JP3059680B2 - Method for forming composite insulator and manufacturing apparatus for composite insulator - Google Patents
Method for forming composite insulator and manufacturing apparatus for composite insulatorInfo
- Publication number
- JP3059680B2 JP3059680B2 JP24044896A JP24044896A JP3059680B2 JP 3059680 B2 JP3059680 B2 JP 3059680B2 JP 24044896 A JP24044896 A JP 24044896A JP 24044896 A JP24044896 A JP 24044896A JP 3059680 B2 JP3059680 B2 JP 3059680B2
- Authority
- JP
- Japan
- Prior art keywords
- forming
- core member
- jacket
- mold
- hollow core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、複合碍管成形用金
型を用いる複合碍管の成形方法に関する。ここに、複合
碍管とは、繊維強化プラスチック製の中空コア部材及び
該中空コア部材の外周面に絶縁性高分子材料で形成した
外被とを有する。一般には、外被は、中空コア部材の外
周面に沿って伸びる円筒状のシース部と軸方向に互いに
離間して形成される複数の笠部とから形成されている。
絶縁性高分子材料としては、例えばシリコーンゴム、エ
チレンープロピレン共重合体（ＥＰＤＭ），エチレンー
プロピレンージエン共重合体（ＥＰＤＭ）等が用いられ
る。本願でいう複合碍管は直円筒形状及びテーパ形状の
複合碍管を含む。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for forming a composite insulator using a composite insulator molding die. Here, the composite insulator has a hollow core member made of fiber reinforced plastic and a jacket formed of an insulating polymer material on the outer peripheral surface of the hollow core member. Generally, the jacket is formed of a cylindrical sheath portion extending along the outer peripheral surface of the hollow core member, and a plurality of cap portions formed apart from each other in the axial direction.
As the insulating polymer material, for example, silicone rubber, ethylene-propylene copolymer (EPDM), ethylene-propylene diene copolymer (EPDM) and the like are used. The composite insulator referred to in the present application includes a composite insulator having a straight cylindrical shape and a tapered shape.
【０００２】[0002]
【従来の技術】従来、複合碍管成形用金型を用いて複合
碍管を成形する場合、中空コア部材を金型内に配置し型
締めをした後、該中空コア部材の回りの外被形成用空隙
に外被形成材料を充填し、金型の温度を所定の外被形成
材料硬化温度まで上昇させ、この温度に所定の時間保持
することによって、外被形成材料を硬化させていた。2. Description of the Related Art Conventionally, when forming a composite insulator using a composite insulator molding die, a hollow core member is disposed in a mold, clamped, and then formed into a jacket around the hollow core member. The space is filled with the jacket material, the temperature of the mold is raised to a predetermined jacket material curing temperature, and the temperature is maintained for a predetermined time to cure the jacket material.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、金型の
みを加熱することによって外被形成材料を硬化する場合
には、外被形成材料の硬化時間が長くなり、生産性が悪
かった。また、金型を加熱して外被形成材料を硬化させ
る場合には金型内の外被形成用空隙の内壁部から中空コ
ア部材に向かって外被形成材料の硬化が進むので、加熱
硬化時の外被形成材料の内圧上昇が大きくそれに見合っ
て金型の締め付け力を大きくしなければならず、また装
置に要求される機械的強度も大きく設定する必要があっ
た。さらに、充填された外被形成材料の外周部から硬化
する場合、未硬化外被形成材料が内部に閉じ込められる
ことになり外被内の内圧が上昇するため、テーパ形状の
複合碍管の場合、中空コア部材に対する軸力が大きくな
り、その結果外被形成材料と中空コア部材の外表面との
間の接着性が低下する可能性もあった。However, when the jacket material is hardened by heating only the mold, the hardening time of the jacket material is prolonged, and the productivity is poor. In addition, when the mold is heated to cure the jacket material, the jacket material is hardened toward the hollow core member from the inner wall portion of the jacket forming gap in the mold. Accordingly, the internal pressure of the material for forming the outer cover increases greatly, and accordingly, the clamping force of the mold must be increased, and the mechanical strength required for the apparatus also needs to be set high. In addition, when the material is hardened from the outer peripheral portion of the filled material, the uncured material is confined inside and the internal pressure in the material increases. The axial force on the core member was increased, and as a result, there was a possibility that the adhesiveness between the envelope forming material and the outer surface of the hollow core member was reduced.
【０００４】[0004]
【課題を解決するための手段】本発明は、従来の複合碍
管成形用金型を用いる複合碍管の成形方法の有する問題
点を解消するもので、複合碍管成形用金型内に中空コア
部材を配置し、該中空コア部材の回りの外被形成用空隙
に室温硬化型シリコーンゴムからなる外被形成材料を充
填し、金型温度を所定の外被形成材料硬化温度まで上昇
させることにより外被形成材料を硬化させることによっ
て複合碍管を成形する方法であって、金型を加熱する前
から複合碍管の成形が完了する迄中空コア部材を所定の
温度に加熱することを特徴とする複合碍管の成形方法を
提供するものである。SUMMARY OF THE INVENTION The present invention solves the problems of the conventional method for forming a composite insulator using a composite insulator molding die, and includes a method for forming a hollow core member in a composite insulator molding die. It is arranged, and the space for forming the jacket around the hollow core member is filled with a jacket-forming material made of room-temperature-curable silicone rubber, and the mold is heated to a predetermined jacket-forming material curing temperature to thereby increase the jacket. A method of forming a composite insulator by curing a forming material, wherein the hollow core member is heated to a predetermined temperature before the mold is heated until the molding of the composite insulator is completed. A molding method is provided.
【０００５】さらに、本発明は、１対の金型ユニットか
らなる複合碍管成形用金型及び金型加熱手段を有し、該
金型ユニットのそれぞれには笠部及びシース部からなる
外被を中空コア部材の外周に形成するための外被形成空
隙が設けられ、複合碍管成形用金型内に中空コア部材を
配置し、型締めした後該中空コア部材の回りの外被形成
用空隙に外被形成材料を充填し、金型を所定の外被形成
材料硬化温度まで加熱することによって外被形成材料を
硬化させる複合碍管成形装置であって、さらに複合碍管
を金型内で成形時に中空コア部材を加熱する加熱手段を
備えていることを特徴とする複合碍管成形装置を提供す
るものである。Further, the present invention has a composite insulator tube forming mold and a mold heating means comprising a pair of mold units, and each of the mold units is provided with a jacket comprising a cap portion and a sheath portion. A jacket forming gap for forming on the outer periphery of the hollow core member is provided, and the hollow core member is disposed in the composite insulator molding die, and after clamping, the jacket forming gap is formed around the hollow core member. A composite porcelain tube molding device for curing a jacket material by filling a jacket material and heating a mold to a predetermined jacket material curing temperature, and further forming a hollow composite insulator tube in the mold during molding. An object of the present invention is to provide a composite porcelain tube forming apparatus, comprising a heating means for heating a core member.
【０００６】本発明の複合碍管成形用金型を用いる複合
碍管の成形方法及び複合碍管成形装置によれば、金型内
の外被形成空隙内に充填された外被形成材料を複合碍管
成形時に金型及び中空コア部材の両側から硬化させるこ
とができるので、外被形成材料の硬化時間を短縮するこ
とができ生産性を上げることが可能となる。また、金型
を加熱して外被形成材料を硬化させる場合には金型内の
外被形成用空隙の内壁部から中空コア部材に向かって及
び中空コア部材の外周面から外被形成用空隙の内壁部に
向かって外被形成材料の硬化が行われているので、加熱
硬化時の外被形成材料の内圧上昇を低減できそれに見合
って金型の締め付け力も低減でき得る。さらに、充填さ
れた外被形成材料の外周部から硬化する場合、未硬化外
被形成材料が内部に閉じ込められることによる外被内の
内圧の上昇が抑制されるため、テーパ形状の複合碍管の
場合、中空コア部材に対する軸力を小さくでき、その結
果外被形成材料と中空コア部材の外表面との間の接着性
が低下を防止できる。According to the method and the apparatus for forming a composite insulator using the composite mold for molding a composite insulator of the present invention, the material for forming the envelope filled in the cavity for forming the envelope in the mold is used for molding the composite insulator. Since the curing can be performed from both sides of the mold and the hollow core member, the curing time of the outer cover forming material can be shortened and the productivity can be increased. Further, when the mold is heated to cure the jacket forming material, the jacket forming gap is formed from the inner wall portion of the jacket forming gap in the mold toward the hollow core member and from the outer peripheral surface of the hollow core member. Since the coating material is hardened toward the inner wall portion, the rise in the internal pressure of the coating material during heat curing can be reduced, and the tightening force of the mold can be reduced correspondingly. Furthermore, in the case of hardening from the outer peripheral portion of the filled jacket forming material, the rise of the internal pressure in the jacket due to the uncured jacket forming material being confined inside is suppressed. In addition, the axial force on the hollow core member can be reduced, and as a result, a decrease in the adhesiveness between the jacket forming material and the outer surface of the hollow core member can be prevented.
【０００７】[0007]
【発明の実施の形態】以下に、本発明の実施の態様につ
いて述べる。本発明の複合碍管の成形方法では，例え
ば、中空コア部材を複合碍管成形用金型に設置した後、
型締めを行い室温硬化型ゴム（ＲＴＶ）あるいは低温硬
化型ゴム（ＬＴＶ）をゴム注入温度３０°で、複合碍管
成形用金型の中空コア部材の回りの外被形成用空隙に注
入し、その後中空コア部材を所定の温度及び時間で加熱
する。中空コア部材を加熱するには、例えば、中空コア
部材の中空部に所定温度の熱風を循環して流すことによ
って行う。The embodiments of the present invention will be described below. In the method for forming a composite insulator according to the present invention, for example, after the hollow core member is set in the composite insulator forming die,
The mold is clamped, and room temperature curing rubber (RTV) or low temperature curing rubber (LTV) is injected at a rubber injection temperature of 30 ° into the cavity for forming a jacket around the hollow core member of the composite insulator molding die, and thereafter The hollow core member is heated at a predetermined temperature and time. The heating of the hollow core member is performed, for example, by circulating hot air at a predetermined temperature in the hollow portion of the hollow core member.
【０００８】成形しようとする複合碍管の寸法が比較的
小さい場合には、即ち、外被形成用空隙が小さい場合に
は、該空隙内に外被形成材料が短時間で注入が完了する
ため、（１）中空コア部材の回りの外被形成用空隙に外
被形成材料を充填し、その後中空コア部材の内面を所定
の温度に加熱し、金型温度を所定の外被形成材料硬化温
度まで上昇させることによって、外被形成材料を硬化し
ても良いし、あるいは（２）外被形成用空隙に外被形成
材料を充填し、中空コア部材及び金型温度を所定の外被
形成材料硬化温度まで上昇させることによって、外被形
成材料を硬化しても良いし、（３）外被形成用空隙に外
被形成材料を充填し、中空コア部材または金型温度を所
定の外被形成材料硬化温度まで上昇させ所定時間後金型
又は中空コア部材を所定の外被形成材料硬化温度までに
加熱することによって、外被形成材料を硬化しても良
い。また、（４）中空コア部材を所定の外被形成材料硬
化温度に加熱した状態で外被形成用空隙に外被形成材料
を充填し、その後金型を所定の外被形成材料硬化温度に
加熱することによって外被形成材料を硬化させても良
い。When the size of the composite insulator tube to be formed is relatively small, that is, when the space for forming the jacket is small, the material for forming the jacket is completed within the gap in a short time. (1) Fill the jacket forming material around the hollow core member with the jacket forming material, and then heat the inner surface of the hollow core member to a predetermined temperature, and reduce the mold temperature to the predetermined jacket forming material curing temperature. The coating material may be cured by raising the temperature, or (2) the coating material is filled in the coating material forming gap, and the temperature of the hollow core member and the mold is set to a predetermined value. By raising the temperature to the temperature, the jacket forming material may be cured, or (3) the jacket forming material is filled in the jacket forming gap, and the hollow core member or the mold temperature is set to a predetermined jacket forming material. Mold or hollow core member after a predetermined time after raising to the curing temperature By heating up to a predetermined encrustation material curing temperature may be cured encrustation material. (4) Filling the jacket forming gap with the jacket forming material while the hollow core member is heated to the predetermined jacket forming material curing temperature, and then heating the mold to the predetermined jacket forming material curing temperature. By doing so, the outer cover forming material may be cured.
【０００９】複合碍管が比較的大型の場合には、金型あ
るいは中空コア部材を予め加熱しておいて、外被形成材
料を外被形成用空隙内に注入する場合には、注入された
外被形成材料が外被形成用空隙内部に均一に分配される
前に硬化し良好な複合碍管が得られない可能性がある。
従って、複合碍管が大型の場合には、外被形成材料を外
被形成用空隙内に注入後に中空コア部材の内面を所定の
温度に加熱し、金型温度を所定の外被形成材料硬化温度
まで上昇させることによって外被形成材料を硬化する。
この場合、上記中空コア部材の内面を先に所定の温度に
加熱し、その後金型を加熱することが好ましい。こうす
ることによって、充填された外被形成材料は中空コア部
材の外周面から硬化するため、硬化時の外被形成用空隙
内部の内圧の上昇を抑制でき、中空コア部材の外被形成
材料に対する軸力を抑制でき、それによって硬化初期で
の中空コア部材と外被形成材料との接着剥離を生じさせ
る力が低下し、また中空コア部材の外被形成材料に対す
る位置ずれを回避できる。なお、上記のように複合碍管
が比較的小さいかあるいは比較的大きいかどうかの基準
は当業者であれば容易に判断でき、それによって適正な
成形方法の選択が可能となる。When the composite insulator tube is relatively large, the mold or the hollow core member is heated in advance, and when the material for forming the jacket is injected into the space for forming the jacket, the injected outer material is used. Before the material to be formed is uniformly distributed inside the space for forming the outer cover, the material may be hardened and a good composite insulator may not be obtained.
Therefore, when the composite insulator tube is large, the inner surface of the hollow core member is heated to a predetermined temperature after the material for forming the jacket is injected into the space for forming the jacket, and the mold temperature is set to a predetermined curing temperature for the material for forming the jacket. The material is hardened by raising it to
In this case, it is preferable to first heat the inner surface of the hollow core member to a predetermined temperature and then heat the mold. By doing so, the filled outer cover forming material is cured from the outer peripheral surface of the hollow core member, so that an increase in the internal pressure inside the outer cover forming gap during curing can be suppressed, and the hollow core member with respect to the outer cover forming material The axial force can be suppressed, whereby the force that causes the adhesive between the hollow core member and the jacket forming material at the early stage of curing is reduced, and the displacement of the hollow core member with respect to the jacket forming material can be avoided. It should be noted that a criterion for determining whether the composite insulator tube is relatively small or relatively large as described above can be easily determined by those skilled in the art, and thereby an appropriate molding method can be selected.
【００１０】外被形成材料が、室温硬化型シリコーンゴ
ムの場合には、ゴム注入温度を例えば３０°Ｃとし、中
空コア部材及び金型の加熱温度を５０−８０°Ｃ、好ま
しくは６０°Ｃ近傍とし、好ましくは複合碍管の成形が
完了するまで中空コア部材の加熱を行う。例えば、金型
内部で形成材料を硬化させるのに従来では１時間かかっ
ていた場合に硬化時間を４０分位に短縮できる。When the material for forming the outer cover is a room-temperature-curable silicone rubber, the rubber injection temperature is, for example, 30 ° C. and the heating temperature of the hollow core member and the mold is 50-80 ° C., preferably 60 ° C. In the vicinity, preferably, the hollow core member is heated until the forming of the composite insulator tube is completed. For example, if it conventionally took one hour to cure the forming material inside the mold, the curing time can be reduced to about 40 minutes.
【００１１】通常、生産性及び離型性等を考慮して、所
定の時間金型内部で中空コア部材の外周に形成材料を硬
化した後複合碍管を金型から離型した後熟成炉において
例えば硬化温度より１０−２０°Ｃ高い温度で２４時間
２時硬化させる。Usually, in consideration of productivity, mold release, etc., after the forming material is hardened on the outer periphery of the hollow core member inside the mold for a predetermined time, the composite insulator tube is released from the mold, and then, for example, in an aging furnace. Cure at 2: 00 ° C for 2 hours at a temperature 10-20 ° C higher than the curing temperature.
【００１２】[0012]
【実施例】図１は、金型を用いた本発明の複合碍管の成
形方法を模式的に示す。図中、１は１対の金型ユニット
の一方の金型ユニットを示し、該金型ユニット１には、
笠部及びシース部からなる外被を中空コア部材の外周に
形成するための外被形成空隙２が設けられている。３は
外被形成空隙２の中央に配置したコア部材で、コア部材
３の両端部には取付け金具４が取付けられ金型の外被形
成空隙２の両端部に位置されている。取付け板の外側に
は封止板５が取り付け、封止板５の開口６を介してコア
部材の中空部は循環路で連結されている。循環路７には
加熱装置８、ブローア９及び開閉弁１０が配置され、所
定の温度の熱風を中空コア部材の中空部に循環させ中空
のコア部材を所定の温度に加熱するようになっている。
一方、金型は図示しない加熱装置によって加熱するよう
になっている。一対の金型ユニットを型締めしたのち、
上述したように外被形成材料を充填し、中空コア部材及
び金型を加熱することによって中空コア部材の外周部に
外被を形成し複合碍管を成形する。FIG. 1 schematically shows a method of forming a composite insulator tube of the present invention using a mold. In the figure, reference numeral 1 denotes one mold unit of a pair of mold units.
A jacket forming gap 2 for forming a jacket including a cap portion and a sheath portion on the outer periphery of the hollow core member is provided. Reference numeral 3 denotes a core member arranged at the center of the jacket-forming gap 2. At both ends of the core member 3, mounting brackets 4 are attached, and are located at both ends of the jacket-forming gap 2 of the mold. A sealing plate 5 is attached to the outside of the mounting plate, and the hollow portion of the core member is connected to the hollow portion of the core member by a circulation path through an opening 6 of the sealing plate 5. A heating device 8, a blower 9, and an on-off valve 10 are arranged in the circulation path 7, and circulate hot air of a predetermined temperature through the hollow portion of the hollow core member to heat the hollow core member to a predetermined temperature. .
On the other hand, the mold is heated by a heating device (not shown). After clamping the pair of mold units,
As described above, the sheath forming material is filled, and the hollow core member and the mold are heated to form a jacket on the outer peripheral portion of the hollow core member, thereby forming a composite insulator tube.
【図１】金型を用いた本発明の複合碍管の成形方法を模
式的に示す。FIG. 1 schematically shows a method for forming a composite insulator tube of the present invention using a mold.
１ 金型ユニット、２ 金型外被形成空隙、３ コア部
材、４取付け金具、５ 封止板、６ 開口、７ 循環
路、８ 加熱装置、９ ブローア、１０ 開閉弁DESCRIPTION OF SYMBOLS 1 Mold unit, 2 Mold jacket space, 3 core members, 4 mounting brackets, 5 sealing plates, 6 openings, 7 circulation paths, 8 heating devices, 9 blowers, 10 opening / closing valves
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ // Ｂ２９Ｋ 83:00 105:20 (56)参考文献 特開 平８−1828（ＪＰ，Ａ) 特開 平８−185747（ＪＰ，Ａ) 特開 平８−174568（ＪＰ，Ａ) 特開 平１−152021（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) H01B 17/00 - 19/04 B29C 39/00 - 39/44 ──────────────────────────────────────────────────続 き Continuation of the front page (51) Int.Cl. 7 Identification code FI // B29K 83:00 105: 20 (56) References JP-A-8-1828 (JP, A) JP-A 8-185747 ( JP, A) JP-A-8-174568 (JP, A) JP-A-1-152202 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) H01B 17/00-19/04 B29C 39/00-39/44
Claims (6)
置し、該中空コア部材の回りの外被形成用空隙に室温硬
化型シリコーンゴムからなる外被形成材料を充填し、金
型を所定の外被形成材料硬化温度まで加熱し外被形成材
料を硬化させることによって複合碍管を成形する方法に
おいて、金型を加熱する前から複合碍管の成形が完了す
る迄中空コア部材を所定の温度に加熱することを特徴と
する複合碍管の成形方法。A hollow core member is disposed in a composite insulator tube forming mold, and room temperature hardening is performed in a space for forming a jacket around the hollow core member.
In a method of forming a composite insulator tube by filling a jacket-forming material made of modified silicone rubber, heating the mold to a predetermined jacket-forming material curing temperature, and curing the jacket-forming material, the mold is heated. The molding of the composite insulator has been completed before
And heating the hollow core member to a predetermined temperature.
外被形成材料を充填し、次に中空コア部材を所定の温度
で所定の時間加熱し、その後金型を所定の外被形成材料
硬化温度まで加熱することによって外被形成材料を硬化
させることを特徴とする請求項１に記載の複合碍管の成
形方法。2. A space for forming a jacket around the hollow core member is filled with a jacket forming material, and then the hollow core member is heated at a predetermined temperature for a predetermined period of time. The method for forming a composite insulator tube according to claim 1, wherein the jacket forming material is cured by heating to a forming material curing temperature.
成用空隙に外被形成材料を充填することを特徴とする請
求項１に記載の複合碍管の成形方法。3. The method for forming a composite insulator tube according to claim 1, wherein the sheath forming material is filled in the jacket forming gap while the hollow core member is heated.
空部に熱風を循環させて流すことによって行うことを特
徴とする請求項１乃至３のいずれかに記載の複合碍管の
成形方法。4. The method for forming a composite insulator tube according to claim 1, wherein the heating of the hollow core member is performed by circulating hot air through a hollow portion of the hollow core member.
用金型及び金型加熱手段を有し、該金型ユニットのそれ
ぞれには笠部及びシース部からなる外被を中空コア部材
の外周に形成するための外被形成空隙が設けられ、複合
碍管成形用金型内に中空コア部材を配置し、型締めした
後該中空コア部材の回りの外被形成用空隙に外被形成材
料を充填し、金型を所定の外被形成材料硬化温度まで加
熱することによって外被形成材料を硬化させる複合碍管
成形装置であって、さらに複合碍管を金型内成形時に中
空コア部材を加熱する加熱手段を備えていることを特徴
とする複合碍管成形装置。5. A mold for forming a composite insulator tube comprising a pair of mold units and a mold heating means, wherein each mold unit is provided with a jacket comprising a cap portion and a sheath portion of a hollow core member. A jacket forming gap for forming on the outer periphery is provided, a hollow core member is arranged in a composite insulator forming mold, and after the mold is clamped, a jacket forming material is formed in the jacket forming gap around the hollow core member. filled with the mold a composite hollow insulator forming apparatus for curing the encrustation material by heating to a predetermined encrustation material curing temperature, further medium <br/> empty composite porcelain bushing during the molding A composite insulator forming apparatus comprising a heating means for heating a core member.
空部に熱風を循環させる熱風循環手段であることを特徴
とする請求項５に記載した複合碍管成形装置。6. A composite insulator tube forming apparatus according to claim 5, wherein said hollow core member heating means is hot air circulation means for circulating hot air in a hollow portion of said core member.