JP2018167390A - Saw wire and cut-off device - Google Patents

Abstract

To provide a saw wire that is thinner than a piano wire, has approximately twice the elastic modulus of the piano wire and has a tensile strength equal to or higher than that of a piano wire.SOLUTION: A saw wire 10 includes a metal wire made of alloy made of rhenium and tungsten. In the metal wire, a percentage content of rhenium is 0.1 wt% or more and 10 wt% or less. The metal wire has a wire diameter of 60 μm or less.SELECTED DRAWING: Figure 3

Description

  The present invention relates to a saw wire and a cutting device including the saw wire.

  Conventionally, a multi-wire saw that slices a silicon ingot using a wire made of a piano wire is known (see, for example, Patent Document 1).

JP 2008-213111 A

  In the wire saw, scraps corresponding to the wire diameter are generated. The above-mentioned conventional multi-wire saw uses a wire made of piano wire, but it is difficult to make a piano wire thin. At present, it is difficult to manufacture a piano wire having a wire diameter of less than 60 μm, and the elastic modulus of the piano wire. Is 150 GPa to 250 GPa, so that even if the diameter can be reduced, wrinkles occur during slicing. For this reason, the thinned piano wire is not suitable for slicing a wire saw.

  Therefore, the present invention provides a saw wire that is thinner than a piano wire and has a modulus of elasticity about twice that of the piano wire and has a tensile strength equal to or higher than that of the piano wire, and a cutting device including the saw wire. With the goal.

  In order to achieve the above object, a saw wire according to one embodiment of the present invention includes a metal wire made of an alloy of rhenium and tungsten, and the rhenium content of the metal wire is 0.1 wt% or more and 10 wt% or less. The diameter of the metal wire is 60 μm or less.

  The saw wire according to one embodiment of the present invention includes a metal wire made of tungsten doped with potassium, and the potassium content of the metal wire is 0.005 wt% or more and 0.010 wt% or less, The wire diameter of the metal wire is 60 μm or less.

  Moreover, the cutting device which concerns on 1 aspect of this invention is equipped with the said saw wire.

  According to the present invention, there is provided a saw wire that is thinner than a piano wire and has an elastic modulus approximately twice that of the piano wire, and has a tensile strength equal to or higher than that of the piano wire, and a cutting device including the saw wire. Can do.

It is a perspective view of the cutting device concerning an embodiment. It is sectional drawing which shows the mode of the slice of the ingot by the cutting device which concerns on embodiment. It is a state transition diagram which shows the manufacturing method of the saw wire which concerns on embodiment.

  Below, the saw wire and the cutting device which concern on embodiment of this invention are demonstrated in detail using drawing. Each of the embodiments described below shows a specific example of the present invention. Therefore, numerical values, shapes, materials, components, arrangement and connection forms of components, steps, order of steps, and the like shown in the following embodiments are merely examples, and are not intended to limit the present invention. Therefore, among the constituent elements in the following embodiments, constituent elements that are not described in the independent claims showing the highest concept of the present invention are described as optional constituent elements.

  Each figure is a mimetic diagram and is not necessarily illustrated strictly. Therefore, for example, the scales and the like do not necessarily match in each drawing. Moreover, in each figure, the same code | symbol is attached | subjected about the substantially same structure, The overlapping description is abbreviate | omitted or simplified.

  Further, in this specification, terms indicating a relationship between elements such as parallel or equal, terms indicating a shape of an element such as a circle, and numerical ranges are not expressions expressing only a strict meaning, In other words, it is an expression meaning that a difference of about several percent, for example, is included.

(Embodiment)
[Cutting device]
First, the outline | summary of a cutting device provided with the saw wire which concerns on this Embodiment is demonstrated using FIG. FIG. 1 is a perspective view of a cutting device 1 according to the present embodiment.

  As shown in FIG. 1, the cutting device 1 is a multi-wire saw including a plurality of saw wires 10. The cutting device 1 manufactures a wafer by, for example, cutting the ingot 20 into a thin plate shape. The ingot 20 is, for example, a silicon ingot composed of single crystal silicon. Specifically, the cutting device 1 slices the ingot 20 with a plurality of saw wires 10 to simultaneously manufacture a plurality of silicon wafers.

  The ingot 20 is not limited to a silicon ingot, and may be another ingot such as silicon carbide or sapphire. Alternatively, the object to be cut by the cutting device 1 may be concrete or glass.

  As shown in FIG. 1, the cutting device 1 further includes two guide rollers 2, a support portion 3, and a tension relaxation device 4.

  A plurality of saw wires 10 are wound around the two guide rollers 2. The two guide rollers 2 rotate the plurality of saw wires 10 at a predetermined speed by rotating in a state where the plurality of saw wires 10 are straightly stretched with a predetermined tension. The plurality of saw wires 10 are parallel to each other and arranged at equal intervals. Specifically, each of the two guide rollers 2 is provided with a plurality of grooves into which the saw wire 10 is inserted at a predetermined pitch. The pitch of the grooves is determined according to the thickness of the wafer to be cut out. The width of the groove is substantially the same as the wire diameter φ of the saw wire 10.

  Note that the cutting device 1 may include three or more guide rollers 2. A plurality of saw wires 10 may be wound around three or more guide rollers 2.

  The support part 3 supports the ingot 20 which is a cutting object. The support 3 pushes the ingot 20 toward the plurality of saw wires 10, so that the ingot 20 is sliced by the plurality of saw wires 10.

  The tension relaxation device 4 is a device that relaxes the tension applied to the saw wire 10. For example, the tension relaxation device 4 is an elastic body such as a helical spring or a leaf spring. As shown in FIG. 1, the tension relaxation apparatus 4 which is a helical spring, for example, has one end connected to the guide roller 2 and the other end fixed to a predetermined wall surface. By adjusting the position of the guide roller 2 by the tension relaxation device 4, the tension applied to the saw wire 10 can be relaxed.

  Although not shown, the cutting device 1 is a loose abrasive type cutting device, and may include a supply device that supplies slurry to the plurality of saw wires 10. The slurry is obtained by dispersing abrasive grains in a cutting fluid such as a coolant. Since the abrasive grains contained in the slurry adhere to the saw wire 10, the ingot 20 can be easily cut.

  FIG. 2 is a cross-sectional view showing a state of slicing the ingot 20 by the cutting device 1 according to the present embodiment. FIG. 2 shows a part of a cross section taken along line II-II shown in FIG. 1 and perpendicular to the extending direction of the saw wire 10. Specifically, a state in which the ingot 20 is sliced by three saw wires 10 among the plurality of saw wires 10 is shown.

  By pushing the ingot 20 toward the plurality of saw wires 10, the ingot 20 is simultaneously divided into a plurality of divided pieces 21 by the plurality of saw wires 10. The gap 22 between the adjacent divided pieces 21 is a space formed by scraping the ingot 20 by the saw wire 10. That is, the size of the gap 22 corresponds to the loss of the ingot 20.

  The width d of the gap 22 depends on the wire diameter φ of the saw wire 10. That is, as the wire diameter φ of the saw wire 10 increases, the width d increases and the loss of the ingot 20 increases. As the wire diameter φ of the saw wire 10 is smaller, the width d is smaller and the loss of the ingot 20 is smaller.

  Specifically, the width d of the gap 22 is larger than the wire diameter φ. The difference between the width d and the wire diameter φ is a size that depends on the size of the abrasive grains adhering to the saw wire 10 and the vibration amplitude of the saw wire 10 during rotation. At this time, the swing width of the saw wire 10 can be suppressed by strongly stretching the saw wire 10. The higher the tensile strength of the saw wire 10 and the higher the elastic modulus, the stronger the saw wire 10 can be stretched. For this reason, the swinging width of the saw wire 10 is reduced, the width d of the gap 22 can be reduced, and the loss of the ingot 20 can be further reduced.

  The thickness D of the split piece 21 depends on the arrangement interval of the plurality of saw wires 10. For this reason, the plurality of saw wires 10 are arranged at intervals obtained by adding a desired thickness D and a predetermined margin. Specifically, the margin is a difference between the width d and the wire diameter φ, and is a value determined according to the swing width of the saw wire 10 and the grain size of the abrasive grains.

  From the above, it can be seen that the wire diameter φ, the tensile strength, and the elastic modulus of the saw wire 10 are important parameters in order to reduce the loss of the ingot 20. Specifically, the loss of the ingot 20 can be reduced by reducing the wire diameter φ of the saw wire 10 or increasing the tensile strength and the elastic modulus of the saw wire 10. The saw wire 10 according to the present embodiment generally has a wire diameter φ smaller than that of a piano wire having a wire diameter of about 80 μm, and is generally equal to or greater than a piano wire having a tensile strength of 3500 MPa or more. Has tensile strength.

  Below, the structure and manufacturing method of the saw wire 10 are demonstrated.

[Saw wire]
The saw wire 10 according to the present embodiment includes a metal wire made of an alloy (ReW) of rhenium (Re) and tungsten (W). In the present embodiment, the saw wire 10 is a metal wire itself.

  The saw wire 10 contains tungsten as a main component and contains rhenium at a predetermined ratio. The rhenium content of the saw wire 10 is not less than 0.1 wt% and not more than 10 wt%. For example, the rhenium content may be 0.5 wt% or more and 5 wt% or less, and is 3 wt% as an example, but may be 1 wt%. Increasing the rhenium content increases the tensile strength of the saw wire 10. On the other hand, when the rhenium content is too high, it is difficult to make the saw wire 10 thinner.

  A metal wire made of a ReW alloy has a higher tensile strength as the wire diameter φ decreases. That is, by using a metal wire made of a ReW alloy, the saw wire 10 having a small wire diameter φ and high tensile strength can be realized, and loss of the ingot 20 can be suppressed.

  Specifically, the tensile strength of the saw wire 10 is 3500 MPa or more. For example, the tensile strength of the saw wire 10 is not less than 3500 MPa and not more than 5000 MPa. For example, the tensile strength of the saw wire 10 may be 4000 MPa or more.

  The elastic modulus of the saw wire 10 is not less than 350 GPa and not more than 450 GPa. The elastic modulus is a longitudinal elastic modulus. That is, the saw wire 10 has an elastic modulus about twice that of the piano wire.

  The wire diameter φ of the saw wire 10 is 60 μm or less. For example, the wire diameter φ of the saw wire 10 may be 40 μm or less, or 30 μm or less. The wire diameter φ of the saw wire 10 is specifically 20 μm, but may be 10 μm. When diamond particles are attached, the wire diameter φ of the saw wire 10 may be, for example, 10 μm or more. The saw wire 10 has a uniform wire diameter φ. Since the wire diameter φ of the saw wire 10 is 60 μm or less, the saw wire 10 has flexibility and is easily bent sufficiently. For this reason, the saw wire 10 can be easily wound between the guide rollers 2.

  The saw wire 10 is, for example, a metal wire having a circular cross section perpendicular to the extending direction of the wire, but is not limited thereto. The cross-sectional shape of the saw wire 10 may be a rectangle such as a square or an ellipse.

[Saw wire manufacturing method]
Below, the manufacturing method of the saw wire 10 which has the said characteristic is demonstrated using FIG. FIG. 3 is a state transition diagram showing a method for manufacturing the saw wire 10 according to the present embodiment.

  First, as shown in FIG. 3A, tungsten powder 11a and rhenium powder 11b are prepared at a predetermined ratio. Specifically, rhenium powder 11b is prepared in a range of 0.1% to 10% of the total weight of tungsten powder 11a and rhenium powder 11b, and the rest is made tungsten powder 11a. The average particle diameter of each of the tungsten powder 11a and the rhenium powder 11b is, for example, 5 μm, but is not limited thereto.

  Next, a ReW ingot made of an alloy of tungsten and rhenium is produced by pressing and sintering (sintering) the mixture of the tungsten powder 11a and the rhenium powder 11b. A swaging process for forging and compressing the ingot from the surroundings to perform extension is performed on the ReW ingot, thereby producing a wire-like ReW line 12 as shown in FIG. For example, a ReW ingot that is a sintered body has a wire diameter of about 15 mm, whereas a wire-like ReW wire 12 has a wire diameter of about 3 mm.

  Next, as shown in FIG. 3C, a drawing process using a wire drawing die is performed.

  Specifically, first, as shown in (c1) of FIG. 3, the ReW line 12 is annealed. Specifically, not only the ReW line 12 is directly heated by the burner, but also the ReW line 12 is heated while passing an electric current. The annealing process is performed in order to remove processing strain caused by swaging processing or drawing processing.

  Next, as shown in (c2) of FIG. 3, the ReW line 12 is drawn using the wire drawing die 30, that is, the wire is drawn. Since the ReW wire 12 is heated and softened by the previous annealing step, the wire drawing can be easily performed. As the ReW line 12 is thinned, its tensile strength increases. That is, the ReW line 13 that has been thinned by the drawing process has higher tensile strength than the ReW line 12. In addition, although the wire diameter of the ReW line 13 is 0.6 mm, for example, it is not restricted to this.

  Next, as shown in (c3) of FIG. 3, dice exchange is performed. Specifically, a wire drawing die 31 having a smaller diameter than the wire drawing die 30 is selected as a die used for the next wire drawing process. The wire drawing dies 30 and 31 are diamond dies composed of, for example, sintered diamond or single crystal diamond.

  3 (c1) to (c3) are repeatedly performed until the wire diameter of the ReW wire 13 reaches a desired wire diameter φ (specifically, 60 μm or less). At this time, the wire drawing step shown in (c2) of FIG. 3 is performed according to the wire diameter of the target ReW wire, the shape and hardness of the wire drawing die 30 or 31, the lubricant to be used, and the temperature of the ReW wire. It is done by adjusting etc.

  Similarly, in the annealing step shown in FIG. 3 (c1), the annealing conditions are adjusted according to the diameter of the target ReW line. Specifically, annealing is performed at a higher temperature as the diameter of the ReW line is larger, and annealing is performed at a lower temperature as the diameter of the ReW line is smaller. For example, when the wire diameter of the ReW line is large, specifically, annealing is performed at a temperature of 1400 ° C. to 1800 ° C. in the annealing process in the first drawing process. In the final annealing process at the time of final drawing to obtain a desired wire diameter, heating is performed at a temperature of 1200 ° C to 1500 ° C. In the final annealing step, it is not necessary to energize the ReW line.

  Further, the annealing step may be omitted when the drawing process is repeated. For example, the final annealing step may be omitted. Specifically, the final annealing step may be omitted, and the shape and hardness of the lubricant and wire drawing die may be adjusted.

  Finally, as shown in FIG. 3D, the surface of the ReW line 14 is smoothed by performing electrolytic polishing on the ReW line 14 having a desired wire diameter φ. As shown in FIG. 3 (d), the electrolytic polishing step is performed by immersing the ReW wire 14 and the counter electrode 41 such as a carbon rod in an electrolytic solution 40 such as an aqueous sodium hydroxide solution. This is performed by energizing between the counter electrode 41.

  Through the above steps, the saw wire 10 is manufactured as shown in FIG.

  FIG. 3 schematically shows each step of the method for manufacturing the saw wire 10. Each process may be performed individually, or each process may be performed inline. For example, a plurality of wire drawing dies are arranged in order of decreasing diameter on the production line, and a heating device or the like that performs an annealing process is arranged between the wire drawing dies, so that the wire drawing dies having the smallest diameter are arranged. An electropolishing apparatus or the like may be disposed after the step.

[Effects, etc.]
As described above, the saw wire 10 according to the present embodiment includes a metal wire made of an alloy of rhenium and tungsten, and the rhenium content of the metal wire is 0.1 wt% or more and 10 wt% or less, The elastic modulus of the wire is 350 GPa or more and 450 GPa or less, the tensile strength of the metal wire is 3500 MPa or more, and the wire diameter of the metal wire is 60 μm or less. For example, the tensile strength of a metal wire is 5000 MPa or less.

  Thus, since the metal wire contains tungsten as a main component, the tensile strength increases as the wire becomes thinner, and becomes harder to break. Furthermore, since the metal wire contains rhenium, the strength can be increased as compared with the pure tungsten wire. Thereby, even if it makes a metal wire thin, it becomes difficult to cut | disconnect, Therefore The tensile strength equivalent to or more than a piano wire is realizable. Therefore, according to the present embodiment, it is possible to provide the saw wire 10 that is thinner than the piano wire and has an elastic modulus approximately twice that of the piano wire and has a tensile strength equal to or higher than that of the piano wire.

  Since the tensile strength of the saw wire 10 according to the present embodiment is high, it can be stretched between the guide rollers 2 with a strong tension. For this reason, vibration of the saw wire 10 when the ingot 20 is cut can be suppressed.

  Thus, since the wire diameter of the saw wire 10 is small, the tensile strength is high, and the elastic modulus is high, the shavings generated when the ingot 20 is sliced, that is, the loss of the ingot 20 can be reduced. Therefore, the number of wafers cut out from one ingot 20 can be increased.

  Since the alloy wire of rhenium tungsten has a feature that the tensile strength increases by thinning, it is very useful that the saw wire 10 is composed of an alloy wire of rhenium tungsten.

  Moreover, the cutting device 1 according to the present embodiment includes a saw wire 10.

  Thereby, since the wire diameter of the saw wire 10 becomes small, the number of wafers cut out from one ingot 20 can be increased. Further, it is possible to reduce the shavings generated when the ingot 20 is sliced. Limited resources such as the material of the ingot 20 can be used effectively.

  For example, the cutting device 1 includes a tension relaxation device 4 that relaxes the tension applied to the saw wire 10.

  Thereby, since it can suppress that strong tension | tensile_strength is applied to the saw wire 10, the disconnection etc. of the saw wire 10 can be suppressed.

  (Modification) Next, a modification of the above embodiment will be described. Below, it demonstrates centering around difference with said embodiment, description of a common point is abbreviate | omitted or simplified.

  The saw wire according to this modification includes a metal wire made of tungsten doped with potassium (K) instead of the ReW alloy. The saw wire according to this modification is a metal wire itself.

  The saw wire contains tungsten as a main component and contains potassium at a predetermined ratio. The content rate of potassium of saw wire is 0.005 wt% or more and 0.010 wt% or less.

  A metal wire composed of tungsten doped with potassium (potassium-doped tungsten wire) has a higher tensile strength as the wire diameter φ decreases. That is, by using a potassium-doped tungsten wire, a saw wire having a small wire diameter φ and high tensile strength can be realized, and loss of the ingot 20 can be suppressed.

  The tensile strength, elastic modulus, wire diameter φ, and the like of the saw wire according to this modification are the same as those of the saw wire 10 according to the embodiment.

  As described above, the saw wire according to this modification includes a metal wire made of tungsten doped with potassium, and the content of potassium in the metal wire is 0.005 wt% or more and 0.010 wt% or less. The elastic modulus of the wire is 350 GPa or more and 450 GPa or less, the tensile strength of the metal wire is 3500 MPa or more, and the wire diameter of the metal wire is 60 μm or less.

  Thus, when tungsten contains a trace amount of potassium, crystal grain growth in the radial direction of the metal wire is suppressed. For this reason, the saw wire according to this modification has higher strength at high temperatures than pure tungsten.

(Other)
As described above, the saw wire and the cutting device according to the present invention have been described based on the above-described embodiments and modifications. However, the present invention is not limited to the above-described embodiments.

  For example, in the above-described embodiment and modification, an example in which the saw wire 10 is a metal wire itself has been described, but the present invention is not limited thereto. The saw wire 10 may include a metal wire and a plurality of abrasive grains attached to the surface of the metal wire. That is, the saw wire 10 may be a wire used in the free abrasive method as shown in the embodiment, or may be a wire used in the fixed abrasive method. The abrasive grains are, for example, diamond or CBN (legislative boron nitride).

  For example, the cutting device 1 may not be a multi-wire saw, and may be a wire saw device that cuts out wafers one by one by slicing the ingot 20 with one saw wire 10. Moreover, the cutting device 1 shown in FIG. 1 is only an example, and for example, the tension relaxation device 4 may not be provided.

  In addition, the embodiment can be realized by arbitrarily combining the components and functions in each embodiment without departing from the scope of the present invention, or a form obtained by subjecting each embodiment to various modifications conceived by those skilled in the art. Forms are also included in the present invention.

1 Cutting device 4 Strain relief device 10 Saw wire

Claims (5)

It has a metal wire made of an alloy of rhenium and tungsten,
The rhenium content of the metal wire is 0.1 wt% or more and 10 wt% or less,
The wire diameter of the said metal wire is 60 micrometers or less. Comprising a metal wire made of tungsten doped with potassium;
The potassium content of the metal wire is 0.005 wt% or more and 0.010 wt% or less,
The wire diameter of the said metal wire is 60 micrometers or less. The saw wire according to claim 1 or 2, wherein the metal wire has a tensile strength of 5000 MPa or less.   A cutting device provided with the saw wire of any one of Claims 1-3. The cutting device according to claim 4, further comprising a tension relaxation device that relaxes a tension applied to the saw wire.