JP4235707B2 - Wood preservative and method of treating wood using the same - Google Patents
Wood preservative and method of treating wood using the same Download PDFInfo
- Publication number
- JP4235707B2 JP4235707B2 JP2003139715A JP2003139715A JP4235707B2 JP 4235707 B2 JP4235707 B2 JP 4235707B2 JP 2003139715 A JP2003139715 A JP 2003139715A JP 2003139715 A JP2003139715 A JP 2003139715A JP 4235707 B2 JP4235707 B2 JP 4235707B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- parts
- wood
- ionette
- nonionic surfactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】
【発明の属する技術の分野】
この発明は、木材防腐剤およびそれを用いる木材の処理方法に関する。さらに詳しくは、オオウズラタケ、カワラタケおよびナミダタケなどによる木材の腐朽を防止または抑制しうる、安全性に優れた木材防腐剤およびそれを用いる木材の処理方法に関する。
【０００２】
【従来の技術】
木材は軽量でありながら強度が大きいことや、加工のしやすさ、人体にやさしいなど、その優れた特質により様々な分野で重用されている。しかしながら、生物系材料であるために避けられない幾つかの欠点、すなわち燃え易い、狂い易い、腐り易い、虫に食われ易い、変色し易い、割れ易いなどの性質を併せもっている。これらの欠点、特に木材腐朽菌による腐朽や、シロアリなどによる虫害を防ぐことは、木材の供用期間の延長や木材製品の信頼性向上のために必要不可欠であり、これらの欠点が克服されれば、資源としての木材をより一層有効に利用でき、ひいては地球環境の保全に大きく寄与できる。
【０００３】
このような点に鑑み、木材腐朽菌を防除する薬剤、すなわち木材防腐剤として、フェノール系化合物、有機ハロゲン系化合物、有機錫系化合物、ナフテン酸系化合物およびタール系化合物などの有機系薬剤や、銅化合物、クロム化合物とヒ素化合物との混合物であるＣＣＡ薬剤、銅化合物と有機系薬剤との併用、ならびに第４級アンモニウム塩とホウ酸系化合物と水溶性アルカノールアミンと亜鉛イオン供給化合物とから構成される木材防腐剤などが提案されている。
【０００４】
上記の木材防腐剤は重金属、ハロゲン化合物あるいは発ガン性の疑いのある化合物を含むものがほとんどであり、注入作業時、供用時および廃棄時における安全性や環境への影響性の点で問題があった。
そこで、優れた安全性と効力持続性を兼ね備えた木材防腐剤の早期開発が望まれている。
【０００５】
【発明が解決しようとする課題】
この発明は、オオウズラタケ、カワラタケおよびナミダタケなどの木材腐朽菌に対して強力な防除効果を発揮し、かつ安全性の高い木材防腐剤を提供することを課題とする。
【０００６】
【課題を解決するための手段】
この発明の発明者らは、上記の課題を解決すべく鋭意研究を行った結果、ココナットアミンアセテートが顕著な木材防腐効果を有する事実を見出し、この発明を完成するに到った。
【０００７】
かくして、この発明によれば、ココナットアミンアセテートを有効成分として含有することを特徴とする木材防腐剤が提供される。
【０００８】
また、この発明によれば、ココナットアミンアセテートを有効成分として含有する木材防腐剤で木材を処理することを特徴とする木材の防腐処理方法が提供される。
【０００９】
【発明の実施の形態】
この発明で用いられるアルキルアミンアセテートとしては、ココナットアミンアセテートやステアリルアミンアセテートなどが挙げられ、カチオン性界面活性剤として市販されているものを好適に用いることができる。
【００１０】
この発明の木材防腐剤の剤型としては、使用目的により液剤（例えば水溶剤、乳剤、水和剤（フロアブル製剤）、油剤）、固型剤（例えば粉剤、粒剤）、エアゾール剤など種々の剤型が可能であるが、水溶剤、乳剤または油剤が好ましい。上記のいずれの製剤も公知の方法を利用して製剤化することができる。
以下に、この発明の木材防腐剤の製剤法について述べる。
【００１１】
水溶剤とする場合には、通常、有効成分をアルコール系溶媒などの有機溶媒に溶解したものを界面活性剤および水に加えて製剤化する。また、水溶剤を木材に塗布処理した場合の被膜形成のために、必要に応じて水溶剤に樹脂エマルションを添加してもよい。
【００１２】
界面活性剤としては、カチオン系界面活性剤、アニオン系界面活性剤、ノニオン系界面活性剤または両性界面活性剤のいずれも使用できるが、製剤の安定性の点でノニオン系界面活性剤が好ましい。ノニオン系界面活性剤としては、例えば、ソルビタン脂肪酸エステル（ＨＬＢ：１４．９、１６．７）などが挙げられる。
【００１３】
また、樹脂エマルションとしては、例えば、ポリ酢酸ビニル樹脂エマルション（樹脂固形分率４０〜５０％、平均分子量２，０００〜１００，０００）、ポリ酢酸ビニル・エチレン共重合体樹脂エマルション（樹脂固形分率４０〜５０％、平均分子量２，０００〜１００，０００）、ポリアクリル酸エステル樹脂エマルション（樹脂固形分率３０〜４０％、粘度１００〜５００ｃＰｓ、平均分子量３，０００〜５０，０００）が挙げられる。
【００１４】
乳剤とする場合には、通常、有効成分を有機溶媒に溶解したものを界面活性剤に加え、適宜水を添加し製剤化する。界面活性剤は、水溶剤で例示されたものを使用することができる。また、乳剤を木材に塗布処理した場合の被膜形成のために、必要に応じて水溶剤で例示された樹脂エマルションを乳剤に添加してもよい。乳剤において、有効成分を溶解させる有機溶媒としては、疎水性有機溶媒が好適に用いられる。
【００１５】
この発明の木材防腐剤を乳剤とする場合に好適に用いられる有機溶媒を以下に例示する。
１） 脂肪族炭化水素系
ｎ−ヘキサン、シクロヘキサン、ヘプタン、オクタンなど
２） 芳香族炭化水素系
キシレン、トルエン、エチルベンゼン、クメン、モノイソプロピルナフタレン、ジイソプロピルナフタレン、モノイソプロピルビフェニルなど
３） エステル系
酢酸エチル、酢酸メチル、酢酸ｎ−ブチル、酢酸アミルなど
４） アルコール系
イソブタノール、ｓｅｃ−ブタノール、２−エチル−１−ブタノール、イソペンタノール、１−ヘプタノール、１−オクタノール、ネオペンチルアルコール、ジエチレングリコールモノメチルエーテル（ＭＤＧ）、ジエチレングリコール（ＤＥＧ）、ジエチレングリコールモノブチルエーテル（ＢＤＧ）、２−ヒドロキシエチルブチルエーテル（ＢＧ）、プロピレングリコールモノメチルエーテル（ＭＰＧ）など
５） ケトン系
アセトン、メチルエチルケトン、メチルイソブチルケトン、メチルアミルケトン、シクロヘキサノンなど
６） カーボネート
プロピレンカーボネートなど
上記の有機溶媒は、単独でまたは２種以上のものを組み合わせて用いることができる。
【００１６】
水溶剤とする場合には、通常、有効成分を例えばアルコール系溶媒に溶解したものを界面活性剤および水に加えて製剤化する。水溶剤は、製剤を１００重量部としたとき、有効成分量が１〜５０重量部、残部を有機溶媒、界面活性剤および水とするのが好ましい。これらの水溶剤は、使用時に水で所定の倍率、例えば１〜１０倍、好ましくは１〜５倍に希釈して使用する。
【００１７】
乳剤とする場合には、通常、有効成分を有機溶媒に溶解したものを界面活性剤に加え、適宜水を添加し製剤化する。乳剤は、製剤を１００重量部としたとき、有効成分量が１〜５０重量部で、残部を有機溶媒および界面活性剤、さらに適宜水を添加してもよい。これらの乳剤は、使用時に水で所定の倍率、例えば２〜１０倍に希釈して使用することができる。
【００１８】
また、水和剤（フロアブル製剤）とする場合には、製剤を１００重量部としたとき、有効成分が１〜５０重量部、乳化剤または増粘剤（例えばポリアクリル酸またはその塩、ポリビニルアルコール）が１０〜４０重量部程度とするのが好ましい。
【００１９】
油剤とする場合には、乳剤で例示された有機溶媒の他、灯油、重油、スピンドル油などの炭化水素溶媒を用いて製剤化する。油剤は、製剤を１００重量部としたとき、有効成分量が１〜５０重量部、アルコール系溶媒が１０〜５０重量部、残部を炭化水素溶媒とするのが好ましい。
【００２０】
粉剤とする場合には、通常、有効成分を固体希釈剤（例えばカオリン、クレー、ベントナイト、ＣＭＣ、二酸化チタン、ホワイトカーボン、タルク、木粉、澱粉、デキストリン、シリカゲル粉末、水酸化カルシウムなどのカルシウム塩、無水石膏など）で希釈し、混合粉砕して製剤化する。
また、粒剤とする場合には、前記粉剤を成形して製剤化する。
粉剤および粒剤のような固型剤は、製剤を１００重量部としたとき、有効成分量が１〜５０重量部、残部を固体希釈剤とするのが好ましい。
【００２１】
また、エアゾール剤とする場合には、有機溶媒としては、水溶剤で例示された有機溶媒を使用することができる。また、噴射剤としては、代替フロン、液化天然ガスを好適に用いることができる。使用時には、これを噴霧部と弁を備えた気密容器に加圧充填して用いる。
【００２２】
この発明によれば、ココナットアミンアセテートを有効成分とする木材防腐剤で木材を処理することを特徴とする木材の処理方法が提供される。具体的には、木材処理用の減圧・加圧可能な注入缶、薬液貯蔵・回収用タンクおよびこれらを接続する配管から構成される木材注入処理系内で、木材を常法により処理することからなる木材の防腐処理方法が提供される。
木材の処理方法は、この減圧・加圧注入法のほかに、噴霧、塗布、浸漬などの通常の方法であってもよい。
【００２３】
この方法で木材に注入されるべき処理剤中のココナットアミンアセテートの量は、処理される木材の種類や用途、形状によっても左右されるが、通常、木材１ｍ３当たり、約１〜３０ｋｇである。そのためには処理液中のココナットアミンアセテートの濃度を５〜１５０ｇ／ｋｇとすると都合がよい。
【００２４】
この発明の木材防腐剤は、多くの既存の木材防腐・防蟻・防カビ剤と混合して使用することができる。特に、ヒノキチオール（別名：β−ツヤプリシン）、α−ツヤプリシン、γ−ツヤプリシン、β−ドラブリンなどのトロポロン系化合物と混合して使用するのが好ましい実施態様である。
【００２５】
その他、混合できる木材防腐剤としては、例えば、４−クロルフェニル−３−ヨードプロパギルフォルマール、３−エトキシカルビニルオキシ−１−ブロム−１，２−ヨードプロペン、３−ヨード−２−ユーピロベニルブチルカーバメートなどの有機ヨード系化合物類、ナフテン酸銅、ナフテン酸亜鉛などのナフテン酸金属塩類、Ｎ−ニトロン−シクロヘキシルヒドロキシルアミンアルミニウムなどのヒドロキシルアミン系化合物類、モノクロルナフタリンなどのナフタリン系化合物類、Ｎ−メトキシ−Ｎ−シクロヘキシル−４−（２，５−ジメイルフラン）カルバリニドなどのアニリド系化合物類、Ｎ，Ｎ−ジメチル−Ｎ'−フェニル−Ｎ'（ジクロフルオロメチルチオ）スルファミドなどのハロアルキルチオ系化合物類、テトラクロルイソフタロニトリルなどのニトリル系化合物類、クレオソート油などのタール系化合物類、ジニトロフェノール、ジニトロクレゾール、クロロニトロフェノール、２，５−ジクロロ−４−ブロモフェノール、オイゲノールなどのフェノール類、ジデシルジメチルアンモニウムクロライド、デシルジメチルアンモニウムアジペート、Ｎ−アルキルベンジルメチルアンモニウムクロライド、ココアルキルアンモニウムクロライドなどの第４級アンモニウム塩類、ホルマリン、グルタルアルデヒド、パラホルムアルデヒド、桂皮アルデヒド、桂皮アルデヒド誘導体などのアルデヒド類、デカン酸、ドデカン酸、ウンデカン酸などの直鎖脂肪酸、桂皮酸、フェルラ酸などの芳香族カルボン酸、ＴＢＴＯ、トリブチルスズフタレートなどの有機スズ類、エタノール、イソプロパノール、プロパノールなどのアルコール類、５−クロロ−２−メチル−４−イソチアゾリン−３−オン、１，２−ベンゾイソチアゾリン−３−オン、２−ｎ−オクチル−４−イソチアゾリン−３−オン、４，５−ジクロロ−２−オクチル−４−イソチアゾリン−３−オン、またはそれらの金属塩などのイソチアゾロン系化合物類、その他パーメスリン、テブコナゾール、ジプロコナゾール、プロピコナゾール、アザコナゾール、２−メルカプトベンゾチアゾールなどの有機化合物類、ヒ素化合物、五酸化二ヒ素、ヒ酸水素ナトリウム、ヒ酸、クロム化合物、三酸化クロム、二クロム酸カリウム、二クロム酸ナトリウム、二クロム酸アンモニウム、銅化合物、酸化第二銅、硫酸銅、硝酸銀、ふっ化ナトリウム、けいふっ化銅、けいふっ化亜鉛、ホウ酸、ホウ酸ナトリウム、酸化アンチモンなどの無機化合物類などが挙げられる。
【００２６】
また、混合できる木材防蟻剤としては、例えばホキシム、クロルホピリス、ピリダフェンチオン、テトラクロルビンホス、フェニトロチオン、プロペンタンホスなどの有機リン系化合物類、ペルメトリン、トラロメスリン、アレスリンなどのピレスロイド系化合物類、シラフルオフェン、エントフェンブロックスなどのピレスロイド様化合物類、プロボクサル、バッサなどのカーバメイト系化合物類、トリプロピルイソシアヌレートなどのトリアジン系化合物類、モノクロルナフタリンなどのナフタリン系化合物類、オクタクロロジプロピルエーテルなどの塩素化ジアルキルエーテル添加系化合物類、イミダクロプリドなどのクロルニコチニル化合物類などが挙げられる。
【００２７】
さらに、木材防カビ剤としては、例えば２−（４−チアゾリル）ベンツイミダゾール、３−ヨード−２−プロピニルブチルカーバメート、２−（４−チオシアノメチルチオ）ベンゾチアゾール、メチレンビスチオシアネートなどが挙げられる
。
【００２８】
また、この発明の木材防腐剤は、一般に建築用、土木工事用および紙・パルプなど工業製品製造用繊維原料用の木材を対象とするが、特に環境、種々の条件などにより木材腐朽菌が発生しやすいアカマツ、スギおよびブナなどに好適に用いることができる。
【００２９】
この発明の木材防腐剤で処理された木材を、浸透性・造膜性を有する硬化型合成樹脂塗料でさらに全面塗装処理すれば、処理済みの木材を屋外で使用しても防腐有効成分の揮発や溶脱が抑制され、防腐効果がより一層補強され、屋外での長期使用にも十分耐え得る性能を付与することができる。そのような硬化型合成樹脂塗料としては、例えばポリウレタン樹脂塗料などが挙げられる。
【００３０】
【実施例】
この発明を実施例によりさらに詳細に説明するが、これらの実施例によりこの発明が限定されるものではない。
【００３１】
下記の有効成分、乳化剤および有機溶媒を混合、撹拌することにより乳剤を調製した。
製剤例１
ココナットアミンアセテート ４重量部
（花王株式会社製、アセタミン２４）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００３２】
製剤例２
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ヒバ油（ヒノキチオールを２重量％含有） ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００３３】
製剤例３
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ホウ酸 ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００３４】
製剤例４
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ホウ酸ナトリウム ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００３５】
製剤例５
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
４−クロルフェニル−３−ヨードプロパギルフォルマール ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００３６】
製剤例６
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ナフテン酸銅 ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
テレピン油 １０重量部
水 ７２重量部
【００３７】
製剤例７
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ナフテン酸亜鉛 ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
テレピン油 １０重量部
水 ７２重量部
【００３８】
製剤例８
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ジデシルジメチルアンモニウムクロライド ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００３９】
製剤例９
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ポリオキシエチレンココアルキルメチルアンモニウムクロライド ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４０】
製剤例１０
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ココアルキルビス(2-ヒドロキシエチル)メチルアンモウムクロライド ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４１】
製剤例１１
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ココアルキルビストリメチルアンモニウムクロライド ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４２】
製剤例１２
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ジデシルジメチルアンモニウムアジペート ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４３】
製剤例１３
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
ジプロコナゾール ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４４】
製剤例１４
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
プロピコナゾール ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４５】
製剤例１５
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
テブコナゾール ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４６】
製剤例１６
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
アザコナゾール ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４７】
製剤例１７
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
３−ヨード−２−プロピニルブチルカーバメート ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４８】
製剤例１８
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
５−クロル−２−メチル−４−イソチアゾリン−３−オン ２重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８２重量部
【００４９】
製剤例１９
ココナットアミンアセテート ２重量部
（花王株式会社製、アセタミン２４）
桂皮アルデヒド ２重量部
塩酸ヒドロキシルアミン １重量部
水酸化ナトリウム ０．６重量部
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−２０ｃ）
ノニオン系界面活性剤 ２重量部
（三洋化成株式会社製、イオネットＴ−６０ｃ）
ジエチレングリコールモノメチルエーテル（ＭＤＧ） １０重量部
水 ８０．４重量部
【００５０】
試験例１（木材腐朽菌抑制効果確認試験）
（Ｂ培地の調製）
ペプトン ５ｇ
マルトエキス １０ｇ
グルコース ２５ｇ
リン酸二水素カリウム ３ｇ
硫酸マグネシウム・７水和物 ２ｇ
上記組成に純水を添加して１０００ｍｌ溶液を調製した後、寒天２０ｇを添加して、Ｂ培地を得た。
【００５１】
農林水産省森林総合研究所（ＦＦＰＲＩ）で分離した木材防腐剤防腐性能試験用標準菌より継代培養したカワラタケ（Trametes versicolor(L.:Fr.)Pilat FFPRI 1030、以下「ＣＯＶ」と略す。）とオオウズラタケ（Fomitopsis palustris(Berk.et Curt.)Gilbn.&Ryv. FFPRI 0507、以下「ＴＹＰ」と略す。）を接種し、予め２６〜２７℃で一週間培養した。滅菌済みのペトリ皿に、表１に示す供試薬剤２ｍＬずつを表１に記載の各濃度になるように添加した後、別に調製したＢ培地１８ｍＬを添加、混合し凝固させた後、一夜静置した。予め培養したＣＯＶおよびＴＹＰを直径５ｍｍの円筒状に取り出し、一夜静置したＢ培地の中央部に接種した。接種から経日的に菌糸が成長した培地面積を算出した（単位：ｃｍ２）。得られた結果を供試薬剤およびその添加量と共に表１に示す。
なお、ココナットアミンアセテートとしては「アセタミン２４」（花王株式会社製）を用いた。
【００５２】
【表１】
試験例２（木材防腐効果確認試験）
製剤例２につき、試験菌種としてＣＯＶとＴＹＰを用い、スギ辺材（木口面：２０×２０ｍｍ、高さ：１０ｍｍ）において、ＪＩＳ Ｋ１５７１で規定された「木材防腐剤の性能基準及び試験方法」に準じて木材防腐試験を行なった。その結果を表２に示す。
【００５４】
【表２】
【発明の効果】
この発明によれば、オオウズラタケ、カワラタケおよびナミダタケなどの木材腐朽菌に対して強力な防除効果を発揮し、かつ安全性の高い木材防腐剤を提供することができる。[0001]
[Field of the Invention]
The present invention relates to a wood preservative and a method for treating wood using the same. More specifically, the present invention relates to a wood preservative with excellent safety capable of preventing or suppressing the decay of wood caused by Prunus edulis, Kawaratake, Namidatake, and the like, and a method for treating wood using the same.
[0002]
[Prior art]
Wood is widely used in various fields due to its excellent characteristics such as light weight, high strength, ease of processing, and gentleness to the human body. However, it has some disadvantages that are unavoidable because it is a biological material, that is, flammable, crazy, easily rotted, easily eaten by insects, easily discolored, and easily broken. Preventing these disadvantages, especially decay caused by wood-rotting fungi and insects caused by termites, is essential for extending the service period of wood and improving the reliability of wood products. This makes it possible to make more effective use of wood as a resource and thus contribute greatly to the conservation of the global environment.
[0003]
In view of such points, as an agent for controlling wood decay fungi, that is, as a wood preservative, an organic agent such as a phenol compound, an organic halogen compound, an organic tin compound, a naphthenic acid compound and a tar compound, Consists of copper compound, CCA agent which is a mixture of chromium compound and arsenic compound, combined use of copper compound and organic agent, and quaternary ammonium salt, boric acid compound, water-soluble alkanolamine and zinc ion supply compound Wood preservatives have been proposed.
[0004]
Most of the wood preservatives mentioned above contain heavy metals, halogen compounds or compounds that are suspected of causing carcinogenicity, and there are problems in terms of safety and environmental impact during injection, operation and disposal. there were.
Therefore, early development of wood preservatives that combine excellent safety and sustained efficacy is desired.
[0005]
[Problems to be solved by the invention]
It is an object of the present invention to provide a highly safe wood preservative that exerts a strong control effect against wood-rotting fungi such as Ozuratake, Kawaratake and Namidatake.
[0006]
[Means for Solving the Problems]
The inventors of the present invention conducted intensive research to solve the above-mentioned problems, and as a result, found the fact that coconut amine acetate has a remarkable wood preservative effect and completed the present invention.
[0007]
Thus , according to the present invention, there is provided a wood preservative characterized by containing coconut amine acetate as an active ingredient.
[0008]
According to the present invention, there is also provided a method for preserving wood, characterized in that wood is treated with a wood preservative containing coconut amine acetate as an active ingredient.
[0009]
DETAILED DESCRIPTION OF THE INVENTION
Examples of the alkylamine acetate used in the present invention include coconut amine acetate and stearylamine acetate, and those commercially available as cationic surfactants can be suitably used.
[0010]
As the dosage form of the wood preservative of this invention, there are various types such as a liquid agent (for example, an aqueous solvent, an emulsion, a wettable powder (flowable preparation), an oil agent), a solid mold (for example, a powder agent, a granule), an aerosol agent, etc. Although dosage forms are possible, aqueous solvents, emulsions or oils are preferred. Any of the above preparations can be formulated using a known method.
Below, the formulation method of the wood preservative of this invention is described.
[0011]
When an aqueous solvent is used, the active ingredient is usually dissolved in an organic solvent such as an alcohol solvent and added to a surfactant and water to prepare a formulation. In addition, a resin emulsion may be added to the aqueous solvent as necessary for forming a film when the aqueous solvent is applied to wood.
[0012]
As the surfactant, any of a cationic surfactant, an anionic surfactant, a nonionic surfactant, and an amphoteric surfactant can be used, but a nonionic surfactant is preferable in terms of stability of the preparation. Examples of nonionic surfactants include sorbitan fatty acid esters (HLB: 14.9, 16.7).
[0013]
Examples of the resin emulsion include a polyvinyl acetate resin emulsion (resin solid content ratio 40 to 50%, average molecular weight 2,000 to 100,000), a polyvinyl acetate / ethylene copolymer resin emulsion (resin solid content ratio). 40-50%, average molecular weight 2,000-100,000), polyacrylate resin emulsion (resin solid fraction 30-40%, viscosity 100-500 cPs, average molecular weight 3,000-50,000). .
[0014]
In the case of preparing an emulsion, usually, an active ingredient dissolved in an organic solvent is added to a surfactant, and water is appropriately added to prepare a formulation. As the surfactant, those exemplified for the aqueous solvent can be used. Further, for the formation of a film when the emulsion is coated on wood, a resin emulsion exemplified by an aqueous solvent may be added to the emulsion as necessary. In the emulsion, a hydrophobic organic solvent is preferably used as the organic solvent for dissolving the active ingredient.
[0015]
Examples of organic solvents that can be suitably used when the wood preservative of the present invention is used as an emulsion are shown below.
1) Aliphatic hydrocarbon n-hexane, cyclohexane, heptane, octane, etc. 2) Aromatic hydrocarbon xylene, toluene, ethylbenzene, cumene, monoisopropylnaphthalene, diisopropylnaphthalene, monoisopropylbiphenyl, etc. 3) Ester ethyl acetate, 4) Alcohol isobutanol, sec-butanol, 2-ethyl-1-butanol, isopentanol, 1-heptanol, 1-octanol, neopentyl alcohol, diethylene glycol monomethyl ether ( MDG), diethylene glycol (DEG), diethylene glycol monobutyl ether (BDG), 2-hydroxyethyl butyl ether (BG), propylene glycol monomethyl ether (M 5) Ketone-based acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl amyl ketone, cyclohexanone, etc. 6) The above organic solvents such as carbonate propylene carbonate can be used alone or in combination of two or more.
[0016]
In the case of using an aqueous solvent, the active ingredient dissolved in an alcohol solvent is usually added to a surfactant and water for preparation. It is preferable that the amount of the active ingredient is 1 to 50 parts by weight and the remainder is an organic solvent, a surfactant and water when the formulation is 100 parts by weight. These aqueous solvents are used by diluting with water at a predetermined magnification, for example, 1 to 10 times, preferably 1 to 5 times.
[0017]
In the case of preparing an emulsion, usually, an active ingredient dissolved in an organic solvent is added to a surfactant, and water is appropriately added to prepare a formulation. When the formulation is 100 parts by weight, the amount of the active ingredient may be 1 to 50 parts by weight, and the remainder may be added an organic solvent and a surfactant, and water may be added as appropriate. These emulsions can be used after diluting with water at a predetermined magnification, for example, 2 to 10 times.
[0018]
Further, in the case of a wettable powder (flowable preparation), when the preparation is 100 parts by weight, the active ingredient is 1 to 50 parts by weight, an emulsifier or a thickener (for example, polyacrylic acid or a salt thereof, polyvinyl alcohol). Is preferably about 10 to 40 parts by weight.
[0019]
In the case of an oil agent, it is formulated using a hydrocarbon solvent such as kerosene, heavy oil, spindle oil, etc. in addition to the organic solvent exemplified in the emulsion. When the formulation is 100 parts by weight, the amount of the active ingredient is preferably 1 to 50 parts by weight, the alcohol solvent is 10 to 50 parts by weight, and the remainder is preferably a hydrocarbon solvent.
[0020]
In the case of powders, the active ingredient is usually a solid diluent (eg kaolin, clay, bentonite, CMC, titanium dioxide, white carbon, talc, wood powder, starch, dextrin, silica gel powder, calcium hydroxide, etc.) , Diluted with anhydrous gypsum, etc.), mixed and pulverized into a formulation.
Moreover, when setting it as a granule, the said powder agent is shape | molded and formulated.
Solid dosages such as powders and granules preferably contain 1 to 50 parts by weight of the active ingredient and the remainder as a solid diluent when the formulation is 100 parts by weight.
[0021]
Moreover, when setting it as an aerosol agent, the organic solvent illustrated by the water solvent can be used as an organic solvent. Further, as the propellant, alternative chlorofluorocarbon and liquefied natural gas can be suitably used. At the time of use, this is used by pressurizing and filling an airtight container provided with a spray part and a valve.
[0022]
According to the present invention, there is provided a wood treatment method characterized by treating wood with a wood preservative containing coconut amine acetate as an active ingredient. Specifically, wood is treated in a conventional manner in a wood injection treatment system consisting of a decompression / pressurization injection can for wood treatment, a tank for chemical storage / recovery, and piping connecting them. A method for preserving wood is provided.
The wood treatment method may be a normal method such as spraying, coating, or dipping in addition to the reduced pressure / pressure injection method.
[0023]
The amount of coconut amine acetate in the treatment agent to be injected into the wood by this method depends on the type, use and shape of the wood to be treated, but is usually about 1-30 kg per 1 m 3 of wood. is there. For this purpose, it is convenient to set the concentration of coconut amine acetate in the treatment liquid to 5 to 150 g / kg.
[0024]
The wood preservative of the present invention can be used by mixing with many existing wood preservatives / anticides / mold inhibitors. In particular, it is a preferred embodiment to be used by mixing with a tropolone-based compound such as hinokitiol (also known as β-tyaprisin), α-tyaprisin, γ-tyaprisin, β-drabrin and the like.
[0025]
Other wood preservatives that can be mixed include, for example, 4-chlorophenyl-3-iodopropargyl formal, 3-ethoxycarbvinyloxy-1-bromo-1,2-iodopropene, 3-iodo-2-you Organic iodo compounds such as pyrobenyl butyl carbamate, naphthenic acid metal salts such as copper naphthenate and zinc naphthenate, hydroxylamine compounds such as N-nitrone-cyclohexylhydroxylamine aluminum, and naphthalene compounds such as monochloronaphthalene , Anilide compounds such as N-methoxy-N-cyclohexyl-4- (2,5-dimethylfuran) carbalinide, haloalkylthio such as N, N-dimethyl-N′-phenyl-N ′ (dichlorofluoromethylthio) sulfamide Compounds, tetrachloroiso Nitrile compounds such as talonitrile, tar compounds such as creosote oil, phenols such as dinitrophenol, dinitrocresol, chloronitrophenol, 2,5-dichloro-4-bromophenol, eugenol, didecyldimethylammonium chloride , Quaternary ammonium salts such as decyldimethylammonium adipate, N-alkylbenzylmethylammonium chloride, cocoalkylammonium chloride, aldehydes such as formalin, glutaraldehyde, paraformaldehyde, cinnamaldehyde, cinnamaldehyde derivatives, decanoic acid, dodecanoic acid , Straight chain fatty acids such as undecanoic acid, aromatic carboxylic acids such as cinnamic acid and ferulic acid, organotins such as TBTO and tributyltin phthalate, etano Alcohol, isopropanol, propanol, 5-chloro-2-methyl-4-isothiazolin-3-one, 1,2-benzisothiazolin-3-one, 2-n-octyl-4-isothiazoline-3- , 4,5-dichloro-2-octyl-4-isothiazolin-3-one, or isothiazolone compounds such as metal salts thereof, other permethrin, tebuconazole, diproconazole, propiconazole, azaconazole, 2-mercapto Organic compounds such as benzothiazole, arsenic compound, arsenic pentoxide, sodium hydrogen arsenate, arsenic acid, chromium compound, chromium trioxide, potassium dichromate, sodium dichromate, ammonium dichromate, copper compound, oxidation Cupric, copper sulfate, silver nitrate, sodium fluoride, copper fluorofluoride, Ifukka zinc borate, sodium borate, and the like inorganic compounds such as antimony oxide.
[0026]
Examples of wood ant control agents that can be mixed include organophosphorus compounds such as phoxime, chlorhopilis, pyridafenthion, tetrachlorvinphos, fenitrothion, and propentanephos, pyrethroid compounds such as permethrin, tralomethrin, and allethrin, silafluophene, Pyrethroid-like compounds such as enphenblox, carbamate compounds such as provoxal and bassa, triazine compounds such as tripropyl isocyanurate, naphthalene compounds such as monochloronaphthalene, chlorinated dialkyls such as octachlorodipropyl ether Examples include ether-added compounds and chlornicotinyl compounds such as imidacloprid.
[0027]
Furthermore, examples of the wood fungicide include 2- (4-thiazolyl) benzimidazole, 3-iodo-2-propynylbutyl carbamate, 2- (4-thiocyanomethylthio) benzothiazole, methylenebisthiocyanate, and the like.
[0028]
The wood preservatives of the present invention are generally intended for wood for construction, civil engineering, and fiber raw materials for manufacturing industrial products such as paper and pulp. However, wood decay fungi are generated especially by the environment and various conditions. It can be suitably used for red pine, cedar, beech and the like.
[0029]
If the wood treated with the wood preservative of the present invention is further fully coated with a curable synthetic resin paint having penetrability and film-forming properties, volatilization of the preservative active ingredient can be achieved even when the treated wood is used outdoors. And leaching are suppressed, the antiseptic effect is further reinforced, and performance that can sufficiently withstand long-term outdoor use can be imparted. Examples of such curable synthetic resin paints include polyurethane resin paints.
[0030]
【Example】
The present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples.
[0031]
An emulsion was prepared by mixing and stirring the following active ingredients, an emulsifier and an organic solvent.
Formulation Example 1
4 parts by weight of coconut amine acetate (Acetamine 24, manufactured by Kao Corporation)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 2
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Hiba oil (containing 2% by weight of hinokitiol) 2 parts by weight nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 3
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Boric acid 2 parts by weight Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 4
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Sodium borate 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Kasei Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 5
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
4-chlorophenyl-3-iodopropargyl formal 2 parts by weight nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 6
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Copper naphthenate 2 parts by weight Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Turpin oil 10 parts by weight Water 72 parts by weight
Formulation Example 7
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Zinc naphthenate 2 parts by weight Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Turpin oil 10 parts by weight Water 72 parts by weight
Formulation Example 8
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Didecyldimethylammonium chloride 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Chemical Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 9
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Polyoxyethylene cocoalkylmethylammonium chloride 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Kasei Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 10
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Cocoalkylbis (2-hydroxyethyl) methylammonium chloride 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Chemical Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 11
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Cocoalkylbistrimethylammonium chloride 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Kasei Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 12
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Didecyldimethylammonium adipate 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Kasei Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 13
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Diproconazole 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Kasei Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 14
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Propiconazole 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Kasei Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 15
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Tebuconazole 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Kasei Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 16
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Azaconazole 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Kasei Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 17
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
3-Iodo-2-propynyl butyl carbamate 2 parts by weight Nonionic surfactant 2 parts by weight (Sanyo Kasei Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 18
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
2-chloro-2-methyl-4-isothiazolin-3-one 2 parts by weight nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 82 parts by weight
Formulation Example 19
2 parts by weight of coconut amine acetate (made by Kao Corporation, acetamine 24)
Cinnamic aldehyde 2 parts by weight Hydroxylamine hydrochloride 1 part by weight Sodium hydroxide 0.6 part by weight Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Industries, Ionette T-20c)
Nonionic surfactant 2 parts by weight (manufactured by Sanyo Chemical Co., Ltd., Ionette T-60c)
Diethylene glycol monomethyl ether (MDG) 10 parts by weight Water 80.4 parts by weight
Test Example 1 (Confirmation test for inhibiting wood decay fungi)
(Preparation of medium B)
Peptone 5g
10g malt extract
Glucose 25g
Potassium dihydrogen phosphate 3g
Magnesium sulfate heptahydrate 2g
Pure water was added to the above composition to prepare a 1000 ml solution, and then 20 g of agar was added to obtain B medium.
[0051]
Kawaratake (Trametes versicolor (L .: Fr.) Pilat FFPRI 1030, hereinafter abbreviated as “COV”) subcultured from a standard fungus for preservatives of wood preservatives isolated by the Forestry Research Institute of Agriculture, Forestry and Fisheries (FFPRI) And Ozuuratake (Fomitopsis palustris (Berk. Et Curt.) Gilbn. & Ryv. FFPRI 0507, hereinafter abbreviated as “TYP”), and cultured in advance at 26 to 27 ° C. for one week. To each sterilized petri dish, 2 mL of the reagent agent shown in Table 1 is added to each concentration shown in Table 1, 18 mL of B medium prepared separately is added, mixed and coagulated, and then allowed to stand overnight. I put it. Pre-cultured COV and TYP were taken out in a cylindrical shape with a diameter of 5 mm and inoculated into the central part of B medium which was allowed to stand overnight. The area of the medium in which the mycelium grew day after inoculation was calculated (unit: cm 2 ). The obtained results are shown in Table 1 together with the reagent reagent and the amount added.
“Acetamine 24” (manufactured by Kao Corporation) was used as coconut amine acetate.
[0052]
[Table 1]
Test example 2 (wood antiseptic effect confirmation test)
For Formulation Example 2, COV and TYP were used as the test strains, and the performance standards and test methods for wood preservatives defined by JIS K1571 for cedar sapwood (Kiguchi surface: 20 × 20 mm, height: 10 mm) A wood preservative test was conducted according to the above. The results are shown in Table 2.
[0054]
[Table 2]
【The invention's effect】
According to the present invention, it is possible to provide a highly safe wood preservative that exerts a powerful control effect against wood-rotting fungi such as Prunus edulis, Kawaratake and Namidatake.
Claims (5)