JP2023018654A - 歯付ベルトおよびその製造方法 - Google Patents
歯付ベルトおよびその製造方法 Download PDFInfo
- Publication number
- JP2023018654A JP2023018654A JP2022107110A JP2022107110A JP2023018654A JP 2023018654 A JP2023018654 A JP 2023018654A JP 2022107110 A JP2022107110 A JP 2022107110A JP 2022107110 A JP2022107110 A JP 2022107110A JP 2023018654 A JP2023018654 A JP 2023018654A
- Authority
- JP
- Japan
- Prior art keywords
- rubber layer
- rubber
- mass
- tooth
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
ベルト周方向に沿って延びる心線が埋設された背部と、
前記背部の内周面に、ベルト周方向に間隔をおいて形成された複数の歯部とを備え、
前記心線に対してベルト外周側に形成されている背ゴム層と、前記心線に対してベルト内周側に形成されている第1ゴム層および第2ゴム層とを含み、かつ
ベルト内周面が歯布で構成された歯付ベルトであって、
前記背部は前記背ゴム層を含み、
前記第1ゴム層の弾性率が前記第2ゴム層の弾性率よりも大きく、
前記歯部が、前記歯布と、前記歯布に沿って形成された前記第1ゴム層と、この第1ゴム層と前記心線との間に介在する前記第2ゴム層とを含む。
前記第2ゴム層が、第2ゴム成分、第2架橋剤および第2共架橋剤を含む第2架橋ゴム組成物で形成され、
前記第1ゴム成分が、水素化ニトリルゴムと不飽和カルボン酸金属塩とを含む第1複合ポリマーを含み、
前記第2ゴム成分が、水素化ニトリルゴムと不飽和カルボン酸金属塩とを含む第2複合ポリマーを含み、
前記第1共架橋剤の割合が、前記第1ゴム成分100質量部に対して1~40質量部であり、かつ
前記第2共架橋剤の割合が、前記第2ゴム成分100質量部に対して0.2~25質量部である態様である。
前記第1架橋ゴム組成物が、第1補強性無機充填剤をさらに含み、
前記第2架橋ゴム組成物が、第2補強性無機充填剤をさらに含み、
前記第1複合ポリマーの割合が、前記第1ゴム成分中80質量%以上であり、
前記第2複合ポリマーの割合が、前記第2ゴム成分中30質量%以上であり、
前記第1架橋剤が第1有機過酸化物を含み、前記第1有機過酸化物の割合が、前記第1ゴム成分100質量部に対して1~20質量部であり、
前記第2架橋剤が第2有機過酸化物を含み、前記第2有機過酸化物の割合が、前記第2ゴム成分100質量部に対して0.5~5質量部であり、
前記第1補強性無機充填剤の割合が、前記第1ゴム成分100質量部に対して10質量部以下であり、かつ
前記第2補強性無機充填剤の割合が、前記第2ゴム成分100質量部に対して10質量部以下である態様である。
以下に、必要に応じて、添付図面を参照しつつ、本発明の歯付ベルトの一例について詳細に説明する。
歯部は、表面が歯布で構成されており、歯部の輪郭に沿って、歯布と接する表面側(内表面側)に配置される第1ゴム層と、第1ゴム層と接する内部側に配置される第2ゴム層とを含む。第1ゴム層と第2ゴム層とは、異なる架橋ゴム組成物で形成され、第1ゴム層の弾性率(モジュラス)が相対的に大きく、第2ゴム層の弾性率(モジュラス)が相対的に小さい。本発明の歯付ベルトでは、歯部を形成する架橋ゴム組成物がこのような二層構造を有することにより、歯部の剛性と屈曲性とを両立できる。このメカニズムについて、図3を参照して説明する。なお、本願において、歯部を形成するゴム層は、心線と歯布との間に介在するゴム層を意味する。また、歯部を形成するゴム層である第1ゴム層と第2ゴム層とを総称して歯ゴム層と呼ぶ。
第1ゴム層および第2ゴム層は、歯付ベルトのゴム組成物として慣用的に利用されている架橋ゴム組成物で形成されていてもよい。架橋ゴム組成物は、ゴム成分を含む架橋ゴム組成物であってもよく、組成物の組成を適宜調整することにより、ゴム層を構成する各層、特に第1ゴム層および第2ゴム層の弾性率(モジュラス)などの機械的物性を調整できる。弾性率(モジュラス)等の調整方法としては、特に限定されず、組成物を構成する成分の組成および/または種類を変えて調整してもよく、簡便性などの点から、架橋系配合剤、短繊維、フィラーの割合および/または種類を変えて調整するのが好ましい。
第1ゴム層および第2ゴム層を形成する架橋ゴム組成物のゴム成分(第1ゴム成分および第2ゴム成分)としては、例えば、ジエン系ゴム[天然ゴム(NR)、イソプレンゴム(IR)、ブタジエンゴム(BR)、クロロプレンゴム(CR)、ブチルゴム(IIR)、スチレン-ブタジエンゴム(SBR)、ビニルピリジン-スチレン-ブタジエンゴム、アクリロニトリル-ブタジエンゴム(ニトリルゴム:NBR)、アクリロニトリル-クロロプレンゴム、水素化ニトリルゴム(HNBR)など]、エチレン-α-オレフィンエラストマー(エチレン-プロピレン共重合体(EPM)、エチレン-プロピレン-ジエン三元共重合体(EPDM)など)、クロロスルホン化ポリエチレンゴム(CSM)、アルキル化クロロスルホン化ポリエチレンゴム(ACSM)、エピクロルヒドリンゴム、アクリル系ゴム、シリコーンゴム、ウレタンゴム、フッ素ゴムなどが例示できる。これらのゴム成分は、カルボキシル化SBR、カルボキシル化NBRなどのように、カルボキシル化されていてもよい。これらのゴム成分は、単独でまたは二種以上組み合わせて使用できる。
架橋ゴム組成物(第1架橋ゴム組成物および第2架橋ゴム組成物)は、充填系配合剤(フィラー)をさらに含んでいてもよい。充填系配合剤(第1充填系配合剤および第2充填系配合剤)としては、補強性無機充填剤、非補強性充填剤、短繊維などが例示できる。
ゴム組成物は、ゴム成分を架橋させるための架橋剤(加硫剤)が配合され、必要に応じて、共架橋剤、架橋助剤(加硫助剤)、架橋促進剤(加硫促進剤)、架橋遅延剤(加硫遅延剤)などが配合される。これらのうち、架橋系配合剤(第1架橋系配合剤および第2架橋系配合剤)は、少なくとも架橋剤および共架橋剤(架橋助剤)を含むのが好ましく、架橋剤と共架橋剤との組み合わせが特に好ましい。
架橋ゴム組成物は、歯付ベルトのゴム組成物に使用される慣用の添加剤をさらに含んでいてもよい。慣用の添加剤としては、例えば、金属酸化物(酸化カルシウム、酸化バリウム、酸化鉄、酸化銅、酸化チタン、酸化アルミニウムなど)、軟化剤(パラフィンオイルやナフテン系オイルなどのオイル類など)、加工剤または加工助剤(ステアリン酸またはその金属塩、ワックス、パラフィン、脂肪酸アマイドなど)、可塑剤[脂肪族カルボン酸系可塑剤(アジピン酸エステル系可塑剤、セバシン酸エステル系可塑剤など)、芳香族カルボン酸エステル系可塑剤(フタル酸エステル系可塑剤、トリメリット酸エステル系可塑剤など)、オキシカルボン酸エステル系可塑剤、リン酸エステル系可塑剤、エーテル系可塑剤、エーテルエステル系可塑剤など]、老化防止剤(酸化防止剤、熱老化防止剤、屈曲き裂防止剤、オゾン劣化防止剤など)、着色剤、粘着付与剤、可塑剤、カップリング剤(シランカップリング剤など)、安定剤(紫外線吸収剤、熱安定剤など)、難燃剤、帯電防止剤などが挙げられる。また、架橋ゴム組成物は、必要により、接着性改善剤(レゾルシン-ホルムアルデヒド共縮合物、アミノ樹脂など)を含んでいてもよい。これらの添加剤は、単独でまたは二種以上組み合わせて使用できる。
第1ゴム層および第2ゴム層の弾性率(モジュラス)は、ゴム層の弾性率に影響を及ぼす所定の成分とその量的割合を変化させて調整することができる。例えば、充填系配合剤(フィラー、短繊維)、架橋系配合剤[架橋剤、共架橋剤(ビスマレイミド類など)]などから選択された少なくとも一種の成分の含有量を、第2ゴム層よりも第1ゴム層で増加することにより調整してもよい。特に、本発明の歯付ベルトでは、共架橋剤(特に、ビスマレイミド類)の含有量の調整により、第1ゴム層と第2ゴム層との弾性率(引張弾性率)をバランスよく好適に調整でき、背反関係にある歯部の剛性(耐変形性)と屈曲性(しなやかさ)とを両立できる。
ベルト内周面(歯部および歯底部の表面)を構成する歯布は、例えば、織布、編布、不織布などの布帛などで形成してもよい。慣用的には織布(帆布)である場合が多く、ベルト幅方向に延在する経糸とベルト周方向に延在する緯糸とを織成してなる織物で構成される。織布の織り組織は、経糸と緯糸とが規則的に縦横方向に交差した組織であれば特に制限されず、平織、綾織(または斜文織)、朱子織(繻子織、サテン)などのいずれであってもよく、これらの組織を組み合わせた織り組織であってもよい。好ましい織布は、綾織および朱子織組織を有している。
歯布は、歯部の表面を構成するとともに、背部の歯部側の表面(歯底部の表面)も構成している。
背部は、内周面において前記歯部および歯底部が形成されるとともに、その外周面側では、ベルト外周面を形成する背ゴム層を有している。さらに、前記背ゴム層は、架橋ゴム組成物(第4架橋ゴム組成物)で形成されている。図1~3の態様では、歯部が形成されていない側の他方の表面(ベルト背面)は布帛(織布、編布、不織布等)で被覆されていないが、必要に応じて被覆されていてもよい。この布帛は、好ましい態様も含めて、歯布として例示された布帛から選択できる。
第4架橋ゴム組成物の硬度は、ベルトの曲げ剛性を小さくし、屈曲性(プーリとの巻き付け性)や耐屈曲疲労性を確保できる点から、歯部を構成する第1架橋ゴム組成物および第2架橋ゴム組成物の硬度よりも小さい方が好ましい。
背部には、前記背ゴム層の内周側において、ベルト周方向に沿って延びる心線が埋設されている。この心線は、抗張体として作用し、歯付ベルトの走行安定性および強度を向上できる。さらに、背部では、通常、ベルト周方向に沿って延びる撚りコードである心線が、ベルト幅方向に所定の間隔を空けて埋設されており、長手方向に平行な複数本の心線が配設されていてもよいが、生産性の点から、通常、螺旋状に埋設されている。螺旋状に配設する場合、ベルト長手方向に対する心線の角度は、例えば5°以下であってもよく、ベルト走行性の点から、0°に近いほど好ましい。
本発明の歯付ベルトは、例えば、以下の工法(予備成形工法)で作製してもよい。まず、歯布を形成する歯布前駆体、複数のゴム層を形成する未架橋ゴムシート、例えば、第1ゴム層(表部ゴム層)を形成する未架橋ゴムシート、第2ゴム層(内部ゴム層)を形成する未架橋ゴムシート、背ゴム層を形成する未加硫ゴムシートを作製する。
次に、歯付ベルトの歯部に対応する複数の溝部(凹条)を有する円筒状モールドの外周面に、歯布を形成する歯布前駆体を巻き付ける。続いて、その外周に第1ゴム層(表部ゴム層)を形成する未架橋ゴムシート、第2ゴム層(内部ゴム層)を形成する未架橋ゴムシートを、順に巻き付けた積層体を形成し、所定の装置でゴム組成物が軟化する程度の温度(例えば、70~90℃程度)に加熱しつつ、外周側から積層体を加圧し、未架橋ゴムシートのゴム組成物と歯布前駆体とを円筒状モールドの溝部(凹条)に圧入させて歯部を形成し、半架橋状態の予備成形体を得る。この圧入させて歯部を形成する過程で、歯布が歯部の輪郭に沿った形態に伸張して最表面に配置され、その内部側に第1ゴム層が歯部の輪郭に沿って配置され、さらに内部側に第2ゴム層が配置される層構造が形成される。
得られた予備成形体の外周面に、心線を構成する撚りコードを螺旋状に所定のピッチで(円筒状モールドの軸方向に所定のピッチを有するように)巻き付ける。さらにその外周側に、背ゴム層を形成する未架橋ゴムシートを巻き付けて未架橋のベルト成形体(未架橋積層体)を形成する。
最後に、円筒状モールドから脱型した架橋ベルトスリーブを所定の幅に切断することにより、複数の歯付ベルトが得られる。
HNBR:日本ゼオン(株)製「Zetpol2010」、ヨウ素価11mg/100mg
不飽和カルボン酸金属塩を含むHNBR:日本ゼオン(株)製「Zeoforte ZSC2295CX」、ベースHNBR:不飽和カルボン酸金属塩(質量比)=100:110、ベースHNBRのヨウ素価28mg/100mg
アラミド短繊維:帝人(株)製「コーネックス」、平均繊維長3mm、平均繊維径14μm
ステアリン酸:日油(株)製「ステアリン酸つばき」
カーボンブラックSRF:東海カーボン(株)製「シーストS」、平均粒子径66nm、ヨウ素吸着量26mg/g
シリカ:エボニック・デグサ・ジャパン(株)製「ウルトラシルVN-3」、比表面積155~195m2/g
炭酸カルシウム:丸尾カルシウム(株)製「スーパー#1500」、平均粒子径1.5μm
酸化亜鉛:堺化学工業(株)製「酸化亜鉛2種」、平均粒子径0.55μm
老化防止剤:p,p’-ジオクチルジフェニルアミン、精工化学(株)製「ノンフレックスOD3」
有機過酸化物:1,3-ビス(t-ブチルパーオキシイソプロピル)ベンゼン、理論活性酸素量9.45%
共架橋剤:N,N’-m-フェニレンジマレイミド、大内新興化学(株)製「バルノックPM」
可塑剤:(株)ADEKA製「アデカサイザーRS700」。
12Kのマルチフィラメント糸[東レ(株)製「トレカT700SC-12000」、単糸繊度0.67dtex、総繊度800tex]1本を片撚りした炭素繊維コード(12K-1/0,引張弾性率230GPa)を作製し、HNBR系オーバーコート処理剤による接着処理を行って、心線径1.1mmの心線を得た。
表2に示す織布をRFL処理液およびゴム糊を用いて浸漬処理して歯布前駆体を作製した。詳しくは、RFL処理は、表3に示す2種類のRFL処理液(RFL1、RFL2)を用い、RFL1、RFL2の順に浸漬処理を行った。さらに、ゴム糊処理も、表4に示す2種類のゴム糊(ゴム糊1、ゴム糊2)を用い、ゴム糊1、ゴム糊2の順に浸漬処理を行った。
歯部および背部(背ゴム層)を形成するための未架橋ゴムシートとして、表1に示す配合の各ゴム組成物について、バンバリーミキサーを用いて混練し、得られた混練ゴムをカレンダーロールで所定の厚みに圧延し、未架橋ゴムシートを作製した。未架橋ゴムシート中に含まれる短繊維は、圧延方向に配向していた。本願では、各ゴム組成物をR1~R12で表記する。
未架橋ゴムシートを温度165℃、時間30分でプレス加熱し、架橋ゴムシート(100mm×100mm×2mm厚み)を作製した。架橋ゴムシートを3枚重ね合わせた積層物を試料とし、JIS K6253(2012)(加硫ゴムおよび熱可塑性ゴム-硬さの求め方-)に規定されているスプリング式デュロメータ硬さ試験に準拠して、タイプDデュロメータを用いて、架橋ゴムシートの硬度(タイプD)を測定した。
未架橋ゴムシートを温度165℃、時間30分でプレス加熱し、架橋ゴムシート(100mm×100mm×2mm厚み)を作製し、JIS K6251(2017)に準じ、ダンベル状(5号形)に打ち抜いた試験片を作製した。短繊維を含む試料においては、短繊維の配列方向(列理平行方向)が引張方向となるようにダンベル状試験片を採取した。そして、試験片の両端をチャック(掴み具)で掴み、試験片を500mm/minの速度で引っ張り、所定の伸び(1%)を与えたときの引張力を試験片の初期断面積で除した値(1%伸びにおける引張応力)を引張弾性率(モジュラス)とした。各ゴム組成物の引張弾性率を表5に示す。
未架橋ゴムを温度165℃、時間30分でプレス加熱し、JIS K6254(2016)C法に準じた架橋ゴム試験片(円柱状;厚さ25mm、直径17.8mm)を作製した。短繊維を含む試料においては、短繊維の配列方向(列理平行方向)が円柱状試験片の周方向となるように配置した。そして、シリコーンオイルを塗布した金属板で試験片を挟み、試験片が5%のひずみに達するまで10mm/分の速度で圧縮し、直ちに10mm/分の速度で力を取り除く操作を、連続して更に3回繰り返して計4回の圧縮力とひずみとの関係(圧縮力-変形曲線)を記録した。そして、4回目の曲線を用いて、曲線の立ち上がる点を原点として1回目の圧縮前の試験片の厚さに対して圧縮ひずみ2%のときの圧縮力を、試験片の初期断面積で除した値(圧縮ひずみ2%における圧縮応力)を圧縮弾性率(モジュラス)とした。
実施例および比較例では、以下に示すように、本実施形態で説明した予備成形工法を用いて、全厚5.6mm、歯型G8M、歯高さ(歯布含む)3.5mm、歯ピッチ8mm、歯数140、周長1120mm、幅12mmの歯付ベルトを作製した。
歯付ベルトの歯部に対応する複数の溝部(凹条)を有するプレスモールド(平型)に、歯布を形成する歯布前駆体、第1ゴム層を形成する未架橋ゴムシート(R6、シート厚み0.20mm)、第2ゴム層を形成する未架橋ゴムシート(R2、シート厚み1.50mm)の順に積層し、温度90℃、プレス圧(面圧)20.2MPaの条件で160秒間プレスし、半架橋状態の予備成形体を作製した。
第1ゴム層を形成する未架橋ゴムシートの厚みを0.35mm、第2ゴム層を形成する未架橋ゴムシートの厚みを1.35mmとしたことを除いては、実施例1と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートの厚みを0.70mm、第2ゴム層を形成する未架橋ゴムシートの厚みを1.00mmとしたことを除いては、実施例1と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートの厚みを1.00mm、第2ゴム層を形成する未架橋ゴムシートの厚みを0.70mmとしたことを除いては、実施例1と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートの厚みを1.35mm、第2ゴム層を形成する未架橋ゴムシートの厚みを0.35mmとしたことを除いては、実施例1と同様の方法で歯付ベルトを作製した。
歯部を形成する未架橋ゴムシートをR2(シート厚み1.70mm)の1種類のみとしたことを除いては、実施例1と同様の方法で歯付ベルトを作製した。
歯部を形成する未架橋ゴムシートをR6(シート厚み1.70mm)の1種類のみとしたことを除いては、実施例1と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR2(シート厚み0.85mm)、第2ゴム層を形成する未架橋ゴムシートをR6(シート厚み0.85mm)としたことを除いては、実施例1と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR3(シート厚み0.70mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR4(シート厚み0.70mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR7(シート厚み0.70mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR8(シート厚み0.70mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR9(シート厚み0.70mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR3(シート厚み0.20mm)としたことを除いては、実施例1と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR7(シート厚み1.00mm)としたことを除いては、実施例4と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR7(シート厚み1.35mm)としたことを除いては、実施例5と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR3(シート厚み0.70mm)、第2ゴム層を形成する未架橋ゴムシートをR1(シート厚み1.00mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR6(シート厚み0.70mm)、第2ゴム層を形成する未架橋ゴムシートをR3(シート厚み1.00mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR8(シート厚み0.70mm)、第2ゴム層を形成する未架橋ゴムシートをR3(シート厚み1.00mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR7(シート厚み0.70mm)、第2ゴム層を形成する未架橋ゴムシートをR4(シート厚み1.00mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR9(シート厚み0.70mm)、第2ゴム層を形成する未架橋ゴムシートをR4(シート厚み1.00mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR7(シート厚み0.70mm)、第2ゴム層を形成する未架橋ゴムシートをR5(シート厚み1.00mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR9(シート厚み0.70mm)、第2ゴム層を形成する未架橋ゴムシートをR5(シート厚み1.00mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR9(シート厚み0.70mm)、第2ゴム層を形成する未架橋ゴムシートをR1(シート厚み1.00mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
第1ゴム層を形成する未架橋ゴムシートをR11(シート厚み0.70mm)、第2ゴム層を形成する未架橋ゴムシートをR10(シート厚み1.00mm)としたことを除いては、実施例3と同様の方法で歯付ベルトを作製した。
歯付ベルトについて、JIS K7106(1995)に従い、オルゼン式曲げ試験機を用いた曲げ試験より、歯付ベルトの曲げこわさErを求め、得られたErに下記式(1)より算出した歯付ベルトの断面2次モーメントIrを乗じて、下記式(2)より歯付ベルトの曲げ剛性ErIrを算出した。ここで、歯付ベルト試験片のサイズは、長さ:80mm、幅:12mm、厚み:2.1mmとするとともに、支柱間距離Sを25.4mm、荷重目盛100%における振り子のモ-メントMを0.343N・mとした。また、試験は、温度23±2℃、湿度65±5%の条件下で行った。曲げ剛性の値が小さいほど、屈曲性(しなやかさ)に優れることを示す。曲げ剛性の判定基準を以下に示す。
[式中、Ir:試験片の断面2次モーメント(mm4)、b:試験片の幅(mm)、h:試験片の厚み(mm)を示す]
ErIr=[(S×M)/300]×[N/(D×0.01745)] (2)
[式中、Er:試験片の曲げこわさ(N/mm2)、Ir:試験片の断面2次モーメント(mm4)、S:支点間距離(mm)、M:振り子モーメント(N・m)、D:曲げ角度(度)(1度=π/180=0.01745ラジアン)、N:曲げ角度(度)に対応する荷重目盛板の読み(%)を示す]。
a:曲げ剛性が700MPa未満(合格)
b:曲げ剛性が700MPa以上、800MPa未満(合格)
c:曲げ剛性が800MPa以上(不合格)。
図4に示すように、歯付ベルト1の歯部を歯せん断治具(歯付プーリの歯形状を想定した剛体)11の突起部11aに引っ掛け、1つの歯を一定圧力(締め付けトルク0.98cNm/1mm幅)で押え付けた状態で、オートグラフによって1mm/minの速度で引っ張った時の変位に対する歯荷重を歯部の剛性(歯剛性)と定義して評価した。変位に対する歯荷重の値は、数値が安定する3サイクル目を採用し、図5に示すように歯荷重50~400N/12mm幅の区間の線形近似により求めた。歯剛性の値が大きいほど、歯部の剛性(耐変形性)に優れることを示す。歯剛性の判定基準を以下に示す。
a:歯剛性が1300N/mm以上(合格)
b:歯剛性が1100N/mm以上、1300N/mm未満(合格)
c:歯剛性が1100N/mm未満(不合格)
2軸トルク測定試験機を使用し、駆動プーリ(歯数:22)と従動プーリ(歯数:22)との間に歯付ベルトを巻き掛けて、ベルト張力が230Nとなるようにプーリの軸間距離を調整した。そして、駆動プーリを1,800rpmで回転させてベルトを走行させながら従動プーリへの負荷を連続的に上げていき、ジャンピング(歯飛び)が発生した時の駆動プーリに掛かる負荷トルクをジャンピングトルクとして測定した。ジャンピングトルクの数値をジャンピング性の指標とし、ジャンピングトルク値が大きいほど歯飛びしにくい優れた歯付ベルトと云える。
a:ジャンピングトルクが1.10超え(補強効果あり)
b:ジャンピングトルクが1.00超え、1.10以下(補強効果あり)
c:ジャンピングトルクが1.00(補強効果なし)
d:ジャンピングトルクが1.00未満(補強効果なし)
駆動プーリ(歯数:22)と従動プーリ(歯数:22)とを備えた2軸走行試験機に歯付ベルトを取り付け、歯付ベルトに故障(歯部の欠損)が発生するまでの走行時間を走行寿命として測定した。歯付ベルトの取付張力は230N、駆動プーリの回転数は1800rpm、従動プーリの負荷は9.0kW、雰囲気温度は25℃(室温)とした。
a:故障までの走行時間が1.50超え(補強効果あり)
b:故障までの走行時間が1.00超え、1.50以下(補強効果あり)
c:故障までの走行時間が1.00(補強効果なし)
d:故障までの走行時間が1.00未満(補強効果なし)
ジャンピングトルクおよび耐久走行性を以下の判定基準で総合評価した。
Aランク:ジャンピングトルク、耐久走行が共にa判定である場合(合格)
Bランク:ジャンピングトルク、耐久走行が共にb判定、または一方がa判定/もう一方がb判定の場合(合格)
Cランク:ジャンピングトルク、耐久走行の一方がc判定、もう一方がaまたはb判定の場合(合格)
Dランク:ジャンピングトルク、耐久走行が共にc判定、または一方がd判定である場合(不合格)
歯部を、歯部の輪郭に沿って表面側に配置される第1ゴム層(表部ゴム層)と、歯部の内部に配置される第2ゴム層(内部ゴム層)との2層構造として、第1ゴム層を引張弾性率5.7MPaのR6(架橋ゴム)、第2ゴム層を引張弾性率2.3MPaのR2(架橋ゴム)で形成した歯付ベルトの例である。第2ゴム層の引張弾性率に対する第1ゴム層の引張弾性率の比は2.5である。なお、以下ではこの比(第1ゴム層の引張弾性率/第2ゴム層の引張弾性率)を「2層の引張弾性率の比」と表す。
比較例1は、歯部を形成するゴム層全体を、実施例1~5の第2ゴム層を形成した引張弾性率2.3MPa(相対的に低弾性率)のR2(架橋ゴム)のみで形成した歯付ベルトの例である。曲げ剛性は553MPa(a判定)で実施例よりも良好であったが、歯剛性は1,092N/mm(c判定)と不合格であった。動的性能では、ジャンピングトルクは101N・mと低く、耐久走行(故障までの走行時間)も52時間と短かった。そのため、比較例1は、総合判定としても不合格(Dランク)であった。
実施例1~5の中で、最も耐久走行性が優れていた実施例3(歯部の断面視で、歯部を構成する全ゴム層に対する第1ゴム層の占める面積の割合が40%)の構成に対し、実施例6~10は、第1ゴム層に異なる弾性率のゴム組成物を用いた歯付ベルトの例である。実施例6ではR3(引張弾性率3.1MPa)、実施例7ではR4(引張弾性率4.0MPa)、実施例3ではR6(引張弾性率5.7MPa)、実施例8ではR7(引張弾性率7.0MPa)、実施例9ではR8(引張弾性率9.2MPa)、実施例10ではR9(引張弾性率12.0MPa)を用い第1ゴム層を形成している。
歯部の断面視で、歯部を構成する全ゴム層に対する第1ゴム層の占める面積の割合(以下、面積割合)と、第1ゴム層の弾性率(第1ゴム層に含まれる第1共架橋剤の割合)との関連について検証した例である。実施例11は、補強効果の下限付近(面積割合が小さく、弾性率も小さい場合)の例であり、面積割合10%、引張弾性率3.1MPa(第1共架橋剤3質量部)としている。逆に、実施例12、13は補強効果の上限付近(面積割合が大きく、弾性率も大きい場合)の例であり、実施例12では面積割合60%、引張弾性率7.0MPa(第1共架橋剤14質量部)、実施例13では面積割合80%、引張弾性率7.0MPa(第1共架橋剤14質量部)としている。
実施例1~5の中で、最も耐久走行性が優れていた実施例3(歯部の断面視で、歯部を構成する全ゴム層に対する第1ゴム層の占める面積の割合が40%)の構成に対し、実施例14~21は、第1ゴム層および第2ゴム層に用いる架橋ゴム組成物の弾性率の組み合わせを変えた歯付ベルトの例である。
実施例22は、実施例1~21の中で最も耐久走行性が優れていた実施例7の構成(第1ゴム層がR4、第2ゴム層がR2)に対し、補強性無機充填剤(カーボンブラック)を用いない歯付ベルトの例である。すなわち、第1ゴム層はR4からカーボンブラックを除いた組成であるR11(引張弾性率3.9MPa)、第2ゴム層はR2からカーボンブラックを除いた組成であるR10(引張弾性率2.3MPa)の架橋ゴム組成物で形成した歯付ベルトの例である。
1a…歯部
1b…歯底部
1c…背部
2…歯布
3…第1ゴム層
4…第2ゴム層
5…心線
6…背ゴム層
Claims (7)
- ベルト周方向に沿って延びる心線が埋設された背部と、
前記背部の内周面に、ベルト周方向に間隔をおいて形成された複数の歯部とを備え、
前記心線に対してベルト外周側に形成されている背ゴム層と、前記心線に対してベルト内周側に形成されている第1ゴム層および第2ゴム層とを含み、かつ
ベルト内周面が歯布で構成された歯付ベルトであって、
前記背部は前記背ゴム層を含み、
前記第1ゴム層の弾性率が前記第2ゴム層の弾性率よりも大きく、
前記歯部が、前記歯布と、前記歯布に沿って形成された前記第1ゴム層と、この第1ゴム層と前記心線との間に介在する前記第2ゴム層とを含む歯付ベルト。 - 前記第1ゴム層の面積割合が、ベルト周方向の断面視において、前記第1ゴム層および前記第2ゴム層の合計面積に対して10~80面積%である請求項1記載の歯付ベルト。
- 前記第1ゴム層の引張弾性率が0.6~20MPaであり、前記第2ゴム層の引張弾性率が0.5~5MPaである請求項1または2記載の歯付ベルト。
- 前記第1ゴム層の引張弾性率が、前記第2ゴム層の引張弾性率に対して1.2~4倍である請求項1~3のいずれか一項に記載の歯付ベルト。
- 前記第1ゴム層が、第1ゴム成分、第1架橋剤および第1共架橋剤を含む第1架橋ゴム組成物で形成され、
前記第2ゴム層が、第2ゴム成分、第2架橋剤および第2共架橋剤を含む第2架橋ゴム組成物で形成され、
前記第1ゴム成分が、水素化ニトリルゴムと不飽和カルボン酸金属塩とを含む第1複合ポリマーを含み、
前記第2ゴム成分が、水素化ニトリルゴムと不飽和カルボン酸金属塩とを含む第2複合ポリマーを含み、
前記第1共架橋剤の割合が、前記第1ゴム成分100質量部に対して1~40質量部であり、かつ
前記第2共架橋剤の割合が、前記第2ゴム成分100質量部に対して0.2~25質量部である請求項1~4のいずれか一項に記載の歯付ベルト。 - 前記第1架橋ゴム組成物が、第1補強性無機充填剤をさらに含み、
前記第2架橋ゴム組成物が、第2補強性無機充填剤をさらに含み、
前記第1複合ポリマーの割合が、前記第1ゴム成分中80質量%以上であり、
前記第2複合ポリマーの割合が、前記第2ゴム成分中30質量%以上であり、
前記第1架橋剤が第1有機過酸化物を含み、前記第1有機過酸化物の割合が、前記第1ゴム成分100質量部に対して1~20質量部であり、
前記第2架橋剤が第2有機過酸化物を含み、前記第2有機過酸化物の割合が、前記第2ゴム成分100質量部に対して0.5~5質量部であり、
前記第1補強性無機充填剤の割合が、前記第1ゴム成分100質量部に対して10質量部以下であり、かつ
前記第2補強性無機充填剤の割合が、前記第2ゴム成分100質量部に対して10質量部以下である請求項5記載の歯付ベルト。 - 歯布を形成するための歯布前駆体と、第1ゴム層を形成するための未架橋ゴムシートと、第2ゴム層を形成するための未架橋ゴムシートとが積層した予備成形体を作製する予備成形工程を含む請求項1~6のいずれか一項に記載の歯付ベルトの製造方法。