JP3454908B2 - Cosmetics - Google Patents

Cosmetics

Info

Publication number
JP3454908B2
JP3454908B2 JP04490994A JP4490994A JP3454908B2 JP 3454908 B2 JP3454908 B2 JP 3454908B2 JP 04490994 A JP04490994 A JP 04490994A JP 4490994 A JP4490994 A JP 4490994A JP 3454908 B2 JP3454908 B2 JP 3454908B2
Authority
JP
Japan
Prior art keywords
mica titanium
coated
powder
iron oxide
coated mica
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP04490994A
Other languages
Japanese (ja)
Other versions
JPH07228509A (en
Inventor
康明 伊藤
尚紀 坂谷
Original Assignee
有限会社野々川商事
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 有限会社野々川商事 filed Critical 有限会社野々川商事
Priority to JP04490994A priority Critical patent/JP3454908B2/en
Publication of JPH07228509A publication Critical patent/JPH07228509A/en
Application granted granted Critical
Publication of JP3454908B2 publication Critical patent/JP3454908B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】本発明は皮膚に使用する化粧料に
関する。さらに詳しくは、顔面部で陰影をつけることを
目的とするメイクアップ化粧料に関する。
FIELD OF THE INVENTION The present invention relates to a cosmetic for use on the skin. More specifically, the present invention relates to a makeup cosmetic for the purpose of creating a shade on the face.

【0002】[0002]

【従来の技術】顔を美しくみせるために、化粧方法の1
つとして明度差をつけてより立体的にみせることがあげ
られる。これまで、顔に明度差をつけるには次のような
方法で行われてきた。顔面において凸にみせたい部位に
は明度の高い化粧料を塗布し、凹にみせたい部位には明
度の低い化粧料を塗布してきた。このように顔をより立
体的にみせるためには数種の化粧料を使用しなくてはな
らず、又、かなり高度なメイクテクニックが必要であ
る。
2. Description of the Related Art To make a face look beautiful, one of makeup methods
One of them is to add a difference in brightness to make it look more three-dimensional. Up to now, the following methods have been used to make the face different in brightness. We have applied high-brightness cosmetics to the parts of the face that are desired to be convex, and low-brightness cosmetics to the parts that are desired to be concave. In order to make the face look more three-dimensional in this way, several kinds of cosmetics must be used, and a fairly sophisticated makeup technique is required.

【0003】これまで、アルミニウム末は化粧品原料と
して知られてはいるが配合すると化粧料自体がくすんだ
きたない色になり商品価値がなくなってしまう為、配合
料も微量であるのが現状であった。又、アルミニウム末
を配合することにより関単に立体感が出せることは全く
知られていなかった。
Up to now, aluminum powder has been known as a raw material for cosmetics, but when it is blended, the cosmetic itself becomes dull color and loses its commercial value. It was Further, it has not been known at all that a three-dimensional effect can be easily obtained by adding aluminum powder.

【0004】[0004]

【発明が解決しようとする課題】これまで顔面に明暗を
つけるために数種類の化粧料を使用し、手間やテクニッ
クが必要であった。しかし、一種類の化粧料で明暗を付
けることができれば、幾つもの化粧料を使用する必要は
なくなる。又、明暗の異なる化粧料を隣どうしに塗布す
るときにできる境目がなくなる。そのため、ぼかしとい
ったような化粧テクニックがいらなくなり、容易に明暗
をつけることができる。
[Problems to be Solved by the Invention] Up to now, several kinds of cosmetics have been used to lighten and darken the face, and labor and technique have been required. However, if it is possible to add light and shade with one kind of cosmetics, it is not necessary to use many kinds of cosmetics. In addition, there is no boundary between cosmetics having different lightness and darkness applied to each other. Therefore, makeup techniques such as blurring are not needed, and it is possible to easily add contrast.

【0005】本発明は、顔面に塗布することにより、明
暗をつけることを目的とする。
The object of the present invention is to make light and dark by applying it to the face.

【0006】[0006]

【課題を解決するための手段】すなわち、本発明はテク
ニックが必要でなく簡単に立体感を出すためにアルミニ
ウム末を配合することを試みた。
That is, the present invention has attempted to blend aluminum powder in order to easily give a three-dimensional effect without requiring a technique.

【0007】アルミニウム末は光を当てた時、正反射の
割合が高い。アルミニウム末配合化粧料を塗布すると、
顔を正面からみた場合、頬や目尻の様な部分は光の反射
が少ないため暗くみえ、奥に引っ込んだ様に見える。そ
して瞼の中央や頬骨辺りでは光の反射が多いため明るく
なり、飛び出した様に見える。そして、顔全体で見ると
顔の凹凸がはっきりして立体感のある美しい顔立ちにな
る。
Aluminum powder has a high proportion of specular reflection when exposed to light. Applying aluminum powder mixed cosmetics,
When you look at your face from the front, parts such as the cheeks and outer corners of the eyes look dark because there is little reflection of light, and it looks like you are recessed. And since there is a lot of reflection of light in the center of the eyelids and around the cheekbones, it becomes bright and looks like it has popped out. And when you look at the whole face, the unevenness of the face becomes clear and it becomes a beautiful feature with a three-dimensional effect.

【0008】しかし、アルミニウム末を未処理のまま配
合すると、化粧料の外観色や塗布色において彩度の低い
くすんだ色となってしまう。化粧料としては、アルミニ
ウム末を配合しても色調の鮮やかさを有する必要性があ
る。この点を発明者等は鋭意研究を行った結果、アルミ
ニウム末を板状無機粉体に被覆することにより、その被
覆粉体を配合することで顔を立体的にみせ、且つ美しく
みせ、又、顔面塗布時の色の鮮やかさを保つことができ
る化粧料を完成した。本発明に使用されるアルミニウム
末で被覆された無機粉体は完全に表面を覆われていない
ため、無機粉体自体の色調が損なわれることがない。つ
まり、本発明の粉体を化粧料に配合すれば、化粧料の鮮
やかさを保ったままアルミニウム末の配合が可能となる
ことを見い出し本発明を完成した。
[0008] However, if the aluminum powder is blended as it is, the appearance color and the coating color of the cosmetic material will be a dull color with low saturation. As a cosmetic, it is necessary to have a vivid color tone even if aluminum powder is mixed. As a result of the inventors' earnest research on this point, the aluminum powder is coated on the plate-like inorganic powder to make the face three-dimensionally and beautifully by blending the coating powder. We have completed a cosmetic that can maintain the vividness of colors when applied to the face. Since the surface of the inorganic powder coated with the aluminum powder used in the present invention is not completely covered, the color tone of the inorganic powder itself is not impaired. That is, when the powder of the present invention was blended with a cosmetic, it was possible to blend aluminum powder while maintaining the vividness of the cosmetic, and completed the present invention.

【0009】以下に本発明の構成について述べる。本発
明の化粧料は、皮膚に使用するメイクアップ化粧料でフ
ァンデーション、パウダー、頬紅、アイシャドウ、アイ
ブロウ、口紅等がある。
The structure of the present invention will be described below. The cosmetics of the present invention are makeup cosmetics used on the skin and include foundations, powders, blushers, eye shadows, eyebrows, lipsticks and the like.

【0010】本発明で用いられるアルミニウム末を無機
粉体に被覆した粉体(以下アルミニウム処理粉体と略
す)とは 、板状無機粉体に機械的な力によりアルミニ
ウム末を被覆させたものである。アルミニウム末の粒径
は、1〜30μmのものが好ましい。例えば、化粧品原
料基準原料規格(以下粧原基と略す)のアルミニウム末
等である。板状無機粉体とは、雲母チタン、化粧品種別
許可基準1993(厚生省薬務局審査課)記載の、カル
ミン被覆雲母チタン,カルミン・コンジョウ被覆雲母チ
タン,黒酸化鉄被覆雲母チタン,黒酸化鉄・カルミン被
覆雲母チタン,黒酸化鉄・コンジョウ被覆雲母チタン,
コンジョウ被覆雲母チタン,コンジョウ・酸化クロム被
覆雲母チタン,酸化クロム被覆雲母チタン,ベンガラ被
覆雲母チタン,ベンガラ・カルミン被覆雲母チタン,ベ
ンガラ・黒酸化鉄・コンジョウ被覆雲母チタン,ベンガ
ラ・コンジョウ被覆雲母チタン,ベンガラ・黒酸化鉄被
覆雲母チタン、その他では、化粧品原料基準外成分規格
1993追補案(厚生省薬務局審査課)記載の、黄酸化
鉄被覆雲母チタン,黄酸化鉄・カルミン被覆雲母チタ
ン,黄酸化鉄・コンジョウ被覆雲母チタンである。
The powder obtained by coating the inorganic powder with the aluminum powder used in the present invention (hereinafter referred to as "aluminum-treated powder") is a plate-shaped inorganic powder coated with the aluminum powder by mechanical force. is there. The particle size of the aluminum powder is preferably 1 to 30 μm. For example, it is an aluminum powder or the like according to the raw material standard for cosmetics (hereinafter abbreviated as cosmetics base). Plate-shaped inorganic powder is mica titanium, classified by makeup type
Cal according to permission standard 1993 (Ministry of Health and Welfare Pharmaceutical Affairs Bureau examination section)
Min Coated Mica Titanium, Carmine Konjou Coated Mica Chi
Tan, black iron oxide coated mica titanium, black iron oxide / carmine coating
Mica Titanium, Black Iron Oxide / Conju Coated Mica Titanium,
Konjau-coated mica titanium, Konjou-chromium oxide coating
Mica mica titanium, chromium oxide coated mica titanium, red iron oxide coating
Mica Titanium, Bengala Carmine Coated Mica Titanium, B
Ngara, black iron oxide, konjau coated mica titanium, benga
La Kongou coated mica titanium, red iron oxide, black iron oxide coating
In case of mica mica titanium and others, non-standard ingredients for cosmetics
Yellow oxidation described in 1993 Supplement (Ministry of Health and Welfare Pharmaceutical Affairs Bureau Examination Division)
Iron coated mica titanium, yellow iron oxide / carmine coated mica chita
And yellow iron oxide and konjac-coated mica titanium.

【0011】本発明に使用されるアルミニウム末の量は
処理粉体全重量に対して、好ましくは1〜30重量%で
あり、更に好ましくは2〜20重量%である。1重量%
未満では本発明の効果が期待できない場合があり、30
重量%以上では、板状無機粉体がアルミニウム末によっ
て完全に被覆されてしまうため彩度の低い粉体となり、
その結果満足のいく色調が得られなくなる。また、本発
明で用いられる板状無機粉体の粒子の大きさは、特に限
定されないが好ましくは、10〜100μmであり、更
に好ましくは20〜50μmである。10μm未満では
アルミニウム末の被覆がうまく行われなく、100μm
を超えると肌に塗布した際に、ざらつき感があり好まし
くない。又、本発明のアルミニウム処理粉体の化粧料へ
の配合量は、1〜60重量%であり、好ましくは5〜5
0重量%である。60重量%以上では、ざらついた使用
感の化粧料となってしまう。1重量%以下では効果が期
待できない。
The amount of aluminum powder used in the present invention is preferably 1 to 30% by weight, more preferably 2 to 20% by weight, based on the total weight of the treated powder. 1% by weight
If it is less than 30%, the effect of the present invention may not be expected.
If it is more than wt%, the plate-like inorganic powder will be completely covered by the aluminum powder, resulting in a powder with low saturation,
As a result, a satisfactory color tone cannot be obtained. Further, the particle size of the plate-like inorganic powder used in the present invention is not particularly limited, but is preferably 10 to 100 μm, and more preferably 20 to 50 μm. If the thickness is less than 10 μm, the coating of aluminum powder is not performed well,
If it exceeds the range, it is not preferable because it has a rough feeling when applied to the skin. The content of the aluminum-treated powder of the present invention in cosmetics is 1 to 60% by weight, preferably 5 to 5%.
It is 0% by weight. If it is 60% by weight or more, the resulting cosmetic composition has a rough feel. If it is less than 1% by weight, no effect can be expected.

【0012】本発明のアルミニウム処理粉体の製造方法
は、特に限定されないが、例えば、アルミニウム末と板
状無機粉体を、乾式で混合する方法である。この方法に
よって無機粉体の表面にアルミニウム末が均一に付着し
た粉体が製造される。混合装置としては、例えば、各種
ボールミル,乳鉢,らい潰器,ミキサーなどがある。
The method for producing the aluminum-treated powder of the present invention is not particularly limited, but is, for example, a method in which the aluminum powder and the plate-like inorganic powder are dry-mixed. By this method, a powder in which aluminum powder is uniformly attached to the surface of the inorganic powder is manufactured. Examples of the mixing device include various ball mills, mortars, grinders, mixers, and the like.

【0013】本発明の化粧料には上記に加えて、配合す
る化粧料原料としては特に制約はなく、例えば、油剤、
界面活性剤、顔料、増粘剤、染料、香料、栄養剤、ビタ
ミン、保湿剤、抗酸化剤、着色剤、紫外線吸収剤等を配
合してもよい。
In addition to the above, the cosmetic material of the present invention is not particularly limited as a raw material for the cosmetic material to be blended.
You may mix | blend a surface active agent, a pigment, a thickener, a dye, a fragrance | flavor, a nutrient, a vitamin, a moisturizer, an antioxidant, a coloring agent, an ultraviolet absorber, etc.

【0014】[0014]

【実施例】次に実施例によって、本発明をさらに詳細に
説明する。尚、配合量は重量%である。
By the following Examples, illustrate the invention in more detail. The blending amount is% by weight.

【0015】 アイシャドウ 実施例−1 比較例−1 比較例−2 (1)赤色226号 4.0部 4.0部 4.0部 (2)コンジョウ被覆雲母チタン − 17.0 20.0 (40μm) (3)アルミニウム末(10μm) − 3.0 − (4)アルミニウム処理粉体 20.0 − − (5)マイカ 5.0 5.0 5.0 (6)タルク 20.9 20.9 20.9 (7)セリサイト 40.0 40.0 40.0 (8)酸化チタン 5.0 5.0 5.0 (9)スクワラン 3.0 3.0 3.0 (10)リンゴ酸ジイソステアリル 2.0 2.0 2.0 (11)香料 0.1 0.1 0.1 (4は、粒子径が40μmのコンジョウ被覆雲母チタン
に対し、粒子径が10μmのアルミニウム末を15重量
%、ミキサーで混合して被覆させた粉体)
Eye Shadow Example- 1 Comparative Example-1 Comparative Example-2 (1) Red No. 226 4.0 parts 4.0 parts 4.0 parts (2) Konjou-coated mica titanium-17.0 20.0 ( 40 μm) (3) Aluminum powder (10 μm) − 3.0 − (4) Aluminum treated powder 20.0 − − (5) Mica 5.0 5.0 5.0 5.0 (6) Talc 20.9 20.9 20.9 (7) Sericite 40.0 40.0 40.0 (8) Titanium oxide 5.0 5.0 5.0 5.0 (9) Squalane 3.0 3.0 3.0 3.0 (10) Dimalate Isostearyl 2.0 2.0 2.0 2.0 (11) Perfume 0.1 0.1 0.1 0.1 (4 is 15 parts by weight of aluminum powder having a particle size of 10 μm for titanium mica coated with a particle size of 40 μm. %, Powder coated by mixing with a mixer)

【0016】 アイシャドウ 実施例−2 比較例−3 比較例−4 (1)赤色226号 4.0部 4.0部 4.0部 (2)コンジョウ被覆雲母チタン − 34.0 40.0 (40μm) (3)アルミニウム末(10μm) − 6.0 − (4)アルミニウム処理粉体 40.0 − − (5)マイカ 5.0 5.0 5.0 (6)タルク 20.9 20.9 20.9 (7)セリサイト 20.0 20.0 20.0 (8)酸化チタン 5.0 5.0 5.0 (9)スクワラン 3.0 3.0 3.0 (10)リンゴ酸ジイソステアリル 2.0 2.0 2.0 (11)香料 0.1 0.1 0.1 (4は、粒子径が40μmのコンジョウ被覆雲母チタン
に対し、粒子径が10μmのアルミニウム末を15重量
%、ミキサーで混合して被覆させた粉体)
Eye Shadow Example- 2 Comparative Example-3 Comparative Example-4 (1) Red No. 226 4.0 parts 4.0 parts 4.0 parts (2) Konjou coated mica titanium-34.0 40.0 ( 40 μm) (3) Aluminum powder (10 μm) − 6.0 − (4) Aluminum treated powder 40.0 − − (5) Mica 5.0 5.0 5.0 5.0 (6) Talc 20.9 20.9 20.9 (7) Sericite 20.0 20.0 20.0 (8) Titanium oxide 5.0 5.0 5.0 5.0 (9) Squalane 3.0 3.0 3.0 (10) Dimalate Isostearyl 2.0 2.0 2.0 2.0 (11) Perfume 0.1 0.1 0.1 0.1 (4 is 15 parts by weight of aluminum powder with a particle size of 10 μm for titanium mica-coated mica with a particle size of 40 μm. %, Powder coated by mixing with a mixer)

【0017】 アイシャドウ 実施例−3 比較例−5 比較例−6 (1)赤色226号 3.0部 3.0部 3.0部 (2)青色404号 1.0部 1.0部 1.0部 (3)ベンガラ被覆雲母チタン − 7.0 10.0 (60μm) (4)アルミニウム末(15μm) − 3.0 − (5)アルミニウム処理粉体 10.0 − − (6)タルク 25.9 25.9 25.9 (7)セリサイト 50.0 50.0 50.0 (8)酸化チタン 5.0 5.0 5.0 (9)スクワラン 1.0 1.0 1.0 (10)ジメチルシリコン 4.0 4.0 4.0 (11)香料 0.1 0.1 0.1 (5は、粒子径が60μmのベンガラ被覆雲母チタンに
対し、粒子径が15μmのアルミニウム末を30重量
%、らい潰器で摺合わして被覆させた粉体)成分1〜1
0を混合粉砕し、金皿にプレスする。
Eye Shadow Example- 3 Comparative Example-5 Comparative Example-6 (1) Red No. 226 3.0 parts 3.0 parts 3.0 parts (2) Blue No. 404 1.0 parts 1.0 parts 1 0.0 part (3) red iron oxide coated mica titanium-7.0 10.0 (60 μm) (4) aluminum powder (15 μm) -3.0- (5) aluminum-treated powder 10.0- (6) talc 25 9.9 25.9 25.9 (7) Sericite 50.0 50.0 50.0 (8) Titanium oxide 5.0 5.0 5.0 5.0 (9) Squalane 1.0 1.0 1.0 ( 10) Dimethyl silicon 4.0 4.0 4.0 4.0 (11) Perfume 0.1 0.1 0.1 0.1 (5 is a powder of red iron oxide coated with red iron oxide having a particle diameter of 60 μm and an aluminum powder having a particle diameter of 15 μm. 30% by weight, powder coated by rubbing with a crusher) Components 1-1
0 is mixed and ground, and pressed into a gold plate.

【0018】 アイシャドウ 実施例−4 比較例−7比較例−8 (1)赤色226号 3.0部 3.0部 3.0部 (2)青色404号 1.0部 1.0部 1.0部 (3)ベンガラ被覆雲母チタン − 21.0 30.0 (60μm) (4)アルミニウム末(15μm) − 9.0 − (5)アルミニウム処理粉体 30.0 − − (6)タルク 25.9 25.9 25.9 (7)セリサイト 30.0 30.0 30.0 (8)酸化チタン 5.0 5.0 5.0 (9)スクワラン 1.0 1.0 1.0 (10)ジメチルシリコン 4.0 4.0 4.0 (11)香料 0.1 0.1 0.1 (5は、粒子径が60μmのベンガラ被覆雲母チタンに
対し、粒子径が15μmのアルミニウム末を30重量
%、らい潰器で摺合わして被覆させた粉体)成分1〜1
0を混合粉砕し、金皿にプレスする。
Eye Shadow Example- 4 Comparative Example-7 Comparative Example-8 (1) Red No. 226 3.0 parts 3.0 parts 3.0 parts (2) Blue No. 404 1.0 parts 1.0 parts 1 0.0 parts (3) red iron oxide-coated mica titanium-21.0 30.0 (60 μm) (4) aluminum powder (15 μm) -9.0- (5) aluminum-treated powder 30.0 − − (6) talc 25 9.9 25.9 25.9 (7) Sericite 30.0 30.0 30.0 (8) Titanium oxide 5.0 5.0 5.0 5.0 (9) Squalane 1.0 1.0 1.0 ( 10) Dimethyl silicon 4.0 4.0 4.0 4.0 (11) Perfume 0.1 0.1 0.1 0.1 (5 is a powder of red iron oxide coated with red iron oxide having a particle diameter of 60 μm and an aluminum powder having a particle diameter of 15 μm. 30% by weight, powder coated by rubbing with a crusher) Components 1-1
0 is mixed and ground, and pressed into a gold plate.

【0019】実施例1,実施例2,比較例1,比較例
2,比較例3,比較例4を、立体感のある仕上がり,化
粧料の鮮やかさ,塗布した色調の鮮やかさ,そして、総
合評価の4項目について20人の専門パネラーにより判
断した。その結果を表1に示す。
Example 1, Example 2, Comparative Example 1, Comparative Example 2, Comparative Example 3, and Comparative Example 4 were finished with a three-dimensional finish, the vividness of the cosmetic material, the vividness of the applied color tone, and the total. The four items of the evaluation were judged by 20 expert panelists. The results are shown in Table 1 .

【0020】[0020]

【表1】 [Table 1]

【0021】実施例3,実施例4,比較例5,比較例
6,比較例7,比較例8を、立体感のある仕上がり,化
粧料の鮮やかさ,塗布した色調の鮮やかさ,そして、総
合評価の4項目について20人の専門パネラーにより判
断した。その結果を表2に示す。
Example 3, Example 4, Comparative Example 5, Comparative Example 6, Comparative Example 7, and Comparative Example 8 were finished with a three-dimensional finish, the vividness of the cosmetic material, the vividness of the applied color tone, and the total. The four items of the evaluation were judged by 20 expert panelists. The results are shown in Table 2 .

【0022】[0022]

【表2】 [Table 2]

【0023】評価項目は下記に示すようである。 A:立体感のある仕上がり B:化粧料の鮮やかさ C:塗布した色調の鮮やかさ D:総合評価The evaluation items are as shown below. A: 3D finish B: Brightness of cosmetics C: Vividness of applied color tone D: Comprehensive evaluation

【0024】表中の記号は下記の通りである。 (立体感のある仕上がり,総合評価) ◎:20名中16名以上 がよいと判断 ○: 〃 11〜15名 〃 △: 〃 6〜10名 〃 ×: 〃 0〜 5名 〃 (化粧料の鮮やかさ,塗布した色調の鮮やかさ) ◎:20名中16名以上 が鮮やかと判断 ○: 〃 11〜15名 〃 △: 〃 6〜10名 〃 ×: 〃 0〜 5名 〃The symbols in the table are as follows. (Three-dimensional finish, comprehensive evaluation) ◎: determined that 16 or more out of 20 are good ○: 〃 11 to 15 people 〃 △: 6-10 people 〃 ×: 〃 0-5 people 〃 (Vividness of cosmetics, vividness of applied color tone) ◎: 16 or more out of 20 judged to be vivid ○: 〃 11 to 15 people 〃 △: 6-10 people 〃 ×: 〃 0-5 people 〃

【0025】表1及び表2の結果より本発明のアルミニ
ウム処理粉体を化粧料に配合することにより、化粧料の
色調の鮮やかさを損なわず、化粧料を顔面に塗布した場
合、ぼかし等のテクニックなしに陰影をつけ美しく見せ
ることができる。
From the results shown in Tables 1 and 2 , by incorporating the aluminum-treated powder of the present invention into a cosmetic composition, the vividness of the color tone of the cosmetic composition is not impaired, and when the cosmetic composition is applied to the face, there is no blurring. You can add shadows and look beautiful without any technique.

【0026】 以下の実施例により、本発明を更に詳しく
説明するが、実施例に限定されるものではない。
[0026] The present invention will be described in more detail with reference to the following examples.
Although described, the present invention is not limited to the example.

【0027】実施例− 頬紅 (1)カオリン 16.0 部 (2)タルク 15.0 (3)酸化チタン 12.0 (4)ベンガラ 5.0 (5)赤色202号 2.4 (6)アルミニウム処理粉体 40.0 (7)スクワラン 4.0 (8)ジメチルポリシロキサン 4.0 (9)香料 0.1 (10)マイカにて全量を100とする (6は、粒子径が50μmのベンガラ被覆雲母チタンに
対し、粒子径が20μmのアルミニウム末を10重量
%、ミキサーで混合して被覆させた粉体)成分1〜10
を混合粉砕し、金皿にプレスする。実施例−の頬紅
は、鮮やかで顔の立体感をはっきりさせた。
Example- 5 Blusher (1) Kaolin 16.0 parts (2) Talc 15.0 (3) Titanium oxide 12.0 (4) Red iron oxide 5.0 (5) Red No. 202 2.4 (6) Aluminum-treated powder 40.0 (7) Squalane 4.0 (8) Dimethylpolysiloxane 4.0 (9) Fragrance 0.1 (10) The total amount is 100 with mica (6 has a particle diameter of 50 μm Powders obtained by mixing 10% by weight of aluminum powder having a particle diameter of 20 μm with a red iron oxide-coated mica titanium with a mixer and coating the components) Components 1 to 10
Are crushed and pressed into a gold plate. The blusher of Example- 5 had a vivid and clear three-dimensional effect on the face.

【0028】実施例− リップスティック (1)赤色201号 0.4 部 (2)赤色202号 1.2 (3)酸化チタン 1.5 (4)パラフィン 10.0 (5)マイクロクリスタリンワックス 7.0 (6)カルナウバワックス 0.5 (7)ポリエチレン 0.5 (8)メトキシケ皮酸オクチル 1.0 (9)ラノリン 10.0 (10)メチルフェニルポリシロキサン 5.0 (11)オレイルアルコール 1.0 (12)ショ糖脂肪酸エステル 5.0 (13)アルミニウム処理粉体 15.0 (14)香料 0.02 (15)ジペンタエリトリット脂肪酸エステル 5.0 (16)トリイソステアリン酸ジグリセリンにて全量を100とする (13は、粒子径が35μmのカルミン被覆雲母チタン
に対し、粒子径が6μmのアルミニウム末を10重量
%、ボールミルで混合して被覆させた粉体)成分1〜
3,16を三本ローラーで練る。成分4〜12,15を
加熱溶解し前者に加え混合する。成分13,14を加え
均一とする。これを金型に流し込み成型する。実施例−
のリップスティックは、立体感のある魅力的な唇に仕
上げた。
Example 6 Lipstick (1) Red No. 201 0.4 part (2) Red No. 202 1.2 (3) Titanium oxide 1.5 (4) Paraffin 10.0 (5) Microcrystalline wax 7 .0 (6) Carnauba wax 0.5 (7) Polyethylene 0.5 (8) Octyl methoxycinnamate 1.0 (9) Lanolin 10.0 (10) Methylphenyl polysiloxane 5.0 (11) Oleyl alcohol 1.0 (12) Sucrose fatty acid ester 5.0 (13) Aluminum treated powder 15.0 (14) Perfume 0.02 (15) Dipentaerythritol fatty acid ester 5.0 (16) Diglycerin triisostearate The total amount is 100 (13 is carmine coated mica titanium with a particle size of 35 μm, and aluminum powder with a particle size of 6 μm is used. 10 wt%, the powder was coated by mixing in a ball mill) component 1
Knead No. 3, 16 with three rollers. Ingredients 4 to 12 and 15 are melted by heating and added to the former and mixed. Add ingredients 13 and 14 to make uniform. This is poured into a mold and molded. Example-
Lipstick No. 6 has a three-dimensional, attractive lips finish.

【0029】[0029]

【発明の効果】本発明のアルミニウム処理粉体を配合し
た化粧料を用いることにより、ぼかし等の化粧テクニッ
クを用いなくても顔に陰影を付けることが容易にでき
る。そして、美しい仕上がりが得られる。
[Effects of the Invention] By using the cosmetic containing the aluminum-treated powder of the present invention, it is possible to easily shade the face without using a makeup technique such as blurring. And a beautiful finish is obtained.

───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭63−27418(JP,A) 特開 昭63−254169(JP,A) 特開 平1−143821(JP,A) 特開 昭63−126818(JP,A) (58)調査した分野(Int.Cl.7,DB名) A61K 7/00 - 7/50 ─────────────────────────────────────────────────── ─── Continuation of the front page (56) Reference JP-A 63-27418 (JP, A) JP-A 63-254169 (JP, A) JP-A 1-143821 (JP, A) JP-A 63- 126818 (JP, A) (58) Fields surveyed (Int.Cl. 7 , DB name) A61K 7/ 00-7/50

Claims (4)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】雲母チタン,カルミン被覆雲母チタン,カ
ルミン・コンジョウ被覆雲母チタン,黒酸化鉄被覆雲母
チタン,黒酸化鉄・カルミン被覆雲母チタン,黒酸化鉄
・コンジョウ被覆雲母チタン,コンジョウ被覆雲母チタ
ン,コンジョウ・酸化クロム被覆雲母チタン,酸化クロ
ム被覆雲母チタン,ベンガラ被覆雲母チタン,ベンガラ
・カルミン被覆雲母チタン,ベンガラ・黒酸化鉄・コン
ジョウ被覆雲母チタン,ベンガラ・コンジョウ被覆雲母
チタン,ベンガラ・黒酸化鉄被覆雲母チタン,黄酸化鉄
被覆雲母チタン,黄酸化鉄・カルミン被覆雲母チタン,
黄酸化鉄・コンジョウ被覆雲母チタンから選ばれる板状
無機粉体にアルミニウム末を被覆した粉体を配合したこ
とを特徴とするメイクアップ化粧料。
1. Mica titanium, carmine-coated mica titanium, carmine / conju-coated mica titanium, black iron oxide-coated titanium mica, black iron oxide / carmine-coated mica titanium, black iron oxide / conju-coated mica titanium, mosquito-coated mica titanium, Konjaku / Chromium oxide coated mica titanium, Chromium oxide coated mica titanium, Bengala coated mica titanium, Bengala / Carmine coated mica titanium, Bengala / black iron oxide / Conjuu coated mica titanium, Bengala / konjou coated mica titanium, Bengala / black iron oxide coated Mica titanium, yellow iron oxide coated mica titanium, yellow iron oxide / carmine coated mica titanium,
A makeup cosmetic characterized in that a plate-like inorganic powder selected from iron oxide yellow and turquoise coated mica titanium is mixed with powder coated with aluminum powder.
【請求項2】アルミニウム末の粒子径が1〜30μmで
あることを特徴とする請求項1に記載の化粧料。
2. The cosmetic material according to claim 1, wherein the particle size of the aluminum powder is 1 to 30 μm.
【請求項3】板状無機粉体が、コンジョウ処理雲母チタ
ン,カルミン処理雲母チタン,または酸化鉄処理雲母チ
タンから選ばれ、かつ、アルミニウム末の粒子径が1〜
30μmであり1〜30重量%被覆した粉体であること
を特徴とする請求項1のメイクアップ化粧料。
3. The plate-like inorganic powder is selected from turquoise-treated mica titanium, carmine-treated mica titanium, or iron oxide-treated mica titanium, and the aluminum powder has a particle diameter of 1 to 1.
The make-up cosmetic composition according to claim 1, which is a powder having a thickness of 30 μm and coated with 1 to 30% by weight.
【請求項4】アルミニウム末を被覆した粉体を1〜60
重量%配合したことを特徴とする請求項3に記載のメイ
クアップ化粧料。
4. A powder coated with aluminum powder is contained in an amount of 1 to 60.
4. The may according to claim 3, which is blended in a weight percentage.
Makeup cosmetics.
JP04490994A 1994-02-17 1994-02-17 Cosmetics Expired - Fee Related JP3454908B2 (en)