CN104783596A - Melamine utensil - Google Patents
Melamine utensil Download PDFInfo
- Publication number
- CN104783596A CN104783596A CN201410029155.8A CN201410029155A CN104783596A CN 104783596 A CN104783596 A CN 104783596A CN 201410029155 A CN201410029155 A CN 201410029155A CN 104783596 A CN104783596 A CN 104783596A
- Authority
- CN
- China
- Prior art keywords
- resistance
- ware
- grain
- vessel
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a melamine utensil. A melamine powder primary material and a granular melamine particle primary material coagulated by melamine powder are fully mixed and stirred and then subjected to heat pressure to form the melamine utensil, wherein the melamine powder primary material mixed with the melamine particle primary material presents a single color, the melamine particle primary material can be of a single color or various types of colors, and particles are of the same or different size; the melamine powder primary material in the single color is mutually mixed with the melamine particle primary material in the single color or the various types of colors and having the same or the different sizes, and the two materials are fully stirred and subjected to the hot-pressing to form the melamine utensil. By means of the above structure, since only one time of hot-pressing is needed in the whole manufacturing process, the advantages that the manufacturing is faster and the manufacturing cost is lower are achieved by the one time hot-pressing process, and various types of funny utensils or utensils imitating ceramic appearance of melamine can be formed, and the requirements of each technical field are better met.
Description
Technical field
The vessel of the resistance to ware of U.S. of the present invention, utilize the U.S. grain of resistance to ware material and U.S.'s powder of resistance to ware material agitating heating injection-compression molding about one, make the vessel of the resistance to ware of U.S. of the various interesting or imitative ceramic outward appearance of formation whereby.
Background technology
U.S. resistance to ware, it has tasteless, nontoxic, temperature tolerance is good, case hardness is high, rub resistance, painted free and glossiness good, and not easily cause the characteristics such as environmental pollution, be therefore widely used in various articles for daily use, such as various tableware, fruit tray, salad bowl, cutter, fork, outside the kitchen articles such as spoon, also be made into bath articles, its range of application is very extensive, but, because the resistance to ware of U.S. is widely used, how to promote its advantage, reduce its manufacturing cost, make it more to meet modern Man's Demands, become the emphasis that technical staff falls over each other research and inquirement, and the vessel structure of the resistance to ware of existing U.S., have U.S.'s vessel of resistance to ware that are wooden and/or similar material composition that have of No. M323265th, the patent No., it is by resistance to ware material portion of U.S., melamine applique resin material portion, and multiple xylem is formed, its Sino-U.S. resistance to ware material portion utilizes the U.S. powder of resistance to ware/grain material hot pressing to be formed, fuse into one with melamine applique resin, and stick together and be coated on multiple xylem and make the U.S. vessel of resistance to ware, and resistance to ware material portion of U.S. of its above-mentioned material, melamine applique resin material portion, and xylem all need first indivedual formed via hot pressing after, then the heat of mixing is pressed into the U.S. vessel of resistance to ware, and namely need through repeatedly hot pressing, work processed is complicated, and manufacturing cost is high, the vessel structure of the resistance to ware of another kind of existing U.S., i.e. a kind of U.S.'s vessel of resistance to ware with secondary material component of No. I304384th, patent No. number, it utilizes the powder of U.S. resistance to ware or granular former material to borrow U.S.'s resistance to ware material of hot-forming processing procedure and hot pressing formation, after mixing with U.S.'s particle of resistance to ware shape secondary material of hot-forming mistake, again through once hot-forming, its feature is its these particle shape secondary materials, and no longer hot melt is softening, therefore, these are irregular, not of uniform size and the particle shape secondary material of multiple color, its color and shape can know be apparent in the U.S. vessel of resistance to ware outer surface on, but, this kind of U.S.'s vessel of resistance to ware, the U.S. secondary of the resistance to ware material of its U.S. used resistance to ware material all needs through hot-forming action, and this U.S. secondary of resistance to ware material also needs through pulverization process, need again hot-forming after U.S.'s resistance to ware material mixes with U.S. secondary of resistance to ware material, whole processing procedure is complicated, manufacturing cost still can be in any more.
Summary of the invention
The vessel of the resistance to ware of U.S. of the present invention, its purpose of design, at minimizing processing procedure, reduces costs, has simultaneously and can specify according to client, makes U.S.'s vessel of resistance to ware of various interesting or imitative pottery.
The vessel of the resistance to ware of U.S. of the present invention, the vessel of the resistance to ware of a kind of U.S., is characterized in that, are the vessel formed body utilizing once hot-forming process to make, comprise the U.S. powder of resistance to ware material, the U.S. grain of resistance to ware material, phenolic moulding powder/grain and urea powder/grain, wherein:
The U.S. grain of resistance to ware material is granular by U.S.'s powder of resistance to ware material system of coagulating, and it mixes with U.S. powder of resistance to ware material, makes the U.S. vessel of resistance to ware, and its color can be apparent on the outer surface of the U.S. vessel of resistance to ware by hot-forming.
U.S.'s powder of the resistance to ware material wherein mixed with U.S. grain of resistance to ware material is solid color, and can or U.S. resistance to ware grain material mixing hot pressing that varies in size identical with single or multiple color, grain type size and make the U.S. vessel of resistance to ware.
Its Sino-U.S.'s grain of resistance to ware material can be replaced by phenolic moulding powder/grain or urea powder/grain, gets it suitably and the ratio of safety non-toxic and U.S.'s powder of resistance to ware material heat of mixing are pressed into the U.S. vessel of resistance to ware.
Its Sino-U.S.'s powder of resistance to ware material can be replaced by phenolic moulding powder/grain or urea powder/grain, gets it suitably and the ratio of safety non-toxic and U.S.'s grain of resistance to ware material heat of mixing are pressed into the U.S. vessel of resistance to ware.
Wherein phenolic moulding powder/grain or urea powder/grain can get it suitably and the ratio of safety non-toxic and U.S.'s powder of resistance to ware material and the U.S. grain of resistance to ware material heat of mixing are pressed into the U.S. vessel of resistance to ware.
Vessel for the resistance to ware of U.S., are the vessel formed body utilizing once hot-forming processing procedure to make, comprise the U.S. grain of resistance to ware material, phenolic moulding powder/grain and urea powder/grain, wherein:
The U.S. grain of resistance to ware material is granular by U.S.'s powder of resistance to ware material system of coagulating, makes U.S.'s grain of resistance to ware mutual heat of mixing of material of two or more color be pressed into the U.S. vessel of resistance to ware, and its color can be apparent on the outer surface of the U.S. vessel of resistance to ware.
The grain type size of its Sino-U.S.'s grain of resistance to ware material is identical or vary in size.
Its Sino-U.S.'s grain of resistance to ware desirable part of material is replaced by phenolic moulding powder/grain or urea powder/grain, gets it suitably and the ratio of safety non-toxic and U.S.'s grain of resistance to ware material heat of mixing are pressed into the U.S. vessel of resistance to ware.
The present invention has the following advantages:
The present invention generates heat the U.S. grain of resistance to ware material according to need, by U.S.'s powder of resistance to ware material directly solidifying system form the granular of shades of colour and size, completely without the need to through hot-forming processing procedure, and itself and U.S.'s powder of resistance to ware material are mixed and made into the whole processing procedure of U.S. resistance to ware, only need through once hot-forming, namely can be made into the vessel of U.S. resistance to ware, manufacture quicker, and more reduce manufacturing cost.
Because U.S. of the present invention grain of resistance to ware material is can not break with during U.S.'s powder of resistance to ware material mixing hot pressing, only meeting diffusion deformation, therefore it is after U.S. powder of resistance to ware material is combined, and can display clear for its color, forms the vessel of the resistance to ware of U.S. of various interesting or imitative ceramic outward appearance.
The vessel of the resistance to ware of U.S. of various interesting or imitative ceramic outward appearance can be formed due to the present invention, therefore according to the demand of corporate boss, the color of the change U.S. grain of a resistance to ware material can be borrowed to create its resistance to ware of exclusive U.S., more meet the needs of each technical field.
Accompanying drawing explanation
Fig. 1 is stereogram of the present invention.
In figure:
1: the U.S. vessel of resistance to ware;
10: the U.S. powder of resistance to ware material;
11: the U.S. grain of resistance to ware material.
Detailed description of the invention
Below in conjunction with the drawings and specific embodiments, the invention will be further described, can better understand the present invention and can be implemented, but illustrated embodiment is not as a limitation of the invention to make those skilled in the art.
The vessel (referring to shown in Fig. 1) of the resistance to ware of U.S. of the present invention, its U.S.'s vessel of resistance to ware 1 made can be moulding required arbitrarily, by U.S.'s powder of resistance to ware material 10 and coagulated by U.S.'s material of resistance to ground rice and make granular U.S.'s grain of resistance to ware material 11 fully after mix and blend, add hot pressing and form the U.S. vessel of resistance to ware 1, wherein, U.S.'s powder of resistance to ware material 11 that should mix mutually with U.S.'s grain of resistance to ware material 11 is in solid color; The U.S. grain of resistance to ware material 11 is formed by U.S.'s powder of resistance to ware material system of coagulating, and can be various different colours, not of uniform size granular.
Make U.S.'s powder of resistance to ware material 10 and the solid color of solid color, U.S.'s grain of resistance to ware material 11 that size is identical is mutually fully uniformly mixed and is hot pressed into the vessel of resistance to ware 1, because U.S.'s grain of resistance to ware material 11 is can not break with during U.S.'s powder of resistance to ware material 10 Hybrid Heating injection-compression molding, only diffusion can be out of shape, and its color clearly can be apparent in the outer surface of the U.S. vessel of resistance to ware 1, and form U.S.'s vessel of resistance to ware 1 of various interesting or imitative pottery.
Before hot pressing, color selecting can be carried out with regard to U.S.'s powder of resistance to ware material 10 of solid color, and after the proportion of composing allocating the large and small grain of the U.S. grain of a resistance to ware material 11 and color, then carry out hot pressing, make needed for the finished product made meets.
The present invention also can make two or more color, U.S.'s grain of resistance to ware material 11 not of uniform size is hot pressed into the U.S. vessel of resistance to ware 1 with the mutual mix and blend of U.S.'s powder of resistance to ware material 11 of solid color.
U.S. of the present invention vessel of resistance to ware 1 also can be heated pressure injection and be become the U.S. vessel of resistance to ware 1 by two or more color, the mutual mix and blend of size U.S.'s grain of resistance to ware material 11 that is identical or that vary in size.
U.S. of the present invention grain of resistance to ware material 11 also can be replaced by phenolic moulding powder/grain or urea powder/grain, gets it suitably and the ratio of safety non-toxic and U.S.'s powder of resistance to ware material 10 heat of mixing are pressed into the U.S. vessel of resistance to ware 1.
U.S. of the present invention powder of resistance to ware material 10 also can be replaced by phenolic moulding powder/grain or urea powder/grain, gets it suitably and the ratio of safety non-toxic and U.S.'s grain of resistance to ware material 11 heat of mixing are pressed into the U.S. vessel of resistance to ware 1.
Phenolic moulding powder/grain that the present invention is above-mentioned or urea powder/grain also desirable its suitably and the ratio of safety non-toxic and U.S.'s powder of resistance to ware material 10 and the U.S. grain of resistance to ware material 11 heat of mixing are pressed into the U.S. vessel of resistance to ware 1.
The above embodiment is only that protection scope of the present invention is not limited thereto in order to absolutely prove the preferred embodiment that the present invention lifts.The equivalent alternative or conversion that those skilled in the art do on basis of the present invention, all within protection scope of the present invention.Protection scope of the present invention is as the criterion with claims.
Claims (8)
1. vessel for the resistance to ware of U.S., is characterized in that, are the vessel formed body utilizing once hot-forming process to make, comprise the U.S. powder of resistance to ware material, the U.S. grain of resistance to ware material, phenolic moulding powder/grain and urea powder/grain, wherein:
The U.S. grain of resistance to ware material is granular by U.S.'s powder of resistance to ware material system of coagulating, and it mixes with U.S. powder of resistance to ware material, makes the U.S. vessel of resistance to ware, and its color can be apparent on the outer surface of the U.S. vessel of resistance to ware by hot-forming.
2. the vessel of the resistance to ware of U.S. according to claim 1, it is characterized in that, U.S.'s powder of the resistance to ware material wherein mixed with U.S. grain of resistance to ware material is solid color, and can or U.S. resistance to ware grain material mixing hot pressing that varies in size identical with single or multiple color, grain type size and make the U.S. vessel of resistance to ware.
3. the vessel of the resistance to ware of U.S. according to claim 1, is characterized in that, its Sino-U.S.'s grain of resistance to ware material can be replaced by phenolic moulding powder/grain or urea powder/grain, get it suitably and the ratio of safety non-toxic and U.S.'s powder of resistance to ware material heat of mixing are pressed into the U.S. vessel of resistance to ware.
4. the vessel of the resistance to ware of U.S. according to claim 1, is characterized in that, its Sino-U.S.'s powder of resistance to ware material can be replaced by phenolic moulding powder/grain or urea powder/grain, get it suitably and the ratio of safety non-toxic and U.S.'s grain of resistance to ware material heat of mixing are pressed into the U.S. vessel of resistance to ware.
5. the vessel of the resistance to ware of U.S. according to claim 1, is characterized in that, wherein phenolic moulding powder/grain or urea powder/grain can get it suitably and the ratio of safety non-toxic and U.S.'s powder of resistance to ware material and the U.S. grain of resistance to ware material heat of mixing are pressed into the U.S. vessel of resistance to ware.
6. vessel for the resistance to ware of U.S., is characterized in that, are the vessel formed body utilizing once hot-forming processing procedure to make, comprise the U.S. grain of resistance to ware material, phenolic moulding powder/grain and urea powder/grain, wherein:
The U.S. grain of resistance to ware material is granular by U.S.'s powder of resistance to ware material system of coagulating, makes U.S.'s grain of resistance to ware mutual heat of mixing of material of two or more color be pressed into the U.S. vessel of resistance to ware, and its color can be apparent on the outer surface of the U.S. vessel of resistance to ware.
7. the vessel of the resistance to ware of U.S. according to claim 6, is characterized in that, the grain type size of its Sino-U.S.'s grain of resistance to ware material is identical or vary in size.
8. the vessel of the resistance to ware of U.S. according to claim 6; it is characterized in that; its Sino-U.S.'s grain of resistance to ware desirable part of material is replaced by phenolic moulding powder/grain or urea powder/grain, gets it suitably and the ratio of safety non-toxic and U.S.'s grain of resistance to ware material heat of mixing are pressed into the U.S. vessel of resistance to ware.