JP2022104946A - 防眩フィルム並びにその製造方法及び用途 - Google Patents
防眩フィルム並びにその製造方法及び用途 Download PDFInfo
- Publication number
- JP2022104946A JP2022104946A JP2022053963A JP2022053963A JP2022104946A JP 2022104946 A JP2022104946 A JP 2022104946A JP 2022053963 A JP2022053963 A JP 2022053963A JP 2022053963 A JP2022053963 A JP 2022053963A JP 2022104946 A JP2022104946 A JP 2022104946A
- Authority
- JP
- Japan
- Prior art keywords
- meth
- antiglare
- acrylate
- weight
- antiglare film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
レイなどの各種表示装置に利用できる防眩フィルム並びにその製造方法及び用途に関する
。
の外景の映り込みを防止し、視認性を向上させるためのフィルムとして広く利用されてい
る。防眩フィルムでは、表面に凹凸形状を形成して外光を散乱反射させることにより、防
眩性を発現しているが、外光の散乱光が強すぎる場合には、画像表示装置の表示全体が白
くなったり、表示が濁った色になり、視認性が低下し易い。また、表面の凹凸形状と画像
表示装置の画素とが干渉して輝度分布が見え難くなり、ギラツキが発生し易くなる。
特開2016-33659号公報(特許文献1)には、透明支持体と、その上に形成され
た表面凹凸形状を有する防眩層とを備える防眩フィルムであって、全ヘイズが0.1~3
%であり、表面ヘイズが0.1~2%であり、正反射光込み方式で測定した視感反射率R
SCIと正反射光除去方式で測定した視感反射率RSCEとの比RSCE/RSCIが0
.1以下であり、前記Z表面凹凸形状の凸部の頂点を母点としてその表面をボロノイ分割
したときに形成される多角形の面積の平均値が50~150μm2であり、かつ前記多角
形の面積の変動係数が40~80%である防眩フィルムが開示されている。
性が十分ではなかった。すなわち、従来の防眩フィルムでは、単に蛍光灯をぼかして眩し
さを抑制することを指向しており、反射感(特に正反射による反射光)による眩しさは低
減されていなかった。また、視認性を向上させるためには、光散乱性を弱めてヘイズを低
下させる必要があり、必然的に防眩性は低下する傾向がある。すなわち、防眩性と視認性
とはトレードオフの関係にあり、これらの特性を同時に充足させるのは非常に困難であっ
た。特に、中型スクリーンの表示装置(例えば、ノート型又はラップトップ型PCやデス
クトップ型PCなどのPC、テレビなど)では、視認性、反射防止性を含む防眩性、透明
性などのいずれの特性も高度に要求されるため、バランスを取るのが困難である。
び用途を提供することにある。
ルム並びにその製造方法及び用途を提供することにある。
であり、かつヘイズが40%以上である防眩フィルムを調製することにより、反射防止性
を向上できることを見出し、本発明を完成した。
が40%以上である。この防眩フィルムは、60度グロス(光沢)が15%以下であって
もよい。前記防眩フィルムは、透明基材層と、この透明基材層の少なくとも一方の面に形
成された防眩層とを含み、前記防眩層が、1種以上のポリマー成分及び1種以上の硬化樹
脂前駆体成分を含む硬化性組成物の硬化物であってもよい。前記硬化性組成物は、ポリマ
ー成分及び硬化樹脂前駆体成分から選択される少なくとも2つの成分が、湿式スピノーダ
ル分解により相分離可能であってもよい。前記ポリマー成分は、セルロースエステル類及
び/又は重合性基を有していてもよい(メタ)アクリル系重合体を含んでいてもよい。前
記硬化樹脂前駆体成分は、多官能(メタ)アクリレート、エポキシ(メタ)アクリレート
、ポリエステル(メタ)アクリレート、ウレタン(メタ)アクリレート及びシリコーン(
メタ)アクリレートから選択された少なくとも1種を含んでいてもよい。前記硬化樹脂前
駆体成分は、シリカナノ粒子及び/又はフッ素原子を含んでいてもよい。
防眩フィルムの製造方法も含まれる。この製造方法は、支持体の上に、1種以上のポリマ
ー成分及び1種以上の硬化樹脂前駆体成分を含む硬化性組成物を塗布して乾燥することに
より、ポリマー成分及び硬化樹脂前駆体成分から選択される少なくとも2つの成分を、湿
式スピノーダル分解により相分離させる相分離工程をさらに含んでいてもよい。前記硬化
工程は、相分離した硬化性組成物を熱又は活性エネルギー線で硬化させる硬化工程であっ
てもよい。
Lディスプレイ又は液晶表示装置であってもよい。
し、防眩フィルムの防眩性及び視認性を向上する方法も含まれる。
エステル、アクリル酸エステルの双方を含む。
以上であるため、反射防止性を向上できる。すなわち、本発明の防眩フィルムでは、反射
率を低下させることにより目に入る光の量を低減し、眩しさを抑制できるが、ヘイズも高
いため、蛍光灯などの映り込みをぼかして眩しさを抑制する防眩性も向上できる。さらに
、特定の硬化性組成物を湿式スピノーダル分解することにより、画像の視認性と透明性と
防眩性とをいずれも充足できる。
本発明の防眩フィルムは、視感度反射率及びヘイズが特定の範囲に調整されているため
、反射防止性も含む防眩性を向上できる。
から、例えば0.5~3.7%、好ましくは1~3.6%、さらに好ましくは1.5~3
.5%(特に2~3%)程度であってもよい。このような範囲を有する視感度反射率は、
中型スクリーンの表示装置のなかでも、精細度50~150ppi程度の表示装置(ラッ
プトップ型又はデスクトップ型PC、テレビなど)に対して特に有効である。さらに、中
型スクリーンの表示装置のなかでも、精細度が150ppiを超えて300ppi以下程
度である表示装置(ノート型PCやタブレットPCなど)に対しては、視認性と透明性と
防眩性とのバランスを取れる点から、例えば2~3.8%、好ましくは3~3.78%、
さらに好ましくは3.5~3.75%程度であってもよい。視感度反射率が高すぎると、
反射光によって視認性が低下する。
準拠して測定でき、詳細には、後述する実施例に記載の方法で測定できる。
、具体的なヘイズは40%以上であればよいが、防眩性を向上できる点から、例えば40
~100%、好ましくは50~99.9%(例えば80~99.5%)、さらに好ましく
は85~99%(特に90~98%)程度である。このような範囲を有するヘイズは、中
型スクリーンの表示装置のなかでも、精細度50~150ppi程度の表示装置に対して
特に有効である。さらに、中型スクリーンの表示装置のなかでも、精細度が150ppi
を超えて300ppi以下程度である表示装置に対しては、視認性と透明性と防眩性との
バランスを取れる点から、ヘイズは、例えば40~70%、好ましくは42~60%、さ
らに好ましくは43~50%程度であってもよい。ヘイズが低すぎると、防眩性が低下す
る。一方、ヘイズが高すぎると、視認性が低下する虞がある。
、好ましくは80~99.9%、さらに好ましくは85~99%(特に90~98%)程
度である。全光線透過率が低すぎると、透明性が低下する虞がある。
7105に準拠して、ヘイズメーター(日本電色工業(株)製「NDH-5000W」)
を用いて測定できる。
体である場合、防眩層表面の60度グロス)は15%以下であってもよく、視認性を向上
できる点から、例えば0~13%、好ましくは0.1~12%(例えば0.2~10%)
、さらに好ましくは0.3~5%(特に0.5~1%)程度である。このような範囲を有
する60度グロスは、中型スクリーンの表示装置のなかでも、精細度50~150ppi
程度の表示装置に対して特に有効である。さらに、中型スクリーンの表示装置のなかでも
、精細度が150ppiを超えて300ppi以下程度である表示装置に対しては、視認
性と透明性と防眩性とのバランスを取れる点から、60度グロスは、例えば3~15%、
好ましくは5~12%、さらに好ましくは6~10%程度であってもよい。60度グロス
が大きすぎると、防眩性が低下する虞がある。
て、グロスメーター((株)堀場製作所製「IG-320」)を用いて測定できる。
%以下であってもよく、例えば1~80%、好ましくは3~70%(例えば5~60%)
、さらに好ましくは10~50%(特に30~40%)程度である。このような範囲を有
する透過像鮮明度は、中型スクリーンの表示装置のなかでも、精細度50~150ppi
程度の表示装置に対して特に有効である。さらに、中型スクリーンの表示装置のなかでも
、精細度が150ppiを超えて300ppi以下程度である表示装置に対しては、視認
性と透明性と防眩性とのバランスを取れる点から、0.5mm光学櫛を使用した透過像鮮
明度は、例えば1~30%、好ましくは1.5~20%(例えば2~10%)、さらに好
ましくは3~7%(特に4~6%)程度である。透過像鮮明度が大きすぎると、防眩性が
低下する虞がある。
像鮮明度は、フィルムからの透過光を移動する光学櫛を通して測定し、光学櫛の明暗部の
光量により値を算出する。すなわち、フィルムが透過光をぼやかす場合、光学櫛上に結像
されるスリットの像は太くなるため、透過部での光量は100%以下となり、一方、不透
過部では光が漏れるため0%以上となる。透過像鮮明度の値Cは光学櫛の透明部の透過光
最大値Mと不透明部の透過光最小値mから次式により定義される。
すなわち、Cの値が100%に近づく程、防眩フィルムによる像のボケが小さい[参考
文献;須賀、三田村,塗装技術,1985年7月号]。
1DPが使用できる。光学櫛としては、0.125~2mm幅の光学櫛を用いることがで
きる。
本発明の防眩フィルムは、前記光学特性を発現するための防眩層を含んでいればよく、
材質や構造は限定されないが、通常、微細な凹凸形状が表面に形成された透明材料で形成
されており、この凹凸形状によって表面反射による外景の映り込みを抑制して防眩性を向
上できる。
明基材層の少なくとも一方の面に形成された防眩層とを含んでいてもよい。
形成されていてもよいが、生産性や取り扱い性などの点から、樹脂成分を含む組成物で形
成された防眩層が好ましい。防眩層の表面は、前述のように、通常、凹凸形状を有してお
り、この凹凸形状は、特に限定されず、物理的な加工や型を用いた転写などによって形成
された凹凸形状であってもよいが、生産性などの点から、樹脂成分を含む組成物で形成さ
れた防眩層において、樹脂成分の相分離構造によって形成された微細な凹凸形状や粒子の
形状に対応した微細な凹凸形状であってもよい。なかでも、1種以上の硬化樹脂前駆体成
分を含む硬化性組成物の硬化物において、液相からのスピノーダル分解(湿式スピノーダ
ル分解)により形成された凹凸形状や、粒子(例えば、ポリアミド粒子などの熱可塑性樹
脂粒子や、架橋ポリ(メタ)アクリル酸エステル粒子、架橋ポリスチレン系粒子、架橋ポ
リウレタン粒子などの架橋高分子粒子など)を含有させて粒子形状によって形成された凹
凸形状が好ましく、視認性と透明性と防眩性とを両立できる凹凸形状を形成し易い点から
、湿式スピノーダル分解により形成された凹凸形状が特に好ましい。
ー成分及び1種以上の硬化樹脂前駆体成分を含む硬化性組成物の硬化物であってもよい。
詳しくは、防眩層は、1種以上のポリマー成分と1種以上の硬化樹脂前駆体成分と溶媒と
を含む組成物(混合液)を用い、この組成物の液相から、溶媒を乾燥などにより蒸発又は
除去する過程で、濃度の濃縮に伴って、スピノーダル分解による相分離が生じ、相間距離
が比較的規則的な相分離構造を形成できる。より具体的には、前記湿式スピノーダル分解
は、通常、前記組成物(均一溶液)を支持体にコーティングし、塗布層から溶媒を蒸発さ
せることにより行うことができる。前記支持体として剥離性支持体を用いる場合には、防
眩層を支持体から剥離することにより防眩層単独で構成された防眩フィルムを得ることが
でき、支持体として透明な非剥離性支持体(透明基材層)を用いることにより、透明基材
層と防眩層とで構成された積層構造の防眩フィルムを得ることができる。
ポリマー成分としては、通常、熱可塑性樹脂が使用される。熱可塑性樹脂としては、透
明性が高く、スピノーダル分解により前述の表面凹凸形状を形成できれば特に限定されな
いが、例えば、スチレン系樹脂、(メタ)アクリル系重合体、有機酸ビニルエステル系重
合体、ビニルエーテル系重合体、ハロゲン含有樹脂、ポリオレフィン(脂環式ポリオレフ
ィンを含む)、ポリカーボネート、ポリエステル、ポリアミド、熱可塑性ポリウレタン、
ポリスルホン系樹脂(ポリエーテルスルホン、ポリスルホンなど)、ポリフェニレンエー
テル系樹脂(2,6-キシレノールの重合体など)、セルロース誘導体(セルロースエス
テル類、セルロースカーバメート類、セルロースエーテル類など)、シリコーン樹脂(ポ
リジメチルシロキサン、ポリメチルフェニルシロキサンなど)、ゴム又はエラストマー(
ポリブタジエン、ポリイソプレンなどのジエン系ゴム、スチレン-ブタジエン共重合体、
アクリロニトリル-ブタジエン共重合体、アクリルゴム、ウレタンゴム、シリコーンゴム
など)などが例示できる。これらの熱可塑性樹脂は、単独で又は二種以上組み合わせて使
用できる。
ル系重合体、ビニルエーテル系重合体、ハロゲン含有樹脂、脂環式ポリオレフィン、ポリ
カーボネート、ポリエステル、ポリアミド、セルロース誘導体、シリコーン系樹脂、ゴム
又はエラストマーなどが汎用される。また、ポリマー成分としては、通常、非結晶性であ
り、かつ有機溶媒(特に複数のポリマー成分や硬化樹脂前駆体成分を溶解可能な共通溶媒
)に可溶なポリマー成分が使用される。特に、成形性又は製膜性、透明性や耐候性の高い
ポリマー成分、例えば、スチレン系樹脂、(メタ)アクリル系重合体、脂環式ポリオレフ
ィン、ポリエステル系樹脂、セルロース誘導体(セルロースエステル類など)などが好ま
しく、(メタ)アクリル系重合体、セルロースエステル類が特に好ましい。
(メタ)アクリル系単量体と共重合性単量体との共重合体などが使用できる。(メタ)ア
クリル系単量体には、例えば、(メタ)アクリル酸;(メタ)アクリル酸メチル、(メタ
)アクリル酸エチル、(メタ)アクリル酸ブチル、(メタ)アクリル酸t-ブチル、(メ
タ)アクリル酸イソブチル、(メタ)アクリル酸ヘキシル、(メタ)アクリル酸オクチル
、(メタ)アクリル酸2-エチルヘキシルなどの(メタ)アクリル酸C1-10アルキル
;(メタ)アクリル酸フェニルなどの(メタ)アクリル酸アリール;ヒドロキシエチル(
メタ)アクリレート、ヒドロキシプロピル(メタ)アクリレートなどのヒドロキシアルキ
ル(メタ)アクリレート;グリシジル(メタ)アクリレート;N,N-ジアルキルアミノ
アルキル(メタ)アクリレート;(メタ)アクリロニトリル;トリシクロデカンなどの脂
環式炭化水素基を有する(メタ)アクリレートなどが例示できる。共重合性単量体には、
スチレンなどのスチレン系単量体、ビニルエステル系単量体、無水マレイン酸、マレイン
酸、フマル酸などが例示できる。これらの単量体は、単独で又は二種以上組み合わせて使
用できる。
タ)アクリル酸エステル、メタクリル酸メチル-(メタ)アクリル酸共重合体、メタクリ
ル酸メチル-(メタ)アクリル酸エステル共重合体、メタクリル酸メチル-アクリル酸エ
ステル-(メタ)アクリル酸共重合体、(メタ)アクリル酸エステル-スチレン共重合体
(MS樹脂など)などが例示できる。これらのうち、ポリ(メタ)アクリル酸メチルなど
のポリ(メタ)アクリル酸C1-6アルキル、特にメタクリル酸メチルを主成分(50~
100重量%、好ましくは70~100重量%程度)とするメタクリル酸メチル系重合体
が好ましい。
ート、セルローストリアセテートなどのセルロースアセテート;セルロースプロピオネー
ト、セルロースブチレート、セルロースアセテートプロピオネート、セルロースアセテー
トブチレートなどのC1-6脂肪族カルボン酸エステルなど)、芳香族有機酸エステル(
セルロースフタレート、セルロースベンゾエートなどのC7-12芳香族カルボン酸エス
テル)、無機酸エステル類(例えば、リン酸セルロース、硫酸セルロースなど)などが例
示でき、酢酸・硝酸セルロースエステルなどの混合酸エステルであってもよい。これらの
セルロースエステル類は、単独で又は二種以上組み合わせて使用できる。これらのうち、
セルロースジアセテート、セルローストリアセテート、セルロースアセテートプロピオネ
ート、セルロースアセテートブチレートなどのセルロースC2―4アシレートが好ましく
、セルロースアセテートプロピオネートなどのセルロースアセテートC3-4アシレート
が特に好ましい。
硬化樹脂前駆体成分と反応可能な官能基)を有するポリマーであってもよい。前記ポリマ
ーは、官能基を主鎖に有していてもよく、側鎖に有していてもよい。前記官能基は、共重
合や共縮合などにより主鎖に導入されてもよいが、通常、側鎖に導入される。このような
官能基としては、縮合性基や反応性基(例えば、ヒドロキシル基、酸無水物基、カルボキ
シル基、アミノ基又はイミノ基、エポキシ基、グリシジル基、イソシアネート基など)、
重合性基(例えば、ビニル、プロペニル、イソプロペニル、ブテニル、アリルなどのC2
-6アルケニル基、エチニル、プロピニル、ブチニルなどのC2-6アルキニル基、ビニ
リデンなどのC2-6アルケニリデン基、又はこれらの重合性基を有する基[(メタ)ア
クリロイル基など)など]などが例示できる。これらの官能基のうち、重合性基が好まし
い。
有する熱可塑性樹脂と、前記官能基との反応性基を有する重合性化合物とを反応させる方
法などが例示できる。
水物基、ヒドロキシル基、アミノ基、エポキシ基などが例示できる。
脂である場合、前記官能基との反応性基を有する重合性化合物としては、例えば、エポキ
シ基やヒドロキシル基、アミノ基、イソシアネート基などを有する重合性化合物などが例
示できる。これらのうち、エポキシ基を有する重合性化合物、例えば、エポキシシクロヘ
キセニル(メタ)アクリレートなどのエポキシシクロC5-8アルケニル(メタ)アクリ
レート、グリシジル(メタ)アクリレート、アリルグリシジルエーテルなどが汎用される
。
キシ基含有化合物、特に(メタ)アクリル系重合体((メタ)アクリル酸-(メタ)アク
リル酸エステル共重合体など)とエポキシ基含有(メタ)アクリレート(エポキシシクロ
アルケニル(メタ)アクリレートやグリシジル(メタ)アクリレートなど)との組み合わ
せが例示できる。具体的には、(メタ)アクリル系重合体のカルボキシル基の一部に重合
性不飽和基を導入したポリマー、例えば、(メタ)アクリル酸-(メタ)アクリル酸エス
テル共重合体のカルボキシル基の一部に、3,4-エポキシシクロヘキセニルメチルアク
リレートのエポキシ基を反応させて、側鎖に重合性基(光重合性不飽和基)を導入した(
メタ)アクリル系重合体(サイクロマーP、(株)ダイセル製)などが使用できる。
性樹脂1kgに対して、0.001~10モル、好ましくは0.01~5モル、さらに好
ましくは0.02~3モル程度である。
複数のポリマーで構成されていてもよい。複数のポリマーは、湿式スピノーダル分解によ
り、相分離可能であってもよい。また、複数のポリマーは、互いに非相溶であってもよい
。複数のポリマーを組み合わせる場合、第1のポリマーと第2のポリマーとの組み合わせ
は特に制限されないが、加工温度付近で互いに非相溶な複数のポリマー、例えば、互いに
非相溶な2つのポリマーとして適当に組み合わせて使用できる。例えば、第1のポリマー
が(メタ)アクリル系重合体(例えば、ポリメタクリル酸メチル、重合性基を有する(メ
タ)アクリル系重合体など)である場合、第2のポリマーは、セルロースエステル類(セ
ルロースアセテートプロピオネートなどのセルロースアセテートC3-4アシレートなど
)、ポリエステル(ウレタン変性ポリエステルなど)であってもよい。
マー、例えば、互いに非相溶なポリマーのうち一方のポリマー(第1のポリマーと第2の
ポリマーとを組み合わせる場合、少なくとも一方のポリマー)が硬化樹脂前駆体成分と反
応可能な官能基(特に重合性基)を側鎖に有するポリマーであるのが好ましい。
9.9/0.1、好ましくは5/95~99.5/0.5程度の範囲から選択できる。特
に、第1のポリマーが(メタ)アクリル系重合体であり、第2のポリマーがセルロースエ
ステル類である場合、両ポリマーの重量割合は、精細度50~150ppi程度の表示装
置(特に中型スクリーン表示装置)では、50/50~99/1、好ましくは55/45
~90/10、さらに好ましくは60/40~80/20(特に65/35~75/25
)程度であり、精細度が150ppiを超えて300ppi以下程度である表示装置(特
に中型スクリーンの表示装置)では、前者/後者=50/50~99.5/0.5、好ま
しくは70/30~99/1、さらに好ましくは90/10~98.5/1.5(特に9
5/5~98/2)程度である。
外にも、前記熱可塑性樹脂や他のポリマーが含まれていてもよい。
~230℃、さらに好ましくは0~200℃程度(例えば50~180℃程度)の範囲か
ら選択できる。なお、表面硬度の観点から、ガラス転移温度は50℃以上(例えば70~
200℃程度)、好ましくは100℃以上(例えば100~170℃程度)であるのが有
利である。ポリマー成分の重量平均分子量は、例えば1,000,000以下、好ましく
は1,000~500,000程度の範囲から選択できる。
硬化樹脂前駆体成分としては、熱や活性エネルギー線(紫外線や電子線など)などによ
り反応する官能基を有する化合物であり、熱や活性エネルギー線などにより硬化又は架橋
して樹脂(特に硬化又は架橋樹脂)を形成可能な種々の硬化性化合物を使用できる。前記
硬化樹脂前駆体成分としては、例えば、熱硬化性化合物又は樹脂[エポキシ基、重合性基
、イソシアネート基、アルコキシシリル基、シラノール基などを有する低分子量化合物(
例えば、エポキシ系樹脂、不飽和ポリエステル系樹脂、ウレタン系樹脂、シリコーン系樹
脂など)など]、活性光線(紫外線など)により硬化可能な光硬化性化合物(光硬化性モ
ノマー、オリゴマーなどの紫外線硬化性化合物など)などが例示でき、光硬化性化合物は
、EB(電子線)硬化性化合物などであってもよい。なお、光硬化性モノマー、オリゴマ
ーや低分子量であってもよい光硬化性樹脂などの光硬化性化合物を、単に「光硬化性樹脂
」という場合がある。
含まれる。
)アクリル系単量体、ビニルピロリドンなどのビニル系単量体、イソボルニル(メタ)ア
クリレート、アダマンチル(メタ)アクリレートなどの橋架環式炭化水素基を有する(メ
タ)アクリレートなど]、少なくとも2つの重合性不飽和結合を有する多官能性単量体[
エチレングリコールジ(メタ)アクリレート、プロピレングリコールジ(メタ)アクリレ
ート、ブタンジオールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アク
リレート、ヘキサンジオールジ(メタ)アクリレートなどのアルキレングリコールジ(メ
タ)アクリレート;ジエチレングリコールジ(メタ)アクリレート、ジプロピレングリコ
ールジ(メタ)アクリレート、ポリオキシテトラメチレングリコールジ(メタ)アクリレ
ートなどの(ポリ)オキシアルキレングリコールジ(メタ)アクリレート;トリシクロデ
カンジメタノールジ(メタ)アクリレート、アダマンタンジ(メタ)アクリレートなどの
橋架環式炭化水素基を有するジ(メタ)アクリレート;グリセリントリ(メタ)アクリレ
ート、トリメチロールプロパントリ(メタ)アクリレート、トリメチロールエタントリ(
メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ジトリメチロー
ルプロパンテトラ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレ
ート、ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘ
キサ(メタ)アクリレートなどの3~6程度の重合性不飽和結合を有する多官能性単量体
など]などが例示できる。
タ)アクリレート、エポキシ(メタ)アクリレート[ビスフェノールA型エポキシ(メタ
)アクリレート、ノボラック型エポキシ(メタ)アクリレートなど]、ポリエステル(メ
タ)アクリレート[例えば、脂肪族ポリエステル型(メタ)アクリレート、芳香族ポリエ
ステル型(メタ)アクリレートなど]、(ポリ)ウレタン(メタ)アクリレート[ポリエ
ステル型ウレタン(メタ)アクリレート、ポリエーテル型ウレタン(メタ)アクリレート
など]、シリコーン(メタ)アクリレートなどが例示できる。
、短時間で硬化できる光硬化性化合物、例えば、紫外線硬化性化合物(モノマー、オリゴ
マーや低分子量であってもよい樹脂など)、EB硬化性化合物が好ましい。特に、実用的
に有利な樹脂前駆体は、紫外線硬化性樹脂である。さらに、耐擦傷性などの耐性を向上さ
せるため、光硬化性樹脂は、分子中に2以上(好ましくは2~6、さらに好ましくは2~
4程度)の重合性不飽和結合を有する化合物であるのが好ましい。
クロマトグラフィ(GPC)において、ポリスチレン換算で、ポリマーとの相溶性を考慮
して5000以下、好ましくは2000以下、さらに好ましくは1000以下程度である
。
ィラー及び/又はフッ素原子を含有していてもよい。
子などの無機粒子、架橋(メタ)アクリル系重合体粒子、架橋スチレン系樹脂粒子などの
有機粒子を含んでいてもよい。これらのフィラーは、単独で又は二種以上組み合わせて使
用できる。
性を両立できる凹凸形状を形成し易い点から、ナノメータサイズのシリカ粒子(シリカナ
ノ粒子)が好ましい。シリカナノ粒子は、防眩フィルムの黄色度を抑制できる点から、中
実のシリカナノ粒子が好ましい。また、シリカナノ粒子の平均粒径は、例えば1~800
nm、好ましくは3~500nm、さらに好ましくは5~300nm程度である。
0重量%程度であってもよく、例えば10~80重量%、好ましくは15~70重量%、
さらに好ましくは20~50重量%程度である。
素系化合物)としては、前記単量体及びオリゴマーのフッ化物、例えば、フッ化アルキル
(メタ)アクリレート[例えば、パーフルオロオクチルエチル(メタ)アクリレートやト
リフルオロエチル(メタ)アクリレートなど]、フッ化(ポリ)オキシアルキレングリコ
ールジ(メタ)アクリレート[例えば、フルオロエチレングリコールジ(メタ)アクリレ
ート、フルオロポリエチレングリコールジ(メタ)アクリレート、フルオロプロピレング
リコールジ(メタ)アクリレートなど]、フッ素含有エポキシ樹脂、フッ素含有ウレタン
系樹脂などが挙げられる。これらのうち、(メタ)アクリロイル基を有するフルオロポリ
エーテル化合物が好ましい。フッ素含有硬化性化合物は、市販のフッ素系重合性レベリン
グ剤であってもよい。
、熱硬化性樹脂では、アミン類、多価カルボン酸類などの硬化剤を含んでいてもよく、光
硬化性樹脂では光重合開始剤を含んでいてもよい。光重合開始剤としては、慣用の成分、
例えば、アセトフェノン類又はプロピオフェノン類、ベンジル類、ベンゾイン類、ベンゾ
フェノン類、チオキサントン類、アシルホスフィンオキシド類などが例示できる。光重合
開始剤などの硬化剤の割合は、硬化樹脂前駆体成分全体に対して0.1~20重量%、好
ましくは0.5~10重量%、さらに好ましくは1~8重量%程度である。
は、光硬化促進剤、例えば、第三級アミン類(ジアルキルアミノ安息香酸エステルなど)
、ホスフィン系光重合促進剤などを含んでいてもよい。
タエリスリトールヘキサ(メタ)アクリレートなどの2~8程度の重合性基を有する(メ
タ)アクリレートなど)、エポキシ(メタ)アクリレート、ポリエステル(メタ)アクリ
レート、ウレタン(メタ)アクリレート、シリコーン(メタ)アクリレートなどが好まし
い。さらに、硬化樹脂前駆体成分は、シリカナノ粒子及び/又はフッ素原子を含むのが好
ましく、シリカナノ粒子含有光硬化性化合物[特に、シリカナノ粒子を含む多官能性(メ
タ)アクリレート、シリカナノ粒子を含むウレタン(メタ)アクリレート、シリカナノ粒
子を含むシリコーン(メタ)アクリレート]及びフッ素含有硬化性化合物を含むのが特に
好ましい。
合物とシリコーン(メタ)アクリレートとの組み合わせ、ウレタン(メタ)アクリレート
と3~6官能(メタ)アクリレートとシリコーン(メタ)アクリレートとフッ素含有硬化
性化合物との組み合わせ、シリカナノ粒子含有光硬化性化合物とフッ素含有硬化性化合物
との組み合わせであり、特に好ましい組み合わせは、精細度50~150ppi程度の表
示装置(特に中型スクリーン表示装置)では、シリカナノ粒子含有光硬化性化合物とフッ
素含有硬化性化合物との組み合わせであり、精細度が150ppiを超えて300ppi
以下程度である表示装置(特に中型スクリーンの表示装置)では、ウレタン(メタ)アク
リレートとシリコーン(メタ)アクリレートとの組み合わせである。
リカナノ粒子が硬化樹脂前駆体成分全体に対して前記割合となるように、硬化樹脂前駆体
成分中に、シリカナノ粒子含有硬化樹脂前駆体成分を含むのが好ましい。また、フッ素含
有硬化性化合物の割合は、硬化樹脂前駆体成分全体に対して例えば0.001~1重量%
(例えば0.01~0.5重量%)、好ましくは0.02~0.3重量%(例えば0.0
3~0.2重量%)、さらに好ましくは0.05~0.1重量%程度である。
合、シリコーン(メタ)アクリレートの割合は、ウレタン(メタ)アクリレート100重
量部に対して、例えば0.1~10重量部、好ましくは0.3~5重量部、さらに好まし
くは0.5~3重量部(特に1~2重量部)程度である。
本発明では、前記ポリマー成分及び前記硬化樹脂前駆体成分のうち、少なくとも2つの
成分が、加工温度付近で互いに相分離する組み合わせで使用される。相分離する組み合わ
せとしては、例えば、(a)複数のポリマー成分同士が互いに非相溶で相分離する組み合
わせ、(b)ポリマー成分と硬化樹脂前駆体成分とが非相溶で相分離する組み合わせ、(
c)複数の硬化樹脂前駆体成分同士が互いに非相溶で相分離する組み合わせなどが挙げら
れる。これらの組み合わせのうち、通常、(a)複数のポリマー成分同士の組み合わせや
、(b)ポリマー成分と硬化樹脂前駆体成分との組み合わせであり、特に(a)複数のポ
リマー成分同士の組み合わせが好ましい。相分離させる両者の相溶性が高い場合、溶媒を
蒸発させるための乾燥過程で両者が有効に相分離せず、防眩層としての機能が低下する。
成分と硬化樹脂前駆体成分とが非相溶で相分離する場合に、ポリマー成分として複数のポ
リマー成分を用いてもよい。複数のポリマー成分を用いる場合、少なくとも1つのポリマ
ー成分が硬化樹脂前駆体成分に対して非相溶であればよく、他のポリマー成分は前記硬化
樹脂前駆体成分と相溶してもよい。また、互いに非相溶な2つのポリマー成分と硬化樹脂
前駆体成分(特に、複数の硬化性官能基を有するモノマー又はオリゴマー)との組み合わ
せであってもよい。
脂前駆体成分は、非相溶な複数のポリマーのうち、少なくとも1つのポリマー成分と加工
温度付近で互いに相溶する組合せで使用される。すなわち、互いに非相溶な複数のポリマ
ー成分を、例えば、第1のポリマーと第2のポリマーとで構成する場合、硬化樹脂前駆体
成分は、第1のポリマー又は第2のポリマーのいずれかと相溶すればよく、両方のポリマ
ー成分と相溶してもよいが、好ましくは一方のポリマー成分のみと相溶する方がよい。両
方のポリマー成分に相溶する場合、第1のポリマー及び硬化樹脂前駆体成分を主成分とし
た混合物と、第2のポリマー及び硬化樹脂前駆体成分を主成分とした混合物との少なくと
も二相に相分離する。
ポリマー成分同士が有効に相分離せず、防眩層としての機能が低下する。複数のポリマー
成分の相分離性は、双方の成分に対する良溶媒を用いて均一溶液を調製し、溶媒を徐々に
蒸発させる過程で、残存固形分が白濁するか否かを目視にて確認することにより簡便に判
定できる。
橋樹脂とは互いに屈折率が異なる。また、複数のポリマー成分(第1のポリマーと第2の
ポリマー)の屈折率も互いに異なる。ポリマー成分と硬化又は架橋樹脂との屈折率の差、
複数のポリマー成分(第1のポリマーと第2のポリマーと)の屈折率の差は、例えば0.
001~0.2、好ましくは0.05~0.15程度であってもよい。
前者/後者=1/99~95/5程度の範囲から選択でき、例えば2/98~90/10
、好ましくは3/97~80/20、さらに好ましくは5/95~70/30程度である
。また、精細度50~150ppi程度の表示装置(特に中型スクリーン表示装置)では
、ポリマー成分と硬化樹脂前駆体成分との割合(重量比)は、例えば2/98~30/7
0、好ましくは3/97~20/80、さらに好ましくは5/95~15/85程度であ
ってもよい。さらに、精細度が150ppiを超えて300ppi以下程度である表示装
置(特に中型スクリーンの表示装置)では、例えば10/90~60/40、好ましくは
20/80~50/50、さらに好ましくは35/65~45/55程度であってもよい
。
樹脂成分を含む組成物で形成された防眩層は、種々の添加剤、例えば、レベリング剤、
安定剤(酸化防止剤、紫外線吸収剤など)、界面活性剤、水溶性高分子、充填剤、架橋剤
、カップリング剤、着色剤、難燃剤、滑剤、ワックス、防腐剤、粘度調整剤、増粘剤、消
泡剤などを含んでいてもよい。添加剤の割合は、例えば、防眩層全体に対して、例えば0
.01~10重量%(特に0.1~5重量%)程度である。
防眩層の厚み(平均厚み)は、例えば0.3~20μm程度、好ましくは1~15μm
(例えば1~10μm)程度であってもよく、通常3~12μm(特に4~10μm)程
度である。なお、防眩層単独で防眩フィルムを構成する場合、防眩層の厚み(平均厚み)
は、例えば1~100μm、好ましくは3~50μm程度である。
透明基材層は、透明材料で形成されていればよく、用途に応じて選択でき、ガラスなど
の無機材料であってもよいが、強度や成形性などの点から、有機材料が汎用される。有機
材料としては、例えば、セルロース誘導体、ポリエステル、ポリアミド、ポリイミド、ポ
リカーボネート、(メタ)アクリル系重合体などが例示できる。これらのうち、セルロー
スエステル、ポリエステルなどが汎用される。
アセテート、セルロースアセテートプロピオネート、セルロースアセテートブチレートな
どのセルロースアセテートC3-4アシレートなどが挙げられる。ポリエステルとしては
、ポリエチレンテレフタレート(PET)、ポリエチレンナフタレート(PEN)などの
ポリアルキレンアリレートなどが挙げられる。
どのポリC2-4アルキレンアリレートが好ましい。
合も防眩層と同様である。
的に等方性に優れる点から、未延伸フィルムであってもよい。
や紫外線照射処理など)されていてもよく、易接着層を有していてもよい。
0μm、さらに好ましくは20~500μm程度である。
本発明の防眩フィルムは、スマートフォンやPC(タブレットPCなど)などを含む各
種のタッチパネル表示装置の保護フィルムとしても使用可能である。これらの用途では、
前記透明基材層の他方の面の少なくとも一部に粘着層が形成されていてもよい。
着剤、アクリル系粘着剤、オレフィン系粘着剤(変性オレフィン系粘着剤など)、シリコ
ーン系粘着剤などが例示できる。これらの粘着剤のうち、光学特性やリワーク性などの点
から、シリコーン系粘着剤が好ましい。
くは20~70μm(特に25~50μm)程度である。
してもいずれでもよい。さらに、周縁部に形成する場合、貼着のための取り扱い性を向上
させる目的で、防眩フィルムの周縁部に枠状部材(例えば、周縁部にプラスチックシート
を積層)を形成し、枠状部材に粘着層を形成してもよい。
本発明の防眩フィルムの製造方法は、特に限定されず、材料の種類に応じて、適宜選択
でき、物理的な加工や型を用いた転写などにより形成してもよいが、生産性などの点から
、硬化性組成物を熱又は活性エネルギー線で硬化させる硬化工程を経て製造する方法が好
ましい。特に、湿式スピノーダル分解により形成された凹凸形状を有する防眩層を含む防
眩フィルムでは、支持体(特に、透明基材層)の上に、1種以上のポリマー成分及び1種
以上の硬化樹脂前駆体成分を含む硬化性組成物を塗布して乾燥することにより、ポリマー
成分及び硬化樹脂前駆体成分から選択される少なくとも2つの成分を、湿式スピノーダル
分解により相分離させる相分離工程、相分離した硬化性組成物を熱又は活性エネルギー線
で硬化させる硬化工程を経る方法であってもよい。
成分及び硬化樹脂前駆体成分の種類及び溶解性に応じて選択でき、少なくとも固形分(例
えば、複数のポリマー成分及び硬化樹脂前駆体成分、反応開始剤、その他添加剤)を均一
に溶解できる溶媒であればよい。特に、ポリマー成分及び硬化樹脂前駆体に対する溶媒の
溶解性を調整することにより、相分離構造を制御してもよい。そのような溶媒としては、
例えば、ケトン類(アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘ
キサノンなど)、エーテル類(ジオキサン、テトラヒドロフランなど)、脂肪族炭化水素
類(ヘキサンなど)、脂環式炭化水素類(シクロヘキサンなど)、芳香族炭化水素類(ト
ルエン、キシレンなど)、ハロゲン化炭素類(ジクロロメタン、ジクロロエタンなど)、
エステル類(酢酸メチル、酢酸エチル、酢酸ブチルなど)、水、アルコール類(エタノー
ル、イソプロパノール、ブタノール、シクロヘキサノールなど)、セロソルブ類[メチル
セロソルブ、エチルセロソルブ、プロピレングリコールモノメチルエーテル(1-メトキ
シ-2-プロパノール)など]、セロソルブアセテート類、スルホキシド類(ジメチルス
ルホキシドなど)、アミド類(ジメチルホルムアミド、ジメチルアセトアミドなど)など
が例示できる。また、溶媒は混合溶媒であってもよい。
類と、アルコール類(ブタノールなど)及び/又はセロソルブ類(1-メトキシ-2-プ
ロパノールなど)との混合溶媒が特に好ましい。混合溶媒において、アルコール類及び/
又はセロソルブ類(両者を混合する場合、総量)の割合は、精細度50~150ppi程
度の表示装置(特に中型スクリーン表示装置)では、ケトン類100重量部に対して、例
えば10~150重量部、好ましくは15~100重量部、さらに好ましくは20~80
重量部(特に25~50重量部)程度であり、精細度が150ppiを超えて300pp
i以下程度である表示装置(特に中型スクリーンの表示装置)では、ケトン類100重量
部に対して、例えば3~100重量部、好ましくは5~50重量部、さらに好ましくは1
0~30重量部(特に15~20重量部)程度である。アルコール類とセロソルブ類とを
組み合わせる場合、セロソルブ類の割合は、アルコール類100重量部に対して、例えば
10~120重量部、好ましくは30~100重量部、さらに好ましくは50~80重量
部(特に60~70重量部)程度である。本発明では、溶媒を適宜組み合わせることによ
り、スピノーダル分解による相分離を調整し、視認性と透明性と防眩性とを両立できる凹
凸形状を形成できる。
濃度は、相分離が生じる範囲及び流延性やコーティング性などを損なわない範囲で選択で
き、例えば1~80重量%、好ましくは10~70重量%、さらに好ましくは20~60
重量%(特に30~55重量%)程度である。
ードコーター、ロッドコーター、リバースコーター、バーコーター、コンマコーター、デ
ィップ・スクイズコーター、ダイコーター、グラビアコーター、マイクログラビアコータ
ー、シルクスクリーンコーター法、ディップ法、スプレー法、スピナー法などが挙げられ
る。これらの方法のうち、バーコーター法やグラビアコーター法などが汎用される。なお
、必要であれば、塗布液は複数回に亘り塗布してもよい。
りも1~120℃、好ましくは5~50℃、特に10~50℃程度低い温度)で溶媒を蒸
発させることにより、スピノーダル分解による相分離を誘起することができる。溶媒の蒸
発は、通常、乾燥、例えば、溶媒の沸点に応じて、30~200℃(例えば30~100
℃)、好ましくは40~120℃、さらに好ましくは50~90℃(特に60~85℃)
程度の温度で乾燥させることにより行うことができる。
距離に規則性又は周期性を付与できる。
より最終的に硬化させることにより、スピノーダル分解により形成された相分離構造を直
ちに固定化できる。硬化性組成物の硬化は、硬化樹脂前駆体成分の種類に応じて、加熱、
光照射などを組み合わせてもよい。
硬化成分などの種類に応じて選択でき、通常、紫外線、電子線などが利用できる。汎用的
な光源は、通常、紫外線照射装置である。
高圧水銀ランプ、超高圧水銀ランプ、ハロゲンランプ、レーザー光源(ヘリウム-カドミ
ウムレーザー、エキシマレーザーなどの光源)などを利用できる。照射光量(照射エネル
ギー)は、塗膜の厚みにより異なり、例えば10~10000mJ/cm2、好ましくは
20~5000mJ/cm2、さらに好ましくは30~3000mJ/cm2程度である
。光照射は、必要であれば、不活性ガス雰囲気中で行ってもよい。
本発明の防眩フィルムは、透明性と防眩性とを両立できるため、種々の表示装置、例え
ば、液晶表示装置(LCD)、有機ELディスプレイ、タッチパネル付き表示装置などの
光学部材として利用でき、特に、LCD、有機ELディスプレイの光学要素として有用で
ある。
射型LCDであってもよく、表示ユニットを照明するためのバックライトユニットを備え
た透過型LCDであってもよい。反射型LCDでは、外部からの入射光を、表示ユニット
を介して取り込み、表示ユニットを透過した透過光を反射部材により反射して表示ユニッ
トを照明できる。反射型LCDでは、前記反射部材から前方の光路内に本発明の防眩フィ
ルムを配設できる。例えば、本発明の防眩フィルムは、表示ユニットの前面(視認側前面
)などに配設又は積層でき、特に、コリメートバックライトユニットを有し、かつプリズ
ムシートを有さないLCDの前面に配設してもよい。
光ダイオードなどの点状光源など)からの光を一方の側部から入射させて前面の出射面か
ら出射させるための導光板(例えば、断面楔形状の導光板)を備えていてもよい。また、
必要であれば、導光板の前面側にはプリズムシートを配設してもよい。なお、通常、導光
板の裏面には、光源からの光を出射面側へ反射させるための反射部材が配設されている。
このような透過型LCDでは、通常、光源から前方の光路内に、本発明の防眩フィルムを
配設できる。例えば、導光板と表示ユニットとの間、表示ユニットの前面などに前記、本
発明の防眩フィルムを配設又は積層できる。
、この発光素子は、通常、金属などの陰電極/電子注入層/電子輸送層/発光層/正孔輸
送層/正孔注入層/ITOなどの陽電極/ガラス板や透明のプラスチック板などの基板で
形成されている。有機ELディスプレイにおいても、本発明の防眩フィルムを光路内に配
設してもよい。
含む)や有機ELディスプレイ(タッチパネル付き表示装置でもある有機ELディスプレ
イを含む)の傷つきを防止するためのアフターマーケット向け保護又はプロテクトフィル
ムとして利用してもよい。
よって限定されるものではない。実施例及び比較例で用いた原料は以下の通りであり、得
られた防眩フィルムを以下の方法で評価した。
重合性基を有するアクリル系重合体:ダイセル・オルネクス(株)製「サイクロマーP
」
セルロースアセテートプロピオネート:イーストマン社製「CAP-482-20」、
アセチル化度=2.5%、プロピオニル度=46%、ポリスチレン換算の数平均分子量7
5000
シリコーンアクリレート:ダイセル・オルネクス(株)製「EB1360」
シリコーン系ハードコート材:(株)トクシキ製「AS-201S」
ウレタンアクリレートA:新中村化学工業(株)製「U-15HA」
ウレタンアクリレートB:(株)トクシキ製「AU-230」
ジペンタエリスリトールヘキサアクリレート:ダイセル・オルネクス(株)製「DPH
A」
ナノシリカ含有アクリル系紫外線硬化性化合物:モメンティブ・パフォーマンス・マテ
リアルズ・ジャパン合同会社製「XR39-C6210」
シリカ含有アクリル系紫外線硬化性化合物:アイカ工業(株)製「Z-757-4RL
」
アクリル系紫外線硬化性化合物:アイカ工業(株)製「Z-757-4CL」
PMMAビーズA:積水化学工業(株)製「SSX-115」
PMMAビーズB:積水化学工業(株)製「SSX-105」
架橋スチレンビーズ:綜研化学(株)製「SX-130H」
重合性基を有するフッ素系化合物:(株)ネオス製「フタージェント602A」
光開始剤A:BASFジャパン(株)製「イルガキュア184」
光開始剤B:BASFジャパン(株)製「イルガキュア907」
ポリエチレンテレフタレート(PET)フィルム:三菱樹脂(株)製「ダイアホイル」
セルローストリアセテート(TAC)フィルム:富士フイルム(株)製「フジタックT
G60UL」。
光学式膜厚計を用いて、任意の10箇所を測定し、平均値を算出した。
JIS Z8701に準拠して分光光度計((株)日立ハイテクサイエンス製「U-3
900H」)を用いて測定した。防眩フィルムは市販の黒色アクリル板に光学糊で貼り付
け、裏面からの反射ができるだけ影響しないようにしたものを測定対象とした。
ヘイズメーター(日本電色(株)製「NDH-5000W」)を用いて、JIS K7
136に準拠し、凹凸構造を有する表面が受光器側となるように配置して測定した。
JIS K7105に準拠してグロスメーター((株)掘場製作所製「IG-320」
)を用いて角度60度で測定した。
防眩フィルムの写像鮮明度を、写像測定器(スガ試験機(株)製、商品名「ICM-1
T」)を用いて、JIS K7105に基づき、フィルムの製膜方向と光学櫛の櫛歯の方
向とが平行になるようにフィルムを設置して測定を行った。写像測定器の光学櫛のうち、
0.5mm幅の光学櫛における写像鮮明度を測定した。
作製した防眩フィルムを市販の黒色アクリル板に光学糊で貼り付け、三波長蛍光灯を照
らしたときの反射像を目視で確認し、以下の基準で評価した。
○:蛍光灯の輪郭がぼける
△:蛍光灯の輪郭が認識できる。
作製した防眩フィルムを市販の黒色アクリル板に光学糊で貼り付け、三波長蛍光灯を照
らしたときの反射光の強さを目視で確認し、以下の基準で評価した。
○:反射光が少し見える
△:反射光がはっきり見える。
作製した防眩フィルムを液晶モニター(ヒューレットパッカード社製「P222va」
、精細度102ppi)に光学糊で貼り付け、文字を表示したときのボケを目視確認し、
以下の基準で評価した。
○:わずかに文字がボケているが、読み取りに影響はない
△:明らかに文字がボケており、難しいが読み取りは可能である
×:ボケが強く文字をほとんど認識できない。
作製した防眩フィルムを液晶タブレット(アップル社製「iPad Air(登録商標
)」、精細度264ppi)に光学糊で貼り付け、文字を表示したときのボケを目視確認
し、以下の基準で評価した。
○:わずかに文字がボケているが、読み取りに影響はない
△:明らかに文字がボケており、難しいが読み取りは可能である
×:ボケが強く文字をほとんど認識できない。
重合性基を有するアクリル系重合体15.0重量部、セルロースアセテートプロピオネ
ート3重量部、ナノシリカ含有アクリル系紫外線硬化性化合物の150重量部、シリコー
ンアクリレート1重量部を、メチルエチルケトン101重量部と1-ブタノール24重量
部との混合溶媒に溶解し、溶液を調製した。
℃のオーブン内に1分間放置し、溶媒を蒸発させて厚さ約9μmのコート層を形成した。
0mJ/cm2照射、以下同様)コート層を紫外線硬化処理し、防眩フィルムを得た。
重合性基を有するアクリル系重合体12.5重量部、セルロースアセテートプロピオネ
ート4重量部、ナノシリカ含有アクリル系紫外線硬化性化合物150重量部、シリコーン
アクリレート1重量部を、メチルエチルケトン81重量部と1-ブタノール24重量部と
1-メトキシ-2-プロパノール13重量部との混合溶媒に溶解し、溶液を調製した。
℃のオーブン内に1分間放置し、溶媒を蒸発させて厚さ約9μmのコート層を形成した。
硬化処理し、防眩フィルムを得た。
重合性基を有するアクリル系重合体45.6重量部、セルロースアセテートプロピオネ
ート2.3重量部、ウレタンアクリレートA70.7重量部、ジペンタエリスリトールヘ
キサアクリレート8.2重量部、シリコーンアクリレート0.6重量部、重合性基を有す
るフッ素系化合物0.1重量部、光開始剤A1重量部、光開始剤B1重量部を、メチルエ
チルケトン128重量部と1-ブタノール25重量部とシクロヘキサノン31重量部との
混合溶媒に溶解し、溶液を調製した。
℃のオーブン内に1分間放置し、溶媒を蒸発させて厚さ約7μmのコート層を形成した。
硬化処理し、防眩フィルムを得た。
重合性基を有するアクリル系重合体12.5重量部、セルロースアセテートプロピオネ
ート5.5重量部、ナノシリカ含有アクリル系紫外線硬化性化合物149重量部、重合性
基を有するフッ素系化合物0.1重量部を、メチルエチルケトン129重量部と1-ブタ
ノール24重量部と1-メトキシ-2-プロパノール13重量部との混合溶媒に溶解し、
溶液を調製した。
℃のオーブン内に1分間放置し、溶媒を蒸発させて厚さ約5μmのコート層を形成した。
硬化処理し、防眩フィルムを得た。
重合性基を有するアクリル系重合体7.5重量部、セルロースアセテートプロピオネー
ト5.5重量部、ナノシリカ含有アクリル系紫外線硬化性化合物151.5重量部、シリ
コーンアクリレート1重量部、メチルエチルケトン129重量部と1-ブタノール24重
量部と1-メトキシ-2-プロパノール15重量部との混合溶媒に溶解し、溶液を調製し
た。
℃のオーブン内に1分間放置し、溶媒を蒸発させて厚さ約5μmのコート層を形成した。
硬化処理し、防眩フィルムを得た。
重合性基を有するアクリル系重合体50重量部、セルロースアセテートプロピオネート
4重量部、ウレタンアクリレートA76重量部、シリコーンアクリレート1重量部、光開
始剤A1重量部、光開始剤B1重量部を、メチルエチルケトン176重量部と1-ブタノ
ール28重量部との混合溶媒に溶解し、溶液を調製した。
℃のオーブン内に1分間放置し、溶媒を蒸発させて厚さ約8μmのコート層を形成した。
硬化処理し、防眩フィルムを得た。
セルロースアセテートプロピオネート3重量部、ウレタンアクリレートA97重量部、
PMMAビーズB90重量部、光開始剤A1重量部、光開始剤B1重量部を、メチルエチ
ルケトン277重量部と1-ブタノール23重量部との混合溶媒に溶解し、溶液を調製し
た。
のオーブン内に1分間放置し、溶媒を蒸発させて厚さ約1μmのコート層を形成した。
硬化処理し、防眩フィルムを得た。
ウレタンアクリレートB39重量部、シリコーン系ハードコート材15.7重量部、P
MMAビーズA0.3重量部、架橋スチレンビーズ6.1重量部をメチルエチルケトン3
8重量部に溶解、溶液を調製した。
℃のオーブン内に1分間放置し、溶媒を蒸発させて厚さ約6μmのコート層を形成させた
。
硬化処理し、防眩フィルムを得た。
シリカ含有アクリル系紫外線硬化性化合物50質量部とアクリル系紫外線硬化性化合物
150質量部とを混合した溶液を調製した。この溶液を、ワイヤーバー(#14)を用い
て、PETフィルム上に流延した後、80℃のオーブン内に1分間放置し、溶媒を蒸発さ
せて厚さ約7μmのコート層を形成した。
防眩フィルムを得た。
制され、視認性も優れていた。
は無機ELディスプレイ、フィールドエミッションディスプレイ(FED)、表面電界デ
ィスプレイ(SED)、リアプロジェクションテレビディスプレイ、プラズマディスプレ
イ、タッチパネル付き表示装置などの表示装置に利用される防眩フィルムとして利用でき
る。
スクリーンの表示装置(例えば、カーナビゲーション用ディスプレイ、ゲーム機器、スマ
ートフォン、タブレットPCなどのディスプレイ及びタッチパネル付き表示装置など)、
中型スクリーンの表示装置(例えば、ノート型又はラップトップ型PCやデスクトップ型
PCなどのPC、テレビなど)、大型スクリーンの表示装置(例えば、デジタルサイネー
ジなど)などに利用できる。これらのうち、解像度の違いに応じて適宜選択できるが、視
認性と防眩性とを両立できる点から、中型スクリーンの表示装置に好適に利用できる。さ
らに、中型スクリーンの表示装置のなかでも、精細度50~150ppi程度の表示装置
(ラップトップ型又はデスクトップ型PC、テレビなど)や、精細度が150ppiを超
えて300ppi以下程度である表示装置(ノート型PCやタブレットPCなど)などに
特に好適に利用できる。
や有機ELディスプレイのアフターマーケット向け保護フィルム(プロテクトフィルム)
としても利用できる。
Claims (9)
- 透明基材層と、この透明基材層の少なくとも一方の面に形成された防眩層とを含み、視感度反射率が3~3.8%であり、0.5mm幅の光学櫛を使用した透過像鮮明度が8~25%であり、60度グロスが15%以下であり、かつヘイズが40~70%である防眩フィルムであって、
前記防眩層が、セルロースエステル類及び/又は重合性基を有する(メタ)アクリル系重合体、並びに1種以上の硬化樹脂前駆体成分を含む硬化性組成物の硬化物である防眩フィルム。 - セルロースエステル類及び/又は重合性基を有する(メタ)アクリル系重合体、並びに硬化樹脂前駆体成分から選択される少なくとも2つの成分が、湿式スピノーダル分解により相分離可能である請求項1記載の防眩フィルム。
- 硬化樹脂前駆体成分が、多官能(メタ)アクリレート、エポキシ(メタ)アクリレート、ポリエステル(メタ)アクリレート、ウレタン(メタ)アクリレート及びシリコーン(メタ)アクリレートから選択された少なくとも1種を含む請求項1又は2記載の防眩フィルム。
- 硬化樹脂前駆体成分が、シリカナノ粒子及び/又はフッ素原子を含む請求項1~3のいずれかに記載の防眩フィルム。
- 硬化性組成物を熱又は活性エネルギー線で硬化させる硬化工程を含む請求項1~4のいずれかに記載の防眩フィルムの製造方法。
- 支持体の上に、セルロースエステル類及び/又は重合性基を有する(メタ)アクリル系重合体、並びに1種以上の硬化樹脂前駆体成分を含む硬化性組成物を塗布して乾燥することにより、セルロースエステル類及び/又は重合性基を有する(メタ)アクリル系重合体、並びに硬化樹脂前駆体成分から選択される少なくとも2つの成分を、湿式スピノーダル分解により相分離させる相分離工程をさらに含み、硬化工程が、相分離した硬化性組成物を熱又は活性エネルギー線で硬化させる硬化工程である請求項5記載の防眩フィルムの製造方法。
- 請求項1~4のいずれかに記載の防眩フィルムを備えた表示装置。
- 有機ELディスプレイ又は液晶表示装置である請求項7記載の表示装置。
- 透明基材層と、この透明基材層の少なくとも一方の面に形成された防眩層とを含み、前記防眩層が、セルロースエステル類及び/又は重合性基を有する(メタ)アクリル系重合体、並びに1種以上の硬化樹脂前駆体成分を含む硬化性組成物の硬化物である防眩フィルムにおいて、視感度反射率、0.5mm幅の光学櫛を使用した透過像鮮明度、60度グロス及びヘイズを、それぞれ3~3.8%、8~25%、15%以下及び40~70%に調整し、防眩フィルムの防眩性及び視認性を向上する方法。