said radically polymerizable compound, According to the objective, it can select suitably.
The non-crosslinked polymer compound is not particularly limited and may be appropriately selected depending on the intended purpose. For example, polyamide, polyurethane, epoxy resin, polyketone, polycarbonate, silicone resin, acrylic resin, polyvinyl butyral, polyvinyl formal , Polyvinyl ketone, polystyrene, poly-N-vinyl carbazole, polyacrylamide, polyvinyl benzal, polyester, phenoxy resin, vinyl chloride-vinyl acetate copolymer, polyvinyl acetate, polyphenylene oxide, polyvinyl pyridine, cellulosic resin, casein, Examples thereof include polyvinyl alcohol and polyvinyl pyrrolidone. In addition, the radical polymerizable compound and the non-crosslinked polymer compound may be used either alone or as a mixture of two or more. Furthermore, a radical polymerizable compound and a non-crosslinked polymer compound may be used in combination as long as sufficient adhesiveness is obtained. The charge transport material used in the present invention may be used or used in combination. Moreover, if it aims at improving adhesiveness, you may use an additive suitably.
The adhesive layer is formed by applying a coating solution prepared by dissolving or dispersing a compound formulated in a predetermined formulation in a solvent such as tetrahydrofuran, dioxane, dichloroethane, or cyclohexane by a dip coating method, spray coating, bead coating, ring coating, or the like. Can be formed.
The thickness of the adhesive layer is preferably 0.1 μm to 5 μm, and more preferably 0.1 μm to 3 μm.

<Laminated photosensitive layer>
In the laminated photosensitive layer, the charge generation function and the charge transport function are independent layers. Therefore, the layer structure of the photosensitive layer is a structure in which at least a charge generation layer and a charge transport layer are stacked on a support. . The order of stacking is not particularly limited, but many charge generation materials have poor chemical stability, and the charge generation efficiency decreases when exposed to acidic gases such as discharge products around the charger in the electrophotographic imaging process. Cause. For this reason, a charge transport layer is preferably laminated on the charge generation layer.

-Charge generation layer-
The charge generation layer contains a charge generation material having a charge generation function as a main component, and a binder resin can be used in combination as necessary.

As the charge generation material, inorganic materials and organic materials can be used.
The inorganic material is not particularly limited and may be appropriately selected depending on the purpose. For example, crystalline selenium, amorphous selenium, selenium-tellurium, selenium-tellurium-halogen, selenium-arsenic compound, amorphous Silicon etc. are mentioned. As amorphous silicon, dangling bonds terminated with hydrogen atoms or halogen atoms, or doped with boron atoms, phosphorus atoms or the like are preferably used.
The organic material is not particularly limited and may be appropriately selected from known materials according to the purpose. For example, phthalocyanine pigments such as metal phthalocyanine and metal-free phthalocyanine, azulenium salt pigments, squaric acid Methine pigment, azo pigment having carbazole skeleton, azo pigment having triarylamine skeleton, azo pigment having diphenylamine skeleton, azo pigment having dibenzothiophene skeleton, azo pigment having fluorenone skeleton, azo pigment having oxadiazole skeleton, Azo pigments having a bis stilbene skeleton, azo pigments having a distyryl oxadiazole skeleton, azo pigments having a distyryl carbazole skeleton, perylene pigments, anthraquinone or polycyclic quinone pigments, quinoneimine pigments, diphenylmethane and triphenyl Enirumetan pigments, benzoquinone and naphthoquinone pigments, cyanine and azomethine pigments, indigoid pigments, and bisbenzimidazole pigments. These charge generation materials can be used alone or as a mixture of two or more.

The binder resin is not particularly limited and may be appropriately selected depending on the intended purpose.For example, polyamide, polyurethane, epoxy resin, polyketone, polycarbonate, silicone resin, acrylic resin, polyvinyl butyral, polyvinyl formal, polyvinyl ketone, Polystyrene, poly-N-vinylcarbazole, polyacrylamide, polyvinyl benzal, polyester, phenoxy resin, vinyl chloride-vinyl acetate copolymer, polyvinyl acetate, polyphenylene oxide, polyvinyl pyridine, cellulosic resin, casein, polyvinyl alcohol, polyvinyl Examples include pyrrolidone and the like. These binder resins can be used alone or as a mixture of two or more.
The content of the binder resin is preferably 500 parts by mass or less, more preferably 10 parts by mass to 300 parts by mass with respect to 100 parts by mass of the charge generation material. The binder resin may be added before or after dispersion.

Examples of the method for forming the charge generation layer include a vacuum thin film preparation method and a casting method from a solution dispersion system. As the former method, a vacuum deposition method, a glow discharge decomposition method, an ion plating method, a sputtering method, a reactive sputtering method, a CVD method, or the like is used, and the above-described inorganic materials and organic materials can be satisfactorily formed. In addition, in order to provide the charge generation layer by the latter casting method, the inorganic or organic charge generation material described above, together with a binder resin, if necessary, tetrahydrofuran, dioxane, dioxolane, toluene, dichloromethane, monochlorobenzene, dichloroethane, cyclohexanone, cyclohexane. It can be formed by dispersing with a ball mill, attritor, sand mill, bead mill or the like using a solvent such as pentanone, anisole, xylene, methyl ethyl ketone, acetone, ethyl acetate, butyl acetate, etc., and applying the solution after appropriately diluting the dispersion. Moreover, leveling agents, such as a dimethyl silicone oil and a methylphenyl silicone oil, can be added as needed. The application can be performed by dip coating, spray coating, bead coating, ring coating, or the like.
The thickness of the charge generation layer is preferably 0.01 μm to 5 μm, more preferably 0.05 μm to 2 μm.

-Charge transport layer-
The charge transport layer is a layer having a charge transport function, and is a layer mainly composed of a charge transport material and a binder resin.

Examples of the charge transport material include a hole transport material and an electron transport material as described in the section of the surface layer. A similar material can be used in the charge transport layer.
Examples of the binder resin include those described in the section of the surface layer.
The transport material and the binder resin can be appropriately selected and used so as to satisfy the function of the charge transport layer.
The content of the charge transport material is preferably 20 parts by mass to 300 parts by mass, and more preferably 40 parts by mass to 150 parts by mass with respect to 100 parts by mass of the binder resin. However, when a polymer charge transport material is used, it may be used alone or in combination with a binder resin.

The charge transport layer can be formed by dissolving or dispersing the charge transport material and the binder resin in an appropriate solvent, applying the solution, and drying.
Examples of the solvent include tetrahydrofuran, dioxane, toluene, dichloromethane, monochlorobenzene, dichloroethane, cyclohexanone, methyl ethyl ketone, and acetone. These may be used alone or in combination of two or more.
Furthermore, a plasticizer and a leveling agent can be added as necessary. As the plasticizer used for the charge transport layer, those used as plasticizers for general resins such as dibutyl phthalate and dioctyl phthalate can be used as they are, and the amount used is 30 masses with respect to 100 mass parts of the binder resin. Part or less is preferred. Examples of leveling agents that can be used in the charge transport layer include silicone oils such as dimethyl silicone oil and methylphenyl silicone oil, and polymers or oligomers having a perfluoroalkyl group in the side chain. 1 mass part or less is preferable with respect to a mass part.
The thickness of the charge transport layer is preferably 30 μm or less, more preferably 25 μm or less, from the viewpoint of resolution and responsiveness. The lower limit varies depending on the system to be used (particularly charging potential), but is preferably 5 μm or more.

<Single layer type photosensitive layer>
The photosensitive layer having a single layer structure is a layer having a charge generation function and a charge transport function at the same time. The photosensitive layer can be formed by dissolving or dispersing a charge generating substance, a charge transporting substance, and a binder resin in a suitable solvent, and applying and drying them. Moreover, a plasticizer, a leveling agent, antioxidant, etc. can also be added as needed.
As the binder resin, in addition to the binder resin previously mentioned in the charge transport layer, the binder resin mentioned in the charge generation layer may be mixed and used. Polymer charge transport materials can also be used favorably. The amount of the charge generation material with respect to 100 parts by mass of the binder resin is preferably 5 parts by mass to 40 parts by mass, and the amount of the charge transport material is preferably 190 parts by mass or less, and more preferably 50 parts by mass to 150 parts by mass.
The single-layer type photosensitive layer is a dip coating method, spray coating, a coating solution in which a charge generating material, a binder resin and a charge transport material are dispersed together with a dispersing machine using a solvent such as tetrahydrofuran, dioxane, dichloroethane, and cyclohexane. It can be formed by coating with bead coat or ring coat.
The thickness of the single-layer type photosensitive layer is preferably 5 μm to 25 μm.

  In the electrophotographic photoreceptor of the present invention, the surface layer, the charge transport layer, the charge generation layer, and the single layer are used for the purpose of preventing the decrease in sensitivity and the increase in residual potential, in order to improve environmental resistance. An antioxidant, a plasticizer, a lubricant, an ultraviolet absorber and a leveling agent can be added to each layer such as a type photosensitive layer. In addition, a dispersion stabilizer can be added to improve filler dispersibility in the coating liquid.

Examples of the antioxidant include phenolic compounds, paraphenylenediamines, hydroquinones, organic sulfur compounds, and organic phosphorus compounds. These may be used individually by 1 type and may use 2 or more types together.
Examples of the phenol compound include 2,6-di-t-butyl-p-cresol, butylated hydroxyanisole, 2,6-di-t-butyl-4-ethylphenol, stearyl-β- (3, 5-di-t-butyl-4-hydroxyphenyl) propionate, 2,2'-methylene-bis- (4-methyl-6-t-butylphenol), 2,2'-methylene-bis- (4-ethyl- 6-t-butylphenol), 4,4′-thiobis- (3-methyl-6-tert-butylphenol), 4,4′-butylidenebis- (3-methyl-6-tert-butylphenol), 1,1,3 -Tris- (2-methyl-4-hydroxy-5-t-butylphenyl) butane, 1,3,5-trimethyl-2,4,6-tris (3,5-di-t-butyl-4-hydroxy Ben ) Benzene, tetrakis- [methylene-3- (3 ′, 5′-di-t-butyl-4′-hydroxyphenyl) propionate] methane, bis [3,3′-bis (4′-hydroxy-3 ′) -T-butylphenyl) butyric acid] cricol ester, tocopherols, and the like.
Examples of the paraphenylenediamines include N-phenyl-N′-isopropyl-p-phenylenediamine, N, N′-di-sec-butyl-p-phenylenediamine, N-phenyl-N-sec-butyl- p-phenylenediamine, N, N′-di-isopropyl-p-phenylenediamine, N, N′-dimethyl-N, N′-di-t-butyl-p-phenylenediamine, and the like.
Examples of the hydroquinones include 2,5-di-t-octyl hydroquinone, 2,6-didodecyl hydroquinone, 2-dodecyl hydroquinone, 2-dodecyl-5-chlorohydroquinone, 2-t-octyl-5-methyl. And hydroquinone and 2- (2-octadecenyl) -5-methylhydroquinone.
Examples of the organic sulfur compounds include dilauryl-3,3′-thiodipropionate, distearyl-3,3′-thiodipropionate, ditetradecyl-3,3′-thiodipropionate, and the like. It is done.
Examples of the organic phosphorus compounds include triphenylphosphine, tri (nonylphenyl) phosphine, tri (dinonylphenyl) phosphine, tricresylphosphine, tri (2,4-dibutylphenoxy) phosphine, and the like.
In addition, these compounds are known as antioxidants, such as rubber | gum, a plastic, and fats and oils, and a commercial item can be obtained easily.
There is no restriction | limiting in particular in the addition amount of the said antioxidant, According to the objective, it can select suitably, 0.01 mass part-10 mass parts are preferable with respect to the total mass of the layer to add.

Examples of the plasticizer include phosphate ester plasticizers, phthalate ester plasticizers, aromatic carboxylic acid ester plasticizers, aliphatic dibasic acid ester plasticizers, fatty acid ester derivatives, and oxyacid ester plasticizers. Agents, epoxy plasticizers, dihydric alcohol ester plasticizers, chlorine-containing plasticizers, polyester plasticizers, sulfonic acid derivatives, citric acid derivatives, and other plasticizers. These may be used individually by 1 type and may use 2 or more types together.
Examples of the phosphate ester plasticizer include triphenyl phosphate, tricresyl phosphate, trioctyl phosphate, octyl diphenyl phosphate, trichloroethyl phosphate, cresyl diphenyl phosphate, tributyl phosphate, tri-2 phosphate. -Ethylhexyl, triphenyl phosphate and the like.
Examples of the phthalate ester plasticizer include dimethyl phthalate, diethyl phthalate, diisobutyl phthalate, dibutyl phthalate, diheptyl phthalate, di-2-ethylhexyl phthalate, diisooctyl phthalate, and di-n-phthalate. Octyl, dinonyl phthalate, diisononyl phthalate, diisodecyl phthalate, diundecyl phthalate, ditridecyl phthalate, dicyclohexyl phthalate, butyl benzyl phthalate, butyl lauryl phthalate, methyl oleyl phthalate, octyl decyl phthalate, dibutyl fumarate, And dioctyl fumarate.
Examples of the aromatic carboxylic acid ester plasticizer include trioctyl trimellitic acid, tri-n-octyl trimellitic acid, octyl oxybenzoate, and the like.
Examples of the aliphatic dibasic acid ester plasticizer include dibutyl adipate, di-n-hexyl adipate, di-2-ethylhexyl adipate, di-n-octyl adipate, and adipic acid n-octyl- n-decyl, diisodecyl adipate, dicapryl adipate, di-2-ethylhexyl azelate, dimethyl sebacate, diethyl sebacate, dibutyl sebacate, di-n-octyl sebacate, di-2-ethylhexyl sebacate, sebacic acid And di-2-ethoxyethyl, dioctyl succinate, diisodecyl succinate, dioctyl tetrahydrophthalate, di-n-octyl tetrahydrophthalate, and the like.
Examples of the fatty acid ester derivatives include butyl oleate, glycerin monooleate, methyl acetylricinoleate, pentaerythritol ester, dipentaerythritol hexaester, triacetin, tributyrin, and the like.
Examples of the oxyester plasticizer include methyl acetyl ricinoleate, butyl acetyl ricinoleate, butyl phthalyl butyl glycolate, and tributyl acetyl citrate.
Examples of the epoxy plasticizer include epoxidized soybean oil, epoxidized linseed oil, butyl epoxy stearate, decyl epoxy stearate, octyl epoxy stearate, benzyl epoxy stearate, dioctyl epoxy hexahydrophthalate, epoxy hexahydrophthal And didecyl acid.
Examples of the dihydric alcohol ester plasticizer include diethylene glycol dibenzoate and triethylene glycol di-2-ethylbutyrate.
Examples of the chlorine-containing plasticizer include chlorinated paraffin, chlorinated diphenyl, chlorinated fatty acid methyl, methoxy chlorinated fatty acid methyl, and the like.
Examples of the polyester plasticizer include polypropylene adipate, polypropylene sebacate, polyester, acetylated polyester, and the like.
Examples of the sulfonic acid derivative include p-toluenesulfonamide, o-toluenesulfonamide, p-toluenesulfoneethylamide, o-toluenesulfoneethylamide, toluenesulfone-N-ethylamide, p-toluenesulfone-N-cyclohexyl. Amide, and the like.
Examples of the citric acid derivative include triethyl citrate, triethyl acetyl citrate, tributyl citrate, tributyl acetyl citrate, tri-2-ethylhexyl acetyl citrate, and acetyl citrate-n-octyldecyl.
Examples of the other plasticizers include terphenyl, partially hydrogenated terphenyl, camphor, 2-nitrodiphenyl, dinonylnaphthalene, and methyl abietic acid.
The addition amount of the plasticizer in the present invention is not particularly limited as long as a plasticizing effect can be obtained, and can be appropriately selected according to the purpose. 10 parts by mass.

Examples of the lubricant include hydrocarbon compounds, fatty acid compounds, fatty acid amide compounds, ester compounds, alcohol compounds, metal soaps, natural waxes, and other lubricants. These may be used individually by 1 type and may use 2 or more types together.
Examples of the hydrocarbon compound include liquid paraffin, paraffin wax, microwax, and low-polymerized polyethylene.
Examples of the fatty acid compounds include lauric acid, myristic acid, palmitic acid, stearic acid, arachidic acid, and behenic acid.
Examples of the fatty acid amide compounds include stearyl amide, palmityl amide, olein amide, methylene bis-stearamide, ethylene bis-stearamide, and the like.
Examples of the ester compounds include lower alcohol esters of fatty acids, polyhydric alcohol esters of fatty acids, and fatty acid polyglycol esters.
Examples of the alcohol compound include cetyl alcohol, stearyl alcohol, ethylene glycol, polyethylene glycol, and polyglycerol.
Examples of the metal soap include lead stearate, cadmium stearate, barium stearate, calcium stearate, zinc stearate, magnesium stearate, and the like.
Examples of the natural wax include carnauba wax, candelilla wax, beeswax, whale wax, ibota wax, and montan wax.
Examples of the other lubricants include silicone compounds and fluorine compounds.
The addition amount of the lubricant in the present invention is not particularly limited as long as the effect of the lubricant can be obtained, and can be appropriately selected according to the purpose. 10 parts by mass.

Examples of the ultraviolet absorber include benzophenone compounds, salicylate compounds, benzotriazole compounds, cyanoacrylate compounds, quencher (metal complex) compounds, HALS (hindered amine) compounds, and the like. These may be used individually by 1 type and may use 2 or more types together.
Examples of the benzophenone compounds include 2-hydroxybenzophenone, 2,4-dihydroxybenzophenone, 2,2 ′, 4-trihydroxybenzophenone, 2,2 ′, 4,4′-tetrahydroxybenzophenone, and 2,2 ′. -Dihydroxy 4-methoxybenzophenone, and the like.
Examples of the salicylate compounds include phenyl salicylate, 2,4 di-t-butylphenyl 3,5-di-t-butyl 4-hydroxybenzoate, and the like.
Examples of the benzotriazole-based compound include (2′-hydroxyphenyl) benzotriazole, (2′-hydroxy5′-methylphenyl) benzotriazole, (2′-hydroxy5′-methylphenyl) benzotriazole, (2 '-Hydroxy 3'-tertiarybutyl 5'-methylphenyl) 5-chlorobenzotriazole, and the like.
Examples of the cyanoacrylate compound include ethyl-2-cyano-3,3-diphenyl acrylate, methyl 2-carbomethoxy 3 (paramethoxy) acrylate, and the like.
Examples of the quencher (metal complex salt) compound include nickel (2,2′thiobis (4-t-octyl) phenolate) normal butylamine, nickel dibutyldithiocarbamate, nickel dibutyldithiocarbamate, cobalt dicyclohexyldithiophosphate, and the like. Is mentioned.
Examples of the HALS (hindered amine) compound include bis (2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis (1,2,2,6,6-pentamethyl-4-piperidyl) sebacate, 1- [2- [3- (3,5-Di-tert-butyl-4-hydroxyphenyl) propionyloxy] ethyl] -4- [3- (3,5-di-tert-butyl-4-hydroxyphenyl) ) Propionyloxy] -2,2,6,6-tetramethylpyridine, 8-benzyl-7,7,9,9-tetramethyl-3-octyl-1,3,8-triazaspiro [4,5] undecane- 2,4-dione, 4-benzoyloxy-2,2,6,6-tetramethylpiperidine, and the like.
The addition amount of the ultraviolet absorber in the present invention is not particularly limited as long as the effect of the ultraviolet absorber can be obtained, and can be appropriately selected according to the purpose. 01 parts by mass to 10 parts by mass.

<Support>
The support is not particularly limited as long as it has a volume resistance of 10 ¹⁰ Ω · cm or less, and can be appropriately selected according to the purpose. For example, aluminum, nickel, chromium, nichrome, copper Metals such as gold, silver and platinum; metal oxides such as tin oxide and indium oxide deposited or sputtered on a film or cylindrical plastic, paper, or aluminum, aluminum alloy, nickel, stainless steel, etc. And a tube subjected to surface treatment such as cutting, super-finishing, polishing, etc. can be used. Further, an endless nickel belt and an endless stainless steel belt disclosed in JP-A-52-36016 can also be used as a support.

In addition, what coated and disperse | distributed conductive powder to the appropriate binder resin on the said support body can also be used as a support body in this invention.
Examples of the conductive powder include carbon black, acetylene black, metal powder such as aluminum, nickel, iron, nichrome, copper, zinc and silver, or metal oxide powder such as conductive tin oxide and ITO. Etc. The binder resin used at the same time includes polystyrene, styrene-acrylonitrile copolymer, styrene-butadiene copolymer, styrene-maleic anhydride copolymer, polyester, polyvinyl chloride, vinyl chloride-vinyl acetate copolymer, Polyvinyl acetate, polyvinylidene chloride, polyarylate resin, phenoxy resin, polycarbonate, cellulose acetate resin, ethyl cellulose resin, polyvinyl butyral, polyvinyl formal, polyvinyl toluene, poly-N-vinylcarbazole, acrylic resin, silicone resin, epoxy resin, melamine Examples thereof include thermoplastic resins such as resins, urethane resins, phenol resins, and alkyd resins, thermally crosslinkable resins, and photocrosslinkable resins.
The conductive layer can be provided by dispersing and applying these conductive powder and binder resin in a suitable solvent such as tetrahydrofuran, dichloromethane, methyl ethyl ketone, and toluene.
Furthermore, a heat-shrinkable tube in which the conductive powder is contained in a material such as polyvinyl chloride, polypropylene, polyester, polystyrene, polyvinylidene chloride, polyethylene, chlorinated rubber, and polytetrafluoroethylene-based fluororesin on a suitable cylindrical substrate. Those provided with a conductive layer can be used favorably as the support of the present invention.

  As will be described later, a highly coherent laser may be used to form a latent image in the electrophotographic process. As described above, the support is often made of a metal material, many of which are considered to have high surface reflectance. When an electrophotographic photosensitive member is produced by applying the inorganic semiconductor material of the present invention on this support, there is a concern that writing light and reflected light from the support cause interference and image defects may occur. . For this reason, when the reflectance of a support body is high, it is preferable to give an unevenness | corrugation to the surface of a support body and to reduce a reflectance. Further, projections or the like that are potentially present on the raw tube may cause image defects when the photosensitive layer is laminated. By roughening this to an appropriate surface roughness, a smooth support surface without protrusions can be provided. As the surface irregularities, arithmetic ten-point average surface roughness (Rz) measured by the method described in JIS B0601-1982 was used as a representative characteristic value.

  As a method for measuring the surface roughness (Rz), for example, Surfcom 1400D (manufactured by Tokyo Seimitsu Co., Ltd.) was used, and the surface roughness (Rz) was measured with respect to an evaluation length of 2.5 mm and a reference length of 0.5 mm. Measurement points were 80 mm from both ends of the drum in the axial direction, 3 points in the center of the drum, and 4 types of 90 degrees in the circumferential direction. A total of 12 points were measured, and the average value was defined as the surface roughness (Rz) of the drum. The surface roughness (Rz) is preferably 0.6 μm or more. If Rz is smaller than this, moire due to writing light is likely to occur, which is not preferable. Further, even if Rz is large, there is no significant problem in use. However, if Rz is too large, it is difficult to form the intermediate layer uniformly, so care must be taken. From this viewpoint, the surface roughness (Rz) of the support is preferably 3.0 μm or less.

Examples of the roughening method include honing and centerless polishing. The honing process is preferably used because it is inexpensive and the surface roughness can be easily adjusted. There are dry and wet processing methods for the honing process, and any of them may be used. Wet (liquid) honing is a method in which a powdery abrasive (abrasive grain) is suspended in a liquid such as water and sprayed onto the surface of the support at high speed to roughen the surface. The pressure, speed, amount, type, shape, size, hardness, specific gravity or suspension concentration of the abrasive can be controlled. Similarly, the dry honing process is a method in which an abrasive is sprayed onto the support surface with air at a high speed to roughen the surface, and the surface roughness can be controlled in the same manner as the wet honing process. Examples of the abrasive used in these wet or dry honing processes include particles such as silicon carbide, alumina, zirconia, stainless steel, iron, glass beads, and plastic shots.
However, in liquid honing using dry sandblasting or amorphous alumina abrasive grains, the abrasive grains may pierce the surface of the support, and when an electrophotographic photosensitive member is produced, black spots on white images in the reversal development system, normal rotation It appears as white spots on a black image in the development system. In liquid honing using glass beads, it is difficult to control the roughness because the glass breaks immediately and pierces the support surface. Therefore, after roughening the support by liquid honing using spherical alumina abrasive grains or stainless abrasive grains as an abrasive, an undercoat layer and a photosensitive layer are formed to produce an electrophotographic photoreceptor. It is common. Further, in the roughening treatment of the support, an interference fringe prevention function from the viewpoint of processing time, amount of abrasive grains used, amount of energy consumption, and ease of removing residual abrasive grains from the roughened substrate. It is preferable to make the treatment conditions as mild as possible within the range satisfying the above and to keep the surface roughness (Rz) small.

(Image forming method and image forming apparatus)
The image forming apparatus of the present invention comprises at least an electrophotographic photosensitive member, a charging unit, an exposure unit, a developing unit, and a transfer unit, and other units appropriately selected as necessary, for example, The image forming apparatus includes a fixing unit, a cleaning unit, a charge eliminating unit, a recycling unit, a control unit, and the like.
The electrophotographic photoreceptor is the electrophotographic photoreceptor of the present invention.
The image forming method used in the present invention includes at least a charging step, an exposure step, a development step, and a transfer step, and further other steps appropriately selected as necessary, for example, a fixing step, a cleaning step, and a static elimination step. Process, recycling process, control process, etc.

  The image forming method used in the present invention can be preferably implemented by the image forming apparatus of the present invention, the charging step can be performed by the charging unit, and the exposure step can be performed by the exposing unit. The developing step can be performed by the developing unit, the transferring step can be performed by the transferring unit, the fixing step can be performed by the fixing unit, and the cleaning step can be performed by the cleaning unit. The other steps can be performed by the other means.

-Charging step and charging means-
The charging step is a step of charging the surface of the electrophotographic photosensitive member, and is performed by the charging unit.
The charging means is not particularly limited as long as it can uniformly apply a voltage to the surface of the electrophotographic photosensitive member, and can be appropriately selected depending on the purpose. A non-contact charging means for charging the photoconductor in a non-contact manner is used.
As the non-contact charging means, for example, a non-contact charger using a corona discharge, a needle electrode device, a solid discharge element; conductive or semiconductive disposed with a minute gap with respect to the electrophotographic photosensitive member And a charging roller. Among these, corona discharge is particularly preferable.

The corona discharge is a non-contact charging method that gives positive or negative ions generated by corona discharge in the air to the surface of the electrophotographic photosensitive member, and has a characteristic of giving a certain amount of charge to the electrophotographic photosensitive member. There are a charger and a scorotron charger having a characteristic of giving a constant potential.
The coroton charger is composed of a casing electrode that occupies a half space around the discharge wire, and a discharge wire placed almost at the center thereof.
The scorotron charger is obtained by adding a grid electrode to the corotron charger, and the grid electrode is provided at a position 1.0 mm to 2.0 mm away from the surface of the electrophotographic photosensitive member.

-Exposure process and exposure means-
The exposure can be performed, for example, by exposing the surface of the electrophotographic photosensitive member imagewise using the exposure unit.
The optical system in the exposure is roughly classified into an analog optical system and a digital optical system. The analog optical system is an optical system that directly projects an original onto an electrophotographic photosensitive member by an optical system, and the digital optical system receives image information as an electrical signal, converts this into an optical signal, and converts it into an electrophotographic image. It is an optical system that exposes a photoreceptor to form an image.
The exposure unit is not particularly limited as long as the surface of the electrophotographic photosensitive member charged by the charging unit can be exposed like an image to be formed, and can be appropriately selected according to the purpose. However, various exposure devices such as a copying optical system, a rod lens array system, a laser optical system, a liquid crystal shutter optical system, and an LED optical system can be used.
In the present invention, an optical backside system that performs imagewise exposure from the backside of the electrophotographic photosensitive member may be employed.

-Development process and development means-
The developing step is a step of developing the electrostatic latent image using a toner or a developer to form a visible image.
The visible image can be formed, for example, by developing the electrostatic latent image using the toner or the developer, and can be performed by the developing unit.
The developing unit is not particularly limited as long as it can be developed using, for example, the toner or the developer, and can be appropriately selected from known ones. For example, the toner or developer is accommodated. Preferred examples include those having at least a developing unit capable of bringing the toner or developer into contact or non-contact with the electrostatic latent image.

  The developing unit may be a dry developing type, a wet developing type, a single color developing unit, or a multi-color developing unit. For example, a toner having a stirrer for charging the toner or the developer by frictional stirring and a rotatable magnet roller is preferable.

  In the developing device, for example, the toner and the carrier are mixed and agitated, and the toner is charged by friction at that time, and held on the surface of the rotating magnet roller in a raised state to form a magnetic brush. . Since the magnet roller is disposed in the vicinity of the electrophotographic photosensitive member (photosensitive member), a part of the toner constituting the magnetic brush formed on the surface of the magnet roller is caused by an electric attractive force. It moves to the surface of the electrophotographic photoreceptor. As a result, the electrostatic latent image is developed with the toner, and a visible image is formed with the toner on the surface of the electrophotographic photosensitive member.

  The developer accommodated in the developing device is a developer containing the toner, but the developer may be a one-component developer or a two-component developer.

-Transfer process and transfer means-
The transfer step is a step of transferring the visible image onto a recording medium. After the primary transfer of the visible image onto the intermediate transfer member using an intermediate transfer member, the visible image is transferred onto the recording medium. A primary transfer step of forming a composite transfer image by transferring a visible image onto an intermediate transfer body using two or more colors, preferably a full color toner, as the toner, and a composite transfer image; A mode including a secondary transfer step of transferring the transfer image onto the recording medium is more preferable.
The transfer can be performed, for example, by charging the electrophotographic photosensitive member with the transfer charger using the visible image, and can be performed by the transfer unit. The transfer means includes a primary transfer means for transferring a visible image onto an intermediate transfer member to form a composite transfer image, and a secondary transfer means for transferring the composite transfer image onto a recording medium. Embodiments are preferred.
The intermediate transfer member is not particularly limited and may be appropriately selected from known transfer members according to the purpose. For example, a transfer belt and the like are preferable.

The transfer unit (the primary transfer unit and the secondary transfer unit) includes at least a transfer unit that peels and charges the visible image formed on the electrophotographic photosensitive member toward the recording medium. preferable. There may be one transfer means or two or more transfer means. Examples of the transfer device include a corona transfer device using corona discharge, a transfer belt, a transfer roller, a pressure transfer roller, and an adhesive transfer device.
The recording medium is typically plain paper, but is not particularly limited as long as it can transfer an unfixed image after development, and can be appropriately selected according to the purpose. PET for OHP A base or the like can also be used.

-Fixing process and fixing means-
The fixing step is a step of fixing the visible image transferred to the recording medium using a fixing device, and may be performed each time the toner of each color is transferred to the recording medium, or for the toner of each color. You may perform this simultaneously in the state which laminated | stacked this.

The fixing unit is not particularly limited and may be appropriately selected depending on the intended purpose. A fixing unit and a heat source for heating the fixing member are used.
Examples of the fixing member include a combination of an endless belt and a roller, a combination of a roller and a roller, etc., but the warm-up time can be shortened, and in terms of realizing energy saving, A combination of an endless belt and a roller having a small heat capacity is preferable in terms of expansion of the fixable width.

-Cleaning process and cleaning means-
The cleaning step is a step of removing the toner remaining on the electrophotographic photosensitive member, and can be suitably performed by a cleaning unit. In addition, it is also possible to employ a method in which the charge of the residual toner is made uniform by the rubbing member and collected by the developing roller without using the cleaning means.
The cleaning means is not particularly limited as long as it can remove the electrophotographic toner remaining on the electrophotographic photosensitive member, and can be appropriately selected from known cleaners. For example, a magnetic brush cleaner Suitable examples include electrostatic brush cleaners, magnetic roller cleaners, blade cleaners, brush cleaners, web cleaners, and the like.

--- Static elimination process and static elimination means-
The neutralization step is a step of performing neutralization by applying a neutralization bias to the electrophotographic photosensitive member, and can be suitably performed by a neutralization unit.
The neutralizing means is not particularly limited and may be appropriately selected from known neutralizers as long as it can apply a neutralizing bias to the electrophotographic photosensitive member. For example, a neutralizing lamp is preferably used. Can be mentioned.

--Recycling process and recycling means--
The recycling step is a step of recycling the toner removed by the cleaning step to the developing unit, and can be suitably performed by the recycling unit. There is no restriction | limiting in particular as said recycling means, A well-known conveyance means etc. are mentioned.

-Control process and control means-
The control step is a step of controlling each of the steps, and can be suitably performed by a control unit.
The control means is not particularly limited as long as the movement of each means can be controlled, and can be appropriately selected according to the purpose. Examples thereof include devices such as a sequencer and a computer.

Next, the image forming apparatus and the process cartridge of the present invention will be described in detail with reference to the drawings.
The image forming apparatus of the present invention uses the electrophotographic photosensitive member of the present invention. For example, at least after the photosensitive member is charged, exposed to an image, and developed, the toner image is transferred to an image holding member (transfer paper). And fixing and cleaning the surface of the photoreceptor.
In some cases, an image forming apparatus that directly transfers an electrostatic latent image to a recording medium and develops it does not necessarily have the above-described process disposed on a photoconductor.

FIG. 4 is a schematic diagram illustrating an example of an image forming apparatus. A charging charger 3 is used as a means for charging the photosensitive member on average. As the charging means, a corotron device, a scorotron device, a solid discharge element, a needle electrode device, a roller charging device, a conductive brush device, or the like is used, and a known system can be used.
Next, the image exposure unit 5 is used to form an electrostatic latent image on the uniformly charged photoreceptor 1. As the light source, all luminescent materials such as a fluorescent lamp, a tungsten lamp, a halogen lamp, a mercury lamp, a sodium lamp, a light emitting diode (LED), a semiconductor laser (LD), and an electroluminescence (EL) can be used. Various types of filters such as a sharp cut filter, a band pass filter, a near infrared cut filter, a dichroic filter, an interference filter, and a color temperature conversion filter can be used to irradiate only light in a desired wavelength range.
Next, the developing unit 6 is used to visualize the electrostatic latent image formed on the photoreceptor 1. Development methods include a one-component development method using a dry toner, a two-component development method, and a wet development method using a wet toner. When the photosensitive member is positively (negatively) charged and image exposure is performed, a positive (negative) electrostatic latent image is formed on the surface of the photosensitive member. A positive image can be obtained by developing this with negative (positive) toner (electrodetection fine particles), and a negative image can be obtained by developing with positive (negative) toner.
Next, a transfer charger 10 is used to transfer the toner image visualized on the photoreceptor onto the recording medium 9. In addition, a pre-transfer charger 7 may be used for better transfer. As these transfer means, a transfer charger, an electrostatic transfer method using a bias roller, a mechanical transfer method such as an adhesive transfer method and a pressure transfer method, and a magnetic transfer method can be used. As the electrostatic transfer method, the charging means can be used.
Next, a separation charger 11 and a separation claw 12 are used as means for separating the recording medium 9 from the photoreceptor 1. As other separation means, electrostatic adsorption induction separation, side end belt separation, tip grip conveyance, curvature separation, and the like are used. As the separation charger 11, the charging means can be used.
Next, a fur brush 14 and a cleaning blade 15 are used to clean the toner remaining on the photoconductor after transfer. Further, a pre-cleaning charger 13 may be used in order to perform cleaning more efficiently. Other cleaning means include a web method, a magnet brush method, and the like, but each may be used alone or in combination.
Further, a charge eliminating unit is used for the purpose of removing the latent image on the photosensitive member as necessary. As the charge removal means, the charge removal lamp 2 and the charge removal charger are used, and the exposure light source and the charging means can be used respectively.
In addition, known processes can be used for reading, feeding, fixing, paper discharge and the like that are not close to the photoconductor.

The present invention is an image forming method and an image forming apparatus using the electrophotographic photoreceptor according to the present invention for such image forming means.
The image forming means may be fixedly incorporated in a copying apparatus, facsimile, or printer, but may be incorporated in these apparatuses in the form of a process cartridge and detachable. An example of the process cartridge is shown in FIG.
The process cartridge includes a photosensitive member 101, and further includes at least one of a charging unit 102, a developing unit 104, a transfer unit 106, a cleaning unit 107, and a charge eliminating unit (not shown). It is a device (part) that is detachable.
The image forming process using the process cartridge shown in FIG. 5 will be described. The photosensitive member 101 is charged by the charging unit 102 and exposed by the exposure unit 103 while rotating in the direction of the arrow. The electrostatic latent image is developed with toner by the developing unit 104, and the toner development is transferred to the recording medium 105 by the transfer unit 106 and printed out. Next, the surface of the photoconductor after the image transfer is cleaned by the cleaning unit 107 and further neutralized by a neutralizing unit (not shown), and the above operation is repeated again.

  An image forming method, an image forming apparatus, and a process cartridge according to the present invention include at least a binder resin, a surface layer containing a filler, and an intermediate layer made of an amorphous oxide semiconductor. Therefore, even when used for a long time, deterioration in electrophotographic characteristics such as reduction in chargeability is extremely small, and high-quality images with few defects can be continuously obtained.

  Examples of the present invention will be described below, but the present invention is not limited to these examples.

Example 1
<Production of electrophotographic photoreceptor>
An aluminum cylinder having a surface roughness (Rz) of 0.9 μm, a diameter of 30 mm, and a length of 360 mm was prepared as a support. The surface roughness (Rz) of the support was measured using Surfcom 1400D (manufactured by Tokyo Seimitsu Co., Ltd.) and the surface roughness (Rz) was measured with respect to an evaluation length of 2.5 mm and a reference length of 0.5 mm. Measurement points were 80 mm from both ends of the drum in the axial direction, 3 points in the center of the drum, and 4 types of 90 degrees in the circumferential direction. A total of 12 points were measured, and the average value was defined as the surface roughness (Rz) of the drum.
An intermediate layer was formed using an RF sputtering apparatus improved so that the film could be formed while rotating the aluminum cylinder as the support. A cooling jacket was provided inside the cylinder to prevent overheating of the substrate temperature during sputtering. Further, using a 150 mm × 400 mm target made of a polycrystalline sintered body (composition ratio (In: Ga: Zn) = 1: 1: 1) containing indium, zinc, and gallium, from indium, zinc, and gallium. An amorphous oxide film (hereinafter sometimes referred to as “In—Ga—ZnO _x ”) was formed as an intermediate layer. The film forming conditions were as follows.

-Cooling temperature of support: 30 ° C
Sputter output: 11.2 W / cm ²
・ Target-substrate distance: 50mm
・ Back pressure: 5.0 × 10 ⁻⁶ torr or less ・ Film forming pressure: 3.0 × 10 ⁻³ torr
・ Inert gas: Argon ・ Oxygen partial pressure: 3 vol% with respect to the total amount of inert gas and oxygen gas
Under the above conditions, In—Ga—ZnO _X having a thickness of 0.5 μm was formed as an intermediate layer. The thickness of the obtained intermediate layer was measured with a reflection spectral film thickness meter (FE-3000, manufactured by Otsuka Electronics Co., Ltd.).

<Surface resistivity of amorphous oxide semiconductor>
As an electrical resistance evaluation of the manufactured amorphous oxide semiconductor having a thickness of 0.5 μm in Example 1, the surface resistivity was measured by the method described below.
As the substrate for forming the amorphous oxide semiconductor, an alkali-free glass (Corning # 1737) is used instead of the support, and the other conditions are the amorphous oxide semiconductor formed under the conditions described in Example 1, It used for surface resistivity measurement. When measuring surface resistivity, a 25 μm gap, 10 mm long Au electrode was formed by vapor deposition on an amorphous oxide semiconductor formed on an alkali-free glass, and a bias was applied between the electrodes. This was done by measuring the passing current in the semiconductor. The surface resistivity was measured 10 times at different locations and the average value was calculated. As a result, the surface resistivity of the amorphous oxide semiconductor having a thickness of 0.5 μm was 5.0 × 10 ⁶ Ω / cm ^2. Met.

  Next, a charge generation layer coating liquid and a charge transport layer coating liquid having the following composition are sequentially applied and dried to form a charge generation layer having a thickness of 0.2 μm and a charge transport layer having a thickness of 20 μm. did.

[Coating liquid for charge generation layer]
-Bisazo pigment represented by the following structural formula (1): 2.5 parts by mass
・ Polyvinyl butyral (XYHL, manufactured by UCC): 0.5 part by mass ・ Cyclohexanone: 200 part by mass ・ Methyl ethyl ketone: 80 part by mass

[Coating liquid for charge transport layer]
-Bisphenol Z polycarbonate (Panlite TS-2050, manufactured by Teijin Chemicals Ltd.) ... 10 parts by mass-Low molecular charge transport material represented by the following structural formula (2) ... 7 parts by mass
Tetrahydrofuran: 100 parts by mass Tetrahydrofuran solution of 1% by mass silicone oil (KF50-100CS, manufactured by Shin-Etsu Chemical Co., Ltd.): 1 part by mass

Next, a surface layer coating solution having the following composition was applied on a laminate composed of a support, an intermediate layer, a charge generation layer, and a charge transport layer using a spray coating method, and then at 150 ° C. By performing drying for 20 minutes, a surface layer having a thickness of 5 μm was formed. As a result, an electrophotographic photoreceptor comprising a support, an intermediate layer, a charge generation layer, a charge transport layer, and a surface layer was produced.
[Coating liquid for surface layer]
-Bisphenol Z polycarbonate (Panlite TS-2050, manufactured by Teijin Chemicals Ltd.) ... 4 parts by mass-Low molecular charge transport material represented by the above structural formula (2) ... 3 parts by mass-Alumina fine particles (AA03 Manufactured by Sumitomo Chemical Co., Ltd.) 3 parts by mass Tetrahydrofuran 170 parts by mass Cyclohexanone 50 parts by mass

<Structural analysis of amorphous oxide semiconductor>
It was evaluated by crystal structure analysis by X-ray diffraction that the oxide semiconductor made of indium, zinc, and gallium manufactured in Example 1 was amorphous.
[X-ray diffraction evaluation method]
Evaluation device: X-ray diffractometer X 'Part Pro (manufactured by Philips)
・ X-ray source: Cu (encapsulated tube)
-Filter: None-Scan axis: 2θ / θ
-Measurement angle range: 10 ° -100 °
The measurement results are shown in FIG. From the results of FIG. 6, it was found that the produced intermediate layer was an amorphous oxide semiconductor.

<Composition of amorphous oxide semiconductor>
The constituent components and composition ratios of the amorphous oxide semiconductor produced in Example 1 were evaluated using the following fluorescent X-ray analysis method. In addition, the composition profile in the depth direction of the amorphous oxide semiconductor was evaluated using the following Auger electron spectroscopy.
[Fluorescence X-ray method evaluation method]
-Measuring device: Wavelength dispersive X-ray fluorescence analyzer (RIX3000, manufactured by Rigaku Corporation)
・ X-ray tube: Rh
・ Output: 50kV
・ Current: 50 mA
From the evaluation results under these conditions, the amorphous oxide semiconductor obtained in Example 1 is an oxide composed of indium, zinc, and gallium, and the composition ratio thereof is In: Zn: Ga = 100: 112: 117. It was found to be an amorphous oxide semiconductor.
[Auger electron spectroscopy evaluation method]
・ Measuring device: FE-SAM680 (manufactured by Phi)
・ Acceleration voltage: 10 kV
-Amount of current: 10 nA
Sputter etching conditions: Ar ion / acceleration voltage 1 kV
The measurement results are shown in FIG. From the results of FIG. 7, it was found that the constituent elements (indium, zinc, gallium, oxygen) have almost no variation in the depth direction and are extremely homogeneous amorphous oxide semiconductors.

(Example 2)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the surface layer coating solution in Example 1 was changed to the following surface layer coating solution.
[Coating liquid for surface layer]
Bisphenol Z polycarbonate (Panlite TS-2050, manufactured by Teijin Chemicals Ltd.) 4 parts by mass Low molecular charge transport material represented by the above structural formula (2) 3 parts by mass Silica fine particles (KMPX100 , Manufactured by Shin-Etsu Chemical Co., Ltd.) 3 parts by mass Tetrahydrofuran 170 parts Cyclohexanone 50 parts by mass

(Example 3)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the surface layer coating solution in Example 1 was changed to the following surface layer coating solution.
[Coating liquid for surface layer]
-Bisphenol Z polycarbonate (Panlite TS-2050, manufactured by Teijin Chemicals Ltd.) ... 4 parts by mass-Low molecular charge transport material represented by the above structural formula (2) ... 3 parts by mass-Titania fine particles (CR97 Manufactured by Ishihara Sangyo Co., Ltd.) 3 parts by mass Tetrahydrofuran 170 parts by weight Cyclohexanone 50 parts by weight

Example 4
-Production of electrophotographic photoreceptor-
Electrophotographic photosensitivity in the same manner as in Example 1 except that the bisphenol Z polycarbonate used in the surface layer coating solution of Example 1 was changed to 4 parts by mass of polyarylate resin (U-6000, manufactured by Unitika Ltd.). The body was made.

(Example 5)
-Production of electrophotographic photoreceptor-
Electrophotographic photosensitivity in the same manner as in Example 2, except that the bisphenol Z polycarbonate used in the surface layer coating liquid of Example 2 was changed to 4 parts by mass of polyarylate resin (U-6000, manufactured by Unitika Ltd.). The body was made.

(Example 6)
-Production of electrophotographic photoreceptor-
Electrophotographic photosensitivity in the same manner as in Example 3 except that the bisphenol Z polycarbonate used in the surface layer coating solution of Example 3 was changed to 4 parts by mass of polyarylate resin (U-6000, manufactured by Unitika Ltd.). The body was made.

(Example 7)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the surface layer coating solution in Example 1 was changed to the following surface layer coating solution.
[Coating liquid for surface layer]
-Polymer charge transport material (molecular weight Mw 130,000) represented by the following structural formula (3): 7 parts by mass

・ Alumina fine particles (AA03, manufactured by Sumitomo Chemical Co., Ltd.) 3 parts by mass Tetrahydrofuran 170 parts by mass Cyclohexanone 50 parts by mass

(Example 8)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the surface layer coating solution in Example 1 was changed to the following surface layer coating solution.
[Coating liquid for surface layer]
-Polymer charge transport material represented by the above structural formula (3) (molecular weight Mw 130,000)-7 parts by mass-Silica fine particles (KMPX100, manufactured by Shin-Etsu Chemical Co., Ltd.)-3 parts by mass-Tetrahydrofuran ... 170 parts by massCyclohexanone ... 50 parts by mass

Example 9
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the surface layer coating solution in Example 1 was changed to the following surface layer coating solution.
[Coating liquid for surface layer]
-Polymer charge transport material represented by the above structural formula (3) (molecular weight Mw 130,000) ... 7 parts by mass-Titania fine particles (CR97, manufactured by Ishihara Sangyo Co., Ltd.) ... 3 parts by mass-Tetrahydrofuran・ ・ 170 parts by mass ・ Cyclohexanone: 50 parts by mass

(Example 10)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the surface roughness (Rz) of the support of Example 1 was 0.2 μm.

(Example 11)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Example 4 except that the surface roughness (Rz) of the support of Example 4 was 0.2 μm.

(Example 12)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Example 7, except that the surface roughness (Rz) of the support of Example 7 was 0.2 μm.

(Example 13)
-Production of electrophotographic photoreceptor-
Except for changing the alumina fine particles used in the surface layer coating liquid of Example 1 to 3 parts by mass of alumina fine particles (AKP-G008 / θ-alumina, manufactured by Sumitomo Chemical Co., Ltd.), the same as in Example 1, An electrophotographic photosensitive member was produced.

(Example 14)
-Production of electrophotographic photoreceptor-
Except for changing the alumina fine particles used in the surface layer coating liquid of Example 1 to 3 parts by mass of alumina fine particles (AKP-G015 / γ-alumina, manufactured by Sumitomo Chemical Co., Ltd.), the same as in Example 1, An electrophotographic photosensitive member was produced.

(Example 15)
-Production of electrophotographic photoreceptor-
Except that the thickness of the intermediate layer of Example 1 was 0.05 μm (the film was formed under the film forming conditions described in Example 1, and the film formation time was set to 1/10 of Example 1). In the same manner as in Example 1, an electrophotographic photosensitive member was produced.

(Example 16)
-Production of electrophotographic photoreceptor-
Implementation was carried out except that the thickness of the intermediate layer of Example 1 was 0.15 μm (produced under the film production conditions described in Example 1, and the film formation time was set to 3/10 of Example 1). In the same manner as in Example 1, an electrophotographic photosensitive member was produced.

(Example 17)
-Production of electrophotographic photoreceptor-
Implementation was performed except that the thickness of the intermediate layer of Example 1 was 0.8 μm (the film was formed under the film forming conditions described in Example 1, and only the film forming time was 1.6 times that of Example 1). In the same manner as in Example 1, an electrophotographic photosensitive member was produced.

(Example 18)
-Production of electrophotographic photoreceptor-
Example 1 except that the thickness of the intermediate layer of Example 1 was 1.0 μm (produced under the film-forming conditions described in Example 1 and made only the film-forming time twice that of Example 1). In the same manner as above, an electrophotographic photosensitive member was produced.

(Example 19)
-Production of electrophotographic photoreceptor-
Of the intermediate layer manufacturing method of Example 4, a polycrystalline sintered body containing indium, zinc, and gallium has a composition ratio (In: Ga: Zn) of indium, zinc, and gallium of 1: 1.5: 1. An electrophotographic photosensitive member was produced in the same manner as in Example 4 except that the polycrystalline sintered body was changed.
As a result of measuring the composition ratio of the amorphous oxide semiconductor using the evaluation method described in Example 1 for the obtained electrophotographic photoreceptor of Example 19, the composition ratio (In: Zn: Ga) was 100: 108. 137.
The surface resistivity of the amorphous oxide semiconductor measured in the same manner as in Example 1 was 4.9 × 10 ⁷ Ω / cm ² .

(Example 20)
-Production of electrophotographic photoreceptor-
Of the intermediate layer manufacturing method of Example 4, a polycrystalline sintered body containing indium, zinc, and gallium has a composition ratio (In: Ga: Zn) of indium, zinc, and gallium of 1: 0.75: 1. An electrophotographic photosensitive member was produced in the same manner as in Example 4 except that the polycrystalline sintered body was changed.
As a result of measuring the composition ratio of the amorphous oxide semiconductor using the evaluation method described in Example 1 for the obtained electrophotographic photoreceptor of Example 20, the composition ratio (In: Zn: Ga) was 100: 110. : 105.
The surface resistivity of the amorphous oxide semiconductor measured in the same manner as in Example 1 was 6.2 × 10 ⁵ Ω / cm ² .

( Reference Example 21)
-Production of electrophotographic photoreceptor-
Of the intermediate layer manufacturing method of Example 1, a polycrystalline sintered body containing indium, zinc, and gallium is changed into a polycrystalline sintered body having a composition ratio (In: Ga) of indium and gallium of 1: 1. An electrophotographic photosensitive member was produced in the same manner as in Example 1 except for the change.
As a result of measuring the composition ratio of the amorphous oxide semiconductor using the evaluation method described in Example 1 for the obtained electrophotographic photoreceptor of Reference Example 21, the composition ratio (In: Ga) was 100: 125. It was.
The surface resistivity of the amorphous oxide semiconductor measured in the same manner as in Example 1 was 6.7 × 10 ⁷ Ω / cm ² .

( Reference Example 22)
-Production of electrophotographic photoreceptor-
Of the intermediate layer manufacturing method of Example 1, the polycrystalline sintered body containing indium, zinc, and gallium is changed to a polycrystalline sintered body having a composition ratio (In: Zn) of indium and zinc of 1: 1. An electrophotographic photosensitive member was produced in the same manner as in Example 1 except for the change.
As a result of measuring the composition ratio of the amorphous oxide semiconductor for the obtained electrophotographic photoreceptor of Reference Example 22 using the evaluation method described in Example 1, the composition ratio (In: Zn) was 100: 111. It was.
The surface resistivity of the amorphous oxide semiconductor measured in the same manner as in Example 1 was 7.5 × 10 ⁶ Ω / cm ² .

(Example 23)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the surface layer coating solution in Example 1 was changed to the following surface layer coating solution.
[Coating liquid for surface layer]
-Bisphenol Z polycarbonate (Panlite TS-2050, manufactured by Teijin Chemicals Ltd.) ... 12 parts by mass-Low molecular charge transport material represented by the above structural formula (2) ... 9 parts by mass-Alumina fine particles (Fluoro) -A, manufactured by Shamrock Technologies) ... 8 parts by mass-Tetrahydrofuran ... 160 parts by mass-Cyclohexanone ... 40 parts by mass

(Comparative Example 1)
-Production of electrophotographic photoreceptor-
On the support used in Example 1 (aluminum cylinder having a surface roughness (Rz) of 0.9 μm, a diameter of 30 mm, and a length of 360 mm), the charge generation layer coating solution used in Example 1 and charge transport By sequentially applying and drying the layer coating liquid, a 0.2 μm-thick charge generation layer and a 20 μm-thick charge transport layer are formed, whereby a support, a charge generation layer, and a charge transport layer are formed. An electrophotographic photosensitive member comprising:

(Comparative Example 2)
-Production of electrophotographic photoreceptor-
A surface layer coating solution having the following composition was applied on the electrophotographic photoreceptor obtained in Comparative Example 1 by spray coating, and then dried at 150 ° C. for 20 minutes to form a surface layer having a thickness of 5 μm. Thus, an electrophotographic photosensitive member comprising a support, a charge generation layer, a charge transport layer, and a surface layer was produced.

[Coating liquid for surface layer]
-Bisphenol Z polycarbonate (Panlite TS-2050, manufactured by Teijin Chemicals Ltd.) ... 4 parts by mass-Low molecular charge transport material represented by the above structural formula (2) ... 3 parts by mass-Tetrahydrofuran ... 170 parts by mass ・ Cyclohexanone: 50 parts by mass

(Comparative Example 3)
-Production of electrophotographic photoreceptor-
A surface layer coating solution having the following composition was applied on the electrophotographic photoreceptor obtained in Comparative Example 1 by spray coating, and then dried at 150 ° C. for 20 minutes to form a surface layer having a thickness of 5 μm. Thus, an electrophotographic photosensitive member comprising a support, a charge generation layer, a charge transport layer, and a surface layer was produced.
[Coating liquid for surface layer]
-Bisphenol Z polycarbonate (Panlite TS-2050, manufactured by Teijin Chemicals Ltd.) ... 4 parts by mass-Low molecular charge transport material represented by the above structural formula (2) ... 3 parts by mass-Alumina fine particles (AA03 Manufactured by Sumitomo Chemical Co., Ltd.) 3 parts by mass Tetrahydrofuran 170 parts by mass Cyclohexanone 50 parts by mass

(Comparative Example 4)
-Production of electrophotographic photoreceptor-
A surface layer coating solution having the following composition was applied on the electrophotographic photoreceptor obtained in Comparative Example 1 by spray coating, and then dried at 150 ° C. for 20 minutes to form a surface layer having a thickness of 5 μm. Thus, an electrophotographic photosensitive member comprising a support, a charge generation layer, a charge transport layer, and a surface layer was produced.
[Coating liquid for surface layer]
-Polymer charge transport material (molecular weight Mw 130,000) represented by the structural formula (3) ... 7 parts by mass-Tetrahydrofuran ... 170 parts by mass-Cyclohexanone ... 50 parts by mass

(Comparative Example 5)
-Production of electrophotographic photoreceptor-
A surface layer coating solution having the following composition was applied on the electrophotographic photoreceptor obtained in Comparative Example 1 by spray coating, and then dried at 150 ° C. for 20 minutes to form a surface layer having a thickness of 5 μm. Thus, an electrophotographic photosensitive member comprising a support, a charge generation layer, a charge transport layer, and a surface layer was produced.
[Coating liquid for surface layer]
-Polymer charge transport material represented by the above structural formula (3) (molecular weight Mw 130,000) ... 7 parts by mass-Alumina fine particles (AA03, manufactured by Sumitomo Chemical Co., Ltd.) ... 3 parts by mass-Tetrahydrofuran・ ・ 170 parts by mass ・ Cyclohexanone: 50 parts by mass

(Comparative Example 6)
-Production of electrophotographic photoreceptor-
On the support used in Example 1 (aluminum cylinder having a surface roughness (Rz) of 0.9 μm, a diameter of 30 mm, and a length of 360 mm), an intermediate layer coating solution having the following composition was used in Example 1. By sequentially applying and drying the charge generation layer coating solution and the charge transport layer coating solution used in Example 1, an intermediate layer having a thickness of 3.5 μm, a charge generation layer having a thickness of 0.2 μm, A charge transport layer having a thickness of 20 μm was formed, whereby an electrophotographic photosensitive member comprising a support, an intermediate layer, a charge generation layer, and a charge transport layer was produced.
[Coating liquid for intermediate layer]
・ Alkyd resin (Beckosol 1307-60-EL, manufactured by Dainippon Ink & Chemicals, Inc.) ... 6 parts by mass Melamine resin (Super Becamine G-821-60, manufactured by Dainippon Ink & Chemicals, Inc.)・ 4 parts by mass ・ Titanium oxide: 40 parts by mass ・ Methyl ethyl ketone: 50 parts by mass

(Comparative Example 7)
-Production of electrophotographic photoreceptor-
The surface layer coating solution described in Comparative Example 2 is sprayed onto an electrophotographic photosensitive member comprising a support formed by the method described in Comparative Example 6, an intermediate layer, a charge generation layer, and a charge transport layer. After coating by a coating method, a surface layer having a thickness of 5 μm is formed by drying at 150 ° C. for 20 minutes, whereby a support, an intermediate layer, a charge generation layer, a charge transport layer, a surface layer, An electrophotographic photosensitive member comprising:

(Comparative Example 8)
-Production of electrophotographic photoreceptor-
The surface layer coating solution described in Comparative Example 3 is sprayed onto the electrophotographic photosensitive member comprising the support formed by the method described in Comparative Example 6, the intermediate layer, the charge generation layer, and the charge transport layer. After coating by a coating method, a surface layer having a thickness of 5 μm is formed by drying at 150 ° C. for 20 minutes, whereby a support, an intermediate layer, a charge generation layer, a charge transport layer, a surface layer, An electrophotographic photosensitive member comprising:

(Comparative Example 9)
-Production of electrophotographic photoreceptor-
The surface layer coating solution described in Comparative Example 4 is sprayed onto an electrophotographic photosensitive member comprising a support formed by the method described in Comparative Example 6, an intermediate layer, a charge generation layer, and a charge transport layer. After coating by a coating method, a surface layer having a thickness of 5 μm is formed by drying at 150 ° C. for 20 minutes, whereby a support, an intermediate layer, a charge generation layer, a charge transport layer, a surface layer, An electrophotographic photosensitive member comprising:

(Comparative Example 10)
-Production of electrophotographic photoreceptor-
The surface layer coating solution described in Comparative Example 5 is sprayed onto the electrophotographic photosensitive member comprising the support formed by the method described in Comparative Example 6, the intermediate layer, the charge generation layer, and the charge transport layer. After coating by a coating method, a surface layer having a thickness of 5 μm is formed by drying at 150 ° C. for 20 minutes, whereby a support, an intermediate layer, a charge generation layer, a charge transport layer, a surface layer, An electrophotographic photosensitive member comprising:

(Comparative Example 11)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Comparative Example 6 except that the intermediate layer coating solution of Comparative Example 6 was changed to the following composition and the thickness of the intermediate layer was 2.0 μm.
[Coating liquid for intermediate layer]
・ Alkyd resin (Beckosol 1307-60-EL, manufactured by Dainippon Ink and Chemicals, Inc.) ... 6 parts by mass Melamine resin (Super Becamine G-821-60, manufactured by Dainippon Ink and Chemicals, Inc.)・ 4 parts by mass ・ Methyl ethyl ketone: 50 parts by mass

(Comparative Example 12)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Comparative Example 7, except that the intermediate layer coating solution of Comparative Example 7 was changed to the following composition and the thickness of the intermediate layer was 2.0 μm.
[Coating liquid for intermediate layer]
・ Alkyd resin (Beckosol 1307-60-EL, manufactured by Dainippon Ink and Chemicals, Inc.) ... 6 parts by mass Melamine resin (Super Becamine G-821-60, manufactured by Dainippon Ink and Chemicals, Inc.)・ 4 parts by mass ・ Methyl ethyl ketone: 50 parts by mass

(Comparative Example 13)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Comparative Example 8 except that the intermediate layer coating solution of Comparative Example 8 was changed to the following composition and the thickness of the intermediate layer was 2.0 μm.
[Coating liquid for intermediate layer]
・ Alkyd resin (Beckosol 1307-60-EL, manufactured by Dainippon Ink and Chemicals, Inc.) ... 6 parts by mass Melamine resin (Super Becamine G-821-60, manufactured by Dainippon Ink and Chemicals, Inc.)・ 4 parts by mass ・ Methyl ethyl ketone: 50 parts by mass

(Comparative Example 14)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Comparative Example 9, except that the intermediate layer coating solution of Comparative Example 9 was changed to the following composition and the thickness of the intermediate layer was 2.0 μm.
[Coating liquid for intermediate layer]
・ Alkyd resin (Beckosol 1307-60-EL, manufactured by Dainippon Ink and Chemicals, Inc.) ... 6 parts by mass Melamine resin (Super Becamine G-821-60, manufactured by Dainippon Ink and Chemicals, Inc.)・ 4 parts by mass ・ Methyl ethyl ketone: 50 parts by mass

(Comparative Example 15)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member was produced in the same manner as in Comparative Example 10, except that the intermediate layer coating solution of Comparative Example 10 was changed to the following composition and the thickness of the intermediate layer was 2.0 μm.
[Coating liquid for intermediate layer]
・ Alkyd resin (Beckosol 1307-60-EL, manufactured by Dainippon Ink and Chemicals, Inc.) ... 6 parts by mass Melamine resin (Super Becamine G-821-60, manufactured by Dainippon Ink and Chemicals, Inc.)・ 4 parts by mass ・ Methyl ethyl ketone: 50 parts by mass

(Comparative Example 16)
-Production of electrophotographic photoreceptor-
An electrophotographic photosensitive member comprising a support, an intermediate layer, a charge generation layer, and a charge transport layer was produced in the same manner as in Example 1 except that the surface layer was not formed.

(Comparative Example 17)
-Production of electrophotographic photoreceptor-
In the same manner as in Example 1, the surface layer coating solution described in Comparative Example 2 was applied by a spray coating method onto a laminate composed of a support, an intermediate layer, a charge generation layer, and a charge transport layer. And then drying at 150 ° C. for 20 minutes to form a surface layer having a thickness of 5 μm, whereby an electrophotographic image comprising a support, an intermediate layer, a charge generation layer, a charge transport layer and a surface layer A photoconductor was prepared.

(Comparative Example 18)
-Production of electrophotographic photoreceptor-
In the same manner as in Example 1, the surface layer coating liquid described in Comparative Example 4 was applied by a spray coating method onto a laminate composed of a support, an intermediate layer, a charge generation layer, and a charge transport layer. After that, by drying at 150 ° C. for 20 minutes, a surface layer having a thickness of 5 μm is formed. A photoconductor was prepared.

(Comparative Example 19)
-Production of electrophotographic photoreceptor-
In the same manner as in Comparative Example 6, except that the intermediate layer of Comparative Example 6 was tin oxide which was a crystalline oxide produced under the following conditions using the modified RF sputtering apparatus described in Example 1, A photographic photoreceptor was prepared.
(Intermediate layer forming method)
-Target: Polycrystalline sintered body made of tin oxide-Cooling temperature of support: 30 ° C
Sputter output: 11.2 W / cm ²
・ Target-substrate distance: 50mm
・ Back pressure: 5.0 × 10 ⁻⁶ torr or less ・ Film forming pressure: 3.0 × 10 ⁻³ torr
・ Inert gas: Argon ・ Oxygen partial pressure: 5 vol% with respect to the total amount of inert gas and oxygen gas

(Comparative Example 20)
-Production of electrophotographic photoreceptor-
In the same manner as in Comparative Example 7, except that the intermediate layer of Comparative Example 7 was tin oxide, which was a crystalline oxide produced under the following conditions using the modified RF sputtering apparatus described in Example 1, A photographic photoreceptor was prepared.
(Intermediate layer forming method)
-Target: Polycrystalline sintered body made of tin oxide-Cooling temperature of support: 30 ° C
Sputter output: 11.2 W / cm ²
・ Target-substrate distance: 50mm
・ Back pressure: 5.0 × 10 ⁻⁶ torr or less ・ Film forming pressure: 3.0 × 10 ⁻³ torr
・ Inert gas: Argon ・ Oxygen partial pressure: 5 vol% with respect to the total amount of inert gas and oxygen gas

(Comparative Example 21)
-Production of electrophotographic photoreceptor-
In the same manner as in Comparative Example 8, except that the intermediate layer of Comparative Example 8 was tin oxide, which was a crystalline oxide produced under the following conditions using the modified RF sputtering apparatus described in Example 1, A photographic photoreceptor was prepared.
(Intermediate layer forming method)
-Target: Polycrystalline sintered body made of tin oxide-Cooling temperature of support: 30 ° C
Sputter output: 11.2 W / cm ²
・ Target-substrate distance: 50mm
・ Back pressure: 5.0 × 10 ⁻⁶ torr or less ・ Film forming pressure: 3.0 × 10 ⁻³ torr
・ Inert gas: Argon ・ Oxygen partial pressure: 5 vol% with respect to the total amount of inert gas and oxygen gas

(Comparative Example 22)
-Production of electrophotographic photoreceptor-
In the same manner as in Comparative Example 9, except that the intermediate layer of Comparative Example 9 was tin oxide which was a crystalline oxide produced under the following conditions using the modified RF sputtering apparatus described in Example 1, A photographic photoreceptor was prepared.
(Intermediate layer forming method)
-Target: Polycrystalline sintered body made of tin oxide-Cooling temperature of support: 30 ° C
Sputter output: 11.2 W / cm ²
・ Target-substrate distance: 50mm
・ Back pressure: 5.0 × 10 ⁻⁶ torr or less ・ Film forming pressure: 3.0 × 10 ⁻³ torr
・ Inert gas: Argon ・ Oxygen partial pressure: 5 vol% with respect to the total amount of inert gas and oxygen gas

(Comparative Example 23)
-Production of electrophotographic photoreceptor-
In the same manner as in Comparative Example 10, except that the intermediate layer of Comparative Example 10 was tin oxide, which was a crystalline oxide produced under the following conditions using the modified RF sputtering apparatus described in Example 1, A photographic photoreceptor was prepared.
(Intermediate layer forming method)
-Target: Polycrystalline sintered body made of tin oxide-Cooling temperature of support: 30 ° C
Sputter output: 11.2 W / cm ²
・ Target-substrate distance: 50mm
・ Back pressure: 5.0 × 10 ⁻⁶ torr or less ・ Film forming pressure: 3.0 × 10 ⁻³ torr
・ Inert gas: Argon ・ Oxygen partial pressure: 5 vol% with respect to the total amount of inert gas and oxygen gas

Next, the following tests were carried out on the electrophotographic photoreceptors of Examples 1 to 20, Reference Examples 21 to 22, Example 23, and Comparative Examples 1 to 23 that were produced. The results are shown in Table 1.

<Abrasion durability evaluation>
The abrasion durability of the electrophotographic photoreceptors produced in Examples 1 to 20, Reference Examples 21 to 22, Example 23, and Comparative Examples 1 to 23 was evaluated by the following method.
The produced electrophotographic photosensitive member was mounted on a process cartridge for an electrophotographic apparatus, and the initial dark part potential was set to −800 V with a remodeled iPsio CX9000 using a 655 nm semiconductor laser as an image exposure light source. Thereafter, A4 size paper passing running was performed. In the following manner, the film thickness of the photosensitive member at the initial stage and at 50,000 sheets was measured to determine the film thickness reduction amount. Further, as the electrical characteristics, the dark part potential and the exposed part potential at the initial stage and at 50,000 sheets were measured. The results are shown in Table 1.
-Measurement of film thickness of electrophotographic photosensitive member-
The film thickness of the electrophotographic photosensitive member was measured using an eddy current film thickness measuring device (manufactured by Fischer Instrument Co.).

From the results in Table 1, Examples 1 to 20, Reference Examples 21 to 22, Example 23 and Comparative Examples 3, 5, 8, 10, 13 , 15 among the electrophotographic photoreceptors having the surface layer described in the present invention. This electrophotographic photosensitive member has less wear due to running and has very excellent wear durability compared to an electrophotographic photosensitive member having no surface layer and an electrophotographic photosensitive member not containing a filler in the surface layer. It was found to be a surface layer.
Further, among electrophotographic photoreceptors having no surface layer (Comparative Examples 1, 6, 11, and 16) and electrophotographic photoreceptors that do not contain a filler in the surface layer, Comparative Examples 2, 7, 12, and 17 have a wear amount. There were so many cases that charging failure and paper jam occurred during the running of 50,000 sheets, so the running was stopped at about 15,000 to 20,000 sheets, and the result could not withstand long-term use. .
From the results of the surface potential of the photoreceptor, the electrophotographic photoreceptors obtained in Examples 1 to 20, Reference Examples 21 to 22 and Example 23 and the electrophotographic photoreceptor obtained in Comparative Example 18 are all initial and 50,000 sheets. After running, both exposed area potentials were low and stable. On the other hand, the electrophotographic photoreceptors obtained in Comparative Examples 6 to 15 tend to have a high exposure area potential from the beginning, and after 50,000 sheets are run, the exposure area is 3 times or more of the photoreceptor obtained in the examples. Some showed potential. For this reason, the electrophotographic photoreceptors obtained in Examples 1 to 20, Reference Examples 21 to 22 and Example 23 in short-term paper running have little photoreceptor wear and little fluctuation in photoreceptor characteristics. It was shown that there is.
The electrophotographic photoreceptors obtained in Comparative Examples 19 to 23 could not be charged enough immediately after the start of running, and could not be used for running.

Based on the results of Table 1, the surface layers (thickness 5.0 μm) of Examples 1 to 20, Reference Examples 21 to 22, Example 23, Comparative Examples 3 to 5, 8 to 10, 13 to 15, and 18 were obtained. The number of running sheets required to disappear due to wear was calculated. The results are shown in Table 2.

When the wear durability life of the electrophotographic photoreceptors produced in Examples 1 to 20, Reference Examples 21 to 22 and Example 23 is the running number required until the disappearance of the surface layer shown in Table 2, In other words, it has a wear durability life of about 200,000 to 500,000 sheets. Therefore, it is necessary for the electrostatic durability focused in the present invention to have a durability equal to or greater than the wear durability life shown here.

<Evaluation of electrostatic durability>
If the wear durability life shown in Table 2 shows that there is little decrease in various characteristics of the photoreceptor after running at least 500,000 sheets, an electrophotographic photoreceptor excellent in wear durability and electrostatic durability can be obtained. I can say that. However, since it is not realistic to run all the electrophotographic photosensitive members shown in the examples and comparative examples by running the number of sheets and evaluate the electrostatic durability, the following method is used for the electrophotographic photosensitive member. Electrostatic fatigue was loaded on the photographic photoreceptor and the electrostatic durability was evaluated.
A unit obtained by removing a member (cleaning blade, etc.) excluding the charging unit from the photoreceptor unit of Imagio Neo 271 manufactured by Ricoh Co., Ltd. was used in the running test.
The modified photoreceptor unit to which the photoreceptors produced in Examples and Comparative Examples were attached was set in an Imagio Neo 271 modified machine manufactured by Ricoh Co., Ltd., so that only charging and development could be repeatedly performed without passing paper.
As charging conditions, a charging roller is used, an alternating voltage obtained by superimposing an AC voltage on a DC voltage is applied, a peak-to-peak voltage Vpp of the AC voltage is about 1.9 kV, a frequency f is about 900 Hz, and a DC voltage is -800 V. The rotational speed of the electrophotographic photosensitive member was set to 125 mm / sec. As the development conditions, a 650 nm LD was used, and the writing pattern was a 100% writing pattern (all solid). In order to load the electrophotographic photosensitive member with electrostatic fatigue equivalent to the above-mentioned 500,000 running (5% test pattern / charging-exposure potential difference 750V / electrophotographic photosensitive member capacitance 110 pF / cm ² ) under these conditions. Shows that it can be achieved by running for about 10 hours from passing charge calculation.
In this evaluation, Examples 1 to 20, Reference Examples 21 to 22 and Example 23, Comparative Examples 3 to 5, 8 to 10 having durability against 50,000 sheets of paper running in wear durability evaluation, For each of the electrophotographic photoreceptors 13 to 15 and 18, the charging potential and the exposed portion potential before and after the running test were measured. In addition, using a remodeled iPsio CX9000 made by Ricoh Co., Ltd. used for wear durability evaluation, 0% test pattern (solid white) image and halftone image were output (continuous 5 sheets). The occurrence status was confirmed. The results are shown in Table 3.

From the results shown in Table 3, the electrophotographic photosensitive members of Examples 1 to 20, Reference Examples 21 to 22 and Example 23 all have small fluctuations in the charging potential and the exposure portion potential, and the occurrence of background contamination and image defects. Almost never occurred. In Examples 10 to 12, some moiré occurred in the halftone output.
On the other hand, the electrophotographic photoreceptors of Comparative Examples 3 to 5, 8 to 10, and 13 to 15 have large fluctuation amounts of the charging potential and the exposure portion potential as compared with Examples, and in particular, the electrons of Comparative Examples 13 to 15 are used. In the photographic photosensitive member, the potential of the exposed portion became very large, and the change in image density due to this was markedly exhibited. Further, the electrophotographic photoreceptors of Comparative Examples 3 to 5, 8 to 10, and 13 to 15 all had image defects after electrostatic fatigue.
The electrophotographic photosensitive member of Comparative Example 18 has small variations in both the charging potential and the exposed portion potential, but as shown in the wear durability evaluation, the wear durability is poor, and Examples 1 to 20 and Reference Example 21 are poor. Although the electrophotographic photosensitive members of ˜22 and Example 23 have a durability of about 200,000 to 500,000, they generally have a durability of about 100,000, less than half. It was shown in
From the above, the electrophotographic photoreceptors of Examples 1 to 20, Reference Examples 21 to 22 and Example 23 have small characteristic fluctuations even with respect to an electrostatic load, and are related to image quality over a long period of time. It turns out that there are few defects.

  The image forming apparatus, the image forming method, and the process cartridge according to the present invention are extremely low in characteristics such as wear durability and electrostatic durability without causing an increase in potential of an exposed portion even when used for a long time. Because it uses an electrophotographic photosensitive member, it is widely used in laser printers, direct digital plate-making machines, full-color copiers using direct or indirect electrophotographic multicolor image development systems, full-color laser printers, full-color plain paper fax machines, etc. it can.

FIG. 1 is a schematic sectional view showing an example of the layer structure of the electrophotographic photosensitive member of the present invention. FIG. 2 is a schematic sectional view showing another example of the layer structure of the electrophotographic photosensitive member of the present invention. FIG. 3 is a schematic sectional view showing still another example of the layer structure of the electrophotographic photosensitive member of the present invention. FIG. 4 is a schematic view showing an example of the image forming apparatus of the present invention. FIG. 5 is a schematic view showing an example of the process cartridge of the present invention. FIG. 6 is a diagram showing a crystal structure analysis result by an X-ray diffraction method of an amorphous oxide semiconductor made of indium, zinc, and gallium manufactured in Example 1. FIG. 7 is a diagram showing an evaluation result by Auger electron spectroscopy of an amorphous oxide semiconductor made of indium, zinc, and gallium manufactured in Example 1.

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 Photoconductor 2 Static elimination lamp 3 Charger charger 4 Toner cleaning member 5 Image exposure part 6 Developing unit 7 Charger before transfer 8 Charge auxiliary brush 9 Recording medium 10 Transfer charger 11 Separation charger 12 Separation claw 13 Charger before cleaning 14 Fur brush 15 Cleaning blade Reference Signs List 31 Support 32 Intermediate Layer 33 Charge Generation Layer 34 Charge Transport Layer 35 Surface Layer 36 Single-Layer Photosensitive Layer 101 Photoreceptor 102 Charging Unit 103 Exposure Unit 104 Development Unit 105 Recording Medium 106 Transfer Unit 107 Cleaning Unit

Claims (15)

A support, and at least an intermediate layer, a photosensitive layer, and a surface layer in this order on the support;
The surface layer contains at least a binder resin and a filler,
The intermediate layer contains an amorphous oxide semiconductor ;
The electrophotographic photosensitive member, wherein the amorphous oxide semiconductor contains at least indium, zinc, and gallium . The electrophotographic photosensitive member according to claim 1, wherein the intermediate layer has a thickness of 0.1 μm or more and 0.9 μm or less. The electrophotographic photosensitive member according to claim 1, wherein the support has a surface roughness (Rz) of 0.6 μm or more. The electrophotographic photosensitive member according to claim 1, wherein the filler is a metal oxide. The metal oxide is at least one selected from aluminum oxide, titanium oxide and silica
The electrophotographic photosensitive member according to claim 4, which is any one of them. The electrophotographic photosensitive member according to claim 4, wherein the metal oxide is α-alumina. The binder resin is at least one of polycarbonate resin and polyarylate resin
The electrophotographic photosensitive member according to any one of claims 1 to 6. The electrophotographic photosensitive member according to claim 1, wherein the binder resin is a polymer charge transport material. Polymer charge transport materials include polycarbonate, polyurethane, polyester and polyester.
The electrophotographic photoreceptor according to claim 8, which is at least one polymer selected from tellurium. The electrophotographic photosensitive member according to claim 8, wherein the polymer charge transport material has a triarylamine structure. The electrophotographic photosensitive member according to claim 1, wherein the surface layer further contains a charge transport material. The electrophotographic photosensitive member according to claim 1, wherein the photosensitive layer is a laminated type comprising a charge generation layer and a charge transport layer. A charging process for charging the surface of the electrophotographic photosensitive member, and exposing the charged electrophotographic photosensitive member surface
An exposure process for forming an electrostatic latent image, and developing the electrostatic latent image with toner to form a visible image
An image form including at least a developing step and a transfer step of transferring the visible image to a recording medium
In the creation method,
The image forming method according to claim 1, wherein the electrophotographic photosensitive member is the electrophotographic photosensitive member according to claim 1. An electrophotographic photosensitive member, a charging means for charging the surface of the electrophotographic photosensitive member, and a charged electrophotographic photosensitive member.
An exposure means for exposing the surface of the true photoconductor to form an electrostatic latent image, and the electrostatic latent image using toner
Developing means for developing a visible image and transfer means for transferring the visible image to a recording medium;
In an image forming apparatus having at least
An image forming apparatus, wherein the electrophotographic photosensitive member is the electrophotographic photosensitive member according to claim 1. An electrophotographic photosensitive member according to any one of claims 1 to 12, and at least developing means for developing an electrostatic latent image formed on the electrophotographic photosensitive member using a toner to form a visible image. A process cartridge which is detachable from the main body of the image forming apparatus.