JP4782451B2 - Method for producing breathable wallpaper - Google Patents
Method for producing breathable wallpaper Download PDFInfo
- Publication number
- JP4782451B2 JP4782451B2 JP2005084092A JP2005084092A JP4782451B2 JP 4782451 B2 JP4782451 B2 JP 4782451B2 JP 2005084092 A JP2005084092 A JP 2005084092A JP 2005084092 A JP2005084092 A JP 2005084092A JP 4782451 B2 JP4782451 B2 JP 4782451B2
- Authority
- JP
- Japan
- Prior art keywords
- wallpaper
- breathable
- paper
- weight
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、日本の風土に合った通気性を有する壁紙およびその製造方法に関するものである。 The present invention relates to a wallpaper having air permeability suitable for a Japanese climate and a method for manufacturing the wallpaper.
従来において、住宅等の内装材として、建築物等の内壁面や天井面等に対する装飾性を高めるために、意匠的審美性に優れたシート状の壁紙が広く使用されている。しかも、この種の壁紙は、壁面等への貼付の便宜性等を考慮して、例えばその基材として不燃紙等の紙基材が使用されている。また、その表面には、絵柄の印刷以外にも、耐汚染性、耐擦傷性等の表面物性の付与や、エンボスによる立体的な装飾性の付与、発泡による柔軟性の付与等の目的から、例えばポリ塩化ビニル樹脂またはアクリル系樹脂等からなる樹脂層を設けた構成とすることが、一般的に知られている。 2. Description of the Related Art Conventionally , sheet-like wallpaper having excellent design aesthetics has been widely used as an interior material for houses and the like in order to enhance the decorativeness of inner wall surfaces and ceiling surfaces of buildings and the like. In addition, this type of wallpaper uses, for example, a paper base material such as non-combustible paper as a base material in consideration of the convenience of sticking to a wall surface or the like. In addition to the printing of the pattern on the surface, for the purpose of imparting surface physical properties such as stain resistance and scratch resistance, imparting three-dimensional decorativeness by embossing, imparting flexibility by foaming, etc. For example, it is generally known that a resin layer made of polyvinyl chloride resin or acrylic resin is provided.
今日において、住宅等の内装材としての壁紙の大部分は、前述したポリ塩化ビニル樹脂からなる樹脂層を設けたものであり、この種の壁紙は、その市場において９５％以上を占有し、流通しているのが現状である。そして、この種の壁紙について、内装材のリフォーム等が行われる際に、その現場において気が付くことは、壁紙を剥がした壁面等に多量のカビや細菌が発生していることである。 Nowadays, most of the wallpaper as interior materials for homes is provided with the resin layer made of the above-mentioned polyvinyl chloride resin, and this kind of wallpaper occupies over 95% in the market and is distributed. This is the current situation. When this type of wallpaper is subjected to renovation of the interior material, what is noticed at the site is that a large amount of mold and bacteria are generated on the wall surface from which the wallpaper has been removed.
すなわち、前記壁紙を剥がした石膏ボード等の壁の表面は、カビや細菌で汚染ないし汚損されると共に、その内側に配設される断熱材として使用されるガラスウォールもカビや細菌で汚染され、さらにその周囲に形成されるアルミサッシまでもカビや細菌による腐食が発生している。その他、絨毯や浴室のタイルの目地に、カビや細菌が集中的に繁殖していることが確認される。 That is, the surface of the wall such as gypsum board from which the wallpaper has been peeled is contaminated or soiled with mold and bacteria, and the glass wall used as a heat insulating material disposed inside thereof is also contaminated with mold and bacteria. Furthermore, even the aluminum sash formed around it is corroded by mold and bacteria. In addition, it is confirmed that mold and bacteria are intensively breeding on the joints of carpets and bathroom tiles.
また、日本の風土におけるコンクリート建築の家屋は、夏場は湿度が高いために鬱陶しく、冬場は暖房の影響で室内の壁面が激しく結露する傾向にある。これらの原因は、建築基準法に基づき、一般マンションの外壁の厚さは１０ｃｍしかないのに、冬場における室内の壁面は、外部から簡単に冷えるため、その壁面には夥しい結露が発生することになる。このため、日本の家屋における壁紙によるカビや細菌の発生についての問題は極めて重要である。 In addition, concrete-built houses in the Japanese climate tend to be annoying due to high humidity in the summer, and in the winter, there is a tendency for the indoor wall surface to condense strongly due to the effect of heating. These causes are based on the Building Standards Law, but the wall surface of a typical apartment building is only 10cm thick, but the indoor wall surface in the winter can be easily cooled from the outside, so that severe dew condensation occurs on the wall surface. Become. For this reason, the problem of mold and bacteria generation by wallpaper in Japanese houses is extremely important.
そこで、本発明者は、先に、紙基材すなわち一般に裏打紙と称されている原紙１ｍ2 に対して、合成繊維を５％以上または無機質材料を５％以上添加することにより、前述した壁紙としての紙質である水中伸度を０．１％未満に設定することができ、これにより通気性を良好にして、カビ抵抗性も増大させることができる壁紙を得ることができることを突き止め、特許出願を行った（特許文献１参照）。 Therefore, the present inventor previously added 5% or more of synthetic fiber or 5% or more of inorganic material to 1 m 2 of a paper base, that is, a base paper generally referred to as backing paper, to obtain the above-mentioned wallpaper. As a paper quality, it is possible to set the degree of elongation in water to less than 0.1%, thereby obtaining a wallpaper that can improve the air permeability and increase the mold resistance. (See Patent Document 1).
また、壁紙等の内装材の表面材料として、従来多く用いられていたポリ塩化ビニルシートに代えて、不織布を使用することが提案されている。すなわち、不織布は廃棄時に公害問題を起こさない環境にやさしい素材であり、また繊維特有の高級な外観や手触りを有していながら、価格的に手頃である等の特性を持っているからである。 In addition, as a surface material for interior materials such as wallpaper, it has been proposed to use a non-woven fabric in place of the conventionally used polyvinyl chloride sheet. That is, non-woven fabric is an environmentally friendly material that does not cause pollution problems at the time of disposal, and it has a high-quality appearance and feel peculiar to fibers, and has such characteristics as being affordable.
しかしながら、不織布を使用する場合、裏打紙との接着には、一般に水系の樹脂エマルジョンや澱粉水溶液等が用いられるが、このような場合においては、不織布や裏打紙が水分を含むことになり、この水分を蒸発除去するための熱エネルギーが必要となり、接着に要する費用が嵩む等の難点がある。 However, when a nonwoven fabric is used, a water-based resin emulsion or an aqueous starch solution is generally used for adhesion to the backing paper. In such a case, the nonwoven fabric or backing paper will contain moisture. Heat energy for evaporating and removing moisture is required, and there is a problem that the cost required for adhesion increases.
そこで、前述した裏打紙と不織布からなる表面材料とを貼り合わせる接合剤として、溶融押し出しされた熱可塑性の合成樹脂、例えばポリエチレンやポリプロピレン等のポリオレフィン系樹脂や、ポリアミド、ポリエステル、合成ゴム、ポリビニルアルコール系あるいは酢酸ビニル共重合体等の樹脂により、裏打紙と不織布とを貼り合わせてなる壁紙等の内装材が提案されている（特許文献２参照）。 Therefore, as a bonding agent for bonding the above-mentioned backing paper and a non-woven fabric surface material, a melt-extruded thermoplastic synthetic resin, for example, a polyolefin-based resin such as polyethylene or polypropylene, polyamide, polyester, synthetic rubber, polyvinyl alcohol An interior material such as a wallpaper in which a backing paper and a nonwoven fabric are bonded together with a resin such as a system or a vinyl acetate copolymer has been proposed (see Patent Document 2).
しかしながら、裏打紙と不織布とを貼り合わせてなる壁紙等の内装材は、裏打紙と不織布とを貼り合わせ加工において、壁紙としての風合いが良く、しかも全体を均質かつ安定にして、しかも連続的な量産を可能にし得るように、有効な接着剤の適用および処理作業の適正化を行うことが困難であった。従って、従来においては、この種の通気性壁紙の量産化が困難であることから、その製造コストも増大し、通気性壁紙の普及を遅らせる要因ともなっている。 However, interior materials such as wallpaper made by laminating backing paper and non-woven fabric have a good texture as wallpaper when laminating backing paper and non-woven fabric, and the whole is homogeneous and stable and continuous. It has been difficult to apply effective adhesives and optimize processing operations to enable mass production. Therefore, conventionally, since it is difficult to mass-produce this type of breathable wallpaper, the manufacturing cost thereof is increased, which is a factor for delaying the spread of the breathable wallpaper.
このような観点から、本発明者は、さらに検討並びに試作を重ねた結果、不織布と多孔質フィルムとを積層してなる通気性積層シートを作成し、この通気性積層シートの一側面に貼合用接着剤を介して裏打紙を貼り合わせ、さらに前記通気性積層シートの他側面に印刷適性を有する繊維材料等からなる化粧層を形成することにより、建物の壁面に対する空気の流通を可能にして建物の水分含有率を一定に保つことができ、壁面と壁紙との間におけるカビや細菌の発生を有効に防止することができ、しかも意匠的審美性に優れた通気性壁紙の開発に成功し、特許出願を行った（特許文献３参照）。 From such a viewpoint, as a result of further examination and trial production, the present inventor created a breathable laminated sheet formed by laminating a nonwoven fabric and a porous film, and bonded to one side of the breathable laminated sheet. By adhering the backing paper through the adhesive, and forming a decorative layer made of a fiber material having printability on the other side of the breathable laminated sheet, it is possible to distribute air to the wall surface of the building. Succeeded in developing a breathable wallpaper that can keep the moisture content of the building constant, can effectively prevent the generation of mold and bacteria between the wall and the wallpaper, and has excellent design aesthetics. A patent application was filed (see Patent Document 3).
すなわち、前記開発に係る通気性壁は、不織布と多孔質フィルムとを積層してなる通気性積層シートを使用し、この通気性積層シートの一側面に貼合用接着剤を介して裏打紙を貼り合わせ、さらに前記通気性積層シートの他側面に印刷適性を有する繊維材料等からなる化粧層を形成したことを特徴とするものである。 That is, the breathable wall according to the development uses a breathable laminated sheet formed by laminating a nonwoven fabric and a porous film, and a backing paper is attached to one side of the breathable laminated sheet via a bonding adhesive. In addition, a decorative layer made of a fiber material having printability or the like is formed on the other side of the breathable laminated sheet.
この場合、通気性積層シートを形成する不織布としては、例えば木綿、ビスコースレーヨン、パルプ等のセルロース系繊維や、ポリエステル、ポリアミド、ポリプロピレン、ポリビニルアルコール、アクリル系等の合成繊維等から構成され、スパンレース法、スパンボンド法、湿式法、サーマル法、ニードルリング法、乾式法、乾式パルプ法、メルトブロー法、フラッシュ紡糸式、エアーレイド式、バインダ接着法等で繊維を結合させて製造したものを適用することができる。 In this case, the nonwoven fabric forming the breathable laminated sheet is composed of cellulose fibers such as cotton, viscose rayon and pulp, synthetic fibers such as polyester, polyamide, polypropylene, polyvinyl alcohol, acrylic, etc. Applicable products manufactured by bonding fibers by lace method, spunbond method, wet method, thermal method, needle ring method, dry method, dry pulp method, melt blow method, flash spinning method, air raid method, binder bonding method, etc. can do.
特に、ポリエステル、アクリル系等の合成繊維を多量に含有する抄紙機により抄造した紙または不織布により製造された従来の通気性壁紙においては、壁面等に対する施工に際し、糊の水分が壁紙の表側に直ちに滲出するため、例えば糊付機により糊付けを行う場合、糊付けして折り畳み、数ｍの壁面まで移動する間に、水分が壁紙に吸収されてしまい、貼着作業が著しく困難となる難点がある。 In particular, in conventional breathable wallpaper made from paper or non-woven fabric made with a paper machine containing a large amount of synthetic fibers such as polyester and acrylic, the moisture content of the glue is immediately on the front side of the wallpaper when applied to the wall surface. In order to exude, for example, when gluing with a gluing machine, moisture is absorbed by the wallpaper while gluing and folding and moving to a wall of several meters, and there is a difficulty that the pasting work becomes extremely difficult.
また、この種の従来における通気性壁紙においては、特にデンプン糊で施工した場合には、水分の除去ないし蒸発がし難いために、栄養分と温度の増大によりカビの発生原因となる難点がある。
さらに、従来における通気性壁紙においては、向こう貼り（壁面への糊付け）には適さないため、壁紙の施工時における寸法安定性に欠けることから、異種の素材（特に和紙等）を積層した施工の容易かつ簡便な通気性壁紙を得ることができない。
In addition, in this type of conventional air-permeable wallpaper, it is difficult to remove or evaporate water, particularly when applied with starch glue, and thus there is a difficulty that causes mold generation due to an increase in nutrients and temperature.
Furthermore, conventional breathable wallpaper is not suitable for pasting (gluing to the wall surface), so it lacks dimensional stability at the time of wallpaper construction. An easy and simple breathable wallpaper cannot be obtained.
そこで、本発明者は、鋭意研究並びに試作を重ねた結果、全重量当りポリエステルまたはアクリル系等の合成繊維を５〜４５重量％と、パルプ、レーヨン等のセルロース系繊維を５５〜９５重量％とを、それぞれ混合した後、抄紙機により抄造し、水中伸度を０．１％未満に設定することにより、前述した種々の問題点を解消することができる通気性壁紙を得ることに成功した。 Therefore, as a result of intensive research and trial production, the inventor of the present invention has 5 to 45% by weight of synthetic fiber such as polyester or acrylic based on the total weight, and 55 to 95% by weight of cellulose fiber such as pulp and rayon. After mixing each, the paper was made by a paper machine and the underwater elongation was set to less than 0.1%, thereby succeeding in obtaining a breathable wallpaper capable of solving the various problems described above.
また、全重量当りポリエステルまたはアクリル系等の合成繊維を５〜４５重量％と、パルプ、レーヨン等のセルロース系繊維を５５〜９５重量％とを、それぞれ混合ないし複合した状態でウェブ状に集積し、不織布として結合成形し、水中伸度を０．１％未満に設定することによっても、前述した種々の問題点を解消することができる通気性壁紙が得られることを突き止めた。 In addition, 5 to 45% by weight of synthetic fiber such as polyester or acrylic based on the total weight and 55 to 95% by weight of cellulose fiber such as pulp and rayon are accumulated in a web state in a mixed or composite state. It was also found that a breathable wallpaper capable of solving the above-mentioned various problems can be obtained by bonding and molding as a nonwoven fabric and setting the underwater elongation to less than 0.1%.
なお、本発明において使用するポリエステルまたはアクリル系等の合成繊維としては、例えば、芯成分が結晶性ポリプロピレンで、鞘成分が芯成分より低融点の特殊ポリオレフィンで被覆したポリオレフィン系熱接着性芯鞘型複合繊維〔ダイワボウ製のＮＢＦ（Ｅ）〕、芯成分がポリエステルで、鞘成分が低融点ポリマーからなる共重合ポリエステルで被覆したポリエステル系芯鞘型複合繊維〔帝人製のテルピス（登録商標）低融点バインダーファイバー〕、あるいはポリエステルホットメルト型の繊維状バインダーであるポリエステルバインダーファイバー〔ユニチカ製のユニチカエステルバインダー“メルティ”（芯鞘構造型／単一ポリマー型〕等を好適に使用することができる。特に、ポリオレフィン系熱接着性芯鞘型複合繊維は、乾式不織布あるいは湿式不織布の用途として有効であり、またポリエステルバインダーファイバーも湿式不織布の用途として有効である。 The synthetic fiber such as polyester or acrylic used in the present invention is, for example, a polyolefin-based heat-adhesive core-sheath type in which the core component is crystalline polypropylene and the sheath component is coated with a special polyolefin having a melting point lower than that of the core component. Composite fiber [Daiwabo NBF (E)], polyester core-sheath type composite fiber coated with a polyester having a core component made of polyester and a sheath component made of a low-melting-point polymer [Terith's Terpis (registered trademark) low-melting point Binder fibers] or polyester binder fibers (unitika ester binder “Melty” (core-sheath structure type / single polymer type) manufactured by Unitika) which are polyester hot melt type fibrous binders can be preferably used. Polyolefin-based heat-adhesive core-sheath composite fibers are dry It is effective as use of nonwoven fabric or wet-laid nonwoven fabric, and polyester binder fibers is also effective as use of the wet-laid nonwoven fabric.
従って、本発明の目的は、壁面等に対する施工に際し、糊の水分が壁紙の表側に直ちに滲出することなく、糊付機により糊付けおよび貼付け作業を容易かつ円滑に行うことができると共に、通気性が良好にしてカビの発生を確実に防止することができ、しかも優れた寸法安定性を有することから異種の素材を積層して意匠的審美性をより一層向上させることができる通気性壁紙の製造方法を提供することにある。 Accordingly, an object of the present invention is to allow easy and smooth gluing and pasting operations with a gluing machine without causing the moisture of the glue to ooze out immediately on the front side of the wallpaper when performing construction on a wall surface or the like, and providing air permeability. A method for producing a breathable wallpaper, which can improve the design aesthetics by stacking dissimilar materials because it can be reliably prevented from generating mold and has excellent dimensional stability. Is to provide.
前記目的を達成するため、本発明の請求項１に記載の通気性壁紙の製造方法は、全重量当りポリエステルからなる合成繊維を５〜４５重量％と、パルプ、レーヨンからなるセルロース系繊維を５５〜９５重量％とを、含有する通気性壁紙を使用し、前記通気性壁紙の表面に、発泡剤入りの塩ビペーストを塗布し、これをゲル化、低温予備発泡させた後、多価カルボン酸または多価カルボン酸無水物を混入した発泡抑制インキを使用し、前記予備発泡させた塩ビペーストに対し凹部とすべき模様部分に印刷加工を施して、加熱発泡させることにより凹凸模様を形成し、立体感のある化粧層を形成することを特徴とする。 In order to achieve the above object, the method for producing a breathable wallpaper according to claim 1 of the present invention comprises 5 to 45% by weight of synthetic fibers made of polyester per total weight and 55 cellulose fibers made of pulp and rayon. -95% by weight containing a breathable wallpaper, and applying a vinyl chloride paste containing a foaming agent to the surface of the breathable wallpaper, gelling it, and pre-foaming it at low temperature, Or using a foam suppression ink mixed with polyvalent carboxylic acid anhydride, applying a printing process to the pattern portion that should be a recess with respect to the pre-foamed PVC paste , forming a concavo-convex pattern by heating and foaming , It is characterized by forming a three-dimensional decorative layer.
本発明の請求項１に記載の製造方法により得られる通気性壁紙よれば、壁面等に対する施工に際し、糊の水分が壁紙の表側に直ちに滲出することなく、糊付機により糊付けおよび貼付け作業を容易かつ円滑に行うことができると共に、通気性が良好にしてカビの発生を確実に防止し、しかも優れた寸法安定性を有する通気性壁紙を得ることができる。 According breathable picture obtained by the production method according to claim 1 of the present invention, upon installation against a wall surface or the like, without water glue immediately exuded on the front side of the wallpaper, facilitate gluing and joining operations by gluing machine In addition, it is possible to obtain a breathable wallpaper that can be smoothly performed, has good breathability, reliably prevents mold generation, and has excellent dimensional stability.
特に、本発明の請求項１に記載の通気性壁紙の製造方法によれば、全重量当りポリエステルからなる合成繊維を５〜４５重量％と、パルプ、レーヨンからなるセルロース系繊維を５５〜９５重量％とにより、抄紙機により抄造した紙として、およびウェブ状に集積して結合成形した不織布として、糊付機により糊付けおよび貼付け作業を容易かつ円滑に行うことができ、通気性が良好にしてカビの発生を確実に防止し、しかも優れた寸法安定性を有する通気性壁紙を、低コストに製造することができる。 In particular, from 55 to 95 weight according to the manufacturing method of breathable wallpaper according, and 5 to 45% by weight of synthetic fibers made of the total weight per polyester, pulp, cellulosic fibers consisting of rayon to claim 1 of the present invention Can be easily and smoothly glued and pasted with a gluing machine as a paper made by a paper machine and as a non-woven fabric that is accumulated in a web and bonded and molded. The air-permeable wallpaper which prevents generation | occurrence | production reliably and has the outstanding dimensional stability can be manufactured at low cost.
次に、本発明に係る通気性壁紙の製造方法につき、通気性壁紙の基本構成とその応用実施例との関係において、添付図面を参照しながら以下詳細に説明する。 Next, a method for producing a breathable wallpaper according to the present invention will be described in detail below with reference to the accompanying drawings in relation to the basic configuration of the breathable wallpaper and its application examples .
図１は、本発明に係る通気性壁紙の基本構成を示す断面構成図である。すなわち、本実施例の通気性壁紙１０Ａは、全重量当りポリエステル系またはアクリル系等の合成繊維を５〜４５重量％と、パルプ、レーヨン等のセルロース系繊維を５５〜９５重量％とを、それぞれ混合して抄紙機により抄造した構成からなる。
FIG. 1 is a cross-sectional configuration diagram showing a basic configuration of a breathable wallpaper according to the present invention. That is, the
このように構成される本実施例の通気性壁紙１０Ａは、次のような特性を有する。
(1) 坪量：７０〔ｇ／ｍ2 〕［標準偏差：２．３］
(2) 厚さ：１５７〔μｍ〕［標準偏差：８］
(3) 浸透性（ 196Ｐa ）：７０〔Ｌ／Ｍ2 ／Ｓ〕［標準偏差：１２］
(4) 引張り強さ（縦方向）：４６５０〔Ｎ／Ｍ〕［標準偏差：５５８］
引張り強さ（横方向）：２９５０〔Ｎ／Ｍ〕［標準偏差：３５４］
(5) 伸び（縦方向）：３〔％〕
伸び（横方向）：８〔％〕
(6) 引裂き（縦方向）：１４５〔Ｇrs〕
引裂き（横方向）：１７５〔Ｇrs〕
(7) 湿気／乾燥比：２２〔％〕
(8) 白色度：７０．５〔％〕
(9) 不透明性：９４．５〔％〕
(10)水滴テスト：９９９〔Ｓeconde〕
The air-
(1) Basis weight: 70 [g / m 2 ] [standard deviation: 2.3]
(2) Thickness: 157 [μm] [Standard deviation: 8]
(3) Permeability (196 Pa): 70 [L / M 2 / S] [Standard deviation: 12]
(4) Tensile strength (longitudinal direction): 4650 [N / M] [standard deviation: 558]
Tensile strength (lateral direction): 2950 [N / M] [standard deviation: 354]
(5) Elongation (longitudinal direction): 3 [%]
Elongation (lateral direction): 8 [%]
(6) Tear (longitudinal direction): 145 [Grs]
Tear (lateral direction): 175 [Grs]
(7) Moisture / dry ratio: 22 [%]
(8) Whiteness: 70.5 [%]
(9) Opacity: 94.5 [%]
(10) Water drop test: 999 [Seconde]
また、本発明に係る通気性壁紙１０Ａは、前記全重量当りポリエステル系またはアクリル系等の合成繊維を５〜４５重量％と、パルプ、レーヨン等のセルロース系繊維を５５〜９５重量％とを、それぞれ混合ないし複合した状態でウェブ状に集積し、結合して不織布とした構成とすることができる。
Further, the
本実施例において適用する合成繊維としては、ポリエステル、ポリアミド、ポリプロピレン、ポリビニルアルコール、アクリル系等の合成繊維を使用することができる。特に、本発明に係る通気性壁紙を製造するに際しては、前述した市販されているポリオレフィン系熱接着性芯鞘型複合繊維〔ダイワボウ製のＮＢＦ（Ｅ）〕、ポリエステル系芯鞘型複合繊維〔帝人製のテルピス（登録商標）低融点バインダーファイバー〕、あるいはポリエステルバインダーファイバー〔ユニチカ製のユニチカエステルバインダー“メルティ”（芯鞘構造型／単一ポリマー型〕を好適に使用することができる。 As synthetic fibers applied in this embodiment, synthetic fibers such as polyester, polyamide, polypropylene, polyvinyl alcohol, and acrylic can be used. In particular, when producing the breathable wallpaper according to the present invention, the above-mentioned commercially available polyolefin-based heat-adhesive core-sheath type composite fiber [NBF (E) manufactured by Daiwabo], polyester-type core-sheath type composite fiber [Teijin Terpis (registered trademark) low melting point binder fiber) or polyester binder fiber [Unitika ester binder “Melty” (core-sheath structure type / single polymer type) manufactured by Unitika] can be preferably used.
本実施例において適用するセルロース系繊維としては、例えば木材パルプ、リンター、その他各種の非木材植物繊維等の天然セルロース繊維、または、針葉樹や広葉樹の化学パルプや機械パルプ等の木材パルプ、古紙パルプ、麻や綿等の非木材天然パルプ、合成化学パルプ、レーヨン等を好適に使用することができる。 Examples of the cellulosic fibers used in this embodiment include natural cellulose fibers such as wood pulp, linter and other various non-wood plant fibers, or wood pulp such as chemical pulp and mechanical pulp of conifers and hardwood, waste paper pulp, Non-wood natural pulp such as hemp and cotton, synthetic chemical pulp, rayon and the like can be suitably used.
なお、本実施例における通気性壁紙１０Ａは、前記構成からなる紙または不織布の製造に際し、水中伸度を０．１％未満に設定することにより、通気性の良好な紙または不織布からなる通気性壁紙１０Ａを得ることができる。
In addition, the air-
図２は、前記実施例１に記載の通気性壁紙１０Ａの応用実施例を示すものである。すなわち、本実施例の通気性壁紙１０Ｂは、前記通気性壁紙１０Ａの表面に、グラビア印刷、フレキソ印刷またはＵＶ印刷等による化粧層１２を施したものである。
FIG. 2 shows an application example of the
図３は、前記実施例１に記載の通気性壁紙１０Ａの最も好適な応用実施例を示すものである。すなわち、本実施例の通気性壁紙１０Ｂ′は、前記通気性壁紙１０Ａの表面の化粧層として、発泡インキまたは発泡抑制インキを使用した発泡印刷により、印刷面に凹凸模様等を設けて、立体感のある化粧層１３を形成したものである。なお、本実施例においては、前述した実施例２におけるグラビア印刷、フレキソ印刷またはＵＶ印刷等による化粧層１２の形成方法を併用することができる。
FIG. 3 shows a most preferred application example of the
特に、本実施例においては、発泡インキとして、例えば水性インキ、有機溶剤型インキを使用し、グラビア印刷やスクリーン印刷により模様の印刷加工を施し、加熱により発泡させて凹凸効果を得るものである。また、発泡抑制インキとしては、例えば無水トリメリット酸のような多価カルボン酸または多価カルボン酸無水物を混入したインキを使用し、壁紙に発泡剤入りの塩ビペーストを塗布し、これをゲル化、低温予備発泡させた後、凹部とすべき模様部分を前記発泡抑制インキにより印刷加工を施し、必要に応じてその上面へ透明塩ビ層を作成して、加熱発泡させることにより凹凸効果を得て、立体感のある化粧層１３を形成したものである。
In particular, in this embodiment, as the foamed ink, for example, water-based ink or organic solvent-type ink is used, a pattern printing process is performed by gravure printing or screen printing, and foaming is performed by heating to obtain an uneven effect. In addition, as the foam suppression ink, for example, an ink mixed with a polyvalent carboxylic acid such as trimellitic anhydride or a polyvalent carboxylic acid anhydride is used. reduction, after cold pre-expanded, the pattern portion to be a concave portion by printing processing by the foam control ink, creating a transparent PVC layer to the upper surface thereof as required, the more uneven effect be heated foam Thus, a
図４は、前記実施例１に記載の通気性壁紙１０Ａの別の応用実施例である。すなわち、本実施例の通気性壁紙１０Ｃは、前記通気性壁紙１０Ａに対し、全面的または部分的に、エンボス加工１４を施したものである。
FIG. 4 is another application example of the
図５は、前記実施例１に記載の通気性壁紙１０Ａの他の応用実施例を示すものである。すなわち、本実施例の通気性壁紙１０Ｄは、前記通気性壁紙１０Ａの表面に、接着材料層１６をラミネート加工し、この接着材料層１６の上面に、洋紙、和紙、襖紙等の紙壁紙１８を貼り合わせたものである。
FIG. 5 shows another application example of the air-
本実施例において、前記接着材料層１６としては、本発明者が先に紙壁紙の製造方法として提案し、特開平１０−２６６０９９号公報に開示された、酢酸ビニル系エマルジョン、アクリル系エマルジョン、エポキシ系エマルジョンおよびウレタン系エマルジョンからなる群から選択された水性の合成樹脂エマルジョン接着剤を好適に使用することができる。このような接着材料層１６を使用することにより、紙壁紙１８の貼り合わせに際して、寸法安定性に優れ、高品質の通気性壁紙１０Ｄを得ることができる。
In this embodiment, as the
また、前記紙壁紙１８として、特に手漉き和紙や機械漉き和紙を使用する場合には、吸水および乾燥による伸縮が著しく、寸法安定性に問題がある。しかし、前述したように、通気性壁紙１０Ａの表面に、接着材料層１６をラミネート加工することにより、紙壁紙１８として機械漉き和紙を貼り合わせ、しかも前記和紙の表面に適宜処理剤を多層に設けることにより、和紙の特性を充分に備え、インクジェットによる印刷可能な通気性を有する和紙壁紙１０Ｄを得ることができる。
Further, when handmade Japanese paper or machine-made Japanese paper is used as the
図６は、前記実施例１に記載の通気性壁紙１０Ａのさらに他の応用実施例である。すなわち、本実施例の通気性壁紙１０Ｅは、接着材料層１６をラミネート加工した前記通気性壁紙１０Ａの前記接着材料層１６の上面に、織物壁紙２０を貼り合わせたものである。本実施例においても、前記実施例と同様に、接着材料層１６を使用することによって、織物壁紙２０の貼り合わせに際して、寸法安定性に優れ、高品質の通気性を有する織物壁紙１０Ｅを得ることができる。
FIG. 6 shows still another application example of the
次に、前述した実施例１に記載される本発明の通気性壁紙１０Ａについて、カビ抵抗性試験を行った。なお、一般建築から検出されるカビ（菌）の種類として、５７種の菌が確認されている。
Next, a mold resistance test was performed on the
（カビ抵抗性試験）
Ａ．壁紙試料
(1) 生分解性壁紙［２８０ｇ／ｍ2 ］（試料Ｎo.１,２）
(2) 本発明に係る通気性壁紙［２３０ｇ／ｍ2 ］（試料Ｎo.３,４,５）
(3) 塩ビ（ＰＶＣ）壁紙［２９０ｇ／ｍ2 ］（試料Ｎo.６,７,８）
Ｂ．壁紙用接着剤
(1) ドイツ、ヘンケル社の接着剤［ヘンケル剤］（試料Ｎo.１,４,７）
(2) ドイツ、ヘンケル社の防カビ剤入り接着剤［防カビ剤］（試料Ｎo.２,５,８）
(3) 市販のデンプン糊［デンプン糊］（試料Ｎo.３）
(Mold resistance test)
A. Wallpaper sample
(1) Biodegradable wallpaper [280 g / m 2 ] (Sample No. 1, 2 )
(2) Breathable wallpaper according to the present invention [230 g / m 2 ] (Sample No. 3, 4, 5 )
(3) PVC (PVC) wallpaper [290 g / m 2 ] (Sample No. 6, 7, 8 )
B. Adhesive for wallpaper
(1) Adhesive [Henkel Agent] from Henkel, Germany (Sample No. 1, 4, 7 )
(2) Germany, Henkel Corporation of fungicide containing adhesive [fungicide] (sample No.2,5,8)
(3) Commercial starch paste [ starch paste] (Sample No. 3 )
Ｃ．カビ抵抗性試験結果
以上のカビ抵抗性試験結果から、本発明に係る通気性壁紙（試料Ｎo.３,４,５）は、壁紙用接着剤の種類に関係なくカビ抵抗性に優れていることが確認された。また、その他の壁紙については、防カビ剤入り接着剤を使用することにより、カビ抵抗性を高めることができることが確認された。 From the above mold resistance test results, it was confirmed that the breathable wallpaper according to the present invention (sample No. 3, 4, 5 ) was excellent in mold resistance regardless of the type of the wallpaper adhesive. For other wallpaper, it was confirmed that the mold resistance can be increased by using an anti-mold adhesive.
以上、本発明の好適な実施例について説明したが、本発明は前記実施例に限定されることなく、例えば本発明の実施例１で得られる通気性壁紙は、各種の壁紙のベースペーパーないしは裏打ち紙として広範囲に適用することができると共に、その他本発明の精神を逸脱しない範囲内において、多くの設計変更が可能である。 The preferred embodiments of the present invention have been described above. However, the present invention is not limited to the above-described embodiments. For example, the breathable wallpaper obtained in the first embodiment of the present invention is a base paper or backing of various types of wallpaper. The present invention can be applied to a wide range of paper, and many other design changes can be made without departing from the spirit of the present invention.
１０Ａ、１０Ｂ、１０Ｂ′、１０Ｃ、１０Ｄ、１０Ｅ 通気性壁紙
１２ 化粧層
１３ 印刷発泡による化粧層
１４ エンボス加工
１６ 接着材料層
１８ 紙壁紙
２０ 織物壁紙
10A, 10B, 10B ', 10C, 10D, 10E
Claims (1)
前記通気性壁紙の表面に、発泡剤入りの塩ビペーストを塗布し、これをゲル化、低温予備発泡させた後、多価カルボン酸または多価カルボン酸無水物を混入した発泡抑制インキを使用し、前記予備発泡させた塩ビペーストに対し凹部とすべき模様部分に印刷加工を施して、加熱発泡させることにより凹凸模様を形成し、立体感のある化粧層を形成することを特徴とする通気性壁紙の製造方法。 Using a breathable wallpaper containing 5 to 45% by weight of synthetic fiber made of polyester and 55 to 95% by weight of cellulosic fiber made of pulp and rayon per total weight,
After applying a vinyl chloride paste containing a foaming agent to the surface of the breathable wallpaper, gelling it, pre-foaming it at low temperature, and then using a foam suppression ink mixed with polyvalent carboxylic acid or polyvalent carboxylic acid anhydride. The air permeability is characterized in that the pre-foamed PVC paste is subjected to a printing process on a pattern portion to be formed into a recess, and is heated and foamed to form a concavo-convex pattern to form a three-dimensional decorative layer. Wallpaper manufacturing method.