JP2020120615A

JP2020120615A - Fishing rod tip

Info

Publication number: JP2020120615A
Application number: JP2019014909A
Authority: JP
Inventors: 博桑原; Hiroshi Kuwabara; 典誠神谷; Tensei Kamiya; 拓梶本; Hiroshi Kajimoto; 潤太郎竹内; Juntaro Takeuchi
Original assignee: Gamakatsu Co Ltd
Current assignee: Gamakatsu Co Ltd
Priority date: 2019-01-30
Filing date: 2019-01-30
Publication date: 2020-08-13

Abstract

To provide an advantageous fishing rod tip having an appropriate size and weight, and actually easy to use.SOLUTION: A fishing rod tip 1 has a taper portion 1b with a tapered shape and is a hollow or solid metal to be connected to a tip of a fishing rod, where the metal is a beta titanium, an outside diameter of a forefront part 1a is 1.5 mm or less, the taper is 8/1000 or more and 20/1000 or less, the full length is 100 mm or more and 200 mm or less, and the beta titanium is Ti-22V-4AL (where a unit for numbers is wt.%) in composition.SELECTED DRAWING: Figure 1

Description

本発明は、釣竿の先に連結されて使用される釣竿穂先に関するものである。 The present invention relates to a fishing rod tip that is used by being connected to the tip of a fishing rod.

各種の釣竿は、繊維強化された樹脂材料で形成されるのが一般的である。しかし最近では、その最先端部分に、弾性に富んだ金属製の穂先をつなぐ例が知られている。負荷が集中しがちな穂先部分の強度を高めるとともに、その金属の撓みやすさに基づいて目視または手感度によって魚信（アタリ）を得やすくするためである。金属製の穂先を使用する釣竿の例は、下記の特許文献１にも示されている。 Various types of fishing rods are generally formed of a fiber-reinforced resin material. However, recently, an example is known in which the tip of the metal, which is rich in elasticity, is connected to the tip of the tip. This is to increase the strength of the tip portion, where the load tends to concentrate, and to make it easier to obtain fish-eye contact by visual or hand sensitivity based on the flexibility of the metal. An example of a fishing rod using a metal tip is also shown in Patent Document 1 below.

特開２０１４−８７３００号公報JP, 2014-87300, A

特許文献１には、繊維強化樹脂材料によって形成された釣竿（穂持部）の先に、金属管材料で形成された穂先（穂先部）を接続することが記載されている。そして当該穂先の金属として、ニッケルチタン等のチタン合金を使用するのがよいとされている。 Patent Document 1 describes connecting a tip (a tip portion) formed of a metal pipe material to a tip of a fishing rod (a tip portion) formed of a fiber reinforced resin material. It is said that a titanium alloy such as nickel titanium is preferably used as the metal of the tip.

しかし、釣竿の先に金属製の穂先を接続して使用するためには、穂先に十分な強度があることに加えて、穂先が重くならずに、つねに適度に撓んでくれること等が重要である。十分な強度が必要であることは言うまでもないが、穂先が重くなると釣竿の使い勝手が悪くなるうえアタリに対する反応が低下する。また、釣糸の張力を受けて適度に撓むようでないと十分な魚信を得ることができない。さらには、その撓み方が夏季にも冬季にも変わらないものであることも求められる。そして当然ながら、金属製穂先のために過剰なコストを要することとなるのは歓迎されない。
特許文献１には金属製穂先の材質や寸法等に関して具体的な記載がなく、そのために、穂先の重量や撓み、コスト等について必ずしも有利なものを提供できるか否か不明であった。 However, in order to connect and use a metal tip to the tip of a fishing rod, it is important that the tip has sufficient strength and that the tip does not become heavy and always bends appropriately. is there. Needless to say, sufficient strength is required, but if the tip becomes heavy, the fishing rod becomes unusable and the reaction to atari deteriorates. In addition, it is not possible to obtain a sufficient fish line unless the fishing line tension causes it to bend appropriately. Furthermore, it is also required that the flexure does not change in summer and winter. And of course, the excessive cost of metal tips is not welcome.
In Patent Document 1, there is no specific description regarding the material, dimensions, etc. of the metal tip, and therefore it was unclear whether or not it is possible to provide an advantageous weight, bending, cost, etc. of the tip.

本願請求項に係る発明は、以上の点から、寸法や重量について好ましく、適度に撓んで魚信を得やすいなど、実際に使いやすい有利な釣竿穂先を提供するものである。 From the above points of view, the invention according to the claims of the present application provides an advantageous fishing rod tip which is preferable in terms of size and weight, and which is easily bent to obtain fish stock and is actually easy to use.

発明による釣竿穂先は、先細りのテーパ部分を有していて釣竿の先に連結される中空（内部に空洞部を有する）または中実（空洞部を有しない）の金属製の釣竿穂先（中空部分と中実部分とをともに有する場合をも含む）であって、
・上記の金属がベータチタンであること、
・最先端部分の外径（直径）が1.5mm以下であること、
・上記のテーパが8/1000以上・20/1000以下であること、
・および、全長が100mm以上・200mm以下であること
を特徴とする。なお、上記テーパの数値は、テーパ部分において先端側の細い部分からの直径の増分を長さで除した値である。 The fishing rod tip according to the present invention has a hollow (having a hollow portion inside) or a solid (without a hollow portion) metal fishing rod tip (a hollow portion) that has a tapered portion and is connected to the tip of the fishing rod. Including the case of having both the solid part and the solid part),
-The above metal is beta titanium,
・The outer diameter (diameter) of the leading edge is 1.5 mm or less,
・The taper above is 8/1000 or more・20/1000 or less,
・And the total length is 100 mm or more and 200 mm or less. The numerical value of the taper is a value obtained by dividing the increment of the diameter from the thin portion on the tip side in the tapered portion by the length.

前述のように、釣竿穂先としてチタン合金等の金属製のものを使用することにより、穂先の強度を高め、穂先を適度に撓ませることが可能になる。しかし本発明の穂先は、穂先の金属としてベータチタンを採用するため、弾性に富んでいて張りが強く、釣竿の先につないで使用するうえでとくに好ましい。すなわち、ベータチタンは、高強度（高引張強度）であって低ヤング率（バネ性に優れる）である点で釣竿に適した特性を有しており、張りがあるうえに弾性変形域が広い。また、温度変化があってもその機械的特性がほとんど変化しないという面でも、他のチタン合金とは違って釣竿での使用に適しており、夏季にも冬季にも変化のない撓み方をする。このように、弾性変形によってつねに適度に撓むということは、釣竿穂先として必要な強度を確保しつつ、目視や手感度によって魚信を得やすいという効果をもたらす。なお、ベータチタンは、他のチタン合金と同様に軽量（低比重）であるほか耐食性にすぐれており、その点でも釣具部品としての使用に適している。
発明による上記の穂先は、寸法に関しても（したがって重量の面でも）釣竿の先に設けるうえで好ましい。金属製の穂先は、中空であっても中実であっても、外径を太くすると一般に重くなり、また適切な撓みが生じにくいので魚信も得にくい。しかし、釣竿との接続のために後端部分では2.0mm程度以上の太さが必要であるから、先端部分を細くした場合、テーパを適切に設定しないと全長が長くなってやはり重くなる。以上の点を考慮すると、上記のとおり、最先端部分の外径を1.5mm以下（かつ、後端部分の外径を2.0mm程度以上）とし、テーパを8/1000以上に大きくとって全長を200mm以下に抑えるのが有利なのである。
なお、もし全長が200mmを超えるような穂先では、軽量化のために径を細くすることと機械的強度を確保することとの両立が難しい。また、上記のテーパとして20/1000を超える大きなものにする場合には、加工上のコストが上昇する点で不利がともなう。 As described above, by using a fishing rod tip made of a metal such as titanium alloy, the strength of the tip can be increased and the tip can be appropriately bent. However, since the tip of the present invention employs beta-titanium as the metal of the tip, it is highly elastic and strong in tension, and is particularly preferable for use by connecting to the tip of a fishing rod. That is, beta titanium has characteristics suitable for fishing rods in that it has high strength (high tensile strength) and low Young's modulus (excellent springiness), and has a wide elastic deformation range in addition to being tight. .. In addition, it is suitable for use with fishing rods, unlike other titanium alloys, in that its mechanical properties hardly change even when there is a temperature change, and it flexes in the same manner in both summer and winter. .. As described above, the fact that the elastic deformation always causes the fishing rod tip to be bent appropriately, has the effect of easily obtaining the fishnet by visual inspection or hand sensitivity while ensuring the strength required for the fishing rod tip. Beta titanium is lightweight (low specific gravity) like other titanium alloys and has excellent corrosion resistance, and is also suitable for use as a fishing tackle component in that respect.
The above-mentioned tip according to the invention is preferred in terms of size (and therefore also in terms of weight) to be provided on the tip of the fishing rod. Whether the tip is made of metal, whether it is hollow or solid, it generally becomes heavier when the outer diameter is made thicker, and it is also difficult for proper bending to occur, so that it is difficult to obtain fish. However, since the rear end requires a thickness of about 2.0 mm or more to connect with the fishing rod, if the tip is thin, the overall length becomes long and heavy unless the taper is set properly. In consideration of the above points, the outer diameter of the tip part is set to 1.5 mm or less (and the outer diameter of the rear end part is about 2.0 mm or more) and the taper is set to 8/1000 or more to make the total length as described above. It is advantageous to keep it below 200 mm.
If the tip has a total length of more than 200 mm, it is difficult to reduce the diameter and secure the mechanical strength in order to reduce the weight. In addition, when the taper is larger than 20/1000, there is a disadvantage in that the processing cost is increased.

発明の釣竿穂先については、上記のベータチタンがTi-22V-4AL（各数値はwt％）の組成のものであると、とくに有利である。
Ti-22V-4ALのベータチタンは、JIS H 4600-80種に規定され、化学成分（各wt％）がN≦0.05、C≦0.10、H≦0.0150、Fe≦1.00、O≦0.25、3.50≦Al≦4.50、20.00≦V≦23.00、残部がTiであって、「DAT51」とも呼ばれるチタン合金である。高強度であってバネ性に優れることに加え、絞り特性が高くて冷間加工性に優れるという特性をも有している。
上記合金が冷間加工性に優れることから、この釣竿穂先はテーパ加工等が容易であり、したがって、特別なコストをかけることなく素材に上記の大きめのテーパを付与する等して、好ましい釣竿穂先を製造することを可能にする。 Regarding the fishing rod tip of the invention, it is particularly advantageous that the above-mentioned beta titanium has a composition of Ti-22V-4AL (each numerical value is wt%).
The beta titanium of Ti-22V-4AL is specified in JIS H 4600-80 type, and the chemical composition (each wt%) is N≦0.05, C≦0.10, H≦0.0150, Fe≦1.00, O≦0.25, 3.50≦ Al ≤ 4.50, 20.00 ≤ V ≤ 23.00, the balance being Ti, and is a titanium alloy also called "DAT51". In addition to high strength and excellent spring properties, it also has high drawing properties and excellent cold workability.
Since the above alloy is excellent in cold workability, this fishing rod tip can be easily tapered and the like, therefore, the above-mentioned large taper can be given to the material without incurring a special cost, and the like. It is possible to manufacture.

上記の釣竿穂先において、外表面にイオンプレーティング処理が施されているとさらに好ましい。
イオンプレーティング処理によって外表面に薄い皮膜を形成することにより、ユーザーに好まれる彩色や光沢を釣竿穂先にもたせることができ、また、耐食性等をさらに高めて美観や使用可能性を長期間維持できるようにし得るからである。
また、外表面にイオンプレーティング処理を施すのは、釣糸のガイドを取り付けるうえでも有利である。チタン合金の表面には一般に接着剤による接合が困難である。上述のとおり大きめのテーパが設けられていると、その接合が外れる可能性はとくに高い。しかし発明者らは、当該表面にイオンプレーティング処理を施すことによって、上記釣竿穂先の外表面に釣糸ガイドの脚部を強固に接合することを可能にした。すなわち、チタン合金（ベータチタン）製の穂先であっても、イオンプレーティング処理を施された部分には、アンカー効果に基づき接着剤によってガイドを固定することができ、釣竿の先端に取り付けて使用するうえで好ましい穂先となる。 It is more preferable that the outer surface of the fishing rod tip is subjected to ion plating treatment.
By forming a thin film on the outer surface by ion plating, the coloring and luster preferred by users can be added to the fishing rod tip, and corrosion resistance can be further improved to maintain aesthetics and usability for a long time. Because it can be done.
Further, the ion plating treatment on the outer surface is also advantageous in attaching the fishing line guide. It is generally difficult to bond the surface of a titanium alloy with an adhesive. If a large taper is provided as described above, the possibility that the joint will come off is particularly high. However, the present inventors have made it possible to firmly join the leg portion of the fishing line guide to the outer surface of the fishing rod tip by subjecting the surface to ion plating treatment. That is, even if the tip is made of titanium alloy (beta titanium), the guide can be fixed to the ion-plated part with an adhesive based on the anchor effect, and it can be used by attaching it to the tip of the fishing rod. It is a preferable tip for doing.

上記のイオンプレーティング処理については、当該処理によって窒化クロム（CrN）の皮膜が形成され、その外表面にエポキシ系接着剤によって釣糸のガイドが固定されているのがよい。
窒化クロムはベータチタンを上回る硬さを有していて耐食性にも優れるため、上記のようにされた釣竿穂先においては、釣糸のガイドがしっかりと固定されることに加え、傷が付きにくく耐食性がさらに優れた長期間使用可能なものとなる。窒化クロムの皮膜は彩色や光沢の面でも好ましい。 Regarding the above-mentioned ion plating treatment, it is preferable that a chromium nitride (CrN) film is formed by the treatment and the fishing line guide is fixed to the outer surface thereof by an epoxy adhesive.
Chromium nitride has a hardness higher than that of beta titanium and is also excellent in corrosion resistance.Therefore, in the fishing rod tip as described above, in addition to firmly fixing the guide of the fishing line, scratch resistance and corrosion resistance It will be even more excellent in long-term use. The chromium nitride film is also preferable in terms of coloring and gloss.

発明による釣竿穂先が中実の（内部、とくに先端部付近に空洞部を有しない）ものである場合は、最先端部分の外径が0.8mm以下であり、また、中心線に沿って延びた連結用のストレート孔を後端部に有するのがよい。
中実の穂先については、同じサイズであれば中空のものよりも剛性が高いことから、最先端部分の外径を0.8mm以下とやや細めにするのが好ましい。そのような小径のものであっても、中実の穂先であれば必要な剛性を発揮できる。小径であることは軽量化を図るうえでも好ましい。
そして上記のように後端部に釣竿との連結用の孔を設けておくと、釣竿との連結が容易である。なお、連結用のその孔は、内径が一定のストレート孔である方が穂先の抜け防止をはかるうえで有利である。なお、連結に使用されない部分にも中空部を設けると、穂先を軽量化できるメリットがある。 In the case where the fishing rod tip according to the invention is solid (there is no cavity inside, especially near the tip), the outer diameter of the tip is 0.8 mm or less, and it extends along the center line. It is preferable to have a straight hole for connection at the rear end.
Since the solid tip has a higher rigidity than a hollow tip with the same size, it is preferable to make the outer diameter of the tip end portion slightly smaller than 0.8 mm. Even with such a small diameter, a solid tip can exhibit the required rigidity. A small diameter is also preferable in terms of weight reduction.
When the hole for connecting with the fishing rod is provided in the rear end portion as described above, the connection with the fishing rod is easy. In addition, it is advantageous that the connecting hole is a straight hole having a constant inner diameter in order to prevent the tip from coming off. It should be noted that providing a hollow portion even in a portion that is not used for connection has an advantage that the tip can be reduced in weight.

一方、発明による釣竿穂先が中空の（内部に空洞部を有するパイプ状の）ものである場合は、外表面か中空部に面する内側の面かのいずれかに長さ方向に延びる筋状の凹凸があり、また、中心線に沿って延びた連結用のストレート孔を後端部に有するのがよい。
中空の穂先においても、連結用のストレート孔が後端部にあると釣竿との連結が容易である。また、内側の面に長さ方向に延びる筋状の凹凸を設けると、軽量化をはかりながらも曲げに対する剛性を確保するうえで有利である。 On the other hand, in the case where the fishing rod tip according to the invention is hollow (pipe-shaped having a hollow portion inside), a streak extending in the longitudinal direction is provided on either the outer surface or the inner surface facing the hollow portion. It is preferable that the rear end has a concavity and a straight hole for connection extending along the center line.
Even in a hollow tip, if the straight hole for connection is provided at the rear end, connection with the fishing rod is easy. Further, it is advantageous to provide the inner surface with streaky unevenness extending in the length direction in order to secure rigidity against bending while reducing the weight.

発明による釣竿穂先は、高強度・低ヤング率であって温度による特性変化が少ないという特性を有するベータチタンを素材とするため、釣竿穂先として必要な強度を確保しつつ目視や手感度によって夏季にも冬季にも魚信を得やすいものである。
また、発明の釣竿穂先は寸法設定等が適切であるため、重さや機械的強度、撓み特性、釣竿との接続可能性およびコストに関して有利である。すなわち、軽量であって違和感なく使用でき、釣竿穂先としての十分な強度があり、つねに適度に撓んで明確な魚信をもたらしてくれるうえ、釣竿との接続部分の強度等も確保しやすい。
外表面にイオンプレーティング処理を施すと、釣竿穂先に接着剤で釣糸ガイドを固定することが容易になる。同時に、ユーザーに好まれる彩色や光沢をもたせることができ、耐食性等をさらに高めて長期間使用できるよう構成することもできる。 The fishing rod tip according to the invention is made of beta titanium, which has the characteristics of high strength, low Young's modulus and little change in characteristics due to temperature. It is also easy to get fish notice in winter.
In addition, since the fishing rod tip of the invention has appropriate dimensions and the like, it is advantageous in terms of weight, mechanical strength, bending characteristics, connectability with a fishing rod, and cost. That is, it is lightweight and can be used without any discomfort, has sufficient strength as a tip of a fishing rod, always bends moderately to bring a clear fish line, and it is easy to secure the strength of the connecting portion with the fishing rod.
When the outer surface is subjected to ion plating treatment, it becomes easy to fix the fishing line guide to the tip of the fishing rod with an adhesive. At the same time, the coloring and luster preferred by the user can be provided, and the corrosion resistance and the like can be further enhanced to be configured to be used for a long period of time.

発明の一実施形態として中空の釣竿穂先１を示す縦断面図である。なお、図面上の各部の寸法比率は現物を忠実に表すものではない。It is a longitudinal cross-sectional view showing a hollow fishing rod tip 1 as one embodiment of the invention. In addition, the dimensional ratio of each part on the drawings does not faithfully represent the actual product. 発明の他の実施形態として中実の釣竿穂先２を示す縦断面図である。なお、図面上の各部の寸法比率は現物を忠実に表すものではない。It is a longitudinal cross-sectional view showing a solid fishing rod tip 2 as another embodiment of the invention. In addition, the dimensional ratio of each part on the drawings does not faithfully represent the actual product. 図１または図２の釣竿穂先１（または２）を有する釣竿１０の全体側面図である。It is the whole side view of the fishing rod 10 which has the fishing rod tip 1 (or 2) of FIG. 1 or FIG.

発明による釣竿穂先を有する釣竿について、一例を図３に示す。
図３の釣竿１０は、鮎釣り等に使用される振出竿であり、元竿１０Ａの中に収められる複数の竿１０Ｂ、１０Ｂ…を図示のように引き出して使用するものである。そして最も先の竿１０Ｂの先端に、穂先１（または２）を連結して使用する。 An example of a fishing rod having a fishing rod tip according to the invention is shown in FIG.
The fishing rod 10 of FIG. 3 is a swing-out rod used for ayu fishing or the like, and uses a plurality of rods 10B, 10B,... Then, the tip 1 (or 2) is connected to the tip of the earliest rod 10B and used.

元竿１０Ａと複数の竿１０Ｂとで構成される図３の釣竿１０は、繊維強化樹脂材料を主材料として形成したものである。すなわち、カーボンシート（炭素繊維）を複数層巻き付けてエポキシ樹脂等でそれらを接着し、加熱・加圧して円筒状にすることにより、各竿１０Ａ・１０Ｂを構成する。手感度によって魚信を得るうえでは、高弾性のカーボンシート（たとえば５０トンカーボン以上のもの）を使用することによって竿本体を弾性の高いものにするのが好ましい。また、さらに振動減衰率を小さくするため、樹脂率が15〜20％の低樹脂カーボンを含めて使用するとよい。 The fishing rod 10 of FIG. 3, which is composed of the original rod 10A and the plurality of rods 10B, is formed by using a fiber reinforced resin material as a main material. That is, each of the rods 10A and 10B is formed by winding a plurality of layers of carbon sheets (carbon fibers), adhering them with an epoxy resin or the like, and heating and pressurizing them into a cylindrical shape. In order to obtain a fishstring by hand sensitivity, it is preferable to make the rod body highly elastic by using a highly elastic carbon sheet (for example, 50 ton carbon or more). Further, in order to further reduce the vibration damping rate, low resin carbon having a resin rate of 15 to 20% may be included and used.

図１・図２のそれぞれには、釣竿１０の先端に連結した穂先（釣竿穂先）１・２と、それに直接つながった竿１０Ｂとの連結状態とを拡大して示している。
図１の穂先１は金属製であり、図示のように先細りのテーパ部分を有する中空のものである。金属製とするのは、負荷が集中しやすい穂先の強度を高めるとともに、穂先を撓みやすくして魚信を得やすくするためである。この例では、穂先１の金属としてベータチタン（とくに、JIS H 4600-80種に規定のTi-22V-4AL合金）を使用している。使用したベータチタンは、高強度であるとともに弾性に富んでいて、張りが強いうえに弾性変形域が広く、またそのような機械的特性が夏季にも冬季にもほとんど変化しないため、釣竿穂先として好適である。 1 and 2 respectively show enlarged views of the tips of the fishing rod 10 (fishing rod tips) 1.2 connected to the tip of the fishing rod 10 and the rod 10B directly connected thereto.
The tip 1 of FIG. 1 is made of metal and is hollow as shown in the drawing having a tapered portion. It is made of metal in order to increase the strength of the tip where the load is likely to concentrate and to make it easier to bend and to obtain the fish stock. In this example, beta titanium (in particular, Ti-22V-4AL alloy specified in JIS H 4600-80 type) is used as the metal of the tip 1. Beta-titanium used has high strength and is highly elastic, has a strong tension, and has a wide elastic deformation range.Because such mechanical properties hardly change in summer and winter, it is used as a fishing rod tip. It is suitable.

穂先１は、最先端部分１ａの外径（直径）を0.90mmとし、それより後方にテーパ部分１ｂを形成して後部の最大外径を2.30mmとし、そのさらに後方に、後端部分１ｄまで太さが一定であるストレート部分１ｃを設けている。そして全長域を中空としたので、テーパ部分１ｂとストレート部分１ｃとの内側に空洞部１ｅがある。テーパ部分１ｂの長さ１ｘは100mm、その部分の肉厚は0.4mmである。ストレート部分１ｃは竿１０Ｂとの接続のための部分であり、長さ１ｙが25mm、外径が2.30mm、肉厚が0.3mm、内径が1.7mmである。 The tip 1 has an outer diameter (diameter) of the tip portion 1a of 0.90 mm, a tapered portion 1b is formed rearward of the tip portion to have a maximum outer diameter of 2.30 mm, and further rearward thereof, up to a rear end portion 1d. A straight portion 1c having a constant thickness is provided. Since the entire length area is hollow, there is a hollow portion 1e inside the tapered portion 1b and the straight portion 1c. The length 1x of the tapered portion 1b is 100 mm, and the wall thickness of that portion is 0.4 mm. The straight portion 1c is a portion for connection with the rod 10B, and has a length 1y of 25 mm, an outer diameter of 2.30 mm, a wall thickness of 0.3 mm, and an inner diameter of 1.7 mm.

テーパ部分１ｂの最大太さとストレート部分１ｃの太さは、竿１０Ｂとの接続が容易であるよう大きめに定め、テーパ部分１ｂの長さは、穂先１の力学的負荷が過剰にならないよう短めに設定している。そのため、テーパ部分１ｂのテーパ（直径の増加割合）は、14.00/1000と大きくしている。 The maximum thickness of the tapered portion 1b and the thickness of the straight portion 1c are set to be large so that the connection with the rod 10B is easy, and the length of the tapered portion 1b is set to be short so that the mechanical load on the tip 1 does not become excessive. It is set. Therefore, the taper of the tapered portion 1b (the increase rate of the diameter) is set to 14.00/1000.

ベータチタン製の中空材は、たとえば、中実棒材に機械加工を施して穿孔管としたり、板材を丸めたうえ継目を溶接して電縫管としたり、あるいは、マンネスマン圧延穿孔機と各種の仕上げミルとの組合せにより圧延管材としたりすることによって、得ることができる。また、上記のテーパ部分１ｂは、そうして得た中空材にスエージング加工を施すことによって形成することができる。この例で使用する上記のTi-22V-4AL合金は冷間加工性に優れていて加工上有利である。そしてそのような加工の終了後に、焼入れ・焼戻し等の熱処理を行うことにより、しなやかな弾力を有する穂先１を完成できる。
なお、中空の穂先１においては、外表面か、空洞部１ｅに面する内側の面かに、長さ方向に延びる筋状の凹凸を形成すると好ましい。そのような筋状の凹凸を設けると、穂先１を軽量化しながらも曲げに対する剛性を確保することが可能だからである。たとえばレーザー加工によって外表面等にそのような凹凸を形成することができる。 The hollow material made of beta-titanium is, for example, machined into a solid bar to form a perforated pipe, or rolled into a plate and welded at seams to form an electric resistance welded pipe, or a Mannesmann rolling perforator. It can be obtained by forming a rolled pipe material by combining with a finishing mill. The tapered portion 1b can be formed by subjecting the hollow material thus obtained to swaging. The Ti-22V-4AL alloy used in this example is excellent in cold workability and advantageous in working. Then, after such processing is completed, heat treatment such as quenching and tempering is performed, whereby the tip 1 having supple elasticity can be completed.
In addition, in the hollow tip 1, it is preferable that streaky unevenness extending in the length direction is formed on the outer surface or the inner surface facing the cavity 1e. This is because by providing such streaky irregularities, it is possible to secure rigidity against bending while reducing the weight of the tip 1. For example, such unevenness can be formed on the outer surface by laser processing.

穂先１は、図１に示すように中実円柱状の連結体（インロー部材）１１を介して釣竿１０に接続している。すなわち、穂先１の後端部の内側に連結体１１の前部を挿入し、その連結体１１の後部を竿１０Ｂの前端部内側に挿入することとし、前後の挿入部分に接着剤を使用する。連結体１１は、穂先１と同様のベータチタン（Ti-22V-4AL合金）で構成しているが、他の金属、または竿１０Ｂと同じ繊維強化樹脂材料で構成してもよい。連結体１１は、上記した中実円柱状のものに代えて、中空の円筒状のものを使用することもできる。連結体１１を用いた穂先１と竿１０Ｂとの連結部分付近が、負荷を受けたとき滑らかなカーブを描くように連結体１１の曲げ剛性を定めると好ましい。 As shown in FIG. 1, the tip 1 is connected to a fishing rod 10 via a solid cylindrical connection body (spigot member) 11. That is, the front portion of the connecting body 11 is inserted inside the rear end portion of the tip 1, and the rear portion of the connecting body 11 is inserted inside the front end portion of the rod 10B, and an adhesive is used at the front and rear insertion portions. .. The connector 11 is made of beta titanium (Ti-22V-4AL alloy) similar to the tip 1, but may be made of another metal or the same fiber reinforced resin material as the rod 10B. The connecting body 11 may be a hollow cylindrical body instead of the solid cylindrical body described above. It is preferable to determine the bending rigidity of the connecting body 11 so that the vicinity of the connecting portion between the tip 1 and the rod 10B using the connecting body 11 draws a smooth curve when a load is applied.

穂先１の外表面には、イオンプレーティング処理によって窒化クロム（CrN）の皮膜（膜厚2〜5μｍ程度）を形成している。その皮膜が高硬度であるために、穂先１の外表面が傷付きにくく、また皮膜の耐食性に基づいて光沢が長く保たれる。そしてまた、イオンプレーティングによって表面に微細な凹凸が形成されることから、穂先１の外表面に、接着剤（エポキシ系接着剤）によって釣糸ガイドの脚部（図示省略）を安定的に接合することが可能になる。 On the outer surface of the tip 1, a chromium nitride (CrN) film (film thickness of about 2 to 5 μm) is formed by ion plating. Since the film has high hardness, the outer surface of the tip 1 is not easily scratched, and the gloss is maintained for a long time based on the corrosion resistance of the film. Also, since fine irregularities are formed on the surface by ion plating, the leg portion (not shown) of the fishing line guide is stably joined to the outer surface of the tip 1 with an adhesive (epoxy adhesive). It will be possible.

図２には、最先端部分を含むほとんどの部分（全長の過半部）を中実にした穂先２を示している。この穂先２もベータチタン（穂先１と同じTi-22V-4AL合金）製であり、先細りのテーパ部分２ｂを有していて最先端部分２ａから直径が次第に拡大し、最大外径部から後端部分２ｄにまで、直径が一定のストレート部分２ｃを連続させている。ストレート部分２ｃは竿１０Ｂとの接続用の部分であって、内側にストレートの空洞部２ｅを設けることにより、図１の場合と同様の連結体１２を挿入して竿１０Ｂに接続できるようにしている。 FIG. 2 shows the tip 2 in which most of the part (the majority of the entire length) including the tip part is solid. The tip 2 is also made of beta titanium (the same Ti-22V-4AL alloy as the tip 1), has a tapered taper portion 2b, and the diameter gradually increases from the tip portion 2a, and from the maximum outer diameter portion to the rear end. The straight portion 2c having a constant diameter is continuous up to the portion 2d. The straight portion 2c is a portion for connecting to the rod 10B, and by providing the straight hollow portion 2e inside, the same connecting body 12 as in the case of FIG. 1 can be inserted to connect to the rod 10B. There is.

主要部が中実であるため中空のものよりも剛性が高くなりやすいことから、最先端部分２ａの外径（直径）は0.60mmと細めにし、ストレート部分２ｃおよび後端部分２ｄの外径も1.90mmと細めにしている。テーパ部分２ｂは、長さ２ｘを125mmとしたため、そのテーパは10.40/1000である。また、テーパ部分２ｂ・ストレート部分２ｃとも肉厚を0.25mmとし、内径が1.40mmの空洞部２ｅを、ストレート部分２ｃの長さ２ｙ（25mm）にわたって形成している。空洞部２ｅの先端側には、軽量化のための空洞部２ｆを形成するのもよい。 Since the main part is solid, the rigidity tends to be higher than that of the hollow one. Therefore, the outer diameter (diameter) of the tip portion 2a is reduced to 0.60 mm, and the outer diameters of the straight portion 2c and the rear end portion 2d are also reduced. It is as thin as 1.90 mm. Since the length 2x of the taper portion 2b is 125 mm, the taper is 10.40/1000. Further, both the tapered portion 2b and the straight portion 2c have a wall thickness of 0.25 mm, and a cavity 2e having an inner diameter of 1.40 mm is formed over the length 2y (25 mm) of the straight portion 2c. A cavity 2f for weight reduction may be formed on the tip side of the cavity 2e.

図２に示す穂先２も、ベータチタン製の棒材にスエージング加工を施すことによってテーパ部分２ｂを形成する。空洞部２ｅや２ｆを形成するには、後端部分２ｄから機械加工によって穿孔するとよい。 The tip 2 shown in FIG. 2 also has a tapered portion 2b formed by subjecting a bar material made of beta titanium to swaging. In order to form the cavities 2e and 2f, the rear end portion 2d may be punched by machining.

この穂先２も、ベータチタンを素材としているために弾性に富み、しなやかに撓んで目視や手感度による好ましい魚信をもたらす。穂先２は、中実であるために製作が容易であることから、図１のものと同様の機能を有するとともに、より低コストの釣竿穂先として構成される。 Since the tip 2 is also made of beta titanium as a material, it is highly elastic, and flexes flexibly to bring about a desirable fisheye by visual and hand sensitivity. Since the tip 2 is solid and easy to manufacture, it has the same function as that of FIG. 1 and is configured as a lower cost fishing rod tip.

なお、穂先２も、図示のとおり連結体（インロー部材）１２を介して釣竿１０に接続するとよい。ベータチタン等の金属や繊維強化樹脂材料で構成した中実円柱体または中空円筒体を連結体１２として、ストレート部分２ｃと竿１０Ｂの内側とにまたがるよう挿入することにより、穂先２と竿１０Ｂとを連結するのである。 The tip 2 may also be connected to the fishing rod 10 via a connecting body (spigot member) 12 as illustrated. By inserting a solid cylindrical body or a hollow cylindrical body made of a metal such as beta titanium or a fiber reinforced resin material as the connecting body 12 so as to straddle the straight portion 2c and the inside of the rod 10B, the tip 2 and the rod 10B are formed. To connect.

また、図２の穂先２についてもイオンプレーティング処理を施すと好ましい。同処理によってたとえば窒化クロムの薄い皮膜を外表面に形成すると、その外表面に釣糸ガイドの脚部（図示省略）を接着剤にて固定することが可能になり、また、美観に富んだ光沢を外表面に付与してそれを長期間維持できるという利点がある。 Further, it is preferable that the tip 2 of FIG. 2 is also subjected to ion plating treatment. If a thin film of chromium nitride, for example, is formed on the outer surface by the same treatment, the legs (not shown) of the fishing line guide can be fixed to the outer surface with an adhesive, and a glossy appearance is provided. It has the advantage that it can be applied to the outer surface and maintained for a long period of time.

すでに述べたように、図１または図２のような穂先１・２を図３のような釣竿１０の先に取り付けると、負荷が集中しやすい穂先部分を高強度にできるとともに、当該部分を弾性的に適度に撓むようにして感度を高め、魚信を得やすくすることができる。しかし、手感度をさらに高めて魚信を得やすくするためには、図３に示すように、釣竿１０の元竿１０Ａの後端部付近（握りの部分）に、チタンやチタン合金（たとえば純チタンやベータチタン）でできた円筒体１０Ｃを接続するのも好ましい。チタン等は低密度であって振動減衰率が小さいために、釣糸や竿１０を経て伝達される振動（魚の動き等に応じたもの）を釣り人の手に伝えやすいからである。図示の例では、長さが30〜50mm程度で厚さが1〜2mm程度のチタン合金製の円筒体１０Ｃを元竿１０Ａの基部にネジ結合し、さらにその後部にステンレス鋼製の尻栓１０Ｄをネジ結合して取り付けている。 As described above, when the tips 1 and 2 as shown in FIG. 1 or 2 are attached to the tip of the fishing rod 10 as shown in FIG. 3, it is possible to increase the strength of the tip portion where load is likely to concentrate and to make the portion elastic. It is possible to flexibly moderately increase the sensitivity and make it easy to obtain fish. However, in order to further increase the hand sensitivity and make it easier to obtain fish meat, as shown in FIG. 3, titanium or a titanium alloy (for example, a pure alloy) is provided near the rear end portion (the grip portion) of the base rod 10A of the fishing rod 10. It is also preferable to connect a cylindrical body 10C made of titanium or beta titanium). This is because titanium or the like has a low density and a small vibration damping rate, so that the vibration (which corresponds to the movement of the fish) transmitted through the fishing line and the rod 10 is easily transmitted to the angler's hand. In the illustrated example, a cylindrical body 10C made of titanium alloy having a length of about 30 to 50 mm and a thickness of about 1 to 2 mm is screwed to the base of the base rod 10A, and a stainless steel bottom plug 10D is further provided at the rear portion thereof. Are attached by screwing.

１・２穂先（釣竿穂先）
１ａ・２ａ最先端部分
１ｂ・２ｂテーパ部分
１ｃ・２ｃストレート部分
１ｅ・２ｅ・２ｆ空洞部
１１・１２連結体
１０釣竿
１０Ａ元竿
１０Ｂ竿 1.2 tip (fishing tip)
1a・2a Leading edge part 1b・2b Tapered part 1c・2c Straight part 1e・2e・2f Cavity part 11・12 Connected body 10 Fishing rod 10A Original rod 10B Rod

Claims

A hollow or solid metal fishing rod tip that has a tapered portion and is connected to the tip of the fishing rod,
The above metal is beta titanium, the outer diameter of the leading edge is 1.5 mm or less, the taper is 8/1000 or more and 20/1000 or less, and the total length is 100 mm or more and 200 mm or less. The tip of a fishing rod.

The fishing rod tip according to claim 1, wherein the beta titanium has a composition of Ti-22V-4AL (each numerical value is wt%).

The fishing rod tip according to claim 1 or 2, wherein the outer surface is subjected to an ion plating treatment.

The fishing line tip according to claim 3, wherein a guide line of the fishing line is fixed by an epoxy adhesive on the outer surface on which the chromium nitride film is formed by the ion plating treatment.

The outer diameter of the most distal end portion is 0.8 mm or less and is solid, and has a straight hole for connection extending along the center line at the rear end portion. The tip of the fishing rod described in any one of.

Being hollow, there should be streaky unevenness extending in the length direction on either the outer surface or the inner surface facing the hollow part, and a straight hole for connection extending along the center line The fishing rod tip according to any one of claims 1 to 4, which is provided at an end portion.