JP2022502532A - 相転移材料として使用するための金属硝酸塩系組成物 - Google Patents
相転移材料として使用するための金属硝酸塩系組成物 Download PDFInfo
- Publication number
- JP2022502532A JP2022502532A JP2021515013A JP2021515013A JP2022502532A JP 2022502532 A JP2022502532 A JP 2022502532A JP 2021515013 A JP2021515013 A JP 2021515013A JP 2021515013 A JP2021515013 A JP 2021515013A JP 2022502532 A JP2022502532 A JP 2022502532A
- Authority
- JP
- Japan
- Prior art keywords
- nitrate
- pcm
- weight percent
- tetrahydrate
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
・共通のイオン(例えばNO3 −)
・PCMの主成分と同様の密度
・PCMの主成分と同様のpH
・PCMの主成分に溶解可能
例1
例2
例3
例4
例5
例6
例7
例8
例9
他の可能な請求項
第2族金属硝酸塩または金属硝酸塩水和物に基づく核生成剤を伴う、相転移材料(PCM)としての金属硝酸塩または金属硝酸塩水和物の使用。
核生成は、過冷却を克服するためにシーディングプロセス(すなわち、上記PCMの成分と同一の化学的同一性の結晶の追加)によって達成される、項目1に記載の使用。
上記核生成剤は、1種類より多くの別のカチオンを有する硝酸塩である、上述の項目のいずれかに記載の使用。
上記核生成剤は、1または複数の種類の第2族金属硝酸塩および/または金属硝酸塩水和物から構成される、上述の項目のいずれかに記載の使用。
上記PCMは、融解プロセス中に高圧に維持される核生成剤を用いて核生成される、上述の項目のいずれかに記載の使用。
上記核生成剤は、金属サンプルの表面上の裂け目における高圧の領域にあることによって、融点より上で固体の状態に維持される上記PCMの1または複数の種類の成分の結晶である、項目5に記載の核生成の方法。
機械加工溝を有する薄い金属ディスクが曲げられ、上記核生成剤を上記バルクPCMに放出する、項目5および6のいずれかに記載の核生成の方法。
第2族金属硝酸塩から構成される上記核生成剤は、硝酸マグネシウムまたはその任意の水和物形態である、上述の項目のいずれかに記載の使用。
第2族金属硝酸塩から構成される上記核生成剤は、硝酸ストロンチウムまたはその任意の水和物形態である、上述の項目のいずれかに記載の使用。
第2族金属硝酸塩から構成される上記核生成剤は、硝酸カルシウムまたはその任意の水和物形態である、上述の項目のいずれかに記載の使用。
第2族金属硝酸塩から構成される上記核生成剤は、硝酸バリウムまたはその任意の水和物形態である、上述の項目のいずれかに記載の使用。
上記核生成剤は、無水物およびその水和物形態の任意の組み合わせを含む、2種類以上の第2族金属硝酸塩の組み合わせである、上述の項目のいずれかに記載の使用。
上記核生成剤は、硝酸ストロンチウムおよび硝酸マグネシウム、または、その任意の水和物形態の組み合わせである、上述の項目のいずれかに記載の使用。
上記核生成剤は、硝酸カルシウムおよび硝酸マグネシウム、または、その任意の水和物形態の組み合わせである、上述の項目のいずれかに記載の使用。
上記核生成剤は、硝酸マグネシウムおよび硝酸バリウム、または、その任意の水和物形態の組み合わせである、上述の項目のいずれかに記載の使用。
上記核生成剤は、硝酸ストロンチウムおよび硝酸バリウム、または、その任意の水和物の形態の組み合わせである、上述の項目のいずれかに記載の使用。
上記核生成剤は、硝酸ストロンチウム、硝酸バリウム、および硝酸マグネシウム、または、その任意の水和物形態の組み合わせである、上述の項目のいずれかに記載の使用。
上記核生成剤は、バルクPCMにおいて、溶解限度より高い濃度で存在する、上述の項目のいずれかに記載の使用。
上記核生成剤は、上記PCMの少なくとも約0.1重量パーセント存在する、上述の項目のいずれかに記載の使用。
硝酸リチウム、硝酸ナトリウム、硝酸カリウム、硝酸カルシウム、硝酸バリウム、硝酸スカンジウム、硝酸亜鉛、硝酸銅、硝酸鉄、硝酸マンガン、硝酸クロム、硝酸ストロンチウム、硝酸銀、硝酸イットリウム、硝酸ジルコニウム、硝酸チタン、任意の硝酸ランタニド金属、硝酸アンモニウム、硝酸アルミニウム、硝酸ビスマス、硝酸ガリウム、硝酸マグネシウム、硝酸鉛から構成される一覧のうちのいずれか1種類、または、それらの組み合わせから選択される少なくとも1種類の金属硝酸塩水和物、および/または、それらから形成される任意の水和物、ならびに、
上述の項目のいずれかによる核生成剤
から構成されるPCM。
上記核生成剤以外の上記PCMは、1種類より多くの金属硝酸塩および/または金属硝酸塩水和物の混合物である、項目20に記載のPCM。
上記PCMは、選択された各成分の個々より低い融解温度を有する、項目20および21のいずれかに記載のPCM。
選択された上記金属硝酸塩および/またはそれらの水和物の量を変更することによって、ある範囲内の値である特定の温度に上記PCMの融点を調整することが可能となる、項目20から22のいずれかに記載のPCM。
上記PCMは選択された上記成分の共晶混合物である、項目20から23のいずれかに記載のPCM。
上記PCMは、選択された上記成分の二成分、三成分または四成分共晶混合物である、項目20から24のいずれかに記載のPCM。
上記PCMは、約98〜99.6重量パーセントの少なくとも1種類の金属硝酸塩水和物と、約0.2〜1重量パーセントの硝酸ストロンチウムまたはその任意の水和物と、約0.2〜1重量パーセントの硝酸マグネシウムまたはその任意の水和物から構成される、項目20から25のいずれかに記載のPCM。
上記PCMは、約0〜99.8重量パーセントの硝酸カルシウム四水和物、約0〜1重量パーセントの硝酸ストロンチウム四水和物、約0〜1重量パーセントの硝酸マグネシウム六水和物、約0〜1重量パーセントの硝酸バリウム、約0〜99.8重量パーセントの硝酸リチウム三水和物、約0〜50重量パーセントの硝酸マンガン四水和物、約0〜99.8重量パーセントの硝酸マンガン六水和物、約0〜99.8重量パーセントの硝酸亜鉛六水和物、約0〜99.8重量パーセントの硝酸銅六水和物、約0〜40重量パーセントの硝酸銅三水和物、約0〜40重量パーセントの硝酸銅ヘミ五水和物、約0〜99.8重量パーセントの硝酸鉄九水和物、約0〜10重量パーセントの硝酸ナトリウム、および、約0〜30重量パーセントの硝酸カリウムから構成される、項目20から26のいずれかに記載のPCM。
上記PCMは、約99.2重量パーセントの硝酸カルシウム四水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物、および、約0.4重量パーセントの硝酸マグネシウム六水和物から構成される、項目20から27のいずれかに記載のPCM。
上記PCMは、約99.3重量パーセントの硝酸カルシウム四水和物、約0.3重量パーセントの硝酸バリウム、および、約0.4重量パーセントの硝酸マグネシウム六水和物から構成される、項目20から28のいずれかに記載のPCM。
上記PCMは、約99.4重量パーセントの硝酸カルシウム四水和物、約0.3重量パーセントの硝酸ストロンチウム、および、約0.3重量パーセントの硝酸マグネシウム二水和物から構成される、項目20から29のいずれかに記載のPCM。
上記PCMは、約57.2重量パーセントの硝酸カルシウム四水和物、約42.0重量パーセントの硝酸リチウム三水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、および、約0.4重量パーセントの硝酸ストロンチウム四水和物から構成される、項目20から31のいずれかに記載のPCM。
上記PCMは、約40.0重量パーセントの硝酸カルシウム四水和物、約29.4重量パーセントの硝酸リチウム三水和物、約29.8重量パーセントの硝酸銅六水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、および、約0.4重量パーセントの硝酸ストロンチウム四水和物から構成される、項目20から31のいずれかに記載のPCM。
上記PCMは、約32.1重量パーセントの硝酸カルシウム四水和物、約23.5重量パーセントの硝酸リチウム三水和物、約23.8重量パーセントの硝酸銅六水和物、約19.8重量パーセントの硝酸亜鉛六水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、および、約0.4重量パーセントの硝酸ストロンチウム四水和物から構成される、項目20から32のいずれかに記載のPCM。
上記PCMは、約24.0重量パーセントの硝酸カルシウム四水和物、約17.6重量パーセントの硝酸リチウム三水和物、約17.9重量パーセントの硝酸銅六水和物、約39.7重量パーセントの硝酸マンガン六水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物から構成される、項目20から33のいずれかに記載のPCM。
上記PCMは、約39.7重量パーセントの硝酸カルシウム四水和物、約59.5重量パーセントの硝酸銅六水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物、および、約0.4重量パーセントの硝酸マグネシウム六水和物から構成される、項目20から34のいずれかに記載のPCM。
上記PCMは、約59.5重量パーセントの硝酸カルシウム四水和物、約39.7重量パーセントの硝酸亜鉛六水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物、および、約0.4重量パーセントの硝酸マグネシウム六水和物から構成される、項目20から35のいずれかに記載のPCM。
上記PCMは、約44.6重量パーセントの硝酸カルシウム四水和物、約54.6重量パーセントの硝酸鉄九水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物、および、約0.4重量パーセントの硝酸マグネシウム六水和物から構成される、項目20から36のいずれかに記載のPCM。
上記PCMは、約69.4重量パーセントの硝酸亜鉛六水和物、約29.8重量パーセントの硝酸リチウム三水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物、および、約0.4重量パーセントの硝酸マグネシウム六水和物から構成される、項目20から37のいずれかに記載のPCM。
上記PCMは、約39.7重量パーセントの硝酸鉄九水和物、約34.1重量パーセントの硝酸カルシウム四水和物、約25.4重量パーセントの硝酸リチウム三水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、および、約0.4重量パーセントの硝酸ストロンチウム四水和物から構成される、項目20から38のいずれかに記載のPCM。
上記PCMは、約14.7重量パーセントの硝酸マンガン六水和物、約83.3重量パーセントの硝酸亜鉛六水和物、約1重量パーセントの硝酸ストロンチウム、および、約1重量パーセントの硝酸バリウムから構成される、項目20から39のいずれかに記載のPCM。
撹拌、再循環、ポンピング、超音波処理、またはそれらの組み合わせを含む、核生成中心の機械的操作によって、上述の項目のいずれかによるPCMの結晶化の速度を増加させる方法。
1または複数の成長する結晶子が上記PCM全体に分散される、結晶化速度を増加させる項目41に記載の方法。
核生成剤が上記PCM全体に分散される、結晶化速度を増加させる項目41および42のいずれかに記載の方法。
1または複数の成長する結晶子が、より多くの数の、より小さい結晶子に分割される、項目41から43のいずれかに記載の結晶化速度を増加させる方法。
少なくとも1種類の金属硝酸塩水和物および少なくとも1種類の他の金属硝酸塩および/または金属硝酸塩水和物を提供する段階と、
1または複数の種類の上記成分の融解転移温度より高い温度に上記混合物を加熱し、撹拌して単一の流し込み可能な液体を形成する段階と
を備える、PCMを調製する項目20から40のいずれかに記載の方法。
無水金属硝酸塩、および/または、最終的なPCM組成物において所望される数より少ない水和数の金属硝酸塩水和物が、ある量の水を追加されて、1または複数の種類の金属硝酸塩水和物の代わりに使用され、上記最終的なPCM組成物が提供される、PCMを調製する項目45に記載の方法。
上記PCM組成物において所望される数より多くの水和数を有する金属硝酸塩水和物が使用され、余分な水が1または複数の種類の無水金属硝酸塩、および/または、より少ない水和数を有する金属硝酸塩水和物によって除去されるか、または飽和され、上記最終的なPCM組成物が提供される、PCMを調製する項目45または46のいずれかに記載の方法。
金属硝酸塩溶液が使用され、余分な水が、1または複数の種類の無水金属硝酸塩、および/または、水和数がより少ない金属硝酸塩水和物を用いて除去または飽和されて上記最終的なPCM組成物が生じる、PCMを調製する項目45から47のいずれかに記載の方法。
上記金属硝酸塩および/または金属硝酸塩水和物が反応によって合成または生成される、PCMを調製する項目45から48のいずれかに記載の方法。
上記PCMは、特定の組成物を実現するための正確な量の水の存在下で、対応する塩基性金属塩による硝酸の中和によって形成される、PCMを調製する項目45から49のいずれかに記載の方法。
上記PCMは、余分な水の存在下で、対応する金属塩基による硝酸の中和によって形成され、上記余分な水は次に、1または複数の種類の無水金属硝酸塩、および/または、水和数がより少ない金属硝酸塩水和物で除去または飽和され、上記最終的なPCM組成物が提供される、PCMを調製する項目45から50のいずれかに記載の方法。
硝酸塩以外の任意のアニオンが、イオン交換、または、適切な金属塩を用いた沈殿およびその後に続く物理的分離によって除去される、PCMを調製する項目45から51のいずれかに記載の方法。
Claims (18)
- 硝酸カルシウム四水和物と、
核生成剤と
から構成されるPCMであって、
前記核生成剤は、
硝酸マグネシウム、または、その任意の水和物形態、
硝酸ストロンチウム、または、その任意の水和物形態、および、
硝酸バリウム、または、その任意の水和物形態
のいずれかの組み合わせから構成される、PCM。 - 前記核生成剤は、
硝酸マグネシウム、または、その任意の水和物形態、および、
硝酸ストロンチウム、または、その任意の水和物形態
の組み合わせから構成される混合物である、請求項1に記載のPCM。 - 前記核生成剤は硝酸マグネシウム六水和物および硝酸ストロンチウム(無水)である、請求項1または2に記載のPCM。
- 前記PCMは、選択された各成分の個々より低い融解温度を有する、請求項1から3のいずれか一項に記載のPCM。
- 選択された金属硝酸塩および/またはその水和物の量を変更することによって、前記PCMの融点を、ある範囲内の値である特定の温度に調整可能である、請求項1から4のいずれか一項に記載のPCM。
- 前記PCMは、選択された成分の共晶混合物である、請求項1から5のいずれか一項に記載のPCM。
- 前記PCMは、選択された成分の二成分、三成分または四成分共晶混合物である、請求項1から6のいずれか一項に記載のPCM。
- 前記PCMは、
約99.2重量パーセントの硝酸カルシウム四水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物、および、約0.4重量パーセントの硝酸マグネシウム六水和物、
約99.3重量パーセントの硝酸カルシウム四水和物、約0.3重量パーセントの硝酸バリウム、および、約0.4重量パーセントの硝酸マグネシウム六水和物、
約99.4重量パーセントの硝酸カルシウム四水和物、約0.3重量パーセントの硝酸ストロンチウム、および、約0.3重量パーセントの硝酸マグネシウム二水和物、
約57.2重量パーセントの硝酸カルシウム四水和物、約42.0重量パーセントの硝酸リチウム三水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、および、約0.4重量パーセントの硝酸ストロンチウム四水和物、
約40.0重量パーセントの硝酸カルシウム四水和物、約29.4重量パーセントの硝酸リチウム三水和物、約29.8重量パーセントの硝酸銅六水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、および、約0.4重量パーセントの硝酸ストロンチウム四水和物、
約32.1重量パーセントの硝酸カルシウム四水和物、約23.5重量パーセントの硝酸リチウム三水和物、約23.8重量パーセントの硝酸銅六水和物、約19.8重量パーセントの硝酸亜鉛六水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、および、約0.4重量パーセントの硝酸ストロンチウム四水和物、
約24.0重量パーセントの硝酸カルシウム四水和物、約17.6重量パーセントの硝酸リチウム三水和物、約17.9重量パーセントの硝酸銅六水和物、約39.7重量パーセントの硝酸マンガン六水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、および、約0.4重量パーセントの硝酸ストロンチウム四水和物、
約39.7重量パーセントの硝酸カルシウム四水和物、約59.5重量パーセントの硝酸銅六水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物、および、約0.4重量パーセントの硝酸マグネシウム六水和物、
約59.5重量パーセントの硝酸カルシウム四水和物、約39.7重量パーセントの硝酸亜鉛六水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物、および、約0.4重量パーセントの硝酸マグネシウム六水和物、
約44.6重量パーセントの硝酸カルシウム四水和物、約54.6重量パーセントの硝酸鉄九水和物、約0.4重量パーセントの硝酸ストロンチウム四水和物、および、約0.4重量パーセントの硝酸マグネシウム六水和物、または、
約39.7重量パーセントの硝酸鉄九水和物、約34.1重量パーセントの硝酸カルシウム四水和物、約25.4重量パーセントの硝酸リチウム三水和物、約0.4重量パーセントの硝酸マグネシウム六水和物、および、約0.4重量パーセントの硝酸ストロンチウム四水和物
から構成される、請求項1から7のいずれか一項に記載のPCM。 - 前記核生成剤は、
硝酸ストロンチウムおよび硝酸マグネシウム、または、それらの任意の水和物形態の組み合わせ、
硝酸マグネシウムおよび硝酸バリウム、または、それらの任意の水和物形態の組み合わせ、
硝酸ストロンチウムおよび硝酸バリウム、または、それらの任意の水和物形態の組み合わせ、または、
硝酸ストロンチウム、硝酸バリウム、および硝酸マグネシウム、または、それらの任意の水和物形態の組み合わせ
である、請求項1から8のいずれか一項に記載のPCM。 - 前記核生成剤は、前記PCMの少なくとも約0.1重量パーセント存在する、請求項1から9のいずれか一項に記載のPCM。
- 請求項1から10のいずれか一項に記載のPCMを調製する方法であって、
硝酸カルシウム四水和物の混合物と、
核生成剤と
を提供する段階であって、前記核生成剤は、
硝酸マグネシウム、または、その任意の水和物形態、
硝酸ストロンチウム、または、その任意の水和物形態、および、
硝酸バリウム、または、その任意の水和物形態
のいずれかの組み合わせである、段階と、
前記混合物を、
硝酸マグネシウム、または、その任意の水和物形態、
硝酸ストロンチウム、または、その任意の水和物形態、および、
硝酸バリウム、または、その任意の水和物形態
のうち1または複数の融解転移温度より高い温度に加熱し、撹拌して、単一の流し込み可能な液体を形成する段階と
を備えるPCM調製方法。 - 無水金属硝酸塩、および/または、最終的な前記PCMの組成物において所望される数より少ない水和数を有する金属硝酸塩水和物が、ある量の水を追加されて、1または複数の種類の金属硝酸塩水和物の代わりに使用され、最終的な前記PCMの組成物が提供される、請求項11に記載のPCM調製方法。
- 前記PCMの組成物において所望される数より多くの水和数を有する金属硝酸塩水和物が使用され、余分な水が1または複数の種類の無水金属硝酸塩、および/または、より少ない水和数を有する金属硝酸塩水和物によって除去されるか、または飽和され、最終的な前記PCMの組成物が提供される、請求項11または12に記載のPCM調製方法。
- 金属硝酸塩溶液が使用され、余分な水が、1または複数の種類の無水金属硝酸塩、および/または、より少ない水和数を有する金属硝酸塩水和物で除去または飽和され、最終的な前記PCMの組成物が提供される、
請求項11から13のいずれか一項に記載のPCM調製方法。 - 硝酸マグネシウム、または、その任意の水和物形態、
硝酸ストロンチウム、または、その任意の水和物形態、および、
硝酸バリウム、または、その任意の水和物形態
は、反応によって合成または生成される、請求項11から14のいずれか一項に記載のPCM調製方法。 - 前記PCMは、特定の組成物を実現するための正確な量の水の存在下で、対応する塩基性金属塩による硝酸の中和によって形成される、請求項11から15のいずれか一項に記載のPCM調製方法。
- 前記PCMは、余分な水の存在下で、対応する金属塩基による硝酸の中和によって形成され、前記余分な水は次に、1または複数の種類の無水金属硝酸塩、および/または、より少ない水和数を有する金属硝酸塩水和物で除去または飽和され、最終的な前記PCMの組成物が提供される、請求項11から16のいずれか一項に記載のPCM調製方法。
- 硝酸塩以外の任意のアニオンが、イオン交換、または、適切な金属塩を用いた沈殿およびその後に続く物理的分離によって除去される、請求項11から17のいずれか一項に記載のPCM調製方法。