JP2022073793A - Artificial nail manufacturing method - Google Patents
Artificial nail manufacturing method Download PDFInfo
- Publication number
- JP2022073793A JP2022073793A JP2020183990A JP2020183990A JP2022073793A JP 2022073793 A JP2022073793 A JP 2022073793A JP 2020183990 A JP2020183990 A JP 2020183990A JP 2020183990 A JP2020183990 A JP 2020183990A JP 2022073793 A JP2022073793 A JP 2022073793A
- Authority
- JP
- Japan
- Prior art keywords
- nail
- person
- gel
- impression material
- artificial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明の実施形態は、つけ爪の製造方法に関する。 The embodiment of the present invention relates to a method for manufacturing artificial nails.
つけ爪の上に所定の図柄を描き、かかるつけ爪を人の爪の上に貼ることによる美容が楽しまれている。かかるつけ爪については、人の爪に貼ったときに、よくフィットすることが求められている。 Beauty is enjoyed by drawing a predetermined pattern on the artificial nails and sticking the artificial nails on the human nails. Such artificial nails are required to fit well when attached to human nails.
本発明が解決しようとする課題は、人の爪によくフィットするつけ爪を、遠隔で製造することが出来るつけ爪の製造方法を提供することである。 An object to be solved by the present invention is to provide a method for manufacturing artificial nails, which can remotely manufacture artificial nails that fit well to human nails.
実施形態のつけ爪の製造方法は、第1の人が、第1歯科用シリコーン印象材を保護具に詰める工程と、第1の人が、保護具に詰められた第1歯科用シリコーン印象材を、保護具を介して第1の人の爪に押し当てて、第1の人の爪の爪型を製造する工程と、第2の人が、爪型の中に第1歯科用シリコーン印象材より硬度の高い第2歯科用シリコーン印象材を詰めることにより、第1の人の、爪部分を有する指モデルを製造する工程と、第2の人が、爪部分の上に第1ジェルを塗布する工程と、第2の人が、第1ジェルの上に、第1ジェルよりセルフレベリング性の高い第2ジェルを塗布する工程と、第2の人が、第1ジェル及び第2ジェルの硬化により得られたつけ爪を、指モデルから剥離する工程と、を備える。 In the method of manufacturing the nail nail of the embodiment, the first person packs the first dental silicone impression material into the protective tool, and the first person packs the first dental silicone impression material into the protective tool. The process of manufacturing the nail mold of the first person's nail by pressing it against the nail of the first person through a protective device, and the second person's impression of the first dental silicone in the nail mold. The process of manufacturing a finger model with a nail part of the first person by packing a second dental silicone impression material that is harder than the material, and the second person puts the first gel on the nail part. The step of applying, the step of the second person applying the second gel having higher self-leveling property than the first gel on the first gel, and the second person of the first gel and the second gel It comprises a step of peeling the nail obtained by curing from the finger model.
以下、図面を参照しつつ本発明の実施形態を説明する。なお、以下の説明では、同一の部材等には同一の符号を付し、一度説明した部材等については適宜その説明を省略する。 Hereinafter, embodiments of the present invention will be described with reference to the drawings. In the following description, the same members and the like are designated by the same reference numerals, and the description of the members and the like once described will be omitted as appropriate.
(第1実施形態)
本実施形態のつけ爪の製造方法は、第1の人が、第1歯科用シリコーン印象材を保護具に詰める工程と、第1の人が、保護具に詰められた第1歯科用シリコーン印象材を、保護具を介して第1の人の爪に押し当てて、第1の人の爪の爪型を製造する工程と、第2の人が、爪型の中に第1歯科用シリコーン印象材より硬度の高い第2歯科用シリコーン印象材を詰めることにより、第1の人の、爪部分を有する指モデルを製造する工程と、第2の人が、爪部分の上に第1ジェルを塗布する工程と、第2の人が、第1ジェルの上に、第1ジェルよりセルフレベリング性の高い第2ジェルを塗布する工程と、第2の人が、第1ジェル及び第2ジェルの硬化により得られたつけ爪を、指モデルから剥離する工程と、を備える。
(First Embodiment)
In the method of manufacturing the nail nail of the present embodiment, the first person packs the first dental silicone impression material into the protective tool, and the first person packs the first dental silicone impression material into the protective tool. The process of pressing the material against the nail of the first person through a protective device to manufacture the nail mold of the nail of the first person, and the second person in the nail mold the first dental silicone. The process of manufacturing a finger model having a nail part of the first person by packing a second dental silicone impression material having a hardness higher than that of the impression material, and a first gel on the nail part by the second person. The step of applying the second gel, the second person applies the second gel having higher self-leveling property than the first gel, and the second person applies the first gel and the second gel. It is provided with a step of peeling the nail obtained by the curing of the fingernail from the finger model.
図1は、本実施形態のつけ爪100の製造方法のフローチャートである。
FIG. 1 is a flowchart of a method for manufacturing
図2乃至図4は、本実施形態のつけ爪100の製造工程を模式的に示す写真である。
2 to 4 are photographs schematically showing the manufacturing process of the
図1乃至図4を用いて、本実施形態のつけ爪100の製造方法について説明をする。
A method for manufacturing the
本実施形態のつけ爪100の製造方法は、お客様の爪N1につけるつけ爪100を製造する方法である。
The method of manufacturing the
まず、お客様が、第1歯科用シリコーン印象材10を保護具に詰める(図1のS10、図2(a)、図2(b)及び図2(c))。
First, the customer packs the first dental
第1歯科用シリコーン印象材10は、例えば、歯の型を取る場合や、上下の歯の噛み合わせを記録する際に使用される、シリコーン印象材である。第1歯科用シリコーン印象材10は、例えば、2液(2ペースト性)の付加硬化タイプの歯科用シリコーン印象材である。図2(a)には、第1歯科用シリコーン印象材10の製造に用いられる、第1ペースト12と第2ペースト14が図示されている。なお、図2(a)には、お客様の手H1が、あわせて示されている。
The first dental
例えば、第1ペースト12と第2ペースト14を、お客差が図2(b)のように練り合わせることにより、第1歯科用シリコーン印象材10が製造される。なお、第1歯科用シリコーン印象材10は、上記のものに限定されるものではない。
For example, the first dental
保護具20は、硬化前の第1歯科用シリコーン印象材10を載せて、後述するお客様の爪N1に押し当てるための、皿状の薄い台である。保護具20の大きさは、例えば、お客様の爪N1と同程度の大きさである。ここで、爪のサイズにはかなりの個人差がある。爪の大きさは、必ずしも手の大きさに比例するわけではない。手が大きい人であっても、相対的に爪の大きさが小さいこともある。そこで、保護具20の大きさは、お客様の爪N1の大きさにあわせて、適宜選択することになる。例えば、世界共通の10サイズ又は12サイズを有するネイルチップを、保護具20として使用することができる。しかし、保護具20として適用できるものは、かかるネイルチップに限定されるものではない。
The
次に、お客様が、保護具20に詰められた第1歯科用シリコーン印象材10を、保護具20を介してお客様の爪N1に押し当てる。そして、お客様の爪N1の爪型30を製造する(図1のS14、図2(d)、図3(a)及び図3(b))。
Next, the customer presses the first dental
図2(d)は、お客様が、保護具20に詰められた第1歯科用シリコーン印象材10を、お客様の指(右手親指)F1の、お客様の爪N1に押し当てている図である。このときに、ここで、お客様は、お客様の指(左手親指)F2を用いて、保護具20を押している。保護具20には、第1歯科用シリコーン印象材10が詰められている。そして、かかる第1歯科用シリコーン印象材10は、保護具20を介して、お客様の爪N1に押し当てられている。言い換えると、お客様は、お客様の指(左手親指)F2が第1歯科用シリコーン印象材10に直接触れた状態で、お客様の爪N1に第1歯科用シリコーン印象材を押し当てているのではない。お客様は、保護具20を使って、間接的に、第1歯科用シリコーン印象材10を、お客様の爪N1に押し当てているのである。
FIG. 2D is a diagram in which the customer presses the first dental silicone impression material 10 packed in the
図3(a)は、第1歯科用シリコーン印象材10を、お客様の指(右手親指)F1に押し当てて、第1歯科用シリコーン印象材10を硬化させている図である。このときに、お客様は、保護具20から第1歯科用シリコーン印象材10がはみ出すように、第1歯科用シリコーン印象材10を押し当てることが好ましい。また、お客様の爪N1は、第1歯科用シリコーン印象材10により完全に覆われた状態とすることが好ましい。図3(b)には、第1歯科用シリコーン印象材10の硬化により製造された爪型30を示している。
FIG. 3A is a diagram in which the first dental
次に、ネイリストが、爪型30の中に第2歯科用シリコーン印象材40を詰めることにより、お客様の、爪部分52を有する指モデル50を製造する(図1のS18、図3(c)及び図3(d))。
Next, the nail technician fills the
例えば、お客様によって製造された爪型30は、輸送手段によって輸送され、ネイリストの元に届けられる。そして、ネイリストは、かかる爪型30を用いて、指モデル50を製造する。なお、ネイリストは、第2の人の一例である。
For example, the
第2歯科用シリコーン印象材40は、例えば、歯の型を取る場合や、上下の歯の噛み合わせを記録する際に使用される、シリコーン印象材である。第2歯科用シリコーン印象材40は、例えば、2液(2ペースト性)の付加硬化タイプの歯科用シリコーン印象材である。図3(c)には、第2歯科用シリコーン印象材40の製造に用いられる、第3ペースト42と第4ペースト44が図示されている。なお、図3(c)には、ネイリストの手H2が、あわせて示されている。
The second dental silicone impression material 40 is a silicone impression material used, for example, when taking a tooth mold or recording the engagement of upper and lower teeth. The second dental silicone impression material 40 is, for example, a two-component (two-pasty) addition-curing type dental silicone impression material. FIG. 3 (c) illustrates the
例えば、第3ペースト42と第4ペースト44を、ネイリストが図3(c)のように練り合わせることにより、第2歯科用シリコーン印象材40が製造される。そして、ネイリストは、かかる第2歯科用シリコーン印象材40を、図3(d)に示すように、爪型30の中に詰める。このようにして、ネイリストは、お客様の、爪部分52を有する指モデル50を製造する。なお、爪部分52及び指モデル50は、図4(a)に図示されている。
For example, the second dental silicone impression material 40 is manufactured by kneading the
第2歯科用シリコーン印象材40の硬度は、第1歯科用シリコーン印象材10の硬度より高いことが好ましい。
The hardness of the second dental silicone impression material 40 is preferably higher than the hardness of the first dental
なお、第2歯科用シリコーン印象材40は、上記のものに限定されるものではない。 The second dental silicone impression material 40 is not limited to the above.
次に、ネイリストが、指モデル50の爪部分52の上に、第1ジェル60を塗布する(図1のS24及び図4(a))。この後、ネイリストは、第1ジェル60を硬化させる。第1ジェル60及び後述する第2ジェル62は、硬化により後につけ爪100となるジェルである。第1ジェル60及び第2ジェル62は、例えばUV(Ultraviolet)硬化性のジェルである。第1ジェル60及び第2ジェル62は、例えば筆Bにより塗布されるが、塗布の方法はこれに限定されるものではない。
Next, the nail technician applies the
なお、図4(a)において示されている指モデル50の爪部分52は、爪部分52の先端に、爪が長くされた部分54が設けられることにより、長くされている。爪が長くされた部分54は、第1ジェル60の塗布の前に、ネイリストが、例えば第2歯科用シリコーン印象材を爪部分52に付け加えることにより製造されていることが好ましい。しかし、ネイリストは、第2歯科用シリコーン印象材以外のものを爪部分52に付け加えることにより、爪部分52を長くしてもかまわない。
The
次に、ネイリストが、第1ジェル60の上に、第1ジェル60よりセルフレベリング性の高い第2ジェル62を塗布する(図1のS26、図4(b))。この後に、ネイリストは、第2ジェル62を硬化させる。なお、第1ジェル60及び第2ジェル62の代わりに、アクリル(アクリリック)を用いてもかまわないことは勿論である。
Next, the nail technician applies the
次に、ネイリストは、第1ジェル60及び第2ジェル62の硬化により得られたつけ爪100を、指モデル50から剥離する(図1のS30)。そしてネイリストは、適宜つけ爪100の上に装飾を施す。図5(a)は、本実施形態のつけ爪100の製造方法により得られたつけ爪100の一例を示す写真である。かかるつけ爪100は、両面テープを用いて、図5(b)に示すように、お客様の指Fに固定される。ここで、爪が長くされた部分54を有しない指モデル50を用いて作成されたつけ爪100の場合には、膜厚0.13mm以上0.35未満の両面テープ(第1両面テープの一例)を用いて固定することが好ましい。また、爪が長くされた部分54を有する指モデル50を用いて作成されたつけ爪100の場合には、膜厚0.35mm以上0.55mm以下の両面テープ(第2両面テープの一例)を用いて固定することが好ましい。
Next, the nail technician peels off the
次に、本実施形態のつけ爪の製造方法の作用効果を記載する。 Next, the action and effect of the artificial nail manufacturing method of the present embodiment will be described.
ネイルサロンで装飾をお客様の爪に施してもらう場合と比較して、つけ爪を用いると、1日単位で簡単につけ外しが可能であるというメリットがある。特に、例えば医療従事者のように衛生面に気を使う職業についているお客様の場合は、自爪に直接装飾を施しても業務の際にそれを落とすこととなる。しかしつけ爪の場合には、より手軽に爪の装飾を楽しむことが出来る。 Compared to having your nails decorated at a nail salon, using artificial nails has the advantage that you can easily remove them on a daily basis. In particular, for customers who are in a hygiene-conscious profession, such as medical professionals, even if they directly decorate their nails, they will be dropped during work. However, in the case of artificial nails, you can enjoy the decoration of the nails more easily.
また、新型コロナウィルス感染症を含む感染症が流行した場合、お客様がネイルサロンに出かける際に、感染症に感染するリスクが生じる。しかしつけ爪の場合には、自宅内で爪の装飾を楽しむことが出来るため、感染症に感染するリスクを抑制することが出来る。 In addition, if an infectious disease including a new coronavirus infection is prevalent, there is a risk of being infected with the infectious disease when the customer goes to a nail salon. However, in the case of artificial nails, you can enjoy the decoration of the nails at home, so you can reduce the risk of getting an infectious disease.
一方で、つけ爪が使いにくい理由として、少なくとも三つの理由が挙げられる。一つ目は、通常つけ爪は世界共通の12サイズを有しているが、かかる12サイズのつけ爪では、お客様の爪にはフィットしない場合が多いからである。爪の形状には、少なくとも円形型爪、マムシ爪、噛み爪、台形型爪、そり爪及び深爪がある。そして、人が持っている10本指それぞれで、爪の形状は異なっている。そのため、爪の形状は大変バラエティに富んでいる。このような、バラエティに富んだ爪の形状を、上記の12サイズのつけ爪でカバーすることは極めて困難である。具体的には、例えば、つけ爪がお客様の爪からはみだしたり、逆にお客様の爪がつけ爪からはみ出したり、つけ爪の曲率とお客様の爪の曲率があわなかったりするという問題点があった。 On the other hand, there are at least three reasons why artificial nails are difficult to use. The first is that artificial nails usually have 12 sizes that are common in the world, but such 12 size artificial nails often do not fit your nails. Claw shapes include at least circular claws, beetle claws, biting claws, trapezoidal claws, sled claws and deep claws. The shape of the nail is different for each of the 10 fingers that a person has. Therefore, the shape of the nail is very diverse. It is extremely difficult to cover such a variety of nail shapes with the above-mentioned 12 size artificial nails. Specifically, for example, there was a problem that the artificial nails protruded from the customer's nails, the customer's nails protruded from the artificial nails, and the curvature of the artificial nails did not match the curvature of the customer's nails. ..
理由の二つ目は、世界共通の12サイズで作られたつけ爪では、デザインの数が少なく、お客様の好みに合わない場合が多いためである。 The second reason is that artificial nails made in 12 sizes, which are common throughout the world, have a small number of designs and often do not suit the tastes of customers.
理由の三つ目は、世界共通の12サイズで作られたつけ爪は多くの場合プラスチック製であり、十分にお客様の爪にフィットしない場合があるためである。 The third reason is that artificial nails made in 12 sizes, which are common throughout the world, are often made of plastic and may not fit your nails sufficiently.
そこで、本実施形態のつけ爪の製造方法では、お客様が、第1歯科用シリコーン印象材を保護具に詰める工程と、お客様が、保護具に詰められた第1歯科用シリコーン印象材を、保護具を介してお客様の爪に押し当てて、お客様の爪の爪型を製造する工程と、ネイリストが、爪型の中に第1歯科用シリコーン印象材より硬度の高い第2歯科用シリコーン印象材を詰めることにより、お客様の、爪部分を有する指モデルを製造する工程と、ネイリストが、爪部分の上に第1ジェルを塗布する工程と、ネイリストが、第1ジェルの上に、第1ジェルよりセルフレベリング性の高い第2ジェルを塗布する工程と、ネイリストが、第1ジェル及び第2ジェルの硬化により得られたつけ爪を、指モデルから剥離する工程と、を備える。 Therefore, in the method for manufacturing a nail nail of the present embodiment, the customer protects the first dental silicone impression material packed in the protective tool and the customer protects the first dental silicone impression material packed in the protective tool. The process of manufacturing the nail mold of the customer's nail by pressing it against the customer's nail through the tool, and the nail technician has a second dental silicone impression material that is harder than the first dental silicone impression material in the nail mold. The process of manufacturing the customer's finger model with the nail part by packing, the process of the nail technician applying the first gel on the nail part, and the process of the nail technician applying the first gel on the first gel. It comprises a step of applying a second gel having a higher self-leveling property, and a step of a nail technician peeling off the nails obtained by curing the first gel and the second gel from the finger model.
上記の製造方法によれば、お客様がお客様の爪の爪型を製造する。そして、ネイリストが、かかる爪型を用いて、つけ爪を製造する。爪型はごく小さいものであるため、お客様は容易に爪型をネイリストに送付可能である。そのため、お客様が感染症に感染するリスクは抑制される。一方、ネイリストはネイリストの技術を駆使し、お客様の好みにあわせてつけ爪に装飾をすることが可能である。 According to the above manufacturing method, the customer manufactures the nail mold of the customer's nail. Then, the nail technician manufactures artificial nails using such a nail mold. Since the nail mold is so small, the customer can easily send the nail mold to the nail technician. Therefore, the risk of the customer getting an infectious disease is reduced. On the other hand, the nail technician can make full use of the nail technician's technique to decorate the artificial nails according to the customer's taste.
より具体的には、お客様は、第1歯科用シリコーン印象材10を保護具20に詰める。そして、お客様が、保護具20に詰められた第1歯科用シリコーン印象材10を、保護具20を介してお客様の爪N1に押し当てて、お客様の爪N1の爪型30を製造する。
More specifically, the customer packs the first dental
歯科用シリコーン印象材は、精密に爪の形を再現した爪型の製造にすぐれている。特に、爪には細かい凹部と凸部があるが、特に細かい凹部を精密に再現できる点で優れている。細かい凹部には、凸部と異なり印象材が侵入していくことが求められるが、歯科用シリコーン印象材は凹部に侵入していきやすいためである。 Dental silicone impression materials are excellent in producing nail molds that accurately reproduce the shape of the nail. In particular, the nail has fine concave portions and convex portions, but it is particularly excellent in that the fine concave portions can be accurately reproduced. Unlike the convex portion, the impression material is required to invade the fine concave portion, but the dental silicone impression material easily invades the concave portion.
保護具20の大きさは、お客様の爪N1の大きさにあわせて、適宜選択する。
The size of the
一例としては、お客様が、お客様の爪N1に、保護具20から第1歯科用シリコーン印象材10がはみ出すように、第1歯科用シリコーン印象材10を押し当てることが好ましい。その理由は、「保護具20から第1歯科用シリコーン印象材10がはみ出していれば、爪N1は、第1歯科用シリコーン印象材10により十分に覆われている」といった簡単な判断基準を適用することができるためである。
As an example, it is preferable that the customer presses the first dental
特に、本実施形態のつけ爪の製造方法においては、作業に慣れているネイリストが爪型30を作成するのではなく、作業に慣れていないお客様が爪型30を作成する。よって、適切な大きさの保護具20を用いる点は重要である。
In particular, in the method for manufacturing artificial nails according to the present embodiment, the nail technician who is accustomed to the work does not create the
保護具20を介して第1歯科用シリコーン印象材10を押し当てると、直接第1歯科用シリコーン印象材10にお客様の手が触れないため、押し当てる力が強すぎたり弱すぎたりすることが少なくなる。
When the first dental
そして、ネイリストが、爪型30の中に第2歯科用シリコーン印象材40を詰める。これにより、爪部分52を有する指モデル50を製造する。ここで、第2歯科用シリコーン印象材40の硬度が第1歯科用シリコーン印象材10の硬度より高い理由は、後工程で指モデル50を削る場合、硬度が高い方が指モデル50の形状が崩れにくく、指モデル50の加工が容易であるためである。なお、ここからの製造工程は、ネイリストが担当するため、より品質のより高いつけ爪100を製造するがことできる。
Then, the nail technician fills the
次に、ネイリストが、爪部分52の上に、第1ジェル60を塗布する。次に、ネイリストが、第1ジェル60の上に、第1ジェル60よりセルフレベリング性の高い第2ジェル62を塗布する。第1ジェル60として、例えば、流動性が低く、表面張力があまり働かないジェルを用いる。このため、爪部分52の端の部分まで第1ジェル60を塗布しても、ジェルが縮んだりせずに、お客様の爪N1の端までサイズが良く合ったつけ爪100を製造できる。一方、例えば筆Bを使って第1ジェル60を塗布する場合には、筆の跡がそのまま残ってしまう。そこで、第1ジェル60を、人間の爪と同様の、「腹爪」「腹爪の上の中間爪」「中間爪の上の背爪」の三層構造になるように塗布することが好ましい。ここで「腹爪」については、第1ジェル60を爪部分52に対して縦方向に塗布して形成する。また、「中間爪」については、第1ジェル60を爪部分52に対して横方向に塗布して形成する。また、「背爪」については、第1ジェル60を爪部分52に対して縦方向に塗布して形成する。上記のように第1ジェル60を塗布した後に、よりセルフレベリング性の高い第2ジェルを用いてつけ爪の表面を滑らかにする。このようにジェルを用いて製造されたつけ爪は、例えばアクリリックのつけ爪と異なり、人の指の動きやしなりについていって変形するので、装着時に違和感が少なく、心地よく過ごすことが出来る。そのため、人の爪によくフィットするつけ爪の製造が可能となる。なお、一般的には、指モデル50の爪部分52に、先に柔らかいジェルを塗布し、その上に硬いジェルを塗布する。先に柔らかいジェルを塗布する理由は、爪との密着性があり、爪から浮き上がりにくく、剥がれにくいためである。しかし、爪部分52の端の部分にかかる柔らかいジェルを塗布すると、柔らかいジェルが縮んでしまい、製造されたつけ爪の端の部分が十分にフィットしない。
Next, the nail technician applies the
お客様がつけ爪100を固定する際には、膜厚0.13mm以上0.35mm以下の第1両面テープを用いて固定することが好ましい。また、お客様がつけ爪100を固定する際には、膜厚が0.35mmより厚く0.55mm以下の第2両面テープを用いて固定することもまた好ましい。膜厚0.13mm以上0.35mm以下の第1両面テープを用いる場合、比較的膜厚が薄いため、つけ爪100がより爪にフィットした感覚を得ることができる。また、膜厚が0.35mmより厚く0.55mm以下の第2両面テープを用いて固定する場合、よりしっかりとつけ爪100を固定することが出来るため、例えばつけ爪100を水で洗った場合であっても、つけ爪100が落下しにくくなる。なお、両面テープの膜厚が0.13mmより薄い場合、十分な粘着力でつけ爪100を固定することが難しくなるため、つけ爪100が手から落ちやすくなる。一方、両面テープの膜厚が0.55mmより厚い場合には、つけ爪100が十分に爪にフィットした感覚を得ることが難しくなる。
When the customer fixes the
本実施形態のつけ爪の製造方法によれば、人の爪によくフィットするつけ爪を、遠隔で製造することが出来るつけ爪の製造方法の提供が可能となる。 According to the method for manufacturing artificial nails according to the present embodiment, it is possible to provide a method for manufacturing artificial nails that can remotely manufacture artificial nails that fit well with human nails.
(実施例)
以下に、実施例を、比較例と対比しながらより詳細に説明する。
(Example)
Hereinafter, the examples will be described in more detail in comparison with the comparative examples.
(実施例1)
まず。お客様が、第1歯科用シリコーン印象材10としての、市販の2ペースト性の歯科用シリコーン印象材を、30秒で混ぜ合わせた上で、保護具20に詰めた。保護具20は、例えばプラスチック製のネイルチップであるが、これに限定されるものではない。
(Example 1)
first. The customer mixed a commercially available 2-paste dental silicone impression material as the first dental
次に、お客様が、保護具20に詰められた上記の歯科用シリコーン印象材を、保護具20を介して、保護具20から歯科用シリコーン印象材がはみ出すようにお客様の爪N1に押し当てて、お客様の爪の爪型30を製造した。
Next, the customer presses the above - mentioned dental silicone impression material packed in the
次に、ネイリストが、第2歯科用シリコーン印象材40としての、他の市販の2ペースト性の歯科用シリコーン印象材を爪型30の中に詰めて、お客様の、爪部分52を有する指モデル50を製造した。
Next, the nail technician packs another commercially available two-paste dental silicone impression material as the second dental silicone impression material in the
次に、ネイリストが、爪部分52の上に、第1ジェル60を塗布した。次に、ネイリストが、第1ジェル60を例えばUVライトで硬化させた後に、第1ジェル60の上に、第2ジェル62を塗布した。次に、ネイリストが、第2ジェル62を例えばUVライトで硬化させた。
Next, the nail technician applied the
次に、ネイリストが、第1ジェル60及び第2ジェル62の硬化により得られたつけ爪を、指モデル50から剥離した。
Next, the nail technician peeled off the artificial nails obtained by curing the
次に、お客様が、かかるつけ爪を、膜厚0.13mmの両面テープを用いて、お客様の爪N1に固定した。かかるつけ爪は、お客様の爪N1に大変良くフィットした。また、お客様が手を水で50回洗った後でも、つけ爪が落ちることはなかった。
Next, the customer fixed the artificial nail to the customer's nail N1 using a double - sided tape having a film thickness of 0.13 mm. Such artificial nails fit the customer's nail N1 very well. In addition, even after the customer washed his hands with
(実施例2)
実施例1と同様に作成されたつけ爪を、お客様が、膜厚0.28mmの両面テープを用いて、お客様の爪N1に固定した。かかるつけ爪は、お客様の爪N1に大変良くフィットした。また、お客様が手を水で50回洗った後でも、つけ爪が落ちることはなかった。
(Example 2)
The customer fixed the artificial nail created in the same manner as in Example 1 to the customer's nail N1 using a double-sided tape having a film thickness of 0.28 mm. Such artificial nails fit the customer's nail N1 very well. In addition, even after the customer washed his hands with
(実施例3)
実施例1と同様に作成されたつけ爪を、お客様が、膜厚0.34mmの両面テープを用いて、お客様の爪N1に固定した。かかるつけ爪は、お客様の爪N1に大変良くフィットした。また、お客様が手を水で50回洗った後でも、つけ爪が落ちることはなかった。
(Example 3)
The customer fixed the artificial nail created in the same manner as in Example 1 to the customer's nail N1 using a double-sided tape having a film thickness of 0.34 mm. Such artificial nails fit the customer's nail N1 very well. In addition, even after the customer washed his hands with
(実施例4)
実施例1と同様に作成されたつけ爪を、お客様が、膜厚0.35mmの両面テープを用いて、お客様の爪N1に固定した。かかるつけ爪は、お客様の爪N1に良くフィットした。また、お客様が手を水で100回洗った後でも、つけ爪が落ちることはなかった。
(Example 4)
The customer fixed the artificial nail created in the same manner as in Example 1 to the customer's nail N1 using a double-sided tape having a film thickness of 0.35 mm. Such artificial nails fit the customer's nail N1 well. In addition, even after the customer washed his
(実施例5)
実施例1と同様に作成されたつけ爪を、お客様が、膜厚0.46mmの両面テープを用いて、お客様の爪N1に固定した。かかるつけ爪は、お客様の爪N1に良くフィットした。また、お客様が手を水で100回洗った後でも、つけ爪が落ちることはなかった。
(Example 5)
The artificial nail created in the same manner as in Example 1 was fixed to the customer's nail N1 by the customer using a double-sided tape having a film thickness of 0.46 mm. Such artificial nails fit the customer's nail N1 well. In addition, even after the customer washed his
(実施例6)
実施例1と同様に作成されたつけ爪を、お客様が、膜厚0.50mmの両面テープを用いて、お客様の爪N1に固定した。かかるつけ爪は、お客様の爪N1に良くフィットした。また、お客様が手を水で100回洗った後でも、つけ爪が落ちることはなかった。
(Example 6)
The customer fixed the artificial nail created in the same manner as in Example 1 to the customer's nail N1 using a double-sided tape having a film thickness of 0.50 mm. Such artificial nails fit the customer's nail N1 well. In addition, even after the customer washed his
(実施例7)
実施例1と同様に作成されたつけ爪を、お客様が、膜厚0.55mmの両面テープを用いて、お客様の爪N1に固定した。かかるつけ爪は、お客様の爪N1に良くフィットした。また、お客様が手を水で100回洗った後でも、つけ爪が落ちることはなかった。
(Example 7)
The customer fixed the artificial nail created in the same manner as in Example 1 to the customer's nail N1 using a double-sided tape having a film thickness of 0.55 mm. Such artificial nails fit the customer's nail N1 well. In addition, even after the customer washed his
(実施例8)
ネイリストは、爪部分52の先端に、実施例1で用いた、第2歯科用シリコーン印象材40としての、他の市販の2ペースト性の歯科用シリコーン印象材を付け加えて、爪が長くされた部分54を製造した。その後に、ネイリストは、第1ジェル60の塗布を行った。その他は、実施例1と同様に、つけ爪の製造を行った。お客様は、かかるつけ爪を、膜厚0.28mmの両面テープを用いて、お客様の爪N1に固定した。かかるつけ爪は、お客様の爪N1に大変良くフィットした。また、お客様が手を水で50回洗った後でも、つけ爪が落ちることはなかった。
(Example 8)
The nail technician added another commercially available 2-paste dental silicone impression material as the second dental silicone impression material 40 used in Example 1 to the tip of the
(比較例1)
図6に、第2歯科用シリコーン印象材40を用いて作成した指モデル50と、市販の技師用シリコーン印象材を用いて作成した指モデル500を示した。指モデル50は、爪の先端の形がきれいにお客様の爪N1の形状を再現している。しかし、指モデル500は、爪の先端が欠けてしまい、お客様の爪N1の形状を再現していない。
(Comparative Example 1)
FIG. 6 shows a
このように、歯科用シリコーン印象材を用いると、お客様の爪N1の形状がきれいに再現できることがわかった。 As described above, it was found that the shape of the customer's nail N1 can be reproduced beautifully by using the dental silicone impression material.
(比較例2)
図7(a)に示すように、歯科用シリコーン印象材を保護具に詰めずに扁平状の形にして、1本1本お客様の指を押し当てて、図7(b)に示すように、一つの歯科用シリコーン印象材で5本分の爪型を製造した。
(Comparative Example 2)
As shown in FIG. 7 (a), the dental silicone impression material is not packed in the protective device but is formed into a flat shape, and the customer's finger is pressed one by one, as shown in FIG. 7 (b). , Five nail molds were manufactured with one dental silicone impression material.
しかしこのようにした場合、5本の指を交代に押し当てている間に、歯科用シリコーン印象材の硬化がはじまってしまうため、きれいに爪型を製造できないことがわかった。また、急いで次々に指を交代に押し当てようとすると、爪型が十分に硬くなる前に次の指を押し当てることになるため、きれいに爪型を製造できないことがわかった。また、1本の指を押し当てると、すでに製造された他の指の型が歪んでしまい、きれいに爪型を製造できないことがわかった。 However, in this case, it was found that the dental silicone impression material started to harden while the five fingers were alternately pressed, so that the nail mold could not be manufactured neatly. It was also found that if one tries to press the fingers one after another in a hurry, the next finger is pressed before the nail mold becomes sufficiently hard, so that the nail mold cannot be manufactured neatly. It was also found that when one finger was pressed against the mold, the molds of the other fingers that had already been manufactured were distorted, and the nail mold could not be manufactured neatly.
なお、これに対して本実施形態のつけ爪の製造方法においては、比較的少量の第1歯科用シリコーン印象材を、1本ずつ指に押し当てていくため、上記のような問題は生じない。 On the other hand, in the method for manufacturing artificial nails of the present embodiment, since a relatively small amount of the first dental silicone impression material is pressed against the finger one by one, the above-mentioned problem does not occur. ..
(比較例3)
図8に示すように、5本の指で一つの歯科用シリコーン印象材を握ることにより爪型301を製造した。そして、かかる爪型301を用いて、指モデル501を製造した。
(Comparative Example 3)
As shown in FIG. 8, the
しかしこのようにした場合、爪型301の製造中においてどうしても指先がぶれてしまい、うまく爪型301をつくることができないことがわかった。その理由は、それぞれの指は第1関節、第2関節及び第3関節を有しており、大変動きやすい状態にあり、指を静止させることが困難であるためである。
However, it was found that in this case, the fingertips inevitably shake during the manufacturing of the
なお、これに対して本実施形態のつけ爪の製造方法においては、保護具に第1歯科用シリコーン印象材10を詰めて、1本ずつ指に押し当てていく。そのため、たとえ爪型の製造中に指の関節が動いても、保護具及び第1歯科用シリコーン印象材は、その動きに容易についていく。そのため、きれいに爪型を製造することが出来る。
On the other hand, in the method for manufacturing artificial nails according to the present embodiment, the protective device is filled with the first dental
(比較例4)
図16に示すような、指の第1関節の部分を全体的に覆うような保護具302を用いて爪型を作成した。
(Comparative Example 4)
A nail mold was created using a
しかし、大きな量のシリコーン印象材を指にかぶせることになるため、素早く全ての指の爪型を製造することが難しい。そのため、安定して爪型を製造することが難しいことがわかった。 However, since a large amount of silicone impression material is put on the finger, it is difficult to quickly manufacture all fingernail molds. Therefore, it was found that it is difficult to stably manufacture a nail mold.
なお、これに対して本実施形態のつけ爪の製造方法においては、保護具20に第1歯科用シリコーン印象材10を詰めて、指に押し当てていく。この場合には、使用するシリコーン印象材の量が少なく、簡単に爪型を爪から外すことができるため、比較的素早く全ての指の爪型を製造することが出来る。
On the other hand, in the method for manufacturing artificial nails according to the present embodiment, the
(第2実施形態)
本実施形態のつけ爪の製造方法は、第2の人が、爪型の中に第1歯科用シリコーン印象材より硬度の高い第2歯科用シリコーン印象材を詰めることにより、第1の人の、爪部分を有する指モデルを製造する工程と、第2の人が、爪部分の上に第1ジェルを塗布する工程と、の間に、アクリルパウダー及びモノマーリキッドを爪部分の上に塗布する工程と、をさらに備える点で、第1実施形態のつけ爪の製造方法と異なっている。ここで、第1実施形態と重複する記載は省略する。
(Second Embodiment)
In the method for manufacturing artificial nails according to the present embodiment, a second person fills a nail mold with a second dental silicone impression material having a hardness higher than that of the first dental silicone impression material. Acrylic powder and monomer liquid are applied on the nail part between the process of manufacturing a finger model having a nail part and the step of applying the first gel on the nail part by a second person. It is different from the method for manufacturing artificial nails in the first embodiment in that it further includes a step. Here, the description overlapping with the first embodiment is omitted.
図10は、本実施形態のつけ爪の製造方法のフローチャートである。アクリルパウダー及びモノマーリキッドを混ぜ合わせて、爪部分52の上に塗布する(S23)。 FIG. 10 is a flowchart of the method for manufacturing artificial nails according to the present embodiment. Acrylic powder and monomer liquid are mixed and applied on the nail portion 52 (S23).
本実施形態のつけ爪の製造方法においても、人の爪によくフィットするつけ爪を、遠隔で製造することが出来るつけ爪の製造方法の提供が可能となる。 Also in the method for manufacturing artificial nails of the present embodiment, it is possible to provide a method for manufacturing artificial nails that can remotely manufacture artificial nails that fit well with human nails.
(第3実施形態)
本実施形態のつけ爪の製造方法は、第2の人が、爪型の中に第1歯科用シリコーン印象材より硬度の高い第2歯科用シリコーン印象材を詰めることにより、第1の人の、爪部分を有する指モデルを製造する工程の後で、第2の人が、爪部分の上に第1ジェルを塗布する工程の前に、第2の人が、指モデルを削る点で、第1及び第2実施形態のつけ爪の製造方法と異なっている。ここで、第1及び第2実施形態と重複する記載は省略する。
(Third Embodiment)
In the method for manufacturing artificial nails according to the present embodiment, the second person fills the nail mold with the second dental silicone impression material having a hardness higher than that of the first dental silicone impression material. In that the second person scrapes the finger model after the process of manufacturing the finger model with the nail part, and before the step of applying the first gel on the nail part by the second person. It is different from the manufacturing method of artificial nails of the first and second embodiments. Here, the description overlapping with the first and second embodiments is omitted.
図11は、本実施形態のつけ爪の製造方法のフローチャートである。ネイリストが、指モデル50を削っている(S22)。なお、図11のフローチャートでは、「ネイリストが、爪部分の長さを長くする工程(S20)」及び「ネイリストが、爪部分の上にアクリルパウダー・モノマーリキッドを塗布する工程(S23)」があわせて図示されている。しかし、(S20)及び(S23)は、なくてもかまわない工程である。 FIG. 11 is a flowchart of the method for manufacturing artificial nails according to the present embodiment. The manicurist is scraping the finger model 50 (S22). In the flowchart of FIG. 11, the "step of the nail technician increasing the length of the nail portion (S20)" and the "step of the nail technician applying the acrylic powder / monomer liquid on the nail portion (S23)" are combined. Is illustrated. However, (S20) and (S23) are steps that may not be necessary.
図12は、本実施形態のつけ爪の製造方法の適用に適した指モデル50の一例である。凹部53を有する爪部分52の場合、爪型30を取った後、所定の期間が経過するとかかる凹部53が爪先の方に移動してしまい、十分にフィットしなくなる。そこでこのような場合には、ネイリストが凹部53を削ってから第1ジェル60を塗布することが好ましい。
FIG. 12 is an example of a
本実施形態のつけ爪の製造方法においても、人の爪によくフィットするつけ爪を、遠隔で製造することが出来るつけ爪の製造方法の提供が可能となる。 Also in the method for manufacturing artificial nails of the present embodiment, it is possible to provide a method for manufacturing artificial nails that can remotely manufacture artificial nails that fit well with human nails.
なお、ネイリストは、通常、お客様の指Fを、ネイリストの親指と人差し指で保持しながら施術を行う。ここで、お客様の爪N1の端まできれいに第1ジェル60及び第2ジェル62を塗布するためには、お客様の爪N1の横のネイルウォール(サイドウォール)と呼ばれる肉を広げる、又は下げて、ネイルウォールに色やジェルが付かないようにすることが好ましい。さらに、つけ爪100も、お客様の爪N1の端までサイズをあわせて作らないと、つけ爪100をつけたときにつけ爪100の脇の下から自爪(お客様の爪N1)が出てしまう。ここで、指モデル50を使ってつけ爪100を作る場合には、お客様の指Fを目の前にしている場合と異なり、ネイルウォールを広げたり下げたりすることが出来ない。そのため、ネイリストが、指モデル50の凹部53を削る、又はつけ爪100を指モデルから剥離した後に、あとからつけ爪100を削ることがあり得る。特に、つけ爪100の外周部分が厚いと醜く自然でない。本来爪というものは、指の中から生えてきて、一部がネイルウォールの中に埋まっていることが自然であるためである。そのために、つけ爪100の外周部分を削ることがある。なお、削られるつけ爪100の部分は、つけ爪100の外周部分に限定されない。
In addition, the nail technician usually performs the treatment while holding the customer's finger F with the thumb and index finger of the nail technician. Here, in order to apply the first
本発明のいくつかの実施形態及び実施例を説明したが、これらの実施形態及び実施例は、例として提示したものであり、発明の範囲を限定することは意図していない。これら新規な実施形態は、その他の様々な形態で実施されることが可能であり、発明の要旨を逸脱しない範囲で、種々の省略、置き換え、変更を行うことが出来る。これら実施形態やその変形は、発明の範囲や要旨に含まれると共に、特許請求の範囲に記載された発明とその均等の範囲に含まれる。 Although some embodiments and examples of the present invention have been described, these embodiments and examples are presented as examples and are not intended to limit the scope of the invention. These novel embodiments can be implemented in various other embodiments, and various omissions, replacements, and changes can be made without departing from the gist of the invention. These embodiments and modifications thereof are included in the scope and gist of the invention, and are also included in the scope of the invention described in the claims and the equivalent scope thereof.
10 第1歯科用シリコーン印象材
12 第1ペースト
14 第2ペースト
20 保護具(台)
30 爪型
40 第2歯科用シリコーン印象材
42 第3ペースト
44 第4ペースト
50 指モデル
52 爪部分
53 凹部
54 爪が長くされた部分
60 第1ジェル
62 第2ジェル
100 つけ爪
B 筆
F お客様の指
F1 お客様の指(右手親指)
F2 お客様の指(左手親指)
N1 お客様の爪
H1 お客様の手
H2 ネイリストの手
10 1st Dental
30 Nail type 40 2nd dental
F 2 Customer's finger (left thumb)
N 1 Customer's nail H 1 Customer's hand H 2 Nail technician's hand
Claims (9)
前記第1の人が、前記保護具に詰められた前記第1歯科用シリコーン印象材を、前記保護具を介して前記第1の人の爪に押し当てて、前記第1の人の前記爪の爪型を製造する工程と、
第2の人が、前記爪型の中に前記第1歯科用シリコーン印象材より硬度の高い第2歯科用シリコーン印象材を詰めることにより、前記第1の人の、爪部分を有する指モデルを製造する工程と、
前記第2の人が、前記爪部分の上に第1ジェルを塗布する工程と、
前記第2の人が、前記第1ジェルの上に、前記第1ジェルよりセルフレベリング性の高い第2ジェルを塗布する工程と、
前記第2の人が、前記第1ジェル及び前記第2ジェルの硬化により得られたつけ爪を、前記指モデルから剥離する工程と、
を備えるつけ爪の製造方法。 The process by which the first person packs the first dental silicone impression material into the protective equipment,
The first person presses the first dental silicone impression material packed in the protective device against the nail of the first person through the protective device, and the nail of the first person. The process of manufacturing the nail mold and
A second person fills the nail mold with a second dental silicone impression material having a hardness higher than that of the first dental silicone impression material, thereby creating a finger model of the first person having a nail portion. Manufacturing process and
The step of the second person applying the first gel on the nail portion,
A step in which the second person applies a second gel having a higher self-leveling property than the first gel onto the first gel.
A step in which the second person peels off the artificial nails obtained by curing the first gel and the second gel from the finger model.
A method of manufacturing artificial nails.
請求項1記載のつけ爪の製造方法。 The first person presses the first person's nail against the nail so that the first dental silicone impression material protrudes from the protective device.
The method for manufacturing artificial nails according to claim 1.
前記第2の人が、前記爪部分の上に前記第1ジェルを塗布する工程の前に、
前記第2の人が、前記爪部分の長さを長くする工程と、
をさらに備える請求項1又は請求項2記載のつけ爪の製造方法。 The second person has the nail portion of the first person by filling the nail mold with the second dental silicone impression material having a hardness higher than that of the first dental silicone impression material. After the process of manufacturing the finger model,
Before the step of the second person applying the first gel on the nail portion,
The step of the second person increasing the length of the nail portion,
The method for manufacturing artificial nails according to claim 1 or 2, further comprising.
前記第2の人が、前記爪部分の上に前記第1ジェルを塗布する工程の前に、
アクリルパウダー及びモノマーリキッドを混ぜ合わせて前記爪部分の上に塗布する工程と、
をさらに備える請求項1乃至請求項4いずれか一項記載のつけ爪の製造方法。 The second person has the nail portion of the first person by filling the nail mold with the second dental silicone impression material having a hardness higher than that of the first dental silicone impression material. After the process of manufacturing the finger model,
Before the step of the second person applying the first gel on the nail portion,
The process of mixing acrylic powder and monomer liquid and applying it on the nail part,
The method for manufacturing artificial nails according to any one of claims 1 to 4, further comprising.
前記第1の人が、前記つけ爪を、前記第1の人の前記爪に、膜厚0.13mm以上0.35mm以下の第1両面テープを用いて固定する工程と、
をさらに備える請求項1乃至請求項5いずれか一項記載のつけ爪の製造方法。 After the step of the second person peeling the artificial nail obtained by curing the first gel and the second gel from the finger model,
A step in which the first person fixes the artificial nail to the nail of the first person using a first double-sided tape having a film thickness of 0.13 mm or more and 0.35 mm or less.
The method for manufacturing artificial nails according to any one of claims 1 to 5, further comprising.
前記第1の人が、前記つけ爪を、前記第1の人の前記爪に、膜厚0.35mmより厚く0.55mm以下の第2両面テープを用いて固定する工程と、
をさらに備える請求項1乃至請求項5いずれか一項記載のつけ爪の製造方法。 After the step of the second person peeling the artificial nail obtained by curing the first gel and the second gel from the finger model,
A step in which the first person fixes the artificial nail to the nail of the first person using a second double-sided tape having a thickness of more than 0.35 mm and a thickness of 0.55 mm or less.
The method for manufacturing artificial nails according to any one of claims 1 to 5, further comprising.
前記第2の人が、前記爪部分の上に前記第1ジェルを塗布する工程の前に、
前記第2の人が、前記指モデルを削る工程と、
をさらに備える請求項1又は請求項2記載のつけ爪の製造方法。 The second person has the nail portion of the first person by filling the nail mold with the second dental silicone impression material having a hardness higher than that of the first dental silicone impression material. After the process of manufacturing the finger model,
Before the step of the second person applying the first gel on the nail portion,
The process in which the second person scrapes the finger model,
The method for manufacturing artificial nails according to claim 1 or 2, further comprising.
前記第1の人が、前記つけ爪を、前記第1の人の前記爪に、膜厚0.41mmより厚く0.55mm以下の第2両面テープを用いて固定する工程と、
をさらに備える請求項8記載のつけ爪の製造方法。 After the step of the second person peeling the artificial nail obtained by curing the first gel and the second gel from the finger model,
A step in which the first person fixes the artificial nail to the nail of the first person using a second double-sided tape having a film thickness of more than 0.41 mm and a thickness of 0.55 mm or less.
8. The method for manufacturing artificial nails according to claim 8.