JP4070680B2 - Method for producing ultrafine silica dispersion slurry for resin filling - Google Patents
Method for producing ultrafine silica dispersion slurry for resin filling Download PDFInfo
- Publication number
- JP4070680B2 JP4070680B2 JP2003284694A JP2003284694A JP4070680B2 JP 4070680 B2 JP4070680 B2 JP 4070680B2 JP 2003284694 A JP2003284694 A JP 2003284694A JP 2003284694 A JP2003284694 A JP 2003284694A JP 4070680 B2 JP4070680 B2 JP 4070680B2
- Authority
- JP
- Japan
- Prior art keywords
- coupling agent
- silane coupling
- ultrafine silica
- silica
- ultrafine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、樹脂組成物、特にエポキシ樹脂組成物を製造するのに有用な超微粉シリカ分散スラリーの製造方法に関する。 The present invention relates to a method for producing an ultrafine silica-dispersed slurry useful for producing a resin composition, particularly an epoxy resin composition.
超微粉シリカは、嵩密度が大きく、静電気による飛散などして取り扱いにくいので、これをエポキシ樹脂等樹脂のフィラーとして用いる場合にはスラリー化することの提案があるが（特許文献１）、長期間の静置によってシリカが沈降し、またそれを再分散させがたい問題点がある。
本発明の目的は、上記に鑑み、沈降安定性、再分散性に優れた超微粉シリカ分散スラリーの製造方法を提供することである。本発明の目的は、孤立シラノール基を有するシリカ表面を、末端がフェニル基であるシランカップリング剤による特定処理によって達成することができる。 In view of the above, an object of the present invention is to provide a method for producing an ultrafine silica dispersion slurry having excellent sedimentation stability and redispersibility. The object of the present invention can be achieved by a specific treatment with a silane coupling agent having a terminal phenyl group on a silica surface having an isolated silanol group.
すなわち、本発明は、孤立シラノール基を有する超微粉シリカに、末端がフェニル基であるシランカップリング剤を、その最小被覆面積から算出した被覆率が１０〜５０％となる量を添加してから、孤立シラノール基に化学結合させたシランカップリング剤と化学結合をしていないシランカップリング剤とが混在する状態に処理した後、それを溶媒に分散させてなること特徴とする樹脂充填用超微粉シリカ分散スラリーの製造方法である。この場合において、添加されたシランカップリング剤の７０〜９５質量％を超微粉シリカの孤立シラノール基に化学結合させることが好ましい。また、超微粉シリカの孤立シラノール基の数が１〜１０個／ｎｍ２であり、溶媒がメチルエチルケトン又はメチルイソブチルケトンであり、シランカップリング剤で処理された超微粉シリカのスラリー中の含有率が５０〜９０質量％であることが好ましい。 That is, in the present invention, after adding an amount of a silane coupling agent having a terminal phenyl group to the ultrafine silica having an isolated silanol group, the covering ratio calculated from the minimum covering area is 10 to 50%. The resin-filled super-characteristic is characterized in that a silane coupling agent chemically bonded to an isolated silanol group and a silane coupling agent not chemically bonded are mixed and then dispersed in a solvent. It is a manufacturing method of a fine silica dispersion slurry. In this case, it is preferable that 70 to 95% by mass of the added silane coupling agent is chemically bonded to the isolated silanol group of the ultrafine silica. The number of isolated silanol groups of ultrafine silica is 1 to 10 / nm 2, the solvent is methyl ethyl ketone or methyl isobutyl ketone, the content of the slurry of ultrafine silica treated with a silane coupling agent It is preferable that it is 50-90 mass%.
本発明によれば、超微粉シリカ分散スラリーのシリカが沈降しがたくなるという効果を発現する。 According to the present invention, the effect that the silica of the ultrafine silica dispersion slurry is difficult to settle is exhibited.
本発明で用いられる超微粉シリカは、シリカ粉末と、金属シリコン粉末及び／又は炭素粉末からなる還元剤と、水とを含む混合原料を、還元雰囲気下の高温で熱処理をしてＳｉＯ含有ガスを生成させ、それを速やかに酸素を含む雰囲気中で冷却し、微粒子を捕集する方法（特開２０００−２４７６２６号公報）、酸素を含む雰囲気内に形成された化学炎に、金属シリコン粉末を粉塵雲が形成される程度の量投入し、爆燃を起こさせて超微粒子を製造する方法（特公平１−５５２０１号公報）などによって製造することができる。このような超微粉シリカは、大気中で製造されるため、その表面に孤立シラノール基がある。平均粒径は２．０μm以下、特に１．０〜０．１μmであることが好ましい。また、比表面積は３〜２０ｍ２／ｇであることが好ましい。 The ultrafine silica used in the present invention is a mixed raw material containing silica powder, a reducing agent composed of metal silicon powder and / or carbon powder, and water, and heat-treated at a high temperature in a reducing atmosphere to produce SiO-containing gas A method of generating and quickly cooling it in an atmosphere containing oxygen to collect fine particles (Japanese Patent Laid-Open No. 2000-247626), and dusting metal silicon powder into a chemical flame formed in an atmosphere containing oxygen It can be manufactured by a method of introducing ultrafine particles by introducing an amount sufficient to form a cloud and causing deflagration (Japanese Patent Publication No. 1-55201). Since such ultrafine silica is produced in the atmosphere, there are isolated silanol groups on its surface. The average particle diameter is preferably 2.0 μm or less, particularly 1.0 to 0.1 μm. Moreover, it is preferable that a specific surface area is 3-20 m < 2 > / g.
シラノール基の中でも孤立シラノール基は反応性が高く、シランカップリング剤をシリカ表面に化学結合させる。孤立シラノール基は、赤外吸収スペクトル分析装置、例えばＰｅｒｋｉｎ Ｅｌｍｅｒ社製商品名「Ｓｐｅｃｔｒｕｍ Ｏｎｅ」を用い、孤立シラノール基に帰属される波数３７４０［ｃｍ−１］の吸収スペクトルの存否によってその存在の有無を確認することができる。孤立シラノール基の定量は、カールフィッシャー水分計による水分測定によって行われる。すなわち、試料を管状炉で９００℃まで段階的に加熱し、２００℃で除去された水分を吸着水、５５０℃で除去された水分を水素結合シラノール基、９００℃で除去された水分を孤立シラノール基によるものとみなして、単位表面積当たりの孤立シラノール基量を求めることができる。孤立シラノール基量は、超微粉シリカを加湿処理または９００℃以上で加熱することで減少させることができ、また、ＴＥＯＳ（テトラエトキシシラン）で処理することによって増加させることができるので、これらの操作と条件を適宜組み合わせることによって孤立シラノール基量を調整することができる。 Among silanol groups, isolated silanol groups are highly reactive and chemically bond the silane coupling agent to the silica surface. The presence or absence of an isolated silanol group is determined by the presence or absence of an absorption spectrum having a wavenumber of 3740 [cm −1 ] attributed to the isolated silanol group, using an infrared absorption spectrum analyzer such as “Spectrum One” manufactured by Perkin Elmer. Can be confirmed. The quantification of the isolated silanol group is performed by moisture measurement using a Karl Fischer moisture meter. That is, the sample is heated stepwise to 900 ° C. in a tubular furnace, the water removed at 200 ° C. is adsorbed water, the water removed at 550 ° C. is hydrogen-bonded silanol groups, and the water removed at 900 ° C. is isolated silanol. The amount of isolated silanol groups per unit surface area can be determined by assuming that it is based on groups. The amount of isolated silanol groups can be reduced by humidifying ultrafine silica or heating at 900 ° C. or higher, and can be increased by treating with TEOS (tetraethoxysilane). The amount of isolated silanol groups can be adjusted by appropriately combining the above and conditions.
本発明においては、超微粉シリカの孤立シラノール基量は、１〜１０個／ｎｍ２であることが好ましい。孤立シラノール基が１個／ｎｍ２未満であると、シランカップリング剤の処理効果が不十分となり、１０個／ｎｍ２をこえると、粒子の凝集が起こりやすくなる。 In the present invention, the amount of isolated silanol groups in the ultrafine silica is preferably 1 to 10 / nm 2 . When the number of isolated silanol groups is less than 1 / nm 2 , the treatment effect of the silane coupling agent is insufficient, and when the number of isolated silanol groups exceeds 10 / nm 2 , particle aggregation tends to occur.
本発明で用いられる末端にフェニル基を有するシランカップリング剤としては、γ−フェニルアミノプロピルトリメトキシシラン、フェニルトリエトキシシランなどがあげられるが、好ましくはγ−フェニルアミノプロピルトリメトキシシランである。これらの一種以上を用いることによって、優れた沈降安定性、再分散性を実現できる。シランカップリング剤の添加量は、超微粉シリカの比表面積にもとづいて変量される。すなわち、本発明においては、超微粉シリカ表面の１０〜５０％が被覆される量のシランカップリング剤を添加する。被覆率が１０％未満では処理効果は不十分であり、５０％を超えるとシリカ粒子が凝集し単分散が困難となる。シランカップリング剤の添加量ｄ（ｇ）は、シリカの比表面積ａ（ｍ２／ｇ）と、超微粉シリカの質量ｂ（ｇ）と、シランカップリング剤の最小被覆面積すなわちシランカップリング剤１ｇで被覆できる面積ｃ（ｍ２／ｇ）とから、式、１０％＜（ｃ×ｄ）×１００／（ａ×ｂ）＜５０％、によって算出される。 Examples of the silane coupling agent having a phenyl group at the terminal used in the present invention include γ-phenylaminopropyltrimethoxysilane and phenyltriethoxysilane, and γ-phenylaminopropyltrimethoxysilane is preferred. By using one or more of these, excellent sedimentation stability and redispersibility can be realized. The amount of the silane coupling agent added is varied based on the specific surface area of the ultrafine silica. That is, in the present invention, an amount of silane coupling agent that covers 10 to 50% of the ultrafine silica surface is added. When the coverage is less than 10%, the treatment effect is insufficient, and when it exceeds 50%, the silica particles aggregate and monodispersion becomes difficult. The addition amount d (g) of the silane coupling agent includes the specific surface area a (m 2 / g) of silica, the mass b (g) of ultrafine silica, and the minimum coating area of the silane coupling agent, that is, the silane coupling agent. From the area c (m 2 / g) that can be covered with 1 g, it is calculated by the formula: 10% <(c × d) × 100 / (a × b) <50%.
超微粉シリカの被覆は、振動流動槽を用い、超微粉シリカを振動流動化させた状態でシランカップリング剤の液滴をミストスプレーで直接噴霧して混合する方法、シランカップリング剤の液滴をミストスプレーで超微粉シリカに直接噴霧した後、ボールミル、ヘンシェルミキサーなどを用いて混合してから放置する方法によって行うことができる。シランカップリング剤をあらかじめ水などで加水分解させてから噴霧する従来法は、本発明では好ましくない。 The coating of ultrafine silica is performed by using a vibrating fluid tank and mixing the droplets of the silane coupling agent by directly spraying the silane coupling agent with mist spray in a state where the ultrafine silica is vibrated and fluidized. Can be carried out by spraying directly onto ultrafine silica by mist spraying, then mixing using a ball mill, a Henschel mixer or the like and then leaving it to stand. The conventional method in which the silane coupling agent is previously hydrolyzed with water and then sprayed is not preferable in the present invention.
本発明で重要なことは、上記被覆率を満たす範囲内で添加されたシランカップリング剤が、超微粉シリカの孤立シラノール基と化学結合したものと、化学結合をしていないものとが混在するように処理してから溶媒と混合することである。このような処理は、２０〜５０℃好ましくは２５〜３０℃の相対湿度５０％以上の空気雰囲気下において、シランカップリング剤を超微粉シリカに添加（噴霧）混合して超微粉シリカをシランカップリング剤で被覆した後、２０〜５０℃好ましくは２５〜３０℃の相対湿度５０％以上の空気雰囲気下、１０〜１００時間保持することによって行うことができる。この操作は、従来法が、添加されたシランカップリング剤の全てを孤立シラノール基と化学結合させるべく、より高温かつより長時間で保持されていたことと比較して特異的である。 What is important in the present invention is that the silane coupling agent added within the range satisfying the above-mentioned coverage ratio includes a combination of chemically bonded with the isolated silanol group of ultrafine silica and a non-chemically bonded one. And then mixing with a solvent. Such treatment is carried out by adding (spraying) a silane coupling agent to ultrafine silica in an air atmosphere of 20 to 50 ° C., preferably 25 to 30 ° C. and a relative humidity of 50% or more. After covering with a ring agent, it can be carried out by holding for 10 to 100 hours in an air atmosphere of 20 to 50 ° C., preferably 25 to 30 ° C. and a relative humidity of 50% or more. This operation is specific compared to the conventional method being held at a higher temperature and for a longer time to chemically bond all of the added silane coupling agent to the isolated silanol groups.
シランカップリング剤が孤立シラノール基と化学結合したことは、波数３７４０［ｃｍ−１］の吸収スペクトルの減少又は消失によって確認することができる。定量的には、シランカップリング剤で処理された超微粉シリカをエタノールで超音波洗浄し、ろ過、乾燥後の全炭素量と、エタノール未洗浄の全炭素量とを測定し、式、（添加されたシランカップリング剤が孤立シラノール基と化学結合した比率）＝（エタノール洗浄後全炭素）／（未洗浄全炭素）、によって求めることができる。本発明においては、化学結合したシランカップリング剤の比率が０．７〜０．９５特に０．８〜０．９であることが好ましい。なお、全炭素量は、炭素／硫黄同時分析計（例えばＬＥＣＯ社製商品名「ＣＳ−４４４ＬＳ型」）で炭素量を測定し、検量線法にて定量することができる。 The chemical bonding of the silane coupling agent with the isolated silanol group can be confirmed by a decrease or disappearance of the absorption spectrum at a wave number of 3740 [cm −1 ]. Quantitatively, ultrafine silica treated with a silane coupling agent was ultrasonically cleaned with ethanol, and the total amount of carbon after filtration and drying and the total amount of carbon that had not been washed with ethanol were measured using the formula (addition The ratio of chemically bonded silane coupling agents to isolated silanol groups) = (total carbon after ethanol cleaning) / (total carbon not cleaned). In the present invention, the ratio of the chemically bonded silane coupling agent is preferably 0.7 to 0.95, particularly preferably 0.8 to 0.9. The total carbon amount can be quantified by a calibration curve method by measuring the carbon amount with a carbon / sulfur simultaneous analyzer (for example, trade name “CS-444LS type” manufactured by LECO).
ついで、シランカップリング剤で処理された超微粉シリカは、溶媒と混合さて本発明のシリカ分散スラリーとなる。溶媒としては、メチルアルコール、エチルアルコール、イソプロピルアルコール、アセトン、メチルエチルケトン、メチルイソブチルケトン、酢酸メチル、酢酸エチル等の極性溶媒が用いられるが、メチルエチルケトン、メチルイソブチルケトンが好適である。溶媒量は、目的とするスラリー濃度に応じて適宜変量されるが、良好な沈降安定性を保つ点から、超微粉シリカ濃度が５０〜９０質量％となる量が望ましい。超微粉シリカ濃度が５０質量％未満では、長期間静置によって上澄み層が厚くなりスラリーが不均一となり、９０質量％をこえると、もはやスラリー状態とは言えなくなる。 Next, the ultrafine silica treated with the silane coupling agent is mixed with a solvent to form the silica-dispersed slurry of the present invention. As the solvent, polar solvents such as methyl alcohol, ethyl alcohol, isopropyl alcohol, acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl acetate, and ethyl acetate are used, and methyl ethyl ketone and methyl isobutyl ketone are preferable. The amount of the solvent is appropriately changed according to the intended slurry concentration, but is preferably an amount that makes the ultrafine silica concentration 50 to 90% by mass from the viewpoint of maintaining good sedimentation stability. If the ultrafine silica concentration is less than 50% by mass, the supernatant layer becomes thick due to standing for a long period of time and the slurry becomes non-uniform, and if it exceeds 90% by mass, it can no longer be said to be in a slurry state.
シランカップリング剤で処理された超微粉シリカと溶媒との混合には、通常のボールミル等で十分であるが、高圧ホモジナイザーと呼ばれている市販混合機、例えば吉田機械興業社製商品名「ナノマイザー」、スギノマシン社製商品名「アルティマイザー」などを用いることは好ましい。これらの装置の基本構成は、スラリーを加圧する高圧発生部と絞り機構からなる。これらの装置はいずれも流通式であり、超音波ホモジナイザーなどのバッチ式とは異なる。また、メディア媒体型分散装置を使用する場合に比べて、不純物の混入が少ないこと、大量処理に適用可能であることなどの工業的利点がある。 A normal ball mill or the like is sufficient for mixing the ultrafine silica treated with the silane coupling agent and the solvent, but a commercial mixer called a high-pressure homogenizer, for example, “Nanomizer, trade name manufactured by Yoshida Kikai Kogyo Co., Ltd.” It is preferable to use a trade name “Ultimizer” manufactured by Sugino Machine. The basic configuration of these apparatuses is composed of a high-pressure generator that pressurizes the slurry and a throttling mechanism. These devices are all flow-through types, and are different from batch types such as an ultrasonic homogenizer. In addition, there are industrial advantages such as less contamination of impurities and applicability to mass processing compared to the case of using a media medium type dispersion apparatus.
超微粉シリカとして、電気化学工業社製商品名「ＳＦＰ−３０Ｍ」（平均粒径０．６μm、比表面積５．８ｍ２／ｇ）を用いた。この超微粉シリカは、波数３７４０［ｃｍ−１］に吸収スペクトルがあり、孤立シラノール基が存在することが確認された。５５０℃超９００℃までの加熱によって発生した水分量から求めた孤立シラノール基量は４．５個／ｎｍ２であった。 As ultrafine silica, trade name “SFP-30M” (average particle size 0.6 μm, specific surface area 5.8 m 2 / g) manufactured by Denki Kagaku Kogyo Co., Ltd. was used. This ultrafine silica had an absorption spectrum at a wave number of 3740 [cm −1 ], and it was confirmed that an isolated silanol group was present. The amount of isolated silanol groups determined from the amount of water generated by heating above 550 ° C. to 900 ° C. was 4.5 / nm 2 .
超微粉シリカ１００ｇ当たり、γ−フェニルアミノプロピルシランカップリング剤（信越化学社製商品名「ＫＢＭ−５７３」、最小被覆面積：３０７ｍ２／ｇ）０．６ｇをミストスプレーで直接噴霧した後、２７℃下、ボールミルで１時間混合した。シランカップリング剤の被覆面積は１８４ｍ２（３０７ｍ２／ｇ×０．６ｇ）であり、またシリカの表面積は５８０ｍ２となったことから、シリカ表面の３２％がシランカップリング剤で被覆されていることになる（シランカップリング剤による被覆率３２％）。 After directly spraying 0.6 g of γ-phenylaminopropylsilane coupling agent (trade name “KBM-573” manufactured by Shin-Etsu Chemical Co., Ltd., minimum covering area: 307 m 2 / g) per 100 g of ultrafine silica, 27 The mixture was mixed with a ball mill at 1 ° C. for 1 hour. The coating area of the silane coupling agent was 184 m 2 (307 m 2 /g×0.6 g), and the surface area of the silica was 580 m 2 , so 32% of the silica surface was coated with the silane coupling agent. (The coverage with the silane coupling agent is 32%).
ついで、これを２７℃の相対湿度７５％の空気雰囲気下、２４時間放置してから、エタノール洗浄前後の全炭素量を測定して孤立シラノール基と化学結合しているシランカップリング剤の比率を上記に従って算出する一方、この超微粉シリカ６０質量部とメチルイソブチルケトン４０質量部とを、ボールミルで２時間混合してスラリーを製造した。得られたスラリーを円筒状ガラス容器に移し、１５日間静置後の上澄み液層の厚みと液層全体に対する厚みを測定し、（上澄み液層の厚み）／（液層全体の厚み）、により沈降安定性を評価した。それらの結果を表１に示す。 Next, this was left in an air atmosphere at 27 ° C. and 75% relative humidity for 24 hours, and then the total amount of carbon before and after ethanol washing was measured to determine the ratio of the silane coupling agent chemically bonded to the isolated silanol group. While calculating according to the above, 60 parts by mass of this ultrafine silica and 40 parts by mass of methyl isobutyl ketone were mixed with a ball mill for 2 hours to produce a slurry. The obtained slurry was transferred to a cylindrical glass container, and the thickness of the supernatant liquid layer after standing for 15 days and the thickness of the whole liquid layer were measured, and (thickness of supernatant liquid layer) / (total thickness of liquid layer) Sedimentation stability was evaluated. The results are shown in Table 1.
γ−フェニルアミノプロピルシランカップリング剤の添加量０．３ｇ（シランカップリング剤による被覆率１６％）としたこと以外は実施例１と同様にしてスラリーを製造した。 A slurry was produced in the same manner as in Example 1 except that the addition amount of γ-phenylaminopropylsilane coupling agent was 0.3 g (the coverage with the silane coupling agent was 16%).
γ−フェニルアミノプロピルシランカップリング剤の添加量０．８ｇ（シランカップリング剤による被覆率４３％）としたこと以外は実施例１と同様にしてスラリーを製造した。 A slurry was produced in the same manner as in Example 1 except that the addition amount of γ-phenylaminopropylsilane coupling agent was 0.8 g (covering ratio with silane coupling agent was 43%).
溶媒をメチルエチルケトンとしたこと以外は実施例１と同様にしてスラリーを製造した。 A slurry was produced in the same manner as in Example 1 except that methyl ethyl ketone was used as the solvent.
シランカップリング剤をフェニルシランカップリング剤（日本ユニカー社製商品名「Ａ−１５３」、最小被覆面積：３２６ｍ２／ｇ）に変え、添加量を０．５ｇ（シランカップリング剤による被覆率２８％）としたこと以外は実施例１と同様にしてスラリーを製造した。 The silane coupling agent is changed to a phenyl silane coupling agent (trade name “A-153” manufactured by Nihon Unicar Co., Ltd., minimum covering area: 326 m 2 / g), and the addition amount is 0.5 g (coverage rate by silane coupling agent 28 %), And a slurry was produced in the same manner as in Example 1.
超微粉シリカとして、平均粒径０．５μm、比表面積７．２ｍ２／ｇ、孤立シラノール基量は５．５個／ｎｍ２（電気化学工業社製）を用い、γ−フェニルアミノプロピルシランカップリング剤の添加量０．６ｇ（シランカップリング剤による被覆率２６％）としたこと以外は実施例１と同様にしてスラリーを製造した。 As an ultrafine silica, an average particle size of 0.5 μm, a specific surface area of 7.2 m 2 / g, and an isolated silanol group amount of 5.5 / nm 2 (manufactured by Denki Kagaku Kogyo Co., Ltd.) were used, and a γ-phenylaminopropylsilane cup A slurry was produced in the same manner as in Example 1 except that the addition amount of the ring agent was 0.6 g (the coverage with the silane coupling agent was 26%).
比較例１
γ−フェニルアミノプロピルシランカップリング剤の添加量を０．１ｇ（シランカップリング剤による被覆率５％）としたこと以外は実施例１と同様にしてスラリーを製造した。
Comparative Example 1
A slurry was produced in the same manner as in Example 1 except that the amount of γ-phenylaminopropylsilane coupling agent added was 0.1 g (the coverage with the silane coupling agent was 5%).
比較例２
γ−フェニルアミノプロピルシランカップリング剤の添加量を１．２ｇ（シランカップリング剤による被覆率６５％）としたこと以外は実施例１と同様にしてスラリーを製造した。
Comparative Example 2
A slurry was produced in the same manner as in Example 1 except that the amount of the γ-phenylaminopropylsilane coupling agent added was 1.2 g (the coverage with the silane coupling agent was 65%).
比較例３
シランカップリング剤を末端にフェニル基を持たないアミノプロピルシランカップリング剤（日本ユニカー社製商品名「Ａ−１１００」、最小被覆面積：３５３ｍ２／ｇ）に変え、添加量を０．７ｇ（シランカップリング剤による被覆率４３％）としたこと以外は実施例１と同様にしてスラリーを製造した。
Comparative Example 3
The silane coupling agent is changed to an aminopropylsilane coupling agent having no phenyl group at the end (trade name “A-1100”, manufactured by Nihon Unicar Co., Ltd., minimum covering area: 353 m 2 / g), and the addition amount is 0.7 g ( A slurry was produced in the same manner as in Example 1 except that the coverage with the silane coupling agent was 43%.
比較例４
シランカップリング剤を末端にフェニル基を持たないγ−グリシドキシプロピルシランカップリング剤（日本ユニカー社製商品名「Ａ−１８７」、最小被覆面積：３３０ｍ２／ｇ）に変え、添加量を０．５ｇ（シランカップリング剤による被覆率２３％）としたこと以外は実施例１と同様にしてスラリーを製造した。
Comparative Example 4
Change the silane coupling agent to a γ-glycidoxypropyl silane coupling agent having no phenyl group at the end (trade name “A-187” manufactured by Nihon Unicar Co., Ltd., minimum coating area: 330 m 2 / g) A slurry was produced in the same manner as in Example 1 except that the amount was 0.5 g (the coverage with the silane coupling agent was 23%).
比較例５
シランカップリング剤で処理していないこと以外は実施例１と同様にしてスラリーを製造した。
Comparative Example 5
A slurry was produced in the same manner as in Example 1 except that it was not treated with a silane coupling agent.
沈降安定性評価後の各スラリーを振盪機によって振盪して再分散性の難易を評価した。その結果、実施例１〜６では沈降物は速やかに分散したが、比較例１、５では沈降物は容器の底面に固着した状態であった。 Each slurry after the sedimentation stability evaluation was shaken with a shaker to evaluate the difficulty of redispersibility. As a result, in Examples 1 to 6, the sediment was quickly dispersed, but in Comparative Examples 1 and 5, the sediment was fixed to the bottom surface of the container.
本発明によって製造された超微粉シリカ分散スラリーは、沈降安定性、再分散性に優れたものとなる。これをビスフェノールＡ等のエポキシ樹脂に混合された樹脂組成物用いて積層基板を製造すると、凝集粒子のない信頼性に優れた積層基板となる。 The ultrafine silica dispersion slurry produced by the present invention has excellent sedimentation stability and redispersibility. When a laminated substrate is produced using a resin composition mixed with an epoxy resin such as bisphenol A, a laminated substrate excellent in reliability without aggregated particles is obtained.
Claims (3)
The number of isolated silanol groups in the ultrafine silica is 1 to 10 / nm 2 , the solvent is methyl ethyl ketone or methyl isobutyl ketone, and the content of the ultrafine silica in the slurry treated with the silane coupling agent is 50 to 50 It is 90 mass%, The manufacturing method of the ultra fine powder silica dispersion slurry for resin filling of Claim 1 or 2 characterized by the above-mentioned.