JP5093368B2 - Method for judging welding characteristics of tin-plated steel sheets for welding cans - Google Patents
Method for judging welding characteristics of tin-plated steel sheets for welding cans Download PDFInfo
- Publication number
- JP5093368B2 JP5093368B2 JP2011002951A JP2011002951A JP5093368B2 JP 5093368 B2 JP5093368 B2 JP 5093368B2 JP 2011002951 A JP2011002951 A JP 2011002951A JP 2011002951 A JP2011002951 A JP 2011002951A JP 5093368 B2 JP5093368 B2 JP 5093368B2
- Authority
- JP
- Japan
- Prior art keywords
- tin
- welding
- steel sheet
- plated steel
- steel plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、溶接缶に使用される溶接性に優れた錫めっき鋼板の溶接特性判定方法に関するものである。 The present invention relates to a method for determining a welding property of a tin-plated steel sheet excellent in weldability used for a welding can.
食品や飲み物等を保存するための缶の製造工程は、素材となる鋼板を圧延し、さらに電気錫めっき処理と合金化処理を施して錫めっき鋼板を製造する工程と、その錫めっき鋼板を所定の寸法に切断して円筒状に加工し、端部を溶接して缶を製造する工程とに大別される。
溶接缶に使用される錫めっき鋼板(以下、溶接缶用錫めっき鋼板という)は図1に示すような構成になっており、その製造工程では、素材となる鋼板2(以下、素材鋼板という)を圧延した後、その素材鋼板2に電気錫めっき処理を施し、さらに合金化処理(いわゆるリフロー処理)を行なって、素材鋼板2の表(おもて)面2aおよび裏面2bともに錫めっき層3を形成する。こうして形成される錫めっき層3は、溶接缶用錫めっき鋼板1の両側端部で厚くなる。この現象はオーバーコートと呼ばれている。オーバーコートが発生する理由は、電気錫めっきを行なう際に、電流が素材鋼板2の両側端部に集中するからである。
The manufacturing process of cans for storing food, drinks, etc. includes rolling a steel plate as a raw material, further performing an electrotin plating process and an alloying process to manufacture a tin plated steel sheet, and the tin plated steel sheet The process is roughly divided into the steps of manufacturing a can by cutting it into a cylindrical shape, processing it into a cylindrical shape, and welding the ends.
A tin-plated steel sheet used for a welding can (hereinafter referred to as a tin-plated steel sheet for a welding can) has a structure as shown in FIG. 1, and a steel sheet 2 (hereinafter referred to as a material steel sheet) as a material in the manufacturing process. After rolling, the
このため、溶接缶用錫めっき鋼板1は、上記した電気錫めっき処理および合金化処理が施された後、図6に示すように、両側端部を切断して除去(いわゆる耳切り)して、溶接缶用錫めっき鋼板とされる。めっきままの溶接缶用錫めっき鋼板1の両側端部は、錫めっき層3の厚さが増加しているので、後述する溶接において溶接性に問題が発生しやすい。耳切りは、この溶接缶用錫めっき鋼板1の両側端部を除去する処理である。耳切りによって除去される部位4(以下、耳切り部という)の幅W1 は、錫めっき層3の厚さや溶接缶用錫めっき鋼板1の歩留り等を考慮して設定される。
For this reason, the tin-plated steel sheet 1 for welding cans is subjected to the above-described electrotin plating treatment and alloying treatment, and then, as shown in FIG. The tin-plated steel sheet for welding cans. Since the thickness of the
このようにして製造された溶接缶用錫めっき鋼板1は、缶の製造工程へ送給され、図2に示すように、さらに缶の寸法を合わせるため、通常W21を1mm以上として除去され、複数のブランク板5に分割される。ブランク板5の幅W2 は、缶の寸法に応じて設定される。
分割されたブランク板5は、さらに缶の寸法に応じて分割され、図3に示すように、円筒状に加工され、その端部を重ね合わせてシーム溶接される。ここで、缶胴板のシーム溶接作業で、一般的に問題になるのが、スプラッシユ(散り)の発生や、弱溶接(溶接強度不足)である。スプラッシュは、基本的には、過電流が流れるために発生し、弱溶接は、必要な電流が鋼板同士の接合面に十分に流れないために発生するものである。シーム溶接で、これら両欠陥をともに生じさせないための適正電流範囲(溶接可能範囲、以下単に「ACR」と記す)が存在し、その範囲が大きい方が良い。
The tin-plated steel sheet 1 for welding cans thus manufactured is fed to the can manufacturing process, and as shown in FIG. 2, in order to further adjust the dimensions of the can, it is usually removed with W 21 of 1 mm or more, Divided into a plurality of
The divided
ACRが小さいと、スプラッシュ発生を防ぐために電流値を小さくすれば、弱溶接が発生しやすく、逆に弱溶接が発生しないように電流値を大きくすれば、スプラッシュが発生することになる。このため、溶接缶用鋼板には基本的にACRが大きい素材が要求される。また、従来知られているように、錫めっき鋼板の溶接性は、合金化していない金属錫の付着量が大きく影響する。 If the ACR is small, weak welding is likely to occur if the current value is reduced in order to prevent the occurrence of splash. Conversely, if the current value is increased so that weak welding does not occur, splash will occur. For this reason, the steel plate for welding cans basically requires a material having a large ACR. Moreover, as conventionally known, the weldability of a tin-plated steel sheet is greatly influenced by the amount of metal tin that has not been alloyed.
ブランク板5は溶接缶用錫めっき鋼板1と同様に図1のような構成になっており、錫めっき層3が厚い場合には、金属錫付着量も多く、低電流では錫の合金化に熱が奪われ、発熱が不足し、弱溶接が発生して、ACRが狭くなりやすい。一方、錫めっき層3が薄い場合には、金属錫付着量も少なくなりやすく、低電流で溶接できるものの、過電流となりやすく、スプラッシュが発生しやすい。
The
そこで、ACRが大きく、溶接性に優れた溶接缶用錫めっき鋼板を製造する技術が種々検討されている。
たとえば特許文献1には、素材鋼板の表面から深さ20μmの成分とその表面の錫付着量とを規定した溶接缶用錫めっき鋼板が開示されている。特許文献1には、素材鋼板の表面から深さ20μmの成分を所定の範囲内に調整する方法は具体的に開示されていないが、極めて高度な技術を駆使する必要があることは明白である。したがって特許文献1に開示された技術を適用すれば、溶接缶用錫めっき鋼板の製造コストが上昇するのは避けられない。
Therefore, various techniques for producing tin-plated steel sheets for welding cans having a large ACR and excellent weldability have been studied.
For example, Patent Document 1 discloses a tin-plated steel sheet for a welding can that defines a component having a depth of 20 μm from the surface of a raw steel sheet and a tin adhesion amount on the surface. Patent Document 1 does not specifically disclose a method for adjusting a component having a depth of 20 μm from a surface of a raw steel plate within a predetermined range, but it is apparent that it is necessary to make use of a very advanced technique. . Therefore, if the technique disclosed in Patent Document 1 is applied, it is inevitable that the manufacturing cost of the tin-plated steel sheet for welding can rises.
また特許文献1に開示された技術のみならず、特許文献2にも開示されている通り、素材鋼板の表面の金属錫付着量は溶接缶用錫めっき鋼板の溶接性に多大な影響を及ぼすので、金属錫付着量を所定の範囲内に調整する必要がある。そのため溶接缶用錫めっき鋼板の製造工程では、製造した溶接缶用錫めっき鋼板を缶の製造工程へ送給するに先立って金属錫付着量を測定し、その測定値が所定の範囲内を満足する溶接缶用錫めっき鋼板を缶の製造工程へ送給している。
Further, as disclosed in
このような溶接缶用錫めっき鋼板の製造工程における金属錫付着量の測定は、従来、片面ずつ行なわれている。
ところが図1に示すように、溶接缶用錫めっき鋼板1の錫めっき層3は、素材鋼板2のおもて面2aおよび裏面2bともに形成され、それをブランク板5に分割して端部を溶接する際には、図3に示すように素材鋼板おもて面2aに形成された錫めっき層と素材鋼板裏面2bに形成された錫めっき層が接触して溶接される。つまり従来から知られている技術では、素材鋼板2の表裏両面に形成される錫めっき層3の厚さが溶接缶用錫めっき鋼板1の溶接性に影響を及ぼすにも関わらず、片面ずつ錫めっき層3の厚さを測定して、その溶接性を判定している。したがって従来の判定方法では、判定の精度が低下し、各々の付着量が管理範囲内にあるにも関わらず、ACRが狭く、溶接性に問題がある場合があった。
Conventionally, the measurement of the metal tin adhesion amount in the manufacturing process of such a tin-plated steel sheet for welding cans has been performed one side at a time.
However, as shown in FIG. 1, the tin-plated
本発明は上記のような問題を解消し、溶接缶用錫めっき鋼板の溶接性を精度良く判定する方法を提供することを目的とする。 An object of the present invention is to solve the above problems and to provide a method for accurately determining the weldability of a tin-plated steel sheet for a welding can.
本発明は、素材鋼板に電気錫めっき処理を施し、さらに合金化処理後、耳切りを施して得た、素材鋼板の表裏両面に錫めっき層を形成した溶接缶用錫めっき鋼板の溶接性を判定する溶接特性判定方法において、溶接缶用錫めっき鋼板の両側端部の1mm幅部を除く内側領域の板幅方向3ケ所以上の測定位置で、素材鋼板の表裏両面に付着した金属錫の付着量をそれぞれ測定し、1対をなす表裏両面の測定値をそれぞれ合算して各測定位置の両面付着量を算出し、各測定位置における両面付着量が素材鋼板1m2 あたり 1.0〜2.0gの範囲内を満足すれば良好な溶接性が確保できると判定し、各測定位置における両面付着量が素材鋼板1m2 あたり 1.0〜2.0gの範囲内を外れた場合に溶接不良が発生する可能性が高いと判定する溶接缶用錫めっき鋼板の溶接特性判定方法である。 The present invention provides the weldability of a tin-plated steel sheet for a welding can, in which a tin-plated layer is formed on both the front and back surfaces of the material steel sheet, which is obtained by subjecting the material steel sheet to electrotin plating, and further alloying and then cutting off the ears. In the welding characteristic judgment method to judge, adhesion of metallic tin adhered to both front and back surfaces of the material steel plate at three or more measurement positions in the plate width direction of the inner region excluding the 1mm width part of both ends of the tinned steel plate for welding cans the amount was measured, the measurements of the front and back surfaces that form a pair to calculate the duplex adhesion amounts of the respective measurement position by summing each range duplex adhesion amount of 1.0~2.0g per base steel sheet 1 m 2 at each measurement position If it satisfies the above, it is judged that good weldability can be secured, and there is a high possibility that poor welding will occur when the adhesion amount on both sides at each measurement position is out of the range of 1.0 to 2.0 g per 1 m 2 of the steel plate. Of tinned steel sheet for welding can A contact characteristic judging method.
本発明の溶接缶用錫めっき鋼板の溶接特性判定方法においては、素材鋼板の表裏両面それぞれ両側端から1mmの位置および板幅方向の中央で金属錫の付着量を測定することが好ましい。 In the method for determining the welding characteristics of a tin-plated steel sheet for welding cans according to the present invention, it is preferable to measure the amount of metal tin deposited at a position 1 mm from the both side ends and the center in the sheet width direction of the raw steel sheet.
本発明によれば、溶接缶用錫めっき鋼板の溶接性を精度良く判定できる。 ADVANTAGE OF THE INVENTION According to this invention, the weldability of the tin plating steel plate for welding cans can be determined with sufficient precision.
本発明を適用する溶接缶用錫めっき鋼板は、素材鋼板を圧延した後、その素材鋼板に電気錫めっき処理を施し、さらに合金化処理を施すことによって、素材鋼板の表裏両面に錫めっき層を形成した溶接缶用錫めっき鋼板である。
すなわち図1に示すように、素材鋼板2の表(おもて)面2a(上面ともいう)および裏面2b(下面ともいう)には、いずれも錫めっき層3が形成される。本発明では、溶接缶用錫めっき鋼板の溶接性を確保するために、合金化処理を施した後の金属錫の付着量の好適範囲を規定する。そこで合金化処理条件を調整するとともに、合金化処理に先立って、予め電気錫めっき処理を施す際に、素材鋼板の搬送速度や電極に印加する電圧を調整して錫めっきの厚さを制御することによって、合金化処理を施した後の金属錫の付着量が好適範囲を満足するように調整する。
The tin-plated steel sheet for welding cans to which the present invention is applied, after rolling the raw steel sheet, subjecting the raw steel sheet to electrotin plating, and further subjecting it to alloying, thereby providing tin plating layers on both the front and back surfaces of the raw steel sheet. It is the formed tin-plated steel sheet for welding cans.
That is, as shown in FIG. 1, a
ところが図4に示すように、電気錫めっき設備に配設される電極7は、素材鋼板2より大きいので、電極7から素材鋼板2に流れる電流9が、素材鋼板2の両側端部に集中する。そこで電極7と素材鋼板2との中間に遮蔽板8を前後進可能に配設し、素材鋼板2の両側端部に集中する電流を遮断する。その結果、素材鋼板2の幅方向全域にわたって均一な電流を流すことができる。なお図4には素材鋼板2の上面2a側のみ示す。素材鋼板2の下面2b側は図示を省略するが、図4と同様に遮蔽板8を用いて電流の一部を遮蔽することによって、素材鋼板2の幅方向全域にわたって均一な電流を流すことができる。また、素材鋼板2の搬送速度や電極に印加する電圧を調整して錫めっきの厚さを制御する代わりに、遮蔽板8を用いることによって、素材鋼板2の幅方向全域にわたって流す電流を調整して錫めっきの厚さを制御することもできる。
However, as shown in FIG. 4, the electrode 7 disposed in the electrotin plating facility is larger than the
このようにして素材鋼板2の上下両面の幅方向全域にわたって、均一な厚さの錫めっきを形成することができ、さらに合金化処理を施すことによって、金属錫の付着量が均一に分布した溶接缶用錫めっき鋼板を得ることができる。本発明の溶接缶用錫めっき鋼板の上面2aにおける金属錫の付着量の分布の例を図5に示す。金属錫の付着量は、JIS規格G3303 の附属書1に準拠して測定する。下面2bにおける金属錫の付着量は図示を省略するが、図5と同様の分布を示すことは言うまでもない。
In this way, it is possible to form tin plating with a uniform thickness over the entire width direction of the upper and lower surfaces of the
図4中の矢印Aは、遮蔽板8の移動方向を示す。つまり遮蔽板8は、矢印Aの方向に前後進できるように配設される。その結果、素材鋼板2の寸法が変更された場合にも、素材鋼板2の両側端部に集中する電流を遮断することができる。
このようにして溶接缶用錫めっき鋼板を製造することによって、金属錫の付着量は、図5に示すように素材鋼板2の幅方向のほぼ全域にわたって、均一に分布する。ただし両側端部(幅W1 )では金属錫の付着量が急激に増加している。これは、電気錫めっき処理を行なう際に、図4に示すような遮蔽板8を使用しても、一部の電流が素材鋼板2の両側端部に集中するのを防止できないからである。ただし、その金属錫が多量に付着した部位の幅は10mm程度以下に抑えられ、この金属錫の付着量が急激に増加した両側端部の部位(幅W1 )は、図6に示すように耳切り(除去)され、溶接缶用錫めっき鋼板1として缶の製造工程へ送給される。このような耳切りを行なった溶接缶用錫めっき鋼板1の金属錫の付着量は、素材鋼板2の幅方向全域にわたって概ね均一に分布するが、缶の製造工程でもさらに通常幅方向両側端部で各々1mm以上が除去される。
An arrow A in FIG. 4 indicates the moving direction of the
By manufacturing the tin-plated steel sheet for a welding can in this way, the amount of metal tin deposited is uniformly distributed over substantially the entire width of the
したがって溶接缶用錫めっき鋼板の製造工程において、金属錫の付着量を規定する必要があるのは、溶接缶用錫めっき鋼板として缶の製造工程へ送給された後に切除される部分(幅W21)を除く内側の領域である。
このようにして缶の製造工程において除去される部分(幅W21)を除く内側の領域における金属錫の付着量は、素材鋼板2の単位面積(=1m2 )あたり、表裏両面(上下両面)に付着した金属錫の測定値が表裏両面の合計で1.0〜2.0 gの範囲内を満足する必要がある。なお金属錫の付着量は、JIS規格G3303 の附属書1に準拠して測定する。
Therefore, in the manufacturing process of the tin-plated steel sheet for welding cans, it is necessary to regulate the adhesion amount of metallic tin as a portion (width W) cut after being fed to the can manufacturing process as a tin-plated steel sheet for welding cans. 21 ) The inner area excluding.
In this way, the amount of metal tin deposited in the inner region excluding the portion (width W 21 ) removed in the can manufacturing process is the front and back surfaces (upper and lower surfaces) per unit area (= 1 m 2 ) of the
ここで、従来金属錫の付着量は、前述のように表(おもて)面,裏面での付着量を各々別個に管理していた。しかしながら、発明者らの検討では、各面が管理値の範囲内にある場合でも、溶接性が問題となる場合があり、この点を検討した結果、金属錫の付着量を表裏合計の値で管理することにより、溶接性を正確に評価でき、溶接性に優れる溶接缶用錫めっき鋼板を製造できることが判明した。 Here, as for the adhesion amount of the conventional metal tin, the adhesion amount on the front (front) surface and the back surface was separately managed as described above. However, in the inventors' investigation, even when each surface is within the range of the control value, weldability may be a problem, and as a result of examining this point, the adhesion amount of metal tin is the total value of the front and back sides. It has been found that, by managing, the weldability can be accurately evaluated, and a tin-plated steel sheet for a welding can excellent in weldability can be produced.
表裏両面の金属錫の付着量が合計 1.0g/m2 未満では、低電流で溶接できるものの、過電流となりやすく、スプラッシュが発生しやすい。一方、金属錫の付着量が合計 2.0g/m2 を超えると、低電流では錫の合金化に熱が奪われ、発熱が不足し、弱溶接が発生しやすい。特にスプラッシュが発生すると、溶接部における錫めっき層3の防錆効果が劣化し、缶内に収容される食品や飲み物等が変質,腐敗するおそれがある。
If the total amount of metallic tin on both the front and back surfaces is less than 1.0 g / m 2 , welding can be performed at a low current, but overcurrent tends to occur and splash is likely to occur. On the other hand, if the total amount of metal tin deposited exceeds 2.0 g / m 2 , heat is lost to the alloying of tin at low current, heat generation is insufficient, and weak welding is likely to occur. In particular, when splash occurs, the rust prevention effect of the tin-plated
合金化処理を施した溶接缶用錫めっき鋼板1の両側の缶の製造工程での除去部(幅W21)を除く内側の領域における金属錫の付着量が、素材鋼板2の単位面積(=1m2 )あたり、表裏両面で合計 1.0〜2.0gの範囲内を満足すれば、缶の製造工程において弱溶接やスプラッシュの発生を防止し、良好な溶接性を確保できる。したがって、溶接缶用錫めっき鋼板1表裏両面の金属錫の付着量を測定することによって、溶接缶用錫めっき鋼板1の溶接性を判定することが可能である。 The adhesion amount of metallic tin in the inner region excluding the removal part (width W 21 ) in the can manufacturing process on both sides of the tin-plated steel plate 1 for welding can subjected to alloying treatment is the unit area (= If the total range of 1.0 to 2.0 g per 1 m 2 ) is satisfied on both the front and back surfaces, it is possible to prevent weak welding and splash in the can manufacturing process and to ensure good weldability. Therefore, it is possible to determine the weldability of the tin-plated steel sheet 1 for welding cans by measuring the adhesion amount of metal tin on both front and back surfaces of the tin-plated steel sheet 1 for welding cans.
金属錫の付着量の測定は、合金化処理を施した溶接缶用錫めっき鋼板1の各測定位置の表裏両面から試料(測定領域:幅1mm,長さ10mm)を採取して、JIS規格G3303 の附属書1に準拠して行なう。金属錫の付着量の測定位置(すなわち試験片を採取する位置)は、缶の製造工程での除去部(幅W21)を除く内側の領域における板幅方向に3ケ所以上とし、各測定位置においてそれぞれ表裏両面に付着した金属錫の付着量を測定する。次いで、各測定位置における表(おもて)面に付着した金属錫の付着量と裏面に付着した金属錫の付着量との1対をなす測定値を合算して合計値(以下、両面付着量という)を算出する。各測定位置における両面付着量のいずれもが 1.0〜2.0g/m2 の範囲内を満足すれば良好な溶接性が確保でると判定し、各測定位置における両面付着量のいずれかが 1.0〜2.0g/m2 の範囲を外れた場合はスプラッシュや弱溶接が発生しやすいと判定する。 To measure the amount of metal tin deposited, samples (measurement area: 1 mm wide, 10 mm long) were taken from both front and back surfaces of the tin-plated steel sheet 1 for welding cans that had been alloyed, and JIS standard G3303. In accordance with Annex 1. The measurement position of the amount of adhesion of metal tin (that is, the position where the test piece is collected) is at least three locations in the plate width direction in the inner area excluding the removal part (width W 21 ) in the can manufacturing process. The amount of metal tin adhering to both front and back surfaces is measured. Next, the total value (hereinafter referred to as double-sided adhesion) is obtained by adding together a pair of measured values of the amount of metal tin adhering to the front (front) surface and the amount of metal tin adhering to the back surface at each measurement position. (Referred to as quantity). If any of the double-sided adhesion amounts at each measurement position satisfies the range of 1.0 to 2.0 g / m 2 , it is determined that good weldability is ensured, and any of the double-sided adhesion amounts at each measurement position is 1.0 to 2.0. When it is out of the range of g / m 2 , it is determined that splash or weak welding is likely to occur.
溶接性の判定精度は、金属錫の付着量の測定位置が多いほど向上する。しかし試料が増加すれば、測定に要する費用や時間が増大する。したがって溶接性判定のコスト削減および能率向上の観点から、金属錫の付着量の測定位置は少ない方が好ましい。図5に示すように、合金化処理を行ない、耳切り部(幅W1 )を除いた後の内側の領域では、金属錫の付着量は均一に分布するので、金属錫の付着量の測定位置は板幅方向の中央と両側耳切り部の近傍(合計3ケ所)で金属錫の付着量を測定すれば、十分な判定精度を維持できる。既に説明した通り、本発明の溶接缶用錫めっき鋼板では、缶の製造工程において耳切り部として1mm以上除去されるため、溶接缶用錫めっき鋼板の両側端から1mmの位置および板幅方向の中央(合計3ケ所)で、上下両面に付着した金属錫の付着量を測定するのが好ましい。 The determination accuracy of weldability is improved as the measurement position of the adhesion amount of metallic tin is increased. However, as the number of samples increases, the cost and time required for measurement increase. Therefore, from the viewpoint of cost reduction and efficiency improvement in weldability determination, it is preferable that the number of measurement positions of the amount of metal tin deposited is small. As shown in FIG. 5, the amount of metal tin deposited is uniformly distributed in the inner region after the alloying process is performed and the edge cut portion (width W 1 ) is removed. A sufficient determination accuracy can be maintained by measuring the amount of metal tin deposited at the center in the width direction of the plate and in the vicinity of both side edge cut portions (total of three locations). As already described, in the tin-plated steel sheet for welding cans of the present invention, 1 mm or more is removed as the edge cut portion in the can manufacturing process. It is preferable to measure the amount of metal tin adhering to the upper and lower surfaces at the center (total of three locations).
素材鋼板( DT5CA相当:厚さ0.2mm ,幅843mm )に対して金属錫付着量の目標範囲を片面あたり 0.6〜1.2g/m2 として両面に電気錫めっき処理および合金化処理を施した後、幅両側から各々10mmづつ耳切りし、溶接缶用錫めっき鋼板を製造した。電気錫めっき処理では、図4に示すように遮蔽板8を使用して、電流9が素材鋼板2の両側端部に集中するのを防止するとともに、素材鋼板2の搬送速度を調整して、金属錫の付着量が目標範囲を満足するように制御した。ここで一部について本発明の例として、合金化処理を施した溶接缶用錫めっき鋼板の表裏両面に付着した金属錫の付着量が合計 1.0〜2.0g/m2 の範囲内を満足するように設定した。
After subjecting the steel sheet (equivalent to DT5CA: thickness 0.2mm, width 843mm) to a target range of metal tin adhesion of 0.6 to 1.2g / m 2 per side, both sides were electrotin plated and alloyed. A tin-plated steel sheet for welding cans was manufactured by cutting off each edge 10 mm from both sides of the width. In the electrotin plating process, as shown in FIG. 4, the shielding
得られた溶接缶用錫めっき鋼板の両側端から1mmの位置および板幅方向の中央で試料を採取し、上下両面に付着した金属錫の付着量を測定した。各測定位置における上面の付着量と下面の付着量の1対をなす測定値を合算して両面付着量を算出した。こうして求めた3ケの両面付着量が3ケ所とも 1.0〜2.0g/m2 の範囲内を満足する溶接缶用錫めっき鋼板を選別した。これを好適例とする。なお、上記した本発明例は全て好適例となっていた。 A sample was taken at a position 1 mm from the both ends of the obtained tin-plated steel sheet for welding cans and in the center in the sheet width direction, and the amount of metal tin adhering to both the upper and lower surfaces was measured. The double-sided adhesion amount was calculated by adding together the measurement values forming a pair of the upper surface adhesion amount and the lower surface adhesion amount at each measurement position. The tin-plated steel sheets for welding cans were selected so that the three double-sided adhesion amounts thus obtained satisfied the range of 1.0 to 2.0 g / m 2 at all three locations. This is a preferred example. The above-described examples of the present invention are all suitable examples.
一方、好適例以外の、両面付着量が 1.0〜2.0g/m2 の範囲を外れる溶接缶用錫めっき鋼板は、比較例として区分した。
好適例と比較例の溶接缶用錫めっき鋼板を缶の製造工程へ送給し、図2に示すように、幅W21=1mmの除去を行ない、かつ幅W2 =120mm のブランク板5に分割した。さらにブランク板5を長さ210mm に切断して円筒状に加工し、その端部を重ね合わせて溶接を行なった。
On the other hand, the tin-plated steel sheet for welding cans other than the preferred examples, in which the double-sided adhesion amount is out of the range of 1.0 to 2.0 g / m 2 was classified as a comparative example.
The tinned steel sheets for welding cans of the preferred and comparative examples are fed to the can manufacturing process, and as shown in FIG. 2, the width W 21 = 1 mm is removed and the
溶接は、銅ワイヤー型電気抵抗加熱シーム溶接機(商用機)を用いて下記の条件にて行ない、ACRを求めた。
缶型 ; 350g飲料缶胴
銅ワイヤー直径; 1.3mm
通板速度 ; 120m/分
溶接圧力 ; 392N(40 kgf)
周波数 ; 700Hz
溶接ラップ代 ; 0.5mm
ここでACRを求めるにあたり、上限電流値はスプラッシュが発生しない電流値とした。また、下限電流値は弱溶接が発生しない電流値をピール溶接強度で評価し、すなわち溶接部の一端に切り込みを入れ、溶接部を缶胴から引き剥がすピールテストにより、溶接部の全長が引きちぎれるものが強度が十分と判定、引き剥がしの途中で接合面が剥離する場合を強度不十分(弱溶接)と判定して、下限電流値を求めた。このようにして求めた上限電流値と下限電流値の差を溶接可能範囲ACRとした。
Welding was performed under the following conditions using a copper wire type electric resistance heating seam welding machine (commercial machine) to obtain ACR.
Can type; 350g beverage can body Copper wire diameter; 1.3mm
Plate speed: 120 m / min Welding pressure: 392 N (40 kgf)
Frequency: 700Hz
Welding lap allowance: 0.5mm
Here, in obtaining ACR, the upper limit current value is a current value at which splash does not occur. In addition, the lower limit current value is evaluated by peel welding strength at a current value at which weak welding does not occur, that is, the entire length of the welded part is torn off by a peel test in which a cut is made at one end of the welded part and the welded part is peeled off from the can body. It was determined that the strength was sufficient, and the case where the joint surface peeled during peeling was determined as insufficient strength (weak welding), and the lower limit current value was determined. The difference between the upper limit current value and the lower limit current value obtained in this way was defined as a weldable range ACR.
好適例では全幅にわたり、缶の製造上、問題のない良好なACRを確保できた。好適例は、両面付着量が 1.0〜2.0g/m2 の範囲を外れる比較例のACRを超えるACRを確保することができた。 In the preferred example, a good ACR having no problem in manufacturing the can was secured over the entire width. In the preferred example, the ACR exceeding the ACR of the comparative example in which the double-sided adhesion amount is out of the range of 1.0 to 2.0 g / m 2 could be secured.
本発明によれば、溶接缶用錫めっき鋼板の溶接性を精度良く判定できるので、産業上格段の効果を奏する。 According to the present invention, since the weldability of the tin-plated steel sheet for welding cans can be determined with high accuracy, the industrially significant effect is achieved.
1 溶接缶用錫めっき鋼板
2 素材鋼板
2a 素材鋼板表面
2b 素材鋼板裏面
3 錫めっき層
4 耳切り部
5 ブランク板
51 缶の製造工程での除去部
6 溶接部
7 電極
8 遮蔽板
9 電流
1 Tinned steel plate for
2a Material steel plate surface
2b Back surface of
51 Removal part in can manufacturing process 6 Welded part 7
Claims (2)
The welding characteristic determination of the tin-plated steel sheet for welding cans according to claim 1, wherein the adhesion amount of the metal tin is measured at a position of 1 mm from both ends of the front and back surfaces of the material steel sheet and at the center in the sheet width direction. Method.