JP5077510B2 - Secondary battery negative electrode binder composition, secondary battery negative electrode slurry, and secondary battery negative electrode - Google Patents

Description

  The present invention relates to a binder composition for a secondary battery electrode, a slurry for a secondary battery electrode, and a secondary battery electrode. More specifically, the present invention has excellent adhesion to a current collector and can be charged even under high and low temperature conditions. Binder composition for secondary battery electrode capable of providing a secondary battery having excellent discharge cycle characteristics, slurry for secondary battery electrode, and good adhesion between the electrode layer and the current collector, The present invention relates to a secondary battery electrode capable of providing a secondary battery excellent in charge / discharge cycle characteristics even under high temperature and low temperature conditions.

  In recent years, electronic devices have been remarkably reduced in size and weight, and accordingly, there is an extremely strong demand for downsizing and weight reduction of batteries as a power source. Various secondary batteries have been developed in order to satisfy such requirements. For example, nickel hydride secondary batteries and lithium ion secondary batteries have been put into practical use.

  As a method of manufacturing an electrode which is a constituent member of these secondary batteries, an active material such as a hydrogen storage alloy or graphite, carboxymethyl cellulose as a thickener, styrene butadiene copolymer latex as a binder, dispersion There is a method of applying and drying a paste obtained by kneading water as a medium on the surface of a current collector (see, for example, Patent Documents 1 and 2).

  Here, the binder functions to improve the adhesion between the electrode layer containing the active material and the current collector. However, the styrene butadiene copolymer latex has not always been sufficient in adhesion to the current collector. In a secondary battery using an electrode in which the adhesion between the electrode layer and the current collector is not sufficient, there is a problem that battery characteristics such as charge / discharge cycle characteristics cannot be improved.

  As a related prior art, a carboxy-modified styrene butadiene copolymer latex having a gel content in a predetermined range is included to improve the adhesion of the electrode layer and the current collector to improve the characteristics of the secondary battery. A conductive binder composition for electrodes is disclosed (for example, see Patent Document 3). Further, it is disclosed that an aqueous dispersion composition containing polytetrafluoroethylene and polyoxyethylene alkyl ether is suitable as a binder for batteries (see, for example, Patent Document 4).

However, even the binders (binders) and the like disclosed in Patent Documents 3 and 4 are not necessarily sufficient for improving the adhesion between the electrode layer and the current collector. In addition, when a secondary battery equipped with an electrode having insufficient adhesion is repeatedly used under special conditions such as high temperature and low temperature, the charge / discharge cycle characteristics tend to be reduced, which is solved. There is a need to take countermeasures.
Japanese Patent Laid-Open No. 11-7948 Japanese Patent Laid-Open No. 2001-210318 JP-A-9-320604 JP-A-8-269285

  The present invention has been made in view of such problems of the prior art, and the problem is that it has excellent adhesion to the current collector and is charged and discharged even under high and low temperature conditions. Binder composition for secondary battery electrode capable of providing secondary battery with excellent cycle characteristics, slurry for secondary battery electrode, and good adhesion between electrode layer and current collector, high temperature Another object of the present invention is to provide a secondary battery electrode capable of providing a secondary battery excellent in charge / discharge cycle characteristics even under low temperature conditions.

  As a result of intensive studies to achieve the above-mentioned problems, the present inventors have added the above-mentioned problems to specific polymers by adding and mixing a compound having a cloud point within a predetermined numerical range at a specific ratio. The inventors have found that it is possible to achieve this, and have completed the present invention.

  That is, according to this invention, the binder composition for secondary battery electrodes, the slurry for secondary battery electrodes, and a secondary battery electrode which are shown below are provided.

[1] (A) 100 parts by mass of an aqueous polymer dispersion selected from the group consisting of a styrene-butadiene copolymer latex and an acrylic emulsion (but as a solid content), and (B) a cloud point of 70 ° C. or less The binder composition for secondary battery electrodes containing 1-20 mass parts of these.
[2] The binder composition for a secondary battery electrode according to [1], which is for a negative electrode.

[ 3 ] The binder composition for secondary battery electrodes according to [1] or [2] , wherein the compound (B) is a nonionic surfactant and / or a thermosensitive polymer.

[ 4 ] The nonionic surfactant is at least one selected from the group consisting of polyoxyethylene alkyl ether derivatives, polyoxyethylene-polyoxypropylene condensates, and polyoxyethylene-polyoxypropylene alkyl ether derivatives. The binder composition for secondary battery electrodes according to [ 3 ].

[5] The heat-sensitive polymer, a secondary battery electrode binder composition according to the a port Li N- isopropylacrylamide [3] or [4].

[ 6 ] A slurry for a secondary battery electrode, comprising the binder composition for a secondary battery electrode according to any one of [1] to [ 5 ] and an electrode active material.

[ 7 ] The slurry for secondary battery electrodes according to [ 6 ], containing 0.1 to 10 parts by mass (but as a solid content) of the binder for secondary battery electrode with respect to 100 parts by mass of the electrode active material. .

[ 8 ] A secondary battery comprising: a current collector; and an electrode layer formed by applying and drying the slurry for a secondary battery electrode according to [ 6 ] or [ 7 ] on a surface of the current collector. electrode.

  The binder composition for a secondary battery electrode of the present invention is excellent in adhesiveness with a current collector, and can provide a secondary battery excellent in charge / discharge cycle characteristics even under high temperature and low temperature conditions. This is an effect.

  Moreover, the slurry for secondary battery electrodes of the present invention is excellent in adhesion to the current collector, and can provide a secondary battery excellent in charge / discharge cycle characteristics even under high temperature and low temperature conditions. This is an effect.

  The secondary battery electrode of the present invention has good adhesion between the electrode layer and the current collector, and can provide a secondary battery excellent in charge / discharge cycle characteristics even under high temperature and low temperature conditions. There is an effect that there is.

  BEST MODE FOR CARRYING OUT THE INVENTION The best mode for carrying out the present invention will be described below, but the present invention is not limited to the following embodiment, and is based on the ordinary knowledge of those skilled in the art without departing from the gist of the present invention. It should be understood that modifications and improvements as appropriate to the following embodiments also fall within the scope of the present invention.

(Binder composition for secondary battery electrode)
One embodiment of the binder composition for a secondary battery electrode of the present invention is (A) at least one polymer aqueous dispersion selected from the group consisting of a styrene-butadiene copolymer latex and an acrylic emulsion (hereinafter referred to as “(A ) Component ”) 100 parts by mass (but as solid content) and (B) a compound having a cloud point of 70 ° C. or less (hereinafter also referred to as“ component (B) ”) 1-20 parts by mass. Is. The details will be described below.

(A) component (A) component contained in the binder composition for secondary battery electrodes of this embodiment is at least selected from the group consisting of (i) styrene butadiene copolymer latex and (ii) acrylic emulsion. It is a kind of polymer aqueous dispersion.

(I) Styrene butadiene copolymer latex The styrene butadiene copolymer latex is synthesized by a usual emulsion polymerization method. The styrene butadiene copolymer contained in the styrene butadiene copolymer latex is composed of a structural unit composed of an aliphatic conjugated diene monomer, a structural unit composed of an aromatic vinyl compound monomer, and a vinyl monomer having an acid component. It is a copolymer composed of structural units composed of a body. Examples of the aliphatic conjugated diene monomer include 1,3-butadiene, isoprene, 2-chloro-1,3-butadiene, chloroprene and the like. Among these, 1,3-butadiene is preferable in terms of improving adhesion to the current collector. These aliphatic conjugated diene monomers can be used alone or in combination of two or more. The butadiene bond content of the styrene-butadiene copolymer is preferably 30 to 85% by mass, more preferably 30 to 70% by mass, and particularly preferably 30 to 60% by mass. When the butadiene bond content is less than 30% by mass, the adhesion to the current collector and the flexibility of the electrode tend to be insufficient. On the other hand, if it exceeds 85% by mass, the adhesion to the current collector tends to be insufficient.

  Examples of the aromatic vinyl compound monomer include styrene, α-methylstyrene, p-methylstyrene, vinyltoluene, and chlorostyrene. Among these, styrene is preferable. These aromatic vinyl compound monomers can be used alone or in combination of two or more. The content of styrene in the styrene-butadiene copolymer is preferably 3 to 60% by mass, and more preferably 10 to 60% by mass. When the content ratio of styrene is less than 3% by mass, the stability of the slurry for secondary battery electrodes using the same tends to decrease. On the other hand, if it exceeds 60% by mass, the resulting polymer becomes too hard and tends to have poor adhesion.

  In preparing the styrene-butadiene copolymer latex, it is preferable to use 0.1 to 8% by mass of the carboxyl group-containing vinyl monomer for carboxy modification, and 0.5 to 6% by mass of the total monomers. % Is more preferable, and 1 to 4% by mass is particularly preferable. When the amount of the carboxyl group-containing vinyl monomer used is less than 0.1% by mass, the adhesion with the current collector tends to be insufficient. On the other hand, if it exceeds 8% by mass, the surface of the active material or conductive carbon is excessively covered, and the overvoltage tends to increase. Specific examples of the carboxyl group-containing vinyl monomer include itaconic acid, acrylic acid, methacrylic acid, fumaric acid, maleic acid and the like. Among these, itaconic acid, acrylic acid, and methacrylic acid are preferable in terms of polymerization stability and dispersion stability. These carboxyl group-containing vinyl monomers can be used alone or in combination of two or more.

  Furthermore, the styrene butadiene copolymer latex is a structural unit comprising an aliphatic conjugated diene monomer, an aromatic vinyl compound monomer, and other monomers copolymerizable with a carboxyl group-containing vinyl monomer. It is preferable to contain 0.1-50 mass%. When the content ratio of the constituent units composed of other monomers is less than 0.1% by mass, the stability of the secondary battery electrode slurry tends to decrease. On the other hand, if it exceeds 50% by mass, the resulting polymer becomes too hard and tends to have poor adhesion. Examples of other monomers include, for example, methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, n-butyl (meth) acrylate, isobutyl (meth) acrylate, and t-butyl. (Meth) acrylate, pentyl (meth) acrylate, hexyl (meth) acrylate, heptyl (meth) acrylate, octyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, nonyl (meth) acrylate, decyl (meth) acrylate, etc. (Meth) acrylic acid ester monomers, nitrile group-containing monomers such as (meth) acrylonitrile, (meth) acrylamide, N-methylol (meth) acrylamide, N-ethylol (meth) acrylamide, dimethyl (meth) acrylamide, The (Meth) acrylamide monomers such as chill (meth) acrylamide, sulfonic acid group-containing monomers such as acrylamide methylpropane sulfonic acid and styrene sulfonate, divinylbenzene, ethylene glycol dimethacrylate, isopropylene glycol diacrylate, Bifunctional monomers such as tetramethylene glycol dimethacrylate, hydroxyl group-containing monomers such as 2-hydroxyethyl methacrylate, 3-hydroxybutyl methacrylate, 2-hydroxyethyl acrylate, 3-hydroxybutyl acrylate, 3-methacryloxypropyl Examples thereof include alkoxysilane group-containing monomers such as methyldimethoxysilane, 3-methacryloxypropyltrimethoxysilane, and 3-methacryloxypropyltriethoxysilane.

The gel content of the styrene butadiene copolymer latex is preferably 20 to 95% by mass, more preferably 40 to 95% by mass, and particularly preferably 65 to 95% by mass. In addition, "gel content" as used in this specification means the ratio of the insoluble content (toluene insoluble content) with respect to toluene contained in a polymer (styrene butadiene copolymer latex). The gel content can be measured as follows. First, a polymer aqueous dispersion adjusted to pH 7 to 8 with 0.5N ammonia water or 1N sodium hydroxide aqueous solution is dried at 120 ° C. for 1 hour to form a film to obtain a dry film. The obtained dry film is placed in a container such as an Erlenmeyer flask with 100 times the amount (mass ratio) of toluene and shaken for 3 hours, and then filtered through a 200 mesh filter to collect insoluble matter. The collected insoluble matter is dried at 120 ° C. for 1 hour, the dry mass (toluene insoluble matter mass) is measured, and the “gel content” can be calculated from the following formula (1).
Gel content (mass%) = (toluene insoluble mass / dry film mass) × 100 (1)

  When the gel content of the styrene-butadiene copolymer latex is more than 95% by mass, the binder performance of the secondary battery electrode binder composition using the styrene-butadiene copolymer latex is insufficient, and the adhesion to the current collector tends to be lowered. When the amount of the binder composition used is increased in order to compensate for the shortage of the binder performance, the overvoltage tends to increase, making it difficult to obtain a secondary battery with high characteristics. On the other hand, when the gel content of the styrene butadiene copolymer latex is less than 20% by mass, a polymer flow is generated when the electrode is formed and dried by heating, and the active material and the conductive carbon are excessively coated. Tend to rise. For adjusting the gel content, general methods such as adjustment of the polymerization temperature, adjustment of the polymerization initiator amount, adjustment of the polymerization conversion rate, adjustment of the chain transfer agent amount and the like are employed.

  The particle size of the styrene butadiene copolymer latex is preferably 0.01 to 0.5 μm, and more preferably 0.01 to 0.3 μm. When the particle diameter is less than 0.01, the viscosity of the resulting slurry for secondary battery electrodes tends to be too high. On the other hand, when the particle diameter is more than 0.5 μm, the binder performance is insufficient and the adhesion to the current collector tends to be lowered.

(Ii) Acrylic emulsion The acrylic emulsion contains at least a (meth) acrylic acid ester and a copolymer obtained from a vinyl monomer having an acid component. Specific examples of (meth) acrylic acid esters include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, n-butyl (meth) acrylate, isobutyl (meth) acrylate, and t-butyl (meth). Examples include acrylate, pentyl (meth) acrylate, hexyl (meth) acrylate, heptyl (meth) acrylate, octyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, nonyl (meth) acrylate, decyl (meth) acrylate, and the like. it can. Among these, methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, n-butyl acrylate, heptyl acrylate, octyl acrylate, 2-ethylhexyl acrylate, and nonyl acrylate are preferable, and methyl methacrylate and 2-ethylhexyl acrylate are more preferable.

  Specific examples of the vinyl monomer having an acid component include acrylic acid, methacrylic acid, maleic acid and the like. Among these, acrylic acid and methacrylic acid are preferable.

  The composition ratio of each monomer component constituting the copolymer contained in the acrylic emulsion is 65 to 99.8% by mass of (meth) acrylic acid ester and 0.2% of vinyl monomer having an acid component. It is preferable that it is -35 mass%. In addition, it is still more preferable that (meth) acrylic acid ester is 65-90 mass%, and the vinyl monomer which has an acid component is 1-25 mass%.

  The copolymer contained in the acrylic emulsion may be obtained from (meth) acrylic acid ester and other monomers copolymerizable with a vinyl monomer having an acid component. Examples of other copolymerizable monomers include aromatic vinyl compound monomers such as styrene, α-methylstyrene, p-methylstyrene, vinyltoluene and chlorostyrene, and nitrile group-containing monomers such as (meth) acrylonitrile. Monomers, (meth) acrylamide monomers such as (meth) acrylamide, N-methylol (meth) acrylamide, N-ethylol (meth) acrylamide, dimethyl (meth) acrylamide, diethyl (meth) acrylamide, and acrylamide methylpropane sulfone Acid, sulfonic acid group-containing monomers such as styrene sulfonate, bifunctional monomers such as divinylbenzene, ethylene glycol dimethacrylate, isopropylene glycol diacrylate, tetramethylene glycol dimethacrylate, 2-hydroxyethyl methacrylate Hydroxyl group-containing monomers such as 3-hydroxybutyl methacrylate, 2-hydroxyethyl acrylate, 3-hydroxybutyl acrylate, 3-methacryloxypropylmethyldimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-methacrylate An alkoxysilane group-containing monomer such as loxypropyltriethoxysilane can be exemplified.

  In preparing the acrylic emulsion, the above-mentioned bifunctional monomer can be used as a crosslinking agent. These crosslinking agents are preferably used in an amount of 15% by mass or less, more preferably 10% by mass or less. The acrylic emulsion may be a crosslinked type or a non-crosslinked type. The polymerization method of the copolymer contained in the acrylic emulsion may be any of solution polymerization, emulsion polymerization, suspension polymerization, and gas phase polymerization. Further, the structure of the obtained copolymer may be any of a random type, a graft type, and a block type.

  The acrylic emulsion preferably contains an anionic or nonionic surfactant. The content of these surfactants is preferably 0.01 to 3% by mass, more preferably 0.1 to 2% by mass, and more preferably 0.5 to 1.% by mass with respect to the copolymer. It is especially preferable that it is 5 mass%.

  In addition, the acrylic emulsion includes a fluorine-containing polymer obtained from a monomer component containing vinylidene fluoride and propylene hexafluoride described in JP-A-10-302799, and (meth) acrylic acid alkyl esters. And an aqueous dispersion of a complex with a functional group-containing polymer obtained from a monomer component containing a functional group-containing unsaturated monomer.

(B) component (B) component contained in the binder composition for secondary battery electrodes of this embodiment is a compound with a cloud point of 70 degrees C or less. By including this component (B), the adhesion of the obtained binder composition for secondary battery electrodes to the current collector can be improved, and charge / discharge cycle characteristics even under high and low temperature conditions. It is possible to provide a secondary battery excellent in. As used herein, the “cloud point” refers to the temperature at which an aqueous solution of an apparently transparent sample is heated to gradually increase its temperature and the sample begins to precipitate and the aqueous solution begins to become cloudy. Say. A specific method for measuring the cloud point will be described below. First, a 1% by mass aqueous solution of a sample to be measured is prepared. As shown in FIG. 1, 100 g of the prepared aqueous solution 6 is put into a container 5 of a measuring device 4 equipped with a heater 1, a thermometer 2, and a stirring blade 3. Next, heating and stirring is performed while rotating the stirring blade 3 at a rotational speed of 200 rpm until it can be confirmed that the aqueous solution 6 is transparent (the sample is sufficiently dissolved). If it can be confirmed that the aqueous solution 6 is transparent, the rotational speed of the stirring blade 3 is set to 80 rpm, and the temperature is increased at a rate of 1 ° C./1 minute by heating. The temperature at which the milky discontinuous phase appears is “cloudy” Measure as “point”.

  When the cloud point of the component (B) contained in the binder composition for a secondary battery electrode is not higher than a predetermined temperature, the water solubility of the component (B) is abrupt when the secondary battery electrode binder composition is heated and dried. Instability of the binder composition for secondary battery electrodes occurs due to the change to This is because the moisture in the binder composition for secondary battery electrodes is restrained from moving component (A) as it evaporates to the side opposite to the current collector / active material interface side. It is assumed that there is. As a result, the component (A) tends to stay in the vicinity of the current collector / active material interface, and it is assumed that the adhesion to the current collector can be improved.

  The binder composition for a secondary battery electrode of the present embodiment contains 1 to 20 parts by mass of the component (B) with respect to 100 parts by mass of the component (A) (but as a solid content), preferably 3 to 15 parts by mass, more preferably 3 to 10 parts by mass is contained.

  Moreover, the cloud point of (B) component is 70 degrees C or less, It is preferable that it is 0-70 degreeC, and it is still more preferable that it is 25-68 degreeC. When the temperature is lower than 0 ° C., the viscosity of the binder composition for secondary battery electrodes tends to be too high. On the other hand, if it exceeds 70 ° C., the adhesion with the current collector tends to be lowered.

  As a (B) component contained in the binder composition for secondary battery electrodes of this embodiment, a nonionic surfactant and / or a thermosensitive polymer can be mentioned as a suitable example. Preferable examples of nonionic surfactants include polyoxyethylene alkyl ether derivatives, polyoxyethylene-polyoxypropylene condensates, and polyoxyethylene-polyoxypropylene alkyl ether derivatives. Examples of polyoxyethylene alkyl ether derivatives include the Emulgen series (manufactured by Kao Corporation), Adekatol NP, Adekatol OPL, Adekatol LA series (Asahi Denka Kogyo Co., Ltd.), Neugen ET series, Neugen EA series (Daiichi Kogyo Seiyaku Co., Ltd.) ). Preferable examples of the polyoxyethylene-polyoxypropylene condensate include, for example, Adekapluronic L, P, F series (Asahi Denka Kogyo Co., Ltd.), Epan 400, 700 series (Daiichi Kogyo Seiyaku Co., Ltd.). it can. Examples of the polyoxyethylene-polyoxypropylene alkyl ether derivative include Adecatol LB series (manufactured by Asahi Denka Kogyo Co., Ltd.). Examples of the thermosensitive polymer include polyvinyl methyl ether and poly N-isopropylacrylamide (N-isopropylacrylamide homopolymer). Polyvinyl methyl ether and poly N-isopropyl acrylamide are disclosed in J. Org. Colloid Interface Sci. , 35, 77 (1971), and J. Org. Macromol. Sci. Chem. , A2, 1441 (1968).

  The component (A) contained in the binder composition for secondary battery electrodes of the present embodiment is usually emulsion polymerization of various monomer components in an aqueous medium using an emulsifier, a polymerization initiator, etc. Can be prepared. Examples of the emulsifier include anionic surfactants, nonionic surfactants, and amphoteric surfactants. These emulsifiers can be used alone or in combination of two or more.

  Examples of the anionic surfactants include higher alcohol sulfates, alkylbenzene sulfonates, aliphatic sulfonates, and polyethylene glycol alkyl ether sulfates. Examples of the nonionic surfactant include an alkyl ester type, an alkyl ether type, or an alkyl phenyl ether type polyethylene glycol. Examples of the amphoteric surfactant include those having a carboxylate, sulfate ester, sulfonate, and phosphate ester salt as the anion moiety, and those having an amine salt and a quaternary ammonium salt as the cation moiety. Specific examples include betaines such as lauryl betaine and stearyl betaine, amino acid type compounds such as lauryl-β-alanine, stearyl-β-alanine, lauryl di (aminoethyl) glycine, octyldi (aminoethyl) glycine, and the like. Can do.

  Moreover, when emulsion polymerization is performed using a reactive emulsifier, the amount of the emulsifier used can be reduced. In particular, since the amount of the emulsifier liberated in the active material paste can be reduced, a secondary battery electrode binder composition with less foaming and excellent adhesion can be obtained. Examples of the reactive emulsifier include an emulsifier having an ethylenically unsaturated group as a radical reactive group, a polyoxyalkylene group, a sulfone group, a sulfuric acid group as a hydrophilic group, and an alkyl group as a hydrophobic group in one molecule. it can.

  Commercially available products of such reactive emulsifiers include, for example, “Latemul S-180A”, “Latemul PD-104” (trade name (manufactured by Kao Corporation)), “Eleminol JS-2” (trade name (Sanyo Kasei Co., Ltd.) )), "AQUALON HS-10", "AQUALON BC-10", "AQUALON KH-10" (trade name (Daiichi Kogyo Seiyaku Co., Ltd.)), "ADEKA rear soap SE-10N", "ADEKA rear soap" SR-10 "(trade name (Asahi Denka Kogyo Co., Ltd.)) and other anionic reactive emulsifiers," Aqualon RS-20 "(trade name (Daiichi Kogyo Seiyaku Co., Ltd.))," Adekaria soap NE-20 " Non-ionic reactive emulsifiers such as (trade name (Asahi Denka Kogyo Co., Ltd.)) can be mentioned. These can be used alone or in combination of two or more. It is preferable to use 0.2 to 20 parts by mass of the emulsifier described above with respect to 100 parts by mass of the monomer component.

  Examples of the polymerization initiator include water-soluble polymerization initiators represented by persulfates such as sodium persulfate, potassium persulfate, and ammonium persulfate, cumene hydroperoxide, diisopropylbenzene hydroperoxide, paramentane hydroperoxide, and the like. Oil-soluble polymerization initiators typified by hydroperoxides can be used. It is preferable to use 0.01 to 10 parts by mass of these water-soluble polymerization initiator and oil-soluble initiator with respect to 100 parts by mass of the monomer component.

  In addition, redox polymerization initiators and the like based on a combination of a polymerization initiator and a reducing agent can be used alone or in combination of two or more. Examples of the reducing agent include ersorbic acid, sodium sorbate, potassium sorbate, ascorbic acid, sodium ascorbate, potassium ascorbate, saccharides, longgarite (sodium formaldehyde sulfoxylate), sodium bisulfite, potassium bisulfite, sulfite. Sulfites such as sodium and potassium sulfite, sodium pyrosulfite, potassium pyrosulfite, sodium pyrosulfite, pyrosulfite such as potassium pyrosulfite, sodium thiosulfate, potassium thiosulfate, phosphorous acid, sodium phosphite, potassium phosphite , Phosphites such as sodium hydrogen phosphite and potassium hydrogen phosphite, pyrophosphorous acid such as pyrophosphorous acid, sodium pyrophosphite, potassium pyrophosphite, sodium hydrogen phosphite, potassium hydrogen phosphite , Mention may be made of a mercaptan. It is preferable to use 0.01 to 10 parts by mass of these reducing agents with respect to 100 parts by mass of the monomer component.

  In addition, as a specific method for adding an initiator and a reducing agent, for example, a method of adding both into a polymerization reactor simultaneously and continuously from separate supply pipes, a polymerization in which the initiator is present in excess of the reducing agent. Examples thereof include a method of continuously adding a reducing agent into the system and a method of continuously adding an initiator into a polymerization system in which the reducing agent is present in excess of the initiator. The equivalence ratio between the initiator and the reducing agent is preferably 100/1 to 1/100. In addition to the initiator and the reducing agent, an oxidation-reduction catalyst can be further added to the polymerization system to perform emulsion polymerization.

  In emulsion polymerization of the monomer component, a polymerization chain transfer agent, a chelating agent, an inorganic electrolyte, or the like can be used as necessary. Examples of the polymerization chain transfer agent include mercaptans such as octyl mercaptan, n-dodecyl mercaptan, t-dodecyl mercaptan, n-hexadecyl mercaptan, n-tetradecyl mercaptan, t-tetradecyl mercaptan; dimethylxanthogen disulfide, diethylxanthogen Xanthogen disulfides such as disulfide and diisopropylxanthogen disulfide; thiuram disulfides such as tetramethylthiuram disulfide, tetraethylthiuram disulfide and tetrabutylthiuram disulfide; halogenated hydrocarbons such as chloroform, carbon tetrachloride and ethylene bromide; pentaphenylethane , Hydrocarbons such as α-methylstyrene dimer; acrolein, methacrolein, allyl alcohol, 2-ethyl Carboxylate thioglycolate, terpinolene, alpha-terpinene, .gamma.-terpinene, it can be mentioned dipentene and the like. These polymerization chain transfer agents can be used alone or in combination of two or more. Of these polymerization chain transfer agents, mercaptans, xanthogen disulfides, thiuram disulfides, carbon tetrachloride, α-methylstyrene dimer, and the like can be preferably used.

  Examples of the chelating agent include ethylenediaminetetraacetic acid, nitrilotriacetic acid, diethylenetriaminepentaacetic acid, and hydroxyethylethylenediaminetriacetic acid. Examples of the inorganic electrolyte include sodium carbonate, sodium hydrogen carbonate, potassium carbonate, potassium hydrogen carbonate, ammonium carbonate, sodium sulfate, potassium sulfate, and ammonium sulfate.

  Examples of the polymerization method include a one-step polymerization method, a method in which a part of the monomer is polymerized, and then the remainder is continuously or intermittently added, or a method in which the monomer is continuously added from the beginning of the polymerization. However, it is not particularly limited, and any polymerization method may be used. The temperature in the reaction vessel is preferably polymerized within a range of 5 to 100 ° C, more preferably polymerized within a range of 20 to 90 ° C, and particularly preferably polymerized within a range of 30 to 85 ° C. preferable. The component (A) obtained by polymerization at a temperature within this range has a good balance between slurry viscosity stability and adhesion, and has a small amount of residual chain transfer agent and a low odor.

  There is no restriction | limiting in particular in the particle diameter of (A) component contained in the binder composition for secondary battery electrodes of this embodiment. However, it is preferably 30 to 300 nm at the stage after the polymerization and before adding the pH adjuster. If it is less than 30 nm, the polymerization stability tends to be inferior. On the other hand, when it exceeds 300 nm, the adhesion tends to be lowered. (A) The particle diameter of a component can be adjusted by adjusting the usage-amounts, such as an emulsifier at the time of superposition | polymerization, water, an initiator.

  The glass transition temperature (Tg) of the component (A) contained in the binder composition for a secondary battery electrode of the present embodiment is preferably −60 to 20 ° C., and further preferably −40 to 10 ° C. preferable. When the glass transition temperature of the component (A) is less than −60 ° C., the dispersion stability tends to be inferior. On the other hand, when it exceeds 20 ° C., the adhesion tends to be inferior. The glass transition temperature of the component (A) can be adjusted by adjusting the composition ratio of the monomer components.

  The solid content concentration of the binder composition for a secondary battery electrode of the present embodiment is not particularly limited, but is preferably 10 to 65% by mass, and more preferably 20 to 65% by mass.

(Slurry for secondary battery electrode)
Next, an embodiment of the slurry for secondary battery electrodes of the present invention will be described. The slurry for secondary battery electrodes of this embodiment contains any of the binder compositions for secondary battery electrodes described so far and an electrode active material. In addition, the slurry for secondary battery electrodes of the present embodiment is obtained by mixing the binder composition for secondary battery electrodes and the electrode active material together with various additives added as necessary in an aqueous medium. Can be prepared.

  The secondary battery electrode slurry of the present embodiment preferably contains 0.1 to 10 parts by mass of the secondary battery electrode binder as a solid content with respect to 100 parts by mass of the electrode active material. More preferably, the content is 2 to 5 parts by mass, and particularly preferably 0.3 to 4 parts by mass. When the amount of the secondary battery electrode binder is less than 0.1 parts by mass, good adhesion tends to be not obtained. On the other hand, if it exceeds 10 parts by mass, the overvoltage tends to increase and affect the battery characteristics. In addition, various kneaders, bead mills, high-pressure homogenizers, etc. can be used for mixing the binder composition for secondary battery electrodes and the electrode active material.

  As various additives added to the secondary battery electrode slurry of the present embodiment as necessary, a water-soluble thickener, conductive carbon such as graphite, conductive material such as metal powder, etc. may be added. it can. Examples of the water-soluble thickener include carboxymethyl cellulose, methyl cellulose, hydroxymethyl cellulose, ethyl cellulose, polyvinyl alcohol, polyacrylic acid (salt), oxidized starch, phosphorylated starch, and casein.

As the electrode active material contained in the slurry for the secondary battery electrode of the present embodiment, a hydrogen storage alloy powder is preferably used in an aqueous battery, for example, a nickel metal hydride battery. More specifically, a material obtained by substituting a part of Ni with an element such as Mn, Al, Co or the like based on MmNi ₅ is preferably used. “Mm” represents misch metal which is a mixture of rare earth elements. The electrode active material is preferably a powder having a particle diameter of 3 to 400 μm and having passed through 100 mesh. In a non-aqueous battery, for example, MnO ₂ , MoO ₃ , V ₂ O ₅ , V ₆ O ₁₃ , Fe ₂ O ₃ , Fe ₃ O ₄ , Li _(1-x) CoO ₂ , Li _{(1-x ) · NiO 2, Li x Co} y Sn z O 2, Li (1-x) Co (1-y) Ni y O 2, TiS 2, TiS 3, MoS 3, FeS 2, CuF 2, NiF 2 , etc. Inorganic compounds: Carbon materials such as carbon fluoride, graphite, vapor-grown carbon fiber and / or pulverized product thereof, PAN-based carbon fiber and / or pulverized product thereof, pitch-based carbon fiber and / or pulverized product thereof; polyacetylene, poly Examples thereof include conductive polymers such as -p-phenylene. In _{particular, Li (1-x) CoO} 2, Li (1-x) NiO 2, Li x Co y Sn z O 2, Li (1-x) Co (1-y) Li-ion containing such Ni _y O ₂ When a composite oxide is used, it is preferable because both positive and negative electrodes can be assembled in a discharged state.

  Examples of the negative electrode active material include carbon fluoride, graphite, vapor-grown carbon fiber and / or pulverized product thereof, PAN-based carbon fiber and / or pulverized product thereof, pitch-based carbon fiber and / or pulverized product thereof, and the like. Preferable examples include carbon materials, conductive polymers such as polyacetylene and poly-p-phenylene, and amorphous compounds composed of compounds such as tin oxide and fluorine. In particular, when a graphite material such as natural graphite, artificial graphite, or graphitized mesophase carbon having a high graphitization degree is used, a battery having good charge / discharge cycle characteristics and high capacity can be obtained. In addition, when a carbonaceous material is used as the negative electrode active material, the average particle size of the carbonaceous material is reduced current efficiency, reduced slurry stability, increased interparticle resistance in the resulting electrode coating film, etc. Is preferably 0.1 to 50 μm, more preferably 1 to 45 μm, and particularly preferably 3 to 40 μm.

(Secondary battery electrode)
Next, an embodiment of the secondary battery electrode of the present invention will be described. The secondary battery electrode of the present embodiment includes a current collector and an electrode layer formed by applying and drying the above-described secondary battery electrode slurry on the surface of the current collector.

  Examples of the current collector include water-based batteries such as Ni mesh, Ni-plated punching metal, expanded metal, wire mesh, foam metal, and reticulated metal fiber sintered body. Moreover, in a non-aqueous battery, members, such as aluminum foil and copper foil, can be mentioned as a suitable example, for example. If the electrode layer is formed by applying the above-mentioned slurry for a secondary battery electrode to a predetermined thickness on at least one surface of the current collector, followed by heating and drying, the secondary of the present embodiment A battery electrode can be obtained. As a method for applying the slurry for the secondary battery electrode on the surface of the current collector, a method using an arbitrary coater head such as a reverse roll method, a comma bar method, a gravure method, or an air knife method can be employed.

  Moreover, as a method of heating and drying the slurry for the secondary battery electrode applied on the surface of the current collector, for example, in addition to the method of naturally drying by leaving, air blow dryer, hot air dryer, infrared heater, Alternatively, a drying method using a far-infrared heater or the like can be employed. The drying temperature is usually preferably 20 to 250 ° C, more preferably 130 to 170 ° C. The drying time is preferably 1 to 120 minutes, more preferably 5 to 60 minutes.

  The secondary battery electrode of the present embodiment can be suitably used as an electrode for any one of an aqueous battery and a non-aqueous battery. A nickel-hydrogen battery negative electrode can be used as an aqueous battery, and an alkaline secondary battery negative electrode or a lithium ion battery negative electrode can be used as a non-aqueous battery.

When a battery is assembled using the secondary battery electrode of the present embodiment, as the non-aqueous electrolyte solution, one in which an electrolyte is dissolved in a non-aqueous solvent is usually used. No particular limitation is imposed on the electrolyte, To illustrate in an alkaline secondary _{battery, LiClO 4, LiBF 4, LiAsF} 6, CF 3 SO 3 Li, LiPF 6, LiI, LiAlCl 4, NaClO 4, NaBF 4, NaI, (N-Bu) ₄ NClO ₄ , (n-Bu) ₄ NBF ₄ , KPF _{6 and the} like can be mentioned.

  Examples of the solvent used in the electrolytic solution include ethers, ketones, lactones, nitriles, amines, amides, sulfur compounds, chlorinated hydrocarbons, esters, carbonates, nitro compounds, and phosphoric acid. An ester compound, a sulfolane compound, or the like can be used. Among these, ethers, ketones, nitriles, chlorinated hydrocarbons, carbonates, and sulfolane compounds are preferable. Specifically, tetrahydrofuran, 2-methyltetrahydrofuran, 1,4-dioxane, anisole, monoglyme, diglyme, triglyme, acetonitrile, propionitrile, 4-methyl-2-pentanone, butyronitrile, valeronitrile, benzonitrile, 1, 2-dichloroethane, γ-butyrolactone, dimethoxyethane, methyl formate, propylene carbonate, ethylene carbonate, dimethylformamide, dimethyl sulfoxide, dimethylthioformamide, sulfolane, 3-methyl-sulfolane, trimethyl phosphate, or triethyl phosphate, or These mixed solvents can be mentioned. As an electrolytic solution for an aqueous battery, a 5N or higher potassium hydroxide aqueous solution is usually used.

  Furthermore, if necessary, a battery is configured using components such as a separator, a terminal, and an insulating plate. Further, the structure of the battery is not particularly limited, but the positive electrode, the negative electrode, and, if necessary, a paper type battery in which the separator is a single layer or multiple layers, or the positive electrode, the negative electrode, and if necessary, the separator is rolled. Examples thereof include a cylindrical battery wound in a shape. The secondary battery manufactured using the secondary battery electrode of the present embodiment can be suitably used for, for example, AV equipment, OA equipment, communication equipment, and the like.

  EXAMPLES Hereinafter, although this invention is demonstrated concretely based on an Example, this invention is not limited to these Examples. In the examples and comparative examples, “parts” and “%” are based on mass unless otherwise specified. Moreover, the measuring method of various physical-property values and the evaluation method of various characteristics are shown below.

  [Peel Strength]: A test piece having a width of 3 cm and a length of 8 cm was cut out from the battery electrode (negative electrode), and the current collector (copper foil) side was attached to an aluminum plate with a double-sided tape. When a 18 mm wide tape (trade name “Cerotape (registered trademark)” (manufactured by Nichiban)) (specified in JIS Z1522) is applied to the surface of the test piece, and the tape is peeled off at a speed of 10 mm / min in the 90 ° direction. The strength (g / cm) was measured 5 times, and the average value was calculated as the peel strength (g / cm). In addition, it can be evaluated that the larger the peel strength value, the higher the adhesion strength between the current collector and the electrode layer, and the more difficult the electrode layer peels from the current collector.

[Capacity Preservation Rate] For the prepared bipolar coin cell, charging and discharging were repeated 400 times in a 25 ° C. atmosphere and charged to 4 V by a constant current method of 0.2 C and then discharged to 3 V. The discharge capacity (mAh / g (discharge capacity per 1 g of active material)) at the fifth cycle and the discharge capacity (mAh / g) at the 400th cycle are measured, and the capacity storage rate (%) is calculated from the following formula (2). did.
Capacity storage rate (%) = {(discharge capacity at 400th cycle) / (discharge capacity at 5th cycle)} × 100 (2)

[Charge / Discharge Cycle Characteristics]: With respect to the prepared bipolar coin cell, charging / discharging to 3 V at 10 mA after charging to 4 V by a constant current method of 0.2 C in an atmosphere of 65 ° C. and −10 ° C. Repeated. The discharge capacity (mAh / g) at the 5th cycle and the discharge capacity (mAh / g) at the 50th cycle were measured, and charge / discharge cycle characteristics (%) were calculated from the following formula (3). In addition, it can be evaluated that it is a favorable result, so that the value of charging / discharging cycling characteristics is so large that there is little decrease in the discharge capacity in each test temperature. The discharge capacity at the fifth cycle at each test temperature was defined as the initial discharge capacity (mAh / g). It can be evaluated that the larger the value of the initial discharge capacity, the larger the discharge capacity at each test temperature.
Charging / discharging cycle characteristics (%) = {(discharge capacity at 50th cycle) / (discharge capacity at 5th cycle)} × 100 (3)

(Synthesis Example 1)
In an autoclave equipped with a stirrer and adjustable in temperature, 400 parts of water, 1 part of sodium dodecylbenzenesulfonate, 1 part of potassium persulfate, 0.5 part of α-methylstyrene dimer, 1 part of t-dodecyl mercaptan, 1 part , 3-butadiene 35 parts, styrene 27 parts, methyl methacrylate 35 parts, itaconic acid 1 part, and acrylic acid 2 parts were collectively charged and reacted at 60 ° C. for 12 hours. The polymerization conversion rate was 98%. After neutralizing to pH 7.5 with a 10% aqueous sodium hydroxide solution, the residual monomer was removed by steam distillation to obtain a polymer aqueous dispersion A1. The average particle diameter of the polymer aqueous dispersion A1 was 200 nm, the gel content was 80%, and Tg was −3 ° C.

(Synthesis Example 2)
In a separable flask equipped with a stirrer and capable of temperature adjustment, 400 parts of water, 0.5 part of reactive emulsifier (trade name “ADEKA rear soap SR-10” (manufactured by Asahi Denka Kogyo)), sodium persulfate 0 .3 parts, 50 parts of 2-ethylhexyl acrylate, 27 parts of styrene, 19 parts of methyl methacrylate, 2 parts of 2-hydroxyethyl methacrylate, and 2 parts of acrylic acid were collectively charged and reacted at 80 ° C. for 6 hours. The polymerization conversion rate was 99%. The mixture was neutralized with 10% aqueous sodium hydroxide solution to pH 7.5 to obtain a polymer aqueous dispersion A2. The average particle size of the polymer aqueous dispersion A2 was 150 nm, the gel content was 70%, and Tg was −3 ° C.

(PTFE water dispersion)
As an aqueous dispersion of polytetrafluoroethylene (abbreviation: PTFE), Polyflon PTFE D-1E (trade name, solid content 61%, manufactured by Daikin Industries, Ltd.) was used.

Example 1
100 parts of natural graphite (trade name “NC-C” (manufactured by Kansai Thermochemical Co., Ltd.)), 5 parts of conductive carbon (trade name “Denka Black” (manufactured by Asahi Denka Co., Ltd.)), carboxymethylcellulose (manufactured by Daicel Chemical Industries) 1 1 part of the polymer aqueous dispersion A1 as the component (A), and the trade name “Emulgen 1108” (manufactured by Kao Corporation) (cloud point: 66 ° C.) as the component (B) with respect to 100 parts by mass of the component (A) A uniform battery electrode slurry was prepared by using 5 parts by volume and adding ion-exchanged water and stirring so that the slurry solid content concentration was 45%. The prepared battery electrode slurry was uniformly coated on the surface of a copper foil having a thickness of 18 μm by a doctor blade method. After drying with a dryer at 120 ° C. for 15 minutes, it was further dried under reduced pressure at 5 mmHg and 150 ° C. for 2 hours with a vacuum dryer. After cooling to room temperature, it roll-pressed so that an active material density might be 1.7 g / cm < ³ >, and the battery electrode (negative electrode) was obtained. The peel strength of the obtained negative electrode was 108 g / cm.

100 parts of LiCoO _{2 having an} average particle size of 6 μm, 7.5 parts of graphite powder, and 2.5 parts of acetylene black were mixed to obtain a mixed powder, and an N-methylpyrrolidone solution of PVDF (concentration of 12) was added to the obtained mixed powder. %) Was added and mixed and stirred to prepare a coating solution. The prepared coating solution was uniformly applied by a doctor blade method on the surface of a commercially available aluminum foil having a thickness of 15 μm. After drying with a dryer at 150 ° C. for 20 minutes, it was further dried under reduced pressure at 5 mmHg and 180 ° C. for 5 hours with a vacuum dryer. After cooling to room temperature, it roll-pressed so that an active material density might be 3.1 g / cm < ³ >, and the battery electrode (positive electrode) was obtained.

A negative electrode punched out to a diameter of 16.16 mm was put into a two-pole coin cell (trade name “HS Flat Cell” (manufactured by Hosen Co., Ltd.)) with the electrode layer surface facing upward. Next, a separator (trade name “Celguard # 2400” (manufactured by Celgard)) made of a polypropylene porous film punched to a diameter of 18 mm was placed, and an electrolyte was injected so that air did not enter. Thereafter, a positive electrode punched out to 15.95 mm was placed, and the outer body was closed with a screw and sealed to produce a secondary battery. The electrolytic solution used was a solution in which LiPF ₆ was dissolved at a concentration of 1 mol / liter in a solvent of ethylene carbonate / ethyl methyl carbonate = 1/2. The produced secondary battery had an initial discharge capacity of 341 mAh / g at 65 ° C. and a charge / discharge cycle characteristic of 82%. The initial discharge capacity at −10 ° C. was 334 mAh / g, and the charge / discharge cycle characteristics were 81%. Furthermore, the capacity retention at room temperature (25 ° C.) was 95%.

(Examples 2-5, Comparative Examples 1-5)
A battery electrode slurry was prepared in the same manner as in Example 1 except that the formulation shown in Table 1 was used. Moreover, the negative electrode and the positive electrode were obtained in the same manner as in Example 1 described above. Table 1 shows the peel strength of the obtained negative electrode. Further, a secondary battery was produced in the same manner as in Example 1 described above. Table 1 shows various physical property values of the fabricated secondary battery. In Table 1, “Emulgen 1108 (cloud point: 66 ° C.)” and “Emulgen 109P (cloud point: 83 ° C.)” are trade names of polyoxyethylene alkyl ether (manufactured by Kao Corporation), “Adeka Pluronic L-62”. (Cloud point: 32 ° C.) ”is a trade name of polyoxyethylene-polyoxypropylene condensate (manufactured by Asahi Denka Co., Ltd.). “Adecatol LB-83 (cloud point: 54 ° C.)” is a trade name of polyoxyethylene-polyoxypropylene alkyl ether (manufactured by Asahi Denka Co., Ltd.). “Poly N-isopropylacrylamide (cloud point: 32 ° C.)” is disclosed in J. Org. Macromol. Sci. Chem. , A2, 1441 (1968).

  As shown in Table 1, when the binder composition for secondary battery electrodes of Examples 1 to 5 and the slurry for secondary battery electrodes were used, the binder composition for secondary battery electrodes of Comparative Examples 1 to 5 Compared to the case of using a slurry for secondary battery electrodes, it is possible to produce an electrode having excellent adhesion between the current collector and the electrode layer, and charge / discharge cycle characteristics even under high and low temperature conditions. It is clear that it is possible to provide a secondary battery excellent in. Moreover, when the secondary battery electrode of Examples 1-5 is used, even if it is a high temperature and low temperature condition compared with the case where the secondary battery electrode of Comparative Examples 1-5 is used, it is a charge / discharge cycle characteristic. It is clear that it is possible to provide a secondary battery excellent in.

  If the binder composition for secondary battery electrodes of the present invention is used, a secondary battery excellent in charge / discharge cycle characteristics can be provided even under high temperature and low temperature conditions.

It is a schematic diagram which shows the measuring apparatus of a cloud point.

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 ... Heater, 2 ... Thermometer, 3 ... Stirrer blade, 4 ... Measuring apparatus, 5 ... Container, 6 ... Aqueous solution.

Claims (5)

(A) 100 parts by mass (but as a solid content) of at least one polymer aqueous dispersion selected from the group consisting of a styrene-butadiene copolymer latex and an acrylic emulsion;
(B) at least one non-selective material selected from the group consisting of polyoxyethylene alkyl ether derivatives, polyoxyethylene-polyoxypropylene condensates, and polyoxyethylene-polyoxypropylene alkyl ether derivatives having a cloud point of 70 ° C. or lower. The binder composition for secondary battery negative electrodes containing 1-20 mass parts of ionic surfactants . (A) 100 parts by mass (but as a solid content) of at least one polymer aqueous dispersion selected from the group consisting of a styrene-butadiene copolymer latex and an acrylic emulsion;
(B) The binder composition for secondary battery negative electrodes containing 1-20 mass parts of poly N-isopropylacrylamide whose cloud point is 70 degrees C or less. The slurry for secondary battery negative electrodes containing the binder composition for secondary battery negative electrodes of Claim 1 or Claim 2 , and an electrode active material. Wherein the electrode active material 100 parts by weight, the secondary battery negative Kyokuyo binder 0.1 to 10 parts by weight (as where solids) containing a secondary battery negative electrode slurry according to claim 3. Power collector and, claim 3 or secondary battery negative electrode, comprising: a secondary battery negative electrode slurry is coated and dried electrode layer formed, a according to claim 4 on a surface of the current collector.