JP3191478U - Melamine vessel - Google Patents
Melamine vessel Download PDFInfo
- Publication number
- JP3191478U JP3191478U JP2014001101U JP2014001101U JP3191478U JP 3191478 U JP3191478 U JP 3191478U JP 2014001101 U JP2014001101 U JP 2014001101U JP 2014001101 U JP2014001101 U JP 2014001101U JP 3191478 U JP3191478 U JP 3191478U
- Authority
- JP
- Japan
- Prior art keywords
- melamine
- powder
- container
- base material
- grain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
【課題】短時間で製造することができる上、製造コストを下げることができるメラミンの器を提供する。
【解決手段】メラミンの器１は、１次熱圧プレス成型工程により器状に作成されるとともに、メラミン粉材１０、メラミン粒基材１１、ベークライト粉／粒及び尿素粉／粒を含む。メラミン粒基材１１は、メラミン粉材１０の粒状からなり、メラミン粉材１０と混合され、熱圧プレス成型によりメラミンの器１が作成され、メラミンの器１の外表面に色が表される。メラミン粒基材１１と混合されたメラミン粉材１０は単色である。単色又は多色で粒のサイズが同じか異なるメラミン粒基材１１と混合され、熱圧プレス成型によりメラミンの器１が作成される。
【選択図】図１To provide a melamine container that can be manufactured in a short time and can reduce the manufacturing cost.
A melamine container 1 is formed into a container shape by a primary hot press molding process, and includes a melamine powder material 10, a melamine particle base material 11, bakelite powder / particles, and urea powder / particles. The melamine granule base material 11 is composed of particles of the melamine powder material 10, mixed with the melamine powder material 10, the melamine container 1 is created by hot press molding, and the color is expressed on the outer surface of the melamine container 1. . The melamine powder material 10 mixed with the melamine grain base material 11 is monochromatic. A melamine container 1 is prepared by hot-pressing molding by mixing with a melamine grain base material 11 having a single color or multiple colors and having the same or different grain size.
[Selection] Figure 1
Description
本考案は、メラミンの器に関し、特に、メラミン粒基材とメラミン粉基材との撹拌加熱射出成形により、見た目が良い上、セラミックに似た見た目を有するメラミンの器を形成する技術に関する。 The present invention relates to a melamine vessel, and more particularly, to a technology for forming a melamine vessel having a good appearance and a ceramic-like appearance by stirring and heating injection molding of a melamine granular substrate and a melamine powder substrate.
メラミンは、無臭かつ無毒で、耐熱性に優れ、表面硬度が高く、耐磨耗性を有し、着色自在で光沢性に優れ、環境汚染を発生させないなどの特性を有するため、各種日用品に広く応用されている。食器、果物用皿、サラダ用碗、ナイフ、フォーク、スプーンなど様々なキッチン用品以外に、浴室用品として作成することができ、その応用範囲は非常に広かった。メラミンは応用範囲が広く、その長所を高めながら、製造コストを下げることは現代人のニーズを満たすことができるため、メーカにとって重要な研究対象となっている。従来のメラミンの器構造は、メラミン基材（ｍｅｌａｍｉｎｅ ｂａｓｉｃ ｍａｔｅｒｉａｌ）、メラミン樹脂基材及び複数の木材料部材から構成されている。メラミン基材は、メラミン粉／粒材を熱圧プレス成型し、メラミン樹脂と溶接して一体化し、接着して複数の木材料部を覆ってメラミンの器を作成する。上述した材料のメラミン基材、メラミン樹脂基材及び木質部のそれぞれを混合し、熱圧プレス成型によりメラミンの器を作成する。このように多数の熱圧プレス、複雑な製造工程を行うため、製造コストが高くなった。他の従来のメラミンの器構造では、メラミンの粉状又は粒状の材料を利用し、熱圧プレス成型工程によりメラミン基材を成形し、熱圧プレス成型されたメラミン粉砕状二次材と混合した後、１次熱圧プレス成型を行うが、その特徴としては粉砕状二次材が熱熔融により軟化しないため、形状が不規則であり、サイズが不均一で多種類の色の粉砕状二次材は、その色彩及び形状をメラミンの器の外表面にはっきりと表すことができる点であるが、このようなメラミンの器が使用するメラミン基材及びメラミン二次材は、それぞれ熱圧成形を行い、メラミン二次材をさらに粉砕処理する必要があるため、メラミン基材とメラミン二次材とを再び熱圧プレス成型しなければならず、全体の製造工程が複雑となり、製造コストが依然として高かった。 Melamine is odorless and non-toxic, has excellent heat resistance, high surface hardness, wear resistance, colorability and gloss, and does not cause environmental pollution. Applied. In addition to various kitchen utensils such as tableware, fruit dishes, salad bowls, knives, forks, and spoons, they could be made as bathroom utensils, and their application range was very wide. Melamine has a wide range of applications, and it has become an important research object for manufacturers because it can meet the needs of modern people while lowering manufacturing costs while increasing its advantages. The conventional vessel structure of melamine is composed of a melamine base material, a melamine resin base material, and a plurality of wood material members. The melamine base material is formed by hot pressing a melamine powder / granular material, welding and integrating with a melamine resin, and bonding to cover a plurality of wood material portions to create a melamine container. Each of the melamine base material, the melamine resin base material, and the wood part of the materials described above is mixed, and a melamine container is created by hot press molding. As described above, since many hot presses and complicated manufacturing processes are performed, the manufacturing cost is increased. In other conventional melamine vessel structures, a melamine powder or granular material is used, a melamine base material is formed by a hot press molding process, and mixed with a hot press molded melamine secondary material. After that, primary hot press molding is performed, but the characteristic is that the pulverized secondary material is not softened by heat melting, so the shape is irregular, the size is uneven, and the pulverized secondary of various colors The material is that the color and shape can be clearly expressed on the outer surface of the melamine vessel, but the melamine base material and the melamine secondary material used by such melamine vessel are respectively hot-pressed. And the melamine secondary material needs to be further pulverized, so the melamine base material and the melamine secondary material must be hot-pressed again, which complicates the entire manufacturing process and the manufacturing cost is still high. It was.
本考案の第１の目的は、メラミン粒基材が必要に応じてメラミン粉材を様々な色及び大きさに形成された粒状からなり、熱圧プレス成型を何度も行わなくとも、メラミン粉材と混合してメラミンを作成する際、１回だけの熱圧プレス成型によりメラミンの器を作成するため、短時間で製造することができる上、製造コストを下げることができるメラミンの器を提供することにある。
本考案の第２の目的は、メラミン粒基材がメラミン粉材と混合されて熱圧プレス成型が行われても破裂しないで拡散・変形だけが生じるため、メラミン粉材と結合された後、色がはっきりと表され、見た目が良い上、セラミックに似た見た目を有するメラミンの器を提供することにある。
本考案の第３の目的は、見た目が良い上、セラミックに似た見た目を有するメラミンの器を形成するため、製造メーカの必要に応じてメラミン粒基材の色を変化させ、各メーカの必要性を満たすメラミンの器を提供することにある。
The first object of the present invention is that a melamine powder base material is made of melamine powder material in various colors and sizes as required, and the melamine powder can be formed without repeated hot press molding. When creating melamine by mixing with the material, the melamine container can be manufactured in a short time and the manufacturing cost can be reduced because the melamine container is created by hot press molding only once. There is to do.
The second object of the present invention is that, since the melamine granule base material is mixed with the melamine powder material and hot press molding is performed, it does not rupture but only diffuses and deforms. Therefore, after being combined with the melamine powder material, The object is to provide a melamine bowl which is clearly colored, looks good and has a ceramic-like appearance.
The third object of the present invention is to create a melamine vessel that looks good and looks similar to ceramic. Therefore, the color of the melamine grain base material is changed according to the manufacturer's needs, and each manufacturer's needs The purpose is to provide a container of melamine that satisfies sex.
図１を参照する。図１に示すように、本考案の一実施形態に係るメラミンの器１は、必要に応じて形状を設計することが可能で、メラミン粉材１０と、メラミン粉材により作成された粒状のメラミン粒基材１１とを十分に混合撹拌した後、熱圧プレスによりメラミンの器１を作成する。メラミン粒基材１１と混合されるメラミン粉材１０は、単色を呈する。メラミン粒基材１１は、メラミン粉材１０により作成され、色及びサイズが異なる粒状でもよい。 Please refer to FIG. As shown in FIG. 1, a melamine container 1 according to an embodiment of the present invention can be designed in shape as necessary, and a melamine powder material 10 and a granular melamine made from a melamine powder material. After sufficiently mixing and stirring the granule base material 11, a container 1 for melamine is prepared by hot pressing. The melamine powder material 10 mixed with the melamine grain base material 11 exhibits a single color. The melamine grain base material 11 may be made of the melamine powder material 10 and may have a different color and size.
単色のメラミン粉材１０と、単色でサイズが異なるメラミン粒基材１１とを十分に撹拌・混合し、熱圧プレス成型によりメラミンの器１を作成し、メラミン粒基材１１とメラミン粉材１０とが混合されて熱圧プレスされて射出成形されるため破裂せず、単に変形・拡散される。また色彩がメラミンの器１の外表面にはっきりと表れるため、見た目が良い上、セラミックに似た見た目を有するメラミンの器１を作成することができる。 A single color melamine powder material 10 and a single color melamine particle base material 11 having different sizes are sufficiently stirred and mixed, and a melamine container 1 is prepared by hot press molding. The melamine particle base material 11 and the melamine powder material 10 Are mixed, hot-pressed and injection molded, so they do not rupture but are simply deformed and diffused. Moreover, since the color appears clearly on the outer surface of the melamine container 1, the melamine container 1 having a good appearance and having an appearance similar to ceramic can be produced.
熱圧プレスを行う前に、単色のメラミン粉材１０により色を選択し、メラミン粒基材１１の大粒・小粒を組み合わせる割合及び色彩を調整してから熱圧プレスを行い、作成の完成品のニーズを満たす。 Before performing the hot-pressing, the color is selected by the single-colored melamine powder material 10, the ratio and the color of the melamine grain base material 11 are combined and the color is adjusted, and then the hot-pressing is performed. Satisfy your needs.
本実施形態はさらに２種類以上の色、サイズのメラミン粒基材１１と単色のメラミン粒基材１１とを混合・撹拌してメラミンの器１を作成する。 In this embodiment, the melamine container 1 is prepared by further mixing and stirring the melamine particle base material 11 of two or more colors and sizes and the monochromatic melamine particle base material 11.
本実施形態のメラミンの器１は、２種類又は３種類以上の色と、同じ又は異なるサイズとを有するメラミン粒基材１１を互いに混合・撹拌して熱圧プレスして射出成形される。 The melamine container 1 of the present embodiment is injection-molded by mixing and stirring melamine particle base materials 11 having two or three or more colors and the same or different sizes, and agitation with each other.
本実施形態のメラミン粒基材１１は、ベークライト粉（ｂａｋｅｌｉｔｅ ｐｏｗｄｅｒ）／粒又は尿素粉／粒により代替され、安全かつ無毒な割合を適用してメラミン粉材１０と混合され、熱圧プレス成型によりメラミンの器１を作成してもよい。 The melamine grain base material 11 of this embodiment is replaced with bakelite powder / grains or urea powder / grains, mixed with the melamine powder material 10 by applying a safe and non-toxic ratio, and subjected to hot press molding. A melamine vessel 1 may be created.
本実施形態のメラミン粉材１０は、ベークライト粉／粒又は尿素粉／粒により代替され、安全かつ無毒な割合によりメラミン粒基材１１と混合され、熱圧プレス成型によりメラミンの器１を作成してもよい。 The melamine powder material 10 of this embodiment is replaced with bakelite powder / grains or urea powder / grains, mixed with the melamine grain base material 11 at a safe and non-toxic ratio, and the melamine container 1 is prepared by hot press molding. May be.
本実施形態のベークライト粉／粒又は尿素粉／粒は、安全かつ無毒な割合でメラミン粉材１０及びメラミン粒基材１１と混合され、熱圧プレス成型によりメラミンの器１を作成してもよい。 The bakelite powder / grain or urea powder / grain of this embodiment may be mixed with the melamine powder material 10 and the melamine grain base material 11 at a safe and non-toxic ratio, and the melamine container 1 may be created by hot press molding. .
１ メラミンの器
１０ メラミン粉材
１１ メラミン粒基材
1 Melamine vessel 10 Melamine powder 11 Melamine grain base material
メラミンは、無臭かつ無毒で、耐熱性に優れ、表面硬度が高く、耐磨耗性を有し、着色自在で光沢性に優れ、環境汚染を発生させないなどの特性を有するため、各種日用品に広く応用されている。食器、果物用皿、サラダ用碗、ナイフ、フォーク、スプーンなど様々なキッチン用品以外に、浴室用品として作成することができ、その応用範囲は非常に広かった。メラミンは応用範囲が広く、その長所を高めながら、製造コストを下げることは現代人のニーズを満たすことができるため、メーカにとって重要な研究対象となっている。従来のメラミンの器構造は、メラミン基材（ｍｅｌａｍｉｎｅ ｂａｓｉｃ ｍａｔｅｒｉａｌ）、メラミン樹脂基材及び複数の木材料部材から構成されている。メラミン基材は、メラミン粉及び粒材を熱圧プレス成型し、メラミン樹脂と溶接して一体化し、接着して複数の木材料部を覆ってメラミンの器を作成する。上述した材料のメラミン基材、メラミン樹脂基材及び木質部のそれぞれを混合し、熱圧プレス成型によりメラミンの器を作成する。このように多数の熱圧プレス、複雑な製造工程を行うため、製造コストが高くなった。他の従来のメラミンの器構造では、メラミンの粉状又は粒状の材料を利用し、熱圧プレス成型工程によりメラミン基材を成形し、熱圧プレス成型されたメラミン粉砕状二次材と混合した後、１次熱圧プレス成型を行うが、その特徴としては粉砕状二次材が熱熔融により軟化しないため、形状が不規則であり、サイズが不均一で多種類の色の粉砕状二次材は、その色彩及び形状をメラミンの器の外表面にはっきりと表すことができる点であるが、このようなメラミンの器が使用するメラミン基材及びメラミン二次材は、それぞれ熱圧成形を行い、メラミン二次材をさらに粉砕処理する必要があるため、メラミン基材とメラミン二次材とを再び熱圧プレス成型しなければならず、全体の製造工程が複雑となり、製造コストが依然として高かった。 Melamine is odorless and non-toxic, has excellent heat resistance, high surface hardness, wear resistance, colorability and gloss, and does not cause environmental pollution. Applied. In addition to various kitchen utensils such as tableware, fruit dishes, salad bowls, knives, forks, and spoons, they could be made as bathroom utensils, and their application range was very wide. Melamine has a wide range of applications, and it has become an important research object for manufacturers because it can meet the needs of modern people while lowering manufacturing costs while increasing its advantages. The conventional vessel structure of melamine is composed of a melamine base material, a melamine resin base material, and a plurality of wood material members. The melamine base material is formed by hot-pressing melamine powder and granules, welding and integrating with the melamine resin, and bonding them to cover a plurality of wood material portions to create a melamine container. Each of the melamine base material, the melamine resin base material, and the wood part of the materials described above is mixed, and a melamine container is created by hot press molding. As described above, since many hot presses and complicated manufacturing processes are performed, the manufacturing cost is increased. In other conventional melamine vessel structures, a melamine powder or granular material is used, a melamine base material is formed by a hot press molding process, and mixed with a hot press molded melamine secondary material. After that, primary hot press molding is performed, but the characteristic is that the pulverized secondary material is not softened by heat melting, so the shape is irregular, the size is uneven, and the pulverized secondary of various colors The material is that the color and shape can be clearly expressed on the outer surface of the melamine vessel, but the melamine base material and the melamine secondary material used by such melamine vessel are respectively hot-pressed. And the melamine secondary material needs to be further pulverized, so the melamine base material and the melamine secondary material must be hot-pressed again, which complicates the entire manufacturing process and the manufacturing cost is still high. It was.
本実施形態のメラミン粒基材１１は、ベークライト粉（ｂａｋｅｌｉｔｅ ｐｏｗｄｅｒ）及び粒、または尿素粉及び粒により代替され、安全かつ無毒な割合を適用してメラミン粉材１０と混合され、熱圧プレス成型によりメラミンの器１を作成してもよい。 The melamine grain base material 11 of this embodiment is replaced with bakelite powder and grains , or urea powder and grains, and is mixed with the melamine powder material 10 by applying a safe and non-toxic ratio, and hot press molding. The melamine vessel 1 may be created by
本実施形態のメラミン粉材１０は、ベークライト粉及び粒、または尿素粉及び粒により代替され、安全かつ無毒な割合によりメラミン粒基材１１と混合され、熱圧プレス成型によりメラミンの器１を作成してもよい。 The melamine powder material 10 of the present embodiment is replaced with bakelite powder and grains , or urea powder and grains, mixed with the melamine grain base material 11 at a safe and non-toxic ratio, and the melamine container 1 is created by hot press molding. May be.
本実施形態のベークライト粉及び粒、または尿素粉及び粒は、安全かつ無毒な割合でメラミン粉材１０及びメラミン粒基材１１と混合され、熱圧プレス成型によりメラミンの器１を作成してもよい。 Even if the bakelite powder and grains , or the urea powder and grains of this embodiment are mixed with the melamine powder material 10 and the melamine grain base material 11 at a safe and non-toxic ratio, the melamine container 1 is produced by hot press molding. Good.
Claims (8)
上記メラミン粒基材は、メラミン粉材の粒状からなり、メラミン粉材と混合され、熱圧プレス成型によりメラミンの器が作成され、メラミンの器の外表面に色が表されることを特徴とするメラミンの器。 A melamine container containing a melamine powder material, a melamine granule base material, a bakelite powder / grain and a urea powder / grain, which is created in a vessel shape by a primary hot press molding process,
The melamine granule base material is composed of particles of melamine powder material, mixed with the melamine powder material, a melamine container is created by hot press molding, and a color is expressed on the outer surface of the melamine container. A melamine container.
単色又は多色で粒のサイズが同じか異なるメラミン粒基材と混合され、熱圧プレス成型によりメラミンの器が作成されることを特徴とする請求項１に記載のメラミンの器。 The melamine powder material mixed with the melamine grain base is a single color,
2. The melamine container according to claim 1, wherein the melamine container is mixed with a melamine particle base material having a single color or multiple colors and having the same or different particle size, and a melamine container is formed by hot press molding.
上記メラミン粒基材は、メラミン粉材の粒状からなり、２種類又は３種類以上の色のメラミン粒基材と混合され、熱圧プレス成型によりメラミンの器が作成され、メラミンの器の外表面に色が表されることを特徴とするメラミンの器。 A melamine vessel made by a primary hot press molding process and containing a melamine granule base material, bakelite powder / grain and urea powder / grain,
The melamine granule base material is made of melamine powder and mixed with two or more melamine granule base materials, and a melamine container is created by hot press molding. The outer surface of the melamine container A melamine vessel characterized by its color.