  The present invention relates to an adhesive optical film. Furthermore, the present invention relates to an image display device such as a liquid crystal display device, an organic EL display device, a CRT, or a PDP using the adhesive optical film.

  The pressure-sensitive adhesive optical film of the present invention has a liquid crystal optical compensation layer and is useful as an optical compensation film for improving display contrast and viewing angle characteristics of display colors. It is useful as an elliptically polarizing plate with an optical compensation function. In particular, the liquid crystal optical compensation layer is useful in the case of a discotic liquid crystal layer in which a discotic liquid crystal compound is aligned.

  Liquid crystal display devices are rapidly marketed in watches, mobile phones, PDAs, notebook computers, personal computer monitors, DVD players, TVs, and the like. A liquid crystal display device visualizes a change in polarization state due to switching of liquid crystal, and a polarizer is used from the display principle. In particular, displays with higher brightness and higher contrast are required for applications such as TV, and light polarizers with higher brightness (high transmittance) and higher contrast (high polarization degree) have been developed and introduced. Yes.

  At present, the mainstream method of a general liquid crystal display device is a TFT-LCD using a TN liquid crystal. This method has advantages such as high response speed and high contrast. However, when the display of a panel using TN liquid crystal is viewed from an angle inclined from the normal direction, the contrast is remarkably lowered, and gradation inversion that reverses the gradation display occurs. It has the characteristic that the viewing angle is narrow. On the other hand, in applications such as large PC monitors and televisions, high contrast, wide viewing angle, and small display color change due to viewing angle are required. Therefore, when a TN mode TFT-LCD is used for such applications, a retardation film for compensating the viewing angle is indispensable.

  As this retardation film, a stretched birefringent polymer film has been conventionally used. Recently, it has been proposed to use an optical compensation film having an optically anisotropic layer formed of liquid crystalline molecules on a transparent support, instead of an optical compensation film made of a stretched birefringent film. Since liquid crystal molecules have various alignment forms, it has become possible to realize optical properties that cannot be obtained with conventional stretched birefringent polymer films by using liquid crystal molecules.

  As a viewing angle compensation retardation film as described above, for example, a wide view film manufactured by Fuji Photo Film Co., Ltd. using a discotic liquid crystal having negative refractive index anisotropy has been proposed (Patent Document 1, Patent Document 2). This retardation film has a discotic liquid crystal layer having an optical axis inclined and oriented on one side of a transparent substrate film. This retardation film is mainly intended to improve viewing angle characteristics in a voltage application state for black display. That is, in a voltage application state, the liquid crystal molecules in the liquid crystal cell exhibit positive refractive index anisotropy having an optical axis inclined from the glass substrate. In order to compensate for the retardation due to the refractive index anisotropy, the retardation film uses a liquid crystalline molecule having an optical axis inclined from the normal direction of the film and having negative refractive index anisotropy.

  In the retardation film for compensating the viewing angle, a polarizer is laminated on the transparent substrate film and used as an elliptically polarizing plate, while an adhesive layer is laminated on the discotic liquid crystal layer. An adhesive optical film such as a retardation film or an elliptically polarizing plate on which the pressure-sensitive adhesive layer is laminated is used by being bonded to a liquid crystal cell or the like via the pressure-sensitive adhesive layer. However, when the above-mentioned retardation film or elliptically polarizing plate for viewing angle compensation is combined with a liquid crystal cell or the like via an adhesive layer together with a backlight (lighted state), a liquid crystal display There is a problem that unevenness (hereinafter referred to as window frame unevenness) occurs in the vicinity of the frame of the apparatus, and visibility is lowered. In particular, when the temperature is increased or the size of the liquid crystal display device is increased, the window frame unevenness becomes remarkable.

  If a liquid crystal display device or the like in which the elliptically polarizing plate or the like is bonded to a liquid crystal cell or the like through an adhesive layer is left under heating conditions, there is a problem that the hue differs between the central portion and the outer peripheral portion of the polarizer. (Hereafter, this is called frame unevenness). Frame unevenness occurs as a phenomenon different from window frame unevenness. In order to solve the frame unevenness, for example, it has been proposed to add an antioxidant (0.001 to 3 parts by weight to 100 parts by weight of the base polymer of the adhesive) in the adhesive layer (Patent Document 3). ). However, in the case where the antioxidant is mixed in the pressure-sensitive adhesive layer as described above, the problem of window frame unevenness cannot be solved even if the frame unevenness can be solved.

JP-A-8-95032 Japanese Patent No. 2767382 JP 2003-49143 A

  The present invention is a pressure-sensitive adhesive optical film having a liquid crystal optical compensation layer on one side of a transparent substrate film, and further having a pressure-sensitive adhesive layer laminated on the liquid crystal optical compensation layer, and a lighting state of a backlight It aims at providing the adhesive optical film which can suppress the window frame nonuniformity in.

  Another object of the present invention is to provide an image display device using the adhesive optical film.

  As a result of intensive studies to solve the above problems, the present inventors have found that the above object can be achieved by the following pressure-sensitive adhesive optical film, and have completed the present invention.

That is, the present invention is an adhesive optical film in which an adhesive layer is provided on the liquid crystal optical compensation layer of an optical film having a liquid crystal optical compensation layer on one side of a transparent substrate film via an undercoat layer.
The undercoat layer relates to a pressure-sensitive adhesive optical film characterized by containing polymers and an antioxidant.

  In the pressure-sensitive adhesive optical film, the undercoat layer preferably contains 0.01 to 1000 parts by weight of an antioxidant with respect to 100 parts by weight of the polymers. In particular, the undercoat layer preferably contains 5 to 1000 parts by weight of an antioxidant with respect to 100 parts by weight of the polymers.

  The adhesive optical film can be suitably applied when the liquid crystal optical compensation layer is a discotic liquid crystal layer.

  In the pressure-sensitive adhesive optical film, the polymer of the undercoat layer is preferably a polymer having a primary amino group at the terminal. The polymer having a primary amino group at the terminal is preferably a poly (meth) acrylic acid ester having a primary amino group at the terminal.

  In the adhesive optical film, the antioxidant is preferably at least one selected from phenol-based, phosphorus-based, sulfur-based and amine-based antioxidants.

  In the pressure-sensitive adhesive optical film, the pressure-sensitive adhesive layer is preferably formed of an acrylic pressure-sensitive adhesive containing an acrylic polymer and a crosslinking agent, and the crosslinking agent preferably contains a peroxide.

  In the pressure-sensitive adhesive optical film, as the optical film, a film in which a polarizer is laminated on one side of a transparent substrate film on the side where a liquid crystal optical compensation layer is not formed can be used.

  The present invention also relates to an image display device using the adhesive optical film.

  Conventionally, a liquid crystal display device using an adhesive optical film having a liquid crystal optical compensation layer that functions as an optical compensation layer has a front phase difference in the window frame portion more than the front portion when the backlight is lit for a long time As the value increased, window frame unevenness occurred. In the pressure-sensitive adhesive optical film of the present invention, the liquid crystal optical compensation layer is provided with a pressure-sensitive adhesive layer through an undercoat layer containing polymers and an antioxidant. Window frame unevenness due to an increase in the phase difference value can be suppressed. The window frame unevenness is likely to occur when the liquid crystal optical compensation layer is a discotic liquid crystal layer. Therefore, the present invention is particularly effective when the discotic liquid crystal layer is used as an optical compensation layer.

  Since the window frame unevenness is likely to occur when the liquid crystal display device is large, the adhesive optical film of the present invention is particularly effective for an adhesive optical film having a large size. Moreover, since window frame unevenness is likely to occur when the environmental temperature is high, the adhesive optical film of the present invention is particularly effective for an adhesive optical film used in a high temperature environment.

  The pressure-sensitive adhesive optical film of the present invention is suitable when the pressure-sensitive adhesive layer is formed of an acrylic pressure-sensitive adhesive containing an acrylic polymer and a crosslinking agent, and a peroxide is used as the crosslinking agent. It is. When a peroxide is used as the crosslinking agent for the pressure-sensitive adhesive, a trace amount of peroxide remaining in the pressure-sensitive adhesive layer or an acid formed by decomposition of the peroxide may affect the liquid crystal optical compensation layer. However, according to the pressure-sensitive adhesive optical film of the present invention, the residual peroxide or acid or the like exerts on the liquid crystal optical compensation layer by adding an antioxidant to the undercoat layer. Influence can be suppressed and window frame unevenness can be suppressed.

  The present invention will be described below with reference to the drawings. As shown in FIG. 1, the pressure-sensitive adhesive optical film of the present invention has a liquid crystal optical compensation layer (for example, a discotic liquid crystal layer) 3 on one side of a transparent substrate film 1, and the liquid crystal optical compensation layer 3 has The pressure-sensitive adhesive layer 5 is provided via the undercoat layer 4. Although FIG. 1 illustrates the case where the alignment film 2 is provided between the transparent base film 1 and the liquid crystal optical compensation layer 3, instead of the alignment film 2, one side of the transparent base film 1 is rubbed. Can be used.

  2 shows the adhesive optical film of FIG. 1 in which a polarizer 6 and then a transparent protective film 7 are laminated on one side of the transparent substrate film 1 on the side where the liquid crystal optical compensation layer 3 is not formed. This is the case. In FIG. 2, the transparent substrate film 1 also serves as a transparent protective film for the polarizer 6.

  Various transparent materials can be used as the transparent substrate film. For example, polyester polymers such as polyethylene terephthalate and polyethylene naphthalate, cellulose polymers such as diacetyl cellulose and triacetyl cellulose, acrylic polymers such as polymethyl methacrylate, styrene such as polystyrene and acrylonitrile / styrene copolymer (AS resin) -Based polymer, polycarbonate-based polymer and the like. In addition, polyethylene, polypropylene, polyolefins having a cyclo or norbornene structure, polyolefin polymers such as ethylene / propylene copolymers, vinyl chloride polymers, amide polymers such as nylon and aromatic polyamide, imide polymers, sulfone polymers , Polyether sulfone polymer, polyether ether ketone polymer, polyphenylene sulfide polymer, vinyl alcohol polymer, vinylidene chloride polymer, vinyl butyral polymer, arylate polymer, polyoxymethylene polymer, epoxy polymer, or the above Polymer blends and the like are also examples of polymers that form the transparent substrate film.

  Moreover, the polymer film described in JP-A-2001-343529 (WO01 / 37007), for example, (A) a thermoplastic resin having a substituted and / or unsubstituted imide group in the side chain, and (B) a substitution in the side chain And / or a resin composition containing a thermoplastic resin having unsubstituted phenyl and a nitrile group. A specific example is a film of a resin composition containing an alternating copolymer composed of isobutylene and N-methylmaleimide and an acrylonitrile / styrene copolymer. As the film, a film made of a mixed extruded product of the resin composition or the like can be used.

  Although the thickness of a transparent base film can be determined suitably, generally it is about 1-500 micrometers from points, such as workability | operativity, such as intensity | strength and handleability, and thin film property. In particular, 5 to 200 μm is preferable.

  Moreover, it is preferable that a transparent base film has as little coloring as possible. Therefore, Rth = (nx−nz) · d (where nx is the refractive index in the slow axis direction in the film plane, nz is the refractive index in the film thickness direction, and d is the film thickness). A protective film having a direction retardation of −90 nm to +75 nm is preferably used. By using a film having a retardation value (Rth) in the thickness direction of −90 nm to +75 nm, the coloring (optical coloring) of the polarizing plate caused by the transparent substrate film can be almost eliminated. The thickness direction retardation (Rth) is more preferably -80 nm to +60 nm, and particularly preferably -70 nm to +45 nm.

  The transparent substrate film is preferably a cellulose polymer such as triacetyl cellulose or a norbornene polymer from the viewpoints of polarization characteristics and durability. In particular, a cellulose polymer such as triacetylcellulose is preferable.

  For forming the liquid crystal optical compensation layer, for example, a polymerizable liquid crystal monomer and / or a liquid crystal polymer are used. These polymerizable liquid crystal monomers and / or liquid crystal polymers can form a liquid crystal optical compensation layer by being oriented and cured (solidified) after coating on a transparent substrate film. When the polymerizable liquid crystal monomer is used, a photopolymerization initiator is usually used. Various photopolymerization initiators can be used without particular limitation.

  An example of the optical compensation layer is a discotic liquid crystal layer. The discotic liquid crystal layer is formed by alignment and curing of a discotic liquid crystal compound having a polymerizable unsaturated group. The discotic liquid crystal layer is useful as an optical compensation layer, and can improve the viewing angle, contrast, brightness, and the like. The discotic liquid crystal compound has a polymerizable unsaturated group, and the discotic liquid crystal layer is formed by aligning and curing the compound. The discotic liquid crystal layer is preferably one in which a discotic liquid crystal compound is tilted. The thickness of the discotic liquid crystal layer is usually about 0.5 to 10 μm.

  The discotic liquid crystal compound has a negative refractive index anisotropy (uniaxiality). Destrade et al., Mol. Cryst. 71, 111 (1981), benzene derivatives and B.I. Kohne et al., Angew. Chem. 96, page 70 (1984) and the cyclohexane derivatives described in J. Am. M.M. Lehn et al. Chem. Commun. , 1794 (1985), J. Am. Zhang et al., J. Am. Chem. Soc. 116, 2655 (1994), such as azacrown and phenylacetylene macrocycles, etc., which are generally used as a mother nucleus at the center of a molecule, and are a linear alkyl group or alkoxy group, substituted A structure in which a benzoyloxy group or the like is radially substituted as a straight chain thereof exhibits liquid crystallinity and includes what is generally called a discotic liquid crystal. However, the molecule itself is not limited to the above description as long as the molecule itself has negative uniaxiality and can give a certain orientation. In the present invention, the discotic liquid crystal compound has a polymerizable unsaturated group (for example, acryloyl group, methacryloyl group, vinyl group, allyl group, etc.) that undergoes a curing reaction with heat, light, or the like. Note that the discotic liquid crystal layer does not necessarily need to be a final product, and includes a liquid crystal layer that has been polymerized or cross-linked by the reaction of a polymerizable unsaturated group to increase the molecular weight and lose liquid crystallinity.

  In addition, discotic liquid crystal compounds are optical molecules such as reaction products of discotic liquid crystals that no longer exhibit liquid crystallinity due to reactions with various discotic liquid crystal compounds and other low molecular compounds and polymers. In general, it means all compounds having negative uniaxiality.

  For the alignment treatment of the discotic liquid crystal, the surface of the transparent substrate film is rubbed or an alignment film is used. Examples of the alignment film include an inorganic oblique deposition film or an alignment film obtained by rubbing a specific organic polymer film. There is a thin film in which isomerization is caused by light, such as an LB film made of an azobenzene derivative, and molecules are uniformly arranged with directionality. Examples of the organic alignment film include polyimide films, and organic polymer films that form a hydrophobic surface such as alkyl chain-modified poval, polyvinyl butyral, and polymethyl methacrylate. In addition, a SiO oblique vapor deposition film is an example of the inorganic oblique vapor deposition film.

  The discotic liquid crystal compound is tilted and aligned. For example, a discotic liquid crystal compound (polymerizable liquid crystal compound) is applied to form a tilted alignment state by forming an alignment film on a transparent substrate film. Thereafter, a method such as fixing by irradiation with light such as ultraviolet light or heat can be used. It is also possible to form the discotic liquid crystal on another alignment substrate by tilting and then transferring it onto a transparent support using an optically transparent adhesive or pressure sensitive adhesive. is there.

  As such a discotic liquid crystal layer, those described in Patent Documents 1 and 2 are preferably used. A wide-view film manufactured by Fuji Photo Film Co., Ltd. is one in which such a discotic liquid crystal inclined alignment layer is formed on a cellulosic polymer film.

  The liquid crystal optical compensation layer other than the above can be formed of, for example, a nematic liquid crystalline monomer and / or polymer.

  Examples of the nematic liquid crystalline monomer include those having a polymerizable functional group such as an acryloyl group or a methacryloyl group at the terminal and a mesogenic group composed of a cyclic unit or the like. In addition, as a polymerizable functional group, one having two or more acryloyl groups, methacryloyl groups and the like can be used to introduce a crosslinked structure to improve durability. Examples of the cyclic unit serving as a mesogenic group include biphenyl, phenylbenzoate, phenylcyclohexane, azoxybenzene, azomethine, azobenzene, phenylpyrimidine, diphenylacetylene, diphenylbenzoate, and bicyclohexane. Cyclohexylbenzene, terphenyl and the like. In addition, the terminal of these cyclic units may have substituents, such as a cyano group, an alkyl group, an alkoxy group, a halogen group, for example.

  Examples of the main chain type liquid crystal polymer include condensation polymers having a structure in which mesogenic groups composed of aromatic units or the like are bonded, for example, polymers such as polyester, polyamide, polycarbonate, and polyesterimide. Examples of the aromatic unit that becomes a mesogenic group include phenyl, biphenyl, and naphthalene types, and these aromatic units have substituents such as a cyano group, an alkyl group, an alkoxy group, and a halogen group. May be.

  Examples of the side chain type liquid crystal polymer include those having a polyacrylate-based, polymethacrylate-based, polysiloxane-based, or polymalonate-based main chain as a skeleton, and a mesogenic group composed of a cyclic unit or the like in the side chain. Examples of the cyclic unit serving as a mesogenic group include biphenyl, phenylbenzoate, phenylcyclohexane, azoxybenzene, azomethine, azobenzene, phenylpyrimidine, diphenylacetylene, diphenylbenzoate, and bicyclohexane. Cyclohexylbenzene, terphenyl and the like. In addition, the terminal of these cyclic units may have substituents, such as a cyano group, an alkyl group, an alkoxy group, a halogen group, for example.

  Any mesogenic group of the polymerizable liquid crystal monomer or the liquid crystal polymer may be bonded via a spacer portion that imparts flexibility. Examples of the spacer part include a polymethylene chain and a polyoxymethylene chain. The number of repeating structural units forming the spacer portion is appropriately determined depending on the chemical structure of the mesogenic portion, but the repeating unit of the polymethylene chain is 0 to 20, preferably 2 to 12, and the repeating unit of the polyoxymethylene chain is 0 to 0. 10, preferably 1-3.

A cholesteric liquid crystalline monomer and a chiral agent can be blended with the nematic liquid crystalline monomer and liquid crystalline polymer so as to exhibit a cholesteric phase in a liquid crystal state. A cholesteric liquid crystalline polymer can also be used. The obtained cholesteric liquid crystal phase is used as a selective reflection film. The chiral agent is not particularly limited as long as it has an optically active group and does not disturb the alignment of a nematic liquid crystalline monomer or the like. The chiral agent may or may not have liquid crystallinity, but those exhibiting cholesteric liquid crystallinity can be preferably used. As the chiral agent, those having or not having a reactive group can be used, but those having a reactive group are preferred from the viewpoint of heat resistance and solvent resistance of a cholesteric liquid crystal alignment film obtained by curing. Examples of the reactive group include an acryloyl group, a methacryloyl group, an azide group, and an epoxy group.

  The liquid crystal monomer and liquid crystal polymer can be developed on the alignment film. As the alignment film, various conventionally known ones can be used. For example, a film formed by rubbing a thin film made of polyimide, polyvinyl alcohol or the like on a transparent base material, transparent A stretched film obtained by stretching the film, a polymer having a cinnamate skeleton or an azobenzene skeleton, or a polyimide irradiated with polarized ultraviolet rays can be used.

  The undercoat layer is formed of an undercoat containing a polymer and an antioxidant. Desirably, the polymer material is a material that exhibits good adhesion to both the pressure-sensitive adhesive layer and the liquid crystal optical compensation layer and forms a film having excellent cohesive strength.

  Examples of the polymers include polyurethane resins, polyester resins, and polymers containing amino groups in the molecule. The polymer may be used in any of solvent-soluble type, water-dispersed type, and water-soluble type. For example, water-soluble polyurethane, water-soluble polyester, water-soluble polyamide, etc. and water-dispersible resins (ethylene-vinyl acetate emulsion, (meth) acrylic emulsion, etc.) can be mentioned. The water-dispersed type is obtained by emulsifying various resins such as polyurethane, polyester and polyamide using an emulsifier, or by introducing an anionic group, a cationic group or a nonionic group of a water-dispersible hydrophilic group into the resin. The self-emulsified product can be used. Moreover, an ionic polymer complex can be used.

  For example, when the pressure-sensitive adhesive layer contains an isocyanate compound, the polymer preferably has a functional group having reactivity with the isocyanate compound. As the polymers, polymers containing an amino group in the molecule are preferable. In particular, those having a primary amino group at the terminal are preferably used, and are firmly adhered by reaction with an isocyanate compound. The polymer having a primary amino group at the terminal is preferably a poly (meth) acrylic acid ester having a primary amino group at the terminal.

  Examples of polymers containing an amino group in the molecule include polymers of amino group-containing monomers such as polyethyleneimine, polyallylamine, polyvinylamine, polyvinylpyridine, polyvinylpyrrolidine, and dimethylaminoethyl acrylate. Can do. Among these, polyethyleneimine type is preferable. As the polyethyleneimine-based material, any material having a polyethyleneimine structure may be used, and examples thereof include polyethyleneimine, an ethyleneimine adduct and / or a polyethyleneimine adduct to polyacrylic acid ester. In particular, an ethyleneimine adduct and / or a polyethyleneimine adduct to a polyacrylic acid ester, which is a poly (meth) acrylic acid ester having a primary amino group at the terminal, is preferable.

  Polyethyleneimine is not particularly limited, and various types can be used. The weight average molecular weight of polyethyleneimine is not particularly limited, but is usually about 1 to 1,000,000. Examples of commercially available polyethyleneimine products include Epomin SP series (SP-003, SP006, SP012, SP018, SP103, SP110, SP200, etc.) manufactured by Nippon Shokubai Co., Ltd., and Epomin P-1000. Of these, Epomin P-1000 is preferred.

  The polyacrylic acid ester of an ethyleneimine adduct and / or a polyethyleneimine adduct to a polyacrylic acid ester is an alkyl (meth) acrylate that constitutes a base polymer (acrylic polymer) of an acrylic pressure-sensitive adhesive described later and a copolymer thereof. It can be obtained by emulsion polymerization of monomers according to a conventional method. As the copolymerization monomer, a monomer having a functional group such as a carboxyl group for reacting ethyleneimine or the like is used. The proportion of the monomer having a functional group such as a carboxyl group is appropriately adjusted depending on the proportion of ethyleneimine to be reacted. Further, as the copolymerization monomer, it is preferable to use a styrene monomer. Moreover, it can also be set as the addition product which grafted polyethyleneimine by making the polyethyleneimine separately synthesize | combined react with the carboxyl group etc. in acrylic ester. For example, as an example of a commercially available product, POLYMENT NK-380 manufactured by Nippon Shokubai Co., Ltd. can be mentioned.

  Further, an ethyleneimine adduct and / or a polyethyleneimine adduct of an acrylic polymer emulsion can be used. For example, as an example of a commercially available product, POLYMENT SK-1000 manufactured by Nippon Shokubai Co., Ltd. can be mentioned.

  In addition to the above, as a polymer having a primary amino group at the terminal, a carboxyl group or a hydroxyl group in the polyacrylate ester is reacted with an excess diisocyanate, and further reacted with an excess diamine to form a primary amino group at the terminal. What has been introduced. The poly (meth) acrylic acid ester having a primary amino group at the terminal can be obtained by copolymerizing the (meth) acrylic acid ester and a monomer having a primary amino group at the terminal. Examples of the monomer having a primary amino group at the terminal include aminoethyl (meth) acrylate and aminopropyl (meth) acrylate.

  Examples of the antioxidant contained in the undercoat layer include phenol-based, phosphorus-based, sulfur-based and amine-based antioxidants, and at least one selected from these is used. Among these, a phenolic antioxidant is preferable.

  Specific examples of phenolic antioxidants include 2,6-di-t-butyl-p-cresol, 2,6-di-t-butyl-4-ethylphenol, 2,6- Dicyclohexyl-4-methylphenol, 2,6-diisopropyl-4-ethylphenol, 2,6-di-t-amyl-4-methylphenol, 2,6-di-t-octyl-4-n-propylphenol, 2,6-dicyclohexyl-4-n-octylphenol, 2-isopropyl-4-methyl-6-t-butylphenol, 2-t-butyl-4-ethyl-6-t-octylphenol, 2-isobutyl-4-ethyl- 6-t-hexylphenol, 2-cyclohexyl-4-n-butyl-6-isopropylphenol, styrenated mixed cresol, DL- -Tocopherol, stearyl β- (3,5-di-t-butyl-4-hydroxyphenyl) propionate and the like as a bicyclic phenol compound, 2,2′-methylenebis (4-methyl-6-t-butylphenol), 4,4'-butylidenebis (3-methyl-6-t-butylphenol), 4,4'-thiobis (3-methyl-6-t-butylphenol), 2,2'-thiobis (4-methyl-6-t) -Butylphenol), 4,4'-methylenebis (2,6-di-t-butylphenol), 2,2'-methylenebis [6- (1-methylcyclohexyl) -p-cresol], 2,2'-ethylidenebis (4,6-di-t-butylphenol), 2,2'-butylidenebis (2-t-butyl-4-methylphenol), 3,6-dioxaoctamethy Renbis [3- (3-t-butyl-4-hydroxy-5-methylphenyl) propionate], triethylene glycol bis [3- (3-t-butyl-5-methyl-4-hydroxyphenyl) propionate], 1 , 6-hexanediol bis [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate], 2,2′-thiodiethylenebis [3- (3,5-di-t-butyl- 4-hydroxyphenyl) propionate] or the like as a tricyclic phenol compound, 1,1,3-tris (2-methyl-4-hydroxy-5-tert-butylphenyl) butane, 1,3,5-tris (2 , 6-Dimethyl-3-hydroxy-4-tert-butylbenzyl) isocyanurate, 1,3,5-tris [(3,5-di-tert-butyl-4-hydroxyl Nyl) propionyloxyethyl] isocyanurate, tris (4-t-butyl-2,6-dimethyl-3-hydroxybenzyl) isocyanurate, 1,3,5-trimethyl-2,4,6-tris (3,5 -Di-t-butyl-4-hydroxybenzyl) benzene or the like as a tetracyclic phenol compound, tetrakis [methylene-3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate] methane or the like, Examples of phosphorus-containing phenol compounds include bis (3,5-di-t-butyl-4-hydroxybenzylphosphonate ethyl) calcium and bis (3,5-di-t-butyl-4-hydroxybenzylphosphonate ethyl) nickel. Can be mentioned.

  Specific examples of phosphorus antioxidants include trioctyl phosphite, trilauryl phosphite, tristridecyl phosphite, trisisodecyl phosphite, phenyl diisooctyl phosphite, phenyl diisodecyl phosphite, phenyl di (tridecyl) phos Phyto, diphenylisooctyl phosphite, diphenylisodecyl phosphite, diphenyl tridecyl phosphite, triphenyl phosphite, tris (nonylphenyl) phosphite, tris (2,4-di-t-butylphenyl) phosphite, tris (Butoxyethyl) phosphite, tetratridecyl-4,4'-butylidenebis (3-methyl-6-tert-butylphenol) -diphosphite, 4,4'-isopropylidene-diphenol alkylphosphine (Wherein alkyl has about 12 to 15 carbon atoms), 4,4'-isopropylidenebis (2-t-butylphenol) .di (nonylphenyl) phosphite, tris (biphenyl) phosphite, tetra (tridecyl)- 1,1,3-tris (2-methyl-5-tert-butyl-4-hydroxyphenyl) butanediphosphite, tris (3,5-di-tert-butyl-4-hydroxyphenyl) phosphite, hydrogenation -4,4'-isopropylidenediphenol polyphosphite, bis (octylphenyl) -bis [4,4'-butylidenebis (3-methyl-6-tert-butylphenol)], 1,6-hexanediol diphosphite Hexatridecyl-1,1,3-tris (2-methyl-4-hydroxy-5-tert-butylphenol) diphosphine And tris [4,4'-isopropylidenebis (2-t-butylphenol)] phosphite, tris (1,3-distearoyloxyisopropyl) phosphite, 9,10-dihydro-9-phosphaphenanthrene -10-oxide, tetrakis (2,4-di-t-butylphenyl) -4,4'-biphenylenediphosphonite, distearyl pentaerythritol diphosphite, di (nonylphenyl) pentaerythritol diphosphite, phenyl 4,4'-isopropylidenediphenol pentaerythritol diphosphite, bis (2,4-di-t-butylphenyl) pentaerythritol diphosphite, bis (2,6-di-t-butyl-4-methyl) Phenyl) pentaerythritol diphosphite and phenylbisph Such as Nord -A- pentaerythritol diphosphite, and the like.

  As the sulfur-based antioxidant, dialkylthiodipropionate and polyhydric alcohol esters of alkylthiopropionic acid are preferably used. The dialkylthiodipropionate used here is preferably a dialkylthiodipropionate having an alkyl group having 6 to 20 carbon atoms, and the polyhydric alcohol ester of alkylthiopropionic acid is an alkyl having 4 to 20 carbon atoms. Polyalkyl alcohol esters of alkylthiopropionic acid having a group are preferred. In this case, examples of the polyhydric alcohol constituting the polyhydric alcohol ester include glycerin, trimethylolethane, trimethylolpropane, pentaerythritol, and trishydroxyethyl isocyanurate. Examples of such dialkylthiodipropionate include dilauryl thiodipropionate, dimyristyl thiodipropionate, and distearyl thiodipropionate. On the other hand, as the polyhydric alcohol ester of alkylthiopropionic acid, for example, glycerin tributylthiopropionate, glycerin trioctylthiopropionate, glycerin trilauryl thiopropionate, glycerin tristearyl thiopropionate, trimethylol ethane tributyl Thiopropionate, trimethylol ethane trioctyl thiopropionate, trimethylol ethane trilauryl thiopropionate, trimethylol ethane tristearyl thiopropionate, pentaerythritol tetrabutyl thiopropionate, pentaerythritol tetraoctyl thiopro Pionate, pentaerythritol tetralauryl thiopropionate, pentaerythritol tetrastearyl thiopropionate, etc. It can be mentioned.

  Specific examples of amine-based antioxidants include bis (2,2,6,6-tetramethyl-4-piperidyl) sebacate, dimethyl succinate and 1- (2-hydroxyethyl) -4-hydroxy-2,2 , 6,6-tetramethylpiperidineethanol polycondensate, N, N ′, N ″, N ″ ″-tetrakis- (4,6-bis- (butyl- (N-methyl-2,2,6 , 6-Tetramethylpiperidin-4-yl) amino) -triazin-2-yl) -4,7-diazadecane-1,10-diamine, dibutylamine 1,3,5-triazine N, N′-bis (2,2,6,6-tetramethyl-4-piperidyl-1,6-hexamethylenediamine and N- (2,2,6,6-tetramethyl-4-piperidyl) butylamine polycondensate, poly [ {6- (1,1,3,3-Te Lamethylbutyl) amino-1,3,5-triazine-2,4-diyl} {(2,2,6,6-tetramethyl-4-piperidyl) imino} hexamethylene {(2,2,6,6-tetra Methyl-4-piperidyl) imino}], tetrakis (2,2,6,6-tetramethyl-4-piperidyl) -1,2,3,4-butanetetracarboxylate, 2,2,6,6-tetra Methyl-4-piperidylbenzoate, bis- (1,2,6,6-pentamethyl-4-pepyridyl) -2- (3,5-di-t-butyl-4-hydroxybenzyl) -2-n-butylmalo Nate, bis- (N-methyl-2,2,6,6-tetramethyl-4-piperidyl) sebacate, 1,1 '-(1,2-ethanediyl) bis (3,3,5,5-tetramethyl Piperazinone), (Mi Xust 2,2,6,6-tetramethyl-4-piperidyl / tridecyl) -1,2,3,4-butanetetracarboxylate, (mixed 1,2,2,6,6-pentamethyl-4-piperidyl / Tridecyl) -1,2,3,4-butanetetracarboxylate, mixed [2,2,6,6-tetramethyl-4-piperidyl / β, β, β ′, β′-tetramethyl-3, 9- [2,4,8,10-tetraoxaspiro (5,5) undecane] diethyl] -1,2,3,4-butanetetracarboxylate, mixed [1,2,2,6,6- Pentamethyl-4-piperidyl / β, β, β ′, β′-tetramethyl-3,9- [2,4,8,10-tetraoxaspiro (5,5) undecane] diethyl] -1,2,3 , 4-Butanetetracarboxylate N, N'-bis (3-aminopropyl) ethylenediamine-2,4-bis [N-butyl-N- (1,2,2,6,6-pentamethyl-4-piperidyl) amino] -6-chloro- 1,3,5-triazine condensate, poly [6-N-morpholyl-1,3,5-triazine-2,4-diyl] [(2,2,6,6-tetramethyl-4-piperidyl) imino ] Hexamethylene [(2,2,6,6-tetramethyl-4-piperidyl) imide], N, N'-bis (2,2,6,6-tetramethyl-4-piperidyl) hexamethylenediamine and 1 , 2-dibromoethane condensate [N- (2,2,6,6-tetramethyl-4-piperidyl) -2-methyl-2- (2,2,6,6-tetramethyl-4- And piperidyl) imino] propionamide It can be.

  The undercoat layer contains polymers and an antioxidant, and usually contains 0.01 to 1000 parts by weight of an antioxidant with respect to 100 parts by weight of the polymers. If the usage ratio of the antioxidant is less than 0.01 parts by weight, the window frame unevenness may not be sufficiently suppressed. On the other hand, when it exceeds 1000 weight part, it is unpreferable at the point of anchoring property or an external appearance. The use ratio of the antioxidant is preferably 0.1 to 500 parts by weight, more preferably 1 to 100 parts by weight when emphasis is given to anchoring properties and appearance. On the other hand, from the viewpoint of suppressing the window frame unevenness even in a high temperature environment for a long time and at a high temperature reliability test, it is preferable that the proportion of the antioxidant used is large to some extent. The ratio is preferably 5 to 1000 parts by weight, more preferably 10 to 700 parts by weight, and further preferably 100 to 500 parts by weight.

  Moreover, in forming the undercoat layer, a crosslinking agent can be contained in addition to the polymers. For example, the compound which reacts with the polymer containing an amino group can be mixed and cross-linked to improve the strength of the undercoat layer. Examples of the compound that reacts with the polymer containing an amino group include an epoxy compound.

  The undercoat layer is formed on the liquid crystal optical compensation layer of the optical film. The undercoat layer is formed, for example, by applying and drying a solution of the undercoat containing the polymers and the antioxidant using a coating method such as a coating method, a dipping method, or a spray method to form an undercoat layer. . The thickness of the undercoat layer is preferably about 10 to 5000 nm, more preferably in the range of 50 to 500 nm. When the thickness of the undercoat layer is reduced, it does not have bulk properties, does not exhibit sufficient strength, and sufficient adhesion may not be obtained. Moreover, when too thick, there exists a possibility of causing the fall of an optical characteristic. The coating amount (solid content) of the undercoat layer is preferably 0.1 to 5 cubic centimeters per square meter. Furthermore, it is preferably 0.1 to 1 cubic centimeter, more preferably 0.1 to 0.5 cubic centimeter.

  The pressure-sensitive adhesive forming the pressure-sensitive adhesive layer is not particularly limited, and various pressure-sensitive adhesives such as rubber-based pressure-sensitive adhesives, acrylic pressure-sensitive adhesives, and silicone-based pressure-sensitive adhesives can be used. A good acrylic pressure-sensitive adhesive is generally used.

  The acrylic pressure-sensitive adhesive has an acrylic polymer having a main skeleton of an alkyl (meth) acrylate monomer unit as a base polymer. (Meth) acrylate refers to acrylate and / or methacrylate, and (meth) of the present invention has the same meaning. The average carbon number of the alkyl group of the alkyl (meth) acrylate constituting the main skeleton of the acrylic polymer is about 1 to 12, and specific examples of the alkyl (meth) acrylate include methyl (meth) acrylate, ethyl (Meth) acrylate, n-butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isooctyl (meth) acrylate, isononyl (meth) acrylate, lauryl (meth) acrylate, etc. can be exemplified, and these are used alone or in combination. it can. Among these, alkyl (meth) acrylates having 1 to 9 carbon atoms in the alkyl group are preferable.

  In the acrylic polymer, one or more kinds of various monomers are introduced by copolymerization for the purpose of improving adhesiveness and heat resistance. Specific examples of such copolymerization monomers include, for example, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, (meth) acrylic acid 6 Hydroxyl group-containing monomers such as hydroxyhexyl, 8-hydroxyoctyl (meth) acrylate, 10-hydroxydecyl (meth) acrylate, 12-hydroxylauryl (meth) acrylate and (4-hydroxymethylcyclohexyl) -methyl acrylate Carboxyl group-containing monomers such as (meth) acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, itaconic acid, maleic acid, fumaric acid and crotonic acid; acid anhydrides such as maleic anhydride and itaconic anhydride Monomer-containing monomer; Caprolac of acrylic acid Adducts such as styrene sulfonic acid, allyl sulfonic acid, 2- (meth) acrylamide-2-methylpropane sulfonic acid, (meth) acrylamide propane sulfonic acid, sulfopropyl (meth) acrylate, (meth) acryloyloxynaphthalene sulfonic acid, etc. And sulfonic acid group-containing monomers such as 2-hydroxyethyl acryloyl phosphate.

  Further, nitrogen-containing vinyl monomers can be mentioned. For example, maleimide, N-cyclohexylmaleimide, N-phenylmaleimide; N-acryloylmorpholine; (meth) acrylamide, N, N-dimethyl (meth) acrylamide, N, N-diethyl (meth) acrylamide, N-hexyl ( (N-substituted) such as (meth) acrylamide, N-methyl (meth) acrylamide, N-butyl (meth) acrylamide, N-butyl (meth) acrylamide, N-methylol (meth) acrylamide, and N-methylolpropane (meth) acrylamide ) Amide monomer; aminoethyl (meth) acrylate, aminopropyl (meth) acrylate, N, N-dimethylaminoethyl (meth) acrylate, t-butylaminoethyl (meth) acrylate, 3- (3- Pyridinyl) propyl (meth) acrelane (Meth) acrylic acid alkylaminoalkyl monomers such as (meth) acrylic acid methoxyethyl, (meth) acrylic acid alkoxyalkyl monomers such as ethoxyethyl; N- (meth) acryloyloxymethylene succinimide, Succinimide monomers such as N- (meth) acryloyl-6-oxyhexamethylene succinimide, N- (meth) acryloyl-8-oxyoctamethylene succinimide, N-acryloylmorpholine, and the like are also examples of monomers for modification.

  Further, vinyl acetate, vinyl propionate, N-vinyl pyrrolidone, methyl vinyl pyrrolidone, vinyl pyridine, vinyl piperidone, vinyl pyrimidine, vinyl piperazine, vinyl pyrazine, vinyl pyrrole, vinyl imidazole, vinyl oxazole, vinyl morpholine, N-vinyl carboxylic acid amide , Vinyl monomers such as styrene, α-methylstyrene, N-vinylcaprolactam; cyanoacrylate monomers such as acrylonitrile and methacrylonitrile; epoxy group-containing acrylic monomers such as glycidyl (meth) acrylate; (meth) acrylic Polyethylene glycol acid, polypropylene glycol (meth) acrylate, methoxyethylene glycol (meth) acrylate, methoxypolypropylene (meth) acrylate Glycol acrylic ester monomers such as recall; (meth) acrylic acid tetrahydrofurfuryl, fluorine (meth) acrylate, silicone (meth) acrylate and acrylic acid ester monomers such as 2-methoxyethyl acrylate, etc. may also be used.

  Among these, when using an isocyanate type crosslinking agent as a crosslinking agent, a hydroxyl group-containing monomer is preferably used from the viewpoint of good reactivity with an isocyanate group. Further, from the viewpoint of adhesion to the liquid crystal cell and adhesion durability, a carboxyl group-containing monomer such as acrylic acid is preferably used. In particular, acrylic acid is preferably used. Also,

  The ratio of the copolymerization monomer in the acrylic polymer is not particularly limited, but is preferably about 0.1 to 10% by weight in weight ratio. More preferably, it is 0.5-8 weight%, More preferably, it is 1-6 weight%.

  The average molecular weight of the acrylic polymer is not particularly limited, but the weight average molecular weight is preferably about 300,000 to 2.5 million. The acrylic polymer can be produced by various known methods. For example, a radical polymerization method such as a bulk polymerization method, a solution polymerization method, or a suspension polymerization method can be appropriately selected. As the radical polymerization initiator, various known azo and peroxide initiators can be used. The reaction temperature is usually about 50 to 80 ° C., and the reaction time is 1 to 8 hours. Among the above production methods, the solution polymerization method is preferable, and ethyl acetate, toluene and the like are generally used as the solvent for the acrylic polymer. The solution concentration is usually about 20 to 80% by weight.

  The pressure-sensitive adhesive forming the pressure-sensitive adhesive layer of the present invention can contain a crosslinking agent in addition to the base polymer. The cross-linking agent can improve the adhesion and durability with the optical film, and can maintain the reliability at high temperature and the shape of the pressure-sensitive adhesive itself. When the base polymer is an acrylic polymer, an isocyanate, epoxy, peroxide, metal chelate, oxazoline, or the like can be appropriately used as the crosslinking agent. These crosslinking agents can be used alone or in combination of two or more. As a crosslinking agent, when a peroxide is contained, this invention is applied suitably. Moreover, a peroxide and an isocyanate type crosslinking agent are suitable for a crosslinking agent.

  Various peroxides are used as the peroxide-based crosslinking agent. Peroxides include di (2-ethylhexyl) peroxydicarbonate, di (4-t-butylcyclohexyl) peroxydicarbonate, di-sec-butylperoxydicarbonate, t-butylperoxyneodecanoate , T-hexylperoxypivalate, t-butylperoxypivalate, dilauroyl peroxide, di-n-octanoyl peroxide, 1,1,3,3-tetramethylbutylperoxyisobutyrate, 1,3,3-tetramethylbutylperoxy 2-ethylhexanoate, di (4-methylbenzoyl) peroxide, dibenzoyl peroxide, t-butylperoxyisobutyrate, and the like. Of these, di (4-t-butylcyclohexyl) peroxydicarbonate, dilauroyl peroxide, and dibenzoyl peroxide, which are particularly excellent in crosslinking reaction efficiency, are preferably used.

  As the isocyanate-based crosslinking agent, an isocyanate compound is used. Isocyanate compounds include tolylene diisocyanate, chlorophenylene diisocyanate, hexamethylene diisocyanate, tetramethylene diisocyanate, isophorone diisocyanate, xylylene diisocyanate, diphenylmethane diisocyanate, hydrogenated diphenylmethane diisocyanate, and the like. Adduct isocyanate compounds in which monomers are added with trimethylolpropane, etc .; isocyanurates, burette type compounds, and urethane prepolymers obtained by addition reaction of known polyether polyols, polyester polyols, acrylic polyols, polybutadiene polyols, polyisoprene polyols, etc. Examples thereof include polymer type isocyanate.

  Examples of the epoxy-based crosslinking agent include bisphenol A epichlorohydrin type epoxy resins. Examples of the epoxy crosslinking agent include ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, glycerin diglycidyl ether, glycerin triglycidyl ether, 1,6-hexanediol diglycidyl ether, trimethylolpropane triglycidyl ether, Diglycidylaniline, N, N, N ′, N′-tetraglycidyl-m-xylylenediamine, 1,3-bis (N, N-diglycidylaminomethyl) cyclohexane, N, N, N ′, N′- Examples include tetraglycidylaminophenyl methane, triglycidyl isocyanurate, m-N, N-diglycidylaminophenyl glycidyl ether, N, N-diglycidyl toluidine, and N, N-diglycidyl aniline.

  The amount of the crosslinking agent used is 10 parts by weight or less, preferably 0.01 to 5 parts by weight, and more preferably 0.02 to 3 parts by weight with respect to 100 parts by weight of the acrylic polymer. When the proportion of the crosslinking agent used exceeds 10 parts by weight, it is not preferable in that crosslinking may proceed excessively and adhesiveness may be lowered.

  In particular, when a peroxide is used as the crosslinking agent, the peroxide is preferably about 0.05 to 1 part by weight, more preferably 0.06 to 0.5 part by weight, based on 100 parts by weight of the acrylic polymer. Is preferred. In the case where a peroxide is used as the polymerization initiator for the acrylic polymer, and the peroxide remains in the acrylic polymer, the residual peroxide is blended with the peroxide. Included in the quantity. Moreover, when using together an isocyanate type crosslinking agent with a peroxide, it is preferable that the ratio of an isocyanate type crosslinking agent is about 0.01-1.5 weight part, Furthermore, it is preferable that it is 0.02-1 weight part. .

  Furthermore, the pressure-sensitive adhesive may include a tackifier, a plasticizer, glass fiber, glass beads, metal powder, other inorganic powders, a pigment, a colorant, a filler, an antioxidant, if necessary. Various additives may be used as appropriate, such as an agent, an ultraviolet absorber, a silane coupling agent, and the like without departing from the object of the present invention. Moreover, it is good also as an adhesive layer etc. which contain microparticles | fine-particles and show light diffusibility.

  The pressure-sensitive adhesive layer is formed by laminating on the undercoat layer. The forming method is not particularly limited, and examples thereof include a method of applying and drying a pressure-sensitive adhesive (solution), a method of transferring with a release sheet provided with a pressure-sensitive adhesive layer, and the like. As a coating method, a roll coating method such as reverse coating or gravure coating, a spin coating method, a screen coating method, a fountain coating method, a dipping method, or a spray method can be adopted.

  In the pressure-sensitive adhesive optical film of the present invention, window frame unevenness tends to occur when the pressure-sensitive adhesive layer is thin. Therefore, the pressure-sensitive adhesive optical film of the present invention is particularly suitable when the thickness of the pressure-sensitive adhesive layer is as thin as 5 to 40 μm, further 5 to 25 μm. In addition, in the adhesive optical film of this invention, when an adhesive layer is hard, a window frame nonuniformity tends to arise.

  As a constituent material of the release sheet, paper, polyethylene, polypropylene, polyethylene terephthalate and other synthetic resin films, rubber sheets, paper, cloth, non-woven fabric, nets, foam sheets and metal foils, and appropriate thin leaf bodies such as laminates thereof Etc. In order to improve the peelability from the pressure-sensitive adhesive layer, the surface of the release sheet 4 may be subjected to a peeling treatment such as silicone treatment, long-chain alkyl treatment, or fluorine treatment as necessary.

As a constituent material of the release sheet, paper, polyethylene, polypropylene, polyethylene terephthalate and other synthetic resin films, rubber sheets, paper, cloth, non-woven fabric, nets, foam sheets and metal foils, and appropriate thin leaf bodies such as laminates thereof Etc. In order to improve the peelability from the pressure-sensitive adhesive layer, the surface of the release sheet may be subjected to a low-adhesive release treatment such as silicone treatment, long-chain alkyl treatment, and fluorine treatment as necessary.

  An antistatic agent can also be used in the adhesive optical film in order to impart antistatic properties. The antistatic agent can be contained in each layer, and an antistatic layer can be separately formed. Antistatic agents include ionic surfactant systems; conductive polymer systems such as polyaniline, polythiophene, polypyrrole, and polyquinoxaline; metal oxide systems such as tin oxide, antimony oxide, and indium oxide. From the viewpoint of appearance, antistatic effect, and stability of the antistatic effect when heated and humidified, a conductive polymer system is preferably used. Among these, water-soluble conductive polymers such as polyaniline and polythiophene or water-dispersible conductive polymers are particularly preferably used. This is preferable in the case where a water-soluble conductive polymer or a water-dispersible conductive polymer is used as a material for forming the antistatic layer from the viewpoint of suppressing deterioration of the optical film substrate due to an organic solvent during the coating process.

  As shown in FIG. 2, the optical film of the present invention has a polarizer 6 and then a transparent protective film 7 laminated on one side of the transparent base film 1 on the side where the liquid crystal optical compensation layer 3 is not formed. Can be used.

  The polarizer 6 is bonded to the transparent substrate film 1 using an adhesive. In FIG. 2, the transparent base film 1 also serves as a transparent protective film for the polarizer 6, but the transparent base film 1 has a polarizing plate having a transparent protective film on one or both sides of the polarizer. It can also be laminated.

  The polarizer is not particularly limited, and various types can be used. Examples of polarizers include dichroic iodine and dichroic dyes on hydrophilic polymer films such as polyvinyl alcohol films, partially formalized polyvinyl alcohol films, and ethylene / vinyl acetate copolymer partially saponified films. Examples thereof include polyene-based oriented films such as those obtained by adsorbing substances and uniaxially stretched, polyvinyl alcohol dehydrated products and polyvinyl chloride dehydrochlorinated products. Among these, a polarizer composed of a polyvinyl alcohol film and a dichroic material such as iodine is preferable. The thickness of these polarizers is not particularly limited, but is generally about 5 to 80 μm.

  A polarizer obtained by dyeing a polyvinyl alcohol film with iodine and uniaxially stretching it can be prepared by, for example, dying polyvinyl alcohol in an aqueous solution of iodine and stretching it 3 to 7 times the original length. If necessary, it can be immersed in an aqueous solution such as potassium iodide which may contain boric acid, zinc sulfate, zinc chloride or the like. Further, if necessary, the polyvinyl alcohol film may be immersed in water and washed before dyeing. In addition to washing the polyvinyl alcohol film surface with dirt and anti-blocking agents by washing the polyvinyl alcohol film with water, it also has the effect of preventing unevenness such as uneven coloring by swelling the polyvinyl alcohol film. is there. Stretching may be performed after dyeing with iodine, may be performed while dyeing, or may be dyed with iodine after stretching. The film can be stretched even in an aqueous solution such as boric acid or potassium iodide or in a water bath.

  As a material for forming the transparent protective film provided on one side or both sides of the polarizer, a material excellent in transparency, mechanical strength, thermal stability, moisture barrier property, isotropy and the like is preferable. The transparent protective film can use the same material as the transparent substrate film. The same applies to the thickness.

  The transparent substrate film and the transparent protective film may use the same polymer material or different polymer materials.

  The polarizer, the transparent substrate film, and the transparent protective film are usually in close contact with each other through an aqueous adhesive or the like. Examples of the water-based adhesive include an isocyanate-based adhesive, a polyvinyl alcohol-based adhesive, a gelatin-based adhesive, a vinyl-based latex, a water-based polyurethane, and a water-based polyester. In addition, in bonding of a polarizer, a transparent base film, and a transparent protective film, an activation process can be performed to a transparent base film and a transparent protective film. Various methods can be employed for the activation treatment, for example, saponification treatment, corona treatment, low-pressure UV treatment, plasma treatment, or the like. The activation treatment is effective particularly when the transparent substrate film is triacetyl cellulose, norbornene resin, polycarbonate, polyolefin resin, or the like.

  The surface of the transparent protective film to which the polarizer is not adhered may be subjected to a treatment for the purpose of hard coat layer, antireflection treatment, sticking prevention, diffusion or antiglare.

  The hard coat treatment is applied for the purpose of preventing scratches on the surface of the polarizing plate. For example, a transparent protective film with a cured film excellent in hardness, sliding properties, etc. by an appropriate ultraviolet curable resin such as acrylic or silicone is used. It can be formed by a method of adding to the surface of the film. The antireflection treatment is performed for the purpose of preventing reflection of external light on the surface of the polarizing plate, and can be achieved by forming an antireflection film or the like according to the conventional art. Further, the sticking prevention treatment is performed for the purpose of preventing adhesion between adjacent layers of other members.

  Anti-glare treatment is applied for the purpose of preventing external light from being reflected on the surface of the polarizing plate and obstructing the visibility of the light transmitted through the polarizing plate. For example, the surface is roughened by sandblasting or embossing. It can be formed by imparting a fine concavo-convex structure to the surface of the transparent protective film by an appropriate method such as a method or a compounding method of transparent fine particles. Examples of the fine particles to be included in the formation of the surface fine concavo-convex structure include conductive materials made of silica, alumina, titania, zirconia, tin oxide, indium oxide, cadmium oxide, antimony oxide, and the like having an average particle diameter of 0.5 to 50 μm. In some cases, transparent fine particles such as inorganic fine particles and organic fine particles (including beads) made of a crosslinked or uncrosslinked polymer are used. When forming a surface fine uneven structure, the amount of fine particles used is generally about 2 to 50 parts by weight, preferably 5 to 25 parts by weight, based on 100 parts by weight of the transparent resin forming the surface fine uneven structure. The anti-glare layer may also serve as a diffusion layer (such as a visual enlargement function) for diffusing the light transmitted through the polarizing plate to enlarge vision.

  The antireflection layer, antisticking layer, diffusion layer, antiglare layer, and the like can be provided on the transparent protective film itself, or can be provided separately from the transparent protective film as an optical layer.

  In addition to the optical film in which the polarizing plate is laminated, as an optical film used for the pressure-sensitive adhesive optical film of the present invention, an optical layer used for forming an image display device such as a liquid crystal display device may be laminated. it can. For example, an optical layer that may be used for forming a liquid crystal display device such as a reflection plate, an anti-transmission plate, a retardation plate (including wavelength plates such as 1/2 and 1/4), and a brightness enhancement film. can give. These can be used alone as an optical film, or can be laminated on the polarizing plate for practical use and used as one layer or two or more layers.

  In particular, a reflective polarizing plate or a semi-transmissive polarizing plate in which a polarizing plate is further laminated with a reflecting plate or a semi-transmissive reflecting plate, an elliptical polarizing plate or a circular polarizing plate in which a retardation plate is further laminated with a polarizing plate, or A polarizing plate obtained by further laminating a brightness enhancement film on the polarizing plate is preferable.

  A reflective polarizing plate is a polarizing plate provided with a reflective layer, and is used to form a liquid crystal display device or the like that reflects incident light from the viewing side (display side). Such a light source can be omitted, and the liquid crystal display device can be easily thinned. The reflective polarizing plate can be formed by an appropriate method such as a method in which a reflective layer made of metal or the like is attached to one surface of the polarizing plate via a transparent protective layer or the like as necessary.

  Specific examples of the reflective polarizing plate include those in which a reflective layer is formed by attaching a foil or a vapor deposition film made of a reflective metal such as aluminum on one side of a transparent protective film matted as necessary. In addition, the transparent protective film may contain fine particles to form a surface fine concavo-convex structure, and a reflective layer having a fine concavo-convex structure thereon. The reflective layer having the fine concavo-convex structure has an advantage that incident light is diffused by irregular reflection to prevent directivity and glaring appearance and to suppress unevenness in brightness and darkness. Moreover, the protective film containing fine particles also has an advantage that incident light and its reflected light are diffused when passing through it and light and dark unevenness can be further suppressed. The reflective layer of the fine concavo-convex structure reflecting the surface fine concavo-convex structure of the transparent protective film is formed by, for example, applying metal to the surface of the transparent protective layer by an appropriate method such as a vacuum deposition method, an ion plating method, a sputtering method, or a plating method. It can be performed by a method of attaching directly to the screen.

  Instead of the method of directly applying the reflecting plate to the transparent protective film of the polarizing plate, the reflecting plate can be used as a reflecting sheet provided with a reflecting layer on an appropriate film according to the transparent film. Since the reflective layer is usually made of metal, the usage form in which the reflective surface is covered with a transparent protective film, a polarizing plate or the like is used to prevent the reflectance from being lowered due to oxidation, and thus to maintain the initial reflectance for a long time. In addition, it is more preferable to avoid a separate attachment of the protective layer.

  The semi-transmissive polarizing plate can be obtained by using a semi-transmissive reflective layer such as a half mirror that reflects and transmits light with the reflective layer. A transflective polarizing plate is usually provided on the back side of a liquid crystal cell, and displays an image by reflecting incident light from the viewing side (display side) when a liquid crystal display device is used in a relatively bright atmosphere. In a relatively dark atmosphere, a liquid crystal display device of a type that displays an image using a built-in power source such as a backlight built in the back side of the transflective polarizing plate can be formed. In other words, the transflective polarizing plate can be used to form liquid crystal display devices that can save energy when using a light source such as a backlight in a bright atmosphere and can be used with a built-in power supply even in a relatively dark atmosphere. It is.

  An elliptically polarizing plate or a circularly polarizing plate in which a retardation plate is further laminated on a polarizing plate will be described. A phase difference plate or the like is used when changing linearly polarized light to elliptically polarized light or circularly polarized light, changing elliptically polarized light or circularly polarized light to linearly polarized light, or changing the polarization direction of linearly polarized light. In particular, a so-called quarter-wave plate (also referred to as a λ / 4 plate) is used as a retardation plate that changes linearly polarized light into circularly polarized light or changes circularly polarized light into linearly polarized light. A half-wave plate (also referred to as a λ / 2 plate) is usually used when changing the polarization direction of linearly polarized light.

  The elliptically polarizing plate is effectively used for black and white display without the above color by compensating (preventing) the coloration (blue or yellow) generated by the birefringence of the liquid crystal layer of the super twist nematic (STN) type liquid crystal display device. It is done. Further, the one in which the three-dimensional refractive index is controlled is preferable because it can compensate (prevent) coloring that occurs when the screen of the liquid crystal display device is viewed from an oblique direction. The circularly polarizing plate is effectively used, for example, when adjusting the color tone of an image of a reflective liquid crystal display device in which an image is displayed in color, and also has an antireflection function.

  Examples of the retardation plate include a birefringent film obtained by uniaxially or biaxially stretching a polymer material, a liquid crystal polymer alignment film, and a liquid crystal polymer alignment layer supported by a film. The thickness of the retardation plate is not particularly limited, but is generally about 20 to 150 μm.

  Examples of the polymer material include polyvinyl alcohol, polyvinyl butyral, polymethyl vinyl ether, polyhydroxyethyl acrylate, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, polycarbonate, polyarylate, polysulfone, polyethylene terephthalate, polyethylene naphthalate, polyether sulfone, Polyphenylene sulfide, polyphenylene oxide, polyallylsulfone, polyamide, polyimide, polyolefin, polyvinyl chloride, cellulose polymer, norbornene resin, or binary, ternary copolymers, graft copolymers, Examples include blends. These polymer materials become an oriented product (stretched film) by stretching or the like.

  Examples of the liquid crystal polymer include various main chain types and side chain types in which a conjugated linear atomic group (mesogen) imparting liquid crystal alignment is introduced into the main chain or side chain of the polymer. . Specific examples of the main chain type liquid crystal polymer include a nematic alignment polyester liquid crystal polymer, a discotic polymer, and a cholesteric polymer having a structure in which a mesogenic group is bonded at a spacer portion that imparts flexibility. Specific examples of the side chain type liquid crystal polymer include polysiloxane, polyacrylate, polymethacrylate or polymalonate as a main chain skeleton and a nematic alignment imparting para-substitution through a spacer part composed of a conjugated atomic group as a side chain. Examples thereof include those having a mesogenic part composed of a cyclic compound unit. These liquid crystal polymers are prepared by, for example, applying a solution of a liquid crystalline polymer on an alignment treatment surface such as a surface of a thin film such as polyimide or polyvinyl alcohol formed on a glass plate, or an oblique deposition of silicon oxide. This is done by developing and heat treatment.

  The retardation plate may have an appropriate retardation according to the purpose of use, such as for the purpose of compensating for coloring, vision, etc. due to birefringence of various wave plates and liquid crystal layers, and may be two or more types. It may be one in which retardation plates are stacked and optical characteristics such as retardation are controlled.

  The elliptical polarizing plate and the reflective elliptical polarizing plate are obtained by laminating a polarizing plate or a reflective polarizing plate and a retardation plate in an appropriate combination. Such an elliptically polarizing plate or the like can also be formed by sequentially laminating them sequentially in the manufacturing process of the liquid crystal display device so as to be a combination of a (reflective) polarizing plate and a retardation plate. An optical film such as a polarizing plate has an advantage that it can improve the production efficiency of a liquid crystal display device and the like because of excellent quality stability and lamination workability.

  A polarizing plate obtained by bonding a polarizing plate and a brightness enhancement film is usually provided on the back side of a liquid crystal cell. The brightness enhancement film reflects a linearly polarized light with a predetermined polarization axis or a circularly polarized light in a predetermined direction when natural light is incident due to a backlight such as a liquid crystal display device or reflection from the back side, and transmits other light. In addition, a polarizing plate in which a brightness enhancement film is laminated with a polarizing plate allows light from a light source such as a backlight to enter to obtain transmitted light in a predetermined polarization state, and reflects light without transmitting the light other than the predetermined polarization state. The The light reflected on the surface of the brightness enhancement film is further inverted through a reflective layer or the like provided behind the brightness enhancement film and re-incident on the brightness enhancement film, and part or all of the light is transmitted as light having a predetermined polarization state. Luminance can be improved by increasing the amount of light transmitted through the enhancement film and increasing the amount of light that can be used for liquid crystal display image display or the like by supplying polarized light that is difficult to be absorbed by the polarizer. That is, when light is incident through the polarizer from the back side of the liquid crystal cell without using a brightness enhancement film, light having a polarization direction that does not coincide with the polarization axis of the polarizer is almost polarized. It is absorbed by the polarizer and does not pass through the polarizer. That is, although depending on the characteristics of the polarizer used, approximately 50% of the light is absorbed by the polarizer, and accordingly, the amount of light that can be used for liquid crystal image display or the like is reduced and the image becomes dark. The brightness enhancement film reflects light that has a polarization direction that is absorbed by the polarizer without being incident on the polarizer, and is reflected by the brightness enhancement film, and then inverted through a reflective layer or the like provided behind the brightness enhancement film. The brightness enhancement film transmits only the polarized light in which the polarization direction of the light reflected and inverted between the two is allowed to pass through the polarizer. Since the light is supplied to the polarizer, light such as a backlight can be efficiently used for displaying an image on the liquid crystal display device, and the screen can be brightened.

  A diffusion plate may be provided between the brightness enhancement film and the reflective layer. The polarized light reflected by the brightness enhancement film is directed to the reflective layer or the like, but the installed diffuser plate uniformly diffuses the light passing therethrough and simultaneously cancels the polarized state and becomes a non-polarized state. That is, the light in the natural light state is directed to the reflection layer or the like, reflected through the reflection layer or the like, and again passes through the diffusion plate and reenters the brightness enhancement film. In this way, by providing a diffuser plate that returns polarized light to the original natural light between the brightness enhancement film and the reflective layer, the brightness of the display screen is maintained, and at the same time, the brightness of the display screen is reduced and uniform. Can provide a bright screen. By providing such a diffuser plate, it is considered that the first incident light has a moderate increase in the number of repetitions of reflection, and in combination with the diffusion function of the diffuser plate, a uniform bright display screen can be provided.

  The brightness enhancement film has a characteristic of transmitting linearly polarized light having a predetermined polarization axis and reflecting other light, such as a multilayer thin film of dielectric material or a multilayer laminate of thin film films having different refractive index anisotropies. Such as an alignment film of a cholesteric liquid crystal polymer or an alignment liquid crystal layer supported on a film substrate, which reflects either left-handed or right-handed circularly polarized light and transmits other light. Appropriate things, such as a thing, can be used.

  Therefore, in the brightness enhancement film of the type that transmits linearly polarized light having the predetermined polarization axis as described above, the transmitted light is incident on the polarizing plate with the polarization axis aligned as it is, thereby efficiently transmitting while suppressing absorption loss due to the polarizing plate. Can be made. On the other hand, in a brightness enhancement film of a type that transmits circularly polarized light such as a cholesteric liquid crystal layer, it can be incident on a polarizer as it is, but from the point of suppressing absorption loss, the circularly polarized light is converted into linearly polarized light through a retardation plate. It is preferably incident on the polarizing plate. Note that circularly polarized light can be converted to linearly polarized light by using a quarter wave plate as the retardation plate.

  A retardation plate that functions as a quarter-wave plate at a wide wavelength in the visible light region or the like exhibits, for example, a retardation plate that functions as a quarter-wave plate for light-colored light having a wavelength of 550 nm and other retardation characteristics. It can be obtained by a method in which a phase difference layer, for example, a phase difference layer that functions as a half-wave plate is superimposed. Therefore, the retardation plate disposed between the polarizing plate and the brightness enhancement film may be composed of one or more retardation layers.

  In addition, a cholesteric liquid crystal layer having a reflection structure that reflects circularly polarized light in a wide wavelength range such as a visible light range can be obtained by combining two or more layers with different reflection wavelengths to form an overlapping structure. Based on this, transmitted circularly polarized light in a wide wavelength range can be obtained.

  Further, the polarizing plate may be formed by laminating a polarizing plate and two or more optical layers as in the above-described polarization separation type polarizing plate. Therefore, a reflective elliptical polarizing plate or a semi-transmissive elliptical polarizing plate in which the above-described reflective polarizing plate or semi-transmissive polarizing plate and a retardation plate are combined may be used.

  An optical film in which the optical layer is laminated on a polarizing plate can be formed by a method of sequentially laminating separately in the manufacturing process of a liquid crystal display device or the like. There is an advantage that the manufacturing process of a liquid crystal display device or the like can be improved because of excellent stability and assembly work. For the lamination, an appropriate adhesive means such as an adhesive layer can be used. When adhering the polarizing plate and the other optical layer, their optical axes can be set at an appropriate arrangement angle in accordance with the target phase difference characteristic.

  In addition, each layer such as an optical film or an adhesive layer of the pressure-sensitive adhesive optical film of the present invention includes, for example, an ultraviolet ray such as a salicylic acid ester compound, a benzophenol compound, a benzotriazole compound, a cyanoacrylate compound, or a nickel complex compound. What gave the ultraviolet absorptivity by systems, such as a system processed with an absorber, may be used.

  The pressure-sensitive adhesive optical film of the present invention can be preferably used for forming various image display devices such as liquid crystal display devices. The liquid crystal display device can be formed according to the conventional method. That is, a liquid crystal display device is generally formed by appropriately assembling components such as a liquid crystal cell, an adhesive optical film, and an illumination system as necessary, and incorporating a drive circuit. There is no particular limitation except that an adhesive optical film is used. As the liquid crystal cell, any type such as a TN type, an STN type, or a π type can be used.

  An appropriate liquid crystal display device such as a liquid crystal display device in which an adhesive optical film is disposed on one side or both sides of a liquid crystal cell, or a backlight or a reflector used in an illumination system can be formed. In that case, the optical film according to the present invention can be installed on one side or both sides of the liquid crystal cell. When optical films are provided on both sides, they may be the same or different. Further, when forming a liquid crystal display device, for example, a single layer or a suitable part such as a diffusing plate, an antiglare layer, an antireflection film, a protective plate, a prism array, a lens array sheet, a light diffusing plate, a backlight, etc. Two or more layers can be arranged.

  Next, an organic electroluminescence device (organic EL display device) will be described. The optical film (polarizing plate or the like) of the present invention can also be applied to an organic EL display device. Generally, in an organic EL display device, a transparent electrode, an organic light emitting layer, and a metal electrode are sequentially laminated on a transparent substrate to form a light emitter (organic electroluminescent light emitter). Here, the organic light emitting layer is a laminate of various organic thin films, for example, a laminate of a hole injection layer made of a triphenylamine derivative and the like and a light emitting layer made of a fluorescent organic solid such as anthracene, Alternatively, a structure having various combinations such as a laminate of such a light-emitting layer and an electron injection layer composed of a perylene derivative or the like, or a laminate of these hole injection layer, light-emitting layer, and electron injection layer is known. It has been.

  In organic EL display devices, holes and electrons are injected into the organic light-emitting layer by applying a voltage to the transparent electrode and the metal electrode, and the energy generated by recombination of these holes and electrons excites the phosphor material. Then, light is emitted on the principle that the excited fluorescent material emits light when returning to the ground state. The mechanism of recombination in the middle is the same as that of a general diode, and as can be predicted from this, the current and the emission intensity show strong nonlinearity with rectification with respect to the applied voltage.

  In an organic EL display device, in order to extract light emitted from the organic light emitting layer, at least one of the electrodes must be transparent, and a transparent electrode usually formed of a transparent conductor such as indium tin oxide (ITO) is used as an anode. It is used as. On the other hand, in order to facilitate electron injection and increase luminous efficiency, it is important to use a material having a small work function for the cathode, and usually metal electrodes such as Mg—Ag and Al—Li are used.

  In the organic EL display device having such a configuration, the organic light emitting layer is formed of a very thin film having a thickness of about 10 nm. For this reason, the organic light emitting layer transmits light almost completely like the transparent electrode. As a result, light that is incident from the surface of the transparent substrate at the time of non-light emission, passes through the transparent electrode and the organic light emitting layer, and is reflected by the metal electrode is again emitted to the surface side of the transparent substrate. The display surface of the organic EL display device looks like a mirror surface.

  In an organic EL display device comprising an organic electroluminescent light emitting device comprising a transparent electrode on the surface side of an organic light emitting layer that emits light upon application of a voltage and a metal electrode on the back side of the organic light emitting layer, the surface of the transparent electrode While providing a polarizing plate on the side, a retardation plate can be provided between the transparent electrode and the polarizing plate.

  Since the retardation plate and the polarizing plate have a function of polarizing light incident from the outside and reflected by the metal electrode, there is an effect that the mirror surface of the metal electrode is not visually recognized by the polarization action. In particular, the mirror surface of the metal electrode can be completely shielded by configuring the retardation plate with a quarter-wave plate and adjusting the angle formed by the polarization direction of the polarizing plate and the retardation plate to π / 4. .

  That is, only the linearly polarized component of the external light incident on the organic EL display device is transmitted through the polarizing plate. This linearly polarized light becomes generally elliptically polarized light by the phase difference plate, but becomes circularly polarized light particularly when the phase difference plate is a quarter wavelength plate and the angle formed by the polarization direction of the polarizing plate and the phase difference plate is π / 4. .

  This circularly polarized light is transmitted through the transparent substrate, the transparent electrode, and the organic thin film, is reflected by the metal electrode, is again transmitted through the organic thin film, the transparent electrode, and the transparent substrate, and becomes linearly polarized light again on the retardation plate. And since this linearly polarized light is orthogonal to the polarization direction of a polarizing plate, it cannot permeate | transmit a polarizing plate. As a result, the mirror surface of the metal electrode can be completely shielded.

  EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples. In addition, all the parts and% in each example are based on weight.

Example 1
<Preparation of acrylic adhesive>
As a base polymer, an acrylic polymer having a weight average molecular weight of 16.5 million consisting of a copolymer of butyl acrylate: acrylic acid 4-hydroxybutylethyl acrylate = 99: 1 (weight ratio) And a solution containing 0.3 part of 2,2′-azobisisobutyronitrile) (solid content 15.5%) was used. For 100 parts of the solid content of the acrylic polymer solution, 0.3 parts of dibenzoyl peroxide (manufactured by NOF Corporation, Niper BMT40SV) and trimethylolpropane xylene diisocyanate (Mitsui Takeda Chemical Co., Ltd.) ), Takenate D110N) 0.02 part, and acetoacetyl group-containing silane coupling agent (manufactured by Soken Chemical Co., Ltd., A-100) 0.2 part, and the adhesive solution (solid content 12%) Prepared.

<Formation of adhesive layer>
The obtained pressure-sensitive adhesive solution was applied on a separator made of a release-treated polyester film (thickness 38 μm) by a reverse roll coating method so that the thickness of the pressure-sensitive adhesive layer after drying was 20 μm. It heat-processed for 3 minutes at 155 degreeC, the solvent was volatilized, and the adhesive layer was obtained.

<Optical film>
A wide view (WV) film manufactured by Fuji Photo Film Co., Ltd. was used. The WV film had a discotic liquid crystal layer in which discotic liquid crystal molecules were tilted and aligned on a cellulose polymer film that was a transparent substrate film.

  The WV film was separated into an inclined alignment layer of discotic liquid crystal molecules, and the characteristics at λ = 590 nm were measured with KOBRA-21ADH manufactured by Oji Scientific Instruments. The in-plane maximum refractive index was nx, the refractive index in the direction perpendicular to the direction having the in-plane maximum refractive index was ny, and the refractive index in the thickness direction was nz. The thickness was d. The transparent support had Δnd = (nx−ny) × d = 12 nm and Rth = (nx−nz) × d = 100 nm. On the other hand, the tilted alignment layer measured the phase difference by changing the incident angle from −50 ° to 50 ° in the direction in which the optical axis is tilted. As a result, Δnd = 30 nm, Rth = 150 nm, and average tilt angle θ = 17 °. Met.

  After the saponification treatment of the transparent substrate film side of the WV film, the saponification treatment surface and a polyvinyl alcohol polarizer having a thickness of 20 μm (manufactured by Nitto Denko Corporation, SEG-5424WL) It bonded together with the adhesive agent. On the other hand, a transparent protective film (triacetyl cellulose film, thickness 80 μm) is bonded to the other surface of the polarizer with the same polyvinyl alcohol-based adhesive as described above, and an optical film having a polarizing plate (polarized light with an optical compensation layer) Board).

<Preparation of primer>
A phenolic antioxidant (manufactured by Ciba Specialty Chemicals Co., Ltd.) was added to a solution obtained by diluting acrylic acid ester having primary amino at the terminal (manufactured by Nippon Shokubai Co., Ltd., Poliment NK380) in toluene so that the solid content was 2%. A primer was prepared by adding 1 part of Irganox 1010) to 100 parts of the solid content of the solution.

<Preparation of adhesive optical film>
On the surface of the discotic liquid crystal layer of the polarizing plate with the optical compensation layer, the undercoat is applied and dried using a bar coater to form an undercoat layer (thickness: 80 nm) having a coating amount of 0.2 cubic centimeters. did. Subsequently, the release sheet in which the said adhesive layer was formed was bonded to the undercoat layer, and the adhesive optical film was produced.

Examples 2-7
In Example 1, a pressure-sensitive adhesive optical film was produced in the same manner as in Example 1 except that the amount of the phenolic antioxidant was changed as shown in Table 1 in preparing the primer.

Example 8
In Example 1, in preparing the primer, a phenolic antioxidant (manufactured by Ciba Specialty Chemicals, Irganox 1010) and a phosphorus antioxidant (manufactured by Ciba Specialty Chemicals, Irganox B225) were used as antioxidants. Example 1 except that, in the ratio of phenolic antioxidant: phosphorous antioxidant = 1: 1 (weight ratio), the total of these was added 1 part to 100 parts of the solid content of the solution. In the same manner, an adhesive optical film was produced.

Comparative Example 1
In Example 1, a pressure-sensitive adhesive optical film was produced in the same manner as in Example 1 except that no phenolic antioxidant was blended in preparing the primer.

Comparative Example 2
In Example 1, no phenolic antioxidant was blended in the preparation of the primer, and in the preparation of the acrylic pressure-sensitive adhesive, the phenolic antioxidant (Ciba Specialty) was used for 100 parts of the solid content of the pressure-sensitive adhesive solution. An adhesive optical film was produced in the same manner as in Example 1 except that 1 part of Irganox 1010) manufactured by Chemicals Inc. was added.

  The following evaluation was performed about the adhesive optical film obtained above. The results are shown in Table 1.

<Window frame unevenness>
From the obtained adhesive optical film (size: 300 mm × 220 mm), a sample excluding the polyester film subjected to the release treatment was bonded to a glass substrate for testing with a roller. An alkali-free glass plate (thickness 0.7 mm, size 350 mm × 250 mm) was used as the test glass substrate. After bonding, the sample was put into an autoclave (50 ° C., 5 atm × 15 minutes). Thereafter, a window frame unevenness test was performed. In the window frame unevenness test, the backlight was turned on in an atmosphere of 80 ° C., and the sample was placed thereon. It was visually evaluated according to the following criteria whether window frame unevenness occurred in the peripheral part (within 10 mm from the edge) of the optical film. The lighting time was confirmed for 0 hours, 120 hours, and 240 hours.
○: No unevenness in the periphery.
Δ: Unevenness can be confirmed slightly in the periphery in a dark place.
X: Unevenness can be clearly observed in the periphery in a dark place.
XX: Unevenness can be confirmed slightly in the periphery in the light place.
XXX: Unevenness can be confirmed clearly in the periphery in a bright place.

It is sectional drawing of an example of the adhesive optical film of this invention. It is sectional drawing of an example of the adhesive optical film of this invention.

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 Transparent base film 2 Alignment film 3 Liquid crystal optical compensation layer (discotic liquid crystal layer)
4 Undercoat layer 5 Adhesive layer 6 Polarizer 7 Transparent protective film

Claims (10)

In the pressure-sensitive adhesive optical film in which the pressure-sensitive adhesive layer is provided via the undercoat layer on the liquid crystal optical compensation layer of the optical film having the liquid crystal optical compensation layer on one side of the transparent substrate film,
The undercoat layer contains a polymer and an antioxidant, and is an adhesive optical film.   The pressure-sensitive adhesive optical film according to claim 1, wherein the undercoat layer contains 0.01 to 1000 parts by weight of an antioxidant with respect to 100 parts by weight of the polymers.   The pressure-sensitive adhesive optical film according to claim 1, wherein the undercoat layer contains 5 to 1000 parts by weight of an antioxidant with respect to 100 parts by weight of the polymers.   The pressure-sensitive adhesive optical film according to claim 1, wherein the liquid crystal optical compensation layer is a discotic liquid crystal layer.   The pressure-sensitive adhesive optical film according to claim 1, wherein the polymer of the undercoat layer is a polymer having a primary amino group.   6. The pressure-sensitive adhesive optical film according to claim 5, wherein the polymer having a primary amino group is a poly (meth) acrylic acid ester having a primary amino group at a terminal.   The pressure-sensitive adhesive optical film according to any one of claims 1 to 6, wherein the antioxidant is at least one selected from phenol-based, phosphorus-based, sulfur-based and amine-based antioxidants. .   The pressure-sensitive adhesive layer is formed of an acrylic pressure-sensitive adhesive containing an acrylic polymer and a crosslinking agent, and the crosslinking agent contains a peroxide. The adhesive optical film as described.   The pressure-sensitive adhesive optical film according to claim 1, wherein a polarizer is laminated on one side of the transparent substrate film on the side where the liquid crystal optical compensation layer is not formed.   An image display device using at least one adhesive optical film according to claim 1.