JP3440758B2 - Sealed container - Google Patents
Sealed containerInfo
- Publication number
- JP3440758B2 JP3440758B2 JP16114497A JP16114497A JP3440758B2 JP 3440758 B2 JP3440758 B2 JP 3440758B2 JP 16114497 A JP16114497 A JP 16114497A JP 16114497 A JP16114497 A JP 16114497A JP 3440758 B2 JP3440758 B2 JP 3440758B2
- Authority
- JP
- Japan
- Prior art keywords
- container
- laminated
- sealed
- polypropylene
- container body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は内容物である、未調
理、調理済食品を充填収納する容器本体に、一定のシー
ル強度で蓋材を密封した容器で、そのまま電子レンジ等
で加熱しても破裂することがない密封容器に関するもの
である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a container body in which uncooked and cooked foods, which are the contents, are filled and stored, and a lid member is hermetically sealed with a certain sealing strength. It also relates to a sealed container that does not burst.
【０００２】[0002]
【従来の技術】冷凍食品等を収納する容器として、例え
ば、特公昭５２−４３１５号に示されるように、合成樹
脂をコーティングした板紙からなるブランクを組み立て
た、トレイ状の容器が提案され、実用されている。この
トレイ状容器は、内面に合成樹脂がコーティングされ、
しかもコーナー部で、ブランクの端面が露出しないよう
に、重ね合わさるように折り返して成形するので、液状
物を含む内容物、あるいは浸透性のある内容物に対して
も使用可能であった。2. Description of the Related Art As a container for storing frozen foods, for example, as shown in Japanese Patent Publication No. 52-3415, a tray-shaped container in which a blank made of paperboard coated with a synthetic resin is assembled has been proposed and put into practical use. Has been done. This tray-shaped container is coated with synthetic resin on the inner surface,
In addition, since the blanks are folded and formed so as to be overlapped with each other so that the end faces of the blanks are not exposed at the corners, the blanks can be used for contents containing a liquid substance or contents having permeability.
【０００３】一方、近年、このような紙製のトレイ状容
器に、調理済食品、あるいは半調理食品を充填後、蓋材
で密封し、使用時には、このトレイ状の密封容器をその
まま、電子レンジ、またはオーブンにより加熱、あるい
は加熱調理し、そのまま食器として使用する要求があ
る。そこで、内面に設ける合成樹脂として、耐熱性、ヒ
ートシール性を兼ね備えているホリプロピレンが好適
で、しかも加熱工程に耐えるためには、１００μｍ以上
のフィルムを使用するのが好ましい。On the other hand, in recent years, such a paper tray container is filled with cooked food or semi-cooked food and then sealed with a lid material, and when used, the tray container is used as it is in a microwave oven. Or, it is required to heat it in an oven or cook it and use it as tableware as it is. Therefore, as the synthetic resin provided on the inner surface, polypropylene having both heat resistance and heat sealability is preferable, and in order to withstand the heating step, it is preferable to use a film having a thickness of 100 μm or more.
【０００４】しかし、前記密封容器を電子レンジ加熱す
る場合、密封した蓋材を、容器本体から、一部または全
部剥離しなければならなかった。このように、加熱使用
する前は、密封性が優れ、また使用時には、開封性が優
れていなければならない、いわゆる相反する機能が求め
られていた。However, when the sealed container is heated in a microwave oven, the sealed lid material must be partly or wholly peeled from the container body. As described above, the so-called contradictory functions, which are required to have excellent sealing property before heating and use and excellent opening property at the time of use, have been demanded.
【０００５】また、容器本体として、例えば、実公昭５
１−３１２０２号、実公昭５４−４２８３０号に示され
るように、紙製の外容器の内面に、合成樹脂樹脂フィル
ムを加熱軟化させ、真空成形等の手段により、積層接着
したトレイ状容器が提案されている。このトレイ状容器
は、フランジ部に段差が生じない構造とすることがで
き、密封性の良好な容器として使用可能であった。Further, as the container body, for example, Jitsuko Sho 5
As shown in No. 1-312202 and Japanese Utility Model Publication No. 54-42830, a tray-like container in which a synthetic resin film is softened by heating on the inner surface of an outer container made of paper and laminated and adhered by means such as vacuum forming is proposed. Has been done. This tray-shaped container can be used as a container having a good sealing property because the tray-shaped container can have a structure in which there is no step in the flange portion.
【０００６】また、ポリプロピレン層を内面に用いた容
器本体の、開口を密封する蓋材の内面シール層には、前
記ポリプロピレン層と一定の接着強度を有するプラスチ
ックが使用されていた。一定の接着強度と、剥離性を鑑
みてポリエチレン系樹脂を使用するのが一般的であっ
た。Further, a plastic having a certain adhesive strength with the polypropylene layer has been used for the inner surface sealing layer of the lid member for sealing the opening of the container body using the polypropylene layer on the inner surface. It was common to use a polyethylene-based resin in view of a certain adhesive strength and peelability.
【０００７】[0007]
【発明が解決しようとする課題】このように、容器本体
のポリプロピレン層と、蓋材のシール層のポリエチレン
系樹脂を密封シールした状態で、そのまま加熱、あるい
は加熱調理すると、蒸気が排出されず、破裂する危険が
あるため、加熱前に、蓋材の一部を開封して加熱しなけ
ればならなかった。Thus, if the polypropylene layer of the container body and the polyethylene resin of the sealing layer of the lid material are hermetically sealed and heated or cooked as they are, steam is not discharged, Due to the risk of bursting, a portion of the lid had to be opened and heated before heating.
【０００８】[0008]
【課題を解決するための手段】本発明は、トレイ状容器
本体内に内容物を充填後、蓋材により封緘し密封された
密封容器であって封緘密封状態で加熱あるいは加熱調理
する密封容器において、前記容器本体は、上面が開口
し、かつ開口周縁にフランジを有する紙基材と、その紙
基材の容器内面側にポリプロピレンフィルム単体を積層
した材料、またはその紙基材の容器内面側にポリプロピ
レンフィルムを積層した積層構成の材料からなり、かつ
蓋材の内面にシングルサイト触媒を用いて合成した、ポ
リエチレンまたはエチレン−αオレフィン共重合体のい
ずれかからなる融点が８５℃〜１１０℃のシール層を設
け、前記容器本体のフランジ部に蓋材を、蓋材のシール
層の融点以上、かつ容器本体のポリプロピレンフィルム
の融点以下の温度でヒートシールして密封したことを特
徴とする密封容器である。According to the present invention, a tray-shaped container body is filled with contents and then sealed and sealed by a lid member .
Heated or cooked in a sealed container and sealed.
In a sealed container which, the container body includes a paper substrate having a flange upper surface is opened, and the opening edge, the paper
Laminated polypropylene film alone on the inner surface of the base material container
On the inside surface of the container of the
A seal having a melting point of 85 ° C. to 110 ° C., which is made of a material having a laminated structure in which ren films are laminated and which is synthesized by using a single-site catalyst on the inner surface of the lid material and is made of either polyethylene or an ethylene-α olefin copolymer. A layer is provided, and a lid material is attached to the flange of the container body, and the lid material is sealed.
A hermetically sealed container characterized by being heat-sealed and sealed at a temperature not lower than the melting point of the layer and not higher than the melting point of the polypropylene film of the container body.
【０００９】また、本発明は、前記容器本体が、紙を基
材とした外容器の内面にポリプロピレンフィルム単体を
積層した前記積層構成の材料、または容器内面側にポリ
プロピレンフィルムを積層した前記積層構成の材料を、
真空成形、または真空成形と圧空成形の併用により一体
化した密封容器である。また、本発明は、前記ポリプロ
ピレンフィルムが、ポリプロピレン単体、またはポリプ
ロピレンにエチレン系樹脂を混合した、いずれかの樹脂
からなる密封容器である。また、本発明は、前記蓋材の
シール層が共押出しフィルムである密封容器。Further, in the present invention, the container body comprises a polypropylene film simple substance on the inner surface of an outer container made of paper as a base material.
The material of the laminated constitution that is laminated, or the inner surface of the container
The material of the laminated constitution in which propylene films are laminated,
It is a sealed container that is integrated by vacuum forming or by combining vacuum forming and pressure forming. The present invention also relates to the above polypro
The pyrene film is a sealed container made of either polypropylene alone or a mixture of polypropylene and ethylene resin. Further, the present invention provides the lid member
A sealed container in which the sealing layer is a co-extruded film.
【００１０】[0010]
【発明の実施の形態】以下本発明の実施の形態につき説
明する。本発明は図１に示すように、トレイ状の容器本
体１０の開口を蓋材２０により密封した密封容器であ
る。トレイ状の容器本体１０は、矩形状の底面板１の四
辺に上方に向かって外側に傾斜して対向する一対の側面
板２、２と、もう一対の側面板３、３を備える。そし
て、各々側面板２、２の側辺に逆２等辺三角形状の三角
コーナー板６、及び重合片７を張り出し設け、該重合片
７を側板３、３の側縁内面に重ねることで、前記三角コ
ーナー板により形成されるコーナー部を備える。また、
前記側面板２、２の上端に外側に向かって水平に張り出
すフランジ４を設け、前記側板３の上端に外側に向かっ
て水平に張り出すフランジ５を設け、該フランジ５の両
側に、前記三角コーナー板６の上方で外側に向かって水
平に張り出すフランジ８を設けてなる。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described below. The present invention is, as shown in FIG. 1, a sealed container in which the opening of a tray-shaped container body 10 is sealed with a lid member 20. The tray-shaped container body 10 is provided with a pair of side surface plates 2 and 2 facing the four sides of a rectangular bottom plate 1 and inclined upward toward the outside, and another pair of side surface plates 3 and 3. Then, an inverted isosceles triangular triangular corner plate 6 and an overlapped piece 7 are provided on each side of the side plates 2 and 2, and the overlapped piece 7 is overlapped on the inner surface of the side edge of each of the side plates 3 and 3. A corner portion formed by a triangular corner plate is provided. Also,
A flange 4 is provided at the upper ends of the side plates 2 and 2 so as to horizontally project outward, and a flange 5 is provided at the upper end of the side plate 3 so as to horizontally project outward, and the triangles are provided on both sides of the flange 5. A flange 8 is provided above the corner plate 6 so as to horizontally project outward.
【００１１】そして、前記紙製トレイ状容器本体１０の
内面に、真空成形、または真空成形と圧空成形の併用に
よって合成樹脂フィルム４０を積層接着し、一体化す
る。さらに、前記トレイ状容器１０の、前記底面板１、
側面板２、２と側面板３、３、三角コーナー板６、フラ
ンジ４、５、及び８の外側の全面、または部分的に印刷
層３０を設けたものである。Then, the synthetic resin film 40 is laminated and adhered to the inner surface of the paper tray-shaped container body 10 by vacuum forming or by a combination of vacuum forming and pressure forming. Furthermore, the bottom plate 1 of the tray-shaped container 10,
The printing layer 30 is provided on the entire outer surface of the side plates 2 and 2, the side plates 3 and 3, the triangular corner plate 6, the flanges 4, 5 and 8 or partially.
【００１２】また、トレイ状容器本体は、図４、図５に
示すように、三角コーナー板６を設けなくてもよい。ト
レイ状容器本体の剛度を得るために、隣接する側板に重
なる重合片を張り出し設けることは必要である。また、
重合片の重ね合わせは、隣接する側板の内面にする必要
がある。この状態にすることで、合成樹脂フィルムを積
層接着し、一体化した時にこの重合片も合成樹脂フィル
ムにより接着されるためである。さらに、トレイ状容器
本体は、図５に示すように８角形トレー容器のような、
多角形トレーとすることもできる。Further, as shown in FIGS. 4 and 5 , the tray-shaped container body may not be provided with the triangular corner plate 6. In order to obtain the rigidity of the tray-shaped container body, it is necessary to overhang the overlapping polymer pieces on the adjacent side plates. Also,
The superposition of polymer pieces should be on the inner surface of the adjacent side plates. This is because, in this state, when the synthetic resin films are laminated and adhered and integrated , the polymer pieces are also adhered by the synthetic resin film. Further, the tray-shaped container main body has a structure such as an octagonal tray container as shown in FIG.
It can also be a polygonal tray.
【００１３】一方、トレイ状容器本体の開口部を密封す
る蓋材２０は、前記トレイ状容器１０のフランジ４、
５、及び８に合致する形状、寸法の蓋材であり、内面に
シール層を積層接着し、外面の全面、または適宜部分に
印刷層３０を設けたものである。蓋材２０の形状も前記
トレー状容器本体に応じて種々の形状とすることが可能
である。On the other hand, the lid member 20 for sealing the opening of the tray-shaped container main body is composed of the flange 4 of the tray-shaped container 10,
The lid material has a shape and size that match 5 and 8, and a sealing layer is laminated and adhered on the inner surface, and a printing layer 30 is provided on the entire outer surface or at an appropriate portion. The shape of the lid member 20 can be various shapes according to the tray-shaped container body.
【００１４】そして、前記トレイ状容器本体１０に食品
を充填した後、該トレイ状容器本体１０のフランジ４、
５、及び８に、前記蓋材２０を重ね、両部材の内面同士
を熱融着により封止して密封して使用する。After filling the tray-shaped container body 10 with food, the flange 4 of the tray-shaped container body 10,
The lid member 20 is overlaid on 5 and 8, and the inner surfaces of both members are sealed by heat fusion and sealed before use.
【００１５】本発明は、図３に示す様にトレイ状容器本
体１０、蓋材２０の内面にのみに合成樹脂フィルム４０
を設ける必要がある。これは、電子レンジ、オーブン等
により、容器を加熱すると基材である紙５０の水分が沸
騰蒸発し、紙の表面にでてくるという現象がおこる。こ
のことにより、紙の両面に合成樹脂フィルムを設ける
と、この蒸気により紙と合成樹脂フィルムとの間の接着
を剥がしてしまうという問題が発生する。この時、合成
樹脂フィルムとして融点が低いものを配置すると、この
合成樹脂フィルム自体の溶融と、前記蒸気の噴出により
合成樹脂フィルムが発泡してしまうという問題が発生す
る。According to the present invention, as shown in FIG. 3, the synthetic resin film 40 is provided only on the inner surfaces of the tray-shaped container body 10 and the lid member 20.
Need to be provided. This occurs when the container 50 is heated by a microwave oven, an oven or the like, the water content of the paper 50, which is the base material, evaporates by boiling and appears on the surface of the paper. As a result, when the synthetic resin film is provided on both sides of the paper, the vapor causes a problem of peeling the adhesion between the paper and the synthetic resin film. At this time, if a synthetic resin film having a low melting point is arranged, there arises a problem that the synthetic resin film itself is melted and the synthetic resin film is foamed by the jetting of the vapor.
【００１６】そこで、本発明は、紙基材を用いる場合
は、内面にのみ合成樹脂フィルムを設け、外面には設け
ず、蒸気の放出を阻害しないようにしている。 また、
外側にも合成樹脂フィルムを配置する場合、このような
蒸気の放出を阻害しない他の手段としては、微細貫通孔
を有するなど、高い通気性の合成樹脂フィルムを積層接
着することにより可能である。Therefore, in the present invention, when a paper base material is used, the synthetic resin film is provided only on the inner surface and not on the outer surface so that vapor emission is not hindered. Also,
When arranging the synthetic resin film on the outer side, another means that does not impede such vapor emission can be achieved by laminating and adhering synthetic resin films having high air permeability such as having fine through holes.
【００１７】前記トレイ状容器本体１０、蓋材２０に用
いる紙基材５０としては、適度な剛度を有する（例え
ば、坪量２００〜５００ｇ／ｍ2 ）はもちろんのこと、
電子レンジ、オーブン等にによる加熱に対する耐性を持
たせるために、加熱による臭気の発生がないか、または
低い材質を使用する必要がある。この要求を満たす材質
としてはバージンパルプにより製紙したものが適してい
る。また加熱調理により発生する水分の付着を防止する
必要から耐水性、端面からの水分の吸収性のない、また
は低い材質を用いる必要がある。この要求を満たす材質
として、一般にカップ原紙と呼ばれるものが適してい
る。As the paper base material 50 used for the tray-shaped container body 10 and the lid member 20, it is needless to say that the paper base material 50 has an appropriate rigidity (for example, a basis weight of 200 to 500 g / m 2 ).
In order to have resistance to heating by a microwave oven, oven, etc., it is necessary to use a material that does not generate odor due to heating or has a low odor. As a material satisfying this requirement, paper made from virgin pulp is suitable. Further, since it is necessary to prevent the adhesion of water generated by heating and cooking, it is necessary to use a material that is water resistant and has no or low absorption of water from the end surface. A material generally called a cup base paper is suitable as a material satisfying this requirement.
【００１８】これらの要求品質は、本密封紙製容器を冷
蔵庫等で冷凍，冷蔵保存した時、また、その保存状態か
ら消費者が購入し持ち帰るまでの間におこる容器表面の
結露による容器の劣化防止の目的からも有効なものとな
る。また、必要に応じて耐油性を持たせることもでき
る。さらに、開封時に蓋体との剥離強度において、紙剥
けのしない材質である必要がある。These required qualities are the deterioration of the container due to dew condensation on the surface of the container when the sealed paper container is frozen or refrigerated and stored in a refrigerator or the like, and between the storage state and the time when the consumer purchases and takes it home. It is also effective for the purpose of prevention. Also, oil resistance can be imparted if necessary. Further, it is necessary that the material is a material that does not peel off the paper in terms of the peel strength with the lid when opening.
【００１９】前記トレイ状容器本体１０に用いる合成樹
脂フィルム４０は、耐水性に優れ、内容物を充填密封後
の冷蔵冷凍等の保存時に十分な密封性を保ち、かつ、熱
融着性に優れることはもちろんのこと、電子レンジ、オ
ーブン等の加熱に対する耐性が必要となる。つまり、高
い耐水性と耐熱性が必要である。The synthetic resin film 40 used for the tray-shaped container body 10 has excellent water resistance, maintains sufficient sealing property during storage such as refrigeration and freezing after filling and sealing the contents, and also has excellent heat-sealing property. Needless to say, resistance to heating of microwave oven, oven, etc. is required. That is, high water resistance and heat resistance are required.
【００２０】例えば、内容物と接する層をポリプロピレ
ン（ＰＰ）とし、具体的には、ホモポリプロピレン、ラ
ンダムポリプピレン共重合体、ブロックポリプロピレン
共重合体であり、特に、ランダムポリプロピレン共重合
体を用いるのが好ましい。また、外容器と接する層は、
カルボニル基を有するエチレン系共重合体層を用い、こ
の少なくとも２層からなる合成樹脂フィルムである。こ
の合成樹脂フィルムの厚さは、成形性、耐熱性、内容物
保護性のため１００μｍ以上必要であり、好ましくは１
００〜２００μｍの範囲がである。For example, polypropylene (PP) is used as the layer in contact with the contents, specifically, homopolypropylene, random polypropylene copolymer, block polypropylene copolymer, and especially random polypropylene copolymer is used. Is preferred. Also, the layer in contact with the outer container,
A synthetic resin film comprising at least two layers using an ethylene copolymer layer having a carbonyl group. The thickness of the synthetic resin film needs to be 100 μm or more for moldability, heat resistance, and content protection, and preferably 1
The range is from 00 to 200 μm.
【００２１】前記カルボニル基を含むエチレン系共重合
体として、具体的には、エチレン─メチルメタアクリレ
ート共重合体、エチレン−酢酸ビニル共重合体、または
エチレン−アクリル酸エステル−無水マレイン酸三元共
重合体が上げられる。この合成樹脂フィルム４０は、前
記構成の他、ＰＰ層として、ＰＰの単体以外に、内容物
に接する側に用いたＰＰ以外のＰＰ、ポリエチレン、あ
るいは非晶質ポリエステルとを組み合わせた多層構成と
してもよい。前記合成樹脂フィルムは、それぞれドライ
ラミネート法により積層してもよいが、同時に溶融押出
しする、共押出し法により形成したフィルムが好まし
い。Specific examples of the ethylene-based copolymer having a carbonyl group include ethylene-methyl methacrylate copolymer, ethylene-vinyl acetate copolymer, or ethylene-acrylic acid ester-maleic anhydride ternary copolymer. The polymer is raised. In addition to the above structure, the synthetic resin film 40 may have a multi-layer structure in which, in addition to the simple substance of PP, PP other than PP used on the side in contact with the contents, polyethylene, or amorphous polyester is combined as the PP layer. Good. The synthetic resin films may be laminated by a dry laminating method, but a film formed by a coextrusion method in which they are simultaneously melt extruded is preferable.
【００２２】一方、前記トレイ状容器本体の開口部を密
封する蓋材は、密封性と、開封性を兼ね備える必要があ
り、開封時の易開封性を向上させるために合成樹脂フィ
ルムとして、ピーラブル樹脂を積層することが好まし
い。このピーラブル樹脂として、融点が８５℃〜１１０
℃のシングルサイト触媒により重合したポリエチレン、
あるいはエチレン−αオレフィン共重合体、マルチサイ
ト触媒により重合したエチレン−αオレフィン共重合体
を混合した樹脂を用いることが好ましい。そして、蓋材
のシール層に用いる樹脂の融点以上、ポリプロピレン層
の融点以下の温度でヒートシールして密封する。On the other hand, the lid member for sealing the opening of the tray-shaped container body needs to have both the sealing property and the unsealing property. In order to improve the easy unsealing property at the time of unsealing, a peelable resin is used as the synthetic resin film. Are preferably laminated. This peelable resin has a melting point of 85 ° C to 110 ° C.
Polyethylene polymerized by single-site catalyst at ℃,
Alternatively, it is preferable to use a resin in which an ethylene-α olefin copolymer and an ethylene-α olefin copolymer polymerized by a multisite catalyst are mixed. Then, heat sealing is performed at a temperature not lower than the melting point of the resin used for the sealing layer of the lid material and not higher than the melting point of the polypropylene layer for sealing.
【００２３】前記トレイ状容器本体１０に印刷層３０を
設ける場合は、インキとしては電子レンジ、オーブン等
による加熱に対する耐性を持たせる必要がある。つま
り、高い耐熱性が必要である。また加熱による臭気の発
生がない、または低いことが必要である。さらに、前記
した加熱による紙からの蒸気の放出を阻害しないために
通気性が必要となる。When the printing layer 30 is provided on the tray-shaped container body 10, the ink needs to have resistance to heating by a microwave oven, an oven or the like. That is, high heat resistance is required. In addition, it is necessary that no odor is generated by heating or the odor is low. Further, air permeability is required in order to prevent the release of steam from the paper due to the above heating.
【００２４】前記トレイ状容器本体１０に用いる印刷層
３０は、絵柄形成用のインキ３２に加えて、印刷層の最
外面にオーバーコートニス（ＯＰニス）３１を設けるこ
とも可能である。このＯＰニスを設けることで、トレイ
状容器を製造する際、合成樹脂フィルムを真空成形、ま
たは真空圧空成形の併用で、紙基材と積層接着し、一体
化することを金型内で行う時、ＯＰニスを設けておくこ
とにより、金型からのトレイ状容器の取り出しが容易と
なり、取り出し工程におけるトレイ状容器本体の変形、
破壊を防止できる。また、このＯＰニスも、他のインキ
と同様に、耐熱性、通気性、加熱による臭気の発生がな
い、または臭気の発生が低いことを、備えている必要が
ある。The printing layer 30 used in the tray-shaped container body 10 may be provided with an overcoat varnish (OP varnish) 31 on the outermost surface of the printing layer in addition to the ink 32 for forming a pattern. By providing this OP varnish, when a tray-shaped container is manufactured, a synthetic resin film is laminated and adhered to a paper substrate by vacuum forming or vacuum pressure forming together, and is integrated in a mold. By providing the OP varnish, it becomes easy to take out the tray-shaped container from the mold, and the tray-shaped container body is deformed in the taking-out step,
Can prevent destruction. Also, this OP varnish, like other inks, does not generate heat or breathability and odor due to heating.
Or low odor generation should be prepared.
【００２５】[0025]
【発明の効果】本発明は以上の構成であるから、下記に
示す如き効果がある。即ち、内面にポリプロピレン層を
真空成形、または真空成形と圧空成形の併用により、少
なくとも内容物と接する層を形成し、一方面蓋材のシー
ル層としてシングルサイト触媒により重合したポリエチ
レン、あるいはエチレン−αオレフィン共重合体、また
は前記樹脂にマルチサイト触媒により重合したエチレン
−αオレフィン共重合体を混合した樹脂を用いたので、
加熱前は、完全な密封性があり、しかも電子レンジ等で
加熱した場合、発生した蒸気をそのまま排気することが
でき、電子レンジ、オーブン等での容器を簡単に加熱調
理容器として使用できる。Since the present invention has the above-mentioned constitution, it has the following effects. That is, a polypropylene layer is formed on the inner surface by vacuum forming, or a combination of vacuum forming and pressure forming is used to form a layer in contact with at least the content, and polyethylene which is polymerized by a single-site catalyst as a sealing layer of the one-side lid material, or ethylene-α. Since an olefin copolymer or a resin obtained by mixing an ethylene-α olefin copolymer polymerized by a multi-site catalyst into the resin is used,
Before heating, it has a perfect sealing property, and when it is heated in a microwave oven or the like, the generated steam can be exhausted as it is, and a container in a microwave oven or an oven can be easily used as a cooking vessel.
【図１】本発明の一実施例を示す斜視図である。FIG. 1 is a perspective view showing an embodiment of the present invention.
【図２】本発明の容器本体の実施例を示す平面図であ
る。FIG. 2 is a plan view showing an embodiment of the container body of the present invention.
【図３】本発明の容器本体の同実施例を示す断面図であ
る。FIG. 3 is a sectional view showing the same embodiment of the container body of the present invention.
【図４】本発明の容器本体の第２の実施例を示す平面図
である。FIG. 4 is a plan view showing a second embodiment of the container body of the present invention.
【図５】本発明の容器本体の第３の実施例を示す平面図
である。FIG. 5 is a plan view showing a third embodiment of the container body of the present invention.
１０ ‥‥‥‥‥ 容器本体 ２０ ‥‥‥‥‥ 蓋材 ３０ ‥‥‥‥‥ 印刷層 ３１ ‥‥‥‥‥ ＯＰニス ４０ ‥‥‥‥‥ 合成樹脂フィルム ５０ ‥‥‥‥‥ 紙基材 １ ‥‥‥‥‥ 底面板 ２、３ ‥‥‥‥‥ 側板 ４、５、８ ‥‥ フランジ ７ ‥‥‥‥‥ 重合片 10 ‥‥‥‥‥‥ Container body 20: Lid material 30 ・ ・ ・ Printing layer 31 ‥‥‥‥‥ OP varnish 40: Synthetic resin film 50 ‥‥‥‥‥‥ Paper base material 1 ... Bottom plate 2, 3 ... Side plate 4, 5, 8 Flange 7: Polymerized pieces
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) B65D 5/64 B32B 27/10 B32B 27/32 B65D 81/34 ─────────────────────────────────────────────────── ─── Continuation of front page (58) Fields surveyed (Int.Cl. 7 , DB name) B65D 5/64 B32B 27/10 B32B 27/32 B65D 81/34
Claims (4)
材により封緘し密封された密封容器であって封緘密封状
態で加熱あるいは加熱調理する密封容器において、前記
容器本体は、上面が開口し、かつ開口周縁にフランジを
有する紙基材と、その紙基材の容器内面側にポリプロピ
レンフィルム単体を積層した材料、またはその紙基材の
容器内面側にポリプロピレンフィルムを積層した積層構
成の材料からなり、かつ蓋材の内面にシングルサイト触
媒を用いて合成した、ポリエチレンまたはエチレン−α
オレフィン共重合体のいずれかからなる融点が８５℃〜
１１０℃のシール層を設け、前記容器本体のフランジ部
に蓋材を、蓋材のシール層の融点以上、かつ容器本体の
ポリプロピレンフィルムの融点以下の温度でヒートシー
ルして密封したことを特徴とする密封容器。1. A hermetically sealed container in which a tray-shaped container body is filled with contents and then sealed and sealed by a lid material.
In a hermetically sealed container that is heated or cooked in a stationary state, the container body has a paper base material having an open upper surface and a flange at the opening periphery, and a polypropylene container on the inner surface side of the container of the paper base material.
Len film laminated material or its paper base
Laminated structure with polypropylene film laminated on the inner surface of the container
It consists formation material, and was synthesized using a single-site catalyst to the inner surface of the lid, polyethylene or ethylene -α
The melting point of any one of the olefin copolymers is 85 ° C to
A sealing layer of 110 ° C. is provided, and a lid member is heat-sealed at the flange portion of the container body at a temperature not lower than the melting point of the sealing layer of the cover member and not higher than the melting point of the polypropylene film of the container body. Sealed container to do.
内面にポリプロピレンフィルム単体を積層した前記積層
構成の材料、または容器内面側にポリプロピレンフィル
ムを積層した前記積層構成の材料を、真空成形、または
真空成形と圧空成形の併用により一体化した請求項１に
記載の密封容器。2. The laminated body, wherein the container body comprises a polypropylene film simple substance laminated on the inner surface of an outer container made of paper as a base material.
Material of composition or polypropylene fill on the inner surface of the container
The sealed container according to claim 1, wherein the materials of the laminated constitution in which the layers are laminated are integrated by vacuum forming or by combined use of vacuum forming and pressure forming.
ン単体、またはポリプロピレンにエチレン系樹脂を混合
した、いずれかの樹脂からなる請求項１、または請求項
２のいずれかに記載の密封容器。3. The hermetically sealed container according to claim 1, wherein the polypropylene film is made of polypropylene alone or a resin obtained by mixing polypropylene with an ethylene resin.
る、請求項１乃至請求項３のいずれか１項に記載の密封
容器。4. The sealed container according to claim 1, wherein the sealing layer of the lid material is a coextruded film.