JP2022524852A - ラピッドプロトタイピングプロセスまたはラピッドマニュファクチャリングプロセスで使用するための放射線硬化性組成物 - Google Patents
ラピッドプロトタイピングプロセスまたはラピッドマニュファクチャリングプロセスで使用するための放射線硬化性組成物 Download PDFInfo
- Publication number
- JP2022524852A JP2022524852A JP2021555160A JP2021555160A JP2022524852A JP 2022524852 A JP2022524852 A JP 2022524852A JP 2021555160 A JP2021555160 A JP 2021555160A JP 2021555160 A JP2021555160 A JP 2021555160A JP 2022524852 A JP2022524852 A JP 2022524852A
- Authority
- JP
- Japan
- Prior art keywords
- monomer
- mixture
- composition
- weight
- monomers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
(a)特に少なくとも1つの第1のモノマーとして、1,3,5-トリス(ヒドロキシアルキル)イソシアヌレートから誘導される少なくとも1つのトリアクリレートであって、ここで、ヒドロキシアルキル基は、それぞれ独立して1~8個のC原子を含み、特に3~8個のC原子を有し、直鎖状、分岐状および/または環状であり、特に1~6個のC原子、好ましくは1~4個のC原子、好ましくは1~3個のC原子を有し、特に好ましくはヒドロキシエチルであるものとするトリアクリレートと、任意に
(b)二価脂環式基を有する二官能性アクリレートおよび二価脂環式基を有する二官能性メタクリレートと、任意に
(c)特に少なくとも1つの第2のモノマーとして、脂環式基を有する少なくとも1つの単官能性アクリレートおよび/または脂環式基を有する単官能性メタクリレートと
を含む組成物が好ましい。
(i)組成物中に、アルカノールが1~6個のC原子を含むトリシクロデカンアルカノールをベースとする単官能性アクリレートエステルが15~25重量%存在し、任意に、アルカノールが1~6個のC原子を含むトリシクロデカンジアルカノールをベースとするジアクリレートエステルが5~15重量%存在し、ここで、全組成物は100重量%であるか、または
(ii)アルカノールが1~6個のC原子を含むトリシクロデカンジアルカノールをベースとするジアクリレートエステルが5~15重量%存在し、アルカノールが1~6個のC原子を含むトリシクロデカンアルカノールをベースとする単官能性アクリレートエステルが15~25重量%存在し、特に(ii)では、1,3,5-トリス(ヒドロキシアルキル)イソシアヌレートから誘導されるトリアクリレートが存在せず、ここで、全組成物は100重量%であるか、または
(iii)アルカノールが1~6個のC原子を含むトリシクロデカンアルカノールをベースとする単官能性アクリレートエステルと、アルカノールが1~6個のC原子を含むトリシクロデカンジアルカノールをベースとするジアクリレートエステルとを含む混合物が15~45重量%存在し、特に(iii)では、1,3,5-トリス(ヒドロキシアルキル)イソシアヌレートから誘導されるトリアクリレートが存在せず、ここで、全組成物は100重量%である。
- (a)少なくとも1つの第1のモノマーまたは第1のモノマーの混合物であって、対応する第1のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が120℃以上である第1のモノマーまたは第1のモノマーの混合物が40~99.99重量%存在し、かつ
- (b)少なくとも1つの第2のモノマーまたは第2のモノマーの混合物であって、対応する第2のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が100℃以下である第2のモノマーまたは第2のモノマーの混合物が0~60重量%、特に0~10重量%存在し、
- 少なくとも1つのさらなる成分であって、UVおよび/もしくはVisスペクトル領域の少なくとも1つの光開始剤、またはUVおよび/もしくはVisスペクトル領域の光開始剤系、ならびに任意にUVおよび/もしくはVisスペクトル領域の少なくとも1つの安定剤、ならびに任意に少なくとも1つの顔料および/もしくは染料、ならびにさらなる慣用的な添加剤を含むさらなる成分が0.01~5重量%存在し、
ここで、全組成物は100重量%であり、特に、周囲室温(約20℃~23℃)での組成物の粘度は、3000mPas以下、特に500~2500mPas未満である。
(e)二価アルキレン基を有する二官能性ウレタン(メタ)アクリレートから選択される少なくとも1つの二官能性ウレタン(メタ)アクリレート、および/または
(f.1)少なくとも1つの単官能性、三官能性、四官能性または多官能性モノマーであって、特にウレタン(メタ)アクリレートではないもの、特にポリエーテルのアクリレートエステルおよび/またはメタクリレートエステルであり、ポリエーテルのジメタクリレートエステル、ポリエーテルの三官能性、四官能性または多官能性メタクリレートエステル、ポリエーテルのジアクリレートエステル、ポリエーテルの三官能性、四官能性および/または多官能性アクリレートエステルから選択されるもの
を含むことができる。
(c)脂環式基を有する少なくとも1つの単官能性アクリレートおよび/または脂環式基を有する単官能性メタクリレートであって、特に(オクタヒドロ-4,7-メタノ-1H-インデニル)メタノールアクリレート、(オクタヒドロ-4,7-メタノ-1H-インデニル)メタノールメタクリレート、(オクタヒドロ-4,7-メタノ-1H-インデニル)エタノールアクリレートおよび(オクタヒドロ-4,7-メタノ-1H-インデニル)エタノールメタクリレートから選択されるもの、
(f.2)少なくとも1つの単官能性、二官能性、三官能性、四官能性または多官能性モノマーであって、特にウレタン(メタ)アクリレートではないもの、特にポリエーテルのアクリレートエステルおよび/またはメタクリレートエステルであり、ポリエーテルのジメタクリレートエステル、ポリエーテルの三官能性、四官能性または多官能性メタクリレートエステル、ポリエーテルのジアクリレートエステル、ポリエーテルの三官能性、四官能性および/または多官能性アクリレートエステルから選択されるもの
を含む第2のモノマーを含む組成物が好ましい。
(f.3)少なくとも1つの単官能性、三官能性、四官能性または多官能性モノマーであって、特にウレタン(メタ)アクリレートではないもの、特にポリエーテルのアクリレートエステルおよび/またはメタクリレートエステルであって、ポリエーテルのジメタクリレートエステル、ポリエーテルの三官能性、四官能性または多官能性メタクリレートエステル、ポリエーテルのジアクリレートエステル、ポリエーテルの三官能性、四官能性および/または多官能性アクリレートエステルから選択されるもの
を含むことができる。
- (a)第1のモノマーまたは第1のモノマーの混合物であって、対応する第1のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が120℃以上であり、第1のモノマーまたは第1のモノマーの混合物は、二価脂環式基を有する少なくとも1つの二官能性アクリレートおよび/または二価脂環式基を有する少なくとも1つの二官能性メタクリレート、および任意に二価アルキレン基を有する二官能性ウレタン(メタ)アクリレートから選択される少なくとも1つの二官能性ウレタン(メタ)アクリレートを含むものとする、第1のモノマーまたは第1のモノマーの混合物70~99.99重量%、特に80~99.99重量%と、
- 少なくとも(b)1つの第2のモノマーまたは第2のモノマーの混合物であって、対応する第2のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が100℃以下であり、第2のモノマーまたは第2のモノマーの混合物は、それぞれのホモポリマーのTGが30℃以上である少なくとも1つの第2のモノマーまたは第2のモノマーの混合物を含み、好ましくは、TGが30℃以上100℃以下の範囲である第2のモノマーが含まれており、特に好ましくは、TGが50℃以上100℃以下の範囲である第2のモノマーが含まれているものとする、第2のモノマーまたは第2のモノマーの混合物、特に単官能性および/または二官能性アクリレートおよび/またはメタクリレート、好ましくは二環式脂環式アクリレートおよび/またはメタクリレート0~30重量%、特に0~20重量%、好ましくは1~15重量%と、任意に、
- 第3のモノマーであって、それぞれのホモポリマーのTGが100℃超、特に105℃以上115℃以下、特に118℃以下である第3のモノマー0~10重量%と、
- 少なくとも1つのさらなる成分であって、UVおよび/もしくはVisスペクトル領域の少なくとも1つの光開始剤、またはUVおよび/もしくはVisスペクトル領域の光開始剤系、ならびに任意にUVおよび/もしくはVisスペクトル領域の少なくとも1つの安定剤、ならびに任意に少なくとも1つの顔料および/もしくは染料、ならびにさらなる慣用的な添加剤を含むさらなる成分0.01~5重量%と
を含むモノマーを含むことができる。
- (i)(a)第1のモノマーまたは第1のモノマーの混合物であって、対応する第1のモノマーまたは第1のモノマーの混合物のそれぞれのホモポリマーのTG(ガラス転移点)が120℃以上であり、第1のモノマーまたは第1のモノマーの混合物は、二価脂環式基を有する少なくとも1つの二官能性アクリレートおよび/または二価脂環式基を有する少なくとも1つの二官能性メタクリレート、および任意に二価アルキレン基を有する二官能性ウレタン(メタ)アクリレートから選択される少なくとも1つの二官能性ウレタン(メタ)アクリレートを含むものとする、第1のモノマーまたは第1のモノマーの混合物75~99.99重量%、特に80~99.99重量%と、
- 少なくとも(b)1つの第2のモノマーまたは第2のモノマーの混合物であって、対応する第2のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が100℃以下であり、第2のモノマーまたは第2のモノマーの混合物は、脂環式基を有する少なくとも1つの単官能性アクリレートおよび/または脂環式基を有する単官能性メタクリレートを含むものとする、第2のモノマーまたは第2のモノマーの混合物0~25重量%、特に0~20重量%、好ましくは1~20重量%と、
- 少なくとも1つのさらなる成分であって、UVおよび/もしくはVisスペクトル領域の少なくとも1つの光開始剤、またはUVおよび/もしくはVisスペクトル領域の光開始剤系、ならびに任意にUVおよび/もしくはVisスペクトル領域の少なくとも1つの安定剤、ならびに任意に少なくとも1つの顔料および/もしくは染料、ならびにさらなる慣用的な添加剤を含むさらなる成分0.01~5重量%と
を含むことができ、ここで、全組成物は100重量%であり、特に、周囲室温(約20℃~23℃)での組成物の粘度は、3000mPas以下、特に500~2500mPas未満である。
1/TG(合計)=w1/TG(1)+w2/TG(2)+w3/TG(3)+任意に、w4/TG(4)+任意に、w5/TG(5)+任意に、wn/TG(n)
にしたがって求められ、ここで、w1、w2、w3、w4、w5、およびwnはそれぞれ、少なくとも第1および第2のモノマーの全混合物100重量%中のそれぞれのモノマーの、特にそれぞれの第1のモノマーの、それぞれの第2のモノマーの、または任意にそれぞれの第3のモノマーの、重量割合であり、n=6~50であり、TG(合計)は、80℃以上、特に100℃以上、好ましくは120℃以上、有利には170℃以上であり、周囲室温(約20℃~23℃)での組成物の粘度は、3000mPas以下、特に500~2500mPas未満である。
ここで、w1、w2、w3、w4、w5、およびwnはそれぞれ、第1および第2のモノマーならびに任意に第3のモノマーの全組成物100重量%中のモノマーの重量割合であり、n=6~50であり、TGは100℃以上であり、重合組成物は、特に水中にて55℃で測定した場合に40MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/またはb)特に水中にて55℃で測定した場合に800MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有する。
(ii)UVおよび/もしくはVisスペクトル領域の光開始剤、またはUVおよび/もしくはVisスペクトル領域の光開始剤系0.01~2重量%、ならびに安定剤0.01~2重量%と、任意に
(g)無機酸化物または無機混合酸化物および/または歯科用ガラスを含む無機フィラー、特に二酸化ジルコニウム、酸化ジルコニウムと二酸化ケイ素との混合酸化物、二酸化ケイ素0~10重量%、特に0.01~7.5重量%と
を含むことができ、ここで、全組成物は100重量%である。
ii)a)特に水中にて37℃で測定した場合に70MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/もしくはb)特に水中にて37℃で測定した場合に2000MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有し、かつ/または
iii)a)特に水中にて45℃で測定した場合に50MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/もしくはb)特に水中にて45℃で測定した場合に1500MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有し、かつ/または
iv)a)特に水中にて55℃で測定した場合に40MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/もしくはb)特に水中にて55℃で測定した場合に900MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有し、特に重合性組成物の照射によって得ることができる。
a.2)特に水中にて45℃で測定した場合に50MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/またはb.2)特に水中にて45℃で測定した場合に1500MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有し、かつ任意に
iv)a)特に水中にて55℃で測定した場合に40MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/またはb)特に水中にて55℃で測定した場合に900MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有する。
全般的な製造例:開始剤を、(オクタヒドロ-4,7-メタノ-1H-インデニル)メチルアクリレートまたはトリシクロデカンジメタノールジアクリレートに事前に溶解させる。次いで他のモノマーを加え、この混合物を均質化する。顔料濃縮物または顔料を加えることができる。次いで、この組成物を有利には均質化する。製造したこの組成物は、3Dプリンターでの処理が可能である。感光性開始剤は、周囲光と反応して望ましくない重合を生じ得ることに留意すべきである(組成物を、有利には適切な措置の下で印刷浴に移す)。385~405nmで照射し、例えば実験用照明装置HiLite Power3Dを使用して後硬化または後熱処理を行う。
Claims (16)
- (i)モノマーと、
(ii)少なくとも1つのさらなる成分と
を含む、重合可能な放射線硬化性組成物であって、
(i)前記モノマーは、少なくとも(a)1つの第1のモノマーであって、前記第1のモノマーのホモポリマーのTG(ガラス転移点)が120℃以上である第1のモノマーと、少なくとも(b)1つの第2のモノマーであって、前記第2のモノマーのホモポリマーのTG(ガラス転移点)が100℃以下である第2のモノマーとを含み、前記少なくとも1つの第1のモノマーまたは前記少なくとも1つの第2のモノマーのうちの少なくとも1つは、脂環式基を有しており、かつ
(ii)前記少なくとも1つのさらなる成分は、UVおよび/もしくはVisスペクトル領域の少なくとも1つの光開始剤、またはUVおよび/もしくはVisスペクトル領域の光開始剤系を含む
ことを特徴とする、組成物。 - 周囲室温(約20℃~23℃)での前記組成物の粘度が、3000mPas以下、特に500~2500mPas未満であることを特徴とする、請求項1記載の組成物。
- (i)前記モノマーが、
(a)1,3,5-トリス(ヒドロキシアルキル)イソシアヌレートから誘導される少なくとも1つのトリアクリレートであって、ここで、ヒドロキシアルキル基は、それぞれ独立して1~8個のC原子を含むものとするトリアクリレートと、任意に
(b)二価脂環式基を有する二官能性アクリレートおよび二価脂環式基を有する二官能性メタクリレートと、任意に
(c)脂環式基を有する少なくとも1つの単官能性アクリレートおよび/または脂環式基を有する単官能性メタクリレートと
を含むことを特徴とする、請求項1または2記載の組成物。 - (i)前記モノマーが、
(a)少なくとも1つの第1のモノマーまたは第1のモノマーの混合物であって、前記それぞれの第1のモノマーのホモポリマーのTG(ガラス転移点)は120℃以上であり、前記第1のモノマーまたは第1のモノマーの混合物は、アルカノールが1~6個のC原子を含むトリシクロデカンジアルカノールをベースとする少なくとも1つのジアクリレートエステル、またはその混合物を含むものとする、第1のモノマーまたは第1のモノマーの混合物と、
(b)少なくとも1つの第2のモノマーまたは第2のモノマーの混合物であって、前記それぞれの第2のモノマーのホモポリマーのTG(ガラス転移点)はそれぞれ100℃以下であり、前記第2のモノマーまたは第2のモノマーの混合物は、アルカノールが1~6個のC原子を含むトリシクロデカンアルカノールをベースとする少なくとも1つの単官能性アクリレートエステル、またはその混合物、および任意に、二価アルキレン基を有する二官能性ウレタン(メタ)アクリレートから選択される少なくとも1つの二官能性ウレタン(メタ)アクリレートを含むものとする、第2のモノマーまたは第2のモノマーの混合物と
を含み、ここで、有利には
(i)前記組成物中に、アルカノールが1~6個のC原子を含むトリシクロデカンアルカノールをベースとする単官能性アクリレートエステルが15~25重量%存在し、任意に、アルカノールが1~6個のC原子を含むトリシクロデカンジアルカノールをベースとするジアクリレートエステルが5~15重量%存在し、ここで、全組成物は100重量%であるか、または
(ii)アルカノールが1~6個のC原子を含むトリシクロデカンジアルカノールをベースとするジアクリレートエステルが5~15重量%存在し、アルカノールが1~6個のC原子を含むトリシクロデカンアルカノールをベースとする単官能性アクリレートエステルが15~25重量%存在し、特に(ii)では、1,3,5-トリス(ヒドロキシアルキル)イソシアヌレートから誘導されるトリアクリレートが存在せず、ここで、全組成物は100重量%であるか、または
(iii)アルカノールが1~6個のC原子を含むトリシクロデカンアルカノールをベースとする単官能性アクリレートエステルと、アルカノールが1~6個のC原子を含むトリシクロデカンジアルカノールをベースとするジアクリレートエステルとを含む混合物が15~45重量%存在し、特に(iii)では、1,3,5-トリス(ヒドロキシアルキル)イソシアヌレートから誘導されるトリアクリレートが存在せず、ここで、全組成物は100重量%であることを特徴とする、請求項3記載の組成物。 - 前記組成物中に、
- (i)(a)少なくとも1つの第1のモノマーまたは第1のモノマーの混合物であって、対応する第1のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が120℃以上である第1のモノマーまたは第1のモノマーの混合物が40~99.99重量%存在し、かつ
- 少なくとも(b)1つの第2のモノマーまたは第2のモノマーの混合物であって、対応する第2のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が100℃以下である第2のモノマーまたは第2のモノマーの混合物が0~60重量%存在し、
- 前記少なくとも1つのさらなる成分であって、UVおよび/もしくはVisスペクトル領域の少なくとも1つの光開始剤、またはUVおよび/もしくはVisスペクトル領域の光開始剤系、ならびに任意にUVおよび/もしくはVisスペクトル領域の少なくとも1つの安定剤、ならびに任意に少なくとも1つの顔料および/もしくは染料、ならびにさらなる慣用的な添加剤を含むさらなる成分が0.01~5重量%存在し、
ここで、全組成物は100重量%であり、特に、周囲室温(約20℃~23℃)での前記組成物の粘度が、3000mPas以下、特に500~2500mPas未満であることを特徴とする、請求項1から4までのいずれか1項記載の組成物。 - (b)が、トリシクロデカンジメタノールジアクリレート、トリシクロデカンジメタノールジメタクリレート、トリシクロデカンジエタノールジアクリレート、トリシクロデカンジエタノールジメタクリレートおよび/またはその混合物から選択されることを特徴とする、請求項1から5までのいずれか1項記載の組成物。
- (i)前記第1のモノマーが、
(e)二価アルキレン基を有する二官能性ウレタン(メタ)アクリレートから選択される少なくとも1つの二官能性ウレタン(メタ)アクリレート、および/または
(f.1)少なくとも1つの単官能性、三官能性、四官能性または多官能性モノマーであって、特にウレタン(メタ)アクリレートではないもの、特にポリエーテルのアクリレートエステルおよび/またはメタクリレートエステルであり、ポリエーテルのジメタクリレートエステル、ポリエーテルの三官能性、四官能性または多官能性メタクリレートエステル、ポリエーテルのジアクリレートエステル、ポリエーテルの三官能性、四官能性および/または多官能性アクリレートエステルから選択されるもの
を含むことを特徴とする、請求項4記載の組成物。 - (i)前記第2のモノマーが、
(c)脂環式基を有する少なくとも1つの単官能性アクリレートおよび/または脂環式基を有する単官能性メタクリレートであって、特に(オクタヒドロ-4,7-メタノ-1H-インデニル)メタノールアクリレート、(オクタヒドロ-4,7-メタノ-1H-インデニル)メタノールメタクリレート、(オクタヒドロ-4,7-メタノ-1H-インデニル)エタノールアクリレートおよび(オクタヒドロ-4,7-メタノ-1H-インデニル)エタノールメタクリレートから選択されるもの、
(f.2)少なくとも1つの単官能性、三官能性、四官能性または多官能性モノマーであって、特にウレタン(メタ)アクリレートではないもの、特にポリエーテルのアクリレートエステルおよび/またはメタクリレートエステルであり、ポリエーテルのジメタクリレートエステル、ポリエーテルの三官能性、四官能性または多官能性メタクリレートエステル、ポリエーテルのジアクリレートエステル、ポリエーテルの三官能性、四官能性および/または多官能性アクリレートエステルから選択されるもの
を含むことを特徴とする、請求項4記載の組成物。 - 前記組成物中に、(i)以下:
- (a)第1のモノマーまたは第1のモノマーの混合物であって、対応する第1のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が120℃以上であり、前記第1のモノマーまたは第1のモノマーの混合物は、二価脂環式基を有する少なくとも1つの二官能性アクリレートおよび/または二価脂環式基を有する少なくとも1つの二官能性メタクリレート、および任意に二価アルキレン基を有する二官能性ウレタン(メタ)アクリレートから選択される少なくとも1つの二官能性ウレタン(メタ)アクリレートを含むものとする、第1のモノマーまたは第1のモノマーの混合物70~99.99重量%と、
- 少なくとも(b)1つの第2のモノマーまたは第2のモノマーの混合物であって、対応する第2のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が100℃以下であり、前記第2のモノマーまたは第2のモノマーの混合物は、それぞれのホモポリマーのTGが30℃以上である少なくとも1つのモノマーまたは第2のモノマーの混合物を含み、好ましくは、TGが30℃以上100℃以下の範囲である第2のモノマーが含まれており、特に好ましくは、TGが50℃以上100℃以下の範囲である第2のモノマーが含まれているものとする、第2のモノマーまたは第2のモノマーの混合物0~30重量%と、
- 前記少なくとも1つのさらなる成分であって、UVおよび/もしくはVisスペクトル領域の少なくとも1つの光開始剤、またはUVおよび/もしくはVisスペクトル領域の光開始剤系、ならびに任意にUVおよび/もしくはVisスペクトル領域の少なくとも1つの安定剤、ならびに任意に少なくとも1つの顔料および/もしくは染料、ならびにさらなる慣用的な添加剤を含むさらなる成分0.01~5重量%と
を含むモノマーが存在することを特徴とする、請求項1から8までのいずれか1項記載の組成物。 - 前記組成物中に、(i)以下:
- (a)第1のモノマーまたは第1のモノマーの混合物であって、対応する第1のモノマーまたは第1のモノマーの混合物のそれぞれのホモポリマーのTG(ガラス転移点)が120℃以上であり、前記第1のモノマーまたは第1のモノマーの混合物は、二価脂環式基を有する少なくとも1つの二官能性アクリレートおよび/または二価脂環式基を有する少なくとも1つの二官能性メタクリレート、および任意に二価アルキレン基を有する二官能性ウレタン(メタ)アクリレートから選択される少なくとも1つの二官能性ウレタン(メタ)アクリレートを含むものとする、第1のモノマーまたは第1のモノマーの混合物75~99.99重量%と、
- 少なくとも(b)1つの第2のモノマーまたは第2のモノマーの混合物であって、対応する第2のモノマーのそれぞれのホモポリマーのTG(ガラス転移点)が100℃以下であり、前記第2のモノマーまたは第2のモノマーの混合物は、脂環式基を有する少なくとも1つの単官能性アクリレートおよび/または脂環式基を有する単官能性メタクリレートを含むものとする、第2のモノマーまたは第2のモノマーの混合物0~25重量%と、
- 前記少なくとも1つのさらなる成分であって、UVおよび/もしくはVisスペクトル領域の少なくとも1つの光開始剤、またはUVおよび/もしくはVisスペクトル領域の光開始剤系、ならびに任意にUVおよび/もしくはVisスペクトル領域の少なくとも1つの安定剤、ならびに任意に少なくとも1つの顔料および/もしくは染料、ならびにさらなる慣用的な添加剤を含むさらなる成分0.01~5重量%と
を含むモノマーが存在し、
ここで、全組成物は100重量%であり、特に、周囲室温(約20℃~23℃)での前記組成物の粘度が、3000mPas以下、特に500~2500mPas未満であることを特徴とする、請求項1から9までのいずれか1項記載の組成物。 - 前記(i)モノマーおよび前記(ii)少なくとも1つのさらなる成分が、以下の式
1/TG(合計)=w1/TG(1)+w2/TG(2)+w3/TG(3)+任意に、w4/TG(4)+任意に、w5/TG(5)+任意に、wn/TG(n)
にしたがって前記組成物中に存在し、ここで、
w1、w2、w3、w4、w5、およびwnはそれぞれ、前記第1および前記第2のモノマーならびに任意に第3のモノマーの全混合物100重量%中の前記モノマーの重量割合であり、n=6~50であり、TGは100℃以上であり、
- 周囲室温(約20℃~23℃)での前記組成物の粘度が、3000mPas以下、特に500~2500mPas未満であることを特徴とする、請求項1から10までのいずれか1項記載の組成物。 - 前記(i)モノマーが、以下の式
1/TG(合計)=w1/TG(1)+w2/TG(2)+w3/TG(3)+任意に、w4/TG(4)+任意に、w5/TG(5)+任意に、wn/TG(n)
にしたがって前記組成物中に存在し、ここで、
w1、w2、w3、w4、w5、およびwnはそれぞれ、前記第1および前記第2のモノマーならびに任意に前記第3のモノマーの全混合物100重量%中の前記モノマーの重量割合であり、n=6~50であり、TGは100℃以上であり、重合組成物は、特に水中にて55℃で測定した場合に40MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/またはb)特に水中にて55℃で測定した場合に800MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有することを特徴とする、請求項1から11までのいずれか1項記載の重合組成物。 - 前記重合組成物が、代替的または累積的に、
i)a)75MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/もしくはb)2000MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有し、かつ/または
ii)a)特に水中にて37℃で測定した場合に70MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/もしくはb)特に水中にて37℃で測定した場合に2000MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有し、かつ/または
iii)a)特に水中にて45℃で測定した場合に50MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/もしくはb)特に水中にて45℃で測定した場合に1500MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有し、かつ/または
iv)a)特に水中にて55℃で測定した場合に40MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/もしくはb)特に水中にて55℃で測定した場合に900MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有することを特徴とする、請求項1から11までのいずれか1項記載の、または請求項12記載の重合組成物。 - 歯科用補綴部品、整形外科用器具または歯科用プリフォームを製造するための、請求項1から13までのいずれか1項記載の重合組成物の3次元成形体の形態のブランクであって、前記ブランクが、a.1)75MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/またはb.1)2000MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有し、かつ任意にa.2)特に水中にて45℃で測定した場合に50MPa以上の曲げ強さ(DIN EN ISO 20795-2に準拠)を有し、かつ/またはb.2)特に水中にて45℃で測定した場合に1500MPa以上の弾性率(DIN EN ISO 20795-2に準拠)を有することを特徴とする、ブランク。
- 解剖学的模型、解剖学的卓上型模型、歯科用作業用模型、歯科用完全模型、歯科用ダイ模型、解剖学的または歯科用ソーカット模型、特に状況模型、反対咬合模型、機能模型、プレ模型、修復用模型、精密模型、歯科用歯列石膏模型を代替するための解剖学的模型、アライナー、歯科用スプリント、補綴部品、歯科用補綴部品、整形外科用器具または歯科用プリフォームを製造するための、特にラピッドプロトタイピングプロセス、またはラピッドマニュファクチャリングプロセスまたはラピッドツーリングプロセスにおける、請求項1から11までのいずれか1項記載の組成物の使用。
- 前記歯科用補綴部品が、補綴ベースまたはその部品、人工歯、一体的に歯間接続されている少なくとも2~16本の人工歯を有する歯列、クラウン、プロビショナルクラウン、全補綴物、全クラウン、歯科矯正補正用スプリント(インビザラインと同様)、歯科用ブリッジ、アバットメント、スープラストラクチャー、歯科用バー、インレー、アンレー、整形外科用器具、例えば咬合スプリント、人工歯の歯科用プリフォーム、インプラント歯科学のサージカルガイド、マウスガードおよび/またはインプラントを含むことを特徴とする、請求項15記載の使用。