JP3017265B2 - 光記録媒体 - Google Patents

光記録媒体

Info

Publication number
JP3017265B2
JP3017265B2 JP2265364A JP26536490A JP3017265B2 JP 3017265 B2 JP3017265 B2 JP 3017265B2 JP 2265364 A JP2265364 A JP 2265364A JP 26536490 A JP26536490 A JP 26536490A JP 3017265 B2 JP3017265 B2 JP 3017265B2
Authority
JP
Japan
Prior art keywords
recording
recording medium
optical recording
recording film
wavelength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP2265364A
Other languages
English (en)
Other versions
JPH04141490A (ja
Inventor
高士 山田
文雄 松井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pioneer Corp
Original Assignee
Pioneer Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pioneer Corp filed Critical Pioneer Corp
Priority to JP2265364A priority Critical patent/JP3017265B2/ja
Priority to DE19914112402 priority patent/DE4112402A1/de
Publication of JPH04141490A publication Critical patent/JPH04141490A/ja
Priority to US07/999,659 priority patent/US5292615A/en
Application granted granted Critical
Publication of JP3017265B2 publication Critical patent/JP3017265B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、光記録媒体、特に主成分としてフタロシア
ニン系色素を含有する記録膜を有する光記録媒体に関す
る。
〔従来の技術〕 光記録媒体は、一般に記憶容量が大きく、しかも書き
込みまたは読み出しが非接触で行なわれる等、優れた特
徴を備えており、その開発が従来から活発に行なわれて
きている。
このような光記録媒体の１例として、例えば追記型光
ディスクがあり、このものは、記録膜の微小面積にレー
ザビームを集光させ、それを熱エネルギーに変換し、記
録膜の性状を変えて（ピット形成）記録し、未記録部分
との反射光量の違いによって再生を行うようにしてい
る。
このような媒体の記録膜の材質としては、大きな反射
率変化を与えるものが好ましく、また無害であること、
そして、より高感度化する必要があること、より製造コ
ストを安価にする必要があることから、色素を主とした
有機材料系の記録膜を用いた光記録媒体の提案が種々な
されている（特開昭第58−112790号公報、同第58−1149
89号公報、同第58−125246号公報、同第60−71295号公
報等）。
このような有機材料系の色素を記録膜として実用化す
るに当たっては、上記の特性を満足することはもとよ
り、特に読み出し光による再生劣化を防止し、しかも情
報を長期にわたって確実に保存できるように、極めて優
れた耐光性、耐環境性が要求される。
このような耐光性に優れる色素としては、フタロシア
ニン系色素が良く知られている。
〔発明が解決しようとする課題〕
しかしながら、フタロシアニン系色素は、他の色素に
比べて分解点が高く、しかも通常の記録波長域に吸収を
示さない。そのためこのものを用いた記録膜にレーザビ
ームを照射しピットを形成した場合、形状の整ったきれ
いなピットが形成されず、ピット後尾部が融解流動し、
尾を引く形状となる。そのため、記録再生波形におい
て、いわゆるハンプ（hump）現象が生じ、十分な再生特
性がとれないという不都合が生じる。
そこで、本発明は、上記の問題点を解決し、耐光性に
優れ、しかも記録時に形状の整ったきれいなピットが形
成され、十分な再生特性を有する光記録媒体を提供する
ことを目的とする。
〔課題を解決するための手段〕
このような課題を解決するため、本発明は、基板上に
記録膜を有する光記録媒体において、前記記録膜は、フ
タロシアニン系色素と共に、レーザ記録波長の波長帯域
に吸収をもつ光吸収剤を、フタロシアニン系色素に対し
て５〜20wt％含有するように構成した。
本発明に用いられる基板は、光透過性であれば特に限
定はないが、生産性向上の観点から、いわゆる射出成形
基板が好ましい。射出成形基板とは、平板状の基板と、
この基板の片面に設けられるグルーブ、アドレス等とを
同一材料で一体的にワンショットの射出成形で形成した
基板をいう。
このような基板は、例えばポリカーボネート樹脂（P
C）、ポリメタクリル酸メチル樹脂（PMMA）等のプラス
チック材料から形成される。
このような基板上には、記録膜が成膜され、この記録
膜には、フタロシアニン系色素が主成分として、さらに
レーザ記録波長の波長帯域に吸収をもつ光吸収剤が添加
剤として含有される。
前記フタロシアニン系色素は、下記一般式［Ｉ］で表
わされる。
一般式［Ｉ］ 上記一般式［Ｉ］において、R1は直鎖アルキル基を表
し、R2は、Cl、CH3、SO2、芳香族化合物等を表し、Me
は、金属を表す。Meとしては、特に、Si、Ｖ、Fe、Al等
が好ましい。
さらに本発明の記録膜には、前述したように添加剤と
してレーザ記録波長の波長帯域に吸収をもつ光吸収剤が
含有される。レーザ記録波長の波長帯域は通常、760〜8
30nm程度であり、これらの波長帯域に光吸収特性を有す
る光吸収剤は、例えば、シアニン色素が挙げられる。な
かでも下記一般式［II］で示されるシアニン色素が特に
好ましい。
一般式［II］ 式［II］においてR3およびR4はそれぞれ、炭素数１〜
５、好ましくは１〜３のアルキル基を表し、R5は水素ま
たはこれに代わる置換基を表わす。置換基としては、例
えば、Cl、CH3、フェニル基等が挙げられる。ＸはCl
O4、Ｉ等のカウンターイオンを表す。
R3,R4,R5およびＸは、用いるレーザ記録波長の波長に
応じて適宜、選定される。
このような光吸収剤は，上記フタロシアニン系色素に
対して、５〜20wt％、より好ましくは５〜10wt％含有さ
れる。この値が20wt％を越えると、吸収による光反射が
著しく低下し、プレーヤビリティの欠除という不都合が
生じ、また、この値が5wt％未満になると、本来のフタ
ロシアニンの光記録膜の流動という不都合が生じる。
このようにフタロシアニン系色素および光吸収剤を含
有する記録膜は、例えばスピンコート法等の常用手段に
より塗設される。塗設される記録膜の厚さは40〜100nm
程度である。なお、塗布に用いる溶媒としては、ジアセ
トンアルコール、エチルセロソルブ、メチルセロソル
ブ、イソホロン、メタノール、テトラフルオロプロパノ
ール等が挙げられる。
本発明の記録媒体に適用されるレーザ光は前述したよ
うに波長760〜830nmの半導体レーザが好ましい。
本発明の記録媒体は、前述したように、いわゆる射出
成形基板上に記録膜を設けて形成されるが、このものを
２枚用意し、記録膜を対向して配置した、いわゆるエア
ーサンドイッチ構造としてもよい。
〔作用〕
本発明の媒体には、一般に回転下において、記録光が
パルス状に照射される。
このとき記録膜の一部が融解、除去されピットが形成
される。
このように形成されたピットは、やはり媒体の回転
下、読み出し光の反射光の差を検出することによって行
なわれる。
〔実施例〕
以下、本発明の実施例を示して本発明をさらに詳細に
説明する。
記録膜に含有されるフタロシアニン系色素としては、
ごく一般的なAlフタロシアニンを用い、光吸収剤として
は、ヘプタメチンシアニン色素を用い、これらをエチル
セロソルブ溶媒中に溶解し、直径13cmのポリカーボネー
ト（PC）基板上に、60nmの厚さに塗設し、本発明の光記
録媒体（本発明サンプル）を作製した。なお、光吸収剤
は、フタロシアニン系色素に対して10wt％とした。
次いで、比較サンプルとして光吸収剤を添加せずフタ
ロシアニン系色素のみとした記録膜を有するサンプルを
作製した（比較サンプル）。
これらの各サンプルについて、EFM信号、単一周波信
号（200KHz,400KHz）を以下の条件で記録再生した。
EEM信号記録条件 波長:780nm,線速:1.4m/s リードパワー:0.5mW, ライトパワー:6mW 単一周波信号（200KHz,400KHz） 波長:780nm、線速:1.4m/s リードパワー:0.5mW ライトパワー:6mW これらの記録再生波形を第１図〜第３図に示す。第１
図（ａ），第２図（ａ）および第３図（ａ）は本発明サ
ンプルを用いた場合、第１図（ｂ），第２図（ｂ）およ
び第３図（ｂ）は比較サンプルを用いた場合のものであ
る。第１図によれば本発明のサンプルは規則正しいアイ
パターンが形成されており、さらに第２図および第３図
によれば本発明のものはハンプ現象が生じておらず、本
発明サンプルの記録されたピットは、極めて歪みが少な
くきれいな形状に形成されていることが確認された。
また、さらに本発明サンプルの光吸収剤を、フタロシ
アニン系色素に対して2.5wt％、5wt％、10wt％、20wt
％、30wt％とした各種サンプルを作製し、上記と同様な
記録再生試験をおこなったところ、５〜20wt％の範囲の
ものが良好な結果が得られた。
〔発明の効果〕
以上の結果より本発明の効果は明らかである。
すなわち、本発明の光記録媒体の記録膜は、フタロシ
アニン系色素と、レーザ記録波長の波長帯域に吸収をも
つ光吸収剤とを含有するので、耐光性に優れ、しかも記
録時に形状の整ったきれいなピットが形成され、十分な
再生特性を有するという効果を奏する。
【図面の簡単な説明】
第１図乃至第３図は、それぞれEFM信号と単一波形信号
（200KHz,400KHz）の記録再生波形を示すグラフであ
る。
フロントページの続き (56)参考文献 特開 昭63−242588（ＪＰ，Ａ) 特開 昭64−9794（ＪＰ，Ａ) 特開 昭63−312892（ＪＰ，Ａ) 特開 昭63−306091（ＪＰ，Ａ) 特開 昭63−252792（ＪＰ，Ａ) 特開 平２−179790（ＪＰ，Ａ) 特開 平３−281288（ＪＰ，Ａ) 特開 平３−124488（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) B41M 5/26

Claims (2)

    (57)【特許請求の範囲】
  1. 【請求項１】基板上に記録膜を有する光記録媒体におい
    て、 前記記録膜は、フタロシアニン系色素と共に、レーザ記
    録波長の波長帯域に吸収をもつ光吸収剤を、フタロシア
    ニン系色素に対して５〜20wt％含有することを特徴とす
    る光記録媒体。
  2. 【請求項２】前記光吸収剤は、シアニン色素であること
    を特徴とする請求項１記載の光記録媒体。
JP2265364A 1990-10-03 1990-10-03 光記録媒体 Expired - Lifetime JP3017265B2 (ja)