JP4057626B2 - Electrical Zn-plated steel sheet with excellent stain resistance - Google Patents

Description

  The present invention relates to an electric Zn-plated steel sheet excellent in stain resistance and a method for producing the same, and more specifically, an electric Zn-plated steel sheet having a resin film that does not substantially contain Cr, and Na in the resin film The present invention relates to a technique for improving stain-stain resistance that can effectively suppress (make it inconspicuous) the appearance unevenness of stain-stain caused by. The electric Zn-plated steel sheet of the present invention is suitably used for applications mainly used indoors, such as chassis and case parts, steel furniture, and the like of home appliances and OA equipment.

  From the viewpoint of regulations on the use of hazardous substances, electric Zn-plated steel sheets (non-chromate electric Zn-plated steel sheets) equipped with a chromate-free chemical conversion coating film that does not contain hexavalent chromium are widely used. Such non-chromate electric Zn-plated steel sheets are often used without painting in response to user requests for omission of painting. For example, when storing coils after production, at home appliance manufacturers and OA equipment manufacturers. During processing, the user may be exposed to a hot and humid environment for a long time during use.

However, when a non-chromate electrical Zn-plated steel sheet crescent or under a hot and humid environment for a long time [eg 504 hours (21 days) of about] put on the surface of the steel sheet, as shown in FIG. 1 A to be described later, stain It has been found by experiments by the present inventors that the appearance unevenness (color difference) occurs in the form as described above.

  Such a phenomenon (hereinafter sometimes referred to as “stain stain”) has not been observed in the electroplated Zn-plated steel sheet subjected to the chromate treatment. Further, the stain stain is a corrosion phenomenon that has been reported so far, typically white rust generated in a humid environment where chlorine ions exist [usually 96 hours after the salt spray test defined in JIS Z2371 ( 4th) Evaluate on the eyes] and blackening that occurs in a relatively mild corrosive environment seen before (initial) white rust [usually 72 at 50 ° C under constant temperature and humidity of 95% or more. Unlike the evaluation after time (3 days)], in particular, it can be seen for the first time by exposing a non-chromate electro-Zn plated steel sheet containing Na in the film to a high temperature and humidity environment for an extremely long time of about half a month or more. found.

However, the technique for improving the appearance unevenness of the electroplated Zn-plated steel sheet proposed so far relates to a method for preventing white rust and blackening before white rust occurs (for example, Patent Documents 1 to 4). There is no provision for improving the appearance unevenness for the purpose of preventing this.
Japanese Patent No. 3043336 Japanese Patent No. 3499544 Japanese Patent No. 3499543 JP 2004-263252 A

  The present invention has been made paying attention to the above circumstances, and its purpose is not only excellent in white rust resistance but also non-chromate electric Zn-plated steel sheet excellent in stain resistance and method for producing the same Is to provide.

  The electric Zn-plated steel sheet of the present invention that has been able to solve the above-described problems does not substantially contain Cr on the electric Zn-plated layer, and 0.05 to 5% (% means% by mass). , The same), an electric Zn-plated steel sheet provided with a resin film containing, wherein the electric Zn-plated layer comprises Ni, Fe, Cr, Mo, Sn, Cu, Cd, Ag, Si, Co, In, Ir, And at least one selected from the group consisting of W and W, in terms of atoms, Ni: 60 to 6000 ppm (ppm means mass ppm, hereinafter the same), Fe: 60 to 600 ppm, Cr: 0.5 to 5 ppm, Mo : 30-500 ppm, Sn: 0.6-20 ppm, Cu: 8-3000 ppm, Cd: 0.0001-0.02 ppm, Ag: 1.0-400 ppm, Si: 30-2000 ppm, Co: 0.003 to 0.3 ppm, In: 0.1 to 30 ppm, Ir: 0.01 to 10 ppm, W: 0.1 to 50 ppm, and the resin film contains 0.05 to 5 mass of Na. It has a gist in containing.

  In a preferred embodiment, the resin film contains a carboxyl group-containing resin and a Si-based inorganic compound. A representative example of the Si-based inorganic compound is, for example, colloidal silica.

  In a preferred embodiment, the resin film further contains a silane coupling agent.

The method for producing an electric Zn-plated steel sheet according to the present invention, which was able to solve the above problems,
(1) Ni: 20 to 2000 ppm, Fe ²⁺ : 50 to 5000 ppm, Fe ³⁺ : 50 to 5000 ppm, Cr: 5 to 2000 ppm, Mo: 50 to 2000 ppm, Sn: 0.05 to 20 ppm, Cu: 0.05 to 50 ppm Cd: 0.05-5 ppm, Ag: 0.05-5 ppm, Si: 20-2000 ppm, Co: 0.05-50 ppm, In: 0.5-50 ppm, Ir: 0.05-5 ppm, and W: Performing electro-Zn plating using an acidic plating solution containing at least one element selected from the group consisting of 0.5 to 50 ppm;
(2) forming a resin film containing 0.05 to 5% by mass of Na;
It has a gist to include.

  Since the electric Zn plated steel sheet of the present invention is configured as described above, the white rust resistance and stain stain resistance of the non-chromated steel sheet are greatly improved.

  The “stain stain” phenomenon has not been recognized in the conventional chromate-treated steel sheets, and according to the inventor's experiments, in particular, an electro-zinc-plated steel sheet containing Na in the chromate-free resin film is used in a high-temperature and high-humidity environment. It has been found that it is observed by exposing it underneath for a long time (generally, about 504 hours). Na is added mainly for the purpose of increasing the strength of the chromate-free resin film and improving the abrasion resistance (anti-glazing) (details will be described later). The non-chromate resin film containing Na is It has become widely used in the field of non-chromate treated steel sheets.

  Therefore, the present inventor provides a technique capable of preventing (inconspicuous) the appearance unevenness of “stain stain” that occurs when a non-chromate electro-Zn plated steel sheet not subjected to chromate treatment is stored in a high temperature and high humidity environment for an extremely long period of time. In order to do so, it has been studied repeatedly.

  As a result, among the impurity elements unavoidably present in the plating layer due to the raw materials of Zn plating, etc., there are cases where they are referred to as specific elements described below in detail (“stain stain resistance improving element”). ) Was controlled within a predetermined range, the stain resistance was improved, and the present invention was completed.

  In addition, although it is not a stain | pollution | contamination dirt-resistant improvement technique like this invention, in patent document 1-patent document 4 mentioned above, white rust resistance is controlled by controlling content of the predetermined | prescribed element in an electric Zn plating layer. A method for improving this problem has been proposed. Among these, some elements that are used in the present invention and whose contents partially overlap are disclosed. Specifically, in order to prevent uneven appearance such as white rust, Patent Documents 1 to 3 add an element (Ni, In, Cu, Ag, Co) nobler than Zn in the plating bath. A method is disclosed, and Patent Document 4 discloses an element (Fe, Co, Ni, Mn, Mg, Al, Ce, In) that forms a hardly soluble hydroxide in an alkali region in which Zn dissolves, A method is disclosed in which elements (Si, Ti, V, Mo, Zr) that are stable in the nature range and can exist stably in the corrosive environment are added to the plating bath.

  However, it is presumed that the appearance irregularities that are the targets of both are different in their cause of occurrence and different in their generation mechanism (mechanism) as described below.

  That is, the appearance unevenness of “stain stain” targeted in the present invention occurs only when the non-chromate electro-zinc plated steel sheet is exposed to high temperature and high humidity for a very long time, and white rust and It is considered that the generation mechanism is different from the appearance irregularity of blackening caused by exposure to high temperature and high humidity for a short time. In addition, the above-mentioned “stain stain” is a phenomenon that is first seen when Na is contained in the non-chromate chemical conversion coating film, and it is considered that the generation mechanism is different from the appearance irregularity of white rust and blackening. It is done. Even if these patent documents are scrutinized, it is not described at all that the Na-containing non-chromate film was used.

  In addition, as shown in the examples described later, the types and contents of stain resistance improving elements used in the present invention are the types of white rust resistance improving elements whose effects were confirmed in the above-mentioned patent document. It was also found that it is difficult to apply the method described in the above-mentioned patent document as it is to the stain and stain resistance improving technology as it is.

  Hereinafter, the electric Zn plated steel sheet of the present invention will be described in detail.

  The electric Zn-plated steel sheet of the present invention is an electric Zn-plated steel sheet that is substantially free of Cr on the electric Zn-plated layer and provided with a resin film containing 0.05 to 5% of Na, The electrical Zn plating layer is made of at least one element selected from the group consisting of Ni, Fe, Cr, Mo, Sn, Cu, Cd, Ag, Si, Co, In, Ir, and W (stain stain resistance improving element) ) In terms of atoms: Fe: 60 to 600 ppm, Cr: 0.5 to 5 ppm, Mo: 30 to 500 ppm, Sn: 0.6 to 20 ppm, Cu: 8 to 3000 ppm, Cd: 0.0001 to 0.02 ppm , Ag: 1.0 to 400 ppm, Si: 30 to 2000 ppm, Co: 0.0003 to 0.3 ppm, In: 0.1 to 30 ppm, Ir: 0.01 to 10 ppm, W: 0.1 to 50 p It comprises in the range of m.

FIG. 1 shows a photograph of an electric Zn-plated steel sheet in which stain stain has occurred. Specifically, FIG. 1 shows a photograph (5 cm × 5 cm) when an electro-Zn plated steel sheet having a Na-containing non-chromate film is stored for 504 hours (21 days) under high temperature and high humidity at a temperature of 50 ° C. and a relative humidity of 95%. 1A to 1C are respectively No. 1 in Table 1 of Example 1 described later. 2 (Evaluation Criteria 3 , stains occur ), No. 2 4 (Evaluation Criteria 2, slight stains occur), No. 4 6 (Evaluation Criteria 1 , no stains at all ). As shown in FIG. 1 A, the electric Zn plated steel sheet, the coating surface blackish and (brown) discolored area (Na aggregated portion), a whitish area discoloration does not occur (non-aggregated portion Na is not aggregated) And a mottled pattern like a spot (stain stain) is observed in the entire film. It is thought that the main reason for the appearance unevenness of the stain stain is that only the Na agglomerated portion is discolored.

  Although the mechanism that can effectively prevent stain stain by adding the stain-stain resistance improving element used in the present invention is unknown, Zn plating is provided by providing an electric Zn plating layer containing a predetermined amount of the above-mentioned elements. In order to affect the crystal form and surface oxide (for example, a Zn hydroxide layer containing the above-mentioned additive element inevitably generated on the surface of the Zn plating) It is conceivable that the difference in color tone can be almost eliminated. As a result, it is possible to eliminate uneven appearance due to stains.

  All of the above elements have an effect of improving stain resistance, but can be broadly classified as follows: (1) Elements (Ni, Fe, Sn, Cd, Ir, In, Cu, Ag, nobler than Zn) Co) and (2) elements (Cr, Mo, Si, W) that are not more noble than Zn but form oxides. These elements may be used alone or in combination of two or more.

  In order to effectively exhibit the effect of improving stain resistance by the above elements, the content of each element contained in the electric Zn plating layer is 60 ppm or more (preferably 600 ppm or more), Ni in terms of atoms, and Fe. 60 ppm or more (preferably 80 ppm or more), Cr 0.5 ppm or more (preferably 0.8 ppm or more), Mo 30 ppm or more (preferably 100 ppm or more), Sn 0.6 ppm or more (preferably 1.5 ppm or more), Cu is 8.0 ppm or more (preferably 100 ppm or more), Cd is 0.0001 ppm or more (preferably 0.01 ppm or more), Ag is 1.0 ppm or more (preferably 30 ppm or more), and Si is 30 ppm or more (preferably 80 ppm or more). ), Co 0.0003 ppm or more (preferably 0.001 ppm or more) , In is 0.1 ppm or more (preferably 1.0 ppm or more), Ir is 0.01 ppm or more (preferably 0.1 ppm or more), and W is 0.1 ppm or more (preferably 1.0 ppm or more) (described later). See Examples).

  However, if added excessively, the following problems occur. First, when Fe or Si is added excessively, as shown in Examples described later, the stain stain resistance improving action is lowered, and the corrosion resistance (particularly, white rust resistance) is also lowered. On the other hand, when an excessive stain resistance improving element other than Fe or Si is added, the stain resistance is good but the white rust resistance is lowered as shown in the examples described later. In order to satisfy both the stain stain resistance and the white rust resistance characteristics and to obtain an excellent surface appearance, the content of each element contained in the electric Zn plating layer is set to Ni of 6000 ppm or less, Fe 600 ppm or less, Cr 5.0 ppm or less, Mo 500 ppm or less, Sn 20 ppm or less, Cu 3000 ppm or less, Cd 0.02 ppm or less, Ag 400 ppm or less, Si 2000 ppm or less, Co 0.3 ppm or less, In is 30 ppm or less, Ir is 10 ppm or less, and W is 50 ppm or less.

  Among the above elements, Ni, Fe, Cr, Mo, Si, Cu, Co, W, In, Cu, and Ag are particularly preferable as the elements excellent in the effect of improving stain resistance. Are Ni, Fe, Mo, Cr, W.

  The amount of the stain resistance improving element contained in the electroplated Zn layer is, for example, a method such as atomic absorption spectrometry, inductively coupled plasma emission spectroscopy (ICP), or inductively coupled plasma mass spectrometry (ICP-MS). Can be used for analysis. A detailed analysis method is described in the column of Examples described later. In the analysis, it is preferable to dilute the plating layer with hydrochloric acid or the like in order to eliminate measurement errors caused by matrix elements such as Zn, Na, and S contained in the plating solution. The dilution rate may be appropriately controlled within an appropriate range depending on the concentration of the matrix element and the amount of the stain resistance improving element to be measured. In Examples described later, the content of elements in the plating layer is analyzed after the plating layer is diluted with hydrochloric acid diluted twice.

In consideration of the crystal size of the Zn single crystal deposited on the surface of the plating layer, the amount of adhesion of electro-Zn plating is preferably generally 40 g / m ² or less, and more preferably 30 g / m ² or less. In addition, the lower limit is not particularly limited from the above viewpoint, but considering sacrificial anticorrosive action by Zn, it is preferably 3 g / m ² and more preferably 10 g / m ² .

  The electric Zn plating layer only needs to be provided at least on a predetermined surface of the steel plate as the base material, and may be provided only on one surface of the steel plate, or may be provided on both surfaces.

  The resin film (non-chromate resin film) contains about 0.05 to 5% (preferably 0.1% or more and 3% or less, more preferably 1% or less) of Na. In order to improve the strength of the non-chromate resin film (preferably containing a Si-based inorganic compound such as a carboxyl group-containing resin and colloidal silica), Na is usually contained in the carboxyl group-containing resin or colloidal silica. It has been added. When the Na content is less than 0.05%, for example, Na cross-linking is not sufficiently generated between the carboxyl group and Na in the carboxyl group-containing resin, and the strength of the film is reduced. On the other hand, the Na content If it exceeds 5%, the amount of soluble Na contained in the film increases and the abrasion resistance decreases. The amount of Na contained in the resin film is represented by the total amount of Na in the solid content of each component (resin component, Si-based inorganic compound, silane coupling agent contained as necessary) constituting the resin film. The

  The resin film does not substantially contain Cr. Here, “substantially does not contain” means that an amount of Cr inevitably mixed in the process of producing the resin film is acceptable. For example, in the present invention, a small amount of Cr may be added to the plating layer as an element for improving stain resistance, but the Cr in the plating layer may be mixed into the resin film. In addition, for example, when a trace amount of Cr compound is eluted from a manufacturing container, a coating apparatus, etc. in the process of preparation and application of a treatment liquid used for a non-chromic resin film, Cr may be mixed into the resin film. . Even in such a case, the amount of Cr contained in the resin film is preferably within a range of approximately 0.01% or less.

  The resin film preferably contains a resin component of a carboxyl group-containing resin and an Si-based inorganic compound (typically colloidal silica). By using a resin film containing these, the corrosion resistance, alkali degreasing resistance, paintability, etc. of the film are improved.

  The carboxyl group-containing resin is not particularly limited as long as it has a carboxyl group. For example, a polymer synthesized by polymerization using a monomer having a carboxyl group such as an unsaturated carboxylic acid as a part or all of a raw material, or And a resin modified with a carboxylic acid using a functional group reaction.

A commercially available product may be used as the carboxyl group-containing resin, and examples thereof include Hitech S3141 (manufactured by Toho Chemical).
The resin component may contain an organic resin other than the carboxyl group-containing resin described above.

  Examples of the Si-based inorganic compound include silicate and / or silica. These may be used alone or in combination of two or more.

  Among these, examples of the silicate include potassium silicate and lithium silicate.

  Typical examples of silica include colloidal silica and scaly silica. In addition, dry silica such as pulverized silica, gas phase method silica, silica sol, and fumed silica may be used.

  Of these, the use of colloidal silica is particularly preferred. As a result, the strength of the resin film is increased, and in a corrosive environment, silica is concentrated in the heel portion of the film, and the corrosion of Zn is suppressed and the corrosion resistance is further enhanced.

  As the colloidal silica, commercially available products may be used. For example, Snowtex series “ST-40”, “ST-XS”, “ST-N”, “ST-20L”, “ST-20L” manufactured by Nissan Chemical Industries, Ltd., “ ST-UP "," ST-ZL "," ST-SS "," ST-O "," ST-AK ", and the like. These usually contain Na.

  The mass ratio between the resin component constituting the resin film and the Si-based inorganic compound (typically colloidal silica) is generally in the range of resin component: Si-based inorganic compound = 5 parts to 45 parts: 55 parts to 95 parts. It is preferable that If the content of the resin component is small, the corrosion resistance, alkali degreasing resistance, paintability, etc. tend to decrease. On the other hand, if the content of the resin component is large, the abrasion resistance, conductivity, etc. will decrease. . In addition, when the content of the Si-based inorganic compound is small, abrasion resistance, conductivity, etc. tend to decrease, and when the content of the Si-based inorganic compound is large, the resin component is decreased, so that the resin film is formed. As a result, the corrosion resistance decreases.

  The resin film may further contain a silane coupling agent. By adding the silane coupling agent, the bond between the carboxyl group-containing resin and the Si-based inorganic compound is strengthened, so that elution of Na ions is reduced and the stain resistance is further improved.

  The silane coupling agent preferably has a lower alkoxy group such as an alkyl group having 1 to 5 carbon atoms, an allyl group, or an aryl group. Specifically, for example, glycidoxy group-containing γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropylmethyldimethoxysilane, γ-glycidoxypropyltriethoxysilane, γ-glycidoxymethyldimethoxysilane, etc. Silane coupling agent; γ-aminopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, N- (β-aminoethyl) -γ-aminopropyltrimethoxysilane, N- (β-aminoethyl) -γ-amino Amino group-containing silane coupling agents such as propylmethyldimethoxysilane; Vinyl group-containing silane coupling agents such as vinyltrimethoxysilane, vinyltriethoxysilane, and vinyltris (β-methoxyethoxy) silane; γ-methacryloxypropyltrimethoxysilane Meta Riloxy group-containing silane coupling agents; mercapto group-containing silane coupling agents such as γ-mercaptopropyltrimethoxysilane and γ-mercaptopropylmethyldimethoxysilane; halogens such as γ-chloropropylmethoxysilane and γ-chloropropyltrimethoxysilane Examples thereof include a group-containing silane coupling agent. These silane coupling agents may be used alone or in combination of two or more.

  Among the above, the glycidoxy group-containing silane coupling agent is preferably used because it has particularly high reactivity and is excellent in corrosion resistance and alkali resistance.

  A commercially available product may be used as the silane coupling agent, and examples thereof include γ-glycidoxypropyltrimethoxysilane “KBM403” (manufactured by Shin-Etsu Chemical Co., Ltd.).

  The content of the silane coupling agent is preferably in the range of approximately 5 parts by mass to 25 parts by mass with respect to 100 parts by mass in total of the resin component and the Si-based inorganic compound. When the content of the silane coupling agent is low, the stain resistance improving effect is not exhibited effectively, and the reactivity between the carboxyl group-containing resin and the Si-based inorganic compound is reduced, resulting in abrasion resistance, paintability, Corrosion resistance is reduced. On the other hand, when there is much content of a silane coupling agent, stability of the film preparation liquid used for preparation of a resin film will fall, and there exists a possibility of gelatinizing. Moreover, since the quantity of the silane coupling agent which does not contribute to reaction increases, there exists a possibility that the adhesiveness of a Zn plating layer and a resin film may fall.

  Hereinafter, the case where the following resin films are used as typical non-chromate resin films used in the present invention will be described. This resin film is a urethane resin improved film disclosed by the applicant's application, and details are as described in JP-A-2006-43913 (see, for example, paragraphs [0020] to [0071]). ). Although the structure and preparation method of the said resin film are demonstrated easily below, the resin film used for this invention is not the meaning limited to this.

  The resin film is obtained from the following aqueous resin liquid. The aqueous resin liquid is a silica particle having 5 to 45 parts by mass of an aqueous carboxylate-containing polyurethane resin liquid and an aqueous ethylene-unsaturated carboxylic acid copolymer dispersion as a nonvolatile resin component, and an average particle diameter of 4 to 20 nm. Contains 55 to 95 parts by mass in total, and further contains a silane coupling agent in a ratio of 5 to 25 parts by mass with respect to the total of 100 parts by mass. The compounding ratio of the component (PU) and the nonvolatile resin component (EC) of the ethylene-unsaturated carboxylic acid copolymer aqueous dispersion is PU: EC = 9: 1 to 2: 1 in terms of mass ratio.

  First, the carboxyl group-containing polyurethane resin aqueous solution will be described.

  As the aqueous carboxyl group-containing polyurethane resin liquid, either an aqueous dispersion in which a carboxyl group-containing polyurethane resin is dispersed in an aqueous medium or an aqueous solution in which the carboxyl group-containing polyurethane resin is dissolved in an aqueous medium can be used. The aqueous medium may contain a trace amount of a hydrophilic solvent such as alcohol, N-methylpyrrolidone and acetone in addition to water.

  The carboxyl group-containing polyurethane resin is preferably obtained by subjecting a urethane prepolymer to a chain extension reaction with a chain extender, and the urethane prepolymer reacts, for example, a polyisocyanate component and a polyol component described later. Obtained.

  As the polyisocyanate component constituting the urethane prepolymer, at least one polyisocyanate selected from the group consisting of tolylene diisocyanate (TDI), diphenylmethane diisocyanate (MDI), and dicyclohexylmethane diisocyanate (hydrogenated MDI) is used. It is preferable. Here, as the polyol component constituting the urethane prepolymer, 1,4-cyclohexanedimethanol, polyether polyol, and all three types of polyols having a carboxyl group are used, preferably all three types are used. Is a diol. The polyether polyol is not particularly limited as long as it has at least two hydroxyl groups in the molecular chain and the main skeleton is composed of alkylene oxide units. For example, polyoxyethylene glycol, polyoxypropylene glycol And polyoxytetramethylene glycol.

  The chain extender for chain extending reaction of the urethane prepolymer described above is not particularly limited, and examples thereof include polyamines, low molecular weight polyols, and alkanolamines.

  A known method can be used to prepare the aqueous solution of the carboxyl group-containing polyurethane resin. For example, the carboxyl group of the carboxyl group-containing urethane prepolymer is neutralized with a base, and emulsified and dispersed in an aqueous medium. There are a method of extending the reaction, a method of emulsifying and dispersing the carboxyl group-containing polyurethane resin in the presence of an emulsifier with a high shearing force, and the like.

  Next, the ethylene-unsaturated carboxylic acid copolymer aqueous dispersion will be described.

  The ethylene-unsaturated carboxylic acid copolymer aqueous dispersion is not particularly limited as long as the ethylene-unsaturated carboxylic acid copolymer is a liquid in which the ethylene-unsaturated carboxylic acid copolymer is dispersed in an aqueous medium. Is a copolymer of ethylene and an ethylenically unsaturated carboxylic acid. Examples of the unsaturated carboxylic acid include (meth) acrylic acid, crotonic acid, isocrotonic acid, maleic acid, fumaric acid, itaconic acid, and the like. A copolymer can be obtained by polymerization using a legal method or the like.

  The ethylene-unsaturated carboxylic acid copolymer has a carboxyl group, and the carboxyl group is neutralized with an organic base (for example, an amine having a boiling point of 100 ° C. or less) or a monovalent metal ion such as Na. Thus, an aqueous dispersion can be obtained.

  Here, monovalent metal ions are used for neutralization as described above, but are effective in improving solvent resistance and film hardness. The monovalent metal compound preferably contains one or more metals selected from sodium, potassium, and lithium, and a hydroxide, carbonate, or oxide of these metals is preferable. Among these, NaOH, KOH, LiOH and the like are preferable, and NaOH has the best performance and is preferable. The present invention improves the blot stain phenomenon derived from NaOH.

  The amount of the monovalent metal compound may be in the range of 0.02 to 0.4 mol (2 to 40 mol%) with respect to 1 mol of the carboxyl group in the ethylene-unsaturated carboxylic acid copolymer. preferable. When the amount of the metal compound is less than 0.02 mol, the emulsion stability becomes insufficient. However, when the amount exceeds 0.4 mol, the hygroscopicity (particularly with respect to the alkaline solution) of the resulting resin film increases, and degreasing Since corrosion resistance after a process deteriorates, it is not preferable. The lower limit of the more preferable amount of the metal compound is 0.03 mol, and the more preferable lower limit is 0.1 mol. The upper limit of the more preferable amount of the metal compound is 0.5 mol, and the more preferable upper limit is 0.2 mol.

  If the total amount (neutralization amount) of the organic base (preferably an amine having a boiling point of 100 ° C. or less) and a monovalent metal compound is too large, the viscosity of the aqueous dispersion may rapidly increase and solidify. In addition, since excessive alkali content causes deterioration of corrosion resistance, a large amount of energy is required for volatilization, which is not preferable. However, if the neutralization amount is too small, the emulsifiability is inferior, which is not preferable. Therefore, the total amount of the organic base and the monovalent metal compound is preferably in the range of 0.3 to 1.0 mol with respect to 1 mol of the carboxyl group in the ethylene-unsaturated carboxylic acid copolymer.

  The ethylene-unsaturated carboxylic acid copolymer aqueous dispersion described above is an extremely small fine particle (oil droplet) state having an average particle size of 5 to 50 nm by emulsifying an organic base and a monovalent metal ion in combination. To obtain a dispersion in an aqueous medium. For this reason, it is presumed that the film forming property of the obtained resin film, the adhesion to the metal plate, the densification of the film are achieved, and the corrosion resistance is improved. The aqueous medium may contain a hydrophilic solvent such as alcohol or ether in addition to water. The particle diameter of the resin particles in the aqueous dispersion can be measured by a laser diffraction method using, for example, a light scattering photometer (manufactured by Otsuka Electronics Co., Ltd.).

  As a method for preparing the ethylene-unsaturated carboxylic acid copolymer aqueous dispersion, the ethylene-unsaturated carboxylic acid copolymer is put together with an aqueous medium into, for example, a homogenizer device or the like, and heated at 70 to 250 ° C. as necessary. And an organic base such as an amine having a boiling point of 100 ° C. or lower and a monovalent metal compound is appropriately added in the form of an aqueous solution or the like (an amine having a boiling point of 100 ° C. or lower is added first, or an amine having a boiling point of 100 ° C. or lower is added. The monovalent metal compound is added almost simultaneously) and stirred with high shearing force.

Next, the carboxyl group-containing polyurethane resin aqueous liquid and the ethylene-unsaturated carboxylic acid copolymer aqueous dispersion obtained by the above-described method are blended with silica particles and a silane coupling agent in a predetermined amount, and if necessary, a wax is added. A desired aqueous resin solution is obtained by blending a crosslinking agent and the like. Silica particles, silane coupling agent, wax, cross-linking agent, etc. may be added at any stage, but after adding the cross-linking agent and silane coupling agent, heat is applied so that the cross-linking reaction will not proceed and gel. It is desirable not to multiply.
The typical resin film used in the present invention has been described above.

  In addition to the above-mentioned components, the resin film normally contains components that do not impair the effects of the present invention (for example, anti-skinning agents, leveling agents, antifoaming agents, penetrating agents, emulsifying agents, film-forming aids, coloring). Containing pigments, lubricants, surfactants, conductive additives to impart electrical conductivity, thickeners, dispersants, drying agents, stabilizers, antifungal agents, preservatives, antifreeze agents, etc.) Also good.

  In general, the thickness of the resin film is preferably in the range of 0.1 to 2 μm, and more preferably in the range of 0.2 to 1.0 μm. When the thickness of the resin film is less than 0.1 μm, the corrosion resistance is lowered, whereas when it exceeds 2 μm, the conductivity is lowered.

  Films such as organic resin films, organic / inorganic composite films, inorganic films, and electrodeposition coating films are provided on the resin film for the purpose of improving corrosion resistance (particularly white rust resistance) and paintability. It may be.

  Here, as the organic resin film, for example, urethane resin, epoxy resin, acrylic resin, polyethylene, polypropylene, olefin resin such as ethylene-acrylic acid copolymer, styrene resin such as polystyrene, polyester, or these Examples thereof include a film formed by combining a known resin for coatings such as a copolymer or a modified product with colloidal silica, a solid lubricant, a crosslinking agent, or the like, if necessary.

  A typical example of the organic / inorganic composite film is a film formed by combining the organic resin and a water glass forming component such as sodium silicate.

  Typical examples of the inorganic film include a water glass film and a film formed from lithium silicate.

  Next, the manufacturing method of the non-chromate electric Zn plating steel plate concerning the present invention is explained.

  First, a base steel plate (plating original plate) serving as a base material is prepared. The base steel plate is not particularly limited as long as it is usually used for an electric Zn-plated steel plate. For example, various steel plates such as a normal steel plate, an Al killed steel plate, and a high-tensile steel plate can be used. The plating original plate is preferably subjected to pretreatment such as degreasing and pickling before performing electro-Zn plating.

  Next, an electric Zn plating layer is formed on the base steel plate by an electric Zn plating method to produce an electric Zn plating steel plate.

In an acidic bath used for electro-Zn plating, Ni: 20 to 2000 ppm, Fe ²⁺ : 50 to 5000 ppm, Fe ³⁺ : 50 to 50 in an acidic solution such as sulfuric acid or hydrochloric acid so that a desired plating layer is formed. 5000 ppm, Cr: 5-2000 ppm, Mo: 50-2000 ppm, Sn: 0.05-20 ppm, Cu: 0.05-50 ppm, Cd: 0.05-5 ppm, Ag: 0.05-5 ppm, Si: 20- At least one element selected from the group consisting of 2000 ppm, Co: 0.05-50 ppm, In: 0.5-50 ppm, Ir: 0.05-5 ppm, and W: 0.5-50 ppm is added. If the amount of each element is less than the above lower limit, stain stain resistance will not be exhibited effectively. On the other hand, if the amount of each element exceeds the above upper limit, properties such as stain stain resistance and white rust resistance will be exhibited. (Refer to the examples described later).

The preferable addition amount of each element is Ni: 200 ppm to 2000 ppm, Fe ²⁺ : 200 ppm to 2000 ppm, Fe ³⁺ : 500 ppm to 2000 ppm, Cr: 50 ppm to 2000 ppm, Mo: 200 ppm to 2000 ppm, Sn: 0 0.5 ppm to 5 ppm, Cu: 2 ppm to 50 ppm, Cd: 0.5 ppm to 5 ppm, Ag: 0.5 ppm to 5 ppm, Si: 50 ppm to 800 ppm, Co: 0.5 ppm to 5 ppm, In: 2 ppm 20 ppm or less, Ir: 0.5 ppm or more and 5 ppm or less, W: 2 ppm or more and 50 ppm or less.

  The addition form of the element into the plating bath is not particularly limited, and can take any form as long as the addition amount of each element in terms of atoms satisfies the above range. For example, it may be added to the plating solution in a metal state such as metal powder or metal foil, or added in the form of a metal salt such as sulfate, chloride, phosphate, carbonate, oxide salt. Also good. When adding in the form of a metal salt, the valence of the element is not particularly limited, and a value that can be normally taken can be adopted. For example, Cr may be trivalent or hexavalent. Mo, W, etc. may be either tetravalent or hexavalent. As shown in the examples described later, the above elements may be added in the form of hydrates.

In addition to the above elements, other components that are usually added may be added to the plating solution. For example, a conductive auxiliary agent such as Na ₂ SO ₄ , (NH ₄ ) ₂ SO ₄ , KCl, or NaCl may be added for the purpose of increasing conductivity and reducing power consumption.

  The production method of the present invention is characterized in that a predetermined amount of the above element having an effect of improving stain resistance and stain resistance is added to the plating solution to form a desired electric Zn plating layer. Although it is appropriately determined as long as the operation of the present invention is not impaired, for example, the following control is preferable.

  The pH of the plating solution is preferably within the range of 0.5 to 4.0, preferably within the range of 1.0 to 2.0, in consideration of the relationship with current efficiency and plating burn phenomenon. Is more preferable.

  It is preferable that the temperature of the plating solution is approximately in the range of 50 to 70 ° C.

  It is preferable that the relative flow rate of the plating solution is generally in the range of 0.3 to 5 m / sec. Here, the relative flow velocity means the difference between the flow direction velocity of the plating solution and the plate passage direction velocity of the steel plate that is the plating original plate.

  The type of electrode (anode) used for electroplating is not particularly limited as long as it is normally used. For example, Pb—Sn electrode, Pb—In electrode, Pb—Ag electrode, Pb—In—Ag electrode, etc. In addition to lead-based electrodes, examples include iridium oxide electrodes and zinc electrodes.

  As the plating cell, either a vertical cell or a horizontal cell can be used. The method of electro Zn plating is not particularly limited, and examples thereof include constant current plating and pulse plating.

  After forming the plating layer as described above, a resin film (non-chromate film) is formed as follows. Prior to the formation of the resin film, for example, amines such as Co, Ni, Mo, V, phosphate, and nitrate were used on the surface of the plating layer for the purpose of improving film adhesion, improving corrosion resistance, and controlling appearance. A known pretreatment may be performed.

  Specifically, first, a chromate-free chemical conversion treatment liquid (hereinafter simply referred to as “treatment liquid”) containing a predetermined amount of a resin component of a carboxyl group-containing resin and a Si-based inorganic compound, preferably containing a predetermined amount of a silane coupling agent. Prepared). The treatment liquid is obtained by dissolving and dispersing in an aqueous solvent (for example, hydrochloric acid or nitric acid solution) that can completely dissolve the following components.

  The mass ratio of the resin component and the Si-based inorganic compound contained in the treatment liquid is preferably generally within the range of resin component: Si-based inorganic compound = 5 parts to 45 parts: 55 parts to 95 parts. If the amount of the resin component such as carboxyl group-containing resin is small, the corrosion resistance, alkali degreasing resistance, paintability, etc. tend to decrease. On the other hand, if the amount of the resin component is large, the abrasion resistance, conductivity, etc. decrease. Will come to do. Also, if the amount of colloidal silica is small, the abrasion resistance, conductivity, etc. tend to decrease, and if the amount of colloidal silica is large, the resin component is reduced and the film-forming property of the resin film is reduced, resulting in corrosion resistance. Will fall.

  The treatment liquid may further contain a silane coupling agent. The content of the silane coupling agent contained in the treatment liquid is generally in the range of 5 to 25 parts by mass with respect to a total of 100 parts by mass of the resin component and the Si-based inorganic compound, as shown in the examples described later. It is preferable. If the content of the silane coupling agent is low, the stain resistance improving effect is not exhibited effectively, and the reactivity between the carboxyl group-containing resin and the Si-based inorganic compound is reduced, resulting in abrasion resistance, paintability, corrosion resistance, etc. Decreases. On the other hand, when there is much content of a silane coupling agent, stability of the film preparation liquid used for preparation of a resin film will fall, and there exists a possibility of gelatinizing. Moreover, since the quantity of the silane coupling agent which does not contribute to reaction increases, there exists a possibility that the adhesiveness of a Zn plating layer and a resin film may fall.

  In addition to the above components, a wax or a crosslinking agent may be added to the treatment liquid as necessary. Further, the treatment liquid usually contains components (for example, anti-skinning agents, leveling agents, antifoaming agents, penetrating agents, emulsifying agents, film-forming aids, color pigments, lubricants) as long as the effects of the present invention are not impaired. Agents, surfactants, conductive additives for imparting conductivity, thickeners, dispersants, drying agents, stabilizers, antifungal agents, preservatives, antifreeze agents, etc.).

  The treatment liquid containing the above components can be obtained by using a known method such as a roll coating method, a spray coating method, a curtain flow coater method, a knife coater method, a bar coating method, a dip coating method, or a brush coating method. When applied to one or both sides of the plate, and then heated and dried, an electric Zn-plated steel plate provided with a desired resin film is obtained.

  The heating / drying temperature is preferably a temperature at which the crosslinking reaction between the carboxyl group-containing resin to be used and the Si-based inorganic compound proceeds sufficiently (for example, approximately a plate temperature of 90 to 100 ° C.). In addition, when spherical polyethylene wax is used as the lubricant, it is possible to perform drying in the range of about 70 to 130 ° C. because maintaining the spherical shape improves the workability in the subsequent processing step. desirable.

  Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited by the following examples, and may be implemented with appropriate modifications within a range that can meet the purpose described above and below. It is possible and such an aspect is also included in the technical scope of the present invention.

Example 1
In this example, the effect of the type and content of elements contained in the plating layer on stain resistance and white rust resistance was examined. Here, the resin film is produced in the same manner as the method described in Example 1 of JP-A-2004-224454 described above.

(1) Preparation of Resin Aqueous Liquid Here, a resin film is formed from an aqueous resin liquid containing a carboxyl group-containing polyurethane resin aqueous liquid, an ethylene-unsaturated carboxylic acid copolymer aqueous dispersion, silica particles, and a silane coupling agent. Produced. A specific manufacturing method is as follows.

(1-1) Preparation of carboxyl group-containing polyurethane resin aqueous liquid Polytetramethylene ether glycol manufactured by Hodogaya Chemical Co., Ltd. 60 g of an average molecular weight of 1000), 14 g of 1,4-cyclohexanedimethanol and 20 g of dimethylolpropionic acid were charged, and 30.0 g of N-methylpyrrolidone was further added as a reaction solvent. 104 g of tolylene diisocyanate (hereinafter sometimes simply referred to as “TDI”) was added as an isocyanate component, and the temperature was raised from 80 to 85 ° C. and reacted for 5 hours. The obtained prepolymer had an NCO content of 8.9%. Further, 16 g of triethylamine was added for neutralization, a mixed aqueous solution of 16 g of ethylenediamine and 480 g of water was added, emulsified at 50 ° C. for 4 hours, and chain extension reaction was performed to obtain an aqueous polyurethane resin dispersion (nonvolatile resin component 29 0.1%, acid value 41.4).

(1-2) Preparation of Ethylene-Unsaturated Carboxylic Acid Copolymer Aqueous Dispersion Into an autoclave of an emulsification facility having an internal capacity of 0.8 L equipped with a stirrer, thermometer and temperature controller, 626 parts by mass of water, ethylene- 160 parts by mass of an acrylic acid copolymer (acrylic acid 20% by mass, melt index (MI) 300) is added, and 40% by mol of triethylamine, sodium hydroxide with respect to 1 mol of the carboxyl group of the ethylene-acrylic acid copolymer. Was added at a high speed under an atmosphere of 150 ° C. and 5 Pa, and cooled to 40 ° C. to obtain an aqueous dispersion of an ethylene-acrylic acid copolymer. Subsequently, 4,4′-bis (ethyleneiminocarbonylamino) diphenylmethane (manufactured by Nippon Shokubai, Chemite DZ-22E, “Chemite” is a registered trademark), ethylene-acrylic acid copolymer as a crosslinking agent in the aqueous dispersion. It added so that it might become a ratio of 5 mass parts with respect to 100 mass parts of united non-volatile resin components.

(1-3) Preparation of resin aqueous liquid Carboxy group-containing polyurethane resin aqueous liquid obtained above, ethylene-acrylic acid copolymer aqueous dispersion, colloidal silica (“ST-XS” manufactured by Nissan Chemical Industries, Ltd., A total of 100 parts by mass in terms of non-volatile components is blended so that the blending ratio of the average particle diameter of 4 to 6 nm is 5 parts by mass: 25 parts by mass: 70 parts by mass. An aqueous resin liquid was prepared by adding 10 parts by mass of γ-glycidoxypropyltrimethoxysilane (“KBM403” manufactured by Shin-Etsu Chemical) as a ring agent.

(2) Production of electric Zn-plated steel sheet An Al-killed cold-rolled steel sheet produced by a conventional method was used as a plating original sheet. This was degreased and pickled, and then electroplated under the following conditions using a sulfate bath in a circulation type plating apparatus having a plating area of 180 mm × 300 mm to obtain an electrical Zn-plated steel sheet.

(Plating solution composition)
While containing the following components, the plating solution which added the various elements of Tables 1-3 in the range shown in the said table | surface was used, respectively. As shown in the above table, Ni, Fe, Cr, Sn, Cu, Cd, Co, and W are all sulfates, Mo is sodium molybdate, Si is colloidal silica, Ag is silver nitrate, In Was added as a hydroxide and Ir as a bromide. For comparison, a plating solution without any of these elements was also prepared.
ZnSO ₄ · 7H ₂ O 350 g / L
Na ₂ SO ₄ 70 g / L
H ₂ SO ₄ 20 g / L

Other electroplating conditions are as follows.
Current density: 100 A / dm ²
・ Plating bath temperature: 60 ± 5 ℃
・ Plating solution flow rate: 1.3m / sec
-Electrode (anode): IrOx electrode-Amount of plating: 20 g / m ²

(3) Production of electro-Zn-plated steel sheet provided with resin film The aqueous resin solution obtained in (1) above is applied onto the Zn-plated layer obtained in (2) above by roll drawing (single-sided application) Then, in an experimental furnace, heat drying was performed at a furnace temperature of 220 ° C. and a plate temperature of 95 ° C. to obtain an electric Zn-plated steel sheet having a resin film (non-chromate film) with a thickness of 0.4 μm.

  The resin film thus obtained contains a resin component, colloidal silica, and a silane coupling agent in a mass ratio, and generally contains resin component: colloidal silica: silane coupling agent = 30 parts: 70 parts: 10 parts. ing.

  Moreover, it was 1.2 mass% when Na contained in said resin film was confirmed by the atomic absorption photometry method (apparatus: SOLARA-M6 made from a jarrel ash company was used). In detail, Na content contained in the resin component which comprises a resin film was 0.55 mass%, and Na content contained in colloidal silica was 1.7 mass%.

(4) Analysis of stain resistance improving element in plating layer The amount of stain resistance improving element contained in the plating layer thus obtained was analyzed by the following method.

  First, an analytical sample obtained by cutting the electro-Zn-plated steel sheet obtained as described above into a 50 × 50 mm size is prepared and placed in a hydrochloric acid solution diluted twice, until the Zn dissolution reaction is completed. Immersion was performed to obtain an immersion liquid (1). In this example, in order to eliminate the measurement error caused by substitutional precipitation of the stain resistance improving element once dissolved on the steel plate surface as the base material, immediately after the dissolution reaction of Zn, the above sample is pulled up again, It was immersed in a newly prepared hydrochloric acid solution (2-fold diluted solution) for 30 seconds to obtain an immersion solution (2). Thereafter, the immersion liquids (1) and (2) obtained as described above were combined and the volume was adjusted. Then, using an ICP-MS analyzer (PLASMAQUAD type manufactured by VGI), the stain resistance improving element (Cu ) Was analyzed. Cu was analyzed using an ICP analyzer (ICPV-1000 manufactured by Shimadzu Corporation).

(5) Evaluation of stain / stain resistance Each electric Zn-plated steel sheet obtained as described above was placed in a constant temperature and humidity test apparatus having a temperature of 50 ° C. and a relative humidity of 95% or more, and stored for 504 hours. Then, the appearance of the surface was observed, and the stain resistance was evaluated according to the following criteria. In this example, the evaluation criterion “1” or “2” was determined to be acceptable (example of the present invention).
1: When there is no stain stain 2: When there is a slight stain stain 3: When a stain stain occurs

(6) Evaluation of white rust resistance About each electric Zn plating steel plate obtained as mentioned above, the salt spray test prescribed to JIS Z2371 is carried out, and the white rust generation area ratio after 96 hours is based on the following criteria. Judgment was made and white rust resistance was evaluated. In this example, the evaluation standard “◎” or “◯” was determined to be acceptable (example of the present invention).
◎: Less than 5% ○: 5% or more and less than 10% △: 10% or more and less than 50% ×: 50% or more

  These results are also shown in Tables 1 to 3. For reference, Tables 1 to 3 also show the results of an example (No. 1) in which no element is added to the plating layer.

  In Table 3, No. 77, “<0.0001”, and “<1” in 83 indicates that each was below the measurement limit.

  From Tables 1 to 3, it can be considered as follows.

No. 3-7 (examples containing Ni), No. 3 11-14 (Fe ²⁺ containing example), No. 18-20 (Fe ³⁺ containing example), No. 23-28 (examples containing Cr), No. 32-35 (examples containing Na), No. 38-42 (Si containing example), No. 46-49 (Sn containing example), No. 52-56 (Cu containing example), No. 59-62 (Co-containing example), No. 66-69 (examples containing W), No. 72-75 (In-containing example), No. 78-81 (Cd-containing example), No. 84-87 (Ag containing example), No. Nos. 90 to 93 (Ir-containing examples) are examples of the present invention in which the addition amount of the stain resistance improving element in the plating solution and the plating layer satisfies the scope of the present invention. Compared with 1 (no element added), a non-chromate electric Zn-plated steel sheet excellent in both stain resistance and white rust resistance was obtained.

In contrast, no. No. 2 is an example in which the Ni content in the plating solution and the plating layer is low. Nos. 9 and 10 are examples having a low Fe ²⁺ content. Nos. 16 and 17 are examples in which the content of Fe ³⁺ is low. No. 22 is an example with a low Cr content, No. 22 Nos. 30 and 31 are examples in which the Na content is low. No. 37 is an example with a low Si content. Nos. 44 and 45 are examples in which the Sn content is low. No. 51 is an example having a low Cu content. No. 58 is an example having a low Co content. No. 65 is an example having a small W containing layer, No. 71 is an example in which the content of In is low. No. 77 is an example having a low Cd content. No. 82 is an example in which the content of Ag is low. No. 89 is an example in which the content of Ir is low. Compared to 1 (no element added), stain resistance was reduced.

  On the other hand, no. No. 8 is an example in which the Ni content in the plating solution and the plating layer is large. No. 29 is an example with a high Cr content, No. 29. No. 36 is an example with a high Na content, No. 36. No. 43 is an example having a large Si content, No. 43. No. 50 is an example having a high Sn content, No. 50. No. 64 is an example having a high Co content, No. 64. No. 70 is an example with many W-containing layers, No. 70. No. 76 is an example with a large In content, No. 76. No. 82 is an example having a high Cd content. No. 94 is an example having a large Ir content. Compared to 1 (no additive), stain stain resistance was good, but white rust resistance was reduced.

No. No. 15 is an example having a high Fe ²⁺ content, No. 15 No. 21 is an example in which the content of Fe ³⁺ is large. No. 43 is an example having a high Si content. As compared with 1 (no additive), stain resistance was reduced. No. 15 and 21 also had reduced white rust resistance.

Example 2
In this example, the effect of improving stain resistance by adding a silane coupling agent was examined. Here, as shown below, non-chromate electric Zn-plated steel sheets having three types of resin films with different mixing ratios of resin components and colloidal silica were produced, and the influence of the silane coupling agent on each non-chromate electric Zn-plated steel sheet I investigated.

(No. 95-98)
In Example 1 described above, the carboxyl group-containing polyurethane resin aqueous solution, ethylene-acrylic acid copolymer aqueous dispersion, colloidal silica (mixing ratio = 5 parts by mass: “(1-3) Preparation of resin aqueous solution”). 25 parts by mass: 70 parts by mass) In addition to adding a silane coupling agent within the range of 0, 10 parts by mass, 20 parts by mass, and 30 parts by mass, as shown in Table 4, for 100 parts by mass in total. Produced a resin film in the same manner as in Example 1.

  Further, in the above-mentioned “(2) Preparation of electro-Zn plated steel sheet” in Example 1, the electro-Zn was performed in the same manner as in Example 1 except that a plating solution containing all the elements shown in Table 5 was used. A plated steel sheet was produced. Each element described in Table 5 is added in the form described in Example 1 described above.

  Subsequently, a non-chromate electric Zn-plated steel sheet was produced in the same manner as in Example 1, and stain resistance and white rust resistance were evaluated.

(No. 99-102)
In Example 1 described above, sodium hydroxide was not added in "(1-2) Preparation of ethylene-unsaturated carboxylic acid copolymer aqueous dispersion", and "(1-3) Resin aqueous liquid". As the colloidal silica in “Preparation of”, “ST-AK” manufactured by Nissan Chemical Industries, Ltd., and a carboxyl group-containing polyurethane resin aqueous solution, an ethylene-acrylic acid copolymer aqueous dispersion (containing no Na), The compounding ratio of the colloidal silica is 5 parts by mass: 30 parts by mass: 65 parts by mass. A resin film was prepared in the same manner as in Example 1 except that it was added within the range of 30 parts by mass.

  Further, in the above-mentioned “(2) Preparation of electro-Zn plated steel sheet” in Example 1, the electro-Zn was performed in the same manner as in Example 1 except that a plating solution containing all the elements shown in Table 5 was used. A plated steel sheet was produced. Each element described in Table 5 is added in the form described in Example 1 described above.

  Subsequently, a non-chromate electric Zn-plated steel sheet was produced in the same manner as in Example 1, and stain resistance and white rust resistance were evaluated.

(No. 103-106)
In Example 1 mentioned above, 5.1 mass% of NaOH was added as a colloidal silica in “(1-3) Preparation of aqueous resin liquid” for the purpose of improving strength in “ST-XS” manufactured by Nissan Chemical Industries, Ltd. The blended ratio of the added carboxyl group-containing polyurethane resin aqueous solution, ethylene-acrylic acid copolymer aqueous dispersion, and colloidal silica was 6 parts by mass: 34 parts by mass: 60 parts by mass, and the total amount was 100. As shown in Table 4, the resin film was formed in the same manner as in Example 1 except that the silane coupling agent was added within the range of 0, 10 parts by mass, 20 parts by mass, and 30 parts by mass with respect to parts by mass. Was made.

  Further, in the above-mentioned “(2) Preparation of electro-Zn plated steel sheet” in Example 1, the electro-Zn was performed in the same manner as in Example 1 except that a plating solution containing all the elements shown in Table 5 was used. A plated steel sheet was produced. Each element described in Table 5 is added in the form described in Example 1 described above.

  Subsequently, a non-chromate electric Zn-plated steel sheet was produced in the same manner as in Example 1, and stain resistance and white rust resistance were evaluated.

These results are also shown in Table 4.
In Table 4, the Na content contained in the resin component and colloidal silica constituting the resin film, and the Na content contained in the resin film are also shown.

  As shown in Table 4, when the silane coupling agent was added within the preferred range of the present invention, all of the above characteristics increased as compared with the case where no silane coupling agent was added. In addition, in the example which added 30 mass parts of silane coupling agents, since the process liquid gelatinized and it was not able to apply | coat on a plating layer, the external appearance was not able to be evaluated.

1A shows No. 1 of Example 1. FIG. It is a photograph of 2. 1B shows No. 1 of Example 1. 4 is a photograph. 1C shows No. 1 of Example 1. FIG. 6 pictures.

Claims (4)

It is an electric Zn plated steel sheet provided with a resin film substantially free of Cr on the electric Zn plated layer and containing Na of 0.05 to 5% (% means mass%, hereinafter the same). And
The electric Zn plating layer is , in terms of atoms, Ni: 60 to 6000 ppm (ppm means mass ppm, hereinafter the same), Fe: 60 to 600 ppm, Cr: 0.5 to 5 ppm, Mo: 30 to 500 ppm, Sn : 0.6 to 20 ppm, Cu: 8 to 3000 ppm, Cd: 0.0001 to 0.02 ppm, Ag: 1.0 to 400 ppm, Si: 30 to 2000 ppm, Co: 0.0003 to 0.3 ppm, In: 0 An electro-Zn-plated steel sheet excellent in stain resistance, characterized by containing within a range of 1 to 30 ppm, Ir: 0.01 to 10 ppm, and W: 0.1 to 50 ppm.   The electric Zn-plated steel sheet according to claim 1, wherein the resin film contains a carboxyl group-containing resin and a Si-based inorganic compound.   The electric Zn-plated steel sheet according to claim 2, wherein the resin film further contains a silane coupling agent. (1) Ni: 20 to 2000 ppm, Fe ²⁺ : 50 to 5000 ppm, Fe ³⁺ : 50 to 5000 ppm, Cr: 5 to 2000 ppm, Mo: 50 to 2000 ppm, Sn: 0.05 to 20 ppm, Cu: 0.05 to 50 ppm Cd: 0.05-5 ppm, Ag: 0.05-5 ppm, Si: 20-2000 ppm, Co: 0.05-50 ppm, In: 0.5-50 ppm, Ir: 0.05-5 ppm, and W: Performing electro-Zn plating using an acidic plating solution containing 0.5 to 50 ppm;
(2) forming a resin film containing 0.05 to 5% by mass of Na;
A method for producing an electro-Zn-plated steel sheet having excellent stain and dirt resistance, characterized by comprising