JP2003237816A - Lid material - Google Patents

Lid material

Info

Publication number
JP2003237816A
JP2003237816A JP2002041101A JP2002041101A JP2003237816A JP 2003237816 A JP2003237816 A JP 2003237816A JP 2002041101 A JP2002041101 A JP 2002041101A JP 2002041101 A JP2002041101 A JP 2002041101A JP 2003237816 A JP2003237816 A JP 2003237816A
Authority
JP
Japan
Prior art keywords
layer
paper
heat
lid
lid material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2002041101A
Other languages
Japanese (ja)
Inventor
Hiroshi Takahashi
拓 高橋
Yasuharu Sugiyama
康晴 杉山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP2002041101A priority Critical patent/JP2003237816A/en
Publication of JP2003237816A publication Critical patent/JP2003237816A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a lid material of adequate heat sealability without using any aluminum foil, and excellent easy unsealability, dead-hold property and flatness without generating any uneven projections, stringiness or paper-peel when a lid is unsealed, and to provide a packaged product of excellent touch to the mouth when a consumer eats/drinks the content. <P>SOLUTION: The lid material is formed of a laminate consisting of at least a base layer formed of a paper layer, an intermediate layer and a heat-seal layer, and the thickness of the heat-seal layer is ≥3 μm to <20 μm. <P>COPYRIGHT: (C)2003,JPO

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【発明の属する技術分野】本発明は、紙製、合成樹脂製
等の各種のカップ状容器の開口部を密閉するために使用
する蓋材に関するものである。さらに詳しくは、アルミ
ニウム箔を含まない構成の易開封性包装材料からなる蓋
材に関するものである。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lid member used to seal the opening of various cup-shaped containers made of paper, synthetic resin or the like. More specifically, the present invention relates to a lid material made of an easily openable packaging material that does not contain aluminum foil.

【0002】[0002]

【従来技術】従来、即席ラーメン麺、ソバ、菓子等を充
填包装する紙製あるいは合成樹脂製のカップの開口部を
密閉する蓋材としては、種々のものが知られているが、
現在、印刷層、紙層、ポリエチレン層、アルミニウム箔
層、ポリエチレン層、ホットメルト層を順に積層してな
る蓋材が、最も多く使用されている。
2. Description of the Related Art Conventionally, various lid materials for sealing the opening of a cup made of paper or synthetic resin for filling and packaging instant ramen noodles, buckwheat, confectionery, etc. have been known.
At present, a lid material formed by laminating a printing layer, a paper layer, a polyethylene layer, an aluminum foil layer, a polyethylene layer, and a hot melt layer in order is most often used.

【0003】従来、上記のような蓋材において、アルミ
ニウム箔は、カップ内にお湯を注ぐ時に容器の蓋を一部
開口して起立し、その後は再密閉できるように、蓋材に
折癖を保持するために使用されるものである。すなは
ち、アルミニウム箔をラミネートした蓋材は、蓋を起こ
して開けた場合でも、そのままの起こした状態が保持さ
れ開封したままの状態を維持させる性質(以下、「デッ
ドホールド性」という。)を有するものである。また、
アルミニウム箔をラミネートした蓋材は、カール性を生
じにくい性質(以下「フラット性」という。)も有す
る。このため、アルミニウム箔をラミネートした蓋材
は、特に枚葉の蓋材として容器にヒートシールする際、
自動供給などの作業性が良いものである。
Conventionally, in the lid material as described above, the aluminum foil has a crease in the lid material so that when the hot water is poured into the cup, the lid of the container is partially opened to stand up and then can be resealed. It is used to hold. That is, the lid material laminated with the aluminum foil has a property of keeping the raised state and maintaining the opened state even when the lid is raised and opened (hereinafter referred to as “dead hold property”). Is to have. Also,
The lid material laminated with the aluminum foil also has a property of not easily curling (hereinafter referred to as “flatness”). For this reason, the lid material laminated with aluminum foil, especially when heat-sealed into a container as a single-wafer lid material,
It has good workability such as automatic supply.

【0004】[0004]

【発明が解決しようとする課題】しかしながら、近年、
アルミニウム箔は、包装材料の環境問題から環境破壊の
元凶の一つであるとされ、その使用が避けられているも
のである。また、上記のような蓋材を使用して密閉して
なる紙製あるいは合成樹脂製のカップ等においては、内
容物に金属等の不純物が混入している場合、これを金属
探知機等で検査しても、蓋材のアルミニウム箔が障害と
なって不純物を検査することが困難であるという問題点
がある。また、電子レンジで使用するような場合、アル
ミニウム箔の利用を避けなければならないという問題点
がある。上記のような問題点を改良するために、アルミ
ニウム箔を使用しない蓋材であって、且つ、デッドホー
ルド性を向上する技術として、特開2000−2036
16号公報がある。しかしながら、図3に示すように、
例えば、内面にポリエチレン層がコートされた紙容器に
ヒートシールした場合、開封時にヒートシール部の剥離
面に凸凹の突起を生じ、消費者が内容物を摂取する際
に、口当たりが悪いという問題点がある。また、開封時
にヒートシール部の剥離面にヒートシール層の樹脂が繊
維状に残存する現象(以下「糸曳き」という。)を生じ
やすいという問題がある。
However, in recent years,
Aluminum foil is one of the main causes of environmental damage due to the environmental problems of packaging materials, and its use is avoided. In addition, in the case of paper or synthetic resin cups etc. that are sealed using the lid material as described above, if impurities such as metal are mixed in the contents, inspect this with a metal detector etc. However, there is a problem in that it is difficult to inspect for impurities because the aluminum foil of the lid material becomes an obstacle. Further, when using in a microwave oven, there is a problem that the use of aluminum foil must be avoided. In order to improve the above problems, a lid material not using an aluminum foil and a technique for improving the dead hold property is disclosed in JP-A-2000-2036.
There is No. 16 publication. However, as shown in FIG.
For example, when heat-sealed in a paper container coated with a polyethylene layer on the inner surface, uneven peeling occurs on the peeled surface of the heat-sealed portion at the time of opening, and the consumer feels uncomfortable when ingesting the contents. There is. In addition, there is a problem that a phenomenon in which the resin of the heat seal layer remains in a fibrous state on the peeled surface of the heat seal portion (hereinafter referred to as "stringing") is likely to occur at the time of opening the package.

【0005】[0005]

【課題を解決するための手段】そこで本発明者らは、上
記の課題を解決するために、鋭意研究の結果、アルミニ
ウム箔を使用することなく、金属探知機等の検査も可能
であり、かつ商品の流通段階では十分に強固に接着して
その密閉性を有すると共に易開封性を有し、更にその開
封および密閉に際しては、糸曳き、紙剥けがなく、デッ
ドホールド性、フラット性に優れた蓋材を見出したもの
である。本発明は、少なくとも紙層からなる基材層、中
間層、ヒートシール層との積層体で形成されると共に、
ヒートシール層の厚みが、3μm以上20μm未満の範
囲であることを特徴とする蓋材にかかるものである。上
記において、前記の紙層が、坪量80〜200g/
2、平滑度800秒以上、MD方向の剛度50〜15
0、MD方向の紙間強度50〜100N/mであること
を特徴とする蓋材を提供することもできる。尚、上記に
おいて、紙層のMD方向とは、蓋材のラミネート工程、
打ち抜き工程、成形工程での機械における流れ方向を指
すものである。また、前記のヒートシール層が、低密度
ポリエチレン100重量部に対してポリブデン−1のホ
モポリマー33〜82重量部の割合で混合されてなる樹
脂層で形成されることを特徴とする蓋材を提供すること
もできる。また、前記のヒートシール層の厚みが3〜1
0μmの範囲にあることを特徴とする蓋材を提供するこ
ともできる。更に、前記のヒートシール層と前記の中間
層とが、共押し出し法による積層体で形成されることを
特徴とする蓋材を提供することもできる。
In order to solve the above problems, the inventors of the present invention have conducted intensive studies and as a result, can inspect a metal detector or the like without using an aluminum foil, and In the distribution stage of the product, it has a sufficiently strong adhesion and has an airtight property as well as an easy-to-open property. Furthermore, when opening and sealing the product, there is no stringing, no peeling of the paper, and excellent dead-hold property and flatness. This is the discovery of the lid material. The present invention, at least a base material layer consisting of a paper layer, an intermediate layer, and formed with a laminate with a heat seal layer,
The cover material is characterized in that the thickness of the heat seal layer is in the range of 3 μm or more and less than 20 μm. In the above, the paper layer has a basis weight of 80 to 200 g /
m 2 , smoothness of 800 seconds or more, MD direction stiffness of 50 to 15
It is also possible to provide a lid material having a paper-to-paper strength of 50 to 100 N / m in the MD direction. In the above, the MD direction of the paper layer means a laminating step of the lid material,
It indicates the machine direction in the punching process and the forming process. In addition, the heat-sealing layer is formed of a resin layer obtained by mixing 100 parts by weight of low-density polyethylene with 33 to 82 parts by weight of a homopolymer of polybutene-1. It can also be provided. The thickness of the heat seal layer is 3 to 1
It is also possible to provide a lid material characterized by being in the range of 0 μm. Furthermore, it is also possible to provide a lid member in which the heat seal layer and the intermediate layer are formed as a laminate by a coextrusion method.

【0006】[0006]

【発明の実施の形態】以下、本発明を具体的に説明す
る。図1は、本発明の蓋材の一例を示す断面図である。
図2は、本発明の蓋材を用いた剥離の状態を説明する概
念図で、(a)ヒートシールした状態、(b)ヒートシ
ール部を剥離した状態である。図1に示すように、本発
明にかかる蓋材は、少なくとも紙層からなる基材、中間
層、層厚み20μm未満のヒートシール層との積層体で
形成され、更に具体的には、紙層の片方の面に、必要な
らば、アンカーコート層を介してヒ−トシ−ル層を順次
に設け、他方、上記の紙層の他の面に、必要に応じ、紙
層からなる基材の上に文字、図形、絵柄、記号等の印刷
絵柄層を形成し、更に該印刷絵柄層を保護する表面保護
層を設けた構成からなるものである。層構成としては、
表面保護層/印刷絵柄層/基材層/アンカーコート層/
中間層/ヒートシール層からなる積層体である。
BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be specifically described below. FIG. 1 is a sectional view showing an example of the lid member of the present invention.
FIG. 2 is a conceptual diagram illustrating a peeling state using the lid member of the present invention, in which (a) the heat-sealed state and (b) the heat-sealed portion is peeled off. As shown in FIG. 1, the lid material according to the present invention is formed of a laminate of at least a base material consisting of a paper layer, an intermediate layer, and a heat-sealing layer having a layer thickness of less than 20 μm. If necessary, a heat seal layer is sequentially provided on one surface of the paper layer on the other side, and on the other side of the above paper layer, if necessary, a base material made of a paper layer. A print pattern layer of characters, figures, patterns, symbols, etc. is formed on the surface, and a surface protective layer for protecting the print pattern layer is further provided. As for the layer structure,
Surface protection layer / printed pattern layer / base material layer / anchor coat layer /
It is a laminate comprising an intermediate layer / heat seal layer.

【0007】次に、上記のような本発明にかかる蓋材を
構成する材料、及び、その製造方法等について説明す
る。本発明にかかる基材層としては、蓋材としての強
度、シール時の耐熱性、デッドホールド性、フラット性
等を保持させるために使用するものである。また、所望
の印刷絵柄等を設ける場合もあることから印刷適性を有
し、また、他の基材と積層することから積層適性等を有
することが好ましい。本発明に係る蓋材を構成する基材
層としては、少なくとも、紙を用い、例えば、シリカ、
アルミナのような酸化物が形成された2種以上のプラス
チックフィルムを積層して使用することができる。紙と
しては、例えば、模造紙、クレイコート紙、クラフト
紙、板紙、合成紙等の各種の紙を使用することができ
る。
Next, the materials constituting the lid material according to the present invention as described above, the manufacturing method thereof and the like will be described. The base material layer according to the present invention is used to maintain the strength as a lid material, the heat resistance during sealing, the dead hold property, the flatness and the like. Further, it is preferable that the ink composition has printability since a desired print pattern or the like may be provided, and that it has lamination suitability because it is laminated with another substrate. As the base material layer constituting the lid material according to the present invention, at least paper is used, for example, silica,
Two or more kinds of plastic films on which an oxide such as alumina is formed can be laminated and used. As the paper, various papers such as imitation paper, clay-coated paper, kraft paper, paperboard, and synthetic paper can be used.

【0008】その秤量としては、約80g/m2 〜20
0g/m2 位のものを使用することが好ましい。秤量が
80g/m2未満の場合は、開封時に紙剥けを発生し、
また、フラット性、デッドホールド性を維持できず、好
ましくないものである。逆に、秤量が200g/m2
越える場合は、フラット性に問題が無いものの、デッド
ホールド性がなく、また、「紙剥け」を生じ、使用上、
取り扱いにくいため、好ましくない。ここで、「紙剥
け」とは、ヒートシール部を剥離する際に、紙層が破壊
される現象をいう。
The weight is about 80 g / m 2 to 20
It is preferable to use one having a position of 0 g / m 2 . If the weighing amount is less than 80 g / m 2 , paper peeling may occur when opening,
Further, the flatness and the dead hold property cannot be maintained, which is not preferable. On the other hand, when the weight exceeds 200 g / m 2 , there is no problem in flatness, but there is no dead-holding property, and “paper peeling” occurs, and
It is not preferable because it is difficult to handle. Here, "paper peeling" refers to a phenomenon in which the paper layer is destroyed when the heat-sealed portion is peeled off.

【0009】また、上記の紙のMD方向の平滑度として
は、800秒以上であるものを使用することが好まし
い。平滑度が800秒未満の場合は、印刷適性が低下す
るため、好ましくないものである。尚、本発明でいう平
滑性性とは、JIS P−8119「紙及び板紙のベッ
ク試験機による平滑度試験方法」による測定値である。
The smoothness in the MD direction of the above paper is preferably 800 seconds or more. When the smoothness is less than 800 seconds, printability is deteriorated, which is not preferable. The smoothness referred to in the present invention is a value measured by JIS P-8119 "Smoothness test method for paper and board by Beck tester".

【0010】その剛度は、50〜150m2 位のものを
使用することが好ましいものである。剛度が50未満で
あると、蓋体の剛度が不足して、デッドホールド性がな
く、また、打ち抜き、及び、成形が困難となり、好まし
くないものである。一方、剛度が150を越えると蓋体
の厚み、重量等の点で不経済となる。尚、本発明でいう
剛度とは、JIS P−8143「紙のクラークこわさ
試験機によるこわさ試験方法」による測定値である。
It is preferable to use one having a rigidity of about 50 to 150 m 2 . If the rigidity is less than 50, the rigidity of the lid is insufficient, there is no dead hold property, and punching and molding become difficult, which is not preferable. On the other hand, if the rigidity exceeds 150, it becomes uneconomical in terms of the thickness and weight of the lid. The stiffness referred to in the present invention is a value measured according to JIS P-8143 "Clarke stiffness test method for paper using a stiffness tester".

【0011】その紙間強度は、50〜100N/m位の
ものを使用することが好ましい。紙間強度が50未満で
あると、開封時に紙剥けが生じるため、好ましくない。
尚、本発明でいう紙間強度とは、JIS P−8129
「紙及び板紙の表面強さ試験方法」による測定値であ
る。
It is preferable to use one having a paper-to-paper strength of about 50 to 100 N / m. If the paper-to-paper strength is less than 50, paper peeling may occur at the time of opening, which is not preferable.
The paper-to-paper strength referred to in the present invention means JIS P-8129.
It is the value measured by the "surface strength test method for paper and board".

【0012】必要があれば、このような紙層の中間層形
成面側に、アンカーコート層を設けても良い。アンカー
コート層は、基材中にしみ込み、紙間強度を向上させる
と共にヒートシール層の中間層との接着力を高めるのに
有効である。アンカーコート剤としては、具体的には、
例えば、有機チタン系アンカーコーティング剤、イソシ
アネート系アンカーコーティング剤、ポリエチレンイミ
ン系アンカーコーティング剤、ポリブタジェン系アンカ
ーコーティング剤等を使用することができる。而して、
本発明においては、上記のようなアンカーコーティング
剤を使用して、例えば、グラビアコート、ロールコート
等の通常のコーティング法でコーティングしてプライマ
ー層を形成することができる。また、そのコート量とし
ては、1〜5g/m2 位が好ましい。また、このような
紙層の中間層形成面側には、中間層との接着力を高める
ために、予め、コロナ放電処理を施してもよい。
If necessary, an anchor coat layer may be provided on the intermediate layer forming surface side of such a paper layer. The anchor coat layer penetrates into the substrate and is effective in improving the inter-paper strength and enhancing the adhesive force of the heat seal layer to the intermediate layer. As the anchor coating agent, specifically,
For example, an organic titanium-based anchor coating agent, an isocyanate-based anchor coating agent, a polyethyleneimine-based anchor coating agent, a polybutadiene-based anchor coating agent and the like can be used. Therefore,
In the present invention, the above-mentioned anchor coating agent can be used to form a primer layer by coating with a usual coating method such as gravure coating or roll coating. The coating amount is preferably 1 to 5 g / m @ 2. In addition, a corona discharge treatment may be performed in advance on the surface of the paper layer on which the intermediate layer is formed in order to enhance the adhesive strength with the intermediate layer.

【0013】また、蓋材の表面には、装飾、内容物の表
示、賞味期間の表示、製造者、販売者等の表示、その他
等の表示のために、文字、絵柄、図形、記号等の任意の
印刷絵柄層を設けるものである。かかる印刷絵柄層は、
例えば、通常のインキ組成物を使用してオフセット印刷
あるいはグラビア印刷等の通常の印刷法等によって形成
することができる。
Further, on the surface of the lid material, characters, pictures, figures, symbols, etc. are displayed for decoration, display of contents, display of shelf life, display of manufacturer, seller, etc. An arbitrary printed pattern layer is provided. Such a printed pattern layer,
For example, it can be formed by an ordinary printing method such as offset printing or gravure printing using an ordinary ink composition.

【0014】更に、本発明においては、上記の印刷絵柄
層を保護するために表面保護層を設けることが好まし
く、例えば、樹脂のフィルムないしシートをラミネート
することにより、あるいは樹脂をビヒクルの主成分とす
る組成物をコーティングしてコーティング膜等を形成す
ることによって、表面保護層を設けることができる。上
記の樹脂としては、例えば、ポリオレフィン系樹脂、ア
クリル系樹脂、ポリエステル系樹脂、ポリウレタン系樹
脂、ポリアミド系樹脂、セルロース系樹脂、その他等を
使用することができる。
Further, in the present invention, it is preferable to provide a surface protective layer for protecting the above-mentioned printed pattern layer, for example, by laminating a resin film or sheet, or by using the resin as a main component of the vehicle. The surface protective layer can be provided by coating the composition described above to form a coating film or the like. As the above resin, for example, a polyolefin resin, an acrylic resin, a polyester resin, a polyurethane resin, a polyamide resin, a cellulose resin, or the like can be used.

【0015】次に、本発明にかかるヒートシール層とし
ては、低密度ポリエチレン100重量部に対して、ポリ
ブデン−1のホモポリマーが33〜82重量部の割合で
混合されてなる樹脂層で形成される。前記のヒートシー
ル層は、加熱によって溶融し相互に融着し得るヒ−トシ
−ル性を有し、開封時に凝集破壊を生じる樹脂のフィル
ムないしシ−トを使用して形成するを形成するものであ
る。ポリブデン−1は、低密度ポリエチレンと実質的に
非相溶であり、その混合物は、いわゆる海島構造を形成
する。このため、海成分の低密度ポリエチレン中に島成
分のポリブデン−1が分散した状態となる。従って、中
間層の凝集力が適度に低下し、良好な凝集破壊タイプの
易開封性が発現される。
Next, the heat-sealing layer according to the present invention is formed of a resin layer obtained by mixing a homopolymer of polybutene-1 in an amount of 33 to 82 parts by weight with respect to 100 parts by weight of low-density polyethylene. It The heat-sealing layer has a heat-sealing property such that it can be melted by heating and fused to each other, and is formed by using a resin film or sheet which causes cohesive failure when opened. Is. Polybuden-1 is substantially incompatible with low density polyethylene and the mixture forms a so-called sea-island structure. Therefore, the island component polybuden-1 is dispersed in the sea component low density polyethylene. Therefore, the cohesive force of the intermediate layer is appropriately reduced, and good cohesive failure type easy-opening property is exhibited.

【0016】ヒートシール層の低密度ポリエチレンとポ
リブデン−1との混合割合は、低密度ポリエチレン10
0重量部に対して、ポリブデン−1のホモポリマーが3
3〜82重量部の範囲が好ましい。ポリブデン−1の上
記の混合量が33重量部未満の場合は、ヒートシール強
度が強くなりすぎ、易開封性包装材料を例えばポリエチ
レンコート紙を用いた紙カップ容器などの蓋材として使
用する場合、紙剥けを生じる恐れがあり好ましくない。
ポリブデン−1の上記の混合量が82重量部を超える場
合は、ヒートシール強度が弱くなりすぎ、また、糸曳き
が生じやすくなるため好ましくない。
The mixing ratio of low-density polyethylene and polybutene-1 in the heat-sealing layer is such that the low-density polyethylene 10
0 parts by weight of polybutene-1 homopolymer is 3
A range of 3 to 82 parts by weight is preferable. When the above-mentioned mixed amount of polybutene-1 is less than 33 parts by weight, the heat-sealing strength becomes too strong, and when the easy-open packaging material is used as a lid material such as a paper cup container using polyethylene-coated paper, paper It may cause peeling, which is not preferable.
If the above-mentioned amount of polybutene-1 to be mixed exceeds 82 parts by weight, the heat-sealing strength becomes too weak and stringing is likely to occur, which is not preferable.

【0017】ヒートシール層の低密度ポリエチレンとし
ては、融点110℃以下、密度0.915〜0.920
g/cm3の範囲である高圧法低密度ポリエチレンが好
適に用いられる。ヒートシール層のポリブデン−1とし
ては、融点120℃以上、密度0.905〜0.917
g/cm3の範囲であるホモポリマーが好適に用いられ
る。例えば、前記のポリブデン−1を主体とするホモポ
リマーでなく、ブデン−1を主体とする他のオレフィン
との共重合体を利用した場合は、シール強度が強くな
り、紙剥けしやすくなるため、好ましくない。
The low density polyethylene for the heat seal layer has a melting point of 110 ° C. or less and a density of 0.915 to 0.920.
High-pressure low density polyethylene having a range of g / cm 3 is preferably used. Polybutene-1 of the heat seal layer has a melting point of 120 ° C. or higher and a density of 0.905 to 0.917.
A homopolymer having a range of g / cm 3 is preferably used. For example, when not a homopolymer mainly composed of the above polybutene-1, but a copolymer with another olefin mainly composed of Buden-1 is used, the sealing strength becomes strong and the paper peels easily, Not preferable.

【0018】ヒートシール層の厚みとしては、20μm
未満であることが好ましく、3μm〜10μmの範囲に
あることが望ましい。上記の樹脂、および、厚みとする
ことで、内面にポリエチレン層がコートされた紙容器に
ヒートシールした場合、開封時にヒートシール部の剥離
面に凸凹状の突起や、糸曳き現象や、紙剥けがなく、密
封性と耐熱性に優れ、剥離面が滑らかで、消費者が内容
物を摂取する際に、口当たりが良い容器を得ることがで
きる。ヒートシール層の厚みが3μm未満の場合は、シ
ール強度、ピール強度が不安定となり、挟雑物介在シー
ル性も不充分となるため好ましくない。ヒートシール層
の厚みが20μm以上の場合は、内面にポリエチレン層
がコートされた紙容器にヒートシールした場合、開封時
のヒートシール層の凝集破壊により、剥離する際に剥離
面の起伏の激しい凸凹状の突起が生じ、糸曳きを生じや
すく、口当たりの悪い容器となるため、好ましくない。
また、コスト面においても、不利となるため、好ましく
ない。
The thickness of the heat seal layer is 20 μm
It is preferably less than 3 μm and more preferably in the range of 3 μm to 10 μm. When heat-sealed to a paper container whose inner surface is coated with a polyethylene layer by using the above-mentioned resin and thickness, uneven protrusions on the peeling surface of the heat-sealing portion at the time of opening, stringing phenomenon, or peeling of paper It is possible to obtain a container that is free from heat, has excellent sealability and heat resistance, has a smooth peeling surface, and has a pleasant mouthfeel when the consumer ingests the contents. If the thickness of the heat-sealing layer is less than 3 μm, the sealing strength and peeling strength become unstable, and the intervening substance-sealing property becomes insufficient, which is not preferable. When the thickness of the heat-sealing layer is 20 μm or more, when heat-sealed in a paper container having an inner surface coated with a polyethylene layer, cohesive failure of the heat-sealing layer at the time of opening causes rough unevenness of the peeling surface when peeling. -Shaped projections are formed, stringing is likely to occur, and the container has a bad mouth feel, which is not preferable.
In addition, it is disadvantageous in terms of cost, which is not preferable.

【0019】更に、本発明にかかる中間層としては、エ
チレン・不飽和カルボン酸共重合体からなる樹脂層で形
成される。エチレン・不飽和カルボン酸共重合体として
は、例えば、エチレン・メタクリル酸共重合体(以下
「EMAA樹脂」という。)、エチレン・アクリル酸共
重合体(以下「EAA樹脂」という。)を好適に使用す
ることができ、なかでも、EMAA樹脂を使用すること
が熱安定性に優れ、臭気の少ない点から望ましい。EM
AA樹脂としては、密度0.930〜0.940g/c
3、融点96〜100℃であるものが望ましい。本発
明において、中間層は、紙間強度を向上させるととも
に、基材とヒートシール材との接着力を高め、また、基
材層にシーラント層を積層した際に発生するカールを抑
制し、デッドホールド性、及び、フラット性を保持する
ために使用するものである。而して、不飽和カルボン酸
共重合体からなる樹脂は、ポリエチレン100重量部に
対して、メタクリル酸樹脂が7〜12重量部の割合で混
合されてなる混合樹脂で形成される。且つ、中間層の厚
みが、10〜50μmの範囲にあるものが望ましい。中
間層の厚みが10μm以下の場合は、基材と積層した時
のカールが大きくなるため、好ましくない。中間層の厚
みが50μm以上の場合は、不経済となり、好ましくな
い。また、中間層の厚みは、ヒートシール層の厚みと同
じか、それ以上であることが好ましく、ヒートシール層
の厚みの5倍程度までの範囲の厚みが好ましい。中間層
の厚みが、ヒートシール層の厚みよりも薄い場合は、基
材と積層した時のカールが大きくなり、更に、共押し出
し法による中間層とヒートシール層の積層加工も難しく
なるため好ましくない。また、中間層の厚みが少ない
と、フランジ部に段差を有する紙カップ容器の蓋材とし
てしようしした場合、密封性が得られないことがある。
Further, the intermediate layer according to the present invention is formed of a resin layer made of an ethylene / unsaturated carboxylic acid copolymer. As the ethylene / unsaturated carboxylic acid copolymer, for example, ethylene / methacrylic acid copolymer (hereinafter referred to as “EMAA resin”) and ethylene / acrylic acid copolymer (hereinafter referred to as “EAA resin”) are suitable. It is possible to use, and it is preferable to use the EMAA resin because of its excellent thermal stability and low odor. EM
As AA resin, density 0.930 to 0.940 g / c
m 3, it it is desirable with a melting point 96-100 ° C.. In the present invention, the intermediate layer improves the inter-paper strength, enhances the adhesive force between the base material and the heat-sealing material, and suppresses curling that occurs when the sealant layer is laminated on the base material layer, thereby reducing dead. It is used to hold and hold flatness. Thus, the resin composed of the unsaturated carboxylic acid copolymer is formed of a mixed resin in which a methacrylic acid resin is mixed in a ratio of 7 to 12 parts by weight with respect to 100 parts by weight of polyethylene. Moreover, the thickness of the intermediate layer is preferably in the range of 10 to 50 μm. When the thickness of the intermediate layer is 10 μm or less, the curl when laminated with the base material becomes large, which is not preferable. When the thickness of the intermediate layer is 50 μm or more, it is uneconomical and not preferable. The thickness of the intermediate layer is preferably equal to or greater than the thickness of the heat seal layer, and is preferably within the range of about 5 times the thickness of the heat seal layer. If the thickness of the intermediate layer is thinner than the thickness of the heat-sealing layer, the curl when laminated with the base material becomes large, and further, it becomes difficult to laminate the intermediate layer and the heat-sealing layer by the coextrusion method, which is not preferable. . Further, if the thickness of the intermediate layer is small, the sealing property may not be obtained when it is used as a lid material for a paper cup container having a step in the flange portion.

【0020】なお、本発明ではヒートシール層、及び、
中間層には、酸化防止剤、熱安定剤、紫外線吸収剤、可
塑剤、粘度調節剤、滑剤、顔料等を必要に応じて添加し
てもよい。
In the present invention, the heat seal layer, and
Antioxidants, heat stabilizers, ultraviolet absorbers, plasticizers, viscosity modifiers, lubricants, pigments and the like may be added to the intermediate layer as needed.

【0021】上記の中間層と層厚みが20μm未満のヒ
ートシール層を設け、両者を積層してなる積層体は、共
押し出し法をとることにより、両者の間に接着剤層が介
在しないため、開封時のヒートシール層の凝集破壊を中
間層とヒートシール層の界面近傍に集中させることがで
き、ヒートシール強度を安定化し、糸曳きの発生を防止
することができる。また、共押し出し法をとることによ
り、膜厚が比較的薄い場合でも所定の層比で容易に形成
することができる。
A laminate obtained by providing the above-mentioned intermediate layer and a heat-sealing layer having a layer thickness of less than 20 μm, and laminating the two layers by the co-extrusion method has no adhesive layer between the two layers. Cohesive failure of the heat seal layer at the time of opening can be concentrated near the interface between the intermediate layer and the heat seal layer, the heat seal strength can be stabilized, and the occurrence of stringing can be prevented. Further, by adopting the co-extrusion method, it is possible to easily form a film with a predetermined layer ratio even when the film thickness is relatively thin.

【0022】次に、本発明において、前記のシーラント
層と、前記の紙で構成される基材層に中間層を対向する
ように、基材にラミネートしてされることにより、本発
明にかかる蓋材を得ることができる。ラミネート方法と
しては、ドライラミネーション法、押し出しラミネーシ
ョン法、共押し出しコート法のいずれの方法でも積層す
ることができる。ドライラミネーション法または押し出
しラミネーション法で積層する場合は、中間層とヒート
シール層の積層フィルムを予め共押し出し法で作製する
必要があるが、共押し出しコート法を採る場合は、中間
層とヒートシール層の積層フィルムを同時に基材層に積
層することができるので、工程が簡略化され生産性を向
上させることができる。
Next, according to the present invention, the sealant layer and the base material layer composed of the paper are laminated on a base material so as to face the intermediate layer. A lid material can be obtained. As a laminating method, any of a dry lamination method, an extrusion lamination method and a coextrusion coating method can be used for lamination. When laminating by dry lamination method or extrusion lamination method, it is necessary to prepare a laminated film of an intermediate layer and a heat seal layer in advance by a coextrusion method, but when adopting a coextrusion coating method, an intermediate layer and a heat seal layer are used. Since the laminated film of 1) can be laminated on the base material layer at the same time, the process can be simplified and the productivity can be improved.

【0023】また、開封用のタブとしては、紙目方向に
対して、±50度の範囲内の開封方向に設けることによ
り、優れたデッドホールド性を得ることができる。
Further, when the opening tab is provided in the opening direction within a range of ± 50 degrees with respect to the paper grain direction, an excellent dead hold property can be obtained.

【0024】以上に説明した本発明にかかる蓋体を、枚
葉供給方式の自動装置で、内容物を充填した容器に供給
する際、中間層、ヒートシール層、基材層のそれぞれの
厚み、および、および両者の厚みのバランスが適する範
囲に形成されるため、カールが小さく、適度な剛度で、
フラット性に優れた蓋材のため、ハンドリングにおいて
問題なく、供給することができる。
When the lid according to the present invention described above is fed to a container filled with contents by an automatic single-wafer feeding system, the thickness of each of the intermediate layer, the heat-sealing layer, and the substrate layer, And, and since the thickness balance of both is formed in a suitable range, the curl is small, the rigidity is moderate,
Since the lid material has excellent flatness, it can be supplied without any problem in handling.

【0025】また、充填する内容物としては、例えば、
即席ラ−メン、ソバ、麺、ゼリ−状菓子、ジュ−ス、そ
の他等の種々のものをあげることができる。
The contents to be filled are, for example,
Various items such as instant ramen, buckwheat, noodles, jelly-like confectionery, juice and the like can be mentioned.

【0026】而して、本発明かかる蓋体による開封につ
いて説明する。図2(a)に示すように、本発明の蓋体
を被着体にそれぞれのヒートシール層を対面させて、ヒ
ートシール用熱板によって、ヒートシールして、ヒート
シール部を形成する。該ヒートシール部を剥離(開封)
すると、図2(b)に示すように、中間層とヒートシー
ル層の界面近傍にヒートシール層の凝集破壊が起こり、
糸曳きのない平滑な剥離面が形成される。
The opening with the lid according to the present invention will be described. As shown in FIG. 2 (a), the lid of the present invention is adhered to the adherend, and the respective heat-sealing layers are faced to each other and heat-sealed by a heat-sealing hot plate to form a heat-sealing portion. Peel off (open) the heat seal part
Then, as shown in FIG. 2B, cohesive failure of the heat seal layer occurs near the interface between the intermediate layer and the heat seal layer,
A smooth release surface without stringing is formed.

【0027】従って、上記に説明した通り、本発明の蓋
体を用いることにより、アルミニウム箔を使用すること
なく、ヒートシール強度を安定化し、また、開封時にお
いては、適度のヒートシール強度で凝集破壊され、剥離
面に凹凸状の突起、糸曳き、紙剥けの発生を防止するこ
とができるため、滑らかで、きれいな状態の剥離面を得
ることができる。また、蓋体を真ん中位まで剥離して、
お湯を注ぐ際に、デッドホールド性を有する蓋体を用い
ることにより、垂れることなく、起立させることができ
るため、注湯作業に優れる包装体を得ることができる。
また、注湯の際、蓋体を閉じた際に、剥離面が平滑なた
め、閉蓋性に優れるため、内容物である食品の調理性に
優れた包装体を得ることができる。また、内容物を摂取
する際、容器のフランジが平滑なため、口当たりの良い
包装体を得ることができる。
Therefore, as explained above, by using the lid of the present invention, the heat seal strength is stabilized without using the aluminum foil, and at the time of opening, the heat seal strength is moderate. Since it is possible to prevent the occurrence of breakage, uneven projections, stringing, and paper peeling on the peeling surface, it is possible to obtain a smooth and clean peeling surface. Also, peel the lid to the middle position,
When pouring hot water, by using a lid body having a dead-hold property, it is possible to stand up without drooping, and thus it is possible to obtain a package excellent in pouring work.
In addition, when pouring hot water, when the lid is closed, the peeling surface is smooth, so that the lid is excellent in closure property, and thus a package excellent in cookability of the food product, which is the content, can be obtained. In addition, since the flange of the container is smooth when the contents are ingested, it is possible to obtain a palatable package.

【0028】[0028]

【実施例】次に、本発明について実施例を挙げて更に具
体的に本発明を説明する。但し、本発明は、これらの実
施例に限定されるものではない。(実施例1)融点10
5℃の低密度ポリエチレン62量部と融点125℃のポ
リブデン−1、38量部との混合物である7μmのヒー
トシール層を用い、融点98℃のエチレン・メタクリル
酸共重合体(以下「EMAA」と記載する。)の30μ
mの中間層を用い、坪量110g/m2のクレイコート
紙に、紙層の中間層側にポリウレタン系のアンカーコー
ト材を塗布し、押し出し温度300℃で両者を共押し出
しラミネートし、下記構成の実施例1の蓋材を作製し
た。 (層構成)紙100g/m2/EMAA30μm/混合
樹脂によるヒートシール層7μm なお、紙は、下記の物性値のものを使用した。 平滑度:858秒 剛度:118(MD方向)、82(TD方向) 紙間強度:78N/m(MD方向)、71N/m(TD
方向) 尚、上記において、紙層のMD方向とは、前述した通
り、蓋材のラミネート工程、打ち抜き工程、成形工程で
の機械における流れ方向を指すものである。紙層のTD
方向とは、蓋材のラミネート工程、打ち抜き工程、成形
工程での機械における流れ方向と交差する方向を指すも
のである。
EXAMPLES Next, the present invention will be described more specifically with reference to Examples. However, the present invention is not limited to these examples. (Example 1) Melting point 10
Using a 7 μm heat-sealing layer, which is a mixture of 62 parts by weight of low-density polyethylene at 5 ° C. and 38 parts by weight of polybutene-1, having a melting point of 125 ° C., an ethylene / methacrylic acid copolymer having a melting point of 98 ° C. (hereinafter “EMAA”) is used. 30 μ)
Using an intermediate layer of m, a polyurethane-based anchor coat material is applied to the intermediate layer side of the paper layer on a clay-coated paper having a basis weight of 110 g / m 2 , and both are extruded at an extrusion temperature of 300 ° C. and laminated to form the following composition. The lid material of Example 1 was manufactured. (Layer structure) Paper 100 g / m 2 / EMAA 30 μm / Heat-sealing layer 7 μm with mixed resin The paper used had the following physical properties. Smoothness: 858 seconds Rigidity: 118 (MD direction), 82 (TD direction) Paper strength: 78 N / m (MD direction), 71 N / m (TD
Direction) In the above description, the MD direction of the paper layer refers to the machine flow direction in the lid material laminating step, punching step, and molding step, as described above. TD of paper layer
The direction refers to a direction intersecting the machine flow direction in the lid material laminating process, punching process, and molding process.

【0029】(試験)以上のように作製した実施例1の
蓋材を評価するために、下記の試験を実施した。内面に
融点106℃のポリエチレン層が厚み20μmになるよ
う押し出しコートされたカップ用紙(坪量280g/m
2)をテーパー付き紙カップ(上部の端部は、外側にカ
ーリングしたもの)に成形した紙カップ(開口部の直径
99mm、容器の高さ110mm、フランジ巾3mm)
を作製した。上記で作製した紙カップに、水を充填した
後、その開口部にフラットな蓋体に打ち抜いた実施例1
の蓋材を、シール温度160℃、シール圧150kP
a、シール時間1秒のシール条件で熱接着して密封した
容器を作製した。
(Test) In order to evaluate the lid member of Example 1 produced as described above, the following test was conducted. Cup paper extruded and coated on its inner surface so that the polyethylene layer having a melting point of 106 ° C. has a thickness of 20 μm (basis weight: 280 g / m
2 ) is formed into a tapered paper cup (the upper end is curled to the outside) (opening diameter 99 mm, container height 110 mm, flange width 3 mm)
Was produced. Example 1 in which the paper cup prepared above was filled with water and then punched into a flat lid at its opening
Sealing material of 160 ℃, sealing pressure of 150kP
a, a container was prepared by heat-sealing and sealing under a sealing condition of a sealing time of 1 second.

【0030】(評価)この容器を用い、容器から蓋材の
密封性、開封性(剥離する時の剥離強度とその時のフラ
ンジ部の紙剥けの有無、糸曳きの有無)、デッドホール
ド性、フラット性(カール状態)を評価した。
(Evaluation) Using this container, the sealing property of the lid material from the container, the opening property (peeling strength at the time of peeling and the presence or absence of peeling of the flange portion at that time, the presence or absence of string pulling), dead hold property, flatness The property (curled state) was evaluated.

【0031】(密封性評価方法)引張り試験機(株)島
津製作所製テンシロンを用いて、剥離角度180°、引
張り速度300mm/分にてヒートシール強度(kg/15
mm)を測定した。1.0kg/15mm以上を密封性良好と
し、1.0kg/15mm未満を密封性不良として評価し
た。
(Evaluation method of sealing property) Using a tensile tester Tensilon manufactured by Shimadzu Corporation, heat seal strength (kg / 15) at a peeling angle of 180 ° and a pulling speed of 300 mm / min.
mm) was measured. A sealability of 1.0 kg / 15 mm or more was evaluated as good and a sealability of less than 1.0 kg / 15 mm was evaluated as poor.

【0032】(開封性評価方法)接着強度が1.0kg/
15mm〜2.2kg/15mmの範囲内にあるとき、開封性
良好として評価した。また、剥離面の紙剥けの有無、糸
曳きの有無を目視にて評価した。
(Opening property evaluation method) Adhesive strength is 1.0 kg /
When it was within the range of 15 mm to 2.2 kg / 15 mm, it was evaluated as good openability. Further, the presence or absence of peeling of the paper on the peeled surface and the presence or absence of stringing were visually evaluated.

【0033】(デッドホールド性)タブの先端から蓋の
真ん中の位置48mmのところまで開封後、タブを手か
ら放し、タブの先端とカップの開口部までの距離を測定
した。25mm以上をデッドホールド性良好とし、25mm
未満を密封性不良として評価した。
(Dead hold property) After opening from the tip of the tab to a position 48 mm in the middle of the lid, the tab was released from the hand, and the distance between the tip of the tab and the opening of the cup was measured. 25mm or more is considered as a good dead hold property, and 25mm
Less than 1 was evaluated as a poor sealing property.

【0034】(フラット性)実施例1の蓋材を直径10
0mmの円形に打ち抜き、フラットなガラス板上に静置
し、タブの先端とガラス面までの距離を測定した。7mm
以下をフラット性良好とし、7mmを超えるとフラット性
不良として評価した。その他に、タブの先端から蓋の真
ん中の位置48mmのところまで開封後、蓋を再密閉
し、カールの状態を目視観察し、評価した。
(Flatness) The lid material of Example 1 has a diameter of 10
It was punched out into a circle of 0 mm and left still on a flat glass plate, and the distance between the tip of the tab and the glass surface was measured. 7 mm
The following was evaluated as good flatness, and when it exceeded 7 mm, it was evaluated as poor flatness. In addition, after opening from the tip of the tab to a position 48 mm in the middle of the lid, the lid was resealed, and the curled state was visually observed and evaluated.

【0035】(測定結果)実施例1の蓋材の密封性、開
封性(剥離強度、紙剥け発生、糸曳き発生)、デッドホ
ールド性、平滑性(カール発生)は、次の通りであっ
た。 剥離強度:1.5kg/15mm 紙剥け発生:なし 糸曳き発生:なし デッドホールド性:30.5mm カール性:3mm
(Measurement Results) The lid material of Example 1 had the following sealing properties, unsealing properties (peeling strength, paper peeling, string pulling), dead hold properties, and smoothness (curling). . Peel strength: 1.5 kg / 15 mm Paper peeling: None Stringing: None Dead hold: 30.5 mm Curl: 3 mm

【0036】以上の結果から明らかなように、実施例1
の蓋材は、ヒートシール性による密封性に優れ、良好な
開封性、即ち、手で開封した際、適度の剥離強度で蓋体
を剥離することができ、また、紙剥け、糸曳きの発生も
みられず、平滑できれいな剥離面を得ることができた。
また、剥離面の断面を顕微鏡観察した結果、蓋材のヒー
トシール層が、蓋材側とカップ側の双方に観察され、ヒ
ートシール層が開封時に凝集破壊がされたことが確認で
き、更に、蓋材のヒートシール層が、ヒートシール層と
中間層の界面の近傍に凝集破壊面が観察された。また、
カールに関しても、小さく、自動充填シール機等に対す
る機械適性も良好であった。また、蓋体を中央部まで剥
離して開口したところ、蓋体は起立状態がそのまま維持
され、支障なく、湯を注ぐことができた。また、再封時
においても、蓋体はフラットで、開くことがなかった。
As is clear from the above results, Example 1
The lid material is excellent in heat-sealing sealing property and has good opening property, that is, the lid member can be peeled with an appropriate peeling strength when opened by hand, and paper peeling and stringing occur. No rust was seen, and a smooth and clean peeled surface could be obtained.
Further, as a result of microscopic observation of the cross section of the peeled surface, the heat seal layer of the lid material was observed on both the lid material side and the cup side, and it was possible to confirm that the heat seal layer was cohesively broken at the time of opening, and further, A cohesive failure surface was observed in the heat seal layer of the lid material near the interface between the heat seal layer and the intermediate layer. Also,
The curl was also small, and the machine suitability for an automatic filling and sealing machine was good. Further, when the lid was peeled off to the central portion and opened, the lid was kept in an upright state, and hot water could be poured without any trouble. Further, even when resealing, the lid was flat and could not be opened.

【0037】[0037]

【発明の効果】以上の説明で明らかなように、本発明
は、少なくとも紙層からなる基材層、中間層、ヒートシ
ール層を順次積層した積層体で形成され、これを紙製あ
るいは合成樹脂製のカップの蓋材として使用することが
できる。その結果、アルミニウム箔を使用することな
く、ヒートシール強度を安定化し、開封時において、適
度のヒートシール強度で凝集破壊され、剥離面に凹凸状
の突起、糸曳き、紙剥けの発生を防止することができ、
滑らかで、きれいな状態の剥離面を得ることができる。
このため、内容物を摂取する際、容器のフランジが平滑
なため、口当たりの良い包装体を提供することができる
ものである。更に、半分まで剥離して開封してカップ内
にお湯を注ぐ場合において、開口して起立し、また再密
閉もするときにも、容易に閉じることも可能な蓋材を提
供することができ、内容物の電子レンジによる調理が可
能なものであり、その廃棄に際しては燃焼ゴミとして処
分することができ、また、包装体の異物検査に際しても
金属探知機等の検査を可能なため安全性の高い包装製品
を提供することができるものである。
As is apparent from the above description, the present invention is formed of a laminated body in which a base material layer consisting of at least a paper layer, an intermediate layer, and a heat seal layer are sequentially laminated. It can be used as a lid material for a cup made of. As a result, the heat seal strength is stabilized without using an aluminum foil, and when opened, cohesive failure occurs with moderate heat seal strength, preventing the occurrence of uneven projections, stringing and paper peeling on the release surface. It is possible,
A smooth and clean release surface can be obtained.
For this reason, when the contents are ingested, the flange of the container is smooth, so that it is possible to provide a package having a pleasant mouthfeel. Furthermore, it is possible to provide a lid material that can be easily closed even when it is peeled up to half and opened, and hot water is poured into the cup to open and stand up, and also when resealing, The contents can be cooked in a microwave oven and can be disposed of as burnt garbage when it is discarded. Also, the inspection of foreign substances in the package can be inspected with a metal detector, etc. A packaged product can be provided.

【図面の簡単な説明】[Brief description of drawings]

【図1】本発明にかかる蓋材の層構成を示す断面図であ
る。
FIG. 1 is a cross-sectional view showing a layer structure of a lid member according to the present invention.

【図2】本発明の蓋材を用いた剥離の状態を説明する概
念図で、(a)ヒートシールした状態、(b)ヒートシ
ール部を剥離した状態である。
FIG. 2 is a conceptual diagram illustrating a peeling state using the lid member of the present invention, in which (a) the heat-sealed state and (b) the heat-sealed portion is peeled off.

【図3】従来の蓋材を用いた剥離の状態を説明する概念
図で、(a)ヒートシールした状態、(b)ヒートシー
ル部を剥離した状態である。
FIG. 3 is a conceptual diagram illustrating a peeling state using a conventional lid member, in which (a) the heat-sealed state and (b) the heat-sealed portion is peeled off.

【符号の説明】[Explanation of symbols]

1 表面保護層 2 印刷絵柄層 3 基材層(紙層) 4 中間層 5 ヒートシール層 6 介在樹脂層 10 蓋材 11 ヒートシール部 12 剥離部 30 被着体 31 被着体ヒートシール層 32 被着体基材層 1 Surface protection layer 2 Printed pattern layer 3 Base material layer (paper layer) 4 Middle class 5 Heat seal layer 6 Intervening resin layer 10 Lid material 11 Heat seal part 12 Peeling part 30 adherend 31 Adherend heat seal layer 32 Adhesive substrate layer

フロントページの続き Fターム(参考) 3E084 AA06 AA12 AA37 BA01 BA07 BA08 BA09 CA01 CC04 FD13 GB08 HA01 HB01 HC08 HD01 LA01 4F100 AK04B AK06C AK09C AK24B AK25B AK51 AK70 AL05B AL05C BA03 BA07 DA03 DG10A EH20 EJ65 GB18 JA04B JA13B JA20B JA20C JK15 JL12 JL12C JL14 YY00B YY00C 4F207 AA04 AA07 AC03 AD06 AG03 AH57 KA01 KA17 KB13 Continued front page    F term (reference) 3E084 AA06 AA12 AA37 BA01 BA07                       BA08 BA09 CA01 CC04 FD13                       GB08 HA01 HB01 HC08 HD01                       LA01                 4F100 AK04B AK06C AK09C AK24B                       AK25B AK51 AK70 AL05B                       AL05C BA03 BA07 DA03                       DG10A EH20 EJ65 GB18                       JA04B JA13B JA20B JA20C                       JK15 JL12 JL12C JL14                       YY00B YY00C                 4F207 AA04 AA07 AC03 AD06 AG03                       AH57 KA01 KA17 KB13

Claims (6)

【特許請求の範囲】[Claims] 【請求項1】 少なくとも紙層からなる基材層、中間
層、ヒートシール層との積層体で形成されると共に、ヒ
ートシール層の厚みが、3μm以上20μm未満の範囲
であることを特徴とする蓋材。
1. A laminate comprising a base material layer comprising at least a paper layer, an intermediate layer and a heat seal layer, and the thickness of the heat seal layer is in the range of 3 μm or more and less than 20 μm. Lid material.
【請求項2】 前記の紙層が、坪量80〜200g/m
2、平滑度800秒以上、MD方向の剛度50〜15
0、MD方向の紙間強度50〜100N/mであること
を特徴とする請求項1記載の蓋材。
2. The paper layer has a basis weight of 80 to 200 g / m 2.
2 , smoothness of 800 seconds or more, MD direction stiffness of 50 to 15
The lid material according to claim 1, wherein the inter-paper strength in the MD direction is 0 to 50 N / m.
【請求項3】 前記の中間層が、ポリエチレン100
重量部に対して、不飽和カルボン酸樹脂が7〜12重量
部の割合で混合されてなる樹脂層で形成されると共に、
密度0.930〜0.940g/cm3、融点96〜1
00℃であり、且つ、該中間層の厚みが10〜50μm
の範囲にあって、且つ、該中間層の厚みが該ヒートシー
ル層の厚み以上であることを特徴とする請求項1、2の
いずれかに記載の蓋材。
3. The polyethylene 100 as the intermediate layer.
The unsaturated carboxylic acid resin is formed in a resin layer formed by mixing 7 to 12 parts by weight with respect to parts by weight, and
Density 0.930 to 0.940 g / cm 3 , melting point 96 to 1
00 ° C., and the thickness of the intermediate layer is 10 to 50 μm
3. The lid material according to claim 1, wherein the thickness of the intermediate layer is equal to or larger than the thickness of the heat seal layer.
【請求項4】 前記のヒートシール層が、低密度ポリ
エチレン100重量部に対してポリブデン−1のホモポ
リマー33〜82重量部の割合で混合されてなる樹脂層
で形成されることを特徴とする請求項1〜3のいずれか
に記載の蓋材。
4. The heat-sealing layer is formed of a resin layer obtained by mixing 100 parts by weight of low-density polyethylene with 33 to 82 parts by weight of a homopolymer of polybutene-1. The lid member according to claim 1.
【請求項5】 前記のヒートシール層の厚みが3〜1
0μmの範囲にあることを特徴とする請求項1〜4のい
ずれかに記載の蓋材。
5. The thickness of the heat seal layer is 3 to 1
The lid material according to any one of claims 1 to 4, wherein the lid material is in a range of 0 µm.
【請求項6】 前記のヒートシール層と前記の中間層
とが、共押し出し法による積層体で形成されることを特
徴とする請求項1〜5のいずれかに記載の蓋材。
6. The lid member according to claim 1, wherein the heat seal layer and the intermediate layer are formed as a laminate by a coextrusion method.
JP2002041101A 2002-02-19 2002-02-19 Lid material Pending JP2003237816A (en)