JP3018330B2 - Manufacturing method of artificial stone - Google Patents
Manufacturing method of artificial stoneInfo
- Publication number
- JP3018330B2 JP3018330B2 JP1252746A JP25274689A JP3018330B2 JP 3018330 B2 JP3018330 B2 JP 3018330B2 JP 1252746 A JP1252746 A JP 1252746A JP 25274689 A JP25274689 A JP 25274689A JP 3018330 B2 JP3018330 B2 JP 3018330B2
- Authority
- JP
- Japan
- Prior art keywords
- slag
- artificial stone
- manufacturing
- electric furnace
- molten
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 産業上の利用分野 本発明は電気炉製鋼過程で発生する溶融スラグから人
造石を製造する方法に関する。Description: TECHNICAL FIELD The present invention relates to a method for producing artificial stone from molten slag generated in an electric furnace steelmaking process.
従来の技術及び発明が解決しようとする問題点 従来、アルミニウム等の還元剤で鉄等の有価金属を回
収した後の溶融電気炉スラグは、冷却後破砕されて一部
が砕石として利用されているだけで大部分は産業廃棄物
として処理されており、十分に有効利用されていないの
が現状である。Problems to be Solved by Conventional Techniques and Inventions Conventionally, molten electric furnace slag after recovering valuable metals such as iron with a reducing agent such as aluminum is crushed after cooling and partially used as crushed stone. However, most of them are treated as industrial waste and are not fully utilized at present.
問題点を解決するための手段 本発明はこのような問題点を解決するための手段とし
て、電気炉スラグから還元鉄を回収した後の溶融状態に
ある残留スラグ中に空気を用いてランス管から珪砂と含
硼素化合物を吹き込んで改質した後、型枠に流し込んで
冷却するようにした。Means for Solving the Problems The present invention, as means for solving such problems, uses air in the molten slag after recovering the reduced iron from the electric furnace slag, using a lance tube from the lance tube. After reforming by blowing silica sand and a boron-containing compound, the mixture was poured into a mold and cooled.
発明の効果 天然石に近い人造石が得られる。Effect of the Invention An artificial stone close to natural stone can be obtained.
実施例 1 電気炉スラグから還元鉄等の有価金属を回収すると同
時に、スラグの成分を調整するために、アルミ灰、塩化
ナトリウム、弗化カルシウム及び金属珪素粉から構成さ
れる添加剤Aを溶融スラグに吹き込む。Example 1 At the same time as recovering valuable metals such as reduced iron from electric furnace slag, an additive A composed of aluminum ash, sodium chloride, calcium fluoride and metal silicon powder was melted to adjust the components of the slag. Blow into
即ち第1図に示す滓鍋1に第1表左欄の組成を有する
溶融電気炉スラグ5トンを充填して、添加剤A1,200Kgを
ランス管2から2.5〜5kg/cm2の窒素をキヤリアガスとし
て6〜10分間吹き込んだところ、滓鍋1の底に溶鋼3が
溜まつたので取出口栓4を抜いて溶鋼3を抜いた後、残
留スラグ5に含硼素化合物と珪砂から構成される添加剤
B1,000Kgを空気を用いてランス管2から吹き込んだとこ
ろ、激しくバブリングしながら反応しスラグ中に溶融し
た。このようにして改質された残留スラグの組成を第1
表右欄に示す。That is, the slag pot 1 shown in FIG. 1 is filled with 5 tons of molten electric furnace slag having the composition shown in the left column of Table 1 and 1,200 kg of the additive A is supplied from a lance tube 2 with 2.5 to 5 kg / cm 2 of nitrogen. When the molten steel 3 was collected at the bottom of the slag pot 1, the outlet plug 4 was removed and the molten steel 3 was removed. Then, the residual slag 5 was added with a boron-containing compound and silica sand. Agent
When 1,000 kg of B was blown in from the lance tube 2 using air, it reacted while bubbling vigorously and melted in the slag. The composition of the residual slag thus modified is
It is shown in the right column of the table.
この改質残留スラグを型枠に流し込んで冷却固化した
後、表面を研磨した結果、暗緑色の光沢のある強固な人
造石が得られた。これは建材、特に、壁や床の化粧材と
して好適である。又、この人造石をみかげ石と比較する
と組成は相当異なるが物性は第2表に示すように類似
し、特に曲げ強度、硬度、耐熱性に於いてはみかげ石よ
り優れている。 The modified residual slag was poured into a mold, cooled and solidified, and the surface was polished. As a result, a dark green glossy and strong artificial stone was obtained. This is suitable as a building material, especially as a decorative material for walls and floors. The composition of this artificial stone is considerably different from that of granite, but the physical properties are similar as shown in Table 2, and are superior to granite in bending strength, hardness and heat resistance.
第1図は本発明の実施に使用する滓鍋の断面図である。 1:滓鍋、2:ランス管、3:溶鋼、5:溶融スラグ FIG. 1 is a sectional view of a slag pot used for carrying out the present invention. 1: slag pot, 2: lance tube, 3: molten steel, 5: molten slag
Claims (1)
融状態にある残留スラグ中に空気を用いてランス管から
珪砂と含硼素化合物を吹き込んで改質した後、型枠に流
し込んで冷却する人造石の製造方法。1. A method in which silica sand and a boron-containing compound are reformed by blowing air into a molten slag after recovery of reduced iron from an electric furnace slag from a lance tube using air, and then poured into a mold to cool. Manufacturing method of artificial stone.