JP5262199B2 - Chloroprene latex and process for producing the same - Google Patents

Chloroprene latex and process for producing the same Download PDF

Info

Publication number
JP5262199B2
JP5262199B2 JP2008060069A JP2008060069A JP5262199B2 JP 5262199 B2 JP5262199 B2 JP 5262199B2 JP 2008060069 A JP2008060069 A JP 2008060069A JP 2008060069 A JP2008060069 A JP 2008060069A JP 5262199 B2 JP5262199 B2 JP 5262199B2
Authority
JP
Japan
Prior art keywords
latex
weight
alkali metal
chloroprene
metal salt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2008060069A
Other languages
Japanese (ja)
Other versions
JP2009215418A (en
Inventor
俊裕 齋藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tosoh Corp
Original Assignee
Tosoh Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tosoh Corp filed Critical Tosoh Corp
Priority to JP2008060069A priority Critical patent/JP5262199B2/en
Publication of JP2009215418A publication Critical patent/JP2009215418A/en
Application granted granted Critical
Publication of JP5262199B2 publication Critical patent/JP5262199B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide a chloroprene latex with a sufficient adhesion property being not freezed even if it is stored at low temperatures. <P>SOLUTION: The chloroprene latex containing an emulsifier comprising an alkali metal salt of a carboxylic acid and a nonionic emulsifier having an HLB of 9-16 and represented by general formula (1): R-O(CH<SB>2</SB>CXHO)nH (wherein R represents a lipophilic group comprising a 9-16C alkyl chain and a branch; X represents hydrogen or a 1-2C alkyl chain; and n represents an integer of a range that HLB of the nonionic emulsifier becomes 9-16). The method for production thereof is also provided. <P>COPYRIGHT: (C)2009,JPO&amp;INPIT

Description

本発明は、低温で保存しても凍結せず、接着物性が良好であるクロロプレンラテックス及びその製造法に関するものである。なお、本発明における低温とは0℃以下を指す。   The present invention relates to a chloroprene latex that does not freeze even when stored at a low temperature and has good adhesive properties, and a method for producing the same. In addition, the low temperature in this invention refers to 0 degrees C or less.

クロロプレンゴム等をベースとした溶剤系接着剤は、その良好な作業性や接着物性から各種用途に用いられてきた。   Solvent-based adhesives based on chloroprene rubber and the like have been used for various applications because of their good workability and adhesive properties.

しかし、使用される有機溶剤は地球環境や作業者の健康に悪影響を与え、時には作業場の火災等を引き起こす危険性を有している。そのため、脱溶剤の要求が高まっている。   However, the organic solvent used has an adverse effect on the global environment and the health of workers, and sometimes has a risk of causing a fire in the workplace. Therefore, the demand for solvent removal is increasing.

脱溶剤化の手法の一つとして、ラテックス系接着剤による代替が考えられている。クロロプレンラテックスとしては各種のものが知られている(例えば、特許文献1〜特許文献4)。   As one of the methods for removing the solvent, substitution with a latex adhesive is considered. Various types of chloroprene latex are known (for example, Patent Documents 1 to 4).

しかし、特許文献1,2に示されるように、ポリビニルアルコール等の水溶性高分子を用いた場合、その保護コロイド性から優れたラテックスの安定性を示す一方で、期待される接着物性が得られず、特に耐水性が低くなる。   However, as shown in Patent Documents 1 and 2, when a water-soluble polymer such as polyvinyl alcohol is used, the latex exhibits excellent latex stability due to its protective colloid properties, while the expected adhesive properties are obtained. In particular, the water resistance is lowered.

また、特許文献3,4に示されるように、ロジン酸の金属塩からなる乳化剤を用いた場合、クロロプレンゴムの保管中における脱塩酸や、接着剤配合の際のpHの低下によりラテックスの安定性が低下し、ゴムが析出するなどの問題が生じる。   In addition, as shown in Patent Documents 3 and 4, when an emulsifier composed of a metal salt of rosin acid is used, the stability of the latex is reduced by dehydrochlorination during storage of chloroprene rubber or by lowering the pH when the adhesive is blended. Lowers and causes problems such as precipitation of rubber.

この特徴をうまく利用し、グリシンなどのアミノ酸でpHを調節し、湿潤状態での接着物性を向上させる方法がある(例えば、特許文献5)。   There is a method of making good use of this feature and adjusting the pH with an amino acid such as glycine to improve adhesive properties in a wet state (for example, Patent Document 5).

しかし、クロロプレンは保管中に脱塩酸するため、それによりpHが低下することで安定性が更に低下し、ゴムが析出してしまうなどの問題が生じる。   However, since chloroprene dehydrochlorinates during storage, the pH is lowered, thereby further reducing the stability and causing problems such as rubber precipitation.

一方、溶剤系接着剤と比較してラテックス系接着剤はコンタクト性が低い。この問題を解決する方法の1つとして、クロロホルムに溶解した際に不溶部となるゲル分を含まないクロロプレン系共重合体ラテックス及びそれを用いた接着剤組成物が知られている。(例えば、特許文献6、及び非特許文献1)。この方法で物性を向上させる場合、分子量が増加しゲルが生じると物性が低下することから、保管中に分子量が安定でゲル分が発生しないことが非常に重要となる。   On the other hand, latex adhesives have lower contact properties than solvent adhesives. As one of the methods for solving this problem, a chloroprene copolymer latex not containing a gel component that becomes an insoluble part when dissolved in chloroform and an adhesive composition using the same are known. (For example, Patent Document 6 and Non-Patent Document 1). When the physical properties are improved by this method, the physical properties are lowered when the molecular weight is increased and a gel is formed. Therefore, it is very important that the molecular weight is stable and no gel is generated during storage.

しかし、上記のようにクロロプレンゴムは保管中に脱塩酸し、それに伴い分子量増加が生じるため、保管中の脱塩酸の進行を遅らせることが重要となる。脱塩酸量は熱により増加するため低温保管が有効であるが、クロロプレンラテックスはその約半分を水が占める為、0℃以下で保管すると凍結してしまう危険性がある。   However, as described above, chloroprene rubber is dehydrochlorinated during storage, and the molecular weight increases accordingly, so it is important to delay the progress of dehydrochlorination during storage. Since the amount of dehydrochlorination increases due to heat, low-temperature storage is effective. However, since chloroprene latex occupies about half of the water, there is a risk of freezing if stored at 0 ° C. or lower.

特許文献7ではノニオン系乳化剤を使用することで低温安定性が改善するとされているが、5℃における1週間の評価であり、冬季や寒冷地では外気温が0℃以下となることも多く、これでは不十分である。   In Patent Document 7, it is said that the low-temperature stability is improved by using a nonionic emulsifier, but it is an evaluation for 1 week at 5 ° C., and the outside temperature is often 0 ° C. or less in winter and cold regions, This is not enough.

特開平6−287360号公報JP-A-6-287360 特開平11−335491号公報JP 11-335491 A 特公昭51−39262号公報Japanese Patent Publication No.51-39262 特開昭51−136733号公報Japanese Patent Laid-Open No. 51-136733 特開2001−19922号公報JP 2001-19922 A 特開平9−31429号公報JP-A-9-31429 特開2001−49043号公報JP 2001-49043 A JETI Vol.44 No.12(88頁)JETI Vol. 44 no. 12 (88 pages)

本発明はこの問題点に鑑みてなされたものであり、その目的は、カルボン酸のアルカリ金属塩からなる乳化剤を含むクロロプレンラテックスについて、0℃以下の低温保管での凍結を抑制し、低温保管を可能とすることで保管中のpH低下及び分子量変化を最小限に抑え、更には寒冷地への輸送・保管を容易とし、接着剤として用いた場合に良好な接着物性を示すクロロプレンラテックス及びその製造法を提供するものである。   The present invention has been made in view of this problem. The purpose of the present invention is to suppress freezing in a low-temperature storage at 0 ° C. or less for a chloroprene latex containing an emulsifier made of an alkali metal salt of a carboxylic acid. By making it possible to minimize pH drop and molecular weight change during storage, further facilitate transportation and storage in cold regions, and exhibit good adhesive properties when used as an adhesive, and its production It provides the law.

本発明者は、このような背景の下、上記課題を解決するため鋭意検討した結果、カルボン酸のアルカリ金属塩からなる乳化剤を含むクロロプレンラテックスについて、特定構造を有するノニオン系乳化剤を含有することで低温での保管が可能となり、保管中の分子量変化を抑え、良好な物性を長期間維持できることを見出し本発明を完成させるに至った。即ち、本発明は、カルボン酸のアルカリ金属塩からなる乳化剤及び、特定のノニオン系乳化剤を含むことを特徴とするクロロプレンラテックス、その製造法並びにそれを含有することを特徴とする接着剤組成物である。   As a result of intensive investigations to solve the above-described problems, the present inventor has found that a chloroprene latex containing an emulsifier composed of an alkali metal salt of a carboxylic acid contains a nonionic emulsifier having a specific structure. It has been found that storage at low temperatures is possible, molecular weight changes during storage can be suppressed, and good physical properties can be maintained for a long time, and the present invention has been completed. That is, the present invention relates to a chloroprene latex characterized by containing an emulsifier composed of an alkali metal salt of a carboxylic acid and a specific nonionic emulsifier, a method for producing the same, and an adhesive composition comprising the same. is there.

以下、本発明について詳細に説明する。   Hereinafter, the present invention will be described in detail.

本発明のクロロプレンラテックスは、カルボン酸のアルカリ金属塩からなる乳化剤及び、HLBが9〜16である下記一般式(1)で表されるノニオン系乳化剤を含むものである。   The chloroprene latex of the present invention contains an emulsifier composed of an alkali metal salt of a carboxylic acid and a nonionic emulsifier represented by the following general formula (1) having an HLB of 9 to 16.

R−O(CHCXHO)nH (1)
(式中、Rは炭素数9〜16で分岐を有するアルキル鎖からなる親油基を表し、Xは水素又は炭素数1〜2のアルキル鎖を表し、nはノニオン系乳化剤のHLBが9〜16になる範囲の整数を表す。)
本発明のクロロプレンラテックスとは、2−クロロ−1,3−ブタジエンであるクロロプレンの単量体を重合して得られたラテックスであり、必要に応じて、クロロプレン単量体と共重合可能な単量体を用いても良い。クロロプレン単量体と共重合可能な単量体としては、例えば、2,3−ジクロロ−1,3ブタジエン、ブタジエン、イソプレン、スチレン、アクリロニトリル、メチルメタクリレート、ヒドロキシエチルメタクリレート、ヒドロキシプロピルメタクリレート、ポリエチレングリコールモノアクリレート、ポリエチレングリコールモノメタクリレート、グリセリンモノメタクリレート、アクリル酸、メタクリル酸、フマル酸、マレイン酸、クロトン酸、シトラコン酸、2−メタクリロイロキシエチルコハク酸等があげられるが、これらを、例えばクロロプレン単量体100重量部に対し、20重量部以下で用いる。
R—O (CH 2 CXHO) nH (1)
(In the formula, R represents a lipophilic group composed of an alkyl chain having 9 to 16 carbon atoms and a branched chain, X represents hydrogen or an alkyl chain having 1 to 2 carbon atoms, and n represents 9 to 9 HLB of a nonionic emulsifier. Represents an integer in the range of 16.)
The chloroprene latex of the present invention is a latex obtained by polymerizing a monomer of chloroprene, which is 2-chloro-1,3-butadiene, and can be copolymerized with the chloroprene monomer as required. A mer may be used. Examples of the monomer copolymerizable with the chloroprene monomer include 2,3-dichloro-1,3-butadiene, butadiene, isoprene, styrene, acrylonitrile, methyl methacrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, and polyethylene glycol mono Examples include acrylate, polyethylene glycol monomethacrylate, glycerin monomethacrylate, acrylic acid, methacrylic acid, fumaric acid, maleic acid, crotonic acid, citraconic acid, 2-methacryloyloxyethyl succinic acid, and the like. It is used at 20 parts by weight or less with respect to 100 parts by weight of the body.

本発明のクロロプレンラテックスは、カルボン酸のアルカリ金属塩からなる乳化剤を含むものである。カルボン酸のアルカリ金属塩からなる乳化剤を含むことにより、pH調節により接着物性を向上させることが可能である。この乳化剤の含有量は特に限定するものではないが、ラテックスの配合における安定性や、接着物性とのバランスから、ラテックス100重量部に対して1.5〜3.5重量部が好ましい。ここに、カルボン酸のアルカリ金属塩からなる乳化剤としては、例えば、ロジン酸のアルカリ金属塩、脂肪酸のアルカリ金属塩、アルケニルコハク酸のアルカリ金属塩、ポリカルボン酸のアルカリ金属塩の高分子化合物等があげられる。アルカリ金属塩としてはリチウム、ナトリウム、カリウム、セシウムなどがあげられる。これらは、1種類でも良く、2種類以上を含んでいても良い。重合安定性及び接着性能の観点から、ロジン酸のアルカリ金属塩が好ましい。   The chloroprene latex of the present invention contains an emulsifier composed of an alkali metal salt of a carboxylic acid. By including an emulsifier composed of an alkali metal salt of carboxylic acid, it is possible to improve the adhesive properties by adjusting the pH. The content of the emulsifier is not particularly limited, but is preferably 1.5 to 3.5 parts by weight with respect to 100 parts by weight of the latex from the viewpoint of stability in the blending of the latex and adhesive properties. Here, as the emulsifier composed of an alkali metal salt of carboxylic acid, for example, an alkali metal salt of rosin acid, an alkali metal salt of fatty acid, an alkali metal salt of alkenyl succinic acid, a polymer compound of an alkali metal salt of polycarboxylic acid, etc. Can be given. Examples of the alkali metal salt include lithium, sodium, potassium, cesium and the like. These may be one type or may include two or more types. From the viewpoint of polymerization stability and adhesive performance, an alkali metal salt of rosin acid is preferred.

本発明のクロロプレンラテックスは、HLBが9〜16である下記一般式(1)で表されるノニオン系乳化剤を含むものである。   The chloroprene latex of the present invention contains a nonionic emulsifier represented by the following general formula (1) having an HLB of 9 to 16.

R−O(CHCXHO)nH (1)
(式中、Rは炭素数9〜16で分岐を有するアルキル鎖又からなる親油基を表し、Xは水素又は炭素数1〜2のアルキル鎖を表し、nはノニオン系乳化剤のHLBが9〜16になる範囲の整数を表す。)
一般式(1)で表されるノニオン系乳化剤とは、炭素数9〜16で分岐を有するアルキル鎖を有し、HLBが9〜16であるポリオキシアルキレン構造を有するノニオン系乳化剤をいい、例えば、ポリオキシエチレンイソデシルエーテル、ポリオキシプロピレンイソデシルエーテル、炭素数が9〜16のポリオキシエチレン分岐アルキルエーテル、炭素数が9〜16のポリオキシプロピレン分岐アルキルエーテル(具体的には、ポリオキシプロピレン分岐デシルエーテル、ポリオキシプロピレン分岐ドデシルエーテル等)等があげられる。アルキル鎖が分岐を有しない場合には、凍結に対する安定性が低い。HLBが9未満の場合は曇点が低いため熱に弱く、製造工程上で不具合が生じる可能性があり、16を超える場合には、凍結に対する安定性が低くなる。これらをラテックス100重量部に対して0.1〜3.0重量部含むことが好ましく、0.2〜2.0重量部含むことがさらに好ましい。
R—O (CH 2 CXHO) nH (1)
(In the formula, R represents a lipophilic group composed of an alkyl chain having 9 to 16 carbon atoms and a branched chain, X represents hydrogen or an alkyl chain having 1 to 2 carbon atoms, and n represents 9 HLB of a nonionic emulsifier. Represents an integer in the range of ~ 16.)
The nonionic emulsifier represented by the general formula (1) refers to a nonionic emulsifier having a polyoxyalkylene structure having a C9 to C16 branched alkyl chain and an HLB of 9 to 16, for example, , Polyoxyethylene isodecyl ether, polyoxypropylene isodecyl ether, polyoxyethylene branched alkyl ether having 9 to 16 carbon atoms, polyoxypropylene branched alkyl ether having 9 to 16 carbon atoms (specifically, polyoxyethylene Propylene branched decyl ether, polyoxypropylene branched dodecyl ether, etc.). If the alkyl chain is not branched, stability to freezing is low. If the HLB is less than 9, the cloud point is low, so it is weak against heat and may cause problems in the production process. If it exceeds 16, the stability against freezing is low. These are preferably contained in an amount of 0.1 to 3.0 parts by weight, more preferably 0.2 to 2.0 parts by weight, based on 100 parts by weight of latex.

本発明のクロロプレンラテックスは、ラテックスの安定性確保のために、さらにスルホン酸のアルカリ金属塩及び/又は硫酸エステルのアルカリ金属塩からなる安定剤を含有することが好ましい。スルホン酸のアルカリ金属塩からなる安定剤としては、例えば、ペンタンスルホン酸のアルカリ金属塩,オクタンスルホン酸のアルカリ金属塩などの脂肪族スルホン酸のアルカリ金属塩、トルエンスルホン酸のアルカリ金属塩,スチレンスルホン酸のアルカリ金属塩,ナフタレンスルホン酸のアルカリ金属塩,ブチルナフタレンスルホン酸のアルカリ金属塩などの芳香族スルホン酸のアルカリ金属塩、及びこれらのスルホン酸化合物のアルカリ金属塩を有する各種化合物等があげられる。スルホン酸化合物のアルカリ金属塩を有する各種化合物としては、ナフタレンスルホン酸のアルカリ金属塩とホルマリンの縮合物、不飽和結合を有するスルホン酸のアルカリ金属塩とそれと共重合可能な単量体との各種共重合体などがあり、不飽和結合を有するスルホン酸のアルカリ金属塩としては、例えば、ビニルスルホン酸のアルカリ金属塩、アリルスルホン酸のアルカリ金属塩、メタリルスルホン酸のアルカリ金属塩、イソプレンスルホン酸のアルカリ金属塩、スチレンスルホン酸のアルカリ金属塩などがあげられ、それと共重合可能な単量体としてはアクリル酸、メタクリル酸、フマル酸、マレイン酸、メチルメタクリレートなどがあげられる。硫酸エステルのアルカリ金属塩からなる安定剤としては、例えば、ラウリル硫酸のアルカリ金属塩などのアルキル硫酸エステル塩、ポリオキシエチレンラウリルエーテル硫酸のアルカリ金属塩などのポリオキシエチレンアルキルエーテル硫酸エステルアルカリ金属塩等があげられる。アルカリ金属塩としてはリチウム、ナトリウム、カリウム、セシウムなどがあげられる。これらは、1種類でも良く、2種類以上含んでいても良い。これらの中でも、重合安定性の面及び湿潤状態における接着物性の面から、ナフタレンスルホン酸のアルカリ金属塩とホルマリンの縮合物又はスチレンスルホン酸のアルカリ金属塩とメタクリル酸のアルカリ金属塩の共重合体が好ましい。スルホン酸のアルカリ金属塩及び/又は硫酸エステルのアルカリ金属塩からなる安定剤の含有量は特に限定するものではないが、重合およびラテックスの安定性確保のため、ラテックス100重量部に対して0.01〜2.0重量部が好ましい。   The chloroprene latex of the present invention preferably further contains a stabilizer composed of an alkali metal salt of sulfonic acid and / or an alkali metal salt of sulfate ester in order to ensure the stability of the latex. Examples of the stabilizer composed of an alkali metal salt of sulfonic acid include alkali metal salts of aliphatic sulfonic acids such as alkali metal salts of pentane sulfonic acid, alkali metal salts of octane sulfonic acid, alkali metal salts of toluene sulfonic acid, and styrene. Alkali metal salts of sulfonic acids, alkali metal salts of naphthalene sulfonic acid, alkali metal salts of aromatic sulfonic acids such as alkali metal salts of butyl naphthalene sulfonic acid, and various compounds having alkali metal salts of these sulfonic acid compounds can give. Examples of various compounds having an alkali metal salt of a sulfonic acid compound include condensates of an alkali metal salt of naphthalene sulfonic acid and formalin, an alkali metal salt of a sulfonic acid having an unsaturated bond, and a monomer copolymerizable therewith. Examples of the alkali metal salt of sulfonic acid having a copolymer and having an unsaturated bond include, for example, alkali metal salts of vinyl sulfonic acid, alkali metal salts of allyl sulfonic acid, alkali metal salts of methallyl sulfonic acid, and isoprene sulfone. Examples thereof include alkali metal salts of acids and alkali metal salts of styrene sulfonic acid, and monomers copolymerizable therewith include acrylic acid, methacrylic acid, fumaric acid, maleic acid, methyl methacrylate and the like. Examples of the stabilizer comprising an alkali metal salt of a sulfate ester include an alkyl sulfate ester salt such as an alkali metal salt of lauryl sulfate, and a polyoxyethylene alkyl ether sulfate alkali metal salt such as an alkali metal salt of polyoxyethylene lauryl ether sulfate. Etc. Examples of the alkali metal salt include lithium, sodium, potassium, cesium and the like. These may be one type or two or more types. Among these, from the viewpoint of polymerization stability and adhesive properties in a wet state, a condensate of an alkali metal salt of naphthalene sulfonic acid and formalin or a copolymer of an alkali metal salt of styrene sulfonic acid and an alkali metal salt of methacrylic acid. Is preferred. The content of the stabilizer composed of the alkali metal salt of sulfonic acid and / or the alkali metal salt of sulfate ester is not particularly limited, but is 0.1. 01 to 2.0 parts by weight are preferred.

クロロプレンラテックス中のポリマーのゲル分は、特に室温乾燥における初期の接着性を良好にするため、1重量%以下であることが好ましい。   The gel content of the polymer in the chloroprene latex is preferably 1% by weight or less in order to improve the initial adhesion particularly at room temperature drying.

本発明のクロロプレンラテックスの製造法としては、例えば、カルボン酸のアルカリ金属塩からなる乳化剤の存在下でクロロプレン単量体又はクロロプレン単量体とこの単量体と共重合可能な単量体を重合する際に、HLBが9〜16である下記一般式(1)で表されるノニオン系乳化剤を添加するものである。   As a method for producing the chloroprene latex of the present invention, for example, in the presence of an emulsifier composed of an alkali metal salt of a carboxylic acid, a chloroprene monomer or a monomer copolymerizable with this monomer is polymerized. In this case, a nonionic emulsifier represented by the following general formula (1) having an HLB of 9 to 16 is added.

R−O(CHCXHO)nH (1)
(式中、Rは炭素数9〜16で分岐を有するアルキル鎖からなる親油基を表し、Xは水素又は炭素数1〜2のアルキル鎖を表し、nはノニオン系乳化剤のHLBが9〜16になる範囲の整数を表す。)
カルボン酸のアルカリ金属塩からなる乳化剤の使用量は特に限定するものではないが、重合およびラテックスの安定性確保のため、クロロプレン単量体100重量部に対して3〜6重量部が好ましい。
R—O (CH 2 CXHO) nH (1)
(In the formula, R represents a lipophilic group composed of an alkyl chain having 9 to 16 carbon atoms and a branched chain, X represents hydrogen or an alkyl chain having 1 to 2 carbon atoms, and n represents 9 to 9 HLB of a nonionic emulsifier. Represents an integer in the range of 16.)
Although the usage-amount of the emulsifier which consists of an alkali metal salt of carboxylic acid is not specifically limited, 3-6 weight part is preferable with respect to 100 weight part of chloroprene monomers for ensuring stability of superposition | polymerization and latex.

一般式(1)で表されるノニオン系乳化剤の使用量は特に限定するものではないが、凍結に対する安定性確保のために、クロロプレン単量体100重量部に対して0.2重量部以上が好ましく、接着物性維持のためクロロプレン単量体100重量部に対して5重量部以下が好ましい。   The amount of the nonionic emulsifier represented by the general formula (1) is not particularly limited, but in order to ensure stability against freezing, 0.2 part by weight or more is required with respect to 100 parts by weight of the chloroprene monomer. Preferably, 5 parts by weight or less is preferable with respect to 100 parts by weight of the chloroprene monomer for maintaining adhesive properties.

一般式(1)で表されるノニオン系乳化剤は、重合開始時、重合中及び重合終了後のうち、何れかの段階で1回以上添加するものである。
The nonionic emulsifier represented by the general formula (1) is added one or more times at any stage of the start of polymerization, during the polymerization and after the completion of the polymerization.

スルホン酸のアルカリ金属塩及び/又は硫酸エステルのアルカリ金属塩からなる安定剤を使用する場合の量は特に限定するものではないが、重合安定性のため、クロロプレン単量体100重量部に対して0.01〜3.0重量部が好ましく、0.1〜1.5重量部がさらに好ましい。   The amount in the case of using a stabilizer comprising an alkali metal salt of sulfonic acid and / or an alkali metal salt of sulfate ester is not particularly limited, but for polymerization stability, it is based on 100 parts by weight of chloroprene monomer. 0.01-3.0 weight part is preferable and 0.1-1.5 weight part is further more preferable.

重合の方法としては特に制限のあるものではなく、例えば、クロロプレン単量体、又はクロロプレン単量体とこの単量体と共重合可能なその他の単量体をラジカル乳化重合すればよい。乳化重合は、上記の単量体、及び乳化剤を、重合開始剤、連鎖移動剤等と共に乳化し、所定温度にて行い、所定の転化率で重合停止剤を添加すれば良い。   The polymerization method is not particularly limited, and for example, chloroprene monomer, or chloroprene monomer and another monomer copolymerizable with this monomer may be subjected to radical emulsion polymerization. Emulsion polymerization may be carried out by emulsifying the above-mentioned monomer and emulsifier together with a polymerization initiator, a chain transfer agent, etc. at a predetermined temperature, and adding a polymerization terminator at a predetermined conversion rate.

重合開始剤としては、公知のフリーラジカル性物質、例えば、過硫酸カリウム、過硫酸アンモニウム等の過酸化物、過酸化水素、ターシャリーブチルヒドロパーオキサイド等の無機又は有機過酸化物等を用いることができる。また、これらは単独又は還元性物質、例えば、チオ硫酸塩、チオ亜硫酸塩、ハイドロサルファイト、有機アミン等との併用レドックス系で用いても良い。   As the polymerization initiator, a known free radical substance such as a peroxide such as potassium persulfate or ammonium persulfate, or an inorganic or organic peroxide such as hydrogen peroxide or tertiary butyl hydroperoxide may be used. it can. These may be used alone or in combination with a reducing substance, for example, a combined redox system with thiosulfate, thiosulfite, hydrosulfite, organic amine and the like.

連鎖移動剤としては、例えば、アルキルメルカプタン、ハロゲン炭化水素、アルキルキサントゲンジスルフィド、硫黄等の分子量調節剤等があげられ、これらのうち、臭気及び作業性の面からn−ドデシルメルカプタンが好ましく、その使用量はクロロプレン単量体100重量部に対して0.01〜1.0重量部が好ましく、0.1〜0.5重量部がさらに好ましい。   Examples of chain transfer agents include molecular weight regulators such as alkyl mercaptans, halogen hydrocarbons, alkyl xanthogen disulfides, sulfur, etc. Among these, n-dodecyl mercaptan is preferred in terms of odor and workability, and its use The amount is preferably from 0.01 to 1.0 part by weight, more preferably from 0.1 to 0.5 part by weight, based on 100 parts by weight of the chloroprene monomer.

重合温度は特に限定するものではなく、0〜80℃の範囲で行うことができ、好ましくは10〜50℃の範囲である。   The polymerization temperature is not particularly limited and can be carried out in the range of 0 to 80 ° C, preferably in the range of 10 to 50 ° C.

重合終了時期は特に限定するものでないが、生産性、及び良好な接着物性を得るため、単量体の転化率が60〜100%まで重合を行うことが好ましい。   Although the completion | finish time of superposition | polymerization is not specifically limited, In order to obtain productivity and favorable adhesive property, it is preferable to superpose | polymerize until the conversion rate of a monomer is 60-100%.

重合停止剤としては、通常用いられる停止剤であれば特に限定するものでなく、例えば、フェノチアジン、2,6−t−ブチル−4−メチルフェノール、ヒドロキシルアミン等が使用できる。   The polymerization terminator is not particularly limited as long as it is a commonly used terminator, and for example, phenothiazine, 2,6-tert-butyl-4-methylphenol, hydroxylamine and the like can be used.

また、ラテックスの安定性を更に良好にするため、重合中、及び重合終了後に上記の乳化剤や安定剤のうち1種類以上を添加しても良い。   Further, in order to further improve the stability of the latex, one or more of the above-mentioned emulsifiers and stabilizers may be added during and after the polymerization.

本発明のクロロプレンラテックスは、単独でも接着剤として使用可能であるが、粘着付与樹脂や架橋剤を添加することで接着物性が向上する。   The chloroprene latex of the present invention can be used alone as an adhesive, but the adhesive properties are improved by adding a tackifying resin or a crosslinking agent.

粘着付与樹脂としては特に限定するものではなく、例えば、フェノール系樹脂、テルペン系樹脂、ロジン誘導体樹脂、石油系炭化水素等があげられ、例えば、重合ロジン、ロジン変性樹脂、ロジン変性フェノール樹脂、ロジンエステル、アルキルフェノール樹脂、テルペン樹脂、テルペンフェノール、水添ロジン、水添ロジンのペンタエリスリトールエステル、石油樹脂、クマロン樹脂等が使用される。   The tackifying resin is not particularly limited, and examples thereof include phenol resins, terpene resins, rosin derivative resins, petroleum hydrocarbons, and the like, such as polymerized rosin, rosin modified resin, rosin modified phenol resin, rosin. Esters, alkylphenol resins, terpene resins, terpene phenols, hydrogenated rosins, hydrogenated rosin pentaerythritol esters, petroleum resins, coumarone resins, and the like are used.

架橋剤としては、クロロプレンラテックスに均一に混合できる化合物であれば用いることができ、例えば、エポキシ樹脂、ポリイソシアネート化合物等が使用できる。   As the cross-linking agent, any compound that can be uniformly mixed with chloroprene latex can be used. For example, an epoxy resin, a polyisocyanate compound, or the like can be used.

クロロプレンラテックスを主成分とする接着剤の粘度は、各種増粘剤、例えば、ポリアルキレンオキサイド、ポリビニルアルコール、疎水化セルロース、会合型ノニオン界面活性剤等の水溶性ポリマー、及びカルボキシル基含有ポリマーから構成されるアルカリ可溶型の増粘剤、ヘクトライト等のシリケート化合物等の配合により所望の粘度に調整できる。また必要に応じて、老化防止剤、防腐剤、凍結防止剤、造膜助剤、可塑剤、クレー等の各種充填剤を適宜配合しても良い。   The viscosity of the adhesive mainly composed of chloroprene latex is composed of various thickeners, for example, water-soluble polymers such as polyalkylene oxide, polyvinyl alcohol, hydrophobic cellulose, associative nonionic surfactants, and carboxyl group-containing polymers. The viscosity can be adjusted to a desired level by blending an alkali-soluble thickener and a silicate compound such as hectorite. Moreover, you may mix | blend various fillers, such as anti-aging agent, antiseptic | preservative, antifreezing agent, film-forming aid, a plasticizer, clay, as needed.

本発明のクロロプレンラテックスは、上記の通りすることにより、長期間の保管において分子量の上昇が少なく、低温で保存しても凍結せず、その結果、これを含有する接着剤組成物は安定して良好な接着物性を示すものである。   As described above, the chloroprene latex of the present invention has little increase in molecular weight during long-term storage and does not freeze even when stored at a low temperature. As a result, the adhesive composition containing the latex is stable. It exhibits good adhesive properties.

以下、本発明を実施例によって具体的に説明するが、本発明はこれらの実施例のみに限定されるものではない。   EXAMPLES Hereinafter, the present invention will be specifically described with reference to examples, but the present invention is not limited to only these examples.

ラテックスのpH、機械的安定性、配合安定性、ポリマーの溶液粘度、接着剤配合物の常温接着強度は以下の方法で測定した。   Latex pH, mechanical stability, blending stability, polymer solution viscosity, and normal temperature adhesive strength of the adhesive blend were measured by the following methods.

<pH>
pHメーター((株)堀場製作所製)により、23℃におけるラテックスのpHを測定した。
<PH>
The pH of the latex at 23 ° C. was measured with a pH meter (manufactured by Horiba, Ltd.).

<ポリマーのゲル分及び溶液粘度>
ラテックスをシャーレ上に広げ、ドライアイス/メタノールの冷媒にて冷却・凍結後、真空乾燥機において30℃以下で凍結乾燥を実施した。16時間以上経過後に秤量し、更に2時間後に再度秤量を実施して重量変化が1%以下となるまで乾燥した。その後、ゴムが重量換算で0.6%の濃度となるようにトルエンを加え、マグネットスターラーを用いて20時間以上混合・溶解した。得られた溶液を2500RPMで30分遠心分離をかけた後、200メッシュの金網にてろ過し、残渣を110℃で20分乾燥してその重量と溶解したゴムの重量の比をゲル分とした。またゲル分同様にゴムを重量換算で10%の濃度となるようにトルエンに溶解し、その粘度をB型粘度計を用いて測定した。測定は、試料容器を23℃の恒温槽に1時間浸漬した後に、No.3ローターを用いて60rpmで測定、60秒後の値を用いた。測定範囲外の高粘度の場合は12rpmで再度測定した。
<Polymer gel content and solution viscosity>
The latex was spread on a petri dish, cooled and frozen with a dry ice / methanol refrigerant, and then lyophilized at 30 ° C. or lower in a vacuum dryer. After weighing for 16 hours or more, the sample was weighed, and after another 2 hours, weighed again and dried until the weight change became 1% or less. Thereafter, toluene was added so that the rubber had a concentration of 0.6% in terms of weight, and mixed and dissolved for 20 hours or more using a magnetic stirrer. The resulting solution was centrifuged at 2500 RPM for 30 minutes and then filtered through a 200 mesh wire mesh. The residue was dried at 110 ° C. for 20 minutes, and the ratio of the weight of the dissolved rubber to the weight of the dissolved rubber was taken as the gel content. . Similarly to the gel content, rubber was dissolved in toluene so as to have a concentration of 10% in terms of weight, and the viscosity was measured using a B-type viscometer. The measurement was conducted by immersing the sample container in a thermostat at 23 ° C. for 1 hour, Measurement was performed at 60 rpm using 3 rotors, and the value after 60 seconds was used. In the case of high viscosity outside the measurement range, the measurement was performed again at 12 rpm.

<配合安定性>
接着剤配合時のゴム析出有無を観察した。
<Compounding stability>
The presence or absence of rubber precipitation during the blending of the adhesive was observed.

<塩素イオン濃度測定>
純水150mlにラテックス5ml及び10%硝酸水溶液0.1mlを混合し、1/20硝酸銀水溶液を滴定液として電位差自動滴定装置(KYOTO ELECTRONICS製AT−400)にてラテックス中の塩素イオンの濃度を測定した。
<Chlorine ion concentration measurement>
Mixing 5 ml of latex and 0.1 ml of 10% nitric acid aqueous solution with 150 ml of pure water, and measuring the concentration of chloride ion in latex with potentiometric automatic titrator (AT-400 manufactured by KYOTO ELECTRONICS) using 1/20 silver nitrate aqueous solution as titrant did.

<接着強度>
9号帆布2枚(約150mm×60mm)それぞれの片面に下塗りとして刷毛で接着剤組成物を約250g/m塗布し、80℃で5分乾燥後冷却を行うことで被着体を作製した。それに、接着剤組成物を刷毛で110g/m塗布した後23℃にて所定時間乾燥し、ハンドローラーを用いて圧着し、150mm×25mmのサイズに切り出したものを測定用の試験片とした。接着強度の測定はテンシロン型引っ張り試験機を用いて23℃の雰囲気下にて100mm/minの剥離速度で180°方向のT字型剥離試験にて行った。測定は圧着してから2分後及び1日後に実施した。
<Adhesive strength>
The adhesive composition was prepared by applying about 250 g / m 2 of the adhesive composition with a brush as an undercoat on one side of each of No. 9 canvas (about 150 mm × 60 mm), drying at 80 ° C. for 5 minutes and then cooling. . Then, the adhesive composition was applied at 110 g / m 2 with a brush, dried at 23 ° C. for a predetermined time, pressure-bonded using a hand roller, and cut into a size of 150 mm × 25 mm as a test specimen for measurement. . The adhesive strength was measured by a T-shaped peel test in a 180 ° direction at a peel rate of 100 mm / min in a 23 ° C. atmosphere using a Tensilon type tensile tester. The measurement was carried out 2 minutes and 1 day after the pressure bonding.

実施例1
表1で示した割合のクロロプレン単量体、n−ドデシルメルカプタン、ロジン酸カリウム(商品名:ロンヂスK−25、荒川化学(株))、ナフタレンスルホン酸ナトリウムとホルムアルデヒドの縮合物(商品名:デモールN、花王(株))、水酸化ナトリウム、ハイドロサルファイトナトリウム、及び純水を攪拌機付き10Lオートクレーブ中10℃で重合を行い、クロロプレンラテックスを作製した。重合は窒素雰囲気下で0.35重量%の過硫酸カリウム水溶液を連続的に滴下して行い、重合転化率が約90%となった時点で重合停止剤として2,6−ターシャリーブチル−4−メチルフェノール0.05重量部を添加し重合を停止した。その後、減圧下で未反応単量体の除去及び濃縮によりラテックスの固形分を55%に調整しラテックスAを得た。ラテックスA中のポリマーのゲル分は0.2重量%であった。
Example 1
Chloroprene monomer, n-dodecyl mercaptan, potassium rosinate (trade name: Longis K-25, Arakawa Chemical Co., Ltd.), sodium naphthalene sulfonate and formaldehyde condensate (trade name: demole) in the proportions shown in Table 1 N, Kao Corporation), sodium hydroxide, hydrosulfite sodium, and pure water were polymerized at 10 ° C. in a 10 L autoclave equipped with a stirrer to prepare chloroprene latex. Polymerization was carried out by continuously dropping a 0.35% by weight aqueous potassium persulfate solution under a nitrogen atmosphere, and 2,6-tertiarybutyl-4 as a polymerization terminator when the polymerization conversion reached about 90%. -The polymerization was stopped by adding 0.05 parts by weight of methylphenol. Thereafter, the solid content of the latex was adjusted to 55% by removing and concentrating unreacted monomers under reduced pressure to obtain Latex A. The gel content of the polymer in Latex A was 0.2% by weight.

Figure 0005262199
ラテックスA100重量部に対し、ポリオキシエチレンイソデシルエーテル(商品名:ノイゲンSD−80、第一工業製薬(株)HLB=14.3)の20%水溶液を純分換算で0.25重量部となるよう添加(クロロプレン単量体100重量部に対して約0.45重量部相当)してラテックスを得た(ラテックス中のポリマーのゲル分:0.2重量%)。
Figure 0005262199
With respect to 100 parts by weight of latex A, a 20% aqueous solution of polyoxyethylene isodecyl ether (trade name: Neugen SD-80, Daiichi Kogyo Seiyaku HLB = 14.3) is 0.25 parts by weight in terms of pure content. This was added (corresponding to about 0.45 parts by weight with respect to 100 parts by weight of the chloroprene monomer) to obtain a latex (the polymer gel content in the latex: 0.2% by weight).

得られたラテックスの一部を容器に入れ、−3〜−7℃の雰囲気で1週間保管し、保管によるラテックスの凍結の有無を確認した。また、ラテックスに樹脂エマルジョン、金属酸化物、増粘剤を配合して接着剤組成物を作製し、その配合安定性、常温接着強度を測定した。配合を表2に示し、結果を表3に示す。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。   Part of the obtained latex was put in a container and stored in an atmosphere at -3 to -7 ° C for 1 week, and it was confirmed whether or not the latex was frozen by storage. Moreover, resin emulsion, a metal oxide, and a thickener were mix | blended with latex, the adhesive composition was produced, and the mixing | blending stability and normal temperature adhesive strength were measured. The formulation is shown in Table 2, and the results are shown in Table 3. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

Figure 0005262199
Figure 0005262199

Figure 0005262199
実施例2
ラテックスA100重量部に対するポリオキシエチレンイソデシルエーテルの添加量を2重量部(クロロプレン単量体100重量部に対して約3.6重量部相当)に変更した以外は実施例1に従ってラテックスを得て(ラテックス中のポリマーのゲル分:0.2重量%)評価を実施した。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。
Figure 0005262199
Example 2
A latex was obtained according to Example 1 except that the amount of polyoxyethylene isodecyl ether added to 100 parts by weight of latex A was changed to 2 parts by weight (equivalent to about 3.6 parts by weight with respect to 100 parts by weight of chloroprene monomer). (Gel content of polymer in latex: 0.2% by weight) Evaluation was performed. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

実施例3
ポリオキシエチレンイソデシルエーテルを、ポリオキシプロピレン分岐デシルエーテルA(商品名:ノイゲンXL−60、第一工業製薬(株)HLB=12.5)に変更した以外は実施例1に従ってラテックスを得て(ラテックス中のポリマーのゲル分:0.2重量%)評価を実施した。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。
Example 3
A latex was obtained according to Example 1 except that polyoxyethylene isodecyl ether was changed to polyoxypropylene branched decyl ether A (trade name: Neugen XL-60, Daiichi Kogyo Seiyaku HLB = 12.5). (Gel content of polymer in latex: 0.2% by weight) Evaluation was performed. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

実施例4
ポリオキシエチレンイソデシルエーテルを、ポリオキシプロピレン分岐デシルエーテルB(商品名:ノイゲンXL−100、第一工業製薬(株)HLB=14.7)に変更した以外は実施例1に従ってラテックスを得て(ラテックス中のポリマーのゲル分:0.2重量%)評価を実施した。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。
Example 4
A latex was obtained according to Example 1 except that polyoxyethylene isodecyl ether was changed to polyoxypropylene branched decyl ether B (trade name: Neugen XL-100, Daiichi Kogyo Seiyaku HLB = 14.7). (Gel content of polymer in latex: 0.2% by weight) Evaluation was performed. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

実施例5
ポリオキシエチレンイソデシルエーテルを、ポリオキシエチレン分岐アルキルエーテルA(商品名:エマルゲン705、花王(株)HLB=10.5)に変更した以外は実施例1に従ってラテックスを得て(ラテックス中のポリマーのゲル分:0.2重量%)評価を実施した。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。
Example 5
A latex was obtained in accordance with Example 1 except that polyoxyethylene isodecyl ether was changed to polyoxyethylene branched alkyl ether A (trade name: Emulgen 705, Kao Corporation HLB = 10.5) (polymer in latex) The gel content: 0.2% by weight) was evaluated. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

実施例6
ポリオキシエチレンイソデシルエーテルを、ポリオキシエチレン分岐アルキルエーテルB(商品名:エマルゲン707、花王(株)HLB=12.1)に変更した以外は実施例1に従ってラテックスを得て(ラテックス中のポリマーのゲル分:0.2重量%)評価を実施した。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。
Example 6
A latex was obtained according to Example 1 except that polyoxyethylene isodecyl ether was changed to polyoxyethylene branched alkyl ether B (trade name: Emulgen 707, Kao Corporation HLB = 12.1) (polymer in latex) The gel content: 0.2% by weight) was evaluated. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

実施例7
ポリオキシエチレンイソデシルエーテルを、ポリオキシエチレン分岐アルキルエーテルC(商品名:エマルゲン709、花王(株)HLB=13.3)に変更した以外は実施例1に従ってラテックスを得て(ラテックス中のポリマーのゲル分:0.2重量%)評価を実施した。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。
Example 7
A latex was obtained (polymer in latex) according to Example 1 except that polyoxyethylene isodecyl ether was changed to polyoxyethylene branched alkyl ether C (trade name: Emulgen 709, Kao Corporation HLB = 13.3). The gel content: 0.2% by weight) was evaluated. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

実施例8
表1で示した割合のクロロプレン単量体、n−ドデシルメルカプタン、ロジン酸カリウム(商品名:ロンヂスK−25、荒川化学(株))、スチレンスルホン酸ナトリウム−メタクリル酸ナトリウム共重合体、水酸化ナトリウム、ハイドロサルファイトナトリウム、及び純水を攪拌機付き10Lオートクレーブ中10℃で重合を行い、クロロプレンラテックスを作製した。重合は窒素雰囲気下で0.35重量%の過硫酸カリウム水溶液を連続的に滴下して行い、重合転化率が約90%となった時点で重合停止剤として2,6−ターシャリーブチル−4−メチルフェノール0.05重量部を添加し重合を停止した。その後、減圧下で未反応単量体の除去及び濃縮によりラテックスの固形分を55%に調整しラテックスBを得た。ラテックスB中のポリマーのゲル分は0.3重量%であった。
Example 8
Chloroprene monomer, n-dodecyl mercaptan, potassium rosinate (trade name: Longes K-25, Arakawa Chemical Co., Ltd.), sodium styrenesulfonate-sodium methacrylate copolymer, hydroxylated in the proportions shown in Table 1 Sodium, hydrosulfite sodium, and pure water were polymerized at 10 ° C. in a 10 L autoclave with a stirrer to prepare chloroprene latex. Polymerization was carried out by continuously dropping a 0.35% by weight aqueous potassium persulfate solution under a nitrogen atmosphere, and 2,6-tertiarybutyl-4 as a polymerization terminator when the polymerization conversion reached about 90%. -The polymerization was stopped by adding 0.05 parts by weight of methylphenol. Thereafter, the solid content of the latex was adjusted to 55% by removing and concentrating unreacted monomers under reduced pressure to obtain Latex B. The gel content of the polymer in Latex B was 0.3% by weight.

ラテックスB100重量部に対し、ポリオキシエチレンイソデシルエーテル(商品名:ノイゲンSD−80、第一工業製薬(株)HLB=14.3)の20%水溶液を純分換算で0.25重量部となるよう添加(クロロプレン単量体100重量部に対して約0.45重量部相当)してラテックスを得た(ラテックス中のポリマーのゲル分:0.3重量%)。   With respect to 100 parts by weight of latex B, a 20% aqueous solution of polyoxyethylene isodecyl ether (trade name: Neugen SD-80, Daiichi Kogyo Seiyaku Co., Ltd., HLB = 14.3) is 0.25 parts by weight in terms of pure content. This was added (corresponding to about 0.45 parts by weight with respect to 100 parts by weight of the chloroprene monomer) to obtain a latex (the gel content of the polymer in the latex: 0.3% by weight).

得られたラテックスの一部を容器に入れ、−3〜−7℃の雰囲気で1週間保管し、保管によるラテックスの凍結の有無を確認した。また、ラテックスに樹脂エマルジョン、金属酸化物、増粘剤を配合して接着剤組成物を作製し、その配合安定性、常温接着強度を測定した。配合を表2に示し、結果を表3に示す。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。   Part of the obtained latex was put in a container and stored in an atmosphere at -3 to -7 ° C for 1 week, and it was confirmed whether or not the latex was frozen by storage. Moreover, resin emulsion, a metal oxide, and a thickener were mix | blended with latex, the adhesive composition was produced, and the mixing | blending stability and normal temperature adhesive strength were measured. The formulation is shown in Table 2, and the results are shown in Table 3. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

実施例9
ポリオキシエチレンイソデシルエーテルを、ポリオキシプロピレン分岐デシルエーテルB(商品名:ノイゲンXL−100、第一工業製薬(株)HLB=14.7)に変更した以外は実施例8に従ってラテックスを得て(ラテックス中のポリマーのゲル分:0.3重量%)評価を実施した。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。
Example 9
A latex was obtained according to Example 8 except that polyoxyethylene isodecyl ether was changed to polyoxypropylene branched decyl ether B (trade name: Neugen XL-100, Daiichi Kogyo Seiyaku HLB = 14.7). (Gel content of polymer in latex: 0.3% by weight) Evaluation was carried out. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

実施例10
ポリオキシエチレンイソデシルエーテルを、ポリオキシエチレン分岐アルキルエーテルC(商品名:エマルゲン709、花王(株)HLB=13.3)に変更した以外は実施例8に従ってラテックスを得て(ラテックス中のポリマーのゲル分:0.3重量%)評価を実施した。表3の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。
Example 10
A latex was obtained according to Example 8 except that the polyoxyethylene isodecyl ether was changed to polyoxyethylene branched alkyl ether C (trade name: Emulgen 709, Kao Corporation HLB = 13.3) (polymer in latex) The gel content: 0.3 wt%) was evaluated. From the results shown in Table 3, the latex has good freezing stability and good adhesion strength without freezing even at -7 ° C.

実施例11
表1で示した割合のクロロプレン単量体、n−ドデシルメルカプタン、ロジン酸カリウム(商品名:ロンヂスK−25、荒川化学(株))、スチレンスルホン酸ナトリウム−メタクリル酸ナトリウム共重合体、水酸化ナトリウム、ハイドロサルファイトナトリウム、及び純水を攪拌機付き10Lオートクレーブ中30℃で重合を行い、クロロプレンラテックスを作製した。重合は窒素雰囲気下で0.35重量%の過硫酸カリウム水溶液を連続的に滴下して行い、重合転化率が約90%となった時点で重合停止剤として2,6−ターシャリーブチル−4−メチルフェノール0.05重量部を添加し重合を停止した。その後、減圧下で未反応単量体の除去及び濃縮によりラテックスの固形分を55%に調整しラテックスCを得た。ラテックスC中のポリマーのゲル分は0.3重量%であった。
Example 11
Chloroprene monomer, n-dodecyl mercaptan, potassium rosinate (trade name: Longes K-25, Arakawa Chemical Co., Ltd.), sodium styrenesulfonate-sodium methacrylate copolymer, hydroxylated in the proportions shown in Table 1 Sodium, hydrosulfite sodium and pure water were polymerized at 30 ° C. in a 10 L autoclave with a stirrer to prepare a chloroprene latex. Polymerization was carried out by continuously dropping a 0.35% by weight aqueous potassium persulfate solution under a nitrogen atmosphere, and 2,6-tertiarybutyl-4 as a polymerization terminator when the polymerization conversion reached about 90%. -The polymerization was stopped by adding 0.05 parts by weight of methylphenol. Thereafter, the solid content of the latex was adjusted to 55% by removing and concentrating unreacted monomers under reduced pressure to obtain Latex C. The gel content of the polymer in Latex C was 0.3% by weight.

ラテックスC100重量部に対し、ポリオキシエチレン分岐アルキルエーテルA(商品名:エマルゲン705、花王(株)HLB=10.5)の20%水溶液を純分換算で0.25重量部となるよう添加(クロロプレン単量体100重量部に対して約0.45重量部相当)してラテックスを得た(ラテックス中のポリマーのゲル分:0.3重量%)。   A 20% aqueous solution of polyoxyethylene branched alkyl ether A (trade name: Emulgen 705, Kao Corporation HLB = 10.5) is added to 100 parts by weight of latex C so as to be 0.25 parts by weight in terms of pure content ( A latex was obtained (corresponding to about 0.45 parts by weight with respect to 100 parts by weight of the chloroprene monomer) (the polymer gel content in the latex: 0.3% by weight).

得られたラテックスの一部を容器に入れ、−3〜−7℃の雰囲気で1週間保管し、保管によるラテックスの凍結の有無を確認した。また、ラテックスに樹脂エマルジョン、金属酸化物、増粘剤を配合して接着剤組成物を作製し、その配合安定性、常温接着強度を測定した。配合を表2に示し、結果を表4に示す。表4の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。   Part of the obtained latex was put in a container and stored in an atmosphere at -3 to -7 ° C for 1 week, and it was confirmed whether or not the latex was frozen by storage. Moreover, resin emulsion, a metal oxide, and a thickener were mix | blended with latex, the adhesive composition was produced, and the mixing | blending stability and normal temperature adhesive strength were measured. The formulation is shown in Table 2, and the results are shown in Table 4. From the results shown in Table 4, the latex had a good freezing stability and a good adhesive strength without freezing even at -7 ° C.

Figure 0005262199
実施例12
表1で示した割合のクロロプレン単量体、n−ドデシルメルカプタン、ロジン酸カリウム(商品名:ロンヂスK−25、荒川化学(株))、ナフタレンスルホン酸ナトリウムとホルムアルデヒドの縮合物(商品名:デモールN、花王(株))、ポリオキシエチレンイソデシルエーテル(商品名:ノイゲンSD−80、第一工業製薬(株)HLB=14.3)、水酸化ナトリウム、ハイドロサルファイトナトリウム、及び純水を攪拌機付き10Lオートクレーブ中10℃で重合を行い、クロロプレンラテックスを作製した。重合は窒素雰囲気下で0.35重量%の過硫酸カリウム水溶液を連続的に滴下して行い、重合転化率が約90%となった時点で重合停止剤として2,6−ターシャリーブチル−4−メチルフェノール0.05重量部を添加し重合を停止した。その後、減圧下で未反応単量体の除去及び濃縮によりラテックスの固形分を55%に調整しラテックスDを得た。ラテックスD中のポリマーのゲル分は0.4重量%であった。
Figure 0005262199
Example 12
Chloroprene monomer, n-dodecyl mercaptan, potassium rosinate (trade name: Longis K-25, Arakawa Chemical Co., Ltd.), sodium naphthalene sulfonate and formaldehyde condensate (trade name: demole) in the proportions shown in Table 1 N, Kao Corporation), polyoxyethylene isodecyl ether (trade name: Neugen SD-80, Daiichi Kogyo Seiyaku HLB = 14.3), sodium hydroxide, hydrosulfite sodium, and pure water. Polymerization was carried out at 10 ° C. in a 10 L autoclave with a stirrer to prepare a chloroprene latex. Polymerization was carried out by continuously dropping a 0.35% by weight aqueous potassium persulfate solution under a nitrogen atmosphere, and 2,6-tertiarybutyl-4 as a polymerization terminator when the polymerization conversion reached about 90%. -The polymerization was stopped by adding 0.05 parts by weight of methylphenol. Thereafter, the solid content of the latex was adjusted to 55% by removing and concentrating unreacted monomers under reduced pressure to obtain Latex D. The gel content of the polymer in latex D was 0.4% by weight.

ラテックスDの一部を容器に入れ、−3〜−7℃の雰囲気で1週間保管し、保管によるラテックスの凍結の有無を確認した。また、ラテックスに樹脂エマルジョン、金属酸化物、増粘剤を配合して接着剤組成物を作製し、その配合安定性、常温接着強度を測定した。配合を表2に示し、結果を表4に示す。表4の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。   A part of latex D was put in a container and stored in an atmosphere of -3 to -7 ° C for 1 week, and it was confirmed whether or not the latex was frozen by storage. Moreover, resin emulsion, a metal oxide, and a thickener were mix | blended with latex, the adhesive composition was produced, and the mixing | blending stability and normal temperature adhesive strength were measured. The formulation is shown in Table 2, and the results are shown in Table 4. From the results shown in Table 4, the latex had a good freezing stability and a good adhesive strength without freezing even at -7 ° C.

実施例13
表1で示した割合のクロロプレン単量体、n−ドデシルメルカプタン、ロジン酸カリウム(商品名:ロンヂスK−25、荒川化学(株))、スチレンスルホン酸ナトリウム−メタクリル酸ナトリウム共重合体、ポリオキシプロピレン分岐デシルエーテル(商品名:ノイゲンXL−100、第一工業製薬(株)HLB=14.7)、水酸化ナトリウム、ハイドロサルファイトナトリウム、及び純水を攪拌機付き10Lオートクレーブ中10℃で重合を行い、クロロプレンラテックスを作製した。重合は窒素雰囲気下で0.35重量%の過硫酸カリウム水溶液を連続的に滴下して行い、重合転化率が約90%となった時点で重合停止剤として2,6−ターシャリーブチル−4−メチルフェノール0.05重量部を添加し重合を停止した。その後、減圧下で未反応単量体の除去及び濃縮によりラテックスの固形分を55%に調整しラテックスEを得た。ラテックスE中のポリマーのゲル分は0.4重量%であった。
Example 13
Chloroprene monomer, n-dodecyl mercaptan, potassium rosinate (trade name: Longes K-25, Arakawa Chemical Co., Ltd.), sodium styrenesulfonate-sodium methacrylate copolymer, polyoxy in the proportions shown in Table 1 Polymerization of propylene branched decyl ether (trade name: Neugen XL-100, Daiichi Kogyo Seiyaku Co., Ltd. HLB = 14.7), sodium hydroxide, sodium hydrosulfite, and pure water at 10 ° C. in a 10 L autoclave with a stirrer And chloroprene latex was prepared. Polymerization was carried out by continuously dropping a 0.35% by weight aqueous potassium persulfate solution under a nitrogen atmosphere, and 2,6-tertiarybutyl-4 as a polymerization terminator when the polymerization conversion reached about 90%. -The polymerization was stopped by adding 0.05 parts by weight of methylphenol. Thereafter, the solid content of the latex was adjusted to 55% by removing and concentrating unreacted monomers under reduced pressure to obtain Latex E. The gel content of the polymer in Latex E was 0.4% by weight.

ラテックスEの一部を容器に入れ、−3〜−7℃の雰囲気で1週間保管し、保管によるラテックスの凍結の有無を確認した。また、ラテックスに樹脂エマルジョン、金属酸化物、増粘剤を配合して接着剤組成物を作製し、その配合安定性、常温接着強度を測定した。配合を表2に示し、結果を表4に示す。表4の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。   A part of latex E was put in a container and stored in an atmosphere of −3 to −7 ° C. for 1 week, and it was confirmed whether or not the latex was frozen by storage. Moreover, resin emulsion, a metal oxide, and a thickener were mix | blended with latex, the adhesive composition was produced, and the mixing | blending stability and normal temperature adhesive strength were measured. The formulation is shown in Table 2, and the results are shown in Table 4. From the results shown in Table 4, the latex had a good freezing stability and a good adhesive strength without freezing even at -7 ° C.

実施例14
表1で示した割合のクロロプレン単量体、n−ドデシルメルカプタン、ロジン酸カリウム(商品名:ロンヂスK−25、荒川化学(株))、スチレンスルホン酸ナトリウム−メタクリル酸ナトリウム共重合体、ポリオキシエチレン分岐アルキルエーテル(商品名:エマルゲン709、花王(株)HLB=13.3)、水酸化ナトリウム、ハイドロサルファイトナトリウム、及び純水を攪拌機付き10Lオートクレーブ中10℃で重合を行い、クロロプレンラテックスを作製した。重合は窒素雰囲気下で0.35重量%の過硫酸カリウム水溶液を連続的に滴下して行い、重合転化率が約90%となった時点で重合停止剤として2,6−ターシャリーブチル−4−メチルフェノール0.05重量部を添加し重合を停止した。その後、減圧下で未反応単量体の除去及び濃縮によりラテックスの固形分を55%に調整しラテックスFを得た。ラテックスF中のポリマーのゲル分は0.4重量%であった。
Example 14
Chloroprene monomer, n-dodecyl mercaptan, potassium rosinate (trade name: Longes K-25, Arakawa Chemical Co., Ltd.), sodium styrenesulfonate-sodium methacrylate copolymer, polyoxy in the proportions shown in Table 1 Ethylene branched alkyl ether (trade name: Emulgen 709, Kao Corporation HLB = 13.3), sodium hydroxide, sodium hydrosulfite, and pure water were polymerized at 10 ° C. in a 10 L autoclave equipped with a stirrer to obtain a chloroprene latex. Produced. Polymerization was carried out by continuously dropping a 0.35% by weight aqueous potassium persulfate solution under a nitrogen atmosphere, and 2,6-tertiarybutyl-4 as a polymerization terminator when the polymerization conversion reached about 90%. -The polymerization was stopped by adding 0.05 parts by weight of methylphenol. Thereafter, the solid content of the latex was adjusted to 55% by removing and concentrating unreacted monomers under reduced pressure to obtain Latex F. The gel content of the polymer in latex F was 0.4% by weight.

ラテックスFの一部を容器に入れ、−3〜−7℃の雰囲気で1週間保管し、保管によるラテックスの凍結の有無を確認した。また、ラテックスに樹脂エマルジョン、金属酸化物、増粘剤を配合して接着剤組成物を作製し、その配合安定性、常温接着強度を測定した。配合を表2に示し、結果を表4に示す。表4の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。   A part of latex F was put in a container and stored for 1 week in an atmosphere of −3 to −7 ° C., and it was confirmed whether or not the latex was frozen by storage. Moreover, resin emulsion, a metal oxide, and a thickener were mix | blended with latex, the adhesive composition was produced, and the mixing | blending stability and normal temperature adhesive strength were measured. The formulation is shown in Table 2, and the results are shown in Table 4. From the results shown in Table 4, the latex had a good freezing stability and a good adhesive strength without freezing even at -7 ° C.

実施例15
ラテックスB100重量部に対し、ナフタレンスルホン酸ナトリウムとホルムアルデヒドの縮合物(商品名:デモールN、花王(株))を0.5重量部、ポリオキシプロピレン分岐デシルエーテルA(商品名:ノイゲンXL−60、第一工業製薬(株)HLB=12.5)を0.25重量部(クロロプレン単量体100重量部に対して約0.45重量部相当)、添加してラテックスを得た(ラテックス中のポリマーのゲル分:0.4重量%)以外は、実施例1に従って評価を実施した。表4の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。
Example 15
0.5 parts by weight of a condensate of sodium naphthalenesulfonate and formaldehyde (trade name: Demol N, Kao Co., Ltd.) and polyoxypropylene branched decyl ether A (trade name: Neugen XL-60) with respect to 100 parts by weight of latex B , Daiichi Kogyo Seiyaku Co., Ltd., HLB = 12.5) was added in an amount of 0.25 parts by weight (equivalent to about 0.45 parts by weight relative to 100 parts by weight of the chloroprene monomer) to obtain a latex (in the latex The polymer was evaluated according to Example 1 except that the polymer gel content was 0.4% by weight. From the results shown in Table 4, the latex had a good freezing stability and a good adhesive strength without freezing even at -7 ° C.

実施例16
表1で示した割合のクロロプレン単量体、n−ドデシルメルカプタン、ロジン酸カリウム(商品名:ロンヂスK−25、荒川化学(株))、スチレンスルホン酸ナトリウム−メタクリル酸ナトリウム共重合体、ポリオキシプロピレン分岐デシルエーテル(商品名:ノイゲンXL−100、第一工業製薬(株)HLB=14.7)、水酸化ナトリウム、ハイドロサルファイトナトリウム、及び純水を攪拌機付き10Lオートクレーブ中10℃で重合を行い、クロロプレンラテックスを作製した。重合は窒素雰囲気下で0.35重量%の過硫酸カリウム水溶液を連続的に滴下して行い、重合転化率が約90%となった時点で重合停止剤として2,6−ターシャリーブチル−4−メチルフェノール0.05重量部を添加し重合を停止した。その後、減圧下で未反応単量体の除去及び濃縮によりラテックスの固形分を55%に調整しラテックスGを得た。ラテックスG中のポリマーのゲル分は0.5重量%であった。
Example 16
Chloroprene monomer, n-dodecyl mercaptan, potassium rosinate (trade name: Longes K-25, Arakawa Chemical Co., Ltd.), sodium styrenesulfonate-sodium methacrylate copolymer, polyoxy in the proportions shown in Table 1 Polymerization of propylene branched decyl ether (trade name: Neugen XL-100, Daiichi Kogyo Seiyaku Co., Ltd. HLB = 14.7), sodium hydroxide, sodium hydrosulfite, and pure water at 10 ° C. in a 10 L autoclave with a stirrer And chloroprene latex was prepared. Polymerization was carried out by continuously dropping a 0.35% by weight aqueous potassium persulfate solution under a nitrogen atmosphere, and 2,6-tertiarybutyl-4 as a polymerization terminator when the polymerization conversion reached about 90%. -The polymerization was stopped by adding 0.05 parts by weight of methylphenol. Thereafter, the solid content of the latex was adjusted to 55% by removing and concentrating unreacted monomers under reduced pressure to obtain Latex G. The gel content of the polymer in latex G was 0.5% by weight.

ラテックスG100重量部に対し、ポリオキシプロピレン分岐デシルエーテルA(商品名:ノイゲンXL−60、第一工業製薬(株)HLB=12.5)を0.125重量部(クロロプレン単量体100重量部に対して約0.227重量部相当)添加してラテックスを得て(ラテックス中のポリマーのゲル分:0.5重量%)、実施例1に従って評価を実施した。表4の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。   0.125 parts by weight of polyoxypropylene branched decyl ether A (trade name: Neugen XL-60, Daiichi Kogyo Seiyaku HLB = 12.5) (100 parts by weight of chloroprene monomer) with respect to 100 parts by weight of latex G The latex was obtained by adding (corresponding to about 0.227 parts by weight with respect to the polymer) (the gel content of the polymer in the latex: 0.5% by weight) and evaluated according to Example 1. From the results shown in Table 4, the latex had a good freezing stability and a good adhesive strength without freezing even at -7 ° C.

実施例17
表1で示した割合のクロロプレン単量体、n−ドデシルメルカプタン、ロジン酸カリウム(商品名:ロンヂスK−25、荒川化学(株))、水酸化ナトリウム、ハイドロサルファイトナトリウム、及び純水を攪拌機付き10Lオートクレーブ中10℃で重合を行い、クロロプレンラテックスを作製した。重合は窒素雰囲気下で0.35重量%の過硫酸カリウム水溶液を連続的に滴下して行い、重合転化率が約90%となった時点で重合停止剤として2,6−ターシャリーブチル−4−メチルフェノール0.05重量部を添加し重合を停止した。その後、減圧下で未反応単量体の除去及び濃縮によりラテックスの固形分を55%に調整しラテックスHを得た。ラテックスH中のポリマーのゲル分は0.5重量%であった。
Example 17
Stirrer of chloroprene monomer, n-dodecyl mercaptan, potassium rosinate (trade name: Longes K-25, Arakawa Chemical Co., Ltd.), sodium hydroxide, hydrosulfite sodium and pure water in the proportions shown in Table 1 Polymerization was carried out at 10 ° C. in a 10 L autoclave with a chloroprene latex. Polymerization was carried out by continuously dropping a 0.35% by weight aqueous potassium persulfate solution under a nitrogen atmosphere, and 2,6-tertiarybutyl-4 as a polymerization terminator when the polymerization conversion reached about 90%. -The polymerization was stopped by adding 0.05 parts by weight of methylphenol. Thereafter, the solid content of the latex was adjusted to 55% by removing and concentrating unreacted monomers under reduced pressure to obtain Latex H. The gel content of the polymer in latex H was 0.5% by weight.

ラテックスH100重量部に対し、ポリオキシプロピレン分岐デシルエーテルA(商品名:ノイゲンXL−60、第一工業製薬(株)HLB=12.5)20%水溶液を純分換算で0.25重量部(クロロプレン単量体100重量部に対して約0.45重量部相当)、添加してラテックスを得た(ラテックス中のポリマーのゲル分:0.1重量%)。   Polyoxypropylene branched decyl ether A (trade name: Neugen XL-60, Daiichi Kogyo Seiyaku Co., Ltd. HLB = 12.5) 20% aqueous solution with respect to 100 parts by weight of latex H 0.25 parts by weight in terms of pure content ( A latex was obtained by adding about 0.45 parts by weight to 100 parts by weight of chloroprene monomer) (gel content of polymer in latex: 0.1% by weight).

得られたラテックスの一部を容器に入れ、−3〜−7℃の雰囲気で1週間保管し、保管によるラテックスの凍結の有無を確認した。また、ラテックスに樹脂エマルジョン、金属酸化物、増粘剤を配合して接着剤組成物を作製し、その配合安定性、常温接着強度を測定した。配合を表2に示し、結果を表4に示す。表4の結果より、−7℃の保管でも凍結することなく、ラテックスの凍結安定性は良好であり、接着強度も良好な値であった。   Part of the obtained latex was put in a container and stored in an atmosphere at -3 to -7 ° C for 1 week, and it was confirmed whether or not the latex was frozen by storage. Moreover, resin emulsion, a metal oxide, and a thickener were mix | blended with latex, the adhesive composition was produced, and the mixing | blending stability and normal temperature adhesive strength were measured. The formulation is shown in Table 2, and the results are shown in Table 4. From the results shown in Table 4, the latex had a good freezing stability and a good adhesive strength without freezing even at -7 ° C.

比較例1
ポリオキシエチレンイソデシルエーテルを加えないこと以外は実施例1に従って評価を実施した。結果を表5に示す。表5の結果より、−3℃の保管でラテックスが凍結した。
Comparative Example 1
Evaluation was performed according to Example 1 except that polyoxyethylene isodecyl ether was not added. The results are shown in Table 5. From the results in Table 5, the latex was frozen by storage at -3 ° C.

Figure 0005262199
比較例2
ポリオキシエチレンイソデシルエーテルを加えないこと以外は実施例8に従って評価を実施した。結果を表5に示す。表5の結果より、−3℃の保管でラテックスが凍結した。
Figure 0005262199
Comparative Example 2
Evaluation was performed according to Example 8 except that no polyoxyethylene isodecyl ether was added. The results are shown in Table 5. From the results in Table 5, the latex was frozen by storage at -3 ° C.

比較例3
ポリオキシエチレン分岐アルキルエーテルAを加えないこと以外は実施例11に従って評価を実施した。結果を表5に示す。表5の結果より、−3℃の保管でラテックスが凍結した。
Comparative Example 3
Evaluation was performed according to Example 11 except that no polyoxyethylene branched alkyl ether A was added. The results are shown in Table 5. From the results in Table 5, the latex was frozen by storage at -3 ° C.

比較例4
ポリオキシエチレンイソデシルエーテルを、ポリオキシエチレンラウリルエーテル(商品名:エマルゲン109P、花王(株)HLB=13.6)に変更した以外は実施例1に従って評価を実施した。結果を表5に示す。表5の結果より、−5℃の保管でラテックスが凍結した。
Comparative Example 4
Evaluation was carried out according to Example 1 except that polyoxyethylene isodecyl ether was changed to polyoxyethylene lauryl ether (trade name: Emulgen 109P, Kao Corporation HLB = 13.6). The results are shown in Table 5. From the results in Table 5, the latex was frozen by storage at -5 ° C.

比較例5
ポリオキシエチレンイソデシルエーテルを、ポリオキシエチレンプロピレンアルキルエーテル(商品名:エマルゲンLS−110、花王(株)HLB=13.4)に変更した以外は実施例1に従って評価を実施した。結果を表5に示す。表5の結果より、−5℃の保管でラテックスが凍結した。
Comparative Example 5
Evaluation was carried out according to Example 1 except that polyoxyethylene isodecyl ether was changed to polyoxyethylene propylene alkyl ether (trade name: Emulgen LS-110, Kao Corporation HLB = 13.4). The results are shown in Table 5. From the results in Table 5, the latex was frozen by storage at -5 ° C.

比較例6
ポリオキシエチレンイソデシルエーテルを、ポリオキシエチレンジスチレンフェニルエーテル(商品名:エマルゲンA−60、花王(株)HLB=12.8)に変更した以外は実施例1に従って評価を実施した。結果を表5に示す。表5の結果より、−7℃の保管でラテックスが凍結した。
Comparative Example 6
Evaluation was carried out according to Example 1 except that polyoxyethylene isodecyl ether was changed to polyoxyethylene distyrene phenyl ether (trade name: Emulgen A-60, Kao Corporation HLB = 12.8). The results are shown in Table 5. From the results in Table 5, the latex was frozen by storage at -7 ° C.

比較例7
ポリオキシエチレンイソデシルエーテルを、ポリオキシプロピレン分岐デシルエーテルD(商品名:ノイゲンXL−400、第一工業製薬(株)HLB=18.4)に変更した以外は実施例1に従って評価を実施した。結果を表5に示す。表5の結果より、−5℃の保管でラテックスが凍結した。
Comparative Example 7
Evaluation was performed according to Example 1 except that polyoxyethylene isodecyl ether was changed to polyoxypropylene branched decyl ether D (trade name: Neugen XL-400, Daiichi Kogyo Seiyaku HLB = 18.4). . The results are shown in Table 5. From the results in Table 5, the latex was frozen by storage at -5 ° C.

実施例18
ラテックスEを−1℃にて100日間保管し、その前後におけるpH、ラテックス中の塩素イオン濃度、10%トルエン溶液粘度及びゲル分の変化を測定した。結果を表6に示す。表6の結果より、保管の前後で物性の変化は殆どなかった。
Example 18
Latex E was stored at -1 ° C for 100 days, and the pH before and after that, the chloride ion concentration in the latex, the viscosity of 10% toluene solution and the change in gel content were measured. The results are shown in Table 6. From the results in Table 6, there was almost no change in physical properties before and after storage.

Figure 0005262199
比較例8
ラテックスBを−1℃にて100日間保管し、その前後におけるpH、ラテックス中の塩素イオン濃度、10%トルエン溶液粘度及びゲル分の変化を測定した。結果を表6に示す。表6の結果より、保管によりラテックスが凍結した。
Figure 0005262199
Comparative Example 8
Latex B was stored at -1 ° C for 100 days, and the pH before and after that, the chloride ion concentration in the latex, the viscosity of 10% toluene solution and the change in gel content were measured. The results are shown in Table 6. From the results in Table 6, latex was frozen by storage.

比較例9
ラテックスEを25℃にて100日間保管し、その前後におけるpH、ラテックス中の塩素イオン濃度、10%トルエン溶液粘度及びゲル分の変化を測定した。結果を表6に示す。表6の結果より、保管により塩素イオン濃度、10%トルエン溶液粘度、ゲル分が増加し、ラテックスのpHが低下した。
Comparative Example 9
Latex E was stored at 25 ° C. for 100 days, and the pH before and after that, the chloride ion concentration in the latex, the viscosity of 10% toluene solution, and the change in gel content were measured. The results are shown in Table 6. From the results shown in Table 6, the chloride ion concentration, the 10% toluene solution viscosity, and the gel content increased and the pH of the latex decreased due to storage.

Claims (7)

カルボン酸のアルカリ金属塩からなる乳化剤及び、炭素数9〜16で分岐を有するアルキル鎖を有し、HLBが9〜16である下記一般式(1)で表されるノニオン系乳化剤を含むことを特徴とするクロロプレンラテックス。
R−O(CHCXHO)nH (1)
(式中、Rは炭素数9〜16で分岐を有するアルキル鎖からなる親油基を表し、Xは水素又は炭素数1〜2のアルキル鎖を表し、nはノニオン系乳化剤のHLBが9〜16になる範囲の整数を表す。)
An emulsifier composed of an alkali metal salt of a carboxylic acid and a nonionic emulsifier represented by the following general formula (1) having an alkyl chain having 9 to 16 carbon atoms and a branched chain and having an HLB of 9 to 16 A featured chloroprene latex.
R—O (CH 2 CXHO) nH (1)
(In the formula, R represents a lipophilic group composed of an alkyl chain having 9 to 16 carbon atoms and a branched chain, X represents hydrogen or an alkyl chain having 1 to 2 carbon atoms, and n represents 9 to 9 HLB of a nonionic emulsifier. Represents an integer in the range of 16.)
カルボン酸のアルカリ金属塩からなる乳化剤が、ロジン酸のアルカリ金属塩であることを特徴とする請求項1に記載のクロロプレンラテックス。 The chloroprene latex according to claim 1, wherein the emulsifier composed of an alkali metal salt of carboxylic acid is an alkali metal salt of rosin acid. 安定剤としてスルホン酸のアルカリ金属塩及び/又は硫酸エステルのアルカリ金属塩を含むことを特徴とする請求項1又は請求項2に記載のクロロプレンラテックス。 The chloroprene latex according to claim 1 or 2, wherein the stabilizer comprises an alkali metal salt of a sulfonic acid and / or an alkali metal salt of a sulfate ester. 安定剤が、ナフタレンスルホン酸とホルムアルデヒドの縮合物及び/又はスチレンスルホン酸ナトリウムとメタクリル酸ナトリウムの共重合体であることを特徴とする請求項3に記載のクロロプレンラテックス。 The chloroprene latex according to claim 3, wherein the stabilizer is a condensate of naphthalenesulfonic acid and formaldehyde and / or a copolymer of sodium styrenesulfonate and sodium methacrylate. ラテックス中のポリマーのゲル分が1重量%以下であることを特徴とする請求項1〜請求項4のいずれかの項に記載のクロロプレンラテックス。 The chloroprene latex according to any one of claims 1 to 4, wherein the gel content of the polymer in the latex is 1% by weight or less. カルボン酸のアルカリ金属塩からなる乳化剤の存在下でクロロプレン単量体又はクロロプレン単量体とこの単量体と共重合可能な単量体を重合する際に、HLBが9〜16である下記一般式(1)で表されるノニオン系乳化剤を重合開始時、重合中及び重合終了後のうち、何れかの段階で1回以上添加することを特徴とする請求項1〜請求項5のいずれかの項に記載のクロロプレンラテックスの製造法。
R−O(CHCXHO)nH (1)
(式中、Rは炭素数9〜16で分岐を有するアルキル鎖からなる親油基を表し、Xは水素又は炭素数1〜2のアルキル鎖を表し、nはノニオン系乳化剤のHLBが9〜16になる範囲の整数を表す。)
When polymerizing a chloroprene monomer or a chloroprene monomer and a monomer copolymerizable with this monomer in the presence of an emulsifier comprising an alkali metal salt of a carboxylic acid, the following general formulas having an HLB of 9 to 16 The nonionic emulsifier represented by the formula (1) is added one or more times at any stage among polymerization at the start of polymerization, during polymerization and after completion of polymerization. The manufacturing method of the chloroprene latex as described in the term.
R—O (CH 2 CXHO) nH (1)
(In the formula, R represents a lipophilic group composed of an alkyl chain having 9 to 16 carbon atoms and a branched chain, X represents hydrogen or an alkyl chain having 1 to 2 carbon atoms, and n represents 9 to 9 HLB of a nonionic emulsifier. Represents an integer in the range of 16.)
請求項1〜請求項5のいずれかの項に記載のクロロプレンラテックスを含有することを特徴とする接着剤組成物。 An adhesive composition comprising the chloroprene latex according to any one of claims 1 to 5.
JP2008060069A 2008-03-10 2008-03-10 Chloroprene latex and process for producing the same Active JP5262199B2 (en)