JP2021054429A

JP2021054429A - Pouch

Info

Publication number: JP2021054429A
Application number: JP2019176536A
Authority: JP
Inventors: 愛子藤田; Aiko Fujita; 康晴上原; Yasuharu Uehara; 村上　亮; Ryo Murakami; 亮村上
Original assignee: Dai Nippon Printing Co Ltd
Current assignee: Dai Nippon Printing Co Ltd
Priority date: 2019-09-27
Filing date: 2019-09-27
Publication date: 2021-04-08

Abstract

To provide a pouch that can be easily hung even with a simple configuration.SOLUTION: A pouch has at least a front surface, a back surface, and a bottom surface, and comprises an upper edge 16, a lower edge 17 facing the upper edge 16, and a first side edge and a second side edge extending between the upper edge 16 and the lower edge 17. A first side seal portion 5a is formed so as to include the first side edge, and a second side seal portion 5b is formed so as to include the second side edge. The bottom surface has a first bottom seal portion 6a joined respectively to an inner surface side of the front surface and an inner surface side of the back surface, and a second bottom seal portion 6b which is surrounded by the first bottom seal portion 6a and to which the front surface and the back surface are directly joined. When a distance from the upper edge 16 to the lower edge 17 is L1 and a distance from the center of gravity of the second bottom seal portion 6b to the upper edge 16 is L2, the distance L2/distance L1 is 0.4 or more and 0.9 or less.SELECTED DRAWING: Figure 1

Description

本発明は、店舗などの陳列箇所において、吊り下げて陳列するためのパウチに関する。 The present invention relates to a pouch for hanging and displaying at a display location such as a store.

従来、表面と裏面の間に底部が挟み込まれ、この底部を開くことにより自立させることが可能なスタンディングパウチが知られている。本来、スタンディングパウチは、底部を下方に向けた状態で載置することにより自立させることができる。しかし、このようなスタンディングパウチを吊り下げて利用したいという要望もある。このため、スタンディングパウチの一部に吊り下げ孔を形成したものも提案されている（例えば特許文献１参照）。 Conventionally, there is known a standing pouch in which a bottom portion is sandwiched between the front surface and the back surface and can be made independent by opening the bottom portion. Originally, the standing pouch can be made to stand on its own by placing it with its bottom facing downward. However, there is also a desire to hang such a standing pouch for use. For this reason, it has been proposed that a hanging hole is formed in a part of the standing pouch (see, for example, Patent Document 1).

特開２００２−１０４４４６号公報JP-A-2002-104446

しかしながら、特許文献１に記載のパウチでは、パウチの一部に吊り下げ孔をわざわざ形成しなけなければならないという問題がある。 However, the pouch described in Patent Document 1 has a problem that a hanging hole must be purposely formed in a part of the pouch.

そこで、本発明は、簡易な構成でありながら、容易に吊り下げを行うことが可能なパウチを提供することを課題とする。 Therefore, an object of the present invention is to provide a pouch that can be easily suspended even though it has a simple structure.

上記課題を解決するため、本発明は、
少なくとも表面と裏面と底面とを有し、上縁と上縁と対向する下縁と、上縁と下縁との間に延びる第１側縁と第２側縁とを備えたパウチであって、
前記第１側縁を含むように第１側部シール部が形成されており、
前記第２側縁を含むように第２側部シール部が形成されており、
前記底面が、前記表面の内面側、前記裏面の内面側とそれぞれ接合された第１底部シール部と、
前記第１底部シール部に囲まれており、前記表面と前記裏面がそれぞれの内面側において直接接合された第２底部シール部と、を有し、
前記上縁から下縁までの距離をＬ１、前記第２底部シール部の重心位置から前記上縁までの距離をＬ２としたとき、距離Ｌ２／距離Ｌ１が０．４以上０．９以下であることを特徴とする。 In order to solve the above problems, the present invention
A pouch having at least a front surface, a back surface, and a bottom surface, and having a lower edge facing the upper edge and an upper edge, and a first side edge and a second side edge extending between the upper edge and the lower edge. ,
The first side seal portion is formed so as to include the first side edge.
The second side seal portion is formed so as to include the second side edge.
The bottom surface is a first bottom seal portion joined to the inner surface side of the front surface and the inner surface side of the back surface, respectively.
It is surrounded by the first bottom seal portion, and has a second bottom seal portion in which the front surface and the back surface are directly joined on the inner surface side thereof.
When the distance from the upper edge to the lower edge is L1 and the distance from the center of gravity of the second bottom seal portion to the upper edge is L2, the distance L2 / distance L1 is 0.4 or more and 0.9 or less. It is characterized by that.

また、本発明のパウチは、
前記底面フィルムの折込部が前記上縁側に形成されていることを特徴とする。 Further, the pouch of the present invention is
It is characterized in that the folded portion of the bottom film is formed on the upper edge side.

また、本発明のパウチは、
前記底面フィルムの折込部が前記下縁側に形成されていることを特徴とする。 Further, the pouch of the present invention is
It is characterized in that the folded portion of the bottom film is formed on the lower edge side.

また、本発明のパウチは、
前記表面、裏面の互いに対向する内面側には、開封後に再封するための咬合具が形成されていることを特徴とする。 Further, the pouch of the present invention is
An occlusal tool for resealing after opening is formed on the inner surfaces of the front surface and the back surface facing each other.

本発明によれば、簡易な構成でありながら、容易に吊り下げを行うことが可能なパウチを提供することができる。 According to the present invention, it is possible to provide a pouch that can be easily suspended even though it has a simple structure.

本発明第１の実施形態に係るパウチを示す正面図である。It is a front view which shows the pouch which concerns on 1st Embodiment of this invention. 本発明第１の実施形態に係るパウチを構成するフィルム構成を示す分解図である。It is an exploded view which shows the film structure which comprises the pouch which concerns on 1st Embodiment of this invention. 本発明第１の実施形態に係るパウチを吊り下げた状態の正面図である。It is a front view of the state which the pouch which concerns on 1st Embodiment of this invention is hung. 図１に示すＢ−Ｂ線に対応する断面図である。It is sectional drawing corresponding to line BB shown in FIG. 本発明第２の実施形態に係るパウチを示す正面図である。It is a front view which shows the pouch which concerns on 2nd Embodiment of this invention. 本発明第２の実施形態に係るパウチを吊り下げた状態の正面図である。It is a front view of the state which the pouch which concerns on 2nd Embodiment of this invention is hung.

以下、本発明の好適な実施形態について、図面を参照して詳細に説明する。
＜＜第１の実施形態＞＞
第１の実施形態について説明する。図１は、本発明第１の実施形態に係るパウチを示す図である。図１（ａ）は、表面側から見た正面図であり、図１（ｂ）は、図１（ａ）のＡ−Ａ線に対応する断面図であり、図１（ｃ）は、図１（ａ）のＤ−Ｄ線に対応する断面図である。また、図２は、本発明第１の実施形態に係るパウチを構成するフィルム構成を示す分解図である。 Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the drawings.
<< First Embodiment >>
The first embodiment will be described. FIG. 1 is a diagram showing a pouch according to the first embodiment of the present invention. 1 (a) is a front view seen from the front surface side, FIG. 1 (b) is a cross-sectional view corresponding to the line AA of FIG. 1 (a), and FIG. 1 (c) is a view. It is sectional drawing corresponding to the DD line of 1 (a). Further, FIG. 2 is an exploded view showing a film structure constituting the pouch according to the first embodiment of the present invention.

図１に示した第１の実施形態のパウチは、内容物が充填される前の状態（内容物が充填されていない状態）のパウチを示したものである。本実施形態のパウチは、正面視において長方形状である。また、本実施形態のパウチは、上下方向においてやや下方の位置にガセット部９を有している。本実施形態において、長方形とは、四隅が直角の長方形だけでなく、長方形の四隅が面取りされて、外に凸の円弧状となったものも含む概念である。本発明において、パウチは、内容物が充填されていない状態のパウチに限らず、内容物が充填されている状態のパウチも含む概念である。 The pouch of the first embodiment shown in FIG. 1 shows a pouch in a state before the contents are filled (a state in which the contents are not filled). The pouch of the present embodiment has a rectangular shape when viewed from the front. Further, the pouch of the present embodiment has a gusset portion 9 at a position slightly lower in the vertical direction. In the present embodiment, the rectangle is a concept including not only a rectangle having four corners at right angles but also a rectangle in which the four corners of the rectangle are chamfered to form an arc shape that is convex outward. In the present invention, the pouch is a concept that includes not only a pouch in a state in which the contents are not filled but also a pouch in a state in which the contents are filled.

＜＜構成部材＞＞
本実施形態のパウチは、図２に示すように、略長方形状の表面フィルム１と、表面フィルム１と同一形状の裏面フィルム２と、略長方形状の底面フィルム３の３つの部材（フィルム）で構成されている。パウチの表面、裏面、底面は、それぞれ表面フィルム１、裏面フィルム２、底面フィルム３により構成されている。本実施形態のパウチは、表面フィルム１、裏面フィルム２、底面フィルム３の３枚のフィルムが所定の箇所においてシール（熱融着）されることにより形成される。 << Components >>
As shown in FIG. 2, the pouch of the present embodiment is composed of three members (films) of a substantially rectangular front surface film 1, a back surface film 2 having the same shape as the front surface film 1, and a substantially rectangular bottom surface film 3. It is configured. The front surface, the back surface, and the bottom surface of the pouch are composed of a front surface film 1, a back surface film 2, and a bottom surface film 3, respectively. The pouch of the present embodiment is formed by sealing (heat-sealing) three films of the front surface film 1, the back surface film 2, and the bottom surface film 3 at predetermined positions.

図２に示すように、底面フィルム３は、２つ折りされており、折込部３ａを境界にして第１部分３ｆと第２部分３ｇとに区分される。底面フィルム３には、側縁を切り欠くように４つの半円弧状の切り欠き部３ｂ、３ｃ、３ｄ、３ｅが設けられており、切り欠き部３ｂと３ｃ、および、切り欠き部３ｄと３ｅは２つ折りしたときに対応する位置に設けられている。この切り欠き部３ｂ〜３ｅを介して、後述する第２底部シール部６ｂが形成される。第１部分３ｆ、第２部分３ｇにおいて折込部３ａと対向する部分は、端部３ｈ、３ｈとなっている。また、スタンディングパウチとして自立性を安定させる観点から、折込部３ａと直交する方向における、第１部分３ｆ、第２部分３ｇの長さは３５ｍｍ以上とすることができる。 As shown in FIG. 2, the bottom film 3 is folded in two, and is divided into a first portion 3f and a second portion 3g with the folded portion 3a as a boundary. The bottom film 3 is provided with four semicircular notches 3b, 3c, 3d, and 3e so as to cut out the side edges, and the notches 3b and 3c and the notches 3d and 3e are provided. Is provided at the corresponding position when folded in half. A second bottom seal portion 6b, which will be described later, is formed through the cutout portions 3b to 3e. The portions of the first portion 3f and the second portion 3g that face the folding portion 3a are the end portions 3h and 3h. Further, from the viewpoint of stabilizing the independence as a standing pouch, the lengths of the first portion 3f and the second portion 3g in the direction orthogonal to the folding portion 3a can be 35 mm or more.

＜＜各シール部＞＞
本実施形態のパウチは、図１に示すように、第１側部シール部５ａと、第２側部シール部５ｂと、第１底部シール部６ａと、第２底部シール部６ｂと、咬合具２０と、を備え、上縁１６を含む上部に開口部１５が形成されている。図１においては、各シール部を斜線で網掛けして示している。第１側部シール部５ａ、第２側部シール部５ｂは、表面フィルム１と裏面フィルム２がシールされて接合されたものである。第１側部シール部５ａの咬合具部分５ａｂと、第２側部シール部５ｂの咬合具部分５ｂｂは、表面フィルム１、裏面フィルム２が、それぞれ咬合具２０とシールされて接合されたものである。第１側部シール部５ａの咬合具部分５ａｂと、第２側部シール部５ｂの咬合具部分５ｂｂにおいては、咬合具２０同士も溶着されている。第１側部シール部５ａは、第１側縁（図１における左端）を含むように形成されており、第２側部シール部５ｂは、第２側縁（図１における右端）を含むように形成されている。第１側部シール部５ａ、第２側部シール部５ｂのシール幅Ｗ１は、８ｍｍ以上１５ｍｍ以下とすることが好ましい。なお、シール幅Ｗ１は、シール部が延びる方向と直交する方向における幅である。 << Each seal >>
As shown in FIG. 1, the pouch of the present embodiment includes a first side seal portion 5a, a second side seal portion 5b, a first bottom seal portion 6a, a second bottom seal portion 6b, and an occlusion tool. 20 and an opening 15 is formed in the upper portion including the upper edge 16. In FIG. 1, each seal portion is shaded with diagonal lines. The first side seal portion 5a and the second side seal portion 5b are formed by sealing and joining the front surface film 1 and the back surface film 2. The occlusal portion 5ab of the first side sealing portion 5a and the occlusal portion 5bb of the second side sealing portion 5b are formed by joining the front surface film 1 and the back surface film 2 so as to be sealed with the occlusal tool 20, respectively. is there. The occlusal tools 20 are also welded to each other in the occlusal portion 5ab of the first side sealing portion 5a and the occlusal portion 5bb of the second side sealing portion 5b. The first side seal portion 5a is formed so as to include the first side edge (left end in FIG. 1), and the second side seal portion 5b includes the second side edge (right end in FIG. 1). Is formed in. The seal width W1 of the first side seal portion 5a and the second side seal portion 5b is preferably 8 mm or more and 15 mm or less. The seal width W1 is a width in a direction orthogonal to the direction in which the seal portion extends.

底部シール部６は、折込部３ａと端部３ｈの間に形成されるシール部であり、第１底部シール部６ａと、第２底部シール部６ｂで構成されている。第１底部シール部６ａは、表面フィルム１と底面フィルム３の第１部分３ｆ、および、裏面フィルム２と底面フィルム３の第２部分３ｇがシールされたものである。すなわち、第１底部シール部６ａでは、底面フィルム３が、表面フィルム１の内面側、裏面フィルム２の内面側とそれぞれ接合されている。第２底部シール部６ｂは、表面フィルム１と裏面フィルム２が直接接合（シール）されたものである。すなわち、第２底部シール部６ｂでは、表面フィルム１と裏面フィルム２の内面側において直接接合されている。第２底部シール部６ｂは、面方向において、第１底部シール部６ａに囲まれた状態で形成されている。第２底部シール部６ｂは、ほぼ半楕円形状である。本来、第２底部シール部６ｂとなる部分は、半円形であってもよいが、位置が表面フィルム１と裏面フィルム２で位置ずれが生じることを考慮して、半楕円形状としている。例えば長径（図１における左右方向）１７ｍｍ、短径（図１における左右方向）１５ｍｍの楕円を２つに分けた半楕円形状とすることができる。 The bottom seal portion 6 is a seal portion formed between the folded portion 3a and the end portion 3h, and is composed of a first bottom seal portion 6a and a second bottom seal portion 6b. The first bottom sealing portion 6a is formed by sealing the first portion 3f of the front surface film 1 and the bottom surface film 3 and the second portion 3g of the back surface film 2 and the bottom surface film 3. That is, in the first bottom sealing portion 6a, the bottom surface film 3 is joined to the inner surface side of the front surface film 1 and the inner surface side of the back surface film 2, respectively. The second bottom sealing portion 6b is formed by directly joining (sealing) the front surface film 1 and the back surface film 2. That is, in the second bottom sealing portion 6b, the front surface film 1 and the back surface film 2 are directly bonded to each other on the inner surface side. The second bottom seal portion 6b is formed in a state of being surrounded by the first bottom seal portion 6a in the surface direction. The second bottom seal portion 6b has a substantially semi-elliptical shape. Originally, the portion to be the second bottom seal portion 6b may be semi-circular, but the position is semi-elliptical in consideration of the misalignment between the front surface film 1 and the back surface film 2. For example, an ellipse having a major axis (horizontal direction in FIG. 1) of 17 mm and a minor axis (horizontal direction in FIG. 1) of 15 mm can be formed into a semi-elliptical shape divided into two.

第１側部シール部５ａの咬合具部分５ａｂと、第２側部シール部５ｂの咬合具部分５ｂｂは、咬合具２０を表面フィルム１、裏面フィルム２に固定するためのシール部である。第１側部シール部５ａの咬合具部分５ａｂと、第２側部シール部５ｂの咬合具部分５ｂｂは、表面フィルム１と咬合具２０の雄部材２１、咬合具２０の雌部材２２、および裏面フィルム２が一体となるようにシールされたものである。咬合具２０は、開封開始手段１４よりも下縁１７寄りに位置するようにすることが好ましい。そのため、少なくとも咬合具２０の上端２０ｄは、開封開始手段１４よりも下縁１７寄りに位置するように形成する。 The occlusal portion 5ab of the first side sealing portion 5a and the occlusal portion 5bb of the second side sealing portion 5b are sealing portions for fixing the occlusal tool 20 to the front surface film 1 and the back surface film 2. The occlusal portion 5ab of the first side seal portion 5a and the occlusal portion 5bb of the second side seal portion 5b are the front surface film 1, the male member 21 of the occlusal tool 20, the female member 22 of the occlusal tool 20, and the back surface. The film 2 is sealed so as to be integrated. It is preferable that the occlusal tool 20 is located closer to the lower edge 17 than the opening starting means 14. Therefore, at least the upper end 20d of the occlusal tool 20 is formed so as to be located closer to the lower edge 17 than the opening start means 14.

＜＜ガセット部＞＞
底面フィルム３の第１部分３ｆと、表面フィルム１の底面フィルム３の第１部分３ｆに対応する部分と、で第１ひだ部が形成され、そして、底面フィルム３の第２部分３ｇと、裏面フィルム２の底面フィルム３の第２部分３ｇに対応する部分と、で第２ひだ部が形成されている。そして、第１ひだ部と第２ひだ部とで、ガセット部９が形成されている。図１の正面図においては、折込部３ａより下方において、第１ひだ部が見える状態となっている。第１の実施形態においては、ガセット部９を形成するために、底面フィルム３の折込部３ａが上縁１６側に形成されている。すなわち、折込部３ａが上縁１６を向き、端部３ｈが下縁１７側を向くように配置されて形成されている。 << Gusset section >>
The first fold portion is formed by the first portion 3f of the bottom film 3 and the portion corresponding to the first portion 3f of the bottom film 3 of the surface film 1, and the second portion 3g of the bottom film 3 and the back surface. A second fold portion is formed by a portion corresponding to the second portion 3g of the bottom surface film 3 of the film 2. A gusset portion 9 is formed by the first fold portion and the second fold portion. In the front view of FIG. 1, the first fold portion can be seen below the folding portion 3a. In the first embodiment, in order to form the gusset portion 9, the folded portion 3a of the bottom film 3 is formed on the upper edge 16 side. That is, the folded portion 3a is arranged so as to face the upper edge 16 and the end portion 3h faces the lower edge 17 side.

従来のスタンディングパウチでは、ガセット部は、その下端が下縁１７にほとんど達するような位置に形成されている。これに対して、本実施形態のパウチでは、ガセット部９の下端となる底面フィルム３の折込部３ａと対向する２つの端部３ｈが、下縁１７から離れた位置になるように形成されている。底面フィルム３の折込部３ａと対向する２つの端部３ｈと、下縁１７との位置関係は、適宜設定することができる。ただし、本実施形態では、上縁１６から下縁１７までの距離をＬ１、第２底部シール部６ｂの重心位置から上縁１６までの距離をＬ２としたとき、距離Ｌ２の距離Ｌ１に対する比率である距離Ｌ２／距離Ｌ１が０．４以上０．９以下であることが好ましく、０．４以上０．７以下であることがより好ましい。距離Ｌ２／距離Ｌ１が上記下限より小さい場合は、収容部１１の大きさが相対的に小さくなり過ぎてしまい、距離Ｌ２／距離Ｌ１が上記上限より大きい場合は、上縁１６が下方を向いてしまう可能性が高まってしまうためである。２つの端部３ｈより下縁１７寄りの部分（上げ底部分）は、壁かけ時に支えになる。 In the conventional standing pouch, the gusset portion is formed at a position where the lower end thereof almost reaches the lower edge 17. On the other hand, in the pouch of the present embodiment, the two end portions 3h facing the folded portion 3a of the bottom film 3 which is the lower end of the gusset portion 9 are formed so as to be located away from the lower edge 17. There is. The positional relationship between the two end portions 3h facing the folded portion 3a of the bottom film 3 and the lower edge 17 can be appropriately set. However, in the present embodiment, when the distance from the upper edge 16 to the lower edge 17 is L1 and the distance from the center of gravity position of the second bottom seal portion 6b to the upper edge 16 is L2, the ratio of the distance L2 to the distance L1 is used. A certain distance L2 / distance L1 is preferably 0.4 or more and 0.9 or less, and more preferably 0.4 or more and 0.7 or less. If the distance L2 / distance L1 is smaller than the above lower limit, the size of the accommodating portion 11 becomes relatively too small, and if the distance L2 / distance L1 is larger than the above upper limit, the upper edge 16 faces downward. This is because there is a high possibility that it will end up. The portion closer to the lower edge 17 than the two end portions 3h (raised bottom portion) serves as a support when hanging on the wall.

図３は、円弧状部分を備えたフックにより、本実施形態のパウチを吊り下げた状態を示す正面図である。図３の例では、上部シール予定部４ａにヒートシールがされて上部シール部４が形成された後の状態のパウチを示している。図１（ｃ）に示すように、第１底部シール部６ａでは、表面フィルム１と裏面フィルム２が接合されておらず外部に連通する空間が存在し、第２底部シール部６ｂでは、表面フィルム１と裏面フィルム２が接合されている。第１底部シール部６ａにおける外部に連通する空間がフック挿入孔としての機能を果たす。このため、図３に示すように、側壁Ｋから突出するような円弧状部分を備えたフックＨの先端を第１底部シール部６ａに差し込むことにより、第２底部シール部６ｂの下方を支持し、パウチを吊り下げることができる。 FIG. 3 is a front view showing a state in which the pouch of the present embodiment is suspended by a hook provided with an arc-shaped portion. In the example of FIG. 3, the pouch in the state after the upper seal portion 4a is heat-sealed to form the upper seal portion 4 is shown. As shown in FIG. 1 (c), in the first bottom sealing portion 6a, the front surface film 1 and the back surface film 2 are not joined and there is a space that communicates with the outside, and in the second bottom sealing portion 6b, the surface film 1 and the back surface film 2 are joined. The space communicating with the outside in the first bottom seal portion 6a functions as a hook insertion hole. Therefore, as shown in FIG. 3, the lower end of the second bottom seal portion 6b is supported by inserting the tip of the hook H having an arc-shaped portion protruding from the side wall K into the first bottom seal portion 6a. , The pouch can be hung.

このとき、第２底部シール部６ｂが、距離Ｌ２の距離Ｌ１に対する比率である距離Ｌ２／距離Ｌ１が０．４以上０．９以下で形成されており、フックＨが側壁Ｋから延びていることにより、下縁１７と一方の側縁が交差する下端部が、側壁Ｋで抑えられ、上縁１６が下方に向くことを抑止することができる。図３の例では、上縁１６が水平方向を向いた図１の状態から２０°傾いた状態となっている。 At this time, the second bottom seal portion 6b is formed so that the distance L2 / distance L1 which is the ratio of the distance L2 to the distance L1 is 0.4 or more and 0.9 or less, and the hook H extends from the side wall K. As a result, the lower end portion where the lower edge 17 and one side edge intersect is suppressed by the side wall K, and the upper edge 16 can be prevented from facing downward. In the example of FIG. 3, the upper edge 16 is tilted by 20 ° from the state of FIG. 1 facing the horizontal direction.

一般に、店舗等で商品を吊り下げるためのフックＨは、鉛直方向に沿った側壁Ｋから延びるように設置されていることが多い。本実施形態のパウチは、第２底部シール部６ｂが、距離Ｌ２の距離Ｌ１に対する比率である距離Ｌ２／距離Ｌ１が０．４以上０．９以下で形成された構成であることにより、内容物が底面フィルム３で形成される底部に保持された状態で陳列等を行うことができる。すなわち上縁１６が上方を向いた状態から大きく傾かないような状態で陳列することができる。また、フックＨにより吊り下げられた状態で、開封開始手段１４を用いて開封して内容物の一部を取り出した後、咬合具２０を用いて再封するなどして利用することもできる。距離Ｌ２／距離Ｌ１＝０．９の場合のように、少しでも上げ底になっていれば、すなわち底面フィルム３の下端が下縁１７から離れた位置に形成されていれば、上げ底部分が側壁Ｋと当たりやすく、傾きを抑え易くなる。ただし、距離Ｌ２／距離Ｌ１が大きいと、パウチの重心位置が低すぎて内容物の重さに負ける可能性が高くなるので、距離Ｌ２／距離Ｌ１は０．４以上０．７以下がより好ましい。 In general, the hook H for suspending a product in a store or the like is often installed so as to extend from a side wall K along the vertical direction. The pouch of the present embodiment has a structure in which the second bottom seal portion 6b is formed so that the distance L2 / distance L1 which is the ratio of the distance L2 to the distance L1 is 0.4 or more and 0.9 or less. Can be displayed or the like while being held by the bottom portion formed of the bottom surface film 3. That is, the display can be performed in a state in which the upper edge 16 does not tilt significantly from the state in which it faces upward. Further, it can also be used by opening the package with the opening start means 14 in a state of being suspended by the hook H, taking out a part of the contents, and then resealing the contents with the occlusal tool 20. As in the case of distance L2 / distance L1 = 0.9, if the bottom is raised even a little, that is, if the lower end of the bottom film 3 is formed at a position away from the lower edge 17, the raised bottom portion is the side wall K. It is easy to hit and it is easy to suppress the inclination. However, if the distance L2 / distance L1 is large, the position of the center of gravity of the pouch is too low and there is a high possibility that the weight of the contents will be lost. Therefore, the distance L2 / distance L1 is more preferably 0.4 or more and 0.7 or less. ..

＜＜収容部＞＞
開口部１５を介して内容物が収容された後、図１において４ａと示されている上部シール予定部４ａ（一点鎖線より上側）に上部シール部４が形成され、パウチが封止される。上部シール部４は、第１側部シール部５ａから第２側部シール部５ｂに亘って形成される。収容部１１は、第１側部シール部５ａの内縁と、第２側部シール部５ｂの内縁と、第１底部シール部６ａの内縁と、上部シール部４の内縁と、で画成されている。 << Containment section >>
After the contents are accommodated through the opening 15, the upper seal portion 4 is formed on the upper seal planned portion 4a (above the alternate long and short dash line) shown as 4a in FIG. 1, and the pouch is sealed. The upper seal portion 4 is formed from the first side seal portion 5a to the second side seal portion 5b. The accommodating portion 11 is defined by an inner edge of the first side seal portion 5a, an inner edge of the second side seal portion 5b, an inner edge of the first bottom seal portion 6a, and an inner edge of the upper seal portion 4. There is.

＜＜内容物＞＞
内容物としては、食品、非食品等、様々なものが挙げられる。食品の場合、グミ、チョコレート、ピーナッツ、スナック菓子等を挙げることができる。非食品の場合、消臭剤、芳香剤、防虫剤等を挙げることができる。また、固形物だけでなく、粉体や液体を内容物とすることもできる。 << Contents >>
Examples of the contents include various things such as foods and non-foods. In the case of foods, gummies, chocolates, peanuts, snacks and the like can be mentioned. In the case of non-food products, deodorants, air fresheners, insect repellents and the like can be mentioned. Moreover, not only a solid substance but also a powder or a liquid can be used as the content.

＜＜フィルムの詳細＞＞
パウチの表面・裏面・底面は、積層フィルムである表面フィルム１・裏面フィルム２・底面フィルム３により構成することができる。積層フィルムは、少なくとも、外側から、基材層、シーラント層を含む積層体である。例えば、積層フィルムは、外側から順に、基材層、印刷層、他の層、シーラント層を積層して形成されている。印刷層、他の層は必須ではない。シーラント層は、パウチの最内面を構成する層である。パウチが熱に対する耐性を必要とされる場合は、基材層は、耐熱性をもつ材料からなることが好ましい。例えば、基材層の材料としては、ポリエチレンテレフタレート、ポリブチレンテレフタレートなどのポリエステルフィルム、ナイロンなどのポリアミドフィルム、ポリプロピレンフィルムなどを用いることができる。厚みは、１０μｍ〜５０μｍ程度である。基材層は、二軸延伸されていることが好ましい。 << Details of film >>
The front surface, back surface, and bottom surface of the pouch can be composed of a front surface film 1, a back surface film 2, and a bottom surface film 3, which are laminated films. The laminated film is a laminated body including at least a base material layer and a sealant layer from the outside. For example, the laminated film is formed by laminating a base material layer, a printing layer, another layer, and a sealant layer in this order from the outside. The print layer and other layers are not essential. The sealant layer is a layer that constitutes the innermost surface of the pouch. If the pouch is required to be heat resistant, the substrate layer is preferably made of a heat resistant material. For example, as the material of the base material layer, a polyester film such as polyethylene terephthalate and polybutylene terephthalate, a polyamide film such as nylon, and a polypropylene film can be used. The thickness is about 10 μm to 50 μm. The base material layer is preferably biaxially stretched.

また、積層フィルムは、複数の基材層を備えていてもよい。複数の基材層として第１基材層、第２基材層を備えることができる。第１基材層、第２基材層としては、上記材料の中から、適宜組み合わせて採用することができる。例えば、最外層である第１基材層としてポリエチレンテレフタレートを用い、内層（シーラント層側）である第２基材層としてポリアミドを用いることができる。第２基材層は、一方の側縁から他方の側縁に向かって延伸されている。第２基材層としては、例えば、バリア性に優れたＭＸＤ（メタキシレンジアミン）を含む、ユニチカ株式会社製「エンブレム（登録商標）ＮＣ」を用いることができる。また、第２基材層として、ユニチカ株式会社製「エンブレット（登録商標）ＰＣ」や、ユニチカ株式会社製「エンブレット（登録商標）ＰＣＢＣ」などのポリエステルを用いてもよい。第１基材層と第２基材層は、例えばドライラミネート法を用いて積層することができる。 Further, the laminated film may include a plurality of base material layers. A first base material layer and a second base material layer can be provided as a plurality of base material layers. As the first base material layer and the second base material layer, the above materials can be appropriately combined and adopted. For example, polyethylene terephthalate can be used as the outermost first base material layer, and polyamide can be used as the second base material layer which is the inner layer (sealant layer side). The second substrate layer extends from one side edge to the other side edge. As the second base material layer, for example, "Emblem (registered trademark) NC" manufactured by Unitika Ltd. containing MXD (methxylylenediamine) having excellent barrier properties can be used. Further, as the second base material layer, polyester such as "Emblet (registered trademark) PC" manufactured by Unitika Ltd. or "Emblet (registered trademark) PCBC" manufactured by Unitika Ltd. may be used. The first base material layer and the second base material layer can be laminated by using, for example, a dry laminating method.

印刷層は、商品内容を表示したり美感を付与したりカット部分を表示したりするために設けられる。印刷層は、バインダーと顔料を含む印刷インキにより形成される。シーラント層は、積層フィルムのうち、製袋してパウチとするときの最も内方となる側に配置される。シーラント層の材料としては、ポリエチレン、ポリプロピレン、エチレン−酢酸ビニル共重合体、エチレン−プロピレンブロック共重合体などのポリオレフィン系樹脂などが採用できる。シーラント層の厚みは、３０μｍ以上１００μｍ以下である。シーラント層は無延伸であることが好ましい。 The print layer is provided to display the product contents, give an aesthetic impression, and display the cut portion. The printing layer is formed by a printing ink containing a binder and a pigment. The sealant layer is arranged on the innermost side of the laminated film when the bag is made into a pouch. As the material of the sealant layer, polyolefin resins such as polyethylene, polypropylene, ethylene-vinyl acetate copolymer, and ethylene-propylene block copolymer can be adopted. The thickness of the sealant layer is 30 μm or more and 100 μm or less. The sealant layer is preferably non-stretched.

積層フィルムは、他の層を含んでいてもよい。他の層は、基材層の外側に設けられていてもよいし、基材層とシーラント層の間に設けられていてもよい。他の層としては、水蒸気その他のガスバリア性、遮光性など、必要とされる機能に応じて、適切なものが選択される。例えば、他の層がガスバリア層の場合、アルミニウムなどの金属や酸化アルミニウムなどの金属酸化物や酸化珪素などの無機酸化物の蒸着層が設けられる。蒸着層は、基材層に積層してもよいし、シーラント層に蒸着してもよい。あるいは、アルミニウムなどの金属箔を設けてもよい。その他にも、エチレン−ビニルアルコール共重合体（ＥＶＯＨ）、ポリ塩化ビニリデン樹脂（ＰＶＤＣ）や、ナイロンＭＸＤ６などの芳香族ポリアミド等の、ガスバリア性を有する樹脂層を設けてもよい。各層は、ドライラミネート法や溶融押し出し法などを用いて積層することができる。 The laminated film may include other layers. The other layer may be provided outside the base material layer, or may be provided between the base material layer and the sealant layer. As the other layer, an appropriate layer is selected according to the required functions such as water vapor and other gas barrier properties and light shielding properties. For example, when the other layer is a gas barrier layer, a vapor deposition layer of a metal such as aluminum, a metal oxide such as aluminum oxide, or an inorganic oxide such as silicon oxide is provided. The thin-film deposition layer may be laminated on the base material layer or may be vapor-deposited on the sealant layer. Alternatively, a metal foil such as aluminum may be provided. In addition, a resin layer having a gas barrier property such as an ethylene-vinyl alcohol copolymer (EVOH), a polyvinylidene chloride resin (PVDC), or an aromatic polyamide such as nylon MXD6 may be provided. Each layer can be laminated by using a dry laminating method, a melt extrusion method, or the like.

＜＜開封手段＞＞
本実施形態では、咬合具２０と上縁１６との間に開封手段が形成されている。開封手段は、易開封線１９と開封開始手段１４からなる。開封開始手段１４は切り込みであり、第１側部シール部５ａおよび第２側部シール部５ｂに設けられている。開封開始手段１４は切り欠きであってもよい。これらの開封開始手段は、第１側部シール部５ａおよび第２側部シール部５ｂのどちらか一方のみに設けるようにしてもよい。易開封線１９は、第１側部シール部５ａから第２側部シール部５ｂに向かって延びる線である。易開封線は、基材層を貫通し、且つ、シーラント層を貫通しないハーフカット線としてもよい。ハーフカット線は、刃物を用いて形成してもよいし、レーザー加工により形成してもよい。また、易開封線１９は、連続的に延びる線であってもよいし、断続的に延びる線であってもよい。また、易開封線１９は、パウチの一方の側縁から他方の側縁に至るように設けてもよい。 << Opening means >>
In the present embodiment, an opening means is formed between the occlusal tool 20 and the upper edge 16. The opening means includes an easy-opening line 19 and an opening starting means 14. The opening start means 14 is a notch and is provided in the first side seal portion 5a and the second side seal portion 5b. The opening start means 14 may be a notch. These opening start means may be provided only on either one of the first side seal portion 5a and the second side seal portion 5b. The easy-opening line 19 is a line extending from the first side sealing portion 5a toward the second side sealing portion 5b. The easy-open wire may be a half-cut wire that penetrates the base material layer and does not penetrate the sealant layer. The half-cut line may be formed by using a cutting tool or by laser processing. Further, the easy-opening line 19 may be a line extending continuously or a line extending intermittently. Further, the easy-opening line 19 may be provided so as to extend from one side edge of the pouch to the other side edge.

本実施形態では、易開封線１９をハーフカット線により実現している。ここで、ハーフカット線とは、積層フィルムの全ての層を貫通しない線を意味する。本実施形態では、易開封線１９は、積層フィルムの最外面となる基材層のみを貫通するハーフカット線となっている。 In the present embodiment, the easy-opening line 19 is realized by a half-cut line. Here, the half-cut line means a line that does not penetrate all the layers of the laminated film. In the present embodiment, the easy-opening wire 19 is a half-cut wire that penetrates only the base material layer that is the outermost surface of the laminated film.

＜＜開閉手段＞＞
開閉手段である咬合具２０について説明する。図４は、咬合具２０の断面図である。このうち、図４は、図１に示すＢ−Ｂ線に対応する断面図である。咬合具２０は、開封によって生じた開口を再封するため、表面フィルム１、裏面フィルム２の互いに対向する内面側に形成されている。図１、図４に示すように、表面フィルム１と裏面フィルム２は、咬合具２０により封止される。図１、図４に示すように、帯状の咬合具２０は、上縁１６側に上縁１６の長手方向（図１における左右方向）に沿って設けられており、雄部材２１は帯状の第一基部２１ａと、第一基部２１ａの一方の側に雄型咬合部２１ｂを備え、第一基部２１ａの他方の側は表面フィルム１に接合されている。雌部材２２は帯状の第二基部２２ａと、第二基部２２ａの一方の側に雌型咬合部２２ｂを備え、第二基部２２ａの他方の側は裏面フィルム２に接合されている。 << Opening and closing means >>
The occlusal tool 20 which is an opening / closing means will be described. FIG. 4 is a cross-sectional view of the occlusal tool 20. Of these, FIG. 4 is a cross-sectional view corresponding to line BB shown in FIG. The occlusal tool 20 is formed on the inner surface side of the front surface film 1 and the back surface film 2 facing each other in order to reseal the opening created by opening. As shown in FIGS. 1 and 4, the front surface film 1 and the back surface film 2 are sealed by the occlusal tool 20. As shown in FIGS. 1 and 4, the band-shaped occlusal tool 20 is provided on the upper edge 16 side along the longitudinal direction of the upper edge 16 (left-right direction in FIG. 1), and the male member 21 is a band-shaped first member. A male occlusal portion 21b is provided on one side of a base portion 21a and a first base portion 21a, and the other side of the first base portion 21a is joined to the surface film 1. The female member 22 is provided with a band-shaped second base portion 22a and a female occlusal portion 22b on one side of the second base portion 22a, and the other side of the second base portion 22a is joined to the back surface film 2.

このような上縁１６に沿って形成された咬合具２０は、いわゆるジッパーとして用いることができ、収容部１１を開封したり、再封したりする開閉手段として機能する。なお、咬合具２０は図１、図４に限定されるものではなく、第一基部２１ａは裏面フィルム２に接合され、第二基部２２ａは第一基部２１ａと反対側の表面フィルム１に接合されていてもよい。 The occlusal tool 20 formed along the upper edge 16 can be used as a so-called zipper, and functions as an opening / closing means for opening or resealing the accommodating portion 11. The occlusal tool 20 is not limited to FIGS. 1 and 4, and the first base portion 21a is joined to the back surface film 2 and the second base portion 22a is joined to the front surface film 1 on the opposite side of the first base portion 21a. May be.

咬合具２０の材料としては、パウチの表面フィルム１及び裏面フィルム２のシーラント層と相溶性を有する樹脂を用いることができる。咬合具２０は、図４に示すように雄部材２１と雌部材２２からなり、雄部材２１は表面フィルム１に、雌部材２２は裏面フィルム２にヒートシールされる。ヒートシール時には、雄部材２１と雌部材２２の間に遮熱板（図示省略）を介在させることにより、雄部材２１と雌部材２２の熱融着を防止する。図１、図４に示した例では、開閉手段として咬合具２０を用いた例について説明したが、収容部の開口を開閉することができれば、公知の他の開閉手段を用いてもよい。 As the material of the occlusal tool 20, a resin having compatibility with the sealant layer of the front surface film 1 and the back surface film 2 of the pouch can be used. As shown in FIG. 4, the occlusal tool 20 is composed of a male member 21 and a female member 22, and the male member 21 is heat-sealed on the front surface film 1 and the female member 22 is heat-sealed on the back surface film 2. At the time of heat sealing, a heat shield plate (not shown) is interposed between the male member 21 and the female member 22 to prevent heat fusion between the male member 21 and the female member 22. In the examples shown in FIGS. 1 and 4, an example in which the occlusal tool 20 is used as the opening / closing means has been described, but other known opening / closing means may be used as long as the opening of the accommodating portion can be opened / closed.

＜＜製造方法＞＞
３枚の積層フィルムである表面フィルム１、裏面フィルム２、底面フィルム３を用意する。そして、図２に示すように、表面フィルム１、裏面フィルム２に対しては、互いに対向しない側の面である最外側の基材層に、易開封線１９を形成する。さらに、表面フィルム１、裏面フィルム２に対しては、互いに対向する側の面である最内側のシーラント層に、咬合具２０の雄部材２１、雌部材２２をそれぞれ接合する。そして、図２に示すように、底面フィルム３を折込部３ａで折り返し、折込部３ａを上縁１６側、端部３ｈ、３ｈを下縁１７側に向けて、表面フィルム１、裏面フィルム２の間に挟み込む。そして、側部、底部をヒートシールすることにより、第１側部シール部５ａ、第２側部シール部５ｂ、第１底部シール部６ａ、第２底部シール部６ｂが形成され、図１に示したような開口部１５を有するパウチが得られる。そして、内容物を開口部１５から充填し、収容部１１に収容した後、上部をヒートシールして上部シール部を形成することにより、内容物が収容されたパウチが得られる。 << Manufacturing method >>
Prepare the front surface film 1, the back surface film 2, and the bottom surface film 3 which are three laminated films. Then, as shown in FIG. 2, the easy-opening line 19 is formed on the outermost base material layer, which is a surface on the side that does not face each other with respect to the front surface film 1 and the back surface film 2. Further, with respect to the front surface film 1 and the back surface film 2, the male member 21 and the female member 22 of the occlusal tool 20 are joined to the innermost sealant layer, which is a surface facing each other. Then, as shown in FIG. 2, the bottom surface film 3 is folded back at the folding portion 3a, the folding portion 3a is directed to the upper edge 16 side, the end portions 3h and 3h are directed to the lower edge 17 side, and the front surface film 1 and the back surface film 2 are formed. Put it in between. Then, by heat-sealing the side portion and the bottom portion, the first side portion seal portion 5a, the second side portion seal portion 5b, the first bottom portion seal portion 6a, and the second bottom portion seal portion 6b are formed, and are shown in FIG. A pouch having such an opening 15 is obtained. Then, after filling the contents through the opening 15 and accommodating them in the accommodating portion 11, the upper portion is heat-sealed to form the upper sealing portion, whereby a pouch containing the contents can be obtained.

＜＜使用時における開封について＞＞
内容物が収容されたパウチは、製品として市場に流通し、店舗等に陳列され最終消費者に届けられる。消費者は、切り込み等の開封開始手段１４から開封を開始する。具体的には、開封開始手段１４の上側と下側をそれぞれ掴み、互いに逆方向に力を加えることにより、切り込みを拡大する。さらに、力を加えると、易開封線１９に沿って表面フィルム１、裏面フィルムの基材層以外の層にも切り込みが入り、パウチの易開封線１９より上側の部分が分離される。 << About opening when using >>
The pouch containing the contents is distributed to the market as a product, displayed in stores, etc., and delivered to the final consumer. The consumer starts opening from the opening starting means 14 such as a notch. Specifically, the cut is enlarged by grasping the upper side and the lower side of the opening start means 14, respectively, and applying forces in opposite directions to each other. Further, when a force is applied, a cut is made in a layer other than the base film layer of the front surface film 1 and the back surface film along the easy-opening line 19, and the portion above the easy-opening line 19 of the pouch is separated.

この状態で、収容部１１から内容物を自由に取り出すことが可能になる。そして、内容物の一部が残っている場合等には、咬合具２０の雄部材２１と雌部材２２を咬み合わせてパウチを再封することができる。 In this state, the contents can be freely taken out from the accommodating portion 11. Then, when a part of the contents remains, the male member 21 and the female member 22 of the occlusal tool 20 can be occluded to reseal the pouch.

＜＜第２の実施形態＞＞
第２の実施形態について説明する。図５は、本発明第２の実施形態に係るパウチを示す正面図である。図５（ａ）は、表面側から見た正面図であり、図５（ｂ）は、図５（ａ）のＣ−Ｃ線に対応する断面図であり、図５（ｃ）は、図１（ａ）のＥ−Ｅ線に対応する断面図である。図５に示した第２の実施形態のパウチは、図１に示した第１の実施形態と同様、内容物が充填される前の状態（内容物が充填されていない状態）のパウチを示したものである。第２の実施形態のパウチについては、第１の実施形態のパウチとの相違点を中心に説明し、第１の実施形態のパウチと同様の点については、説明を省略する。 << Second Embodiment >>
A second embodiment will be described. FIG. 5 is a front view showing a pouch according to a second embodiment of the present invention. 5 (a) is a front view seen from the front surface side, FIG. 5 (b) is a cross-sectional view corresponding to line CC of FIG. 5 (a), and FIG. 5 (c) is a view. It is sectional drawing corresponding to line EE of 1 (a). The pouch of the second embodiment shown in FIG. 5 shows a pouch in a state before the contents are filled (a state in which the contents are not filled), similarly to the first embodiment shown in FIG. It is. The pouch of the second embodiment will be described mainly on the differences from the pouch of the first embodiment, and the same points as the pouch of the first embodiment will be omitted.

第２の実施形態においては、底面フィルム３の構造自体は、第１の実施形態と同様であるが、底面フィルム３の配置の向きが第１の実施形態とは上下反転した状態となっている。具体的には、第１の実施形態では、図１に示すように、折込部３ａを上縁１６側に向けた状態で配置しているが、第２の実施形態では、図５に示すように、折込部３ａを下縁１７側に向け、端部３ｈ、３ｈを上縁１６側に向けた状態で配置している。したがって、底面フィルム３の折込部３ａが下縁１７側に形成されている。すなわち、折込部３ａが下縁１７を向き、端部３ｈが上縁１６側を向くように配置されて形成されている。 In the second embodiment, the structure of the bottom film 3 itself is the same as that of the first embodiment, but the orientation of the bottom film 3 is upside down from that of the first embodiment. .. Specifically, in the first embodiment, as shown in FIG. 1, the folding portion 3a is arranged in a state of facing the upper edge 16 side, but in the second embodiment, as shown in FIG. The folding portion 3a is arranged toward the lower edge 17 side, and the end portions 3h and 3h are arranged toward the upper edge 16 side. Therefore, the folded portion 3a of the bottom film 3 is formed on the lower edge 17 side. That is, the folded portion 3a is arranged so as to face the lower edge 17 and the end portion 3h faces the upper edge 16 side.

また、第２の実施形態においては、底面フィルム３を、表面フィルム１、裏面フィルム２と接合したシール部の位置が、第１の実施形態とは異なっている。具体的には、第１の実施形態では、図１に示すように、第１底部シール部６ａを船底状に形成しているが、第２の実施形態では、図５に示すように、上下の２つに分かれた第１側部シール部５ａを結ぶ部分と、上下の２つに分かれた第２側部シール部５ｂを結ぶ部分のみである。２つの第１底部シール部６ａは、それぞれ第１側縁、第２側縁を含むように形成されている。 Further, in the second embodiment, the position of the sealing portion where the bottom surface film 3 is joined to the front surface film 1 and the back surface film 2 is different from that of the first embodiment. Specifically, in the first embodiment, as shown in FIG. 1, the first bottom seal portion 6a is formed in the shape of the bottom of the ship, but in the second embodiment, as shown in FIG. 5, the upper and lower parts are formed. There is only a portion connecting the first side seal portion 5a divided into the two parts and a portion connecting the second side seal portion 5b divided into the upper and lower parts. The two first bottom seal portions 6a are formed so as to include a first side edge and a second side edge, respectively.

第１の実施形態では、折込部３ａが上縁１６側に向けて形成されているので、第１底部シール部６ａを第１側縁から第２側縁に亘って形成しないと、内容物が下方から脱落する可能性がある。このため、第１底部シール部６ａを船底状に形成し、収容部１１の下方を封止している。これに対して、第２の実施形態では、折込部３ａが下縁１７側に向けて形成されているので、折込部３ａが底となって、内容物が下方から脱落することを防ぐことができる。このため、第２の実施形態では、第１底部シール部６ａを、第１側部シール部５ａ、第２側部シール部５ｂに沿った所定の範囲にのみ形成するだけでよい。 In the first embodiment, since the folding portion 3a is formed toward the upper edge 16 side, the contents must be formed from the first side edge to the second side edge unless the first bottom sealing portion 6a is formed. It may fall off from below. Therefore, the first bottom seal portion 6a is formed in the shape of the bottom of the ship, and the lower part of the accommodating portion 11 is sealed. On the other hand, in the second embodiment, since the folding portion 3a is formed toward the lower edge 17 side, the folding portion 3a becomes the bottom and the contents can be prevented from falling off from below. it can. Therefore, in the second embodiment, it is only necessary to form the first bottom seal portion 6a only in a predetermined range along the first side seal portion 5a and the second side seal portion 5b.

第１底部シール部６ａは、表面フィルム１と底面フィルム３の第１部分３ｆ、および、裏面フィルム２と底面フィルム３の第２部分３ｇがシールされたものであり、第２底部シール部６ｂは、表面フィルム１と裏面フィルム２が直接シールされたものである点は、第１の実施形態と同様である。したがって、図５（ｃ）に示すように、第１底部シール部６ａにおいては、底面フィルム３の第１部分３ｆと第２部分３ｇの間が接合されていないことになる。このため、収容部１１が第１底部シール部６ａを介して外部に連通することになる。このような構造から、第２の実施形態のパウチでは、内容物として粉体や液体を収容することはできない。したがって、第２の実施形態のパウチでは、内容物としては、個包装されたものが好ましく、２次包装に向いている。 The first bottom sealing portion 6a is formed by sealing the first portion 3f of the front surface film 1 and the bottom film 3, and the second portion 3g of the back surface film 2 and the bottom film 3, and the second bottom sealing portion 6b is formed. , The point that the front surface film 1 and the back surface film 2 are directly sealed is the same as that of the first embodiment. Therefore, as shown in FIG. 5C, in the first bottom sealing portion 6a, the first portion 3f and the second portion 3g of the bottom film 3 are not joined. Therefore, the accommodating portion 11 communicates with the outside via the first bottom seal portion 6a. Due to such a structure, the pouch of the second embodiment cannot contain powder or liquid as the contents. Therefore, in the pouch of the second embodiment, the contents are preferably individually wrapped and suitable for secondary packaging.

図６は、円弧状部分を備えたフックにより、第２の実施形態のパウチを吊り下げた状態を示す正面図である。図６の例では、上部シール予定部４ａにヒートシールがされて上部シール部４が形成された後の状態を示している。上述のように、第１底部シール部６ａでは、表面フィルム１と裏面フィルム２が接合されておらず外部に連通する空間が存在し、第２底部シール部６ｂでは、表面フィルム１と裏面フィルム２が接合されている。このため、図６に示すように、側壁Ｋから突出するような円弧状部分を備えたフックＨの先端を第１底部シール部６ａに差し込むことにより、第２底部シール部６ｂの下方を支持し、パウチを吊り下げることができる。すなわち上縁１６が上方を向いた状態から大きく傾かないような状態で陳列することができる。 FIG. 6 is a front view showing a state in which the pouch of the second embodiment is suspended by a hook provided with an arc-shaped portion. In the example of FIG. 6, the state after the planned upper seal portion 4a is heat-sealed to form the upper seal portion 4 is shown. As described above, in the first bottom sealing portion 6a, the front surface film 1 and the back surface film 2 are not bonded and there is a space for communicating with the outside, and in the second bottom sealing portion 6b, the front surface film 1 and the back surface film 2 are present. Are joined. Therefore, as shown in FIG. 6, the lower end of the second bottom seal portion 6b is supported by inserting the tip of the hook H having an arc-shaped portion protruding from the side wall K into the first bottom seal portion 6a. , The pouch can be hung. That is, the display can be performed in a state in which the upper edge 16 does not tilt significantly from the state in which it faces upward.

＜＜実施例１＞＞
厚みが１２μｍのＰＥＴフィルムに印刷層を形成した後、接着剤層を介して印刷層の面と厚み７μｍのアルミニウム箔を貼り合わせた。続いて、接着剤層を介してアルミニウム箔と厚み４０μｍの無延伸ポリプロピレン（ＣＰＰ）フィルムを貼り合わせた。これにより、ポリエチレンテレフタレート／印刷層／接着剤層（ＤＬ）／アルミニウム箔（ＡＬ）／接着剤層（ＤＬ）／無延伸ポリプロピレン（ＣＰＰ）が順に積層された積層フィルムである表面フィルム１、裏面フィルム２、底面フィルム３を形成した。接着剤層は、アクリルポリオールとイソシアネート化合物との硬化物である。 << Example 1 >>
After forming a print layer on a PET film having a thickness of 12 μm, the surface of the print layer and an aluminum foil having a thickness of 7 μm were bonded to each other via an adhesive layer. Subsequently, the aluminum foil and the unstretched polypropylene (CPP) film having a thickness of 40 μm were bonded to each other via the adhesive layer. As a result, the front surface film 1 and the back surface film, which are laminated films in which polyethylene terephthalate / printing layer / adhesive layer (DL) / aluminum foil (AL) / adhesive layer (DL) / unstretched polypropylene (CPP) are laminated in this order. 2. The bottom film 3 was formed. The adhesive layer is a cured product of an acrylic polyol and an isocyanate compound.

続いて、表面フィルム１、裏面フィルム２の最外面となる基材層側からレーザーによりハーフカット加工を行い、基材層であるポリエチレンテレフタレートを貫通し、中間層であるアルミニウム箔に達しない易開封線１９を形成した。 Subsequently, half-cut processing is performed by a laser from the base material layer side which is the outermost surface of the front surface film 1 and the back surface film 2, and the polyethylene terephthalate which is the base material layer is penetrated and easily opened which does not reach the aluminum foil which is the intermediate layer. Line 19 was formed.

次に、積層フィルムの最内層に位置するシーラント層と相溶性を有する無延伸ポリプロピレン（ＣＰＰ）製の咬合具２０の雄部材２１、雌部材２２を、それぞれ表面フィルム１、裏面フィルム２のシーラント層側にヒートシールして、雄部材２１、雌部材２２を表面フィルム１、裏面フィルム２に固定した。その後、底面フィルム３を折込部３ａにより折り返して、折込部３ａを上縁１６側に向けた状態で表面フィルム１、裏面フィルム２の間に挟み込み、互いにヒートシールして第１側部シール部５ａ、第２側部シール部５ｂ、第１底部シール部６ａ、第２底部シール部６ｂを形成した。すなわち、第１の実施形態であるパウチを形成した。第１側部シール部５ａ、第２側部シール部５ｂにおいて、咬合具２０が存在する箇所では、雄部材２１、雌部材２２が溶ける温度でヒートシールを行い、一体となって表面フィルム１、裏面フィルム２に固着された。 Next, the male member 21 and the female member 22 of the occlusal tool 20 made of unstretched polypropylene (CPP) having compatibility with the sealant layer located in the innermost layer of the laminated film are attached to the sealant layers of the front surface film 1 and the back surface film 2, respectively. The male member 21 and the female member 22 were fixed to the front surface film 1 and the back surface film 2 by heat-sealing to the side. After that, the bottom surface film 3 is folded back by the folding portion 3a, sandwiched between the front surface film 1 and the back surface film 2 with the folding portion 3a facing the upper edge 16 side, and heat-sealed with each other to heat-seal the first side portion sealing portion 5a. , The second side seal portion 5b, the first bottom seal portion 6a, and the second bottom seal portion 6b were formed. That is, the pouch which is the first embodiment was formed. In the first side seal portion 5a and the second side seal portion 5b, where the occlusal tool 20 exists, heat sealing is performed at a temperature at which the male member 21 and the female member 22 melt, and the surface film 1 and the surface film 1 are integrated. It was fixed to the back surface film 2.

＜＜実施例２＞＞
積層フィルムの構成を、ポリエチレンテレフタレート（ＰＥＴ）１２μｍ／印刷層／接着剤層（ＤＬ）／真空蒸着ポリエチレンテレフタレート（ＰＥＴ）１２μｍ／アンカーコート（ＡＣ）／ポリエチレン（ＰＥ）２０μｍ／直鎖状低密度ポリエチレン（ＬＬＤＰＥ）４０μｍとし、積層フィルムの最内層に位置するシーラント層と相溶性を有する直鎖状低密度ポリエチレン（ＬＬＤＰＥ）製の咬合具２０を用いた以外は、実施例１と同様にしてパウチを作成した。 << Example 2 >>
The composition of the laminated film is polyethylene terephthalate (PET) 12 μm / printing layer / adhesive layer (DL) / vacuum vapor deposition polyethylene terephthalate (PET) 12 μm / anchor coat (AC) / polyethylene (PE) 20 μm / linear low density polyethylene. The pouch was made in the same manner as in Example 1 except that the bite tool 20 made of linear low density polyethylene (LLDPE) having a thickness of 40 μm and compatible with the sealant layer located in the innermost layer of the laminated film was used. Created.

＜＜実施例３＞＞
積層フィルムの構成を、ポリエチレンテレフタレート（ＰＥＴ）１２μｍ／印刷層／接着剤層（ＤＬ）／延伸ナイロン（ＯＮＹ）１５μｍ／接着剤層（ＤＬ）／直鎖状低密度ポリエチレン（ＬＬＤＰＥ）１００μｍとし、積層フィルムの最内層に位置するシーラント層と相溶性を有する直鎖状低密度ポリエチレン（ＬＬＤＰＥ）製の咬合具２０を用いた以外は、実施例１と同様にしてパウチを作成した。 << Example 3 >>
The structure of the laminated film is polyethylene terephthalate (PET) 12 μm / printing layer / adhesive layer (DL) / stretched nylon (ONY) 15 μm / adhesive layer (DL) / linear low density polyethylene (LLDPE) 100 μm. A pouch was prepared in the same manner as in Example 1 except that a linear low density polyethylene (LLDPE) occlusal tool 20 compatible with the sealant layer located in the innermost layer of the film was used.

＜＜実施例４＞＞
底面フィルム３を折込部３ａにより折り返して、折込部３ａを下縁１７側に向けた状態で表面フィルム１、裏面フィルム２の間に挟み込み、互いにヒートシールして第１側部シール部５ａ、第２側部シール部５ｂ、第１底部シール部６ａ、第２底部シール部６ｂを形成して、第２の実施形態に示した態様のパウチを形成した以外は、実施例１と同様にしてパウチを作成した。 << Example 4 >>
The bottom film 3 is folded back by the folding portion 3a, sandwiched between the front surface film 1 and the back surface film 2 with the folding portion 3a facing the lower edge 17, and heat-sealed with each other to heat-seal the first side portion sealing portion 5a, first. A pouch in the same manner as in the first embodiment except that the two side seal portion 5b, the first bottom seal portion 6a, and the second bottom seal portion 6b are formed to form the pouch of the embodiment shown in the second embodiment. It was created.

＜＜実施例５＞＞
底面フィルム３を折込部３ａにより折り返して、折込部３ａを下縁１７側に向けた状態で表面フィルム１、裏面フィルム２の間に挟み込み、互いにヒートシールして第１側部シール部５ａ、第２側部シール部５ｂ、第１底部シール部６ａ、第２底部シール部６ｂを形成して、第２の実施形態に示した態様のパウチを形成した以外は、実施例２と同様にしてパウチを作成した。 << Example 5 >>
The bottom film 3 is folded back by the folding portion 3a, sandwiched between the front surface film 1 and the back surface film 2 with the folding portion 3a facing the lower edge 17, and heat-sealed with each other to heat-seal the first side portion sealing portion 5a, first. A pouch in the same manner as in the second embodiment except that the two side seal portion 5b, the first bottom seal portion 6a, and the second bottom seal portion 6b are formed to form the pouch of the embodiment shown in the second embodiment. It was created.

＜＜実施例６＞＞
底面フィルム３を折込部３ａにより折り返して、折込部３ａを下縁１７側に向けた状態で表面フィルム１、裏面フィルム２の間に挟み込み、互いにヒートシールして第１側部シール部５ａ、第２側部シール部５ｂ、第１底部シール部６ａ、第２底部シール部６ｂを形成して、第２の実施形態に示した態様のパウチを形成した以外は、実施例３と同様にしてパウチを作成した。 << Example 6 >>
The bottom film 3 is folded back by the folding portion 3a, sandwiched between the front surface film 1 and the back surface film 2 with the folding portion 3a facing the lower edge 17 side, and heat-sealed with each other to heat-seal the first side portion sealing portion 5a, first. A pouch in the same manner as in the third embodiment except that the two side seal portion 5b, the first bottom seal portion 6a, and the second bottom seal portion 6b are formed to form the pouch of the embodiment shown in the second embodiment. It was created.

＜＜評価＞＞
図３、図６に示したように、下方に突出するような円弧状部分を備えたフックＨの先端を第１底部シール部６ａに差し込むことにより、第２底部シール部６ｂの下方を支持し、パウチを吊り下げた。実施例１〜実施例６のいずれのパウチでも、上縁１６が下方に向かない状態で吊り下げることができ、開封開始手段１４を用いて開封した状態でも内容物が零れ落ちなかった。 << Evaluation >>
As shown in FIGS. 3 and 6, the lower end of the second bottom seal portion 6b is supported by inserting the tip of the hook H having an arc-shaped portion so as to project downward into the first bottom seal portion 6a. , Suspended the pouch. In any of the pouches of Examples 1 to 6, the upper edge 16 could be hung without facing downward, and the contents did not spill even when opened by using the opening start means 14.

以上、本発明の好適な実施形態について説明したが、本発明は、上記実施形態に限定されず種々の変形が可能である。例えば、上記実施形態では、表面、裏面、底面を、表面フィルム１、裏面フィルム２、底面フィルム３の３枚のフィルムで構成するようにしたが、２枚のフィルムで構成してもよい。例えば、表面フィルムと裏面フィルムを連設したフィルムと、底面フィルムからなる計２枚のフィルムを用いてパウチの表面、裏面、底面を構成してもよい。この場合、加工工程において、表面フィルムと裏面フィルムを連設したフィルムの上縁１６に相当する位置で折り畳むことにより、表面と裏面に区分される。 Although the preferred embodiment of the present invention has been described above, the present invention is not limited to the above embodiment and can be modified in various ways. For example, in the above embodiment, the front surface, the back surface, and the bottom surface are composed of three films, the front surface film 1, the back surface film 2, and the bottom surface film 3, but the front surface, the back surface, and the bottom surface may be composed of two films. For example, the front surface, the back surface, and the bottom surface of the pouch may be formed by using a film in which a front surface film and a back surface film are continuously provided and a total of two films including the bottom surface film. In this case, in the processing step, the front surface film and the back surface film are divided into a front surface and a back surface by folding at a position corresponding to the upper edge 16 of the film in which the front surface film and the back surface film are continuously provided.

また、上記実施形態に示したパウチに公知の様々な部材を組み合わせるようにしてもよい。例えば、上記実施形態の上縁１６付近に、スパウトを付加するようにしてもよい。スパウト付きのパウチにすることにより、開封後もキャップを再封して補間が可能となる。 Further, various known members may be combined with the pouch shown in the above embodiment. For example, a spout may be added near the upper edge 16 of the above embodiment. By using a pouch with a spout, the cap can be resealed and interpolated even after opening.

１・・・表面フィルム
２・・・裏面フィルム
３・・・底面フィルム
４・・・上部シール部
４ａ・・・上部シール予定部
５ａ・・・第１側部シール部
５ｂ・・・第２側部シール部
６ａ・・・第１底部シール部
６ｂ・・・第２底部シール部
９・・・ガセット部
１１・・・収容部
１４・・・開封開始手段
１５・・・開口部
１６・・・上縁
１７・・・下縁
１９・・・易開封線
２０・・・咬合具（開閉手段）
２０ｄ・・・咬合具の上端
２１・・・雄部材
２１ａ・・・第一基部
２１ｂ・・・雄型咬合部
２２・・・雌部材
２２ａ・・・第二基部
２２ｂ・・・雌型咬合部
Ｌ１・・・上縁１６から下縁１７までの距離
Ｌ２・・・第２底部シール部６ｂの重心位置から上縁１６までの距離
Ｗ１・・・第１側部シール部５ａ、第２側部シール部５ｂのシール幅 1 ... Front surface film 2 ... Back surface film 3 ... Bottom film 4 ... Top seal part 4a ... Top seal planned part 5a ... 1st side seal part 5b ... 2nd side Part seal part 6a ・・・ 1st bottom seal part 6b ・・・ 2nd bottom seal part 9 ・・・ gusset part 11 ・・・ accommodating part 14 ・・・ opening start means 15 ・・・ opening 16 ・・・Upper edge 17 ... Lower edge 19 ... Easy opening line 20 ... Occlusal tool (opening and closing means)
20d ... Upper end of occlusal tool 21 ... Male member 21a ... First base 21b ... Male occlusal part 22 ... Female member 22a ... Second base 22b ... Female occlusal part L1 ... Distance from the upper edge 16 to the lower edge 17 L2 ... Distance from the center of gravity of the second bottom seal portion 6b to the upper edge W1 ... First side seal portion 5a, second side portion Seal width of seal portion 5b

Claims

A pouch having at least a front surface, a back surface, and a bottom surface, and having a lower edge facing the upper edge and an upper edge, and a first side edge and a second side edge extending between the upper edge and the lower edge. ,
The first side seal portion is formed so as to include the first side edge.
The second side seal portion is formed so as to include the second side edge.
The bottom surface is a first bottom seal portion joined to the inner surface side of the front surface and the inner surface side of the back surface, respectively.
It is surrounded by the first bottom seal portion, and has a second bottom seal portion in which the front surface and the back surface are directly joined on the inner surface side thereof.
When the distance from the upper edge to the lower edge is L1 and the distance from the center of gravity of the second bottom seal portion to the upper edge is L2, the distance L2 / distance L1 is 0.4 or more and 0.9 or less. A pouch characterized by that.

The pouch according to claim 1, wherein the folded portion of the bottom surface is formed on the upper edge side.

The pouch according to claim 1, wherein the folded portion of the bottom surface is formed on the lower edge side.

The pouch according to any one of claims 1 to 3, wherein an occlusal tool for resealing after opening is formed on the inner surfaces of the front surface and the back surface facing each other.