JP5034223B2 - Substrate to which a paper label is attached - Google Patents
Substrate to which a paper label is attached Download PDFInfo
- Publication number
- JP5034223B2 JP5034223B2 JP2005333831A JP2005333831A JP5034223B2 JP 5034223 B2 JP5034223 B2 JP 5034223B2 JP 2005333831 A JP2005333831 A JP 2005333831A JP 2005333831 A JP2005333831 A JP 2005333831A JP 5034223 B2 JP5034223 B2 JP 5034223B2
- Authority
- JP
- Japan
- Prior art keywords
- paper
- layer
- paper label
- adherend
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は紙ラベルが貼り付けられているプラスチックボトル、ガラスボトル等の被着体に関するものである。
The present invention relates to an adherend such as a plastic bottle or a glass bottle to which a paper label is attached .
食品や非食品などの各種内容物を充填密封したポリエステルボトル等のプラスチックボトルあるいはガラスボトルには、意匠性を向上させ、販売促進を図る等の目的で絵柄などを印刷した各種ラベルが多く装着されている。前記各種ラベルとしては、基材がプラスチックフィルムのものや紙のものが多く使用されている。近年、循環型社会構築の為に、充填された中身が無くなった後に廃棄されたガラスボトルやポリエステルボトルは再利用される場合が多く、その場合表面に装着されているラベルは表面から引き剥がす必要がある。シュリンクラベルの場合は一部を手でカットして引き剥がすことができるが、紙ラベルの場合はボトル表面に種々の接着層を介して接着されているので簡単に引き剥がすことが難しい。紙ラベルとして種々のものが提案されている（例えば、特許文献１参照。）
しかしながら、前記提案されている紙ラベルは、被着体に貼りつけた後に簡単に引き剥がすことが困難であった。 However, it has been difficult to easily peel off the proposed paper label after being attached to an adherend.
本発明の課題は、被着体に貼りつけられた後、保管時や輸送段階で剥がれることがなく、引き剥がす時は紙剥けしないで容易に剥離できる紙ラベルが貼り付けられている被着体を提供することにある。
The problem of the present invention is that the adherend is attached to the adherend, and is not peeled off during storage or transportation, and when peeled off, the adherend is attached with a paper label that can be easily peeled off without peeling off the paper. Is to provide.
本発明の請求項１に係る発明は、少なくとも、紙からなる基材層の一方の面に材料がポリプロピレンフィルムまたは高密度ポリエチレンからなる紙剥け防止層、感熱接着層を積層した積層材料からなる紙ラベルが貼り付けられている被着体において、
前記基材層の紙の層間強度Ａ（Ｎ／ｍｍ）、前記紙剥け防止層の材料の引張強さＤ（Ｎ／ｍｍ）、前記感熱接着層の材料の凝集剥離強度Ｂ（Ｎ／ｍｍ）、該感熱接着層の材料の前記被着体への接着強度Ｃ（Ｎ／ｍｍ）とすると、該紙剥け防止層が、
Ｄ＞Ａ、Ｂ、Ｃ
を満たす材料からなり、該感熱接着層が
Ｂ＞Ｃ
を満たす材料からなり、
且つ、Ｄが１Ｎ／ｍｍ以上で、Ａが０．１Ｎ／ｍｍ未満であることを特徴とする紙ラベルが貼り付けられている被着体である。
The invention according to
Interlayer strength A (N / mm) of the paper of the base material layer, tensile strength D (N / mm) of the material of the paper peeling prevention layer, cohesive peel strength B (N / mm) of the material of the heat-sensitive adhesive layer When the adhesive strength C (N / mm) of the heat-sensitive adhesive layer material to the adherend is determined, the paper peeling prevention layer is
D> A, B, C
And the heat-sensitive adhesive layer is B> C
Made of materials that satisfy
And it is the adherend to which the paper label characterized by D being 1 N / mm or more and A being less than 0.1 N / mm is affixed.
本発明の紙ラベルが貼り付けられている被着体は、少なくとも、紙からなる基材層の一方の面に材料がポリプロピレンフィルムまたは高密度ポリエチレンからなる紙剥け防止層、感熱接着層を積層した積層材料からなる紙ラベルが貼り付けられている被着体において、
基材層の紙の層間強度Ａ（Ｎ／ｍｍ）、紙剥け防止層の材料の引張強さＤ（Ｎ／ｍｍ）、感熱接着層の材料の凝集剥離強度Ｂ（Ｎ／ｍｍ）、感熱接着層の材料の被着体への接着強度Ｃ（Ｎ／ｍｍ）とすると、該紙剥け防止層が、
Ｄ＞Ａ、Ｂ、Ｃ
を満たす材料からなり、該感熱接着層が
Ｂ＞Ｃ
を満たす材料からなり、
且つ、Ｄが１Ｎ／ｍｍ以上で、Ａが０．１Ｎ／ｍｍ未満であるので、被着体から、保管時や輸送段階で紙ラベルが剥がれ落ちることがなく、引き剥がす時は紙剥けしないで容易に引き剥がすことができる。
The adherend to which the paper label of the present invention is affixed is formed by laminating at least one surface of a base material layer made of paper with a paper peeling prevention layer and a heat-sensitive adhesive layer made of a polypropylene film or high-density polyethylene . In an adherend to which a paper label made of a laminated material is attached ,
Interlayer strength A (N / mm) of the paper of the base material layer, tensile strength D (N / mm) of the material of the paper peeling prevention layer, cohesive peel strength B (N / mm) of the material of the heat-sensitive adhesive layer, heat-sensitive adhesion When the adhesive strength C (N / mm) of the material of the layer to the adherend is used,
D> A, B, C
And the heat-sensitive adhesive layer is B> C
Ri Do from a material that meets the,
In addition, since D is 1 N / mm or more and A is less than 0.1 N / mm , the paper label does not peel off from the adherend during storage or transportation, and do not peel off when peeling off. It can be easily peeled off.
本発明の紙ラベルが貼り付けられている被着体に用いる紙ラベルを、実施の形態に沿って以下に詳細に説明する。図２（ａ）は本発明に用いる紙ラベルに使用する積層材料の一
実施形態を示す側断面図であり、積層材料（１０）は厚み方向に順に、印刷層（１５）、基材層（１１）、接着剤層（１４）、紙剥け防止層（１２）、感熱接着層（１３）が積層された構成であり、（ｂ）は積層材料の他の実施形態を示す側断面図であり、積層材料（１０′）は厚み方向に順に、印刷層（１５）、基材層（１１）、紙剥け防止層（１２）、感熱接着層（１３）が積層された構成である。
The paper label used for the adherend to which the paper label of the present invention is affixed will be described in detail below along the embodiments. Fig.2 (a) is a sectional side view which shows one Embodiment of the laminated material used for the paper label used for this invention, a laminated material (10) is a printing layer (15) and a base material layer (in order of thickness direction) in order. 11), an adhesive layer (14), a paper peeling prevention layer (12), and a heat-sensitive adhesive layer (13) are laminated, and (b) is a side sectional view showing another embodiment of a laminated material. The laminated material (10 ′) has a structure in which a printing layer (15), a base material layer (11), a paper peeling prevention layer (12), and a heat-sensitive adhesive layer (13) are laminated in order in the thickness direction.
以下、基材層（１１）に使用する紙の層間強度Ａ（Ｎ／ｍｍ）、紙剥け防止層（１２）に使用する材料の引張強さＤ（Ｎ／ｍｍ）、感熱接着層（１３）に使用する材料の凝集剥離強度Ｂ（Ｎ／ｍｍ）、感熱接着層（１３）に使用する材料の被着体への接着強度Ｃ（Ｎ／ｍｍ）とする。 Hereinafter, the interlayer strength A (N / mm) of the paper used for the base material layer (11), the tensile strength D (N / mm) of the material used for the paper peeling prevention layer (12), and the heat-sensitive adhesive layer (13) The cohesive peel strength B (N / mm) of the material used for the heat treatment and the adhesive strength C (N / mm) of the material used for the heat-sensitive adhesive layer (13) to the adherend.
前記基材層（１１）は、坪量２０〜２００ｇ／ｍ2の紙又は前記紙にアルミニウムを蒸着したアルミニウム蒸着紙からなっており、使用される紙の種類としては、晒クラフト紙、未晒クラフト紙、アート紙、上質紙、純白ロール紙、模造紙などがあり、これらの紙の層間強度Ａはいずれも０．１Ｎ／ｍｍ未満である。 The base material layer (11) is made of paper having a basis weight of 20 to 200 g / m 2 or aluminum vapor-deposited paper obtained by vapor-depositing aluminum on the paper, and the type of paper used is bleached kraft paper, unbleached There are craft paper, art paper, high-quality paper, pure white roll paper, imitation paper, etc., and the interlayer strength A of these papers is less than 0.1 N / mm.
前記感熱接着層（１３）は、Ｂ〉Ｃを満たす材料からなっており、Ｂ〉Ｃを満たすことにより、被着体から引き剥がす時に使用されている材料が被着体表面に部分的に残らない特徴を有する。使用できる材料としては、ポリエチレン、ポリプロピレン、エチレン・メタクリル酸共重合体、エチレン・アクリル酸共重合体、エチレン・メチルアクリレート共重合体、アイオノマー、ポリアミド、ポリブタジエン、ポリエステルなどの熱可塑性樹脂、エチレン・酢酸ビニル共重合体樹脂又はポリアミド系樹脂とワックス類他の混合組成物からなるホットメルト剤、上記熱可塑性樹脂に各種添加剤を配合してなる感熱性粘着剤などがある。前記材料はいずれもその凝集剥離強度Ｂが被着体への接着強度Ｃより大きく、さらに加熱して可塑化した後の被着体表面への接着性が優れている。従って、紙ラベルを使用する時の高速ライン適性も良い。積層方法は使用する材料により、溶融押出コーティング法、ロールコート法、グラビアコート法などの方法を適宜選定し、部分コートあるいは全面コートして形成する。 The heat-sensitive adhesive layer (13) is made of a material satisfying B> C, and by satisfying B> C, the material used when being peeled off from the adherend partially remains on the adherend surface. Has no features. Usable materials include polyethylene, polypropylene, ethylene / methacrylic acid copolymer, ethylene / acrylic acid copolymer, ethylene / methyl acrylate copolymer, ionomer, polyamide, polybutadiene, polyester and other thermoplastic resins, ethylene / acetic acid Examples thereof include a hot melt agent composed of a vinyl copolymer resin or a polyamide-based resin and a mixture of waxes and the like, and a heat-sensitive adhesive obtained by blending various additives with the above thermoplastic resin. Each of the materials has a cohesive peel strength B greater than the adhesion strength C to the adherend, and is excellent in adhesion to the adherend surface after being plasticized by heating. Therefore, high-speed line suitability when using a paper label is also good. The lamination method is selected by appropriately selecting a melt extrusion coating method, a roll coating method, a gravure coating method or the like depending on the material to be used, and is formed by partial coating or entire surface coating.
前記紙剥け防止層（１２）は、Ｄ〉Ａ、Ｂ、Ｃを持たす材料からなっており、Ｄ〉Ａ、Ｂ、Ｃを満たすことにより、被着体から紙ラベルを引き剥がす時に基材層（１１）に使用した紙の層間剥離が起らないで、容易に引き剥がすことが可能になる。使用される材料としては、不織布、混抄紙、ポリオレフィン系樹脂単独、ポリエステル系樹脂単独、ポリアミド系樹脂単独、前記樹脂／接着性樹脂の２層樹脂、あるいは前記単独樹脂若しくは２層樹脂からなるフィルムなどがあり、前記材料はいずれもその引張強さＤは１Ｎ／ｍｍ以上を有している。厚みは５〜１００μｍが好ましい。 The paper peeling prevention layer (12) is made of a material having D> A, B, and C. When D> A, B, and C are satisfied, the base material layer is peeled off from the adherend. The paper used in (11) can be easily peeled off without delamination. Materials used include nonwoven fabric, mixed paper, polyolefin resin alone, polyester resin alone, polyamide resin alone, two-layer resin of the resin / adhesive resin, or a film made of the single resin or two-layer resin. Each of the materials has a tensile strength D of 1 N / mm or more. The thickness is preferably 5 to 100 μm.
前記接着剤層（１４）は、酢酸ビニル樹脂やエチレン・酢酸ビニル共重合体樹脂を主成分とする水性エマルジョン系接着剤、又はポリウレタン系接着剤からなっている。基材層（１１）と紙剥け防止層（１２）の積層方法は、水性エマルジョン系接着剤の場合は公知のウエットラミネーション法で実施し、ポリウレン系接着剤の場合は、公知のドライラミネーション法で実施する。 The adhesive layer (14) is made of a water-based emulsion adhesive or a polyurethane adhesive mainly composed of vinyl acetate resin or ethylene / vinyl acetate copolymer resin. The lamination method of the base material layer (11) and the paper peeling prevention layer (12) is carried out by a known wet lamination method in the case of an aqueous emulsion adhesive, and by a known dry lamination method in the case of a polyurene adhesive. carry out.
前記印刷層（１５）は、印刷インキ被膜からなっており、例えば、ポリアミド系樹脂と顔料及びその他添加剤が配合された印刷インキを用いて形成する。 The said printing layer (15) consists of a printing ink film, for example, is formed using the printing ink with which the polyamide-type resin, the pigment, and the other additive were mix | blended.
図１は本発明の紙ラベルが貼り付けられている被着体の一実施形態を示す平面図であり、紙ラベル（１）は四角形状のもので、表面には印刷層（１５）を有している。紙ラベルの形状は特に限定されず、四角形状の他に例えば、円形状、楕円形状などの各種形状のものがある。
FIG. 1 is a plan view showing an embodiment of an adherend to which a paper label of the present invention is attached . The paper label (1) has a rectangular shape and has a printed layer (15) on the surface. is doing. The shape of the paper label is not particularly limited, and there are various shapes such as a circular shape and an elliptical shape in addition to the rectangular shape.
図３（ａ）は本発明の紙ラベルが貼り付けられている被着体を示す説明図であり、ボトル形状の被着体（２）の表面に紙ラベル（１）が貼りつけられており、（ｂ）は紙ラベルを引き剥がす状態を示す説明図であり、ボトル形状の被着体（２）の表面に貼りつけられた紙ラベル（１）は応力（Ｐ）で周縁部分から容易に引き剥がすことができ、紙ラベル（１）が引き剥がれた後の被着体は再利用される。
3 (a) is an explanatory view showing the adherend paper label is attached to the present invention, a paper label (1) is adhered to the surface of the adherend (2) of the bottle shape (B) is explanatory drawing which shows the state which peels off a paper label, and the paper label (1) affixed on the surface of the bottle-shaped to-be-adhered body (2) is easily from a peripheral part with stress (P). The adherend after the paper label (1) has been peeled off can be reused.
本発明に用いる紙ラベルを、以下に具体的な実施例に従って説明するが、本発明がこれらの実施例に限定されるものではない。
The paper labels used in the present invention are described below according to specific examples, but the present invention is not limited to these examples.
基材層（１１）として、坪量８４．９ｇ／ｍ２で、層間強度Ａが０．０４Ｎ／ｍｍの片アート紙を使用し、接着剤層（１４）の接着剤として、酢酸ビニル系エマルジョン接着剤を使用し、紙剥け防止層（１２）として、厚さ２０μｍで、引張強さＤが１．３Ｎ／ｍｍの二軸延伸ポリプロピレンフィルム（ＯＰＰフィルム）を使用し、感熱接着層（１３）の形成剤として、エチレン・酢酸ビニル共重合体樹脂（酢酸ビニル含有率、２０重量％）／水添ロジン＝８０／２０（重量％比率）の配合割合の混合樹脂をトルエンで溶解した総固
形分３０重量％の塗布剤を使用し、印刷層（１５）のインキとして、ポリアミド樹脂系印刷インキを使用して、印刷層／片アート紙／酢酸ビニル系接着剤（５ｇ／ｍ２、乾燥状態）／ＯＰＰフィルム（２０μｍ）／混合樹脂（１０ｇ／ｍ２、乾燥状態）の構成の積層材料を作成した。その積層材料を用いて７０ｍｍ×５０ｍｍの大きさに打ち抜いて、本発明に用いる紙ラベルを得た。
A piece of art paper having a basis weight of 84.9 g / m 2 and an interlayer strength A of 0.04 N / mm is used as the base material layer (11), and a vinyl acetate emulsion is used as the adhesive of the adhesive layer (14). A biaxially stretched polypropylene film (OPP film) having a thickness of 20 μm and a tensile strength D of 1.3 N / mm is used as the paper peeling prevention layer (12) using an adhesive, and a heat-sensitive adhesive layer (13). As a forming agent, ethylene / vinyl acetate copolymer resin (vinyl acetate content, 20% by weight) / hydrogenated rosin = 80/20 (% by weight) is a total solid content obtained by dissolving a mixed resin in toluene. Using 30% by weight coating agent, using polyamide resin printing ink as printing layer (15) ink, printing layer / single art paper / vinyl acetate adhesive (5 g / m 2 , dry state) / OPP film (20μm ) / Mixed resin (10 g / m 2 , dry state). The laminated material was punched into a size of 70 mm × 50 mm to obtain a paper label used in the present invention.
基材層（１１）として、坪量８４．９ｇ／ｍ２で、層間強度Ａが０．０４Ｎ／ｍｍの片アート紙を使用し、接着剤層（１４）として、ポリウレタン系接着剤を使用し、紙剥け防止層（１２）として、厚さ２０μｍで、引張強さＤが１．３Ｎ／ｍｍの二軸延伸ポリプロピレンフィルム（ＯＰＰフィルム）を使用し、感熱接着層（１３）として、エチレン・メタクリル酸共重合体（ＥＭＡＡ）樹脂を使用し、印刷層（１５）のインキとして、ポリアミド樹脂系印刷インキを使用して、印刷層／片アート紙／ポリウレタン系接着剤（５ｇ／ｍ２、乾燥状態）／ＯＰＰフィルム（２０μｍ）／オゾン処理ＥＭＡＡ樹脂（２０μｍ）の構成の積層材料を作成した。その積層材料を用いて７０ｍｍ×５０ｍｍの大きさに打ち抜いて、本発明に用いる紙ラベルを得た。
A piece of art paper having a basis weight of 84.9 g / m 2 and an interlayer strength A of 0.04 N / mm is used as the base material layer (11), and a polyurethane adhesive is used as the adhesive layer (14). A biaxially oriented polypropylene film (OPP film) having a thickness of 20 μm and a tensile strength D of 1.3 N / mm was used as the paper peeling prevention layer (12), and ethylene / methacrylic was used as the heat-sensitive adhesive layer (13). Using acid copolymer (EMAA) resin, and using polyamide resin printing ink as printing layer (15) ink, printing layer / single art paper / polyurethane adhesive (5 g / m 2 , dry state) ) / OPP film (20 μm) / ozone-treated EMAA resin (20 μm). The laminated material was punched into a size of 70 mm × 50 mm to obtain a paper label used in the present invention.
基材層（１１）として、坪量８４．９ｇ／ｍ２で、層間強度Ａが０．０４Ｎ／ｍｍの片アート紙を使用し、印刷層（１５）のインキとして、ポリアミド樹脂系印刷インキを使用し、紙剥け防止層（１２）の樹脂として、引張強さＤが１．４Ｎ／ｍｍの高密度ポリエチレン樹脂を使用し、感熱接着層（１３）の樹脂として、接着性ポリオレフィン樹脂（三井化学（株）、商品名：アドマー樹脂）とエチレン・メタクリル酸共重合体（ＥＭＡＡ）樹脂の２種類の樹脂を使用して、それぞれ印刷機及び多層共押出コーテング機を用いて、印刷層／片アート紙／高密度ポリエチレン樹脂（１５μｍ）／アドマー樹脂（３μｍ）／ＥＭＡＡ樹脂（２０μｍ）の構成の積層材料を作成した。その積層材料を用いて７０ｍｍ×５０ｍｍの大きさに打ち抜いて、本発明に用いる紙ラベルを得た。
As the base material layer (11), a piece of art paper having a basis weight of 84.9 g / m 2 and an interlayer strength A of 0.04 N / mm is used, and a polyamide resin printing ink is used as the printing layer (15) ink. Use a high-density polyethylene resin with a tensile strength D of 1.4 N / mm as the resin for the paper peeling prevention layer (12), and an adhesive polyolefin resin (Mitsui Chemicals) as the resin for the heat-sensitive adhesive layer (13). Co., Ltd., trade name: Admer Resin) and ethylene / methacrylic acid copolymer (EMAA) resin, respectively, using a printing machine and multilayer coextrusion coating machine, respectively. A laminated material having a structure of paper / high-density polyethylene resin (15 μm) / admer resin (3 μm) / EMAA resin (20 μm) was prepared. The laminated material was punched into a size of 70 mm × 50 mm to obtain a paper label used in the present invention.
以下に、本発明の比較用の実施例について説明する。 Hereinafter, comparative examples of the present invention will be described.
厚さ２０μｍの二軸延伸ポリプロピレンフィルム（ＯＰＰフィルム）を積層しなかった以外は、実施例１と同様にして比較用の積層材料を作成し、その積層材料を用いて７０ｍｍ×５０ｍｍの大きさに打ち抜いて、比較用に用いる紙ラベルを得た。
A comparative laminate material was prepared in the same manner as in Example 1 except that a 20 μm thick biaxially stretched polypropylene film (OPP film) was not laminated, and the laminate material was used to make a size of 70 mm × 50 mm. Punched out to obtain a paper label used for comparison.
＜評価＞
実施例１〜３の本発明に用いる紙ラベル及び実施例４の比較用に用いる紙ラベルを用いて、各紙ラベルの感熱接着層面に１２０℃の温風を０．５秒間、あるいは１５０℃の温風を０．５秒間あてて、可塑化し、内容量が２０００ｍｌのポリエステルボトルの表面に貼りつけた。貼りつけた後のそれぞれの紙ラベルの剥離性の良否、紙ラベル剥離時の紙剥けの有無及び紙ラベル剥離後の感熱接着層の材料のボトル表面への残りの有無を評価した。その結果を表１に示す。
<Evaluation>
Using the paper label used in the present invention in Examples 1 to 3 and the paper label used for comparison in Example 4, 120 ° C hot air was applied to the surface of the heat-sensitive adhesive layer of each paper label for 0.5 seconds or 150 ° C. The wind was applied for 0.5 seconds to plasticize, and affixed to the surface of a polyester bottle having an internal volume of 2000 ml. The peelability of each paper label after pasting was evaluated, whether or not the paper label was peeled off when the paper label was peeled off, and whether or not the material of the heat-sensitive adhesive layer after the paper label peeling was left on the bottle surface. The results are shown in Table 1.
１…紙ラベル
２…被着体
１０，１０′…積層材料
１１…基材層
１２…紙剥け防止層
１３…感熱接着層
１４…接着剤層
１５…印刷層
Ｐ…応力
DESCRIPTION OF
Claims (1)
前記基材層の紙の層間強度Ａ（Ｎ／ｍｍ）、前記紙剥け防止層の材料の引張強さＤ（Ｎ／ｍｍ）、前記感熱接着層の材料の凝集剥離強度Ｂ（Ｎ／ｍｍ）、該感熱接着層の材料の前記被着体への接着強度Ｃ（Ｎ／ｍｍ）とすると、該紙剥け防止層が、
Ｄ＞Ａ、Ｂ、Ｃ
を満たす材料からなり、該感熱接着層が
Ｂ＞Ｃ
を満たす材料からなり、
且つ、Ｄが１Ｎ／ｍｍ以上で、Ａが０．１Ｎ／ｍｍ未満であることを特徴とする紙ラベルが貼り付けられている被着体。 In an adherend in which a paper label made of a laminate material in which a material is made of a polypropylene film or high-density polyethylene and a heat-sensitive adhesive layer is laminated on at least one surface of a base material layer made of paper ,
Interlayer strength A (N / mm) of the paper of the base material layer, tensile strength D (N / mm) of the material of the paper peeling prevention layer, cohesive peel strength B (N / mm) of the material of the heat-sensitive adhesive layer When the adhesive strength C (N / mm) of the heat-sensitive adhesive layer material to the adherend is determined, the paper peeling prevention layer is
D> A, B, C
And the heat-sensitive adhesive layer is B> C
Made of materials that satisfy
An adherend to which a paper label is attached, wherein D is 1 N / mm or more and A is less than 0.1 N / mm.