  The present invention relates to a method for vacuum injection molding of a spiral guide plate used in a natural flow type vertical sewer pipe or the like.

  Conventionally, when a sewage flows into a manhole, a drop shaft is provided so that the inflowing water flows down along the inner surface of the side wall of the manhole so that the bottom surface of the manhole is not directly eroded by the falling impact of the inflowing water. . This drop shaft is a vertical tube with a spiral guideway, and while flowing down along the spiral guideway, the flow rate of sewage flowing into the vertical tube is attenuated, and erosion at the bottom of the manhole can be suppressed. ing. In addition, a central tube penetrating the center of the spiral guide path is provided in the drop shaft in order to effectively discharge the air in the pipe upward and allow the sewage to flow smoothly downward.

  For example, Patent Document 1 discloses a configuration of a drop shaft that integrally joins a separately manufactured vertical pipe and a spiral guide path using an adhesive or welding. This type of spiral guide path is intended to be easily manufactured by forming a spiral pitch of 1/4 to 2 pitches, and preferably a relatively short pitch of 1 pitch or less. Further, the helical guide path having such a pitch is formed in a spiral shape by cutting an annular thermoplastic resin plate in the radial direction and deforming the cut ends in directions away from each other.

  Since the spiral guide path of such a drop shaft is a large molded body, it is usually formed by a hand lay-up molding method. The hand lay-up molding method is a manufacturing method that is the basis of a fiber-reinforced resin molded product, in which organic or inorganic fibers (for example, glass fibers, etc.) are disposed in a mold that has been subjected to a release treatment in advance, and a resin composition before curing. The fiber is impregnated manually with a roller or brush and laminated to a predetermined thickness while defoaming to obtain a molded product, which is a method that can be easily performed with a simple tool. Also, in the resin impregnation process, using a spray-up machine, glass roving etc. are sprayed continuously and quantitatively while cutting to a predetermined length, and unsaturated polyester resin etc. are continuously sprayed while mixing the catalyst. Lamination is also performed.

  Such a hand lay-up molding method is a molding method that has been widely used in the past, but the impregnation state of the resin to the reinforcing fiber material must be managed manually, and the quality of the molded product is determined by the skill level of the operator. In addition, there was a concern about the influence on workers and the environment because styrene and the like were volatilized during the work.

Therefore, the present applicant has repeatedly developed a manufacturing method of a spiral guide plate by a molding method instead of the above-mentioned hand lay-up molding method, paying attention to the vacuum injection molding method as a method for solving the styrene volatilization problem, and depends on the skill level. The present application has been invented to enable stable product supply. The basic technique of the vacuum injection molding method is disclosed in Patent Document 2, for example.
Japanese Patent Laid-Open No. 9-292065 Japanese National Patent Publication No. 10-504501

  However, the vacuum injection molding method is a technique used for manufacturing a thin molded product among various molding methods, and is not suitable for a molded product having a thickness of 20 mm or more required for a spiral guide plate. It had been. Further, since the spiral guide plate is large and has a complicated curved surface shape, it is difficult to mold the spiral guide plate, and there is a problem that the surface smoothness of the molded product is lowered.

  The present invention has been made in view of the above circumstances, and has established a method for forming a spiral guide plate of a drop shaft by a vacuum injection molding method capable of realizing surface smoothness while ensuring a required thickness. It is intended to provide a method for forming a spiral guide plate with high product stability that does not require a skilled worker, while suppressing the volatilization of styrene during production and giving consideration to workers and the environment.

To achieve the above object, a molding method of the present invention, the spiral guideways of helical shape which are placed in a vertical tube, spiral guide path joining pieces to be joined in the vertical tube circumference provided we are in the outer peripheral edge of the The spiral guide plate provided with is formed. Then, a portion of the spiral guide path as a first shaping member, the guide path forming surface of the spiral-shaped, and the joining pieces forming surface which has been made a curved surface is vertically on the outer periphery corresponding to the vertical pipe inside diameter of the guide passage forming surface And an upper die having a substantially L-shaped cross section that covers at least the outer edge portion of the guide path forming surface and the upper portion of the joining piece forming surface of the forming die .

  In the present invention, a sheet-like reinforcing fiber material is disposed on the mold, and a release sheet that enhances the mold releasability on the reinforcing fiber material, and a resin diffusion net that promotes diffusion of the injected resin are provided. An injection pipe for injecting resin is disposed on the upper surface of the resin diffusion net. The reinforcing fiber material, release sheet, resin diffusion net, and injection tube are hermetically covered with a bag film on a mold to form a molded part, and a decompression source for decompressing the bag film is connected. Then, a resin is injected into the vacuum molded part and impregnated with the reinforcing fiber material to obtain a molded body.

  Here, the spiral shape of the molding die is formed with a length and a gradient when a part of the spiral guide path is defined as one molded body unit, and the outer shape is a spiral shape such as a substantially circular shape or a substantially semicircular shape when viewed from above. Is done. Specifically, when the spiral guide plate to be molded is installed in a longitudinal pipe having a relatively small diameter, several pitches of the entire spiral guide path are formed as one molded body, and this is molded all at once. Preferably, the mold is a spiral body having a substantially circular shape when viewed from above. Further, when the spiral guide plate to be formed is disposed in a longitudinal pipe having a relatively large diameter, one half of the entire spiral guide path or 1/3 pitch is used as one molded body. It is preferable to mold in a divided spiral shape.

  According to such an invention, a spiral guide plate made of fiber-reinforced plastic, which is a lightweight, high-strength and high-rigidity material, can be manufactured while suppressing volatilization of styrene or the like under stable physical properties. Moreover, since the cost required for the mold investment in the formation of the spiral guide plate can be reduced by the above configuration, stable product supply can be performed at low cost.

  In the vacuum injection molding method having the above-described configuration, the present invention provides an upper die having a substantially L-shaped cross section that covers at least the outer edge portion of the guide path forming surface of the molding die and the upper portion of the joining piece forming surface. It is characterized in that it can be installed to form a molding part and the curved surface of the joining piece can be smoothly molded.

  The upper mold includes a first upper mold having a substantially L-shaped cross section that covers an outer edge portion of the guide path forming surface of the mold and an upper portion of the joint piece forming surface, and a second curved surface that covers the middle portion of the joint piece forming surface. The structure which consists of an upper mold | type may be sufficient.

  In the present invention, the upper mold is configured to extend from the outer edge of the guide path forming surface of the molding die in the direction of the spiral center and along the guide path forming surface, and the upper mold includes the guide path forming surface. A groove extending in the circumferential direction may be formed, and an injection tube may be provided on the groove to allow resin injection.

  According to such an invention, it is possible to efficiently mold the surface of the molded spiral guide plate while ensuring surface smoothness without providing wrinkles or irregularities on the surface.

  Further, in the present invention, the upper die is provided with a pressing member in the circumferential direction outside the portion covering the joining piece forming surface, and the upper die is pressed from the outside of the joining piece forming surface toward the spiral center. You may make it do.

  More specifically, the pressing member is preferably a belt material that follows the outer shape of the upper mold.

  By using such a pressing member, it is possible not only to press the upper mold in the direction of the center of the spiral with a vacuum suction force acting on the bag film, but also to form by directly applying an external force from the pressing member to the upper mold. Therefore, the surface of the formed spiral guide plate can be formed smoothly, and unnecessary creases and wrinkles can be prevented from being formed.

  Furthermore, in the present invention, the reinforcing fiber material is provided with notches at appropriate intervals in the portion provided at the lower part of the joining piece forming surface of the mold, and is provided along the curved surface of the joining piece forming surface. Is preferred. More specifically, it is preferable that the cut is formed by cutting the wedge shape into a wedge shape having a wide lower portion and a narrow upper portion.

  By forming the cuts in this way, the reinforcing fiber material can be arranged smoothly without providing creases, and unnecessary creases and wrinkles are prevented from being formed on the joining pieces of the spiral guide plate, and the smoothness is smooth. It can be formed into a curved surface.

  According to the vacuum guide molding method of the spiral guide plate of the present invention configured as described above, the spiral guide plate used for the drop shaft can be molded regardless of the skill level of the operator, and compared with the conventional molding method. Therefore, it is possible to provide a high-quality spiral guide plate with increased strength while suppressing costs. In addition, according to the present invention, it is possible to easily ensure the necessary thickness for the spiral guide plate, and it is possible to mold without impairing the smoothness of the surface.

  Hereinafter, the best mode for carrying out the vacuum injection molding method for a spiral guide plate according to the present invention will be described with reference to the drawings.

  1 to 5 are explanatory views showing a vacuum injection molding method of the spiral guide plate of the present invention, and FIG. 6 is a cross-sectional view schematically showing the vacuum injection molding method. In FIG. 6, in order to make the drawing easier to see, the cross-sectional hatching is omitted for the constituent members such as the mold and the injection tube.

  In the vacuum injection molding method of the spiral guide plate of the present invention, the spiral guide path can be joined to the spiral upper surface guide path installed in the vertical pipe and the outer peripheral edge of the guide path to the inner peripheral surface of the vertical pipe. It is applied to a device provided with a curved joining piece.

  In the illustrated embodiment, the molding die 1 is used in which a unit corresponding to 1/2 pitch of the spiral guide path is used. As shown in FIG. 1, the mold 1 includes a semi-spiral guide path forming surface 11 and a joint that is provided on the outer peripheral edge of the guide path forming surface 11 and has a curved surface corresponding to the inner diameter of the vertical pipe. The shape is provided with a piece forming surface 12. The material of the mold 1 used here may be any material such as fiber reinforced resin, synthetic resin, metal, and the like, and is appropriately selected according to the fluidity and demolding property of the injected resin.

  The spiral guide plate is formed by first disposing the sheet-like reinforcing fiber material 2 on the mold 1. The reinforcing fiber material 2 is preferably a woven or non-woven fabric such as glass fiber or carbon fiber. In the illustrated form, the sheet-like reinforcing fiber material 2 has a notch 21 having an appropriate length from the lower edge of the reinforcing fiber material 2 at a portion disposed below the joining piece forming surface 12 of the mold 1. Are provided at a plurality of locations. That is, the cuts 21 are formed in the boundary corner portion between the guide path of the spiral guide plate and the joining piece within a range in which the strength of the molded body can be ensured.

  As shown in the figure, the reinforcing fiber material 2 is laid on the guide path forming surface 11 of the mold 1, and the notch 21 is overlapped on the joining piece forming surface 12. Thereby, it can arrange | position smoothly on the joining piece formation surface 12 without attaching a crease to the reinforced fiber material 2, and the joining piece formation surface 12 can be formed without forming unnecessary creases and wrinkles on the joining piece of the spiral guide plate. The reinforcing fiber material 2 can be disposed with a predetermined thickness along the curved surface.

  Next, as shown in FIG. 2, a release sheet 3 is laid on the mold 1 on which the reinforcing fiber material 2 is disposed. The release sheet 3 enhances the release property of the cured injection resin, and a sheet made of an injection resin and a non-adhesive material is preferable.

  Next, as shown in FIG. 3, a resin diffusion net 4 is laid on the release sheet 3. The resin diffusion net 4 promotes the diffusion of the injected resin. The resin diffusion net 4 impregnates the injected resin into the reinforcing fiber material 2 evenly and can diffuse the injected resin over the entire desired range on the mold 1. A sheet material is preferred.

  An injection resin injection tube 9 is disposed on the upper surface of the resin diffusion net 4. As the injection tube 9, for example, a porous conduit having a hollow cross section, a conduit formed by spirally winding a long strip member, and the like are preferable. Such an injection tube 9 is installed with an adhesive material, a seal tape, or the like at an appropriately installable position such as the upper surface, the end of the mold 1 or the inside of the mold.

  Subsequently, the upper mold 5 is installed on the mold 1 on which the release sheet 3 and the resin diffusion net 4 are laid. The upper mold 5 has an outer shape slightly larger than that of the mold 1 and is formed so as to cover at least the outer edge portion of the guide path forming surface 11 and the upper portion of the joining piece forming surface 12 of the mold 1. The cross section along the line is substantially L-shaped. The illustrated upper mold 5 is formed to have a size that covers the vicinity of the outer edge of the guide path forming surface 11 of the mold 1 and covers the upper half of the joining piece forming surface 12.

  Further, as illustrated in FIG. 4, the upper mold may be an upper mold in which a curved surface covering the joining piece forming surface 12 is divided into upper and lower parts. The upper mold includes a first upper mold 5a having a substantially L-shaped cross-section that covers the outer edge of the guide path forming surface 11 of the mold 1 and the upper portion of the joining piece forming surface 12, and a middle part of the joining piece forming surface 12. It is composed of a curved upper second mold 5b. When the mold 1 is large, the upper molds 5a and 5b that are divided in this way are easy to work and a good molded body can be obtained.

  Such upper molds 5, 5 a, 5 b may be made of any material such as fiber reinforced resin, synthetic resin (for example, PVC), iron, or synthetic rubber. It is appropriately selected depending on the sex.

  After the upper mold 5 is installed on the mold 1 as shown in FIG. 3, the mold 1 is hermetically covered with the bag film 6 as shown in FIG. 5. The bag film 6 is not particularly limited as long as it is an airtight synthetic resin film material generally used in this type of vacuum injection molding method. Then, the bag film 6 is fixed to the surface of the mold 1 by using a sealing material 7 such as an adhesive material or a seal tape at the peripheral edge of the mold 1. Thereby, between the shaping | molding die 1 and the bag film 6 is comprised as an airtight and sealed shaping | molding part. Further, a decompression source 8 is connected to the end portion of the mold 1 covered with the bag film 6 to suck in the air in the molded portion and depressurize it (see FIG. 6).

  In injecting the resin, the reduced pressure source 8 depressurizes the inside of the molded part of the bag film 6 to make a vacuum state. And resin is inject | poured from the injection | pouring pipe | tube 9 and it diffuses in a shaping | molding part. As the injection resin, for example, a low-viscosity vinyl ester resin, an unsaturated polyester resin, an epoxy resin, and the like are preferable. Further, the viscosity of the injected resin is preferably 0.2 Pa · s (= 2 Poise) or less, and if the viscosity exceeds this, the resin impregnation property to the reinforcing fiber material may be inferior.

  The injected resin is evenly diffused throughout the molded portion through the resin diffusion net 4 and impregnated into the reinforcing fiber material 2. At this time, since the upper die 5 is installed inside the bag film 6, the boundary corner portion between the guide path and the joining piece and the curved surface of the joining piece can be smoothly formed along the forming die 1. When the resin injection is completed, the injected resin is cured while maintaining the vacuum state in the molded portion, and thereby, the resin is impregnated and integrated with the reinforcing fiber material. After removing the solidified molded body from the mold 1, the edge of the molded body can be trimmed to obtain one molded body of the spiral guide plate. The spiral guide plate is formed by joining a plurality of the formed bodies thus formed.

Thus, according to the vacuum injection molding method of the spiral guide plate according to the present invention, a number that is the thickness and the laminated reinforcing fiber material 2, it is possible to secure a required thickness in a helical guide plate, the guide path Even in a complicated shape of a spiral shape having a bonding piece and a joining piece, a molded body can be stably produced without impairing the smoothness of the surface. In addition, since the physical properties can be stabilized compared to conventional molding methods, the product strength can be increased, and a high-quality spiral guide plate can be formed regardless of the skill level of the operator. The volatilization problem such as can be solved.

  Next, Example 1 in the vacuum injection molding method of the spiral guide plate according to the present invention will be described with reference to the drawings.

  FIG. 7 is an explanatory view showing a vacuum injection molding method of a spiral guide plate according to an embodiment of the present invention, FIG. 8 is a plan view showing an example of a reinforcing fiber material to be arranged, and FIG. 9 is an arrangement of injection pipes It is explanatory drawing which shows an example of a form.

  In the following description, the same components as those described above are not described repeatedly, and the same reference numerals are used to replace the description.

  Also in this embodiment, similarly to the above-described method for forming the spiral guide plate, first, a sheet-like reinforcing fiber material 2 having an appropriate thickness and number is laminated on the mold 1 to form the spiral guide plate. Is advanced. As shown in FIG. 8, in the embodiment, the reinforcing fiber material 2 has a notch 21 a provided in the lower part of the joining piece forming surface 12 of the mold 1, and is cut into a wedge shape with the lower part being wider and the upper part being narrower. Is formed. Further, the reinforcing fiber material 2 is in a state where the wedge-shaped cuts 21a are cut to the part disposed at the boundary between the upper joining piece forming surface 12 and the guide path forming surface 11 at the edge. Is formed.

  For example, the notches 21a of the reinforcing fiber material 2 are preferably provided at an interval of about 100 mm. In the case of forming a spiral guide plate having a vertical tube diameter of 1650 mm and a width of 550 mm as an example, The cut depth may be formed by the length of the entire joining piece forming surface 12 in the height direction.

  The reinforcing fiber material 2 is disposed so that the edges of the notches 21a formed in such a wedge shape are brought into contact with each other. Thereby, the reinforcing fiber material 2 can be smoothly arranged along the joining piece forming surface 12 of the mold 1, and unnecessary creases and wrinkles are formed on the joining pieces of the formed spiral guide plate. Can be prevented.

  Next, the release sheet 3 and the resin diffusion net 4 are laid on the mold 1 on which the reinforcing fiber material 2 is disposed. Further, an injection resin injection tube is disposed on the upper surface of the resin diffusion net 4 in the circumferential direction of the guide path forming surface 11.

  In the illustrated embodiment, three injection pipes 91, 92, and 93 are arranged in the circumferential direction. As the injection pipes 91, for example, a porous conduit having a hollow cross section, a conduit formed by spirally winding a long strip member, and the like are preferable. In addition, the injection pipes 91, 92, 93 are arranged at an equal interval of about 100 mm.

  In this case, the upper mold 5 as described above is installed on the resin diffusion net 4, but demolding is easy by arranging the release sheet 3 between the resin diffusion net 4 and the upper mold 5. This is preferable.

  Further, when the first upper mold 5a described above is used, the first upper mold 5a having a substantially L-shaped cross section so as to press down the outer edge portion of the guide path forming surface 11 and the upper portion of the joining piece forming surface 12 of the mold 1 is used. 1 Upper mold 5a is installed. Furthermore, by using the second upper mold 5b having a shape along the joining piece forming surface 12, the smoothness of the surface of the molded body can be improved. When the second upper mold 5b is used, the resin flowing out from the injection pipe 91 is good for the reinforcing fiber material 2 through the resin diffusion net 4 and the release sheet 3 by providing grooves in the circumferential direction of the curved surface. Can be impregnated.

  On the reinforcing fiber material 2, the release sheet 3, the resin diffusion net 4, and the injection tube 9 laid in this way, a molded part in a state where the bag film 6 is covered and is hermetically sealed on the mold 1. Composed. At the periphery of the mold 1, the bag film 6 and the surface of the mold 1 are hermetically fixed by the sealing material 7, and a decompression pipe connected to an appropriate decompression source 8 is disposed.

  The resin injection into the molding part is performed by reducing the pressure inside the back film 6 by the reduced pressure source 8 and making it vacuum, and then injecting the resin from each injection tube 9 and diffusing it into the molding part. At this time, resin injection is started in order from the injection pipes 91 arranged closest to the center in the width direction among the three injection pipes 91, 92, 93 arranged in the circumferential direction.

  Subsequently, resin injection from the injection pipes 92 and 93 disposed on both sides thereof is started simultaneously. The time difference at the start of injection between the injection pipe 91 that has started the resin injection and the injection pipes 92 and 93 that have started the resin injection later is appropriately determined depending on the degree of impregnation of the injection resin into the reinforcing fiber material 2. That is, since the resin impregnation property varies depending on the thickness required for the spiral guide plate to be molded and the viscosity of the injected resin, the resin is injected with a time difference corresponding to the impregnation property.

  For example, when the required thickness of the spiral guide plate to be molded is 30 mm, the time difference for starting the resin injection between the injection pipes 91 and the injection pipes 92 and 93 arranged at intervals of 100 mm is about 5 minutes. . It is preferable to delay the start of resin injection into the injection tube toward the outer side in the width direction of the guide path forming surface 11 of the mold 1.

  As a result, the injection resin is drawn from the injection pipes 91 in the direction of the peripheral edge of the mold 1 and diffused radially in cross section around the injection pipes 91 and impregnated into the reinforcing fiber material 2 via the resin diffusion net 4. To do. Therefore, by sequentially injecting the resin with a time difference as described above, the resin begins to be impregnated in order from the periphery of the injection pipe 91 disposed at the position farthest from the peripheral portion where the decompression pipe is disposed. Thus, the resin around the injection pipes 92 and 93 is impregnated.

  When the resin injection is finished from all of the injection pipes 91..., The resin is uniformly diffused throughout the molded portion, and the reinforcing fiber material 2 can be impregnated.

  Thus, according to the vacuum injection molding method of the spiral guide plate according to the present embodiment, the injection resin is diffused uniformly and efficiently over the entire molded part without producing an unimpregnated portion even in a short injection time. A molded body can be obtained. Further, by providing the cut 21a of the reinforcing fiber material 2 in a wedge shape as described above, unnecessary creases and wrinkles are prevented from being formed on the joining piece of the spiral guide plate, and the surface smoothness is not impaired. A desired spiral guide plate can be formed.

  In addition, the injection pipes arranged in the circumferential direction of the guide path forming surface are not limited to three as described above, but are appropriately determined according to the diameter of the vertical pipe and the width of the spiral guide plate to be formed, Two or four or more may be used.

  Next, Example 2 in the vacuum injection molding method of the spiral guide plate according to the present invention will be described with reference to the drawings. 10 is an explanatory view showing a vacuum injection molding method of the spiral guide plate according to the second embodiment of the present invention, and FIG. 11 schematically shows the vacuum injection molding method of FIG. 10 by a cross section in the width direction (radial direction). FIG.

  The vacuum injection molding method of this embodiment is characterized by an upper mold 5c installed on a molding die 1 in which a reinforcing fiber material 2, a release sheet 3, and a resin diffusion net 4 are laid in order. Therefore, in the following description, the upper mold 5c will be described with emphasis, and the description of the same components as those in the above embodiment will be avoided, and the description will be replaced by using the same reference numerals. To do.

  The upper mold 5c in this embodiment is integrally formed with a substantially L-shaped cross section so as to press down the guide path forming surface 11 and the upper part of the joining piece forming surface 12 of the mold 1. That is, the upper mold 5c extends from the vicinity of the outer edge of the guide path forming surface 11 toward the center of the spiral so as to cover almost the entire upper surface of the guide path forming surface 11 on the upper surface side of the guide path forming surface 11. It is installed. Further, the outer surface side of the joining piece forming surface 12 is formed in a size that can cover at least the upper portion of the joining piece forming surface 12.

  As shown in FIG. 10, the upper mold 5c is formed with three grooves 51 extending in the circumferential direction at equal intervals in a portion disposed on the upper surface side of the guide path forming surface 11. Each groove 51 is provided in a slit shape with a groove width that is slightly smaller than the diameter of the injection tube 9 disposed along the groove 51 (see FIG. 11). As a result, the injection tube 9 can be stably disposed in the circumferential direction on the groove 51, and resin can be injected.

  Furthermore, in the illustrated embodiment, a pressing member 52 is disposed in the circumferential direction on the outer side of the upper mold 5c that covers the bonding piece forming surface 12. The pressing member 52 is disposed along the outer shape of the upper mold 5c so that the guide path forming surface 11 of the molding mold 1 can be pressed in the spiral center direction from the outside of the upper mold 5c.

  For the pressing member 52, it is preferable to use a belt made of a material such as a polyester resin, a polyamide resin such as nylon, or a polyolefin resin such as polypropylene. And it is comprised so that such a pressing member 52 may be fastened to the shaping | molding die 1 in the state along the upper mold | type 5c, and a pressure may be given to a spiral center direction during shaping | molding. And after installing the upper mold | type 5c in the shaping | molding die 1, these outer sides are coat | covered with the bag film 6, the airtight inside of the bag film 6 is ensured using a sealing material, and a shaping | molding part is formed.

  Thereby, not only can the upper die 5c be pressed in the direction of the center of the spiral by the vacuum suction force acting on the bag film 6, but an external force can be directly applied from the pressing member 52 to the upper die 5c. It is possible to prevent the formation of unnecessary folds and wrinkles on the joining piece, and to ensure surface smoothness.

  The pressing member 52 may be fixed by using a fastening band made of a metal such as SUS or a general-purpose wire instead of a belt, and the pressing direction of the upper mold 5c is also in the spiral center direction. It is not limited only to this, For example, the hanging direction of the joining piece formation surface 12 and the diagonally inner direction may be sufficient.

  INDUSTRIAL APPLICABILITY The present invention can be used to manufacture a pipe with an inner surface spiral guide path suitable for use in a natural flow vertical sewer pipe or the like.

It is explanatory drawing which shows the vacuum injection molding method of the spiral guide plate which concerns on this invention. It is explanatory drawing which shows the next procedure of FIG. FIG. 3 is an explanatory diagram showing a procedure subsequent to FIG. 2. It is explanatory drawing which shows the other form of the upper mold | type in the vacuum injection molding method of the spiral guide plate of this invention. FIG. 4 is an explanatory diagram showing a procedure subsequent to FIG. 3. It is sectional drawing which shows typically the vacuum injection molding method of the spiral guide plate which concerns on this invention. It is explanatory drawing which shows the vacuum injection molding method of the spiral guide plate which concerns on Example 1 of this invention. 1 is a plan view showing an example of a reinforcing fiber material disposed in Example 1. FIG. It is explanatory drawing which shows an example of the arrangement | positioning form of the injection tube in Example 1. FIG. It is explanatory drawing which shows the vacuum injection molding method of the spiral guide plate which concerns on Example 2 of this invention. It is sectional drawing of the spiral center direction which showed the vacuum injection molding method of Example 2 typically.

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 Molding die 11 Guide path formation surface 12 Joining piece formation surface 2 Reinforcing fiber material 21,21a Cut 3 Release sheet 4 Resin diffusion net 5 Upper die 5a First upper die 5b Second upper die 5c Upper die 51 Groove 52 Holding member 6 Bag film 7 Sealing material 8 Depressurization source 9 Injection pipe 91, 92, 93 Injection pipe

Claims (5)

A helical guide path of helical shape which are placed vertically pipe, a molding method for molding a helical guide plate having a junction piece which is joined to the outer peripheral edge provided we are in a vertical tube circumferential surface of the spiral guideways ,
A portion of the spiral guide path as a first shaping member,
A mold having a spiral guide path forming surface , and a joining piece forming surface that is suspended from the outer peripheral edge of the guide path forming surface and has a curved surface corresponding to the inner diameter of the longitudinal pipe ;
Using an upper die having a substantially L-shaped cross section that covers at least the outer edge portion of the guide path forming surface of the molding die and the upper portion of the joining piece forming surface ,
A sheet-like reinforcing fiber material is disposed on the mold, and a release sheet that enhances the releasability of the molded body on the reinforcing fiber material, and a resin diffusion net that promotes diffusion of the injected resin are laid in order. An injection tube for injecting resin on the upper surface of the resin diffusion net and the upper mold are disposed,
These reinforcing fiber material, the release sheet, the resin distribution network, infusion tube, and the upper mold was coated in an airtight manner on the mold to form a molded part by bag film, to connect the vacuum source for reducing the pressure within the bag film A method for vacuum injection molding of a spiral guide plate, comprising: injecting a resin into a molded part having a reduced pressure, and impregnating and integrating the injected resin into a reinforcing fiber material to obtain a molded body. In the vacuum injection molding method of the spiral guide plate according to claim 1,
The upper mold is
A first upper die having a substantially L-shaped cross section covering an outer edge portion of the guide path forming surface of the molding die and an upper portion of the joining piece forming surface;
A vacuum injection molding method for a spiral guide plate, comprising: a second upper mold having a curved surface covering a middle portion of a joining piece forming surface . In the vacuum injection molding method of the spiral guide plate according to claim 1,
The upper mold is configured to extend along the guide path forming surface from the outer edge of the guide path forming surface of the mold and extend along the guide path forming surface. The upper mold has a circumferential direction with respect to the guide path forming surface. A method for vacuum injection molding of a spiral guide plate, characterized in that a groove extending in the groove is formed, and an injection tube is disposed on the groove to allow resin injection . In the vacuum injection molding method of the spiral guide plate according to any one of claims 1 to 3,
The upper mold is characterized in that a pressing member is disposed in the circumferential direction outside the portion covering the joining piece forming surface, and the upper die is pressed from the outside of the joining piece forming surface toward the spiral center. A vacuum injection molding method for a spiral guide plate. In the vacuum injection molding method of the spiral guide plate according to claim 4,
The method for vacuum injection molding of a spiral guide plate, wherein the pressing member is a belt material along the outer shape of the upper mold .