JP4083102B2 - Multilayer coating tool and method for coating the same - Google Patents
Multilayer coating tool and method for coating the same Download PDFInfo
- Publication number
- JP4083102B2 JP4083102B2 JP2003345278A JP2003345278A JP4083102B2 JP 4083102 B2 JP4083102 B2 JP 4083102B2 JP 2003345278 A JP2003345278 A JP 2003345278A JP 2003345278 A JP2003345278 A JP 2003345278A JP 4083102 B2 JP4083102 B2 JP 4083102B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- coating
- cutting tool
- coated
- coated cutting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、フライス加工、切削加工、穴加工等に使用される切削工具に関し、耐摩耗皮膜を被覆することにより優れた耐剥離性と切り屑排出性を有し、優れた耐摩耗性を発揮する多層皮膜被覆切削工具及びその被覆方法に関する。 The present invention relates to a cutting tool used for milling, cutting, drilling and the like, and has excellent peeling resistance and chip discharge by coating an abrasion-resistant film, and exhibits excellent wear resistance. The present invention relates to a multilayer film coated cutting tool and a coating method thereof.
切削加工の高能率化に伴い切削工具の耐摩耗皮膜は、高硬度な硬質皮膜の上に摩擦抵抗の極めて低い、例えば炭素系潤滑膜を被覆する多層化の試みが行われ、耐摩耗性と潤滑特性を兼ね備えた硬質皮膜の提案がなされている。
特許文献1は、硬質炭素系潤滑膜と耐摩耗皮膜の密着強度を改善するためにSi中間層を形成することが開示されている。しかし、Siを含む中間層は強度が低く、2層間の密着強度が不十分である。
特許文献2も同様、中間層として、周期律表第4a、5a、6a、3b族元素及びC以外の4b続元素の元素群から選ばれた元素の炭化物を用いているが、2層間の密着強度が不十分であり、切削工具の耐摩耗性を大幅に改善するには至ってはいない。
特許文献3は、高硬度皮膜の下地層と、2硫化モリブデン等の固体潤滑性を有する皮膜が提案されている。しかし、2硫化モリブデンに添加元素を加えた程度では、過酷な切削環境においては2層間の密着強度、表面平滑性が十分ではなく、摩擦抵抗が高く耐摩耗性の改善はなされてはいない。
特許文献4は、耐摩耗性被膜と硬質炭素膜とが交互に積層された切削工具が開示されているが、2層間の密着強度改善に対して、大幅な耐摩耗性の改善がなされてはいない。
特許文献5にも、基体と非晶質カーボン層の間に、密着性の改善を目的として界面層と称するTiN、Ti(CN)、(TiAl)Nが用いられているが、大幅な耐摩耗性の改善が成されてはいない。
As cutting efficiency increases, wear-resistant coatings for cutting tools have been tried to be multi-layered, such as coating a carbon-based lubricating film with a very low frictional resistance on a hard coating with high hardness. Proposals have been made for hard coatings having lubricating properties.
Similarly,
上記特許文献1〜4は、耐摩耗性に優れ、且つ、潤滑特性とを兼ね備えた被覆切削工具は得られてはいない。その原因は、耐摩耗皮膜とその上に被覆される例えば潤滑皮膜との密着性が不十分であることに起因するためである。本発明は、耐摩耗皮膜と潤滑性皮膜を兼ね備え、両者の密着強度が極めて優れる耐摩耗皮膜を提供する。
In
本発明は、基材のCo含有量が重量%で3%以上、12%未満であり、物理蒸着法によって該基材にA層とB層とが被覆され、該A層は、金属元素としてTi、Cr、Al、Si、Nbのうちの少なくとも1種又は2種以上より選択された元素と、非金属元素としてNを含みC、O、Bのうち1種又は2種以上より選択された元素から構成され、N、C、O、Bを原子%で100とした時、Nを60原子%以上含有し、更に結晶構造がfcc構造を有する皮膜であり、該B層は該A層の直上に接する硬質炭素膜、非晶質の硬質炭素膜、Ti、Cr、Al、Si、Mo、Wより選択される1種以上の元素を含有した酸化物、硼化物、硫化物及び窒化硼素、から選択される少なくとも1種以上の潤滑性皮膜であり、該A層と該B層との界面から該A層の膜厚方向に500nm未満の領域における結晶粒径の平均値が、2nm以上、14nm以下であることを特徴とする多層皮膜被覆切削工具であり、本構成を採用することにより、A層及びB層間の密着性が極めて優れ、大幅な耐摩耗性の改善を可能にする。本発明の耐摩耗皮膜は、B層とA層との密着強度を保つために、中間層を用いていない。その代わりとして、A層のfcc構造を維持しながら、該A層と該B層との界面から該A層の膜厚方向に500nm未満の領域における結晶粒径の平均値を2nm以上、14nm以下に制御することが2層間の密着性を維持するために極めて有効な手段となる。 In the present invention, the Co content of the substrate is 3% or more and less than 12% by weight, and the A layer and the B layer are coated on the substrate by physical vapor deposition, and the A layer is used as a metal element. An element selected from at least one or more of Ti, Cr, Al, Si, and Nb, and N as a nonmetallic element, selected from one or more of C, O, and B It is composed of an element, and when N, C, O, and B are defined as 100 in atomic%, N is 60% by atom or more, and the crystal structure has a fcc structure. A hard carbon film directly in contact therewith, an amorphous hard carbon film, an oxide, a boride, a sulfide and a boron nitride containing one or more elements selected from Ti, Cr, Al, Si, Mo, W, represents at least one lubricating coating selected from the from the interface between the a layer and the B layer Average grain size in the region of less than 500nm in the thickness direction of the layer, 2 nm or more, a multilayer film coated cutting tool, characterized in that at 14nm or less, by employing the present configuration, A layer and The adhesion between the B layers is extremely excellent, and the wear resistance can be greatly improved. The wear resistant film of the present invention does not use an intermediate layer in order to maintain the adhesion strength between the B layer and the A layer. Instead, while maintaining the fcc structure of the A layer, the average value of the crystal grain size in the region of less than 500 nm in the film thickness direction of the A layer from the interface between the A layer and the B layer is 2 nm or more and 14 nm or less. It is an extremely effective means for maintaining the adhesion between the two layers.
本発明のA層は、基材と接するように被覆され、Ti、Cr、Al、Si、Nbのうちの少なくとも1種以上より選択された元素の酸窒化物又は硼窒化物であり、更には、該A層の非金属元素のC、O、Bのうち1種又は2種以上が0.1原子%以上、7原子%未満未満含有することである。更に好ましくは、Alを含有し、Al含有量が金属成分のみの原子%で50%以上90%未満である。 The A layer of the present invention is an oxynitride or boronitride of an element coated so as to be in contact with the substrate and selected from at least one of Ti, Cr, Al, Si, and Nb. In addition, one or more of C, O, and B of the nonmetallic elements of the A layer are contained in an amount of 0.1 atomic% or more and less than 7 atomic%. More preferably, Al is contained, and the Al content is 50% or more and less than 90% by atomic% of only the metal component.
本発明のB層は、最表面に被覆されていることであり、表面から膜厚方向に20nm以内の領域に、2原子%以上のOを含有すること、が好ましい。 The B layer of the present invention is coated on the outermost surface, and preferably contains 2 atomic% or more of O in a region within 20 nm from the surface in the film thickness direction.
本発明の耐摩耗皮膜は、ドリル、タップ、リーマ、エンドミル、刃先交換型インサート、歯切り工具、ブローチからなる群より選ばれた工具に被覆されることであり、更にドリルは工具外径に対する加工深さが3倍以上、25倍以下で使用可能なドリルであことである。
本発明の被覆方法は、スパッタリング法、アークイオンプレーティング法(以下、AIP法と言う。)の何れかの方法を用いて被覆するか、両者の方法を同時に用いて被覆するかにより、該A層と該B層とを同一真空容器内で被覆することである。上記の様な構成を採用することで、切削加工の高能率化に有効である切削工具を提供することを可能にし、技術課題を解決するに至った。
The wear-resistant film of the present invention is to be coated on a tool selected from the group consisting of a drill, a tap, a reamer, an end mill, a cutting edge replaceable insert, a gear cutting tool, and a broach. It is a drill that can be used at a depth of 3 to 25 times.
The coating method according to the present invention can be applied depending on whether the coating is performed by using any one of the sputtering method and the arc ion plating method (hereinafter referred to as AIP method) or by using both methods simultaneously. Coating the layer and the B layer in the same vacuum vessel. By adopting the configuration as described above, it has become possible to provide a cutting tool that is effective in improving the efficiency of cutting, and has solved the technical problem.
本発明により、切削加工の高能率化、並びに耐摩耗性を大幅に改善することを可能にし、切削加工における生産性向上並びにコスト低減に極めて有効な多層皮膜被覆切削工具並びに被覆方法を提供することができた。 According to the present invention, it is possible to provide a multi-layer coated coated cutting tool and a coating method that can improve the efficiency of cutting and greatly improve the wear resistance, and are extremely effective in improving productivity and reducing costs in cutting. I was able to.
切削加工において、切削工具の耐摩耗性を維持しつつ、潤滑特性を併せ持つ耐摩耗皮膜が有効ではある。しかしながら、これらの特性を満足させるには、高硬度を有する耐摩耗皮膜に加え、その上に被覆される潤滑特性を持つ皮膜が脱落しないことが前提となる。耐摩耗皮膜と潤滑特性を持つ皮膜との界面が強度不足もしくは密着強度不十分により、潤滑特性を持つ皮膜が脱落した場合、その界面部を起点として、被加工物が工具表面に付着する現象を誘発する(以下、溶着と言う。)。この溶着が連続的に発生すると異常摩耗が発生し、切れ刃のチッピング、欠けにより、切削工具は短寿命となる。そこで本発明は、このA層と潤滑特性を持つB層との2層間の密着性を飛躍的に改善すれば切削寿命が大幅に改善できることに着目し、本発明を完成させた。 In cutting, an abrasion-resistant film having lubrication characteristics while maintaining the abrasion resistance of the cutting tool is effective. However, in order to satisfy these characteristics, it is premised that a film having a lubricating characteristic coated thereon does not fall off in addition to a wear-resistant film having high hardness. When the interface between the wear-resistant coating and the coating with lubrication characteristics is insufficient or the adhesion strength is insufficient, and the coating with lubrication characteristics falls off, the phenomenon that the workpiece adheres to the tool surface starting from the interface Induces (hereinafter referred to as welding). When this welding occurs continuously, abnormal wear occurs, and the cutting tool has a short life due to chipping and chipping of the cutting edge. Therefore, the present invention has been completed by paying attention to the fact that the cutting life can be greatly improved by drastically improving the adhesion between the two layers of the A layer and the B layer having lubricating properties.
本発明は、基材にCoを3重量%以上、12重量%未満含有する場合、特に本発明皮膜との密着性に優れることより、基材のCo含有量を上記範囲に設定した。
A層は、Ti、Cr、Al、Si、Nbのうちの少なくとも1種又は2種以上より選択された元素と、非金属元素として、NとC、O、Bのうち1種又は2種以上より選択された元素から構成され、N、C、O、Bを原子%で100としたときに、Nを60原子%以上含有する必要がある。これらにより構成されるA層は、高硬度で耐摩耗性に優れ、本発明のB層との密着性にも優れるからである。A層のN含有量が60原子%未満の場合、皮膜硬度が十分に得られず、耐摩耗性が得られないばかりでなく、B層との密着強度も低下する。A層は、結晶構造がfcc構造を主体とすることが極めて重要である。これはB層との密着強度を高めるためである。更にB層との密着強度を高めるための手段として、該A層の表面から深さ方向に500nm未満の領域における結晶粒径の平均値が、2nm以上、14nm以下であることが本発明において最も重要な手段となる。上記結晶粒径の制御が、B層との界面において、明瞭な界面を形成し難い構造を形成し、密着強度を著しく改善することを可能にした。また、B層の膜厚は、20nm以上、500nm未満の値が好ましい。この理由は、膜厚が20nm未満では、B層の持つ低摩擦効果が十分ではなく、500nmを越えると、界面破壊もしくは剥離に起因した剥離異常摩耗が発生しやすくなるためである。上記構成を採用することで、A層とB層との界面に中間層を用いなくても、極めて優れた密着強度を得ることができ、極めて長い切削寿命を得ることができる。
In the present invention, when Co is contained in the substrate in an amount of 3 wt% or more and less than 12 wt%, the Co content of the substrate is set in the above range because it is particularly excellent in adhesion to the coating of the present invention.
A layer is an element selected from at least one or more of Ti, Cr, Al, Si, and Nb, and one or more of N, C, O, and B as non-metallic elements. It is comprised from the more selected element, and when N, C, O, and B are set to 100 in atomic%, it is necessary to contain N 60 atomic% or more. This is because the A layer constituted by these has high hardness, excellent wear resistance, and excellent adhesion to the B layer of the present invention. When the N content of the A layer is less than 60 atomic%, the film hardness is not sufficiently obtained, the wear resistance is not obtained, and the adhesion strength with the B layer is also lowered. It is extremely important for the A layer that the crystal structure is mainly an fcc structure. This is to increase the adhesion strength with the B layer. Further, as a means for increasing the adhesion strength with the B layer, the average value of the crystal grain diameter in the region of less than 500 nm in the depth direction from the surface of the A layer is 2 nm or more and 14 nm or less in the present invention. It becomes an important means. The control of the crystal grain size makes it possible to form a structure in which it is difficult to form a clear interface at the interface with the B layer, and to significantly improve the adhesion strength. Further, the thickness of the B layer is preferably 20 nm or more and less than 500 nm. The reason for this is that if the film thickness is less than 20 nm, the low friction effect of the B layer is not sufficient, and if it exceeds 500 nm, abnormal peeling due to interfacial fracture or peeling tends to occur. By adopting the above configuration, extremely excellent adhesion strength can be obtained without using an intermediate layer at the interface between the A layer and the B layer, and an extremely long cutting life can be obtained.
B層は、最表面に被覆されていることが有効であり、この場合、特に耐溶着性に優れるからである。また、B層の上層として、200μm未満の厚さの、A層を用いた場合も、B層の効果が失われず耐溶着性に対して同様な効果が得られる場合もあった。
B層は、硬質炭素膜からなる場合又は非晶質の硬質炭素膜からなる場合に耐溶着性に優れる。更に、Ti、Cr、Al、Si、Mo、Wより選択される1種以上の元素を含有した酸化物、硼化物、硫化物及び窒化硼素から選択される少なくとも1種以上から構成される皮膜である場合にも潤滑性を有し、耐溶着性に優れる。
B層の表面から20nm以内の範囲に、2原子%以上の酸素を含有する場合、そうでないものに比べて、溶着量が少なく、耐溶着性に優れる。20nm以内の範囲が好ましいとした理由は、20nmを超えて大きい場合、耐溶着性が劣化する傾向にあったためである。また、2原子%未満の酸素含有量は、酸素を含有しないものと大きく性能は変わらなかった。上記の理由から、B層の酸素含有の範囲と含有量を上記数値に設定した。
It is effective that the B layer is coated on the outermost surface, and in this case, it is particularly excellent in welding resistance. Further, when the A layer having a thickness of less than 200 μm was used as the upper layer of the B layer, the effect of the B layer was not lost and the same effect on the welding resistance was sometimes obtained.
The B layer is excellent in welding resistance when it is made of a hard carbon film or an amorphous hard carbon film. Furthermore, it is a film composed of at least one selected from oxides, borides, sulfides and boron nitrides containing one or more elements selected from Ti, Cr, Al, Si, Mo and W. In some cases, it has lubricity and has excellent welding resistance.
When 2 atomic% or more of oxygen is contained within the range of 20 nm or less from the surface of the B layer, the amount of welding is small and the welding resistance is excellent as compared with the case where it does not. The reason why the range within 20 nm is preferable is that when it exceeds 20 nm, the welding resistance tends to deteriorate. Moreover, the oxygen content of less than 2 atomic% was not significantly different from that containing no oxygen. For the above reasons, the range and content of oxygen content in the B layer were set to the above numerical values.
A層の非金属元素のC、O、Bのうち1種又は2種以上が0.1原子%以上、7原子%未満とすることにより、0.1原子%未満では、添加効果が十分に確認されなかった。また、7原子%以上の場合は、A層の硬度が低下してしまい、耐摩耗性に劣る場合と、B層との密着性が劣化する場合があった。
A層は、Alを含有し、Al含有量が金属成分のみの原子%で50%以上、90%未満とする。Al含有量が50%未満の場合、並びに90%以上の場合は、皮膜硬度が低下する傾向にあり適切ではない。また、B層との密着強度も低下する傾向にあり、上記の範囲とする。
By making one or more of C, O, and B of the non-metallic elements of the A layer 0.1 atomic% or more and less than 7 atomic%, the effect of addition is sufficiently low if the content is less than 0.1 atomic%. It was not confirmed. Further, in the case of 7 atomic% or more, the hardness of the A layer is lowered, and there are cases where the wear resistance is inferior and the adhesion with the B layer is deteriorated.
The A layer contains Al, and the Al content is 50% or more and less than 90% in atomic% of only the metal component. When the Al content is less than 50%, and when it is 90% or more, the film hardness tends to decrease, which is not appropriate. Moreover, it exists in the tendency for the adhesive strength with B layer to fall, and it is set as said range.
本発明の切削工具は、ドリル、タップ、リーマ、エンドミル、刃先交換型インサート、歯切り工具、ブローチからなる群より選ばれた切削工具であり、これらの切削工具は、本発明皮膜の改善効果が特に顕著に確認できる。更に、本発明の耐摩耗皮膜を、工具外径に対する加工深さが3倍以上、25倍以下で使用可能であるドリルに被覆することにより、特に切削加工の高能率化が可能となる。 The cutting tool of the present invention is a cutting tool selected from the group consisting of a drill, a tap, a reamer, an end mill, a cutting edge replaceable insert, a gear cutting tool, and a broach, and these cutting tools have the effect of improving the coating of the present invention. This is particularly noticeable. Further, by coating the wear resistant coating of the present invention on a drill that can be used at a machining depth of 3 times or more and 25 times or less with respect to the outer diameter of the tool, particularly high efficiency of cutting work can be achieved.
本発明の被覆方法は、スパッタリング法、AIP法の何れかの方法を用いて被覆するか、両者の方法を同時に用いて被覆することにより、A層とB層とを同一真空容器内で連続的に被覆する被覆方法である。AIP法で耐摩耗皮膜を被覆した後に、スパッタリング法で潤滑性皮膜を被覆することも可能であり好ましいが、この時スッパッタリング法のみ別の被覆装置で被覆するよりも、連続して行うことが2層間の密着強度の観点から特に適切である。同様にAIP法とスパッタリング法を同時に行う場合も、2層間の密着強度の改善に有効であり好ましい。耐摩耗皮膜の基材への密着性の改善及び、欠損を防止することを目的とし、被覆前後に、工具切刃を機械的処理によってなじませることにより、突発的な切刃もしくは硬質皮膜のチッピングが抑制され好ましい。また、被覆中に硬質皮膜表面及び硬質皮膜内部に付着したドロップレット等を、機械的処理により除去することも、低摩擦に有効であり異常摩耗の抑制にも効果的であり好ましい。本発明の多層皮膜被覆工具は、被削材として炭素鋼、合金鋼などの鋼や鋳鉄に使用すると効果的である。以下、本発明を実施例に基づいて説明するが、本発明皮膜は下記に限定されるものではなく、適宜変更を行うことは、本技術範囲に含まれるものである。 In the coating method of the present invention, either the sputtering method or the AIP method is used, or both methods are simultaneously used to coat the A layer and the B layer continuously in the same vacuum vessel. It is the coating method which coat | covers. It is possible and preferable to coat the lubricating film by sputtering after coating the wear-resistant film by the AIP method, but at this time, it is performed continuously rather than coating only the sputtering method by another coating apparatus. Is particularly suitable from the viewpoint of adhesion strength between two layers. Similarly, when the AIP method and the sputtering method are simultaneously performed, it is effective and preferable for improving the adhesion strength between the two layers. For the purpose of improving adhesion of the wear-resistant film to the substrate and preventing chipping, sudden cutting of the cutting edge or hard film is performed by applying the tool cutting edge mechanically before and after coating. Is preferable. It is also preferable to remove droplets and the like adhering to the hard coating surface and the hard coating during coating by mechanical treatment, which is effective for low friction and effective in suppressing abnormal wear. The multilayer coated tool of the present invention is effective when used as a work material for steel such as carbon steel and alloy steel and cast iron. EXAMPLES Hereinafter, although this invention is demonstrated based on an Example, this invention film | membrane is not limited to the following, It is contained in this technical scope to change suitably.
AIP法とスパッタリング法との併用が可能な装置による被覆の場合は、以下記載による方法により被覆することが可能である。即ち、目的とする組成となるよう作成した各種合金製ターゲット、並びに各種反応ガスであるN2、C2H2、O2、CH4、CO2、Arの何れかもしくはその組合せによる反応ガスを用いた。また、N、C、Oに関しては、被覆の際にガスを真空容器内に導入することにより硬質皮膜に添加することも可能であるが、別の手段として、金属ターゲットに予め添加することによっても可能である。被覆基材は化学的手段による洗浄と乾燥を行い、アークイオンプレーティング用蒸発源を配備する真空容器内に配置した。ここで、被覆基材は、Co量の異なる超硬合金製の外径6mmの2枚刃ドリルと外径8mmの4枚刃エンドミルを用いた。
基材温度が525℃となるよう加熱及び排気を行い、Arを真空容器内に導入しこれをイオン化して、Arイオンによる被覆基材のクリーニングを行った。反応ガスを真空容器内に導入し、各種合金ターゲット表面にアーク放電を発生させ、負のバイアス電圧を印加して基材に被覆処理を行った。この時のバイアス電圧は−40Vに設定し、所定の膜厚に達した後、A層の最表層の結晶粒径を2nm以上、14nm以下に制御するるための処理を実施した。処理方法としては複数の方法から選択することができる。第1の方法は、A層の被覆終了5分前に、バイアス電圧をパルス状に変化させて、−500V、+20Vのバイアス電圧を印加することにより、結晶粒径を上記範囲に制御することである。第2の方法は、Bを8原子%添加したターゲットを用いることである。第3の方法は、上記のパルス状バイアス電圧に加えて、N2ガスとO2ガスとを、80対20の割合で同時に真空容器内に導入することにより、O2を硬質皮膜内へ添加しながら結晶粒径を制御することである。第4の方法は、O2ガスの代わりに、COガス、CO2ガスを導入することによって、硬質皮膜内への酸素の添加が可能であり、結晶粒径の制御することである。本実施例では、第1の方法を採用した。C2H2ガス、CH4ガス、CO2ガス、CO、O2ガスを真空容器内に導入する場合は、被覆蒸発源とは独立した別の蒸発源でアーク放電を行いながら、被覆することによりガスのイオン化及び反応性が向上し、C、O等の通常の物理的蒸着法による被覆装置ではイオン化が困難であるガス成分を、安定して硬質皮膜内へ添加できることが可能となり、組織構造の制御を容易に行うことができた。前記ガス添加方法としては、硬質皮膜内におけるC、O濃度を調整するために、C、O含有ガスを真空容器内へ導入しながら、被覆用のアーク放電蒸発源とは独立した別のアーク放電蒸発源でCr系、Ti系金属を蒸発させ、その蒸発量を調整させながら、ガス添加量を調整した。この時、被覆用アーク放電蒸発源とは独立した別のアーク放電蒸発源の前面に遮蔽板を設け、ガスイオン化用の蒸発源から被覆されないように配慮した。前記ガスのイオン化の方法は極めてイオン化率が高いため、上記ガスに限定せずとも、Ar、N2などのイオン化にも有効である。
In the case of coating with an apparatus capable of using both the AIP method and the sputtering method, the coating can be performed by the method described below. That is, various alloy targets prepared so as to have a target composition, and reaction gases of any of
Heating and evacuation were performed so that the substrate temperature was 525 ° C., Ar was introduced into the vacuum vessel and ionized, and the coated substrate was cleaned with Ar ions. The reaction gas was introduced into a vacuum vessel, arc discharge was generated on the surfaces of various alloy targets, and a negative bias voltage was applied to coat the substrate. The bias voltage at this time was set to −40 V, and after reaching a predetermined film thickness, a process for controlling the crystal grain size of the outermost layer of the A layer to 2 nm or more and 14 nm or less was performed. A processing method can be selected from a plurality of methods. The first method is to control the crystal grain size within the above range by changing the bias voltage in a pulse form and applying bias voltages of −500 V and +20
上記の被覆方法でA層を被覆し、連続してB層を被覆した。ここで重要となるのがB層の形成に用いるターゲット表面の汚染物質を、A層とB層との界面に存在させないようにすることである。そのため、A層から、B層の被覆プロセスへ移行するステップでは、A層の被覆プロセス終了する5分前に、B層に使用するスパッタリング蒸発源に電流を供給し、ターゲット材のスパッタリングを開始した。スパッタリングターゲットの前面に可動式の遮蔽板を設け、スパッタリングされたターゲット材料及びターゲット表面の汚染物質が基材に到達しないようにした。この汚染物質は、例えば被覆前処理に行うArエッチング中に付着した物質、基材の加熱中に付着した物質もしくは真空容器を開けた際に付着した物質のことを指す。ターゲットの前面に遮蔽板を設けた状態で5分間放電を継続し、ターゲット表面をクリーニングし、次にターゲット前面の遮蔽板を移動させ、イオン化したターゲット材料を基材へと導き、被覆処理を行った。B層が所定の膜厚に達した時点で蒸発源への電流供給を停止し、基材の冷却を行った。更にB層の表面から膜厚方向に20nm以内の領域に2原子%以上の酸素を添加するには、ターゲット材前面の可動式遮蔽板を再びターゲット材前面に移動させてターゲット材料が基材に到達しない様にし、Arに対するO2比率を1:1で真空容器内に導入しながら、バイアス電圧を−300Vに設定し3分間処理を継続させ、B層内へ酸素を添加した。 The A layer was coated by the above coating method, and the B layer was continuously coated. What is important here is that contaminants on the surface of the target used for forming the B layer do not exist at the interface between the A layer and the B layer. Therefore, in the step of shifting from the A layer to the B layer coating process, five minutes before the completion of the A layer coating process, current was supplied to the sputtering evaporation source used for the B layer, and sputtering of the target material was started. . A movable shielding plate was provided on the front surface of the sputtering target so that the sputtered target material and contaminants on the target surface did not reach the substrate. This contaminant refers to, for example, a substance attached during Ar etching performed for pre-coating, a substance attached during heating of the substrate, or a substance attached when the vacuum container is opened. Discharge continues for 5 minutes with the shielding plate in front of the target, cleans the target surface, then moves the shielding plate in front of the target, guides the ionized target material to the base material, and performs the coating process It was. When the layer B reached a predetermined film thickness, the supply of current to the evaporation source was stopped and the substrate was cooled. Further, in order to add 2 atomic% or more of oxygen to a region within 20 nm in the film thickness direction from the surface of the B layer, the movable shielding plate on the front surface of the target material is moved again to the front surface of the target material, and the target material becomes the base material. In order not to reach it, the O 2 ratio to Ar was introduced into the vacuum vessel at 1: 1, while the bias voltage was set to −300 V and the treatment was continued for 3 minutes, and oxygen was added into the B layer.
上記の被覆方法で、表1に示す耐摩耗皮膜を被覆した。
表1〜表3に示す組成の定量分析は、エネルギー分散型X線分光法、オージェ電子分光法及び電子線エネルギーロス分光法を用い、総合的に決定した。表1〜表3に示す組成の表示は金属成分、非金属成分を夫々合わせて100となる様に原子%で表記したが、ここでは金属成分と比金属成分の原子比が1:1であることを意味するものではない。A層及びB層の結晶構造の解析は、X線回折法を用いて行った。結晶粒子径の測定は、例えば硬質皮膜断面を透過型電子顕微鏡によりランダムに選択した視野の断面写真より実測した。図2に結晶粒子径を測定するための1つの方法を模式図により示す。
図1はB層(1)とA層(2)の境界面(4)を示し、本発明の結晶粒子径は、境界面(4)に接するA層(2)の結晶粒子の幅(3)を示し、境界面方向に1μmの領域で測定した場合の平均値である。B層をA層の直上面に被覆した場合、表面から膜厚方向に20nm以内の領域における酸素含有量の決定にはオージェ電子分光法を用いて深さ方向に定量分析を行った。表1中の被覆方法とは、各層の被覆方法を夫々記載したものであり、アークイオンプレーティング法をAIP法として示した。連続処理とは、A層から連続してB層を被覆する処理のことである。
The wear-resistant film shown in Table 1 was coated by the above coating method.
The quantitative analysis of the compositions shown in Tables 1 to 3 was comprehensively determined using energy dispersive X-ray spectroscopy, Auger electron spectroscopy, and electron beam energy loss spectroscopy. The display of the composition shown in Tables 1 to 3 is expressed in atomic% so that the total of the metal component and the non-metal component is 100. Here, the atomic ratio of the metal component and the specific metal component is 1: 1. It doesn't mean that. Analysis of the crystal structures of the A layer and the B layer was performed using an X-ray diffraction method. The crystal particle diameter was measured from, for example, a cross-sectional photograph of a visual field in which a hard film cross section was randomly selected by a transmission electron microscope. FIG. 2 schematically shows one method for measuring the crystal particle diameter.
FIG. 1 shows the boundary surface (4) between the B layer (1) and the A layer (2), and the crystal particle diameter of the present invention is the width of the crystal particle (3) of the A layer (2) in contact with the boundary surface (4). ) And is an average value when measured in a 1 μm region in the boundary surface direction. When the layer B was coated on the immediate upper surface of the layer A, the oxygen content in the region within 20 nm from the surface in the film thickness direction was determined by quantitative analysis in the depth direction using Auger electron spectroscopy. The coating method in Table 1 describes the coating method of each layer, and the arc ion plating method is shown as the AIP method. A continuous process is a process which coat | covers B layer continuously from A layer.
実施例によって得られた耐摩耗皮膜を被覆した超硬合金製2枚刃ドリルを用い、切削試験を行った。評価はドリルコーナー部の摩耗幅が0.2mmに達した時点の穴加工数、切屑が分断されずに排出された時点の穴加工数、ドリルが折れた時点の穴加工数、もしくは切削動力が急上昇し穴加工ができなくなった時点の穴加工数のうち、最も少ない数値を測定した。切削諸元を次に示す。ドリル切削条件1は乾式による切削加工であり、ドリル切削条件2は水溶性切削液を外部より供給しながらの湿式の切削加工を行い、結果を表1に示す。穴加工数値は50穴未満を繰り下げて表示した。
(ドリル切削条件1)
工具:2枚刃ドリル、外径6mm
被覆基材:超硬合金製
切削方法:止まり穴加工
被削材:SCM440(HRC30)
穴深さ:32mm
切削速度:70m/min
送り:0.5mm/rev
切削油:なし、乾式エアーブロー
(ドリル切削条件2)
工具:2枚刃ドリル、外径6mm
被覆基材:超硬合金製
切削方法:止まり穴加工
被削材:SCM440(HRC30)
穴深さ:32mm
切削速度:150m/min
送り:0.3mm/rev
切削油:水溶性エマルションタイプ使用、外部給油による
A cutting test was performed using a cemented carbide two-blade drill coated with the abrasion-resistant film obtained in the examples. The evaluation is based on the number of holes processed when the wear width of the drill corner reaches 0.2 mm, the number of holes processed when chips are discharged without being cut, the number of holes processed when the drill is broken, or the cutting power. The smallest numerical value was measured out of the number of holes drilled at the time when the hole could not be drilled rapidly. The cutting specifications are shown below. The
(Drill cutting condition 1)
Tool: 2-flute drill, outer diameter 6 mm
Covering base material: Cemented carbide made Cutting method: blind hole processing Material: SCM440 (HRC30)
Hole depth: 32mm
Cutting speed: 70 m / min
Feed: 0.5mm / rev
Cutting oil: None, dry air blow (drill cutting condition 2)
Tool: 2-flute drill, outer diameter 6 mm
Covering base material: Cemented carbide made Cutting method: blind hole processing Material: SCM440 (HRC30)
Hole depth: 32mm
Cutting speed: 150 m / min
Feed: 0.3mm / rev
Cutting oil: Water-soluble emulsion type used, by external lubrication
実施例によって得られた耐摩耗皮膜を被覆した超硬合金製4枚刃エンドミルを用い、切削試験を行った。評価は、工具送り方向とは直角方向における加工面粗さが20μmを越えた時点の切削長を測定した。加工面粗さが20μmを超えた状態において工具には多数の溶着物が付着し、工具摩耗も進行する。従って、溶着物が付着しない耐摩耗皮膜程、長い切削長が得られる。切削諸元を示し、その結果を表1〜表3に示す。数値は10m未満を繰り下げて表示した。
(エンドミル切削条件)
工具:4枚刃エンドミル、外径8mm
被覆基材:超硬合金製
切削方法:側面ダウンカット
被削材:Ti−6Al−4V(HRC30)
突き出し長さ:25mm
切削速度:400m/min
送り:0.07mm/刃
切込み:軸方向12mm、径方向0.2mm
切削油:水溶性エマルションタイプ使用、外部給油による。
A cutting test was carried out using a cemented carbide four-blade end mill coated with the abrasion-resistant film obtained in the examples. In the evaluation, the cutting length was measured when the surface roughness in the direction perpendicular to the tool feed direction exceeded 20 μm. In the state where the processed surface roughness exceeds 20 μm, a large number of deposits adhere to the tool, and the tool wear also progresses. Accordingly, a longer cutting length can be obtained as the wear-resistant film to which the welded material does not adhere. Cutting specifications are shown, and the results are shown in Tables 1 to 3. The numerical value is displayed below 10 m.
(End mill cutting conditions)
Tool: 4-flute end mill, outer diameter 8mm
Coated substrate: Cemented carbide made Cutting method: Side down cut Work material: Ti-6Al-4V (HRC30)
Protrusion length: 25mm
Cutting speed: 400 m / min
Feed: 0.07 mm / blade Cutting depth: 12 mm in the axial direction, 0.2 mm in the radial direction
Cutting oil: Use water-soluble emulsion type, external lubrication.
表1、表2に示す本発明例、比較例及び表3に示す従来例と比較して、安定した切削寿命が得られた。以下、本発明例の詳細について述べる。
本発明例1は、基材と接する耐摩耗皮膜がAlTiN皮膜で、その上にA層とB層である硬質炭素膜を被覆した場合を示すが、従来例に比べて切削寿命が長い。本発明例2から本発明例4は、A層が窒酸化膜又は硼窒化膜の場合の事例を示すが、従来例に比べて切削寿命が長い。本発明例5から本発明例15は、基材と接する耐摩耗皮膜が窒酸化膜又は硼窒化膜の場合の事例を示すが、特に切削寿命が長い。一方、比較例18は、耐摩耗皮膜の最表面にA層を0.8μ被覆した場合であるが、B層の効果が確認されなかった。比較例19、比較例21は、A層が、VTiN、ZrTiNの場合の事例を示すが、皮膜硬度が低い上に、B層との密着強度が悪く、異常摩耗が発生し、切削寿命が短い。
Compared with the present invention example shown in Table 1 and Table 2, the comparative example, and the conventional example shown in Table 3, a stable cutting life was obtained. Details of the present invention will be described below.
Inventive Example 1 shows a case where the wear-resistant film in contact with the base material is an AlTiN film, and a hard carbon film which is an A layer and a B layer is coated thereon, but has a longer cutting life than the conventional example. Invention Examples 2 to 4 show examples where the A layer is a oxynitride film or a boronitride film, but the cutting life is longer than that of the conventional example. Invention Examples 5 to 15 show examples where the wear-resistant film in contact with the substrate is a oxynitride film or a boronitride film, and the cutting life is particularly long. On the other hand, Comparative Example 18 is a case where the outermost surface of the abrasion-resistant film was coated with 0.8 μm of the A layer, but the effect of the B layer was not confirmed. Comparative Example 19 and Comparative Example 21 show examples where the A layer is VTiN or ZrTiN, but the film hardness is low, the adhesion strength with the B layer is poor, abnormal wear occurs, and the cutting life is short. .
比較例21は、A層のN含有量が52原子%の場合の事例を示すが、低硬度であり、本発明例に比べて耐摩耗性が劣る結果となった。比較例29から比較例32は、B層が結晶質からなる場合であるが、A層との密着強度が不十分であり異常摩耗を誘発し、本発明例に比べて著しく耐摩耗性に劣る結果となった。以上の実施例により、本発明皮膜は、A層とB層の密着強度が極めて優れ、剥離等による異常摩耗の発生を著しく抑制し、従来例に比べ著しく切削寿命を改善することが可能であることが確認できた。
Comparative Example 21 shows an example in which the N content of the A layer is 52 atomic%, but the hardness is low and results in inferior wear resistance compared to the inventive example. Comparative Examples 29 to 32 are cases where the B layer is made of a crystalline material, but the adhesion strength with the A layer is insufficient and induces abnormal wear, which is remarkably inferior in wear resistance compared to the examples of the present invention. As a result. According to the above examples, the coating of the present invention has extremely excellent adhesion strength between the A layer and the B layer, significantly suppresses the occurrence of abnormal wear due to peeling and the like, and can significantly improve the cutting life compared to the conventional example. I was able to confirm.
1:B層
2:A層
3:B層と接するA層の結晶粒径
4:B層とA層の境界面
1: B layer 2: A layer 3: Crystal grain size of A layer in contact with B layer 4: Interface between B layer and A layer
Claims (7)