JP4080628B2 - Removable foam gasket - Google Patents
Removable foam gasket Download PDFInfo
- Publication number
- JP4080628B2 JP4080628B2 JP08896199A JP8896199A JP4080628B2 JP 4080628 B2 JP4080628 B2 JP 4080628B2 JP 08896199 A JP08896199 A JP 08896199A JP 8896199 A JP8896199 A JP 8896199A JP 4080628 B2 JP4080628 B2 JP 4080628B2
- Authority
- JP
- Japan
- Prior art keywords
- foam
- pressure
- sensitive adhesive
- adhesive
- removable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】
【発明の属する技術分野】
本発明は再剥離性の発泡体ガスケットに関する。更に詳しくは、発泡体ガスケットの少なくも一面にウレタン系の再剥離性粘着剤を施した再剥離性発泡体ガスケットに関する。
【0002】
【従来技術】
従来より再剥離性粘着剤は、事務用ラベル、医療用粘着テープ、ごみ取りローラーなどに応用されている。ここで再剥離性粘着剤とは、被着体に粘着剤をもって貼着物を貼りつけた後、これを剥がした時に、被着体に粘着剤が残留せず、貼着物に粘着剤が残留して剥がすことができ、再度、この貼着物を被着体に貼着できる機能を有する粘着剤を言う。
再剥離性粘着剤はその凝集力が高い為、被着体より貼着物を剥がす時に凝集破壊を起こさず剥がれるものである。しかし、感圧接着性は弱いため、発泡体にその粘着剤をラミネートするのに、通常の両面テープと同様な転写法で行なうことは不可能であった。
この事を改良する為、本発明者等による特願平10−99401で、ポリオールとイソシアナートを主成分とした反応型ポリウレタン系粘着剤を、未硬化の状態で発泡体にラミネートし、粘着剤付き発泡体を得る事が提案されている。これにより、再剥離性の粘着剤付き発泡体が得られた。
しかしながら、本発明者等は、防水性等を要求される用途においては、発泡体自体が防水性等を持つ材料であっても、上記の粘着剤を用いると防水性能が発揮できず、更には、ウレタン粘着剤が被着体に付着するので、再剥離性の性能が低下する事を明らかとした。このことは従来考えられない事で、発泡体自体が止水性を有する場合、その表面に膜状粘着剤を付ければ当然止水性は向上するか、又は向上しないまでも低下しないものと考えることが常識であった。
同様に防湿の目的で発泡体ガスケットに前記のウレタン粘着剤を付けると、驚くべき事に発泡体ガスケット単独の場合よりも防湿性が劣ることが明らかとなった。
【0003】
【発明が解決しようとする課題】
本発明者は、上記問題点を解決し、止水性や防湿性を低下させることなく再剥離性粘着剤付き発泡体ガスケットを得るために種々検討した結果、本発明を完成したもので、本発明の目的は、優れた防水、防湿を有し、且つ、再剥離性を有する発泡体ガスケットを提供する事である。
【0004】
【課題を解決する為の手段】
本発明の要旨は、発泡体シートの少なくとも一面に再剥離性粘着剤をラミネートした再剥離性発泡体ガスケットであって、該発泡体シートは接触角が90度以上の疎水性発泡体であり、該発泡体シートにラミネートした粘着剤は疎水性ポリオールとイソシアナートと触媒を必須成分としたウレタン系粘着剤であり、該ウレタン系粘着剤は前記発泡体とラミネート、硬化後の粘着剤の接触角が90度以上であることを特徴とした再剥離性発泡体ガスケットである。
即ち、本発明は、接触角が90度以上の疎水性発泡体よりなる発泡体シートという特定の特性を有する発泡体シートの少なくとも一面に、硬化後の粘着剤の接触角が90度以上という特定の特性を有する再剥離性粘着剤をラミネートすることによって目的の再剥離性発泡体ガスケットを得ることが出来るのである。なお、発泡体及び粘着剤の接触角の測定については後述する。
【0005】
【発明の実施の形態】
本発明について詳細に述べる。
本発明の発泡体ガスケットとは、低通気性の連通気泡発泡体、又は独立気泡発泡体シートからなる防水、防塵、気密、防湿を目的としたシール材である。そして、この発泡体ガスケットに使用される発泡体シートは、発泡体ブロックよりスライスされた薄いシート状のものと、薄くシート状に発泡されたもので、EPDMゴム、エチレンープロピレンゴム、ポリエチレン、ポリプロピレン、エチレンー酢酸ビニルなどの、ゴム状またはオレフィン系発泡体、ウレタンフォーム、ポリ塩化ビニール発泡体などの可とう性発泡体が挙げられる。
これらの発泡体は独立気泡/連続気泡に関わらず、防水性を満足する為、発泡体は90度以上の疎水性発泡体である。接触角が90度以上のものである必要がある。連続気泡の場合、その通気度は10cc/cm3/sec以下の通気性が低い事が好ましい。これらの発泡体は防水すべき隙間に圧縮し、又は圧縮せず施工する事で、止水する機能を有するものである。
【0006】
発泡体シートの少なくとも一面にラミネートする粘着剤は、疎水性ポリオールとイソシアナートと触媒を必須成分としたウレタン系再剥離性粘着剤である。即ち、本発明の再剥離性の粘着剤は、疎水性ポリオールとイソシアナートを触媒を用いて硬化させたもので、その接触角は90度以上が必要である。接触角が90度以下であると、発泡体が止水性を有していても、粘着剤をラミネートした発泡体シートの止水性が大幅に低下する。更に、この粘着剤の吸水率は1.0%以下が好ましい。このように吸水率が低いと、長期間止水性が維持出来る。
なお、再剥離性と言う機能は前述のとおり、被接着面より粘着剤付きのガスケットを剥がしたときに、被接着表面に粘着剤が残留せず、かつガスケット材料もちぎれず剥がせることである。従って、性能を数値表現する場合に、ガスケット材の種類によっても異なるが、90°ピールで0.5kg/cm以下でかつ、プローブタック値で600g以上が好ましい。
疎水性ポリオールとは後に示す相溶性試験において合格するものをいい、分子骨格が炭化水素の高いポリオールである。それらは、ダイマー酸エステル、ひまし油、ひまし油エステル、炭化水素系ポリオールからなる群から選択された少なくとも1種のポリオール化合物が好ましい。ダイマー酸系ポリオールとして、ダイマー酸とエチレングリコール、ヂエチレングリコール、トリメチロールプロパン、グリセリンなどの多官能性の水酸化物とのエステル化物、及びこれらの脂肪酸、脂肪族アルコール変性品、ひまし油及びひまし油変性品、ポリブタジエン系ポリオール及びその水添品、ポリイソプレン系ポリオール及びその水添品、ダイマー酸の水素還元により得られるダイマージオールトこれを用いたエステル化合物などである。その他に、セバチン酸、リシノレン酸、ヒドロキシステアリン酸などの高級脂肪酸、高級脂肪アルコールを用いたエステル系ポリオールなども含まれる。
ポリオールはその一部又は全てを、後述のイソシアナートとあらかじめ反応させたプレポリマーとして用いても良い。ポリオールの全部をプレポリマーとした場合は、硬化反応を進めるためにエチレングリコール、1、4ーブタンジオールなどの鎖延長剤を用いることが好ましい。
【0007】
イソシアナートとしては、トリレンジイソシアナート(TDI)、ジフェニルメタンジイソシアナート(MDI)、粗製のMDI、ヘキサメチレンヂイソシアナート(HDI)、イソホロンジイソシアナートなどを単独又は2種以上混合して使用することが出来る。そして、これらの化合物はそのまま、又はポリオールと反応させプレポリマーとして使用することができる。
触媒は、ウレタン生産のため通常使われるトリエチレンヂアミンなどのアミン系触媒や、ジブチルチンジラウレート、スタナスオクトエートなどの錫系などの有機金属触媒が用いられる。
粘着剤の接触角を向上させる方法は、疎水性ポリオールを使用する事が良い方法ではあるが、それだけでなく、用いるイソシアナートもTDIよりMDIが良く、イソシアナート部数も少ないより多めが良い。また、触媒の添加は必須で、その添加量は少ないと接触角が向上しにくい。このように粘着剤の接触角はいろいろな要因で変化可能であり、それらは粘着性能などの物性との兼ね合で調整する。これらの組成割合としては、ポリオール成分に対してイソシアネート成分は、2〜20重量部の割合であり、触媒の使用量としては0.05〜0.5部程度である。
ウレタン系粘着剤には、耐候性向上のため、紫外線吸収剤の添加やカーボンブラックの配合が望ましい。特に、カーボンブラックは効果が大きくかつ持続性があるため好ましい。また、粘着力向上のため石油樹脂などの粘着付与剤、プロセスオイルなども添加出来る。
本発明の再剥離性発泡ガスケットの斜視図及び断面図を図1及び図2に示す。図において、本発明の再剥離性発泡ガスケット10は発泡体11の表面に再剥離性粘着剤層12を有し、該再剥離性粘着剤層12の表面にセパレーター13を有する。
【0008】
次に本発明にかかる再剥離性発泡ガスケットの製造方法を述べる。先ず、本発明で使用する粘着剤層の製造方法として、上述の原料を攪判し、剥離性のセパレーター上に塗工する。セパレーターは紙やプラスチックフィルムを基材とし、その表面をシリコーンなどの離型性のあるもので処理したものを用いる。塗工には、ナイフコーター、ロールコーター、ダイスコーター、スプレーコーターなどを用いる。
セパレーターにウレタン系粘着剤を塗工したのち、発泡体をすぐにラミネートしてもよいが、塗工後加熱により反応を進め、指触による増粘を確認した後、又は、糸引き現象を確認後、発泡体をラミネートすると粘着剤の接触角が90°以上に安定してなり易く、防水性が安定して好ましい。
【0009】
本発明の再剥離性発泡体ガスケットの製造方法を図示する。図3は製造方法の説明図であり、図4はその製造方法における粘着剤を塗工する説明図、図5は他の製造方法の概念図である。図3及び図4において、走行するセパレーター13上に再剥離性粘着剤12aを載せ、ドクターナイフ21で均一に塗工して再剥離性粘着剤層12を形成する。次いで、この粘着剤層12の上に予め発泡した発泡体11を載せ一体とする。他の方法としては、図5に示すように、セパレーター13上に再剥離性粘着剤層12をあらかじめ作っておき、これに発泡体の原料であるウレタンフォーム原液11aを塗工し、その後、発泡させて一体とする。このようなウレタンフォーム原液を塗工時にラミネートする方法も防水性が安定して好ましい。
本発明における再剥離性発泡体ガスケットの寸法としては、防水、防湿すべき物品によってことなるが、通常、厚さ0.5〜20mm程度である。
【0010】
【実施例】
次に実施例をもって本発明を更に具体的に説明する。実施例における各測定方法は次の方法によって行った。
(1)相溶性試験方法
試験管(直径18mm、長さ180mm)に試料2.0gを秤量し、ビュレットより溶剤(イソプロプルアルコール/水、75/25g/g)を滴下し、液が次第に濁りをッ生じ、試験官を透かして0.5mmの線が見えなくなった時の溶剤の添加量が2.0g以下の試料を合格とする。この時の液温は25℃とする。
(2)粘着力の測定方法
90度剥離力はJIS−1528に従い測定する。プローブタック力は、クロムメッキされた鏡面仕上げ表面のプローブ(10Φ×14mm,10g)をサンプルの粘着面に20秒靜置後、引っ張り試験機にて垂直方向に300mm/minのスピードで引っ張り、その荷重を読む。
【0011】
(3)防水性の測定方法
図6に示すアクリル製の試験治具を用いる。図6において、幅10mmで50mm角の試料1をアクリル板2および3で50%圧締する。その後注水し、漏水を観察する。
(4)透湿性の測定
アルミニウム製の試験治具を用い、幅1.2mmで100mm×70mmのサンプルを25%圧締する。これを60℃×80%湿度の槽に入れ、アルミニウム製の蓋にセットされた湿度センサーにて治具内の湿度を記録する。
【0012】
(5)接触角の測定
発泡体はアルミ箔にはさみ、約180〜200℃で熱プレスをして非発泡状にする。粘着剤はそのままサンプルとする。接触角は協和接触角計CA−Aを用い、水滴滴下後、2分後の値を読む。
【0013】
実施例1
1.再剥離性粘着剤の製造方法
疎水性ポリオールとして、ダイマー酸とヂエチレングリコールより得られる水酸基価80、相溶性試験値0.1gのポリエステルポリオール100部、トリレンジイソシアナート65/35(2、4/2、6異性体比:日本ポリウレタン(社)製)12.4部、触媒としてジブチルチンジラウレート0.1部を混合し、ダイスコーターを用い、シリコーンで表面処理した離型紙上に100g/m2になるよう塗工した。
2.疎水性発泡体とのラミネート
ポリウレタン発泡体として、接触角98°、密度0.053g/cm3の発泡シーリング材であるスーパーシールW(日本発条株製)の厚さ5mmのシートを、上記の塗工面にラミネートし、100℃のオーブン中で5分間処理した。同様に5mmシートの裏面にも上記の粘着剤をラミネートした。
これらの粘着剤の接触角は95°で、プローブタック値800g、90°ピール値0.2Kg/cmであり、再剥離性を示した。
ここで得られた発泡体ガスケットを、図6で示すアクリル板で50%圧縮時の防水性を試験すると、20cmの水圧で24時間漏水がなかった。一方、粘着剤がついていない場合の水圧は、約13cmであった。
【0014】
比較例1
使用する粘着剤の組成として、下記の表のものを用いた以外、実施例1と同様な方法で、5mmのスーパーシールWの両面に粘着剤がラミネートした製品を作製した。
【0015】
【表1】
【0016】
上記の粘着剤の接触角は70°、プローブタック値900g、90°ピール値0.2Kg/cmであり、再剥離性を示した。
防水性試験では、水圧5cmであっても2時間程度で漏水がみられた。
【0017】
実施例2、比較例2
疎水性発泡体として接触角95°、密度0.53g/cm3の高密度独立気泡ウレタンフォームであるニッパレイExの1mm品を用い、その片面に実施例1と同様の方法で粘着剤をつけた。比較例2として、比較例1で用いた粘着剤を上記のウレタンフォームの片面につけた。
これらのサンプルの透湿性を測定した結果、図7の通りであった。図7は湿度80%に早く到達するほど悪いことを示し、実施例2が優れていることを示す。
【0018】
実施例3、比較例3
疎水性ポリオールとして実施例1のポリオール100部、PML7012を10部、ヂブチルチンジラウレート0.2と、トリレンジイソシアナート(日本ポリウレタン(社)製)65/35(T65)の添加部数を変化して、実施例1と同様な方法で粘着剤を作製した。
疎水性発泡体として接触角98°、密度0.055g/cm3の自己スキン付きウレタンフォームであるスーパーシートH6の5mm品の片側に、上記の粘着剤をラミネートした。
これらのサンプルの防水性、粘着性能は次の表2の通りである。
【0019】
【表2】
【0020】
【発明の効果】
以上の述べたように、本願発明の再剥離性発泡体ガスケットは、
1)発泡体ガスケットの防水機能を満足し、更には被防水面の密着性が高まるため、その種類を問わず防水機能を発揮できる。
2)粘着力を活かし、シールを被防水面に貼着すると、その接着力のため界面からの漏水が防げ、たとえば高圧洗車時の水圧にも耐え得る。
3)防湿性を有する発泡体ガスケットも、その界面からの湿分のリークが防げる。
4)再剥離性の粘着剤である為、貼り間違えをしても、貼りなおしは容易であり、また使い終った後に被接着面より剥がす事も容易である。従って、部品のリサイクルする時に部品の分別が容易となる。
等の効果を奏する。
【図面の簡単な説明】
【図1】本発明における発泡体ガスケットの斜視図
【図2】本発明における発泡体ガスケットの断面図
【図3】本発明における発泡体ガスケットの製造方法の1例を示す説明図
【図4】本発明における発泡体ガスケットの製造方法における粘着剤を塗工する説明図
【図5】本発明における発泡体ガスケットの他の製造方法を示す説明図
【図6】本発明における発泡体ガスケットの防水試験の説明図で、aは試験試料の平面図、bは試験具の斜視図である。
【図7】実施例2及び比較例2の透湿度の測定結果の図
【符号の説明】
10:本発明の発泡体ガスケット 11:発泡体
12:再剥離性粘着剤 13:セパレーター
21:ドクターナイフ
1:試験試料 2、3:アクリル樹脂板 4:スペンサー
5:注水管[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a removable foam gasket. More specifically, the present invention relates to a removable foam gasket in which a urethane-based removable adhesive is applied to at least one surface of the foam gasket.
[0002]
[Prior art]
Conventionally, the releasable adhesive has been applied to office labels, medical adhesive tapes, dust removal rollers and the like. Here, the re-peelable pressure-sensitive adhesive means that the adhesive is not left on the adherend when the adhesive is attached to the adherend and then peeled off, and the adhesive remains on the adherend. The pressure-sensitive adhesive has a function of being able to be peeled off and again being able to stick this stuck article to an adherend.
Since the releasable pressure-sensitive adhesive has a high cohesive force, it peels without causing cohesive failure when the adhered product is peeled off from the adherend. However, since the pressure-sensitive adhesiveness is weak, it has been impossible to laminate the pressure-sensitive adhesive on the foam by the same transfer method as that of a normal double-sided tape.
In order to improve this, in Japanese Patent Application No. 10-99401 by the present inventors, a reactive polyurethane adhesive mainly composed of polyol and isocyanate is laminated to a foam in an uncured state. It has been proposed to obtain an attached foam. As a result, a removable foam with a pressure-sensitive adhesive was obtained.
However, the present inventors have not been able to exhibit waterproof performance when the above adhesive is used, even if the foam itself is a material having waterproof properties, etc., in applications where waterproof properties are required. Since the urethane pressure-sensitive adhesive adheres to the adherend, it has been clarified that the removability performance is lowered. This is unthinkable in the past, and if the foam itself has water-stopping properties, it can be considered that the water-stopping property is improved by adding a film-like pressure-sensitive adhesive to the surface, or will not decrease if not improved. It was common sense.
Similarly, when the urethane adhesive is applied to a foam gasket for the purpose of moisture prevention, it has been surprisingly found that the moisture resistance is inferior to that of the foam gasket alone.
[0003]
[Problems to be solved by the invention]
As a result of various studies to solve the above problems and to obtain a foam gasket with a releasable pressure-sensitive adhesive without reducing water-stopping and moisture-proof properties, the present inventor completed the present invention. An object of the present invention is to provide a foam gasket having excellent waterproof and moisture resistance and having removability.
[0004]
[Means for solving the problems]
The gist of the present invention is a removable foam gasket in which a removable adhesive is laminated on at least one surface of a foam sheet, the foam sheet being a hydrophobic foam having a contact angle of 90 degrees or more, The pressure-sensitive adhesive laminated on the foam sheet is a urethane-based pressure-sensitive adhesive containing hydrophobic polyol, isocyanate and catalyst as essential components, and the urethane-based pressure-sensitive adhesive is a contact angle between the foam, the laminate, and the pressure-sensitive adhesive after curing. Is a removable foam gasket characterized by having a 90 ° or more.
That is, the present invention specifies that a contact angle of a pressure-sensitive adhesive after curing is 90 degrees or more on at least one surface of a foam sheet having a specific characteristic of a foam sheet made of a hydrophobic foam having a contact angle of 90 degrees or more. The desired removable foam gasket can be obtained by laminating a removable pressure-sensitive adhesive having the above characteristics. In addition, the measurement of the contact angle of a foam and an adhesive is mentioned later.
[0005]
DETAILED DESCRIPTION OF THE INVENTION
The present invention will be described in detail.
The foam gasket of the present invention is a sealing material for the purpose of waterproofing, dustproofing, airtightness, and moistureproofing comprising a low-breathing open-cell foam or closed-cell foam sheet. The foam sheet used for this foam gasket is a thin sheet sliced from a foam block and a thin sheet foamed, such as EPDM rubber, ethylene-propylene rubber, polyethylene, polypropylene. And flexible foams such as rubber-like or olefinic foams such as ethylene-vinyl acetate, urethane foams, and polyvinyl chloride foams.
These foams are hydrophobic foams of 90 degrees or more in order to satisfy waterproofness regardless of closed cells / open cells. The contact angle must be 90 degrees or more. In the case of open cells, the air permeability is preferably 10 cc / cm 3 / sec or less and low air permeability. These foams have a function of stopping water by being compressed in a gap to be waterproofed or by being applied without being compressed.
[0006]
The pressure-sensitive adhesive laminated on at least one surface of the foam sheet is a urethane-based releasable pressure-sensitive adhesive having a hydrophobic polyol, an isocyanate and a catalyst as essential components. That is, the re-peelable pressure-sensitive adhesive of the present invention is obtained by curing a hydrophobic polyol and an isocyanate using a catalyst, and the contact angle needs to be 90 degrees or more. When the contact angle is 90 degrees or less, even if the foam has water-stopping property, the water-stopping property of the foam sheet laminated with the pressure-sensitive adhesive is greatly reduced. Furthermore, the water absorption rate of this pressure-sensitive adhesive is preferably 1.0% or less. Thus, when the water absorption rate is low, the water stoppage can be maintained for a long time.
As described above, the function of removability is that when the gasket with the adhesive is peeled off from the adherend surface, the adhesive does not remain on the adherend surface and the gasket material can be peeled off without tearing. . Accordingly, when the performance is expressed numerically, it varies depending on the type of gasket material, but it is preferably 0.5 kg / cm or less at 90 ° peel and 600 g or more in probe tack value.
Hydrophobic polyols are those that pass a compatibility test described later, and are polyols having a high molecular skeleton and a high hydrocarbon content. They are preferably at least one polyol compound selected from the group consisting of dimer acid esters, castor oil, castor oil esters, and hydrocarbon polyols. As dimer acid-based polyols, dimer acid and esterified products of polyfunctional hydroxides such as ethylene glycol, diethylene glycol, trimethylolpropane and glycerin, and their fatty acid, fatty alcohol modified products, castor oil and castor oil modified Products, polybutadiene-based polyols and hydrogenated products thereof, polyisoprene-based polyols and hydrogenated products thereof, dimerdiols obtained by hydrogen reduction of dimer acid, and ester compounds using the same. In addition, higher fatty acids such as sebacic acid, ricinolenic acid and hydroxystearic acid, and ester polyols using higher fatty alcohols are also included.
A part or all of the polyol may be used as a prepolymer that has been reacted in advance with an isocyanate described below. When all of the polyol is a prepolymer, it is preferable to use a chain extender such as ethylene glycol or 1,4-butanediol in order to advance the curing reaction.
[0007]
As the isocyanate, tolylene diisocyanate (TDI), diphenylmethane diisocyanate (MDI), crude MDI, hexamethylene diisocyanate (HDI), isophorone diisocyanate or the like is used alone or in combination. I can do it. These compounds can be used as prepolymers as they are or after reacting with polyols.
As the catalyst, amine-based catalysts such as triethylenediamine, which are usually used for urethane production, and tin-based organometallic catalysts such as dibutyltin dilaurate and stannous octoate are used.
The method for improving the contact angle of the pressure-sensitive adhesive is a good method using a hydrophobic polyol, but not only that, but also the isocyanate used is better than MDI than TDI and more than the smaller number of isocyanate parts. Moreover, addition of a catalyst is essential, and if the addition amount is small, the contact angle is difficult to improve. Thus, the contact angle of the pressure-sensitive adhesive can be changed by various factors, and they are adjusted in consideration of physical properties such as pressure-sensitive adhesive performance. As these composition ratios, the isocyanate component is in a ratio of 2 to 20 parts by weight with respect to the polyol component, and the amount of the catalyst used is about 0.05 to 0.5 part.
In order to improve the weather resistance, it is desirable to add an ultraviolet absorber or blend carbon black into the urethane adhesive. In particular, carbon black is preferable because of its great effect and durability. In addition, tackifiers such as petroleum resins, process oils and the like can be added to improve the adhesive strength.
A perspective view and a sectional view of the removable foam gasket of the present invention are shown in FIGS. In the figure, a
[0008]
Next, a method for producing a removable foam gasket according to the present invention will be described. First, as a method for producing the pressure-sensitive adhesive layer used in the present invention, the above-mentioned raw materials are stirred and coated on a peelable separator. As the separator, a paper or plastic film is used as a base material, and the surface thereof is treated with a releasable material such as silicone. For coating, a knife coater, roll coater, die coater, spray coater or the like is used.
After applying urethane adhesive to the separator, the foam may be laminated immediately. However, after the application, the reaction is promoted by heating and the thickening due to finger touch is confirmed, or the stringing phenomenon is confirmed. Thereafter, when the foam is laminated, the contact angle of the pressure-sensitive adhesive tends to be stable at 90 ° or more, and the waterproof property is stable and preferable.
[0009]
1 illustrates a method for producing a removable foam gasket of the present invention. FIG. 3 is an explanatory diagram of the manufacturing method, FIG. 4 is an explanatory diagram for applying an adhesive in the manufacturing method, and FIG. 5 is a conceptual diagram of another manufacturing method. 3 and 4, the releasable pressure-sensitive adhesive 12 a is placed on the traveling
The size of the removable foam gasket in the present invention varies depending on the article to be waterproofed and moisture-proof, but is usually about 0.5 to 20 mm in thickness.
[0010]
【Example】
Next, the present invention will be described more specifically with reference to examples. Each measuring method in the examples was performed by the following methods.
(1) Compatibility test method Weigh 2.0 g of sample in a test tube (
(2) Measuring method of adhesive strength 90 degree peeling force is measured according to JIS-1528. The probe tack force was determined by placing a chrome-plated mirror-finished surface probe (10Φ × 14mm, 10g) on the adhesive surface of the sample for 20 seconds, and then pulling it vertically at a speed of 300 mm / min with a tensile tester. Read the load.
[0011]
(3) Method for measuring waterproofness An acrylic test jig shown in FIG. 6 is used. In FIG. 6, a sample 1 having a width of 10 mm and a square of 50 mm is pressed with
(4) Measurement of moisture permeability Using a test jig made of aluminum, a 100 mm x 70 mm sample with a width of 1.2 mm is clamped by 25%. This is put in a bath of 60 ° C. × 80% humidity, and the humidity in the jig is recorded by a humidity sensor set on an aluminum lid.
[0012]
(5) Measurement of contact angle The foam is sandwiched between aluminum foils and is hot-pressed at about 180 to 200 ° C. to make it non-foamed. The adhesive is used as a sample. For the contact angle, use a Kyowa contact angle meter CA-A and read the value after 2 minutes after dropping the water droplets.
[0013]
Example 1
1. Method for producing releasable adhesive As the hydrophobic polyol, 100 parts of a polyester polyol having a hydroxyl value of 80 obtained from dimer acid and diethylene glycol and a compatibility test value of 0.1 g, tolylene diisocyanate 65/35 (2, 4 / 2, 6 isomer ratio: manufactured by Nippon Polyurethane Co., Ltd. (12.4 parts), dibutyltin dilaurate (0.1 part) as a catalyst, and 100 g / m on release paper surface-treated with silicone using a die coater. Coated to be 2 .
2. As a laminated polyurethane foam with a hydrophobic foam, a 5 mm thick sheet of Super Seal W (manufactured by Nihon Hojo Co., Ltd.), which is a foam sealant having a contact angle of 98 ° and a density of 0.053 g / cm 3 , is applied. The laminate was laminated on the work surface and treated in an oven at 100 ° C. for 5 minutes. Similarly, the adhesive was laminated on the back surface of a 5 mm sheet.
These adhesives had a contact angle of 95 °, a probe tack value of 800 g, a 90 ° peel value of 0.2 kg / cm, and exhibited removability.
When the foam gasket obtained here was tested for waterproofness when compressed by 50% with the acrylic plate shown in FIG. 6, there was no water leakage at a water pressure of 20 cm for 24 hours. On the other hand, the water pressure when the adhesive was not attached was about 13 cm.
[0014]
Comparative Example 1
As a composition of the pressure-sensitive adhesive to be used, a product in which a pressure-sensitive adhesive was laminated on both surfaces of a 5 mm super seal W was produced in the same manner as in Example 1 except that the one in the table below was used.
[0015]
[Table 1]
[0016]
The pressure-sensitive adhesive had a contact angle of 70 °, a probe tack value of 900 g, a 90 ° peel value of 0.2 kg / cm, and exhibited removability.
In the waterproof test, water leakage was observed in about 2 hours even at a water pressure of 5 cm.
[0017]
Example 2 and Comparative Example 2
A 1 mm product of Nipperlay Ex, which is a high-density closed cell urethane foam having a contact angle of 95 ° and a density of 0.53 g / cm 3 , was used as the hydrophobic foam, and an adhesive was applied to one side thereof in the same manner as in Example 1. . As Comparative Example 2, the adhesive used in Comparative Example 1 was applied to one side of the urethane foam.
As a result of measuring the moisture permeability of these samples, it was as shown in FIG. FIG. 7 shows that the earlier the humidity reaches 80%, the worse it is, and that Example 2 is superior.
[0018]
Example 3 and Comparative Example 3
As the hydrophobic polyol, 100 parts of the polyol of Example 1, 10 parts of PML7012, 0.2 part of dibutyltin dilaurate and 65/35 (T65) of tolylene diisocyanate (manufactured by Nippon Polyurethane Co., Ltd.) Thus, a pressure-sensitive adhesive was produced in the same manner as in Example 1.
The above-mentioned pressure-sensitive adhesive was laminated on one side of a 5 mm product of super sheet H6, which is a urethane foam with a self-skin having a contact angle of 98 ° and a density of 0.055 g / cm 3 as a hydrophobic foam.
The waterproofness and adhesion performance of these samples are as shown in Table 2 below.
[0019]
[Table 2]
[0020]
【The invention's effect】
As described above, the removable foam gasket of the present invention is
1) The waterproof function of the foam gasket is satisfied, and furthermore, the adhesion of the waterproof surface is enhanced, so that the waterproof function can be exhibited regardless of the type.
2) Utilizing adhesive strength and sticking a seal to a waterproof surface, the adhesive force prevents water leakage from the interface, and can withstand water pressure during high-pressure car washing, for example.
3) The moisture-proof foam gasket can also prevent moisture leakage from the interface.
4) Since it is a re-peelable pressure-sensitive adhesive, it can be easily re-applied even if it is misapplied, and it can also be easily peeled off from the adherend surface after use. Accordingly, the parts can be easily separated when the parts are recycled.
There are effects such as.
[Brief description of the drawings]
FIG. 1 is a perspective view of a foam gasket according to the present invention. FIG. 2 is a cross-sectional view of the foam gasket according to the present invention. FIG. 3 is an explanatory view showing an example of a method for producing a foam gasket according to the present invention. FIG. 5 is an explanatory view showing another method for manufacturing a foam gasket according to the present invention. FIG. 6 is a waterproof test for the foam gasket according to the present invention. FIG. 4A is a plan view of a test sample, and b is a perspective view of a test device.
FIG. 7 is a diagram of measurement results of moisture permeability of Example 2 and Comparative Example 2.
10: Foam gasket of the present invention 11: Foam 12: Removable adhesive 13: Separator 21: Doctor knife 1:
Claims (2)