JP3218766B2 - Water disintegrable release liner - Google Patents
Water disintegrable release linerInfo
- Publication number
- JP3218766B2 JP3218766B2 JP00899093A JP899093A JP3218766B2 JP 3218766 B2 JP3218766 B2 JP 3218766B2 JP 00899093 A JP00899093 A JP 00899093A JP 899093 A JP899093 A JP 899093A JP 3218766 B2 JP3218766 B2 JP 3218766B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- release liner
- paper
- disintegrable
- release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、水崩壊性剥離ライナー
に関し、更に詳しくは、現在、クラフト紙、グラシン
紙、パーチメント紙など耐水性の大きい紙にポリエチレ
ン・ラミネートを行い、シリコーン・ポリマーを塗布
し、加熱、重合、硬化によって調製されている廃棄処理
の困難な既存の剥離ライナーの代りに、廃棄処理の容易
な剥離用の素材として使用できる。水崩壊性の剥離ライ
ナーは、主成分が微生物分解性であるので、土中に埋没
処理することにより分解し、環境に対して問題を生ずる
ことがない。従って本発明による水崩壊性剥離ライナー
は、生理帯用粘着剤の剥離ライナーとして使用可能で、
装着時に不用となったライナーをトイレット中に投入す
ることにより水中で崩壊して放流可能となる。また紙お
むつの使用にあたっては、本来は、大便をトイレット中
に処理して一般のゴミと共に廃棄することになっている
が、実際は大便を含んだ状態のものを一般のゴミと捨て
られているのが現状であり、大きな社会的問題となって
いる。この紙おむつの使用に際して、本発明の水崩壊性
剥離ライナーを紙おむつの身体に接触する面に重ねて使
用するときは、小便は既存の紙おむつに吸収されて、ラ
イナーは常に乾燥した状態にあり、大便はこのライナー
で包んでトイレットに投入することにより水中に崩壊し
て放流可能となる。年間消費量は生理帯で約１００億
枚、紙おむつで約６０億枚消費されていることからみる
と非常に大きな市場であることが明らかである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a water-disintegratable release liner, and more particularly, to a method of coating a highly water-resistant paper such as kraft paper, glassine paper or parchment paper with a polyethylene polymer and applying a silicone polymer. Instead of the existing release liner which is difficult to dispose prepared by heating, polymerization and curing, it can be used as a release material which is easy to dispose. Since the main component of the water-disintegrating release liner is biodegradable, it is decomposed by burying it in the soil, and does not cause any environmental problems. Therefore, the water-disintegrating release liner according to the present invention can be used as a release liner for a pressure-sensitive adhesive for sanitary zone,
By disposing the liner that has become unnecessary at the time of mounting into the toilet, it breaks down in the water and can be released. Also, when using disposable diapers, the stool should be disposed of in the toilet and discarded together with general garbage, but in reality the stool containing stool is discarded as general garbage. At present, it is a major social problem. When using the water-disintegrating release liner of the present invention on the surface in contact with the body of the disposable diaper when using the disposable diaper, urine is absorbed by the existing disposable diaper, and the liner is always in a dry state. By wrapping it in this liner and throwing it into the toilet, it collapses into water and can be released. From the fact that the annual consumption is about 10 billion pieces in the menstrual zone and about 6 billion pieces in the disposable diaper, it is clear that this is a very large market.
【０００２】[0002]
【従来の技術】一般に、剥離ライナーとしては、不活性
な表面を形成するシリコーン・ポリマーを塗布、加熱、
重合、硬化した紙が使用されている。既存の剥離ライナ
ーそのものは、使用後、廃棄するのみであるが、前記し
たような処理のため、廃棄後も微生物により生分解され
ることがなく、年間１，７００，０００ｋｍ2 の値が示
す大量消費の商品の一つとして、その廃棄物としての処
理方法が社会問題となっている。剥離ライナーは基材に
よってポリエチレン・ラミネートしたクラフト紙、グラ
シン紙、パーチメント紙などがあげられるが、いずれも
耐水性の大きい紙を使用しているので、古紙の回収プロ
セス、土中への埋没処理に適さず、焼却処理以外に適切
な方法はない。2. Description of the Related Art Generally, as a release liner, a silicone polymer that forms an inert surface is applied, heated,
Polymerized and cured paper is used. The existing release liner itself is only discarded after use, but because of the treatment described above, it is not biodegraded by microorganisms even after disposal, and a large amount of 1,700,000 km 2 per year is shown. As one of the commodities for consumption, a method of treating it as waste has become a social problem. Release liners include kraft paper, glassine paper, parchment paper, etc., which are polyethylene-laminated according to the base material.Since they use highly water-resistant paper, they are used for the recovery process of waste paper and the burial treatment in soil. Not suitable, there is no suitable method other than incineration.
【０００３】[0003]
【発明が解決しようとする課題】前記したように、従来
の剥離性ライナーは耐水性の大きい、硬質の紙にシリコ
ーン・ポリマーを塗布、加熱、重合、硬化させて非常に
不活性な紙質のシリコーン塗布紙が中心となっているの
で、環境上に悪影響を与えない適切な処理方法が見出さ
れていない。つまり、前記したような大量の使用済の剥
離性ライナーを焼却するか、分解しないゴミとして埋め
る方法しか存在しない。従って本発明は、前記した既存
の廃棄処理困難な剥離性ライナーとは全く逆の、水崩壊
性微生物分解性の素材にシリコーン・ポリマーの薄膜を
形成し、使用後は、古紙回収のプロセスを経て、パルプ
を回収するか、土中に埋めて微生物による生分解を行う
かの廃棄処理方法の可能な水崩壊性剥離ライナーを提供
することにある。As described above, a conventional release liner is a highly inert paper-type silicone obtained by applying, heating, polymerizing, and curing a silicone polymer on hard paper having high water resistance. Since the coated paper is mainly used, no suitable treatment method that does not adversely affect the environment has been found. That is, there is only a method of burning a large amount of the used peelable liner as described above or burying it as garbage that does not decompose. Therefore, the present invention forms a thin film of a silicone polymer on a water-disintegrable biodegradable material, which is completely opposite to the above-mentioned existing hard-to-dispose release liner, and after use, passes through a process of collecting used paper. Another object of the present invention is to provide a water-disintegratable release liner which can be used for a disposal method of recovering pulp or burying it in soil to perform biodegradation by microorganisms.
【０００４】[0004]
【課題を解決するための手段】本発明に従えば、平均分
子量１０万〜５００万のポリエチレンオキシドの稀薄溶
液を、水崩壊紙上に塗布、乾燥し、その上に剥離性シリ
コーン・ポリマー薄膜を設けてなる水崩壊性剥離ライナ
ーが提供される。本発明では、例えば通常１〜１５重量
％、好ましくは１〜１０重量％のポリエチレンオキシド
を含む溶液を水崩壊性紙に塗布、乾燥し、その表面に、
従来より知られている、剥離用シリコーン用薄膜を形成
できる反応性ジメチルシロキサン１〜６重量％溶液を塗
布して温度１００〜１２０℃で加熱、重合、硬化させる
ことによって、水崩壊性剥離ライナーを得ることができ
る。According to the present invention, a dilute solution of polyethylene oxide having an average molecular weight of 100,000 to 5,000,000 is coated on a water-disintegrating paper, dried, and a releasable silicone polymer thin film is provided thereon. A water disintegrable release liner is provided. In the present invention, for example, a solution containing 1 to 15% by weight, preferably 1 to 10% by weight of polyethylene oxide is applied to water-disintegrable paper, dried, and
A water-disintegratable release liner is obtained by applying a 1 to 6% by weight solution of a reactive dimethylsiloxane known in the art, which is capable of forming a thin film for silicone for release, and heating, polymerizing and curing at a temperature of 100 to 120 ° C. Obtainable.
【０００５】水崩壊性紙としては従来より知られている
紙が使用できるが、通常ポリビニルアルコール、カルボ
キシルメチルセルロース等の水溶性樹脂を５〜１５重量
％程度混入した紙が使用できる。通常、パルプ、レーヨ
ンなどの繊維をシートにするときに、予じめ水溶性樹脂
を内添しておくことにより水崩壊性紙とすることができ
る。As the water-disintegrable paper, conventionally known papers can be used, but usually paper containing about 5 to 15% by weight of a water-soluble resin such as polyvinyl alcohol or carboxymethyl cellulose can be used. Usually, when fibers such as pulp and rayon are formed into a sheet, a water-disintegrable paper can be obtained by internally adding a water-soluble resin in advance.
【０００６】ポリエチレンオキシドは、エチレンオキシ
ドが開環して多数線状につながり、規則正しいらせん構
造を持った、白色の水溶性熱可塑性樹脂で、平均分子量
１０万〜５００万のものが使用される。ポリエチレンオ
キシドは、水だけでなく、アセトニトリル、塩化エチレ
ン、クロロホルム、トリクロルエチレン、塩化メチレン
等に可溶であり、芳香族系溶剤、脂肪族１価アルコー
ル、１，４−ジオキサン等には、一般に室温では難溶性
であるが、少し温めることにより溶解する。[0006] Polyethylene oxide is a white water-soluble thermoplastic resin having an average molecular weight of 100,000 to 5,000,000. Polyethylene oxide is soluble not only in water but also in acetonitrile, ethylene chloride, chloroform, trichloroethylene, methylene chloride, and the like, and is generally used at room temperature in aromatic solvents, aliphatic monohydric alcohols, 1,4-dioxane, and the like. Although it is hardly soluble in water, it dissolves when heated slightly.
【０００７】本発明においては、例えばアルコール−水
混合溶液に溶解したポリエチレンオキシド溶液をパル
プ、レーヨンまたはこれらの混合素材からなる水崩壊性
紙に塗布、乾燥し、その上に剥離性シリコーン・ポリマ
ー溶液を塗布して、乾燥後、温度１００〜１２０℃で約
１０秒間、加熱、硬化させるときは、前記水崩壊性紙の
表面に剥離性シリコーン・ポリマーの薄膜が生成した剥
離性ライナーが得られる。In the present invention, for example, a polyethylene oxide solution dissolved in an alcohol-water mixed solution is applied to a water-disintegrable paper made of pulp, rayon or a mixed material thereof, dried, and then a peelable silicone polymer solution is applied thereon. Is applied and dried and then heated and cured at a temperature of 100 to 120 ° C. for about 10 seconds to obtain a release liner having a release silicone polymer thin film formed on the surface of the water-disintegrable paper.
【０００８】ここに得られた水崩壊性剥離ライナーは、
アクリル系粘着剤、ゴム系粘着剤、ホットメルト系粘着
剤に対して、すぐれた剥離性をなし、特に生理帯に使用
するときは、その使用時に、不用となった前記ライナー
をトイレットに投入、崩壊、放流することができる。ま
た、紙おむつの身体に接触する内面に重ねて使用すると
きは、小便は容易に紙おむつに浸透吸収されて、崩壊し
ないで湿った感覚はない。また大便は、前記ライナーで
包み、トイレットに投入、崩壊、放流が可能である。[0008] The water-disintegrable release liner obtained here is
Acrylic adhesive, rubber adhesive, hot-melt adhesive, has excellent releasability, especially when used in a sanitary zone, at the time of its use, put the liner that has become unnecessary into the toilet, Disintegrate and release. Also, when used on the inner surface of the disposable diaper which is in contact with the body, the urine easily penetrates and is absorbed by the disposable diaper, and does not disintegrate and has no wet feeling. Further, stool can be wrapped with the liner and thrown into a toilet, collapsed, and discharged.
【０００９】このように、本発明の水崩壊性剥離ライナ
ーは、単に各種粘着剤の剥離ライナーとして使用可能で
あるばかりでなく、紙おむつにおける、使用時は水に崩
壊しない剥離ライナーとしての機能を有し、使用後は大
便を包んでトイレットに投入、崩壊、放流を可能とする
新しい機能を有する素材であり、これらの廃棄物処理に
関する社会的問題を解決するものである。As described above, the water-disintegratable release liner of the present invention can be used not only as a release liner for various adhesives, but also as a release liner in a disposable diaper which does not collapse into water when used. However, after use, it is a material that has a new function that allows it to be wrapped in the stool and put into the toilet, disintegrated, and released, and solves the social problems related to waste disposal.
【００１０】本発明で得られる剥離ライナー表面のシリ
コーン・ポリマー薄膜の厚さは１〜５ミクロンで、剥離
ライナーを水中に浸漬するときは容易に崩壊してスラリ
ー状のパルプ分散液となり、主要成分は微生物によって
生分解される。The thickness of the silicone polymer thin film on the surface of the release liner obtained in the present invention is 1 to 5 μm. When the release liner is immersed in water, it is easily disintegrated to form a slurry-like pulp dispersion. Is biodegraded by microorganisms.
【００１１】[0011]
【実施例】次に実施例で本発明を具体的に説明するが、
本発明をこれらの実施例に限定するものでないことはい
うまでもない。例中「％」とは重量％を示す。 実施例１ 平均分子量約２０万のポリエチレンオキシド５％エタノ
ール／水（１：１）溶液を、パルプ９５％、ポリビニル
アルコール５％からなる水崩壊性紙に塗装、乾燥する。
ここに得られた水崩壊性紙に、反応性ポリシロキサン系
剥離シリコーン５％トルエン溶液を塗布、乾燥した後、
温度１１０〜１２０℃で約１０秒間加熱、硬化させる
と、厚さ約２ミクロンのシリコーン・ポリマーの薄膜を
有する水崩壊性剥離ライナーが得られる。ここに得られ
たライナーは、アクリル系、ゴム系、ホットメルト系粘
着剤に対して良好な剥離性を有し、更に水中に投入した
場合には、容易に溶解してその形状を消失する。更にこ
のものの主成分は微生物によって生分解される。 実施例２ 実施例１で得られた水崩壊性剥離ライナーを、ホットメ
ルト粘着剤を使用した生理帯に使用した。このときの剥
離性の経時変化、接着性保持率の経時変化は次の通りで
あった。なお、剥離性は剥離速度０．３または６０Ｍ
（メーター）で行った結果を示す。Next, the present invention will be described in detail with reference to Examples.
It goes without saying that the invention is not limited to these examples. In the examples, "%" indicates% by weight. Example 1 A solution of polyethylene oxide 5% ethanol / water (1: 1) having an average molecular weight of about 200,000 is applied to a water-disintegrable paper composed of 95% pulp and 5% polyvinyl alcohol, and dried.
After applying a 5% toluene solution of a reactive polysiloxane-based release silicone to the water-disintegrable paper obtained here and drying,
Heating and curing at a temperature of 110-120 ° C. for about 10 seconds yields a water-disintegrable release liner having a silicone polymer film about 2 microns thick. The liner obtained here has good releasability to acrylic, rubber and hot melt pressure-sensitive adhesives, and easily dissolves and loses its shape when put into water. Furthermore, the main components of this are biodegraded by microorganisms. Example 2 The water-disintegrable release liner obtained in Example 1 was used in a sanitary band using a hot melt adhesive. At this time, the change with time of the peeling property and the change with time of the adhesiveness retention were as follows. The peeling property is a peeling rate of 0.3 or 60M.
(Meter) shows the results.
【００１２】 １日 ２８日 剥離性ｇ／５ｃｍ ０．３Ｍ（メーター）／分 ２０ ２２ ６０Ｍ／分 ２２ ２６ 接着性保持率％ ９４ ９２ 前記測定結果は、従来使用されてきた剥離紙と殆ど同じ
値を示し、トイレットに投入するときは容易に水中で崩
壊し放流することができた。 実施例３ 実施例１でパルプの代わりにレーヨンを使用した水崩壊
性剥離性ライナーを、紙おむつの身体に接する内面に重
ねて使用するときは、小便は容易に紙おむつに浸透して
殆ど乾燥した状態を示した。また大便のときは包んでト
イレットに投入して崩壊、放流することができた。1 day 28 days Peelability g / 5 cm 0.3 M (meter) / min 20 22 60 M / min 22 26 Adhesive retention% 94 92 The above measurement results show almost the same values as those of conventionally used release paper. When it was put into a toilet, it easily collapsed in water and could be discharged. Example 3 When a water-disintegratable peelable liner using rayon instead of pulp in Example 1 is used on the inner surface of the disposable diaper in contact with the body, urine easily penetrates into the disposable diaper and is almost dry. showed that. In the case of a stool, it could be wrapped and thrown into the toilet, collapsed and released.
───────────────────────────────────────────────────── フロントページの続き 審査官 中島 庸子 (56)参考文献 特開 平６−33394（ＪＰ，Ａ) 特開 平６−107713（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) D21H 11/00 - 27/42 ────────────────────────────────────────────────── ─── Continued on the front page Examiner Yoko Nakajima (56) References JP-A-6-33394 (JP, A) JP-A-6-107713 (JP, A) (58) Fields investigated (Int. Cl. 7) , DB name) D21H 11/00-27/42
Claims (2)
レンオキシドを含む溶液を塗布、乾燥したパルプ、レー
ヨンまたはそれらの混合物の水崩壊性紙の塗布面に、剥
離用シリコーン層を形成してなることを特徴とする水崩
壊性剥離ライナー。 1. A release silicone layer is formed on the surface of a water-disintegrable paper of pulp, rayon or a mixture thereof coated with a solution containing polyethylene oxide having an average molecular weight of 100,000 to 5,000,000 and dried. A water-disintegrable release liner characterized by the following.
含む溶液を用いる請求項１記載の水崩壊性剥離ライナ
ー。2. A polyethylene oxide containing 1 to 15% by weight.
The water-disintegrable release liner according to claim 1, wherein a solution containing the release liner is used.