JP2952290B2 - レタス包装用フィルム - Google Patents
レタス包装用フィルムInfo
- Publication number
- JP2952290B2 JP2952290B2 JP1227264A JP22726489A JP2952290B2 JP 2952290 B2 JP2952290 B2 JP 2952290B2 JP 1227264 A JP1227264 A JP 1227264A JP 22726489 A JP22726489 A JP 22726489A JP 2952290 B2 JP2952290 B2 JP 2952290B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- layer
- vinyl acetate
- heat
- multilayer laminate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 レタスは一般に非伸縮性の耐熱フィルムによって包装
されている。該フィルムは、ポリエチレン層に結合され
たポリエステル層を含む構造を有する。このフィルムは
低い水分透過度を有しており、この特性はレタス及び同
種の産物の包装に望ましい特性である。しかしながらこ
のフィルムはまた低い気体透過度を有している。このた
め、延伸してヒートセットされたポリエステルが使用さ
れているときは、刻んだレタスの保存期限が短い。
されている。該フィルムは、ポリエチレン層に結合され
たポリエステル層を含む構造を有する。このフィルムは
低い水分透過度を有しており、この特性はレタス及び同
種の産物の包装に望ましい特性である。しかしながらこ
のフィルムはまた低い気体透過度を有している。このた
め、延伸してヒートセットされたポリエステルが使用さ
れているときは、刻んだレタスの保存期限が短い。
この用途で代表的に使用されている別のヒートセット
フィルムの酸素透過率は、73゜F、1気圧、24時間で500
0cc/m2未満である。
フィルムの酸素透過率は、73゜F、1気圧、24時間で500
0cc/m2未満である。
レタス及び同種の産物の包装に関しては、高い気体透
過度、好ましくは5000cc/m2を上回る気体透過度を有
し、同時に食品からの水分損失を防ぐような低い水分透
過度を有する包装材料が望ましい。
過度、好ましくは5000cc/m2を上回る気体透過度を有
し、同時に食品からの水分損失を防ぐような低い水分透
過度を有する包装材料が望ましい。
発明の概要 本発明の1つの目的は、プロピレンホモポリマーまた
はコポリマーから成る多孔第1フィルムと、第1フィル
ムに結合されており、エチレン酢酸ビニルコポリマーか
ら成るコロナ処理された結合層と熱シール性外層とを有
する第2フィルムとを含む多層ラミネートを提供するこ
とである。
はコポリマーから成る多孔第1フィルムと、第1フィル
ムに結合されており、エチレン酢酸ビニルコポリマーか
ら成るコロナ処理された結合層と熱シール性外層とを有
する第2フィルムとを含む多層ラミネートを提供するこ
とである。
本発明の別の目的は、プロピレンホモポリマーまたは
コポリマーから成る多孔第1フィルムを準備し、エチレ
ン酢酸ビニルコポリマーから成る結合層と熱シール性外
層とを有する第2フィルムを同時押出し、第2フィルム
の結合面をコロナ処理し、次いで多孔フィルムに結合さ
せる多層ラミネートの製造方法を提供することである。
コポリマーから成る多孔第1フィルムを準備し、エチレ
ン酢酸ビニルコポリマーから成る結合層と熱シール性外
層とを有する第2フィルムを同時押出し、第2フィルム
の結合面をコロナ処理し、次いで多孔フィルムに結合さ
せる多層ラミネートの製造方法を提供することである。
添付図面に基づく以下の記載より本発明が更に十分に
理解されよう。
理解されよう。
具体例 第1図に示すように多層ラミネート10は開孔14を内在
させた多孔フィルム12を含む。好ましい具体例では層即
ちフィルム12がプロピレンホモポリマー(PP)から構成
されているが、エチレンプロピレンコポリマー(EPC)
のごときプロピレンコポリマーを使用してもよい。種々
のポリプロピレンホモポリマー及びコポリマーが市販さ
れており当業者に公知である。本発明に特に適したフィ
ルムの1つは、W.R.Graces & Co.−ConnのCryovac Div
isionから商品名PYで供給されている市販フィルムであ
る。
させた多孔フィルム12を含む。好ましい具体例では層即
ちフィルム12がプロピレンホモポリマー(PP)から構成
されているが、エチレンプロピレンコポリマー(EPC)
のごときプロピレンコポリマーを使用してもよい。種々
のポリプロピレンホモポリマー及びコポリマーが市販さ
れており当業者に公知である。本発明に特に適したフィ
ルムの1つは、W.R.Graces & Co.−ConnのCryovac Div
isionから商品名PYで供給されている市販フィルムであ
る。
第1図は更に同時押出フィルム16を示す。フィルム16
は結合層18と熱シール性外層20とを含む。好ましい具体
例では結合層18が酢酸ビニル含量の高い低融点エチレン
酢酸ビニルコポリマー(EVA)、例えばdu Pont社のAlat
hon3180から形成される。Alathon3180は、メルトインデ
ックス23〜27g/10分、酢酸ビニル含量27〜29重量%及び
密度約0.948〜0.954g/cm3を有する。熱シール性外層20
は層18と同じ材料から形成されてもよく、または別のエ
チレン酢酸ビニルコポリマー、例えばExxon32.89から形
成されてもよい。Exxon32.89は酢酸ビニル含量約4.5%
のEVAである。層20はまた極低密度ポリエチレン(VLDP
E)から形成されてもよい。
は結合層18と熱シール性外層20とを含む。好ましい具体
例では結合層18が酢酸ビニル含量の高い低融点エチレン
酢酸ビニルコポリマー(EVA)、例えばdu Pont社のAlat
hon3180から形成される。Alathon3180は、メルトインデ
ックス23〜27g/10分、酢酸ビニル含量27〜29重量%及び
密度約0.948〜0.954g/cm3を有する。熱シール性外層20
は層18と同じ材料から形成されてもよく、または別のエ
チレン酢酸ビニルコポリマー、例えばExxon32.89から形
成されてもよい。Exxon32.89は酢酸ビニル含量約4.5%
のEVAである。層20はまた極低密度ポリエチレン(VLDP
E)から形成されてもよい。
第2フィルム16の結合層18の材料として酢酸ビニル含
量の低いEVA樹脂、例えば上記Exxon32.89を使用しても
よい。しかしながら、第2フィルム16を第1フィルム12
に結合するときは、酢酸ビニル含量の低いEVA樹脂は酢
酸ビニル含量の高い樹脂例えば上記のdu Pont社の材料
ほどすぐれた効果を発揮できない。結合層18に最適のEV
A樹脂の特徴は酢酸ビニル含量が高く同時に比較的低い
融点を有することである。
量の低いEVA樹脂、例えば上記Exxon32.89を使用しても
よい。しかしながら、第2フィルム16を第1フィルム12
に結合するときは、酢酸ビニル含量の低いEVA樹脂は酢
酸ビニル含量の高い樹脂例えば上記のdu Pont社の材料
ほどすぐれた効果を発揮できない。結合層18に最適のEV
A樹脂の特徴は酢酸ビニル含量が高く同時に比較的低い
融点を有することである。
第2図は第1図と同様の多層ラミネート21を示すが、
第2フィルム16の結合層18と熱シール性外層20との間に
コア層22が設けられている。結合用コア層22に好ましい
樹脂は線状低密度ポリエチレン(LLDPE)、例えば密度
約0.921g/ccを有するDow社製のDowlex2045である。
第2フィルム16の結合層18と熱シール性外層20との間に
コア層22が設けられている。結合用コア層22に好ましい
樹脂は線状低密度ポリエチレン(LLDPE)、例えば密度
約0.921g/ccを有するDow社製のDowlex2045である。
第3図に示す本発明の別の変形具体例においては、好
ましくはエチレン酢酸ビニルコポリマーから成る中間層
26及び24がコア層22と結合層18との間及びコア層と熱シ
ール性外層20との間に夫々設けられている。これらの中
間層26及び24は層間結合強度の強化、同時押出フィルム
16及びラミネート30の全体的な強度の強化、その他の加
工適性の改良のごとき種々の効果を発揮する。
ましくはエチレン酢酸ビニルコポリマーから成る中間層
26及び24がコア層22と結合層18との間及びコア層と熱シ
ール性外層20との間に夫々設けられている。これらの中
間層26及び24は層間結合強度の強化、同時押出フィルム
16及びラミネート30の全体的な強度の強化、その他の加
工適性の改良のごとき種々の効果を発揮する。
中間層24,26に特に適した樹脂はdu Pont社のElvax PE
−3508である。この材料は、酢酸ビニル含量約12重量%
及びメルトインデックス約0.3g/10分を有する。
−3508である。この材料は、酢酸ビニル含量約12重量%
及びメルトインデックス約0.3g/10分を有する。
多孔フィルム12はポリプロピレンまたはエチレンプロ
ピレンコポリマーフィルムを押出し、火炎穿孔またはニ
ードル穿孔のごとき当業界で公知の手段によって該フィ
ルムは開孔を設けることによって製造され得る。
ピレンコポリマーフィルムを押出し、火炎穿孔またはニ
ードル穿孔のごとき当業界で公知の手段によって該フィ
ルムは開孔を設けることによって製造され得る。
多層第2フィルム16は標準同時押出法によって製造さ
れ得る。
れ得る。
多層第2フィルム16の結合層18の結合面をコロナ処理
し、次いで好ましくはある程度の熱及び圧力下に第2フ
ィルム16を多孔フィルム12に接着することによって、第
2フィルム16を多孔フィルム12に結合させる。結合面は
符号40で図示されている。
し、次いで好ましくはある程度の熱及び圧力下に第2フ
ィルム16を多孔フィルム12に接着することによって、第
2フィルム16を多孔フィルム12に結合させる。結合面は
符号40で図示されている。
従来の貼合わせ接着剤を使用するその他の結合法は好
ましくない。
ましくない。
好ましい具体例によれば、本発明の包装用フィルムは
Kartidg−Pakまたはその他の垂直型充填密封機での使用
に特に適当である。
Kartidg−Pakまたはその他の垂直型充填密封機での使用
に特に適当である。
本発明に従って製造された特定のラミネート構造を示
す表Iを参照することによって本発明が更に十分に理解
されよう。 表I 実施例 1 PP//EVA/VLDPE 2 PP//EVA/LLDPE/EVA 3 PP//EVA/EVA/LLDPE/EVA/EVA 実施例3のフィルムにおいて結合層18及び熱シール性
外層20のEVAの約20%が押出以前にEVAとプレブレンドさ
れたアンチブロッキング剤を含んでいた。使用したアン
チブロッキング剤は90%の低密度ポリエチレンと10%の
コロイドシリカマスターバッチとのブレンドから成る。
す表Iを参照することによって本発明が更に十分に理解
されよう。 表I 実施例 1 PP//EVA/VLDPE 2 PP//EVA/LLDPE/EVA 3 PP//EVA/EVA/LLDPE/EVA/EVA 実施例3のフィルムにおいて結合層18及び熱シール性
外層20のEVAの約20%が押出以前にEVAとプレブレンドさ
れたアンチブロッキング剤を含んでいた。使用したアン
チブロッキング剤は90%の低密度ポリエチレンと10%の
コロイドシリカマスターバッチとのブレンドから成る。
本発明を特定具体例に及び実施例に基づいて説明した
が、特許請求の範囲の要旨及び範囲を逸脱することなく
種々の変形が可能であることは上記の説明から当業者に
容易に理解されよう。
が、特許請求の範囲の要旨及び範囲を逸脱することなく
種々の変形が可能であることは上記の説明から当業者に
容易に理解されよう。
第1図は本発明の多層ラミネートの概略断面図、第2図
は本発明の多層ラミネートの変形具体例の概略断面図、
第3図は本発明の多層ラミネートの別の変形具体例の概
略断面図である。 10,21,30……多層ラミネート、12……第1フィルム、14
……開孔、16……第2フィルム、18……結合層、20……
外層、22……コア層、24,26……中間層。
は本発明の多層ラミネートの変形具体例の概略断面図、
第3図は本発明の多層ラミネートの別の変形具体例の概
略断面図である。 10,21,30……多層ラミネート、12……第1フィルム、14
……開孔、16……第2フィルム、18……結合層、20……
外層、22……コア層、24,26……中間層。
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 FI B65D 81/24 B65D 81/24 D (56)参考文献 特開 昭51−42783(JP,A) 特開 昭64−38226(JP,A) 特開 昭61−290050(JP,A) 特開 昭63−178948(JP,A) (58)調査した分野(Int.Cl.6,DB名) B32B 1/00 - 35/00
Claims (12)
- 【請求項1】(a)プロピレンホモポリマーまたはコポ
リマーから成る多孔第1フィルムと、 (b)第1フィルムに結合されており、エチレン酢酸ビ
ニルコポリマーから成るコロナ処理された結合層と熱シ
ール性外層とを有する第2フィルムとを含むことを特徴
とする多層ラミネート。 - 【請求項2】多孔第1フィルムがプロピレンホモポリマ
ーから成ることを特徴とする請求項1に記載の多層ラミ
ネート。 - 【請求項3】第2フィルムの結合層が、酢酸ビニル含量
27〜29重量%のエチレン酢酸ビニルコポリマーから成る
ことを特徴とする請求項1に記載の多層ラミネート。 - 【請求項4】エチレン酢酸ビニルコポリマーの酢酸ビニ
ル含量が、樹脂の約4.5〜28重量%の範囲であることを
特徴とする請求項1に記載の多層ラミネート。 - 【請求項5】第2フィルムの熱シール性外層がエチレン
酢酸ビニルコポリマーから成ることを特徴とする請求項
1に記載の多層ラミネート。 - 【請求項6】第2フィルムの熱シール性外層が結合層と
同じ材料から成ることを特徴とする請求項5に記載の多
層ラミネート。 - 【請求項7】更に、線状低密度ポリエチレンから成るコ
ア層が結合層と熱シール性外層との間に設けられている
ことを特徴とする請求項5に記載の多層ラミネート。 - 【請求項8】エチレン酢酸ビニルコポリマー層から成る
中間層が、コア層と結合層との間及びコア層と熱シール
性外層との間に夫々設けられこれらの層を互いに結合し
ていることを特徴とする請求項7に記載の多層ラミネー
ト。 - 【請求項9】第2フィルムの熱シール性外層が極低密度
ポリエチレンから成ることを特徴とする請求項1に記載
の多層ラミネート。 - 【請求項10】第2フィルムの熱シール性外層が、エチ
レン酢酸ビニルコポリマーとアンチブロッキング剤マス
ターバッチとのブレンドから成ることを特徴とする請求
項1に記載の多層ラミネート。 - 【請求項11】第2フィルムの熱シール性外層が、約80
%のエチレン酢酸ビニルコポリマーと約20%のアンチブ
ロッキング剤マスターバッチとのブレンドから成ること
を特徴とする請求項10に記載の多層ラミネート。 - 【請求項12】(a)プロピレンホモポリマーまたはコ
ポリマーから成る多孔フィルムを準備し、 (b)エチレン酢酸ビニルコポリマーから成る結合層と
熱シール性外層とを有する第2フィルムを同時押出し、 (c)同時押出第2フィルムの結合面をコロナ処理し、
次に第2フィルムを多孔フィルムに結合させることを特
徴とする多層ラミネートの製造方法。