JP4744483B2 - Manufacturing method of polarizing plate, polarizing plate, optical film, and image display device - Google Patents
Manufacturing method of polarizing plate, polarizing plate, optical film, and image display device Download PDFInfo
- Publication number
- JP4744483B2 JP4744483B2 JP2007169533A JP2007169533A JP4744483B2 JP 4744483 B2 JP4744483 B2 JP 4744483B2 JP 2007169533 A JP2007169533 A JP 2007169533A JP 2007169533 A JP2007169533 A JP 2007169533A JP 4744483 B2 JP4744483 B2 JP 4744483B2
- Authority
- JP
- Japan
- Prior art keywords
- polarizing plate
- polarizer
- adhesive
- film
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、偏光板の製造方法に関する。また本発明は当該製造方法により得られた偏光板に関する。当該偏光板はこれ単独で、またはこれを積層した光学フィルムとして液晶表示装置(LCD)、有機EL表示装置、CRT、PDP等の画像表示装置を形成しうる。 The present invention relates to a method for producing a polarizing plate. Moreover, this invention relates to the polarizing plate obtained by the said manufacturing method. The polarizing plate can form an image display device such as a liquid crystal display device (LCD), an organic EL display device, a CRT, or a PDP alone or as an optical film in which the polarizing plate is laminated.
液晶表示装置は、液晶のスイッチングによる偏光状態を可視化させたものであり、その表示原理から、偏光子の両面に透明保護フィルムを接着剤層により貼り合わせた偏光板が用いられている。偏光子としては、例えばポリビニルアルコールにヨウ素を吸着させ、延伸した構造のヨウ素系偏光子が高透過率、高偏光度を有することから、最も一般的な偏光子として広く使用されている。透明保護フィルムとしては、透湿度の高いトリアセチルセルロース等が用いられる。 The liquid crystal display device visualizes the polarization state by switching of the liquid crystal, and from the display principle, a polarizing plate is used in which a transparent protective film is bonded to both sides of the polarizer with an adhesive layer. As a polarizer, for example, an iodine-based polarizer having a stretched structure obtained by adsorbing iodine to polyvinyl alcohol has a high transmittance and a high degree of polarization, and is therefore widely used as the most common polarizer. As the transparent protective film, triacetyl cellulose having a high moisture permeability is used.
前記接着剤層の形成に用いる接着剤としては、例えば、ポリビニルアルコール系の材料を水に溶解した、いわゆる水系接着剤が用いられている。しかし、ポリビニルアルコール系接着剤は、高温高湿下で長時間放置すると、吸湿して接着力が低下するためフィルムに剥離が生じやすくなったり、偏光板の寸法安定性が低下したりして、液晶ディスプレイの色相変化が生じるという問題がある。上記問題に対して、透明保護フィルムとして用いるトリアセチルセルロースフィルムの表面をケン化処理して、接着剤と透明保護フィルムの接着力を向上させることが提案されている(特許文献1)。また、前記接着剤として、アセトアセチル基含有ポリビニルアルコール系樹脂と架橋剤を含有するものが提案されている(特許文献2)。 As the adhesive used for forming the adhesive layer, for example, a so-called aqueous adhesive in which a polyvinyl alcohol-based material is dissolved in water is used. However, when the polyvinyl alcohol-based adhesive is left for a long time at high temperature and high humidity, the film absorbs moisture and the adhesive strength is reduced, so that the film is easily peeled off, or the dimensional stability of the polarizing plate is reduced. There is a problem that a hue change of a liquid crystal display occurs. In response to the above problem, it has been proposed to improve the adhesive force between the adhesive and the transparent protective film by saponifying the surface of the triacetylcellulose film used as the transparent protective film (Patent Document 1). Moreover, what contains an acetoacetyl group containing polyvinyl alcohol-type resin and a crosslinking agent as said adhesive agent is proposed (patent document 2).
一方、水系接着剤の代わりに、熱硬化型、活性エネルギー線硬化型等の硬化型接着剤を使用することが提案されている(特許文献3)。しかし、これら硬化型接着剤を用いた場合でも、偏光子と透明保護フィルムの接着力は十分ではなかった。偏光板には、偏光子と透明保護フィルムの接着強度をより向上させることが求められている。
本発明は、偏光子と透明保護フィルムとの接着力を向上させることができる、偏光板の製造方法を提供することを目的とする。 An object of this invention is to provide the manufacturing method of a polarizing plate which can improve the adhesive force of a polarizer and a transparent protective film.
また本発明は前記製造方法により得られた偏光板を提供することを目的とする。さらに本発明は、当該偏光板を積層した光学フィルムを提供すること、さらには、当該偏光板、光学フィルムを用いた液晶表示装置等の画像表示装置を提供することを目的とする。 Moreover, this invention aims at providing the polarizing plate obtained by the said manufacturing method. Furthermore, an object of the present invention is to provide an optical film in which the polarizing plate is laminated, and to provide an image display device such as a liquid crystal display device using the polarizing plate and the optical film.
本発明者らは前記課題を解決すべく鋭意検討を重ねた結果、以下に示す偏光板の製造方法により前記目的に達成できることを見出し、本発明を完成するに至った。 As a result of intensive studies to solve the above-mentioned problems, the present inventors have found that the object can be achieved by the following method for producing a polarizing plate, and have completed the present invention.
すなわち本発明は、偏光子の少なくとも一方の面に、接着剤層を介して透明保護フィルムが設けられている偏光板の製造方法であって、
偏光子の接着剤層が設けられる面に活性化処理を施す工程、
偏光子の前記接着剤層を形成する面および/または透明保護フィルムの前記接着剤層を形成する面に、接着剤を塗工する工程、
偏光子と透明保護フィルムとを、前記接着剤を介して貼り合わせる工程、を有することを特徴とする偏光板の製造方法、に関する。
That is, the present invention is a method for producing a polarizing plate in which a transparent protective film is provided on at least one surface of a polarizer via an adhesive layer,
A step of activating the surface on which the adhesive layer of the polarizer is provided,
Applying an adhesive to the surface of the polarizer forming the adhesive layer and / or the surface of the transparent protective film forming the adhesive layer;
It has the process of bonding a polarizer and a transparent protective film through the said adhesive agent, It is related with the manufacturing method of the polarizing plate characterized by the above-mentioned.
前記偏光板の製造方法において、活性化処理としては、コロナ処理、プラズマ処理、グロー処理およびオゾン処理から選ばれるいずれか少なくとも一つの処理を施すことができる。 In the method for producing the polarizing plate, as the activation treatment, at least one treatment selected from corona treatment, plasma treatment, glow treatment, and ozone treatment can be performed.
前記偏光板の製造方法において、偏光子としては、ポリビニルアルコール系偏光子が好適である。 In the method for producing the polarizing plate, a polyvinyl alcohol polarizer is suitable as the polarizer.
前記偏光板の製造方法において、
前記活性化処理によって、偏光子の表面は親水化処理が施されており、かつ、
前記接着剤層は水系接着剤により形成し、
前記貼り合わせ工程の後に、乾燥工程により接着剤層を形成することができる。
In the method for producing the polarizing plate,
The surface of the polarizer has been subjected to a hydrophilic treatment by the activation treatment, and
The adhesive layer is formed of a water-based adhesive,
After the bonding process, an adhesive layer can be formed by a drying process.
前記親水化処理により、偏光子の表面は、対水の接触角が、10〜50°になるように行うことが好ましい。また、水系接着剤としては、ポリビニルアルコール系接着剤が好適である。 It is preferable that the surface of the polarizer is subjected to the hydrophilic treatment so that the contact angle with water is 10 to 50 °. Moreover, as a water-system adhesive agent, a polyvinyl alcohol-type adhesive agent is suitable.
前記偏光板の製造方法において、
前記活性化処理によって、偏光子の表面は活性処理が施されており、かつ、
前記接着剤層はラジカル硬化型接着剤により形成し、
前記貼り合わせ工程の後に、硬化工程により接着剤層を形成することができる。
In the method for producing the polarizing plate,
By the activation treatment, the surface of the polarizer has been activated, and
The adhesive layer is formed of a radical curable adhesive,
After the bonding step, an adhesive layer can be formed by a curing step.
前記ラジカル硬化型接着剤としては電子線硬化型接着剤が好適であり、この場合には、硬化工程として電子線硬化工程が施される。 An electron beam curable adhesive is suitable as the radical curable adhesive, and in this case, an electron beam curing step is performed as a curing step.
また本発明は、前記製造方法により得られた偏光板に関する。 Moreover, this invention relates to the polarizing plate obtained by the said manufacturing method.
また本発明は、前記偏光板が、少なくとも1枚積層されていることを特徴とする光学フィルム、に関する。 The present invention also relates to an optical film in which at least one polarizing plate is laminated.
さらに本発明は、前記偏光板または前記光学フィルムが用いられていることを特徴とする画像表示装置、に関する。 Furthermore, this invention relates to the image display apparatus characterized by using the said polarizing plate or the said optical film.
本発明では、偏光子と透明保護フィルムを、接着剤により貼り合わせる前に偏光子に活性化処理を施している。活性化処理(例えば、コロナ処理)によって、偏光子(ポリビニルアルコール系偏光子)の表面には、親水性官能基(−COOHや−OH)やラジカル活性種が導入されると推測される。かかる活性化処理によって偏光子表面の状態を変化させて、偏光子と接着剤層との接着力を向上させ、ひいては偏光子と透明保護フィルムとを非常に強行に接着している偏光板を得ることができる。 In the present invention, the polarizer and the transparent protective film are subjected to an activation treatment before being bonded together with an adhesive. It is presumed that hydrophilic functional groups (—COOH and —OH) and radical active species are introduced into the surface of the polarizer (polyvinyl alcohol polarizer) by the activation treatment (for example, corona treatment). By such activation treatment, the surface state of the polarizer is changed to improve the adhesive force between the polarizer and the adhesive layer, and as a result, a polarizing plate is obtained in which the polarizer and the transparent protective film are bonded extremely strongly. be able to.
前述の通り偏光子の表面には、前記親水性官能基が導入されると推測されることから、その結果、偏光子表面の濡れ性が向上する。接着剤として水系接着剤を用いた場合には、水系接着剤と偏光子表面の濡れ性が改善され、密着性が向上する。その結果として、水系接着剤と偏光子表面の接着力が向上する。また、コロナ処理によって、導入された親水性官能基(−COOHや−OH)が水系接着剤と反応し、接着力向上に寄与することも考えられる。 As described above, it is assumed that the hydrophilic functional group is introduced into the surface of the polarizer, and as a result, the wettability of the polarizer surface is improved. When a water-based adhesive is used as the adhesive, the wettability between the water-based adhesive and the polarizer surface is improved, and the adhesion is improved. As a result, the adhesive strength between the water-based adhesive and the polarizer surface is improved. It is also conceivable that the introduced hydrophilic functional group (—COOH or —OH) reacts with the water-based adhesive by corona treatment and contributes to an improvement in adhesive strength.
また偏光子の表面には、前記活性化処理によりラジカル活性種が導入されると推測されることから、そこにラジカル硬化型接着剤を塗布して、硬化させることで、偏光子表面のラジカルとラジカル硬化型接着剤が反応して、偏光子と接着剤とが強固に接着する。つまり、偏光子表面にラジカルを発生させることで、偏光子表面とラジカル硬化型接着剤とが反応しやすくなる。 In addition, since it is presumed that radical activation species are introduced into the surface of the polarizer by the activation treatment, a radical curable adhesive is applied to the surface and cured, so that radicals on the surface of the polarizer The radical curable adhesive reacts to firmly bond the polarizer and the adhesive. That is, by generating radicals on the surface of the polarizer, the surface of the polarizer and the radical curable adhesive can easily react.
ラジカル硬化型接着剤としては、紫外線、電子線等の活性化エネルギー線による硬化型接着剤、特に電子線硬化型接着剤が好適である。電子線硬化型接着剤によれば、接着剤の硬化方法に電子線を用いる(すなわちドライラミネーション)ことによって、熱硬化型法、紫外線硬化法のような、加熱工程が不要になり、生産性を非常に高くすることができ、また偏光子の光学特性が劣化するおそれがない。 As the radical curable adhesive, a curable adhesive using activation energy rays such as ultraviolet rays and electron beams, particularly an electron beam curable adhesive is suitable. According to the electron beam curable adhesive, the use of an electron beam as a method for curing the adhesive (that is, dry lamination) eliminates the need for a heating step such as a thermosetting method and an ultraviolet curing method, thereby reducing productivity. It can be very high, and there is no possibility that the optical properties of the polarizer will deteriorate.
本発明の偏光板の製造方法に用いる偏光子は、各種のものを使用できる。偏光子としては、たとえば、ポリビニルアルコール系フィルム、部分ホルマール化ポリビニルアルコール系フィルム、エチレン・酢酸ビニル共重合体系部分ケン化フィルム等の親水性高分子フィルムに、ヨウ素や二色性染料の二色性物質を吸着させて一軸延伸したもの、ポリビニルアルコールの脱水処理物やポリ塩化ビニルの脱塩酸処理物等ポリエン系配向フィルム等があげられる。これらの中でも、ポリビニルアルコール系フィルムとヨウ素などの二色性物質からなる偏光子が好適である。 Various types of polarizers can be used for the polarizing plate production method of the present invention. Examples of polarizers include dichroic iodine and dichroic dyes on hydrophilic polymer films such as polyvinyl alcohol films, partially formalized polyvinyl alcohol films, and ethylene / vinyl acetate copolymer partially saponified films. Examples thereof include polyene-based oriented films such as those obtained by adsorbing substances and uniaxially stretched, polyvinyl alcohol dehydrated products and polyvinyl chloride dehydrochlorinated products. Among these, a polarizer composed of a polyvinyl alcohol film and a dichroic material such as iodine is preferable.
ポリビニルアルコール系偏光子は、ポリビニルアルコール樹脂フィルムを二色性物質(代表的には、ヨウ素、二色性染料)で染色して一軸延伸したものが用いられる。ポリビニルアルコール系樹脂フィルムを構成するポリビニルアルコール系樹脂の重合度は、好ましくは100〜10000、さらに好ましくは1000〜5000である。重合度が低すぎると、所定の延伸を行う際に延伸切れしやすく、また重合度が高すぎると、延伸する際に張力が異常に必要となり、機械的に延伸できなくなるおそれがある。 As the polyvinyl alcohol-based polarizer, one obtained by dying a polyvinyl alcohol resin film with a dichroic substance (typically iodine or a dichroic dye) and uniaxially stretching is used. The polymerization degree of the polyvinyl alcohol-based resin constituting the polyvinyl alcohol-based resin film is preferably 100 to 10,000, more preferably 1000 to 5,000. If the degree of polymerization is too low, the film tends to be stretched when performing predetermined stretching, and if the degree of polymerization is too high, tension may be abnormally required for stretching, and mechanical stretching may not be possible.
偏光子を構成するポリビニルアルコール系樹脂フィルムは、任意の適切な方法(例えば樹脂を水または有機溶剤に溶解した溶液を流延製膜する流延法、キャスト法、押出法)で成形され得る。偏光子の厚みは偏光板が用いられるLCDの目的や用途に応じて適宜設定されるが、通常、10〜300μm程度である。好ましくは20〜100μmである。 The polyvinyl alcohol-based resin film constituting the polarizer can be formed by any appropriate method (for example, a casting method in which a solution obtained by dissolving a resin in water or an organic solvent is cast, a casting method, an extrusion method). The thickness of the polarizer is appropriately set according to the purpose and application of the LCD in which the polarizing plate is used, but is usually about 10 to 300 μm. Preferably it is 20-100 micrometers.
偏光子の製造方法としては、目的、使用材料および条件などに応じて任意の適切な方法が採用される。例えば、上記ポリビニルアルコール系樹脂フィルムを、通常、膨潤、染色、架橋、延伸、水洗および乾燥工程を含む一連の製造工程に供する方式が採用される。乾燥工程を除く各処理工程においては、それぞれの工程に用いられる溶液を含む液中にポリビニルアルコール系樹脂フィルムを浸漬することにより処理を行う。膨潤、染色、架橋、延伸、水洗および乾燥の各処理の順番、回数および実施の有無は、目的、使用材料および条件などに応じて適亘設定されえる。例えば、いくつかの処理を1つの工程で同時に行ってもよく、膨潤処理、染色処理および架橋処理を同時に行ってもよい。また例えば、架橋処理を延伸処理の前後に行うことが、好適に採用され得る。また例えば、水洗処理は、全ての処理の後に行ってもよく、特定の処理の後のみに行ってもよい。 As a manufacturing method of the polarizer, any appropriate method is adopted depending on the purpose, material used, conditions and the like. For example, the system which uses the said polyvinyl alcohol-type resin film for a series of manufacturing processes including a swelling, dyeing | staining, bridge | crosslinking, extending | stretching, a water washing, and a drying process is employ | adopted normally. In each processing step except the drying step, the treatment is performed by immersing the polyvinyl alcohol-based resin film in a liquid containing a solution used in each step. The order, number of times, and presence / absence of each treatment of swelling, dyeing, crosslinking, stretching, washing and drying can be appropriately set according to the purpose, materials used and conditions. For example, several processes may be performed simultaneously in one step, and the swelling process, the dyeing process, and the crosslinking process may be performed simultaneously. Further, for example, it can be suitably employed to perform the crosslinking treatment before and after the stretching treatment. For example, the water washing process may be performed after all the processes, or may be performed only after a specific process.
膨潤工程は、代表的には、上記ポリビニルアルコール系樹脂フィルムを水で満たした処理浴中に浸漬することより行われる。この処理により、ポリビニルアルコール系樹脂フィルム表面の汚れやブロッキング防止剤を洗浄すると共に、ポリビニルアルコール系樹脂フィルムを膨潤させることで染色ムラ等の不均一性を防止できる。膨潤浴には、グリセリンやヨウ化カリウム等が適宜に添加される。膨潤浴の温度は、通常20〜60℃程度であり、膨潤浴への浸漬時間は、通常0.1〜10分間程度である。 The swelling step is typically performed by immersing the polyvinyl alcohol resin film in a treatment bath filled with water. By this treatment, dirt on the surface of the polyvinyl alcohol-based resin film and an anti-blocking agent can be washed, and unevenness such as uneven dyeing can be prevented by swelling the polyvinyl alcohol-based resin film. Glycerin, potassium iodide or the like is appropriately added to the swelling bath. The temperature of the swelling bath is usually about 20 to 60 ° C., and the immersion time in the swelling bath is usually about 0.1 to 10 minutes.
染色工程は、代表的には、上記ポリビニルアルコール系樹脂フィルムを、ヨウ素等の二色性物質を含む処理浴中に浸漬することにより行われる。染色浴の溶液に用いられる溶媒は、水が一般的に使用されるが、水と相溶性を有する有機溶媒が適量添加されていてもよい。二色性物質は、溶媒100重量部に対して、通常、0.01〜0.5重量部、好ましくは0.02〜0.4の割合で用いられる。二色性物質としてヨウ素を用いる場合は、染色浴の溶液はヨウ化物等の助剤をさらに含有することが好ましい。染色効率が改善されるからである。助剤は、溶媒100重量部に対して、好ましくは0.01〜10重量部、さらに好ましくは0.02〜8重量部の割合で用いられる。ヨウ化物の具体例としては、ヨウ化カリウム、ヨウ化リチウム、ヨウ化ナトリウム、ヨウ化亜鉛、ヨウ化アルミニウム、ヨウ化鉛、ヨウ化銅、ヨウ化バリウム、ヨウ化カルシウム、ヨウ化錫、ヨウ化チタンなどがあげられる。染色浴の温度は、通常、20〜70℃程度であり、染色浴への浸漬時間は、通常、1〜20分間程度である。 The dyeing process is typically performed by immersing the polyvinyl alcohol resin film in a treatment bath containing a dichroic substance such as iodine. As the solvent used for the dye bath solution, water is generally used, but an appropriate amount of an organic solvent compatible with water may be added. The dichroic substance is usually used in a proportion of 0.01 to 0.5 parts by weight, preferably 0.02 to 0.4 parts, per 100 parts by weight of the solvent. When iodine is used as the dichroic substance, the dye bath solution preferably further contains an auxiliary agent such as iodide. This is because the dyeing efficiency is improved. The auxiliary is preferably used in a proportion of 0.01 to 10 parts by weight, more preferably 0.02 to 8 parts by weight, with respect to 100 parts by weight of the solvent. Specific examples of iodide include potassium iodide, lithium iodide, sodium iodide, zinc iodide, aluminum iodide, lead iodide, copper iodide, barium iodide, calcium iodide, tin iodide, and iodide. Examples include titanium. The temperature of the dyeing bath is usually about 20 to 70 ° C., and the immersion time in the dyeing bath is usually about 1 to 20 minutes.
架橋工程は、代表的には、上記染色されたポリビニルアルコール系樹脂フィルムを、架橋剤を含む処理欲中に浸漬することによって行われる。架橋割としては任意の適切な架橋剤が採用される。架橋剤の具体例としては、ホウ酸、ホウ砂等のホウ素化合物、グリオキザール、グルタルアルデヒド等があげられる。これらは、単独で、または組み合わせて使用される。架橋浴の溶液に用いられる溶媒は、水が一般的に使用されるが、水と相溶性を有する有機溶媒が適量添加されていてもよい。架橋剤は、溶媒100重量部に対して、通常、2〜15重量部、好ましくは3〜10重量部の割合で用いられる。架橋剤の濃度が1重量部未満の場合は、十分な光学特性を得ることができない。架橋剤の濃度が15重量部を超える場合は、延伸時にフィルムに発生する応力が大きくなり、得られる偏光板が収縮してしまう可能性がある。架橋浴の溶液は、ヨウ化物等の助剤をさらに含有することが望ましい。面内に均一な特性が得られやすいからである。助剤の濃度は好ましくは0.05〜15重量%、さらに好ましくは0.5〜8重量%である。ヨウ化物の具体例は、染色工程の場合と同様である。架橋浴の温度は、通常、20〜70℃程度、好ましくは40〜60℃である。架橋浴への浸漬時間は、通常、1秒間〜15分間程度、好ましくは5秒間〜10分間である。 The crosslinking step is typically performed by immersing the dyed polyvinyl alcohol-based resin film in a treatment desire containing a crosslinking agent. Arbitrary appropriate crosslinking agents are employ | adopted as a crosslinking rate. Specific examples of the crosslinking agent include boron compounds such as boric acid and borax, glyoxal, and glutaraldehyde. These may be used alone or in combination. As the solvent used for the solution of the crosslinking bath, water is generally used, but an appropriate amount of an organic solvent having compatibility with water may be added. The crosslinking agent is usually used at a ratio of 2 to 15 parts by weight, preferably 3 to 10 parts by weight, with respect to 100 parts by weight of the solvent. When the concentration of the crosslinking agent is less than 1 part by weight, sufficient optical properties cannot be obtained. When the concentration of the crosslinking agent exceeds 15 parts by weight, the stress generated in the film during stretching increases, and the resulting polarizing plate may shrink. It is desirable that the solution of the crosslinking bath further contains an auxiliary agent such as iodide. This is because it is easy to obtain uniform characteristics in the plane. The concentration of the auxiliary agent is preferably 0.05 to 15% by weight, more preferably 0.5 to 8% by weight. Specific examples of iodide are the same as those in the dyeing process. The temperature of the crosslinking bath is usually about 20 to 70 ° C, preferably 40 to 60 ° C. The immersion time in the crosslinking bath is usually about 1 second to 15 minutes, preferably 5 seconds to 10 minutes.
延伸工程は、上記のようにいずれの段階で行ってもよい。具体的には、染色処理の後に行ってもよく、染色処理の前に行ってもよく、膨潤処理、染色処理および架橋処理と同時に行ってもよく、架橋処理の後に行ってもよい。ポリビニルアルコール系樹脂フィルムの累積延伸倍率は、通常、4倍以上にする。好ましくは4〜8倍、さらに好ましくは5〜6.5倍である。累積延伸倍率が4倍未満の場合には、高偏光度の偏光板を得ることが困難となる。累積延伸倍率が8倍を超える場合はポリビニルアルコール系樹脂フィルムが破断しやすくなる場合がある。延伸の具体的な方法としては、任意の適切な方法が採用される。例えば、湿式延伸法を採用した場合には、ポリビニルアルコール系樹脂フィルムを処理浴中で所定の倍率に延伸する。延伸浴の溶液としては、水または有機溶媒(例えばエタノール)などの溶媒中に、各種金属塩、ヨウ素、ホウ素または亜鉛の化合物を添加した溶液が好適に用いられる。 The stretching process may be performed at any stage as described above. Specifically, it may be performed after the dyeing process, may be performed before the dyeing process, may be performed simultaneously with the swelling process, the dyeing process, and the crosslinking process, or may be performed after the crosslinking process. The cumulative draw ratio of the polyvinyl alcohol-based resin film is usually 4 times or more. Preferably it is 4-8 times, More preferably, it is 5-6.5 times. When the cumulative draw ratio is less than 4, it becomes difficult to obtain a polarizing plate having a high degree of polarization. When the cumulative draw ratio exceeds 8 times, the polyvinyl alcohol-based resin film may be easily broken. Arbitrary appropriate methods are employ | adopted as a specific method of extending | stretching. For example, when a wet stretching method is employed, a polyvinyl alcohol resin film is stretched at a predetermined magnification in a treatment bath. As the stretching bath solution, a solution in which various metal salts, iodine, boron or zinc compounds are added to a solvent such as water or an organic solvent (for example, ethanol) is preferably used.
水洗工程は、代表的には、上記各種処理を施されたポリビニルアルコール系樹脂フィルムを処理浴中に浸漬することによって行われる。水洗工程によりポリビニルアルコール系樹脂フィルムの不要残存物を洗い流すことができる。水洗浴は、純水であってもよく、ヨウ化物(例えば、ヨウ化カリウム、ヨウ化ナトリウム等)の水溶液であってもよい。ヨウ化物水溶液の濃度は、好ましくは0.1〜10重量%である。ヨウ化物水溶液には硫酸亜鉛、塩化亜鉛などの助剤を添加してもよい。水洗浴の温度は好ましくは10〜60℃、さらに好ましくは30〜40℃である。浸漬時間は1秒間〜1分間である。水洗工程は1回だけでもよく、必要に応じて複数回行ってもよい。複数回実施される場合は、各処理に用いられる水洗浴に含まれる添加剤の種類や濃度は適宜に調整される。例えば、水洗工程は上記各種処理を施されたポリビニルアルコール系樹脂フィルムをヨウ化カリウム水溶液(0.1〜10重量%、10〜60℃)に1秒間〜1分間程度浸漬する工程と、純水ですすぐ工程とを含む。また、水洗工程において、偏光子の表面改質や、偏光子の乾燥効率を上げるために、水と相溶性を有する有機溶媒(例えば、エタノ−ルなど)を適宜添加してもよい。 The water washing step is typically performed by immersing the polyvinyl alcohol-based resin film subjected to the above-described various treatments in a treatment bath. The unnecessary residue of the polyvinyl alcohol-based resin film can be washed away by the water washing step. The washing bath may be pure water or an aqueous solution of iodide (for example, potassium iodide, sodium iodide, etc.). The concentration of the aqueous iodide solution is preferably 0.1 to 10% by weight. An auxiliary agent such as zinc sulfate or zinc chloride may be added to the aqueous iodide solution. The temperature of the washing bath is preferably 10 to 60 ° C, more preferably 30 to 40 ° C. The immersion time is 1 second to 1 minute. The washing step may be performed only once, or may be performed a plurality of times as necessary. When implemented several times, the kind and density | concentration of the additive contained in the washing bath used for each process are adjusted suitably. For example, the water washing step includes a step of immersing the polyvinyl alcohol resin film subjected to the above various treatments in an aqueous potassium iodide solution (0.1 to 10% by weight, 10 to 60 ° C.) for about 1 second to 1 minute, and pure water. Including rinsing process. In the water washing step, an organic solvent having compatibility with water (for example, ethanol) may be added as appropriate in order to improve the surface of the polarizer and increase the drying efficiency of the polarizer.
乾燥工程は、任意の適切な方法(例えば、自然乾燥、送風乾燥、加熱乾燥)が採用されうる。例えば、加熱乾燥の場合の乾燥温度は、通常、20〜150℃程度、好ましくは40〜100℃であり、乾燥時間は、通常、1〜10分間程度である。以上のようにして偏光子が得られる。 Arbitrary appropriate methods (For example, natural drying, ventilation drying, heat drying) may be employ | adopted for a drying process. For example, the drying temperature in the case of heat drying is usually about 20 to 150 ° C., preferably 40 to 100 ° C., and the drying time is usually about 1 to 10 minutes. A polarizer is obtained as described above.
本発明において用いる偏光子は、水分率が好ましくは20重量%以下、より好ましくは0〜17重量%、さらに好ましくは1〜16重量%である。水分率が20重量%より大きいいと、得られた偏光板の寸法変化が大きくなり、高温下あるいは高温高湿下における寸法変化が大きくなってしまうという問題が生じるおそれがある。 The polarizer used in the present invention has a moisture content of preferably 20% by weight or less, more preferably 0 to 17% by weight, and still more preferably 1 to 16% by weight. If the moisture content is larger than 20% by weight, the dimensional change of the obtained polarizing plate becomes large, which may cause a problem that the dimensional change at high temperature or high temperature and high humidity becomes large.
本発明の、偏光子の水分率は、任意の適切な方法で調整すればよい。例えば偏光子の製造工程における乾燥工程の条件を調整することにより制御する方法があげられる。 The moisture content of the polarizer of the present invention may be adjusted by any appropriate method. For example, there is a method of controlling by adjusting the conditions of the drying process in the manufacturing process of the polarizer.
偏光子の水分率は、以下の方法により測定される。すなわち、偏光子を、100×100mmの大きさに切り出して、このサンプルの初期重量を測定した。続いて、このサンプルを120℃で2時間乾燥し、乾燥重量を測定して、下記式により水分率を測定した。水分率(重量%)={(初期重量−乾燥重量)/初期重量}×100。重量の測定はそれぞれ3回ずつ行い、その平均値を用いた。 The moisture content of the polarizer is measured by the following method. That is, the polarizer was cut out to a size of 100 × 100 mm, and the initial weight of this sample was measured. Subsequently, this sample was dried at 120 ° C. for 2 hours, the dry weight was measured, and the moisture content was measured by the following formula. Moisture content (% by weight) = {(initial weight−dry weight) / initial weight} × 100. The weight was measured three times, and the average value was used.
透明保護フィルムを構成する材料としては、例えば透明性、機械的強度、熱安定性、水分遮断性、等方性などに優れる熱可塑性樹脂が用いられる。このような熱可塑性樹脂の具体例としては、トリアセチルセルロース等のセルロース樹脂、ポリエステル樹脂、ポリエーテルスルホン樹脂、ポリスルホン樹脂、ポリカーボネート樹脂、ポリアミド樹脂、ポリイミド樹脂、ポリオレフィン樹脂、(メタ)アクリル樹脂、環状ポリオレフィン樹脂(ノルボルネン系樹脂)、ポリアリレート樹脂、ポリスチレン樹脂、ポリビニルアルコール樹脂、およびこれらの混合物があげられる。なお、偏光子の片側には、透明保護フィルムが接着剤層により貼り合わされるが、他の片側には、透明保護フィルムとして、(メタ)アクリル系、ウレタン系、アクリルウレタン系、エポキシ系、シリコーン系等の熱硬化性樹脂または紫外線硬化型樹脂を用いることができる。透明保護フィルム中には任意の適切な添加剤が1種類以上含まれていてもよい。添加剤としては、例えば、紫外線吸収剤、酸化防止剤、滑剤、可塑剤、離型剤、着色防止剤、難燃剤、核剤、帯電防止剤、顔料、着色剤などがあげられる。透明保護フィルム中の上記熱可塑性樹脂の含有量は、好ましくは50〜100重量%、より好ましくは50〜99重量%、さらに好ましくは60〜98重量%、特に好ましくは70〜97重量%である。透明保護フィルム中の上記熱可塑性樹脂の含有量が50重量%以下の場合、熱可塑性樹脂が本来有する高透明性等が十分に発現できないおそれがある。 As a material constituting the transparent protective film, for example, a thermoplastic resin excellent in transparency, mechanical strength, thermal stability, moisture barrier property, isotropy and the like is used. Specific examples of such thermoplastic resins include cellulose resins such as triacetyl cellulose, polyester resins, polyethersulfone resins, polysulfone resins, polycarbonate resins, polyamide resins, polyimide resins, polyolefin resins, (meth) acrylic resins, cyclic Examples thereof include polyolefin resins (norbornene resins), polyarylate resins, polystyrene resins, polyvinyl alcohol resins, and mixtures thereof. A transparent protective film is bonded to one side of the polarizer by an adhesive layer. On the other side, as a transparent protective film, (meth) acrylic, urethane-based, acrylurethane-based, epoxy-based, silicone A thermosetting resin such as a system or an ultraviolet curable resin can be used. One or more kinds of arbitrary appropriate additives may be contained in the transparent protective film. Examples of the additive include an ultraviolet absorber, an antioxidant, a lubricant, a plasticizer, a release agent, a coloring inhibitor, a flame retardant, a nucleating agent, an antistatic agent, a pigment, and a coloring agent. The content of the thermoplastic resin in the transparent protective film is preferably 50 to 100% by weight, more preferably 50 to 99% by weight, still more preferably 60 to 98% by weight, and particularly preferably 70 to 97% by weight. . When content of the said thermoplastic resin in a transparent protective film is 50 weight% or less, there exists a possibility that the high transparency etc. which a thermoplastic resin originally has cannot fully be expressed.
また、透明保護フィルムとしては、特開2001−343529号公報(WO01/37007)に記載のポリマーフィルム、例えば、(A)側鎖に置換および/または非置換イミド基を有する熱可塑性樹脂と、(B)側鎖に置換および/または非置換フェニルならびにニトリル基を有する熱可塑性樹脂を含有する樹脂組成物があげられる。具体例としてはイソブチレンとN−メチルマレイミドからなる交互共重合体とアクリロニトリル・スチレン共重合体とを含有する樹脂組成物のフィルムがあげられる。フィルムは樹脂組成物の混合押出品などからなるフィルムを用いることができる。これらのフィルムは位相差が小さく、光弾性係数が小さいため偏光板の歪みによるムラなどの不具合を解消することができ、また透湿度が小さいため、加湿耐久性に優れる。 Moreover, as a transparent protective film, the polymer film as described in Unexamined-Japanese-Patent No. 2001-343529 (WO01 / 37007), for example, (A) thermoplastic resin which has a substituted and / or unsubstituted imide group in a side chain, ( B) Resin compositions containing thermoplastic resins having substituted and / or unsubstituted phenyl and nitrile groups in the side chains. A specific example is a film of a resin composition containing an alternating copolymer composed of isobutylene and N-methylmaleimide and an acrylonitrile / styrene copolymer. As the film, a film made of a mixed extruded product of the resin composition or the like can be used. Since these films have a small phase difference and a small photoelastic coefficient, problems such as unevenness due to the distortion of the polarizing plate can be eliminated, and since the moisture permeability is small, the humidification durability is excellent.
透明保護フィルムの厚さは、適宜に決定しうるが、一般には強度や取扱性等の作業性、薄層性などの点より1〜500μm程度である。特に1〜300μmが好ましく、5〜200μmがより好ましい。透明保護フィルムは、5〜150μmの場合に特に好適である。 Although the thickness of a transparent protective film can be determined suitably, generally it is about 1-500 micrometers from points, such as workability | operativity, such as intensity | strength and handleability, and thin layer property. 1-300 micrometers is especially preferable, and 5-200 micrometers is more preferable. The transparent protective film is particularly suitable when the thickness is 5 to 150 μm.
なお、偏光子の両側に透明保護フィルムを設ける場合、その表裏で同じポリマー材料からなる保護フィルムを用いてもよく、異なるポリマー材料等からなる保護フィルムを用いてもよい。 In addition, when providing a transparent protective film on both sides of a polarizer, the protective film which consists of the same polymer material may be used by the front and back, and the protective film which consists of a different polymer material etc. may be used.
本発明の透明保護フィルムとしては、セルロース樹脂、ポリカーボネート樹脂、環状ポリオレフィン樹脂および(メタ)アクリル樹脂から選ばれるいずれか少なくとも1つを用いるのが好ましい。本発明の電子線硬化型偏光板用接着剤は、上記各種の透明保護フィルムに対して、好適な接着性を示す。特に、本発明の電子線硬化型偏光板用接着剤は、接着性を満足することが困難であったアクリル樹脂に対しても良好な接着性を示す。 As the transparent protective film of the present invention, it is preferable to use at least one selected from cellulose resin, polycarbonate resin, cyclic polyolefin resin, and (meth) acrylic resin. The adhesive for electron beam curable polarizing plates of the present invention exhibits suitable adhesion to the various transparent protective films. In particular, the electron beam curable polarizing plate adhesive of the present invention exhibits good adhesion to acrylic resins that have been difficult to satisfy adhesiveness.
セルロース樹脂は、セルロースと脂肪酸のエステルである。このようセルロースエステル系樹脂の具体例としでは、セルローストリアセテート、セルロースジアセテート、セルローストリプロピオネート、セルロースジプロピオネート等があげられる。これらのなかでも、セルローストリアセテートが特に好ましい。セルローストリアセテートは多くの製品が市販されており、入手容易性やコストの点でも有利である。セルローストリアセテートの市販品の例としては、富士フイルム社製の商品名「UV−50」、「UV−80」、「SH−80」、「TD−80U」、「TD−TAC」、「UZ−TAC」や、コニカ社製の「KCシリーズ」等があげられる。一般的にこれらセルローストリアセテートは、面内位相差(Re)はほぼゼロであるが、厚み方向位相差(Rth)は、〜60nm程度を有している。 Cellulose resin is an ester of cellulose and fatty acid. Specific examples of the cellulose ester resin include cellulose triacetate, cellulose diacetate, cellulose tripropionate, and cellulose dipropionate. Among these, cellulose triacetate is particularly preferable. Many products of cellulose triacetate are commercially available, which is advantageous in terms of availability and cost. Examples of commercially available cellulose triacetate include trade names “UV-50”, “UV-80”, “SH-80”, “TD-80U”, “TD-TAC”, and “UZ-” manufactured by Fujifilm Corporation. TAC ”,“ KC series ”manufactured by Konica, and the like. In general, these cellulose triacetates have an in-plane retardation (Re) of almost zero, but a thickness direction retardation (Rth) of about ˜60 nm.
なお、厚み方向位相差が小さいセルロース樹脂フィルムは、例えば、上記セルロース樹脂を処理することにより得られる。例えばシクロペンタノン、メチルエチルケトン等の溶剤を塗工したポリエチレンテレフタレート、ポリプロピレン、ステンレスなどの基材フィルムを、一般的なセルロース系フィルムに貼り合わせ、加熱乾燥(例えば80〜150℃で3〜10分間程度)した後、基材フィルムを剥離する方法;ノルボルネン系樹脂、(メタ)アクリル系樹脂などをシクロペンタノン、メチルエチルケトン等の溶剤に溶解した溶液を一般的なセルロース樹脂フィルムに塗工し加熱乾燥(例えば80〜150℃で3〜10分間程度)した後、塗工フィルムを剥離する方法などがあげられる。 In addition, the cellulose resin film with a small thickness direction phase difference is obtained by processing the said cellulose resin, for example. For example, a base film such as polyethylene terephthalate, polypropylene, and stainless steel coated with a solvent such as cyclopentanone and methyl ethyl ketone is bonded to a general cellulose film and dried by heating (for example, at 80 to 150 ° C. for about 3 to 10 minutes). ) And then peeling the base film; a solution obtained by dissolving norbornene resin, (meth) acrylic resin, etc. in a solvent such as cyclopentanone, methyl ethyl ketone, etc. is applied to a general cellulose resin film and dried by heating ( For example, a method of peeling the coated film after 80 to 150 ° C. for about 3 to 10 minutes is mentioned.
また、厚み方向位相差が小さいセルロース樹脂フィルムとしては、脂肪置換度を制御した脂肪酸セルロース系樹脂フィルムを用いることができる。一般的に用いられるトリアセチルセルロースでは酢酸置換度が2.8程度であるが、好ましくは酢酸置換度を1.8〜2.7に制御することによってRthを小さくすることができる。上記脂肪酸置換セルロース系樹脂に、ジブチルフタレート、p−トルエンスルホンアニリド、クエン酸アセチルトリエチル等の可塑剤を添加することにより、Rthを小さく制御することができる。可塑剤の添加量は、脂肪酸セルロース系樹脂100重量部に対して、好ましくは40重量部以下、より好ましくは1〜20重量部、さらに好ましくは1〜15重量部である。 Moreover, as a cellulose resin film with a small thickness direction retardation, the fatty acid cellulose resin film which controlled the fat substitution degree can be used. Generally used triacetyl cellulose has an acetic acid substitution degree of about 2.8. Preferably, the Rth can be reduced by controlling the acetic acid substitution degree to 1.8 to 2.7. Rth can be controlled to be small by adding a plasticizer such as dibutyl phthalate, p-toluenesulfonanilide, acetyltriethyl citrate to the fatty acid-substituted cellulose resin. The addition amount of the plasticizer is preferably 40 parts by weight or less, more preferably 1 to 20 parts by weight, and still more preferably 1 to 15 parts by weight with respect to 100 parts by weight of the fatty acid cellulose resin.
環状ポリオレフィン樹脂の具体的としては、好ましくはノルボルネン系樹脂である。環状オレフィン系樹脂は、環状オレフィンを重合単位として重合される樹脂の総称であり、例えば、特開平1−240517号公報、特開平3−14882号公報、特開平3−122137号公報等に記載されている樹脂があげられる。具体例としては、環状オレフィンの開環(共)重合体、環状オレフィンの付加重合体、環状オレフィンとエチレン、プロピレン等のα−オレフィンとその共重合体(代表的にはランダム共重合体)、および、これらを不飽和カルボン酸やその誘導体で変性したグラフト重合体、ならびに、それらの水素化物などがあげられる。環状オレフィンの具体例としては、ノルボルネン系モノマーがあげられる。 Specific examples of the cyclic polyolefin resin are preferably norbornene resins. The cyclic olefin-based resin is a general term for resins that are polymerized using a cyclic olefin as a polymerization unit, and is described in, for example, JP-A-1-240517, JP-A-3-14882, JP-A-3-122137, and the like. Resin. Specific examples include ring-opening (co) polymers of cyclic olefins, addition polymers of cyclic olefins, cyclic olefins and α-olefins such as ethylene and propylene (typically random copolymers), And graft polymers obtained by modifying them with an unsaturated carboxylic acid or a derivative thereof, and hydrides thereof. Specific examples of the cyclic olefin include norbornene monomers.
環状ポリオレフィン樹脂としては、種々の製品が市販されている。具体例としては、日本ゼオン株式会社製の商品名「ゼオネックス」、「ゼオノア」、JSR株式会社製の商品名「アートン」、TICONA社製の商品名「トーパス」、三井化学株式会社製の商品名「APEL」があげられる。 Various products are commercially available as the cyclic polyolefin resin. As specific examples, trade names “ZEONEX” and “ZEONOR” manufactured by ZEON CORPORATION, product names “ARTON” manufactured by JSR Corporation, “TOPAS” manufactured by TICONA, and product names manufactured by Mitsui Chemicals, Inc. “APEL”.
(メタ)アクリル系樹脂としては、Tg(ガラス転移温度)が好ましくは115℃以上、より好ましくは120℃以上、さらに好ましくは125℃以上、特に好ましくは130℃以上である。Tgが115℃以上であることにより、偏光板の耐久性に優れたものとなりうる。上記(メタ)アクリル系樹脂のTgの上限値は特に限定きれないが、成形性当の観点から、好ましくは170℃以下である。(メタ)アクリル系樹脂からは、面内位相差(Re)、厚み方向位相差(Rth)がほぼゼロものフィルムを得ることができる。 The (meth) acrylic resin preferably has a Tg (glass transition temperature) of 115 ° C. or higher, more preferably 120 ° C. or higher, still more preferably 125 ° C. or higher, and particularly preferably 130 ° C. or higher. When Tg is 115 ° C. or higher, the polarizing plate can be excellent in durability. Although the upper limit of Tg of the (meth) acrylic resin is not particularly limited, it is preferably 170 ° C. or less from the viewpoint of moldability. From (meth) acrylic resin, a film having in-plane retardation (Re) and thickness direction retardation (Rth) of almost zero can be obtained.
(メタ)アクリル系樹脂としては、本発明の効果を損なわない範囲内で、任意の適切な(メタ)アクリル系樹脂を採用し得る。例えば、ポリメタクリル酸メチルなどのポリ(メタ)アクリル酸エステル、メタクリル酸メチル−(メタ)アクリル酸共重合、メタクリル酸メチル−(メタ)アクリル酸エステル共重合体、メタクリル酸メチル−アクリル酸エステル−(メタ)アクリル酸共重合体、(メタ)アクリル酸メチル−スチレン共重合体(MS樹脂など)、脂環族炭化水素基を有する重合体(例えば、メタクリル酸メチル−メタクリル酸シクロヘキシル共重合体、メタクリル酸メチル−(メタ)アクリル酸ノルボルニル共重合体など)があげられる。好ましくは、ポリ(メタ)アクリル酸メチルなどのポリ(メタ)アクリル酸C1−6アルキルがあげられる。より好ましくはメタクリル酸メチルを主成分(50〜100重量%、好ましくは70〜100重量%)とするメタクリル酸メチル系樹脂があげられる。 As the (meth) acrylic resin, any appropriate (meth) acrylic resin can be adopted as long as the effects of the present invention are not impaired. For example, poly (meth) acrylic acid ester such as polymethyl methacrylate, methyl methacrylate- (meth) acrylic acid copolymer, methyl methacrylate- (meth) acrylic acid ester copolymer, methyl methacrylate-acrylic acid ester- (Meth) acrylic acid copolymer, (meth) methyl acrylate-styrene copolymer (MS resin, etc.), polymer having an alicyclic hydrocarbon group (for example, methyl methacrylate-cyclohexyl methacrylate copolymer, Methyl methacrylate- (meth) acrylate norbornyl copolymer, etc.). Preferably, poly (meth) acrylate C1-6 alkyl such as poly (meth) acrylate methyl is used. More preferred is a methyl methacrylate resin containing methyl methacrylate as a main component (50 to 100% by weight, preferably 70 to 100% by weight).
(メタ)アクリル系樹脂の具体例として、例えば、三菱レイヨン株式会社製のアクリペットVHやアクリペットVRL20A、特開2004−70296号公報に記載の分子内に環構造を有する(メタ)アクリル系樹脂、分子内架橋や分子内環化反応により得られる高Tg(メタ)アクリル樹脂系があげられる。 Specific examples of (meth) acrylic resins include (meth) acrylic resins having a ring structure in the molecule described in, for example, Acrypet VH and Acrypet VRL20A manufactured by Mitsubishi Rayon Co., Ltd., and JP-A-2004-70296. And a high Tg (meth) acrylic resin system obtained by intramolecular crosslinking or intramolecular cyclization reaction.
(メタ)アクリル系樹脂として、ラクトン環構造を有する(メタ)アクリル系樹脂を用いることもできる。高い耐熱性、高い透明性、二軸延伸することにより高い機械的強度を有するからである。 As the (meth) acrylic resin, a (meth) acrylic resin having a lactone ring structure can also be used. It is because it has high mechanical strength by high heat resistance, high transparency, and biaxial stretching.
ラクトン環構造を有する(メタ)アクリル系樹脂としては、特開2000−230016号公報、特開2001−151814号公報、特開2002−120326号公報、特開2002−254544号公報、特開2005−146084号公報などに記載の、ラクトン環構造を有する(メタ)アクリル系樹脂があげられる。 Examples of the (meth) acrylic resin having a lactone ring structure include JP 2000-230016, JP 2001-151814, JP 2002-120326, JP 2002-254544, and JP 2005. Examples thereof include (meth) acrylic resins having a lactone ring structure described in Japanese Patent No. 146084.
ラクトン環構造を有する(メタ)アクリル系樹脂は、好ましくは下記一般式(化1)で表される環擬構造を有する。 The (meth) acrylic resin having a lactone ring structure preferably has a ring pseudo structure represented by the following general formula (Formula 1).
式中、R1、R2およびR3は、それぞれ独立に、水素原子または炭素原子数1〜20の有機残基を示す。なお、有機残基は酸素原子を含んでいてもよい。 Wherein, R 1, R 2 and R 3 each independently represent a hydrogen atom or an organic residue having 1 to 20 carbon atoms. The organic residue may contain an oxygen atom.
ラクトン環構造を有する(メタ)アクリル系樹脂の構造中の一般式(化1)で表されるラクトン環構造の含有割合は、好ましくは5〜90重量%、より好ましくは10〜70重量%、さらに好ましくは10〜60重量%、特に好ましくは10〜50重量%である。ラクトン環構造を有する(メタ)アクリル系樹脂の構造中の一般式(化1)で表されるラクトン環構造の含有割合が5重量%よりも少ないと、耐熱性、耐溶剤性、表面硬度が不十分になるおそれがある。ラクトン環構造を有する(メタ)アクリル系樹脂の構造中の一般式(化1)で表されるラクトン環構造の含有割合が90重量%より多いと、成形加工性に乏しくなるおそれがある。 The content ratio of the lactone ring structure represented by the general formula (Formula 1) in the structure of the (meth) acrylic resin having a lactone ring structure is preferably 5 to 90% by weight, more preferably 10 to 70% by weight, More preferably, it is 10 to 60% by weight, and particularly preferably 10 to 50% by weight. When the content of the lactone ring structure represented by the general formula (Chemical Formula 1) in the structure of the (meth) acrylic resin having a lactone ring structure is less than 5% by weight, the heat resistance, solvent resistance, and surface hardness are low. May be insufficient. If the content of the lactone ring structure represented by the general formula (Chemical Formula 1) in the structure of the (meth) acrylic resin having a lactone ring structure is more than 90% by weight, molding processability may be poor.
ラクトン環構造を有する(メタ)アクリル系樹脂は、質量平均分子量(重量平均分子量と称することも有る)が、好ましくは1000〜2000000、より好ましくは5000〜1000000、さらに好ましくは10000〜500000、特に好ましくは50000〜500000である。質量平均分子量が上記範囲から外れると、成型加工性の点から好ましくない。 The (meth) acrylic resin having a lactone ring structure has a mass average molecular weight (sometimes referred to as a weight average molecular weight) of preferably 1,000 to 2,000,000, more preferably 5,000 to 1,000,000, still more preferably 10,000 to 500,000, and particularly preferably. Is 50,000 to 500,000. If the mass average molecular weight is out of the above range, it is not preferable from the viewpoint of molding processability.
ラクトン環構造を有する(メタ)アクリル系樹脂は、Tgが好ましくは115℃以上、より好ましくは120℃以上、さらに好ましくは125℃以上、特に好ましくは130℃以上である。Tgが115℃以上であることから、例えば、透明保護フィルムとして偏光板に組み入れた場合に、耐久性に優れたものとなる。上記ラクトン環構造を有する(メタ)アクリル系樹脂のTgの上限値は特に限定されないが、成形性などの観点から、好ましくは170℃以下である。 The (meth) acrylic resin having a lactone ring structure preferably has a Tg of 115 ° C. or higher, more preferably 120 ° C. or higher, still more preferably 125 ° C. or higher, and particularly preferably 130 ° C. or higher. Since Tg is 115 ° C. or higher, for example, when incorporated into a polarizing plate as a transparent protective film, it has excellent durability. Although the upper limit of Tg of the (meth) acrylic resin having the lactone ring structure is not particularly limited, it is preferably 170 ° C. or less from the viewpoint of moldability and the like.
ラクトン環構造を有する(メタ)アクリル系樹脂は、射出成形により得られる成形品の、ASTM−D−1003に準じた方法で測定される全光線透過率が、高ければ高いほど好ましく、好ましくは85%以上、より好ましくは88%以上、さらに好ましくは90%以上である。全光線透過率は透明性の目安であり、全光線透過率が85%未満であると、透明性が低下するおそれがある。 The (meth) acrylic resin having a lactone ring structure is preferably as the total light transmittance of a molded product obtained by injection molding measured by a method according to ASTM-D-1003 is higher, preferably 85. % Or more, more preferably 88% or more, and still more preferably 90% or more. The total light transmittance is a measure of transparency. If the total light transmittance is less than 85%, the transparency may be lowered.
前記透明保護フィルムは、正面位相差が40nm未満、かつ、厚み方向位相差が80nm未満であるものが、通常、用いられる。正面位相差Reは、Re=(nx−ny)×d、で表わされる。厚み方向位相差Rthは、Rth=(nx−nz)×d、で表される。また、Nz係数は、Nz=(nx−nz)/(nx−ny)、で表される。[ただし、フィルムの遅相軸方向、進相軸方向及び厚さ方向の屈折率をそれぞれnx、ny、nzとし、d(nm)はフィルムの厚みとする。遅相軸方向は、フィルム面内の屈折率の最大となる方向とする。]。なお、透明保護フィルムは、できるだけ色付きがないことが好ましい。厚み方向の位相差値が−90nm〜+75nmである保護フィルムが好ましく用いられる。かかる厚み方向の位相差値(Rth)が−90nm〜+75nmのものを使用することにより、透明保護フィルムに起因する偏光板の着色(光学的な着色)をほぼ解消することができる。厚み方向位相差値(Rth)は、さらに好ましくは−80nm〜+60nm、特に−70nm〜+45nmが好ましい。 As the transparent protective film, one having a front phase difference of less than 40 nm and a thickness direction retardation of less than 80 nm is usually used. The front phase difference Re is represented by Re = (nx−ny) × d. The thickness direction retardation Rth is represented by Rth = (nx−nz) × d. The Nz coefficient is represented by Nz = (nx−nz) / (nx−ny). [However, the refractive indexes in the slow axis direction, the fast axis direction, and the thickness direction of the film are nx, ny, and nz, respectively, and d (nm) is the thickness of the film. The slow axis direction is the direction that maximizes the refractive index in the film plane. ]. In addition, it is preferable that a transparent protective film has as little color as possible. A protective film having a thickness direction retardation value of −90 nm to +75 nm is preferably used. By using a film having a thickness direction retardation value (Rth) of −90 nm to +75 nm, the coloring (optical coloring) of the polarizing plate caused by the transparent protective film can be almost eliminated. The thickness direction retardation value (Rth) is more preferably −80 nm to +60 nm, and particularly preferably −70 nm to +45 nm.
一方、前記透明保護フィルムとして、正面位相差が40nm以上および/または、厚み方向位相差が80nm以上の位相差を有する位相差板を用いることができる。正面位相差は、通常、40〜200nmの範囲に、厚み方向位相差は、通常、80〜300nmの範囲に制御される。透明保護フィルムとして位相差板を用いる場合には、当該位相差板が透明保護フィルムとしても機能するため、薄型化を図ることができる。 On the other hand, as the transparent protective film, a phase difference plate having a phase difference with a front phase difference of 40 nm or more and / or a thickness direction retardation of 80 nm or more can be used. The front phase difference is usually controlled in the range of 40 to 200 nm, and the thickness direction phase difference is usually controlled in the range of 80 to 300 nm. When a retardation plate is used as the transparent protective film, the retardation plate functions also as a transparent protective film, so that the thickness can be reduced.
位相差板としては、高分子素材を一軸または二軸延伸処理してなる複屈折性フィルム、液晶ポリマーの配向フィルム、液晶ポリマーの配向層をフィルムにて支持したものなどがあげられる。位相差板の厚さも特に制限されないが、20〜150μm程度が一般的である。 Examples of the retardation plate include a birefringent film obtained by uniaxially or biaxially stretching a polymer material, a liquid crystal polymer alignment film, and a liquid crystal polymer alignment layer supported by a film. The thickness of the retardation plate is not particularly limited, but is generally about 20 to 150 μm.
高分子素材としては、例えば、ポリビニルアルコール、ポリビニルブチラール、ポリメチルビニルエーテル、ポリヒドロキシエチルアクリレート、ヒドロキシエチルセルロース、ヒドロキシプロピルセルロース、メチルセルロース、ポリカーボネート、ポリアリレート、ポリスルホン、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリエーテルスルホン、ポリフェニレンスルファイド、ポリフェニレンオキサイド、ポリアリルスルホン、ポリアミド、ポリイミド、ポリオレフィン、ポリ塩化ビニル、セルロース樹脂、環状ポリオレフィン樹脂(ノルボルネン系樹脂)、またはこれらの二元系、三元系各種共重合体、グラフト共重合体、ブレンド物などがあげられる。これらの高分子素材は延伸等により配向物(延伸フィルム)となる。 Examples of the polymer material include polyvinyl alcohol, polyvinyl butyral, polymethyl vinyl ether, polyhydroxyethyl acrylate, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, polycarbonate, polyarylate, polysulfone, polyethylene terephthalate, polyethylene naphthalate, polyether sulfone, Polyphenylene sulfide, polyphenylene oxide, polyallylsulfone, polyamide, polyimide, polyolefin, polyvinyl chloride, cellulose resin, cyclic polyolefin resin (norbornene resin), or any of these binary, ternary copolymers, graft copolymers Examples thereof include polymers and blends. These polymer materials become an oriented product (stretched film) by stretching or the like.
液晶ポリマーとしては、例えば、液晶配向性を付与する共役性の直線状原子団(メソゲン)がポリマーの主鎖や側鎖に導入された主鎖型や側鎖型の各種のものなどをあげられる。主鎖型の液晶ポリマーの具体例としては、屈曲性を付与するスペーサー部でメソゲン基を結合した構造の、例えばネマチック配向性のポリエステル系液晶性ポリマー、ディスコティックポリマーやコレステリックポリマーなどがあげられる。側鎖型の液晶ポリマーの具体例としては、ポリシロキサン、ポリアクリレート、ポリメタクリレート又はポリマロネートを主鎖骨格とし、側鎖として共役性の原子団からなるスペーサー部を介してネマチック配向付与性のパラ置換環状化合物単位からなるメソゲン部を有するものなどがあげられる。これらの液晶ポリマーは、例えば、ガラス板上に形成したポリイミドやポリビニルアルコール等の薄膜の表面をラビング処理したもの、酸化ケイ素を斜方蒸着したものなどの配向処理面上に液晶性ポリマーの溶液を展開して熱処理することにより行われる。 Examples of the liquid crystal polymer include various main chain types and side chain types in which a conjugated linear atomic group (mesogen) imparting liquid crystal alignment is introduced into the main chain or side chain of the polymer. . Specific examples of the main chain type liquid crystal polymer include a nematic alignment polyester liquid crystal polymer, a discotic polymer, and a cholesteric polymer having a structure in which a mesogen group is bonded at a spacer portion that imparts flexibility. Specific examples of the side chain type liquid crystal polymer include polysiloxane, polyacrylate, polymethacrylate, or polymalonate as a main chain skeleton, and a nematic alignment-providing para-substitution through a spacer portion composed of a conjugated atomic group as a side chain. Examples thereof include those having a mesogenic part composed of a cyclic compound unit. These liquid crystal polymers are prepared by, for example, applying a solution of a liquid crystalline polymer on an alignment treatment surface such as a surface of a thin film such as polyimide or polyvinyl alcohol formed on a glass plate or an oblique deposition of silicon oxide. This is done by developing and heat treatment.
位相差板は、例えば各種波長板や液晶層の複屈折による着色や視角等の補償を目的としたものなどの使用目的に応じた適宜な位相差を有するものであって良く、2種以上の位相差板を積層して位相差等の光学特性を制御したものなどであっても良い。 The retardation plate may have an appropriate retardation according to the purpose of use, such as those for the purpose of compensating for various wavelength plates or birefringence of liquid crystal layers and compensation of viewing angle, etc. It may be one in which retardation plates are stacked and optical characteristics such as retardation are controlled.
位相差板は、nx=ny>nz、nx>ny>nz、nx>ny=nz、nx>nz>ny、nz=nx>ny、nz>nx>ny、nz>nx=ny、の関係を満足するものが、各種用途に応じて選択して用いられる。なお、ny=nzとは、nyとnzが完全に同一である場合だけでなく、実質的にnyとnzが同じ場合も含む。 The retardation plate has a relationship of nx = ny> nz, nx> ny> nz, nx> ny = nz, nx> nz> ny, nz = nx> ny, nz> nx> ny, nz> nx = ny. What is satisfactory is selected and used according to various applications. Note that ny = nz includes not only the case where ny and nz are completely the same, but also the case where ny and nz are substantially the same.
例えば、nx>ny>nz、を満足する位相差板では、正面位相差は40〜100nm、厚み方向位相差は100〜320nm、Nz係数は1.8〜4.5を満足するものを用いるのが好ましい。例えば、nx>ny=nz、を満足する位相差板(ポジティブAプレート)では、正面位相差は100〜200nmを満足するものを用いるのが好ましい。例えば、nz=nx>ny、を満足する位相差板(ネガティブAプレート)では、正面位相差は100〜200nmを満足するものを用いるのが好ましい。例えば、nx>nz>ny、を満足する位相差板では、正面位相差は150〜300nm、Nz係数は0を超え〜0.7を満足するものを用いるのが好ましい。また、上記の通り、例えば、nx=ny>nz、nz>nx>ny、またはnz>nx=ny、を満足する用いることができる。 For example, in a phase difference plate that satisfies nx> ny> nz, a surface plate having a front phase difference of 40 to 100 nm, a thickness direction phase difference of 100 to 320 nm, and an Nz coefficient of 1.8 to 4.5 is used. Is preferred. For example, in a retardation plate (positive A plate) that satisfies nx> ny = nz, it is preferable to use a retardation plate that satisfies a front phase difference of 100 to 200 nm. For example, for a retardation plate (negative A plate) that satisfies nz = nx> ny, it is preferable to use a retardation plate that satisfies a front phase difference of 100 to 200 nm. For example, in a retardation plate satisfying nx> nz> ny, it is preferable to use a retardation plate having a front phase difference of 150 to 300 nm and an Nz coefficient exceeding 0 to 0.7. Further, as described above, for example, nx = ny> nz, nz> nx> ny, or nz> nx = ny can be used.
透明保護フィルムは、適用される液晶表示装置に応じて適宜に選択できる。例えば、VA(VerticalAlignment,MVA,PVA含む)の場合は、偏光板の少なくとも片方(セル側)の透明保護フィルムが位相差を有している方が望ましい。具体的な位相差として、Re=0〜240nm、Rth=0〜500nmの範囲である事が望ましい。三次元屈折率で言うと、nx>ny=nz、nx>ny>nz、nx>nz>ny、nx=ny>nz(一軸,二軸,Z化,ネガティブCプレート)の場合が望ましい。液晶セルの上下に偏光板を使用する際、液晶セルの上下共に、位相差を有している、または上下いずれかの透明保護フィルムが位相差を有していてもよい。 The transparent protective film can be appropriately selected according to the applied liquid crystal display device. For example, in the case of VA (including Vertical Alignment, MVA, and PVA), it is desirable that at least one of the polarizing plates (cell side) has a retardation. As specific phase differences, it is desirable that Re = 0 to 240 nm and Rth = 0 to 500 nm. In terms of the three-dimensional refractive index, nx> ny = nz, nx> ny> nz, nx> nz> ny, nx = ny> nz (uniaxial, biaxial, Z-ized, negative C plate) is desirable. When polarizing plates are used above and below the liquid crystal cell, both the upper and lower sides of the liquid crystal cell may have a phase difference, or any one of the upper and lower transparent protective films may have a phase difference.
例えば、IPS(In−Plane Switing,FFS含む)の場合、偏光板の片方の透明保護フィルムが位相差を有している場合、有していない場合のいずれも使用できる。例えば、位相差を有していない場合は、液晶セルの上下(セル側)ともに位相差を有していない場合が望ましい。位相差を有している場合は、液晶セルの上下ともに位相差を有している場合、上下のいずれかが位相差を有している場合が望ましい(例えば、上側にZ化、下側に位相差なしの場合や、上側にAプレート、下側にポジティブCプレートの場合)。位相差を有している場合、Re=−500〜500nm、Rth=−500〜500nmの範囲が望ましい。三次元屈折率で言うと、nx>ny=nz、nx>nz>ny、nz>nx=ny、nz>nx>ny(一軸,Z化,ポジティブCプレート、ポジティブAプレート)が望ましい。 For example, in the case of IPS (including In-Plane Switching, FFS), both cases where the transparent protective film on one side of the polarizing plate has a phase difference and does not have a phase difference can be used. For example, when there is no phase difference, it is desirable that the liquid crystal cell does not have a phase difference both above and below (cell side). When the liquid crystal cell has a phase difference, it is desirable that the liquid crystal cell has a phase difference on both the upper and lower sides. When there is no phase difference, or when the A plate is on the upper side and the positive C plate is on the lower side). When it has a phase difference, it is desirable that Re = −500 to 500 nm and Rth = −500 to 500 nm. In terms of the three-dimensional refractive index, nx> ny = nz, nx> nz> ny, nz> nx = ny, nz> nx> ny (uniaxial, Z-ized, positive C plate, positive A plate) are desirable.
なお、前記位相差を有するフィルムは、位相差を有しない透明保護フィルムに、別途、貼り合せて上記機能を付与することができる。 In addition, the film which has the said phase difference can be separately bonded to the transparent protective film which does not have a phase difference, and the said function can be provided.
前記透明保護フィルムは、接着剤を塗工する前に、偏光子との接着性を向上させるために、表面改質処理を行ってもよい。具体的な処理としては、コロナ処理、プラズマ処理、フレーム処理、オゾン処理、プライマー処理、グロー処理、ケン化処理、カップリング剤による処理などがあげられる。 The transparent protective film may be subjected to surface modification treatment in order to improve adhesiveness with the polarizer before applying the adhesive. Specific examples of the treatment include corona treatment, plasma treatment, flame treatment, ozone treatment, primer treatment, glow treatment, saponification treatment, and treatment with a coupling agent.
前記透明保護フィルムの偏光子を接着させない面には、ハードコート層や反射防止処理、スティッキング防止や、拡散ないしアンチグレアを目的とした処理を施したものであってもよい。 The surface of the transparent protective film to which the polarizer is not adhered may be subjected to a hard coat layer, an antireflection treatment, an antisticking treatment, or a treatment for diffusion or antiglare.
ハードコート処理は偏光板表面の傷付き防止などを目的に施されるものであり、例えばアクリル系、シリコーン系などの適宜な紫外線硬化型樹脂による硬度や滑り特性等に優れる硬化皮膜を透明保護フィルムの表面に付加する方式などにて形成することができる。反射防止処理は偏光板表面での外光の反射防止を目的に施されるものであり、従来に準じた反射防止膜などの形成により達成することができる。また、スティッキング防止処理は隣接層(例えば、バックライト側の拡散板)との密着防止を目的に施される。 The hard coat treatment is applied for the purpose of preventing scratches on the surface of the polarizing plate. For example, a transparent protective film with a cured film excellent in hardness, sliding properties, etc. by an appropriate ultraviolet curable resin such as acrylic or silicone is used. It can be formed by a method of adding to the surface of the film. The antireflection treatment is performed for the purpose of preventing reflection of external light on the surface of the polarizing plate, and can be achieved by forming an antireflection film or the like according to the conventional art. In addition, the sticking prevention treatment is performed for the purpose of preventing adhesion with an adjacent layer (for example, a backlight-side diffusion plate).
またアンチグレア処理は偏光板の表面で外光が反射して偏光板透過光の視認を阻害することの防止等を目的に施されるものであり、例えばサンドブラスト方式やエンボス加工方式による粗面化方式や透明微粒子の配合方式などの適宜な方式にて透明保護フィルムの表面に微細凹凸構造を付与することにより形成することができる。前記表面微細凹凸構造の形成に含有させる微粒子としては、例えば平均粒径が0.5〜20μmのシリカ、アルミナ、チタニア、ジルコニア、酸化錫、酸化インジウム、酸化カドミウム、酸化アンチモン等からなる導電性のこともある無機系微粒子、架橋又は未架橋のポリマー等からなる有機系微粒子などの透明微粒子が用いられる。表面微細凹凸構造を形成する場合、微粒子の使用量は、表面微細凹凸構造を形成する透明樹脂100重量部に対して一般的に2〜70重量部程度であり、5〜50重量部が好ましい。アンチグレア層は、偏光板透過光を拡散して視角などを拡大するための拡散層(視角拡大機能など)を兼ねるものであってもよい。 The anti-glare treatment is applied for the purpose of preventing the outside light from being reflected on the surface of the polarizing plate and obstructing the visibility of the light transmitted through the polarizing plate. For example, the surface is roughened by a sandblasting method or an embossing method. It can be formed by imparting a fine concavo-convex structure to the surface of the transparent protective film by an appropriate method such as a blending method of transparent fine particles. Examples of the fine particles to be included in the formation of the surface fine concavo-convex structure include conductive materials made of silica, alumina, titania, zirconia, tin oxide, indium oxide, cadmium oxide, antimony oxide, and the like having an average particle diameter of 0.5 to 20 μm. In some cases, transparent fine particles such as inorganic fine particles, organic fine particles composed of a crosslinked or uncrosslinked polymer, and the like are used. When forming the surface fine uneven structure, the amount of fine particles used is generally about 2 to 70 parts by weight, preferably 5 to 50 parts by weight, based on 100 parts by weight of the transparent resin forming the surface fine uneven structure. The antiglare layer may also serve as a diffusion layer (viewing angle expanding function or the like) for diffusing the light transmitted through the polarizing plate to expand the viewing angle.
なお、前記反射防止層、スティッキング防止層、拡散層やアンチグレア層等は、透明保護フィルムそのものに設けることができるほか、別途光学層として透明保護フィルムとは別体のものとして設けることもできる。 The antireflection layer, antisticking layer, diffusion layer, antiglare layer, and the like can be provided on the transparent protective film itself, or can be provided separately from the transparent protective film as an optical layer.
前記偏光子と透明保護フィルムの貼り合わせに用いる接着剤層は光学的に透明であれば、特に制限されず水系、溶剤系、ホットメルト系、ラジカル硬化型の各種形態のものが用いられるが、水系接着剤またはラジカル硬化型接着剤が好適である。 The adhesive layer used for laminating the polarizer and the transparent protective film is not particularly limited as long as it is optically transparent, and water-based, solvent-based, hot-melt-based, and radical-curing types are used. A water-based adhesive or a radical curable adhesive is suitable.
水系接着剤としては、ポリビニルアルコール系、ゼラチン系、ビニル系ラテックス系、ポリウレタン系、イソシアネート系、ポリエステル系、エポキシ系等を例示できる。前記接着剤には各種架橋剤を含有することができる。また前記接着剤には、触媒、カップリング剤、各種粘着付与剤、紫外線吸収剤、酸化防止剤、耐熱安定剤、耐加水分解安定剤などの安定剤等を配合することもできる。接着剤の固形分は一般に0.1〜20重量%で用いられる。 Examples of the water-based adhesive include polyvinyl alcohol, gelatin, vinyl latex, polyurethane, isocyanate, polyester, and epoxy. The adhesive may contain various crosslinking agents. In addition, a stabilizer such as a catalyst, a coupling agent, various tackifiers, an ultraviolet absorber, an antioxidant, a heat stabilizer, and a hydrolysis stabilizer can be added to the adhesive. The solid content of the adhesive is generally 0.1 to 20% by weight.
前記接着剤のなかでも、ポリビニルアルコール系接着剤が好ましい。ポリビニルアルコール系接着剤は、ポリビニルアルコール系樹脂と架橋剤を含有する。 Among the adhesives, polyvinyl alcohol-based adhesives are preferable. The polyvinyl alcohol-based adhesive contains a polyvinyl alcohol-based resin and a crosslinking agent.
ポリビニルアルコール系樹脂は、ポリ酢酸ビニルをケン化して得られたポリビニルアルコール;その誘導体;更に酢酸ビニルと共重合性を有する単量体との共重合体のケン化物;ポリビニルアルコールをアセタール化、ウレタン化、エーテル化、グラフト化、リン酸エステル化等した変性ポリビニルアルコールがあげられる。前記単量体としては、(無水)マレイン酸、フマール酸、クロトン酸、イタコン酸、(メタ)アクリル酸等の不飽和カルボン酸及びそのエステル類;エチレン、プロピレン等のα−オレフィン、(メタ)アリルスルホン酸(ソーダ)、スルホン酸ソーダ(モノアルキルマレート)、ジスルホン酸ソーダアルキルマレート、N−メチロールアクリルアミド、アクリルアミドアルキルスルホン酸アルカリ塩、N−ビニルピロリドン、N−ビニルピロリドン誘導体等があげられる。これらポリビニルアルコール系樹脂は一種を単独でまたは二種以上を併用することができる。 Polyvinyl alcohol resin is polyvinyl alcohol obtained by saponifying polyvinyl acetate; a derivative thereof; a saponified product of a copolymer of vinyl acetate and a monomer having copolymerizability; Examples thereof include modified polyvinyl alcohols that have been converted into ethers, ethers, grafts, or phosphoric esters. Examples of the monomer include unsaturated carboxylic acids such as (anhydrous) maleic acid, fumaric acid, crotonic acid, itaconic acid, (meth) acrylic acid, and esters thereof; α-olefins such as ethylene and propylene, (meth) Examples include allyl sulfonic acid (soda), sulfonic acid soda (monoalkyl malate), disulfonic acid soda alkyl maleate, N-methylol acrylamide, acrylamide alkyl sulfonic acid alkali salt, N-vinyl pyrrolidone, N-vinyl pyrrolidone derivatives and the like. . These polyvinyl alcohol resins can be used singly or in combination of two or more.
前記ポリビニルアルコール系樹脂は特に限定されないが、接着性の点からは、平均重合度100〜3000程度、好ましくは500〜3000、平均ケン化度85〜100モル%程度、好ましくは90〜100モル%である。 The polyvinyl alcohol-based resin is not particularly limited, but from the viewpoint of adhesion, the average degree of polymerization is about 100 to 3000, preferably 500 to 3000, the average saponification degree is about 85 to 100 mol%, preferably 90 to 100 mol%. It is.
またポリビニルアルコール系樹脂としては、アセトアセチル基を有するポリビニルアルコール樹脂を用いることができる。アセトアセチル基を有するポリビニルアルコール樹脂は、反応性の高い官能基を有するポリビニルアルコール系接着剤であり、偏光板の耐久性が向上し好ましい。 Moreover, as a polyvinyl alcohol-type resin, the polyvinyl alcohol resin which has an acetoacetyl group can be used. The polyvinyl alcohol resin having an acetoacetyl group is a polyvinyl alcohol-based adhesive having a highly reactive functional group, and is preferable because the durability of the polarizing plate is improved.
アセトアセチル基を含有するポリビニルアルコール系樹脂は、ポリビニルアルコール系樹脂とジケテンとを公知の方法で反応して得られる。たとえば、ポリビニルアルコール系樹脂を酢酸等の溶媒中に分散させておき、これにジケテンを添加する方法、ポリビニルアルコール系樹脂をジメチルホルムアミドまたはジオキサン等の溶媒にあらかじめ溶解しておき、これにジケテンを添加する方法等があげられる。またポリビニルアルコールにジケテンガスまたは液状ジケテンを直接接触させる方法があげられる。 A polyvinyl alcohol-based resin containing an acetoacetyl group is obtained by reacting a polyvinyl alcohol-based resin with diketene by a known method. For example, a method in which a polyvinyl alcohol resin is dispersed in a solvent such as acetic acid and diketene is added thereto, a polyvinyl alcohol resin is previously dissolved in a solvent such as dimethylformamide or dioxane, and diketene is added thereto. And the like. Another example is a method in which diketene gas or liquid diketene is brought into direct contact with polyvinyl alcohol.
アセトアセチル基を含有するポリビニルアルコール系樹脂のアセトアセチル基変性度は、0.1モル%以上であれば特に制限はなない。0.1モル%未満では接着剤層の耐水性が不充分であり不適当である。アセトアセチル基変性度は、好ましくは0.1〜40モル%程度、さらに好ましくは1〜20モル%である。アセトアセチル基変性度が40モル%を超えると架橋剤との反応点が少なくなり、耐水性の向上効果が小さい。アセトアセチル基変性度はNMRにより測定した値である。 The degree of acetoacetyl group modification of the polyvinyl alcohol-based resin containing an acetoacetyl group is not particularly limited as long as it is 0.1 mol% or more. If it is less than 0.1 mol%, the water resistance of the adhesive layer is insufficient and unsuitable. The degree of acetoacetyl modification is preferably about 0.1 to 40 mol%, more preferably 1 to 20 mol%. When the degree of acetoacetyl modification exceeds 40 mol%, the number of reaction points with the cross-linking agent decreases, and the effect of improving water resistance is small. The degree of acetoacetyl modification is a value measured by NMR.
架橋剤としては、ポリビニルアルコール系接着剤に用いられているものを特に制限なく使用できる。架橋剤は、ポリビニルアルコール系樹脂と反応性を有する官能基を少なくとも2つ有する化合物を使用できる。たとえば、エチレンジアミン、トリエチレンジアミン、ヘキサメチレンジアミン等のアルキレン基とアミノ基を2個有するアルキレンジアミン類;トリレンジイソシアネート、水素化トリレンジイソシアネート、トリメチロールプロパントリレンジイソシアネートアダクト、トリフェニルメタントリイソシアネート、メチレンビス(4−フェニルメタントリイソシアネート、イソホロンジイソシアネートおよびこれらのケトオキシムブロック物またはフェノールブロック物等のイソシアネート類;エチレングリコールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、グリセリンジまたはトリグリシジルエーテル、1,6−ヘキサンジオールジグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、ジグリシジルアニリン、ジグリシジルアミン等のエポキシ類;ホルムアルデヒド、アセトアルデヒド、プロピオンアルデヒド、ブチルアルデヒド等のモノアルデヒド類;グリオキザール、マロンジアルデヒド、スクシンジアルデヒド、グルタルジアルデヒド、マレインジアルデヒド、フタルジアルデヒド等のジアルデヒド類;メチロール尿素、メチロールメラミン、アルキル化メチロール尿素、アルキル化メチロール化メラミン、アセトグアナミン、ベンゾグアナミンとホルムアルデヒドとの縮合物等のアミノ−ホルムアルデヒド樹脂;更にナトリウム、カリウム、マグネシウム、カルシウム、アルミニウム、鉄、ニッケル等の二価金属、又は三価金属の塩及びその酸化物があげられる。架橋剤としては、メラミン系架橋剤が好ましく、特にメチロールメラミンが好適である。 As a crosslinking agent, what is used for the polyvinyl alcohol-type adhesive agent can be especially used without a restriction | limiting. As the crosslinking agent, a compound having at least two functional groups having reactivity with the polyvinyl alcohol resin can be used. For example, alkylenediamine having two alkylene groups and two amino groups such as ethylenediamine, triethylenediamine, hexamethylenediamine; tolylene diisocyanate, hydrogenated tolylene diisocyanate, trimethylolpropane tolylene diisocyanate adduct, triphenylmethane triisocyanate, methylene bis (Isocyanates such as 4-phenylmethane triisocyanate, isophorone diisocyanate and ketoxime block product or phenol block product thereof; ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, glycerin di or triglycidyl ether, 1,6-hexane Diol diglycidyl ether, trimethylolpropane triglycidyl ether, di Epoxies such as lysidylaniline and diglycidylamine; monoaldehydes such as formaldehyde, acetaldehyde, propionaldehyde, and butyraldehyde; Dialdehydes; methylol urea, methylol melamine, alkylated methylol urea, alkylated methylolated melamine, acetoguanamine, condensates of benzoguanamine and formaldehyde, etc .; further sodium, potassium, magnesium, calcium, aluminum, iron And a divalent metal such as nickel, or a salt of a trivalent metal and oxides thereof. Melamine is preferred.
前記架橋剤の配合量は、ポリビニルアルコール系樹脂100重量部に対して、通常、0.1〜35重量部程度、好ましくは10〜25重量部である。一方、耐久性をより向上させるには、ポリビニルアルコール系樹脂100重量部に対して、架橋剤を30重量部を超え46重量部以下の範囲で配合することができる。特に、アセトアセチル基を含有するポリビニルアルコール系樹脂を用いる場合には、架橋剤の使用量を30重量部を超えて用いるのが好ましい。架橋剤を30重量部を超え46重量部以下の範囲で配合することにより、耐水性が向上する。 The amount of the crosslinking agent is usually about 0.1 to 35 parts by weight, preferably 10 to 25 parts by weight, with respect to 100 parts by weight of the polyvinyl alcohol resin. On the other hand, in order to further improve the durability, the crosslinking agent can be blended in an amount exceeding 30 parts by weight and not more than 46 parts by weight with respect to 100 parts by weight of the polyvinyl alcohol resin. In particular, when a polyvinyl alcohol-based resin containing an acetoacetyl group is used, it is preferable to use the crosslinking agent in an amount exceeding 30 parts by weight. Water resistance improves by mix | blending a crosslinking agent in the range of more than 30 weight part and 46 weight part or less.
なお、前記接着剤には、さらにシランカップリング剤、チタンカップリング剤などのカップリング剤、各種粘着付与剤、紫外線吸収剤、酸化防止剤、耐熱安定剤、耐加水分解安定剤などの安定剤等を配合することもできる。 The adhesive further includes a silane coupling agent, a coupling agent such as a titanium coupling agent, various tackifiers, an ultraviolet absorber, an antioxidant, a heat stabilizer, a hydrolysis stabilizer, and the like. Etc. can also be blended.
ラジカル硬化型接着剤としては、電子線硬化型、紫外線硬化型等の活性エネルギー線硬化型、熱硬化型等の各種のものを例示できるが、短時間で硬化可能、活性エネルギー線硬化型が好ましい。特に、電子線硬化型が好ましい。 Examples of the radical curable adhesive include an active energy ray curable type such as an electron beam curable type and an ultraviolet ray curable type, and a thermosetting type, but can be cured in a short time, and an active energy ray curable type is preferable. . In particular, an electron beam curable type is preferable.
硬化性成分としては、(メタ)アクリロイル基を有する化合物、ビニル基を有する化合物があげられる。これら硬化性成分は、単官能または二官能以上のいずれも用いることができる。またこれら硬化性成分は、1種を単独で、または2種以上を組み合わせて用いることができる。これら硬化性成分としては、例えば、(メタ)アクリロイル基を有する化合物が好適であり、例えば、各種のエポキシ(メタ)アクリレート、ウレタン(メタ)アクリレート、ポリエステル(メタ)アクリレートや、各種の(メタ)アクリレート系モノマー等があげられる。 Examples of the curable component include a compound having a (meth) acryloyl group and a compound having a vinyl group. These curable components may be monofunctional or bifunctional or higher. Moreover, these curable components can be used individually by 1 type or in combination of 2 or more types. As these curable components, for example, compounds having a (meth) acryloyl group are suitable. For example, various epoxy (meth) acrylates, urethane (meth) acrylates, polyester (meth) acrylates, and various (meth) acrylates. Examples thereof include acrylate monomers.
上記硬化性成分のなかでも、エポキシ(メタ)アクリレート、特に、芳香環およびヒドロキシ基を有する単官能の(メタ)アクリレートが好ましい。(メタ)アクリレートは、アクリレートおよび/またはメタクリレートを意味する。本発明では(メタ)アクリレートはこの意味である。 Among the curable components, epoxy (meth) acrylate, particularly monofunctional (meth) acrylate having an aromatic ring and a hydroxy group is preferable. (Meth) acrylate means acrylate and / or methacrylate. In the present invention, (meth) acrylate has this meaning.
芳香環およびヒドロキシ基を有する単官能の(メタ)アクリレートは、芳香環およびヒドロキシ基を有する、各種の単官能の(メタ)アクリレートを用いることができる。ヒドロキシ基は、芳香環の置換基として存在してもよいが、本発明では、芳香環と(メタ)アクリレートとを結合する有機基(炭化水素基、特に、アルキレン基に結合したもの)として存在するものが好ましい。 As the monofunctional (meth) acrylate having an aromatic ring and a hydroxy group, various monofunctional (meth) acrylates having an aromatic ring and a hydroxy group can be used. The hydroxy group may exist as a substituent of the aromatic ring, but in the present invention, it exists as an organic group (bonded to a hydrocarbon group, particularly an alkylene group) that bonds the aromatic ring and the (meth) acrylate. Those that do are preferred.
前記芳香環およびヒドロキシ基を有する単官能の(メタ)アクリレートとしては、例えば、芳香環を有する単官能のエポキシ化合物と、(メタ)アクリル酸との反応物があげられる。芳香環を有する単官能のエポキシ化合物としては、例えば、フェニルグリシジルエーテル、t‐ブチルフェニルグリシジルエーテル、フェニルポリエチレングリコールグリシジルエーテル等があげられる。芳香環およびヒドロキシ基を有する単官能の(メタ)アクリレートの、具体例としては、例えば、2−ヒドロキシ−3−フェノキシプロピル(メタ)アクリレート、2−ヒドロキシ−3−t−ブチルフェノキシプロピル(メタ)アクリレート、2−ヒドロキシ−3−フェニルポリエチレングリコールプロピル(メタ)アクリレート等があげられる。 Examples of the monofunctional (meth) acrylate having an aromatic ring and a hydroxy group include a reaction product of a monofunctional epoxy compound having an aromatic ring and (meth) acrylic acid. Examples of the monofunctional epoxy compound having an aromatic ring include phenyl glycidyl ether, t-butylphenyl glycidyl ether, and phenyl polyethylene glycol glycidyl ether. Specific examples of the monofunctional (meth) acrylate having an aromatic ring and a hydroxy group include, for example, 2-hydroxy-3-phenoxypropyl (meth) acrylate, 2-hydroxy-3-t-butylphenoxypropyl (meth) Examples thereof include acrylate and 2-hydroxy-3-phenyl polyethylene glycol propyl (meth) acrylate.
また、(メタ)アクリロイル基を有する化合物としては、窒素含有モノマーおよび/またはカルボキシル基モノマーが好適に用いられる。これらモノマーは、接着性の点で好ましい。 Moreover, as a compound which has a (meth) acryloyl group, a nitrogen-containing monomer and / or a carboxyl group monomer are used suitably. These monomers are preferable in terms of adhesiveness.
窒素含有モノマーとしては、例えば、N−アクリロイルモルホリン、N−アクリロイルピペリジン、N−メタクリロイルピペリジン、N−アクリロイルピロリジン等のモルホリン環、ピペリジン環、ピロリジン環、ピペラジン環等の複素環を有する複素環含有アクリルモノマーがあげられる。また、窒素含有モノマーとしては、例えば、マレイミド、N−シクロへキシルマレイミド、N−フェニルマレイミド;(メタ)アクリルアミド、N,N−ジメチル(メタ)アクリルアミド、N,N−ジエチル(メタ)アクリルアミド、N−ヘキシル(メタ)アクリルアミド、N−メチル(メタ)アクリルアミド、N−ブチル(メタ)アクリルアミド、N−ブチル(メタ)アクリルアミドやN−メチロール(メタ)アクリルアミド、N−メチロールプロパン(メタ)アクリルアミドなどの(N−置換)アミド系モノマー;(メタ)アクリル酸アミノエチル、(メタ)アクリル酸アミノプロピル、(メタ)アクリル酸N,N−ジメチルアミノエチル、(メタ)アクリル酸t−ブチルアミノエチル、3−(3−ピリニジル)プロピル(メタ)アクリレートなどの(メタ)アクリル酸アルキルアミノアルキル系モノマー;N−(メタ)アクリロイルオキシメチレンスクシンイミドやN−(メタ)アクリロイル−6−オキシヘキサメチレンスクシンイミド、N−(メタ)アクリロイル−8−オキシオクタメチレンスクシンイミドなどのスクシンイミド系モノマーなどあげられる。窒素含有モノマーは、例えば、複素環含有アクリルモノマーが好ましく、特にN−アクリロイルモルホリンが好ましい。 Examples of the nitrogen-containing monomer include a heterocyclic ring-containing acrylic having a heterocyclic ring such as a morpholine ring such as N-acryloylmorpholine, N-acryloylpiperidine, N-methacryloylpiperidine, and N-acryloylpyrrolidine, a piperidine ring, a pyrrolidine ring, and a piperazine ring. Monomer. Examples of the nitrogen-containing monomer include maleimide, N-cyclohexylmaleimide, N-phenylmaleimide; (meth) acrylamide, N, N-dimethyl (meth) acrylamide, N, N-diethyl (meth) acrylamide, N -Hexyl (meth) acrylamide, N-methyl (meth) acrylamide, N-butyl (meth) acrylamide, N-butyl (meth) acrylamide, N-methylol (meth) acrylamide, N-methylolpropane (meth) acrylamide ( N-substituted) amide monomers; aminoethyl (meth) acrylate, aminopropyl (meth) acrylate, N, N-dimethylaminoethyl (meth) acrylate, t-butylaminoethyl (meth) acrylate, 3- (3-Pyridinyl) propyl (meth) acryl (Meth) acrylic acid alkylaminoalkyl monomers such as N- (meth) acryloyloxymethylenesuccinimide, N- (meth) acryloyl-6-oxyhexamethylenesuccinimide, N- (meth) acryloyl-8-oxyocta Examples thereof include succinimide monomers such as methylene succinimide. For example, the nitrogen-containing monomer is preferably a heterocyclic ring-containing acrylic monomer, and particularly preferably N-acryloylmorpholine.
カルボキシル基モノマーとしては、例えば、(メタ)アクリル酸、カルボキシエチル(メタ)アクリレート、カルボキシペンチル(メタ)アクリレート、などがあげられる。これらのなかでもアクリル酸が好ましい。 Examples of the carboxyl group monomer include (meth) acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, and the like. Of these, acrylic acid is preferred.
上記の他、(メタ)アクリロイル基を有する化合物としては、メチル(メタ)アクリレート、エチル(メタ)アクリレート、n−ブチル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、イソオクチル(メタ)アクリレート、イソノニル(メタ)アクリレート、ラウリル(メタ)アクリレート等の炭素数は1〜12のアルキル(メタ)アクリレート;(メタ)アクリル酸メトキシエチル、(メタ)アクリル酸エトキシエチルなどの(メタ)アクリル酸アルコキシアルキル系モノマー;(メタ)アクリル酸2−ヒドロキシエチル、(メタ)アクリル酸2−ヒドロキシプロピル、(メタ)アクリル酸4−ヒドロキシブチル、(メタ)アクリル酸6−ヒドロキシヘキシル、(メタ)アクリル酸8−ヒドロキシオクチル、(メタ)アクリル酸10−ヒドロキシデシル、(メタ)アクリル酸12−ヒドロキシラウリルや(4−ヒドロキシメチルシクロヘキシル)−メチルアクリレートなどのヒドロキシル基含有モノマー;無水マレイン酸、無水イタコン酸などの酸無水物基含有モノマー;アクリル酸のカプロラクトン付加物;スチレンスルホン酸やアリルスルホン酸、2−(メタ)アクリルアミド−2−メチルプロパンスルホン酸、(メタ)アクリルアミドプロパンスルホン酸、スルホプロピル(メタ)アクリレート、(メタ)アクリロイルオキシナフタレンスルホン酸などのスルホン酸基含有モノマー;2−ヒドロキシエチルアクリロイルホスフェートなどの燐酸基含有モノマーなどがあげられる。 In addition to the above, compounds having a (meth) acryloyl group include methyl (meth) acrylate, ethyl (meth) acrylate, n-butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isooctyl (meth) acrylate, and isononyl. Alkyl (meth) acrylates having 1 to 12 carbon atoms such as (meth) acrylate and lauryl (meth) acrylate; (meth) acrylic acid alkoxyalkyl systems such as (meth) acrylic acid methoxyethyl and (meth) acrylic acid ethoxyethyl Monomer: 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, 6-hydroxyhexyl (meth) acrylate, 8-hydroxy (meth) acrylate Octyl, (meth) acrylic acid 10-H Hydroxyl-containing monomers such as loxydecyl, 12-hydroxylauryl (meth) acrylate and (4-hydroxymethylcyclohexyl) -methyl acrylate; acid anhydride group-containing monomers such as maleic anhydride and itaconic anhydride; caprolactone addition of acrylic acid Products; sulfones such as styrene sulfonic acid, allyl sulfonic acid, 2- (meth) acrylamide-2-methylpropane sulfonic acid, (meth) acrylamide propane sulfonic acid, sulfopropyl (meth) acrylate, (meth) acryloyloxynaphthalene sulfonic acid Acid group-containing monomers; phosphoric acid group-containing monomers such as 2-hydroxyethylacryloyl phosphate.
上記硬化性成分としては、芳香環およびヒドロキシ基を有する単官能の(メタ)アクリレート、窒素含有モノマー、カルボキシル基モノマーが好適に用いられる。これらの成分を、硬化性成分として、50重量%以上を含有することが、偏光子および透明保護フィルムに対して接着性の良好な接着剤層を有する偏光板を得るうえで好ましい。さらには、塗工性、加工性などの点からも好ましい。前記硬化性成分の割合は、60重量%以上であるのが好ましく、さらには70重量%以上であるのが好ましく、さらには80重量%以上であるのが好ましい。 As the curable component, a monofunctional (meth) acrylate having an aromatic ring and a hydroxy group, a nitrogen-containing monomer, and a carboxyl group monomer are preferably used. It is preferable to contain these components as curable components in an amount of 50% by weight or more in order to obtain a polarizing plate having an adhesive layer having good adhesion to the polarizer and the transparent protective film. Furthermore, it is preferable also from points, such as coating property and workability. The ratio of the curable component is preferably 60% by weight or more, more preferably 70% by weight or more, and further preferably 80% by weight or more.
上記硬化性成分としては、二官能以上の硬化性成分を用いることができる。二官能以上の硬化性成分としては、二官能以上の(メタ)アクリレート、特に二官能以上のエポキシ(メタ)アクリレートが好ましい。二官能以上のエポキシ(メタ)アクリレートは、多官能のエポキシ化合物と、(メタ)アクリル酸との反応により得られる。多官能のエポキシ化合物は、各種のものを例示できる。多官能のエポキシ化合物としては、例えば、芳香族エポキシ樹脂、脂環式エポキシ樹脂、脂肪族エポキシ樹脂があげられる。 As the curable component, a bifunctional or higher curable component can be used. The bifunctional or higher curable component is preferably a bifunctional or higher (meth) acrylate, particularly a bifunctional or higher epoxy (meth) acrylate. The bifunctional or higher functional epoxy (meth) acrylate is obtained by reacting a polyfunctional epoxy compound with (meth) acrylic acid. Various examples of the polyfunctional epoxy compound can be exemplified. Examples of the polyfunctional epoxy compound include aromatic epoxy resins, alicyclic epoxy resins, and aliphatic epoxy resins.
芳香族エポキシ樹脂としては、例えば、ビスフェノールAのジグリシジルエーテル、ビスフェールFのジグリシジルエーテル、ビスフェノールSのジグリシジルエーテルのようなビスフェノール型エポキシ樹脂;フェノールノボラックエポキシ樹脂、クレゾールノボラックエポキシ樹脂、ヒドロキシベンズアルデヒドフェノールノボラックエポキシ樹脂のようなノボラック型のエポキシ樹脂;テトラヒドロキシフェニルメタンのグリシジルエーテル、テトラヒドロキシベンゾフェノンのグリシジルエーテル、エポキシ化ポリビニルフェノールのような多官能型のエポキシ樹脂などがあげられる。 Examples of the aromatic epoxy resin include bisphenol type epoxy resins such as diglycidyl ether of bisphenol A, diglycidyl ether of bisphenol F, diglycidyl ether of bisphenol S; phenol novolac epoxy resin, cresol novolac epoxy resin, hydroxybenzaldehyde Examples thereof include novolak-type epoxy resins such as phenol novolac epoxy resins; glycidyl ethers of tetrahydroxyphenylmethane, glycidyl ethers of tetrahydroxybenzophenone, and polyfunctional epoxy resins such as epoxidized polyvinylphenol.
脂環式エポキシ樹脂としては、前記芳香族エポキシ樹脂の水添物、シクロヘキサン系、シクロヘキシルメチルエステル系、シシクロヘキシルメチルエーテル系、スピロ系、トリシクロデカン系等のエポキシ樹脂があげられる。 Examples of the alicyclic epoxy resins include hydrogenated products of the above-mentioned aromatic epoxy resins, cyclohexane-based, cyclohexylmethyl ester-based, cicyclohexylmethyl ether-based, spiro-based, and tricyclodecane-based epoxy resins.
脂肪族エポキシ樹脂としては、脂肪族多価アルコール又はそのアルキレンオキサイド付加物のポリグリシジルエーテルがあげられる。これらの例としては、1,4−ブタンジオールのジグリシジルエーテル、1,6−ヘキサンジオールのジグリシジルエーテル、グリセリンのトリグリシジルエーテル、トリメチロールプロパンのトリグリシジルエーテル、ポリエチレングリコールのジグリシジルエーテル、プロピレングリコールのジグリシジルエーテル、エチレングリコールやプロピレングリコール、グリセリンのような脂肪族多価アルコールに1種又は2種以上のアルキレンオキサイド(エチレンオキサイドやプロピレンオキサイド)を付加することにより得られるポリエーテルポリオールのポリグリシジルエーテルなどがあげられる。 Examples of the aliphatic epoxy resin include polyglycidyl ethers of aliphatic polyhydric alcohols or alkylene oxide adducts thereof. Examples include 1,4-butanediol diglycidyl ether, 1,6-hexanediol diglycidyl ether, glycerin triglycidyl ether, trimethylolpropane triglycidyl ether, polyethylene glycol diglycidyl ether, propylene. Polyethers of polyether polyols obtained by adding one or more alkylene oxides (ethylene oxide or propylene oxide) to aliphatic polyhydric alcohols such as glycol diglycidyl ether, ethylene glycol, propylene glycol, and glycerin Examples thereof include glycidyl ether.
前記エポキシ樹脂の、エポキシ当量は、通常30〜3000g/当量、好ましくは50〜1500g/当量の範囲である。 The epoxy equivalent of the epoxy resin is usually in the range of 30 to 3000 g / equivalent, preferably 50 to 1500 g / equivalent.
前記二官能以上のエポキシ(メタ)アクリレートは、脂肪族エポキシ樹脂のエポキシ(メタ)アクリレートが好ましい、特に、二官能の脂肪族エポキシ樹脂のエポキシ(メタ)アクリレートが好ましい。 The bifunctional or higher epoxy (meth) acrylate is preferably an epoxy (meth) acrylate of an aliphatic epoxy resin, particularly preferably an epoxy (meth) acrylate of a bifunctional aliphatic epoxy resin.
上記硬化性成分のなかで、(メタ)アクリロイル基を有する化合物、特に、芳香環およびヒドロキシ基を有する単官能の(メタ)アクリレート、窒素含有(メタ)アクリレート、カルボキシル基含有(メタ)アクリレートは、電子線硬化型接着剤として適しており、当該接着剤を用いることで、偏光子および透明保護フィルムに対して良好な接着性を有する偏光板が得られる。例えば、低水分率の偏光子を用いた場合にも、また、透明保護フィルムとして透湿度の低い材料を用いた場合にも、本発明の接着剤は、これらに対して良好な接着性を示し、その結果、寸法安定性の良好な偏光板が得られる。 Among the curable components, a compound having a (meth) acryloyl group, in particular, a monofunctional (meth) acrylate having an aromatic ring and a hydroxy group, a nitrogen-containing (meth) acrylate, a carboxyl group-containing (meth) acrylate, It is suitable as an electron beam curable adhesive, and by using the adhesive, a polarizing plate having good adhesion to a polarizer and a transparent protective film can be obtained. For example, even when a polarizer with a low moisture content is used, and when a material with low moisture permeability is used as the transparent protective film, the adhesive of the present invention exhibits good adhesion to them. As a result, a polarizing plate with good dimensional stability can be obtained.
上記硬化性成分を用いる場合には、寸法変化が小さい偏光板を作製できるため、偏光板の大型化にも容易に対応でき、歩留まり、取り数の観点から生産コストを抑えることができる。また、本発明で得られた偏光板は寸法安定性がよいことから、バックライトの外部熱による画像表示装置のムラの発生を抑えることができる。 When the curable component is used, a polarizing plate having a small dimensional change can be produced, so that it is possible to easily cope with an increase in the size of the polarizing plate, and it is possible to suppress the production cost from the viewpoint of yield and number. Further, since the polarizing plate obtained in the present invention has good dimensional stability, it is possible to suppress the occurrence of unevenness in the image display device due to the external heat of the backlight.
また本発明で用いる接着剤には、金属化合物フィラーを含有させることができる。金属化合物フィラーにより、接着剤層の流動性を制御することができ、膜厚を安定化して、良好な外観を有し、面内が均一で接着性のバラツキのない偏光板が得られる。 The adhesive used in the present invention can contain a metal compound filler. With the metal compound filler, the fluidity of the adhesive layer can be controlled, the film thickness can be stabilized, and a polarizing plate having a good appearance, uniform in-plane and no adhesive variation can be obtained.
金属化合物フィラーは、各種のものを用いることができる。金属化合物としては、例えば、アルミナ、シリカ、ジルコニア、チタニア、ケイ酸アルミニウム、炭酸カルシウム、ケイ酸マグネシウム等の金属酸化物;炭酸亜鉛、炭酸バリウム、リン酸カルシウム等の金属塩;セライト、タルク、クレイ、カオリン等の鉱物があげられる。また、これら金属化合物フィラーは、表面改質されたものを用いることができる。 Various types of metal compound fillers can be used. Examples of the metal compound include metal oxides such as alumina, silica, zirconia, titania, aluminum silicate, calcium carbonate and magnesium silicate; metal salts such as zinc carbonate, barium carbonate and calcium phosphate; celite, talc, clay and kaolin And the like. Further, these metal compound fillers may be those having a surface modified.
金属化合物フィラーの平均粒子径は、通常、1〜1000nm程度であり、1〜500nm、さらには10〜200nm、さらには10〜100nmであるのが好ましい。金属化合物フィラーの平均粒子径が前記範囲であれば、接着剤層中において、金属化合物を略均一に分散させることができ、接着性を確保し、かつ良好な外観で、面内の均一な接着性を得られる。 The average particle diameter of the metal compound filler is usually about 1 to 1000 nm, preferably 1 to 500 nm, more preferably 10 to 200 nm, and further preferably 10 to 100 nm. If the average particle diameter of the metal compound filler is within the above range, the metal compound can be dispersed substantially uniformly in the adhesive layer, ensuring adhesion, and having a good appearance and in-plane uniform adhesion. You can get sex.
金属化合物フィラーの配合量は、硬化性成分100重量部に対して、100重量部以下の割合で配合するのが好ましい。また金属化合物フィラーの配合割合を前記範囲とすることで、偏光子と透明保護フィルムとの接着性を確保しながら、かつ良好な外観で、面内の均一な接着性を得られる。金属化合物フィラーの配合割合は、1〜100重量部であるのが好ましく、さらには2〜50重量部、さらには5〜30重量部であるのが好ましい。金属化合物フィラーの配合割合が、硬化性成分100重量部に対して、100重量部を超えると、接着剤中における、硬化性成分の割合が小さくなり、接着性の点から好ましくない。なお、金属化合物フィラーの配合割合は、特に制限されないが、接着性を確保しながら、かつ良好な外観で、面内の均一な接着性を得るには、前記範囲の下限値とするのが好ましい。 It is preferable to mix | blend the compounding quantity of a metal compound filler in the ratio of 100 weight part or less with respect to 100 weight part of sclerosing | hardenable components. In addition, by setting the blending ratio of the metal compound filler in the above range, in-plane uniform adhesiveness can be obtained with a good appearance while ensuring the adhesiveness between the polarizer and the transparent protective film. The blending ratio of the metal compound filler is preferably 1 to 100 parts by weight, more preferably 2 to 50 parts by weight, and further preferably 5 to 30 parts by weight. When the compounding ratio of the metal compound filler exceeds 100 parts by weight with respect to 100 parts by weight of the curable component, the ratio of the curable component in the adhesive is reduced, which is not preferable from the viewpoint of adhesiveness. The mixing ratio of the metal compound filler is not particularly limited, but is preferably set to the lower limit of the above range in order to obtain in-plane uniform adhesiveness while ensuring adhesiveness and good appearance. .
硬化型接着剤は、硬化性成分を含むが、前記成分に加えて、硬化のタイプに応じて、ラジカル開始剤を添加する。前記接着剤を電子線硬化型で用いる場合には、前記接着剤にはラジカル開始剤を含有させることは特に必要ではないが、紫外線硬化型、熱硬化型で用いる場合には、ラジカル開始剤が用いられる。ラジカル開始剤の使用量は硬化性成分100重量部あたり、通常0.1〜10重量部程度、好ましくは、0.5〜3重量部である。 The curable adhesive contains a curable component, and in addition to the above components, a radical initiator is added depending on the type of curing. When the adhesive is used as an electron beam curable type, it is not particularly necessary that the adhesive contains a radical initiator, but when used as an ultraviolet curable type or a thermosetting type, a radical initiator is used. Used. The usage-amount of a radical initiator is about 0.1-10 weight part normally per 100 weight part of sclerosing | hardenable components, Preferably, it is 0.5-3 weight part.
また、前記接着剤は、前記成分に加えて、必要であれば適宜添加剤を添加してもよい。添加剤の例としては、カルボニル化合物などで代表される電子線による硬化速度や感度を上がる増感剤、シランカップリング剤やエチレンオキシドで代表される接着促進剤、透明保護フィルムとの濡れ性を向上させる添加剤、アクリロキシ基化合物や炭化水素系(天然、合成樹脂)などに代表され、機械的強度や加工性などを向上させる添加剤、紫外線吸収剤、老化防止剤、染料、加工助剤、イオントラップ剤、酸化防止剤、粘着付与剤、充填剤(金属化合物フィラー以外)、可塑剤、レベリング剤、発泡抑制剤、帯電防止割などがあげられる。 Moreover, in addition to the said component, the said adhesive agent may add an additive suitably as needed. Examples of additives include sensitizers that increase the curing speed and sensitivity of electron beams typified by carbonyl compounds, adhesion promoters typified by silane coupling agents and ethylene oxide, and improved wettability with transparent protective films. Additives, acryloxy group compounds and hydrocarbons (natural and synthetic resins), additives that improve mechanical strength and processability, UV absorbers, anti-aging agents, dyes, processing aids, ions Examples include trapping agents, antioxidants, tackifiers, fillers (other than metal compound fillers), plasticizers, leveling agents, foaming inhibitors, and antistatics.
本発明の偏光板は、透明保護フィルムと偏光子を、前記接着剤を用いて貼り合わせることにより製造するが、当該貼り合わせ工程の前には、偏光子の接着剤層が設けられる面に活性化処理を施す。偏光子の両面に透明保護フィルムを貼り合わせる場合には、偏光子の両面に活性化処理を施す。偏光子の片面にのみ透明保護フィルムを貼り合わせる場合には、その片面にのみ活性化処理を施してもよく、偏光子の両面に活性化処理を施してもよい。 The polarizing plate of the present invention is produced by laminating a transparent protective film and a polarizer using the adhesive, but before the laminating step, it is active on the surface where the adhesive layer of the polarizer is provided. The process is applied. When a transparent protective film is bonded to both sides of the polarizer, activation treatment is performed on both sides of the polarizer. When a transparent protective film is bonded to only one side of the polarizer, activation treatment may be performed only on one side, or activation treatment may be performed on both sides of the polarizer.
活性化処理としては、コロナ処理、プラズマ処理、グロー処理およびオゾン処理から選ばれるいずれか少なくとも一つの処理が施される。コロナ処理は、例えば、コロナ処理機により常圧空気中で放電する方式により行うことができる。プラズマ処理は、例えば、プラズマ放電機により常圧空気中または窒素、アルゴン等の不活性ガス雰囲気中で放電する方式により行うことができる。グロー処理、オゾン処理についても、常法に従って行うことができる。これらのなかでも、コロナ処理が設備費用・加工費の点で好適である。 As the activation treatment, at least one treatment selected from corona treatment, plasma treatment, glow treatment and ozone treatment is performed. The corona treatment can be performed, for example, by a method of discharging in normal pressure air using a corona treatment machine. The plasma treatment can be performed, for example, by a method in which discharge is performed in a normal pressure air or an inert gas atmosphere such as nitrogen or argon by a plasma discharge machine. Glow treatment and ozone treatment can also be performed according to a conventional method. Among these, corona treatment is preferable in terms of equipment costs and processing costs.
上記の活性化処理により、偏光子の表面を、親水化処理等を施す。水系接着剤を用いる場合には、前記処理の施された偏光子表面は、対水の接触角が、10〜50°であるのが好ましく、さらには15〜35°であるのが好ましい。接着角は、協和界面科学社製のContactAngle meter(MODEL CA‐X)を用いた。具体的には、作成した偏光子をテープを用いてガラス板上に固定し、マイクロシリンジを用いて偏光子表面に水滴を滴下した。滴下してから1秒間後の接触角を測定した。 By the above activation treatment, the surface of the polarizer is subjected to a hydrophilic treatment or the like. In the case of using an aqueous adhesive, the surface of the polarizer subjected to the above treatment preferably has a contact angle with water of 10 to 50 °, and more preferably 15 to 35 °. For the bonding angle, Contact Angle meter (MODEL CA-X) manufactured by Kyowa Interface Science Co., Ltd. was used. Specifically, the prepared polarizer was fixed on a glass plate using a tape, and water droplets were dropped on the surface of the polarizer using a microsyringe. The contact angle after 1 second from dropping was measured.
前記活性化処理としては、活性化処理に応じて、偏光子が上記表面状態になるように、処理条件が設定される。例えば、コロナ処理においては、放電量は10〜500W/m2/min程度、好ましくは20〜300W/m2/minである。 As the activation treatment, treatment conditions are set so that the polarizer is in the surface state according to the activation treatment. For example, in the corona treatment, the discharge amount is about 10 to 500 W / m 2 / min, preferably 20 to 300 W / m 2 / min.
本発明の製造方法では、次いで、前記活性化処理の施された偏光子の表面および/または透明保護フィルムの前記接着剤層を形成する面に、接着剤を塗工する。 In the production method of the present invention, an adhesive is then applied to the surface of the polarizer subjected to the activation treatment and / or the surface of the transparent protective film on which the adhesive layer is to be formed.
接着剤の塗工方式は、接着剤の粘度や目的とする厚みによって適宜に選択される。塗工方式の例として、例えば、リバースコーター、グラビアコーター(ダイレクト,リバースやオフセット)、バーリバースコーター、ロールコーター、ダイコーター、バーコーター、ロッドコーターなどがあげられる。その他、塗工には、デイッピング方式などの方式を適宜に使用することができる。 The adhesive coating method is appropriately selected depending on the viscosity of the adhesive and the target thickness. Examples of the coating method include a reverse coater, a gravure coater (direct, reverse or offset), a bar reverse coater, a roll coater, a die coater, a bar coater, a rod coater, and the like. In addition, for coating, a method such as a dapping method can be appropriately used.
上記のように塗工した接着剤を介して、偏光子と透明保護フィルムとを貼り合わせる。偏光子と透明保護フィルムの貼り合わせは、ロールラミネーター等により行う事ができる。 A polarizer and a transparent protective film are bonded together through the adhesive applied as described above. The polarizer and the transparent protective film can be bonded together using a roll laminator or the like.
前記貼り合わせ工程の後には、接着剤層を形成する。接着剤層の形成は、接着剤の種類に応じて行われる。 An adhesive layer is formed after the bonding step. The formation of the adhesive layer is performed according to the type of adhesive.
接着剤が水系接着剤、溶剤系接着剤の場合には、前記貼り合わせ工程の後に、乾燥工程を施して接着剤層を形成する。前記接着剤としては水系接着剤が好適である。水系接着剤を用いる場合、乾燥工程を、乾燥温度20〜80℃程度、好ましくは、40〜80℃で、1〜10分間程度、好ましくは1〜5分間行うのが好ましい。 When the adhesive is a water-based adhesive or a solvent-based adhesive, a drying step is performed after the bonding step to form an adhesive layer. A water-based adhesive is suitable as the adhesive. When using a water-based adhesive, the drying step is preferably performed at a drying temperature of about 20 to 80 ° C., preferably 40 to 80 ° C. for about 1 to 10 minutes, preferably 1 to 5 minutes.
接着剤がラジカル硬化型接着剤の場合には、前記貼り合わせ工程の後に、硬化工程を施して接着剤層を形成する。ラジカル硬化型接着剤が、電子線硬化型の場合には電子線照射により、紫外線硬化型の場合には紫外線処理により、熱硬化型の場合に熱処理により、それぞれ硬化処理を施す。これら硬化処理は、硬化の種類、接着剤の種類、接着剤層の厚みに対応して、適宜に各条件が設定される。 When the adhesive is a radical curable adhesive, a curing process is performed after the bonding process to form an adhesive layer. When the radical curable adhesive is electron beam curable, it is cured by electron beam irradiation, when it is ultraviolet curable, by ultraviolet treatment, and when it is thermosetting, it is cured by heat treatment. In these curing treatments, each condition is appropriately set according to the type of curing, the type of adhesive, and the thickness of the adhesive layer.
ラジカル硬化型接着剤としては、電子線硬化型接着剤が好適である。電子線の照射方向は、任意の適切な方向から照射することができる。好ましくは、透明保護フィルム側から照射する。偏光子側から照射すると、偏光子が電子線によって劣化するおそれがある。また、電子線照射は、搬送するフィルムの幅方向に均一に照射するのが好ましい。 An electron beam curable adhesive is suitable as the radical curable adhesive. The irradiation direction of the electron beam can be irradiated from any appropriate direction. Preferably, it irradiates from the transparent protective film side. When irradiated from the polarizer side, the polarizer may be deteriorated by the electron beam. Moreover, it is preferable that electron beam irradiation is uniformly irradiated to the width direction of the film to convey.
電子線の照射条件は、前記接着剤を硬化しうる条件であれば、任意の適切な条件を採用できる。例えば、電子線照射は、加速電圧が好ましくは5kV〜300kVであり、さらに好ましくは10kV〜250kVである。加速電圧が5kV未満の場合、電子線が接着剤まで届かず硬化不足となるおそれがあり、加速電圧が300kVを超えると、試料を通る浸透力が強すぎて電子線が跳ね返り、透明保護フィルムや偏光子にダメージを与えるおそれがある。照射線量としては、1〜500kGy、好ましくは10〜100kGy、さらに好ましくは20〜50kGyである。照射線量が1kGy未満の場合は、接着剤が硬化不足となり、500kGyを超えると、透明保護フィルムや偏光子にダメージを与え、機械的強度の低下や黄変を生じ、所定の光学特性を得ることができない。 Any appropriate condition can be adopted as the electron beam irradiation condition as long as the adhesive can be cured. For example, in the electron beam irradiation, the acceleration voltage is preferably 5 kV to 300 kV, and more preferably 10 kV to 250 kV. If the acceleration voltage is less than 5 kV, the electron beam may not reach the adhesive and may be insufficiently cured. If the acceleration voltage exceeds 300 kV, the penetration force through the sample is too strong and the electron beam rebounds, There is a risk of damaging the polarizer. The irradiation dose is 1 to 500 kGy, preferably 10 to 100 kGy, and more preferably 20 to 50 kGy. When the irradiation dose is less than 1 kGy, the adhesive becomes insufficiently cured, and when it exceeds 500 kGy, the transparent protective film and the polarizer are damaged, resulting in a decrease in mechanical strength and yellowing, thereby obtaining predetermined optical characteristics. I can't.
本発明において、電子線照射は、通常、不活性ガス中で照射を行うが、必要であれば大気中や酸素を少し導入した条件で行ってもよい。透明保護フィルムの材料によるが、酸素を適宜導入することによって、最初に電子線があたる透明保護フィルム面にあえて酸素阻害を生じさせ、透明保護フィルムへのダメージを防ぐことができ、接着剤にのみ効率的に電子線を照射させることができる。 In the present invention, electron beam irradiation is usually performed in an inert gas, but if necessary, it may be performed in the atmosphere or under a condition in which oxygen is slightly introduced. Depending on the material of the transparent protective film, by appropriately introducing oxygen, the transparent protective film surface where the electron beam first hits can be obstructed to prevent oxygen damage and prevent damage to the transparent protective film. An electron beam can be irradiated efficiently.
前記製造方法を連続ラインで行う場合、ライン速度は、接着剤の硬化時間によるが、好ましくは1〜500m/min、より好ましくは5〜300m/min、さらに好ましくは10〜100m/minである。ライン速度が小さすぎる場合は、生産性が乏しい、または透明保護フィルムへのダメージが大きすぎ、耐久性試験などに耐えうる偏光板が作製できない。ライン速度が大きすぎる場合は、接着剤の硬化が不十分となり、目的とする接着性が得られない場合がある。 When performing the said manufacturing method by a continuous line, although it depends on the hardening time of an adhesive agent, Preferably it is 1-500 m / min, More preferably, it is 5-300 m / min, More preferably, it is 10-100 m / min. When the line speed is too low, productivity is poor, or damage to the transparent protective film is too great, and a polarizing plate that can withstand a durability test or the like cannot be produced. When the line speed is too high, the adhesive is not sufficiently cured, and the target adhesiveness may not be obtained.
前記製造方法により形成される接着剤層が水系接着剤等により形成される場合には、前記接着剤層の厚みは、30〜300nmであるのが好ましい。前記接着剤層の厚さは、さらに好ましくは60〜250nmである。一方、接着剤層が硬化型接着剤により形成される場合には、前記接着剤層の厚みは、0.1〜200μmであるのが好ましい。より好ましくは、0.5〜50μm、さらに好ましくは0.5〜10μmである。 When the adhesive layer formed by the manufacturing method is formed of a water-based adhesive or the like, the thickness of the adhesive layer is preferably 30 to 300 nm. The thickness of the adhesive layer is more preferably 60 to 250 nm. On the other hand, when the adhesive layer is formed of a curable adhesive, the thickness of the adhesive layer is preferably 0.1 to 200 μm. More preferably, it is 0.5-50 micrometers, More preferably, it is 0.5-10 micrometers.
本発明の偏光板は、実用に際して他の光学層と積層した光学フィルムとして用いることができる。その光学層については特に限定はないが、例えば反射板や半透過板、位相差板(1/2や1/4等の波長板を含む)、視角補償フィルムなどの液晶表示装置等の形成に用いられることのある光学層を1層または2層以上用いることができる。特に、本発明の偏光板に更に反射板または半透過反射板が積層されてなる反射型偏光板または半透過型偏光板、偏光板に更に位相差板が積層されてなる楕円偏光板または円偏光板、偏光板に更に視角補償フィルムが積層されてなる広視野角偏光板、あるいは偏光板に更に輝度向上フィルムが積層されてなる偏光板が好ましい。 The polarizing plate of the present invention can be used as an optical film laminated with another optical layer in practical use. The optical layer is not particularly limited. For example, for forming a liquid crystal display device such as a reflection plate, a semi-transmission plate, a retardation plate (including wavelength plates such as 1/2 and 1/4), and a viewing angle compensation film. One or more optical layers that may be used can be used. In particular, a reflective polarizing plate or a semi-transmissive polarizing plate in which a polarizing plate or a semi-transmissive reflecting plate is further laminated on the polarizing plate of the present invention, an elliptical polarizing plate or a circularly polarizing plate in which a retardation plate is further laminated on the polarizing plate. A wide viewing angle polarizing plate obtained by further laminating a viewing angle compensation film on a plate or a polarizing plate, or a polarizing plate obtained by further laminating a brightness enhancement film on the polarizing plate is preferable.
反射型偏光板は、偏光板に反射層を設けたもので、視認側(表示側)からの入射光を反射させて表示するタイプの液晶表示装置などを形成するためのものであり、バックライト等の光源の内蔵を省略できて液晶表示装置の薄型化を図りやすいなどの利点を有する。反射型偏光板の形成は、必要に応じ透明保護層等を介して偏光板の片面に金属等からなる反射層を付設する方式などの適宜な方式にて行うことができる。 A reflective polarizing plate is a polarizing plate provided with a reflective layer, and is used to form a liquid crystal display device or the like that reflects incident light from the viewing side (display side). Such a light source can be omitted, and the liquid crystal display device can be easily thinned. The reflective polarizing plate can be formed by an appropriate method such as a method in which a reflective layer made of metal or the like is attached to one surface of the polarizing plate via a transparent protective layer or the like as necessary.
反射型偏光板の具体例としては、必要に応じマット処理した透明保護フィルムの片面に、アルミニウム等の反射性金属からなる箔や蒸着膜を付設して反射層を形成したものなどがあげられる。また前記透明保護フィルムに微粒子を含有させて表面微細凹凸構造とし、その上に微細凹凸構造の反射層を有するものなどもあげられる。前記した微細凹凸構造の反射層は、入射光を乱反射により拡散させて指向性やギラギラした見栄えを防止し、明暗のムラを抑制しうる利点などを有する。また微粒子含有の透明保護フィルムは、入射光及びその反射光がそれを透過する際に拡散されて明暗ムラをより抑制しうる利点なども有している。透明保護フィルムの表面微細凹凸構造を反映させた微細凹凸構造の反射層の形成は、例えば真空蒸着方式、イオンプレーティング方式、スパッタリング方式等の蒸着方式やメッキ方式などの適宜な方式で金属を透明保護層の表面に直接付設する方法などにより行うことができる。 Specific examples of the reflective polarizing plate include those in which a reflective layer is formed by attaching a foil or a vapor deposition film made of a reflective metal such as aluminum on one side of a transparent protective film matted as necessary. Moreover, the transparent protective film contains fine particles so as to have a surface fine concavo-convex structure and a reflective layer having a fine concavo-convex structure thereon. The reflective layer having the fine concavo-convex structure has an advantage that incident light is diffused by irregular reflection to prevent directivity and glaring appearance and to suppress unevenness in brightness and darkness. The transparent protective film containing fine particles also has an advantage that incident light and its reflected light are diffused when passing through it, and light and dark unevenness can be further suppressed. The reflective layer of the fine concavo-convex structure reflecting the surface fine concavo-convex structure of the transparent protective film is formed by transparent the metal by an appropriate method such as a vapor deposition method such as a vacuum vapor deposition method, an ion plating method, a sputtering method, or a plating method. It can be performed by a method of directly attaching to the surface of the protective layer.
反射板は前記の偏光板の透明保護フィルムに直接付与する方式に代えて、その透明フィルムに準じた適宜なフィルムに反射層を設けてなる反射シートなどとして用いることもできる。なお反射層は、通常、金属からなるので、その反射面が透明保護フィルムや偏光板等で被覆された状態の使用形態が、酸化による反射率の低下防止、ひいては初期反射率の長期持続の点や、保護層の別途付設の回避の点などより好ましい。 Instead of the method of directly applying the reflecting plate to the transparent protective film of the polarizing plate, the reflecting plate can be used as a reflecting sheet provided with a reflecting layer on an appropriate film according to the transparent film. Since the reflective layer is usually made of metal, the usage form in which the reflective surface is covered with a transparent protective film, a polarizing plate or the like is used to prevent the reflectance from being lowered due to oxidation, and thus to maintain the initial reflectance for a long time. In addition, it is more preferable to avoid a separate attachment of the protective layer.
なお、半透過型偏光板は、上記において反射層で光を反射し、かつ透過するハーフミラー等の半透過型の反射層とすることにより得ることができる。半透過型偏光板は、通常液晶セルの裏側に設けられ、液晶表示装置などを比較的明るい雰囲気で使用する場合には、視認側(表示側)からの入射光を反射させて画像を表示し、比較的暗い雰囲気においては、半透過型偏光板のバックサイドに内蔵されているバックライト等の内蔵光源を使用して画像を表示するタイプの液晶表示装置などを形成できる。すなわち、半透過型偏光板は、明るい雰囲気下では、バックライト等の光源使用のエネルギーを節約でき、比較的暗い雰囲気下においても内蔵光源を用いて使用できるタイプの液晶表示装置などの形成に有用である。 The semi-transmissive polarizing plate can be obtained by using a semi-transmissive reflective layer such as a half mirror that reflects and transmits light with the reflective layer. A transflective polarizing plate is usually provided on the back side of a liquid crystal cell, and displays an image by reflecting incident light from the viewing side (display side) when a liquid crystal display device is used in a relatively bright atmosphere. In a relatively dark atmosphere, a liquid crystal display device or the like that displays an image using a built-in light source such as a backlight built in the back side of the transflective polarizing plate can be formed. In other words, the transflective polarizing plate is useful for forming a liquid crystal display device of a type that can save energy of using a light source such as a backlight in a bright atmosphere and can be used with a built-in light source even in a relatively dark atmosphere. It is.
偏光板に更に位相差板が積層されてなる楕円偏光板または円偏光板について説明する。直線偏光を楕円偏光または円偏光に変えたり、楕円偏光または円偏光を直線偏光に変えたり、あるいは直線偏光の偏光方向を変える場合に、位相差板などが用いられる。特に、直線偏光を円偏光に変えたり、円偏光を直線偏光に変える位相差板としては、いわゆる1/4波長板(λ/4板とも言う)が用いられる。1/2波長板(λ/2板とも言う)は、通常、直線偏光の偏光方向を変える場合に用いられる。 An elliptically polarizing plate or a circularly polarizing plate in which a retardation plate is further laminated on a polarizing plate will be described. A phase difference plate or the like is used when changing linearly polarized light to elliptically polarized light or circularly polarized light, changing elliptically polarized light or circularly polarized light to linearly polarized light, or changing the polarization direction of linearly polarized light. In particular, a so-called quarter-wave plate (also referred to as a λ / 4 plate) is used as a retardation plate that changes linearly polarized light into circularly polarized light or changes circularly polarized light into linearly polarized light. A half-wave plate (also referred to as a λ / 2 plate) is usually used when changing the polarization direction of linearly polarized light.
楕円偏光板はスーパーツイストネマチック(STN)型液晶表示装置の液晶層の複屈折により生じた着色(青又は黄)を補償(防止)して、前記着色のない白黒表示する場合などに有効に用いられる。更に、三次元の屈折率を制御したものは、液晶表示装置の画面を斜め方向から見た際に生じる着色も補償(防止)することができて好ましい。円偏光板は、例えば画像がカラー表示になる反射型液晶表示装置の画像の色調を整える場合などに有効に用いられ、また、反射防止の機能も有する。上記した位相差板の具体例としては、ポリカーボネート、ポリビニルアルコール、ポリスチレン、ポリメチルメタクリレート、ポリプロピレンやその他のポリオレフィン、ポリアリレート、ポリアミドの如き適宜なポリマーからなるフィルムを延伸処理してなる複屈折性フィルムや液晶ポリマーの配向フィルム、液晶ポリマーの配向層をフィルムにて支持したものなどがあげられる。位相差板は、例えば各種波長板や液晶層の複屈折による着色や視角等の補償を目的としたものなどの使用目的に応じた適宜な位相差を有するものであってよく、2種以上の位相差板を積層して位相差等の光学特性を制御したものなどであってもよい。 The elliptically polarizing plate is effectively used for black and white display without the above color by compensating (preventing) the coloration (blue or yellow) generated by the birefringence of the liquid crystal layer of the super twist nematic (STN) type liquid crystal display device. It is done. Further, the one in which the three-dimensional refractive index is controlled is preferable because it can compensate (prevent) coloring that occurs when the screen of the liquid crystal display device is viewed from an oblique direction. The circularly polarizing plate is effectively used, for example, when adjusting the color tone of an image of a reflective liquid crystal display device in which an image is displayed in color, and also has an antireflection function. Specific examples of the retardation plate include a birefringent film obtained by stretching a film made of an appropriate polymer such as polycarbonate, polyvinyl alcohol, polystyrene, polymethyl methacrylate, polypropylene, other polyolefins, polyarylate, and polyamide. And an alignment film of a liquid crystal polymer, and a liquid crystal polymer alignment layer supported by a film. The retardation plate may have an appropriate retardation according to the purpose of use, such as those for the purpose of compensating for various wavelength plates or birefringence of the liquid crystal layer, viewing angle, and the like. What laminated | stacked the phase difference plate and controlled optical characteristics, such as phase difference, etc. may be used.
また上記の楕円偏光板や反射型楕円偏光板は、偏光板又は反射型偏光板と位相差板を適宜な組み合わせで積層したものである。かかる楕円偏光板等は、(反射型)偏光板と位相差板の組み合わせとなるようにそれらを液晶表示装置の製造過程で順次別個に積層することによっても形成しうるが、前記の如く予め楕円偏光板等の光学フィルムとしたものは、品質の安定性や積層作業性等に優れて液晶表示装置などの製造効率を向上させうる利点がある。 The elliptical polarizing plate and the reflective elliptical polarizing plate are obtained by laminating a polarizing plate or a reflective polarizing plate and a retardation plate in an appropriate combination. Such an elliptically polarizing plate or the like can also be formed by sequentially laminating them sequentially in the manufacturing process of the liquid crystal display device so as to be a combination of a (reflection type) polarizing plate and a retardation plate. An optical film such as a polarizing plate has an advantage that it can improve the production efficiency of a liquid crystal display device and the like because of excellent quality stability and lamination workability.
視角補償フィルムは、液晶表示装置の画面を、画面に垂直でなくやや斜めの方向から見た場合でも、画像が比較的鮮明にみえるように視野角を広げるためのフィルムである。このような視角補償位相差板としては、例えば位相差フィルム、液晶ポリマー等の配向フィルムや透明基材上に液晶ポリマー等の配向層を支持したものなどからなる。通常の位相差板は、その面方向に一軸に延伸された複屈折を有するポリマーフィルムが用いられるのに対し、視角補償フィルムとして用いられる位相差板には、面方向に二軸に延伸された複屈折を有するポリマーフィルムとか、面方向に一軸に延伸され厚さ方向にも延伸された厚さ方向の屈折率を制御した複屈折を有するポリマーや傾斜配向フィルムのような二方向延伸フィルムなどが用いられる。傾斜配向フィルムとしては、例えばポリマーフィルムに熱収縮フィルムを接着して加熱によるその収縮力の作用下にポリマーフィルムを延伸処理又は/及び収縮処理したものや、液晶ポリマーを斜め配向させたものなどが挙げられる。位相差板の素材原料ポリマーは、先の位相差板で説明したポリマーと同様のものが用いられ、液晶セルによる位相差に基づく視認角の変化による着色等の防止や良視認の視野角の拡大などを目的とした適宜なものを用いうる。 The viewing angle compensation film is a film for widening the viewing angle so that an image can be seen relatively clearly even when the screen of the liquid crystal display device is viewed from a slightly oblique direction rather than perpendicular to the screen. As such a viewing angle compensation phase difference plate, for example, a retardation film, an alignment film such as a liquid crystal polymer, or an alignment layer such as a liquid crystal polymer supported on a transparent substrate is used. A normal retardation plate uses a birefringent polymer film uniaxially stretched in the plane direction, whereas a retardation plate used as a viewing angle compensation film stretches biaxially in the plane direction. Birefringent polymer film, biaxially stretched film such as polymer with birefringence with a controlled refractive index in the thickness direction that is uniaxially stretched in the plane direction and stretched in the thickness direction, etc. Used. Examples of the inclined alignment film include a film obtained by bonding a heat shrink film to a polymer film and stretching or / and shrinking the polymer film under the action of the contraction force by heating, and a film obtained by obliquely aligning a liquid crystal polymer. Can be mentioned. The raw material polymer for the phase difference plate is the same as the polymer described in the previous phase difference plate, preventing coloration due to a change in the viewing angle based on the phase difference by the liquid crystal cell and expanding the viewing angle for good visual recognition. An appropriate one for the purpose can be used.
また良視認の広い視野角を達成する点などより、液晶ポリマーの配向層、特にディスコティック液晶ポリマーの傾斜配向層からなる光学的異方性層をトリアセチルセルロースフィルムにて支持した光学補償位相差板が好ましく用いうる。 Also, from the viewpoint of achieving a wide viewing angle with good visibility, an optically compensated phase difference in which a liquid crystal polymer alignment layer, in particular an optically anisotropic layer composed of a discotic liquid crystal polymer gradient alignment layer, is supported by a triacetylcellulose film. A plate can be preferably used.
偏光板と輝度向上フィルムを貼り合わせた偏光板は、通常液晶セルの裏側サイドに設けられて使用される。輝度向上フィルムは、液晶表示装置などのバックライトや裏側からの反射などにより自然光が入射すると所定偏光軸の直線偏光または所定方向の円偏光を反射し、他の光は透過する特性を示すもので、輝度向上フィルムを偏光板と積層した偏光板は、バックライト等の光源からの光を入射させて所定偏光状態の透過光を得ると共に、前記所定偏光状態以外の光は透過せずに反射される。この輝度向上フィルム面で反射した光を更にその後ろ側に設けられた反射層等を介し反転させて輝度向上フィルムに再入射させ、その一部又は全部を所定偏光状態の光として透過させて輝度向上フィルムを透過する光の増量を図ると共に、偏光子に吸収させにくい偏光を供給して液晶表示画像表示等に利用しうる光量の増大を図ることにより輝度を向上させうるものである。すなわち、輝度向上フィルムを使用せずに、バックライトなどで液晶セルの裏側から偏光子を通して光を入射した場合には、偏光子の偏光軸に一致していない偏光方向を有する光は、ほとんど偏光子に吸収されてしまい、偏光子を透過してこない。すなわち、用いた偏光子の特性によっても異なるが、およそ50%の光が偏光子に吸収されてしまい、その分、液晶画像表示等に利用しうる光量が減少し、画像が暗くなる。輝度向上フィルムは、偏光子に吸収されるような偏光方向を有する光を偏光子に入射させずに輝度向上フィルムで一旦反射させ、更にその後ろ側に設けられた反射層等を介して反転させて輝度向上フィルムに再入射させることを繰り返し、この両者間で反射、反転している光の偏光方向が偏光子を通過し得るような偏光方向になった偏光のみを、輝度向上フィルムは透過させて偏光子に供給するので、バックライトなどの光を効率的に液晶表示装置の画像の表示に使用でき、画面を明るくすることができる。 A polarizing plate obtained by bonding a polarizing plate and a brightness enhancement film is usually provided on the back side of a liquid crystal cell. The brightness enhancement film reflects a linearly polarized light with a predetermined polarization axis or a circularly polarized light in a predetermined direction when natural light is incident due to a backlight such as a liquid crystal display device or reflection from the back side, and transmits other light. In addition, a polarizing plate in which a brightness enhancement film is laminated with a polarizing plate allows light from a light source such as a backlight to enter to obtain transmitted light in a predetermined polarization state, and reflects light without transmitting the light other than the predetermined polarization state. The The light reflected on the surface of the brightness enhancement film is further inverted through a reflective layer or the like provided behind the brightness enhancement film and re-incident on the brightness enhancement film, and part or all of the light is transmitted as light having a predetermined polarization state. Luminance can be improved by increasing the amount of light transmitted through the enhancement film and increasing the amount of light that can be used for liquid crystal display image display or the like by supplying polarized light that is difficult to be absorbed by the polarizer. That is, when light is incident through the polarizer from the back side of the liquid crystal cell without using a brightness enhancement film, light having a polarization direction that does not coincide with the polarization axis of the polarizer is almost polarized. It is absorbed by the polarizer and does not pass through the polarizer. That is, although depending on the characteristics of the polarizer used, approximately 50% of the light is absorbed by the polarizer, and the amount of light that can be used for liquid crystal image display or the like is reduced accordingly, resulting in a dark image. The brightness enhancement film allows light having a polarization direction that is absorbed by the polarizer to be reflected once by the brightness enhancement film without being incident on the polarizer, and further inverted through a reflective layer provided on the rear side thereof. Repeatedly re-enter the brightness enhancement film, and the brightness enhancement film transmits only polarized light whose polarization direction is such that the polarization direction of light reflected and inverted between the two can pass through the polarizer. Therefore, light such as a backlight can be efficiently used for displaying an image on the liquid crystal display device, and the screen can be brightened.
輝度向上フィルムと上記反射層等の間に拡散板を設けることもできる。輝度向上フィルムによって反射した偏光状態の光は上記反射層等に向かうが、設置された拡散板は通過する光を均一に拡散すると同時に偏光状態を解消し、非偏光状態となる。すなわち、拡散板は偏光を元の自然光状態にもどす。この非偏光状態、すなわち自然光状態の光が反射層等に向かい、反射層等を介して反射し、再び拡散板を通過して輝度向上フィルムに再入射することを繰り返す。このように輝度向上フィルムと上記反射層等の間に、偏光を元の自然光状態にもどす拡散板を設けることにより表示画面の明るさを維持しつつ、同時に表示画面の明るさのむらを少なくし、均一で明るい画面を提供することができる。かかる拡散板を設けることにより、初回の入射光は反射の繰り返し回数が程よく増加し、拡散板の拡散機能と相俟って均一の明るい表示画面を提供することができたものと考えられる。 A diffusion plate may be provided between the brightness enhancement film and the reflective layer. The polarized light reflected by the brightness enhancement film is directed to the reflective layer or the like, but the installed diffuser plate uniformly diffuses the light passing therethrough and simultaneously cancels the polarized state and becomes a non-polarized state. That is, the diffuser plate returns the polarized light to the original natural light state. The light in the non-polarized state, that is, the natural light state is directed toward the reflection layer and the like, reflected through the reflection layer and the like, and again passes through the diffusion plate and reenters the brightness enhancement film. Thus, while maintaining the brightness of the display screen by providing a diffuser plate that returns polarized light to the original natural light state between the brightness enhancement film and the reflective layer, etc., the brightness unevenness of the display screen is reduced at the same time, A uniform and bright screen can be provided. By providing such a diffuser plate, it is considered that the first incident light has a moderate increase in the number of repetitions of reflection, and in combination with the diffusion function of the diffuser plate, a uniform bright display screen can be provided.
前記の輝度向上フィルムとしては、例えば誘電体の多層薄膜や屈折率異方性が相違する薄膜フィルムの多層積層体の如き、所定偏光軸の直線偏光を透過して他の光は反射する特性を示すもの、コレステリック液晶ポリマーの配向フィルムやその配向液晶層をフィルム基材上に支持したものの如き、左回り又は右回りのいずれか一方の円偏光を反射して他の光は透過する特性を示すものなどの適宜なものを用いうる。 The brightness enhancement film has a characteristic of transmitting linearly polarized light having a predetermined polarization axis and reflecting other light, such as a multilayer thin film of dielectric material or a multilayer laminate of thin film films having different refractive index anisotropies. Such as an alignment film of a cholesteric liquid crystal polymer or an alignment liquid crystal layer supported on a film substrate, which reflects either left-handed or right-handed circularly polarized light and transmits other light. Appropriate things, such as a thing, can be used.
従って、前記した所定偏光軸の直線偏光を透過させるタイプの輝度向上フィルムでは、その透過光をそのまま偏光板に偏光軸を揃えて入射させることにより、偏光板による吸収ロスを抑制しつつ効率よく透過させることができる。一方、コレステリック液晶層の如く円偏光を透過するタイプの輝度向上フィルムでは、そのまま偏光子に入射させることもできるが、吸収ロスを抑制する点よりその円偏光を位相差板を介し直線偏光化して偏光板に入射させることが好ましい。なお、その位相差板として1/4波長板を用いることにより、円偏光を直線偏光に変換することができる。 Therefore, in the brightness enhancement film of the type that transmits linearly polarized light having the predetermined polarization axis as described above, the transmitted light is incident on the polarizing plate with the polarization axis aligned as it is, thereby efficiently transmitting while suppressing absorption loss due to the polarizing plate. Can be made. On the other hand, in a brightness enhancement film of a type that transmits circularly polarized light such as a cholesteric liquid crystal layer, it can be directly incident on a polarizer, but from the point of suppressing absorption loss, the circularly polarized light is linearly polarized through a retardation plate. It is preferable to make it enter into a polarizing plate. Note that circularly polarized light can be converted to linearly polarized light by using a quarter wave plate as the retardation plate.
可視光域等の広い波長範囲で1/4波長板として機能する位相差板は、例えば波長550nmの淡色光に対して1/4波長板として機能する位相差層と他の位相差特性を示す位相差層、例えば1/2波長板として機能する位相差層とを重畳する方式などにより得ることができる。従って、偏光板と輝度向上フィルムの間に配置する位相差板は、1層又は2層以上の位相差層からなるものであってよい。 A retardation plate that functions as a quarter-wave plate in a wide wavelength range such as a visible light region exhibits, for example, a retardation layer that functions as a quarter-wave plate for light-color light having a wavelength of 550 nm and other retardation characteristics. It can be obtained by a method of superposing a retardation layer, for example, a retardation layer functioning as a half-wave plate. Therefore, the retardation plate disposed between the polarizing plate and the brightness enhancement film may be composed of one or more retardation layers.
なお、コレステリック液晶層についても、反射波長が相違するものの組み合わせにして2層又は3層以上重畳した配置構造とすることにより、可視光領域等の広い波長範囲で円偏光を反射するものを得ることができ、それに基づいて広い波長範囲の透過円偏光を得ることができる。 In addition, the cholesteric liquid crystal layer can also be obtained by reflecting circularly polarized light in a wide wavelength range such as a visible light region by combining two or more layers having different reflection wavelengths and having an overlapping structure. Based on this, transmitted circularly polarized light in a wide wavelength range can be obtained.
また、偏光板は、上記の偏光分離型偏光板の如く、偏光板と2層又は3層以上の光学層とを積層したものからなっていてもよい。従って、上記の反射型偏光板や半透過型偏光板と位相差板を組み合わせた反射型楕円偏光板や半透過型楕円偏光板などであってもよい。 Further, the polarizing plate may be formed by laminating a polarizing plate and two or three or more optical layers like the above-described polarization separation type polarizing plate. Therefore, a reflective elliptical polarizing plate or a semi-transmissive elliptical polarizing plate in which the above-mentioned reflective polarizing plate or transflective polarizing plate and a retardation plate are combined may be used.
偏光板に前記光学層を積層した光学フィルムは、液晶表示装置等の製造過程で順次別個に積層する方式にても形成することができるが、予め積層して光学フィルムとしたものは、品質の安定性や組立作業等に優れていて液晶表示装置などの製造工程を向上させうる利点がある。積層には粘着層等の適宜な接着手段を用いうる。前記の偏光板やその他の光学フィルムの接着に際し、それらの光学軸は目的とする位相差特性などに応じて適宜な配置角度とすることができる。 An optical film in which the optical layer is laminated on a polarizing plate can be formed by a method of sequentially laminating separately in the manufacturing process of a liquid crystal display device or the like. There is an advantage that the manufacturing process of a liquid crystal display device or the like can be improved because of excellent stability and assembly work. For the lamination, an appropriate adhesive means such as an adhesive layer can be used. When adhering the polarizing plate and other optical films, their optical axes can be set at an appropriate arrangement angle in accordance with the target retardation characteristics.
前述した偏光板や、偏光板を少なくとも1層積層されている光学フィルムには、液晶セル等の他部材と接着するための粘着層を設けることもできる。粘着層を形成する粘着剤は特に制限されないが、例えばアクリル系重合体、シリコーン系ポリマー、ポリエステル、ポリウレタン、ポリアミド、ポリエーテル、フッ素系やゴム系などのポリマーをベースポリマーとするものを適宜に選択して用いることができる。特に、アクリル系粘着剤の如く光学的透明性に優れ、適度な濡れ性と凝集性と接着性の粘着特性を示して、耐候性や耐熱性などに優れるものが好ましく用いうる。 An adhesive layer for adhering to other members such as a liquid crystal cell may be provided on the polarizing plate described above or an optical film in which at least one polarizing plate is laminated. The pressure-sensitive adhesive forming the pressure-sensitive adhesive layer is not particularly limited. For example, an acrylic polymer, silicone polymer, polyester, polyurethane, polyamide, polyether, fluorine-based or rubber-based polymer is appropriately selected. Can be used. In particular, those having excellent optical transparency such as an acrylic pressure-sensitive adhesive, exhibiting appropriate wettability, cohesiveness, and adhesive pressure-sensitive adhesive properties, and being excellent in weather resistance, heat resistance and the like can be preferably used.
また上記に加えて、吸湿による発泡現象や剥がれ現象の防止、熱膨張差等による光学特性の低下や液晶セルの反り防止、ひいては高品質で耐久性に優れる液晶表示装置の形成性などの点より、吸湿率が低くて耐熱性に優れる粘着層が好ましい。 In addition to the above, in terms of prevention of foaming and peeling phenomena due to moisture absorption, deterioration of optical properties and liquid crystal cell warpage due to differences in thermal expansion, etc., as well as formability of liquid crystal display devices with high quality and excellent durability An adhesive layer having a low moisture absorption rate and excellent heat resistance is preferred.
粘着層は、例えば天然物や合成物の樹脂類、特に、粘着性付与樹脂や、ガラス繊維、ガラスビーズ、金属粉、その他の無機粉末等からなる充填剤や顔料、着色剤、酸化防止剤などの粘着層に添加されることの添加剤を含有していてもよい。また微粒子を含有して光拡散性を示す粘着層などであってもよい。 The adhesive layer is, for example, natural or synthetic resins, in particular, tackifier resins, fillers or pigments made of glass fibers, glass beads, metal powders, other inorganic powders, colorants, antioxidants, etc. It may contain an additive to be added to the adhesive layer. Moreover, the adhesion layer etc. which contain microparticles | fine-particles and show light diffusibility may be sufficient.
偏光板や光学フィルムの片面又は両面への粘着層の付設は、適宜な方式で行いうる。その例としては、例えばトルエンや酢酸エチル等の適宜な溶剤の単独物又は混合物からなる溶媒にベースポリマーまたはその組成物を溶解又は分散させた10〜40重量%程度の粘着剤溶液を調製し、それを流延方式や塗工方式等の適宜な展開方式で偏光板上または光学フィルム上に直接付設する方式、あるいは前記に準じセパレータ上に粘着層を形成してそれを偏光板上または光学フィルム上に移着する方式などがあげられる。 Attachment of the adhesive layer to one or both sides of the polarizing plate or the optical film can be performed by an appropriate method. For example, a pressure sensitive adhesive solution of about 10 to 40% by weight in which a base polymer or a composition thereof is dissolved or dispersed in a solvent composed of a suitable solvent alone or a mixture such as toluene and ethyl acetate is prepared. A method in which it is directly attached on a polarizing plate or an optical film by an appropriate development method such as a casting method or a coating method, or an adhesive layer is formed on a separator according to the above, and this is applied to a polarizing plate or an optical film. The method of moving up is mentioned.
粘着層は、異なる組成又は種類等のものの重畳層として偏光板や光学フィルムの片面又は両面に設けることもできる。また両面に設ける場合に、偏光板や光学フィルムの表裏において異なる組成や種類や厚さ等の粘着層とすることもできる。粘着層の厚さは、使用目的や接着力などに応じて適宜に決定でき、一般には1〜40μmであり、5〜30μmが好ましく、特に10〜25μmが好ましい。1μmより薄いと耐久性が悪くなり、また40μmより厚いと発泡などによる浮きや剥がれが生じやすく外観不良となる、 The pressure-sensitive adhesive layer can be provided on one side or both sides of a polarizing plate or an optical film as a superimposed layer of different compositions or types. Moreover, when providing in both surfaces, it can also be set as the adhesion layers of a different composition, a kind, thickness, etc. in the front and back of a polarizing plate or an optical film. The thickness of the pressure-sensitive adhesive layer can be appropriately determined according to the purpose of use and adhesive force, and is generally 1 to 40 μm, preferably 5 to 30 μm, particularly preferably 10 to 25 μm. If it is thinner than 1 μm, the durability will be poor, and if it is thicker than 40 μm, it will be liable to float or peel off due to foaming, resulting in poor appearance.
粘着層の露出面に対しては、実用に供するまでの間、その汚染防止等を目的にセパレータが仮着されてカバーされる。これにより、通例の取扱状態で粘着層に接触することを防止できる。セパレータとしては、上記厚さ条件を除き、例えばプラスチックフィルム、ゴムシート、紙、布、不織布、ネット、発泡シートや金属箔、それらのラミネート体等の適宜な薄葉体を、必要に応じシリコーン系や長鎖アルキル系、フッ素系や硫化モリブデン等の適宜な剥離剤でコート処理したものなどの、従来に準じた適宜なものを用いうる。 On the exposed surface of the adhesive layer, a separator is temporarily attached and covered for the purpose of preventing contamination until it is put to practical use. Thereby, it can prevent contacting an adhesion layer in the usual handling state. As the separator, except for the above thickness conditions, for example, a suitable thin leaf body such as a plastic film, rubber sheet, paper, cloth, non-woven fabric, net, foam sheet, metal foil, laminate thereof, and the like, silicone type or Appropriate conventional ones such as those coated with an appropriate release agent such as long-chain alkyl, fluorine-based, or molybdenum sulfide can be used.
偏光板と粘着剤層との間の密着性を向上させるために、その層間にアンカー層を設けることもできる。 In order to improve the adhesion between the polarizing plate and the pressure-sensitive adhesive layer, an anchor layer can be provided between the layers.
上記アンカー層の形成材としては、好ましくは、ポリウレタン、ポリエステル、分子中にアミノ基を含むポリマー類から選ばれるアンカー剤が用いられ、特に好ましくは、分子中にアミノ基を含んだポリマー類である。分子中にアミノ基を含むポリマー類は、分子中のアミノ基が粘着剤中のカルボキシル基等と反応またはイオン性相互作用などの相互作用を示すため、良好な密着性が確保される。 As the material for forming the anchor layer, an anchor agent selected from polyurethane, polyester, and polymers containing an amino group in the molecule is preferably used, and polymers containing an amino group in the molecule are particularly preferred. . Polymers containing an amino group in the molecule ensure good adhesion because the amino group in the molecule exhibits an interaction such as a reaction or ionic interaction with the carboxyl group in the pressure-sensitive adhesive.
分子中にアミノ基を含むポリマー類としては、例えば、ポリエチレンイミン、ポリアリルアミン、ポリビニルアミン、ポリビニルピリジン、ポリビニルピロリジン、ジメチルアミノエチルアクリレート等の含アミノ基含有モノマーの重合体などをあげることができる。 Examples of polymers containing an amino group in the molecule include polymers of amino-containing group-containing monomers such as polyethyleneimine, polyallylamine, polyvinylamine, polyvinylpyridine, polyvinylpyrrolidine, dimethylaminoethyl acrylate, and the like.
上記アンカー層には、帯電防止性を付与するために、帯電防止剤を添加することもできる。帯電防止性付与のための帯電防止剤としては、イオン性界面活性剤系、ポリアニリン、ポリチオフェン、ポリピロール、ポリキノキサリン等の導電性ポリマー系、酸化スズ、酸化アンチモン、酸化インジウム等の金属酸化物系などがあげられるが、特に光学特性、外観、帯電防止効果、および帯電防止効果の加熱、加湿時での安定性という観点から、導電性ポリマー系が好ましく使用される。この中でも、ポリアニリン、ポリチオフェンなどの水溶性導電性ポリマー、もしくは水分散性導電性ポリマーが特に好ましく使用される。帯電防止層の形成材料として水溶性導電性ポリマーや水分散性導電性ポリマーを用いた場合、塗工に際して有機溶剤による光学フィルム基材への変質を抑えることができる。 An antistatic agent may be added to the anchor layer in order to impart antistatic properties. Antistatic agents for imparting antistatic properties include ionic surfactant systems, conductive polymer systems such as polyaniline, polythiophene, polypyrrole, and polyquinoxaline, metal oxide systems such as tin oxide, antimony oxide, and indium oxide. In particular, from the viewpoint of optical properties, appearance, antistatic effect, and antistatic effect heating and stability during humidification, a conductive polymer system is preferably used. Among these, water-soluble conductive polymers such as polyaniline and polythiophene or water-dispersible conductive polymers are particularly preferably used. When a water-soluble conductive polymer or a water-dispersible conductive polymer is used as a material for forming the antistatic layer, it is possible to suppress deterioration of the optical film substrate due to an organic solvent during coating.
なお本発明において、上記した偏光板を形成する偏光子や透明保護フィルムや光学フィルム等、また粘着層などの各層には、例えばサリチル酸エステル系化合物やベンゾフェノール系化合物、ベンゾトリアゾール系化合物やシアノアクリレート系化合物、ニッケル錯塩系化合物等の紫外線吸収剤で処理する方式などの方式により紫外線吸収能をもたせたものなどであってもよい。 In the present invention, the polarizer, the transparent protective film, the optical film, and the like that form the polarizing plate described above, and each layer such as the adhesive layer include, for example, salicylic acid ester compounds, benzophenol compounds, benzotriazole compounds, and cyanoacrylates. It may be a compound having an ultraviolet absorbing ability by a method such as a method of treating with an ultraviolet absorber such as a compound based on nickel or a nickel complex salt compound.
本発明の偏光板または光学フィルムは液晶表示装置等の各種装置の形成などに好ましく用いることができる。液晶表示装置の形成は、従来に準じて行いうる。すなわち液晶表示装置は一般に、液晶セルと偏光板または光学フィルム、及び必要に応じての照明システム等の構成部品を適宜に組立てて駆動回路を組込むことなどにより形成されるが、本発明においては本発明による偏光板または光学フィルムを用いる点を除いて特に限定はなく、従来に準じうる。液晶セルについても、例えばTN型やSTN型、π型、VA型、IPS型、などの任意なタイプのものを用いうる。 The polarizing plate or the optical film of the present invention can be preferably used for forming various devices such as a liquid crystal display device. The liquid crystal display device can be formed according to the conventional method. That is, a liquid crystal display device is generally formed by appropriately assembling components such as a liquid crystal cell, a polarizing plate or an optical film, and an illumination system as necessary, and incorporating a drive circuit. There is no limitation in particular except the point which uses the polarizing plate or optical film by invention, and it can apply according to the former. As the liquid crystal cell, any type such as a TN type, STN type, π type, VA type, IPS type, or the like can be used.
液晶セルの片側又は両側に偏光板または光学フィルムを配置した液晶表示装置や、照明システムにバックライトあるいは反射板を用いたものなどの適宜な液晶表示装置を形成することができる。その場合、本発明による偏光板または光学フィルムは液晶セルの片側又は両側に設置することができる。両側に偏光板または光学フィルムを設ける場合、それらは同じものであってもよいし、異なるものであってもよい。さらに、液晶表示装置の形成に際しては、例えば拡散板、アンチグレア層、反射防止膜、保護板、プリズムアレイ、レンズアレイシート、光拡散板、バックライトなどの適宜な部品を適宜な位置に1層又は2層以上配置することができる。 An appropriate liquid crystal display device such as a liquid crystal display device in which a polarizing plate or an optical film is disposed on one side or both sides of a liquid crystal cell, or a backlight or a reflector used in an illumination system can be formed. In that case, the polarizing plate or optical film by this invention can be installed in the one side or both sides of a liquid crystal cell. When providing a polarizing plate or an optical film on both sides, they may be the same or different. Further, when forming a liquid crystal display device, for example, a single layer or a suitable part such as a diffusing plate, an antiglare layer, an antireflection film, a protective plate, a prism array, a lens array sheet, a light diffusing plate, a backlight, etc. Two or more layers can be arranged.
次いで有機エレクトロルミネセンス装置(有機EL表示装置)について説明する。一般に、有機EL表示装置は、透明基板上に透明電極と有機発光層と金属電極とを順に積層して発光体(有機エレクトロルミネセンス発光体)を形成している。ここで、有機発光層は、種々の有機薄膜の積層体であり、例えばトリフェニルアミン誘導体等からなる正孔注入層と、アントラセン等の蛍光性の有機固体からなる発光層との積層体や、あるいはこのような発光層とペリレン誘導体等からなる電子注入層の積層体や、またあるいはこれらの正孔注入層、発光層、および電子注入層の積層体等、種々の組み合わせをもった構成が知られている。 Next, an organic electroluminescence device (organic EL display device) will be described. Generally, in an organic EL display device, a transparent electrode, an organic light emitting layer, and a metal electrode are sequentially laminated on a transparent substrate to form a light emitter (organic electroluminescent light emitter). Here, the organic light emitting layer is a laminate of various organic thin films, for example, a laminate of a hole injection layer made of a triphenylamine derivative and the like and a light emitting layer made of a fluorescent organic solid such as anthracene, Alternatively, a structure having various combinations such as a laminate of such a light emitting layer and an electron injection layer composed of a perylene derivative or the like, or a laminate of these hole injection layer, light emitting layer, and electron injection layer is known. It has been.
有機EL表示装置は、透明電極と金属電極とに電圧を印加することによって、有機発光層に正孔と電子とが注入され、これら正孔と電子との再結合によって生じるエネルギーが蛍光物資を励起し、励起された蛍光物質が基底状態に戻るときに光を放射する、という原理で発光する。途中の再結合というメカニズムは、一般のダイオードと同様であり、このことからも予想できるように、電流と発光強度は印加電圧に対して整流性を伴う強い非線形性を示す。 In organic EL display devices, holes and electrons are injected into the organic light-emitting layer by applying a voltage to the transparent electrode and the metal electrode, and the energy generated by recombination of these holes and electrons excites the phosphor material. Then, light is emitted on the principle that the excited fluorescent material emits light when returning to the ground state. The mechanism of recombination in the middle is the same as that of a general diode, and as can be predicted from this, the current and the emission intensity show strong nonlinearity with rectification with respect to the applied voltage.
有機EL表示装置においては、有機発光層での発光を取り出すために、少なくとも一方の電極が透明でなくてはならず、通常酸化インジウムスズ(ITO)などの透明導電体で形成した透明電極を陽極として用いている。一方、電子注入を容易にして発光効率を上げるには、陰極に仕事関数の小さな物質を用いることが重要で、通常Mg−Ag、Al−Liなどの金属電極を用いている。 In an organic EL display device, in order to extract light emitted from the organic light emitting layer, at least one of the electrodes must be transparent, and a transparent electrode usually formed of a transparent conductor such as indium tin oxide (ITO) is used as an anode. It is used as. On the other hand, in order to facilitate electron injection and increase luminous efficiency, it is important to use a material having a small work function for the cathode, and usually metal electrodes such as Mg—Ag and Al—Li are used.
このような構成の有機EL表示装置において、有機発光層は、厚さ10nm程度ときわめて薄い膜で形成されている。このため、有機発光層も透明電極と同様、光をほぼ完全に透過する。その結果、非発光時に透明基板の表面から入射し、透明電極と有機発光層とを透過して金属電極で反射した光が、再び透明基板の表面側へと出るため、外部から視認したとき、有機EL表示装置の表示面が鏡面のように見える。 In the organic EL display device having such a configuration, the organic light emitting layer is formed of a very thin film having a thickness of about 10 nm. For this reason, the organic light emitting layer transmits light almost completely like the transparent electrode. As a result, light that is incident from the surface of the transparent substrate at the time of non-light emission, passes through the transparent electrode and the organic light emitting layer, and is reflected by the metal electrode is again emitted to the surface side of the transparent substrate. The display surface of the organic EL display device looks like a mirror surface.
電圧の印加によって発光する有機発光層の表面側に透明電極を備えるとともに、有機発光層の裏面側に金属電極を備えてなる有機エレクトロルミネセンス発光体を含む有機EL表示装置において、透明電極の表面側に偏光板を設けるとともに、これら透明電極と偏光板との間に位相差板を設けることができる。 In an organic EL display device comprising an organic electroluminescent light emitting device comprising a transparent electrode on the surface side of an organic light emitting layer that emits light upon application of a voltage and a metal electrode on the back side of the organic light emitting layer, the surface of the transparent electrode While providing a polarizing plate on the side, a retardation plate can be provided between the transparent electrode and the polarizing plate.
位相差板および偏光板は、外部から入射して金属電極で反射してきた光を偏光する作用を有するため、その偏光作用によって金属電極の鏡面を外部から視認させないという効果がある。特に、位相差板を1/4波長板で構成し、かつ偏光板と位相差板との偏光方向のなす角をπ/4に調整すれば、金属電極の鏡面を完全に遮蔽することができる。 Since the retardation plate and the polarizing plate have a function of polarizing light incident from the outside and reflected by the metal electrode, there is an effect that the mirror surface of the metal electrode is not visually recognized by the polarization action. In particular, the mirror surface of the metal electrode can be completely shielded by configuring the retardation plate with a quarter-wave plate and adjusting the angle formed by the polarization direction of the polarizing plate and the retardation plate to π / 4. .
すなわち、この有機EL表示装置に入射する外部光は、偏光板により直線偏光成分のみが透過する。この直線偏光は位相差板により一般に楕円偏光となるが、とくに位相差板が1/4波長板でしかも偏光板と位相差板との偏光方向のなす角がπ/4のときには円偏光となる。 That is, only the linearly polarized light component of the external light incident on the organic EL display device is transmitted by the polarizing plate. This linearly polarized light becomes generally elliptically polarized light by the phase difference plate, but becomes circularly polarized light particularly when the phase difference plate is a quarter wavelength plate and the angle formed by the polarization direction of the polarizing plate and the phase difference plate is π / 4. .
この円偏光は、透明基板、透明電極、有機薄膜を透過し、金属電極で反射して、再び有機薄膜、透明電極、透明基板を透過して、位相差板に再び直線偏光となる。そして、この直線偏光は、偏光板の偏光方向と直交しているので、偏光板を透過できない。その結果、金属電極の鏡面を完全に遮蔽することができる。 This circularly polarized light is transmitted through the transparent substrate, the transparent electrode, and the organic thin film, is reflected by the metal electrode, is again transmitted through the organic thin film, the transparent electrode, and the transparent substrate, and becomes linearly polarized light again on the retardation plate. And since this linearly polarized light is orthogonal to the polarization direction of a polarizing plate, it cannot permeate | transmit a polarizing plate. As a result, the mirror surface of the metal electrode can be completely shielded.
以下に、本発明の実施例を記載するが、本発明の実施形態はこれらに限定されない。 Examples of the present invention will be described below, but the embodiments of the present invention are not limited thereto.
(偏光子)
平均重合度2400、ケン化度99.9モル%、厚さ75μmのポリビニルアルコールフィルムを、30℃の温水中に60秒間浸漬して膨潤させた。次いで、3.2重量%(重量比:ヨウ素/ヨウ化カリウム=1/7)の30℃のヨウ素溶液中で30秒間染色しながら、3.3倍まで延伸した。次いで、30℃の3重量%のホウ酸、3重量%のヨウ化カリウム水溶液中に1分間浸漬しながら3.6倍まで延伸した。その後、60℃の4重量%のホウ酸、5重量%のヨウ化カリウム水溶液中に30秒間浸漬しながら総合延伸倍率が6倍まで延伸した。さらに、3重量%のヨウ化カリウム水溶液中に10秒間浸漬してヨウ素イオン含浸処理をした。その後、60℃のオーブンで4分間乾燥を行い、厚さ30μmの偏光子を得た。偏光子の水分率は12重量%であった。
(Polarizer)
A polyvinyl alcohol film having an average polymerization degree of 2400, a saponification degree of 99.9 mol%, and a thickness of 75 μm was immersed in warm water at 30 ° C. for 60 seconds to swell. Subsequently, the film was stretched to 3.3 times while being dyed for 30 seconds in an iodine solution of 3.2 wt% (weight ratio: iodine / potassium iodide = 1/7) at 30 ° C. Next, the film was stretched up to 3.6 times while immersed in an aqueous solution of 3% by weight boric acid at 30 ° C. and 3% by weight potassium iodide for 1 minute. Thereafter, the total draw ratio was stretched to 6 times while being immersed in an aqueous solution of 4 wt% boric acid at 60 ° C. and 5 wt% potassium iodide for 30 seconds. Furthermore, it was immersed in a 3 wt% potassium iodide aqueous solution for 10 seconds to be impregnated with iodine ions. Thereafter, drying was performed in an oven at 60 ° C. for 4 minutes to obtain a polarizer having a thickness of 30 μm. The moisture content of the polarizer was 12% by weight.
(透明保護フィルム)
水系接着剤A及び水系接着剤Bを用いて偏光板を作成する場合には、厚さ80μmのトリアセチルセルロースフィルムを用いた。電子線硬化型接着剤を用いて偏光板を作成する場合には、厚さ40μmのラクトン化ポリメタクリレート系フィルムを用いた。
(Transparent protective film)
When the polarizing plate was prepared using the aqueous adhesive A and the aqueous adhesive B, a triacetyl cellulose film having a thickness of 80 μm was used. When a polarizing plate was prepared using an electron beam curable adhesive, a lactonized polymethacrylate film having a thickness of 40 μm was used.
(水系接着剤A)
アセトアセチル基を含有するポリビニルアルコール系樹脂(平均重合度:1200,ケン化度:98.5モル%,アセトアセチル基変性度:5モル%)100部に対し、メチロールメラミン20部を、30℃の温度条件下に、純水に溶解し、固形分濃度3.2重量%に調整した水溶液を調製した。これを水系接着剤Aとした。
(Water-based adhesive A)
Polyvinyl alcohol-based resin containing acetoacetyl group (average degree of polymerization: 1200, degree of saponification: 98.5 mol%, degree of acetoacetyl group modification: 5 mol%) is 20 parts by weight of methylolmelamine at 30 ° C. The aqueous solution which melt | dissolved in the pure water and adjusted solid content concentration to 3.2 weight% under the temperature conditions of this was prepared. This was designated as water-based adhesive A.
(水系接着剤B)
ポリビニルアルコール系樹脂(平均重合度:1800,ケン化度:98.5モル%,アセトアセチル基変性度:0モル%)100部に対し、メチロールメラミン25部を、30℃の温度条件下に、純水に溶解し、固形分濃度3.5重量%に調整した水溶液を調製した。これを水系接着剤Bとした。
(Water-based adhesive B)
For 100 parts of polyvinyl alcohol resin (average polymerization degree: 1800, saponification degree: 98.5 mol%, acetoacetyl group modification degree: 0 mol%), 25 parts of methylolmelamine are subjected to a temperature condition of 30 ° C. An aqueous solution dissolved in pure water and adjusted to a solid content concentration of 3.5% by weight was prepared. This was designated as water-based adhesive B.
(電子線硬化型接着剤)
2−ヒドロキシ−3−フェノキシプロピルアクリレート(ナガセケムテックス株式会社製,DA−141)を用いた。
(Electron beam curable adhesive)
2-hydroxy-3-phenoxypropyl acrylate (manufactured by Nagase ChemteX Corporation, DA-141) was used.
実施例1
(偏光子の親水化処理)
コロナ照射機(春日電機社製,CT‐0212)によって、上記偏光子の両面を、それぞれ、放電量40W/m2/minでコロナ処理し、偏光子表面を親水化した。得られた偏光子の表面の対水接着角は31°であった。
Example 1
(Polarizer hydrophilic treatment)
Using a corona irradiator (Kasuga Denki Co., Ltd., CT-0212), both surfaces of the polarizer were subjected to corona treatment at a discharge amount of 40 W / m 2 / min to make the polarizer surface hydrophilic. The surface-to-water adhesion angle of the obtained polarizer was 31 °.
(偏光板の作成)
上記透明保護フィルムの片側に、上記水系接着剤Aを、乾燥後の厚さが200nmとなるように塗工した。次いで、これを、上記偏光子の両面より、前記接着剤付き透明保護フィルムをロール機で貼り合わせた。その後、60℃で10分間乾燥して、偏光子の両側に透明保護フィルムを有する偏光板を得た。
(Creation of polarizing plate)
The aqueous adhesive A was applied on one side of the transparent protective film so that the thickness after drying was 200 nm. Subsequently, the transparent protective film with an adhesive was bonded to this from both sides of the polarizer by a roll machine. Then, it dried at 60 degreeC for 10 minute (s), and the polarizing plate which has a transparent protective film on both sides of a polarizer was obtained.
実施例2
実施例1において、偏光子の親水化処理にあたり、コロナ処理の放電量を80W/m2/minに変えたこと以外は、偏光子の親水化処理を行い、また当該得られた偏光子を用いたこと以外は、実施例1と同様にして偏光板を作成した。前記親水化処理により得られた偏光子の表面の対水接着角は28°であった。
Example 2
In Example 1, the polarizer was hydrophilized except that the discharge amount of the corona treatment was changed to 80 W / m 2 / min for the hydrophilic treatment of the polarizer, and the obtained polarizer was used. A polarizing plate was produced in the same manner as in Example 1 except that it was not. The adhesion angle to water of the surface of the polarizer obtained by the hydrophilic treatment was 28 °.
実施例3
実施例1において、偏光子の親水化処理にあたり、コロナ処理の放電量を240W/m2/minに変えたこと以外は、偏光子の親水化処理を行い、また当該得られた偏光子を用いたこと以外は、実施例1と同様にして偏光板を作成した。前記親水化処理により得られた偏光子の表面の対水接着角は30°であった。
Example 3
In Example 1, the hydrophilic treatment of the polarizer was performed except that the discharge amount of the corona treatment was changed to 240 W / m 2 / min in the hydrophilic treatment of the polarizer, and the obtained polarizer was used. A polarizing plate was produced in the same manner as in Example 1 except that it was not. The adhesion angle to water on the surface of the polarizer obtained by the hydrophilization treatment was 30 °.
実施例4
実施例1において、水系接着剤Aの代わりに、水系接着剤Bを用いたこと以外は、実施例1と同様にして偏光板を作成した。
Example 4
In Example 1, a polarizing plate was produced in the same manner as in Example 1 except that the aqueous adhesive B was used instead of the aqueous adhesive A.
実施例5
実施例2において、水系接着剤Aの代わりに、水系接着剤Bを用いたこと以外は、実施例2と同様にして偏光板を作成した。
Example 5
In Example 2, a polarizing plate was produced in the same manner as in Example 2 except that the aqueous adhesive B was used instead of the aqueous adhesive A.
実施例6
実施例3において、水系接着剤Aの代わりに、水系接着剤Bを用いたこと以外は、実施例3と同様にして偏光板を作成した。
Example 6
In Example 3, a polarizing plate was prepared in the same manner as in Example 3 except that the aqueous adhesive B was used instead of the aqueous adhesive A.
実施例7
(偏光子のラジカル活性化処理)
コロナ照射機によって、上記偏光子の両面を、それぞれ、放電量240W/m2/minでコロナ処理し、偏光子表面を活性化した。
Example 7
(Radical activation treatment of polarizer)
Both surfaces of the polarizer were corona-treated at a discharge amount of 240 W / m 2 / min with a corona irradiator to activate the polarizer surface.
(偏光板の作成)
上記透明保護フィルムの片側に、上記電子線硬化型接着剤を、輪転機(回転速度500rpm)を用いて乾燥後の厚さ2μmとなるように塗工した。次いで、これを、上記偏光子の両面より、前記接着剤付き透明保護フィルムをロール機で貼り合わせた。貼り合わせた透明保護フィルム側(両側)から、岩崎電気製電子線照射装置EC110を用いて、電子線を照射して、偏光子の両側に透明保護フィルムを有する偏光板を得た。ライン速度は5m/min、加速電圧は110kV、照射線量は50kGyとした。
(Creation of polarizing plate)
The electron beam curable adhesive was applied to one side of the transparent protective film so as to have a thickness of 2 μm after drying using a rotary press (rotation speed: 500 rpm). Subsequently, the transparent protective film with an adhesive was bonded to this from both sides of the polarizer by a roll machine. An electron beam was irradiated from the bonded transparent protective film side (both sides) using an electron beam irradiation apparatus EC110 manufactured by Iwasaki Electric Co., Ltd., to obtain a polarizing plate having a transparent protective film on both sides of the polarizer. The line speed was 5 m / min, the acceleration voltage was 110 kV, and the irradiation dose was 50 kGy.
比較例1
実施例1において、偏光子に親水化処理(コロナ処理)を施すことなく用いたこと以外は、実施例1と同様にして偏光板を作成した。前記偏光子の表面の対水接着角は55°であった。
Comparative Example 1
In Example 1, a polarizing plate was produced in the same manner as in Example 1 except that the polarizer was used without being subjected to hydrophilic treatment (corona treatment). The adhesion angle to water on the surface of the polarizer was 55 °.
比較例2
実施例1において、偏光子に親水化処理(コロナ処理)を施すことなく、一方、透明保護フィルムは、放電量80W/m2/minでコロナ処理したものを用いたこと以外は、実施例1と同様にして偏光板を作成した。
Comparative Example 2
In Example 1, the polarizer was not subjected to hydrophilic treatment (corona treatment), while the transparent protective film was used except that the one subjected to corona treatment at a discharge amount of 80 W / m 2 / min was used. A polarizing plate was prepared in the same manner as described above.
比較例3
実施例4において、偏光子に親水化処理(コロナ処理)を施すことなく用いたこと以外は、実施例4と同様にして偏光板を作成した。前記偏光子の表面の対水接着角は55°であった。
Comparative Example 3
In Example 4, a polarizing plate was prepared in the same manner as in Example 4 except that the polarizer was used without being subjected to a hydrophilic treatment (corona treatment). The adhesion angle to water on the surface of the polarizer was 55 °.
比較例4
実施例4において、偏光子に親水化処理(コロナ処理)を施すことなく、一方、透明保護フィルムは、放電量80W/m2/minでコロナ処理したものを用いたこと以外は、実施例4と同様にして偏光板を作成した。
Comparative Example 4
In Example 4, the polarizer was not subjected to hydrophilic treatment (corona treatment), while the transparent protective film was used except that the one subjected to corona treatment at a discharge amount of 80 W / m 2 / min was used. A polarizing plate was prepared in the same manner as described above.
比較例5
実施例7において、偏光子にコロナ処理を施すことなく用いたこと以外は、実施例7と同様にして偏光板を作成した。
Comparative Example 5
In Example 7, a polarizing plate was produced in the same manner as in Example 7 except that the polarizer was used without being subjected to corona treatment.
[評価]
実施例および比較例で得られた、偏光板について下記評価を行った。結果を表1に示す。
[Evaluation]
The following evaluation was performed about the polarizing plate obtained by the Example and the comparative example. The results are shown in Table 1.
<接着力>
得られた偏光板を幅15mm、長さ100mmに切断して、サンプルとした。変角度ピール測定機により、サンプルの一端を剥離角度120°、剥離速度37.5mm/minで剥離して接着強度(N/25mm)を測定した。
<Adhesive strength>
The obtained polarizing plate was cut into a width of 15 mm and a length of 100 mm to obtain a sample. One end of the sample was peeled off at a peeling angle of 120 ° and a peeling speed of 37.5 mm / min using a variable angle peel measuring machine, and the adhesive strength (N / 25 mm) was measured.
表1中、フィルム破断は、接着力が強く、フィルム側が破断することを示す。 In Table 1, the film break indicates that the adhesive force is strong and the film side is broken.
Claims (7)
偏光子の接着剤層が設けられる面に活性化処理を施す工程、
偏光子の前記接着剤層を形成する面および/または透明保護フィルムの前記接着剤層を形成する面に、接着剤を塗工する工程、
偏光子と透明保護フィルムとを、前記接着剤を介して貼り合わせる工程、を有し、
前記活性化処理によって、偏光子の表面は活性処理が施されており、かつ、
前記接着剤層はラジカル硬化型接着剤により形成し、
前記貼り合わせ工程の後に、硬化工程により接着剤層を形成することを特徴とする偏光板の製造方法。 A method for producing a polarizing plate, wherein a transparent protective film is provided on at least one surface of a polarizer via an adhesive layer,
A step of activating the surface on which the adhesive layer of the polarizer is provided,
Applying an adhesive to the surface of the polarizer forming the adhesive layer and / or the surface of the transparent protective film forming the adhesive layer;
A polarizer and a transparent protective film, have a step, of bonding via the adhesive,
By the activation treatment, the surface of the polarizer has been activated, and
The adhesive layer is formed of a radical curable adhesive,
After the said bonding process, an adhesive bond layer is formed by a hardening process , The manufacturing method of the polarizing plate characterized by the above-mentioned .