JP4344174B2 - Engine oil composition - Google Patents
Engine oil composition Download PDFInfo
- Publication number
- JP4344174B2 JP4344174B2 JP2003166650A JP2003166650A JP4344174B2 JP 4344174 B2 JP4344174 B2 JP 4344174B2 JP 2003166650 A JP2003166650 A JP 2003166650A JP 2003166650 A JP2003166650 A JP 2003166650A JP 4344174 B2 JP4344174 B2 JP 4344174B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- oil
- carbon atoms
- acid
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】
【発明の属する技術分野】
本発明は、ガソリンエンジン、ディーゼルエンジン等に好適に使用できるエンジン油組成物に関する。
【0002】
【従来の技術】
エンジン内の燃焼によって生じる排気ガスには、窒素酸化物(NOx)、硫黄酸化物(SOx)、微粒子状浮遊物質(PM)等が含まれている。これらの有害物質は、環境汚染、自然破壊、人体への悪影響等を引き起こすことが知られており、できるかぎり大気中に放出しない対策が必要となっている。このため、燃料油中の硫黄含量や窒素含量の低減、エンジンの改良、燃焼方法の改良、排ガス浄化触媒の改良、パティキュレートフィルターの検討等が行なわれている。
一方、エンジン油では、カム、弁、ロッカーアーム等の動弁系の摩耗の低減、摩擦によるエネルギー損失の低減、エンジン油の熱劣化・酸化劣化の抑制、燃料の不完全燃焼物やエンジン油劣化物のエンジン内への堆積抑制等の多くの機能が求められる。このため、エンジン油は、基油である鉱油や合成油に、耐摩耗剤、摩擦低減剤、酸化防止剤、無灰型分散剤、金属系清浄剤、粘度指数向上剤等の多くの添加剤を配合した組成物の状態で用いられている。このような添加剤の中でも、亜鉛ジチオホスフェートは、耐摩耗剤として非常に優れており酸化防止性も優れていることから、実際に使用されているほとんどすべてのエンジン油に、リン含量として800〜1500質量ppm程度配合されてきた。
エンジン油の一部は、燃焼室に入って燃焼し、排ガスと共に排出されるが、エンジン油中のリン成分は、排ガス浄化触媒の活性を低下させることが知られている。また、エンジン油中の硫黄成分は、NOx還元型の排ガス浄化触媒の活性を低下させ、また、硫酸塩として付着して、パティキュレートフィルターの目詰りの原因となる。即ち、排ガス中の有害物質の低減には、エンジン油中のリン含量及び硫黄含量を低減することが好ましい。
エンジン油中のリン成分は、主に亜鉛ジチオホスフェートに由来することから、リン含量を低減するには、亜鉛ジチオホスフェートの含量を低減させる必要がある。しかしながら、亜鉛ジチオホスフェートを含有しない無リンのエンジンでは、耐摩耗剤として多量の硫黄含有化合物を配合する必要があり(特許文献1〜5等を参照)、エンジン油中の硫黄含量が増加してしまうという問題があり、少量の亜鉛ジチオホスフェートを配合せざるを得ないのが現状である。リン含量及び硫黄含量が低減されたエンジン油としては、亜鉛ジチオホスフェート、コハク酸イミド系無灰型分散剤、及び金属系清浄剤を配合することによりリン含量を300〜600質量ppm程度にまで低減したエンジン油(特許文献6、7を参照)も知られているが、耐摩耗性及び酸化安定性が不充分であった。
【0003】
一方、アルカノールアミンの脂肪酸アミド(例えば、特許文献8を参照)、N−アルキルジエタノールアミン(例えば、特許文献9を参照)、N,N−ジアルキルモノエタノールアミン(例えば、特許文献10を参照)、N−(2−ヒドロキシアルキル)ジエタノールアミン(例えば、特許文献11を参照)等のアルカノールアミン化合物又はアルカノールアミド化合物は、エンジン油の添加剤として知られているが、エンジン油中のリン含量及び硫黄含量を低減できることについては明らかではなかった。
【0004】
【特許文献1】
特開昭62−253691号公報
【特許文献2】
特開平6−41568号公報
【特許文献3】
特開昭52−39704号公報
【特許文献4】
特開平7−118680号公報
【特許文献5】
特開2000−63862号公報
【特許文献6】
特開平9−111275号公報
【特許文献7】
特開2002−53888号公報
【特許文献8】
特開昭55−66996号公報
【特許文献9】
特開平7−508049号公報
【特許文献10】
特開2000−34489号公報
【特許文献11】
特開平9−100485号公報
【0005】
【発明が解決しようとする課題】
従って、本発明が解決しようとする課題は、低リン含量及び低硫黄含量であっても、従来のエンジン油と同等又はそれ以上の耐摩耗性及び酸化安定性を有するエンジン油組成物を提供することにある。
【0006】
【課題を解決するための手段】
そこで本発明者らは、低リン含量及び低硫黄含量のエンジン油について鋭意検討し、特定の構造のアルカノールアミン化合物又はアルカノールアミド化合物を配合することにより、亜鉛ジチオホスフェートの配合量が大きく低減できることを見出し、本発明に至った。即ち、本発明は潤滑性基油に、(A)成分として、下記の一般式(1)
【0007】
【化3】
【0008】
(式中、R1及びR2は炭化水素基を表わし、aは0〜1/3の数を表わす。)
で表わされる亜鉛ジチオホスフェートを、リン含量として100〜500質量ppm;
(B)成分として、下記の一般式(2)
【0009】
【化4】
【0010】
(式中、R3は炭素数8〜22のアルキル基、アルケニル基、2−ヒドロキシアルキル基又はアシル基を表わし、R4は炭素数2〜4のアルキレン基を表わし、Xは、R 3 がアルキル基又はアルケニル基の場合には炭素数2〜18の2−ヒドロキシアルキル基又は−CH 2 CH 2 CH 2 N(R 4 OH) 2 を表わし、R 3 が2−ヒドロキシエチル基の場合には、水素原子、炭素数1〜4のアルキル基又は炭素数2〜18の2−ヒドロキシアルキル基を表わし、R 3 がアシル基の場合には、水素原子又は炭素数2〜4の2−ヒドロキシアルキル基を表わす。)
で表わされる窒素含有化合物を0.01〜10質量%;
を含有させてなり、且つリン含量が500質量ppm以下、硫黄含量が3000質量ppm以下であるエンジン油組成物である。
【0011】
【発明の実施の形態】
まず、本発明の(A)成分について説明する。本発明の(A)成分は、一般式(1)で表わされる亜鉛ジチオホスフェートである。
一般式(1)において、R1及びR2は炭化水素基を表わす。炭化水素基としては、例えば、アルキル基、アルケニル基、アリール基、シクロアルキル基、シクロアルケニル基等が挙げられる。
【0012】
アルキル基としては、例えば、メチル、エチル、プロピル、イソプロピル、ブチル、イソブチル、2級ブチル、3級ブチル、ペンチル、イソペンチル、2級ペンチル、ネオペンチル、3級ペンチル、ヘキシル、2級ヘキシル、ヘプチル、2級ヘプチル、オクチル、2−エチルヘキシル、2級オクチル、ノニル、2級ノニル、デシル、2級デシル、ウンデシル、2級ウンデシル、ドデシル、2級ドデシル、トリデシル、イソトリデシル、2級トリデシル、テトラデシル、2級テトラデシル、ヘキサデシル、2級ヘキサデシル、ステアリル、エイコシル、ドコシル、テトラコシル、トリアコンチル、2−ブチルオクチル、2−ブチルデシル、2−ヘキシルオクチル、2−ヘキシルデシル、2−オクチルデシル、2−ヘキシルドデシル、2−オクチルドデシル、2−デシルテトラデシル、2−ドデシルヘキサデシル、2−ヘキサデシルオクタデシル、2−テトラデシルオクタデシル、モノメチル分枝−イソステアリル基等が挙げられる。
【0013】
アルケニル基としては、例えば、ビニル、アリル、プロペニル、イソプロペニル、ブテニル、イソブテニル、ペンテニル、イソペンテニル、ヘキセニル、ヘプテニル、オクテニル、ノネニル、デセニル、ウンデセニル、ドデセニル、テトラデセニル、オレイル基等が挙げられる。
【0014】
アリール基としては、例えば、フェニル、トルイル、キシリル、クメニル、メシチル、ベンジル、フェネチル、スチリル、シンナミル、ベンズヒドリル、トリチル、エチルフェニル、プロピルフェニル、ブチルフェニル、ペンチルフェニル、ヘキシルフェニル、ヘプチルフェニル、オクチルフェニル、ノニルフェニル、デシルフェニル、ウンデシルフェニル、ドデシルフェニル、スチレン化フェニル、p−クミルフェニル、フェニルフェニル、ベンジルフェニル、α−ナフチル、β−ナフチル基等が挙げられる。
【0015】
シクロアルキル基及びシクロアルケニル基としては、例えば、シクロペンチル、シクロヘキシル、シクロヘプチル、メチルシクロペンチル、メチルシクロヘキシル、メチルシクロヘプチル、シクロペンテニル、シクロヘキセニル、シクロヘプテニル、メチルシクロペンテニル、メチルシクロヘキセニル、メチルシクロヘプテニル基等が挙げられる。
【0016】
これらの炭化水素基の中で、R1及びR2としては、アルキル基が好ましく、2級アルキル基が更に好ましい。炭素数は3〜14であることが好ましく、3〜10であることが更に好ましく、3〜8であることが最も好ましい。R1及びR2は、同一の炭化水素基でも異なる炭化水素基でもよい。
また、一般式(1)において、aは0〜1/3の数であり、a=0の場合、中性亜鉛ジチオホスフェートと呼ばれ、a=1/3の場合、塩基性亜鉛ジチオホスフェートと呼ばれる。
【0017】
本発明のエンジン油組成物全量に対する、(A)成分である一般式(1)で表わされる亜鉛ジチオホスフェートの含量は、リン含量として100〜500質量ppmであり、好ましくは150〜480質量ppm、更に好ましくは200〜450質量ppm、最も好ましくは250〜400質量ppmである。(A)成分の含量がリン含量として100質量ppm未満では、耐摩耗性及び酸化安定性が不充分となり、500質量ppmを超えると、排ガス浄化触媒の活性低下が起こり易くなる。
【0018】
次に、本発明の(B)成分について説明する。本発明の(B)成分は、一般式(2)で表わされる窒素含有化合物である。
一般式(2)において、R3は炭素数8〜22のアルキル基、アルケニル基、2−ヒドロキシアルキル基又はアシル基を表わす。炭素数8〜22のアルキル基又はアルケニル基としては、例えば、一般式(1)のR1又はR2で挙げたアルキル基又はアルケニル基のうち、炭素数8〜22であるものが挙げられる。
【0019】
炭素数8〜22の2−ヒドロキシアルキル基としては、2−ヒドロキシオクチル、2−ヒドロキシノニル、2−ヒドロキシデシル、2−ヒドロキシウンデシル、2−ヒドロキシドデシル、2−ヒドロキシトリデシル、2−ヒドロキシテトラデシル、2−ヒドロキシヘキサデシル、2−ヒドロキシオクタデシル、2−ヒドロキシエイコシル、2−ヒドロキシドコシル基等が挙げられる。
【0020】
炭素数8〜22のアシル基としては、例えば、オクタノイル、ノナノイル、デカノイル、ウンデカノイル、ドデカノイル、トリデカノイル、テトラデカノイル、ペンタデカノイル、ヘキサデカノイル、ヘプタデカノイル、オクタデカノイル、ノナデカノイル、エイコサノイル、ヘンエイコサノイル、ドコサノイル、ウンデセノイル、オクタデセノイル、オクタデカジエノイル、12−ヒドロキシオクタデカノイル、12−ヒドロキシオクタデセノイル基等が挙げられる。
これらの中でも、R3は炭素数10〜20のものが好ましく、炭素数12〜18のものが更に好ましく、炭素数12〜18の2−ヒドロキシアルキル基が最も好ましい。
【0021】
R4は炭素数2〜4のアルキレン基を表わす。炭素数2〜4のアルキレン基としては、例えば、エチレン、プロピレン、ブチレン等が挙げられ、中でも、エチレンが好ましい。
【0022】
Xは水素原子、炭素数1〜22のアルキル基、炭素数2〜22の2−ヒドロキシアルキル基又は−CH2CH2CH2N(R4OH)2で表わされる基を表わす。炭素数1〜22のアルキル基としては、例えば、一般式(1)のR1又はR2で挙げたアルキル基のうち、炭素数1〜22であるものが挙げられる。また、炭素数2〜22の2−ヒドロキシアルキル基としては、R3で挙げた、炭素数8〜22の2−ヒドロキシアルキル基に加え、2−ヒドロキシエチル、2−ヒドロキシプロピル、2−ヒドロキシブチル、2−ヒドロキシペンチル、2−ヒドロキシヘキシル、2−ヒドロキシヘプチル基等が挙げられる。R3がアルキル基又はアルケニル基の場合には、Xは炭素数1〜4のアルキル基、炭素数2〜18の2−ヒドロキシアルキル基及び−CH2CH2CH2N(R4OH)2で表わされる基が好ましく、炭素数2〜18の2−ヒドロキシアルキル基が更に好ましく、炭素数2〜4の2−ヒドロキシアルキル基が最も好ましい。R3がアシル基の場合には、Xは水素原子及び炭素数2〜4の2−ヒドロキシアルキル基が好ましく、水素又は2−ヒドロキシエチル基が最も好ましい。また、R3が2−ヒドロキシエチル基の場合には、Xは水素原子、炭素数1〜4のアルキル基及び炭素数2〜18の2−ヒドロキシアルキル基が好ましく、水素及び炭素数2〜18の2−ヒドロキシアルキル基が更に好ましく、炭素数2〜4の2−ヒドロキシアルキル基が最も好ましい。
【0023】
一般式(2)において、R3が炭素数8〜22のアルキル基若しくはアルケニル基である窒素含有化合物は、例えば、下記の一般式(3)〜(5)で表されるアミン化合物に、炭素数2〜4のアルキレンオキシドを、公知の方法により反応させることにより得ることができる。
R5−NH2 (3)
R5−NH−R6 (4)
R5−NHCH2CH2CH2NH2 (5)
(式中、R5は炭素数8〜22のアルキル基若しくはアルケニル基を表わし、R6は炭素数1〜22のアルキル基又は炭素数2〜22の2−ヒドロキシアルキル基を表わす。)
炭素数2〜4のアルキレンオキシドとしては、例えば、エチレンオキシド、プロピレンオキシド、ブチレンオキシド等が挙げられる。
なお、前記一般式(4)で表されるアミン化合物のうち、R6が炭素数2〜22の2−ヒドロキシアルキル基であるものは、前記一般式(3)で表されるアミン化合物に対して炭素数2〜22のアルキレンオキシドを反応させることにより得ることができる。
【0024】
一般式(2)において、R3が炭素数8〜22のアシル基である窒素含有化合物は、例えば、炭素数8〜22の脂肪酸又はその低級アルコールエステルに、アンモニア、モノアルキルアミン、プロピレンジアミン等を反応させて得られるアミド化合物に、炭素数2〜4のアルキレンオキシドを反応させる方法;炭素数8〜22の脂肪酸又はその低級アルコールエステルに、モノエタノールアミン、モノプロパノールアミン、ジエタノールアミン、ジプロパノールアミン等の低分子量アルカノールアミンを反応させる方法等により得られる。
一般式(2)において、R3炭素数が8〜22の2−ヒドロキシアルキル基である窒素含有化合物は、例えば、炭素数8〜22のα−オレフィンオキシドに、低分子量アルカノールアミンを反応させる方法等により得られる。
【0025】
本発明のエンジン油組成物全量に対する(B)成分の含量は、0.01〜10質量%であり、好ましくは0.05〜5質量%、更に好ましくは0.1〜3質量%、最も好ましくは0.1〜1質量%である。(B)成分の含量が0.01質量%未満では、本発明のエンジン油の耐摩耗性及び酸化安定性が不充分となり、10質量%を超えると、含量に見合う効果は得られず、更に温度−粘度特性(粘度指数)が低下する場合があるからである。
【0026】
本発明のエンジン油組成物のリン含量は、500質量ppm以下である。リン含量が500質量ppmを超えると、排ガス浄化触媒の活性低下が起こり易くなるからである。リン含量は、460質量ppm以下が好ましく、430質量ppm以下が更に好ましく、400質量ppm以下が最も好ましい。
【0027】
また、本発明のエンジン油組成物の硫黄含量は、5000質量ppm以下である。硫黄含量が5000質量ppmを超えると、NOx還元型排ガス浄化触媒の活性低下や、パティキュレートフィルターの目詰りが起こり易くなるからである。硫黄含量は、5000質量ppm以下が好ましく、3000質量ppm以下が更に好ましく、2000質量ppm以下が最も好ましい。
【0028】
本発明のエンジン油組成物は優れた耐摩耗性及び酸化安定性を有するが、耐摩耗性を長期間持続させるため、更に(C)成分として、フェノール系酸化防止剤、又はアミン系酸化防止剤を含有することが好ましい。
【0029】
フェノール系酸化防止剤としては、例えば、2,6―ジ―tertiary―ブチルフェノール(以下、tertiary―ブチルをt−ブチルと略記する。)、2,6―ジ―t―ブチル―4―メチルフェノール、2,6―ジ―t―ブチル―4―エチルフェノール、6―t−ブチル−2,4―ジメチルフェノール、4,4’―メチレンビス(2,6―ジ―t−ブチルフェノール)、3,3’,5,5’−テトラ−t−ブチル−4,4’−ジヒドロキシビフェニル、3,3’−ジ−t−ブチル−4,4’−ジヒドロキシ−5,5’−ジメチルビフェニル、2,2’―メチレンビス(6―t−ブチル−4−メチルフェノール)、2,2’―メチレンビス(6―t−ブチル−4−エチルフェノール)、4,4’―ブチリデンビス(6―t―ブチル−3−メチルフェノール)、4,4’―イソプロピリデンビス(2,6―ジ―t―ブチルフェノール)、2,2’―メチレンビス(6―シクロヘキシル−4−メチルフェノール)、2,2’―メチレンビス(4―メチル―6―ノニルフェノール)、2,2’―イソブチリデンビス(4,6―ジメチルフェノール)、2,6―ビス(3’―t―ブチル―2’−ヒドロキシ−5’―メチルベンジル)―4―メチルフェノール、3―t−ブチル−4―ヒドロキシアニソール、2―t―ブチル―4―ヒドロキシアニソール、3−(3,5−ジ―t―ブチル−4−ヒドロキシフェニル)プロピオン酸ステアリル、3−(3,5−ジ―t−ブチル−4−ヒドロキシフェニル)プロピオン酸オレイル、3−(3,5−ジ―t−ブチル−4−ヒドロキシフェニル)プロピオン酸ドデシル、3−(3,5−ジ―t−ブチル−4−ヒドロキシフェニル)プロピオン酸デシル、3−(3,5−ジ―t−ブチル−4−ヒドロキシフェニル)プロピオン酸オクチル、テトラキス{3−(3,5−ジ―t−ブチル−4−ヒドロキシフェニル)プロピオニルオキシメチル}メタン、3−(3,5−ジ―t−ブチル−4−ヒドロキシフェニル)プロピオン酸グリセリンモノエステル、3−(3,5−ジ―t−ブチル−4−ヒドロキシフェニル)プロピオン酸とグリセリンモノオレイルエーテルとのエステル、3−(3,5−ジ―t−ブチル−4−ヒドロキシフェニル)プロピオン酸ブチレングリコールエステル、2,6―ジ―t―ブチル―4―(N,N―ジメチルアミノメチルフェノール)、トリス{(3,5―ジ―t−ブチル―4―ヒドロキシフェニル)プロピオニルオキシエチル}イソシアヌレート、トリス(3,5―ジ―t―ブチル―4―ヒドロキシフェニル)イソシアヌレート、1,3,5―トリス(3,5―ジ―t−ブチル―4―ヒドロキシベンジル)イソシアヌレート、1,3,5―トリス(4―t−ブチル―2,6―ジメチル−3−ヒドロキシベンジル)イソシアヌレート、N,N’―ジ(3,5―ジ―t−ブチル−4―ヒドロキシジヒドロシンナミル)ヘキサメチレン−1,6−ジアミン、3,9−ジ〔1,1−ジメチル−2−{β−(3−t−ブチル−4−ヒドロキシ−5−メチルフェニル)プロピオニルオキシ}エチル〕−2,4,8,10−テトラオキサスピロ[5,5]ウンデカン、1,1,3−トリ(5−t―ブチル−4−ヒドロキシ−2−メチルフェニル)ブタン、1,3,5−トリメチル−2,4,6−トリス(3,5−ジ−t−ブチル−4−ヒドロキシベンジル)ベンゼン、3−(3’−t−ブチル−4’−ヒドロキシフェニル)酪酸グリコールジエステル等の、硫黄原子及びリン原子を含有しないフェノール系酸化防止剤;3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオン酸チオジグリコールエステル、4,4’−チオビス(6−t−ブチル−3−メチルフェノール)、4,4’−チオビス(6−t−ブチル−2−メチルフェノール)、2,2’−チオビス(6−t−ブチル−4−メチルフェノール)、ビス(3,5−ジ−t−ブチル−4−ヒドロキシベンジル)スルフィド、ビス{4−(3−n−アルキルチオプロピオニルオキシ)−5−t−ブチル−2−メチルフェニル}スルフィド、ジ(4−t−ブチル−2,6−ジメチル−3−ヒドロキシベンジル)スルフィド、6−(3,5−ジ−t−ブチル−4−ヒドロキシアニリノ)−2,4−ビス(オクチルチオ)−1,3,5−トリアジン、2,2−チオ−{ジエチル−ビス−3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)}プロピオネート、ビス(5−t−ブチル−4−ヒドロキシ−3−メチルベンジル)スルフィド等の、硫黄原子を含有しリン原子を含有しないフェノール系酸化防止剤;3,5−ジ−t−ブチル−4−ヒドロキシベンジルリン酸ジエステル等の、リン原子を含有し硫黄原子を含有しないフェノール系酸化防止剤等が挙げられる。
【0030】
アミン系酸化防止剤としては、例えば、ナフト−1−イルアミン、N−(ナフト−1−イル)−N−フェニルアミン、N−(ナフト−1−イル)−N−(p―オクチルフェニル)アミン、N−(ナフト−1−イル)−N−(p―ノニルフェニル)アミン、N−(p―ドデシルフェニル)−N−(ナフト−1−イル)アミン、N−(ナフト−2−イル)−N−フェニルアミン等のナフチルアミン系酸化防止剤;N,N’―ジイソプロピル―p―フェニレンジアミン、N,N’―ジイソブチル―p―フェニレンジアミン、N,N’―ジフェニル―p―フェニレンジアミン、N,N’―ジ―β―ナフチル―p―フェニレンジアミン、N―イソプロピル―N’―フェニル―p―フェニレンジアミン、N―シクロヘキシル―N’―フェニル―p―フェニレンジアミン、N―(1,3―ジメチルブチル)―N’―フェニル―p―フェニレンジアミン、ジオクチル―p―フェニレンジアミン、フェニルヘキシル―p―フェニレンジアミン、フェニルオクチル―p―フェニレンジアミン等のフェニレンジアミン系酸化防止剤;ジピリジルアミン、ジフェニルアミン、ジ(p−n―ブチルフェニル)アミン、ジ(p−t−ブチルフェニル)アミン、ジ(p−t−ペンチルフェニル)アミン、ジ(p−オクチルフェニル)アミン、ジ(p−ノニルフェニル)アミン、ジ(p−デシルフェニル)アミン、ジ(p−ドデシルフェニル)アミン、ジ(p−スチリルフェニル)アミン、ジ(p−メトキシフェニル)アミン、4,4’―ビス(4―α,α―ジメチルベンジル)ジフェニルアミン、N−(p―イソプロポキシフェニル)−N−フェニルアミン、ジピリジルアミン等のジフェニルアミン系酸化防止剤;フェノチアジン、N−メチルフェノチアジン、N−エチルフェノチアジン、3,7−ジオクチルフェノチアジン、フェノチアジンカルボン酸エステル、フェノセレナジン等のフェノチアジン系酸化防止剤が挙げられる。
【0031】
(C)成分としては、アミン系酸化防止剤が好ましく、フェニレンジアミン系酸化防止剤及びジフェニルアミン系酸化防止剤が更に好ましく、ジフェニルアミン系酸化防止剤が最も好ましい。(C)成分の配合量は、エンジン油全量に対して、好ましくは0.05〜5質量%、より好ましくは0.08〜3質量%、最も好ましくは0.1〜2質量%である。(C)成分の配合量が0.05質量%未満では、耐摩耗性が長期間維持出来ない場合があり、5質量%を超えると、配合量に見合う効果は得られず、更にオイルシールを劣化させてオイルの漏れを引き起こす場合がある。
【0032】
(A)成分の亜鉛ジチオホスフェートは、リン原子及び硫黄原子を含有する化合物であるが、(A)成分以外にリン成分又は硫黄成分がエンジン油に混入する場合としては、例えば、潤滑性基油として硫黄を含有する鉱油を使用した場合、リン原子又は硫黄原子を含有する潤滑油添加剤を配合した場合等が挙げられる。鉱油は、天然の原油を蒸留分離した後、精製を行って製造される。原油は、主成分の炭化水素の他に、硫黄含有化合物、窒素含有化合物、酸素含有化合物、金属(バナジウム、ニッケル等)含有化合物等の不純物を含有している。これらの不純物は精製により除去されるが、原油の産地や精製方法によっては、不純物が多く残存する。例えば、硫黄含量が10質量ppm以下の鉱油もあるが、1000質量ppmを超える鉱油もある。本発明のエンジン油組成物の潤滑性基油の硫黄含量は、できるだけ低いことが好ましいが、ブローバイガス(燃焼室からクランクケース内に漏洩する燃焼ガス)のNOxによる劣化の起こり難さを考慮すると、硫黄含量が50質量ppm以下であることが好ましく、30質量ppm以下であることが更に好ましく、10質量ppm以下であることが最も好ましい。また、潤滑性基油の動粘度は特に限定されないが、好ましくは100℃で1〜50mm2/s、40℃で10〜1,000mm2/s程度、粘度指数(VI)は好ましくは100以上、より好ましくは120以上、最も好ましくは135以上である。
【0033】
また、リン原子又は硫黄原子を含有する潤滑油添加剤としては、先に挙げた、硫黄原子を含有しリン原子を含有しないフェノール系酸化防止剤、リン原子を含有し硫黄原子を含有しないフェノール系酸化防止剤及びフェノチアジン系酸化防止剤の他に、(D1)リン系耐摩耗剤又はリン系酸化防止剤、(D2)スルホネート系金属清浄剤、(D3)硫黄系極圧剤、(D4)硫黄系酸化防止剤、(D5)チオリン酸系極圧剤、(D6)リン及び/又は硫黄を含有する金属系耐摩耗剤等が挙げられる。
【0034】
(D1)リン系耐摩耗剤又はリン系酸化防止剤としては、例えば、有機ホスフィン、有機ホスフィンオキシド、有機ホスフィナイト、有機ホスホナイト、有機ホスフィネート、有機ホスファイト、有機ホスホネート、有機ホスフェート、有機ホスホロアミデート等が挙げられる。
【0035】
(D2)スルホネート系金属清浄剤としては、例えば、(モノ又はジ)アルキルベンゼンスルホン酸金属塩、(モノ又はジ)アルキルナフタレンスルホン酸金属塩、石油スルホン酸金属塩等が挙げられる。これら金属塩の金属として、ナトリウム、カリウム等のアルカリ金属;マグネシウム、カルシウム、バリウム等のアルカリ土類金属等が挙げられる。
【0036】
(D3)硫黄系極圧剤としては、例えば、硫化油脂、硫化鉱油、有機モノ又はポリスルフィド、ポリオレフィンの硫化物、1,3,4―チアジアゾール誘導体、チウラムジスルフィド、ジチオカルバミン酸エステル等が挙げられる。
【0037】
(D4)硫黄系酸化防止剤としては、例えば、チオジプロピオン酸エステル、チオビス(フェノール)化合物、アルキルチオプロピオン酸の多価アルコールエステル、2−メルカプトベンズイミダゾール、ジラウリルスルフィド、アミルチオグリコレート等が挙げられる。
【0038】
(D5)チオリン酸系極圧剤としては、例えば、有機トリチオホスファイト、有機チオホスフェート等が挙げられる。
【0039】
(D6)リン及び/又は硫黄を含有する金属系耐摩耗剤としては、例えば、ジチオリン酸金属塩、ジチオカルバミン酸金属塩、キサントゲン酸金属塩、メルカプトベンゾチアゾール金属塩、メルカプトベンズイミダゾール金属塩、チオフェノール金属塩等が挙げられる。金属としては、リチウム、ナトリウム、カリウム、マグネシウム、カルシウム、バリウム、チタン、亜鉛、鉛、スズ、鉄、カドミウム、コバルト、ニッケル、マンガン、ストロンチウム、チタン、バナジウム、銅、アンチモン、ビスマス、モリブデン、タングステン等が挙げられる。
【0040】
本発明のエンジン油には、リン又は硫黄を含有する潤滑油添加剤は、配合しないことが好ましいが、本発明のリン含量及び硫黄含量の上限を超えない添加量、即ち、リン含量が500質量ppm以下及び硫黄含量が5000ppm以下となる添加量であれば、必要に応じて配合してもよい。
【0041】
この他、本発明のエンジン油組成物には、通常、エンジン油に使用されるリン原子及び硫黄原子を含有しない潤滑剤を配合することができる。このような潤滑剤としては、(E1)金属清浄剤(スルホネート系を除く)、(E2)無灰型分散剤、(E3)リン原子及び硫黄原子を含有しない金属系耐摩耗剤、(E4)金属、リン原子及び硫黄原子を含有しない油性向上剤、(E5)防錆剤、(E6)粘度指数向上剤、(E7)金属不活性化剤、(E8)消泡剤、(E9)固体潤滑剤等が挙げられる。
【0042】
(E1)金属清浄剤(スルホネート系を除く)としては、例えば、金属フェノレート、金属サリシレート等が挙げられる。金属フェノレートとしては、例えば、(モノ又はジ)アルキルフェノール金属塩、ビス{(モノ又はジ)アルキルヒドロキシフェニル}メチレン金属塩等が挙げられる。金属サリシレートとしては、例えば、(モノ又はジ)アルキルサリチル酸金属塩、ビス{(モノ又はジ)アルキルサリチル酸}スルフィド金属塩、ビス{(モノ又はジ)アルキルサリチル酸}メチレン金属塩等が挙げられる。金属としては、アルカリ土類金属が好ましく、カルシウム、マグネシウムがより好ましい。
又、上記の化合物は一般に中性塩であるが、金属清浄剤としては、これらの中性塩に、二酸化炭素を吹き込みながら金属酸化物又は金属水酸化物等で塩基化処理して、塩基性又は過塩基性としたものが好ましく使用される。これは、金属清浄剤を塩基性又は過塩基性にすることにより、燃料の不完全燃焼物やエンジン油劣化物のエンジン内への堆積抑制の機能の他に、ブローバイガスやエンジン油劣化物に由来する酸性物質を中和し、酸性物質による腐食摩耗を防止する機能を付与するためである。
過塩基性化合物は、通常炭酸塩の形で含有されている。これらの塩基性又は過塩基性の金属清浄剤の全塩基価(TBN)は、一般に200〜500mgKOH/g程度である。(E1)成分の好ましい配合量は、エンジン油組成物全体に対して0.5〜15質量%程度である。
【0043】
(E2)無灰型分散剤としては、例えば、コハク酸イミド、ベンジルアミン、コハク酸エステル又はこれらのホウ素変性物等が挙げられる。コハク酸イミドとしては、例えば、分子量300〜4,000程度のポリブテニル基等のポリアルケニル基を有するコハク酸と、エチレンジアミン、ジエチレントリアミン、トリエチレンテトラミン、テトラエチレンペンタミン、ペンタエチレンヘキサミン等のポリエチレンポリアミンとのモノイミド又はジイミド、若しくはこれらのホウ素変性物;ポリアルケニル基を有するフェノールとホルムアルデヒドと上記ポリエチレンポリアミンとのマンニッヒ反応生成物等が挙げられる。
上記の無灰型分散剤中の窒素含量は、通常0.5〜2.0質量%程度である。これらの無灰分散剤のうちで好ましいものは、コハク酸イミド又はそのホウ素変性物である。(E2)成分の好ましい配合量は、潤滑性基材に対して0.5〜20質量%程度である。
【0044】
(E3)リン原子及び硫黄原子を含有しない金属系耐摩耗剤としては、例えば、チタン、亜鉛、鉛、スズ、鉄、カドミウム、コバルト、ニッケル、マンガン、ストロンチウム、チタン、バナジウム、銅、アンチモン、ビスマス、モリブデン、タングステン等の脂肪酸塩、アルキル若しくはアルケニルコハク酸塩、フェノール塩、サリチル酸塩、アルコラート、グリコール錯体、β−ジケトン錯体、アミン化合物との反応生成物、カルボン酸アルカノールアミド錯体、グリセリンモノカルボン酸エステル錯体等が挙げられる。これらの中でも、特に、リン原子及び硫黄原子を含有しないモリブデン系耐摩耗剤が好ましく、モリブデンとアミン化合物との反応生成物、モリブデンのカルボン酸ジエタノールアミド錯体及びモリブデンのグリセリンモノカルボン酸エステル錯体が更に好ましい。なお、モリブデンとアミン化合物との反応生成物の製造方法は、特開昭61−285293号公報、モリブデンのカルボン酸ジエタノールアミド錯体及びモリブデンのグリセリンモノカルボン酸エステル錯体の製造方法は、特開昭62−108891号公報に記載されている。(E3)成分の好ましい配合量は、潤滑性基材に対して金属原子を基準にして200〜1000質量ppm程度である。(E3)成分の配合量が200質量ppm未満では、充分な添加効果が得られない場合があり、1000質量ppmを超えると、配合量に見合う効果は得られず、更に排ガス浄化触媒の活性を低下させる場合がある。
【0045】
(E4)金属、リン原子及び硫黄原子を含有しない油性向上剤としては、例えば、ヘキサン酸、オクタン酸、ペラルゴン酸、デカン酸、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、オレイン酸、ベヘニン酸、リノール酸、リノレン酸等の脂肪酸;アマニ油、エノ油、オイチシカ油、オリーブ油、カカオ油(油の方が宜しいでしょうか)、カポック油、白カラシ油、ゴマ油、コメヌカ油、サフラワー油、シアナット油、シナキリ油、大豆油、茶実油、ツバキ油、コーン油、ナタネ油、パーム油、パーム核油、ひまし油、ひまわり油、綿実油、ヤシ油、木ロウ、落花生油、馬脂、牛脂、牛脚脂、牛酪脂、豚脂、山羊脂、羊脂、乳脂、魚油、鯨油等の油脂或いはこれらの水素添加物又は部分ケン化物;エポキシ化大豆油、エポキシ化アマニ油等のエポキシ化油脂;エポキシステアリン酸ブチル、エポキシステアリン酸オクチル等のエポキシ化エステル;グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、ドデカン二酸、ダイマー酸等の二塩基酸;リシノール酸(ヒマシ油脂肪酸)、12−ヒドロキシステアリン酸等のヒドロキシステアリン酸の重縮合物又は該重縮合物と脂肪酸とのエステル;ラウリルアルコール、ミリスチルアルコール、パルミチルアルコール、ステアリルアルコール、オレイルアルコール、ベヘニルアルコール等の高級アルコール;ラウリルアミン、ミリスチルアミン、パルミチルアミン、ステアリルアミン、オレイルアミン、ベヘニルアミン等の高級アミン;ラウリルアミド、ミリスチルアミド、パルミチルアミド、ステアリルアミド、オレイルアミド、ベヘニルアミド等の高級アミド;ヘキサン酸モノ/ジ/トリグリセリド、オクタン酸モノ/ジ/トリグリセリド、デカン酸モノ/ジ/トリグリセリド、ラウリン酸モノ/ジ/トリグリセリド、ミリスチン酸モノ/ジ/トリグリセリド、パルミチン酸モノ/ジ/トリグリセリド、ステアリン酸モノ/ジ/トリグリセリド、オレイン酸モノ/ジ/トリグリセリド、ベヘニン酸モノ/ジ/トリグリセリド等のグリセリド;ヘキサン酸ポリグリセリンエステル、オクタン酸ポリグリセリンエステル、デカン酸ポリグリセリンエステル、ラウリン酸ポリグリセリンエステル、ミリスチン酸ポリグリセリンエステル、パルミチン酸ポリグリセリンエステル、ステアリン酸ポリグリセリンエステル、オレイン酸ポリグリセリンエステル、ベヘニン酸ポリグリセリンエステル等のポリグリセリンエステル;ヘキサン酸ソルビタンエステル、オクタン酸ソルビタンエステル、デカン酸ソルビタンエステル、ラウリン酸ソルビタンエステル、ミリスチン酸ソルビタンエステル、パルミチン酸ソルビタンエステル、ステアリン酸ソルビタンエステル、オレイン酸ソルビタンエステル、ベヘニン酸ソルビタンエステル等のソルビタンエステル;ポリグリセリンモノオクチルエーテル、ポリグリセリンモノデシルエーテル、ポリグリセリンモノラウリルエーテル、ポリグリセリンモノオレイルエーテル、ポリグリセリンモノステアリルエーテル等のポリグリセリンエーテル;上記の化合物にエチレンオキシド、プロピレンオキシド、ドデカン−1,2−オキシド等のα−オレフィンオキシドを付加したもの等が挙げられる。(E4)成分の好ましい配合量は、潤滑性基材に対して0.05〜15質量%程度である。(E4)成分の配合量が0.05質量%未満では、充分な添加効果が得られない場合があり、15質量%を超えると、配合量に見合う効果は得られず、更に粘度指数等の粘度特性を低下させる場合がある。
【0046】
(E5)成分の防錆剤としては、例えば、酸化パラフィンワックスカルシウム塩、酸化パラフィンワックスマグネシウム塩、牛脂脂肪酸アルカリ金属塩、アルカリ土類金属塩又はアミン塩、アルケニルコハク酸又はアルケニルコハク酸ハーフエステル(アルケニル基の分子量は100〜300程度)、ソルビタンモノエステル、ペンタエリスリトールモノエステル、グリセリンモノエステル、ノニルフェノールエトキシレート、ラノリン脂肪酸エステル、ラノリン脂肪酸カルシウム塩等が挙げられる。(E5)成分の好ましい配合量は、防錆効果が充分に発揮される範囲として、潤滑性基材に対して0.1〜15質量%程度である。
【0047】
(E6)成分の粘度指数向上剤としては、例えば、ポリ(C1〜18)アルキルメタクリレート、(C1〜18)アルキルアクリレート/(C1〜18)アルキルメタクリレート共重合体、ジエチルアミノエチルメタクリレート/(C1〜18)アルキルメタクリレート共重合体、エチレン/(C1〜18)アルキルメタクリレート共重合体、ポリイソブチレン、ポリアルキルスチレン、エチレン/プロピレン共重合体、スチレン/マレイン酸エステル共重合体、スチレン/マレイン酸アミド共重合体、スチレン/ブタジエン水素化共重合体、スチレン/イソプレン水素化共重合体等が挙げられる。平均分子量は10,000〜1,500,000程度である。(E6)成分の好ましい配合量は、潤滑性基材に対して0.1〜20質量%程度である。
【0048】
(E7)成分の金属不活性化剤としては、例えば、N,N’−サリチリデン−1,2−プロパンジアミン、アリザリン、テトラアルキルチウラムジスルフィド、ベンゾトリアゾール、ベンゾイミダゾール、2−アルキルジチオベンゾイミダゾール、2−アルキルジチオベンゾチアゾール、2−(N,N−ジアルキルチオカルバモイル)ベンゾチアゾール、2,5−ビス(アルキルジチオ)−1,3,4−チアジアゾール、2,5−ビス(N,N−ジアルキルチオカルバモイル)−1,3,4−チアジアゾール等が挙げられる。(E7)成分の好ましい配合量は、潤滑性基材に対して0.01〜5質量%程度である。
【0049】
(E8)成分の消泡剤としては、例えば、ポリジメチルシリコーン、トリフルオロプロピルメチルシリコーン、コロイダルシリカ、ポリアルキルアクリレート、ポリアルキルメタクリレート、アルコールエトキシ/プロポキシレート、脂肪酸エトキシ/プロポキシレート、ソルビタン部分脂肪酸エステル等が挙げられる。(E8)成分の好ましい配合量は、潤滑性基材に対して1〜1000質量ppm程度である。
【0050】
(E9)成分の固体潤滑剤としては、例えば、グラファイト、二硫化モリブデン、ポリテトラフルオロエチレン、脂肪酸アルカリ土類金属塩、雲母、二塩化カドミウム、二ヨウ化カドミウム、フッ化カルシウム、ヨウ化鉛、酸化鉛、チタンカーバイド、窒化チタン、ケイ酸アルミニウム、酸化アンチモン、フッ化セリウム、ポリエチレン、ダイアモンド粉末、窒化ケイ素、窒化ホウ素フッ化炭素、メラミンイソシアヌレート等が挙げられる。(E9)成分の好ましい配合量は、潤滑性基材に対して0.005〜2質量%程度である。0.005質量%未満では添加効果は得られず、2質量%を超えると、エンジン油の流動性に悪影響を与える場合がある。
【0051】
以上の(E1)〜(E9)の各成分は、1種又は2種以上を適宜配合することができる。中でも、(E3)リン原子及び硫黄原子を含有しない金属系耐摩耗剤を配合することが好ましい。
又、本発明のエンジン油組成物中の硫酸灰分量は、1.0質量%以下であることが好ましく、0.8質量%以下であることが更に好ましく、0.6質量%以下であることが最も好ましい。この硫酸灰分量が1.0質量%を超えると、パティキュレートフィルターの目詰りが起こり易くなるからである。なお、硫酸灰分量はJIS K−2272(原油及び石油製品−灰分及び硫酸灰分試験方法)に記載の方法により測定することができる。
本発明のエンジン油組成物は、あらゆる種類のエンジン用のエンジン油として使用することができ、リン含量及び硫黄含量が低いために、排気ガス浄化触媒の活性低下やパティキュレートフィルターの目詰りが起こりにくい。
【0052】
【実施例】
以下、実施例により本発明を更に具体的に説明する。尚、以下の実施例中、%は特に記載が無い限り質量基準である。
各成分として下記のものを用いて、表1に示す配合にて実施例1〜12及び比較例1〜13の各試験油を調製した。なお、各試験油の硫黄含量、リン含量及び硫酸灰分量の分析値を表2に示す。
【0053】
<潤滑性基油>
(基油1)
鉱油系高VI油。動粘度4.1mm2/s(100℃)、18.3mm2/s(40℃)、粘度指数(VI)=126、硫黄含量30質量ppm。
(基油2)
溶剤精製鉱油。動粘度4.2mm2/s(100℃)、20.8mm2/s(40℃)、粘度指数(VI)=108、硫黄含量5000質量ppm。
【0054】
<A成分:亜鉛ジチオホスフェート>
(A1)
一般式(1)において、R1=R2=1,3−ジメチルブチル基、中性塩/塩基性塩=95/5である亜鉛ジチオホスフェート。リン含量9.4%。
(A2)
一般式(1)において、R1=R2=2−エチルヘキシル基、中性塩/塩基性塩=95/5である亜鉛ジチオホスフェート。リン含量8.0%。
【0055】
<B成分:窒素含有化合物>
(B1)
N−オレイルジエタノールアミン。
(B2)
ヤシ油脂肪酸ジエタノールアミド。
(B3)
N−(2−ヒドロキシヘキサデカニル)ジエタノールアミン。
(B4)
N−(2−ヒドロキシオクタデカニル)モノエタノールアミン。
(B5)
N−牛脂アルキル−N,N’,N’−トリ(ヒドロキシエチル)プロピレンジアミン。
【0056】
<C成分:酸化防止剤>
(C1)
4,4’−ブチリデンビス(2,6−ジ−t−ブチルフェノール)。
(C2)
ジ(p−オクチルフェニル)アミン。
【0057】
<D成分:リン原子又は硫黄原子を含有する潤滑油添加剤>
(D1)
トリクレジルフォスフェート。リン含量8.4%。
(D2)
硫化ラード。硫黄含量15%。
(D3)
カルシウムスルホネート。TBN300mgKOH/g、硫黄含量1.6%。
(D4)
硫化オキシモリブデンビス(2−エチルヘキシル)ジチオカルバメート(硫黄含量18%、モリブデン含量20%)。
【0058】
<E成分:その他の成分>
(E1)
カルシウムサリシレート。TBN280mgKOH/g。
(E2)
特開昭61−285293号公報の実施例1に記載の方法に準じ、ジトリデシルアミン2モルと三酸化モリブデン1モルとを反応させて得られた酸化モリブデンのアミン塩。モリブデン含量11%。
(E3)
特開昭62−108891号公報の例Vに記載の方法に準じ、ヤシ油1モル、ジエタノールアミン1.8モル及び三酸化モリブデン1.3モルを用いて得られた、モリブデンのヤシ油カルボン酸ジエタノールアミド錯体及びモリブデンのグリセリンモノヤシ油カルボン酸エステル錯体の混合物。モリブデン含量6%。
(E4)
グリセリンモノオレイン酸エステル。
(E5)
粘度指数向上剤、ホウ素変性型アルケニルコハク酸ビスイミド、防錆剤、他。
【0059】
【表1】
【0060】
【表2】
【0061】
<耐摩耗性試験>
シェル式高速4球試験機を用い、酸化劣化前の各試験油について下記の条件で耐摩耗性試験を行い、試験球の摩耗痕径を測定した。摩耗痕径が小さいほど、耐摩耗性が高いことを示す。これらの結果を表3に示す。
回 転 数:1200rpm
荷 重:39N
測定温度:室温
測定時間:15分
【0062】
<酸化安定性試験(酸化劣化試験)>
JIS K−2514(潤滑油−酸化安定度試験方法)に準拠して、触媒として銅板及び鉄板を入れたガラス容器に、試験油250mLを入れ、1300rpmで空気を巻き込むよう試験油を攪拌しながら、165.5℃で1週間加熱することにより、試験油を酸化劣化させた。酸化劣化後の試験油についても、耐摩耗性試験を行なった。また、酸化劣化前後の試験油について、動粘度(40℃)及び全酸価を測定し、その結果から粘度比(酸化劣化前の動粘度に対する、酸化劣化後の動粘度の比)及び全酸価の増加(酸化劣化後の全酸価から酸化劣化前の全酸価を引いた値)を求めた。酸化劣化前後の摩耗痕径の差が小さく、粘度比が小さく、全酸価の増加が少ないほど酸化安定性が高いことを示す。これらの結果も表3に示す。
【0063】
【表3】
【0064】
表3の結果をまとめると、本発明の実施例のエンジン油が0.00〜0.02mmの摩耗痕径の増加を示したのに対し、比較例のエンジン油は0.00〜0.05mmの摩耗痕径の増加を示した。
また、本発明の実施例のエンジン油の粘度比も、比較例のエンジン油の粘度比を下回り、本発明の実施例のエンジン油の全酸価の増加も、比較例のエンジン油の全酸価の増加を大幅に下回った。
以上より、本発明の組成のエンジン油は、本発明の組成を持たないエンジン油と比較して、優れた耐摩耗性及び酸化安定性を有することが判った。
【0065】
【発明の効果】
エンジン油中のリン成分及び硫黄成分は、排ガス浄化触媒の活性低下やパティキュレートフィルターの目詰りを引き起こすとされている。本発明の効果は、低リン含量及び低硫黄含量でありながら、優れた耐摩耗性及び酸化安定性を有するエンジン油組成物を提供したことにある。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to an engine oil composition that can be suitably used for gasoline engines, diesel engines, and the like.
[0002]
[Prior art]
The exhaust gas generated by combustion in the engine contains nitrogen oxide (NOx), sulfur oxide (SOx), particulate suspended matter (PM), and the like. These harmful substances are known to cause environmental pollution, natural destruction, adverse effects on the human body, etc., and countermeasures are required to prevent them from being released into the atmosphere as much as possible. For this reason, reduction of sulfur content and nitrogen content in fuel oil, improvement of engine, improvement of combustion method, improvement of exhaust gas purification catalyst, examination of particulate filter, and the like are being carried out.
On the other hand, with engine oil, the wear of the valve system such as cams, valves, rocker arms, etc. is reduced, energy loss due to friction is reduced, thermal deterioration / oxidation deterioration of engine oil is suppressed, incomplete combustion of fuel and engine oil deterioration Many functions such as suppression of accumulation of objects in the engine are required. For this reason, engine oil is used as a base oil, such as mineral oil and synthetic oil, with many additives such as antiwear agents, friction reducers, antioxidants, ashless dispersants, metallic detergents, viscosity index improvers, etc. It is used in the state of the composition which mix | blended. Among these additives, zinc dithiophosphate is very excellent as an antiwear agent and excellent in antioxidant properties. Therefore, almost all engine oils actually used have a phosphorus content of 800 to About 1500 mass ppm has been blended.
A part of the engine oil enters the combustion chamber, burns, and is discharged together with the exhaust gas. However, it is known that the phosphorus component in the engine oil reduces the activity of the exhaust gas purification catalyst. In addition, the sulfur component in the engine oil reduces the activity of the NOx reduction type exhaust gas purification catalyst, and adheres as a sulfate, causing clogging of the particulate filter. That is, it is preferable to reduce the phosphorus content and sulfur content in the engine oil in order to reduce harmful substances in the exhaust gas.
Since the phosphorus component in engine oil is mainly derived from zinc dithiophosphate, it is necessary to reduce the zinc dithiophosphate content in order to reduce the phosphorus content. However, in phosphorus-free engines that do not contain zinc dithiophosphate, it is necessary to blend a large amount of sulfur-containing compounds as antiwear agents (see Patent Documents 1 to 5, etc.), and the sulfur content in engine oil increases. The current situation is that a small amount of zinc dithiophosphate must be blended. As engine oil with reduced phosphorus and sulfur contents, the phosphorus content is reduced to about 300-600 ppm by adding zinc dithiophosphate, succinimide ashless dispersant, and metal detergent. Although engine oils (see Patent Documents 6 and 7) are also known, their wear resistance and oxidation stability are insufficient.
[0003]
On the other hand, fatty acid amides of alkanolamine (for example, see Patent Document 8), N-alkyldiethanolamine (for example, see Patent Document 9), N, N-dialkylmonoethanolamine (for example, see Patent Document 10), N Alkanolamine compounds or alkanolamide compounds such as-(2-hydroxyalkyl) diethanolamine (see, for example, Patent Document 11) are known as additives for engine oils. It was not clear that it could be reduced.
[0004]
[Patent Document 1]
JP-A-62-253691
[Patent Document 2]
JP-A-6-41568
[Patent Document 3]
JP 52-39704 A
[Patent Document 4]
Japanese Patent Laid-Open No. 7-118680
[Patent Document 5]
JP 2000-63862 A
[Patent Document 6]
JP-A-9-111275
[Patent Document 7]
JP 2002-53888 A
[Patent Document 8]
JP-A-55-66996
[Patent Document 9]
Japanese Patent Laid-Open No. 7-508049
[Patent Document 10]
JP 2000-34489 A
[Patent Document 11]
JP-A-9-1000048
[0005]
[Problems to be solved by the invention]
Accordingly, the problem to be solved by the present invention is to provide an engine oil composition having wear resistance and oxidation stability equivalent to or higher than that of conventional engine oils even with low phosphorus content and low sulfur content. There is.
[0006]
[Means for Solving the Problems]
Therefore, the present inventors diligently studied engine oils having a low phosphorus content and a low sulfur content, and by adding an alkanolamine compound or an alkanolamide compound having a specific structure, the amount of zinc dithiophosphate can be greatly reduced. The headline, the present invention has been reached. That is, the present invention provides the lubricating base oil with the following general formula (1) as the component (A).
[0007]
[Chemical 3]
[0008]
(Wherein R1And R2Represents a hydrocarbon group, and a represents a number of 0 to 1/3. )
Zinc dithiophosphate represented by a phosphorus content of 100 to 500 ppm by mass;
As the component (B), the following general formula (2)
[0009]
[Formula 4]
[0010]
(Wherein R3Represents an alkyl group having 8 to 22 carbon atoms, an alkenyl group, a 2-hydroxyalkyl group or an acyl group;4Represents an alkylene group having 2 to 4 carbon atoms, and X representsR 3 Is an alkyl group or an alkenyl group, a 2-hydroxyalkyl group having 2 to 18 carbon atoms or —CH 2 CH 2 CH 2 N (R 4 OH) 2 Represents R 3 Is a 2-hydroxyethyl group, it represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms or a 2-hydroxyalkyl group having 2 to 18 carbon atoms, and R 3 When is an acyl group, it represents a hydrogen atom or a 2-hydroxyalkyl group having 2 to 4 carbon atoms.)
0.01 to 10% by mass of a nitrogen-containing compound represented by:
And the phosphorus content is 500 mass ppm or less and the sulfur content is3000It is an engine oil composition having a mass ppm or less.
[0011]
DETAILED DESCRIPTION OF THE INVENTION
First, the component (A) of the present invention will be described. The component (A) of the present invention is zinc dithiophosphate represented by the general formula (1).
In the general formula (1), R1And R2Represents a hydrocarbon group. Examples of the hydrocarbon group include an alkyl group, an alkenyl group, an aryl group, a cycloalkyl group, and a cycloalkenyl group.
[0012]
Examples of the alkyl group include methyl, ethyl, propyl, isopropyl, butyl, isobutyl, secondary butyl, tertiary butyl, pentyl, isopentyl, secondary pentyl, neopentyl, tertiary pentyl, hexyl, secondary hexyl, heptyl, 2 Secondary heptyl, octyl, 2-ethylhexyl, secondary octyl, nonyl, secondary nonyl, decyl, secondary decyl, undecyl, secondary undecyl, dodecyl, secondary dodecyl, tridecyl, isotridecyl, secondary tridecyl, tetradecyl, secondary tetradecyl , Hexadecyl, secondary hexadecyl, stearyl, eicosyl, docosyl, tetracosyl, triacontyl, 2-butyloctyl, 2-butyldecyl, 2-hexyloctyl, 2-hexyldecyl, 2-octyldecyl, 2-hexyldecyl, 2-octyl Dodecyl, 2-decyl tetradecyl, 2-dodecyl-hexadecyl, 2-hexadecyl octadecyl, 2-tetradecyl-octadecyl, monomethyl branched - and the like isostearyl group.
[0013]
Examples of the alkenyl group include vinyl, allyl, propenyl, isopropenyl, butenyl, isobutenyl, pentenyl, isopentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, undecenyl, dodecenyl, tetradecenyl, oleyl group and the like.
[0014]
As an aryl group, for example, phenyl, toluyl, xylyl, cumenyl, mesityl, benzyl, phenethyl, styryl, cinnamyl, benzhydryl, trityl, ethylphenyl, propylphenyl, butylphenyl, pentylphenyl, hexylphenyl, heptylphenyl, octylphenyl, Nonylphenyl, decylphenyl, undecylphenyl, dodecylphenyl, styrenated phenyl, p-cumylphenyl, phenylphenyl, benzylphenyl, α-naphthyl, β-naphthyl group and the like can be mentioned.
[0015]
Examples of the cycloalkyl group and the cycloalkenyl group include a cyclopentyl, cyclohexyl, cycloheptyl, methylcyclopentyl, methylcyclohexyl, methylcycloheptyl, cyclopentenyl, cyclohexenyl, cycloheptenyl, methylcyclopentenyl, methylcyclohexenyl, methylcycloheptenyl group. Etc.
[0016]
Among these hydrocarbon groups, R1And R2Is preferably an alkyl group, more preferably a secondary alkyl group. The number of carbon atoms is preferably 3 to 14, more preferably 3 to 10, and most preferably 3 to 8. R1And R2May be the same or different hydrocarbon groups.
In the general formula (1), a is a number from 0 to 1/3. When a = 0, it is called neutral zinc dithiophosphate, and when a = 1/3, basic zinc dithiophosphate is be called.
[0017]
The content of zinc dithiophosphate represented by the general formula (1) as the component (A) with respect to the total amount of the engine oil composition of the present invention is 100 to 500 ppm by mass, preferably 150 to 480 ppm by mass, as the phosphorus content. More preferably, it is 200-450 mass ppm, Most preferably, it is 250-400 mass ppm. When the content of the component (A) is less than 100 ppm by mass as the phosphorus content, the wear resistance and oxidation stability are insufficient, and when it exceeds 500 ppm by mass, the activity of the exhaust gas purification catalyst is liable to decrease.
[0018]
Next, the component (B) of the present invention will be described. The component (B) of the present invention is a nitrogen-containing compound represented by the general formula (2).
In the general formula (2), R3Represents an alkyl group having 8 to 22 carbon atoms, an alkenyl group, a 2-hydroxyalkyl group or an acyl group. Examples of the alkyl group or alkenyl group having 8 to 22 carbon atoms include R in the general formula (1).1Or R2Among the alkyl groups or alkenyl groups mentioned in the above, those having 8 to 22 carbon atoms can be mentioned.
[0019]
Examples of the 2-hydroxyalkyl group having 8 to 22 carbon atoms include 2-hydroxyoctyl, 2-hydroxynonyl, 2-hydroxydecyl, 2-hydroxyundecyl, 2-hydroxydodecyl, 2-hydroxytridecyl, 2-hydroxytetra Examples include decyl, 2-hydroxyhexadecyl, 2-hydroxyoctadecyl, 2-hydroxyeicosyl, and 2-hydroxydocosyl group.
[0020]
Examples of the acyl group having 8 to 22 carbon atoms include octanoyl, nonanoyl, decanoyl, undecanoyl, dodecanoyl, tridecanoyl, tetradecanoyl, pentadecanoyl, hexadecanoyl, heptadecanoyl, octadecanoyl, nonadecanoyl, eicosanoyl, heneiosa Noyl, docosanoyl, undecenoyl, octadecenoyl, octadecadienoyl, 12-hydroxyoctadecanoyl, 12-hydroxyoctadecenoyl group and the like.
Among these, R3Are preferably those having 10 to 20 carbon atoms, more preferably those having 12 to 18 carbon atoms, and most preferably 2-hydroxyalkyl groups having 12 to 18 carbon atoms.
[0021]
R4Represents an alkylene group having 2 to 4 carbon atoms. Examples of the alkylene group having 2 to 4 carbon atoms include ethylene, propylene, butylene, etc. Among them, ethylene is preferable.
[0022]
X is a hydrogen atom, an alkyl group having 1 to 22 carbon atoms, a 2-hydroxyalkyl group having 2 to 22 carbon atoms, or —CH.2CH2CH2N (R4OH)2Represents a group represented by Examples of the alkyl group having 1 to 22 carbon atoms include R in the general formula (1).1Or R2Among the alkyl groups mentioned above, those having 1 to 22 carbon atoms can be mentioned. In addition, as the 2-hydroxyalkyl group having 2 to 22 carbon atoms, R3In addition to the 2-hydroxyalkyl group having 8 to 22 carbon atoms mentioned above, 2-hydroxyethyl, 2-hydroxypropyl, 2-hydroxybutyl, 2-hydroxypentyl, 2-hydroxyhexyl, 2-hydroxyheptyl group, etc. Can be mentioned. R3Is an alkyl group or an alkenyl group, X represents an alkyl group having 1 to 4 carbon atoms, a 2-hydroxyalkyl group having 2 to 18 carbon atoms, and -CH.2CH2CH2N (R4OH)2Is preferable, a 2-hydroxyalkyl group having 2 to 18 carbon atoms is more preferable, and a 2-hydroxyalkyl group having 2 to 4 carbon atoms is most preferable. R3When is an acyl group, X is preferably a hydrogen atom and a 2-hydroxyalkyl group having 2 to 4 carbon atoms, and most preferably hydrogen or a 2-hydroxyethyl group. R3Is a 2-hydroxyethyl group, X is preferably a hydrogen atom, an alkyl group having 1 to 4 carbon atoms and a 2-hydroxyalkyl group having 2 to 18 carbon atoms, and hydrogen and 2-hydroxy having 2 to 18 carbon atoms. An alkyl group is more preferable, and a 2-hydroxyalkyl group having 2 to 4 carbon atoms is most preferable.
[0023]
In the general formula (2), R3Is a C2-C22 alkyl group or an alkenyl group, for example, an amine compound represented by the following general formulas (3)-(5) is substituted with a C2-C4 alkylene oxide, It can be obtained by reacting by a known method.
R5-NH2 (3)
R5-NH-R6 (4)
R5-NHCH2CH2CH2NH2 (5)
(Wherein R5Represents an alkyl or alkenyl group having 8 to 22 carbon atoms;6Represents an alkyl group having 1 to 22 carbon atoms or a 2-hydroxyalkyl group having 2 to 22 carbon atoms. )
Examples of the alkylene oxide having 2 to 4 carbon atoms include ethylene oxide, propylene oxide, butylene oxide and the like.
Among the amine compounds represented by the general formula (4), R6Can be obtained by reacting an alkylene oxide having 2 to 22 carbon atoms with the amine compound represented by the general formula (3).
[0024]
In the general formula (2), R3Is a amide compound obtained by reacting a fatty acid having 8 to 22 carbon atoms or a lower alcohol ester thereof with ammonia, monoalkylamine, propylenediamine, or the like. , A method of reacting an alkylene oxide having 2 to 4 carbon atoms; a fatty acid having 8 to 22 carbon atoms or a lower alcohol ester thereof is reacted with a low molecular weight alkanolamine such as monoethanolamine, monopropanolamine, diethanolamine or dipropanolamine. It is obtained by a method or the like.
In the general formula (2), R3The nitrogen-containing compound which is a 2-hydroxyalkyl group having 8 to 22 carbon atoms can be obtained by, for example, a method of reacting an α-olefin oxide having 8 to 22 carbon atoms with a low molecular weight alkanolamine.
[0025]
The content of component (B) with respect to the total amount of the engine oil composition of the present invention is 0.01 to 10% by mass, preferably 0.05 to 5% by mass, more preferably 0.1 to 3% by mass, and most preferably. Is 0.1 to 1% by mass. When the content of component (B) is less than 0.01% by mass, the wear resistance and oxidation stability of the engine oil of the present invention are insufficient, and when it exceeds 10% by mass, an effect commensurate with the content cannot be obtained. This is because the temperature-viscosity characteristics (viscosity index) may decrease.
[0026]
The phosphorus content of the engine oil composition of the present invention is 500 ppm by mass or less. This is because when the phosphorus content exceeds 500 ppm by mass, the activity of the exhaust gas purification catalyst is likely to decrease. The phosphorus content is preferably 460 mass ppm or less, more preferably 430 mass ppm or less, and most preferably 400 mass ppm or less.
[0027]
Moreover, the sulfur content of the engine oil composition of the present invention is 5000 mass ppm or less. This is because when the sulfur content exceeds 5000 ppm by mass, the activity of the NOx reduction type exhaust gas purification catalyst is reduced and the particulate filter is easily clogged. The sulfur content is preferably 5000 mass ppm or less, more preferably 3000 mass ppm or less, and most preferably 2000 mass ppm or less.
[0028]
The engine oil composition of the present invention has excellent wear resistance and oxidation stability, but in order to maintain the wear resistance for a long period of time, as a component (C), a phenol-based antioxidant or an amine-based antioxidant It is preferable to contain.
[0029]
Examples of the phenolic antioxidant include 2,6-di-tert-butylphenol (hereinafter, tertiary-butyl is abbreviated as t-butyl), 2,6-di-tert-butyl-4-methylphenol, 2,6-di-tert-butyl-4-ethylphenol, 6-tert-butyl-2,4-dimethylphenol, 4,4′-methylenebis (2,6-di-tert-butylphenol), 3,3 ′ , 5,5′-tetra-t-butyl-4,4′-dihydroxybiphenyl, 3,3′-di-t-butyl-4,4′-dihydroxy-5,5′-dimethylbiphenyl, 2,2 ′ -Methylenebis (6-t-butyl-4-methylphenol), 2,2'-methylenebis (6-t-butyl-4-ethylphenol), 4,4'-butylidenebis (6-t-butyl- -Methylphenol), 4,4'-isopropylidenebis (2,6-di-t-butylphenol), 2,2'-methylenebis (6-cyclohexyl-4-methylphenol), 2,2'-methylenebis (4 -Methyl-6-nonylphenol), 2,2'-isobutylidenebis (4,6-dimethylphenol), 2,6-bis (3'-tert-butyl-2'-hydroxy-5'-methylbenzyl) -4-methylphenol, 3-tert-butyl-4-hydroxyanisole, 2-tert-butyl-4-hydroxyanisole, stearyl 3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate, 3- (3,5-di-tert-butyl-4-hydroxyphenyl) oleyl propionate, 3- (3,5-di-tert-butyl-4-hydroxyphenyl) Dodecyl propionate, 3- (3,5-di-t-butyl-4-hydroxyphenyl) decyl propionate, octyl 3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate, tetrakis { 3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionyloxymethyl} methane, 3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid glycerin monoester, 3- (3,5-di-t-butyl-4-hydroxyphenyl) propionic acid and glycerol monooleyl ether ester, 3- (3,5-di-t-butyl-4-hydroxyphenyl) propionic acid butylene glycol ester 2,6-di-t-butyl-4- (N, N-dimethylaminomethylphenol), tris {(3,5-di-t- Butyl-4-hydroxyphenyl) propionyloxyethyl} isocyanurate, tris (3,5-di-t-butyl-4-hydroxyphenyl) isocyanurate, 1,3,5-tris (3,5-di-t-) Butyl-4-hydroxybenzyl) isocyanurate, 1,3,5-tris (4-tert-butyl-2,6-dimethyl-3-hydroxybenzyl) isocyanurate, N, N′-di (3,5-di) -T-butyl-4-hydroxydihydrocinnamyl) hexamethylene-1,6-diamine, 3,9-di [1,1-dimethyl-2- {β- (3-t-butyl-4-hydroxy-5 -Methylphenyl) propionyloxy} ethyl] -2,4,8,10-tetraoxaspiro [5,5] undecane, 1,1,3-tri (5-tert-butyl-4-hydroxy) -2-methylphenyl) butane, 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxybenzyl) benzene, 3- (3′-tert-butyl) -4'-hydroxyphenyl) butyric acid glycol diester and the like, a phenolic antioxidant containing no sulfur atom and phosphorus atom; 3- (3,5-di-t-butyl-4-hydroxyphenyl) propionic acid thiodiglycol Ester, 4,4′-thiobis (6-t-butyl-3-methylphenol), 4,4′-thiobis (6-t-butyl-2-methylphenol), 2,2′-thiobis (6-t -Butyl-4-methylphenol), bis (3,5-di-t-butyl-4-hydroxybenzyl) sulfide, bis {4- (3-n-alkylthiopropionyloxy) -5-t -Butyl-2-methylphenyl} sulfide, di (4-t-butyl-2,6-dimethyl-3-hydroxybenzyl) sulfide, 6- (3,5-di-t-butyl-4-hydroxyanilino) -2,4-bis (octylthio) -1,3,5-triazine, 2,2-thio- {diethyl-bis-3- (3,5-di-t-butyl-4-hydroxyphenyl)} propionate, Phenolic antioxidants containing sulfur atoms and no phosphorus atoms, such as bis (5-t-butyl-4-hydroxy-3-methylbenzyl) sulfide; 3,5-di-t-butyl-4-hydroxy Examples thereof include phenolic antioxidants containing a phosphorus atom and not containing a sulfur atom, such as benzyl phosphate diester.
[0030]
Examples of amine-based antioxidants include naphth-1-ylamine, N- (naphth-1-yl) -N-phenylamine, and N- (naphth-1-yl) -N- (p-octylphenyl) amine. N- (naphth-1-yl) -N- (p-nonylphenyl) amine, N- (p-dodecylphenyl) -N- (naphth-1-yl) amine, N- (naphth-2-yl) Naphthylamine antioxidants such as N-phenylamine; N, N′-diisopropyl-p-phenylenediamine, N, N′-diisobutyl-p-phenylenediamine, N, N′-diphenyl-p-phenylenediamine, N , N′-di-β-naphthyl-p-phenylenediamine, N-isopropyl-N′-phenyl-p-phenylenediamine, N-cyclohexyl-N′-phenyl-p-pheny Phenylenediamines such as N-diamine, N- (1,3-dimethylbutyl) -N'-phenyl-p-phenylenediamine, dioctyl-p-phenylenediamine, phenylhexyl-p-phenylenediamine, phenyloctyl-p-phenylenediamine Antioxidant; dipyridylamine, diphenylamine, di (pn-butylphenyl) amine, di (pt-butylphenyl) amine, di (pt-pentylphenyl) amine, di (p-octylphenyl) amine , Di (p-nonylphenyl) amine, di (p-decylphenyl) amine, di (p-dodecylphenyl) amine, di (p-styrylphenyl) amine, di (p-methoxyphenyl) amine, 4,4 ′ -Bis (4-α, α-dimethylbenzyl) diphenylamine, N- (p-isopropyl Diphenylamine-based antioxidants such as xylphenyl) -N-phenylamine and dipyridylamine; phenothiazine-based oxidations such as phenothiazine, N-methylphenothiazine, N-ethylphenothiazine, 3,7-dioctylphenothiazine, phenothiazinecarboxylic acid ester, and phenoselenazine An inhibitor.
[0031]
As the component (C), amine-based antioxidants are preferable, phenylenediamine-based antioxidants and diphenylamine-based antioxidants are more preferable, and diphenylamine-based antioxidants are most preferable. The amount of component (C) is preferably 0.05 to 5% by mass, more preferably 0.08 to 3% by mass, and most preferably 0.1 to 2% by mass, based on the total amount of engine oil. If the blending amount of the component (C) is less than 0.05% by mass, the wear resistance may not be maintained for a long period of time. If the blending amount exceeds 5% by mass, an effect commensurate with the blending amount cannot be obtained, and an oil seal should be used. It may deteriorate and cause oil leakage.
[0032]
The component (A), zinc dithiophosphate, is a compound containing a phosphorus atom and a sulfur atom. In addition to the component (A), when a phosphorus component or a sulfur component is mixed into the engine oil, for example, a lubricating base oil When a mineral oil containing sulfur is used, a case where a lubricating oil additive containing a phosphorus atom or sulfur atom is blended can be used. Mineral oil is produced by distilling and separating natural crude oil, followed by refining. Crude oil contains impurities such as sulfur-containing compounds, nitrogen-containing compounds, oxygen-containing compounds, and metal (vanadium, nickel, etc.)-Containing compounds in addition to the main hydrocarbons. These impurities are removed by refining, but a lot of impurities remain depending on the crude oil production area and refining method. For example, some mineral oils have a sulfur content of 10 mass ppm or less, but some mineral oils exceed 1000 mass ppm. The sulfur content of the lubricating base oil of the engine oil composition of the present invention is preferably as low as possible, but considering the difficulty of deterioration due to NOx of blow-by gas (combustion gas leaking from the combustion chamber into the crankcase). The sulfur content is preferably 50 mass ppm or less, more preferably 30 mass ppm or less, and most preferably 10 mass ppm or less. The kinematic viscosity of the lubricating base oil is not particularly limited, but preferably 1 to 50 mm at 100 ° C.2/ S, 10 to 1,000 mm at 40 ° C2The viscosity index (VI) is preferably 100 or more, more preferably 120 or more, and most preferably 135 or more.
[0033]
Moreover, as a lubricating oil additive containing a phosphorus atom or a sulfur atom, the above-mentioned phenolic antioxidant containing a sulfur atom and not containing a phosphorus atom, a phenol type containing a phosphorus atom and containing no sulfur atom In addition to antioxidants and phenothiazine antioxidants, (D1) phosphorus antiwear agents or phosphorus antioxidants, (D2) sulfonate metal detergents, (D3) sulfur extreme pressure agents, (D4) sulfur And (D5) a thiophosphoric acid extreme pressure agent, (D6) a metallic antiwear agent containing phosphorus and / or sulfur, and the like.
[0034]
(D1) Examples of phosphorus antiwear agents or phosphorus antioxidants include organic phosphines, organic phosphine oxides, organic phosphinites, organic phosphonites, organic phosphinates, organic phosphites, organic phosphonates, organic phosphates, and organic phosphoramidates. Etc.
[0035]
Examples of the (D2) sulfonate-based metal detergent include (mono or di) alkyl benzene sulfonic acid metal salt, (mono or di) alkyl naphthalene sulfonic acid metal salt, petroleum sulfonic acid metal salt, and the like. Examples of the metal of these metal salts include alkali metals such as sodium and potassium; alkaline earth metals such as magnesium, calcium and barium.
[0036]
Examples of (D3) sulfur-based extreme pressure agents include sulfurized fats and oils, sulfurized mineral oils, organic mono- or polysulfides, polyolefin sulfides, 1,3,4-thiadiazole derivatives, thiuram disulfides, dithiocarbamic acid esters, and the like.
[0037]
Examples of (D4) sulfur-based antioxidants include thiodipropionic acid esters, thiobis (phenol) compounds, polyhydric alcohol esters of alkylthiopropionic acid, 2-mercaptobenzimidazole, dilauryl sulfide, amylthioglycolate, and the like. Can be mentioned.
[0038]
Examples of the (D5) thiophosphate extreme pressure agent include organic trithiophosphites and organic thiophosphates.
[0039]
(D6) Examples of metal antiwear agents containing phosphorus and / or sulfur include dithiophosphate metal salts, dithiocarbamic acid metal salts, xanthogenic acid metal salts, mercaptobenzothiazole metal salts, mercaptobenzimidazole metal salts, and thiophenol. A metal salt etc. are mentioned. Metals include lithium, sodium, potassium, magnesium, calcium, barium, titanium, zinc, lead, tin, iron, cadmium, cobalt, nickel, manganese, strontium, titanium, vanadium, copper, antimony, bismuth, molybdenum, tungsten, etc. Is mentioned.
[0040]
In the engine oil of the present invention, it is preferable not to add a lubricant additive containing phosphorus or sulfur. However, the additive amount does not exceed the upper limit of the phosphorus content and sulfur content of the present invention, that is, the phosphorus content is 500 mass. If it is an addition amount that results in ppm or less and a sulfur content of 5000 ppm or less, it may be blended as necessary.
[0041]
In addition, the engine oil composition of the present invention can be blended with a lubricant that does not contain phosphorus atoms and sulfur atoms that are usually used in engine oils. Examples of such lubricants include (E1) metal detergents (excluding sulfonates), (E2) ashless dispersants, (E3) metal antiwear agents containing no phosphorus and sulfur atoms, (E4) Oiliness improver containing no metal, phosphorus atom or sulfur atom, (E5) rust inhibitor, (E6) viscosity index improver, (E7) metal deactivator, (E8) antifoaming agent, (E9) solid lubrication Agents and the like.
[0042]
(E1) Examples of the metal detergent (excluding sulfonate type) include metal phenolate and metal salicylate. Examples of the metal phenolate include (mono or di) alkylphenol metal salts, bis {(mono or di) alkylhydroxyphenyl} methylene metal salts, and the like. Examples of the metal salicylates include (mono or di) alkyl salicylic acid metal salts, bis {(mono or di) alkyl salicylic acid} sulfide metal salts, bis {(mono or di) alkyl salicylic acid} methylene metal salts, and the like. As the metal, an alkaline earth metal is preferable, and calcium and magnesium are more preferable.
In addition, the above compounds are generally neutral salts. As metal detergents, these neutral salts are basified with metal oxides or metal hydroxides while blowing carbon dioxide, and thus basic. Alternatively, those which are overbased are preferably used. By making the metal detergent basic or overbased, in addition to the function of suppressing the accumulation of incomplete fuel combustion products and engine oil degradation products in the engine, it can be applied to blowby gas and engine oil degradation products. This is to neutralize the derived acidic substance and to provide a function of preventing corrosive wear caused by the acidic substance.
Overbased compounds are usually contained in the form of carbonates. The total base number (TBN) of these basic or overbased metal detergents is generally about 200 to 500 mg KOH / g. (E1) The preferable compounding quantity of a component is about 0.5-15 mass% with respect to the whole engine oil composition.
[0043]
(E2) Examples of the ashless dispersant include succinimide, benzylamine, succinic acid ester, and boron-modified products thereof. Examples of the succinimide include succinic acid having a polyalkenyl group such as a polybutenyl group having a molecular weight of about 300 to 4,000, and a polyethylene polyamine such as ethylenediamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, and pentaethylenehexamine. Monoimides or diimides of the above, or boron-modified products thereof; Mannich reaction products of phenols having polyalkenyl groups, formaldehyde, and the above-mentioned polyethylene polyamines.
The nitrogen content in the ashless dispersant is usually about 0.5 to 2.0% by mass. Among these ashless dispersants, succinimide or a boron-modified product thereof is preferable. (E2) The preferable compounding quantity of a component is about 0.5-20 mass% with respect to a lubricous base material.
[0044]
(E3) Examples of metallic antiwear agents that do not contain phosphorus and sulfur atoms include titanium, zinc, lead, tin, iron, cadmium, cobalt, nickel, manganese, strontium, titanium, vanadium, copper, antimony, and bismuth. , Fatty acid salts such as molybdenum and tungsten, alkyl or alkenyl succinates, phenol salts, salicylates, alcoholates, glycol complexes, β-diketone complexes, reaction products with amine compounds, carboxylic acid alkanolamide complexes, glycerin monocarboxylic acids An ester complex etc. are mentioned. Among these, in particular, a molybdenum-based antiwear agent containing no phosphorus atom and sulfur atom is preferable, and a reaction product of molybdenum and an amine compound, a carboxylic acid diethanolamide complex of molybdenum, and a glycerin monocarboxylic acid ester complex of molybdenum are further included. preferable. The method for producing a reaction product of molybdenum and an amine compound is disclosed in JP-A-61-285293, and the method for producing a carboxylic acid diethanolamide complex of molybdenum and a glycerin monocarboxylic acid ester complex of molybdenum is disclosed in JP-A-62. -108891. A preferable blending amount of the component (E3) is about 200 to 1000 ppm by mass with respect to the lubricating base material based on metal atoms. When the blending amount of the component (E3) is less than 200 mass ppm, a sufficient addition effect may not be obtained. When the blending amount exceeds 1000 ppm by mass, an effect commensurate with the blending amount cannot be obtained, and the activity of the exhaust gas purification catalyst is further improved. May decrease.
[0045]
(E4) Examples of the oil-based improver containing no metal, phosphorus atom and sulfur atom include hexanoic acid, octanoic acid, pelargonic acid, decanoic acid, lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, and behenic acid. Fatty acids such as linoleic acid and linolenic acid; linseed oil, eno oil, psyllium oil, olive oil, cacao oil (I prefer oil), kapok oil, white mustard oil, sesame oil, rice bran oil, safflower oil, shea nut Oil, cinnabar oil, soybean oil, tea seed oil, camellia oil, corn oil, rapeseed oil, palm oil, palm kernel oil, castor oil, sunflower oil, cottonseed oil, palm oil, tree wax, peanut oil, horse fat, beef tallow, cattle Leg fat, beef dairy fat, pork fat, goat fat, sheep fat, milk fat, fish oil, whale oil, etc., or hydrogenated or partially saponified products thereof; epoxidized soybean oil, epoxidized Epoxidized oils such as linseed oil; Epoxidized esters such as butyl epoxy stearate and octyl epoxy stearate; Basic acid; polycondensate of hydroxystearic acid such as ricinoleic acid (castor oil fatty acid), 12-hydroxystearic acid or ester of the polycondensate and fatty acid; lauryl alcohol, myristyl alcohol, palmityl alcohol, stearyl alcohol, oleyl Higher alcohols such as alcohol and behenyl alcohol; higher amines such as laurylamine, myristylamine, palmitylamine, stearylamine, oleylamine, and behenylamine; laurylamide, myristylamide, palmitylamide, Higher amides such as allylamide, oleylamide, behenylamide; hexanoic acid mono / di / triglyceride, octanoic acid mono / di / triglyceride, decanoic acid mono / di / triglyceride, lauric acid mono / di / triglyceride, myristic acid mono / di / Triglycerides, palmitic acid mono / di / triglycerides, stearic acid mono / di / triglycerides, oleic acid mono / di / triglycerides, behenic acid mono / di / triglycerides and other glycerides; hexanoic acid polyglycerin ester, octanoic acid polyglycerin ester, decane Acid polyglycerin ester, lauric acid polyglycerin ester, myristic acid polyglycerin ester, palmitic acid polyglycerin ester, stearic acid polyglycerin ester, oleic acid polyglycerin Esters, polyglycerol esters such as behenic acid polyglycerol ester; hexanoic acid sorbitan ester, octanoic acid sorbitan ester, decanoic acid sorbitan ester, lauric acid sorbitan ester, myristic acid sorbitan ester, palmitic acid sorbitan ester, stearic acid sorbitan ester, oleic acid Sorbitan esters such as sorbitan ester and behenic acid sorbitan ester; polyglycerol ethers such as polyglycerol monooctyl ether, polyglycerol monodecyl ether, polyglycerol monolauryl ether, polyglycerol monooleyl ether, and polyglycerol monostearyl ether; Α-olefin such as ethylene oxide, propylene oxide, dodecane-1,2-oxide And those obtained by adding N'okishido the like. A preferable blending amount of the component (E4) is about 0.05 to 15% by mass with respect to the lubricating base material. When the blending amount of the component (E4) is less than 0.05% by mass, a sufficient addition effect may not be obtained. When the blending amount exceeds 15% by mass, an effect commensurate with the blending amount cannot be obtained, and the viscosity index and the like are further reduced. Viscosity characteristics may be reduced.
[0046]
Examples of the rust preventive agent for component (E5) include oxidized paraffin wax calcium salt, oxidized paraffin wax magnesium salt, beef tallow fatty acid alkali metal salt, alkaline earth metal salt or amine salt, alkenyl succinic acid or alkenyl succinic acid half ester ( The molecular weight of the alkenyl group is about 100 to 300), sorbitan monoester, pentaerythritol monoester, glycerin monoester, nonylphenol ethoxylate, lanolin fatty acid ester, lanolin fatty acid calcium salt and the like. (E5) The preferable compounding quantity of a component is about 0.1-15 mass% with respect to a lubricous base material as a range by which a rust prevention effect is fully exhibited.
[0047]
Examples of the viscosity index improver for the component (E6) include poly (C1-18) alkyl methacrylate, (C1-18) alkyl acrylate / (C1-18) alkyl methacrylate copolymer, diethylaminoethyl methacrylate / (C1-18). ) Alkyl methacrylate copolymer, ethylene / (C1-18) alkyl methacrylate copolymer, polyisobutylene, polyalkylstyrene, ethylene / propylene copolymer, styrene / maleic ester copolymer, styrene / maleic amide copolymer And a styrene / butadiene hydrogenated copolymer and a styrene / isoprene hydrogenated copolymer. The average molecular weight is about 10,000 to 1,500,000. A preferred blending amount of the component (E6) is about 0.1 to 20% by mass with respect to the lubricating base material.
[0048]
Examples of the metal deactivator for the component (E7) include N, N′-salicylidene-1,2-propanediamine, alizarin, tetraalkylthiuram disulfide, benzotriazole, benzimidazole, 2-alkyldithiobenzimidazole, 2 -Alkyldithiobenzothiazole, 2- (N, N-dialkylthiocarbamoyl) benzothiazole, 2,5-bis (alkyldithio) -1,3,4-thiadiazole, 2,5-bis (N, N-dialkylthio) Carbamoyl) -1,3,4-thiadiazole and the like. (E7) The preferable compounding quantity of a component is about 0.01-5 mass% with respect to a lubricous base material.
[0049]
Examples of the antifoaming agent for component (E8) include polydimethyl silicone, trifluoropropylmethyl silicone, colloidal silica, polyalkyl acrylate, polyalkyl methacrylate, alcohol ethoxy / propoxylate, fatty acid ethoxy / propoxylate, and sorbitan partial fatty acid ester. Etc. (E8) The preferable compounding quantity of a component is about 1-1000 mass ppm with respect to a lubricous base material.
[0050]
Examples of the solid lubricant of component (E9) include graphite, molybdenum disulfide, polytetrafluoroethylene, fatty acid alkaline earth metal salt, mica, cadmium dichloride, cadmium diiodide, calcium fluoride, lead iodide, Examples include lead oxide, titanium carbide, titanium nitride, aluminum silicate, antimony oxide, cerium fluoride, polyethylene, diamond powder, silicon nitride, boron nitride fluorocarbon, and melamine isocyanurate. The preferable compounding amount of the component (E9) is about 0.005 to 2% by mass with respect to the lubricating base material. If the amount is less than 0.005% by mass, the effect of addition cannot be obtained. If the amount exceeds 2% by mass, the fluidity of the engine oil may be adversely affected.
[0051]
Each component of the above (E1)-(E9) can mix | blend 1 type (s) or 2 or more types suitably. Especially, it is preferable to mix | blend the metal type antiwear agent which does not contain (E3) phosphorus atom and a sulfur atom.
The sulfated ash content in the engine oil composition of the present invention is preferably 1.0% by mass or less, more preferably 0.8% by mass or less, and 0.6% by mass or less. Is most preferred. This is because if the amount of sulfated ash exceeds 1.0% by mass, the particulate filter is likely to be clogged. The amount of sulfated ash can be measured by the method described in JIS K-2272 (crude oil and petroleum products—ash and sulfated ash test method).
The engine oil composition of the present invention can be used as an engine oil for all kinds of engines, and since the phosphorus content and sulfur content are low, the activity of the exhaust gas purification catalyst is lowered and the particulate filter is clogged. Hateful.
[0052]
【Example】
Hereinafter, the present invention will be described more specifically with reference to examples. In the following examples,% is based on mass unless otherwise specified.
Each test oil of Examples 1-12 and Comparative Examples 1-13 was prepared with the composition shown in Table 1 using the following as each component. The analytical values of the sulfur content, phosphorus content and sulfated ash content of each test oil are shown in Table 2.
[0053]
<Lubricating base oil>
(Base oil 1)
Mineral oil based high VI oil. Kinematic viscosity 4.1mm2/ S (100 ° C.), 18.3 mm2/ S (40 ° C.), viscosity index (VI) = 126, sulfur content 30 mass ppm.
(Base oil 2)
Solvent refined mineral oil. Kinematic viscosity 4.2mm2/ S (100 ° C), 20.8mm2/ S (40 ° C.), viscosity index (VI) = 108, sulfur content 5000 mass ppm.
[0054]
<A component: Zinc dithiophosphate>
(A1)
In the general formula (1), R1= R2= Zinc dithiophosphate in which 1,3-dimethylbutyl group, neutral salt / basic salt = 95/5. Phosphorus content 9.4%.
(A2)
In the general formula (1), R1= R2= Zinc dithiophosphate in which 2-ethylhexyl group, neutral salt / basic salt = 95/5. Phosphorus content 8.0%.
[0055]
<B component: nitrogen-containing compound>
(B1)
N-oleyl diethanolamine.
(B2)
Palm oil fatty acid diethanolamide.
(B3)
N- (2-hydroxyhexadecanyl) diethanolamine.
(B4)
N- (2-hydroxyoctadecanyl) monoethanolamine.
(B5)
N-tallow alkyl-N, N ', N'-tri (hydroxyethyl) propylenediamine.
[0056]
<C component: antioxidant>
(C1)
4,4'-butylidenebis (2,6-di-t-butylphenol).
(C2)
Di (p-octylphenyl) amine.
[0057]
<D component: Lubricating oil additive containing phosphorus atom or sulfur atom>
(D1)
Tricresyl phosphate. Phosphorus content 8.4%.
(D2)
Sulfurized lard. Sulfur content 15%.
(D3)
Calcium sulfonate. TBN 300 mg KOH / g, sulfur content 1.6%.
(D4)
Sulfurized oxymolybdenum bis (2-ethylhexyl) dithiocarbamate (sulfur content 18%, molybdenum content 20%).
[0058]
<E component: other components>
(E1)
Calcium salicylate. TBN 280 mg KOH / g.
(E2)
An amine salt of molybdenum oxide obtained by reacting 2 mol of ditridecylamine and 1 mol of molybdenum trioxide according to the method described in Example 1 of JP-A-61-285293. Molybdenum content 11%.
(E3)
According to the method described in Example V of JP-A No. 62-108891, obtained by using 1 mol of coconut oil, 1.8 mol of diethanolamine and 1.3 mol of molybdenum trioxide. And a mixture of molybdenum glycerin monococonut oil carboxylic acid ester complex. Molybdenum content 6%.
(E4)
Glycerin monooleate.
(E5)
Viscosity index improver, boron-modified alkenyl succinic acid bisimide, rust preventive, etc.
[0059]
[Table 1]
[0060]
[Table 2]
[0061]
<Abrasion resistance test>
Using a shell type high-speed four-ball tester, each test oil before oxidative deterioration was subjected to an abrasion resistance test under the following conditions, and the wear scar diameter of the test ball was measured. The smaller the wear scar diameter, the higher the wear resistance. These results are shown in Table 3.
Rotation speed: 1200rpm
Load: 39N
Measurement temperature: room temperature
Measurement time: 15 minutes
[0062]
<Oxidation stability test (oxidation degradation test)>
In accordance with JIS K-2514 (Lubricating oil-oxidation stability test method), 250 mL of test oil is put into a glass container containing a copper plate and an iron plate as a catalyst, while stirring the test oil so that air is involved at 1300 rpm, The test oil was oxidatively deteriorated by heating at 165.5 ° C. for 1 week. The test oil after oxidative deterioration was also subjected to an abrasion resistance test. In addition, for the test oil before and after oxidative deterioration, the kinematic viscosity (40 ° C.) and the total acid value are measured, and from the results, the viscosity ratio (ratio of kinetic viscosity after oxidative deterioration to kinetic viscosity before oxidative deterioration) and total acid The increase in value (the value obtained by subtracting the total acid value before oxidative degradation from the total acid value after oxidative degradation) was determined. The smaller the difference in wear scar diameter before and after oxidation degradation, the smaller the viscosity ratio, and the smaller the increase in total acid value, the higher the oxidation stability. These results are also shown in Table 3.
[0063]
[Table 3]
[0064]
When the results of Table 3 are summarized, the engine oil of the example of the present invention showed an increase in wear scar diameter of 0.00 to 0.02 mm, whereas the engine oil of the comparative example was 0.00 to 0.05 mm. The wear scar diameter increased.
Further, the viscosity ratio of the engine oil of the example of the present invention is also lower than the viscosity ratio of the engine oil of the comparative example, and the increase in the total acid value of the engine oil of the example of the present invention is also the same as the total acid of the engine oil of the comparative example. Significantly below the increase in price.
From the above, it was found that the engine oil having the composition of the present invention has excellent wear resistance and oxidation stability as compared with the engine oil not having the composition of the present invention.
[0065]
【The invention's effect】
The phosphorus component and sulfur component in the engine oil are said to cause a decrease in activity of the exhaust gas purification catalyst and clogging of the particulate filter. The effect of the present invention is to provide an engine oil composition having excellent wear resistance and oxidation stability while having a low phosphorus content and a low sulfur content.
Claims (4)
で表わされる亜鉛ジチオホスフェートを、リン含量として100〜500質量ppm;
(B)成分として、下記の一般式(2)
で表わされる窒素含有化合物を0.01〜10質量%;
を含有させてなり、且つリン含量が500質量ppm以下、硫黄含量が3000質量ppm以下であるエンジン油組成物。In the lubricating base oil, as the component (A), the following general formula (1)
Zinc dithiophosphate represented by a phosphorus content of 100 to 500 ppm by mass;
As the component (B), the following general formula (2)
0.01 to 10% by mass of a nitrogen-containing compound represented by:
An engine oil composition having a phosphorus content of 500 mass ppm or less and a sulfur content of 3000 mass ppm or less.