JP4238945B2 - Paper additive and paper manufacturing method - Google Patents
Paper additive and paper manufacturing method Download PDFInfo
- Publication number
- JP4238945B2 JP4238945B2 JP01803399A JP1803399A JP4238945B2 JP 4238945 B2 JP4238945 B2 JP 4238945B2 JP 01803399 A JP01803399 A JP 01803399A JP 1803399 A JP1803399 A JP 1803399A JP 4238945 B2 JP4238945 B2 JP 4238945B2
- Authority
- JP
- Japan
- Prior art keywords
- mol
- papermaking
- anionic
- additive
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】
【発明の属する技術分野】
本発明は、製紙用添加剤および当該製紙用添加剤を用いた紙の製造方法に関する。本発明の製紙用添加剤は抄紙用瀘水剤、紙力増強剤、填料歩留剤、サイズ定着剤等として利用できる。特に、本発明の製紙用添加剤は、抄紙用瀘水剤、紙力増強剤として有用である。
【０００２】
【従来の技術】
従来より、ポリアクリルアミドは、通常、分子量が大きい程良好な瀘水性や紙力増強効果等の製紙用添加剤としての効果を示すことが知られている。しかし、高分子量型のポリアクリルアミドを用いた製紙用添加剤は、非常に高粘度になるために、低分子量型のポリアクリルアミドに比べて作業性が劣っている。一方、低分子量型のものは、作業能率の点では問題はないが、高分子量型と比較して製紙用添加剤としての効果の点で十分でない。これらの問題を改善するために、比較的低粘度のアニオン性ポリアクリルアミドとホフマン変性やマンニッヒ変性をしたカチオン性ポリアクリルアミドを予め混合してパルプスラリーに添加する処方も検討されている。かかる混合処方によれば、ｐＨ４．５〜５．５の範囲で作業能率を低下させることなく、製紙用添加剤としての効果をある程度は発現できる。
【０００３】
しかし、かかる混合処方によっても、製紙用添加剤としての効果、特に瀘水性、紙力強度が十分とはいえなかった。また、かかる混合処方により製紙用添加剤としての効果を向上すべくポリアクリルアミドの分子量を高めた場合には、瀘水性は向上するが地合乱れを誘発し、十分な紙力効果が得られない。さらには、近年、古紙の使用比率が増加していることや、環境対策の一環で紙の製造プロセスにおけるクローズド化などにより、抄紙ｐＨが高くなる傾向があり、原料に起因する抄紙ｐＨの変動が大きく、前記混合処方では安定な操業が困難であった。
【０００４】
【発明が解決しようとする課題】
本発明は、瀘水性、紙力強度等の製紙用添加剤としての諸効果に優れ、しかも抄紙ｐＨの変動に対しても安定して効果を発揮し、操業性に優れる製紙用添加剤および当該製紙用添加剤を用いた紙の製造方法を提供することを目的とする。
【０００５】
【課題を解決するための手段】
本発明者等は、前記課題を解決すべく鋭意検討を重ねた結果、（Ａ）アニオン性または両性のポリアクリルアミドと（Ｂ）アミジン環構造を繰り返し単位として有するカチオン性高分子を含有してなる水性混合物を製紙用添加剤として使用することにより、前記目的を達成できることを見出し、本発明を解決するに至った。
【０００６】
すなわち、本発明は、（Ａ）重量平均分子量３０万〜４００万のアニオン性または両性のポリアクリルアミド、および（Ｂ）１ｍｏｌ／ｌの食塩水中０．１ｇ／ｄｌの溶液として、２５℃で測定した還元粘度の値が０．１〜１０ｄｌ／ｇであるアミジン環構造を繰り返し単位として有するカチオン性高分子を含有し、（Ａ）／（Ｂ）の使用量が、固形分重量比で、９９．５／０．５〜５０／５０である水性混合物からなる製紙用添加剤；さらにはパルプスラリーに、前記製紙用添加剤を添加し、抄造することを特徴とする紙の製造方法、に関する。
【０００７】
【発明の実施の形態】
本発明において用いる（Ａ）アニオン性または両性のポリアクリルアミドは、たとえば、（ａ）（メタ）アクリルアミドおよび（ｂ）アニオン性ビニルモノマー、さらには（ｃ）カチオン性ビニルモノマーを共重合することにより得られる。すなわち、（Ａ）アニオン性ポリアクリルアミドは、（ａ）（メタ）アクリルアミドおよび（ｂ）アニオン性ビニルモノマーを、（Ａ）両性のポリアクリルアミドは、（ａ）（メタ）アクリルアミド、（ｂ）アニオン性ビニルモノマーおよび（ｃ）カチオン性ビニルモノマー共重合することにより得られる。
【０００８】
（ａ）（メタ）アクリルアミドとは、アクリルアミドまたはメタクリルアミドのことを意味し、これらは単独使用または併用できる。経済性の面からはアクリルアミドを単独使用するのがよい。なお、以下本発明において（メタ）とは同様の意味である。（ａ）成分の使用量は、（Ａ）アニオン性または両性のポリアクリルアミドを構成するモノマーの総モル和に対し、通常、６０モル％程度、好ましくは６５モル％である。（ａ）成分が６０モル％に満たない場合には、製紙用添加剤としての十分な紙力効果等を得難い。なお、（ａ）成分の使用量は（ａ）成分以外の成分の残部である。
【０００９】
（ｂ）アニオン性ビニルモノマーとしては、たとえば（メタ）アクリル酸、クロトン酸、（メタ）アリルカルボン酸等のα，β−不飽和一塩基酸酸；マレイン酸、フマール酸、イタコン酸、ムコン酸等のα，β−不飽和二塩基酸酸；ビニルスルホン酸、スチレンスルホン酸、２−アクリルアミド−２−メチルプロパンスルホン酸、（メタ）アリルスルホン酸などの有機スルホン酸；またはこれら各種有機酸のナトリウム塩、カリウム塩等のアルカリ金属塩、アンモニウム塩等があげられる。これらアニオン性ビニルモノマーは１種または２種以上を特に制限なく使用できる。特に、アニオン性ビニルモノマーの１種として、（メタ）アリル基を有するモノマー、殊に（メタ）アリルスルホン酸またはその塩を使用するのが、得られるイオン性ポリアクリルアミドが高分子量化する点で好ましい。また、α，β−不飽和一塩基酸酸、α，β−不飽和二塩基酸酸およびこれらの塩から選ばれる少なくとも１種を使用するのが好ましい。殊にイタコン酸を使用するのが好ましい。なかでも、（メタ）アクリル酸および／またはイタコン酸と（メタ）アリルスルホン酸またはその塩を組み合わせる場合が好ましい。
【００１０】
（ｂ）アニオン性ビニルモノマーの使用量は、（Ａ）アニオン性または両性ポリアクリルアミドを構成するモノマーの総モル和に対し、通常、１〜４０モル％程度、好ましくは３〜４０モル％、より好ましくは３〜３０モル％である。
【００１１】
（ｃ）カチオン性ビニルモノマーとしては、たとえばジメチルアミノエチル（メタ）アクリレート、ジエチルアミノエチル（メタ）アクリレート、ジメチルアミノプロピル（メタ）アクリルアミド、ジエチルアミノプロピル（メタ）アクリルアミドなどの第三級アミノ基を有するビニルモノマーまたはそれらの塩酸、硫酸、酢酸などの無機酸もしくは有機酸の塩類、または該第三級アミノ基含有ビニルモノマーとメチルクロライド、ベンジルクロライド、ジメチル硫酸、エピクロルヒドリンなどの四級化剤との反応によって得られる第四級アンモニウム塩を含有するビニルモノマー等があげられる。
【００１２】
（ｃ）カチオン性ビニルモノマーの使用量は、（Ａ）両性ポリアクリルアミド中のイオン性官能基の当量比（カチオン性基／アニオン性基）が２以下となるような割合で用いるのが好ましい。かかる当量比は（カチオン性基／アニオン性基）は、（Ａ）両性ポリアクリルアミドと、後述する（Ｂ）アミジン環構造を有するカチオン性高分子から得られる水性混合物が、充分な製紙用添加剤としての効果を発現するうえで好ましい。特に前記当量比（カチオン性基／アニオン性基）が１．５以下の範囲になるような割合で用いるのが好ましい。
【００１３】
なお、（Ａ）両性ポリアクリルアミドへ、カチオン性基を付与する手段は、前記のように（ｃ）カチオン性ビニルモノマーを共重合することができる他に、アニオン性アクリルアミドにホルマリン及び第２級アミンを反応させるマンニッヒ変性や、次亜ハロゲン酸塩を反応させるホフマン反応によっても、カチオン性基を導入することができる。このような変性によりカチオン性基を導入する場合にも、（Ａ）イオン性ポリアクリルアミド中の、イオン性官能基の当量比（カチオン性基／アニオン性基）は前記と同様の範囲に調整するのが好ましい。
【００１４】
本発明の（Ａ）アニオン性または両性ポリアクリルアミドは、前記（ａ）成分、（ｂ）成分、（ｃ）成分の他に、一般式（１）：ＣＨ２＝Ｃ（Ｒ１）−ＣＯＮＲ２（Ｒ３）（Ｒ１は水素原子またはメチル基、Ｒ２は水素原子または炭素数１〜４の直鎖もしくは分岐鎖のアルキル基、Ｒ３は炭素数１〜４の直鎖または分岐鎖のアルキル基）で表されるＮ−置換（メタ）アクリルアミド類および／または多官能性モノマーを構成モノマーとして含むことができる。
【００１５】
一般式（１）で表されるＮ−置換（メタ）アクリルアミド類は、Ｎ−アルキル基中のメチル基またはメチレン性基が連鎖移動点として作用し、ポリマーに多くの分岐構造を導入し、ゲル化を伴わない分岐ポリマーが得られる。前記一般式（１）中のＲ２またはＲ３における炭素数１〜４の直鎖または分岐鎖のアルキル基としては、たとえば、メチル基、エチル基、イソプロピル基、ｔ−ブチル基等があげられ、Ｎ−置換（メタ）アクリルアミド類の具体例としては、Ｎ，Ｎ−ジメチル（メタ）アクリルアミド、Ｎ−イソプロピル（メタ）アクリルアミド、Ｎ−メチル（メタ）アクリルアミド、Ｎ−エチル（メタ）アクリルアミド、Ｎ−イソプロピル（メタ）アクリルアミドおよびＮ−ｔ−ブチル（メタ）アクリルアミドがあげられる。これらのなかでも共重合性、連鎖移動性の点でＮ，Ｎ−ジメチルアクリルアミドが好ましい。
【００１６】
また、多官能性モノマーを使用することによっても、架橋構造を（Ａ）アニオン性または両性ポリアクリルアミドに付与できる。多官能性モノマ−としては、エチレングリコールジ（メタ）アクリレート、ジエチレングリコールジ（メタ）アクリレート、トリエチレングリコールジ（メタ）アクリレート等のジ（メタ）アクリレート類、メチレンビス（メタ）アクリルアミド、エチレンビス（メタ）アクリルアミド、ヘキサメチレンビス（メタ）アクリルアミド等のビス（メタ）アクリルアミド類、アジピン酸ジビニル、セバシン酸ジビニル等のジビニルエステル類、アリルメタクリレート、ジアリルアミン、ジアリルジメチルアンモニウム、ジアリルフタレート、ジアリルクロレンデート、ジビニルベンゼン、Ｎ，Ｎ−ジアリルアクリルアミド等の２官能性ビニルモノマー、１，３，５−トリアクリロイルヘキサヒドロ−Ｓ−トリアジン、トリアリルイソシアヌレート、トリアリルアミン、トリアリルトリメリテート等の３官能性ビニルモノマー、テトラメチロールメタンテトラアクリレート、テトラアリルピロメリテート、Ｎ，Ｎ，Ｎ′，Ｎ′−テトラアリル−１，４−ジアミノブタン、テトラアリルアミン塩、テトラアリルオキシエタン等の4官能性ビニルモノマー、その他にＮ−メチロールアクリルアミド等があげられる。これら多官能性モノマーのなかでも１，３，５−トリアクリロイルヘキサヒドロ−Ｓ−トリアジン、トリアリルイソシアヌレート等が好ましい。
【００１７】
一般式（１）で表されるＮ−置換（メタ）アクリルアミド類および／または多官能性モノマーの使用量は、（Ａ）アニオン性または両性のポリアクリルアミドを構成するモノマーの総モル和に対し、通常、１０モル％程度以下、さらには５モル％以下である。一般式（１）で表されるＮ−置換（メタ）アクリルアミド類の機能を発揮するには、０．１モル％以上、より好ましくは０．５モル％以上を使用する。
【００１８】
さらに、（Ａ）アニオン性または両性のポリアクリルアミドには、疎水性を付与するために、前記アニオン性ビニルモノマーのアルキルエステル（アルキル基の炭素数１〜８）、アクリロニトリル、スチレン類、酢酸ビニル、メチルビニルエーテルなどのノニオン性ビニルモノマーを使用することもできる。ノニオン性ビニルモノマーを使用する場合、その使用量は、（Ａ）アニオン性または両性のポリアクリルアミドを構成するモノマーの総モル和に対し、通常、３０モル％程度以下、好ましくは２０モル％以下である。
【００１９】
（Ａ）アニオン性または両性のポリアクリルアミドの合成は、従来公知の各種方法により行うことができる。例えば、所定の反応容器に前記各種モノマーおよび水を仕込み、ラジカル重合開始剤を加え、撹拌下、加温することにより得られる。反応温度は、通常５０〜１００℃程度、反応時間は１〜５時間程度である。反応濃度（モノマー濃度）は、通常１０〜４０重量％程度で行うことができ、高濃度においても重合できる。その他、モノマーの仕込み方法は同時重合、連続滴下重合等の従来公知の各種方法により行うことができる。ラジカル重合開始剤としては、過硫酸カリウム、過硫酸アンモニウム等の過硫酸塩、またはこれらと亜硫酸水素ナトリウムのごとき還元剤とを組み合わせた形のレドックス系重合開始剤等の通常のラジカル重合開始剤を使用できる。また、前記ラジカル重合開始剤には、アゾ系開始剤を用いてもよい。ラジカル重合開始剤の使用量は、モノマーの総重量和の０．０５〜２重量％程度、好ましくは０．１〜０．５重量％である。
【００２０】
（Ａ）アニオン性または両性のポリアクリルアミドの重量平均分子量は、作業性及び経済性を考慮して３０万〜４００万に調製する。好ましくは、１００万〜４００万である。重量平均分子量が３０万未満では紙力効果が不十分であり、他方、４００万を超えるときは作業性の点で好ましくない。また、（Ａ）アニオン性または両性のポリアクリルアミドの粘度は、取扱性の点から、通常、１００００ｃｐｓ程度（２５℃）以下の性状で使用するのがよい。なお、本発明の製紙用添加剤は、固形分濃度１０〜４０重量％に調整される。通常は、固形分濃度を３０重量％以下とするのが好ましい。
【００２１】
本発明において用いる（Ｂ）アミジン環構造を繰り返し単位として有するカチオン性高分子は、高分子の繰り返し単位として、アミジン環構造を有する各種のものを使用できる。
【００２２】
アミジン環構造の繰り返し単位としては、たとえば、下記一般式（２）、一般式（３）、一般式（４）、
【００２３】
【化４】
【化５】
【化６】
（式中Ｒ４、Ｒ５は水素原子またはメチル基を、Ｘ−は陰イオンをそれぞれ表す。）で表される繰り返し単位があげられる。
【００２７】
本発明の（Ｂ）カチオン性高分子は、これら一般式（２）、一般式（３）、一般式（４）で表されるアミジン環構造の繰り返し単位を、（Ｂ）カチオン性高分子の繰り返し単位の、２０〜９０モル％程度含有するものが好ましい。（Ｂ）カチオン性高分子の、パルプに対する凝集作用の効果を高める場合には、分子中に占めるアミジン環構造単位の比率が多い方が性能は優れるため、前記アミジン環構造の繰り返し単位は、３０モル％以上、さらには５０モル％とするのが好ましい。また製造の容易さ等を考慮すれば、前記アミジン環構造の繰り返し単位は、８５モル％以下、さらには８０モル％以下とするのが好ましい。
【００２８】
これらアミジン環構造の繰り返し単位を形成する方法は特に限定されるものではないが、一般的に、前記一般式（２）または（３）で表されるアミジン環構造の繰り返し単位は、一級アミノ基または変換反応により一級アミノ基が生成しうる置換アミノ基を有するエチレン性不飽和モノマー（Ｘ）と（メタ）アクリロニトリル等のニトリル類との共重合体を製造し、更に、該共重合体中のシアノ基と一級アミノ基を反応させてアミジン化することにより形成される。
【００２９】
なお、前記エチレン性不飽和モノマー（Ｘ）としては、たとえば、一般式（５）ＣＨ２＝ＣＲ６ＮＨＣＯＲ７（Ｒ６は水素原子またはメチル基を、Ｒ７は水素原子または炭素数１〜４のアルキル基を表わす。）で表されるエチレン性不飽和モノマーがあげられる。一般式（５）で表されるエチレン性不飽和モノマーに由来する置換アミノ基は、共重合体中において、加水分解あるいは加アルコール分解により容易に一級アミノ基に変換される。一般式（５）で表されるエチレン性不飽和モノマーとしては、たとえば、Ｎ−ビニルホルムアミド（Ｒ６＝Ｈ、Ｒ７＝Ｈ）、Ｎ−ビニルアセトアミド（Ｒ６＝Ｈ、Ｒ７＝ＣＨ３）等が例示される。
【００３０】
前記一般式（２）または（３）で表されるアミジン環構造の繰り返し単位を形成させる場合、エチレン性不飽和モノマー（Ｘ）とニトリル類との重合モル比は、（Ｂ）カチオン性高分子中に占めるアミジン環構造単位の比率が多い方が製紙用添加剤としての性能は優れることから通常２０：８０〜８０：２０、特に４０：６０〜６０：４０とするのが好ましい。所望ならばこの範囲外のモル比、例えば、更にエチレン性不飽和モノマーの比率の大きい重合モル比を採用することもできる。
【００３１】
エチレン性不飽和モノマー（Ｘ）とニトリル類との共重合の方法としては、通常のラジカル重合法が用いられ、塊状重合、水溶液沈殿重合、懸濁重合、乳化重合等のいずれも用いることができる。溶媒中で重合させる場合、原料モノマー濃度が通常５〜８０重量％、好ましくは２０〜６０重量％で実施される。重合開始剤には、一般的なラジカル重合開始剤を用いることができるが、アゾ化合物が好ましく、２，２′−アゾビス−２−アミジノプロパンの塩酸塩等が例示される。また、重合反応は、一般に、不活性ガス気流下、３０〜１００℃の温度で実施される。得られた共重合体は、そのままの状態あるいは希釈して、即ち、溶液状もしくは懸濁状でアミジン化反応に供することができる。また、公知の方法で脱溶媒、乾燥し、共重合体を固体として分離した後、固体状でアミジン化反応に供することもできる。なお、得られる重合体は、ラジカル重合開始剤の使用量、反応温度等を調節することにより適宜、所望の分子量のものを得ることができる。
【００３２】
アミジン化反応は、共重合体の置換アミノ基を一級アミノ基に変換し、次いで、生成した一級アミノ基と隣接するシアノ基と反応させてアミジン環構造を生成させる２段階反応、または該共重合体を、強酸または強塩基の存在下、水またはアルコール溶液中で加熱してアミジン環構造を生成させる一段階反応により行う。アミジン化反応は一段階反応が好ましい。一段階反応は、具体的には、例えば、共重合体に対し、その置換アミノ基に対して通常０．９〜５倍、好ましくは１〜３倍当量の強酸、好ましくは塩酸を加え、通常８０〜１５０℃、好ましくは９０〜１２０℃の温度で、通常０．５〜２０時間加熱することにより行う。一般に置換アミノ基に対する強酸の当量比が大きいほど、かつ、反応温度が高いほど、アミジン化が進行する。また、アミジン化に際しては反応に供する共重合体に対し、通常１０重量％以上、好ましくは２０重量％以上の水を反応系に存在させる。
【００３３】
このようにして得られる（Ｂ）カチオン性高分子は、前記一般式（１）および／または（２）で表されるアミジン環構造の繰り返し単位を通常２０〜９０モル％程度含有する他、前記エチレン性不飽和モノマー（Ｘ）に由来する繰り返し単位を０〜２モル％程度、前記ニトリル類に由来する繰り返し単位を０〜７０モル％程度、エチレン性不飽和モノマー（Ｘ）の変換物（一級アミノ基）に由来する繰り返し単位を０〜７０モル％程度含有している。
【００３４】
かかる（Ｂ）カチオン性高分子中、アミジン環構造の繰り返し単位の多い方が一般に製紙用添加剤としての性能が優れているため、前記一般式（１）および／または（２）で表されるアミジン環構造の繰り返し単位は、ニトリル類の繰り返し単位の０．５〜１０倍、好ましくは２〜５倍とするのが好ましい。
【００３５】
また、一級アミノ基に由来する繰り返し単位はカチオン性であり、アミジン環構造の繰り返し単位と同じく濾水性向上剤としての性能に有効に寄与していると考えられる。したがって、一級アミノ基に由来する繰り返し単位は５〜６０モル％であるのが好ましい。また、一般式（１）および／または（２）で表されるアミジン環構造の繰り返し単位、さらには一級アミノ基に由来する繰り返し単位を含めたカチオン単位の合計は一般に４０モル％以上、好ましくは６０〜９５モル％である。ただし、一般式（１）および／または（２）で表されるアミジン環構造の繰り返し単位が一級アミノ基に由来する繰り返し単位よりも製紙用添加剤の性能により有効に寄与すると考えられるため、前記一般式（１）および／または（２）で表されるアミジン環構造の繰り返し単位は、一級アミノ基に由来する繰り返し単位の０．５〜１０倍、好ましくは２〜５倍とするのが好ましい。
【００３６】
なお、（Ｂ）カチオン性高分子は、一般にそのままでは保存安定性が悪いので、強酸を添加してアミジン環構造および１級アミノ基のカチオン単位は完全に中和しておくことが好ましい。
【００３７】
また、アミジン環構造の繰り返し単位として前記一般式（４）で表される繰り返し単位を有する（Ｂ）カチオン性高分子は、前記エチレン性不飽和モノマー（Ｘ）を重合した後、当該モノマーの置換アミノ基の一部を一級アミノ基に変換するとともに、当該置換アミノ基と変換反応により生成した一級アミノ基とのアミジン化により形成される。アミジン化条件は、溶媒中で通常５０〜１１０℃程度、１〜７２時間程度加熱する。また、反応は通常撹拌下で行い、通常は常圧下で良いが、必要に応じて加圧しても良い。なお、反応温度が５０℃未満では反応速度が遅すぎて効率的ではなく、一方、１１０℃を越えると副反応として架橋化反応などが起こりやすくなり、不溶化する恐れがあるので好ましくない。一般式（４）で表されるアミジン環構造の繰り返し単位は２０モル％以上であるのが好ましい。
【００３８】
また、本発明の（Ｂ）カチオン性高分子は、アニオン性ビニルモノマーに由来する繰り返し単位を含有していてもよい。一般的には、エチレン性不飽和モノマー（Ｘ）等を重合するにあたり、アニオン性ビニルモノマーを共重合させる。アニオン性ビニルモノマーとしては、（Ａ）で使用するものと同様のものがあげられる。アニオン性ビニルモノマーの使用量は、全構成モノマーの通常０〜２０モル％程度が好適であるが、３〜１５モル％がより好ましい。なお、（Ｂ）カチオン性高分子には、（メタ）アクリロニトリルに由来する繰り返し単位の加水分解によって、（メタ）アクリル酸に由来する繰り返し単位が、一般的には０〜５モル生成しうる。
【００３９】
さらに、本発明の（Ｂ）カチオン性高分子には、前述の繰り返し単位の外に更に（メタ）アクリルアミドに由来する繰り返し単位が含まれていても良い。また、（メタ）アクリルアミドに由来する繰り返し単位と（メタ）アクリル酸に由来する繰り返し単位が反応してラクタム環状を一部形成した繰り返し単位が含まれていても良い。
【００４０】
本発明の（Ｂ）カチオン性高分子は、１ｍｏｌ／ｌの食塩水中０．１ｇ／ｄｌの溶液として、２５℃で測定した還元粘度の値が０．１〜１０ｄｌ／ｇである。好ましくは１〜１０ｄｌ／ｇ、更に好ましくは０．５〜４ｄｌ／ｇである。
【００４１】
本発明の製紙用添加剤は、（Ａ）アニオン性または両性のポリアクリルアミドと前記（Ｂ）カチオン性高分子からなる水性混合物である。かかる水性混合物は、（Ａ）アニオン性または両性のポリアクリルアミドと（Ｂ）カチオン性高分子が予め混合されることで、両者が何らかの相互作用を起こし、パルプへの定着率が向上し、より高い瀘水性および紙力効果等を発現する。これらの使用割合は、通常は、固形分重量比で、（Ａ）／（Ｂ）が９９．５／０．５〜５０／５０、好ましくは９９／１〜７０／３０の範囲とするのがよい。
【００４２】
前記水性混合物からなる製紙用添加剤は、パルプスラリーに添加された後、抄造され紙が製造される。抄造は各種の手段を採用できるが、製紙用添加剤のパルプスラリーへの添加は、パルプスラリーに硫酸バンドを添加した後が好ましく、硫酸バンドの添加からある程度時間をあけて添加するのがより好ましい。また生じたフロックに無用のシェアーをかけることなく、直ちに抄造するするのが望ましいため、抄紙用ワイヤー部に近い場所で製紙用添加剤を添加するのが好ましい。特に、ファンポンプサクション口で添加するのが瀘水性および紙力効果等が向上するので好ましい。パルプスラリーのｐＨは通常４〜９の幅広い範囲から選択できる。なお、製紙用添加剤である水性混合物には、必要により水、アルコール類等により適宜に希釈してもよい。また、水性混合物の調製は抄紙系への添加の直前に行ってもよく、別途混合しておいたものを抄紙系に添加してもよい。調製した水性混合物はそのまま流通過程においてもさしつかえない
【００４３】
製紙用添加剤の使用量は、通常と同様でよく、固形分重量比で、パルプに対して、０．００５〜３重量％程度、好ましくは０．０１〜１重量％程度とするのがよい。また、硫酸バンドは、パルプ固形分に対し通常、０．５〜１０重量％である。
【００４４】
かかる抄造工程において、かかる製紙用添加剤は、作業性を低下させることなく、瀘水性および紙力効果等の製紙用添加剤としての効果を向上できる。特に、（Ａ）両性のポリアクリルアミドを使用した場合には、抄紙ｐＨの影響を受けることなく、酸性から中性域での抄造において、安定して効果を発揮することができる。
【００４５】
【発明の効果】
本発明の製紙用添加剤は、瀘水性、紙力強度等の製紙用添加剤としての諸効果に優れ、しかも抄紙ｐＨの範囲が広く、操業性に優れる。特に抄紙ｐＨが酸性から中性の領域において優れている。
【００４６】
【実施例】
以下、実施例及び比較例を挙げて本発明を詳細に説明するが、本発明はこれら各例に限定されるものではない。尚、各例中、部及び％は特記しない限りすべて重量基準である。
【００４７】
製造例１（アニオン性ポリアクリルアミドの製造）
攪拌機、温度計、還流冷却管および窒素ガス導入管を備えた四つ口フラスコに、粉末アクリルアミド３００．２部（モノマーの総モル和に対し、８８モル％、以下同様）、８０％アクリル酸水溶液３８．９部（９モル％）、イタコン酸６．２部（１モル％）、メタアリルスルホン酸ソーダ７．６部（１モル％）、ジメチルアクリルアミド４．８部（１モル％）およびイオン交換水１３００部（モノマー濃度２１％）を仕込み、窒素ガスを通じて反応系の酸素を除去した。系内を４０℃にし攪拌下に重合開始剤として５％過硫酸アンモニウム水溶液７部および５％亜硫酸水素ナトリウム水溶液３部を投入した。９０℃まで昇温した後、２時間保温した。重合終了後、イオン交換水７０部（固形分濃度２０％に調整）を投入し、ｐＨ４．０、固形分２０．２％、粘度（２５℃）が６８００ｃｐｓ、重量平均分子量が２４０万の共重合体水溶液を得た。以下、この水溶液をＡ−１とする。なお、重量平均分子量の測定は、低角度光散乱法（ＧＰＣ−ＬＡＬＬＳ（東ソー（株）製））により、ｐＨ４．２の酢酸と酢酸ソーダを含む水溶液を移動層として用い、試料濃度０．０１２５％で測定した。
【００４８】
製造例２（両性ポリアクリルアミドの製造）
攪拌機、温度計、還流冷却管および窒素ガス導入管を備えた四つ口フラスコに、粉末アクリルアミド２８４．５部（モノマーの総モル和に対し、８５モル％、以下同様）、６２．５％硫酸９．９部、ジメチルアミノエチルメタクリレート２２．２部（３モル％）、８０％アクリル酸水溶液４２．４部（１０モル％）、ジメチルアクリルアミド９．３部（２モル％）およびイオン交換水１３００部（モノマー濃度２１％）を仕込み、窒素ガスを通じて反応系の酸素を除去した。系内を４０℃にし攪拌下に重合開始剤として５％過硫酸アンモニウム水溶液７部および５％亜硫酸水素ナトリウム水溶液３部を投入した。９０℃まで昇温した後、２時間保温した。重合終了後、イオン交換水１００部（固形分濃度２０％に調整）を投入し、ｐＨ４．１、固形分２０．１％、粘度（２５℃）が４６００ｃｐｓ、重量平均分子量が１９０万の共重合体水溶液を得た。以下、この水溶液をＡ−２とする。
【００４９】
製造例３（両性ポリアクリルアミドの製造）
攪拌機、温度計、還流冷却管および窒素ガス導入管を備えた四つ口フラスコに、粉末アクリルアミド２９４．４部（モノマーの総モル和に対し、８９．５モル％、以下同様）、６２．５％硫酸６．５部、ジメチルアミノエチルメタクリレート１４．５部（２モル％）、８０％アクリル酸水溶液１６．７部（４モル％）イタコン酸１２．０部（２モル％）、メタアリルスルホン酸ソーダ１１．０部（１．５モル％）、ジメチルアクリルアミド４．６部（１モル％）およびイオン交換水１３００部（モノマー濃度２１％）を仕込み、窒素ガスを通じて反応系の酸素を除去した。系内を４０℃にし攪拌下に重合開始剤として５％過硫酸アンモニウム水溶液９．８部および５％亜硫酸水素ナトリウム水溶液４部を投入した。９０℃まで昇温した後、２時間保温した。重合終了後、イオン交換水１０５部（固形分濃度２０％に調整）を投入し、ｐＨ３．９、固形分２０．１％、粘度（２５℃）が８５００ｃｐｓ、重量平均分子量が３００万の共重合体水溶液を得た。以下、この水溶液をＡ−３とする。
【００５０】
製造例４（両性ポリアクリルアミドの製造）
攪拌機、温度計、還流冷却管および窒素ガス導入管を備えた四つ口フラスコに、粉末アクリルアミド２８８．７部（モノマーの総モル和に対し、８９．５モル％、以下同様）、６２．５％硫酸１９．２部、ジメチルアミノエチルメタクリレート４２．８部（６モル％）、８０％アクリル酸水溶液１０．２部（２．５モル％）イタコン酸５．９部（１モル％）、ジメチルアクリルアミド４．５部（１モル％）およびイオン交換水１３００部（モノマー濃度２１％）を仕込み、窒素ガスを通じて反応系の酸素を除去した。系内を４０℃にし攪拌下に重合開始剤として５％過硫酸アンモニウム水溶液９．８部および５％亜硫酸水素ナトリウム水溶液４部を投入した。９０℃まで昇温した後、２時間保温した。重合終了後、イオン交換水１０５部（固形分濃度２０％に調整）を投入し、ｐＨ３．９、固形分２０．１％、粘度（２５℃）が５５００ｃｐｓ、重量平均分子量が２２０万の共重合体水溶液を得た。以下、この水溶液をＡ−４とする。
【００５１】
製造例５（両性ポリアクリルアミドの製造）
攪拌機、温度計、還流冷却管および窒素ガス導入管を備えた四つ口フラスコに、５０％アクリルアミド１６２部（モノマーの総モル和に対し、９５モル％、以下同様）、８０％アクリル酸水溶液５．４部（５モル％）、イオン交換水７３７部およびイソプロピルアルコール２．５部を仕込み、４８％カセイソーダでｐＨを５〜５．５に調整し、窒素ガスを通じて反応系の酸素を除去した。攪拌下に重合開始剤として５％過硫酸アンモニウム水溶液２．６部および５％亜硫酸水素ナトリウム水溶液１．１部を投入した後、室温から８０℃まで昇温し、３時間保温した。これを５０℃まで冷却した後、５０％ジメチルアミン水溶液１３．０部と３７％ホルマリン９．８部（アクリルアミド９５モル％の１０％分をマンニッヒ変性）を順に投入し、同温度で１時間保持して、ｐＨ１０．８、固形分１０．４％、粘度（２５℃）が５６００ｃｐｓの重量平均分子量が１００万の両性マンニッヒ変性共重合体の水溶液を得た。以下、この水溶液をＡ−５とする。
【００５２】
製造例６（両性ポリアクリルアミドの製造）
攪拌機、温度計、還流冷却管および窒素ガス導入管を備えた四つ口フラスコに、粉末アクリルアミド２３０．８部（モノマーの総モル和に対し、７８モル％、以下同様）、６２．５％硫酸４４．０部、ジメチルアミノエチルメタクリレート９８．１部（１５モル％）、８０％アクリル酸水溶液１１．３部（３モル％）イタコン酸５．４部（１モル％）、メタアリルスルホン酸ソーダ６．６部（１モル％）、ジメチルアクリルアミド４．１部（１モル％）およびイオン交換水１３００部（モノマー濃度２１％）を仕込み、窒素ガスを通じて反応系の酸素を除去した。系内を４０℃にし攪拌下に重合開始剤として５％過硫酸アンモニウム水溶液１２部および５％亜硫酸水素ナトリウム水溶液３部５部を投入した。９０℃まで昇温した後、２時間保温した。重合終了後、イオン交換水１００部（固形分濃度２０％に調整）を投入し、ｐＨ３．９、固形分２０．１％、粘度（２５℃）が６０００ｃｐｓ、重量平均分子量が２３０万の共重合体水溶液を得た。以下、この水溶液をＡ−６とする。
【００５３】
製造例７（両性ポリアクリルアミドの製造）
攪拌機、温度計、還流冷却管および窒素ガス導入管を備えた四つ口フラスコに、５０％アクリルアミド１６２部（モノマーの総モル和に対し、９５モル％、以下同様）、８０％アクリル酸水溶液５．４部（５モル％）、イオン交換水７３７部およびイソプロピルアルコール２．５部を仕込み、４８％カセイソーダでｐＨを５〜５．５に調整し、窒素ガスを通じて反応系の酸素を除去した。攪拌下に重合開始剤として５％過硫酸アンモニウム水溶液２．６部および５％亜硫酸水素ナトリウム水溶液１．１部を投入した後、室温から８０℃まで昇温し、３時間保温した。これを５０℃まで冷却した後、５０％ジメチルアミン水溶液２５．９部と３７％ホルマリン１９．５部（アクリルアミド９５モル％の２０％分をマンニッヒ変性）を順に投入し、同温度で１時間保持して、ｐＨ１０．８、固形分１０．５％、粘度（２５℃）が５３００ｃｐｓの重量平均分子量が１００万の両性マンニッヒ変性共重合体の水溶液を得た。以下、この水溶液をＡ−７とする。
【００５４】
比較製造例１（アニオン性ポリアクリルアミドの製造）
攪拌機、温度計、還流冷却管および窒素ガス導入管を備えた四つ口フラスコに、粉末アクリルアミド１２８部（モノマーの総モル和に対し、９０モル％、以下同様）、８０％アクリル酸水溶液１８部（１０モル％）、イオン交換水５３０部、およびイソプロピルアルコール８部を仕込み、窒素ガスで反応系内の酸素を除去した。次いで、攪拌下、重合開始剤として５％過硫酸アンモニウム水溶液１０部および５％亜硫酸水素ナトリウム水溶液４．１部を投入した後、室温から８０℃まで昇温し、３時間保温した。その後、イオン交換水２４０部を加え、４８％カセイソーダでｐＨを５に調整し、固形分１５．２％、粘度（２５℃）が６５００ｃｐｓ、重量平均分子量が２５万の共重合体水溶液を得た。以下、この水溶液をＣ−１とする。
【００５５】
【表１】
表中、ＡＭ：アクリルアミド、ＤＭ：Ｎ，Ｎ−ジメチルエチルメタクリレート、ＡＡ：アクリル酸、ＩＡ：イタコン酸、ＳＭＡＳ：メタリルスルフォン酸ナトリウム、ＤＭＡＡ：Ｎ，Ｎ−ジメチルアクリルアミドを表す。なお、製造例５はアクリルアミド９５モル％の１０％分をマンニッヒ変性しており（※１）、製造例７は、アクリルアミド９５モル％の１０％分をマンニッヒ変性している（※２）。
【００５７】
製造例８〜１１（アミジン環構造を有するカチオン性の高分子の製造）
攪拌機、温度計、還流冷却管および窒素ガス導入管を備えた四つ口フラスコに、表２に示す仕込み単量体の混合物６０ｇおよび３４０ｇのイオン交換水を入れた。窒素ガス気流中、撹拌しながら４５℃に昇温したのち、１０％の２，２′−アゾビス−２−アミジノプロパン・２塩酸塩水溶液１．２ｇを添加した。４５℃で４時間、撹拌保持した後、６０℃に昇温し、更に３時間保持し、水中に重合体が析出した懸濁物を得た。該懸濁物に水２００ｇ添加し、次いで、重合体中のホルミル基に対して２当量の濃塩酸を添加して撹拌しつつ９０℃で４時間保持し、重合体をアミジン化した。得られた重合体の溶液をアセトン中に添加し、析出せしめ、これを真空乾燥して重合体Ｂ−１〜Ｂ−４を得た。重合体組成の分析結果、還元粘度を表２に示す。
【００５８】
〔重合体組成の分析法〕
各重合体Ｂ−１〜Ｂ−４を、１３Ｃ−ＮＭＲスペクトル（１３Ｃ−核磁気共鳴スペクトル）の各繰り返し単位に対応した吸収ピ−クの積分値より算出した。
【００５９】
〔還元粘度の測定〕
各重合体Ｂ−１〜Ｂ−４を、１ｍｏｌ／ｌ食塩水中、０．１ｇ／ｄｌの溶液として２５℃でオストワルドの粘度計により還元粘度を測定した。
【００６０】
【表２】
表２中、ＮＶＦ：Ｎ−ビニルホルムアミド、ＡＮ：アクリロニトリル、ＡＡ：アクリル酸を表す。
【００６２】
実施例１〜２３、比較例１〜３
製造例１〜７で得られたＡ−１〜Ａ−７、比較製造例１で得られたＣ−１、製造例８〜１１で得られたＢ−１〜Ｂ−４を表３に示すような割合で混合し水性混合物（製紙用添加剤）を得た。なお、水性混合物は、各々のポリマーの希釈液（１％）を混合して調製した。
【００６３】
試験例１
Ｌ−ＢＫＰをナイアガラ式ビーターにて叩解し、カナディアン・スタンダード・フリーネス（Ｃ．Ｓ．Ｆ）４５０ｍｌに調整したパルプスラリーに、硫酸バンド（Ａｌｕｍ）を対パルプ固形分比２％添加してｐＨ４．７とし、次いで表４に示す水性混合物（対パルプ固形分比０．３％または０．６％）加えた。こうして得られたパルプスラリーについて、タッピ・シートマシンにて坪量１００ｇ／ｍ２となるように抄紙し、４ｋｇ／ｃｍ２で４分プレス脱水した。次いで、回転型乾燥機で１１０℃において３分間乾燥し、２０℃、６５％Ｒ．Ｈ．の条件下に２４時間調湿して紙質試験に供した。また、濾水性をＪＩＳ Ｐ−８１２１に準じて測定した。なお、紙質測定法は、次の通りである。圧縮強度：ＪＩＳＰ−８１２６。破裂強度：ＪＩＳ Ｐ−８１１２。結果を表４に示す。
【００６４】
試験例２
段ボール古紙をナイアガラ式ビーターにて叩解し、カナディアン・スタンダード・フリーネス（Ｃ．Ｓ．Ｆ）４３０ｍｌに調整したパルプスラリーに、硫酸バンド（Ａｌｕｍ）を対パルプ固形分比１．０％添加してｐＨ６．２とし、次いで表５に示す水性混合物（対パルプ固形分比０．３％または０．６％）加えた。こうして得られたパルプスラリーについて、タッピ・シートマシンにて坪量１５０ｇ／ｍ２となるように抄紙し、４ｋｇ／ｃｍ２で４分プレス脱水した。次いで、回転型乾燥機で１１０℃において３分間乾燥し、２０℃、６５％Ｒ．Ｈ．の条件下に２４時間調湿した。上記実施例１と同様の操作を行い、濾水性、圧縮強度および破裂強度を測定した。圧縮強度：ＪＩＳ Ｐ８１２６。破裂強度：ＪＩＳ Ｐ８１３１に準じる。結果を表５に示す。
【００６５】
【表３】
【表４】
【表５】
BACKGROUND OF THE INVENTION
The present invention relates to a papermaking additive and a method for producing paper using the papermaking additive. The papermaking additive of the present invention can be used as a papermaking water-repellent agent, a paper strength enhancer, a filler retention agent, a size fixing agent, and the like. In particular, the papermaking additive of the present invention is useful as a water-repellent agent for papermaking and a paper strength enhancer.
[0002]
[Prior art]
Conventionally, it has been known that polyacrylamide usually exhibits an effect as a papermaking additive such as a good water repellency and paper strength enhancing effect as the molecular weight increases. However, a paper additive using a high molecular weight type polyacrylamide has a very high viscosity, and therefore has poor workability compared to a low molecular weight type polyacrylamide. On the other hand, the low molecular weight type has no problem in terms of working efficiency, but is not sufficient in terms of the effect as a papermaking additive compared to the high molecular weight type. In order to improve these problems, a formulation in which an anionic polyacrylamide having a relatively low viscosity and a cationic polyacrylamide modified with Hoffman or Mannich is mixed in advance and added to the pulp slurry has been studied. According to such a mixed prescription, the effect as an additive for papermaking can be exhibited to some extent without lowering the working efficiency in the range of pH 4.5 to 5.5.
[0003]
However, even with such a mixed formulation, the effect as an additive for papermaking, in particular, water repellency and paper strength were not sufficient. In addition, when the molecular weight of polyacrylamide is increased so as to improve the effect as a paper additive by such a mixed prescription, the water repellency is improved, but turbulence is induced, and sufficient paper strength effect cannot be obtained. . Furthermore, in recent years, there has been a tendency for the papermaking pH to increase due to an increase in the ratio of used paper and due to closed paper manufacturing processes as part of environmental measures. Largely, it was difficult to perform stable operation with the mixed prescription.
[0004]
[Problems to be solved by the invention]
The present invention is excellent in various effects as a paper additive such as water repellency, paper strength, and the like, and exhibits a stable effect against fluctuations in papermaking pH, and has excellent operability and the paper additive An object of the present invention is to provide a method for producing paper using a papermaking additive.
[0005]
[Means for Solving the Problems]
As a result of intensive studies to solve the above problems, the present inventors contain (A) an anionic or amphoteric polyacrylamide and (B) a cationic polymer having an amidine ring structure as a repeating unit. It has been found that the above object can be achieved by using an aqueous mixture as an additive for papermaking, and the present invention has been solved.
[0006]
That is, the present invention was measured at 25 ° C. as a solution of 0.1 g / dl of (A) anionic or amphoteric polyacrylamide having a weight average molecular weight of 300,000 to 4 million and (B) 1 mol / l of saline. Contains a cationic polymer having an amidine ring structure having a reduced viscosity of 0.1 to 10 dl / g as a repeating unit The amount of (A) / (B) used is 99.5 / 0.5 to 50/50 in terms of solid content weight ratio. An additive for papermaking comprising an aqueous mixture; and further relates to a method for producing paper, characterized in that the papermaking additive is added to a pulp slurry to produce paper.
[0007]
DETAILED DESCRIPTION OF THE INVENTION
The (A) anionic or amphoteric polyacrylamide used in the present invention is obtained, for example, by copolymerizing (a) (meth) acrylamide and (b) an anionic vinyl monomer, and further (c) a cationic vinyl monomer. It is done. That is, (A) anionic polyacrylamide is (a) (meth) acrylamide and (b) anionic vinyl monomer, (A) amphoteric polyacrylamide is (a) (meth) acrylamide, (b) anionic It is obtained by copolymerizing a vinyl monomer and (c) a cationic vinyl monomer.
[0008]
(A) (Meth) acrylamide means acrylamide or methacrylamide, which can be used alone or in combination. From the economical aspect, it is better to use acrylamide alone. Hereinafter, in the present invention, (meta) has the same meaning. The amount of component (a) used is usually about 60 mol%, preferably 65 mol%, based on the total molar amount of monomers constituting (A) anionic or amphoteric polyacrylamide. When the component (a) is less than 60 mol%, it is difficult to obtain a sufficient paper strength effect as a papermaking additive. In addition, the usage-amount of (a) component is the remainder of components other than (a) component.
[0009]
(B) Examples of anionic vinyl monomers include α, β-unsaturated monobasic acids such as (meth) acrylic acid, crotonic acid, and (meth) allylcarboxylic acid; maleic acid, fumaric acid, itaconic acid, muconic acid Α, β-unsaturated dibasic acids such as: vinyl sulfonic acid, styrene sulfonic acid, 2-acrylamido-2-methylpropane sulfonic acid, (meth) allyl sulfonic acid and other organic sulfonic acids; or these various organic acids Examples thereof include alkali metal salts such as sodium salt and potassium salt, ammonium salt and the like. These anionic vinyl monomers can be used alone or in combination of two or more. In particular, the use of a monomer having a (meth) allyl group, particularly (meth) allylsulfonic acid or a salt thereof, as one kind of anionic vinyl monomers is that the resulting ionic polyacrylamide has a high molecular weight. preferable. Further, it is preferable to use at least one selected from α, β-unsaturated monobasic acid, α, β-unsaturated dibasic acid and salts thereof. In particular, itaconic acid is preferably used. Of these, it is preferable to combine (meth) acrylic acid and / or itaconic acid with (meth) allylsulfonic acid or a salt thereof.
[0010]
The amount of the (b) anionic vinyl monomer used is usually about 1 to 40 mol%, preferably 3 to 40 mol%, based on the total molar sum of the monomers constituting the (A) anionic or amphoteric polyacrylamide. Preferably it is 3-30 mol%.
[0011]
(C) Examples of cationic vinyl monomers include vinyl having a tertiary amino group such as dimethylaminoethyl (meth) acrylate, diethylaminoethyl (meth) acrylate, dimethylaminopropyl (meth) acrylamide, diethylaminopropyl (meth) acrylamide, and the like. By reaction of monomers or their salts with inorganic or organic acids such as hydrochloric acid, sulfuric acid, acetic acid, or quaternizing agents such as methyl chloride, benzyl chloride, dimethyl sulfate, epichlorohydrin, and the like. Examples thereof include vinyl monomers containing the resulting quaternary ammonium salt.
[0012]
(C) It is preferable to use the cationic vinyl monomer in such a ratio that the equivalent ratio (cationic group / anionic group) of ionic functional groups in (A) amphoteric polyacrylamide is 2 or less. The equivalent ratio (cationic group / anionic group) is such that (A) amphoteric polyacrylamide and an aqueous mixture obtained from (B) a cationic polymer having an amidine ring structure, which will be described later, are sufficient additives for papermaking. It is preferable for expressing the effects as described above. In particular, it is preferable to use at a ratio such that the equivalent ratio (cationic group / anionic group) is in the range of 1.5 or less.
[0013]
In addition, (A) a means for imparting a cationic group to amphoteric polyacrylamide is not only capable of copolymerizing (c) a cationic vinyl monomer as described above, but also an anionic acrylamide with formalin and a secondary amine. Cationic groups can also be introduced by Mannich modification in which the reaction is carried out or Hofmann reaction in which a hypohalite is reacted. Even when a cationic group is introduced by such modification, the equivalent ratio (cationic group / anionic group) of ionic functional groups in (A) ionic polyacrylamide is adjusted to the same range as described above. Is preferred.
[0014]
The (A) anionic or amphoteric polyacrylamide of the present invention has the general formula (1): CH in addition to the components (a), (b) and (c). 2 = C (R 1 ) -CONR 2 (R 3 ) (R 1 Is a hydrogen atom or a methyl group, R 2 Is a hydrogen atom or a linear or branched alkyl group having 1 to 4 carbon atoms, R 3 Can contain N-substituted (meth) acrylamides and / or polyfunctional monomers represented by a linear or branched alkyl group having 1 to 4 carbon atoms as a constituent monomer.
[0015]
In N-substituted (meth) acrylamides represented by the general formula (1), a methyl group or a methylene group in an N-alkyl group acts as a chain transfer point, and introduces a lot of branched structures into the polymer. A branched polymer without conversion is obtained. R in the general formula (1) 2 Or R 3 Examples of the linear or branched alkyl group having 1 to 4 carbon atoms in FIG. Include a methyl group, an ethyl group, an isopropyl group, a t-butyl group, and the like. Specific examples of N-substituted (meth) acrylamides N, N-dimethyl (meth) acrylamide, N-isopropyl (meth) acrylamide, N-methyl (meth) acrylamide, N-ethyl (meth) acrylamide, N-isopropyl (meth) acrylamide and Nt-butyl ( (Meth) acrylamide. Among these, N, N-dimethylacrylamide is preferable from the viewpoint of copolymerization and chain transfer.
[0016]
Moreover, a crosslinked structure can also be provided to (A) anionic or amphoteric polyacrylamide by using a polyfunctional monomer. Examples of multifunctional monomers include di (meth) acrylates such as ethylene glycol di (meth) acrylate, diethylene glycol di (meth) acrylate, and triethylene glycol di (meth) acrylate, methylene bis (meth) acrylamide, and ethylene bis (meth). ) Bis (meth) acrylamides such as acrylamide and hexamethylenebis (meth) acrylamide, divinyl esters such as divinyl adipate and divinyl sebacate, allyl methacrylate, diallylamine, diallyldimethylammonium, diallyl phthalate, diallyl chlorendate, divinyl Benzene, bifunctional vinyl monomers such as N, N-diallylacrylamide, 1,3,5-triacryloylhexahydro-S-triazine, triallyl isocyanurate Trifunctional amine monomers such as triallylamine and triallyl trimellitate, tetramethylolmethane tetraacrylate, tetraallyl pyromellitate, N, N, N ', N'-tetraallyl-1,4-diaminobutane, tetraallylamine salts In addition, tetrafunctional vinyl monomers such as tetraallyloxyethane, and other examples include N-methylolacrylamide. Among these polyfunctional monomers, 1,3,5-triacryloylhexahydro-S-triazine, triallyl isocyanurate and the like are preferable.
[0017]
The amount of the N-substituted (meth) acrylamides and / or multifunctional monomers represented by the general formula (1) is based on the total molar sum of the monomers constituting (A) anionic or amphoteric polyacrylamide. Usually, it is about 10 mol% or less, further 5 mol% or less. In order to exhibit the function of the N-substituted (meth) acrylamides represented by the general formula (1), 0.1 mol% or more, more preferably 0.5 mol% or more is used.
[0018]
Furthermore, in order to impart hydrophobicity to (A) anionic or amphoteric polyacrylamide, an alkyl ester of the anionic vinyl monomer (alkyl group having 1 to 8 carbon atoms), acrylonitrile, styrenes, vinyl acetate, Nonionic vinyl monomers such as methyl vinyl ether can also be used. In the case of using a nonionic vinyl monomer, the amount used is usually about 30 mol% or less, preferably 20 mol% or less, based on the total molar amount of monomers constituting (A) anionic or amphoteric polyacrylamide. is there.
[0019]
(A) Synthesis of anionic or amphoteric polyacrylamide can be carried out by various conventionally known methods. For example, it can be obtained by charging the above-mentioned various monomers and water in a predetermined reaction vessel, adding a radical polymerization initiator, and heating with stirring. The reaction temperature is usually about 50 to 100 ° C., and the reaction time is about 1 to 5 hours. The reaction concentration (monomer concentration) can be usually about 10 to 40% by weight, and the polymerization can be carried out even at a high concentration. In addition, the monomer can be charged by various conventionally known methods such as simultaneous polymerization and continuous dropping polymerization. As the radical polymerization initiator, a normal radical polymerization initiator such as a persulfate such as potassium persulfate or ammonium persulfate, or a redox polymerization initiator in the form of a combination of these with a reducing agent such as sodium bisulfite is used. it can. An azo initiator may be used as the radical polymerization initiator. The amount of the radical polymerization initiator used is about 0.05 to 2% by weight, preferably 0.1 to 0.5% by weight, based on the total weight of the monomers.
[0020]
(A) The weight average molecular weight of anionic or amphoteric polyacrylamide is adjusted to 300,000 to 4,000,000 in consideration of workability and economy. Preferably, it is 1 million to 4 million. If the weight average molecular weight is less than 300,000, the paper strength effect is insufficient. The viscosity of (A) anionic or amphoteric polyacrylamide is preferably about 10,000 cps (25 ° C.) or less from the viewpoint of handleability. The papermaking additive of the present invention is adjusted to a solid content concentration of 10 to 40% by weight. Usually, the solid content concentration is preferably 30% by weight or less.
[0021]
As the cationic polymer (B) having an amidine ring structure as a repeating unit used in the present invention, various polymers having an amidine ring structure can be used as the polymer repeating unit.
[0022]
Examples of the repeating unit of the amidine ring structure include the following general formula (2), general formula (3), general formula (4),
[0023]
[Formula 4]
[Chemical formula 5]
[Chemical 6]
(Where R 4 , R 5 Is a hydrogen atom or a methyl group, X − Each represents an anion. ).
[0027]
The cationic polymer (B) of the present invention comprises repeating units of the amidine ring structure represented by the general formula (2), the general formula (3), and the general formula (4). What contains about 20-90 mol% of a repeating unit is preferable. (B) When increasing the effect of the aggregating action of the cationic polymer on the pulp, the performance is better when the ratio of the amidine ring structural unit in the molecule is larger. Therefore, the repeating unit of the amidine ring structure is 30 It is preferably at least mol%, more preferably 50 mol%. In consideration of ease of production and the like, the repeating unit of the amidine ring structure is preferably 85 mol% or less, more preferably 80 mol% or less.
[0028]
The method for forming these repeating units of the amidine ring structure is not particularly limited. Generally, the repeating unit of the amidine ring structure represented by the general formula (2) or (3) is a primary amino group. Alternatively, a copolymer of an ethylenically unsaturated monomer (X) having a substituted amino group capable of forming a primary amino group by a conversion reaction and a nitrile such as (meth) acrylonitrile is produced. It is formed by reacting a cyano group with a primary amino group to form an amidine.
[0029]
Examples of the ethylenically unsaturated monomer (X) include, for example, the general formula (5) CH 2 = CR 6 NHCOR 7 (R 6 Represents a hydrogen atom or a methyl group, R 7 Represents a hydrogen atom or an alkyl group having 1 to 4 carbon atoms. And ethylenically unsaturated monomers represented by The substituted amino group derived from the ethylenically unsaturated monomer represented by the general formula (5) is easily converted into a primary amino group by hydrolysis or alcoholysis in the copolymer. Examples of the ethylenically unsaturated monomer represented by the general formula (5) include N-vinylformamide (R 6 = H, R 7 = H), N-vinylacetamide (R 6 = H, R 7 = CH 3 And the like.
[0030]
When the repeating unit of the amidine ring structure represented by the general formula (2) or (3) is formed, the polymerization molar ratio between the ethylenically unsaturated monomer (X) and the nitrile is (B) a cationic polymer. Since the performance as an additive for papermaking is excellent when the ratio of the amidine ring structural unit in the interior is large, it is usually preferably 20:80 to 80:20, particularly preferably 40:60 to 60:40. If desired, a molar ratio outside this range, for example, a polymerization molar ratio with a higher ratio of ethylenically unsaturated monomers may be employed.
[0031]
As a method of copolymerizing the ethylenically unsaturated monomer (X) and the nitrile, a normal radical polymerization method is used, and any of bulk polymerization, aqueous solution precipitation polymerization, suspension polymerization, emulsion polymerization, and the like can be used. . When polymerizing in a solvent, the raw material monomer concentration is usually 5 to 80% by weight, preferably 20 to 60% by weight. A general radical polymerization initiator can be used as the polymerization initiator, but an azo compound is preferable, and hydrochloride of 2,2′-azobis-2-amidinopropane and the like are exemplified. The polymerization reaction is generally performed at a temperature of 30 to 100 ° C. under an inert gas stream. The obtained copolymer can be subjected to an amidation reaction as it is or diluted, that is, in the form of a solution or suspension. Alternatively, the solvent can be removed by a known method and dried to separate the copolymer as a solid, and then subjected to an amidation reaction in a solid state. In addition, the polymer obtained can obtain a desired molecular weight suitably by adjusting the usage-amount of a radical polymerization initiator, reaction temperature, etc.
[0032]
The amidine reaction is a two-step reaction in which a substituted amino group of a copolymer is converted into a primary amino group and then reacted with a cyano group adjacent to the generated primary amino group to form an amidine ring structure, The coalescence is carried out by a one-step reaction in which an amidine ring structure is formed by heating in water or an alcohol solution in the presence of a strong acid or base. The amidation reaction is preferably a one-step reaction. Specifically, the one-step reaction is, for example, usually 0.9 to 5 times, preferably 1 to 3 times equivalent of a strong acid, preferably hydrochloric acid, with respect to the substituted amino group. The heating is performed at a temperature of 80 to 150 ° C., preferably 90 to 120 ° C., usually for 0.5 to 20 hours. In general, the larger the equivalent ratio of strong acid to substituted amino group and the higher the reaction temperature, the more the amidation proceeds. In addition, in the case of amidine formation, water of usually 10% by weight or more, preferably 20% by weight or more is present in the reaction system with respect to the copolymer used for the reaction.
[0033]
The cationic polymer (B) thus obtained usually contains about 20 to 90 mol% of the repeating unit of the amidine ring structure represented by the general formula (1) and / or (2), About 0 to 2 mol% of repeating units derived from the ethylenically unsaturated monomer (X), about 0 to 70 mol% of repeating units derived from the nitriles, converted product of ethylenically unsaturated monomer (X) (primary About 0 to 70 mol% of repeating units derived from (amino group).
[0034]
Among these cationic polymers (B), those having more repeating units of the amidine ring structure generally have better performance as an additive for papermaking, and therefore are represented by the general formulas (1) and / or (2). The repeating unit of the amidine ring structure is preferably 0.5 to 10 times, more preferably 2 to 5 times the repeating unit of nitriles.
[0035]
In addition, the repeating unit derived from the primary amino group is cationic, and is considered to contribute to the performance as a drainage improver as well as the repeating unit of the amidine ring structure. Therefore, it is preferable that the repeating unit derived from a primary amino group is 5 to 60 mol%. The total of the cation units including the repeating unit of the amidine ring structure represented by the general formula (1) and / or (2), and further the repeating unit derived from the primary amino group is generally 40 mol% or more, preferably 60 to 95 mol%. However, the repeating unit of the amidine ring structure represented by the general formula (1) and / or (2) is considered to contribute more effectively to the performance of the paper additive than the repeating unit derived from the primary amino group. The repeating unit of the amidine ring structure represented by the general formula (1) and / or (2) is preferably 0.5 to 10 times, preferably 2 to 5 times the repeating unit derived from the primary amino group. .
[0036]
In addition, since the cationic polymer (B) generally has poor storage stability as it is, it is preferable to completely neutralize the amidine ring structure and the cation unit of the primary amino group by adding a strong acid.
[0037]
In addition, the cationic polymer (B) having a repeating unit represented by the general formula (4) as a repeating unit of the amidine ring structure is obtained by polymerizing the ethylenically unsaturated monomer (X), and then replacing the monomer. A part of the amino group is converted into a primary amino group, and formed by amidinization of the substituted amino group and the primary amino group generated by the conversion reaction. As the amidation conditions, heating is usually performed in a solvent at about 50 to 110 ° C. for about 1 to 72 hours. The reaction is usually carried out under stirring, and usually under normal pressure, but may be pressurized as necessary. If the reaction temperature is less than 50 ° C., the reaction rate is too slow and not efficient. On the other hand, if the reaction temperature exceeds 110 ° C., a cross-linking reaction tends to occur as a side reaction, which may cause insolubility. The repeating unit of the amidine ring structure represented by the general formula (4) is preferably 20 mol% or more.
[0038]
The cationic polymer (B) of the present invention may contain a repeating unit derived from an anionic vinyl monomer. In general, an anionic vinyl monomer is copolymerized when the ethylenically unsaturated monomer (X) or the like is polymerized. Examples of the anionic vinyl monomer are the same as those used in (A). The amount of the anionic vinyl monomer used is usually preferably about 0 to 20 mol%, more preferably 3 to 15 mol% of all constituent monomers. In addition, generally (0) -5 mol of repeating units derived from (meth) acrylic acid can be produced in the cationic polymer (B) by hydrolysis of repeating units derived from (meth) acrylonitrile.
[0039]
Furthermore, the (B) cationic polymer of the present invention may further contain a repeating unit derived from (meth) acrylamide in addition to the above repeating unit. Moreover, the repeating unit which the repeating unit derived from (meth) acrylamide and the repeating unit derived from (meth) acrylic acid reacted, and formed a part of lactam ring may be contained.
[0040]
The (B) cationic polymer of the present invention has a reduced viscosity value of 0.1 to 10 dl / g measured at 25 ° C. as a 0.1 g / dl solution in 1 mol / l saline. Preferably it is 1-10 dl / g, More preferably, it is 0.5-4 dl / g.
[0041]
The paper additive of the present invention is an aqueous mixture comprising (A) an anionic or amphoteric polyacrylamide and the (B) cationic polymer. In such an aqueous mixture, (A) an anionic or amphoteric polyacrylamide and (B) a cationic polymer are mixed in advance, so that both cause some interaction, and the fixing rate to the pulp is improved and higher. It exhibits water repellency and paper strength effect. These use ratios are usually in a solid content weight ratio, and (A) / (B) is 99.5 / 0.5 to 50/50, preferably 99/1 to 70/30. Good.
[0042]
The paper additive made of the aqueous mixture is added to the pulp slurry and then made into paper to produce paper. Although various means can be adopted for papermaking, the addition of the papermaking additive to the pulp slurry is preferably after adding the sulfuric acid band to the pulp slurry, and more preferably after some time from the addition of the sulfuric acid band. . In addition, since it is desirable to make paper immediately without applying unnecessary share to the generated floc, it is preferable to add a papermaking additive at a location near the papermaking wire portion. In particular, the addition at the fan pump suction port is preferable because the water repellency and paper strength effect are improved. The pH of the pulp slurry can usually be selected from a wide range of 4-9. The aqueous mixture that is an additive for papermaking may be appropriately diluted with water, alcohols or the like as necessary. In addition, the aqueous mixture may be prepared immediately before addition to the papermaking system, or may be added separately to the papermaking system. The prepared aqueous mixture can be used as it is in the distribution process.
[0043]
The amount of the papermaking additive used may be the same as usual, and is about 0.005 to 3% by weight, preferably about 0.01 to 1% by weight, based on the pulp, in terms of solid content. . Moreover, a sulfuric acid band is 0.5 to 10 weight% normally with respect to pulp solid content.
[0044]
In such a papermaking process, such a paper additive can improve the effect as a paper additive such as water repellency and paper strength without reducing workability. In particular, when (A) amphoteric polyacrylamide is used, the effect can be stably exhibited in papermaking from acidic to neutral range without being affected by papermaking pH.
[0045]
【The invention's effect】
The papermaking additive of the present invention is excellent in various effects as a papermaking additive such as water repellency and paper strength, and has a wide papermaking pH range and excellent operability. In particular, the papermaking pH is excellent in an acidic to neutral range.
[0046]
【Example】
EXAMPLES Hereinafter, although an Example and a comparative example are given and this invention is demonstrated in detail, this invention is not limited to these examples. In each example, all parts and% are based on weight unless otherwise specified.
[0047]
Production Example 1 (Production of anionic polyacrylamide)
In a four-necked flask equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen gas inlet tube, 300.2 parts of powdered acrylamide (88 mol% based on the total molar amount of monomers, the same applies hereinafter), 80% aqueous acrylic acid solution 38.9 parts (9 mol%), 6.2 parts (1 mol%) itaconic acid, 7.6 parts (1 mol%) sodium methallylsulfonate, 4.8 parts (1 mol%) dimethylacrylamide and ions 1300 parts of exchange water (monomer concentration 21%) was charged, and oxygen in the reaction system was removed through nitrogen gas. The system was heated to 40 ° C., and 7 parts of a 5% aqueous ammonium persulfate solution and 3 parts of a 5% aqueous sodium hydrogensulfite solution were added as a polymerization initiator with stirring. After raising the temperature to 90 ° C., the temperature was kept for 2 hours. After completion of the polymerization, 70 parts of ion exchanged water (adjusted to a solid content concentration of 20%) was added, and the pH was 4.0, the solid content was 20.2%, the viscosity (25 ° C.) was 6800 cps, and the weight average molecular weight was 2.4 million. A combined aqueous solution was obtained. Hereinafter, this aqueous solution is referred to as A-1. The weight average molecular weight was measured by a low-angle light scattering method (GPC-LALLS (manufactured by Tosoh Corporation)) using an aqueous solution containing acetic acid and sodium acetate at pH 4.2 as a moving layer, and a sample concentration of 0.0125. %.
[0048]
Production Example 2 (Production of amphoteric polyacrylamide)
In a four-necked flask equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen gas introduction tube, 284.5 parts of powdered acrylamide (85 mol% with respect to the total molar amount of monomers, the same applies hereinafter), 62.5% sulfuric acid 9.9 parts, 22.2 parts (3 mol%) of dimethylaminoethyl methacrylate, 42.4 parts (10 mol%) of 80% aqueous acrylic acid solution, 9.3 parts (2 mol%) of dimethylacrylamide and 1300 ion-exchanged water Parts (monomer concentration 21%) were charged, and oxygen in the reaction system was removed through nitrogen gas. The system was heated to 40 ° C., and 7 parts of a 5% aqueous ammonium persulfate solution and 3 parts of a 5% aqueous sodium hydrogensulfite solution were added as a polymerization initiator with stirring. After raising the temperature to 90 ° C., the temperature was kept for 2 hours. After completion of the polymerization, 100 parts of ion-exchanged water (adjusted to a solid content concentration of 20%) was added, and the pH was 4.1, the solid content was 20.1%, the viscosity (25 ° C.) was 4600 cps, and the weight average molecular weight was 1.9 million. A combined aqueous solution was obtained. Hereinafter, this aqueous solution is referred to as A-2.
[0049]
Production Example 3 (Production of amphoteric polyacrylamide)
In a four-necked flask equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen gas inlet tube, 294.4 parts of powdered acrylamide (89.5 mol% based on the total molar amount of monomers, the same applies hereinafter), 62.5 % Sulfuric acid 6.5 parts, dimethylaminoethyl methacrylate 14.5 parts (2 mol%), 80% aqueous acrylic acid solution 16.7 parts (4 mol%) itaconic acid 12.0 parts (2 mol%), methallylsulfone Sodium acid 11.0 parts (1.5 mol%), dimethylacrylamide 4.6 parts (1 mol%) and ion-exchanged water 1300 parts (monomer concentration 21%) were charged, and oxygen in the reaction system was removed through nitrogen gas. . The system was brought to 40 ° C., and 9.8 parts of 5% ammonium persulfate aqueous solution and 4 parts of 5% sodium hydrogensulfite aqueous solution were added as a polymerization initiator under stirring. After raising the temperature to 90 ° C., the temperature was kept for 2 hours. After completion of the polymerization, 105 parts of ion-exchanged water (adjusted to a solid content concentration of 20%) was added, and the pH was 3.9, the solid content was 20.1%, the viscosity (25 ° C.) was 8500 cps, and the weight average molecular weight was 3 million. A combined aqueous solution was obtained. Hereinafter, this aqueous solution is referred to as A-3.
[0050]
Production Example 4 (Production of amphoteric polyacrylamide)
In a four-necked flask equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen gas inlet tube, 288.7 parts of powdered acrylamide (89.5 mol% with respect to the total molar amount of monomers, the same applies hereinafter), 62.5 % Sulfuric acid 19.2 parts, dimethylaminoethyl methacrylate 42.8 parts (6 mol%), 80% aqueous acrylic acid solution 10.2 parts (2.5 mol%) itaconic acid 5.9 parts (1 mol%), dimethyl 4.5 parts of acrylamide (1 mol%) and 1300 parts of ion exchange water (monomer concentration 21%) were charged, and oxygen in the reaction system was removed through nitrogen gas. The system was brought to 40 ° C., and 9.8 parts of 5% ammonium persulfate aqueous solution and 4 parts of 5% sodium hydrogensulfite aqueous solution were added as a polymerization initiator under stirring. After raising the temperature to 90 ° C., the temperature was kept for 2 hours. After completion of the polymerization, 105 parts of ion-exchanged water (adjusted to a solid content concentration of 20%) was added and the pH was 3.9, the solid content was 20.1%, the viscosity (25 ° C.) was 5500 cps, and the weight average molecular weight was 2.2 million. A combined aqueous solution was obtained. Hereinafter, this aqueous solution is referred to as A-4.
[0051]
Production Example 5 (Production of amphoteric polyacrylamide)
In a four-necked flask equipped with a stirrer, thermometer, reflux condenser and nitrogen gas inlet tube, 162 parts of 50% acrylamide (95 mol% based on the total molar amount of monomers, the same applies hereinafter), 80% aqueous acrylic acid solution 5 .4 parts (5 mol%), 737 parts of ion exchange water and 2.5 parts of isopropyl alcohol were added, the pH was adjusted to 5 to 5.5 with 48% sodium hydroxide, and oxygen in the reaction system was removed through nitrogen gas. Under stirring, 2.6 parts of a 5% aqueous ammonium persulfate solution and 1.1 parts of a 5% aqueous sodium hydrogensulfite solution were added as polymerization initiators, and the temperature was raised from room temperature to 80 ° C. and kept for 3 hours. After cooling to 50 ° C., 13.0 parts of a 50% dimethylamine aqueous solution and 9.8 parts of 37% formalin (mannich modified 10% of acrylamide 95 mol%) were sequentially added and maintained at the same temperature for 1 hour. Thus, an aqueous solution of an amphoteric Mannich-modified copolymer having a pH of 10.8, a solid content of 10.4%, a viscosity (25 ° C.) of 5600 cps and a weight average molecular weight of 1,000,000 was obtained. Hereinafter, this aqueous solution is referred to as A-5.
[0052]
Production Example 6 (Production of amphoteric polyacrylamide)
In a four-necked flask equipped with a stirrer, thermometer, reflux condenser and nitrogen gas inlet tube, 230.8 parts of powdered acrylamide (78 mol% based on the total molar amount of monomers, the same applies hereinafter), 62.5% sulfuric acid 44.0 parts, 98.1 parts (15 mol%) of dimethylaminoethyl methacrylate, 11.3 parts (3 mol%) of 80% aqueous acrylic acid solution, 5.4 parts (1 mol%) itaconic acid, sodium methallylsulfonate 6.6 parts (1 mol%), 4.1 parts (1 mol%) of dimethylacrylamide and 1300 parts of ion exchange water (monomer concentration 21%) were charged, and oxygen in the reaction system was removed through nitrogen gas. The system was brought to 40 ° C., and 12 parts of a 5% aqueous solution of ammonium persulfate and 3 parts of a 5% aqueous solution of sodium hydrogensulfite were added as a polymerization initiator with stirring. After raising the temperature to 90 ° C., the temperature was kept for 2 hours. After completion of the polymerization, 100 parts of ion-exchanged water (adjusted to a solid content concentration of 20%) was added, and the pH was 3.9, the solid content was 20.1%, the viscosity (25 ° C.) was 6000 cps, and the weight average molecular weight was 2.3 million. A combined aqueous solution was obtained. Hereinafter, this aqueous solution is referred to as A-6.
[0053]
Production Example 7 (Production of amphoteric polyacrylamide)
In a four-necked flask equipped with a stirrer, thermometer, reflux condenser and nitrogen gas inlet tube, 162 parts of 50% acrylamide (95 mol% based on the total molar amount of monomers, the same applies hereinafter), 80% aqueous acrylic acid solution 5 4 parts (5 mol%), 737 parts of ion-exchanged water and 2.5 parts of isopropyl alcohol were added, the pH was adjusted to 5 to 5.5 with 48% sodium hydroxide, and oxygen in the reaction system was removed through nitrogen gas. Under stirring, 2.6 parts of a 5% aqueous ammonium persulfate solution and 1.1 parts of a 5% aqueous sodium hydrogensulfite solution were added as polymerization initiators, and the temperature was raised from room temperature to 80 ° C. and kept for 3 hours. After cooling this to 50 ° C., 25.9 parts of a 50% dimethylamine aqueous solution and 19.5 parts of 37% formalin (20% portion of acrylamide 95 mol% modified with Mannich) were sequentially added and kept at the same temperature for 1 hour. Thus, an aqueous solution of an amphoteric Mannich-modified copolymer having a pH of 10.8, a solid content of 10.5%, a viscosity (25 ° C.) of 5300 cps and a weight average molecular weight of 1,000,000 was obtained. Hereinafter, this aqueous solution is referred to as A-7.
[0054]
Comparative Production Example 1 (Production of anionic polyacrylamide)
In a four-necked flask equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen gas inlet tube, 128 parts of powdered acrylamide (90% by mole based on the total mole of monomers, the same applies hereinafter), 18 parts of 80% aqueous acrylic acid solution (10 mol%), 530 parts of ion-exchanged water, and 8 parts of isopropyl alcohol were charged, and oxygen in the reaction system was removed with nitrogen gas. Next, 10 parts of a 5% aqueous ammonium persulfate solution and 4.1 parts of a 5% aqueous sodium hydrogen sulfite solution were added as a polymerization initiator under stirring, and the temperature was raised from room temperature to 80 ° C. and kept for 3 hours. Thereafter, 240 parts of ion-exchanged water was added, the pH was adjusted to 5 with 48% caustic soda, and an aqueous copolymer solution having a solid content of 15.2%, a viscosity (25 ° C.) of 6500 cps, and a weight average molecular weight of 250,000 was obtained. . Hereinafter, this aqueous solution is referred to as C-1.
[0055]
[Table 1]
In the table, AM represents acrylamide, DM: N, N-dimethylethyl methacrylate, AA: acrylic acid, IA: itaconic acid, SMAS: sodium methallylsulfonate, DMAA: N, N-dimethylacrylamide. In Production Example 5, 10% of acrylamide 95 mol% is Mannich modified (* 1), and in Production Example 7, 10% of acrylamide 95 mol% is Mannich modified (* 2).
[0057]
Production Examples 8 to 11 (Production of a cationic polymer having an amidine ring structure)
In a four-necked flask equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen gas introduction tube, 60 g of the charged monomer mixture shown in Table 2 and 340 g of ion-exchanged water were placed. The temperature was raised to 45 ° C. with stirring in a nitrogen gas stream, and 1.2 g of a 10% 2,2′-azobis-2-amidinopropane dihydrochloride aqueous solution was added. After stirring and holding at 45 ° C. for 4 hours, the temperature was raised to 60 ° C. and further maintained for 3 hours to obtain a suspension in which the polymer was precipitated in water. 200 g of water was added to the suspension, and then 2 equivalents of concentrated hydrochloric acid with respect to the formyl group in the polymer was added and kept at 90 ° C. for 4 hours with stirring to amidine the polymer. The obtained polymer solution was added to acetone to cause precipitation, and this was vacuum dried to obtain polymers B-1 to B-4. Table 2 shows the analysis results of the polymer composition and the reduced viscosity.
[0058]
[Analytical method of polymer composition]
Each polymer B-1 to B-4 is 13 C-NMR spectrum ( 13 C-nuclear magnetic resonance spectrum) was calculated from the integrated value of the absorption peak corresponding to each repeating unit.
[0059]
(Measurement of reduced viscosity)
The reduced viscosity of each polymer B-1 to B-4 was measured as a 0.1 g / dl solution in 1 mol / l saline at 25 ° C. using an Ostwald viscometer.
[0060]
[Table 2]
In Table 2, NVF: N-vinylformamide, AN: acrylonitrile, AA: acrylic acid.
[0062]
Examples 1 to 23, Comparative Examples 1 to 3
Table 3 shows A-1 to A-7 obtained in Production Examples 1 to 7, C-1 obtained in Comparative Production Example 1, and B-1 to B-4 obtained in Production Examples 8 to 11. An aqueous mixture (additive for papermaking) was obtained by mixing at such a ratio. The aqueous mixture was prepared by mixing each polymer dilution (1%).
[0063]
Test example 1
L-BKP was beaten with a Niagara-type beater and adjusted to 450 ml of Canadian Standard Freeness (C.S.F), and a sulfuric acid band (Alum) was added to a pulp solid content ratio of 2% to pH 4. 7 and then the aqueous mixture shown in Table 4 (0.3% or 0.6% pulp solids ratio) was added. About the pulp slurry obtained in this way, basis weight 100g / m with a tappi sheet machine 2 Paper is made to be 4kg / cm 2 And press dehydrated for 4 minutes. Next, it was dried at 110 ° C. for 3 minutes in a rotary dryer, and 20 ° C., 65% R.D. H. The sample was conditioned for 24 hours and subjected to a paper quality test. Moreover, the drainage was measured according to JIS P-8121. The paper quality measurement method is as follows. Compressive strength: JISP-8126. Burst strength: JIS P-8112. The results are shown in Table 4.
[0064]
Test example 2
A pulp slurry prepared by beating used corrugated paper with a Niagara-type beater and adjusting to Canadian Standard Freeness (CSF) 430 ml was added with 1.0% sulfuric acid band (Alum) to pulp solid content ratio to pH 6 2 and then the aqueous mixture shown in Table 5 (0.3% or 0.6% pulp solids ratio) was added. About the pulp slurry obtained in this way, basis weight 150g / m with a tappi sheet machine 2 Paper is made to be 4kg / cm 2 And press dehydrated for 4 minutes. Subsequently, it dried for 3 minutes at 110 degreeC with a rotary dryer, and 20 degreeC and 65% R. H. The humidity was adjusted for 24 hours. The same operation as in Example 1 was performed, and the drainage, compressive strength, and burst strength were measured. Compressive strength: JIS P8126. Burst strength: According to JIS P8131. The results are shown in Table 5.
[0065]
[Table 3]
[Table 4]
[Table 5]
Claims (7)
、一般式（３）：
General formula (3):