JP5192752B2 - Method for producing silica nanoparticles using reverse micelle dispersion, silica nanoparticles obtained by the method, and labeling reagent using the same - Google Patents

Description

  The present invention relates to a method for producing nanometer-sized silica nanoparticles having a uniform particle size, which is used as a labeling reagent for detecting or quantifying a specific substance such as protein. In more detail, it is related with the manufacturing method of the silica nanoparticle which uses a reverse micelle dispersion system, the silica nanoparticle obtained by this method, and a labeling reagent using the same.

When water is added to a silane coupling agent typified by tetraethoxysilane (hereinafter sometimes referred to as TEOS) and hydrolyzed, silica particles are formed. A particle size distribution will occur. It has been difficult to control the particle size distribution by a conventional method for producing silica particles in which silica particles are formed in a solvent (for example, ethanol) in which water is uniformly diluted.
On the other hand, there is a manufacturing method using micelles or reverse micelles characterized in that the raw material of particles is generally retained inside micelles or reverse micelles as a method for aligning the sizes of formed particles (for example, (See Patent Document 1). In the case of silica particles using a silane coupling agent, water for hydrolysis is required during the reaction, and therefore a production method using reverse micelles composed of water droplets in a hydrophobic solvent can be employed. For example, n-heptane and di-2-ethylhexyl sulfosuccinate (hereinafter sometimes referred to as AOT) may be used as a combination of a hydrophobic solvent and a surfactant capable of forming nanometer-sized ultra-micro reverse micelles. (For example, refer nonpatent literature 1).
In the case of production using such reverse micelles, the size of the obtained silica particles is reduced by a mechanism in which the reverse micelle structure is destabilized and destroyed due to large growth of the silica particles, and the growth of the silica particles stops. Will be controlled. However, there is a problem that the size of the silica particles to be produced also varies statistically because there is a statistical variation in the limit size at which the reverse micelle structure is destroyed.
Furthermore, in the case of manufacturing using such reverse micelles, TEOS, which is a raw material for silica particles, is dissolved in a hydrophobic solvent, and silica particles are synthesized inside the reverse micelles and the internal TEOS is consumed. The silica particles grow beyond the size of the original reverse micelles while maintaining the reverse micelle structure without stopping the growth of the particles because they are supplied from the outside of the reverse micelles. There was a problem that metric size silica particles could not be obtained.
On the other hand, by adding a dye inside the silica particles to be produced, the silica particles have fluorescence characteristics and light absorption characteristics, and are further selectively bonded by surface modification with molecules that selectively bind to target molecules. The target molecule can be used as a labeling reagent that can be detected with high sensitivity by an optical technique (see, for example, Patent Document 2). At this time, if the fluorescence intensity and the absorption intensity are measured quantitatively, it is possible not only to examine the presence / absence of the target molecule but also to quantitatively evaluate its concentration. However, when large or small silica particles of the labeling reagent are mixed, there is a problem that reproducible measurement results cannot be obtained if the binding property of the target molecule is dependent on the particle size.
Japanese Patent Laid-Open No. 07-062008 EP1036763B1 publication Applied Physics Vol. 70, No. 9 (2001) P1087, “High Quantum Efficiency of Light Emission by Nano-Size of Phosphor Material” Tetsuhiko Isobe

  In view of the above problems, the object of the present invention is to use silica micelles having an average particle size of the order of nm (for example, 300 nm or less) having a narrow particle size distribution and a uniform particle size by using a reverse micelle dispersion system. It is in providing the manufacturing method which manufactures this by a cheap and high yield, and the silica nanoparticle manufactured by it. Another object of the present invention is to provide a labeling reagent that is excellent in reproducibility of measurement results and enables highly sensitive analysis of an extremely small target sample.

The above problems have been achieved by the following means.
(1) A silane coupling agent is added to a reverse micelle dispersion consisting of a surfactant in a hydrophobic solvent, water containing a basic electrolyte, and ethylene glycol, and the silane is added with water inside the reverse micelle. A method for producing silica nanoparticles in which a coupling agent is hydrolyzed and polymerized to form silica nanoparticles,
The method for producing silica nanoparticles , wherein the volume ratio of water inside the reverse micelle and the ethylene glycol is in the range of 3: 7 to 7: 3 ,

(2) the hydrophobic solvent is n- heptane, wherein the surfactant Ri di-2-ethylhexyl sulfosuccinate sodium der, before Symbol silane coupling agent is tetraethoxysilane, The method for producing silica nanoparticles according to (1),
(3) In addition to the silane coupling agent, a dye-containing silica nanoparticle is produced by adding an organic dye compound chemically bonded to a silane compound. (1) or (2) production how of silica particles according to,
(4) a flat Hitoshitsubu diameter 100 to 300 nm, and the CV value, characterized in that the silica particles are obtained is 5-25%, according to any one of (1) to (3) Production method,

(5) wherein (1) obtaining by Ri silica particles in the production method according to any one of - (4), and to the resulting silica particle surface, antibodies, antigens, peptides, DNA, RNA, sugar A method for producing a labeling reagent, comprising a step of binding or adsorbing a substance that recognizes a target biomolecule selected from a chain, a ligand, and a receptor , and (6) the labeling reagent is a biomolecule detection reagent or a biomolecule The method for producing a labeling reagent according to (5), which is a quantitative reagent, a biomolecule separation reagent, a biomolecule recovery reagent or an immunostaining reagent.
Is to provide.
In the present specification and claims, “silica nanoparticles” refer to colloidal silica particles having an average particle size of 300 nm or less. When the silica nanoparticles are used as a labeling reagent, the particle diameters suitable for use depending on the detection substance and the detection method are various, but are often in the range of 100 to 300 nm, and the silica nanoparticles are in this range. It is preferable.
In the present specification and claims, “reverse micelle dispersion” refers to the interface formed around the water and polyol droplets by adding a hydrophobic solvent, surfactant, water and polyol. A dispersion of a spherical shell aggregate (so-called water-in-oil microemulsion) of an active agent.
In the present specification and claims, the “dye-containing silica nanoparticles” refers to silica nanoparticles incorporating an organic dye compound at a high concentration.

In the method for producing silica nanoparticles of the present invention, by incorporating the polyol in the reverse micelle, the obtained silica nanoparticles have a narrow particle size distribution width and uniform particle size, and can control the average particle size.
The method for producing silica nanoparticles of the present invention incorporates an organic dye compound at a higher concentration than the conventional method for producing silica particles in which silica particles are formed in a solvent in which water is uniformly diluted without using reverse micelles. Dye-containing silica nanoparticles can be produced.

Silica nanoparticles obtained by the production method of the present invention have an average particle size of nanometer size, and a narrow particle size distribution and a uniform particle size.
Since the dye-containing silica nanoparticles of the present invention can be obtained by the reverse micelle production method, the organic dye compound can be incorporated at a high concentration to enable high-sensitivity labeling.
Since the labeling reagent of the present invention uses the above-mentioned silica nanoparticles having a uniform average particle diameter, it is possible to perform a highly sensitive analysis of a very small amount of target sample with excellent reproducibility of measurement results and high reliability.

Hereinafter, the manufacturing method of the silica nanoparticle of this invention is demonstrated.
In the method for producing silica nanoparticles of the present invention, a silane coupling agent serving as a silica raw material is added to a reverse micelle dispersion composed of a surfactant, water containing a basic electrolyte, and a polyol in a hydrophobic solvent. The silane coupling agent is hydrolyzed with the water and polymerized to form silica nanoparticles.
In the production method of the present invention, the water is necessary for stably forming reverse micelles, and is also necessary as a substrate for a silica nanoparticle formation reaction by a silane coupling agent. Therefore, in the present invention, the silica particle forming reaction proceeds only inside the reverse micelles where the water exists.

The action mechanism that enables the polyol used in the present invention to produce nanometer-sized silica nanoparticles with a narrowed particle size distribution is not clear, but is estimated as follows.
As described above, the particle size and particle size distribution of the silica nanoparticles are determined by the limit at which the reverse micelle structure is destroyed. The stability of reverse micelles is generally considered highest when the contents of the reverse micelles are water that is not mixed with a hydrophobic solvent outside the reverse micelles, depending on the choice of surfactant.
Therefore, by mixing the polyol with the water inside the reverse micelle, the stability of the reverse micelle is reduced within the range that does not destroy, and the water used for the reaction is reduced, thereby suppressing excessive growth of the silica nanoparticles. It is thought that you can. In other words, by using a polyol that does not destroy reverse micelles and can exist only inside reverse micelles, by performing particle formation reaction in a state where the internal water concentration is reduced to the limit where reverse micelles are formed, Nanoscale silica nanoparticles with a narrow particle size distribution can be produced.
In addition, since the stability of a reverse micelle is high while the silica nanoparticle is small, even if the water concentration inside the reverse micelle decreases, the influence is small.

In this invention, it is preferable that the volume ratio of the water inside the said reverse micelle and the said polyol exists in the range of 3: 7-7: 3, and it is more preferable that it exists in the range of 5: 5-4: 6.
If the amount ratio of water is too large, the particle size becomes too large and the variation in particle size becomes too large. On the other hand, if the amount ratio of water is too small, the reverse micelle structure cannot be maintained and the particle formation reaction is difficult to proceed, resulting in poor yield.
In the present invention, the basic electrolyte used as a reaction catalyst is preferably ammonium ion, and the water containing the basic electrolyte is preferably ammonia water.
Although there is no restriction | limiting in particular as content of the said basic electrolyte, It is preferable to make it contain 3-28 mass% in the water inside a reverse micelle.
Next, the surfactant used in the present invention will be described.
The surfactant depends on the type of the hydrophobic solvent and the polyol used in the present invention. For example, sodium di-2-ethylhexylsulfosuccinate (hereinafter sometimes referred to as AOT), cholic acid. Anionic surfactants such as sodium and sodium caprylate; polyoxyethylene ester, polyoxyethylene ether, polyoxyethylene sorbitan ester, sorbitan ester, various tritons (trade names, manufactured by Rohm and Haas, for example, Triton X- 100, Triton X-114) and other nonionic surfactants; soaps such as potassium oleate and sodium oleate; cetylpyridinium chloride, cetyltrimethylammonium bromide (hereinafter sometimes referred to as CTAB), benzalkonium chloride Cetyl dibromide Cationic surfactants such as methyl ethyl ammonium; N- alkyl -N, N-dimethyl ammonio-1-propanesulfonic acid and CHAPS zwitterionic surfactants. As the surfactant, AOT, Triton X-100 or CTAB is preferable, and AOT is more preferable.
In the present invention, the mass ratio of the surfactant to the water constituting the reverse micelle dispersion (water: surfactant) is adjusted so that the average particle size of the reverse micelle becomes an appropriate value as described later. Therefore, it is preferable to adjust the mass ratio appropriately.
Next, the hydrophobic solvent used in the present invention will be described.
Specific examples of the hydrophobic solvent include alkanes (eg, liquids such as n-heptane, n-hexane, isooctane, octane, nonane, decane, undecane, dodecane), cycloalkanes (eg, cyclohexane, cyclopentane, etc.). ), Aromatic hydrocarbons (eg, benzene, toluene, etc.), and mixtures thereof (eg, petroleum, petroleum derivatives). As the hydrophobic solvent, n-heptane, n-hexane, cyclohexane or isooctane is preferable, n-heptane or n-hexane is more preferable, and n-heptane is further preferable.
In the present invention, the volume ratio of the hydrophobic solvent to the water constituting the reverse micelle dispersion is not particularly limited as long as the reverse micelle dispersion is formed, but is in the range of 1:10 to 1:50. It is preferable.
In the present invention, the reverse micelle dispersion is formed by, for example, mechanically stirring or sonicating sufficiently after adding the surfactant, the water, and the polyol to the hydrophobic solvent. Can do.

Next, the silane coupling agent used in the present invention will be described.
The silane coupling agent is not particularly limited, but tetraalkoxysilane (for example, tetraethoxysilane (TEOS), tetramethoxysilane), mercaptoalkyltrialkoxysilane (for example, γ-mercaptopropyltrimethoxysilane (MPS)). , Γ-mercaptopropyltriethoxysilane), aminoalkyltrialkoxysilane (eg, γ-aminopropyltriethoxysilane (APS)), 3-thiocyanatopropyltriethoxysilane, 3-glycidyloxypropyltriethoxysilane, 3 Mention may be made of -isocyanatopropyltriethoxysilane and 3- [2- (2-aminoethylamino) ethylamino] propyl-triethoxysilane. Among these, TEOS is preferable.
In this invention, the mass ratio of the said silane coupling agent with respect to the said water which comprises the said reverse micelle dispersion system and is a substrate of particle formation reaction is 50 mass parts or less of silane coupling agents with respect to 100 mass parts of water. It is preferable that it is 10 parts by mass or more and 25 parts by mass or less. This is because a by-product (ethanol when TEOS is used) is generated during silica synthesis, and this by-product destabilizes reverse micelles.

As a preferable specific example of the reverse micelle dispersion of the production method of the present invention,
[1] A reverse micelle dispersion in which the surfactant is AOT and the hydrophobic solvent is n-heptane.
[2] A reverse micelle dispersion in which the surfactant is Triton X-100, the hydrophobic solvent is cyclohexane, and n-hexanol is used as a co-surfactant.
[3] A reverse micelle dispersion in which the surfactant is AOT and the hydrophobic solvent is isooctane.
[4] A reverse micelle dispersion system in which the surfactant is CTAB, the hydrophobic solvent is n-hexane, and the co-surfactant is n-hexanol.
Among these, [1] It is more preferable that the surfactant is AOT, and the reverse micelle dispersion system in which the hydrophobic solvent is n-heptane.
In the production method of the present invention, the hydrophobic solvent is n-heptane, the surfactant is AOT, the polyol is ethylene glycol, the silane coupling agent is TEOS, and the basic electrolyte. The water containing is particularly preferably an aqueous ammonia solution.

  According to the production method of the present invention, spherical or nearly spherical silica nanoparticles can be produced. The nearly spherical silica nanoparticles specifically have a shape in which the ratio of major axis to minor axis is 1.2 or less.

As described above, the silica nanoparticles obtained by the production method of the present invention can be made to have an average particle size of nm size with uniform particle size by controlling the composition ratio in the reverse micelle using the polyol.
In the present invention, the average particle diameter is obtained by measuring the diameter of each particle directly from an image of a transmission electron microscope (TEM), a scanning electron microscope (SEM), etc., and calculating the average value. .
The variation coefficient (hereinafter referred to as CV value) of the particle size distribution of the silica nanoparticles obtained by the present invention is preferably 25% or less, more preferably 15% or less, and even more preferably 10% or less. Here, the CV value is a value obtained by dividing the standard deviation of the particle size distribution by the average particle size.
In this invention, when the volume ratio of the water inside the said reverse micelle and the said polyol exists in the range of 3: 7-7: 3, CV value can be 25% or less. Moreover, when it exists in the range of 5: 5 to 3: 7, it can be CV value 20% or less.
In the present specification and claims, monodisperse means a particle group having a CV value of 20% or less.

Next, as a particularly preferred embodiment of the present invention, a method for producing dye-containing silica nanoparticles will be described.
In the production method of the present invention, in addition to the silane coupling agent serving as a silica raw material, an organic dye compound chemically bonded to a silane compound (hereinafter simply referred to as “dye silane composite compound”) is added to the reverse micelle dispersion. It is particularly preferable that the resulting silica nanoparticles are dye-containing silica nanoparticles.
As described above, the reverse micelle dispersion system according to the present invention is more discrete than the conventional silica particle production method in which silica particles are formed in a solvent in which water is uniformly diluted without using reverse micelles. There is a high concentration of water inside the reverse micelle that is the region. In addition, since the silica particle formation reaction proceeds only inside the reverse micelle in which the water is present, the dye silane composite compound also reacts only inside the reverse micelle, and the resulting silica nanoparticle is obtained from the dye silane composite compound. It will be present at a high concentration.
Therefore, the production method of the present invention can produce dye-containing silica nanoparticles incorporating an organic dye compound at a high concentration.
In the production method of the present invention, the addition ratio of the dye silane complex compound and the silane coupling agent to the reverse micelle system is not particularly limited, but the mole of the silane coupling agent with respect to 1 mol of the dye silane complex compound. The ratio is preferably 50 to 40000, more preferably 100 to 2000, and further preferably 150 to 1000. According to the production method of the present invention, the content of the organic dye compound in the obtained dye-containing silica nanoparticles can be controlled by this addition ratio.
The dye silane composite compound, which is an organic dye compound chemically bonded to the silane compound, is prepared by reacting the organic dye compound and the silane compound and then chemically bonding them, such as a covalent bond, an ionic bond, or the like. Can do.
Here, the organic dye compound is not particularly limited as long as it develops color, and examples thereof include a fluorescent dye compound and a light absorbing dye compound. Specific examples include TAMRA and carboxyrhodamine 6G (hereinafter sometimes referred to as “CR6G”) represented by the following formulas.

  The dye silane complex compound has N-hydroxysuccinimide (NHS) ester group, maleimide group, isocyanate group, isothiocyanate group, aldehyde group, paranitrophenyl group, diethoxymethyl group, epoxy group, cyano group and the like. It is preferable to prepare by reacting the organic dye compound having a group with a silane compound having a substituent (for example, an amino group, a hydroxyl group, or a thiol group) that reacts correspondingly with these active groups, and covalently bonding them. .

  Specific examples of the organic dye compound having the active group include organic compounds having NHS ester groups such as 5-TAMRA-NHS ester and 5-CR6G-NHS ester (trade name; manufactured by Invitrogen) represented by the following formulae, respectively. Mention may be made of dye compounds.

The organic dye compound having an NHS ester group can be obtained commercially.
Specific examples of the silane compound having a substituent include γ-aminopropyltriethoxysilane (APS), 3- [2- (2-aminoethylamino) ethylamino] propyl-triethoxysilane, and N-2 (aminoethyl). ) Silane compounds having an amino group, such as 3-aminopropylmethyldimethoxysilane and 3-aminopropyltrimethoxysilane. Of these, APS is preferable.
The reaction between the organic dye compound having an NHS ester group and the silane compound having an amino group is obtained by dissolving in a solvent such as DMSO or water and then reacting with stirring at room temperature (for example, 25 ° C.). It can be carried out.
The ratio of the organic dye compound having the NHS ester group and the silane compound used in the reaction is not particularly limited, but the organic dye compound having the NHS ester group: the silane compound having an amino group = 1: 0.5 to 4 ( (Molar ratio) is preferable, and a ratio of 1: 0.8 to 1.2 (molar ratio) is more preferable.
Thus, the carbonyl group of the organic dye compound and the amino group of the silane compound having an amino group are peptide-bonded (—NHCO—) to obtain a dye silane composite compound. That is, in the dye silane complex compound, the organic dye compound and the silica component are bonded via a peptide bond.

Next, the dye-containing silica nanoparticles obtained by the production method of the present invention will be described.
The dye-containing silica nanoparticles obtained by the production method of the present invention are formed by chemically bonding an organic dye compound and a silica component.
In the dye-containing silica nanoparticles obtained by the production method of the present invention, the organic dye compound can be distributed throughout the silica nanoparticles from the center to the surface of the silica nanoparticles.
Here, “the organic dye compound is distributed throughout the silica nanoparticles” means a state in which at least one organic dye compound is immobilized at a high concentration in the silica nanoparticles, and is contained in the silica nanoparticles per unit weight. The density | concentration of an organic pigment | dye compound can be 150-300 micromol / g, and it is preferable that it is 170-240 micromol / g.
While a free organic dye compound is labeled with one dye per molecule, the organic dye compound group fixed and distributed in the dye-containing silica nanoparticles obtained by the production method of the present invention is integrated. Therefore, the sensitivity can be increased as compared with a free organic dye compound. For example, when the organic dye compound is a fluorescent dye compound, the luminance can be increased as compared with a free fluorescent dye compound. In the case of a fluorescent dye compound, many fluorescent dye compounds can be fixed and included in silica nanoparticles without causing self-quenching (for example, Japanese Patent Application No. 2004-356608). For this reason, the highly sensitive label | marker which can be used also in a micro area | region is possible.

Next, “silica nanoparticle surface modification” will be described.
Silica is generally known to be chemically inert and easy to modify. The silica nanoparticles obtained by the production method of the present invention can also easily bind a desired substance to the surface, and the surface can be made mesoporous or smooth.

Regarding the surface modification of the silica nanoparticles, specifically, silica nanoparticles having an acceptor group on the surface capable of binding to a desired substance can be used according to the kind of the silane coupling agent. Examples of the acceptor group include an amino group, a hydroxyl group, a thiol group, a carboxyl group, a maleimide group, and a succinimidyl ester group.
Table 1 shows the relationship between the silane coupling agent and the acceptor group formed on the surface of the silica nanoparticles obtained thereby.

  In addition, about the obtained silica nanoparticle, when it is desired to introduce an acceptor group different from the acceptor group introduced to the surface by the silane coupling agent, the obtained silica nanoparticle is further different from the silane coupling agent. This can be achieved by treating with a silane coupling agent. This treatment can be performed by performing the same operation as in the production method of the present invention using a silane coupling agent different from the silane coupling agent.

Silica nanoparticles obtained by the production method of the present invention can be modified by binding or adsorbing a substance that recognizes a desired target biomolecule on the surface according to the type of acceptor group on the surface.
When the silica nanoparticles contain the organic dye compound, the target biomolecule (including a physiologically active substance) in a specimen (for example, any cell extract, lysate, medium / culture solution, solution, buffer) is dyed. Can be labeled.
Examples of the substance that recognizes the target biomolecule that modifies the silica nanoparticles include antibodies, antigens, peptides, DNA, RNA, sugar chains, ligands, receptor peptides, chemical substances, and the like.
Here, molecular recognition refers to (1) hybridization between DNA molecules or DNA-RNA molecules, (2) antigen-antibody reaction, (3) reaction between enzyme (receptor) and substrate (ligand), etc. A specific interaction between molecules.

Here, a ligand refers to a substance that specifically binds to a protein, such as a substrate that binds to an enzyme, a coenzyme, a regulatory factor, a hormone, or a neurotransmitter, as well as a low molecular weight molecule or ion. Also includes high molecular weight materials.
The chemical substances are not limited to natural organic compounds, but include artificially synthesized physiologically active compounds and environmental hormones.
Although there is no particular limitation on the method for binding and modifying the target biomolecule-recognizing substance on the surface of the silica nanoparticles obtained by the production method of the present invention, the following examples (i) to (iii) are given. It is done.
(I) The silica nanoparticles having a thiol group prepared on the surface using MPS or the like molecularly recognizes the target biomolecule on the surface via a bond through a disulfide bond, a thioester bond, or a thiol substitution reaction. It can be modified with substances.
(Ii) In particular, when the substance that recognizes the target biomolecule as a molecule has an amino group, the thiol group of the silica nanoparticle and the amino group of the substance that recognizes the target biomolecule as a molecule are succinimidyl-trans- It can also couple | bond using crosslinking agents, such as 4- (N-maleimidylmethyl) cyclohexane-1-carboxylate (SMCC) and N- (6-maleimidocaproyloxy) succinimide (EMCS).
(Iii) In the same manner as described above, the silica nanoparticles having an amino group prepared on the surface using APS or the like have the amino group and a thiol group possessed by a substance that recognizes the target biomolecule, such as SMCC, EMCS, etc. Bonding can be performed using a crosslinking agent. Moreover, this amino group and the amino group which the substance which recognizes the said target biomolecule molecule | numerator has can also be couple | bonded with crosslinking agents, such as glutaraldehyde. Furthermore, the surface can be modified with a substance that recognizes the target biomolecule through a peptide bond or a thiourea bond.
That is, the substance that recognizes the target biomolecule modified with the silica nanoparticle itself becomes a receptor site, for example, antigen-antibody reaction, biotin-avidin reaction, hybridization utilizing the complementarity of the base sequence, etc. Specific molecular recognition can be used to specifically bind to a target biomolecule.

Next, the labeling reagent of the present invention will be described.
The labeling reagent of the present invention uses silica nanoparticles obtained by the production method of the present invention. It is preferable to give a fluorescent or light-absorbing dye label using the dye-containing silica nanoparticles. Furthermore, the silica nanoparticle surface modification is used to modify the surface of the silica particle with a substance that recognizes the target biomolecule such as an antibody or a hormone, and the target biomolecule is to be evaluated visually by an apparatus for detecting optical properties or by visual observation. It can be used as a labeling reagent that makes it possible to evaluate whether or not it exists.
Specific examples of the labeling reagent of the present invention include a biomolecule detection reagent, a biomolecule quantification reagent, a biomolecule separation reagent, a biomolecule recovery reagent, or an immunostaining reagent.
The target biomolecule can be used as an analytical reagent for detecting, quantifying, separating or recovering. Moreover, when the molecular recognition with the said target biomolecule is an antigen-antibody reaction, it can be set as the reagent for immuno-staining which uses the said silica nanoparticle.

Hereinafter, the present invention will be described in more detail based on examples. The present invention is not limited to these examples.
Example 1 (Preparation of silica nanoparticles by the reverse micelle method of the present invention)
A reverse micelle dispersion was prepared by dissolving 0.40 g of AOT in 4.0 ml of n-heptane, adding 0.10 ml of water and an equal amount of ethylene glycol, and stirring sufficiently. However, in the water added at this time, 14% by mass of ammonia serving as a catalyst for the silica synthesis reaction was dissolved in mass concentration with respect to water. When the size of the reverse micelle formed at this time was measured by a dynamic light scattering (DLS) method using Zetasizer Nano (trade name; manufactured by Malvern), the average particle size was about 20 nm. To this reverse micelle dispersion, 40 μl of TEOS was added and stirred at room temperature (around 25 ° C.) for 24 hours to carry out a silica synthesis reaction.

When an equal amount of ethanol is added to the reverse micelle dispersion after the synthesis is completed, the reverse micelles are destroyed and the silica nanoparticles are aggregated and gelled. The dispersion containing the silica nanoparticles was subjected to a centrifugal separation treatment to precipitate the silica nanoparticles to remove the solvent, and the same treatment was performed twice with ethanol and water to wash the silica nanoparticles. As the conditions for the centrifugal separation treatment, in any solvent, most of the particles could be settled in 30 minutes with a centrifugal force of 6000 g. Finally, silica nanoparticles were dispersed in pure water. The obtained silica nanoparticle group also contained a small amount of fine particles having a particle size of 100 nm or less. When this silica colloid dispersion liquid dispersed in pure water was subjected to a centrifugal separation treatment with a centrifugal force of 200 g for 30 minutes, only particles larger than 100 nm could be settled. The particles could be separated and removed.
As a result, silica nanoparticles having an average particle size of 207 nm and a CV value of 16% were produced. Yield 89%.
FIG. 1 shows an SEM image of the silica nanoparticles obtained. In addition, the scale bar in FIG. 1 shows 1.0 micrometer (magnification 30,000 times).
In the figure, spherical substances that appear white are the silica nanoparticles obtained. As is apparent from FIG. 1, it can be seen that the particle size is uniform in the particle size distribution with a CV value of 16%.
The average particle diameter is obtained by measuring the diameter of each particle shown in the SEM image and calculating the average value.

Comparative example It implemented about 1-butanol which is alcohols as a hydrophilic organic solvent.
A reverse micelle dispersion was prepared in the same manner as in Example 1 except that 1-butanol was added in an amount equivalent to the water instead of adding 0.10 ml of water in an amount equivalent to ethylene glycol. However, as a result of DLS measurement, 1-butanol was dispersed on the hydrophobic solvent side in the heptane-AOT reverse micelle system, and the desired reverse micelle dispersion system was not obtained, and silica nanoparticles could not be produced.

Example 2 (Preparation of fluorescent silica nanoparticles by the reverse micelle method of the present invention)
1.0 mg of 5-TAMRA-NHS ester (trade name; manufactured by Invitrogen), which is a rhodamine dye, was dissolved in 240 μl of DMF solvent. 0.45 μl of APS was added thereto and reacted at room temperature for 1 hour to obtain TAMRA (hereinafter referred to as TAMRA-APS) in which APS and a peptide were bonded.
The same synthesis as in Example 1 is performed by adding 10 μl of the obtained TAMRA-APS solution (concentration 8.0 mmol / l) and 40 μl of TEOS to 4.0 ml of the reverse micelle dispersion obtained in Example 1. Thus, fluorescent silica nanoparticles in which the rhodamine dye TAMRA was incorporated inside the particles could be produced. Particle size distribution with a yield of 80%, an average particle size of 224 nm, and a CV value of 7%.
It was confirmed that the rhodamine dye TAMRA incorporated into the silica nanoparticles also showed the same fluorescence characteristics as before incorporation.

FIG. 1 is a diagram showing an SEM image of the silica nanoparticles obtained in Example 1. FIG.

Claims (6)

A silane coupling agent is added to a reverse micelle dispersion comprising a surfactant in a hydrophobic solvent, water containing a basic electrolyte, and ethylene glycol, and the silane coupling agent is added with water inside the reverse micelle. Is a method for producing silica nanoparticles in which silica nanoparticles are hydrolyzed to form silica nanoparticles,
The method for producing silica nanoparticles, wherein the volume ratio of water inside the reverse micelle and the ethylene glycol is in the range of 3: 7 to 7: 3.   The hydrophobic solvent is n-heptane, the surfactant is sodium di-2-ethylhexylsulfosuccinate, and the silane coupling agent is tetraethoxysilane. A method for producing silica nanoparticles. The silica nanoparticle according to claim 1 or 2, wherein, in addition to the silane coupling agent, a dye-containing silica nanoparticle is produced by adding an organic dye compound chemically bonded to a silane compound. of production how. The method for producing silica nanoparticles according to any one of claims 1 to 3, wherein silica nanoparticles having an average particle diameter of 100 to 300 nm and a CV value of 5 to 25% are obtained. Any one in the step of obtaining by Ri silica particles in the production method according to claim 1, and to the resulting silica particle surface, antibodies, antigens, peptides, DNA, RNA, carbohydrate, ligand, and receptor A method for producing a labeling reagent, comprising a step of binding or adsorbing a substance that recognizes a target biomolecule selected from a body . The method for producing a labeling reagent according to claim 5, wherein the labeling reagent is a biomolecule detection reagent, a biomolecule quantification reagent, a biomolecule separation reagent, a biomolecule recovery reagent or an immunostaining reagent .