JP2800620B2 - How to cut transformer core - Google Patents
How to cut transformer coreInfo
- Publication number
- JP2800620B2 JP2800620B2 JP2351093A JP2351093A JP2800620B2 JP 2800620 B2 JP2800620 B2 JP 2800620B2 JP 2351093 A JP2351093 A JP 2351093A JP 2351093 A JP2351093 A JP 2351093A JP 2800620 B2 JP2800620 B2 JP 2800620B2
- Authority
- JP
- Japan
- Prior art keywords
- cutting
- iron core
- plate
- cut
- peripheral side
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】[0001]
【産業上の利用分野】本発明は、変圧器鉄心の切断方法
に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for cutting a transformer core.
【0002】[0002]
【従来の技術】従来、アモルファス磁性薄帯を積層した
変圧器鉄心を切断砥石により切断する場合、鉄心の積層
方向の上下にそれぞれ一枚のとも切板を当てて、鉄心と
ともに2箇所でクランプしていた。これは主に切断部の
クランプ力の強化を目的としたものである。2. Description of the Related Art Conventionally, when a transformer core laminated with an amorphous magnetic ribbon is cut with a cutting wheel, one cutting plate is applied to each of the upper and lower sides in the lamination direction of the core, and clamped at two places together with the core. I was This is intended mainly to enhance the clamping force of the cutting portion.
【0003】[0003]
【発明が解決しようとする課題】しかしながら従来の技
術によるこの方法では、切断砥石に付着した削りくずや
溶融物が側面から鉄心に入り込んでしまい、その結果熱
による切断面の劣化をきたしている。そこで、本発明は
切断砥石に付着した削りくずや溶融物が鉄心に入り込む
のを防止し、熱による鉄心の切断面の劣化を軽減できる
ようにしたものである。However, in this method according to the prior art, shavings and melt adhered to the cutting wheel enter the core from the side surface, and as a result, the cut surface is deteriorated by heat. Therefore, the present invention prevents shavings and molten material adhering to the cutting grindstone from entering the iron core and reduces the deterioration of the cut surface of the iron core due to heat.
【0004】[0004]
【課題を解決するための手段】本発明では、アモルファ
ス磁性薄帯を積層した鉄心の外周側と内周側の相対向す
る位置にそれぞれ一枚のとも切板を当てて上記鉄心をこ
のとも切板と共に2箇所でクランプするとともに、その
2箇所のクランプ位置の間において上記鉄心の少なくと
も切断砥石が入り込む側の側面に保護板を当てて固定
し、その状態で上記2箇所のクランプ位置の間において
上記鉄心を上記とも切板および保護板とともに切断砥石
により切断する。According to the present invention, an iron core on which an amorphous magnetic thin ribbon is laminated is provided with a single cutting plate at opposing positions on the outer peripheral side and the inner peripheral side of the iron core, and the iron core is cut. At the same time as the plate is clamped at two places, and between the two clamp positions, a protective plate is applied and fixed to at least the side surface of the iron core on the side where the cutting grindstone enters, and in that state, between the two clamp positions The above-mentioned iron core is cut together with the cutting plate and the protection plate by a cutting whetstone.
【0005】[0005]
【作用】鉄心を切断砥石により切断すると、切断砥石は
回転しながら連続的に鉄心に入り込むため、切断中の切
断砥石の外周および側面は直前に鉄心を切ったときに発
生した削りくずや溶融物が付着したまま新たに鉄心に入
り込もうとする。ここで切断砥石が鉄心を切断する直前
にとも切板および保護板を切断することにより切断砥石
に付着している削りくずや溶融物が取り除かれた状態
で、切断を行うことができる。[Function] When the iron core is cut by a cutting whetstone, the cutting whetstone continuously enters the iron core while rotating. Therefore, the outer circumference and side surfaces of the cutting whetstone being cut are shavings and molten material generated when the iron core was cut immediately before. Will try to enter the iron core newly with adhered. Here, the cutting can be performed in a state in which the shavings and the melt adhered to the cutting whetstone have been removed by cutting the cutting plate and the protection plate even immediately before the cutting whetstone cuts the iron core.
【0006】[0006]
【実施例】図1に本発明の方法の一例を示す。鉄心1は
アモルファス磁性薄帯を積層した変圧器用のもので、そ
の外周側と内周側の相対向する位置にそれぞれ1枚のと
も切板2を当てて、それぞれ押え棒4と押え台5により
2箇所でクランプする。押え棒4と押え台5は、ボルト
6によりクランプを行い、ボルト6と鉄心1の側面との
間の隙間に保護板3を当てて、2箇所のクランプ位置で
のボルト6と保持用くさび8とにより鉄心1の側面に固
定する。この状態のまま切断砥石7を回転させながら2
箇所のクランプ位置の間を移動させ、とも切板2および
保護板3とともに鉄心1を切断する。切断砥石7を移動
させるかわりに鉄心1を移動させてもよい。FIG. 1 shows an example of the method of the present invention. An iron core 1 is for a transformer in which amorphous magnetic ribbons are laminated, and a pair of cutting plates 2 are applied to opposing positions on the outer peripheral side and the inner peripheral side, respectively. Clamp in two places. The presser bar 4 and the presser base 5 are clamped by bolts 6, and the protective plate 3 is applied to the gap between the bolts 6 and the side surface of the iron core 1, and the bolts 6 and the holding wedges 8 at two clamp positions are provided. Then, it is fixed to the side surface of the iron core 1. While rotating the cutting whetstone 7 in this state,
The iron core 1 is cut together with the cutting plate 2 and the protection plate 3 by moving between the clamp positions. Instead of moving the cutting whetstone 7, the iron core 1 may be moved.
【0007】なお、鉄心1の側面に当てる保護板3は必
要に応じて、図2の切断後の鉄心の断面に示すように、
鉄心1の両側面に設けてもよい。The protective plate 3 applied to the side surface of the iron core 1 may be provided, if necessary, as shown in the cross section of the cut iron core in FIG.
It may be provided on both sides of the iron core 1.
【0008】[0008]
【発明の効果】本発明によれば、切断砥石が鉄心を切断
する直前にとも切板および保護板を切断することによっ
て、切断砥石の外周および側面についた削りくずや溶融
物が除去され、熱による鉄心の切断面の劣化が少なくな
る。According to the present invention, by cutting the cutting plate and the protective plate immediately before the cutting wheel cuts the iron core, shavings and melts on the outer periphery and side surfaces of the cutting wheel are removed, and the heat is removed. Deterioration of the cut surface of the iron core due to the above.
【図1】本発明の方法の一例を示す図である。FIG. 1 shows an example of the method of the present invention.
【図2】本発明の方法の一例による切断後の断面を示す
図である。FIG. 2 is a diagram showing a cross section after cutting according to an example of the method of the present invention.
1 鉄心 2 とも切板 3 保護板 4 押え棒 5 押え台 6 ボルト 7 切断砥石 8 保持用くさび DESCRIPTION OF SYMBOLS 1 Iron core 2 Cutting plate 3 Protective plate 4 Presser bar 5 Presser table 6 Bolt 7 Cutting whetstone 8 Wedge for holding
Claims (1)
外周側と内周側の相対向する位置にそれぞれ一枚のとも
切板を当てて上記鉄心をこのとも切板とともに2箇所で
クランプするとともに、その2箇所のクランプ位置の間
において上記鉄心の少なくとも切断砥石が入り込む側の
側面に保護板を当てて固定し、その状態で上記2箇所の
クランプ位置の間において上記鉄心を上記とも切板およ
び保護板とともに切断砥石により切断する変圧器鉄心の
切断方法。1. An iron core on which an amorphous magnetic thin ribbon is laminated, a pair of cutting plates are respectively applied to opposing positions on an outer peripheral side and an inner peripheral side, and the iron core is clamped together with the cutting plate at two places. , Between the two clamp positions, at least a side surface of the iron core on the side where the cutting grindstone enters is fixed by applying a protective plate, and in that state, between the two clamp positions, the iron core is also a cutting plate. A cutting method for transformer cores that is cut with a cutting wheel together with a protection plate.