JP2022078640A

JP2022078640A - Kitchen towel roll

Info

Publication number: JP2022078640A
Application number: JP2020189463A
Authority: JP
Inventors: 康伸大岡; Yasunobu Ooka; 光佐藤; Hikari Sato; 祐樹藤田; Yuki Fujita; 幸治大篭; Koji Okago
Original assignee: Nippon Paper Crecia Co Ltd
Current assignee: Nippon Paper Crecia Co Ltd
Priority date: 2020-11-13
Filing date: 2020-11-13
Publication date: 2022-05-25
Also published as: JP2024083615A

Abstract

To provide a kitchen towel roll that is reusable, that has a large amount of water absorption, and that has less paper powder and has more than a certain level of wound length.SOLUTION: In the kitchen towel roll, there is taken up in a roll a kitchen towel sheet which contains synthetic fiber and pulp fiber and which is applied with one ply embossing. The basis weight of the kitchen towel sheet is 50 g/m2 or more and 200 g/m2 or less; the depth of embossing is 0.1 mm or more and 2 mm or less; and the wound length of a roll is 5 m or more and 24 m or less.SELECTED DRAWING: Figure 1

Description

本発明は、キッチンタオルロールに関する。 The present invention relates to a kitchen towel roll.

近年、ハンドタオルロール、キッチンタオルロール等の、厚手の紙をロール状に巻き取った製品が市販されている。 In recent years, products such as hand towel rolls and kitchen towel rolls, which are made by winding thick paper into rolls, are on the market.

紙製のキッチンタオルロールのシート（以下、キッチンタオルシートと称する）の問題点としては、繰り返し使うことができないことであり、一度水分や汚れを拭き取ってしまうと、そこから水分を絞ったり汚れを落としたりすることは耐久性の観点から難しく、その時点で捨ててしまうことになる。
一方で、合成繊維を含む不織布からなるキッチンタオルシートは、耐久性に優れることから、汚れを水で洗い流せば繰り返し使うことができるが、吸水量が少なく、多量の水分を拭き取ることはできない。 The problem with paper kitchen towel roll sheets (hereinafter referred to as kitchen towel sheets) is that they cannot be used repeatedly, and once the water and dirt are wiped off, the water is squeezed out and dirt is removed. It is difficult to drop it from the viewpoint of durability, and it will be thrown away at that point.
On the other hand, a kitchen towel sheet made of a non-woven fabric containing synthetic fibers has excellent durability and can be used repeatedly if the dirt is washed away with water, but the amount of water absorption is small and a large amount of water cannot be wiped off.

これらの問題点に対して、合成繊維にパルプ繊維を水流交絡する技術が開発され、注目を集めている。
合成繊維にパルプ繊維を水流交絡する技術の先行技術文献としては、例えば、特許文献１にはパルプ繊維ウエブと合成繊維ウエブとを水流交絡処理して得られる不織布ワイパーであって、パルプ繊維ウエブに含まれるパルプ繊維の平均繊維長が１．０～５．０ｍｍであり、当該不織布ワイパーの坪量が２０～４２ｇ／ｍ^２であり、構成比がパルプ繊維ウエブ７０～５０質量％、合成繊維ウエブ３０～５０質量％である、ことを特徴とする不織布ワイパーが開示されている。 To solve these problems, a technique for water flow entanglement of pulp fibers with synthetic fibers has been developed and is attracting attention.
As a prior art document of the technique of water-flow entanglement of pulp fiber with synthetic fiber, for example, Patent Document 1 is a non-woven fabric wiper obtained by water-flow entanglement treatment of a pulp fiber web and a synthetic fiber web, and is used as a pulp fiber web. The average fiber length of the contained pulp fibers is 1.0 to 5.0 mm, the basis weight of the non-woven fabric wiper is 20 to 42 g / m ² , the composition ratio is 70 to 50% by mass of the pulp fiber web, and the synthetic fiber web. Disclosed are non-woven wipers characterized in that they are 30-50% by mass.

特開２０１８－１９３６３４号公報Japanese Unexamined Patent Publication No. 2018-193634

上記のような合成繊維にパルプ繊維を水流交絡して製造したキッチンタオルシートにおいて、特に吸水量を多くするには、パルプ繊維の量を増やして、坪量を大きく（高く）する必要がある。しかしながら、パルプ繊維の量を増やすと、パルプ繊維の全体を水流交絡することが難しくなり、絡まなかったパルプ繊維が紙粉になりやすい（なお、パルプ繊維１００％のキッチンタオルシートは、パルプ繊維を合成繊維と水流交絡させていないことから、紙粉はより多くなる）。そのため、吸水量が多く、かつ紙粉の少ない、合成繊維及びパルプ繊維を含むキッチンタオルシート及びキッチンタオルロールを作ることは困難であった。 In a kitchen towel sheet manufactured by entwining pulp fibers with synthetic fibers as described above, it is necessary to increase the amount of pulp fibers and increase (higher) the basis weight in order to increase the amount of water absorption. However, if the amount of pulp fiber is increased, it becomes difficult to entangle the entire pulp fiber with water flow, and the pulp fiber that is not entangled tends to become paper powder (note that the kitchen towel sheet made of 100% pulp fiber is made of pulp fiber. Since it is not entangled with synthetic fibers in a water stream, the amount of paper dust is higher). Therefore, it has been difficult to make kitchen towel sheets and kitchen towel rolls containing synthetic fibers and pulp fibers, which have a large amount of water absorption and a small amount of paper dust.

本発明は、このような事情に鑑みてなされたものであり、その目的は、再利用が可能であり、吸水量が多く、かつ紙粉の少ない、一定以上の巻長を有するキッチンタオルロールを提供することを目的とする。 The present invention has been made in view of such circumstances, and an object thereof is to provide a kitchen towel roll which is reusable, has a large amount of water absorption, has a small amount of paper dust, and has a winding length of a certain value or more. The purpose is to provide.

本発明者らは鋭意検討を行い、合成繊維及びパルプ繊維を含み、エンボス加工を施した１プライのキッチンタオルロールにおいて、キッチンタオルシートの坪量、エンボスの深さ及びロールの巻長を所定の数値範囲にすることで、再利用が可能であり、吸水量が多く、かつ紙粉の少ない、一定以上の巻長を有するキッチンタオルロールとすることができ、上記課題を解決できることを見出し、本発明を完成するに至った。
具体的には、本発明は、以下のものを提供する。 The present inventors have conducted diligent studies, and in a one-ply kitchen towel roll containing synthetic fibers and embossed fibers, the basis weight of the kitchen towel sheet, the embossing depth and the roll length are determined. By setting it in the numerical range, it is possible to make a kitchen towel roll that can be reused, has a large amount of water absorption, has a small amount of paper dust, and has a winding length of a certain level or more. The invention was completed.
Specifically, the present invention provides the following.

（１）本発明の第１の態様は、合成繊維及びパルプ繊維を含有し、１プライのエンボス加工を施されたキッチンタオルシートが、ロール状に巻き取られたキッチンタオルロールであって、上記キッチンタオルシートの坪量が５０ｇ／ｍ^２以上２００ｇ／ｍ^２以下であり、上記エンボスの深さが０．１ｍｍ以上２ｍｍ以下であり、上記ロールの巻長が５ｍ以上２４ｍ以下であることを特徴とする、キッチンタオルロールである。
（２）本発明の第２の態様は、（１）に記載のキッチンタオルロールであって、上記ロールのロール密度が０．０６ｇ／ｃｍ^３以上０．１９ｇ／ｃｍ^３以下であることを特徴とするものである。
（３）本発明の第３の態様は、（１）又は（２）に記載のキッチンタオルロールであって、上記キッチンタオルシートの１ｍ^２における吸水量が２７０ｇ以上６００ｇ以下であり、かつ、１ｇにおける吸水量が２．５ｇ以上５．７ｇ以下であることを特徴とするものである。
（４）本発明の第４の態様は、（１）から（３）のいずれかに記載のキッチンタオルロールであって、上記キッチンタオルシートの乾燥時におけるＣＤ方向の引張強度（ＤＣＤＴ）が４Ｎ／２５ｍｍ以上８０Ｎ／２５ｍｍ以下であり、上記キッチンタオルシートの乾燥時におけるＣＤ方向の引張強度（ＤＣＤＴ）に対する、乾燥時におけるＭＤ方向の引張強度（ＤＭＤＴ）の比率（ＤＭＤＴ／ＤＣＤＴ）が１．２以上４．５以下であることを特徴とするものである。
（５）本発明の第５の態様は、（１）から（４）のいずれかに記載のキッチンタオルロールであって、上記キッチンタオルシートの乾燥時におけるＭＤ方向の引張強度（ＤＭＤＴ）が１５Ｎ／２５ｍｍ以上１１５Ｎ／２５ｍｍ以下であることを特徴とするものである。
（６）本発明の第６の態様は、（１）から（５）のいずれかに記載のキッチンタオルロールであって、上記キッチンタオルシートにおける上記合成繊維の含有割合が５％以上４５％以下であり、上記パルプ繊維の含有割合が５５％以上９５％以下であることを特徴とするものである。
（７）本発明の第７の態様は、（１）から（６）のいずれかに記載のキッチンタオルロールであって、上記キッチンタオルシートの乾燥時におけるＭＤ方向の引張強度（ＤＭＤＴ）に対する、湿潤時におけるＭＤ方向の引張強度（ＷＭＤＴ）の比率（（ＷＭＤＴ／ＤＭＤＴ）×１００（％））が５０％以上９５％以下であることを特徴とするものである。
（８）本発明の第８の態様は、（１）から（７）のいずれかに記載のキッチンタオルロールであって、上記キッチンタオルシートの乾燥時におけるＣＤ方向の引張強度（ＤＣＤＴ）に対する、湿潤時におけるＣＤ方向の引張強度（ＷＣＤＴ）の比率（（ＷＣＤＴ／ＤＣＤＴ）×１００（％））が４３％以上８９％以下であることを特徴とするものである。
（９）本発明の第９の態様は、（１）から（８）のいずれかに記載のキッチンタオルロールであって、上記キッチンタオルシートの紙厚が０．４５ｍｍ以上１．８ｍｍ以下であることを特徴とするものである。
（１０）本発明の第１０の態様は、（１）から（９）のいずれかに記載のキッチンタオルロールであって、上記キッチンタオルシートのＣＤ方向における破断伸びが５０％以上１００％以下であることを特徴とするものである。
（１１）本発明の第１１の態様は、（１）から（１０）のいずれかに記載のキッチンタオルロールであって、上記キッチンタオルシートのＭＤ方向における破断伸びが２０％以上６５％以下であることを特徴とするものである。
（１２）本発明の第１２の態様は、（１）から（１１）のいずれかに記載のキッチンタオルロールであって、上記合成繊維の坪量が８ｇ／ｍ^２以上５５ｇ／ｍ^２以下であり、上記パルプ繊維の坪量が３８ｇ／ｍ^２以上１６０ｇ／ｍ^２以下であることを特徴とするものである。 (1) The first aspect of the present invention is a kitchen towel roll containing synthetic fibers and pulp fibers and having a 1-ply embossed kitchen towel sheet wound into a roll. The feature is that the basis weight of the kitchen towel sheet is 50 g / m ² or more and 200 g / m ² or less, the embossing depth is 0.1 mm or more and 2 mm or less, and the winding length of the roll is 5 m or more and 24 m or less. It is a kitchen towel roll.
(2) The second aspect of the present invention is the kitchen towel roll according to (1), wherein the roll density of the roll is 0.06 g / cm ³ or more and 0.19 g / cm ³ or less. Is to be.
(3) The third aspect of the present invention is the kitchen towel roll according to (1) or (2), wherein the water absorption amount in 1 m ² of the kitchen towel sheet is 270 g or more and 600 g or less, and 1 g. The water absorption amount in the above is 2.5 g or more and 5.7 g or less.
(4) The fourth aspect of the present invention is the kitchen towel roll according to any one of (1) to (3), wherein the tensile strength (DCDT) in the CD direction at the time of drying the kitchen towel sheet is 4N. It is / 25 mm or more and 80 N / 25 mm or less, and the ratio (DMDT / DCDT) of the tensile strength (DMDT) in the MD direction to the tensile strength (DCDT) in the CD direction during drying of the kitchen towel sheet is 1.2. It is characterized in that it is 4.5 or less.
(5) The fifth aspect of the present invention is the kitchen towel roll according to any one of (1) to (4), and the tensile strength (DMDT) in the MD direction at the time of drying the kitchen towel sheet is 15N. It is characterized by being / 25 mm or more and 115 N / 25 mm or less.
(6) The sixth aspect of the present invention is the kitchen towel roll according to any one of (1) to (5), wherein the content ratio of the synthetic fiber in the kitchen towel sheet is 5% or more and 45% or less. The pulp fiber content is 55% or more and 95% or less.
(7) The seventh aspect of the present invention is the kitchen towel roll according to any one of (1) to (6), wherein the kitchen towel sheet has a tensile strength (DMDT) in the MD direction at the time of drying. It is characterized in that the ratio ((WMDT / DMDT) × 100 (%)) of the tensile strength (WMDT) in the MD direction at the time of wetting is 50% or more and 95% or less.
(8) An eighth aspect of the present invention is the kitchen towel roll according to any one of (1) to (7), wherein the kitchen towel sheet has a tensile strength (DCDT) in the CD direction when it is dried. It is characterized in that the ratio ((WCDT / DCDT) × 100 (%)) of the tensile strength (WCDT) in the CD direction at the time of wetting is 43% or more and 89% or less.
(9) The ninth aspect of the present invention is the kitchen towel roll according to any one of (1) to (8), wherein the paper thickness of the kitchen towel sheet is 0.45 mm or more and 1.8 mm or less. It is characterized by that.
(10) The tenth aspect of the present invention is the kitchen towel roll according to any one of (1) to (9), wherein the breaking elongation of the kitchen towel sheet in the CD direction is 50% or more and 100% or less. It is characterized by being.
(11) The eleventh aspect of the present invention is the kitchen towel roll according to any one of (1) to (10), wherein the breaking elongation of the kitchen towel sheet in the MD direction is 20% or more and 65% or less. It is characterized by being.
(12) The twelfth aspect of the present invention is the kitchen towel roll according to any one of (1) to (11), wherein the synthetic fiber has a basis weight of 8 g / m ² or more and 55 g / m ² or less. It is characterized in that the basis weight of the pulp fiber is 38 g / m ² or more and 160 g / m ² or less.

本発明によれば、再利用が可能であり、吸水量が多く、かつ紙粉の少ない、一定以上の巻長を有するキッチンタオルロールを提供することができる。 According to the present invention, it is possible to provide a kitchen towel roll that can be reused, has a large amount of water absorption, has a small amount of paper dust, and has a roll length of a certain value or more.

本発明のキッチンタオルロールの全体を示す斜視図である。It is a perspective view which shows the whole of the kitchen towel roll of this invention. マイクロスコープによるＸ－Ｙ平面上の高さプロファイルを濃淡で示す図である。It is a figure which shows the height profile on the XY plane by a microscope by shading. マイクロスコープによるＸ－Ｙ平面上の高さプロファイルをグラフで示す図であるIt is a figure which shows the height profile on the XY plane by a microscope in a graph. 本発明のキッチンタオルロールのエンボスについて、エンボスの深さの求め方を示す図である。It is a figure which shows the method of obtaining the embossing depth about the embossing of the kitchen towel roll of this invention. 本発明のキッチンタオルロールの吸水量の測定方法を示す図である。It is a figure which shows the measuring method of the water absorption amount of the kitchen towel roll of this invention.

以下、本発明を実施するための形態（以下、実施形態）について、図面を参照しながら詳細に説明するが、これらは例示の目的で掲げたもので、これらにより本発明を限定するものではない。 Hereinafter, embodiments for carrying out the present invention (hereinafter referred to as embodiments) will be described in detail with reference to the drawings, but these are listed for the purpose of illustration and do not limit the present invention. ..

１．キッチンタオルロール
図１は、本発明のキッチンタオルロール１の外観を示す斜視図である。本発明のキッチンタオルロール１は、合成繊維及びパルプ繊維を含有し、１プライのエンボス加工を施されたキッチンタオルシート１ｘが、ロール状に巻き取られたキッチンタオルロール１である。なお、キッチンタオルシート１ｘは、流れ方向における等間隔において、幅方向にミシン目を施されていることが好ましい（図示しない）。
なお、本願発明におけるシート１ｘは、キッチンタオル以外にも様々なロール製品として用いることができ、ワイパー、ハンドタオル又はキッチンタオルの用途で使用することが好ましく、キッチンタオルの用途で使用することが最も好ましい。 1. 1. Kitchen Towel Roll FIG. 1 is a perspective view showing the appearance of the kitchen towel roll 1 of the present invention. The kitchen towel roll 1 of the present invention is a kitchen towel roll 1 in which a 1-ply embossed kitchen towel sheet 1x containing synthetic fibers and pulp fibers is wound into a roll. The kitchen towel sheet 1x is preferably perforated in the width direction at equal intervals in the flow direction (not shown).
The sheet 1x in the present invention can be used as various roll products other than kitchen towels, and is preferably used for wipers, hand towels or kitchen towels, and most preferably for kitchen towels. preferable.

また、図１に示すように、キッチンタオルシート１ｘの表面のうち、ロール外側に指向した表面を表面１ａ（キッチンタオルシート１ｘの表面）と称し、ロール中心部に指向した表面を裏面１ｂ（キッチンタオルシート１ｘの裏面）と称する。なお、後述する水流交絡によって、キッチンタオルシート１ｘに含まれる合成繊維の量においては、キッチンタオルシート１ｘの表面側（すなわち表面１ａ側）が多く、裏面１ｂ側が少ないことが好ましい。 Further, as shown in FIG. 1, among the surfaces of the kitchen towel sheet 1x, the surface facing the outside of the roll is referred to as the surface 1a (the surface of the kitchen towel sheet 1x), and the surface facing the center of the roll is referred to as the back surface 1b (kitchen). The back surface of the towel sheet 1x). It is preferable that the amount of synthetic fibers contained in the kitchen towel sheet 1x is large on the front surface side (that is, the front surface 1a side) and small on the back surface 1b side due to the water flow confounding described later.

（巻長及び巻直径）
キッチンタオルロール１の巻長は５ｍ以上２４ｍ以下であり、７ｍ以上２０ｍであることが好ましく、８ｍ以上１６ｍ以下であることがより好ましい。巻長が５ｍ未満であると、通常のキッチンタオルロールに求められる巻長以上にならず、巻長が２４ｍを超えると代わりに坪量を低くする必要があり、吸水量に劣る。
また、キッチンタオルロール１の巻直径ＤＲは１０５ｍｍ以上１５５ｍｍ以下であることが好ましく、１１０ｍｍ以上１４０ｍｍ以下であることがより好ましく、１１５ｍｍ以上１３０ｍｍ以下であることが更に好ましい。巻直径ＤＲが１０５ｍｍ未満であると通常のキッチンタオルロールに求められる巻長以上にならず、巻直径ＤＲが１５５ｍｍを超えるとロール状にした時に大きすぎて使用しにくくなり、また坪量が高くなることで結果として紙粉が多くなる。 (Volume length and winding diameter)
The roll length of the kitchen towel roll 1 is 5 m or more and 24 m or less, preferably 7 m or more and 20 m, and more preferably 8 m or more and 16 m or less. If the winding length is less than 5 m, it does not exceed the winding length required for a normal kitchen towel roll, and if the winding length exceeds 24 m, it is necessary to lower the basis weight instead, and the water absorption is inferior.
Further, the winding diameter DR of the kitchen towel roll 1 is preferably 105 mm or more and 155 mm or less, more preferably 110 mm or more and 140 mm or less, and further preferably 115 mm or more and 130 mm or less. If the winding diameter DR is less than 105 mm, it will not exceed the winding length required for a normal kitchen towel roll, and if the winding diameter DR exceeds 155 mm, it will be too large to be used when rolled, and the basis weight will be high. As a result, the amount of paper dust increases.

巻長は、キッチンタオルロール１のミシン目とミシン目の間のキッチンタオルシート１ｘについて、１０シート分の長さを実測する。その後、キッチンタオルロール１のシート数を実測し、巻長は１０シート分の長さとシート数から比例計算で求める。例えば、１０シート分の長さが１．８０ｍ、シート数が１５０シートの場合、１．８０ｍ×（１５０／１０）＝２７ｍとなる。なお、キッチンタオルロール１にミシン目がない場合は、実測して巻長を測定することができる。また、ロールの巻直径ＤＲは、ムラテックＫＤＳ株式会社製ダイヤメータールールを用いて測定する。測定は、１０個のキッチンタオルロール１を測定し、測定結果を平均する。
また、ミシン目とミシン目の間の長さ（流れ方向のシートの長さ）は、１１０ｍｍ以上３６０ｍｍ以下が好ましく、１６０ｍｍ以上３１０ｍｍ以下がより好ましく、２１０ｍｍ以上２６０ｍｍ以下が更に好ましい。この範囲にすることで、本願のような吸水量が多いキッチンタオルロール１を使用する際、使用する面積が適正になり、多くの水を吸収することができる。 As the winding length, the length of 10 sheets is actually measured for the kitchen towel sheet 1x between the perforations of the kitchen towel roll 1. After that, the number of sheets of the kitchen towel roll 1 is actually measured, and the winding length is calculated proportionally from the length of 10 sheets and the number of sheets. For example, when the length of 10 sheets is 1.80 m and the number of sheets is 150, 1.80 m × (150/10) = 27 m. If the kitchen towel roll 1 has no perforations, the winding length can be measured by actual measurement. Further, the winding diameter DR of the roll is measured by using a dialimeter rule manufactured by Muratec KDS Co., Ltd. For the measurement, 10 kitchen towel rolls 1 are measured and the measurement results are averaged.
The length between the perforations (the length of the sheet in the flow direction) is preferably 110 mm or more and 360 mm or less, more preferably 160 mm or more and 310 mm or less, and further preferably 210 mm or more and 260 mm or less. By setting this range, when using the kitchen towel roll 1 having a large amount of water absorption as in the present application, the area to be used becomes appropriate and a large amount of water can be absorbed.

（ロール幅及びロール重量）
キッチンタオルロール１のロール幅は１５０ｍｍ以上３８０ｍｍ以下であることが好ましく、２００ｍｍ以上３５０ｍｍ以下であることがより好ましく、２５０ｍｍ以上３００ｍｍ以下であることが更に好ましい。この範囲にすることで、本願のような吸水量が多いキッチンタオルロール１を使用する際、使用する面積が適正になり、多くの水を吸収することができる。
また、キッチンタオルロール１のロール重量は１７０ｇ以上４６０ｇ以下であることが好ましく、２５０ｇ以上４１０ｇ以下であることがより好ましく、２８０ｇ以上３６０ｇ以下であることが更に好ましい。ロール重量が１７０ｇ未満であると、通常のキッチンタオルロールに求められる巻長以上にならず、ロール重量が４６０ｇを超えるとキッチンタオルシート１ｘの坪量が高くなり、紙粉が多くなる。
なお、ロール質量は、コア（紙管）を含まないロール幅２７５ｍｍあたりの１ロールの質量とする。ロール幅が２７５ｍｍでない場合は、比例計算により２７５ｍｍあたりの質量に換算する。 (Roll width and roll weight)
The roll width of the kitchen towel roll 1 is preferably 150 mm or more and 380 mm or less, more preferably 200 mm or more and 350 mm or less, and further preferably 250 mm or more and 300 mm or less. By setting this range, when using the kitchen towel roll 1 having a large amount of water absorption as in the present application, the area to be used becomes appropriate and a large amount of water can be absorbed.
The roll weight of the kitchen towel roll 1 is preferably 170 g or more and 460 g or less, more preferably 250 g or more and 410 g or less, and further preferably 280 g or more and 360 g or less. If the roll weight is less than 170 g, the roll length is not longer than that required for a normal kitchen towel roll, and if the roll weight exceeds 460 g, the basis weight of the kitchen towel sheet 1x becomes high and the amount of paper dust increases.
The roll mass is the mass of one roll per roll width of 275 mm excluding the core (paper tube). If the roll width is not 275 mm, it is converted to the mass per 275 mm by proportional calculation.

（コア外径）
また、本発明のキッチンタオルロール１の芯の外径である、コア外径ＤＩは、３０ｍｍ以上６０ｍｍ以下であることが好ましく、３４ｍｍ以上５５ｍｍ以下であることがより好ましく、３７ｍｍ以上５０ｍｍ以下であることが更に好ましい。コア外径ＤＩが３０ｍｍ未満であるとロール状にした時に、コアが小さすぎて使用しにくくなり、コア外径ＤＩが６０ｍｍを超えるとロール状にした時に、コアが大きすぎて使用しにくくなる。
コア外径ＤＩは、ムラテックＫＤＳ株式会社製ダイヤメータールールを用いて測定する。測定は、１０個のキッチンタオルロール１を測定し、測定結果を平均する。 (Core outer diameter)
Further, the core outer diameter DI, which is the outer diameter of the core of the kitchen towel roll 1 of the present invention, is preferably 30 mm or more and 60 mm or less, more preferably 34 mm or more and 55 mm or less, and 37 mm or more and 50 mm or less. Is even more preferable. If the core outer diameter DI is less than 30 mm, the core is too small to be used when rolled, and if the core outer diameter DI is more than 60 mm, the core is too large to be used when rolled. ..
The core outer diameter DI is measured using a dialometer rule manufactured by Muratec KDS Co., Ltd. For the measurement, 10 kitchen towel rolls 1 are measured and the measurement results are averaged.

（ロール密度）
キッチンタオルロール１のロール密度は０．０６ｇ／ｃｍ^３以上０．１９ｇ／ｃｍ^３以下であることが好ましく、０．０９ｇ／ｃｍ^３以上０．１７ｇ／ｃｍ^３以下であることがより好ましく、０．１１ｇ／ｃｍ^３以上０．１５ｇ／ｃｍ^３以下であることが更に好ましい。キッチンタオルロール１のロール密度が０．０６ｇ／ｃｍ^３未満であると、エンボスの深さを確保するために柔らかく巻くことによって、結果的に巻長が短くなり、キッチンタオルロール１のロール密度が０．１９ｇ／ｃｍ^３を超えると、エンボスの深さが浅くなり、紙粉が増える。 (Roll density)
The roll density of the kitchen towel roll 1 is preferably 0.06 g / cm ³ or more and 0.19 g / cm ³ or less, more preferably 0.09 g / cm ³ or more and 0.17 g / cm ³ or less, and 0. It is more preferably .11 g / cm ³ or more and 0.15 g / cm ³ or less. When the roll density of the kitchen towel roll 1 is less than 0.06 g / cm ³ , the roll density of the kitchen towel roll 1 becomes shorter as a result of softly winding to secure the embossing depth. If it exceeds 0.19 g / cm ³ , the embossing depth becomes shallow and paper dust increases.

ロール密度は、（ロール質量）÷（ロールの体積）で表される。ロール質量は、ロール幅２７５ｍｍあたりのキッチンタオルロール１の質量である。ロール体積は［｛ロールの外径（巻直径ＤＲ）部分の断面積｝－（コア外径部分の断面積）］×ロール幅（２７５ｍｍあたりに換算する）で表される。例えば、ロール幅２７５ｍｍあたりのロール質量（コアを除く）が３３７ｇ、巻直径１１９ｍｍ、コアの外径が４９ｍｍの場合、ロール密度＝０．１３ｇ／ｃｍ^３となる。なお、キッチンタオルロール１にコアが無い場合は、中心孔の直径をコア外径ＤＩとする。 The roll density is expressed by (roll mass) ÷ (roll volume). The roll mass is the mass of the kitchen towel roll 1 per roll width of 275 mm. The roll volume is represented by [{cross-sectional area of roll outer diameter (roll diameter DR) portion}-(cross-sectional area of core outer diameter portion)] × roll width (converted to around 275 mm). For example, when the roll mass (excluding the core) per roll width of 275 mm is 337 g, the winding diameter is 119 mm, and the outer diameter of the core is 49 mm, the roll density is 0.13 g / cm ³ . If the kitchen towel roll 1 does not have a core, the diameter of the center hole is defined as the core outer diameter DI.

２．キッチンタオルシート
本発明のキッチンタオルシート１ｘは、上述したように合成繊維及びパルプ繊維を含有する。合成繊維としては、例えばナイロン、ビニロン、ポリエステル、アクリル、ポリエチレン、ポリプロピレン、ポリスチレン等が挙げられるが、本願発明のような、高坪量で所定のエンボスを設けるキッチンタオルシート１ｘを得るには、ポリエチレン、ポリプロピレンが好ましく、ポリプロピレンがより好ましい。また、パルプ繊維としては、針葉樹晒クラフトパルプ（ＮＢＫＰ）、広葉樹晒クラフトパルプ（ＬＢＫＰ）等、一般的なパルプ繊維を用いることができる。パルプ繊維におけるＮＢＫＰとＬＢＫＰの含有割合は、ＮＢＫＰ：ＬＢＫＰ＝５０：５０～１００：０が好ましく、ＮＢＫＰ：ＬＢＫＰ＝７０：３０～１００：０がより好ましく、ＮＢＫＰ：ＬＢＫＰ＝９０：１０～１００：０が更に好ましく、ＮＢＫＰ：ＬＢＫＰ＝１００：０が最も好ましい。ＮＢＫＰとしては、例えばラジアータパイン、スラッシュパイン、サザンパイン、ロッジポールパイン、スプルース及びダグラスファーからなる繊維が好ましい。なお、ＮＢＫＰの代わりにＮＵＫＰ、ＬＢＫＰの代わりにＬＵＫＰを用いることもできる。
このとき、キッチンタオルシート１ｘにおける合成繊維の含有割合が５％以上４５％以下であることが好ましく、９％以上３８％以下であることがより好ましく、１２％以上２８％以下であることが更に好ましい。合成繊維の含有割合が５％未満であると、パルプ繊維を後述する水流交絡させることが難しく、結果としてキッチンタオルシート１ｘの紙粉が多くなり、合成繊維の含有割合が４５％を超えると、キッチンタオルシート１ｘの吸水量に劣る。
また、キッチンタオルシート１ｘにおけるパルプ繊維の含有割合が５５％以上９５％以下であることが好ましく、６２％以上９１％以下であることがより好ましく、７２％以上８８％以下であることが更に好ましい。パルプ繊維の含有割合が５５％未満であると、キッチンタオルシート１ｘの吸水量に劣り、パルプ繊維の含有割合が９５％を超えると、キッチンタオルシート１ｘの紙粉が多くなる。 2. 2. Kitchen towel sheet The kitchen towel sheet 1x of the present invention contains synthetic fibers and pulp fibers as described above. Examples of the synthetic fiber include nylon, vinylon, polyester, acrylic, polyethylene, polypropylene, polystyrene and the like. Polyethylene is used to obtain a kitchen towel sheet 1x having a high basis weight and a predetermined embossing as in the present invention. , Polypropylene is preferred, and polypropylene is more preferred. Further, as the pulp fiber, general pulp fiber such as softwood bleached kraft pulp (NBKP) and broadleaf tree bleached kraft pulp (LBKP) can be used. The content ratio of NBKP and LBKP in the pulp fiber is preferably NBKP: LBKP = 50: 50 to 100: 0, more preferably NBKP: LBKP = 70: 30 to 100: 0, and NBKP: LBKP = 90: 10 to 100: 0. 0 is more preferable, and NBKP: LBKP = 100: 0 is most preferable. As the NBKP, for example, fibers composed of radiata pine, slash pine, southern pine, lodgepole pine, spruce and Douglas-firs are preferable. It is also possible to use NUKP instead of NBKP and LUKP instead of LBKP.
At this time, the content ratio of the synthetic fiber in the kitchen towel sheet 1x is preferably 5% or more and 45% or less, more preferably 9% or more and 38% or less, and further preferably 12% or more and 28% or less. preferable. When the content ratio of the synthetic fiber is less than 5%, it is difficult to entangle the pulp fiber with the water flow described later, and as a result, the amount of paper dust in the kitchen towel sheet 1x increases, and when the content ratio of the synthetic fiber exceeds 45%, Inferior in water absorption of kitchen towel sheet 1x.
Further, the content ratio of the pulp fiber in the kitchen towel sheet 1x is preferably 55% or more and 95% or less, more preferably 62% or more and 91% or less, and further preferably 72% or more and 88% or less. .. When the content ratio of the pulp fiber is less than 55%, the water absorption of the kitchen towel sheet 1x is inferior, and when the content ratio of the pulp fiber exceeds 95%, the amount of paper dust in the kitchen towel sheet 1x increases.

さらに、キッチンタオルシート１ｘには、一般的な湿潤紙力剤を含有することが好ましい。湿潤紙力剤（固形分（有効成分）換算）の含有率は、パルプ繊維（絶乾）に対して、０．０５％以上１．０％以下が好ましく、０．１０％以上０．５０％以下がより好ましく、０．２０％以上０．４０％以下が更に好ましい。湿潤紙力剤の含有率を上記にすることで、本願のような、高坪量で所定のエンボスを設けるキッチンタオルロール１を得ることができる。
また、必要に応じて、本発明の目的を損なわない範囲で、キッチンタオルシート１ｘに耐熱安定剤、滑剤等を配合することができる。耐熱安定剤としては、例えば、ＢＨＴ（２，６－ジ－ｔ－ブチル－４－メチルフェノール）等のフェノール系安定剤等があげられる。 Further, it is preferable that the kitchen towel sheet 1x contains a general wet paper toweling agent. The content of the wet paper strength agent (in terms of solid content (active ingredient)) is preferably 0.05% or more and 1.0% or less, and 0.10% or more and 0.50% with respect to the pulp fiber (absolutely dry). The following is more preferable, and 0.20% or more and 0.40% or less is further preferable. By setting the content of the wetting paper strength agent to the above, it is possible to obtain a kitchen towel roll 1 having a high basis weight and a predetermined embossing as in the present application.
Further, if necessary, a heat-resistant stabilizer, a lubricant, or the like can be added to the kitchen towel sheet 1x as long as the object of the present invention is not impaired. Examples of the heat-resistant stabilizer include phenolic stabilizers such as BHT (2,6-di-t-butyl-4-methylphenol).

（坪量）
キッチンタオルシート１ｘの坪量は、５０ｇ／ｍ^２以上２００ｇ／ｍ^２以下であり、６０ｇ／ｍ^２以上１７０ｇ／ｍ^２以下であることが好ましく、１００ｇ／ｍ^２以上１４０ｇ／ｍ^２以下であることがより好ましい。キッチンタオルシート１ｘの坪量が５０ｇ／ｍ^２未満であると、キッチンタオルシート１ｘの吸水量に劣り、キッチンタオルシート１ｘの坪量が２００ｇ／ｍ^２を超えると、キッチンタオルシート１ｘの紙粉が多くなる。 (Basis weight)
The basis weight of the kitchen towel sheet 1x is 50 g / m ² or more and 200 g / m ² or less, preferably 60 g / m ² or more and 170 g / m ² or less, and 100 g / m ² or more and 140 g / m ² or less. Is more preferable. If the basis weight of the kitchen towel sheet 1x is less than 50 g / m ² , the water absorption of the kitchen towel sheet 1x is inferior, and if the basis weight of the kitchen towel sheet 1x exceeds 200 g / m ² , the paper dust of the kitchen towel sheet 1x Will increase.

また、キッチンタオルシート１ｘに含まれる合成繊維の坪量は、８ｇ／ｍ^２以上５５ｇ／ｍ^２以下であることが好ましく、１２ｇ／ｍ^２以上４５ｇ／ｍ^２以下であることがより好ましく、１５ｇ／ｍ^２以上３８ｇ／ｍ^２以下であることが更に好ましい。合成繊維の坪量が８ｇ／ｍ^２未満であると、パルプ繊維を後述する水流交絡させることが難しく、結果としてキッチンタオルシート１ｘの紙粉が多くなり、合成繊維の坪量が５５ｇ／ｍ^２を超えると、キッチンタオルシート１ｘの吸水量に劣る。
さらに、キッチンタオルシート１ｘに含まれるパルプ繊維の坪量は、３８ｇ／ｍ^２以上１６０ｇ／ｍ^２以下であることが好ましく、４５ｇ／ｍ^２以上１４０ｇ／ｍ^２以下であることがより好ましく、６０ｇ／ｍ^２以上１２０ｇ／ｍ^２以下であることが更に好ましい。パルプ繊維の坪量が３８ｇ／ｍ^２未満であると、キッチンタオルシート１ｘの吸水量に劣り、パルプ繊維の坪量が１６０ｇ／ｍ^２を超えると、キッチンタオルシート１ｘの紙粉が多くなる。
なお、キッチンタオルシート１ｘの坪量はＪＩＳＰ８１２４に基づいて測定するが、合成繊維及びパルプ繊維の坪量は、後述する水流交絡した後に個別に測定することが困難であるため、例えば、以下の方法で測定する。 The basis weight of the synthetic fiber contained in the kitchen towel sheet 1x is preferably 8 g / m ² or more and 55 g / m ² or less, more preferably 12 g / m ² or more and 45 g / m ² or less, and 15 g. It is more preferably / m ² or more and 38 g / m ² or less. If the basis weight of the synthetic fiber is less than 8 g / m ² , it is difficult to entangle the pulp fiber with the water flow described later, and as a result, the amount of paper dust in the kitchen towel sheet 1x increases, and the basis weight of the synthetic fiber is 55 g / m ² . If it exceeds, the water absorption of the kitchen towel sheet 1x is inferior.
Further, the basis weight of the pulp fiber contained in the kitchen towel sheet 1x is preferably 38 g / m ² or more and 160 g / m ² or less, more preferably 45 g / m ² or more and 140 g / m ² or less, and 60 g. It is more preferably / m ² or more and 120 g / m ² or less. When the basis weight of the pulp fiber is less than 38 g / m ² , the water absorption of the kitchen towel sheet 1x is inferior, and when the basis weight of the pulp fiber exceeds 160 g / m ² , the amount of paper dust in the kitchen towel sheet 1x increases.
The basis weight of the kitchen towel sheet 1x is measured based on JIS P 8124, but the basis weight of synthetic fibers and pulp fibers is difficult to measure individually after water flow entanglement, which will be described later. Therefore, for example, the following Measure by the method of.

まず、０．１Ｍ酢酸水溶液と０．１Ｍ酢酸ナトリウム水溶液を調製する。約８３０ｇの０．１Ｍ酢酸水溶液と約１６０ｇの０．１Ｍ酢酸ナトリウム水溶液を混合してｐＨが４となるようにし、これを酢酸緩衝液とする。この酢酸緩衝液にセルラーゼオノズカｐ１５００（ヤクルト薬品工業株式会社製）を添加量が１重量％となるように添加する。
セルラーゼオノズカｐ１５００を添加した酢酸緩衝液５０ｍｌと、キッチンタオルシート１ｘを０．５ｇとをバイアル瓶に入れて、しっかりと蓋をする。次に、１８０ｒｐｍ、４０℃の条件で２４時間振とうした後、バイアル瓶から合成繊維を採取し、合成繊維の質量を測定する。（合成繊維及びパルプ繊維を含む）キッチンタオルシート１ｘの質量（０．５ｇ）と採取した合成繊維の質量から、下記式により、合成繊維及びパルプ繊維のそれぞれの坪量を算出する。
合成繊維の坪量＝
キッチンタオルシート１ｘの坪量×（合成繊維の質量／キッチンタオルシート１ｘの質量）
パルプ繊維の坪量＝
キッチンタオルシート１ｘの坪量×［（キッチンタオルシート１ｘの質量－合成繊維の質量）／キッチンタオルシート１ｘの質量］ First, a 0.1 M aqueous acetic acid solution and a 0.1 M aqueous sodium acetate solution are prepared. About 830 g of a 0.1 M acetic acid aqueous solution and about 160 g of a 0.1 M sodium acetate aqueous solution are mixed so that the pH becomes 4, and this is used as an acetate buffer. Cellulase Onozuka p1500 (manufactured by Yakult Pharmaceutical Co., Ltd.) is added to this acetate buffer so that the addition amount is 1% by weight.
Place 50 ml of acetate buffer containing cellulase Onozuka p1500 and 0.5 g of kitchen towel sheet 1x in a vial and cover tightly. Next, after shaking at 180 rpm and 40 ° C. for 24 hours, the synthetic fiber is collected from the vial and the mass of the synthetic fiber is measured. From the mass (0.5 g) of the kitchen towel sheet (including synthetic fiber and pulp fiber) and the mass of the collected synthetic fiber, the basis weight of each of the synthetic fiber and the pulp fiber is calculated by the following formula.
Basis weight of synthetic fiber =
Kitchen towel sheet 1x basis weight x (mass of synthetic fiber / mass of kitchen towel sheet 1x)
Basis weight of pulp fiber =
Kitchen towel sheet 1x basis weight x [(mass of kitchen towel sheet 1x-mass of synthetic fiber) / mass of kitchen towel sheet 1x]

また、上記の方法で測定が困難な場合は、ＪＩＳＰ８１２４に基づいて測定したキッチンタオルシート１ｘの坪量－用いた合成繊維の坪量＝パルプ繊維の坪量として求めるが、水流交絡後の原反（原紙）とエンボスを設けたキッチンタオルシート１ｘの坪量は異なる（エンボス後は、坪量が低くなる）ので、下記のように補正することで、最終的な合成繊維及びパルプ繊維のそれぞれの坪量とする。
例えば、合成繊維の坪量が２６ｇ／ｍ^２であり、水流交絡後の原紙の坪量が１２８ｇ／ｍ^２、エンボス加工後のキッチンタオルシート１ｘの坪量が１２５ｇ／ｍ^２である場合は、合成繊維の坪量は２６×１２５／１２８＝２５ｇ／ｍ^２、パルプ繊維の坪量は１２５－２５＝１００ｇ／ｍ^２とする。 If it is difficult to measure by the above method, it is calculated as the basis weight of the kitchen towel sheet 1x measured based on JIS P 8124-the basis weight of the synthetic fiber used = the basis weight of the pulp fiber, but after water flow entanglement. Since the basis weight of the kitchen towel sheet 1x with the original fabric (base paper) and the embossed is different (the basis weight becomes lower after embossing), the final synthetic fiber and pulp fiber can be adjusted as follows. Each basis weight.
For example, when the basis weight of the synthetic fiber is 26 g / m ² , the basis weight of the base paper after water flow entanglement is 128 g / m ² , and the basis weight of the kitchen towel sheet 1x after embossing is 125 g / m ² . The basis weight of the synthetic fiber is 26 × 125/128 = 25 g / m ² , and the basis weight of the pulp fiber is 125-25 = 100 g / m ² .

（紙厚及び比容積）
キッチンタオルシート１ｘの紙厚は０．４５ｍｍ以上１．８ｍｍ以下であることが好ましく、０．５５ｍｍ以上１．４５ｍｍ枚以下であることがより好ましく、０．７５ｍｍ以上１．２ｍｍ以下であることが更に好ましい。紙厚が０．４５ｍｍ未満であると、キッチンタオルシート１ｘの吸水量に劣り、１．８ｍｍ枚を超えると、キッチンタオルシート１ｘの紙粉が多くなる。紙厚はシックネスゲージ（株式会社尾崎製作所製のダイヤルシックネスゲージ「ＰＥＡＣＯＣＫ」）を用いて測定する。測定条件は、測定荷重３．７ｋＰａ、測定子直径３０ｍｍで、測定子と測定台の間に試料を置き、測定子を１秒間に１ｍｍ以下の速度で下ろしたときのゲージを読み取る。また、測定を１０回繰り返して測定結果を平均する。なお、測定は３枚のキッチンタオルシート１ｘを重ねて測定し、値を１／３にして、紙厚の値とする。
また、キッチンタオルシート１ｘの比容積は５ｃｍ^３／ｇ以上１５ｃｍ^３／ｇ以下であることが好ましく、６ｃｍ^３／ｇ以上１３ｃｍ^３／ｇ以下であることがより好ましく、７ｃｍ^３／ｇ以上１１ｃｍ^３／ｇ以下であることが更に好ましい。比容積が５ｃｍ^３／ｇ未満であると、キッチンタオルシート１ｘの吸水量に劣り、１５ｃｍ^３／ｇを超えると、キッチンタオルシート１ｘの紙粉が多くなる。比容積は、キッチンタオルシート１ｘの紙厚を坪量で割り、単位ｇあたりの容積ｃｍ^３で表す。 (Paper thickness and specific volume)
The paper thickness of the kitchen towel sheet 1x is preferably 0.45 mm or more and 1.8 mm or less, more preferably 0.55 mm or more and 1.45 mm or less, and more preferably 0.75 mm or more and 1.2 mm or less. More preferred. If the paper thickness is less than 0.45 mm, the water absorption of the kitchen towel sheet 1x is inferior, and if it exceeds 1.8 mm, the amount of paper dust in the kitchen towel sheet 1x increases. The paper thickness is measured using a thickness gauge (dial thickness gauge "PEACOCK" manufactured by Ozaki Seisakusho Co., Ltd.). The measurement conditions are a measuring load of 3.7 kPa, a stylus diameter of 30 mm, a sample is placed between the stylus and the measuring table, and the gauge when the stylus is lowered at a speed of 1 mm or less per second is read. In addition, the measurement is repeated 10 times and the measurement results are averaged. In the measurement, three kitchen towel sheets 1x are stacked and measured, and the value is reduced to 1/3 to obtain the value of the paper thickness.
The specific volume of the kitchen towel sheet 1x is preferably 5 cm ³ / g or more and 15 cm ³ / g or less, more preferably 6 cm ³ / g or more and 13 cm ³ / g or less, and 7 cm ³ / g or more and 11 cm ³ It is more preferably / g or less. If the specific volume is less than 5 cm ³ / g, the water absorption of the kitchen towel sheet 1x is inferior, and if it exceeds 15 cm ³ / g, the amount of paper dust in the kitchen towel sheet 1x increases. The specific volume is expressed by dividing the paper thickness of the kitchen towel sheet 1x by the basis weight and the volume cm ³ per unit g.

（エンボス）
本発明のキッチンタオルロール１（キッチンタオルシート１ｘ）は、エンボス加工が施されてなるものであり、ロールワインダにて施されることが好ましい。なお、エンボス単体の形状は、円形、楕円形、長方形、正方形、花柄、多角形、文字、線、ロゴ等、特に制限なく用いることができ、本願発明のような高坪量で所定のエンボスを設けるキッチンタオルシート１ｘを得るには、六角形状が好ましい。
また、エンボスの深さは０．１ｍｍ以上２ｍｍ以下であり、０．３ｍｍ以上１．５ｍｍ以下であることが好ましく、０．５ｍｍ以上１．０ｍｍ以下であることがより好ましい。エンボスの深さが０．１ｍｍ未満であると、エンボスの凹凸が小さくなることで、紙粉をエンボス部（凹部）でかき取ることができなくなったり、エンボスが浅い分、シートで物を拭いた時に接触面積が増えたりすることで、結果として紙粉が多くなる。深さが２ｍｍを超えると、エンボスの深さを確保するためにロールを柔らかく巻くことになり、結果としてキッチンタオルロール１の巻長が短くなる。 (Embossed)
The kitchen towel roll 1 (kitchen towel sheet 1x) of the present invention is embossed and is preferably applied with a roll winder. The shape of the embossing alone can be a circle, an ellipse, a rectangle, a square, a floral pattern, a polygon, a character, a line, a logo, etc. without particular limitation, and a predetermined embossing with a high basis weight as in the present invention can be used. In order to obtain the kitchen towel sheet 1x provided with the above, a hexagonal shape is preferable.
The embossing depth is 0.1 mm or more and 2 mm or less, preferably 0.3 mm or more and 1.5 mm or less, and more preferably 0.5 mm or more and 1.0 mm or less. If the embossing depth is less than 0.1 mm, the unevenness of the embossing becomes small, so that the paper dust cannot be scraped off by the embossed part (recessed part), or the embossing is shallow, so the object is wiped with a sheet. Occasionally, the contact area increases, resulting in more paper dust. If the depth exceeds 2 mm, the roll will be wound softly in order to secure the embossing depth, and as a result, the winding length of the kitchen towel roll 1 will be shortened.

エンボスの深さは、マイクロスコープを用いて測定する。マイクロスコープとしては、ＫＥＹＥＮＣＥ社製の製品名「ワンショット３Ｄ測定マクロスコープＶＲ－３１００」を使用することができる。マイクロスコープの画像の観察・測定・画像解析ソフトウェアとしては、製品名「ＶＲ－Ｈ１Ａ」を使用することができる。また、測定条件は、倍率１２倍、視野面積２４ｍｍ×１８ｍｍの条件で測定する。測定倍率と視野面積は、求めるエンボスの大きさによって、適宜変更してもよい。 The embossing depth is measured using a microscope. As the microscope, the product name "One-shot 3D measurement macroscope VR-3100" manufactured by KEYENCE can be used. The product name "VR-H1A" can be used as the image observation / measurement / image analysis software of the microscope. The measurement is performed under the conditions of a magnification of 12 times and a visual field area of 24 mm × 18 mm. The measurement magnification and the visual field area may be appropriately changed depending on the desired size of embossing.

図２は、マイクロスコープによるＸ－Ｙ平面上の高さプロファイルを示し、シート表面の高さが濃淡で表されている。図２の濃淡が周辺と異なる六角形状の部位が個々のエンボスを示している。エンボスの深さは、上記マイクロスコープを用いて上述のエンボスの高低差を測定して求める。なお、測定はキッチンタオルシート１ｘの表面１ａ側で行う。また、測定時に、キッチンタオルロール１からキッチンタオルシート１ｘを３周分取り除き、４周目のシートを用いて、シートの状態で測定する。また、ミシン目がある場合は、ミシン目を避けて測定する。
まず、図２のように線分ＡＢを引き、図３の高さプロファイルを得る。なお、線分ＡＢは、エンボスを横切るように引けばよい。また、線分ＡＢは、キッチンタオルの幅方向になるように引くが、エンボスとエンボスの間隔が例えば２ｍｍ以上開いている場合は、線分を斜め方向に引いたり、流れ方向に引いたりしてもよい。高さプロファイルは、実際のシートの試料表面の凹凸を表す（測定）断面曲線Ｓであるが、ノイズ（シートの表面に繊維塊があったり、繊維がヒゲ状に伸びていたり、繊維のない部分に起因した急峻なピーク）をも含んでおり、凹凸の高低差の算出に当たっては、このようなノイズピークを除去する必要がある。
そこで、図３の（測定）断面曲線Ｓを重み平均ラジオボタンのフィルターのサイズを±１２とし、スムージングした図４の断面曲線Ｗを得る。なお、重み平均ラジオボタンのフィルターを用いたスムージングは、上記の解析ソフトを使用すれば、自動で得られる。そして、図４に示すグラフにおいて、グラフの凸部Ｈ１と、Ｈ１に隣接する凸部Ｈ２の縦軸のそれぞれの最大値の平均値を算出し、Ｈ１とＨ２とに挟まれる凹部Ｄ１における縦軸の最小値を求める。このようにして求められた最大値の平均値から最小値を差し引いた数値を暫定的なエンボスの深さとする。そして、図４に示すように、断面曲線上において連続する計２カ所（Ｄ１と、Ｈ２と凸部Ｈ３に挟まれる凹部Ｄ２の連続する計２カ所）について同様の測定を行う（この時点で２つの測定結果が得られる）。その後、キッチンタオルシート１ｘの流れ方向に９０度ずつ３回に分けて回転させた各位置において上記同様の測定を行い（流れ方向における測定位置は計４カ所となる）、合計８カ所（２×４）の平均値をエンボスの深さとして最終的に採用する。 FIG. 2 shows the height profile on the XY plane by the microscope, and the height of the sheet surface is represented by shading. Hexagonal parts with different shades from the periphery in FIG. 2 indicate individual embossing. The depth of embossing is determined by measuring the height difference of the embossing described above using the microscope. The measurement is performed on the surface 1a side of the kitchen towel sheet 1x. At the time of measurement, the kitchen towel sheet 1x is removed from the kitchen towel roll 1 for 3 laps, and the sheet is used for the 4th lap to measure in the state of the sheet. If there are perforations, avoid the perforations when measuring.
First, the line segment AB is drawn as shown in FIG. 2 to obtain the height profile of FIG. The line segment AB may be drawn so as to cross the embossing. In addition, the line segment AB is drawn so as to be in the width direction of the kitchen towel, but if the distance between the embosses is 2 mm or more, for example, the line segment is drawn diagonally or in the flow direction. May be good. The height profile is a (measured) cross-sectional curve S representing the unevenness of the sample surface of the actual sheet, but noise (fiber lumps on the surface of the sheet, fibers extending like a whiskers, or a portion without fibers). It also includes a steep peak due to the above), and it is necessary to remove such a noise peak when calculating the height difference of the unevenness.
Therefore, the (measurement) cross-section curve S in FIG. 3 is set to ± 12 in the size of the filter of the weight average radio button, and the smoothed cross-section curve W in FIG. 4 is obtained. Smoothing using the weight average radio button filter can be automatically obtained by using the above analysis software. Then, in the graph shown in FIG. 4, the average value of the maximum values of the convex portion H1 of the graph and the vertical axis of the convex portion H2 adjacent to H1 is calculated, and the vertical axis of the concave portion D1 sandwiched between H1 and H2 is calculated. Find the minimum value of. The value obtained by subtracting the minimum value from the average value of the maximum values obtained in this way is defined as the provisional embossing depth. Then, as shown in FIG. 4, the same measurement is performed at a total of two consecutive locations on the cross-sectional curve (a total of two consecutive locations of D1 and the concave portion D2 sandwiched between H2 and the convex portion H3) (at this point, 2). Two measurement results are obtained). After that, the same measurement as above was performed at each position rotated by 90 degrees in the flow direction of the kitchen towel sheet 1x in 3 steps (the total number of measurement positions in the flow direction is 4), and a total of 8 points (2x). The average value of 4) is finally adopted as the embossing depth.

（吸水量）
本発明において、キッチンタオルシート１ｘの１ｍ^２あたりの吸水量が２７０ｇ以上６００ｇ以下であることが好ましく、３１０ｇ以上５６０ｇ以下であることがより好ましく、３６０ｇ以上４９０ｇ以下であることが更に好ましい。１ｍ^２あたりの吸水量が２７０ｇ未満であると、キッチンタオルシート１ｘの吸水量に劣り、６００ｇを超えると、キッチンタオルシート１ｘの紙粉が多くなる。
また、キッチンタオルシート１ｘの１ｇあたりの吸水量が２．５ｇ以上５．７ｇ以下であることが好ましく、２．９ｇ以上５．３ｇ以下であることがより好ましく、３．３ｇ以上４．８ｇ以下であることが更に好ましい。１ｇあたりの吸水量が２．５ｇ未満であると、キッチンタオルシート１ｘの１ｇあたりの吸水量に劣る。
なお、キッチンタオルシート１ｘの各吸水量は以下のように測定する。 (Amount of water absorption)
In the present invention, the water absorption amount per 1 m ² of the kitchen towel sheet is preferably 270 g or more and 600 g or less, more preferably 310 g or more and 560 g or less, and further preferably 360 g or more and 490 g or less. When the water absorption amount per 1 m ² is less than 270 g, the water absorption amount of the kitchen towel sheet 1x is inferior, and when it exceeds 600 g, the paper dust of the kitchen towel sheet 1x increases.
Further, the water absorption per 1 g of the kitchen towel sheet 1x is preferably 2.5 g or more and 5.7 g or less, more preferably 2.9 g or more and 5.3 g or less, and 3.3 g or more and 4.8 g or less. Is more preferable. If the amount of water absorbed per 1 g is less than 2.5 g, the amount of water absorbed per 1 g of the kitchen towel sheet 1x is inferior.
The amount of water absorbed by the kitchen towel sheet 1x is measured as follows.

まず、キッチンタオルシート１ｘを採取し、一片が７．６ｃｍ（３インチ）の正方形の型版を用いてカットし、一辺７．６ｃｍの矩形の試験片２００を作製する。その後、吸水前の試験片２００の質量を電子天秤で測定しておく。そして、試験片２００をホルダー２２０（試験片２００の３点を固定するジグで、ジグは水分を吸収しない金属からなる）にセットする。
次に、市販のバットに、蒸留水を深さ２ｃｍ入れ、ホルダー２２０にセットした試験片２００を蒸留水中に２分間浸漬する。２分浸漬後に試験片２００をホルダー２２０と共に蒸留水から取り出し、図５に示すように、試験片２００の１つの隅部２００ｄに帯２１０を貼り付ける。帯２１０は、測定するサンプルと同じキッチンタオルシート１ｘを幅２ｍｍ×長さ１５ｍｍの大きさに切り、試験片２００の隅部２００ｄから中心に向かって６ｍｍの部分に貼り付ける。次に、ホルダー２２０と試験片２００を、隅部２００ｄに対向する隅部２００ａが上になるようにして空の水槽内に設置した棒にぶら下げ、水槽の蓋を閉めて１０分間、放置する。その後、ホルダー２２０と試験片２００を水槽から取り出し、帯２１０とホルダー２２０を外し、電子天秤で試験片２００の質量を測定する。蒸留水に浸す前後での試験片２００の質量変化から、試験片２００の１ｍ^２あたりの蒸留水の吸水量（ｇ（水）／ｍ^２（紙））を計算する。さらに、１ｍ^２あたりの吸水量（ｇ（水）／ｍ^２（紙））を試験片２００の坪量で割ることにより、１ｍ^２あたりの吸水量（ｇ（水）／ｍ^２（紙））／坪量（ｇ（紙）／ｍ^２（紙））＝１ｇあたりの吸水量（ｇ（水）／ｇ（紙））を算出する。測定は各サンプル５回ずつ行い、平均値を採用する。
なお、本測定は、ＪＩＳＰ８１１１法に従い、温度２３±１℃、湿度５０±２％の状態で行う。また、蒸留水は２３±１℃に保持する。 First, a kitchen towel sheet 1x is collected and cut using a square mold having a size of 7.6 cm (3 inches) to prepare a rectangular test piece 200 having a side of 7.6 cm. After that, the mass of the test piece 200 before water absorption is measured with an electronic balance. Then, the test piece 200 is set in the holder 220 (a jig that fixes three points of the test piece 200, and the jig is made of a metal that does not absorb water).
Next, distilled water is placed in a commercially available vat at a depth of 2 cm, and the test piece 200 set in the holder 220 is immersed in the distilled water for 2 minutes. After soaking for 2 minutes, the test piece 200 is taken out from the distilled water together with the holder 220, and the band 210 is attached to one corner 200d of the test piece 200 as shown in FIG. For the band 210, the same kitchen towel sheet 1x as the sample to be measured is cut into a size of 2 mm in width × 15 mm in length, and attached to a portion 6 mm from the corner 200d of the test piece 200 toward the center. Next, the holder 220 and the test piece 200 are hung on a rod installed in an empty water tank with the corner portion 200a facing the corner portion 200d facing up, the lid of the water tank is closed, and the test piece 200 is left for 10 minutes. After that, the holder 220 and the test piece 200 are taken out from the water tank, the band 210 and the holder 220 are removed, and the mass of the test piece 200 is measured with an electronic balance. From the mass change of the test piece 200 before and after immersion in distilled water, the water absorption amount (g (water) / m ² (paper)) of the distilled water per 1 m ² of the test piece 200 is calculated. Further, by dividing the water absorption per 1 m ² (g (water) / m ² (paper)) by the basis weight of the test piece 200, the water absorption per 1 m ² (g (water) / m ² (paper)). / Basis weight (g (paper) / m ² (paper)) = Water absorption per 1 g (g (water) / g (paper)) is calculated. The measurement is performed 5 times for each sample, and the average value is adopted.
This measurement is performed in a state of temperature 23 ± 1 ° C. and humidity 50 ± 2% according to the JIS P 8111 method. The distilled water is kept at 23 ± 1 ° C.

（ＤＭＤＴ及びＤＣＤＴ）
キッチンタオルシート１ｘの、ＪＩＳＰ８１１３に基づく乾燥時におけるＭＤ方向の引張強度ＤＭＤＴ（ＤｒｙＭａｃｈｉｎｅＤｉｒｅｃｔｉｏｎＴｅｎｓｉｌｅＳｔｒｅｎｇｔｈ）は１５Ｎ／２５ｍｍ以上１１５Ｎ／２５ｍｍ以下であることが好ましく、２０Ｎ／２５ｍｍ以上１００Ｎ／２５ｍｍ以下であることがより好ましく、３５Ｎ／２５ｍｍ以上８０Ｎ／２５ｍｍ以下であることが更に好ましい。また、乾燥時におけるＣＤ方向の引張強度ＤＣＤＴ（ＤｒｙＣｒｏｓｓＤｉｒｅｃｔｉｏｎＴｅｎｓｉｌｅＳｔｒｅｎｇｔｈ）は４Ｎ／２５ｍｍ以上８０Ｎ／２５ｍｍ以下であることが好ましく、６Ｎ／２５ｍｍ以上６５Ｎ／２５ｍｍ以下であることがより好ましく、１０Ｎ／２５ｍｍ以上５０Ｎ／２５ｍｍ以下であることが更に好ましい。ＤＭＤＴが１５Ｎ／２５ｍｍ未満であるか、又はＤＣＤＴが４Ｎ／２５ｍｍ未満であると、いずれもキッチンタオルシート１ｘの強度が不十分で破れやすくなり、再利用が難しくなる。ＤＭＤＴが１１５Ｎ／２５ｍｍを超えるか、又はＤＣＤＴが８０Ｎ／２５ｍｍを超えると、坪量が高くなって、いずれもキッチンタオルシート１ｘの紙粉が多くなる。
なお、この場合のＭＤ方向及びＣＤ方向とは、キッチンタオルシート１ｘの製造時における製造方向（流れ方向）がＭＤ方向であり、ＣＤ方向はＭＤ方向に直交する方向である。 (DMDT and DCDT)
The tensile strength DMDT (Dry Machine Direction Tensile Strength) of the kitchen towel sheet 1x in the MD direction at the time of drying based on JIS P 8113 is preferably 15 N / 25 mm or more and 115 N / 25 mm or less, preferably 20 N / 25 mm or more and 100 N / 25 mm or less. It is more preferable that it is 35 N / 25 mm or more and 80 N / 25 mm or less. Further, the tensile strength DCDT (Dry Cross Direction Tensile Strength) in the CD direction at the time of drying is preferably 4N / 25mm or more and 80N / 25mm or less, more preferably 6N / 25mm or more and 65N / 25mm or less, and 10N / It is more preferably 25 mm or more and 50 N / 25 mm or less. If the DMDT is less than 15N / 25mm or the DCDT is less than 4N / 25mm, the strength of the kitchen towel sheet 1x is insufficient and the kitchen towel sheet 1x is easily torn, making it difficult to reuse. When the DMDT exceeds 115 N / 25 mm or the DCDT exceeds 80 N / 25 mm, the basis weight becomes high and the amount of paper dust in the kitchen towel sheet 1x increases.
In this case, the MD direction and the CD direction are the MD direction in the manufacturing direction (flow direction) at the time of manufacturing the kitchen towel sheet 1x, and the CD direction is a direction orthogonal to the MD direction.

また、キッチンタオルシート１ｘの乾燥時におけるＣＤ方向の引張強度（ＤＣＤＴ）に対する、乾燥時におけるＭＤ方向の引張強度（ＤＭＤＴ）の比率（ＤＭＤＴ／ＤＣＤＴ）は１．２以上４．５以下であることが好ましく、１．４以上４．０以下であることがより好ましく、１．６以上３．５以下であることが更に好ましい。比率が１．２未満であると結果として合成繊維の割合が多くなり、吸水量に劣る。比率が４．５を超えるとＤＣＤＴが低くなってキッチンタオルシート１ｘが破れやすくなる場合があり、再利用が難しくなる。 The ratio (DMDT / DCDT) of the tensile strength (DMDT) in the MD direction to the tensile strength (DCDT) in the CD direction when the kitchen towel sheet 1x is dried shall be 1.2 or more and 4.5 or less. It is more preferable, it is more preferably 1.4 or more and 4.0 or less, and further preferably 1.6 or more and 3.5 or less. If the ratio is less than 1.2, the ratio of synthetic fibers is increased as a result, and the amount of water absorption is inferior. If the ratio exceeds 4.5, the DCDT may become low and the kitchen towel sheet 1x may be easily torn, making it difficult to reuse.

（ＷＭＤＴ及びＷＣＤＴ）
キッチンタオルシート１ｘの、旧ＪＩＳＳ３１０４に基づく湿潤時におけるＭＤ方向の引張強さＷＭＤＴ（ＷｅｔＭａｃｈｉｎｅＤｉｒｅｃｔｉｏｎＴｅｎｓｉｌｅＳｔｒｅｎｇｔｈ）が１３Ｎ／２５ｍｍ以上１００Ｎ／２５ｍｍ以下であることが好ましく、１８Ｎ／２５ｍｍ以上８５Ｎ／２５ｍｍ以下であることがより好ましく、２５Ｎ／２５ｍｍ以上７３Ｎ／２５ｍｍ以下であることが更に好ましい。また、湿潤時におけるＣＤ方向の引張強さＷＣＤＴ（ＷｅｔＣｒｏｓｓＤｉｒｅｃｔｉｏｎＴｅｎｓｉｌｅＳｔｒｅｎｇｔｈ）が３Ｎ／２５ｍｍ以上６５Ｎ／２５ｍｍ以下であることが好ましく、４Ｎ／２５ｍｍ以上５５Ｎ／２５ｍｍ以下であることがより好ましく、９Ｎ／２５ｍｍ以上４５Ｎ／２５ｍｍ以下であることが更に好ましい。ＷＭＤＴが１３Ｎ／２５ｍｍ未満であるか、又はＷＣＤＴが３Ｎ／２５ｍｍ未満であると、いずれもキッチンタオルシート１ｘが破れやすくなり、再利用が難しくなる。ＷＭＤＴが１００Ｎ／２５ｍｍを超えるか、又はＷＣＤＴが６５Ｎ／２５ｍｍを超えると、いずれも坪量が高くなり、結果としてキッチンタオルシート１ｘの紙粉が多くなる。 (WMDT and WCDT)
The tensile strength WMDT (Wet Machine Direction Tensile Strength) of the kitchen towel sheet 1x in the MD direction when wet based on the old JIS S 3104 is preferably 13 N / 25 mm or more and 100 N / 25 mm or less, preferably 18 N / 25 mm or more and 85 N / It is more preferably 25 mm or less, and further preferably 25 N / 25 mm or more and 73 N / 25 mm or less. Further, the tensile strength WCDT (Wet Cross Direction Tensile Strength) in the CD direction at the time of wetting is preferably 3N / 25mm or more and 65N / 25mm or less, more preferably 4N / 25mm or more and 55N / 25mm or less, and 9N. It is more preferably / 25 mm or more and 45 N / 25 mm or less. If the WMDT is less than 13N / 25mm or the WCDT is less than 3N / 25mm, the kitchen towel sheet 1x is easily torn and difficult to reuse. When WMDT exceeds 100 N / 25 mm or WCDT exceeds 65 N / 25 mm, the basis weight becomes high, and as a result, the amount of paper dust in the kitchen towel sheet 1x increases.

また、キッチンタオルシート１ｘの湿潤時におけるＣＤ方向の引張強度（ＷＣＤＴ）に対する、湿潤時におけるＭＤ方向の引張強度（ＷＭＤＴ）の比率（ＷＭＤＴ／ＷＣＤＴ）は１．３以上４．６以下であることが好ましく、１．５以上４．１以下であることがより好ましく、１．７以上３．６以下であることが更に好ましい。比率が１．３未満であると結果として合成繊維の割合が多くなり、吸水量に劣る。比率が４．６を超えるとキッチンタオルシート１ｘが破れやすくなり、再利用が難しくなる。 Further, the ratio (WMDT / WCDT) of the tensile strength (WMDT) in the MD direction to the tensile strength (WCDT) in the CD direction when the kitchen towel sheet 1x is wet is 1.3 or more and 4.6 or less. Is preferable, and it is more preferably 1.5 or more and 4.1 or less, and further preferably 1.7 or more and 3.6 or less. If the ratio is less than 1.3, the ratio of synthetic fibers is increased as a result, and the amount of water absorption is inferior. If the ratio exceeds 4.6, the kitchen towel sheet 1x is easily torn and it becomes difficult to reuse it.

さらに、キッチンタオルシート１ｘの乾燥時におけるＭＤ方向の引張強度（ＤＭＤＴ）に対する、湿潤時におけるＭＤ方向の引張強度（ＷＭＤＴ）の比率（（ＷＭＤＴ／ＤＭＤＴ）×１００（％））は５０％以上９５％以下であることが好ましく、６５％以上９３％以下であることがより好ましく、７０％以上９１％以下であることが更に好ましい。同様に、キッチンタオルシート１ｘの乾燥時におけるＣＤ方向の引張強度（ＤＣＤＴ）に対する、湿潤時におけるＣＤ方向の引張強度（ＷＣＤＴ）の比率（（ＷＣＤＴ／ＤＣＤＴ）×１００（％））は４３％以上８９％以下であることが好ましく、６０％以上８６％以下であることがより好ましく、６５％以上８３％以下であることが更に好ましい。（ＷＭＤＴ／ＤＭＤＴ）の比率が５０％未満であるか、又は（ＷＣＤＴ／ＤＣＤＴ）の比率が４３％未満であると、キッチンタオルシート１ｘが破れやすくなり、再利用が難しくなる。（ＷＭＤＴ／ＤＭＤＴ）の比率が９５％を超えるか、又は（ＷＣＤＴ／ＤＣＤＴ）の比率が８９％を超えると、結果として合成繊維の割合が多くなり、吸水量に劣る。 Further, the ratio ((WMDT / DMDT) × 100 (%)) of the tensile strength (WMDT) in the MD direction to the tensile strength (DMDT) in the MD direction when the kitchen towel sheet 1x is dried is 50% or more 95. % Or less, more preferably 65% or more and 93% or less, and even more preferably 70% or more and 91% or less. Similarly, the ratio of the tensile strength (WCDT) in the CD direction (WCDT) to the tensile strength (DCDT) in the CD direction when the kitchen towel sheet 1x is dried is 43% or more ((WCDT / DCDT) × 100 (%)). It is preferably 89% or less, more preferably 60% or more and 86% or less, and further preferably 65% or more and 83% or less. If the ratio of (WMDT / DMDT) is less than 50% or the ratio of (WCDT / DCDT) is less than 43%, the kitchen towel sheet 1x is easily torn and difficult to reuse. When the ratio of (WMDT / DMDT) exceeds 95% or the ratio of (WCDT / DCDT) exceeds 89%, the ratio of synthetic fibers increases as a result, and the amount of water absorption is inferior.

（破断伸び）
キッチンタオルシート１ｘのＭＤ方向の破断伸びは、２０％以上６５％以下であることが好ましく、２８％以上５３％以下であることがより好ましく、３３％以上４８％以下であることが更に好ましい。また、キッチンタオルシート１ｘのＣＤ方向の破断伸びは、５０％以上１００％以下であることが好ましく、６０％以上９５％以下であることがより好ましく、７０％以上９０％以下であることが更に好ましい。キッチンタオルシート１ｘのＭＤ方向又はＣＤ方向の破断伸びを上記の範囲内にすることで、再利用が可能であり、吸水量が多く、かつ紙粉の少ないキッチンタオルロール１を得ることができる。なお、キッチンタオルシート１ｘの各方向の破断伸びは、ＪＩＳＰ８１１３に基づいて測定する。 (Breaking elongation)
The breaking elongation of the kitchen towel sheet 1x in the MD direction is preferably 20% or more and 65% or less, more preferably 28% or more and 53% or less, and further preferably 33% or more and 48% or less. Further, the breaking elongation of the kitchen towel sheet 1x in the CD direction is preferably 50% or more and 100% or less, more preferably 60% or more and 95% or less, and further preferably 70% or more and 90% or less. preferable. By setting the breaking elongation of the kitchen towel sheet 1x in the MD direction or the CD direction within the above range, it is possible to obtain a kitchen towel roll 1 that can be reused, has a large amount of water absorption, and has a small amount of paper dust. The breaking elongation of the kitchen towel sheet 1x in each direction is measured based on JIS P 8113.

３．キッチンタオルシート及びキッチンタオルロールの製造方法
キッチンタオルシート１ｘ及びキッチンタオルロール１は、例えば（１）所定のスパンボンド不織布にパルプ繊維を積層して水流交絡、（２）エンボス処理、（３）ロール巻取り加工の順で製造することができる。
このとき、（１）水流交絡において、合成繊維にパルプ繊維を水流交絡することで、合成繊維及びパルプ繊維を含む不織布を得る。水流交絡の方法に関しては、例えば、特開２０１８－１９３６３４号公報に記載された方法で行うことが好ましい。また、（２）エンボス処理では、マッチドスチール（スチールマッチ）による熱エンボス処理をロールワインダにて実施することが好ましい。エンボスパターンとしては、六角形状であることが好ましい。 3. 3. Manufacturing method of kitchen towel sheet and kitchen towel roll The kitchen towel sheet 1x and kitchen towel roll 1 are, for example, (1) laminating pulp fibers on a predetermined spunbonded non-woven fabric and water flow entanglement, (2) embossing treatment, (3) roll. It can be manufactured in the order of winding.
At this time, in (1) water flow entanglement, the pulp fiber is water flow entangled with the synthetic fiber to obtain a non-woven fabric containing the synthetic fiber and the pulp fiber. As for the method of water flow confounding, for example, it is preferable to use the method described in JP-A-2018-193634. Further, in (2) embossing, it is preferable to carry out heat embossing with matched steel (steel match) with a roll winder. The embossing pattern is preferably hexagonal.

以上、実施形態を用いて本発明を説明したが、本発明の技術的範囲は上記実施形態や実施例に記載の範囲には限定されないことは言うまでもない。上記実施形態に、多様な変更又は改良を加えることが可能であることが、当業者に明らかである。また、そのような変更又は改良を加えた形態も本発明の技術的範囲に含まれ得ることが、特許請求の範囲の記載から明らかである。 Although the present invention has been described above using the embodiments, it goes without saying that the technical scope of the present invention is not limited to the scope described in the above-described embodiments and examples. It will be apparent to those skilled in the art that various changes or improvements can be made to the above embodiments. It is also clear from the description of the claims that the form with such changes or improvements may be included in the technical scope of the present invention.

以下、本発明について、実施例を挙げて詳細に説明する。なお、本発明は、以下に示す実施例に何ら限定されるものではない。 Hereinafter, the present invention will be described in detail with reference to examples. The present invention is not limited to the examples shown below.

（１）水流交絡（２）エンボス処理、（３）ロール巻取り加工の工程を経て、表２に記載された実施例１～１５及び比較例１～７のキッチンタオルロールを作製した。また、市販品の２プライのキッチンタオルロールを用意した。以上の全ての実施例、比較例及び市販品のキッチンタオルロールに関して上述の各パラメーターを測定し、かつ、下記の各評価を行った。なお、下記の表２においては特にパラメーターとして記載していないが、カレンダー条件は統一したため、坪量の高いキッチンタオルシートは、比容積が低くなる傾向にある。
紙粉量：紙粉量の官能評価は３０人で行った。キッチンタオルシート及びキッチンタオルロールを用いて食器を拭いた際に、手に付着したり拭き取った食器に付着したりした紙粉量の評価を次のように行った。特に優れる（顕著に少ない）：５点、優れる（少ない）：４点、良好（問題ない）：３点、劣る（多い）：２点、特に劣る（顕著に多い）：１点
なお、３０人の平均値を算出し、四捨五入して有効数値１桁にした。 Through the steps of (1) water flow entanglement (2) embossing treatment and (3) roll winding processing, kitchen towel rolls of Examples 1 to 15 and Comparative Examples 1 to 7 shown in Table 2 were produced. In addition, a commercially available 2-ply kitchen towel roll was prepared. Each of the above parameters was measured with respect to all the above Examples, Comparative Examples and Commercial Kitchen Towel Rolls, and the following evaluations were performed. Although not described as parameters in Table 2 below, the specific volume of kitchen towel sheets with a high basis weight tends to be low because the calendar conditions are unified.
Amount of paper dust: The sensory evaluation of the amount of paper dust was performed by 30 people. When the tableware was wiped using the kitchen towel sheet and the kitchen towel roll, the amount of paper dust adhering to the hands or the wiped tableware was evaluated as follows. Especially excellent (significantly less): 5 points, excellent (less): 4 points, good (no problem): 3 points, inferior (more): 2 points, especially inferior (significantly more): 1 point In addition, 30 people The average value of was calculated and rounded to one valid value.

吸水量：上述の方法で実測し、各実測値より下記の表１の通り評価を行った。

Water absorption: Measured by the above method, and evaluated from each measured value as shown in Table 1 below.

巻長：巻長を実測して、下記の通り評価を行った。
４ｍ未満：１点
４ｍ以上５ｍ未満：２点
５ｍ以上７ｍ未満：３点
７ｍ以上８ｍ未満：４点
８ｍ以上：５点 Volume length: The volume length was actually measured and evaluated as follows.
Less than 4m: 1 point 4m or more and less than 5m: 2 points 5m or more and less than 7m: 3 points 7m or more and less than 8m: 4 points 8m or more: 5 points

表２に示すように、実施例１～１６のキッチンタオルロールはいずれも吸水量に優れ、巻長も十分なものであり、かつ、紙粉量も少なかった。一方で比較例１～７のキッチンタオルロールは吸水量が少ないか、巻長が短いか、又は紙粉量が多いものであった。
以上より、本発明のキッチンタオルロールは、再利用が可能であり、吸水量が多く、かつ紙粉の少ない、一定以上の巻長を有するキッチンタオルロールを提供することができる。 As shown in Table 2, all of the kitchen towel rolls of Examples 1 to 16 had excellent water absorption, a sufficient winding length, and a small amount of paper dust. On the other hand, the kitchen towel rolls of Comparative Examples 1 to 7 had a small amount of water absorption, a short winding length, or a large amount of paper dust.
From the above, the kitchen towel roll of the present invention can be reused, and it is possible to provide a kitchen towel roll having a certain roll length or more, which has a large amount of water absorption and a small amount of paper dust.

１キッチンタオルロール
１ａ表面
１ｂ裏面
１ｅキッチンタオルシートの最外巻の端縁
１ｘキッチンタオルシート
２００試験片
２００ａ、２００ｄ隅部
２１０帯
２２０ホルダー 1 Kitchen towel roll 1a Front side 1b Back side 1e Outermost edge of kitchen towel sheet 1x Kitchen towel sheet 200 Specimen 200a, 200d Corner 210 Band 220 Holder

Claims

A 1-ply embossed kitchen towel sheet containing synthetic fibers and pulp fibers is a roll-shaped kitchen towel roll.
The basis weight of the kitchen towel sheet is 50 g / m ² or more and 200 g / m ² or less.
The embossing depth is 0.1 mm or more and 2 mm or less.
A kitchen towel roll having a roll length of 5 m or more and 24 m or less.

The kitchen towel roll according to claim 1, wherein the roll density of the roll is 0.06 g / cm ³ or more and 0.19 g / cm ³ or less.

The kitchen according to claim 1 or 2, wherein the kitchen towel sheet has a water absorption of 270 g or more and 600 g or less in 1 m ² , and a water absorption of 2.5 g or more and 5.7 g or less in 1 g. Towel roll.

The tensile strength (DCDT) in the CD direction when the kitchen towel sheet is dried is 4N / 25mm or more and 80N / 25mm or less.
The feature is that the ratio (DMDT / DCDT) of the tensile strength (DMDT) in the MD direction at the time of drying to the tensile strength (DCDT) in the CD direction at the time of drying the kitchen towel sheet is 1.2 or more and 4.5 or less. The kitchen towel roll according to any one of claims 1 to 3.

The kitchen towel roll according to any one of claims 1 to 4, wherein the kitchen towel sheet has a tensile strength (DMDT) in the MD direction of 15 N / 25 mm or more and 115 N / 25 mm or less when the kitchen towel sheet is dried.

Any of claims 1 to 5, wherein the content ratio of the synthetic fiber in the kitchen towel sheet is 5% or more and 45% or less, and the content ratio of the pulp fiber is 55% or more and 95% or less. The kitchen towel roll according to item 1.

The ratio ((WMDT / DMDT) × 100 (%)) of the tensile strength (WMDT) in the MD direction to the tensile strength (DMDT) in the MD direction when the kitchen towel sheet is dried is 50% or more and 95% or less. The kitchen towel roll according to any one of claims 1 to 6, wherein the kitchen towel roll is characterized by the above.

The ratio ((WCDT / DCDT) × 100 (%)) of the tensile strength (WCDT) in the CD direction to the tensile strength (DCDT) in the CD direction when the kitchen towel sheet is dried is 43% or more and 89% or less. The kitchen towel roll according to any one of claims 1 to 7, wherein the kitchen towel roll is characterized by the above.

The kitchen towel roll according to any one of claims 1 to 8, wherein the kitchen towel sheet has a paper thickness of 0.45 mm or more and 1.8 mm or less.

The kitchen towel roll according to any one of claims 1 to 9, wherein the kitchen towel sheet has a breaking elongation of 50% or more and 100% or less in the CD direction.

The kitchen towel roll according to any one of claims 1 to 10, wherein the breaking elongation of the kitchen towel sheet in the MD direction is 20% or more and 65% or less.

Claims 1 to 11 are characterized in that the basis weight of the synthetic fiber is 8 g / m ² or more and 55 g / m ² or less, and the basis weight of the pulp fiber is 38 g / m ² or more and 160 g / m ² or less. The kitchen towel roll according to any one of the above items.