JP4933568B2 - Photocatalyst-coated body and photocatalyst coating liquid therefor - Google Patents
Photocatalyst-coated body and photocatalyst coating liquid therefor Download PDFInfo
- Publication number
- JP4933568B2 JP4933568B2 JP2009003050A JP2009003050A JP4933568B2 JP 4933568 B2 JP4933568 B2 JP 4933568B2 JP 2009003050 A JP2009003050 A JP 2009003050A JP 2009003050 A JP2009003050 A JP 2009003050A JP 4933568 B2 JP4933568 B2 JP 4933568B2
- Authority
- JP
- Japan
- Prior art keywords
- photocatalyst
- parts
- particles
- mass
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、建築物等の外装材の用途に特に適した、透明度が高く、耐候性、有害ガス分解性、および各種被膜特性に優れた光触媒層を備えた光触媒塗装体およびそのための光触媒コーティング液に関する。 The present invention is a photocatalyst-coated body provided with a photocatalyst layer having a high transparency, weather resistance, harmful gas decomposability, and various coating properties, and a photocatalyst coating liquid therefor, which are particularly suitable for the use of exterior materials such as buildings. About.
酸化チタンなどの光触媒が、建築物の外装材など多くの用途において近年利用されている。光触媒の利用により、光エネルギーを利用して種々の有害物質を分解したり、あるいは、光触媒が塗布された基材表面を親水化して表面に付着した汚れを容易に水で洗い流すことが可能となる。このような光触媒を塗布した光触媒塗装体を得る技術としては、以下のものが知られている。 In recent years, photocatalysts such as titanium oxide have been used in many applications such as exterior materials for buildings. By using photocatalyst, it is possible to decompose various harmful substances using light energy, or to make the surface of the substrate coated with photocatalyst hydrophilic and easily wash away dirt adhering to the surface with water. . The following are known as techniques for obtaining a photocatalyst-coated body coated with such a photocatalyst.
光触媒性金属酸化物粒子と、コロイダルシリカと、界面活性剤とを含有する水性分散液を用いて、合成樹脂等の表面に親水性を付与する技術が知られている(例えば、特許文献1(特開平11−140432号公報)参照)。この技術にあっては、界面活性剤を10〜25重量%と多量に含有させることにより親水性を強化している。また、膜厚を0.4μm以下とすることで光の乱反射による白濁を防止している。 A technique for imparting hydrophilicity to the surface of a synthetic resin or the like using an aqueous dispersion containing photocatalytic metal oxide particles, colloidal silica, and a surfactant is known (for example, Patent Document 1 ( (See JP-A-11-14432). In this technique, hydrophilicity is enhanced by containing a surfactant in a large amount of 10 to 25% by weight. Moreover, the cloudiness by the irregular reflection of light is prevented by making a film thickness into 0.4 micrometer or less.
バインダー成分としてのシリカゾルと光触媒性二酸化チタンとを含有する塗膜を基体に形成して光触媒体を得る技術も知られている(例えば、特許文献2(特開平11−169727号公報)参照)。この技術にあっては、シリカゾルの添加量がSiO2基準で二酸化チタンに対して20〜200重量部であるとされており、二酸化チタンの含有比率が高い。また、シリカゾルの粒径も0.1〜10nmと小さい。 A technique for obtaining a photocatalyst by forming a coating film containing silica sol as a binder component and photocatalytic titanium dioxide on a substrate is also known (see, for example, Patent Document 2 (Japanese Patent Laid-Open No. 11-169727)). In this technique, the amount of silica sol added is 20 to 200 parts by weight with respect to titanium dioxide on the basis of SiO2, and the content ratio of titanium dioxide is high. In addition, the particle size of silica sol is as small as 0.1 to 10 nm.
光触媒塗料を用いて波長500nmの光を50%以上透過させ、かつ、320nmの光を80%以上遮断すること光触媒塗膜を形成する技術も知られている(例えば、特許文献3(特開2004−359902号公報)参照)。この技術にあっては、光触媒塗料のバインダーとしてオルガノシロキサン部分加水分解物が用いられており、その配合量は塗料組成物全体の5〜40質量%が好ましいとされている。 There is also known a technique for forming a photocatalyst coating film that transmits 50% or more of light having a wavelength of 500 nm and blocks 80% or more of light having a wavelength of 320 nm using a photocatalyst coating (for example, Patent Document 3 (Japanese Patent Application Laid-Open No. 2004-2004)). No. -359902)). In this technique, an organosiloxane partial hydrolyzate is used as a binder of a photocatalyst coating material, and the blending amount is preferably 5 to 40% by mass of the entire coating composition.
ところで、光触媒層の基材を有機材料で構成すると、光触媒の光触媒活性により有機材料が分解あるいは劣化されるという問題が従来から知られている。この問題に対処するため、光触媒層と担体との間にシリコン変性樹脂等の接着層を設けることで、下地の担体を光触媒作用による劣化から保護する技術が知られている(例えば、特許文献4(国際公開第97/00134号パンフレット)参照)。 By the way, when the base material of a photocatalyst layer is comprised with an organic material, the problem that an organic material is decomposed | disassembled or deteriorated by the photocatalytic activity of a photocatalyst is known conventionally. In order to cope with this problem, a technique for protecting an underlying carrier from deterioration due to photocatalysis by providing an adhesive layer such as a silicon-modified resin between the photocatalyst layer and the carrier is known (for example, Patent Document 4). (See WO 97/00134 pamphlet).
本発明者らは、今般、光触媒粒子と無機酸化物粒子とを特定の質量比率で含み、なおかつ加水分解性シリコーンを含まないか又は極力少量に抑えた特定の組成で光触媒層を構成することにより、基材(特に有機基材)への浸食を抑制しながら、耐候性、有害ガス分解性、および所望の各種被膜特性(紫外線吸収性、透明性、膜強度等)に優れた光触媒塗装体が得られるとの知見を得た。 The inventors of the present invention have recently constituted a photocatalyst layer with a specific composition containing photocatalyst particles and inorganic oxide particles at a specific mass ratio and containing no hydrolyzable silicone or keeping the amount as small as possible. A photocatalyst-coated body excellent in weather resistance, harmful gas decomposability, and various desired film properties (ultraviolet absorption, transparency, film strength, etc.) while suppressing erosion to the substrate (especially organic substrate) The knowledge that it was obtained was obtained.
したがって、本発明の目的は、基材(特に有機基材)に対する浸食を防止しながら、耐候性、有害ガス分解性、および所望の各種被膜特性(紫外線吸収性、透明性、膜強度等)に優れた光触媒層を備えた光触媒塗装体およびそのための光触媒コーティング液を提供することにある。 Accordingly, the object of the present invention is to provide weather resistance, harmful gas decomposability, and various desired film properties (ultraviolet absorption, transparency, film strength, etc.) while preventing erosion of the substrate (especially organic substrate). An object of the present invention is to provide a photocatalyst-coated body having an excellent photocatalyst layer and a photocatalyst coating liquid therefor.
すなわち、本発明による光触媒塗装体は、基材と、該基材上に設けられた光触媒層とを備えた、光触媒塗装体であって、
前記光触媒層が、
5質量部以上15質量部以下の、10nm以上100nm以下の平均粒径を有する光触媒粒子と、
75質量部を超え95質量部以下の無機酸化物粒子と、
シリカ換算で0質量部以上10質量部未満の加水分解性シリコーンの乾燥物と
を、前記光触媒粒子、前記無機酸化物粒子、および前記加水分解性シリコーンのシリカ換算量の合計量が100質量部となるように含み、さらに界面活性剤を0質量部以上10質量部以下含んでなるものである。
That is, the photocatalyst-coated body according to the present invention is a photocatalyst-coated body including a base material and a photocatalyst layer provided on the base material,
The photocatalytic layer is
5 to 15 parts by mass of photocatalyst particles having an average particle diameter of 10 to 100 nm,
More than 75 parts by weight and less than 95 parts by weight of inorganic oxide particles;
A hydrolyzable silicone dry matter having a weight of 0 to less than 10 parts by weight in terms of silica, and the total amount of silica equivalents of the photocatalyst particles, the inorganic oxide particles, and the hydrolyzable silicone is 100 parts by weight. And a surfactant is further contained in an amount of 0 to 10 parts by mass.
また、本発明による光触媒コーティング液は、上記光触媒塗装体の製造に用いられる光触媒コーティング液であって、
溶媒と、
5質量部以上15質量部以下の、10nm以上100nm以下の平均粒径を有する光触媒粒子と、
75質量部を超え95質量部以下の無機酸化物粒子と、
シリカ換算で0質量部以上10質量部未満の加水分解性シリコーンと
を、前記光触媒粒子、前記無機酸化物粒子、および前記加水分解性シリコーンのシリカ換算量の合計量が100質量部となるように含み、さらに界面活性剤を0質量部以上10質量部以下含んでなるものである。
Moreover, the photocatalyst coating liquid according to the present invention is a photocatalyst coating liquid used for producing the photocatalyst-coated body,
A solvent,
5 to 15 parts by mass of photocatalyst particles having an average particle diameter of 10 to 100 nm,
More than 75 parts by weight and less than 95 parts by weight of inorganic oxide particles;
From 0 parts by mass to less than 10 parts by mass of hydrolyzable silicone in terms of silica, the total amount of silica equivalents of the photocatalyst particles, the inorganic oxide particles, and the hydrolyzable silicone is 100 parts by mass. And a surfactant is further contained in an amount of 0 to 10 parts by mass.
光触媒塗装体
本発明による光触媒塗装体は、基材と、この基材上に設けられる光触媒層とを備えてなる。光触媒層は、波長550nmの光の直線透過率が95%以上であり、5質量部以上15質量部以下の、10nm以上100nm以下の平均粒径を有する光触媒粒子と、75質量部を超え95質量部以下の無機酸化物粒子と、任意成分として、シリカ換算で0質量部以上10質量部未満の加水分解性シリコーンの乾燥物とを含んでなる。ここで、光触媒粒子、無機酸化物粒子、および加水分解性シリコーンのシリカ換算量の合計量を100質量部とする。
Photocatalyst-coated body The photocatalyst-coated body according to the present invention comprises a base material and a photocatalyst layer provided on the base material. The photocatalyst layer has a linear transmittance of 95% or more for light having a wavelength of 550 nm, and has an average particle diameter of 10 nm or more and 100 nm or less, 5 parts by mass or more and 15 parts by mass or less, and more than 75 parts by mass and 95 parts by mass. Part or less of inorganic oxide particles and, as an optional component, 0 part by mass or more and less than 10 parts by mass of a hydrolyzable silicone dry matter in terms of silica. Here, the total amount of photocatalyst particles, inorganic oxide particles, and hydrolyzable silicone in terms of silica is 100 parts by mass.
すなわち、本発明による5質量部以上15質量部以下の、10nm以上100nm以下の平均粒径を有する光触媒粒子と、75質量部を超え95質量部以下の無機酸化物粒子とから基本的に構成される。この構成により、基材(特に有機基材)に対する浸食を防止しながら、耐候性、有害ガス分解性、および所望の各種被膜特性(紫外線吸収性、透明性、膜強度等)に優れた光触媒塗装体を得ることが可能となる。これらの幾つもの優れた効果が同時に実現される理由は定かではないが、以下のようなものではないかと考えられる。ただし、以下の説明はあくまで仮説にすぎず、本発明は何ら以下の仮説によって限定されるものではない。まず、光触媒層は、光触媒粒子および無機酸化物粒子の二種類の粒子から基本的に構成されるため、粒子間の隙間が豊富に存在する。光触媒層のバインダーとして広く用いられる加水分解性シリコーンを多量に使用した場合にはそのような粒子間の隙間を緻密に埋めてしまうため、ガスの拡散を妨げるものと考えられる。しかし、本発明の光触媒層は加水分解性シリコーンを含まないか、含むとしても光触媒粒子、無機酸化物粒子、および加水分解性シリコーンの合計量100質量部に対して10質量部未満としているため、粒子間の隙間を十分に確保することができると考えられる。そして、そのような隙間によってNOxやSOx等の有害ガスが光触媒層中に拡散しやすい構造が実現され、その結果、有害ガスが光触媒粒子と効率良く接触して光触媒活性により分解されるのでないかと考えられる。 That is, it is basically composed of 5 parts by mass or more and 15 parts by mass or less of photocatalyst particles having an average particle diameter of 10 nm or more and 100 nm or less, and inorganic oxide particles of more than 75 parts by mass and 95 parts by mass or less. The With this configuration, photocatalyst coating with excellent weather resistance, harmful gas decomposability, and various desired coating properties (ultraviolet absorption, transparency, film strength, etc.) while preventing erosion of substrates (especially organic substrates) The body can be obtained. The reason why these excellent effects are realized at the same time is not clear, but is thought to be as follows. However, the following description is merely a hypothesis, and the present invention is not limited by the following hypothesis. First, since the photocatalyst layer is basically composed of two types of particles, photocatalyst particles and inorganic oxide particles, there are abundant gaps between the particles. When a large amount of hydrolyzable silicone widely used as a binder for the photocatalyst layer is used, it is considered that the gap between the particles is densely filled, and thus gas diffusion is hindered. However, the photocatalyst layer of the present invention does not contain hydrolyzable silicone or even if it contains less than 10 parts by mass with respect to 100 parts by mass of the total amount of photocatalyst particles, inorganic oxide particles, and hydrolyzable silicone, It is considered that a sufficient gap between particles can be secured. Such a gap realizes a structure in which harmful gases such as NOx and SOx are likely to diffuse into the photocatalyst layer, and as a result, the harmful gas may be efficiently contacted with the photocatalyst particles and decomposed by the photocatalytic activity. Conceivable.
同時に、光触媒粒子の配合割合が無機酸化物粒子よりもかなり少ないことで、光触媒粒子の基材との直接的な接触を最小限に抑えることができ、それにより基材(特に有機基材)を浸食しにくくなるものと考えられる。また、光触媒自体による紫外線吸収によって基材に到達する紫外線量を低減して紫外線による基材の損傷も低減できると考えられる。その結果、本発明の光触媒層は少なくともその表面が有機材料で形成された基材に対しても、基材保護のための中間層を介在させることなく、直接塗布して形成することができる。したがって、中間層の形成が不要となる分、光触媒塗装体の製造に要する時間やコストを削減できる。そして、上記したような種々の現象が同時に起こることで、基材(特に有機基材)に対する浸食を防止しながら、耐候性、有害ガス分解性、および所望の各種被膜特性(紫外線吸収性、透明性、膜強度等)に優れた光触媒塗装体が実現されるものと考えられる。 At the same time, the proportion of photocatalyst particles is considerably less than that of inorganic oxide particles, so that direct contact of the photocatalyst particles with the substrate can be minimized, thereby reducing the substrate (especially organic substrate). It is thought that it becomes difficult to erode. Further, it is considered that the amount of ultraviolet rays reaching the substrate can be reduced by the ultraviolet absorption by the photocatalyst itself, and damage to the substrate due to ultraviolet rays can be reduced. As a result, the photocatalyst layer of the present invention can be directly applied to a substrate having at least a surface formed of an organic material without interposing an intermediate layer for protecting the substrate. Therefore, the time and cost required for manufacturing the photocatalyst-coated body can be reduced by the amount that the intermediate layer is not required. The various phenomena described above occur simultaneously, preventing erosion of the base material (especially organic base material), weather resistance, harmful gas decomposability, and various desired film properties (ultraviolet absorption, transparent It is considered that a photocatalyst-coated body excellent in properties, film strength, etc. is realized.
また、波長550nmにおいての光触媒層の直線透過率を95%以上確保することで下地の色味、意匠を損なうことなく表現することが可能となる。また透明度の高いガラスやプラスチックなどにコーティングしても透明性を損なわずに済む。 In addition, by ensuring 95% or more of the linear transmittance of the photocatalyst layer at a wavelength of 550 nm, it is possible to express without impairing the color and design of the base. Moreover, even if it is coated on highly transparent glass or plastic, the transparency is not impaired.
基材
本発明に用いる基材は、その上に光触媒層を形成可能な材料であれば無機材料、有機材料を問わず種々の材料であってよく、その形状も限定されない。材料の観点からみた基材の好ましい例としては、金属、セラミック、ガラス、プラスチック、ゴム、石、セメント、コンクリ−ト、繊維、布帛、木、紙、それらの組合せ、それらの積層体、それらの表面に少なくとも一層の被膜を有するものが挙げられる。用途の観点からみた基材の好ましい例としては、建材、建物外装、窓枠、窓ガラス、構造部材、乗物の外装及び塗装、機械装置や物品の外装、防塵カバー及び塗装、交通標識、各種表示装置、広告塔、道路用遮音壁、鉄道用遮音壁、橋梁、ガードレ−ルの外装及び塗装、トンネル内装及び塗装、碍子、太陽電池カバー、太陽熱温水器集熱カバー、ビニールハウス、車両用照明灯のカバー、屋外用照明器具、台及び上記物品表面に貼着させるためのフィルム、シート、シール等といった外装材全般が挙げられる。
Base Material The base material used in the present invention may be various materials regardless of inorganic materials or organic materials as long as it can form a photocatalyst layer thereon, and the shape is not limited. Preferred examples of the substrate from the viewpoint of materials include metals, ceramics, glass, plastics, rubber, stones, cement, concrete, fibers, fabrics, wood, paper, combinations thereof, laminates thereof, Examples thereof include those having at least one layer of coating on the surface. Preferred examples of base materials from the viewpoint of applications include building materials, building exteriors, window frames, window glass, structural members, exteriors and coatings of vehicles, exteriors of machinery and articles, dust covers and coatings, traffic signs, and various displays Equipment, advertising towers, road noise barriers, railway noise barriers, bridges, guard rail exteriors and paintings, tunnel interiors and paintings, insulators, solar cell covers, solar water heater heat collection covers, plastic houses, vehicle lighting covers General exterior materials such as outdoor lighting fixtures, stands, and films, sheets, seals and the like for attaching to the article surface.
本発明の好ましい態様によれば、基材として、少なくともその表面が有機材料で形成された基材を用いることができ、基材全体が有機材料で構成されているもの、無機材料で構成された基材の表面が有機材料で被覆されたもの(例えば化粧板)のいずれをも包含する。本発明の光触媒層によれば、光触媒活性により損傷を受けやすい有機材料に対しても浸食しにくいことから、中間層を介在させることなく、光触媒層という一つの層で優れた機能を有する光触媒塗装体を製造することができる。その結果、中間層の形成が不要となる分、光触媒塗装体の製造に要する時間やコストを削減できる。 According to a preferred embodiment of the present invention, a substrate having at least a surface formed of an organic material can be used as the substrate, and the entire substrate is formed of an organic material or an inorganic material. Any of those in which the surface of the substrate is coated with an organic material (for example, a decorative board) is included. According to the photocatalyst layer of the present invention, it is difficult to erode even to an organic material that is easily damaged by the photocatalytic activity, and therefore, a photocatalyst coating having an excellent function in one layer called a photocatalyst layer without interposing an intermediate layer The body can be manufactured. As a result, the time and cost required for manufacturing the photocatalyst-coated body can be reduced by the amount that the intermediate layer is not required.
光触媒層およびそのための光触媒コーティング液
本発明の光触媒層は、5質量部以上15質量部以下の、10nm以上100nm以下の平均粒径を有する光触媒粒子と、75質量部を超え95質量部以下の無機酸化物粒子と、シリカ換算で0質量部以上10質量部未満の加水分解性シリコーンの乾燥物とを、光触媒粒子、無機酸化物粒子、および加水分解性シリコーンのシリカ換算量の合計量が100質量部となるように含んでなる。そして、この光触媒層は、光触媒粒子、無機酸化物粒子、および加水分解性シリコーンが上記質量比率で溶媒中に分散されてなる光触媒コーティング液を基材上に塗布することによって形成されることができる。
Photocatalyst layer and photocatalyst coating liquid therefor The photocatalyst layer of the present invention comprises 5 to 15 parts by mass of photocatalyst particles having an average particle diameter of 10 to 100 nm and inorganic of more than 75 to 95 parts by mass The total amount of oxide particles and 0 to 10 parts by mass of hydrolyzable silicone dry matter in terms of silica is 100 masses in terms of the amount of photocatalyst particles, inorganic oxide particles, and hydrolyzable silicone in terms of silica. To be part. The photocatalyst layer can be formed by applying a photocatalyst coating liquid in which the photocatalyst particles, the inorganic oxide particles, and the hydrolyzable silicone are dispersed in the solvent in the above-described mass ratio on the substrate. .
本発明の好ましい態様によれば、光触媒層は0.5μm以上3.0μm以下の膜厚を有するのが好ましく、より好ましくは1.0μm以上2.0μm以下である。このような範囲内であると、光触媒層と基材の界面に到達する紫外線が充分に減衰されるので耐候性が向上する。また、無機酸化物粒子よりも含有比率が低い光触媒粒子を膜厚方向に増加させることができるので、有害ガス分解性も向上する。さらには、紫外線吸収性、透明性、膜強度においても優れた特性が得られる。 According to a preferred embodiment of the present invention, the photocatalyst layer preferably has a film thickness of 0.5 μm or more and 3.0 μm or less, more preferably 1.0 μm or more and 2.0 μm or less. Within such a range, the ultraviolet rays that reach the interface between the photocatalyst layer and the substrate are sufficiently attenuated, thereby improving the weather resistance. Moreover, since the photocatalyst particles having a lower content ratio than the inorganic oxide particles can be increased in the film thickness direction, harmful gas decomposability is also improved. Furthermore, excellent characteristics can be obtained in terms of ultraviolet absorption, transparency, and film strength.
本発明に用いる光触媒粒子は、光触媒活性を有する粒子であれば特に限定されず、あらゆる種類の光触媒の粒子が使用可能である。光触媒粒子の例としては、酸化チタン(TiO2)、ZnO、SnO2、SrTiO3、WO3、Bi2O3、Fe2O3のような金属酸化物の粒子が挙げられ、好ましくは酸化チタン粒子、より好ましくはアナターゼ型酸化チタン粒子である。酸化チタンは、無害で、化学的にも安定で、かつ、安価に入手可能である。また、酸化チタンはバンドギャップエネルギーが高く、従って、光励起には紫外線を必要とし、光励起の過程で可視光を吸収しないので、補色成分による発色が起こらない。酸化チタンは、粉末状、ゾル状、溶液状など様々な形態で入手可能であるが、光触媒活性を示すものであれば、いずれの形態でも使用可能である。本発明の好ましい態様によれば、光触媒粒子が10nm以上100nm以下の平均粒径を有するのが好ましく、より好ましくは10nm以上60nm以下である。なお、この平均粒径は、走査型電子顕微鏡により20万倍の視野に入る任意の100個の粒子の長さを測定した個数平均値として算出される。粒子の形状としては真球が最も良いが、略円形や楕円形でも良く、その場合の粒子の長さは((長径+短径)/2)として略算出される。この範囲内であると、耐候性、有害ガス分解性、および所望の各種被膜特性(紫外線吸収性、透明性、膜強度等)が効率良く発揮される。また、ゾル状で市販されている光触媒を用い、粒子径を30nm以下、好ましくは20nm以下にすることによって、とりわけ透明性が良好な光触媒層を得ることもできる。 The photocatalyst particles used in the present invention are not particularly limited as long as they have photocatalytic activity, and all kinds of photocatalyst particles can be used. Examples of the photocatalyst particles include metal oxide particles such as titanium oxide (TiO 2 ), ZnO, SnO 2 , SrTiO 3 , WO 3 , Bi 2 O 3 , Fe 2 O 3 , and preferably titanium oxide. Particles, more preferably anatase type titanium oxide particles. Titanium oxide is harmless, chemically stable, and available at low cost. Titanium oxide has a high band gap energy, and therefore requires ultraviolet light for photoexcitation and does not absorb visible light in the process of photoexcitation, so that no color formation due to a complementary color component occurs. Titanium oxide is available in various forms such as powder, sol, and solution, but any form can be used as long as it exhibits photocatalytic activity. According to a preferred embodiment of the present invention, the photocatalyst particles preferably have an average particle size of 10 nm to 100 nm, more preferably 10 nm to 60 nm. The average particle diameter is calculated as a number average value obtained by measuring the length of any 100 particles that enter a 200,000-fold field of view with a scanning electron microscope. As the shape of the particle, a true sphere is the best, but it may be approximately circular or elliptical, and the length of the particle in this case is approximately calculated as ((major axis + minor axis) / 2). Within this range, weather resistance, harmful gas decomposability, and various desired film properties (such as ultraviolet absorption, transparency, and film strength) are efficiently exhibited. In addition, a photocatalyst layer having particularly good transparency can be obtained by using a commercially available photocatalyst in sol form and setting the particle diameter to 30 nm or less, preferably 20 nm or less.
本発明の光触媒層およびコーティング液における光触媒粒子の含有量は、光触媒粒子、無機酸化物粒子、および加水分解性シリコーンの合計量100質量部に対して、5質量部以上15質量部以下とし、好ましくは5質量部以上10質量部以下である。このように光触媒粒子の配合割合を少なくすることで、光触媒粒子の基材との直接的な接触をできるだけ少なくして、基材(特に有機材料)に対する浸食を防止することができ、耐候性も向上すると考えられる。それにもかかわらず、有害ガス分解性や紫外線吸収性といった光触媒活性に起因する機能も十分に発揮させることができる。 The content of the photocatalyst particles in the photocatalyst layer and the coating liquid of the present invention is preferably 5 parts by mass or more and 15 parts by mass or less with respect to 100 parts by mass of the total amount of the photocatalyst particles, the inorganic oxide particles, and the hydrolyzable silicone. Is 5 parts by mass or more and 10 parts by mass or less. By reducing the blending ratio of the photocatalyst particles in this way, the direct contact of the photocatalyst particles with the base material can be reduced as much as possible to prevent erosion of the base material (especially organic material) and the weather resistance is also improved. It is thought to improve. Nevertheless, functions due to photocatalytic activity such as decomposability of harmful gas and ultraviolet absorption can be sufficiently exhibited.
本発明の好ましい態様によれば、さらに高い光触媒能を発現するために、チタニアとバナジウム、鉄、コバルト、ニッケル、パラジウム、亜鉛、ルテニウム、ロジウム、銅、銀、白金および金からなる群より選ばれる少なくとも一種の金属および/またはその金属からなる金属化合物を光触媒層および光触媒コーティング液に添加することができる。この添加は、光触媒と前記金属または金属化合物が共存する溶液をそのまま添加する方法、および光触媒酸化還元作用を利用して光触媒上に前記金属または金属化合物を担持する方法のいずれの方法によっても行うことができる。 According to a preferred embodiment of the present invention, the material is selected from the group consisting of titania and vanadium, iron, cobalt, nickel, palladium, zinc, ruthenium, rhodium, copper, silver, platinum and gold in order to develop higher photocatalytic ability. At least one metal and / or a metal compound comprising the metal can be added to the photocatalyst layer and the photocatalyst coating solution. This addition is performed by any of the method of adding a solution in which the photocatalyst and the metal or metal compound coexist as it is, and the method of supporting the metal or metal compound on the photocatalyst using the photocatalytic oxidation-reduction action. Can do.
本発明に用いる無機酸化物粒子は、光触媒粒子と共に層を形成可能な無機酸化物の粒子であれば特に限定されず、あらゆる種類の無機酸化物の粒子が使用可能である。そのような無機酸化物粒子の例としては、シリカ、アルミナ、ジルコニア、セリア、イットリア、ボロニア、マグネシア、カルシア、フェライト、無定型チタニア、ハフニア等の単一酸化物の粒子;およびチタン酸バリウム、ケイ酸カルシウム等の複合酸化物の粒子が挙げられ、より好ましくはシリカ粒子である。これら無機酸化物粒子は、水を分散媒とした水性コロイド;またはエチルアルコール、イソプロピルアルコール、もしくはエチレングリコールなどの親水性溶媒にコロイド状に分散させたオルガノゾルの形態であるのが好ましく、特に好ましくはコロイダルシリカである。 The inorganic oxide particles used in the present invention are not particularly limited as long as they are inorganic oxide particles capable of forming a layer together with photocatalyst particles, and any kind of inorganic oxide particles can be used. Examples of such inorganic oxide particles include single oxide particles such as silica, alumina, zirconia, ceria, yttria, boronia, magnesia, calcia, ferrite, amorphous titania, hafnia; and barium titanate, silica The particle | grains of complex oxides, such as calcium acid, are mentioned, More preferably, it is a silica particle. These inorganic oxide particles are preferably in the form of an aqueous colloid using water as a dispersion medium; or an organosol dispersed in a hydrophilic solvent such as ethyl alcohol, isopropyl alcohol, or ethylene glycol, and particularly preferably. Colloidal silica.
本発明の好ましい態様によれば、前記無機酸化物粒子が10nm以上40nm未満の平均粒径を有するのが好ましく、より好ましくは10nm以上30nm以下である。なお、この平均粒径は、走査型電子顕微鏡により20万倍の視野に入る任意の100個の粒子の長さを測定した個数平均値として算出される。粒子の形状としては真球が最も良いが、略円形や楕円形でも良く、その場合の粒子の長さは((長径+短径)/2)として略算出される。この範囲内であると、耐候性、有害ガス分解性、および所望の各種被膜特性(紫外線吸収性、透明性、膜強度等)が効率良く発揮される。とりわけ透明で密着性が良好な光触媒層を得ることができる。 According to a preferred aspect of the present invention, the inorganic oxide particles preferably have an average particle size of 10 nm or more and less than 40 nm, more preferably 10 nm or more and 30 nm or less. The average particle diameter is calculated as a number average value obtained by measuring the length of any 100 particles that enter a 200,000-fold field of view with a scanning electron microscope. As the shape of the particle, a true sphere is the best, but it may be approximately circular or elliptical, and the length of the particle in this case is approximately calculated as ((major axis + minor axis) / 2). Within this range, weather resistance, harmful gas decomposability, and various desired film properties (such as ultraviolet absorption, transparency, and film strength) are efficiently exhibited. In particular, a photocatalyst layer that is transparent and has good adhesion can be obtained.
本発明の光触媒層およびコーティング液における無機酸化物粒子の含有量は、光触媒粒子、無機酸化物粒子、および加水分解性シリコーンのシリカ換算量の合計量100質量部に対して、75質量部を超え95質量部以下であり、好ましくは80質量部を超え95質量部以下であり、より好ましくは85質量部以上95質量部以下、さらに好ましくは90質量部以上95質量部以下である。 The content of the inorganic oxide particles in the photocatalyst layer and the coating liquid of the present invention exceeds 75 parts by mass with respect to 100 parts by mass as the total amount of silica of the photocatalyst particles, the inorganic oxide particles, and the hydrolyzable silicone. 95 parts by mass or less, preferably more than 80 parts by mass and 95 parts by mass or less, more preferably 85 parts by mass or more and 95 parts by mass or less, and further preferably 90 parts by mass or more and 95 parts by mass or less.
本発明の光触媒層は加水分解性シリコーンの乾燥物を実質的に含まないのが好ましく、より好ましくは全く含まない。加水分解性シリコーンとは、アルコキシ基を有するオルガノシロキサンおよび/またはその部分加水分解縮合物の総称である。しかしながら、本発明の有害ガス分解性を確保できる程度であれば加水分解性シリコーンを任意成分として含有することは許容される。したがって、加水分解性シリコーンの含有量は、シリカ換算で、光触媒粒子、無機酸化物粒子、および加水分解性シリコーンの合計量100質量部に対して、0質量部以上10質量部未満であり、好ましくは5質量部以下、最も好ましくは0質量部である。加水分解性シリコーンとしては、4官能シリコーン化合物がよく使用され、例えば、エチルシリケート40(オリゴマー、Rがエチル基)、エチルシリケート48(オリゴマー、Rがエチル基)メチルシリケート51(オリゴマー、Rがメチル基)(いずれもコルコート社製)の形で市販されている。 The photocatalyst layer of the present invention preferably contains substantially no dried hydrolyzable silicone, and more preferably does not contain at all. The hydrolyzable silicone is a general term for an organosiloxane having an alkoxy group and / or a partially hydrolyzed condensate thereof. However, it is allowed to contain hydrolyzable silicone as an optional component as long as the harmful gas decomposability of the present invention can be ensured. Therefore, the content of the hydrolyzable silicone is 0 parts by mass or more and less than 10 parts by mass with respect to 100 parts by mass of the total amount of the photocatalyst particles, the inorganic oxide particles, and the hydrolyzable silicone in terms of silica. Is 5 parts by mass or less, and most preferably 0 part by mass. As the hydrolyzable silicone, a tetrafunctional silicone compound is often used. For example, ethyl silicate 40 (oligomer, R is an ethyl group), ethyl silicate 48 (oligomer, R is an ethyl group), methyl silicate 51 (oligomer, R is a methyl group) Group) (both manufactured by Colcoat Co.).
光触媒コーティング液には任意成分として界面活性剤を含んでよい。本発明に用いる界面活性剤は、光触媒粒子、無機酸化物粒子、および加水分解性シリコーンの合計量100質量部に対して、0質量部以上10質量部未満光触媒層に含有されていてもよく、好ましくは0質量部以上8質量部以下であり、より好ましくは0以上6質量部以下である。界面活性剤の効果の1つとして基材へのレベリング性があり、コーティング液と基材との組合せによって界面活性剤の量を適宜決めれば良く、その際の下限値は0.1質量部とされてよい。この界面活性剤は光触媒コーティング液の濡れ性を改善するために有効な成分であるが、塗布後に形成される光触媒層にあってはもはや本発明の光触媒塗装体の効果には寄与しない不可避不純物に相当する。したがって、光触媒コーティング液に要求される濡れ性に応じて、上記含有量範囲内において使用されてよく、濡れ性を問題にしないのであれば界面活性剤は実質的にあるいは一切含まなくてよい。使用すべき界面活性剤は、光触媒や無機酸化物粒子の分散安定性、中間層上に塗布した際の濡れ性を勘案し適宜選択されることができるが、非イオン性界面活性剤が好ましく、より好ましくは、エーテル型非イオン性界面活性剤、エステル型非イオン性界面活性剤、ポリアルキレングリコール非イオン性界面活性剤、フッ素系非イオン性界面活性剤、シリコン系非イオン性界面活性剤が挙げられる。 The photocatalyst coating liquid may contain a surfactant as an optional component. The surfactant used in the present invention may be contained in the photocatalyst layer in an amount of 0 to less than 10 parts by mass with respect to 100 parts by mass of the total amount of photocatalyst particles, inorganic oxide particles, and hydrolyzable silicone, Preferably they are 0 mass part or more and 8 mass parts or less, More preferably, they are 0 or more and 6 mass parts or less. One of the effects of the surfactant is leveling to the substrate, and the amount of the surfactant may be appropriately determined depending on the combination of the coating liquid and the substrate, and the lower limit in that case is 0.1 part by mass. May be. This surfactant is an effective component for improving the wettability of the photocatalyst coating solution, but in the photocatalyst layer formed after coating, it is an inevitable impurity that no longer contributes to the effect of the photocatalyst-coated body of the present invention. Equivalent to. Therefore, it may be used within the above-mentioned content range depending on the wettability required for the photocatalyst coating liquid, and if the wettability is not a problem, the surfactant may be contained substantially or not at all. The surfactant to be used can be appropriately selected in consideration of the dispersion stability of the photocatalyst and inorganic oxide particles, and wettability when applied on the intermediate layer, but a nonionic surfactant is preferable, More preferably, an ether type nonionic surfactant, an ester type nonionic surfactant, a polyalkylene glycol nonionic surfactant, a fluorine-based nonionic surfactant, or a silicon-based nonionic surfactant is used. Can be mentioned.
本発明の光触媒コーティング液は、光触媒粒子、無機酸化物粒子、および所望により加水分解性シリコーンおよび界面活性剤を上記特定の配合比率で溶媒中に分散させることにより得ることができる。溶媒としては、上記構成成分を適切に分散可能なあらゆる溶媒が使用可能であり、水および/または有機溶媒であってよい。また、本発明の光触媒コーティング液の固形分濃度は特に限定されないが、1〜10質量%とするのが塗布し易い点で好ましい。なお、光触媒コーティング組成物中の構成成分の分析は、コーティング液を限外ろ過によって粒子成分と濾液に分離し、それぞれを赤外分光分析、ゲルパーミエーションクロマトグラフィー、蛍光X線分光分析などで分析し、スペクトルを解析することによって評価することができる。 The photocatalyst coating liquid of the present invention can be obtained by dispersing photocatalyst particles, inorganic oxide particles, and optionally hydrolyzable silicone and a surfactant in the above-mentioned specific mixing ratio in a solvent. As the solvent, any solvent that can appropriately disperse the above-described constituent components can be used, and water and / or an organic solvent may be used. Moreover, the solid content concentration of the photocatalyst coating liquid of the present invention is not particularly limited, but it is preferably 1 to 10% by mass because it is easy to apply. The components in the photocatalyst coating composition are analyzed by separating the coating solution into particle components and filtrate by ultrafiltration, and analyzing each by infrared spectroscopy, gel permeation chromatography, fluorescent X-ray spectroscopy, etc. It can be evaluated by analyzing the spectrum.
製造方法
本発明の光触媒塗装体は、本発明の光触媒コーティング液を基材上に塗布することにより簡単に製造することができる。光触媒層の塗装方法は、前記液剤を刷毛塗り、ローラー、スプレー、ロールコーター、フローコーター、ディップコート、流し塗り、スクリーン印刷、電着、蒸着等、一般に広く行われている方法を利用できる。コーティング液の基材への塗布後は、常温乾燥させればよく、あるいは必要に応じて加熱乾燥してもよい。このように本発明の光触媒塗装体は、本発明の光触媒層によれば、光触媒活性により損傷を受けやすい有機材料に対しても浸食しにくいことから、中間層を介在させることなく、光触媒層という一つの層で優れた機能を有する光触媒塗装体を製造することができる。その結果、中間層の形成が不要となる分、光触媒塗装体の製造に要する時間やコストを削減できる。
Manufacturing method The photocatalyst coating body of this invention can be easily manufactured by apply | coating the photocatalyst coating liquid of this invention on a base material. As a method for coating the photocatalyst layer, generally used methods such as brush coating, roller, spray, roll coater, flow coater, dip coating, flow coating, screen printing, electrodeposition, vapor deposition and the like can be used. After applying the coating liquid to the substrate, it may be dried at room temperature, or may be heat-dried as necessary. As described above, according to the photocatalyst layer of the present invention, the photocatalyst-coated body of the present invention is not easily eroded even by an organic material that is easily damaged by photocatalytic activity. A photocatalyst-coated body having an excellent function in one layer can be produced. As a result, the time and cost required for manufacturing the photocatalyst-coated body can be reduced by the amount that the intermediate layer is not required.
本発明を以下の例に基づいて具体的に説明するが、本発明はこれらの例に限定されるものではない。
なお、以下の例において光触媒コーティング液の作製に使用した原料は以下の通りである。
光触媒粒子
・チタニア水分散体(平均粒径:30〜60nm、塩基性)
無機酸化物粒子
・水分散型コロイダルシリカ(日産化学工業 社製、商品名:スノーテックス50、粒径:20〜30nm、固形分含有率 48%)(例1〜26、例28、例31〜34で使用)
・水分散型コロイダルシリカ(日産化学工業 社製、商品名:スノーテックス40、粒径:10〜20nm、固形分含有率 40%)(例27で使用)
・水分散型コロイダルシリカ(日産化学工業 社製、商品名:スノーテックスS、粒径:8〜11nm、固形分含有率 30%)(例29で使用)
・水分散型コロイダルシリカ(日産化学工業 社製、商品名:スノーテックスXS、粒径:4〜6nm、固形分含有率 20%)(例30で使用)
加水分解性シリコーン
・テトラメトキシシランの重縮合物(多摩化学工業 社製、商品名:Mシリケート51)
界面活性剤
・ポリエーテル変性シリコーン系界面活性剤(信越化学工業 社製、商品名:シリコーン変性ポリエーテル(KF−643))
The present invention will be specifically described based on the following examples, but the present invention is not limited to these examples.
In the following examples, the raw materials used for preparation of the photocatalyst coating liquid are as follows.
Photocatalyst particles / titania water dispersion (average particle size: 30-60 nm, basic)
Inorganic oxide particles / water-dispersed colloidal silica (manufactured by Nissan Chemical Industries, trade name: Snowtex 50, particle size: 20-30 nm, solid content 48%) (Examples 1-26, Example 28, Example 31- 34)
-Water-dispersed colloidal silica (manufactured by Nissan Chemical Industries, trade name: Snowtex 40, particle size: 10-20 nm, solid content 40%) (used in Example 27)
-Water-dispersed colloidal silica (manufactured by Nissan Chemical Industries, trade name: Snowtex S, particle size: 8-11 nm, solid content 30%) (used in Example 29)
Water-dispersed colloidal silica (manufactured by Nissan Chemical Industries, trade name: Snowtex XS, particle size: 4-6 nm, solid content 20%) (used in Example 30)
Hydrocondensable silicone / tetramethoxysilane polycondensate (manufactured by Tama Chemical Co., Ltd., trade name: M silicate 51)
Surfactant / polyether-modified silicone surfactant (manufactured by Shin-Etsu Chemical Co., Ltd., trade name: silicone-modified polyether (KF-643))
例1〜5:耐候性の評価
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、フロート板ガラス上にカーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としてのチタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、ポリエーテル変性シリコーン系界面活性剤とを表1に示される配合比で混合して、光触媒コーティング液を得た。なお、この光触媒コーティング液は加水分解性シリコーンを含まない。光触媒コーティング液中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。
Examples 1 to 5: Evaluation of weather resistance A photocatalyst-coated body provided with a photocatalyst layer was produced as follows. First, a colored organic coated body was prepared as a base material. This colored organic coated body is obtained by applying general-purpose acrylic silicone to which carbon black powder is added on a float plate glass and sufficiently drying and curing it. On the other hand, a titania aqueous dispersion as a photocatalyst, a water-dispersed colloidal silica as an inorganic oxide, water as a solvent, and a polyether-modified silicone surfactant are mixed at a blending ratio shown in Table 1, A photocatalytic coating solution was obtained. In addition, this photocatalyst coating liquid does not contain hydrolysable silicone. The total solid concentration of the photocatalyst and the inorganic oxide in the photocatalyst coating solution was 5.5% by mass.
得られた光触媒コーティング液をあらかじめ50℃に加熱した上記着色有機塗装体上にスプレー塗布し、120℃で5分乾燥した。こうして、光触媒層を形成させて、光触媒塗装体を得た。走査型電子顕微鏡観察により光触媒層の膜厚を測定したところ、例1〜5のいずれの例においても約0.5μmであった。 The obtained photocatalyst coating liquid was spray-coated on the colored organic coating body previously heated to 50 ° C. and dried at 120 ° C. for 5 minutes. Thus, a photocatalyst layer was formed to obtain a photocatalyst-coated body. When the film thickness of the photocatalyst layer was measured by observation with a scanning electron microscope, it was about 0.5 μm in any of Examples 1 to 5.
こうして得られた50×100mmの大きさの光触媒塗装体について、以下の通り耐候性試験を行った。光触媒塗装体をJIS B7753に規定されるサンシャインウエザオメーター(スガ試験機製、S−300C)に投入した。300hr経過後に試験片を取り出し、日本電色製の測色差計ZE2000にて、促進試験前後で色差を測定し、そのΔb値を比較することで変色の度合いを評価した。 About the photocatalyst coating body of a magnitude | size of 50x100 mm obtained in this way, the weather resistance test was done as follows. The photocatalyst-coated body was put into a sunshine weatherometer (S-300C, manufactured by Suga Test Instruments) defined in JIS B7753. After 300 hours, the test piece was taken out, the color difference was measured before and after the acceleration test with a color difference meter ZE2000 manufactured by Nippon Denshoku, and the degree of color change was evaluated by comparing the Δb values.
得られた結果は表1に示される通りであった。ここで、表中のGはほとんど変色しなかったことを、NGはΔb値がプラス側(黄変側)に推移したことを表す。表1に示されるように、光触媒層中の光触媒の含有量を5質量部以上15質量部以下にすることによって、有機基材上に光触媒層を塗装しても充分な耐候性を有することが分かった。 The obtained results were as shown in Table 1. Here, G in the table indicates that the color has hardly changed, and NG indicates that the Δb value has shifted to the plus side (yellowing side). As shown in Table 1, by setting the content of the photocatalyst in the photocatalyst layer to 5 parts by mass or more and 15 parts by mass or less, the photocatalyst layer has sufficient weather resistance even if the photocatalyst layer is coated on the organic substrate. I understood.
例6〜9:有害ガス分解性の評価
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、フロート板ガラス上にカーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としてのチタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、ポリエーテル変性シリコーン系界面活性剤と、加水分解性シリコーンとしてのテトラメトキシシランの重縮合物とを表2に示される配合比で混合して、光触媒コーティング液を得た。なお、例6および例7の光触媒コーティング液は加水分解性シリコーンを含まない。光触媒コーティング液中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。
Examples 6 to 9: Evaluation of harmful gas decomposability A photocatalyst-coated body provided with a photocatalyst layer was produced as follows. First, a colored organic coated body was prepared as a base material. This colored organic coated body is obtained by applying general-purpose acrylic silicone to which carbon black powder is added on a float plate glass and sufficiently drying and curing it. On the other hand, polycondensation of titania aqueous dispersion as photocatalyst, water-dispersed colloidal silica as inorganic oxide, water as solvent, polyether-modified silicone surfactant, and tetramethoxysilane as hydrolyzable silicone Were mixed at a blending ratio shown in Table 2 to obtain a photocatalyst coating solution. In addition, the photocatalyst coating liquid of Example 6 and Example 7 does not contain hydrolysable silicone. The total solid concentration of the photocatalyst and the inorganic oxide in the photocatalyst coating solution was 5.5% by mass.
得られた光触媒コーティング液をあらかじめ50℃に加熱した上記着色有機塗装体上にスプレー塗布し、120℃で5分乾燥した。こうして、光触媒層を形成させて、光触媒塗装体を得た。走査型電子顕微鏡観察により光触媒層の膜厚(μm)を測定したところ、いずれの例においても約1μmであった。 The obtained photocatalyst coating liquid was spray-coated on the colored organic coating body previously heated to 50 ° C. and dried at 120 ° C. for 5 minutes. Thus, a photocatalyst layer was formed to obtain a photocatalyst-coated body. When the film thickness (μm) of the photocatalyst layer was measured by observation with a scanning electron microscope, it was about 1 μm in any of the examples.
こうして得られた50×100mmの大きさの光触媒塗装体について、以下の通りガス分解性試験を行った。光触媒塗装体に前処理として1mW/cm2のBLB光で12hr以上照射した。JIS R1701に記載の反応容器内に塗装体サンプルを1枚セットした。25℃、50%RHに調整した空気に約1000ppbになるようにNOガスを混合し、遮光した反応容器内に20分導入した。その後ガスを導入したままで3mW/cm2に調整したBLB光を20分間照射した。その後ガスを導入した状態で再度反応容器を遮光した。NOx除去量は、BLB光照射前後でのNO、NO2濃度から下記の式に従って計算した。
NOx除去量=[NO(照射後)−NO(照射時)]−[NO2(照射時)−NO2(照射後)]
The photocatalyst-coated body having a size of 50 × 100 mm thus obtained was subjected to a gas decomposability test as follows. As a pretreatment, the photocatalyst-coated body was irradiated with 1 mW / cm 2 of BLB light for 12 hours or more. One coated body sample was set in the reaction vessel described in JIS R1701. NO gas was mixed with air adjusted to 25 ° C. and 50% RH so as to be about 1000 ppb, and introduced into a light-shielded reaction vessel for 20 minutes. Thereafter, BLB light adjusted to 3 mW / cm 2 was irradiated for 20 minutes while the gas was introduced. Thereafter, the reaction vessel was shielded from light again with the gas introduced. The NOx removal amount was calculated according to the following formula from the NO and NO 2 concentrations before and after the BLB light irradiation.
NOx removal amount = [NO (after irradiation) −NO (at irradiation)] − [NO 2 (at irradiation) −NO 2 (after irradiation)]
得られた結果は表2に示される通りであった。ここで、表中のGはNOx除去量が400ppb以上、NGはNOx除去量が10ppb以下を表す。表2に示されるように、光触媒層を光触媒粒子と無機酸化物から構成し、実質的に加水分解性シリコーンを含まないことにより、良好なNOx分解性を示した。一方、加水分解性シリコーンが10質量部入ったものはNOx分解性が喪失していることが分かった。 The obtained results were as shown in Table 2. Here, G in the table represents a NOx removal amount of 400 ppb or more, and NG represents a NOx removal amount of 10 ppb or less. As shown in Table 2, when the photocatalyst layer was composed of photocatalyst particles and an inorganic oxide and substantially free of hydrolyzable silicone, good NOx decomposability was exhibited. On the other hand, those containing 10 parts by mass of hydrolyzable silicone were found to lose NOx decomposability.
例10〜26:直線透過率および紫外線遮蔽率の測定
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として550nmの波長の透過率が94%のフロート板ガラスを用意した。一方、光触媒としてのチタニア水分散体と、平均粒径20〜30nmの無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、ポリエーテル変性シリコーン系界面活性剤とを表3に示される配合比で混合して、光触媒コーティング液を得た。したがって、この光触媒コーティング液は加水分解性シリコーンを含まない。光触媒コーティング液中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。
Examples 10 to 26: Measurement of linear transmittance and ultraviolet shielding rate A photocatalyst-coated body provided with a photocatalyst layer was produced as follows. First, a float plate glass having a transmittance of 94% at a wavelength of 550 nm was prepared as a substrate. On the other hand, Table 3 shows titania water dispersion as a photocatalyst, water-dispersed colloidal silica as an inorganic oxide having an average particle diameter of 20 to 30 nm, water as a solvent, and a polyether-modified silicone surfactant. The photocatalyst coating liquid was obtained by mixing at a blending ratio. Therefore, this photocatalyst coating liquid does not contain hydrolyzable silicone. The total solid concentration of the photocatalyst and the inorganic oxide in the photocatalyst coating solution was 5.5% by mass.
得られた光触媒コーティング液をあらかじめ50℃に加熱した上記フロート板ガラス板上にスプレー塗布し、120℃で5分乾燥した。こうして、光触媒層を形成させて、光触媒塗装体を得た。走査型電子顕微鏡観察により光触媒層の膜厚(μm)を測定したところ、表3に示される値であった。 The obtained photocatalyst coating liquid was spray-coated on the float plate glass plate heated to 50 ° C. in advance, and dried at 120 ° C. for 5 minutes. Thus, a photocatalyst layer was formed to obtain a photocatalyst-coated body. When the film thickness (μm) of the photocatalyst layer was measured by observation with a scanning electron microscope, the values shown in Table 3 were obtained.
こうして得られた50×100mmの大きさの光触媒塗装体について、以下の通り直線(550nm)透過率および紫外線(300nm)遮蔽率の測定を紫外・可視・近赤外分光光度計(島津製作所製 UV−3150)を用いて行った。 With respect to the photocatalyst-coated body having a size of 50 × 100 mm obtained as described above, the measurement of the linear (550 nm) transmittance and the ultraviolet ray (300 nm) shielding rate was carried out by using an ultraviolet / visible / near infrared spectrophotometer (UV manufactured by Shimadzu Corporation). -3150).
得られた結果は表3に示される通りであった。ここで、直線透過率および紫外線遮蔽率の評価基準は以下の通りとした。
<直線透過率>
A:直線(550nm)透過率が97%以上
B:直線(550nm)透過率が95%以上97%未満
C:直線(550nm)透過率が95%未満
<紫外線遮蔽率>
a:紫外線(300nm)遮蔽率が80%以上
b:紫外線(300nm)遮蔽率が30%以上80%未満
c:紫外線(300nm)遮蔽率が30%未満
表3に示されるように、光触媒層中の光触媒の含有量が5質量部以上15質量部以下では膜厚を0.5μm以上3μm以下にすることで有機物の劣化に起因する紫外線を十分に遮蔽し、かつ透明性も確保できることが分かった。
The obtained results were as shown in Table 3. Here, the evaluation criteria of the linear transmittance and the ultraviolet shielding rate were as follows.
<Linear transmittance>
A: Linear (550 nm) transmittance is 97% or more B: Linear (550 nm) transmittance is 95% or more and less than 97% C: Linear (550 nm) transmittance is less than 95% <UV shielding factor>
a: Ultraviolet (300 nm) shielding rate of 80% or more b: Ultraviolet (300 nm) shielding rate of 30% or more and less than 80% c: Ultraviolet (300 nm) shielding rate of less than 30% As shown in Table 3, in the photocatalyst layer When the content of the photocatalyst is 5 parts by mass or more and 15 parts by mass or less, it was found that by setting the film thickness to 0.5 μm or more and 3 μm or less, it is possible to sufficiently shield the ultraviolet rays caused by the deterioration of organic substances and ensure transparency. .
例27〜30:ヘイズの測定
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として550nmの波長の透過率が94%のフロート板ガラスを用いた。一方、光触媒としてのチタニア水分散体と、表4に示される各種平均粒径の無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、ポリエーテル変性シリコーン系界面活性剤とを表4に示される配合比で混合して、光触媒コーティング液を得た。したがって、この光触媒コーティング液は加水分解性シリコーンを含まない。光触媒コーティング液中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。
Examples 27 to 30: Measurement of haze A photocatalyst-coated body provided with a photocatalyst layer was produced as follows. First, a float plate glass having a transmittance of 94% at a wavelength of 550 nm was used as a substrate. On the other hand, a titania aqueous dispersion as a photocatalyst, water-dispersed colloidal silica as an inorganic oxide having various average particle diameters shown in Table 4, water as a solvent, and a polyether-modified silicone surfactant are listed in Table 4. To obtain a photocatalyst coating liquid. Therefore, this photocatalyst coating liquid does not contain hydrolyzable silicone. The total solid concentration of the photocatalyst and the inorganic oxide in the photocatalyst coating solution was 5.5% by mass.
得られた光触媒コーティング液を先述の基材上に1000rpmで10秒間スピンコートし、120℃で5分乾燥し光触媒層を得た。こうして得られた50×100mmの大きさの光触媒塗装体のヘイズをヘイズ計(Gardner製 haze−gard plus)を用いて測定した。 The obtained photocatalyst coating liquid was spin-coated on the above-mentioned substrate at 1000 rpm for 10 seconds and dried at 120 ° C. for 5 minutes to obtain a photocatalyst layer. The haze of the photocatalyst-coated body having a size of 50 × 100 mm obtained in this manner was measured using a haze meter (haze-gard plus from Gardner).
得られた結果は表4に示される通りであった。表4に示されるように、光触媒層中の金属酸化物の粒径を10〜30nmにすることでヘイズ値を1%未満に抑えることができ透明性が確保できることが分かった。 The obtained results were as shown in Table 4. As shown in Table 4, it was found that by setting the particle size of the metal oxide in the photocatalyst layer to 10 to 30 nm, the haze value can be suppressed to less than 1% and the transparency can be secured.
例31〜34:界面活性剤の添加による影響の評価
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、フロート板ガラス上にカーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としてのチタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、ポリエーテル変性シリコーン系界面活性剤とを表5に示される配合比で混合して、光触媒コーティング液を得た。なお、この光触媒コーティング液は加水分解性シリコーンを含まない。光触媒コーティング液中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。
Examples 31 to 34: Evaluation of influence by addition of surfactant A photocatalyst-coated body provided with a photocatalyst layer was produced as follows. First, a colored organic coated body was prepared as a base material. This colored organic coated body is obtained by applying general-purpose acrylic silicone to which carbon black powder is added on a float plate glass and sufficiently drying and curing it. On the other hand, a titania aqueous dispersion as a photocatalyst, a water-dispersed colloidal silica as an inorganic oxide, water as a solvent, and a polyether-modified silicone surfactant are mixed at a blending ratio shown in Table 5, A photocatalytic coating solution was obtained. In addition, this photocatalyst coating liquid does not contain hydrolysable silicone. The total solid concentration of the photocatalyst and the inorganic oxide in the photocatalyst coating solution was 5.5% by mass.
得られた光触媒コーティング液をあらかじめ50〜60℃に加熱した上記着色有機塗装体上にスプレー塗布し、120℃で5分乾燥した。こうして、光触媒層を形成させて、光触媒塗装体を得た。走査型電子顕微鏡観察により光触媒層の膜厚(μm)を測定したところ、例31〜34のいずれの例においても約1μmであった。 The obtained photocatalyst coating liquid was spray-coated on the colored organic coating body heated to 50 to 60 ° C. in advance, and dried at 120 ° C. for 5 minutes. Thus, a photocatalyst layer was formed to obtain a photocatalyst-coated body. When the film thickness (μm) of the photocatalyst layer was measured by observation with a scanning electron microscope, it was about 1 μm in any of Examples 31 to 34.
こうして得られた50×100mmの大きさの光触媒塗装体について、以下の通りガス分解性試験を行った。光色媒触媒体に前処理として1mW/cm2のBLB光で12hr以上照射した。JIS R1701に記載の反応容器内に塗装体サンプルを1枚セットした。25℃、50%RHに調整した空気に約1000ppbになるようにNOガスを混合し、遮光した反応容器内に20分導入した。その後ガスを導入したままで3mW/cm2に調整したBLB光を20分間照射した。その後ガスを導入した状態で再度反応容器を遮光した。NOx除去量は、BLB光照射前後でのNO、NO2濃度から下記の式に従って計算した。
NOx除去量=[NO(照射後)−NO(照射時)]−[NO2(照射時)−NO2(照射後)]
The photocatalyst-coated body having a size of 50 × 100 mm thus obtained was subjected to a gas decomposability test as follows. The photochromic catalyst body was irradiated with 1 mW / cm 2 of BLB light as a pretreatment for 12 hours or more. One coated body sample was set in the reaction vessel described in JIS R1701. NO gas was mixed with air adjusted to 25 ° C. and 50% RH so as to be about 1000 ppb, and introduced into a light-shielded reaction vessel for 20 minutes. Thereafter, BLB light adjusted to 3 mW / cm 2 was irradiated for 20 minutes while the gas was introduced. Thereafter, the reaction vessel was shielded from light again with the gas introduced. The NOx removal amount was calculated according to the following formula from the NO and NO2 concentrations before and after the BLB light irradiation.
NOx removal amount = [NO (after irradiation) −NO (at irradiation)] − [NO 2 (at irradiation) −NO 2 (after irradiation)]
得られた結果は表5に示される通りであった。ここで、表中のNOx除去率とは例32の除去量を100として相対的に示している。表5に示されるように、界面活性剤の添加量を多くすることで除去率が低下することが分かった。 The results obtained were as shown in Table 5. Here, the NOx removal rate in the table is relatively shown with the removal amount of Example 32 as 100. As shown in Table 5, it was found that the removal rate was lowered by increasing the amount of the surfactant added.
Claims (9)
前記光触媒層が、
5質量部以上15質量部以下の、走査型電子顕微鏡により20万倍の視野に入る任意の100個の粒子の長さを測定することにより算出される、10nm以上100nm以下の個数平均粒径を有する光触媒粒子と、
75質量部を超え95質量部以下の無機酸化物粒子と、
シリカ換算で0質量部以上10質量部未満の加水分解性シリコーンの乾燥物と
を、前記光触媒粒子、前記無機酸化物粒子、および前記加水分解性シリコーンのシリカ換算量の合計量が100質量部となるように含み、
さらに界面活性剤を0質量部以上10質量部以下含んでなる、光触媒塗装体。 A photocatalyst-coated body comprising a substrate and a photocatalyst layer provided on the substrate,
The photocatalytic layer is
The number average particle diameter of 10 nm or more and 100 nm or less , calculated by measuring the length of any 100 particles that fall within a 200,000-fold field of view with a scanning electron microscope of 5 parts by mass or more and 15 parts by mass or less. Having photocatalytic particles,
More than 75 parts by weight and less than 95 parts by weight of inorganic oxide particles;
A hydrolyzable silicone dry matter having a weight of 0 to less than 10 parts by weight in terms of silica, and the total amount of silica equivalents of the photocatalyst particles, the inorganic oxide particles, and the hydrolyzable silicone is 100 parts by weight. Including
Furthermore, a photocatalyst-coated body comprising 0 to 10 parts by mass of a surfactant.
溶媒と、
5質量部以上15質量部以下の、走査型電子顕微鏡により20万倍の視野に入る任意の100個の粒子の長さを測定することにより算出される、10nm以上100nm以下の個数平均粒径を有する光触媒粒子と、
75質量部を超え95質量部以下の無機酸化物粒子と、
シリカ換算で0質量部以上10質量部未満の加水分解性シリコーンと
を、前記光触媒粒子、前記無機酸化物粒子、および前記加水分解性シリコーンのシリカ換算量の合計量が100質量部となるように含み、さらに界面活性剤を0質量部以上10質量部以下含んでなる、光触媒コーティング液。 It is a photocatalyst coating liquid used for manufacture of the photocatalyst coating body as described in any one of Claims 1-4,
A solvent,
The number average particle diameter of 10 nm or more and 100 nm or less , calculated by measuring the length of any 100 particles that fall within a 200,000-fold field of view with a scanning electron microscope of 5 parts by mass or more and 15 parts by mass or less. Having photocatalytic particles,
More than 75 parts by weight and less than 95 parts by weight of inorganic oxide particles;
From 0 parts by mass to less than 10 parts by mass of hydrolyzable silicone in terms of silica, the total amount of silica equivalents of the photocatalyst particles, the inorganic oxide particles, and the hydrolyzable silicone is 100 parts by mass. A photocatalyst coating solution further comprising 0 to 10 parts by mass of a surfactant.