JP2021165527A - Block mat, manufacturing method of block mat, and revetment structure - Google Patents

Block mat, manufacturing method of block mat, and revetment structure Download PDF

Info

Publication number
JP2021165527A
JP2021165527A JP2021118314A JP2021118314A JP2021165527A JP 2021165527 A JP2021165527 A JP 2021165527A JP 2021118314 A JP2021118314 A JP 2021118314A JP 2021118314 A JP2021118314 A JP 2021118314A JP 2021165527 A JP2021165527 A JP 2021165527A
Authority
JP
Japan
Prior art keywords
sheet
adhesive
block
water
block mat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2021118314A
Other languages
Japanese (ja)
Other versions
JP7264947B2 (en
Inventor
卓也 明永
Takuya Akinaga
昭徳 間
Akinori Hazama
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Chemical Infratec Co Ltd
Original Assignee
Mitsubishi Chemical Infratec Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Chemical Infratec Co Ltd filed Critical Mitsubishi Chemical Infratec Co Ltd
Priority to JP2021118314A priority Critical patent/JP7264947B2/en
Publication of JP2021165527A publication Critical patent/JP2021165527A/en
Application granted granted Critical
Publication of JP7264947B2 publication Critical patent/JP7264947B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

To provide a block mat that can prevent water from passing through and that can be efficiently manufactured by using hardened concrete blocks.SOLUTION: A block mat has a plurality of concrete blocks that is fixed on a flexible sheet. The sheet includes a base material sheet on the concrete block side, and an impervious sheet on the opposite side to the concrete blocks. The base material sheet is a porous sheet. The concrete blocks, the base material sheet, and the impervious sheet are integrated by using an adhesive. Viscosity of the adhesive at 23°C is equal to or higher than 50 mPa s and lower than 100,000 mPa s.SELECTED DRAWING: Figure 2

Description

本願は、ブロックマット、該ブロックマットの製造方法、および、該ブロックマットを用いた護岸構造に関する。 The present application relates to a block mat, a method for producing the block mat, and a revetment structure using the block mat.

河川、ダム、遊水池などの法面の保護を目的として、従来、ブロックマットという浸食防止材が用いられている。ブロックマットとは、多数のコンクリートブロックを合成繊維不織布などからなる基材シートに一体化させたものである。ブロックマットは施工が容易であり、耐久性に優れるという特長を有する。 Conventionally, an erosion prevention material called a block mat has been used for the purpose of protecting slopes of rivers, dams, retarding basins, etc. The block mat is a combination of a large number of concrete blocks into a base sheet made of a synthetic fiber non-woven fabric or the like. The block mat is easy to install and has excellent durability.

河川などの法面を構成する堤防は、本来、水を透過し難い土(粘土など)によって造られるべきである。したがって、従来のブロックマットには遮水性を備えさせていないものが多かった。しかしながら、河川などの法面が必ずしも水を透過し難い土で構成されているとは限らず、水を通す虞がある砂などで構成されている場合もあった。堤防が砂などで構成されていると、増水時に最悪の場合は破堤する虞がある。しかしながら、堤防を構成する砂を水を透過し難い土に入れ替えることは困難である。 Embankments that make up slopes such as rivers should be made of soil (clay, etc.) that is impervious to water. Therefore, many conventional block mats are not provided with water impermeability. However, the slope of a river or the like is not always composed of soil that is difficult for water to permeate, and in some cases, it is composed of sand or the like that may allow water to pass through. If the embankment is made of sand or the like, there is a risk of the embankment breaking in the worst case when the water level rises. However, it is difficult to replace the sand that constitutes the embankment with soil that is difficult for water to permeate.

そこで、従来、河川などの法面に浸水することを防止する目的で、遮水性を有するシート(遮水シート)によって法面を覆うことが行われている。また、単に遮水シートを敷設しただけでは耐久性に問題があるため、遮水シート上にブロックを設置することも行われている。特許文献1には、シート材にブロックを列設固定したブロックマット層と、シート材の下に不透水性シート層を備える遮草性地表侵食防止構体が記載されている。また、特許文献2には、遮水層を中間層に有する基材シート上に複数のコンクリートブロックが固定されたブロックマットが記載されている。 Therefore, conventionally, in order to prevent water from entering the slope of a river or the like, the slope is covered with a water-impervious sheet (water-impervious sheet). In addition, since there is a problem in durability simply by laying a water-impervious sheet, a block is also installed on the water-impervious sheet. Patent Document 1 describes a weed-shielding surface erosion prevention structure provided with a block mat layer in which blocks are arranged and fixed to a sheet material and an impermeable sheet layer under the sheet material. Further, Patent Document 2 describes a block mat in which a plurality of concrete blocks are fixed on a base sheet having an impermeable layer as an intermediate layer.

特開昭56−89611号公報Japanese Unexamined Patent Publication No. 56-89611 特許5451919号公報Japanese Patent No. 5451919

しかしながら、特許文献1、2の技術では、複数のブロックと基材シートとを未硬化のコンクリートを基材シートに含浸させて、硬化させることで固定しているため、コンクリートが硬化するまでに時間がかかり製造効率が悪いという課題があった。また、未硬化のコンクリートブロックに基材シートを接着させる必要があるため、既存の硬化したコンクリートブロックを使用できない。よって、既存の硬化したコンクリートブロックを使用してブロックマットを製造したいという要望があった。
以上より、本願では、水の透過を抑制でき、かつ、硬化済みのコンクリートブロックを使用して、効率よく製造できるブロックマットを提供することを課題とする。
However, in the techniques of Patent Documents 1 and 2, since the plurality of blocks and the base sheet are fixed by impregnating the base sheet with uncured concrete and hardening the base sheet, it takes time for the concrete to harden. There was a problem that the manufacturing efficiency was poor. In addition, the existing hardened concrete block cannot be used because the base sheet needs to be adhered to the uncured concrete block. Therefore, there has been a request to manufacture a block mat using an existing hardened concrete block.
Based on the above, it is an object of the present application to provide a block mat that can suppress the permeation of water and can be efficiently manufactured by using a hardened concrete block.

上記課題を解決すべく、本願は、第1の形態として、可撓性を有するシートに複数のコンクリートブロックが固定されたブロックマットであって、
前記シートが、前記コンクリートブロック側の基材シートと前記コンクリートブロックとは反対側の遮水シートとを備え、
前記基材シートが多孔性シートであり、
前記コンクリートブロック、前記基材シート、および、前記遮水シートが接着剤により一体化されている、ブロックマットを開示する。
In order to solve the above problems, the present application is, as a first embodiment, a block mat in which a plurality of concrete blocks are fixed to a flexible sheet.
The sheet includes a base sheet on the concrete block side and a water-impervious sheet on the opposite side of the concrete block.
The base sheet is a porous sheet, and the base sheet is a porous sheet.
Disclosed is a block mat in which the concrete block, the base sheet, and the water-impervious sheet are integrated by an adhesive.

第1の形態のブロックマットにおいて、前記コンクリートブロックと前記基材シートとの間、および、前記基材シートと前記遮水シートとの間に、前記接着剤からなる接着層を備えることが好ましい。 In the block mat of the first embodiment, it is preferable to provide an adhesive layer made of the adhesive between the concrete block and the base sheet, and between the base sheet and the water-impervious sheet.

第1の形態のブロックマットにおいて、前記接着剤の23℃における粘度が、50mPa・s以上100,000mPa・s未満であることが好ましい。 In the block mat of the first embodiment, the viscosity of the adhesive at 23 ° C. is preferably 50 mPa · s or more and less than 100,000 mPa · s.

第1の形態のブロックマットにおいて、前記接着剤が、接着性樹脂およびフィラーを含むことが好ましい。 In the block mat of the first form, it is preferable that the adhesive contains an adhesive resin and a filler.

第1の形態のブロックマットにおいて、前記フィラーの含有量が、接着性樹脂100質量部に対して、1〜450質量部であることが好ましい。 In the block mat of the first embodiment, the content of the filler is preferably 1 to 450 parts by mass with respect to 100 parts by mass of the adhesive resin.

第1の形態のブロックマットにおいて、前記コンクリートブロックと前記基材シートとの間の剥離強度が、30N/50mm以上であることが好ましい。 In the block mat of the first form, the peel strength between the concrete block and the base material sheet is preferably 30 N / 50 mm or more.

第1の形態のブロックマットにおいて、前記遮水シートにおける、基材シート側とは反対側に、凹凸が形成されていることが好ましい。 In the block mat of the first form, it is preferable that unevenness is formed on the side of the water-impervious sheet opposite to the base sheet side.

本願は、第2の形態として、遮水シートと基材シートと複数のコンクリートブロックとを、接着剤を用いて一体化させることを特徴とする、第1の形態のブロックマットの製造方法を開示する。 The present application discloses, as a second form, a method for manufacturing a block mat of the first form, which comprises integrating a water-impervious sheet, a base sheet, and a plurality of concrete blocks with an adhesive. do.

第2の形態の製造方法において、複数のコンクリートブロックの底面に接着剤を塗布する工程、前記コンクリートブロックの接着剤を塗布した面に基材シートを設置する工程、前記基材シートの上に遮水シートを設置する工程、および、前記コンクリートブロックと基材シートと遮水シートとを接着する工程、を備えることが好ましい。 In the manufacturing method of the second embodiment, a step of applying an adhesive to the bottom surface of a plurality of concrete blocks, a step of installing a base sheet on the surface of the concrete block to which the adhesive is applied, a step of shielding the base sheet on the base sheet. It is preferable to include a step of installing the water sheet and a step of adhering the concrete block, the base material sheet, and the impermeable sheet.

本願は、第3の形態として、第1の形態のブロックマットが敷設された護岸構造を開示する。 The present application discloses, as a third form, a revetment structure in which the block mat of the first form is laid.

本開示のブロックマットは、硬化済みのコンクリートブロックを使用して、効率よく製造することができ、また、遮水シートを備えているので、水の透過を抑制できる。 The block mat of the present disclosure can be efficiently manufactured by using a hardened concrete block, and also has a water-impervious sheet, so that water permeation can be suppressed.

図1は、本開示のブロックマット100の平面図である。FIG. 1 is a plan view of the block mat 100 of the present disclosure. 図2は、図1に示したII−II線に沿ったブロックマット100の断面図である。FIG. 2 is a cross-sectional view of the block mat 100 along the line II-II shown in FIG. 図3は、堤内地側法面を保護した場合の護岸構造200の模式図である。FIG. 3 is a schematic view of the revetment structure 200 when the slope on the land side of the embankment is protected.

[ブロックマット]
本開示のブロックマットは、可撓性を有するシートに複数のコンクリートブロックが固定されたブロックマットである。
図1は、ブロックマット100を概略的に示す平面図である。図2は図1に示したII−II線に沿ったブロックマット100の断面を概略的に示す断面図である。
[Block mat]
The block mat of the present disclosure is a block mat in which a plurality of concrete blocks are fixed to a flexible sheet.
FIG. 1 is a plan view schematically showing the block mat 100. FIG. 2 is a cross-sectional view schematically showing a cross section of the block mat 100 along the line II-II shown in FIG.

図1および図2に示したように、ブロックマット100はシート10と該シート10に固定された複数のコンクリートブロック20、20・・・とを備えている。 As shown in FIGS. 1 and 2, the block mat 100 includes a sheet 10 and a plurality of concrete blocks 20, 20, ... Fixed to the sheet 10.

<コンクリートブロック>
コンクリートブロック20、20・・・としては、従来のブロックマットに用いられていたものを特に限定することなく用いることができる。コンクリートブロック20の大きさは特に限定されず、通常、平面視(図1に現れる面)における一辺が15cm以上50cm以下程度であり、高さが4cm以上30cm以下程度である。
また、コンクリートブロック20、20・・・の配列パターンは特に限定されない。ただし、ブロックマット100に可撓性を備えさせるため、隣接するコンクリートブロック20同士の間は5mm以上の隙間を設けることが好ましい。
<Concrete block>
As the concrete blocks 20, 20 ..., Those used for the conventional block mat can be used without particular limitation. The size of the concrete block 20 is not particularly limited, and usually, one side in a plan view (the surface appearing in FIG. 1) is about 15 cm or more and 50 cm or less, and the height is about 4 cm or more and 30 cm or less.
Further, the arrangement pattern of the concrete blocks 20, 20 ... Is not particularly limited. However, in order to make the block mat 100 flexible, it is preferable to provide a gap of 5 mm or more between adjacent concrete blocks 20.

<シート10>
シート10は可撓性を有する積層シートであって、後述する基材シート12と遮水シート14とを備えている。
シート10の大きさは特に限定されないが、通常、幅(図1の左右方向の長さ)は40cm以上2m以下であることが好ましく、長さ(図1の上下方向の長さ)は1m以上10m以下であることが好ましい。ブロックマット100を敷設する際に、ブロックマット10を吊り上げる器具を取り付ける(挟む)ためにシート10の長手方向両端部にはコンクリートブロック20、20・・・が備えられていない部分(挟み代)10a、10bが設けられていることが好ましい。挟み代10a、10bの幅Wa、Wbは、上記器具を取り付けられる大きさであれば特に限定されないが、例えば、400mm以上600mm以下とすることができる。
<Sheet 10>
The sheet 10 is a flexible laminated sheet, and includes a base sheet 12 and a water-impervious sheet 14, which will be described later.
The size of the sheet 10 is not particularly limited, but usually, the width (length in the horizontal direction in FIG. 1) is preferably 40 cm or more and 2 m or less, and the length (length in the vertical direction in FIG. 1) is 1 m or more. It is preferably 10 m or less. When laying the block mat 100, a portion (pinching allowance) 10a in which concrete blocks 20, 20 ... Are not provided at both ends in the longitudinal direction of the sheet 10 for attaching (sandwiching) an instrument for lifting the block mat 10. It is preferable that 10b is provided. The widths Wa and Wb of the sandwiching allowances 10a and 10b are not particularly limited as long as they have a size to which the above-mentioned instrument can be attached, but can be, for example, 400 mm or more and 600 mm or less.

また、後に説明するようにして複数のブロックマット100を幅方向(図1の左右方向)に並べて敷設する場合、シート10の一部を重ねて敷設することが好ましい。したがって、シート10の幅方向片側端部にはコンクリートブロック20、20・・・が備えられていない部分(重ね代)10cが設けられていることが好ましい。重ね代10cの幅Wcは特に限定されないが、例えば、200mm以上400mm以下とすることができる。 Further, when a plurality of block mats 100 are laid side by side in the width direction (left-right direction in FIG. 1) as described later, it is preferable to lay a part of the sheets 10 in an overlapping manner. Therefore, it is preferable that a portion (overlapping allowance) 10c not provided with concrete blocks 20, 20 ... Is provided at one end of the sheet 10 in the width direction. The width Wc of the stacking allowance 10c is not particularly limited, but can be, for example, 200 mm or more and 400 mm or less.

(基材シート12)
シート10は、コンクリートブロック20、20・・・側に基材シート12を備えている。基材シート12としては、多孔性のシートであって、後に説明する接着剤を一方の面から他方の面に浸透させることができるシートであって、かつ、基材として所定の強度を有するシートであれば、特に限定されず使用可能である。基材シート12としては、例えば、織布または不織布を用いることができる。
(Base sheet 12)
The sheet 10 includes a base sheet 12 on the concrete blocks 20, 20 ... Sides. The base material sheet 12 is a porous sheet that allows the adhesive described later to permeate from one surface to the other surface, and has a predetermined strength as the base material. If so, it can be used without particular limitation. As the base sheet 12, for example, a woven fabric or a non-woven fabric can be used.

織布としては、ポリエチレン、ポリプロピレン、ポリエステル等の合成繊維からなる職布(いわゆるフィルタークロス)を用いることが可能である。
また、不織布としては、例えば、ポリプロピレンやポリエチレン、ポリエステル、ナイロン、ビニロン、アクリル、ポリウレタン等の合成繊維による短繊維などを含む不織布を用いることができる。ポリプロピレン又はポリエチレンが耐薬品性に優れていることから好ましい。地盤改良材等にアルカリ性の物質が含まれていることがあるからである。
As the woven fabric, it is possible to use a work cloth (so-called filter cloth) made of synthetic fibers such as polyethylene, polypropylene, and polyester.
Further, as the non-woven fabric, for example, a non-woven fabric containing short fibers made of synthetic fibers such as polypropylene, polyethylene, polyester, nylon, vinylon, acrylic and polyurethane can be used. Polypropylene or polyethylene is preferable because it has excellent chemical resistance. This is because the ground improvement material may contain alkaline substances.

なお、ブロックマット100を吊り上げたりして取り扱うことが可能となるように、基材シート12は、適正な引張強度を備えていることが好ましい。かかる観点から、基材シート12は不織布に補強用の芯材となる織布を挿入して構成されることが好ましい。このような構造の基材シート12は、例えば、抄造機で不織布を抄造する際に織布あるいは長繊維を包み込むことにより不織布と織布あるいは長繊維とを一体化し、ニードルパンチ加工を施して補強することによって製造できる。 The base sheet 12 preferably has an appropriate tensile strength so that the block mat 100 can be lifted and handled. From this point of view, it is preferable that the base material sheet 12 is formed by inserting a woven fabric as a core material for reinforcement into the non-woven fabric. The base material sheet 12 having such a structure is reinforced by integrating the non-woven fabric and the woven fabric or the long fibers by wrapping the woven fabric or the long fibers when the non-woven fabric is made by a paper machine, and performing needle punching. Can be manufactured by

基材シート12の厚さは特に限定されないが、例えば2mm以上10mm以下程度とすることができる。基材シート12の厚さを2mm以上とすることによって、引張強度を確保しやすくなる。一方、基材シート12の厚さを10mm以下とすることによって、後述するように接着剤によってコンクリートブロック、基材シートおよび遮水シートを一体化する際に、接着剤が基材シートの一方の面から他方の面へと染み出し易くなる。 The thickness of the base sheet 12 is not particularly limited, but can be, for example, about 2 mm or more and 10 mm or less. By setting the thickness of the base sheet 12 to 2 mm or more, it becomes easy to secure the tensile strength. On the other hand, by setting the thickness of the base sheet 12 to 10 mm or less, when the concrete block, the base sheet and the water-impervious sheet are integrated with the adhesive as described later, the adhesive is one of the base sheets. It becomes easy to seep from one surface to the other surface.

また、基材シート12の目付け量は、例えばポリプロピレンの場合は100〜900g/mのものを使用することができる。さらに、ポリエステル長繊維などを不織布の縦方向に所定の目付け量で配列させて補強することができ、その際の目付け量は例えば70〜210g/mである。 Further, as the basis weight of the base sheet 12, for example, in the case of polypropylene, one of 100 to 900 g / m 2 can be used. Further, polyester filaments and the like can be arranged and reinforced in the longitudinal direction of the nonwoven fabric with a predetermined basis weight, and the basis weight at that time is, for example, 70 to 210 g / m 2 .

基材シート12の繊度としては、3.3dtex以上20.0dtex以下のものが好ましく、異なる繊度の短繊維を混合して用いることもできる。
3.3dtex以上6.0dtex未満の繊度の細かい繊維を用いることで、低目付け量であっても繊維同士が絡み合いやすく不織布が透けて見えるのを防止し、費用の低減が図れる。
6.0dtex以上、好ましくは10.0dtex以上の繊度の太い繊維を用いることで、繊維が起立しやすく、起立した繊維と繊維の間に接着剤が入り込むことにより、コンクリートブロックと基材シートとの接着性を高めることができる。6.0dtex以上の繊度の太い繊維の混合率は15重量%以上であることが好ましく、30重量%以上であることがさらに好ましい。
The fineness of the base sheet 12 is preferably 3.3 dtex or more and 20.0 dtex or less, and short fibers having different fineness can be mixed and used.
By using fine fibers having a fineness of 3.3 dtex or more and less than 6.0 dtex, the fibers are easily entangled with each other even with a low basis weight, and the non-woven fabric is prevented from being seen through, and the cost can be reduced.
By using thick fibers having a fineness of 6.0 dtex or more, preferably 10.0 dtex or more, the fibers can easily stand up, and the adhesive can enter between the standing fibers, so that the concrete block and the base sheet can be separated from each other. Adhesiveness can be improved. The mixing ratio of thick fibers having a fineness of 6.0 dtex or more is preferably 15% by weight or more, and more preferably 30% by weight or more.

(遮水シート14)
シート10は、コンクリートブロック20、20・・・とは反対側に遮水シート14を備えている。シート10が遮水シート14を備えていることによって、ブロックマット100を法面等に敷設したとき、該法面等に浸水することを抑制できる。
(Immersion sheet 14)
The sheet 10 is provided with a water-impervious sheet 14 on the side opposite to the concrete blocks 20, 20 ... Since the sheet 10 is provided with the water-impervious sheet 14, when the block mat 100 is laid on a slope or the like, it is possible to prevent water from entering the slope or the like.

遮水シート14を構成する材料は、遮水性を有するものであれば特に限定されない。遮水シート14を構成する材料の具体例としては、エチレン−酢酸ビニル共重合樹脂、ゴム、塩化ビニル樹脂、ポリオレフィン系樹脂などを挙げることができる。 The material constituting the water-impervious sheet 14 is not particularly limited as long as it has water-impervious properties. Specific examples of the material constituting the water-impervious sheet 14 include ethylene-vinyl acetate copolymer resin, rubber, vinyl chloride resin, and polyolefin resin.

遮水シート14の目付量は特に限定されないが、例えば、目付量が200g/m以上500g/m以下となるように樹脂で構成されていることが好ましい。遮水シート14を構成する樹脂の目付量を200g/m以上とすることによって、ブロックマット100を敷設した際に小石などによって遮水シート14に孔が開くことを防止しやすくなる。
一方、遮水シート14を構成する樹脂の目付量を500g/m以下とすることによって、必要以上にシート10が厚くなることによるブロックマット100の質量増加を防ぐことができる。
遮水シート14の厚さは特に限定されないが、例えば、厚さが0.15mm以上2.0mm以下となるように構成することが好ましい。
さらに、遮水シート14は基材シート12側の面に厚さ1.0mm〜10.0mm程度の保護層を設けてもよい。保護層は、フィルム、シート、織布、不織布等から選択でき、特に不織布が好ましく用いられる。
The basis weight of the water-impervious sheet 14 is not particularly limited, but for example, it is preferably composed of a resin so that the basis weight is 200 g / m 2 or more and 500 g / m 2 or less. By setting the basis weight of the resin constituting the water-impervious sheet 14 to 200 g / m 2 or more, it becomes easy to prevent holes from being opened in the water-impervious sheet 14 due to pebbles or the like when the block mat 100 is laid.
On the other hand, by setting the basis weight of the resin constituting the water-impervious sheet 14 to 500 g / m 2 or less, it is possible to prevent an increase in the mass of the block mat 100 due to the sheet 10 becoming thicker than necessary.
The thickness of the water-impervious sheet 14 is not particularly limited, but it is preferable that the thickness is 0.15 mm or more and 2.0 mm or less, for example.
Further, the water-impervious sheet 14 may be provided with a protective layer having a thickness of about 1.0 mm to 10.0 mm on the surface on the base sheet 12 side. The protective layer can be selected from films, sheets, woven fabrics, non-woven fabrics and the like, and non-woven fabrics are particularly preferably used.

遮水シート14における、基材シート12側とは反対側に、凹凸が形成されていることが好ましい。これにより、ブロックマット100の法面側の静止摩擦係数が大きくなるため、ブロックマット100を法面に敷設したときにブロックマット100が滑り落ちることを抑制でき、ブロックマットの施行が容易となる。凹凸の形成方法は、特に限定されず、公知の方法にて凹凸が付与された遮水シートを使用することができる。 It is preferable that the water-impervious sheet 14 has irregularities formed on the side opposite to the base sheet 12 side. As a result, the coefficient of static friction on the slope side of the block mat 100 becomes large, so that the block mat 100 can be prevented from slipping down when the block mat 100 is laid on the slope, and the block mat can be easily applied. The method of forming the unevenness is not particularly limited, and a water-impervious sheet to which the unevenness is imparted by a known method can be used.

本開示のブロックマットは、例えば、市販されている遮水シート14を用いて製造することが可能であるので、法面の状態に応じて、種々の、厚み、目付け量の遮水シートを選択でき、また、どの程度の滑り止め効果が必要かによって、種々の凹凸形状を有する遮水シートから最適なものを選択して採用できる。ブロックマットを敷設する現場は多種多様であり、一つとして同じ現場は存在しない。本開示のブロックマット100は、種々のコンクリートブロック、種々の基材シート、および、種々の遮水シートを組み合わせて、小ロット多品種のブロックマットを提供することができるので、その現場に適したブロックマットを容易に提供可能である。 Since the block mat of the present disclosure can be manufactured using, for example, a commercially available water-impervious sheet 14, a various thickness and basis weight of the water-impervious sheet can be selected according to the condition of the slope. Also, depending on how much anti-slip effect is required, the optimum one can be selected and adopted from the water-impervious sheets having various uneven shapes. There are many different sites for laying block mats, and no single site is the same. The block mat 100 of the present disclosure is suitable for the site because it can provide a small lot and a wide variety of block mats by combining various concrete blocks, various base sheets, and various water-impervious sheets. A block mat can be easily provided.

本開示のブロックマット100によれば、シート10が遮水シート14を備えていることによって、従来のブロックマットのように別に遮水性を有するシートを敷設する必要がなく、施工工程を簡略化することができる。また、ブロックマット100によれば、遮水シート14がシート10の一部となっているので、遮水性を有するシートの上にブロックマットを敷設していた従来の工法のように遮水性を有するシートとブロックマットとの間で滑るということがないので、従来のブロックマットよりも法面への敷設が容易になる。 According to the block mat 100 of the present disclosure, since the sheet 10 is provided with the water-impervious sheet 14, it is not necessary to lay a separate sheet having a water-impervious property unlike the conventional block mat, and the construction process is simplified. be able to. Further, according to the block mat 100, since the water-impervious sheet 14 is a part of the sheet 10, it has water-impervious property as in the conventional construction method in which the block mat is laid on the sheet having water-impervious property. Since it does not slip between the sheet and the block mat, it is easier to lay on the slope than the conventional block mat.

なお、ブロックマット100は完全な防水を目的とするものではない。後述するようにして複数のブロックマット100を重ねて配置したときの重ね合わせられた部分や、後述するようにしてブロックマット100を固定するためにアンカーピンを打ち込んだ部分などから、多少は水が漏れると考えられる。このように多少は水が漏れる形態とすることによって、ブロックマット100で覆った堤防などに一旦浸水した水を排出することができる。 The block mat 100 is not intended to be completely waterproof. Some water will come out from the overlapped part when a plurality of block mats 100 are stacked and arranged as described later, and the part where the anchor pin is driven in to fix the block mat 100 as described later. It is thought that it will leak. By adopting a form in which water leaks to some extent in this way, it is possible to discharge the water once infiltrated into the embankment or the like covered with the block mat 100.

<接着層>
本開示のブロックマット100において、コンクリートブロック20、20・・・、基材シート12、および、遮水シート14は、接着剤により一体化されている。よって、図2において、コンクリートブロック20、20・・・と基材シート12との間、および、基材シート12と遮水シート14との間には、不図示の接着剤からなる接着層が存在している。
<Adhesive layer>
In the block mat 100 of the present disclosure, the concrete blocks 20, 20 ..., The base sheet 12, and the water-impervious sheet 14 are integrated by an adhesive. Therefore, in FIG. 2, an adhesive layer made of an adhesive (not shown) is formed between the concrete blocks 20, 20 ... And the base sheet 12, and between the base sheet 12 and the water-impervious sheet 14. Existing.

接着層は、コンクリートブロック20、20・・・の基材シート12側の面の全面、あるいは、基材シート12と遮水シート14の界面の全面に設けてもよいが、所望の接着強度が得られるのであれば、必ずしも全面に設ける必要はない。なお、コンクリートブロック20、20・・・を強固に接着する点から、少なくとも、各コンクリートブロックにおける基材シート12側の面の四隅に接着層を形成することが好ましい。この場合、基材シート12と遮水シート14との間においても、該四隅に対応する位置(図2の紙面において、該四隅の紙面下方向の位置)に、接着層が形成されることが好ましい。 The adhesive layer may be provided on the entire surface of the concrete blocks 20, 20 ... On the base sheet 12 side, or on the entire interface between the base sheet 12 and the water-impervious sheet 14, but the desired adhesive strength is obtained. If it can be obtained, it does not necessarily have to be provided on the entire surface. From the viewpoint of firmly adhering the concrete blocks 20, 20 ..., It is preferable to form adhesive layers at least at the four corners of the surface of each concrete block on the base sheet 12 side. In this case, the adhesive layer may be formed between the base sheet 12 and the water-impervious sheet 14 at the positions corresponding to the four corners (in the paper surface of FIG. 2, the positions below the paper surface of the four corners). preferable.

(接着性樹脂)
接着剤は、接着性樹脂とフィラーとを含むことが好ましい。接着性樹脂としては、エポキシ樹脂、ウレタン樹脂、アクリル樹脂、シリコン樹脂、エポキシアクリレート樹脂、フェノール樹脂等の熱硬化性樹脂を用いたもの、ポリアミド樹脂、ポリエステル樹脂、エチレンビニルアルコール樹脂等の熱可塑性樹脂を用いたものや、スチレンブタジエンゴム、クロロプレンゴム、ブチルゴム等合成ゴムを用いたもの等を用いることができる。中でも、強度及び硬化性の優れたエポキシ樹脂が好ましく用いられる。
(Adhesive resin)
The adhesive preferably contains an adhesive resin and a filler. As the adhesive resin, those using thermosetting resins such as epoxy resin, urethane resin, acrylic resin, silicon resin, epoxy acrylate resin and phenol resin, and thermoplastic resins such as polyamide resin, polyester resin and ethylene vinyl alcohol resin. , And those using synthetic rubber such as styrene butadiene rubber, chloroprene rubber, and butyl rubber can be used. Of these, an epoxy resin having excellent strength and curability is preferably used.

(フィラー)
接着剤は、上記接着性樹脂の他に、フィラーを含んでいることが好ましい。フィラーを含むことにより、コンクリートブロック20、20・・・とシート10との接着強度を向上できる。フィラーとしては、無機フィラーを用いることが好ましく、例えば、炭酸カルシウム、珪砂、珪石粉を挙げることができる。中でも、フィラーとしては、接着強度を向上する点からは、炭酸カルシウム、珪砂を用いることが好ましく、接着剤の流動性(取り扱性)の点からは、珪砂を用いることが好ましい。
(Filler)
The adhesive preferably contains a filler in addition to the adhesive resin described above. By including the filler, the adhesive strength between the concrete blocks 20, 20 ... And the sheet 10 can be improved. As the filler, it is preferable to use an inorganic filler, and examples thereof include calcium carbonate, silica sand, and silica stone powder. Among them, as the filler, calcium carbonate and silica sand are preferably used from the viewpoint of improving the adhesive strength, and silica sand is preferably used from the viewpoint of the fluidity (handleability) of the adhesive.

フィラーの大きさは、0.8mm以下が好ましく、0.4mm以下がより好ましく、0.3mm以下がさらに好ましい。フィラーとして珪砂を使用する場合は、5号珪砂、7号珪砂を使用することが好ましく、7号珪砂を使用することがさらに好ましい。 The size of the filler is preferably 0.8 mm or less, more preferably 0.4 mm or less, and further preferably 0.3 mm or less. When silica sand is used as the filler, it is preferable to use No. 5 silica sand and No. 7 silica sand, and it is more preferable to use No. 7 silica sand.

接着層における、接着性樹脂を100質量部とした場合のフィラーの含有量は、50〜400質量部が好ましく、フィラーとして珪砂を使用する場合は、80〜300質量部がより好ましく、100〜200質量部がさらに好ましく、100〜150質量部が特に好ましく、フィラーとして炭酸カルシウムを使用する場合は、60〜100質量部が好ましい。 When the adhesive resin is 100 parts by mass, the filler content in the adhesive layer is preferably 50 to 400 parts by mass, and when silica sand is used as the filler, 80 to 300 parts by mass is more preferable, and 100 to 200 parts by mass. By mass is more preferable, 100 to 150 parts by mass is particularly preferable, and when calcium carbonate is used as the filler, 60 to 100 parts by mass is preferable.

(接着剤)
接着層を形成する接着剤は、上記した接着性樹脂およびフィラーを含んでなることが好ましく、その粘度(23℃)は、50mPa・s以上、100,000mPa・s未満であり、より好ましくは、50mPa・s以上、10,000mPa・s未満であり、さらに好ましくは、50mPa・s以上、5,000mPa・s未満である。粘度がこの範囲であれば、流動性が良く、コンクリートへの塗布作業時の作業性が向上する。
また、接着剤の粘度が小さすぎると、コンクリート上に塗布した場合に流れてしまい、塗布量を確保できない場合がある、その点から、粘度の下限は、500mPa・s以上が好ましく、1,000mPa・s以上がより好ましい。なお、前記接着剤の粘度は、主剤と硬化剤とを混合したものを23℃で、B型粘度計にて測定した値を示す。
(glue)
The adhesive forming the adhesive layer preferably contains the above-mentioned adhesive resin and filler, and its viscosity (23 ° C.) is 50 mPa · s or more and less than 100,000 mPa · s, more preferably. It is 50 mPa · s or more and less than 10,000 mPa · s, and more preferably 50 mPa · s or more and less than 5,000 mPa · s. When the viscosity is in this range, the fluidity is good and the workability at the time of coating work on concrete is improved.
Further, if the viscosity of the adhesive is too small, it may flow when applied on concrete, and the coating amount may not be secured. From this point, the lower limit of the viscosity is preferably 500 mPa · s or more, and 1,000 mPa. -S or more is more preferable. The viscosity of the adhesive indicates a value measured by a B-type viscometer at 23 ° C., which is a mixture of a main agent and a curing agent.

(剥離強度)
上記した接着層により、コンクリートブロック、基材シートおよび遮水シートが一体化され形成されたブロックマットにおいて、コンクリートブロックと基材シートとの間における、接着後5時間経過後の剥離強度は、30N/50mm以上が好ましく、50N/50mm以上がより好ましく、100N/50mm以上がさらに好ましく、150N/50mm以上がさらに好ましく、200N/50mm以上がさらに好ましく、300N/50mm以上が特に好ましい。
(Peeling strength)
In a block mat formed by integrating a concrete block, a base sheet and a water-impervious sheet with the above-mentioned adhesive layer, the peel strength between the concrete block and the base sheet after 5 hours from adhesion is 30 N. / 50 mm or more is preferable, 50 N / 50 mm or more is more preferable, 100 N / 50 mm or more is further preferable, 150 N / 50 mm or more is further preferable, 200 N / 50 mm or more is further preferable, and 300 N / 50 mm or more is particularly preferable.

[ブロックマットの製造方法]
本開示のブロックマットの製造方法は、遮水シート14、基材シート12、および、複数のコンクリートブロック20、20・・・を、接着剤を用いて一体化させることを特徴とする。本開示の製造方法では、既存の装置を使用して作製した硬化済みのコンクリートブロック20、20・・・を使用してブロックマット100を製造することができる。従来の硬化前のコンクリートブロックの一部を基材である不織布に含浸させて、コンクリートブロックと不織布とを一体化せる方法では、接着強度を発現させ、コンクリートが硬化するのに、数日の養生期間が必要となり、製造効率が悪かった。これに対して、本開示の方法では、数時間で接着剤により一体化が可能であるので、効率的に製造することが可能である。
[Manufacturing method of block mat]
The method for producing a block mat of the present disclosure is characterized in that a water-impervious sheet 14, a base sheet 12, and a plurality of concrete blocks 20, 20, ... Are integrated using an adhesive. In the manufacturing method of the present disclosure, the block mat 100 can be manufactured by using the hardened concrete blocks 20, 20, ... Produced by using the existing apparatus. In the conventional method of impregnating a part of the concrete block before curing with the non-woven fabric as the base material and integrating the concrete block and the non-woven fabric, the adhesive strength is developed and the concrete is cured for several days. It took a long time and the manufacturing efficiency was poor. On the other hand, in the method of the present disclosure, since it is possible to integrate with an adhesive in several hours, it is possible to efficiently manufacture the product.

また、本開示の方法では、市販されている遮水シート14を用いて、これを接着することにより、ブロックマット100を製造することができるので、従来のように基材シートのコンクリートブロック側とは反対側に、樹脂エマルジョンの吹きつけ、または、樹脂コーティングによって、遮水層を形成する方法に比べて、簡易な方法でブロックマット100製造することが可能である。また、ブロックマット100を敷設する法面の状態に応じて、凹凸を有する遮水シート14を選択して使用することが可能である。よって、実際の現場の法面において、ブロックマット100が滑りやすい状況の場合には、その状況に適した凹凸が付与された遮水シートを選択して、現場に適したブロックマットを簡易に提供することが可能である。 Further, in the method of the present disclosure, the block mat 100 can be manufactured by adhering the commercially available water-impervious sheet 14 to the concrete block side of the base sheet as in the conventional case. It is possible to manufacture the block mat 100 by a simple method as compared with the method of forming a water-impervious layer by spraying a resin emulsion or a resin coating on the opposite side. Further, it is possible to select and use the water-impervious sheet 14 having irregularities depending on the condition of the slope on which the block mat 100 is laid. Therefore, when the block mat 100 is slippery on the slope of the actual site, a water-impervious sheet with irregularities suitable for the situation is selected to easily provide a block mat suitable for the site. It is possible to do.

また、遮水シート14、基材シート12、および、複数のコンクリートブロック20、20・・・を一度に接着してブロックマットを製造することができるので、工程が少ないという意味でも、ブロックマット100を効率的に製造することが可能である。 Further, since the block mat can be manufactured by adhering the water-impervious sheet 14, the base sheet 12, and a plurality of concrete blocks 20, 20 ... At once, the block mat 100 also means that the number of steps is small. Can be efficiently manufactured.

本開示のブロックマットの製造方法は、具体的には、複数のコンクリートブロック20、20・・・の底面に接着剤を塗布する工程、前記コンクリートブロックの接着剤を塗布した面に基材シート12を設置する工程、前記基材シート12の上に遮水シート14を設置する工程、および、前記コンクリートブロック20、20・・・と基材シート12と遮水シート14とを接着する工程、を備える。以下、各工程について説明する。 Specifically, the method for manufacturing the block mat of the present disclosure includes a step of applying an adhesive to the bottom surfaces of a plurality of concrete blocks 20, 20 ..., And a base sheet 12 on the surface to which the adhesive of the concrete blocks is applied. The step of installing the impermeable sheet 14 on the base sheet 12, and the step of adhering the concrete blocks 20, 20 ... To the base sheet 12 and the impermeable sheet 14. Be prepared. Hereinafter, each step will be described.

(接着剤塗布工程)
接着剤塗布工程では、複数のコンクリートブロック20、20・・・の底面に接着剤が塗布される。コンクリートブロック20、20・・・の底面とは、ブロックマット100を法面に設置した際において、法面側となるコンクリートブロック20、20・・・の面である。接着剤は、コンクリートブロック20、20・・・の底面の全面に塗布してもよいが、上記した所定の剥離強度が発揮されるのであれば、コンクリートブロック20、20・・・の底面の全面に塗布する必要はない。ただ、コンクリートブロック20、20・・・を強固に接着する点から、各コンクリートブロック20、20・・・の底面の四隅に接着剤を塗布して、該四隅に接着層を形成することが好ましい。
(Adhesive application process)
In the adhesive application step, the adhesive is applied to the bottom surfaces of the plurality of concrete blocks 20, 20 ... The bottom surfaces of the concrete blocks 20, 20 ... Are the surfaces of the concrete blocks 20, 20 ... Which are on the slope side when the block mat 100 is installed on the slope. The adhesive may be applied to the entire bottom surface of the concrete blocks 20, 20 ..., But if the above-mentioned predetermined peel strength is exhibited, the entire surface of the bottom surface of the concrete blocks 20, 20 ... No need to apply to. However, from the viewpoint of firmly adhering the concrete blocks 20, 20 ..., It is preferable to apply an adhesive to the four corners of the bottom surface of each concrete block 20, 20 ... To form an adhesive layer at the four corners. ..

接着剤の塗布量は、コンクリートブロックの底面を基準として、1.0〜3.0kg/mとすることが好ましい。 The amount of the adhesive applied is preferably 1.0 to 3.0 kg / m 2 based on the bottom surface of the concrete block.

(基材シート12設置工程)
底面に接着剤を塗布した複数のコンクリートブロック20、20・・・を、底面を上にして並べて、該底面の上に基材シート12が設置される。基材シート12は多孔性シートであるので、接着剤は該基材シート12に含浸して、コンクリートブロック20、20・・・側の面とは反対の面に染み出す。
(Base sheet 12 installation process)
A plurality of concrete blocks 20, 20 ... With an adhesive applied to the bottom surface are arranged side by side with the bottom surface facing up, and the base sheet 12 is installed on the bottom surface. Since the base sheet 12 is a porous sheet, the adhesive impregnates the base sheet 12 and exudes to a surface opposite to the surface on the concrete blocks 20, 20 ... Side.

(遮水シート14設置工程)
上記で設置した基材シート12の上に、遮水シート14を設置する。基材シート12および遮水シート14は同一形状であることが好ましく、両者が接着することにより、シート10が形成される。
(Immersion sheet 14 installation process)
The water-impervious sheet 14 is installed on the base sheet 12 installed above. The base sheet 12 and the water-impervious sheet 14 preferably have the same shape, and the sheet 10 is formed by adhering them together.

(接着工程)
その後、コンクリートブロック20、20・・・、基材シート12、および、遮水シート14が密着するように、図2紙面の上下方向に所望により加圧することで、これらを接着させることができる。接着強度が発現するための養生時間は、下限が3時間以上が好ましく、4時間以上がより好ましく、上限は10時間以下とすることが好ましく、8時間以下とすることがより好ましい。このように、本開示の方法では比較的短時間にて接着させることが可能である。なお、養生時間の間において、加圧し続けることが好ましい。
(Adhesion process)
After that, the concrete blocks 20, 20 ..., the base sheet 12, and the water-impervious sheet 14 can be adhered to each other by appropriately applying pressure in the vertical direction of the paper surface of FIG. 2 so as to be in close contact with each other. The lower limit of the curing time for developing the adhesive strength is preferably 3 hours or more, more preferably 4 hours or more, and the upper limit is preferably 10 hours or less, more preferably 8 hours or less. As described above, in the method of the present disclosure, it is possible to bond in a relatively short time. It is preferable to continue pressurizing during the curing time.

なお、上記では、接着剤塗布工程において、接着剤をコンクリートブロック20、20・・・の底面に塗布しているが、最終的にコンクリートブロック20、20・・・と基材シート12との間、ならびに、基材シート12と遮水シート14との間に接着層が形成されるのであれば、接着剤の塗布位置はコンクリートブロック20、20・・・の底面に限定されない。例えば、基材シート12の表面であってもよいし、または、遮水シート14の基材シート側の表面であってもよい。 In the above, the adhesive is applied to the bottom surfaces of the concrete blocks 20, 20 ... In the adhesive application step, but finally between the concrete blocks 20, 20 ... And the base sheet 12. , And if an adhesive layer is formed between the base sheet 12 and the impermeable sheet 14, the adhesive application position is not limited to the bottom surfaces of the concrete blocks 20, 20, .... For example, it may be the surface of the base sheet 12, or the surface of the water-impervious sheet 14 on the base sheet side.

[護岸構造]
本開示のブロックマット100は、河川の水流に対して法面を保護するために使用することができる。法面は、堤外地側法面であっても、堤内地側法面であってもいずれでもよい。なお、「堤外地側」とは、河川側(川表側)を意味し、「堤内地側」とは、市街地側(川裏側)を意味する。
[Revetment structure]
The block mat 100 of the present disclosure can be used to protect the slope against the water flow of a river. The slope may be either the slope on the outer side of the embankment or the slope on the inner side of the embankment. The "outside embankment side" means the river side (front side of the river), and the "inside embankment side" means the urban area side (back side of the river).

本開示の護岸構造においては、本開示のブロックマットを、法面の全面に敷設してもよいし、あるいは、コストなどを考慮して、法面の一部(例えば、堤外地側法面)に敷設してもよい。このように、少なくとも、堤外地側法面に本開示のブロックマットを敷設することにより、河川が通常の水流である場合において、法面への浸水を防止して、法面を保護することができる。 In the revetment structure of the present disclosure, the block mat of the present disclosure may be laid on the entire surface of the slope, or a part of the slope (for example, the slope on the outside of the bank) in consideration of cost and the like. It may be laid in. In this way, at least by laying the block mat of the present disclosure on the slope on the outside of the embankment, it is possible to prevent flooding of the slope and protect the slope when the river has a normal water flow. can.

また、本開示のブロックマット100は、河川の越流に対して堤内地側法面を保護するために使用することができる。この場合、河川の堤内地側法面の全面にブロックマット100を敷設してもよいし、コスト面等を考慮して、堤内地側法面の一部に護岸用ブロックマット100を敷設してもよい。 Further, the block mat 100 of the present disclosure can be used to protect the slope on the embankment side against the overflow of a river. In this case, the block mat 100 may be laid on the entire surface of the slope on the inland side of the river, or the block mat 100 for revetment may be laid on a part of the slope on the inland side of the embankment in consideration of cost and the like. May be good.

図3に、河川の越流に対して堤内地側法面を保護した場合の護岸構造200を示す。図3に示すように、護岸構造200においては、ブロックマット100が河川の堤内地側法面に敷設されている。ブロックマット100は、平地から法尻を跨いで堤内地側法面の中腹まで敷設されており、ブロックマット100が法尻を跨いで敷設されることで、越流時の法面の侵食をより適切に抑制できる。 FIG. 3 shows a revetment structure 200 when the slope on the inland side of the embankment is protected against the overflow of the river. As shown in FIG. 3, in the revetment structure 200, the block mat 100 is laid on the slope on the inland side of the river. The block mat 100 is laid from the flat ground to the middle of the slope on the inland side of the embankment across the slope, and by laying the block mat 100 across the slope, erosion of the slope at the time of overflow is further improved. It can be suppressed appropriately.

以下、本開示のブロックマットを実施例に基づいてより詳細に説明する。なお、本開示のブロックマットは、以下の実施例及び比較例によって何ら限定されるものではない。 Hereinafter, the block mat of the present disclosure will be described in more detail based on examples. The block mat of the present disclosure is not limited to the following examples and comparative examples.

<使用原材料>
(不織布)不織布は、目付け量125g/mのポリエステル80wt%と低密度ポリエステル20wt%からなるニードルパンチ製法により得られた厚み3mmの不織布(繊度が3.3〜4.4dtexの繊維70wt%と繊度が6.6dtexの繊維30wt%とからなる混合繊維)を用いた。
<Raw materials used>
(Nonwoven fabric) The non-woven fabric is a non-woven fabric having a thickness of 3 mm (70 wt% of fibers having a fineness of 3.3 to 4.4 dtex) obtained by a needle punching method consisting of 80 wt% of polyester having a grain size of 125 g / m 2 and 20 wt% of low-density polyester. A mixed fiber consisting of 30 wt% of a fiber having a fineness of 6.6 dtex) was used.

(接着剤1)サンユレック社製エポキシ接着剤(サンユボンドA418)100質量部に対して、フィラーとして炭酸カルシウムを80質量部含有したもの
(接着剤2)サンユレック社製エポキシ接着剤(サンユボンドA418)に100重量部に対して、フィラーとして7号珪砂を100質量部含有したもの
(接着剤3)サンユレック社製エポキシ接着剤(サンユボンドA418)に100重量部に対して、フィラーとして7号珪砂を150質量部含有したもの
(接着剤4)サンユレック社製エポキシ接着剤(サンユボンドA418)にフィラーを含まないもの。
(Adhesive 1) 100 parts by mass of calcium carbonate as a filler with respect to 100 parts by mass of Sanyulek epoxy adhesive (Sanyubond A418) (Adhesive 2) 100 parts by Sanyulek epoxy adhesive (Sanyubond A418) 100 parts by mass of No. 7 silica sand as a filler with respect to 100 parts by weight (Adhesive 3) 150 parts by mass of No. 7 silica sand as a filler with 100 parts by weight of an epoxy adhesive (Sanyu Bond A418) manufactured by Sanyulek. Containing (Adhesive 4) An epoxy adhesive (Sanyu Bond A418) manufactured by Sanyu Rec Co., Ltd. that does not contain a filler.

<測定方法>
(粘度、流動性)
B型粘度計を用いて23℃における上記接着剤の粘度を測定した。
また、上記測定した粘度に基づいて接着剤の流動性を以下の基準で評価した。
◎:粘度が50mPa・s以上、5,000mPa・s未満
○:粘度が5,000mPa・s以上、10,000mPa・s未満
△:粘度が10,000mPa・s以上、100,000mPa・s未満
×:粘度が100,000mPa・s以上、または、50mPa・s未満
<Measurement method>
(Viscosity, fluidity)
The viscosity of the adhesive at 23 ° C. was measured using a B-type viscometer.
Further, the fluidity of the adhesive was evaluated based on the measured viscosity according to the following criteria.
⊚: Viscosity is 50 mPa · s or more and less than 5,000 mPa · s ○: Viscosity is 5,000 mPa · s or more and less than 10,000 mPa · s Δ: Viscosity is 10,000 mPa · s or more and less than 100,000 mPa · s × : Viscosity of 100,000 mPa · s or more or less than 50 mPa · s

(剥離強度)
JIS Z 0237(2009)に準拠して、コンクリートブロックと基材シートとの間の180度剥離強度について以下の基準で評価した。
◎:剥離強度が200N/50mm以上
〇:剥離強度が30N/50mm以上、200N/50mm未満
×:剥離強度が30N/50mm未満
(Peeling strength)
According to JIS Z 0237 (2009), the 180 degree peel strength between the concrete block and the base sheet was evaluated according to the following criteria.
⊚: Peeling strength is 200N / 50mm or more 〇: Peeling strength is 30N / 50mm or more, less than 200N / 50mm ×: Peeling strength is less than 30N / 50mm

<実施例1>
250mm×250mmのコンクリート歩道版(ケレンなし)を準備し、接着剤1を表1に記載の塗布量でコンクリート歩道版に塗布した。その上に、幅50mm、長さ250mmの不織布を、5枚を並べて貼り合せ、さらにその上に厚さ0.4mm、幅50mm、長さ250mmのエチレン−酢酸ビニル共重合樹脂(EVA)シートを不織布と同方向に貼り合わせた。これを50℃のオーブンに入れ、5時間経過した後の180度剥離試験の数値を剥離強度とした。結果を表1に示す。
<Example 1>
A 250 mm × 250 mm concrete sidewalk slab (without keren) was prepared, and the adhesive 1 was applied to the concrete sidewalk slab in the amount shown in Table 1. Five non-woven fabrics having a width of 50 mm and a length of 250 mm are laminated side by side on the non-woven fabric, and an ethylene-vinyl acetate copolymer resin (EVA) sheet having a thickness of 0.4 mm, a width of 50 mm and a length of 250 mm is further attached thereto. It was laminated in the same direction as the non-woven fabric. This was placed in an oven at 50 ° C., and the value of the 180-degree peeling test after 5 hours had passed was taken as the peeling strength. The results are shown in Table 1.

(実施例2)
接着剤1を接着剤2に変更し、表1に記載した塗布量とした以外は実施例1と同様にして剥離強度を測定した。
(Example 2)
The peel strength was measured in the same manner as in Example 1 except that the adhesive 1 was changed to the adhesive 2 and the coating amount was set as shown in Table 1.

(実施例3)
接着剤1を接着剤3に変更し、表1に記載した塗布量とした以外は実施例1と同様にして剥離強度を測定した。
(Example 3)
The peel strength was measured in the same manner as in Example 1 except that the adhesive 1 was changed to the adhesive 3 and the coating amount was set as shown in Table 1.

(実施例4)
接着剤3の塗布量を表1のように変更した以外は実施例3と同様にして剥離強度を測定した。
(Example 4)
The peel strength was measured in the same manner as in Example 3 except that the coating amount of the adhesive 3 was changed as shown in Table 1.

(実施例5)
接着剤1を接着剤4に変更し、表1に記載した塗布量とした以外は実施例1と同様にして剥離強度を測定した。
(Example 5)
The peel strength was measured in the same manner as in Example 1 except that the adhesive 1 was changed to the adhesive 4 and the coating amount was set as shown in Table 1.

Figure 2021165527
Figure 2021165527

実施例1〜5においては、コンクリートブロックと基材シートと遮水シートが接着剤によって一体化されたブロックマットが得られた。また、これらは、剥離強度が所望の値以上であり、接着剤が所定の流動性を有しており取扱性が良好であった。実施例5においては、接着剤の粘度が低いために、コンクリート歩道版上に塗布できる接着剤の量が制限されたため、剥離強度が他の例と比べて小さくなった。 In Examples 1 to 5, a block mat in which a concrete block, a base material sheet, and a water-impervious sheet were integrated with an adhesive was obtained. Further, these had a peel strength of more than a desired value, the adhesive had a predetermined fluidity, and the handleability was good. In Example 5, since the viscosity of the adhesive was low, the amount of the adhesive that could be applied on the concrete sidewalk slab was limited, so that the peel strength was smaller than in the other examples.

本開示のブロックマット100は、河川の水流に対して法面を保護するために、法面に敷設して護岸構造を形成することができる。また、設置場所によっては、越流対策用の護岸構造とすることも可能である。 The block mat 100 of the present disclosure can be laid on the slope to form a revetment structure in order to protect the slope against the water flow of the river. In addition, depending on the installation location, it is possible to have a revetment structure for overflow countermeasures.

10:シート
12:基材シート
14:遮水シート
20:コンクリートブロック
100:ブロックマット
200:護岸構造
10: Sheet 12: Base sheet 14: Impermeable sheet 20: Concrete block 100: Block mat 200: Revetment structure

Claims (9)

可撓性を有するシートに複数のコンクリートブロックが固定されたブロックマットであって、
前記シートが、前記コンクリートブロック側の基材シートと前記コンクリートブロックとは反対側の遮水シートとを備え、
前記基材シートが多孔性シートであり、
前記コンクリートブロック、前記基材シート、および、前記遮水シートが接着剤により一体化されており、
前記接着剤の23℃における粘度が、50mPa・s以上、100,000mPa・s未満である、
ブロックマット。
A block mat in which multiple concrete blocks are fixed to a flexible sheet.
The sheet includes a base sheet on the concrete block side and a water-impervious sheet on the opposite side of the concrete block.
The base sheet is a porous sheet, and the base sheet is a porous sheet.
The concrete block, the base sheet, and the water-impervious sheet are integrated by an adhesive .
The viscosity of the adhesive at 23 ° C. is 50 mPa · s or more and less than 100,000 mPa · s.
Block mat.
前記コンクリートブロックと前記基材シートとの間、および、前記基材シートと前記遮水シートとの間に、前記接着剤からなる接着層を備える、請求項1に記載のブロックマット。 The block mat according to claim 1, further comprising an adhesive layer made of the adhesive between the concrete block and the base sheet, and between the base sheet and the water-impervious sheet. 前記接着剤が、接着性樹脂およびフィラーを含む、請求項1または2に記載のブロックマット。 The block mat according to claim 1 or 2 , wherein the adhesive comprises an adhesive resin and a filler. 前記フィラーの含有量が、接着性樹脂100質量部に対して、1〜450質量部である、請求項3に記載のブロックマット。 The block mat according to claim 3, wherein the content of the filler is 1 to 450 parts by mass with respect to 100 parts by mass of the adhesive resin. 前記コンクリートブロックと前記基材シートとの間の剥離強度が、30N/50mm以上である、請求項1〜のいずれかに記載のブロックマット。 The block mat according to any one of claims 1 to 4 , wherein the peel strength between the concrete block and the base material sheet is 30 N / 50 mm or more. 前記遮水シートにおける、基材シート側とは反対側に、凹凸が形成されている、請求項1〜のいずれかに記載のブロックマット。 The block mat according to any one of claims 1 to 5 , wherein an unevenness is formed on the side of the water-impervious sheet opposite to the base sheet side. 遮水シートと基材シートと複数のコンクリートブロックとを、接着剤を用いて一体化させることを特徴とする、請求項1〜のいずれかに記載のブロックマットの製造方法。 The method for manufacturing a block mat according to any one of claims 1 to 6 , wherein the water-impervious sheet, the base sheet, and a plurality of concrete blocks are integrated by using an adhesive. 複数のコンクリートブロックの底面に接着剤を塗布する工程、前記コンクリートブロックの接着剤を塗布した面に前記基材シートを設置する工程、前記基材シートにおける前記コンクリートブロックを設置した面とは反対側に前記遮水シートを設置する工程、および、前記コンクリートブロックと前記基材シートと前記遮水シートとを接着する工程、を備える、請求項に記載のブロックマットの製造方法。 A step of applying an adhesive to the bottom surfaces of a plurality of concrete blocks, a step of installing the base material sheet on the surface of the concrete block to which the adhesive is applied, and a side of the base material sheet opposite to the surface on which the concrete block is installed. The method for manufacturing a block mat according to claim 7 , further comprising a step of installing the water-impervious sheet and a step of adhering the concrete block, the base material sheet, and the water-impervious sheet to the concrete block. 請求項1〜のいずれかに記載のブロックマットが敷設された護岸構造。 A revetment structure in which the block mat according to any one of claims 1 to 6 is laid.
JP2021118314A 2019-01-25 2021-07-16 Block mat, block mat manufacturing method, and bank protection structure Active JP7264947B2 (en)