JP2019089948A - Adhesive sheet, manufacturing method of laminate, and laminate - Google Patents
Adhesive sheet, manufacturing method of laminate, and laminate Download PDFInfo
- Publication number
- JP2019089948A JP2019089948A JP2017219909A JP2017219909A JP2019089948A JP 2019089948 A JP2019089948 A JP 2019089948A JP 2017219909 A JP2017219909 A JP 2017219909A JP 2017219909 A JP2017219909 A JP 2017219909A JP 2019089948 A JP2019089948 A JP 2019089948A
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- adhesive layer
- adhesive sheet
- post
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、粘着シート、積層体の製造方法および積層体に関する。 The present invention relates to a pressure-sensitive adhesive sheet, a method of producing a laminate, and a laminate.
液晶ディスプレイ(LCD)などの表示装置や、タッチパネルなどの表示装置と組み合わせて用いられる入力装置が広く用いられている。これらの表示装置や入力装置の製造等においては、光学部材を貼り合せる用途に透明な粘着シートが使用されており、表示装置と入力装置との貼合にも透明な粘着シートが使用されている。 An input device used in combination with a display device such as a liquid crystal display (LCD) or a display device such as a touch panel is widely used. In the manufacture of these display devices and input devices, a transparent adhesive sheet is used for the purpose of bonding optical members, and a transparent adhesive sheet is also used for bonding a display device and an input device. .
粘着シートを形成する架橋性アクリル重合体の重合方法としては、下記のような数通りの重合方法があることが知られている。具体的には、(1)熱による重合、(2)活性エネルギー線による重合、(3)熱(又は活性エネルギー線)による重合をした後に、活性エネルギー線(又は熱)による重合を行う2段重合、(4)活性エネルギー線による重合をした後に、活性エネルギー線による重合を行う2段重合といった方法がある。 As a polymerization method of a crosslinkable acrylic polymer for forming a pressure-sensitive adhesive sheet, it is known that there are several polymerization methods as described below. Specifically, after performing (1) polymerization by heat, (2) polymerization by active energy rays, (3) polymerization by heat (or active energy rays), two-stage polymerization is performed by active energy rays (or heat) There are methods such as polymerization and (4) two-stage polymerization in which polymerization by active energy rays is performed after polymerization by active energy rays.
近年、上述したような用途に用いられる粘着シートを形成する方法としては、(3)熱(又は活性エネルギー線)による重合をした後に、活性エネルギー線(又は熱)による重合を行う2段重合により硬化する方法が用いられる場合がある。このような粘着シートは、熱硬化性および活性エネルギー線硬化性の両方を備える粘着剤組成物(以下、「デュアル硬化型粘着剤組成物」ということがある。)から形成されるため、熱硬化性と活性エネルギー線硬化性を有している。このため、被着体との貼合前に、例えば熱硬化のみを行うことで仮接着させることができ、その後、さらに活性エネルギー線により硬化させる(後硬化またはアフターキュアと言われる)ことで被着体に強固に接着できる。 In recent years, as a method of forming a pressure-sensitive adhesive sheet used for applications as described above, (3) Two-stage polymerization in which polymerization by active energy rays (or heat) is performed after polymerization by heat (or active energy rays) Methods of curing may be used. Such a pressure-sensitive adhesive sheet is formed from a pressure-sensitive adhesive composition (hereinafter sometimes referred to as "dual-curable pressure-sensitive adhesive composition") provided with both a thermosetting property and an active energy ray-curable property, and therefore, the thermosetting sheet And active energy ray curability. For this reason, prior to bonding with the adherend, for example, temporary bonding can be performed by performing only heat curing, and then curing is further performed by active energy rays (referred to as post curing or after curing). It can be firmly adhered to the garment.
(3)の方法で粘着シートを形成する方法の例が知られている。
例えば、特許文献1には、非架橋性(メタ)アクリル酸エステル単位(a1)及び架橋性官能基を有するアクリル単量体単位(a2)を含むベースポリマー(A)と、ラウリルアクリレート(b1)を含む単量体(B)と、熱によりベースポリマー(A)と反応する架橋剤(C)と、活性エネルギー線の照射により単量体(B)の重合反応を開始させる重合開始剤(D)と、溶剤(E)と、を含有する粘着剤組成物を加熱により半硬化させてなる粘着剤層を含む粘着シートが記載されている。
特許文献2には、板材としてガラス板同士、ガラス板と合成樹脂板又は合成樹脂板同士を少なくとも2枚、紫外線硬化可能な粘着剤層を少なくとも1層以上有する粘着シートで貼り合せた後、板材側から紫外線照射して、粘着剤層を紫外線硬化させる透明積層体の製造方法が記載されている。
The example of the method of forming an adhesive sheet by the method of (3) is known.
For example, Patent Document 1 discloses a base polymer (A) containing a non-crosslinkable (meth) acrylic acid ester unit (a1) and an acrylic monomer unit (a2) having a crosslinkable functional group, and lauryl acrylate (b1) , A crosslinking agent (C) that reacts with the base polymer (A) by heat, and a polymerization initiator (D) that initiates the polymerization reaction of the monomer (B) by irradiation with active energy rays. A pressure-sensitive adhesive sheet is described which includes a pressure-sensitive adhesive layer obtained by semi-curing a pressure-sensitive adhesive composition containing a solvent and a solvent (E) by heating.
In Patent Document 2, after pasting together with a pressure-sensitive adhesive sheet having at least two glass plates as a plate, at least two glass plates and a synthetic resin plate or two synthetic resin plates, and at least one ultraviolet curable adhesive layer, The manufacturing method of the transparent laminated body which carries out ultraviolet irradiation from the side and carries out the ultraviolet curing of the adhesive layer is described.
本発明者らが特許文献1および2に記載の粘着シートの特性を検討したところ、後硬化後の粘着シートの加工性は、通常の上記(1)または(2)の方法で形成された粘着シートと同等程度の性能であり、改善の余地があることがわかった。 When the present inventors examined the characteristics of the pressure-sensitive adhesive sheet described in Patent Documents 1 and 2, the processability of the pressure-sensitive adhesive sheet after post-curing was the adhesion formed by the above-mentioned method (1) or (2). It was found that the performance was comparable to that of the sheet, and there is room for improvement.
本発明が解決しようとする課題は、粘着剤層が後硬化性を有し、粘着剤層が後硬化された場合に加工性に優れる粘着シートを提供することである。 The problem to be solved by the present invention is to provide a pressure-sensitive adhesive sheet having post-curing properties and having excellent processability when the pressure-sensitive adhesive layer is post-cured.
上記の課題を解決するために鋭意検討を行った結果、本発明者らは、後硬化性を有する粘着剤層を用いて、粘着剤層が後硬化された場合の剪断貯蔵弾性率G’を特定の範囲以上とし、粘着剤層が後硬化された場合のプローブタック値を特定の範囲以下とすることにより、粘着剤層が後硬化された場合に加工性に優れる粘着シートを提供できることを見出した。 As a result of intensive studies to solve the above problems, the present inventors used a post-curing adhesive layer to determine the shear storage modulus G ′ when the adhesive layer is post-cured. It is found that a pressure-sensitive adhesive sheet excellent in processability can be provided when the pressure-sensitive adhesive layer is post-cured by setting the probe tack value in the case where the pressure-sensitive adhesive layer is post-cured below the specific range. The
本発明および本発明の好ましい構成は以下のとおりである。
[1] 粘着剤組成物を半硬化状態とした粘着剤層を有し、
粘着剤組成物が架橋性アクリル重合体、架橋剤、分子内に反応性二重結合を2つ以上有する多官能単量体、分子内に反応性二重結合を1つ有する単官能単量体および重合開始剤を含有し、
前記単官能単量体を重合した場合のホモポリマーのガラス転移温度(Tg)が50℃以上200℃未満であり、
粘着剤層は後硬化性を有し、
粘着剤層が後硬化された場合に下記物性群(1)を満たす、粘着シート。
物性群(1):23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×106[Pa]以上であり、75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×105[Pa]以上であり、23℃かつ下記測定条件で測定されるプローブタック値が1.5N/5mmφ以下である。
(プローブタック値の測定条件)
測定機器:NSプローブタックテスター(ニチバン株式会社製)
プローブ直径:5mmφ
プローブ基材:ステンレススチール表面仕上げAA#400研磨による鏡面
ウェイト:19.6±0.2g(真鍮製)
プローブ移動速度:1.0cm/秒
デュエルタイム:1秒間。
[2] 粘着剤層が半硬化状態で下記物性群(2)を満たす[1]に記載の粘着シート。
物性群(2):23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が8.0×105[Pa]以下であり、75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×105[Pa]以下であり、23℃かつ前記測定条件で測定されるプローブタック値が2.0N/5mmφ以上。
[3] 粘着剤層が後硬化された場合に後硬化後のゲル分率が70〜100質量%である[1]または[2]に記載の粘着シート。
[4] 粘着剤層の半硬化状態でのゲル分率が0質量%以上70質量%未満であり、かつ、粘着剤層が後硬化された場合に後硬化後のゲル分率が、半硬化状態でのゲル分率より5質量%以上高くなる[1]〜[3]のいずれかに記載の粘着シート。
[5] 架橋性アクリル重合体が有する架橋性官能基が、カルボキシ基、ヒドロキシ基、アミノ基、アミド基、グリシジル基およびイソシアネート基から選択される1種類または2種類以上である[1]〜[4]のいずれかに記載の粘着シート。
[6] 架橋剤が二官能以上のエポキシ化合物および二官能以上のイソシアネート化合物から選択される1種類または2種類以上である[1]〜[5]のいずれかに記載の粘着シート。
[7] 単官能単量体と多官能単量体の合計含有量が架橋性アクリル重合体100質量部に対して10〜40質量部である[1]〜[6]のいずれかに記載の粘着シート。
[8] 単官能単量体が(メタ)アクリル酸エステルである、[1]〜[7]のいずれかに記載の粘着シート。
[9] 粘着剤組成物が単官能単量体を架橋性アクリル重合体100質量部に対して5〜35質量部含有する、[1]〜[8]のいずれかに記載の粘着シート。
[10] 重合開始剤が活性エネルギー線照射により多官能単量体および/または単官能単量体の重合を開始させるものである[1]〜[9]のいずれかに記載の粘着シート。
[11] 剥離力が互いに異なる1対の剥離シートを粘着剤層の両面に有する構成、または透明基材/粘着剤層/剥離シートの構成である[1]〜[10]のいずれかに記載の粘着シート。
[12] [1]〜[11]のいずれかに記載の粘着シートの粘着剤層を被着体に対して半硬化状態で貼合した後、活性エネルギー線を照射して粘着剤層を後硬化させる工程を含む、積層体の製造方法。
[13] 被着体が、透明フィルム、透明樹脂またはガラスである[12]に記載の積層体の製造方法。
[14] [1]〜[11]のいずれかに記載の粘着シートの粘着剤層に活性エネルギー線を照射して後硬化させた後硬化後の粘着剤層と、被着体とを有する、積層体。
The present invention and preferred configurations of the present invention are as follows.
[1] It has a pressure-sensitive adhesive layer in which the pressure-sensitive adhesive composition is in a semi-cured state,
The pressure-sensitive adhesive composition comprises a crosslinkable acrylic polymer, a crosslinking agent, a polyfunctional monomer having two or more reactive double bonds in the molecule, and a monofunctional monomer having one reactive double bond in the molecule And a polymerization initiator,
The glass transition temperature (Tg) of the homopolymer when the monofunctional monomer is polymerized is 50 ° C. or more and less than 200 ° C.,
The pressure-sensitive adhesive layer has post-curing properties and
A pressure-sensitive adhesive sheet satisfying the following physical property group (1) when the pressure-sensitive adhesive layer is post-cured.
Physical property group (1): Shear storage modulus G ′ measured at 23 ° C. and frequency 1 Hz is 1.0 × 10 6 [Pa] or more, and shear storage modulus G ′ measured at 75 ° C. and frequency 1 Hz Is 1.0 × 10 5 [Pa] or more, and the probe tack value measured at 23 ° C. and the following measurement conditions is 1.5 N / 5 mmφ or less.
(Measurement condition of probe tack value)
Measuring equipment: NS probe tack tester (made by Nichiban Co., Ltd.)
Probe diameter: 5 mmφ
Probe base material: Specular weight by stainless steel surface finish AA # 400 polishing: 19.6 ± 0.2 g (made of brass)
Probe moving speed: 1.0 cm / sec Duel time: 1 sec.
[2] The pressure-sensitive adhesive sheet according to [1], wherein the pressure-sensitive adhesive layer is in a semi-cured state and satisfies the following physical property group (2).
Physical property group (2): Shear storage modulus G ′ measured at 23 ° C. and frequency 1 Hz is 8.0 × 10 5 [Pa] or less, and shear storage modulus G ′ measured at 75 ° C. and frequency 1 Hz Is 1.0 × 10 5 [Pa] or less, and a probe tack value measured at 23 ° C. and under the above measurement conditions is 2.0 N / 5 mmφ or more.
[3] The pressure-sensitive adhesive sheet according to [1] or [2], which has a gel fraction of 70 to 100% by mass after post-curing when the pressure-sensitive adhesive layer is post-cured.
[4] The gel fraction in the semi-cured state of the pressure-sensitive adhesive layer is 0% by mass to less than 70% by mass, and the gel fraction after post-curing is semi-cured when the pressure-sensitive adhesive layer is post-cured The adhesive sheet in any one of [1]-[3] which becomes 5 mass% or more higher than the gel fraction in a state.
[5] The crosslinkable functional group possessed by the crosslinkable acrylic polymer is one or more selected from a carboxy group, a hydroxy group, an amino group, an amido group, a glycidyl group and an isocyanate group [1] to [1] The adhesive sheet in any one of 4].
[6] The pressure-sensitive adhesive sheet according to any one of [1] to [5], wherein the crosslinking agent is one or more selected from an epoxy compound having two or more functional groups and an isocyanate compound having two or more functional groups.
[7] The composition according to any one of [1] to [6], wherein the total content of the monofunctional monomer and the polyfunctional monomer is 10 to 40 parts by mass with respect to 100 parts by mass of the crosslinkable acrylic polymer. Adhesive sheet.
[8] The adhesive sheet in any one of [1]-[7] whose monofunctional monomer is (meth) acrylic acid ester.
[9] The pressure-sensitive adhesive sheet according to any one of [1] to [8], wherein the pressure-sensitive adhesive composition contains 5 to 35 parts by mass of a monofunctional monomer with respect to 100 parts by mass of the crosslinkable acrylic polymer.
[10] The pressure-sensitive adhesive sheet according to any one of [1] to [9], wherein the polymerization initiator initiates polymerization of the polyfunctional monomer and / or the monofunctional monomer by irradiation with active energy rays.
[11] The constitution according to any one of [1] to [10], which comprises a pair of release sheets having different release forces on both sides of the pressure-sensitive adhesive layer, or a configuration of transparent substrate / pressure-sensitive adhesive layer / release sheet Adhesive sheet.
[12] After bonding the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet according to any one of [1] to [11] to an adherend in a semi-cured state, the active energy ray is irradiated to back the pressure-sensitive adhesive layer The manufacturing method of a laminated body including the process to harden.
[13] The method for producing a laminate according to [12], wherein the adherend is a transparent film, a transparent resin or glass.
[14] The pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet according to any one of [1] to [11] is irradiated with active energy rays to cause post-curing, and the pressure-sensitive adhesive layer after curing and an adherend Stack.
本発明によれば、粘着剤層が後硬化性を有し、粘着剤層が後硬化された場合に加工性に優れる粘着シートを提供できる。 According to the present invention, it is possible to provide a pressure-sensitive adhesive sheet which is excellent in processability when the pressure-sensitive adhesive layer has post-curing properties and the pressure-sensitive adhesive layer is post-cured.
以下において、本発明について詳細に説明する。以下に記載する構成要件の説明は、代表的な実施形態や具体例に基づいてなされることがあるが、本発明はそのような実施形態に限定されるものではない。なお、本明細書において「〜」を用いて表される数値範囲は「〜」前後に記載される数値を下限値および上限値として含む範囲を意味する。 Hereinafter, the present invention will be described in detail. The description of the configuration requirements described below may be made based on typical embodiments and specific examples, but the present invention is not limited to such embodiments. In addition, the numerical range represented using "-" in this specification means the range which includes the numerical value described before and after "-" as a lower limit and an upper limit.
なお、本明細書において、“(メタ)アクリレート”はアクリレートおよびメタクリレートの双方、または、いずれかを表し、“(メタ)アクリル酸”はアクリル酸およびメタクリル酸の双方、または、いずれかを表す。
また、本明細書において、“単量体”と“モノマー”とは同義である。
In the present specification, "(meth) acrylate" represents both or either of acrylate and methacrylate, and "(meth) acrylic acid" represents both or either of acrylic acid and methacrylic acid.
In the present specification, "monomer" and "monomer" are synonymous.
[粘着シート]
本発明の粘着シートは、粘着剤組成物を半硬化状態とした粘着剤層を有し、
粘着剤組成物が架橋性アクリル重合体、架橋剤、分子内に反応性二重結合を2つ以上有する多官能単量体、分子内に反応性二重結合を1つ有する単官能単量体および重合開始剤を含有し、
単官能単量体を重合した場合のホモポリマーのガラス転移温度(Tg)が50℃以上200℃未満であり、
粘着剤層は後硬化性を有し、
粘着剤層が後硬化された場合に下記物性群(1)を満たす。
物性群(1):23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×106[Pa]以上であり、75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×105[Pa]以上であり、23℃かつ下記測定条件で測定されるプローブタック値が1.5N/5mmφ以下である。
(プローブタック値の測定条件)
測定機器:NSプローブタックテスター(ニチバン株式会社製)
プローブ直径:5mmφ
プローブ基材:ステンレススチール表面仕上げAA#400研磨による鏡面
ウェイト:19.6±0.2g(真鍮製)
プローブ移動速度:1.0cm/秒
デュエルタイム:1秒間。
この構成により、本発明の粘着シートは、粘着剤層が後硬化性を有し、粘着剤層が後硬化された場合に加工性に優れる。粘着剤層が後硬化された場合に剪断貯蔵弾性率G’が23℃および75℃で特定の範囲以上であることにより、加工性を良好とする硬さとなる。また、粘着剤層が後硬化された場合にプローブタック値が23℃で特定の範囲以下であることにより、例えば打抜き加工時の打抜き刃への粘着剤の付着やそれに伴う粘着剤層の変形などを防ぐことが出来る。
[Adhesive sheet]
The pressure-sensitive adhesive sheet of the present invention has a pressure-sensitive adhesive layer in which the pressure-sensitive adhesive composition is in a semi-cured state,
The pressure-sensitive adhesive composition comprises a crosslinkable acrylic polymer, a crosslinking agent, a polyfunctional monomer having two or more reactive double bonds in the molecule, and a monofunctional monomer having one reactive double bond in the molecule And a polymerization initiator,
When the monofunctional monomer is polymerized, the glass transition temperature (Tg) of the homopolymer is 50 ° C. or more and less than 200 ° C.,
The pressure-sensitive adhesive layer has post-curing properties and
The following physical property group (1) is satisfied when the pressure-sensitive adhesive layer is post-cured.
Physical property group (1): Shear storage modulus G ′ measured at 23 ° C. and frequency 1 Hz is 1.0 × 10 6 [Pa] or more, and shear storage modulus G ′ measured at 75 ° C. and frequency 1 Hz Is 1.0 × 10 5 [Pa] or more, and the probe tack value measured at 23 ° C. and the following measurement conditions is 1.5 N / 5 mmφ or less.
(Measurement condition of probe tack value)
Measuring equipment: NS probe tack tester (made by Nichiban Co., Ltd.)
Probe diameter: 5 mmφ
Probe base material: Specular weight by stainless steel surface finish AA # 400 polishing: 19.6 ± 0.2 g (made of brass)
Probe moving speed: 1.0 cm / sec Duel time: 1 sec.
With this configuration, the pressure-sensitive adhesive sheet of the present invention has post-curing properties and is excellent in processability when the pressure-sensitive adhesive layer is post-cured. When the pressure-sensitive adhesive layer is post-cured, the shear storage elastic modulus G ′ is 23 ° C. and 75 ° C. or more, which is a hardness that makes the processability good. In addition, when the pressure-sensitive adhesive layer is post-cured, the probe tack value is 23 ° C. and below the specific range, for example, adhesion of the pressure-sensitive adhesive to the punching blade during punching and deformation of the pressure-sensitive adhesive layer Can be prevented.
<粘着シートの構成>
まず、本発明の粘着シートの構成を簡単に説明する。図1は、本発明の粘着シートの一例の断面を表す概略図である。
本発明の粘着シート1は、粘着剤層11を有する。粘着シート1は、粘着剤層11のみから構成される単層の粘着シートであってもよい。また、粘着シートは、片面に基材(好ましくは透明基材)を備えた片面粘着シートでも、両面粘着シートでもよい。
片面粘着シートとしては、図1に示すように、粘着剤層11の片面に透明基材12aを備えた構成となる。粘着剤層11のもう一方の面は剥離シート12bによって覆われていることが好ましい。本粘着シートを使用する場合はこの剥離シート12bを剥がして所望の被着体に粘着剤層11が密着するように貼合し、その後エネルギー線照射などで後硬化をすることが好ましい。透明基材としてはポリエチレンテレフタレートフィルムやアクリルフィルム、ポリカーボネートフィルム、トリアセチルセルロースフィルム、シクロオレフィンポリマーフィルムなど光学分野に用いられる一般的なフィルムを用いることが出来る。またこれらの透明基材の粘着剤層側には易接着層を設けていても良い。さらに、透明基材の粘着剤層とは逆面にはハードコート層や反射防止層、防汚層、紫外線吸収層などの機能層を備えていても良い。
両面粘着シートとしては、粘着剤層からなる単層の粘着シート、粘着剤層を複数積層した多層の粘着シート、粘着剤層と粘着剤層の間に他の粘着剤層を積層した多層の粘着シート、粘着剤層と粘着剤層の間に支持体を積層した多層の粘着シート、支持体の片面に粘着剤層が積層し、他方の面に他の粘着剤層が積層した多層の粘着シートが挙げられる。両面粘着シートが支持体を有する場合、支持体として透明な支持体を用いたものが好ましい。支持体としては、透明基材と同様に光学分野に用いられる一般的なフィルムを用いることができる。このような両面粘着シートは、粘着シート全体としての透明性にも優れることから、光学部材同士の接着に好適に用いることができる。
本発明の粘着シートは、(両面粘着シートであって)剥離力が互いに異なる1対の剥離シートを粘着剤層の両面に有する構成、または(片面粘着シートであって)透明基材/粘着剤層/剥離シートの構成であることがより好ましい。本発明の粘着シートは、(片面粘着シートであって)透明基材/粘着剤層/剥離シートの構成であることが特に好ましい。
<Composition of adhesive sheet>
First, the configuration of the pressure-sensitive adhesive sheet of the present invention will be briefly described. FIG. 1 is a schematic view showing a cross section of an example of the pressure-sensitive adhesive sheet of the present invention.
The pressure-sensitive adhesive sheet 1 of the present invention has a pressure-sensitive adhesive layer 11. The pressure-sensitive adhesive sheet 1 may be a single-layer pressure-sensitive adhesive sheet composed only of the pressure-sensitive adhesive layer 11. The pressure-sensitive adhesive sheet may be a single-sided pressure-sensitive adhesive sheet provided with a substrate (preferably a transparent substrate) on one side, or a double-sided pressure-sensitive adhesive sheet.
As a single-sided pressure-sensitive adhesive sheet, as shown in FIG. 1, the
As a double-sided pressure-sensitive adhesive sheet, a single-layer pressure-sensitive adhesive sheet consisting of a pressure-sensitive adhesive layer, a multilayer pressure-sensitive adhesive sheet obtained by laminating a plurality of pressure-sensitive adhesive layers, and a multilayer pressure-sensitive adhesive layer laminated with another pressure-sensitive adhesive layer Sheet, multi-layered adhesive sheet in which a support is laminated between an adhesive layer and an adhesive layer, multi-layered adhesive sheet in which an adhesive layer is laminated on one side of the support and another adhesive layer is laminated on the other side Can be mentioned. When the double-sided pressure-sensitive adhesive sheet has a support, one using a transparent support as the support is preferred. As the support, a general film used in the optical field as well as the transparent substrate can be used. Such a double-sided pressure-sensitive adhesive sheet is also excellent in transparency as the entire pressure-sensitive adhesive sheet, and thus can be suitably used for bonding optical members.
The pressure-sensitive adhesive sheet of the present invention has a structure in which a pair of release sheets (which are double-sided pressure-sensitive adhesive sheets) having mutually different peel strengths on both sides of the pressure-sensitive adhesive layer, or (a single-sided pressure-sensitive adhesive sheet) More preferably, it is a layer / release sheet configuration. The pressure-sensitive adhesive sheet of the present invention is particularly preferably a single-sided pressure-sensitive adhesive sheet (transparent substrate) / pressure-sensitive adhesive layer / release sheet.
<剥離シート>
粘着剤層11の表面は剥離シートによって覆われていることが好ましい。すなわち、粘着シートは、剥離シート付きの粘着シートであることが好ましい。
図1に示された粘着剤層11は剥離シート12b(両面粘着シートの場合は12aも剥離シートとなる)を有しており、図1は、剥離シート付きの粘着シート1の構成の一例を表すものである。
<Peeling sheet>
The surface of the pressure-sensitive adhesive layer 11 is preferably covered with a release sheet. That is, it is preferable that an adhesive sheet is an adhesive sheet with a peeling sheet.
The pressure-sensitive adhesive layer 11 shown in FIG. 1 has a
剥離シートとしては、剥離シート用基材とこの剥離シート用基材の片面に設けられた剥離剤層とを有する剥離性積層シート、あるいは、低極性基材としてポリエチレンフィルムやポリプロピレンフィルム等のポリオレフィンフィルムが挙げられる。
剥離性積層シートにおける剥離シート用基材には、紙類、高分子フィルムが使用される。剥離剤層を構成する剥離剤としては、例えば、汎用の付加型もしくは縮合型のシリコーン系剥離剤や長鎖アルキル基含有化合物が用いられる。特に、反応性が高い付加型シリコーン系剥離剤が好ましく用いられる。
シリコーン系剥離剤としては、具体的には、東レ・ダウコーニングシリコーン社製のBY24−4527、SD−7220等や、信越化学工業(株)製のKS−3600、KS−774、X62−2600などが挙げられる。また、シリコーン系剥離剤中にSiO2単位と(CH3)3SiO1/2単位あるいはCH2=CH(CH3)SiO1/2単位を有する有機珪素化合物であるシリコーンレジンを含有することが好ましい。シリコーンレジンの具体例としては、東レ・ダウコーニングシリコーン社製のBY24−843、SD−7292、SHR−1404等や、信越化学工業(株)製のKS−3800、X92−183等が挙げられる。
剥離性積層シートとして、市販品を用いてもよい。例えば、帝人デュポンフィルム(株)製の離型処理されたポリエチレンテレフタレートフィルムである重セパレータフィルムや、帝人デュポンフィルム(株)製の離型処理されたポリエチレンテレフタレートフィルムである軽セパレータフィルムを挙げることができる。
As a release sheet, a peelable laminate sheet having a release sheet substrate and a release agent layer provided on one side of the release sheet substrate, or a polyolefin film such as a polyethylene film or a polypropylene film as a low polarity substrate Can be mentioned.
Papers and polymer films are used for the release sheet base in the release laminate sheet. As the release agent constituting the release agent layer, for example, a general-purpose addition type or condensation type silicone release agent or a long chain alkyl group-containing compound is used. In particular, an addition-type silicone release agent having high reactivity is preferably used.
Specific examples of silicone release agents include BY24-4527 and SD-7220 manufactured by Toray Dow Corning Silicone Co., Ltd., KS-3600 manufactured by Shin-Etsu Chemical Co., Ltd., KS-774 and X62-2600 etc. Can be mentioned. In addition, a silicone resin which is an organic silicon compound having a SiO 2 unit and a (CH 3 ) 3 SiO 1/2 unit or a CH 2 CHCH (CH 3 ) SiO 1/2 unit in a silicone-based release agent preferable. Specific examples of the silicone resin include BY24-843, SD-7292, SHR-1404, etc. manufactured by Toray Dow Corning Silicone Co., Ltd., KS-3800, X92-183, etc. manufactured by Shin-Etsu Chemical Co., Ltd.
A commercial item may be used as the peelable laminated sheet. For example, mention may be made of a heavy separator film which is a release-treated polyethylene terephthalate film manufactured by Teijin DuPont Films Ltd., and a light separator film which is a release-treated polyethylene terephthalate film manufactured by Teijin DuPont Films Ltd. it can.
本発明の粘着シートが両面粘着シートの場合は、剥離力が互いに異なる1対の剥離シートを有することが好ましい。すなわち、剥離シートは、剥離しやすくするために、剥離シート12aと剥離シート12bとの剥離性を異なるものとすることが好ましい。一方からの剥離性と他方からの剥離性とが異なると、剥離性が高い方の剥離シートだけを先に剥離することが容易となる。その場合、貼合方法や貼合順序に応じて剥離シート12aと剥離シート12bの剥離性を調整すればよい。
When the pressure-sensitive adhesive sheet of the present invention is a double-sided pressure-sensitive adhesive sheet, it is preferable to have a pair of release sheets having different release forces. That is, in order to make it easy to peel off the release sheet, it is preferable that the release properties of the
<粘着剤層>
本発明の粘着シートは、粘着剤組成物を半硬化状態とした粘着剤層を有し、粘着剤層は後硬化性を有し、粘着剤層が後硬化された場合に上述の物性群(1)を満たす。
<Pressure-sensitive adhesive layer>
The pressure-sensitive adhesive sheet of the present invention has a pressure-sensitive adhesive layer in which the pressure-sensitive adhesive composition is in a semi-cured state, and the pressure-sensitive adhesive layer has post-curing properties. Meet 1).
(粘着剤層の物性および特性)
本発明の粘着シートの粘着剤層は、粘着剤組成物を半硬化状態としたものであり、後硬化性を有する。
粘着剤層が半硬化状態であることは、ゲル分率が0質量%以上70質量%未満であることから確認できる。粘着剤層の半硬化状態でのゲル分率は2質量%以上70質量%未満であることが好ましく、5〜65質量%であることが特に好ましい。
粘着剤層が後硬化後であることは、ゲル分率が70〜100質量%であることから確認できる。粘着剤層の後硬化された場合に後硬化後のゲル分率が75〜100質量%であることが特に好ましい。
粘着剤層が後硬化性を有することは、粘着剤層が後硬化された場合に後硬化後のゲル分率が、半硬化状態でのゲル分率より5質量%以上高くなることから確認できる。粘着剤層が後硬化された場合に後硬化後のゲル分率が、半硬化状態でのゲル分率より10質量%以上高くなることが好ましく、15質量%以上高くなることがより好ましい。
(Physical properties and characteristics of adhesive layer)
The pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet of the present invention has the pressure-sensitive adhesive composition in a semi-cured state, and has post-curing properties.
The semi-cured state of the pressure-sensitive adhesive layer can be confirmed from the gel fraction of 0% by mass or more and less than 70% by mass. The gel fraction in the semi-cured state of the pressure-sensitive adhesive layer is preferably 2% by mass or more and less than 70% by mass, and particularly preferably 5-65% by mass.
That the pressure-sensitive adhesive layer is post-cured can be confirmed from the gel fraction of 70 to 100% by mass. It is particularly preferable that the gel fraction after post-curing when it is post-cured is 75 to 100% by mass.
The post-curing property of the pressure-sensitive adhesive layer can be confirmed from the fact that the gel fraction after post-curing when the pressure-sensitive adhesive layer is post-cured is 5% by mass or more higher than the gel fraction in the semi-cured state . When the pressure-sensitive adhesive layer is post-cured, the gel fraction after post-curing is preferably 10% by mass or more higher than the gel fraction in the semi-cured state, and more preferably 15% by mass or more.
「半硬化」は、粘着剤層を初めに熱のみにより硬化させることが好ましい。「半硬化状態」とは熱硬化後であって、活性エネルギー線照射前の柔らかい粘着剤層であることが好ましい。また、「後硬化」は、熱によって半硬化状態とした後に活性エネルギー線によって粘着剤層を硬化することが好ましい。
すなわち、本発明の粘着シートの粘着剤層は、粘着剤組成物を熱硬化させて半硬化状態となっていることが好ましく、かつ、活性エネルギー線硬化性を有することが好ましい。
In the "semi-curing", it is preferable to cure the pressure-sensitive adhesive layer first by heat only. The "semi-cured state" is preferably a soft pressure-sensitive adhesive layer after heat curing and before irradiation with active energy rays. In “post-curing”, it is preferable to cure the pressure-sensitive adhesive layer by active energy rays after being brought into a semi-cured state by heat.
That is, the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet of the present invention is preferably in a semi-cured state by thermally curing the pressure-sensitive adhesive composition, and preferably has active energy ray curability.
−物性群(1)−
本発明では、粘着剤層が後硬化された場合に物性群(1)を満たす。
物性群(1):23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×106[Pa]以上であり、75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×105[Pa]以上であり、23℃かつ上述の測定条件で測定されるプローブタック値が1.5N/5mmφ以下である。
粘着剤層が後硬化された場合に23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’は1.2×106[Pa]以上であることが好ましく、1.5×106[Pa]以上であることがより好ましく、2.0×106[Pa]以上であることがさらに好ましく、3.0×106[Pa]以上であることが特に好ましい。粘着剤層が後硬化された場合に23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’の上限値は特に制限はなく、例えば1.0×108[Pa]以下にすることができる。
粘着剤層が後硬化された場合に75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’は1.1×105[Pa]以上であることが好ましく、1.5×105[Pa]以上であることがより好ましく、2.0×105[Pa]以上であることがさらに好ましい。粘着剤層が後硬化された場合に23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’の上限値は特に制限はなく、例えば1.0×108[Pa]以下にすることができる。
粘着剤層が後硬化された場合に23℃かつ上述の測定条件で測定されるプローブタック値は1.0N/5mmφ以下であることが好ましく、0.5N/5mmφ以下であることがより好ましい。粘着剤層が後硬化された場合に23℃かつ上述の測定条件で測定されるプローブタック値の下限値は特に制限はないが、例えば0.1N/5mmφ以上にすることができる。
-Physical property group (1)-
In the present invention, the physical property group (1) is satisfied when the pressure-sensitive adhesive layer is post-cured.
Physical property group (1): Shear storage modulus G ′ measured at 23 ° C. and frequency 1 Hz is 1.0 × 10 6 [Pa] or more, and shear storage modulus G ′ measured at 75 ° C. and frequency 1 Hz Is 1.0 × 10 5 [Pa] or more, and a probe tack value measured at 23 ° C. and the above-mentioned measurement conditions is 1.5 N / 5 mmφ or less.
When the pressure-sensitive adhesive layer is post-cured, the shear storage modulus G ′ measured at 23 ° C. and a frequency of 1 Hz is preferably 1.2 × 10 6 [Pa] or more, and 1.5 × 10 6 [Pa Or more], more preferably 2.0 × 10 6 [Pa] or more, and particularly preferably 3.0 × 10 6 [Pa] or more. The upper limit of the shear storage modulus G ′ measured at 23 ° C. and a frequency of 1 Hz when the pressure-sensitive adhesive layer is post-cured is not particularly limited, and can be, for example, 1.0 × 10 8 [Pa] or less .
The shear storage modulus G ′ measured at 75 ° C. and a frequency of 1 Hz when the pressure-sensitive adhesive layer is post-cured is preferably 1.1 × 10 5 [Pa] or more, 1.5 × 10 5 [Pa It is more preferable that it is more than, and it is further more preferable that it is 2.0 * 10 < 5 > [Pa] or more. The upper limit of the shear storage modulus G ′ measured at 23 ° C. and a frequency of 1 Hz when the pressure-sensitive adhesive layer is post-cured is not particularly limited, and can be, for example, 1.0 × 10 8 [Pa] or less .
When the pressure-sensitive adhesive layer is post-cured, the probe tack value measured at 23 ° C. and the above-described measurement conditions is preferably 1.0 N / 5 mmφ or less, and more preferably 0.5 N / 5 mmφ or less. The lower limit of the probe tack value measured under the above-mentioned measurement conditions at 23 ° C. when the pressure-sensitive adhesive layer is post-cured is not particularly limited, but can be, for example, 0.1 N / 5 mmφ or more.
−物性群(2)−
本発明では、粘着剤層が半硬化状態で下記物性群(2)を満たすことが好ましい。
物性群(2):23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が8.0×105[Pa]以下であり、75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×105[Pa]以下であり、23℃かつ上述の測定条件で測定されるプローブタック値が2.0N/5mmφ以上。
粘着剤層が半硬化状態である場合に23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’は5.0×105[Pa]以下であることがより好ましく、2.0×105[Pa]以下であることが特に好ましい。粘着剤層が半硬化状態である場合に23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’の下限値は特に制限はなく、例えば1.0×104[Pa]以上にすることができる。
粘着剤層が半硬化状態である場合に75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が5.0×104[Pa]以下であることがより好ましく、3.0×104[Pa]以下であることが特に好ましい。粘着剤層が半硬化状態である場合に75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’の下限値は特に制限はなく、例えば1.0×103[Pa]以上にすることができる。
粘着剤層が半硬化状態である場合に23℃かつ上述の測定条件で測定されるプローブタック値が2.5N/5mmφ以上であることがより好ましく、3.0N/5mmφ以上であることが特に好ましい。粘着剤層が半硬化状態である場合に23℃かつ上述の測定条件で測定されるプローブタック値の上限値は特に制限はないが、例えば20.0N/5mmφ以下にすることができ、15.0N/5mmφ以下にすることが好ましい。
-Physical property group (2)-
In the present invention, it is preferable that the pressure-sensitive adhesive layer satisfy the following physical property group (2) in a semi-cured state.
Physical property group (2): Shear storage modulus G ′ measured at 23 ° C. and frequency 1 Hz is 8.0 × 10 5 [Pa] or less, and shear storage modulus G ′ measured at 75 ° C. and frequency 1 Hz Is 1.0 × 10 5 [Pa] or less, the probe tack value measured at 23 ° C. and the above-mentioned measurement condition is 2.0 N / 5 mmφ or more.
The shear storage modulus G ′ measured at 23 ° C. and a frequency of 1 Hz when the pressure-sensitive adhesive layer is in a semi-cured state is more preferably 5.0 × 10 5 [Pa] or less, 2.0 × 10 5 It is particularly preferable that the pressure is [Pa] or less. The lower limit of the shear storage modulus G ′ measured at 23 ° C. and a frequency of 1 Hz when the pressure-sensitive adhesive layer is in a semi-cured state is not particularly limited, and may be, for example, 1.0 × 10 4 [Pa] or more it can.
When the pressure-sensitive adhesive layer is in a semi-cured state, the shear storage modulus G ′ measured at 75 ° C. and a frequency of 1 Hz is more preferably 5.0 × 10 4 [Pa] or less, 3.0 × 10 4 It is particularly preferable that the pressure is [Pa] or less. The lower limit of the shear storage modulus G ′ measured at 75 ° C. and a frequency of 1 Hz when the pressure-sensitive adhesive layer is in a semi-cured state is not particularly limited, and may be, for example, 1.0 × 10 3 [Pa] or more it can.
When the pressure-sensitive adhesive layer is in a semi-cured state, the probe tack value measured under the measurement conditions described above at 23 ° C. is more preferably 2.5 N / 5 mmφ or more, particularly preferably 3.0 N / 5 mmφ or more preferable. The upper limit of the probe tack value measured under the measurement conditions described above at 23 ° C. when the pressure-sensitive adhesive layer is in a semi-cured state is not particularly limited, but can be, for example, 20.0 N / 5 mmφ or less; It is preferable to set it to 0 N / 5 mmφ or less.
−加工性−
本発明の粘着シートは、後硬化後において、加工性にも優れる。特に、カット端部をこすった場合の剥がれ距離が少ないことが好ましい。後硬化後の加工性は、粘着剤層が後硬化された場合の剪断貯蔵弾性率G’を特定の範囲以上とし、粘着剤層が後硬化された場合のプローブタック値を特定の範囲以下とすることにより、改善することができる。
-Processability-
The pressure-sensitive adhesive sheet of the present invention is also excellent in processability after post-curing. In particular, it is preferable that the peeling distance is small when the cut end is rubbed. The processability after post-curing is such that the shear storage modulus G ′ when the pressure-sensitive adhesive layer is post-cured is equal to or higher than the specific range, and the probe tack value when the pressure-sensitive adhesive layer is post-cured is equal to or lower than the specific range It can be improved by doing.
−端面のベタツキ−
本発明の粘着シートは、後硬化後において、粘着剤層の端面のベタツキ(タック性)が少ない。後硬化後の粘着剤層の端面のベタツキは、粘着剤層が後硬化された場合の剪断貯蔵弾性率G’を特定の範囲以上とし、粘着剤層が後硬化された場合のプローブタック値を特定の範囲以下とすることにより、少なくすることができる。
-Stickiness of end face-
The adhesive sheet of the present invention is less sticky (tackiness) at the end face of the adhesive layer after post-curing. The tackiness of the end face of the pressure-sensitive adhesive layer after post-curing sets the shear storage modulus G ′ when the pressure-sensitive adhesive layer is post-cured to a specific range or higher, and the probe tack value when the pressure-sensitive adhesive layer is post-cured It can reduce by setting it as a specific range or less.
−耐アウトガス性−
本発明の粘着シートは、後硬化後において、耐アウトガス性にも優れる。特に、高温高湿環境下に置いて長時間が経過した後に目視で観察できるような気泡、剥がれが生じない。後硬化後の耐アウトガス性は、半硬化状態での剪断貯蔵弾性率G’を特定の範囲以下とし、後硬化後の剪断貯蔵弾性率G’を特定の範囲以上とすることで、改善することができる。
-Outgassing resistance-
The pressure-sensitive adhesive sheet of the present invention is also excellent in outgas resistance after post-curing. In particular, air bubbles and peeling that can be observed visually after a long period of time under high temperature and high humidity environment does not occur. Improve the outgassing resistance after post-curing by setting the shear storage modulus G 'in the semi-cured state to a specific range or less and the shear storage modulus G' after post-curing to a specific range or more Can.
(厚み)
粘着剤層の厚みは、用途に応じて適宜設定でき、特に限定されないが、5〜500μmの範囲内であることが好ましく、10〜300μmがより好ましく、12〜100μmが特に好ましい。粘着剤層の厚みを上記範囲内とすることにより、基材等の被着体から気泡が発生することを十分に抑制することができる。また、粘着剤のはみ出しやべたつきを抑制することができるため加工性に優れる。さらに、粘着剤層の厚さを上記範囲内とすることにより、両面粘着シートの製造が容易となる。
(Thickness)
The thickness of the pressure-sensitive adhesive layer can be appropriately set depending on the application and is not particularly limited, but is preferably in the range of 5 to 500 μm, more preferably 10 to 300 μm, and particularly preferably 12 to 100 μm. By setting the thickness of the pressure-sensitive adhesive layer within the above range, the occurrence of air bubbles from an adherend such as a substrate can be sufficiently suppressed. Moreover, since the protrusion and stickiness of an adhesive can be suppressed, it is excellent in processability. Furthermore, manufacture of a double-sided adhesive sheet becomes easy by carrying out the thickness of an adhesive layer in the said range.
<粘着剤組成物>
上述の粘着剤層は、粘着剤組成物を半硬化状態としたものである。
本発明では、粘着剤組成物が架橋性アクリル重合体、架橋剤、分子内に反応性二重結合を2つ以上有する多官能単量体、分子内に反応性二重結合を1つ有する単官能単量体および重合開始剤を含有する。ここで、分子内に反応性二重結合を1つ有する単官能単量体を重合した場合のホモポリマーのガラス転移温度(Tg)は50℃以上200℃未満である。
本発明で用いられる粘着剤組成物は、デュアル硬化型粘着剤組成物であることが好ましい。
<Adhesive composition>
The above-mentioned pressure-sensitive adhesive layer is a pressure-sensitive adhesive composition in a semi-cured state.
In the present invention, the pressure-sensitive adhesive composition comprises a crosslinkable acrylic polymer, a crosslinking agent, a polyfunctional monomer having two or more reactive double bonds in the molecule, and a single monomer having one reactive double bond in the molecule. It contains a functional monomer and a polymerization initiator. Here, the glass transition temperature (Tg) of the homopolymer when a monofunctional monomer having one reactive double bond in the molecule is polymerized is 50 ° C. or more and less than 200 ° C.
The pressure-sensitive adhesive composition used in the present invention is preferably a dual-curable pressure-sensitive adhesive composition.
(架橋性アクリル重合体)
本発明では、粘着剤組成物が架橋性アクリル重合体を含有する。
架橋性アクリル重合体は、特に制限はないが、非架橋性(メタ)アクリル酸エステル単位(a1)と、架橋性官能基を有するアクリル単量体単位(a2)を含有することが好ましい。架橋性アクリル重合体は、表示装置の視認性を低下させない程度の透明性を有するものが好ましい。なお、本明細書および特許請求の範囲において、「単位」は重合体を構成する繰り返し単位(単量体単位)である。
(Crosslinkable acrylic polymer)
In the present invention, the pressure-sensitive adhesive composition contains a crosslinkable acrylic polymer.
The crosslinkable acrylic polymer is not particularly limited, but preferably contains a non-crosslinkable (meth) acrylic acid ester unit (a1) and an acrylic monomer unit (a2) having a crosslinkable functional group. The crosslinkable acrylic polymer is preferably one having transparency to such an extent that the visibility of the display device is not reduced. In the present specification and claims, a "unit" is a repeating unit (monomer unit) constituting a polymer.
非架橋性(メタ)アクリル酸エステル単位(a1)は、(メタ)アクリル酸アルキルエステルに由来する繰り返し単位である。(メタ)アクリル酸アルキルエステルとしては、(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸プロピル、(メタ)アクリル酸イソプロピル、(メタ)アクリル酸n−ブチル、(メタ)アクリル酸イソブチル、(メタ)アクリル酸t−ブチル、(メタ)アクリル酸n−ペンチル、(メタ)アクリル酸n−ヘキシル、(メタ)アクリル酸2−エチルヘキシル、(メタ)アクリル酸n−オクチル、(メタ)アクリル酸イソオクチル、(メタ)アクリル酸n−ノニル、(メタ)アクリル酸イソノニル、(メタ)アクリル酸n−デシル、(メタ)アクリル酸イソデシル、(メタ)アクリル酸n−ウンデシル、(メタ)アクリル酸n−ドデシル、(メタ)アクリル酸ステアリル、(メタ)アクリル酸メトキシエチル、(メタ)アクリル酸エトキシエチル、(メタ)アクリル酸シクロヘキシル、(メタ)アクリル酸ベンジル等が挙げられる。これらは1種類を単独で使用してもよいし、2種類以上を併用してもよい。
上記(メタ)アクリル酸アルキルエステルの中でも、粘着性が高くなることから、(メタ)アクリル酸メチル、(メタ)アクリル酸n−ブチル、(メタ)アクリル酸2−エチルヘキシルから選ばれる少なくとも1種類が好ましい。
The non-crosslinkable (meth) acrylic acid ester unit (a1) is a repeating unit derived from a (meth) acrylic acid alkyl ester. As (meth) acrylic acid alkyl ester, methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, isopropyl (meth) acrylate, n-butyl (meth) acrylate, (meth) Isobutyl acrylate, t-butyl (meth) acrylate, n-pentyl (meth) acrylate, n-hexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, n-octyl (meth) acrylate ( (Meth) acrylate isooctyl, (meth) acrylate n-nonyl, (meth) acrylate isononyl, n-decyl (meth) acrylate, isodecyl (meth) acrylate, n-undecyl (meth) acrylate, (meth) N-dodecyl acrylate, stearyl (meth) acrylate, methoxyethyl (meth) acrylate, ) Ethoxyethyl acrylate, cyclohexyl (meth) acrylate include benzyl (meth) acrylate and the like. One of these may be used alone, or two or more may be used in combination.
Among the above (meth) acrylic acid alkyl esters, at least one selected from methyl (meth) acrylate, n-butyl (meth) acrylate and 2-ethylhexyl (meth) acrylate is preferred because the tackiness is high. preferable.
本発明では、架橋性アクリル重合体が有する架橋性官能基が、カルボキシ基、ヒドロキシ基、アミノ基、アミド基、グリシジル基およびイソシアネート基から選択される1種類または2種類以上であることが好ましく、カルボキシ基、ヒドロキシ基、アミノ基およびグリシジル基から選択される1種類または2種類以上であることがより好ましい。
架橋性官能基を有するアクリル単量体単位(a2)は、カルボキシ基含有単量体単位、ヒドロキシ基含有単量体単位、アミノ基含有単量体単位、グリシジル基含有単量体単位が好ましい。
カルボキシ基含有単量体単位としては、アクリル酸、メタクリル酸が挙げられる。
ヒドロキシ基含有単量体単位は、ヒドロキシ基含有単量体に由来する繰り返し単位である。ヒドロキシ基含有単量体としては、例えば、(メタ)アクリル酸2−ヒドロキシエチル、(メタ)アクリル酸4−ヒドロキシブチル、(メタ)アクリル酸2−ヒドロキシプロピルなどの(メタ)アクリル酸ヒドロキシアルキル、(メタ)アクリル酸モノ(ジエチレングリコール)などの(メタ)アクリル酸[(モノ、ジ又はポリ)アルキレングリコール]、(メタ)アクリル酸モノカプロラクトンなどの(メタ)アクリル酸ラクトンが挙げられる。
アミノ基含有単量体単位としては、例えば、(メタ)アクリルアミド、アリルアミン等のアミノ基含有単量体に由来する繰り返し単位が挙げられる。
グリシジル基含有単量体単位としては、(メタ)アクリル酸グリシジル等のグリシジル基含有単量体に由来する繰り返し単位が挙げられる。
In the present invention, the crosslinkable functional group possessed by the crosslinkable acrylic polymer is preferably one or more selected from a carboxy group, a hydroxy group, an amino group, an amido group, a glycidyl group and an isocyanate group, More preferably, it is one or more selected from a carboxy group, a hydroxy group, an amino group and a glycidyl group.
The acrylic monomer unit (a2) having a crosslinkable functional group is preferably a carboxy group-containing monomer unit, a hydroxy group-containing monomer unit, an amino group-containing monomer unit, or a glycidyl group-containing monomer unit.
As a carboxy-group containing monomer unit, acrylic acid and methacrylic acid are mentioned.
The hydroxy group-containing monomer unit is a repeating unit derived from a hydroxy group-containing monomer. As the hydroxy group-containing monomer, for example, hydroxyalkyl (meth) acrylate such as 2-hydroxyethyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, etc. (Meth) acrylic acid [(mono, di or poly) alkylene glycol] such as (meth) acrylic acid mono (diethylene glycol) and (meth) acrylic acid lactone such as (meth) acrylic acid monocaprolactone.
As an amino-group containing monomeric unit, the repeating unit derived from amino-group containing monomers, such as (meth) acrylamide and allylamine, is mentioned, for example.
As a glycidyl group containing monomeric unit, the repeating unit derived from glycidyl group containing monomers, such as glycidyl (meth) acrylate, is mentioned.
架橋性アクリル重合体における架橋性官能基を有するアクリル単量体単位(a2)の含有量は0.01〜40質量%であることが好ましく、0.5〜35質量%であることがより好ましい。架橋性官能基を有するアクリル単量体単位(a2)の含有量が上記範囲の下限値以上であれば、半硬化状態を維持するために必要な架橋性を十分に有しており、上記範囲の上限値以下であれば必要な粘着性を維持しやすい。 The content of the acrylic monomer unit (a2) having a crosslinkable functional group in the crosslinkable acrylic polymer is preferably 0.01 to 40% by mass, and more preferably 0.5 to 35% by mass . When the content of the acrylic monomer unit (a2) having a crosslinkable functional group is at least the lower limit value of the above range, it has sufficient crosslinkability necessary to maintain the semi-cured state, and the above range If it is below the upper limit value of, it is easy to maintain the necessary adhesiveness.
架橋性アクリル重合体は、必要に応じて、非架橋性(メタ)アクリル酸エステル単位(a1)および架橋性官能基を有するアクリル単量体単位(a2)以外の他の単量体単位を有してもよい。他の単量体は、非架橋性(メタ)アクリル酸エステルおよび架橋性官能基を有するアクリル単量体と共重合可能なものであればよく、例えば(メタ)アクリロニトリル、酢酸ビニル、スチレン、塩化ビニル、ビニルピロリドン、ビニルピリジン等が挙げられる。架橋性アクリル重合体における他の単量体単位の含有量は0〜20質量%であることが好ましく、0〜15質量%であることがより好ましい。 The crosslinkable acrylic polymer has, if necessary, other monomer units other than the non-crosslinkable (meth) acrylic acid ester unit (a1) and the acrylic monomer unit (a2) having a crosslinkable functional group. You may Other monomers may be those which can be copolymerized with non-crosslinkable (meth) acrylic acid ester and acrylic monomers having a crosslinkable functional group, and examples thereof include (meth) acrylonitrile, vinyl acetate, styrene, chloride Vinyl, vinyl pyrrolidone, vinyl pyridine and the like can be mentioned. The content of the other monomer units in the crosslinkable acrylic polymer is preferably 0 to 20% by mass, and more preferably 0 to 15% by mass.
架橋性アクリル重合体の重量平均分子量は、10〜200万が好ましく、30〜150万がより好ましい。重量平均分子量が上記範囲内であると、粘着シートの半硬化状態を維持しやすく、かつ後硬化後の硬度を出しやすく、加工性に優れる。なお、架橋性アクリル重合体の重量平均分子量は架橋剤で架橋される前の値である。重量平均分子量は、サイズ排除クロマトグラフィー(SEC)により測定し、ポリスチレン基準で求めた値である。架橋性アクリル重合体としては、市販のものを用いてもよく、公知の方法により合成したものを用いてもよい。 10-2,000,000 are preferable and, as for the weight average molecular weight of a crosslinkable acrylic polymer, 30-150,000 are more preferable. It is easy to maintain the semi-hardened state of an adhesive sheet as a weight average molecular weight is in the said range, and it is easy to take out the hardness after post-hardening, and it is excellent in workability. The weight average molecular weight of the crosslinkable acrylic polymer is a value before being crosslinked by the crosslinking agent. The weight average molecular weight is a value determined by size exclusion chromatography (SEC) and determined based on polystyrene. A commercially available thing may be used as a crosslinkable acrylic polymer, and what was synthesize | combined by the well-known method may be used.
(架橋剤)
本発明では、粘着剤組成物が架橋剤を含有する。
架橋剤は、架橋性アクリル重合体が有する架橋性官能基との反応性を考慮して適宜選択できる。例えばイソシアネート化合物、エポキシ化合物、オキサゾリン化合物、アジリジン化合物、金属キレート化合物、ブチル化メラミン化合物などの公知の架橋剤の中から選択できる。これらの中でも、架橋性官能基を有するアクリル単量体単位(a2)を容易に架橋できることから、イソシアネート化合物やエポキシ化合物が好ましい。本発明では、架橋剤が二官能以上のエポキシ化合物および二官能以上のイソシアネート化合物から選択される1種類または2種類以上であることが好ましい。
例えば、架橋性官能基としてヒドロキシ基を含む場合は、ヒドロキシ基の反応性から、イソシアネート化合物を用いることがより好ましい。
(Crosslinking agent)
In the present invention, the pressure-sensitive adhesive composition contains a crosslinking agent.
A crosslinking agent can be suitably selected in consideration of the reactivity with the crosslinkable functional group which a crosslinkable acrylic polymer has. For example, it can be selected from known crosslinking agents such as isocyanate compounds, epoxy compounds, oxazoline compounds, aziridine compounds, metal chelate compounds and butylated melamine compounds. Among these, an isocyanate compound and an epoxy compound are preferable because the acrylic monomer unit (a2) having a crosslinkable functional group can be easily crosslinked. In the present invention, the crosslinking agent is preferably one or more selected from a difunctional or higher epoxy compound and a difunctional or higher isocyanate compound.
For example, when it contains a hydroxy group as a crosslinkable functional group, it is more preferable to use an isocyanate compound from the reactivity of the hydroxy group.
イソシアネート化合物としては、例えば、トリレンジイソシアネート、キシリレンジイソシアネート、ヘキサメチレンジイソシアネート、イソホロンジイソシアネート等が挙げられる。
エポキシ化合物としては、例えば、エチレングリコールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、プロピレングリコールジグリシジルエーテル、ポリプロピレングリコールジグリシジルエーテル、グリセリンジグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、1,6−ヘキサンジオールジグリシジルエーテル、テトラグリシジルキシレンジアミン、1,3−ビス(N,N−ジグリシジルアミノメチル)シクロヘキサン、トリメチロールプロパンポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ソルビトールポリグリシジルエーテル等が挙げられる。
架橋剤として、市販品を使用できる。市販品の例としては、トリレンジイソシアネート化合物(日本ポリウレタン工業(株)製、コロネートL)、キシリレンジイソシアネート化合物(三井化学(株)製、タケネートD−110N)等が挙げられる。
Examples of the isocyanate compound include tolylene diisocyanate, xylylene diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate and the like.
Examples of epoxy compounds include ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, propylene glycol diglycidyl ether, polypropylene glycol diglycidyl ether, glycerin diglycidyl ether, neopentyl glycol diglycidyl ether, 1,6-hexanediol di Glycidyl ether, tetraglycidyl xylene diamine, 1,3-bis (N, N-diglycidylaminomethyl) cyclohexane, trimethylolpropane polyglycidyl ether, diglycerol polyglycidyl ether, polyglycerol polyglycidyl ether, sorbitol polyglycidyl ether, etc. It can be mentioned.
A commercial item can be used as a crosslinking agent. Examples of commercially available products include tolylene diisocyanate compounds (Coronate L, manufactured by Nippon Polyurethane Industry Co., Ltd.), xylylene diisocyanate compounds (manufactured by Mitsui Chemicals, Inc., Takenate D-110N), and the like.
粘着剤組成物中の架橋剤の含有量は、所望とする粘着性等に応じて適宜選択されるが、架橋性アクリル重合体100質量部に対し、0.01〜5質量部が好ましく、0.1〜3質量部がより好ましい。架橋剤の含有量が上記下限値以上であると半硬化状態での剪断貯蔵弾性率G’が所望の範囲に調整できるため加工性に優れ、上記上限値以下であると初期の基材密着性が優れるため、後硬化後に手でこすっても剥がれず、加工性に優れる。
架橋剤としては1種類を単独で用いても2種類以上を併用してもよく、2種類以上を併用する場合は、合計質量が上記範囲内であることが好ましい。
The content of the crosslinking agent in the pressure-sensitive adhesive composition is appropriately selected according to the desired adhesiveness and the like, but is preferably 0.01 to 5 parts by mass with respect to 100 parts by mass of the crosslinkable acrylic polymer. .1 to 3 parts by mass is more preferable. When the content of the crosslinking agent is at least the above lower limit, the shear storage modulus G 'in the semi-cured state can be adjusted to the desired range, so the processability is excellent, and the initial adhesion to the substrate is at the above upper limit It does not peel off even after rubbing by hand after post curing, and is excellent in processability.
As the crosslinking agent, one type may be used alone, or two or more types may be used in combination. When two or more types are used in combination, the total mass is preferably within the above range.
(多官能単量体)
本発明では、粘着剤組成物が、分子内に反応性二重結合を2つ以上有する多官能単量体を含有する。
(Multifunctional monomer)
In the present invention, the pressure-sensitive adhesive composition contains a polyfunctional monomer having two or more reactive double bonds in the molecule.
多官能単量体としては、例えば、ジ(メタ)アクリル酸エチレングリコール、ジ(メタ)アクリル酸トリエチレングリコール、ジ(メタ)アクリル酸1,3−ブチレングリコール、ジ(メタ)アクリル酸1,4−ブチレングリコール、ジ(メタ)アクリル酸1,9−ノナンジオール、ジアクリル酸1,6−ヘキサンジオール、ジ(メタ)アクリル酸ポリブチレングリコール、ジ(メタ)アクリル酸ネオペンチルグリコール、ジ(メタ)アクリル酸テトラエチレングリコール、ジ(メタ)アクリル酸トリプロピレングリコール、ジ(メタ)アクリル酸ポリプロピレングリコール、ビスフェノールAジグリシジルエーテルのジアクレート、トリ(メタ)アクリル酸トリメチロールプロパン、トリ(メタ)アクリル酸ペンタエリスリトール、テトラ(メタ)アクリル酸ペンタエリスリトール等の多価アルコールの(メタ)アクリル酸エステル類、メタクリル酸ビニル等が挙げられる。 As polyfunctional monomers, for example, ethylene glycol di (meth) acrylate, triethylene glycol di (meth) acrylate, 1,3-butylene glycol di (meth) acrylate, di (meth) acrylic acid 1, 4-butylene glycol, di (meth) acrylic acid 1,9-nonanediol, diacrylic acid 1,6-hexanediol, di (meth) acrylic acid polybutylene glycol, di (meth) acrylic acid neopentyl glycol, di (meth) acrylic acid ) Tetraethylene glycol acrylate, tripropylene glycol di (meth) acrylate, polypropylene glycol di (meth) acrylate, diacrylate of bisphenol A diglycidyl ether, trimethylolpropane tri (meth) acrylate, tri (meth) acrylic acid Pentaerythritol, tetra Meth) polyhydric alcohol (meth) acrylic acid esters such as acrylic acid pentaerythritol, and vinyl methacrylate.
多官能単量体は反応性二重結合を2つ以上有するものであり、中でも、多官能単量体は反応性二重結合を2つ以上5つ未満有するものであることが好ましく、2つ以上4つ未満有するものであることがより好ましい。 The polyfunctional monomer is one having two or more reactive double bonds, and among them, the polyfunctional monomer is preferably one having two or more and less than five reactive double bonds, and two It is more preferable to have more than four.
多官能単量体として、市販品を使用できる。市販品の例としては、東亞合成社製、三官能モノマーM−310(トリメチロールプロパンPO変性トリアクリレート)、東亞合成社製、二官能モノマーM−211B(ビスフェノールA EO変性ジアクリレート等が挙げられる。 A commercial item can be used as a polyfunctional monomer. Examples of commercially available products include Trifunctional Monomer M-310 (trimethylolpropane PO modified triacrylate) manufactured by Toagosei Co., Ltd., and Bifunctional Monomer M-211B (bisphenol A EO modified diacrylate etc.) manufactured by Toagosei Co., Ltd. .
本発明では、粘着剤組成物が上記多官能単量体を架橋性アクリル重合体100質量部に対して5〜35質量部含有することが好ましく、10〜35質量部含有することがより好ましく、15〜35質量部含有することが特に好ましい。上記多官能単量体は1種類を単独で用いても2種類以上を併用してもよく、2種類以上を併用する場合は、合計質量が上記範囲内であることが好ましい。 In the present invention, the pressure-sensitive adhesive composition preferably contains 5 to 35 parts by mass, more preferably 10 to 35 parts by mass, of the polyfunctional monomer based on 100 parts by mass of the crosslinkable acrylic polymer. It is particularly preferable to contain 15 to 35 parts by mass. The above polyfunctional monomers may be used alone or in combination of two or more. When two or more are used in combination, the total mass is preferably within the above range.
(単官能単量体)
本発明では、粘着剤組成物が、分子内に反応性二重結合を1つ有する単官能単量体を含有する。すなわち、本発明の粘着剤組成物は、単量体として、分子内に反応性二重結合を2つ以上有する上記多官能単量体と、分子内に反応性二重結合を1つ有する単官能単量体の両方を含有する。これにより本発明の粘着剤組成物から形成される粘着剤層は上述した物性群(1)を満たし、後硬化後の粘着剤層は優れた加工性を有する。
(Monofunctional monomer)
In the present invention, the pressure-sensitive adhesive composition contains a monofunctional monomer having one reactive double bond in the molecule. That is, the pressure-sensitive adhesive composition of the present invention comprises, as a monomer, the above-described polyfunctional monomer having two or more reactive double bonds in the molecule, and a single monomer having one reactive double bond in the molecule. It contains both functional monomers. Thereby, the adhesive layer formed from the adhesive composition of this invention satisfy | fills the physical-property group (1) mentioned above, and the adhesive layer after post-curing has the outstanding processability.
該単官能単量体を重合した場合のホモポリマーのガラス転移温度(Tg)は50℃以上200℃未満である。該単官能単量体を重合した場合のホモポリマーのガラス転移温度(Tg)は50℃より高いことが好ましく、55℃以上であることがより好ましく、60℃以上であることがさらに好ましい。また、単官能単量体を重合した場合のホモポリマーのガラス転移温度(Tg)は180℃以下であることが好ましく、150℃以下であることがより好ましい。 The glass transition temperature (Tg) of the homopolymer when the monofunctional monomer is polymerized is 50 ° C. or more and less than 200 ° C. The glass transition temperature (Tg) of the homopolymer when the monofunctional monomer is polymerized is preferably higher than 50 ° C., more preferably 55 ° C. or higher, and still more preferably 60 ° C. or higher. In addition, the glass transition temperature (Tg) of the homopolymer when a monofunctional monomer is polymerized is preferably 180 ° C. or less, and more preferably 150 ° C. or less.
単官能単量体は、(メタ)アクリル酸エステルであることが好ましい。(メタ)アクリル酸エステルとしては、例えば、イソボルニルアクリレート、メチルメタクリレート、エチルメタクリレート、ブチルメタクリレート、ベンジルメタクリレートなどを挙げることができる。中でも、単官能単量体はイソボルニルアクリレートであることが好ましい。
単官能単量体として、市販品を使用できる。市販品の例としては、大阪有機化学工業社製、IBXA等が挙げられる。
The monofunctional monomer is preferably a (meth) acrylic acid ester. Examples of (meth) acrylic acid esters include isobornyl acrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate, benzyl methacrylate and the like. Among them, the monofunctional monomer is preferably isobornyl acrylate.
A commercial item can be used as a monofunctional monomer. As an example of a commercial item, Osaka Organic Chemical Industry Ltd. make, IBXA etc. are mentioned.
本発明では、粘着剤組成物の架橋性アクリル重合体100質量部に対する単官能単量体の含有量は5〜35質量部であることが好ましく、5〜20質量部であることがより好ましい。 In the present invention, the content of the monofunctional monomer with respect to 100 parts by mass of the crosslinkable acrylic polymer of the pressure-sensitive adhesive composition is preferably 5 to 35 parts by mass, and more preferably 5 to 20 parts by mass.
(重合開始剤)
本発明では、粘着剤組成物が重合開始剤を含有する。
重合開始剤は、活性エネルギー線照射により多官能単量体および/または単官能単量体の重合を開始させるものであることが好ましく、活性エネルギー線照射により多官能単量体と単官能単量体の重合を開始させるものであることがより好ましい。重合開始剤としては、例えば、光重合開始剤など公知のものを用いることができる。
ここで、「活性エネルギー線」とは電磁波または荷電粒子線の中でエネルギー量子を有するものを意味し、紫外線、電子線、可視光線、X線、イオン線等が挙げられる。中でも、汎用性の点から、紫外線または電子線が好ましく、紫外線が特に好ましい。
(Polymerization initiator)
In the present invention, the pressure-sensitive adhesive composition contains a polymerization initiator.
The polymerization initiator is preferably one that initiates polymerization of a polyfunctional monomer and / or a monofunctional monomer by irradiation with an active energy ray, and the polyfunctional monomer and a monofunctional monomer amount by irradiation with an active energy ray. It is more preferable to initiate the polymerization of the body. As the polymerization initiator, for example, known ones such as a photopolymerization initiator can be used.
Here, "active energy ray" means one having an energy quantum among electromagnetic waves or charged particle beams, and examples include ultraviolet rays, electron rays, visible rays, X-rays, ion rays and the like. Among them, ultraviolet rays or electron beams are preferable, and ultraviolet rays are particularly preferable, from the viewpoint of versatility.
重合開始剤としては、例えばアセトフェノン系開始剤、ベンゾインエーテル系開始剤、ベンゾフェノン系開始剤、ヒドロキシアルキルフェノン系開始剤、チオキサントン系開始剤、アミン系開始剤、アシルフォスフィンオキシド系開始剤等が挙げられる。
アセトフェノン系開始剤として具体的には、ジエトキシアセトフェノン、ベンジルジメチルケタール等が挙げられる。
ベンゾインエーテル系開始剤として具体的には、ベンゾイン、ベンゾインメチルエーテル等が挙げられる。
ベンゾフェノン系開始剤として具体的には、ベンゾフェノン、o−ベンゾイル安息香酸メチル等が挙げられる。
ヒドロキシアルキルフェノン系開始剤として具体的には、1−ヒドロキシ−シクロヘキシル−フェニル−ケトン(BASFジャパン(株)製、IRGACURE184として市販)等が挙げられる。
チオキサントン系開始剤として具体的には、2−イソプロピルチオキサントン、2,4−ジメチルチオキサントン等が挙げられる。
アミン系開始剤として具体的には、トリエタノールアミン、4−ジメチル安息香酸エチル等が挙げられる。
アシルフォスフィンオキシド系開始剤として具体的には、フェニルビス(2,4,6−トリメチルベンゾイル)ホスフィンオキシド(BASFジャパン(株)製、IRGACURE819として市販)等が挙げられる。
Examples of the polymerization initiator include acetophenone initiators, benzoin ether initiators, benzophenone initiators, hydroxyalkylphenone initiators, thioxanthone initiators, amine initiators, and acylphosphine oxide initiators. Be
Specific examples of acetophenone initiators include diethoxyacetophenone, benzyl dimethyl ketal and the like.
Specific examples of the benzoin ether initiator include benzoin and benzoin methyl ether.
Specific examples of benzophenone initiators include benzophenone and methyl o-benzoylbenzoate.
Specific examples of the hydroxyalkyl phenone initiator include 1-hydroxy-cyclohexyl-phenyl-ketone (manufactured by BASF Japan Ltd., commercially available as IRGACURE 184) and the like.
Specific examples of the thioxanthone initiator include 2-isopropyl thioxanthone, 2,4-dimethyl thioxanthone and the like.
Specific examples of the amine initiator include triethanolamine and ethyl 4-dimethylbenzoate.
Specific examples of the acyl phosphine oxide initiator include phenyl bis (2,4,6-trimethyl benzoyl) phosphine oxide (manufactured by BASF Japan Ltd., commercially available as IRGACURE 819) and the like.
粘着剤組成物中の重合開始剤の含有量は、単量体の含有量や後硬化させるときの活性エネルギー線の照射量等に応じて適宜選択される。具体的には、単量体の全質量に対し、0.05〜10質量%であることが好ましく、0.1〜5.0質量%であることがより好ましい。上記下限値以上であれば、後硬化により所望の硬さに調整することができるため加工性が優れる。上記上限値以下であれば、後硬化後の分子量が小さくならず、加工性や耐アウトガス性に優れる。
重合開始剤としては1種類を単独で用いても2種類以上を併用してもよく、2種類以上を併用する場合は、合計質量が上記範囲内であることが好ましい。
The content of the polymerization initiator in the pressure-sensitive adhesive composition is appropriately selected according to the content of the monomer, the irradiation amount of the active energy ray at the time of post-curing, and the like. It is preferable that it is 0.05-10 mass% with respect to the total mass of a monomer, and, specifically, it is more preferable that it is 0.1-5.0 mass%. If it is more than the said lower limit, since it can adjust to desired hardness by post-hardening, processability is excellent. If it is below the said upper limit, the molecular weight after post-curing will not become small, and it is excellent in processability and outgassing resistance.
As the polymerization initiator, one type may be used alone, or two or more types may be used in combination. When two or more types are used in combination, the total mass is preferably within the above range.
(溶剤)
粘着剤組成物は、溶剤を含んでいてもよい。この場合、溶剤は、粘着剤組成物の塗工適性の向上のために用いられる。溶剤としては、例えば、ヘキサン、ヘプタン、オクタン、トルエン、キシレン、エチルベンゼン、シクロヘキサン、メチルシクロヘキサン等の炭化水素類;ジクロロメタン、トリクロロエタン、トリクロロエチレン、テトラクロロエチレン、ジクロロプロパン等のハロゲン化炭化水素類;メタノール、エタノール、プロパノール、イソプロピルアルコール、ブタノール、イソブチルアルコール、ジアセトンアルコール等のアルコール類;ジエチルエーテル、ジイソプロピルエーテル、ジオキサン、テトラヒドロフラン等のエーテル類;アセトン、メチルエチルケトン、メチルイソブチルケトン、イソホロン、シクロヘキサノン等のケトン類;酢酸メチル、酢酸エチル、酢酸ブチル、酢酸イソブチル、酢酸アミル、酪酸エチル等のエステル類;エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノメチルエーテルアセタート、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノメチルエーテルアセタート等のポリオール及びその誘導体が挙げられる。
(solvent)
The pressure-sensitive adhesive composition may contain a solvent. In this case, the solvent is used to improve the coating suitability of the pressure-sensitive adhesive composition. Examples of the solvent include hydrocarbons such as hexane, heptane, octane, toluene, xylene, ethylbenzene, cyclohexane and methylcyclohexane; halogenated hydrocarbons such as dichloromethane, trichloroethane, trichloroethylene, tetrachloroethylene and dichloropropane; methanol, ethanol, Alcohols such as propanol, isopropyl alcohol, butanol, isobutyl alcohol, diacetone alcohol; Ethers such as diethyl ether, diisopropyl ether, dioxane, tetrahydrofuran etc. Ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone, isophorone, cyclohexanone etc. Methyl acetate , Ethyl acetate, butyl acetate, isobutyl acetate, amyl acetate, esters such as ethyl butyrate; Chi glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, propylene glycol monoethyl ether, polyols and derivatives thereof such as propylene glycol monomethyl ether acetate.
粘着剤組成物中の溶剤の含有量は、特に限定されないが、架橋性アクリル重合体100質量部に対し、25〜500質量部が好ましく、30〜400質量部がより好ましい。
また、溶剤の含有量は、粘着剤組成物の全質量に対し、10〜90質量%であることが好ましく、20〜80質量%であることがより好ましい。溶剤は1種類を単独で使用してもよいし、2種類以上を併用してもよく、2種類以上を併用する場合は、合計質量が上記範囲内であることが好ましい。
Although content of the solvent in an adhesive composition is not specifically limited, 25-500 mass parts is preferable with respect to 100 mass parts of crosslinkable acrylic polymers, and 30-400 mass parts is more preferable.
Moreover, it is preferable that it is 10-90 mass% with respect to the total mass of an adhesive composition, and, as for content of a solvent, it is more preferable that it is 20-80 mass%. A solvent may be used individually by 1 type, and 2 or more types may be used together, and when using 2 or more types together, it is preferable that total mass is in the said range.
(可塑剤)
粘着剤組成物は本発明の効果を損なわない範囲で、可塑剤をさらに含んでもよい。粘着剤組成物が可塑剤を含むことにより、粘着シートは、被着体に形成される段差を埋めることができ、凹凸追従性が高められる。可塑剤は、無官能基アクリル重合体であることが好ましい。無官能基アクリル重合体は、アクリレート基以外の官能基を有しないアクリル単量体単位のみからなる重合体、又はアクリレート基以外の官能基を有しないアクリル単量体単位と官能基を有しない非アクリル単量体単位とからなる重合体である。無官能基アクリル重合体は架橋しないため、粘着性に影響を与えずに凹凸追従性を高めることができる。
アクリレート基以外の官能基を有しないアクリル単量体単位としては、例えば非架橋性(メタ)アクリル酸エステル単位(a1)と同様のものが挙げられる。
官能基を有しない非アクリル単量体単位としては、例えば酢酸ビニル、プロピオン酸ビニル、酪酸ビニル、カプロン酸ビニル、カプリル酸ビニル、カプリン酸ビニル、ラウリン酸ビニル、ミリスチン酸ビニル、パルミチン酸ビニル、ステアリン酸ビニル、シクロヘキサンカルボン酸ビニル、安息香酸ビニルのようなカルボン酸ビニルエステル類やスチレン等が挙げられる。
(Plasticizer)
The pressure-sensitive adhesive composition may further contain a plasticizer as long as the effects of the present invention are not impaired. When the pressure-sensitive adhesive composition contains a plasticizer, the pressure-sensitive adhesive sheet can fill the level difference formed on the adherend, and the unevenness followability can be enhanced. The plasticizer is preferably a nonfunctional acrylic polymer. The nonfunctional acrylic polymer is a polymer consisting only of an acrylic monomer unit having no functional group other than an acrylate group, or an acrylic monomer unit having no functional group other than an acrylate group and a nonfunctional group having no functional group. It is a polymer comprising an acrylic monomer unit. Since the non-functional acrylic polymer does not crosslink, it is possible to enhance the unevenness followability without affecting the adhesiveness.
As an acrylic monomer unit which does not have functional groups other than an acrylate group, the thing similar to a non-crosslinkable (meth) acrylic acid ester unit (a1) is mentioned, for example.
As a non-acrylic monomer unit having no functional group, for example, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl caproate, vinyl caprylate, vinyl caprylate, vinyl caprate, vinyl laurate, vinyl myristate, vinyl palmitate, stearin Examples thereof include vinyl acid esters of vinyl acid such as vinyl acid, vinyl cyclohexanecarboxylic acid and vinyl benzoate, and styrene.
(他の成分)
粘着剤組成物は、本発明の効果を損なわない範囲で、上記以外の他の成分を含有してもよい。他の成分としては、粘着剤用の添加剤として公知の成分を挙げることができる。例えば酸化防止剤、金属腐食防止剤、粘着付与剤、シランカップリング剤、紫外線吸収剤、ヒンダードアミン系化合物等の光安定剤等の中から必要に応じて選択できる。
酸化防止剤としては、フェノール系酸化防止剤、アミン系酸化防止剤、ラクトン系酸化防止剤、リン系酸化防止剤、イオウ系酸化防止剤等が挙げられる。これら酸化防止剤は1種類を単独で使用してもよいし、2種類以上を併用してもよい。
金属腐食防止剤としては、粘着剤の相溶性や効果の高さから、ベンゾリアゾール系樹脂を好ましい例として挙げることができる。
粘着付与剤として、例えば、ロジン系樹脂、テルペン系樹脂、テルペンフェノール系樹脂、クマロンインデン系樹脂、スチレン系樹脂、キシレン系樹脂、フェノール系樹脂、石油樹脂などが挙げられる。
シランカップリング剤としては、例えば、メルカプトアルコキシシラン化合物(例えば、メルカプト基置換アルコキシオリゴマー等)などが挙げられる。
紫外線吸収剤としては、例えば、ベンゾトリアゾール系化合物、ベンゾフェノン系化合物などが挙げられる。ただし、後硬化時の活性エネルギー線に紫外線を用いる場合は、重合反応を阻害しない範囲で添加することが好ましい。
(Other ingredients)
The pressure-sensitive adhesive composition may contain other components other than the above as long as the effects of the present invention are not impaired. As other components, components known as additives for pressure-sensitive adhesives can be mentioned. For example, it can be selected as required from light stabilizers such as antioxidants, metal corrosion inhibitors, tackifiers, silane coupling agents, ultraviolet absorbers, hindered amine compounds and the like.
Examples of the antioxidant include phenol based antioxidants, amine based antioxidants, lactone based antioxidants, phosphorus based antioxidants, sulfur based antioxidants and the like. One of these antioxidants may be used alone, or two or more thereof may be used in combination.
As a metal corrosion inhibitor, benzotriazole resin can be mentioned as a preferable example from the compatibility and the effect of an adhesive.
Examples of tackifiers include rosin resins, terpene resins, terpene phenol resins, coumarone indene resins, styrene resins, xylene resins, phenol resins, petroleum resins and the like.
As a silane coupling agent, a mercapto alkoxysilane compound (for example, a mercapto group substituted alkoxy oligomer etc.) etc. are mentioned, for example.
Examples of the UV absorber include benzotriazole compounds and benzophenone compounds. However, when using an ultraviolet-ray for the active energy ray at the time of post-hardening, it is preferable to add in the range which does not inhibit a polymerization reaction.
<粘着シートの製造方法>
粘着シートの製造方法は、特に限定されない。
粘着シートの製造方法は、剥離シート上に粘着剤組成物を塗工して塗膜を形成する工程と、この塗膜を加熱により半硬化状態の硬化物とする工程を含むことが好ましい。
塗膜の加熱により、架橋性アクリル重合体および架橋剤の反応が進行して半硬化状態の硬化物(粘着剤層)が形成される。つまり、加熱の際、塗膜中では重合開始剤による単量体の重合反応が進行しないか、進行してもわずかであるため、粘着剤層中には、粘着剤組成物に含まれる単量体および重合開始剤の少なくとも一部が未反応の状態で含まれている。本発明の粘着シートは、後硬化性を有し、活性エネルギー線硬化性を有していることが好ましい。
粘着剤組成物を半硬化状態とするためには、塗工後溶剤を除去した後に、一定温度で一定期間粘着シートを静置するエージング処理を施すことが好ましい。エージング処理は例えば、23℃で7日間静置して行うことができる。
<Production method of adhesive sheet>
The method for producing the pressure-sensitive adhesive sheet is not particularly limited.
The method for producing the pressure-sensitive adhesive sheet preferably includes the steps of applying a pressure-sensitive adhesive composition on a release sheet to form a coating, and forming the coating as a cured product in a semi-cured state by heating.
By heating the coating, the reaction between the crosslinkable acrylic polymer and the crosslinking agent proceeds to form a cured product (pressure-sensitive adhesive layer) in a semi-cured state. That is, when heating, the polymerization reaction of the monomer by the polymerization initiator does not proceed in the coating film, or it proceeds only slightly, so in the pressure-sensitive adhesive layer, a single amount contained in the pressure-sensitive adhesive composition The body and at least a part of the polymerization initiator are contained in an unreacted state. The pressure-sensitive adhesive sheet of the present invention preferably has post-curing properties and active energy ray curing properties.
In order to bring the pressure-sensitive adhesive composition into a semi-cured state, it is preferable to perform an aging treatment in which the pressure-sensitive adhesive sheet is allowed to stand at a constant temperature for a fixed period after removing the solvent after coating. The aging treatment can be carried out, for example, by leaving at 23 ° C. for 7 days.
本発明の粘着シートの粘着剤層は、基材等の被着体に貼合した後に活性エネルギー線を照射することで後硬化できることが好ましい。本発明の粘着シートは、2段階硬化の粘着シートであり、貼合前は熱のみによって半硬化された粘着剤層を有し、貼合後に活性エネルギー線により粘着剤層は後硬化できることが好ましい。 It is preferable that the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet of the present invention can be post-cured by irradiation with an active energy ray after being bonded to an adherend such as a substrate. The pressure-sensitive adhesive sheet of the present invention is a two-stage-cured pressure-sensitive adhesive sheet, and preferably has a pressure-sensitive adhesive layer semi-cured only by heat before bonding, and can be post-cured by active energy rays after bonding. .
粘着剤組成物の塗工は、公知の塗工装置を用いて実施できる。塗工装置としては、例えば、ブレードコーター、エアナイフコーター、ロールコーター、バーコーター、グラビアコーター、マイクログラビアコーター、ロッドブレードコーター、リップコーター、ダイコーター、カーテンコーター等が挙げられる。 Coating of the pressure-sensitive adhesive composition can be carried out using a known coating apparatus. As a coating apparatus, a blade coater, an air knife coater, a roll coater, a bar coater, a gravure coater, a microgravure coater, a rod blade coater, a lip coater, a die coater, a curtain coater etc. are mentioned, for example.
粘着剤組成物を塗工して形成される塗膜の加熱には、加熱炉、赤外線ランプ等の公知の加熱装置を用いることができる。 For heating the coating film formed by applying the pressure-sensitive adhesive composition, a known heating device such as a heating furnace or an infrared lamp can be used.
(粘着シートの使用方法)
本発明の粘着シートの使用方法においては、粘着シートの粘着剤層を被着体表面に接触させることが好ましい。
本発明の粘着シートの使用方法は、粘着シートの粘着剤層が半硬化状態のときに被着体と貼合し、活性エネルギー線を照射して粘着剤層を後硬化させることが好ましい。
(How to use the adhesive sheet)
In the usage method of the adhesive sheet of this invention, it is preferable to make the adhesive layer of an adhesive sheet contact the to-be-adhered body surface.
In the method of using the pressure-sensitive adhesive sheet of the present invention, it is preferable that the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet be bonded to an adherend when the pressure-sensitive adhesive layer is in a semi-cured state, and the pressure-sensitive adhesive layer be post-cured by irradiating active energy rays.
<粘着シートの用途>
本発明の粘着シートは、耐久性を必要とする光学部材、特に形状が複雑で積層体になってからの打抜き加工が必要な用途に好ましく用いられる。
本発明の粘着シートは、基材等の被着体に貼合し、後硬化させた後、高湿熱環境下に曝した場合であっても、気泡の発生を抑制できることが好ましい。本発明の粘着シートは、基材に貼合する用途に用いられる粘着シートであることが好ましく、ポリカーボネート基材に貼合する用途に用いられる粘着シートであることがより好ましい。ポリカーボネート基材としては、例えば、帝人化成(株)製のPC−1151等を挙げることができる。
<Application of adhesive sheet>
The pressure-sensitive adhesive sheet of the present invention is preferably used for an optical member which requires durability, in particular, in applications where the shape is complicated and it is necessary to perform punching after being formed into a laminate.
The pressure-sensitive adhesive sheet of the present invention is preferably adhered to an adherend such as a base material and post-cured, and then, even when exposed to a high humidity and heat environment, generation of air bubbles can be suppressed. The pressure-sensitive adhesive sheet of the present invention is preferably a pressure-sensitive adhesive sheet used for application to a substrate, and more preferably an adhesive sheet used for application to a polycarbonate substrate. Examples of polycarbonate substrates include PC-1151 manufactured by Teijin Chemicals Ltd., and the like.
本発明の粘着シートは、基材に直接貼合する用途に用いられる粘着シートであることが好ましいが、基材に間接的に貼合する用途で用いられてもよい。例えば、ポリカーボネート基材を含む多層基材に貼合されてもよい。このような多層基材は、ポリカーボネート層とハードコート層を有する基材であることが好ましい。ハードコート層の組成はアクリル系、ウレタン系、シリコーン系、メラミン系、エポキシ系から選択されることが好ましく、アクリル系、シリコーン系がより好ましい。ハードコート層の組成は加工性と硬度の点からアクリル系がより好ましい。なお、本明細書においては、ポリカーボネート基材を含む多層基材についてもポリカーボネート基材と呼ぶ。
ポリカーボネート基材を含む多層基材としては、例えば、三菱ガス化学(株)製のMR−58やIMR05等を用いることができる。ここで、MR−58の構成は、HC(ハードコート)/PMMA(ポリメチルメタクリレート)/PC(ポリカーボネート)/HC(ハードコート)である。MR−58の全体の厚みは0.3mm〜1.2mmであり、ハードコート層の1層の厚みは、0.0005mm〜0.02mmであることが好ましい。また、IMR05の構成は、HC(ハードコート)/PC(ポリカーボネート)である。
The pressure-sensitive adhesive sheet of the present invention is preferably a pressure-sensitive adhesive sheet used for application to be directly bonded to a substrate, but may be used for application to be indirectly attached to a substrate. For example, it may be bonded to a multilayer substrate comprising a polycarbonate substrate. Such a multilayer substrate is preferably a substrate having a polycarbonate layer and a hard coat layer. The composition of the hard coat layer is preferably selected from acrylics, urethanes, silicones, melamines and epoxys, with acrylics and silicones being more preferred. The composition of the hard coat layer is more preferably acrylic in view of processability and hardness. In the present specification, a multilayer substrate including a polycarbonate substrate is also referred to as a polycarbonate substrate.
As a multilayer base material containing a polycarbonate base material, MR-58, IMR05 etc. made from Mitsubishi Gas Chemical Co., Ltd. can be used, for example. Here, the configuration of MR-58 is HC (hard coat) / PMMA (polymethyl methacrylate) / PC (polycarbonate) / HC (hard coat). The total thickness of the MR-58 is preferably 0.3 mm to 1.2 mm, and the thickness of one hard coat layer is preferably 0.0005 mm to 0.02 mm. The configuration of IMR 05 is HC (hard coat) / PC (polycarbonate).
また、本発明の粘着シートは、偏光板などの光学部材に貼合し、後硬化させた後、高湿熱環境下に曝した場合であっても、気泡、剥がれの発生を抑制することができる。ここで、偏光板とは、偏光子と偏光子保護フィルムを含むものであり、本発明の粘着シートは偏光子保護フィルムに貼合されることが好ましい。偏光子保護フィルムとしては、シクロオレフィン系樹脂フィルム、トリアセチルセルロース、ジアセチルセルロースなどの酢酸セルロース系樹脂フィルム、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンテレフタレートなどのポリエステル系樹脂フィルム、ポリカーボネート系樹脂フィルム、アクリル系樹脂フィルム、ポリプロピレン系樹脂フィルムなどが挙げられる。特に、偏光子保護フィルムが酢酸セルロース系樹脂フィルムである場合、本発明の粘着シートを用いることによって、気泡発生抑制効果が発揮される。
本発明では、粘着シートの被着体の気泡の発生を抑制することができるため、粘着シートを表示装置等に組み込んだ場合、視認性の悪化を防ぐことができる。
Further, the pressure-sensitive adhesive sheet of the present invention can be inhibited from the generation of air bubbles and peeling even when exposed to a high humidity and heat environment after being attached to an optical member such as a polarizing plate and post curing. . Here, it is preferable that a polarizing plate contains a polarizer and a polarizer protective film, and the adhesive sheet of this invention is bonded by a polarizer protective film. Examples of polarizer protective films include cycloolefin resin films, cellulose acetate resin films such as triacetyl cellulose and diacetyl cellulose, polyester resins such as polyethylene terephthalate, polyethylene naphthalate and polybutylene terephthalate, polycarbonate resin films, and acrylic Examples of the resin film include polypropylene resin films and the like. In particular, when the polarizer protective film is a cellulose acetate-based resin film, the use of the pressure-sensitive adhesive sheet of the present invention exerts a bubble generation suppressing effect.
In the present invention, since the generation of air bubbles in the adherend of the pressure-sensitive adhesive sheet can be suppressed, when the pressure-sensitive adhesive sheet is incorporated in a display device or the like, the deterioration of visibility can be prevented.
半硬化状態の粘着シートを被着体に貼合することで、凹凸に追従させられることが好ましい。また、活性エネルギー線の照射により粘着剤層を後硬化させることで粘着力及び保持力を高めることができる。 It is preferable to be able to follow unevenness by bonding a semi-cured pressure-sensitive adhesive sheet to an adherend. Further, the adhesive strength and the holding power can be enhanced by post-curing the pressure-sensitive adhesive layer by irradiation of active energy rays.
[積層体]
本発明の積層体は、本発明の粘着シートの粘着剤層に活性エネルギー線を照射して後硬化させた後硬化後の粘着剤層と、被着体とを有する。
積層体に含まれる粘着シートは、2つの被着体(例えば、基材と光学部材)を半硬化状態の粘着シートで貼合した状態で活性エネルギー線を照射することで、後硬化したものであることが好ましい。
[Laminate]
The laminate of the present invention has a pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet of the present invention after irradiation with active energy rays for post-curing, and a pressure-sensitive adhesive layer after curing and an adherend.
The pressure-sensitive adhesive sheet contained in the laminate is post-cured by irradiation with an active energy ray in a state where two adherends (for example, a base and an optical member) are bonded with a semi-cured pressure-sensitive adhesive sheet. Is preferred.
図2は、本発明の積層体の一例の断面を表す概略図である。図2は、本発明の粘着シート21を基材22と光学部材24に貼合した積層体20の構成の一例を表す断面図である。図2に示されているように、本発明の粘着シート21は、基材22に貼合するために用いられることが好ましく、基材22と他の光学部材24の貼合に用いられることが好ましい。なお、本発明の粘着シート21は、偏光板との貼合に用いられてもよい。
FIG. 2 is a schematic view showing a cross section of an example of the laminate of the present invention. FIG. 2 is a cross-sectional view showing an example of the configuration of a laminate 20 in which the pressure-sensitive adhesive sheet 21 of the present invention is bonded to a
積層体に含まれる光学部材としては、タッチパネルや画像表示装置等の光学製品における各構成部材を挙げることができる。タッチパネルの構成部材としては、例えば透明樹脂フィルムにITO膜が設けられたITOフィルム、ガラス板の表面にITO膜が設けられたITOガラス、透明樹脂フィルムに導電性ポリマーをコーティングした透明導電性フィルム、ハードコートフィルム、耐指紋性フィルムなどが挙げられる。画像表示装置の構成部材としては、例えば液晶表示装置に用いられる反射防止フィルム、配向フィルム、偏光フィルム、位相差フィルム、輝度向上フィルムなどが挙げられる。
これらの部材に用いられる材料としては、ガラス、ポリカーボネート,ポリエチレンテレフタレート、ポリメチルメタクリレート、ポリエチレンナフタレート、シクロオレフィンポリマー,トリアセチルセルロース,ポリイミド、セルロースアシレートなどが挙げられる。
As an optical member contained in a laminated body, each structural member in optical products, such as a touch panel and an image display device, can be mentioned. For example, an ITO film in which an ITO film is provided on a transparent resin film, an ITO glass in which an ITO film is provided on the surface of a glass plate, a transparent conductive film obtained by coating a conductive polymer on a transparent resin film Hard coat films, fingerprint resistant films and the like can be mentioned. As a structural member of an image display apparatus, the antireflection film used for a liquid crystal display device, an orientation film, a polarizing film, retardation film, a brightness improvement film etc. are mentioned, for example.
Examples of the material used for these members include glass, polycarbonate, polyethylene terephthalate, polymethyl methacrylate, polyethylene naphthalate, cycloolefin polymer, triacetyl cellulose, polyimide, and cellulose acylate.
本発明の粘着シートが両面粘着シートである場合は、2つの被着体の貼合に用いることができる。この場合、本発明の粘着シートは、タッチパネルの内部における透明光学用フィルム同士の貼合、透明光学用フィルムとガラスとの貼合、タッチパネルの透明光学用フィルムと液晶パネルとの貼合、カバーガラスと透明光学用フィルムとの貼合、カバーガラスと透明光学用フィルムとの貼合などに用いられ、いずれかの部材がポリカーボネート基材であることが好ましい。透明光学用フィルムは、ポリエチレンテレフタレートフィルムやアクリルフィルム、ポリカーボネートフィルム、トリアセチルセルロースフィルム、シクロオレフィンポリマーフィルムなど光学分野に用いられる一般的なフィルムを用いることが出来る。また、透明光学用フィルムやポリカーボネート基材にはハードコート層が設けられていてもよい。 When the pressure-sensitive adhesive sheet of the present invention is a double-sided pressure-sensitive adhesive sheet, it can be used for bonding two adherends. In this case, the pressure-sensitive adhesive sheet of the present invention is formed by bonding transparent optical films to each other in the inside of a touch panel, bonding a transparent optical film to glass, bonding a transparent optical film on a touch panel to liquid crystal panel, and cover glass It is preferable that it is used for bonding of the film for transparent optics, and bonding of a cover glass and the film for transparent optics, and any one member is a polycarbonate base material. The transparent optical film may be a general film used in the optical field, such as polyethylene terephthalate film, acrylic film, polycarbonate film, triacetyl cellulose film, cycloolefin polymer film, and the like. In addition, a hard coat layer may be provided on the transparent optical film or the polycarbonate substrate.
図3は、本発明の積層体の他の一例の断面を表す概略図である。図3に示されているように、被着体は段差部(27a、27b、27c、27d)を有していてもよい。図3では、基材は段差部(27a、27b)を有しており、光学部材が段差部(27c、27d)を有している。なお、段差部(27a、27b、27c、27d)の厚みは、通常5〜60μmである。このように本発明の粘着シート21は、段差部を有する部材にも貼合することができ、段差部から生じる凹凸に追従することができる。 FIG. 3 is a schematic view showing a cross section of another example of the laminate of the present invention. As shown in FIG. 3, the adherend may have stepped portions (27a, 27b, 27c, 27d). In FIG. 3, the base has stepped portions (27a, 27b), and the optical member has stepped portions (27c, 27d). The thickness of the step portion (27a, 27b, 27c, 27d) is usually 5 to 60 μm. Thus, the adhesive sheet 21 of this invention can be bonded also to the member which has a level | step-difference part, and can follow the unevenness | corrugation which arises from a level | step-difference part.
[積層体の製造方法]
本発明の積層体の製造方法は、本発明の粘着シートの粘着剤層を被着体に対して半硬化状態で貼合した後、活性エネルギー線を照射して粘着剤層を後硬化させる工程を含む。
本発明では、半硬化状態の粘着シートを被着体表面に接触させ、その状態で活性エネルギー線を照射して粘着剤層を後硬化させる工程を含むことが好ましい。
被着体は、基材および光学部材であることがより好ましく、ポリカーボネート基材、偏光板、透明フィルム、透明樹脂またはガラスであることが特に好ましい。本発明では、被着体が、透明フィルム、透明樹脂またはガラスであることがより特に好ましい。
[Method of manufacturing laminate]
The process for producing a laminate of the present invention comprises the steps of bonding the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet of the present invention to an adherend in a semi-cured state, and then irradiating the active energy ray to post-cure the pressure-sensitive adhesive layer. including.
In the present invention, it is preferable to include a step of bringing a pressure-sensitive adhesive sheet in a semi-cured state into contact with the surface of an adherend and irradiating the surface with an active energy ray to post-cure the pressure-sensitive adhesive layer.
The adherend is more preferably a substrate and an optical member, and particularly preferably a polycarbonate substrate, a polarizing plate, a transparent film, a transparent resin or glass. In the present invention, the adherend is more particularly preferably a transparent film, a transparent resin or glass.
粘着シートを基材と光学部材に貼合する場合、活性エネルギー線は基材側からでも光学部材側からでも照射できるが、基材側から照射することが好ましい。
活性エネルギー線を照射する前は、粘着シートの粘着剤層は半硬化状態であることから、被着体が段差部を有していても、粘着剤層はその凹凸に追従することができる。このように、粘着シートを貼合し、凹凸に追従させた後、粘着剤層を活性エネルギー線で後硬化させることで、粘着剤層の凝集力が高まり、被着体への粘着性が向上する。また、後硬化した粘着剤層は基材が変形したり、歪んだりすることを防止できる。
When bonding an adhesive sheet to a base material and an optical member, although an active energy ray can be irradiated also from a base material side or an optical member side, it is preferable to irradiate from a base material side.
Before the active energy ray is irradiated, the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet is in a semi-cured state. Therefore, even if the adherend has a stepped portion, the pressure-sensitive adhesive layer can follow the unevenness. As described above, after bonding the pressure-sensitive adhesive sheet and following the unevenness, by post-curing the pressure-sensitive adhesive layer with active energy rays, the cohesive force of the pressure-sensitive adhesive layer is increased, and the adhesion to the adherend is improved. Do. In addition, the post-cured pressure-sensitive adhesive layer can prevent the base from being deformed or distorted.
活性エネルギー線としては、紫外線、電子線、可視光線、X線、イオン線等が挙げられ、粘着剤層に含まれる重合開始剤に応じて適宜選択できる。中でも、汎用性の点から、紫外線または電子線が好ましく、紫外線が特に好ましい。
紫外線の光源としては、例えば、高圧水銀灯、低圧水銀灯、超高圧水銀灯、メタルハライドランプ、カーボンアーク、キセノンアーク、無電極紫外線ランプ等を使用できる。
電子線としては、例えば、コックロフトワルト型、バンデクラフ型、共振変圧型、絶縁コア変圧器型、直線型、ダイナミトロン型、高周波型等の各種類の電子線加速器から放出される電子線を使用できる。
紫外線の照射出力は、積算光量が100〜10000mJ/cm2となるようにすることが好ましく、500〜5000mJ/cm2となるようにすることがより好ましい。
As an active energy ray, an ultraviolet ray, an electron beam, a visible ray, an X ray, an ion beam etc. are mentioned, According to the polymerization initiator contained in an adhesive layer, it can select suitably. Among them, ultraviolet rays or electron beams are preferable, and ultraviolet rays are particularly preferable, from the viewpoint of versatility.
As a light source of ultraviolet light, for example, a high pressure mercury lamp, low pressure mercury lamp, ultra high pressure mercury lamp, metal halide lamp, carbon arc, xenon arc, electrodeless ultraviolet lamp and the like can be used.
As the electron beam, for example, electron beams emitted from various types of electron beam accelerators such as Cockloft Wald type, Bandeklav type, resonant transformer type, insulating core transformer type, linear type, dynamitron type, high frequency type and the like are used it can.
Radiation output of the UV, integrated light quantity is preferably to be a 100~10000mJ / cm 2, and more preferably made to be 500~5000mJ / cm 2.
以下に実施例と比較例を挙げて本発明の特徴をさらに具体的に説明する。以下の実施例に示す材料、使用量、割合、処理内容、処理手順等は、本発明の趣旨を逸脱しない限り適宜変更することができる。したがって、本発明の範囲は以下に示す具体例により限定的に解釈されるべきではない。 The features of the present invention will be more specifically described below with reference to examples and comparative examples. The materials, amounts used, proportions, treatment contents, treatment procedures, etc. shown in the following examples can be appropriately changed without departing from the spirit of the present invention. Therefore, the scope of the present invention should not be construed as limited by the specific examples shown below.
[製造例1]
架橋性アクリル重合体を、酢酸エチル中での溶液重合により作製した。2−ヒドロキシエチルアクリレートモノマー、n−ブチルアクリレートモノマー、及びジメチルアクリルアミドを質量比で0.5:10:2.5となるように配合し、ラジカル重合開始剤としてAIBN(アゾビスイソブチロニトリル)を溶液へ溶解した。溶液を60℃に加熱してランダム共重合させ、架橋性アクリル重合体Aを得た。この架橋性アクリル重合体の35質量%溶液の23℃における溶液粘度は5500mPa・sであった。
Production Example 1
Crosslinkable acrylic polymers were prepared by solution polymerization in ethyl acetate. Blending 2-hydroxyethyl acrylate monomer, n-butyl acrylate monomer, and dimethyl acrylamide in a mass ratio of 0.5: 10: 2.5, and using AIBN (azobisisobutyronitrile) as a radical polymerization initiator Was dissolved in the solution. The solution was heated to 60 ° C. for random copolymerization to obtain a crosslinkable acrylic polymer A. The solution viscosity at 23 ° C. of a 35% by mass solution of this crosslinkable acrylic polymer was 5500 mPa · s.
[実施例1]
架橋性アクリル重合体A100質量部に対して、架橋剤としてキシリレンジイソシアネート化合物(三井化学(株)製、タケネートD−110N)を0.2質量部、分子内に反応性二重結合を2つ以上有する多官能単量体として、トリメチロールプロパンPO変性トリアクリレート(東亞合成(株)製、M−310)を30質量部、単官能単量体としてイソボルニルアクリレート(大阪有機化学工業社製、IBXA、Tg=97℃)を6質量部、重合開始剤として1−ヒドロキシ−シクロヘキシル−フェニル−ケトン(BASFジャパン(株)製、IRGACURE184)を1.12質量部添加し、固形分濃度が30質量%となるように溶剤として酢酸エチルを添加して粘着剤組成物を得た。
Example 1
To 100 parts by mass of the crosslinkable acrylic polymer A, 0.2 parts by mass of xylylene diisocyanate compound (manufactured by Mitsui Chemicals, Inc., Takenate D-110N) as a crosslinking agent, and two reactive double bonds in the molecule 30 parts by mass of trimethylolpropane PO modified triacrylate (manufactured by Toagosei Co., Ltd., M-310) as a polyfunctional monomer possessed above, and isobornyl acrylate (manufactured by Osaka Organic Chemical Industry Co., Ltd.) as a monofunctional monomer 6 parts by mass, IBXA, Tg = 97 ° C., 1.12 parts by mass of 1-hydroxy-cyclohexyl-phenyl-ketone (manufactured by BASF Japan Ltd., IRGACURE 184) as a polymerization initiator, and the solid content concentration is 30 Ethyl acetate was added as a solvent so as to be% by mass to obtain a pressure-sensitive adhesive composition.
上記粘着剤組成物を、第1の剥離シート(重セパレータフィルム、帝人デュポンフィルム(株)製、離型処理されたポリエチレンテレフタレートフィルム)上へ塗工した。塗工は、ヨシミツ精機株式会社製、ドクターブレードYD型を用いて、乾燥後の厚みが50μmとなるように行った。その後、熱風乾燥機にて100℃で3分間乾燥させて溶剤を除去し、半硬化状態の粘着剤層を有する粘着シートを形成した。
この粘着シートの片面に第1の剥離シートより剥離性の高い離型処理が施された第2の剥離シート(軽セパレータフィルム、帝人デュポンフィルム(株)製)を貼り合わせ、剥離シート付きの粘着シートである実施例1の粘着シートを得た。
The pressure-sensitive adhesive composition was applied onto a first release sheet (heavy separator film, a polyethylene terephthalate film release-treated by Teijin DuPont Film Co., Ltd.). The coating was performed using a doctor blade YD type manufactured by Yoshimitsu Seiki Co., Ltd. so that the thickness after drying was 50 μm. Then, it was made to dry at 100 degreeC with a hot air dryer for 3 minutes, the solvent was removed, and the adhesive sheet which has an adhesive layer of a semi-hardened state was formed.
A second release sheet (light separator film, manufactured by Teijin DuPont Film Co., Ltd.), which has been subjected to release treatment with higher release property than the first release sheet, is attached to one side of this pressure-sensitive adhesive sheet. The adhesive sheet of Example 1 which is a sheet was obtained.
[実施例2]
多官能単量体をトリメチロールプロパンPO変性トリアクリレート(東亞合成(株)製、M−321)に変更し、さらに重合開始剤をフェニルビス(2,4,6−トリメチルベンゾイル)ホスフィンオキシド(BASFジャパン(株)製、IRGACURE819に変更した以外は実施例1と同様にして、実施例2の粘着シートを得た。
Example 2
The polyfunctional monomer is changed to trimethylolpropane PO modified triacrylate (manufactured by Toagosei Co., Ltd., M-321), and the polymerization initiator is phenylbis (2,4,6-trimethylbenzoyl) phosphine oxide (BASF) A pressure-sensitive adhesive sheet of Example 2 was obtained in the same manner as Example 1 except that the product was changed to IRGACURE 819 manufactured by Japan Co., Ltd.
[実施例3]
架橋剤の添加部数を0.5質量部に変更した以外は実施例1と同様にして、実施例3の粘着シートを得た。
[Example 3]
A pressure-sensitive adhesive sheet of Example 3 was obtained in the same manner as Example 1, except that the number of added parts of the crosslinking agent was changed to 0.5 parts by mass.
[実施例4]
多官能単量体M‐310の添加部数を15質量部に変更し、単官能単量体IBXAの添加部数を15質量部に変更した以外は実施例3と同様にして実施例4の粘着シートを得た。
Example 4
The pressure-sensitive adhesive sheet of Example 4 in the same manner as Example 3 except that the number of added parts of the polyfunctional monomer M-310 is changed to 15 parts by mass and the number of added parts of the monofunctional monomer IBXA is changed to 15 parts by mass. I got
[実施例5]
架橋剤の添加部数を0.5質量部に変更した以外は実施例2と同様にして、実施例3の粘着シートを得た。
[Example 5]
A pressure-sensitive adhesive sheet of Example 3 was obtained in the same manner as in Example 2 except that the number of added parts of the crosslinking agent was changed to 0.5 parts by mass.
[実施例6]
多官能単量体M‐321の添加部数を15質量部に変更し、単官能単量体IBXAの添加部数を15質量部に変更した以外は実施例5と同様にして実施例6の粘着シートを得た。
[Example 6]
The pressure-sensitive adhesive sheet of Example 6 in the same manner as Example 5 except that the addition number of the polyfunctional monomer M-321 is changed to 15 parts by mass and the addition number of the monofunctional monomer IBXA is changed to 15 parts by mass. I got
[比較例1]
多官能単量体をトリメチロールプロパンPO変性トリアクリレート(東亞合成(株)製、M−321)に変更し、単官能単量体を添加しなかった以外は実施例1と同様にして、比較例1の粘着シートを得た。
Comparative Example 1
Comparison was carried out in the same manner as in Example 1, except that the polyfunctional monomer was changed to trimethylolpropane PO-modified triacrylate (manufactured by Toagosei Co., Ltd., M-321) and no monofunctional monomer was added. The adhesive sheet of Example 1 was obtained.
[比較例2]
多官能単量体、単官能単量体および重合開始剤を用いなかった他は実施例1と同様にして、比較例2の粘着シートを得た。
Comparative Example 2
A pressure-sensitive adhesive sheet of Comparative Example 2 was obtained in the same manner as Example 1, except that the polyfunctional monomer, the monofunctional monomer, and the polymerization initiator were not used.
[評価]
<剪断貯蔵弾性率G’>
粘着剤層を200μmとなるように4枚の粘着シート(1枚50μm)を重ねあわせ、半硬化状態の測定用サンプルを作製した。
粘着剤層を200μmとなるように4枚の粘着シート(1枚50μm)を重ねあわせ、重セパレータフィルムである第1の剥離シート側から紫外線を積算光量が3000mJ/cm2となるように照射し、後硬化後の測定用サンプルを作製した。
各測定用サンプルの粘着シートの粘着剤層について、動的粘弾性装置Rheogel―E4000(株式会社ユービーエム製)を用いて、個体剪断モード、周波数1Hz、歪み0.1%の条件で、0℃〜150℃までの温度領域における粘着剤層の剪断貯蔵弾性率G’を測定した。
23℃および75℃における粘着剤層の剪断貯蔵弾性率G’を、下記表1に記載した。
[Evaluation]
<Shear storage modulus G '>
Four pressure-sensitive adhesive sheets (50 μm each) were stacked so that the pressure-sensitive adhesive layer was 200 μm, to prepare a semi-cured measurement sample.
Four pressure-sensitive adhesive sheets (50 μm each) are stacked so that the pressure-sensitive adhesive layer is 200 μm, and ultraviolet rays are irradiated from the side of the first release sheet which is a heavy separator film so that the integrated light quantity is 3000 mJ / cm 2 , The sample for measurement after post-curing was produced.
The pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet of each measurement sample was subjected to a solid shear mode, a frequency of 1 Hz, and a strain of 0.1% at 0 ° C. using a dynamic viscoelasticity apparatus Rheogel-E4000 (manufactured by UBM Ltd.). The shear storage modulus G ′ of the pressure-sensitive adhesive layer in the temperature range of ̃150 ° C. was measured.
The shear storage modulus G ′ of the pressure-sensitive adhesive layer at 23 ° C. and 75 ° C. is described in Table 1 below.
<ゲル分率>
剪断貯蔵弾性率G’の測定と同様にして、半硬化状態の測定用サンプルおよび後硬化後の測定用サンプルを作製した。
各測定用サンプルの粘着シート約0.1gをサンプル瓶に採取し、酢酸エチル30mlを加えて40℃環境下で24時間振とうした。その後、このサンプル瓶の内容物を150メッシュのステンレス製金網でろ別し、金網上の残留物を100℃で1時間乾燥して乾燥重量W(g)を測定した。得られた乾燥重量から下記式1によりゲル分率を求めた。
ゲル分率(質量%)=(乾燥重量/粘着シートの採取重量)×100・・・式1
<Gel fraction>
In the same manner as in the measurement of the shear storage modulus G ′, a sample for measurement of the semi-cured state and a sample for measurement after the post-curing were prepared.
About 0.1 g of an adhesive sheet of each measurement sample was taken in a sample bottle, and 30 ml of ethyl acetate was added and shaken at 40 ° C. for 24 hours. Thereafter, the contents of this sample bottle were filtered off with a 150 mesh stainless steel wire mesh, and the residue on the wire mesh was dried at 100 ° C. for 1 hour to measure the dry weight W (g). The gel fraction was determined by the following formula 1 from the obtained dry weight.
Gel fraction (mass%) = (dry weight / collected weight of adhesive sheet) × 100 .. Formula 1
<プローブタック値>
粘着シートの軽セパレータフィルムである第2の剥離シートを剥がし、PETフィルムに貼着し、半硬化状態の測定用サンプルを作製した。
同様に粘着シートの軽セパレータフィルムである第2の剥離シートを剥がし、PETフィルムに貼着した。次に重セパレータフィルムである第1の剥離シート側から紫外線を積算光量が3000mJ/cm2となるように照射し、後硬化後の測定用サンプルを作製した。
各測定用サンプルを3cm×3cmにカットし、プローブタック試験機にて、下記条件で測定した。
測定機器:NSプローブタックテスター(ニチバン株式会社製)
プローブ直径:5mmφ
プローブ基材:ステンレススチール表面仕上げAA#400研磨による鏡面
ウェイト:19.6g(真鍮製)
プローブ移動速度:1.0cm/秒
デュエルタイム:1秒間
<Probe Tack Value>
The second release sheet, which is a light separator film of the pressure-sensitive adhesive sheet, was peeled off and attached to a PET film to prepare a semi-cured measurement sample.
Similarly, the second release sheet, which is a light separator film of the pressure-sensitive adhesive sheet, was peeled off and attached to a PET film. Next, ultraviolet light was irradiated from the side of the first release sheet, which is a heavy separator film, so that the integrated light amount would be 3000 mJ / cm 2 , to prepare a post-curing measurement sample.
Each measurement sample was cut into 3 cm × 3 cm and measured with a probe tack tester under the following conditions.
Measuring equipment: NS probe tack tester (made by Nichiban Co., Ltd.)
Probe diameter: 5 mmφ
Probe substrate: Stainless steel surface finish AA # 400 polished specular weight: 19.6 g (brass)
Probe movement speed: 1.0 cm / sec Duel time: 1 sec
<端面ベタツキ>
重セパレータフィルムである第1の剥離シート側から紫外線を積算光量が3000mJ/cm2となるように照射したA4サイズの粘着シートを50枚重ねあわせ、後硬化後の裁断用サンプルを作製した。
後硬化後の裁断用サンプルとした粘着シートをギロチン断裁機にて断裁した際のギロチン刃、粘着シートの断裁面である端面を目視判定した。
粘着シートの断裁面である端面から粘着剤のはみ出しがなく、ギロチン刃および断裁面である端面にベタツキがなく良好・・・○
粘着シートの断裁面である端面から粘着剤のはみ出しが酷く、ギロチン刃および断裁面である端面ベタツキが実用上問題となるレベルである・・・×
<End face stickiness>
Fifty A4-sized pressure-sensitive adhesive sheets were irradiated with ultraviolet light from the side of the first release sheet, which is a heavy separator film, so that the integrated light quantity would be 3000 mJ / cm 2, and a post-curing sample for cutting was prepared.
The guillotine blade at the time of cutting the adhesive sheet as a sample for cutting after post-curing with a guillotine cutting machine and the end face which is the cut surface of the adhesive sheet were visually determined.
There is no protrusion of the adhesive from the end face which is the cut surface of the adhesive sheet, and the guillotine blade and the end face which is the cut surface have no stickiness.
There is severe protrusion of the adhesive from the end face that is the cut surface of the adhesive sheet, and the guillotine blade and the end face stickiness that is the cut surface are at a level that causes problems in practical use ... x
<加工性>
まず、粘着剤層の軽セパレータフィルムである第2の剥離シートを剥がし、厚み25μmのPETフィルムに貼合した。
次に重セパレータフィルムである第1の剥離シートを剥がし、PC板に貼着した。PET/粘着剤層/PCの構成のサンプルをオートクレーブ処理(40℃、0.5MPa、30min)し、次いで、PETフィルム側より紫外線を積算光量が3000mJ/cm2となるように照射し、試験サンプルを得た。次いで、試験サンプルの端部をギロチン断裁機を用いてカットし、カット端部をPC板側から手でPETフィルムを剥がすようにこすった。その際の剥がれを測定した。
剥がれ距離が0.05mm未満・・・◎
剥がれ距離が0.05mm以上0.1mm未満・・・〇
剥がれ距離が0.1mm以上・・・×
<Processability>
First, the 2nd peeling sheet which is a light separator film of an adhesive layer was peeled off, and it bonded to a 25-micrometer-thick PET film.
Next, the first release sheet, which was a heavy separator film, was peeled off and attached to a PC board. The sample of the composition of PET / adhesive layer / PC is autoclaved (40 ° C., 0.5 MPa, 30 min), then UV light is irradiated from the PET film side so that the integrated light quantity becomes 3000 mJ / cm 2, and the test sample I got Then, the end of the test sample was cut using a guillotine cutter, and the cut end was rubbed by hand from the PC plate side so as to peel off the PET film. Peeling at that time was measured.
Peeling distance is less than 0.05 mm ... ◎
Peeling distance is 0.05 mm or more and less than 0.1 mm · · · Peeling distance is 0.1 mm or more · · · ×
<耐アウトガス性>
まず、粘着剤層の軽セパレータフィルムである第2の剥離シートを剥がし、厚み50μmのPETフィルムに貼合した。
次に重セパレータフィルムである第1の剥離シートを剥がし、PC板に貼着した。PET/粘着剤層/PCの構成のサンプルをオートクレーブ処理(40℃、0.5MPa、30min)し、次いで、PETフィルム側より紫外線を積算光量が3000mJ/cm2となるように照射し、試験サンプルを得た。試験サンプルを105℃dryおよび85℃85%の環境下に置き、500時間後の気泡、剥がれを観察した。
どちらの環境下においても気泡、剥がれが観察されない・・・○
少なくとも一方の環境下において1.0mm未満の微小気泡が観察された・・・△
少なくとも一方の環境下において1.0mm以上の気泡、剥がれが観察される・・・×
<Outgas resistance>
First, the 2nd peeling sheet which is a light separator film of an adhesive layer was peeled off, and it bonded to a 50-micrometer-thick PET film.
Next, the first release sheet, which was a heavy separator film, was peeled off and attached to a PC board. The sample of the composition of PET / adhesive layer / PC is autoclaved (40 ° C., 0.5 MPa, 30 min), then UV light is irradiated from the PET film side so that the integrated light quantity becomes 3000 mJ / cm 2, and the test sample I got The test sample was placed in an environment of 105 ° C. dry and 85 ° C. 85%, and after 500 hours, bubbles and peeling were observed.
No bubbles or peelings observed under either environment ... ○
Under at least one environment, micro bubbles of less than 1.0 mm were observed ...
Bubbles of 1.0 mm or more and peeling are observed under at least one of the environments ... ×
上記表1より、本発明の粘着シートは、粘着剤層が後硬化性を有し、粘着剤層が後硬化された場合に加工性に優れることがわかった。なお、本発明の粘着シートは、端面ベタツキおよび耐アウトガス性も良好であった。
比較例1より、後硬化後の粘着剤層が本発明で規定する剪断貯蔵弾性率の下限値を下回る場合は、粘着剤層が後硬化された場合に加工性が劣ることがわかった。
比較例2より、後硬化性の無い粘着剤層は本発明で規定する剪断貯蔵弾性率の下限値を下回り、プローブタック値の上限値を上回るために加工性が劣ることがわかった。
From Table 1 above, it was found that the pressure-sensitive adhesive sheet of the present invention is excellent in processability when the pressure-sensitive adhesive layer has post-curing properties and the pressure-sensitive adhesive layer is post-cured. In addition, the adhesive sheet of this invention was also favorable in the end surface stickiness and outgassing resistance.
From Comparative Example 1, when the pressure-sensitive adhesive layer after post-curing was less than the lower limit value of the shear storage modulus defined in the present invention, it was found that the processability was inferior when the pressure-sensitive adhesive layer was post-cured.
From Comparative Example 2, it was found that the pressure-sensitive adhesive layer having no post-curing property is inferior to the lower limit value of the shear storage modulus defined in the present invention and is inferior in processability because it exceeds the upper limit value of the probe tack value.
1 粘着シート
11 粘着剤層
12a 透明基材または剥離シート
12b 剥離シート
20 積層体
21 粘着シート
22 基材
24 光学部材
27a、27b、27c、27d 段差部
DESCRIPTION OF SYMBOLS 1 adhesive sheet 11
Claims (14)
前記粘着剤組成物が架橋性アクリル重合体、架橋剤、分子内に反応性二重結合を2つ以上有する多官能単量体、分子内に反応性二重結合を1つ有する単官能単量体および重合開始剤を含有し、
前記単官能単量体を重合した場合のホモポリマーのガラス転移温度(Tg)が50℃以上200℃未満であり、
前記粘着剤層は後硬化性を有し、
前記粘着剤層が後硬化された場合に下記物性群(1)を満たす、粘着シート。
物性群(1):23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×106[Pa]以上であり、75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×105[Pa]以上であり、23℃かつ下記測定条件で測定されるプローブタック値が1.5N/5mmφ以下である。
(プローブタック値の測定条件)
測定機器:NSプローブタックテスター(ニチバン株式会社製)
プローブ直径:5mmφ
プローブ基材:ステンレススチール表面仕上げAA#400研磨による鏡面
ウェイト:19.6±0.2g(真鍮製)
プローブ移動速度:1.0cm/秒
デュエルタイム:1秒間。 A pressure-sensitive adhesive layer in which the pressure-sensitive adhesive composition is in a semi-cured state,
The pressure-sensitive adhesive composition is a crosslinkable acrylic polymer, a crosslinking agent, a polyfunctional monomer having two or more reactive double bonds in the molecule, and a monofunctional unit amount having one reactive double bond in the molecule Body and a polymerization initiator,
The glass transition temperature (Tg) of the homopolymer when the monofunctional monomer is polymerized is 50 ° C. or more and less than 200 ° C.,
The pressure-sensitive adhesive layer has post-curing properties,
A pressure-sensitive adhesive sheet satisfying the following physical property group (1) when the pressure-sensitive adhesive layer is post-cured.
Physical property group (1): Shear storage modulus G ′ measured at 23 ° C. and frequency 1 Hz is 1.0 × 10 6 [Pa] or more, and shear storage modulus G ′ measured at 75 ° C. and frequency 1 Hz Is 1.0 × 10 5 [Pa] or more, and the probe tack value measured at 23 ° C. and the following measurement conditions is 1.5 N / 5 mmφ or less.
(Measurement condition of probe tack value)
Measuring equipment: NS probe tack tester (made by Nichiban Co., Ltd.)
Probe diameter: 5 mmφ
Probe base material: Specular weight by stainless steel surface finish AA # 400 polishing: 19.6 ± 0.2 g (made of brass)
Probe moving speed: 1.0 cm / sec Duel time: 1 sec.
物性群(2):23℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が8.0×105[Pa]以下であり、75℃かつ周波数1Hzで測定される剪断貯蔵弾性率G’が1.0×105[Pa]以下であり、23℃かつ前記測定条件で測定されるプローブタック値が2.0N/5mmφ以上。 The pressure-sensitive adhesive sheet according to claim 1, wherein the pressure-sensitive adhesive layer satisfies the following physical property group (2) in a semi-cured state.
Physical property group (2): Shear storage modulus G ′ measured at 23 ° C. and frequency 1 Hz is 8.0 × 10 5 [Pa] or less, and shear storage modulus G ′ measured at 75 ° C. and frequency 1 Hz Is 1.0 × 10 5 [Pa] or less, and a probe tack value measured at 23 ° C. and under the above measurement conditions is 2.0 N / 5 mmφ or more.
前記粘着剤層が後硬化された場合に後硬化後のゲル分率が、半硬化状態でのゲル分率より5質量%以上高くなる、請求項1〜3のいずれか一項に記載の粘着シート。 The gel fraction in the semi-cured state of the pressure-sensitive adhesive layer is 0% by mass or more and less than 70% by mass, and
The adhesion according to any one of claims 1 to 3, wherein when the pressure-sensitive adhesive layer is post-cured, the gel fraction after post-curing is 5% by mass or more higher than the gel fraction in the semi-cured state. Sheet.